Search Documents

By O. R. Morris, G. L. Hawkes

A galvanic cell, using as electrolyte a fused salt solution of calcium carbide and as electrodes carbon and a Fe-C alloy of known composition, has been set up to study the thermodynamics of Fe-C alloys in the temperature rmzge 800" to 1000°C. Time independence and reproducibility of the cell electromotive force were taken as evidence of the reversible behavior of the cell. Carbon was believed to be present in the electrolyte as the so-called acetylide ion, C;-. The plots of the cell electromotive force us temperature for a specific alloy composition were straight lines within the limits of experimental error. The average Partial molar enthalpy of carbon in iron relative to pure carbon was found to be +10,610 i 93 cal per g-atom C. Thermodynamic analysis of the data has led to the following equation for the carbon activity, ac, based upon pure carbon as the standard state: In ac = In Zc + 10,560/RT + (10.02 + 77O/T)ZC - 2.350 where ZC is the lattice ratio [nC/(nF, - nc )] and T is the absolute temperature. This equalion gives carbon activity values generally slightly lower than those from gas equilibration studies reported in the literature. METAL LOGRAPHIC examination of a polished cross section of the steel anode used in the electrolysis studies of fused salt solutions of calcium carbide by Morris and Harry revealed extensive carburization of the steel by the electrodeposited carbon. This carburization was reflected in the variability, with time, of the applied potential to the electrolysis cell, necessary to maintain a constant current density at the electrodes. This observation suggested the setting up of a galvanic cell of the "alloy concentration" type to study the thermodynamics of some metal-carbon alloys. Cells of this general type have been widely used for the study of alloy systems.2 In view of the availability of published data in respect of the austenite phase of the Fe-C system, it was decided to carry out measurements upon these alloys before proceeding to studies of less well documented systems. The galvanic cell may be written: where [C] is carbon dissolved in iron. The electrolyte was a fused salt solution of calcium carbide, containing some 5 to 10 mol pct of carbide. The cell reaction is believed to be: C(s)-[CI [I1 Carbon forms an interstitial solid solution in iron, with the atoms located in the octahedral interstices. In the fcc crystal structure of austenite there is one octahedral interstice per iron atom. Thus, the lattice ratio, ZC, shown by Gurney3 to be the fundamental concentration parameter in the context of interstitial solutions, is given by: where nc and nFe are the number of carbon and iron atoms, respectively. chipman4 has recently shown empirically the advantages of using this concentration parameter instead of the more usual atom ratio or atom fraction. The cell electromotive force, E, assuming reversible behavior, is related to the carbon potential or the partial molar free energy of carbon in the solid solution relative to pure carbon at the same temperature and pressure, GP at the composition ZC, by the equation: where z is the carbide ion valency and F is the Faraday constant. An activity of carbon, ac, in the solution relative to the value of unity assigned to pure carbon, and an activity coefficient, qC , are defined such that: where R is the gas constant and T the absolute temperature. GF is further related to the relative partial molar enthalpy Hm, and the temperature coefficient of the cell electromotive force, (aE/aT)Zc, by the equations: Measurement of the cell electromotive force thus enables calculation of the relative partial molar thermodynamic properties of carbon in iron, if z is known. At E = 0, the solid solution is in equilibrium with pure carbon. More convenient for many purposes is the standard state based upon the infinitely dilute solution, Henry's law. The relationship between the activity coefficient of carbon based upon this standard state, and that based upon the pure carbon standard state, qC , may be obtained by considering the free energy of transfer of carbon from the latter standard state to the former. The relationship is: where +:H is the activity coefficient of carbon in the hypothetical standard state based on a reference of

