By James O. Lewis

Gravity drainage is the self-propulsion of oil downward in the reservoir rock. Under favorable natural and operational conditions, it has been found to effect recoveries comparable to water displacement. With modern technical knowledge, the operator can often make a choice between dissolved gas drive, water drive and gravity drainage as the principal recovery agent in a reservoir. It is desirable that the opeator be able to determine which of the three agents will be most effective under each set of conditions. So far, gravity drainage has received less consideration than the other two. In this paper. an endeavor is made to set forth some of the principles of gravity drainage, to point out the types of reservoirs favorable for it, and to show how it may be applied in them. Field examples are described and discussed. Introduction Since early in the history of the oil industry, it has been recognized that gravity is one of the three important natural forces for expelling oil from the reservoir rock. As knowledge of the technology of oil recovery progressed, ideas changed with respect to the relative importance of the three forces and with respect to the manners in which they functioned. For a time, disproportionate emphasis was placed on the importance and function of gas and the need for conserving gas pressures. More recently, disproportionate emphasis has been placed on encroaching edge water. Only lately has there been evidence that the function and importance of gravity was to receive due consideration. Study of this neglected phase of oil recovery is needed to round out our knowledge of reservoir behaviors and to gain a balanced viewpoint of the interplay of forces that may operate in varying importance in reservoirs. The purpose of this paper is to discuss mainly in a qualitative way, the functions of gravity, to present some concrete instances where it has been important and to raise some questions that should be investigated further. Oil-recovery Agents The important natural agents for effecting oil recovery that may be originally available in a reservoir are gas, both dissolved in the oil and free in gas caps, encroaching edge water and gravity. Each of these agents can act in a dual capacity—physically to overcome the surface energies that hold the oil within the pores and mechanically to overcome viscous . resistance and to propel the oil through the porous reservoir rock to the wells. Advancing edge water displaces the oil from the pores and lifts it updip to structurally lower wells. Gravity drains the oil from the pores and flows it downdip to the wells. Gas displaces oil from the pores, entrains it in the gas stream and flows it to the wells, but gas in solution also affects the physical properties of the oil and thus can influence oil recovery by the other agents, whether or not the mechanical energy in the gas is utilized. Of the two functions of these agents, the more important is the ability to dis-

Jan 1, 1944

By James O. Lewis

Gravity drainage is the self-propulsion of oil downward in the reservoir rock. Under favorable natural and operational conditions, it has been found to effect recoveries comparable to water displacement. With modern technical knowledge, the operator can often make a choice between dissolved gas drive, water drive and gravity drainage as the principal recovery agent in a reservoir. It is desirable that the opeator be able to determine which of the three agents will be most effective under each set of conditions. So far, gravity drainage has received less consideration than the other two. In this paper. an endeavor is made to set forth some of the principles of gravity drainage, to point out the types of reservoirs favorable for it, and to show how it may be applied in them. Field examples are described and discussed. Introduction Since early in the history of the oil industry, it has been recognized that gravity is one of the three important natural forces for expelling oil from the reservoir rock. As knowledge of the technology of oil recovery progressed, ideas changed with respect to the relative importance of the three forces and with respect to the manners in which they functioned. For a time, disproportionate emphasis was placed on the importance and function of gas and the need for conserving gas pressures. More recently, disproportionate emphasis has been placed on encroaching edge water. Only lately has there been evidence that the function and importance of gravity was to receive due consideration. Study of this neglected phase of oil recovery is needed to round out our knowledge of reservoir behaviors and to gain a balanced viewpoint of the interplay of forces that may operate in varying importance in reservoirs. The purpose of this paper is to discuss mainly in a qualitative way, the functions of gravity, to present some concrete instances where it has been important and to raise some questions that should be investigated further. Oil-recovery Agents The important natural agents for effecting oil recovery that may be originally available in a reservoir are gas, both dissolved in the oil and free in gas caps, encroaching edge water and gravity. Each of these agents can act in a dual capacity—physically to overcome the surface energies that hold the oil within the pores and mechanically to overcome viscous . resistance and to propel the oil through the porous reservoir rock to the wells. Advancing edge water displaces the oil from the pores and lifts it updip to structurally lower wells. Gravity drains the oil from the pores and flows it downdip to the wells. Gas displaces oil from the pores, entrains it in the gas stream and flows it to the wells, but gas in solution also affects the physical properties of the oil and thus can influence oil recovery by the other agents, whether or not the mechanical energy in the gas is utilized. Of the two functions of these agents, the more important is the ability to dis-

Jan 1, 1944

By K. K. Rao, M. E. Nicholson

IN a recent paper on the solubility of carbon in Ni-Cu alloys,' Nicholson reported that the carbon solubility appeared to be limited by the electronic structure of the alloys and that the solubility was propor- tional to the density of states at the Fermi surface of the "3d" band. In order to determine whether or not this relationship is a general one, the study has been extended to other systems. One of these is the CO-Ni system. This system was chosen for study because 1) it is adjacent to Ni-Cu system in the periodic table, 2) the alloys of cobalt and nickel do not form stable carbides at 1000°C, and 3) the system exhibits no pronounced change (less than 1 pct) in lattice parameter from cobalt to nickel,' see Fig. 1. The alloys were prepared from -200-mesh 99.92 pct Ni furnished by the International Nickel Co. and spectroscopically pure -200-mesh cobalt sponge obtained from Johns on-Matthey and Co. The powders were weighed, mixed, and pressed using a pressure of 40,000 psi. The samples were sintered for 24 hr at 900° C in dry hydrogen and then cold rolled to a thickness of 0.010 in. (Samples containing more than 70 wt pct Co had to be annealed after cold reductions of about 20 pct to avoid cracking.) The alloys were carburized at 1000°C in an alun-durn boat containing Acheson AUC powdered graphite in an atmosphere of carbon monoxide cylinder gas which had been passed through Ascarite to remove carbon dioxide. After carburizing for either 12 or 24 hr the samples were moved to a cool zone of the furnace to cool. Cooling required about 5 min. The samples were filed to remove about 0.005 in. from the surface and then analyzed using a conventional combustion-gravimetric analytic method. The results of this investigation are shown in the lower portion of Fig. 1 and Tabulated in Table I. The nickel percentages for these alloys were determined from the weights of the powders from which the alloys were made. The solubility of carbon in pure cobalt at 1000°C (fcc) is 0.25 wt pct. This is somewhat less than the 0.33 wt pct measured by Boecker.3 From his data, it would appear Boecker's samples were supersaturated before the equilibrating treatment and that a 20-min treatment was not long enough to achieve equilibrium. Since in the present investigation the 12 and 24 treatments produced essentially equal carbon contents, our figure is presumed to represent more nearly the equilibrium value. The solubility of carbon in nickel of 0.19 wt pct agrees quite well with the value of 0.21 wt pct

Jan 1, 1963

By M. J. Marcinkowski, D. Koskimaki, A. S. Sastri

THIS is the second in a trilogy of investigations carried out in order to understand the solid state transformations and their accompanying effects on the deformation behavior of near-equiatomic Ni-Ti alloys. The first stage of this effort has dealt with the strictly martensitic structures obtainable in these alloys, i.e., those in which diffusion processes were not involved.1,2 These martensites could be produced either by rapid quenching or by plastic deformation of the originally B2 type phase. The present investigation, on the other hand, will deal with those transformations in Ni-Ti which do involve diffusion. A majority of investigators3-10 have shown that the B2 modification of TiNi, which is stable at elevated temperatures, decomposes into one or both of the intermetallic compounds NiTi2 and Ni3Ti below about 650°C. On the other hand, this has been disputed by several Workers was undertaken in order to resolve this discrepancy, as well as to shed more light on the nonmar-tensitic decomposition of B2 NiTi. EXPERIMENTAL PROCEDURE Sample preparation, fabrication, and examination were the same as those described previously in Ref. 2. In addition to the 50 at. pct Ni (55.06 wt pct) hypoeu-tectoid alloy used previously, a second hypereutectoid alloy containing 54.4 at. pct Ni (60 wt pct) was also prepared for this study. RESULTS AND DISCUSSION The equilibrium diagram for the Ni-Ti alloy system in the vicinity of Ni-Ti is shown in Fig. 1. The solid lines have been established by the work of Poole and ~ume-Ftothery4 whereas the dotted lines are based on findings obtained in the present investigation as described below. Structure and Morphology. Fig. 2(a) shows a bright field transmission electron micrograph of a two-phase structure obtained in a polycrystalline Ni-Ti alloy that was furnace cooled (approx 200°C per hr) from 1050' to about 300°C. Large plate-shaped precipitates can be observed in a matrix which was found by electron diffraction to possess the high temperature B2 structure. A selected area diffraction pattern of the region covered by Fig. 2(a) is shown in Fig. 2(b), while Fig. 2(c) is a detailed schematic interpretation of Fig. 2(b). The B2 matrix reflections are illustrated by squares while those of the precipitate are shown as circles. The d values associated with the precipitate reflections could be determined quite accurately since the reflections from the B2 matrix, for which the lattice constant is known precisely, were simultaneously present in the diffraction patterns. All of the reflections

Jan 1, 1970

By T. K. Redden

Protective coatings based on the formation of a surface coating of nickel aluminide (NiAl) were applied to the nickel-base superalloys IN 100, SEL 15, and U-700. Coated specimens were exposed to an oxidizing environment at temperatures between 1600 and 2200 F for times up to 1000 hr. The oxidation resistance and stability of the coating were evaluated by weight gain measurements, metallographic examination, and X-ray diffraction study of surface oxides and coating. The composition of the coating and diffusion zone was determined by electron microprobe traverse of samples before and after high-temperature exposure. Intermediate phases formed in the coating and diffusion zone were identified by X-ray diffraction in situ and after electrolytic extraction. The outer coating was found to consist of the inter-metallic compound, NiAl, while the diffusion zone contained MC, M23C6 or M6C carbides, and a phase in a matrix of NiAl + Nidl. Oxidation resulted in formation of an A1203 n'ch scale containing some Tz02. Depletion of aluminum during oxidation resulted in degradation of the outer coating to Ni3Al and the nickel alloy matrix. Diffusion of aluminum into the base metal was found to be slight and did not influence coating life significantly. The o formed in the diffusion zone during coating decomposed during elevated-temperature exposure to form stable carbide phases characteristic of the base metal. Diffusion zone phase changes were found to have no effect on the life of the aluminide coating in the oxidizing envzron?nent. THE oxidation resistance of many high-strength nickel-base superalloys is inadequate for extended exposure at temperatures above about 1600°F. In addition, some applications for these materials require that they be exposed to environments containing sulfur compounds and sodium salts which can cause surface attalk known as sulfidation or hot corrosion. In order to provide the necessary corrosion resistance to the high-strength alloys, protective coatings based on an aluminizing process have been developed. These processes, usually based on a pack cementation technique, result in the formation of a NiAl-rich outer coating layer either during the coating process or by a subsequent diffusion treatment. The performance of the aluminide coatings is affected by interactions between the coating layer and the base metal both during the coating process and during subsequent exposure at elevated temperatures. Knowledge of these interactions is required to guide the development of coatings capable of longer life and improved reliability. Goward et al.' recently reported the metallurgical factors which influence coating per- formance on MAR-M200. The present work is concerned with correlating the interactions and performance of coating compositions on several representative materials. EXPERIMENTAL PROCEDURES Materials. Three cast nickel-base superalloys which are used for turbine buckets in air-breathing engines were studied: IN 100, U-700, and SEL 15. Their chemical compositions are given in Table I. The alloys were vacuum-induction-melted and cast to slabs approximately 0.3 in. thick from which rectangular specimens 0.25 by 0.5 by 1 in. were machined. Coating Procedures. The machined specimens were coated by CODEP processes which were developed at the author's laboratory. These are based on pack cementation in various media to deposit either aluminum or aluminum in combination with titanium. The coating process which deposits only aluminum is designated CODEP-C, while the CODEP-D process deposits titanium in combination with aluminum. The CODEP-D process was applied only to IN 100. Both CODEP processes are applied at 1950" or 2000°F for 4 hr without need for a subsequent diffusion treatment. An outer coating about 1 mil in thickness is produced by these processes. Test Procedures. Coated specimens were exposed to static oxidation for periods ranging from 24 to 1000 hr at temperatures of 1600" to 2200°F. Terminal weight gain measurements and visual examination were used to evaluate oxidation resistance. including oxide spalling and coating failure. Both as-coated and exposed specimens of each alloy were studied by metallographic examination, electron microprobe analysis (EMA), and X-ray diffraction analysis either of the exposed surfaces or of phases extracted from the coating and diffusion zone. RESULTS As-Coated Condition. The microstructures of as-coated conditions were generally similar, irrespective of base materials or the particular coating process. They are typified by IN 100 coated by CODEP-D as shown in Fig. 1. The predominately single-phase outer layer, area A, Fig. 1, was identified by X-ray diffraction as the intermetallic compound NiA1. The NiAl zone extended inward to the original base metal interface. The diffusion zone, area B, Fig. 1, included carbide phases, a lamellar phase oriented perpendicular to the base metal surface, and a matrix phase consisting of a mixture of NiAl and Ni3Al. The phases in the diffusion zone were electrolytically extracted using a 10 pct HCl in methanol solution at approximately 1.3 amp per sq cm. The extracted phases were found to be M6C, MC, or M=C6 carbides and o as shown in Table I1 for each of the alloys. The d spacings from a typical diffraction pattern are