Jan 1, 1969

By F. D. Rosi

The plastic properties of extended silver and copper crystals of varying purity were studied as a function of crystal orientation in the early stages of flow. Variations in the gross shape of the shear stress-shear diagram and in the properties of critical Variationsshear stress and shear-hardening coefficient were correlated with changes in slip-band developments. The phenomenon of work hardening is discussed in terms of the existing dislocation theory. IT appears certain from the early studies on the deformation characteristics in metal crystals1-3 that plastic flow takes place in a preferred crystallo-graphic slip system which is determined by the geometry of the crystal (law of maximum shear stress), and that the value of shear stress for this system is independent of crystal orientation (law of critical shear stress). Experimentally, it has been demonstrated further that the law of critical shear stress can be extended to include extensive plastic flow.&apos; Thus, the shear-hardening coefficient, which is defined as the slope of the shear stress-shear curve, also is considered to be independent of orientation. It is noteworthy that deviations from this empirical shear-hardening law have been reported in cubic crystals whose initial orientation favors slip on more than two systems.&apos; Moreover, this law appears to have been derived from stress-strain data relating to relatively high values of shear strain (0.5 to 4), where widespread slip and complex distortions can be expected, regardless of crystal orientation. Since existing data indicate that the strain inhomogeneity in a crystal is manifested particularly in the early stages of flow, it would appear that a more exacting test as to the fundamental nature of the shear-hardening law would be to investigate systematically the shape of the stress-strain curve as a function of crystal orientation in the earlier stages of deformation. With regard to the general form of the shear stress-shear curve for cubic crystals, early studies show a parabolic hardening law, where the shear 1 stress is proportional to the square root of the shear-strain. Since this law was predicted theoretically by Taylor" in his original dislocation model for hard- ening, it has been accepted widely as a fundamental flow characteristic of cubic metals. However, it was recently pointed out by Masing6 hat the parabolic law is not the elementary form of hardening in cubic crystals, but instead is a consequence of complexities in the flow process (e. g., deformation bands and unpredicted secondary slip). Thus, in the very early stages of deformation (< 2 pct extension) where the occurrence of such complexities is unlikely, a different strain-hardening behavior might be anticipated. This view is supported by the recent work of Rosi and Mathewson7 on high purity aluminum where a linear law was obtained for extensions up to 2 pct. A linear hardening over a wider range of deformation also was reported by Rohm and Kochendorfer8 ho deformed aluminum crystals under conditions approximating pure shear. Even more pertinent is the recent evidence of Masing and Raffelsieper9 on high purity aluminum crystals. It was found that for crystals having initial orientations near a <l00> or <1ll> axis, a high hardening was obtained, whereas crystals with a <110> orientation exhibited a low and linear hardening curve followed by a region of more rapid hardening. Since much still remains obscure concerning the details of strain hardening as well as slip-band formation in face-centered-cubic crystals in the early stages of deformation, the present study was undertaken to evaluate the effect of crystal orientation on these two important manifestations of glide. It is important to note here that at the time of this study, Lucke and Lange11 presented information on the orientation-dependence of the shape of the strain-hardening curve in aluminum of various purities. Their work, which essentially represents an extension of that of Masing and Raffelsieper, in many respects is parallel to that of the present study. Experimental Procedure Production of Single Crystals: Single crystals of silver and copper of varying purity were used in

Jan 1, 1955

By H. R. Peiffer, R. Geckle

The silver phase of silver and finely divided alumina composites is shown to grow as single crystabs upon solidification from the melt. These crystals grow without the aid of an externally applied thermal gradient or a mold. The single-crystal growth is more readily disrupted as the alumina content varies from the optimum concentration of 20 wt pct. Pretreatment such as variation of fabrication pressure, and presintering of the specimens appear to play a lesser role in this phenomenon. In actual practice the growth of single crystals of metals from the melt is a tedious, painstaking process.&apos; Care must be taken to insure the proper thermal gradients and rate of growth in a vibration-free environment. Excellent single crystals can be grown when these variables are controlled. When a second insoluble and finely divided phase is present in the melt the growth of single crystals is difficult, if not impossible, even under the most favorable conditions outlined above. During the past few years, a composite of silver and alumina has demonstrated an ability to resist flow even though the major phase, silver, is mo1ten. 2 A more surprising feature of this material is the ease with which single crystals of silver grow upon cooling the composite from temperatures above the melting point of silver to temperatures near room temperature. Observations have been made that demonstrate that single crystals of silver will grow even when conditions most unfavorable for growth of pure silver crystals exist. The crystals grown in this manner are imperfect in that a great deal of subgrain structure exists. It is the purpose of this manuscript to qualitatively describe this process and to attempt to isolate the influencing factors of this behavior. MATERIAL PREPARATION The composite material is prepared by powder-metallurgical techniques. Two items of great importance are the introduction of oxygen into the system and the obvious need for a thorough mixing of the metallic and refractory oxide phases. The oxygen is necessary in order that the silver wets the alumina. Without oxygen the phases separate and the material shows no unusual properties. In order to supply the needed oxygen the silver is added in the form of silver oxide which is readily decomposed to oxygen and silver upon heating. The silver oxide is readily obtained in a finely divided form that allows a uniform mixture of the alumina and silver oxide to be prepared. The correct ratio of alumina to silver oxide is mixed in the presence of alcohol in an ordinary food blender. The mixture has the consistency of a thin slurry and after mixing for approximately 20 min is dried and pressed into billets at various pressures. As is shown in Fig. 1, there is no limit to the shape of the specimens obtainable as single crystals. These billets are heated in air in a predeter-