Jan 1, 1969

By T. A. Klinefelter, O&apos, R. G. Meara, Glenn C. Truesdell, Richard W. Smith

The investigation of domestic talcs was undertaken by the Bureau of Mines, Department of the Interior, in cooperation with the University of Alabama, at the request of the U. S. Army, on Dec. 1, 1941: "Considerable concern has been expressed by the Supply Arms and Service over maintaining continued availability of supplies of the necessary raw materials. These ceramic products are used by the Signal Corps in all army radio equipment, and to a greater degree in the new ultra-high-frequency equipment. The Air Corps has become a user of large amounts of radio-grade ceramics for' aircraft spark-plug covers required for high-altitude operations. In addition, the use of this material is essential to the proper functioning of the radio air-navigation aids of the Civil Aeronautics Board." History The use of steatite and talc in ceramic bodies goes back a great many years. If pure, talcs shrink little under heat-treatment and are very resistant to heat shock. The massive form, commonly called "steatite" by the trade, cuts and works easily, and this was naturally the first method used in obtaining articles of talc. When gas was in general use for illuminating purposes, a. large business was carried on in the manufacture of tips for gas burners.' With the development of uses for electricity, low-tension insulators were made in a similar manner; and, in fact, the forming of shapes from massive talc continues. However, as the business increased, cuttings and waste became more and more of a problem. In the twenties, one of the larger producing firms had a cooperative agreement with the Bureau of Mines at its Columbus station to work out a body using the finely powdered material. Somewhat earlier, manufacturers of spark plugs used the finely ground talc as part of the body and to some extent in wall-tile bodies. Somewhat later it came into use for kiln furniture and similar products and still more recently it has been used in some dinnerwares. With the development of the radio and the high-frequency fields generated, it was found that a dense steatite porcelain was far better than even high-tension electrical porcelain, which is a clay-flint-feldspathic type of body. Until the war increased the demand, the several pioneer steatite-porcelain manufacturers were able to furnish adequate supplies. When war began in Europe and Asia, three important foreign sources of raw material were cut off; i.e., the French, Italian, and Man-churian talcs. Domestic producers of high-grade porcelain are few, and the trade

Jan 1, 1948

By C. S. Lyons and. A. L. Johnson

A few years ago a leading American builder of centrifuges said, "No one uses a centrifuge if the job can be done any other way." This statement was essentially true at that time, not because the basic functional and economic principles involved did not frequently favor centrifugal methods, but rather because so many of the highly specialized features of the mechanical and functional peculiarities of continuous centrifuges had not been fully developed. The idea of using centrifuges in mineral dressing is definitely not new. There are literally hundreds of patents on centrifugal machines and processes for the mining industry. Many of them cover principles that are basic to the functioning of most centrifuges in operation today. In spite of this, until 1935, there were practically no successful applications of continuous centrifuges in the United States in the mineral industry, nor for that matter were there more than a mere handful of such machines in operation in North America in any industry. This was true despite the obvious desirability of machines that could furnish the advantages of high centrifugal settling forces in a continuous operation. The reasons for this are simple, even if not obvious: I. Finely divided solids, when thrown out of fluid suspension under high cen- trifugal forces, frequently exhibit physic a properties (particularly rheological or flow properties) that are markedly different from those they possess when settled out by gravity alone, and machines that are not designed in careful detail to cope with these peculiarities 'seldom function satisfactorily. 2. Most continuous centrifuges embody a solids-conveying element in the form of a very special screw conveyor. The rotation of this member under conditions of operation culls for drive designs that were not satisfactorily provided until the introduction of the Bird gear unit about 1934. These matters will be touched on later. Continuous centrifuges are now operating successfully in the mineral industry. Some units have singly handled more than 500,000 tons of solids during the past ten years. Generally their operation has been characterized by large unit capacities, complete elimination of labor, minimum supervision, moderate maintenance and power costs. Typical Centrifuge Applications Most materials classified by centrifuges are of subsieve particle size. Practically speaking, this means her than 100-mesh. A unit of measure other than screens is needed in order to consider these products properly. Such a unit is the micron, which is equal to one one-millionth of a meter; roughly1/25,000 of an inch. The opening in a standard 200-mesh screen is about 75 microns while a 325-mesh opening is roughly 43 microns.

Jan 1, 1948

By Charles A. Morgan

The proms of mire drawing depends upon the property which certain metals possess, termed ductility, which is defined in Brande's Dictionary of Science as a property inconhequcnce of which metals may be drawn out at length wilhotit interrupting the continuity of their constituent parts. As ticfincd thy M. Tresca, it is the property of flowing when subjected to pressure, and ie termed by him the "flow of solids," in his paper, read before the AcaiXemy of Sciences in Paris, November, 1866 * In the simple language of the wire shop, it is that quality in certain metals that thcm to be drawn (or etretched) out througl~ a tapering hole in a metal block or die, the die being more dense and harder than the metal to be redud. It is a fact well known to tllose slrillet1 in the ai*, that to eu~xeed in drawing iron or steel wire, it is of' the utmost, importance to have tborough lubritatiun, as a lack of it woullii udu-se abrasion of the wire, or of the walls of the tapering hole in the dia or plate, and quickly put an end to the operation. In drawing coarse or large sizes of pire, say & inoh diameter, the pressure upon the sides of the tay~dng hole, where the wire comes i.u contact with the die, so great that an ordina,y labricaot is equeezed out when the nsoal rc~luctions iu size are matie, and abrasion takea place. In order to meet this diffic:ulty, and emure proper lubrication, it has been a ccmmon prtictice for yazrs to apply a paste made of rye or wheaten flour, or lime, to the surface of the wire to be drawn, and when the pnstc is dry, to smwr tl~e wire with tallow or grease; the wire is then ready to be draw, the dried pa serving fo prevent the lubricant from being presetf out in the prows. Some years since, when Bessemer metal came iargely into use material for wire, 'the writer fourid that its dmwing requid so much more power than iron wire, that he was led to institute a. series of trials to ascertain the difference in power required. It was fotind that Bessemer wire requircd from 100 to 200 per cent. more power to makc the same reduction in sizes than soft iron wire, the difference depending npou the amount of carbon and other chemical constitu-

Jan 1, 1881

By J. D. Lindner, Gene E. Roark

Waterflooding operations in the Langston-Kleiner field. Young County, Tex., are described. Widespread application of formation fracturing has been practiced in both producing and injection wells. Field performance data arc cited which indicate than no detrimental effect on sweep efficiencies and that probable benefits in imectivily have resulted from the fracture treatments. I N T R O D U C I O N This paper is a report on a waterflood operation which is being carried out in the Lanpston-Kleiner field located in Young County, Tex. The oil reservoir aflected by this flood operation occurs in a Strawn sand member at an approximate depth of 3.550 ft subsurl'ace. The operators of' the project are Kleiner Estate. Turncr. Fiske. and West who are hereinafter collectively referred to as the Operators. Although the operation is unusual in several respects, the distinctive feature of this flood has been the widespread application of hydraulic formation fracturing treatments as a means to improve productivity and injectivity of the wells. It shall he the purpose of this paper to present basic information regarding the reservoir characteristics. op- craling practices, and waterflood behavior so that conclusions may be drawn concerning the effects which the fracture treatments have had on the performance of this water flood to datc. DEVELOP MENT Development of the 3,550 ft Strawn sand reservoir occurred during 1951 and 1952. The early development occurred on the Langston and Davis leases which arc in the northern region of the Operators' holdings and the wells were drilled on 20-acre proration units according to the field rules. However, studies of the economics of this program. coupled with the decision to proceed with pressure maintenance by water injection. resulted in the adoption of wider spacing in the later stages of development. This variation in spacing is apparent upon inspection of Fig. I upon which only the 3,550-ft Strawn sand producing and injection wells have been located on the Operators' properties. The development to the north of the operators leases is Ihe Garvey Strawn field and that to the south is the Taylor Strawn field. It wits determined that unitization of the leases to he involved in the waterflood program was not feasihle. Consequently. a system of offset injection wells, or lease line injection wells, was adopted from place to place as required to protect correlative rights in the program. This resulted in a dispersed array of injection and producing wells with relatively close proximity of wells along lease line areas and wider spacing toward

Jan 1, 1956

By T. A. Klinefelter, Glenn C. Truesdell, Richard W. Smith, R. G. Meara, O&apos

The investigation of domestic talcs was undertaken by the Bureau of Mines, Department of the Interior, in cooperation with the University of Alabama, at the request of the U. S. Army, on Dec. 1, 1941: "Considerable concern has been expressed by the Supply Arms and Service over maintaining continued availability of supplies of the necessary raw materials. These ceramic products are used by the Signal Corps in all army radio equipment, and to a greater degree in the new ultra-high-frequency equipment. The Air Corps has become a user of large amounts of radio-grade ceramics for' aircraft spark-plug covers required for high-altitude operations. In addition, the use of this material is essential to the proper functioning of the radio air-navigation aids of the Civil Aeronautics Board." History The use of steatite and talc in ceramic bodies goes back a great many years. If pure, talcs shrink little under heat-treatment and are very resistant to heat shock. The massive form, commonly called "steatite" by the trade, cuts and works easily, and this was naturally the first method used in obtaining articles of talc. When gas was in general use for illuminating purposes, a. large business was carried on in the manufacture of tips for gas burners.' With the development of uses for electricity, low-tension insulators were made in a similar manner; and, in fact, the forming of shapes from massive talc continues. However, as the business increased, cuttings and waste became more and more of a problem. In the twenties, one of the larger producing firms had a cooperative agreement with the Bureau of Mines at its Columbus station to work out a body using the finely powdered material. Somewhat earlier, manufacturers of spark plugs used the finely ground talc as part of the body and to some extent in wall-tile bodies. Somewhat later it came into use for kiln furniture and similar products and still more recently it has been used in some dinnerwares. With the development of the radio and the high-frequency fields generated, it was found that a dense steatite porcelain was far better than even high-tension electrical porcelain, which is a clay-flint-feldspathic type of body. Until the war increased the demand, the several pioneer steatite-porcelain manufacturers were able to furnish adequate supplies. When war began in Europe and Asia, three important foreign sources of raw material were cut off; i.e., the French, Italian, and Man-churian talcs. Domestic producers of high-grade porcelain are few, and the trade

Jan 1, 1948

By C. S. Lyons and. A. L. Johnson

A few years ago a leading American builder of centrifuges said, "No one uses a centrifuge if the job can be done any other way." This statement was essentially true at that time, not because the basic functional and economic principles involved did not frequently favor centrifugal methods, but rather because so many of the highly specialized features of the mechanical and functional peculiarities of continuous centrifuges had not been fully developed. The idea of using centrifuges in mineral dressing is definitely not new. There are literally hundreds of patents on centrifugal machines and processes for the mining industry. Many of them cover principles that are basic to the functioning of most centrifuges in operation today. In spite of this, until 1935, there were practically no successful applications of continuous centrifuges in the United States in the mineral industry, nor for that matter were there more than a mere handful of such machines in operation in North America in any industry. This was true despite the obvious desirability of machines that could furnish the advantages of high centrifugal settling forces in a continuous operation. The reasons for this are simple, even if not obvious: I. Finely divided solids, when thrown out of fluid suspension under high cen- trifugal forces, frequently exhibit physic a properties (particularly rheological or flow properties) that are markedly different from those they possess when settled out by gravity alone, and machines that are not designed in careful detail to cope with these peculiarities 'seldom function satisfactorily. 2. Most continuous centrifuges embody a solids-conveying element in the form of a very special screw conveyor. The rotation of this member under conditions of operation culls for drive designs that were not satisfactorily provided until the introduction of the Bird gear unit about 1934. These matters will be touched on later. Continuous centrifuges are now operating successfully in the mineral industry. Some units have singly handled more than 500,000 tons of solids during the past ten years. Generally their operation has been characterized by large unit capacities, complete elimination of labor, minimum supervision, moderate maintenance and power costs. Typical Centrifuge Applications Most materials classified by centrifuges are of subsieve particle size. Practically speaking, this means her than 100-mesh. A unit of measure other than screens is needed in order to consider these products properly. Such a unit is the micron, which is equal to one one-millionth of a meter; roughly1/25,000 of an inch. The opening in a standard 200-mesh screen is about 75 microns while a 325-mesh opening is roughly 43 microns.