Jan 1, 1964

By C. H. Herty

The results of a study of the open-hearth process from the physicochemical viewpoint are given. This study includes experimentation in small laboratory furnaces and in standard 100-ton furnaces. The behavior of manganese, carbon and phosphorus are quantitatively explained. The action of "residual" manganese is discussed with reference to its relation to iron oxide dissolved in the metal. The solubility of CO in steel and its relation to dissolved FeO and carbon is given. The equation for phosphorus elimination has been tested out on a 200-ton furnace and the results are given in the text. The effect of temperature and slag composition on the elimination of metalloids in the basic open-hearth process has been qualitatively understood since the early days of steel making. The quantitative effect has, however, only recently been brought to attention. The effect of slag composition has received more attention than that of temperature, primarily because the range of finishing temperatures in the basic open-hearth process is small compared to the large variations found in the composition of the slag at different periods during the process, and to the variations occurring with the use of raw materials of different degrees of impurity. The effect of slag composition on the elimination of metalloids has been studied by Styril from the thermochemical standpoint. This method is open to serious errors, in that thermochemical data at 2900&apos; F. are very inaccurate and in many cases completely lacking. Feild2 has calculated equilibrium constants from the rate at which the metalloids are eliminated. The effect of slag viscosity on rate of elimination will affect the constants calculated by this method. Whitely,a Colcough4 and others have used slag compositions as the basis for calculation of constants by which the extent of elimination may be calculated.

Jan 1, 1926

By R. D. Pehlke, J. V. Gluck

The effect of small additions of silver on the actiziity of zinc in dilute solution with molten bismuth has been determined ill the range 450° to 650°C. Experimental measurements were made in a multi-electrode galvanic cell. All zinc activities showed large positive deviations from Raoult&apos;s Law. The results are expressed in terms of the interaction parameter EJ, as defined by Wagner. In the binary Zn-Bi system, Henry&apos;s Law was followed at zinc concentrations below 5 mol pct, thus indicating that the binary or self-interaction parameter of zinc in bismuth is essentially zero. The Henry&apos;s Law con- THE determination of thermodynamic interaction parameters requires accurate knowledge of solute activities in the dilute-solution region. Dealy and Pehlke1 have summarized the basis for interaction relations, discussed some theoretical implications, and presented a compilation of interaction parameters calculated for molten nonferrous alloys from stant ranged from 2.43 at 650°C to 3.96 at 450°C. The binary zinc activities were consistent with published data for higher zinc concentrations . The ternary interaction parameter ranged from -1.90 at 650°C to -3.30 at 450° C, varying linearly with the reciprocal of the absolute temperature. The negative value for the parameter reflects the fact that addition of silver decreases the activity of zinc in solution with bismuth. data available in the literature. Most of the data were for two-component systems from which only the self-interactions, Ei, could be calculated. Concentration ranges were often such that a considerable extrapolation was required for calculations at lnfinite dilution. The data for ternary systems were quite limited and often unavailable in suitable systematic fashion—thus few values of the parameter e| could be obtained. Knowledge of both the binary and ternary interaction parameters is necessary for the estimation of the activity coefficient of a given dilute solute in