Jan 1, 1948

By R. F. Mehl, B. Lustman

The formation of intermediate phase layers in cementation processes has been subjected to extensive qualitative investigation though to relatively little quantitative study; this work has recently been fully summarized by F. N. Rhines.' It is necessary here only to cnumerate the general conclusions drawn concerning the kinetic laws governing the growth of intermediate layers and to state what is known concerning the structural changes accompanying the generation of phase layers. I. When the intermediate phase is protective in type—i.e., when its density is less than that of the base metal, so that a continuous coating is formed and maintained—the isothermal growth of the phase follows a simple parabolic equation: X2 = kt [i] where X is the thickness of the alloy layer, k thc reaction rate constant, and t the time. The applicability of this equation to diffusion processes is tested by plotting the square of the thickness versus time, or by plotting the thickness versus the square root of time; the resultant achievement of a straight line in such a plot has been considered sufficient proof of the validity of this equation. Exceptions have been found where liquid phases are involved in the reaction, where the diffusion layer is cracked,2 and where thin semimetallic oxide and sulphide coatings are formed on metals.$ In the first two cases the thickness increases linearly with time, and in the latter it is a logarithmic function of time. 2. The rate of thickening varics with temperature according to the Arrhenius equation: k = Ae-Q/RT [2] where k is the parabolic rate constant of Eq. I, or some other rate-descriptive function, A is the action constant, e the base of natural logarithms, Q the heat of activation, R the gas constant, and T absolute temperature. This equation has been found to be generally valid except when transformations occur during reaction in either the base metal or in the reaction layer; in such instances Eq. 2 is still applicable with different values for the constants A and Q above and below the transformation temperature. 3. Ali phases that are stable at the temperature at which diffusion occurs will appear in the interdiffusion of two components. In some cases certain of the phases may be too thin to be observed and identified easily. Nonequilibrium phases have never been noted in thick reaction layers; i.e., layers of a thickness that may be discerned microscopically. The relative thickness of each phase in a diffusion layer is proportional to the concentration gradient and to the rate of diffusion in that phase.4 The reaction layers tend to have a

Jan 1, 1942

By R. F. Mehl, B. Lustman

The formation of intermediate phase layers in cementation processes has been subjected to extensive qualitative investigation though to relatively little quantitative study; this work has recently been fully summarized by F. N. Rhines.' It is necessary here only to cnumerate the general conclusions drawn concerning the kinetic laws governing the growth of intermediate layers and to state what is known concerning the structural changes accompanying the generation of phase layers. I. When the intermediate phase is protective in type—i.e., when its density is less than that of the base metal, so that a continuous coating is formed and maintained—the isothermal growth of the phase follows a simple parabolic equation: X2 = kt [i] where X is the thickness of the alloy layer, k thc reaction rate constant, and t the time. The applicability of this equation to diffusion processes is tested by plotting the square of the thickness versus time, or by plotting the thickness versus the square root of time; the resultant achievement of a straight line in such a plot has been considered sufficient proof of the validity of this equation. Exceptions have been found where liquid phases are involved in the reaction, where the diffusion layer is cracked,2 and where thin semimetallic oxide and sulphide coatings are formed on metals.$ In the first two cases the thickness increases linearly with time, and in the latter it is a logarithmic function of time. 2. The rate of thickening varics with temperature according to the Arrhenius equation: k = Ae-Q/RT [2] where k is the parabolic rate constant of Eq. I, or some other rate-descriptive function, A is the action constant, e the base of natural logarithms, Q the heat of activation, R the gas constant, and T absolute temperature. This equation has been found to be generally valid except when transformations occur during reaction in either the base metal or in the reaction layer; in such instances Eq. 2 is still applicable with different values for the constants A and Q above and below the transformation temperature. 3. Ali phases that are stable at the temperature at which diffusion occurs will appear in the interdiffusion of two components. In some cases certain of the phases may be too thin to be observed and identified easily. Nonequilibrium phases have never been noted in thick reaction layers; i.e., layers of a thickness that may be discerned microscopically. The relative thickness of each phase in a diffusion layer is proportional to the concentration gradient and to the rate of diffusion in that phase.4 The reaction layers tend to have a

Jan 1, 1942

By F. W. Jessen, N. Lamont

The effect of an existing fracture or joint plane, which may exist in a rock, on the extension of a hydraulically induced fracture through the rock has been investigated in the laboratory. By use of a series of models made from various outcrop rocks, the width and orientation of existing fractures do not alter the extension or direction of the hydraulic fracture. The results, which conform quite well with the Grifith theory of failure, are illustrated by a series of photographs of the various models. INTRODUCTION The process of hydraulic fracturing has been widely used in the oil industry since its introduction in 1948 and has made possible the production of many reservoirs which would have been uneconomical prior to this process. Numerous studies of the mechanics of the process2-h nd of the effects of oriented fractures on recovery'.' have appeared in the literature. The increased recoveries led to attempts to predict the orientation of hydraulic fractures at the wellbore and to the development of methods to control this orientation. Field tests have been devised"." which indicate the validity of theoretical predictions of fracture orientation at the borehole. The direction of extension of hydraulic fractures from the borehole has not received much attention since most studies have predicted, at least implicitly, that a fracture will continue in the same plane unless a change of state of stress in the rock occurs. Since such predictions are based on the assumption of rock homogeneity, the effects of rock heterogeneities are left unknown. Most sedimentary rocks are composed of layers which reflect the changing depositional conditions of geological time. In addition, the more competent rocks frequently are fractured and jointed as the result of structural deformations or tectonic movements. Evidence of such joint systems exists in many surface outcrops, and it can be assumed that similar systems occur in many subsurface rocks, although the individual joints may be rather tightly closed due to overburden forces. This paper investigates the effect that an existing fracture in a rock would have on the direction or orientation of an extending or advancing hydraulic fracture when it intersects the existing fracture. The study was conducted on small rock models under triaxial stress conditions. The results indicate that an existing fracture will have little effect on the hydraulic fracture. THE MODEL STUDY The rock model represents an elemental portion of the earth containing an existing fracture which is located at some distance from a borehole from which hydraulic fracture is being extended. A generalized view of a model is presented in Fig. 1. The models were constructed from cement blocks and natural rocks. The various materials tested and some of the physical properties are listed in Table 1. The rocks were cut into rectangular blocks with dimensions of 11/2 X3Y2 X4 to 8 in. An initial slot was cut into the end face of each block along the longitudinal axis normal to the top face. The slot was filled with plastic aluminum along its outer edge to a depth of 1/16 in. A hole of 3/8-in. diameter was drilled into the sealed slot at the center of the end face to serve as an entry port for the fracturing fluid. Existing fractures of various types were simulated in the models. A "hairline" fracture with essentially zero width was created by cutting the model into two parts with a diamond saw and replacing the two parts together along the cut. A finite-width fracture was created by placing a layer of sand grains between the two faces of the cut just described (see Fig. 12). A large open fracture (similar, perhaps, to a vug) was created by cutting the model in two parts and removing a portion of the downstream block to a depth of % in. See Fig. 13. For a fourth

By T. D. Tiemann

The purpose of this writing is to make available additional data, not previously published, on the extraction of silica from certain iron ores of Wisconsin and Minnesota and to discuss a possible method of processing. Results of investigations on the extraction of silica from low grade iron ores have been previously presented and discussed in detail in AIME Transactions.1,2 All of the ores investigated are essentially nonmagnetic and consist mainly of hematite, goethite and quartz. Much of the quartz is microcrystalline, particularly in the taconites. The ore from the Cuyuna range contains in addition manganese oxides. Briefly, the method consists in digesting a sample of the ore under pressure in a solution of sodium hy-

Jan 1, 1965

By G. W. Thomas

A mathematical tnodel of forward combustion in an oil reservoir is treated in this paper. The model describes a radial system having a vertical section of essentially infinite thickness, all of which is permeable to gas flow. Combustion, however, is presumed initiated over a limited thickness of the total vertical section. In the interval supporting cotnbustion, the mechanisms of radial conduction, convection and heat generation are taken into account. Above and below the burning interval, heat transport in the radial direction is by cottduction and convection. Vertical heat losses from the ignited interval are accounted for by conduction alone. A general solution is presented for the temperature distribution caused by radial movement of the combustion front. The results show that no feedback of heat occurs into the ignited interval when convection and conduction are acting in the bounding media. Peak temperatures are also 5 to 10 per cent higher than in the case where heat transport in the bounding media is by conduction alone. We arbitrarily define vertical coverage to be that fraction of the total ignited interval which is at 600F above atnbient, or greater, at any given time. The radial distance at which the vertical coverage becomes zero is the propagation range of the combustion front. It was found that an increase in vertical coverage results when the oxygen concentration, fuel concentration or gas-injection rate is increased. Moreover, the combustion front can be propagated 10 to 15 per cent further than in the case where only conduction is acting above and below the ignited interval. INTRODUCTION In the theoretical treatment of forward combustion in a radial system, one of the problems encountered is the determination of the transient temperature distributions caused by an expanding cylindrical heat source. Bailey and Larkin' and Ramey' simultaneously presented analytical solutions to the problem assuming heat transport by conduction alone. In a subsequent publication, Bailey and Larkin3 included the effects of both conduction and convection while treating linear and radial models. In this latter work, however, vertical heat losses were largely neglected. Selig and Couch' dealt with a radial model in which both conduction and convection were acting. Only a limiting case involving vertical heat losses was considered, however. Namely, temperatures on the boundary of the bed of interest were set equal to zero. Solutions thus obtained were representative of a system having a maximum vertical heat flux. Chu5 recently treated a more general case in which a permeable bed was considered bounded by impermeable media. Conduction and convection took place within the bed, and only conduction outside of the bed. The effects of vertical heat losses were included in his study. Solutions were obtained by numerical techniques. This paper is an extension of the theoretical work of other authors pertaining to forward combustion in a radial system. In particular, a mathematical model of the process is treated in which heat generation occurs over a small vertical interval of a larger permeable section. In the interval supporting heat generation, and above and below this interval, the mechanisms of radial conduction and convection are also presumed acting. Heat losses from the ignited interval are accounted for by vertical conduction. An analytical solution for the temperature distribution caused by radial movement of the burning front is presented. The effects of certain process variables are indicated and comparisons with Chu's results are made. THEORY To render the mechanism of forward combustion tractable to mathematical treatment, we idealize the problem to the extent of assuming continuous reservoir media possessing homogeneous and isotropic properties. The following additional assumptions are implicit in this analysis. 1. The thermal parameters, i.e., heat capacities, thermal conductivities and thermal diffusivities are invariant with temperature and pressure. Moreover, the bounding media possess the same thermal properties as the bed of interest. 2. The temperatures of the porous media and its contained fluids at any point and at any time are equal. 3. The reaction rate between the oxidant gas and the fuel is infinite. This assumption implies that the incoming oxygen concentration instantaneously goes to zero within an infinitesimal distance, i.e., the width of the combustion zone is negligible. 4. The rate of gas injection is constant and corresponds to the average rate throughout the lifetime of the project. 5. The fuel concentration is constant throughout the volume of rock swept out by the burning zone. 6. There is complete burnoff of fuel. This assumption demands that the rate of propagation of the burning front equals the rate of fuel burnoff. In a radial system, with a