Jan 1, 1965

By J. V. Gluck

In the present paper," as in earlier publications, V1&apos;2"1 the authors present experimentally obtained relations for the free energy of solution of oxygen in various metals as a function of temperature. The relations are linear and given in slope-intercept form. The authors give values for the "probable error" of the slope and intercept, citing Birge&apos;s method17 for obtaining these quantities. Birge discussed these methods as early as the period 1929-32.25726 In Ref. 25 the probable error is defined as "the numerical value which the true error is as likely to exceed as not", i.e., 50 pct probability. Ref. 26 is even more detailed and includes a lengthy discussion of the applicability of the Gaussian distribution to experimental data. However, the use of the "probable error" has come under some question. For example, Ezekiel&apos;~ states that "the use of the probable error tends to make the results appear rather more accurate than the standard error". Moroney28 stated (in 1951) that "the term &apos;probable error&apos; was used in former times to denote 0.67450 (50 pct confidence using the normal distribution)....the term, a poor one, is now very much obsolescent. It has been said that &apos;it is neither an error nor probable&apos; ". Bennett and Franklin in 1954" in discussing statistical confidence levels mentioned that "the customary use of the 5 and 1 pct levels is not completely a matter of chance; these levels probably represent a balance between the desire to be correct and the desire to be specific. Also in most people&apos;s minds the borderline between something that could possibly happen and something that is not likely to happen is somewhere in this region. Certainly 5 or 1 pct confidence limits are to be preferred to limits such as the &apos;probable error&apos; which has only a 50/50 chance of including the correct value." It may readily be seen that the 95 pct confidence level, which is given by 1.960 (assuming large sample size), thus corresponds to approximately three times the "probable error". Indeed, limits of one standard deviation correspond only to about 68 pct probability. Even if we triple the tolerances given by the authors in the equations of their Table 111, the deviations do not become excessive and would not detract from their excellent results. It could then be said with a high degree of confidence (95%) that the precision of the slope and intercept values is about *3-5 percent of their absolute levels rather than the 1-2 percent implied in Table 111. This is then compatible with an earlier suggestion of Gokcen~&apos; of a probable accuracy of 5 pct in dissolved oxygen measurements by the technique employed. Alternatively, the authors could have

Jan 1, 1967

By J. L. Taylor, P. Duwez

PARTIAL phase diagrams of titanium with iron, cobalt, and nickel have been established by previous investigators.1-3 These diagrams seem to be reliable, at least for concentrations of titanium ranging from 0 to about 50 at. pct. More recently, Long and his collaborators have presented a tentative titanium-nickel diagram covering the titanium-rich side.&apos; These various studies indicate that in each system three intermediate phases exist and correspond to the compositions Tia, TiX, and TiX2 (or TiX3). The purpose of this paper is to review the available information on the crystal structure of these phases and to give the results of additional X-ray diffraction studies. Previous Work A summary of the work of Wallbaum and his collaborators"-&apos; is presented in table I. The first intermediate phase on the titanium-rich side of the three systems, with iron, cobalt, and nickel, is of the Ti2X type and has a face-centered cubic structure. Although it is stated that the unit cell contains 96 atoms: no lattice parameters are given. The second phase is centered around the compositions TiX for the three systems. The crystal structure of this phase is mentioned in a short note" as being body-centered cubic (CsCl type), but no parameters are given. The analogy between the three systems, which is perfect as far as the two phases of the type Ti2X and TiX are concerned, disappears at the titanium-poor end of the diagrams. In the system titanium- iron, TiFe2 has an hexagonal (MgZn2 type) struc-ture with the parameters given in table I. The existence of TiFe3 has also been reported8 (table I) but was questioned by other investigators2 and is also refuted by the present study. In the system titanium-cobalt, a phase corre-sponding to the composition TiCo2 has been investi-gated by Wallbaum and Witte6 who claim that the structure is cubic (MgCu2 type) for alloys slightly deficient in cobalt and hexagonal (MgNi2 type) for alloys slightly deficient in titanium. The parameters of the two phases are given in table I. In the system titanium-nickel, the nickel-rich phase corresponds to the composition TiNi3 and has been described as hexagonal7 with the parameters given in table I. The present investigation was initiated for the purpose of filling in the gaps in the knowledge con-cerning the structure of the various phases sum-marized in table I. Since the titanium used by Wallbaum and his collaborators was only 95 pct pure,&apos; it was found desirable to redetermine the lattice parameters of the alloys prepared with a