By Takashi Katsura, Avnulf Muan

Equilibrium relations in the system FeO-Fe2O3 Cr2O3 have been determined at 1300°C at oxygen pressures ranging from that of air (0.21 atm) to 1.5 x 10-11 atm. The following oxide phases have stable equilibrium existence under these conditions : a sesquioxide solid solution with corundum-type structure (approximate composition Fe2O3-Cr2O3); a ternary solid solution with spinel-type structure (approximate composition FeO Fe2O3-FeO Cr2O3) and a ternary wüstite solid solution with periclase-type structure and compositions approaching FeO. The metal phase occurring in equilibrium with oxide phase(s) at the lowest oxygen pressures used in the present investigation is almost pure iron. The extent of solid-solution areas and the location of oxygen isobars have been determined. ThE system Fe-Cr-O has attracted a great deal of interest among metallurgists as well as ceramists and geochemists. Metallurgists have studied the system because of its importance in deoxidation equilibria, ceramists because of its importance in basic brick technology, and geochemists because of its importance for an understanding of natural chromite deposits. Chen and chipman1 investigated the Cr-O equilibrium in liquid iron at 1595°C in atmospheres of known oxygen pressures (controlled H2O/H2 ratios). The main purpose of their work was to determine the stability range of the iron-chromite phase. Hilty et al.2 studied oxide phases in equilibrium with liquid Fe-Cr alloys at 1550°, 1600°, and 1650°C. They reported the existence of two previously unknown oxide phases, one a distorted spinel with composition intermediate between FeO Cr203 and Cr3O4, the other Cr3O4 with tetragonal structure. They also sketched diagrams showing the inferred liqui-dus surface and the inferred 1600°C isothermal section for the system Fe-Cr-O. Koch et al3 studied oxide inclusions in Fe-Cr alloys and also observed the distorted spinel phase reported by Hilty et al. Richards and white4 as well as Woodhouse and White5 investigated spinel-sesquioxide equilibria in the system Fe-Cr-O in air in the temperature range of 1420" to 1650°C, and Muan and Somiya6 delineated approximate phase relations in the system in air from 1400" to 2050°C. The present study was carried out at a constant temperature of 1300° C and at oxygen pressures ranging from 0.21 atm (air) to 1.5 x 10-11 atm. The chosen temperature is high enough to permit equilibrium to be attained within a reasonable period of time within most composition areas of the system, and still low enough to permit use of experimental methods which give highly accurate and reliable results. These methods are described in detail in the following. I) EXPERIMENTAL METHODS 1) General Procedures. Two different experimental methods were used in the present investigation: quenching and thermogravimetry. In the quenching method, oxide samples were heated at chosen temperature and chosen oxygen pressure until equilibrium was attained among gas and condensed phases. The samples were then quenched rapidly to room temperature and the phases present determined by X-ray and microscopic examination. Total compositions were determined by chemical analysis after quenching. In the thermogravimetric method, pellets of oxide mixtures were suspended by a thin platinum wire from one beam of an analytical balance, and the weight changes were recorded as a function of oxygen pressure at constant temperature. The data thus obtained were used to locate oxygen isobars. The courses of the latter curves reflect changes in phase assemblages and serve to supplement the observations made by the quenching technique. 2) Materials. Analytical-grade Fe2O3 and Cr2O3 were used as starting materials. Each oxide was first heated separately in air at 1000°C for several hours. Mixtures of desired ratios of the two oxides were then prepared. Each mixture was finely ground and mixed, and heated at 1250" to 1300°C in air for 2 hr, ground and mixed again and heated at the same temperature for 5 to 24 hr, depending on the Cr2O3 content of the mixture. A homogeneous sesquioxide solid solution between the two end members resulted from this treatment. A Part of some of the sesquioxide samples thus prepared was heated for 2 to 3 hr at 1300°C and oxygen pressures of 10-7 or 1.5 x 10-11 atm. Reduced samples (either iron chromite

Jan 1, 1964

By H. Y. Jennings

An extensive field and laboratory experimental program was carried out to compare the waterflood behavior of carefully preserved soft and unconsolidated cores with measurements on the same cores after extraction. Results obtained from using idealized consolidated and unconsolidated porous media in which wettability could be carefully controlled were contrasted with the preserved core data. The controlled tests on idealized porous media investigated the effect of wettability, flood rate, core length, core permeability and consolidation on the displacement of high viscosity oils. It was concluded from these studies that waterfloods are more favorable when carried out with crude oil in preserved soft and unconsolidated cores than with the same cores after they have been extracted and re-saturated. Waterfloods are usually more favorable when carried out with crude oil in extracted .soft and unconsolidated cores than with refined oil of the .same viscosity in the same cores. The less favorable behavior of extracted soft and unconsolidated cores compared to preserved cores is due to alteration of the core by extraction. Preserved cores saturated with native water and oil should be used for laboratory displacement experiments because they more accurately reflect true reservoir behavior INTRODUCTION The demand for low gravity crude oil created by refinery modernization has focused attention on increasing the production of this viscous crude oil. Billions of barrels are in place in fields that are depleted, or nearly depleted, by primary production mechanisms. Since low gravity reservoirs are relatively recent, geologically, the solid matrix material is usually soft and unconsolidated sand. Such formations are also characterized by a high clay content. Evaluation of sophisticated oil recovery processes with the associated high capital investments has increased the demand for special core analysis tests on material from these soft and unconsolidated sand reservoirs. Data in this paper have resulted from an extensive field and laboratory experimental program. The initial objective vras to provide soft and unconsolidated sand cores for laboratory measurements with as little alteration as possible from their reservoir condition. A secondary objective was to compare the waterflood behavior of these carefully preserved cores with measurements on the same cores after they had been extracted and resaturated. When the comparison showed markedly different behavior the final objective was to attempt to explain the difference by making measurements on idealized porous media free of clay in which initial wettability could be carefully controlled. EXPERIMENTS MATERIALS Core Material The preserved cores used in this study were obtained with as little alteration as possible from their reservoir conditions. Special techniques were developed to satisfy this objective. The cores were cut with native crude whenever the crude had the necessary properties to satisfy the minimum drilling fluid requirements. A pure hydrocarbon chromatographic tracer was added to the crude to provide a simple, safe and inexpensive method to distinguish between oil filtrate and formation oil. Details of the tracer technique used in this study and the procedures used to handle and process the soft, unconsolidated cores have been published.' The core samples were then preserved and packaged at the well site with a dip-applied strippable plastic, or by using a rubber sleeve from a rubber-sleeve core barrel. The final step was to insure that the carefully taken and preserved samples were not altered by processing in the laboratory. Some soft and poorly consolidated sands were carefully shaped in the lab and encased in a protective mounting without disturbing their three-dimensional integrity. Many samples were so poorly consolidated that they literally flowed from the package when the seal was broken. A technique was developed to obtain cylindrical plugs from these samples by using liquid nitrogen as the drilling fluid in a conventional core-drill, drill-press assembly. The idealized porous media consisted of sintered rods of Alundum RA 139, outcrop sandstone identified as Al-hambra sandstone and packs of No. 130 Nevada sand. This sand is 95 per cent 140-200 mesh. (Physical properties of these porous media with those representative of preserved cores are in Table 1.) The natural cores and most of the idealized porous media were 1 1/2-in. in diameter and 3-in. long. The samples used to study the effect of core length were 1 1/2-in. in diameter and 12-in. long. Liquids Water and oil produced from the formations being studied were protected from the atmosphere and collected in carefully cleaned glass or plastic-lined containers. The production was free of chemical additives such as emulsion breakers and corrosion inhibitors. The crude oil was

Jan 1, 1967

By A. H. Larson, R. J. McClincy

ALTHOUGH arsenic has a very high vapor pressure and vacuum distillation appears to be a likely method for its removal from lead, the published literature contains virtually no information concerning the vacuum removal of arsenic from lead. Caldwell, Spendlove, and St. Claire1 mention arsenic in their investigation of the removal of volatile metals from lead by vacuum distillation. They do not, however, give any data for arsenic removal or refer to any actual experimental work involving arsenic dissolved in lead. Moriyama, Kozuka, and Miura2 have determined the activity of arsenic in dilute As-Pb alloys in the temperature range from 450" to 600°C using a closed galvanic cell. They found that the activities of both arsenic and lead showed a positive deviation from ideality at 600°C. In view of the lack of experimental data regarding the vaporization of arsenic from As-Pb alloys, a limited vapor pressure study was made on liquid alloys containing from 0.5 to 3.3 wt pct As in lead at 703°C. The pressure of As4(v) above the alloys studied was determined from weight-loss data collected by means of the inert-gas saturation method. The experimental apparatus and procedure used were similar to that discussed by Alcock and Hooper9 with modifications as described by the authors., The technique involved was one of passing a known volume of inert gas over the alloy to be studied in a known amount of time and determining the loss in weight of the sample. Because of the low vapor pressure of lead at 703"C, the observed weight loss could be attributed solely to the vaporization of arsenic as the tetratomic molecule AS43 Measurements of the apparent vapor pressure were repeated at different inert-gas flow rates until from three to five values were obtained which were independent of inert-gas flow rate. This value of the apparent vapor pressure was taken to be the equilibrium vapor pressure of the alloy under consideration. The vapor pressures measured in this investigation have been converted to the activities of arsenic in As-Pb alloys, Table I, by use of the data compiled by Elliott and Gleiser5 for the vapor pressure of pure arsenic. The standard state for arsenic was chosen as the pure, hypothetical, supercooled liquid. The activity of arsenic was calculated from the fourth root of the ratio PAs,/PAS,. The low magnitude of the vapor pressures given in Table I explains the difficulty en- countered by earlier workers in successfully vacuum distilling arsenic from very dilute As-Pb alloys. The data shown in Fig. 1 indicate that the As-Pb system behaves ideally. The apparent outlier represented by the alloy containing 1.43 mol pct As is a result of the fact that the pressure of As, above the alloy was barely detectable by the experimental procedure used in this investigation. Because of this, the apparent vapor pressure determined for this alloy could be in considerable error. Moriyama, Kozuka, and ~iura' have reported that arsenic shows a positive deviation from ideality in dilute solution in lead. However, details of their results have not been made available. This research was made possible by a grant from the National Science Foundation (GK-196) for which the authors are very appreciative.

Jan 1, 1970

By R. L. Orr, J. D. G. Masse, Ralph Hultgren

The relative partial molar enthalpies of gold and tin in liquid Au-Sn alloys have been measured from Xsn = 0.474 to 0.510 at 696°K, slightly above the melting point of solid AuSn. Within an average precision of 6 cal per g-atom, the data are represented by two smooth curves, which satisfy the Gibbs-Duhem relationship and which do not show any anomalous behavior in the range of composition studied. The results give no support to the hypothesis that atomic associations in the equiatomic liquid alloy resemble those in solid AuSu. LITTLE has been firmly established as to the nature of atomic distribution in liquid metallic phases. A favored hypothesis assumes the existence of atomic groupings in the liquid phase which are similar to those in solid phases occurring at lower temperatures. Beginning with this hypothesis, it is often possible to adjust the values of certain parameters (such as degree of association) so that approximate agreement is achieved with certain features of the X-ray diffraction pattern of the liquid, even though many other possible structures might satisfy the data equally well. Thus, in this manner, the structure of liquid tin has been described as a dispersion of fragments of gray tin in a matrix of metallic tin.1 Four X-ray diffraction studies2"5 have been made of the liquid alloy of composition AuSn at temperatures slightly above the melting point of the solid. Each investigator concluded, on somewhat different grounds, that the liquid consisted to a large extent of arrays of atoms similar to the solid, with admixture of more disordered arrays. Solid AuSn has the nickel arsenide crystal structure: each tin atom has six nearest neighbors, all gold atoms; and each gold atom has six tin and two gold atoms as nearest neighbors. It remains highly ordered to the melting point. The liquid alloy has a large exothermic (?H700° K = -2700 cal per g-atom6) enthalpy of formation, favoring ordering and making the hypothetical molecular association not unreasonable. The possible existence of such solidlike arrays, or of a high degree of order that occurs preferentially at a specific composition in a liquid alloy, might also be revealed by thermodynamic behavior somewhat analogous to that in highly ordered solid alloy phases. The latter often exist over wide composition ranges, within which the highest degree of order occurs at the ideal composition for which the atomic fractions are equal to the fractions of sites which are "right" for each kind of atom. On departing from the ideal composition, the excess atoms occupy "wrong" positions, raising the internal energy and making it progressively easier for additional atoms to occupy "wrong" positions. Thus, on either side of the ideal composition, there should be a pronounced rise in the entropy and enthalpy, which would be shown particularly by the change in the relative partial molar enthalpies, ?Hi, since they depend strongly on d?H/dx. In the one case where accurate measurements have been made, the solid AuCu ordered phase, the structure becomes much less ordered as the composition deviates from the ideal, and relative partial molar enthalpies change sharply as shown by the data6 given in Table I. This suggests the possibility of finding similar pronounced changes in the relative partial molar enthalpies of gold and tin in liquid alloys near the composition AuSn if the postulated solidlike ar-

Jan 1, 1967