Jan 1, 1951

By Robert B. Sosman

The chance that a Howe Memorial Lecturer will be able to refer back to a personal contact with the distinguished metallurgist for whom this lectureship is named grows steadily I I did not have the pleasure of his personal acquaintance, but I did receive from him in 1916, quite unexpectedly, a letter commenting On a paper that I had recently published27 On "Types of Prismatic Structure in Igneous Rocks." The paper was written for geologists and petrologists, but it had an application, naturally, to the crystallization of iron and steel in a mold. The letter impressed me at the time, and still does, with the breadth of of Howe&apos;s interests and his perseverance in keeping up with the progress of any branch of knowledge that had metallurgical connotations. Scope of the Lecture During several years preceding the date mentioned I had worked in collaboration with Arthur L. Day and E. T. Allen8 at the Geophysical Laboratory, Carnegie Institution of Washington, on the temperature scale as defined by the nitrogen thermometer at high temperatures. Later (1928-1947) I had the opportunity of helping to apply this experience to the pyro-metric problems of the steel industry. Because of the range of its temperatures, the multiplicity of the methods used, and the variety of its purposes, pyrometry in the open-hearth process has always offered a fertile field for both research and development. I am therefore devoting an hour to the subject of temperatures in the basic open-hearth furnace, the furnace that makes most of our steel in the united States. I would direct your attention particularly to the choice of the first two words in the title of the Lecture. One sometimes hears or reads of the ((temperature of such-and-such a furnace," as if it were a single, measurable, characteristic quantity. I need hardly emphasize to any one who has ever operated a furnace or a kiln that " temperature of the furnace " is a meaningless phrase. Even if we confine our attention to the space enclosed by the roof, walls, and hearth of an open-hearth furnace, it is doubtful whether any such space has ever been so uniform in temperature that the phrase would have a meaning. In any furnace, there are many different temperatures, capable of being measured at many different places, and actually being measured for several different purposes. These pyrometric purposes, methods, and results, if given in detail, would expand this lecture into a book on the basic open-hearth process. I must therefore confine myself to a statement of the range of temperatures as they have been observed in various parts of the furnace, indicating in a general way why they are measured, and mentioning the methods that are available without attempting to describe these

Jan 1, 1949

By Robert B. Sosman

The chance that a Howe Memorial Lecturer will be able to refer back to a personal contact with the distinguished metallurgist for whom this lectureship is named grows steadily I I did not have the pleasure of his personal acquaintance, but I did receive from him in 1916, quite unexpectedly, a letter commenting On a paper that I had recently published27 On "Types of Prismatic Structure in Igneous Rocks." The paper was written for geologists and petrologists, but it had an application, naturally, to the crystallization of iron and steel in a mold. The letter impressed me at the time, and still does, with the breadth of of Howe&apos;s interests and his perseverance in keeping up with the progress of any branch of knowledge that had metallurgical connotations. Scope of the Lecture During several years preceding the date mentioned I had worked in collaboration with Arthur L. Day and E. T. Allen8 at the Geophysical Laboratory, Carnegie Institution of Washington, on the temperature scale as defined by the nitrogen thermometer at high temperatures. Later (1928-1947) I had the opportunity of helping to apply this experience to the pyro-metric problems of the steel industry. Because of the range of its temperatures, the multiplicity of the methods used, and the variety of its purposes, pyrometry in the open-hearth process has always offered a fertile field for both research and development. I am therefore devoting an hour to the subject of temperatures in the basic open-hearth furnace, the furnace that makes most of our steel in the united States. I would direct your attention particularly to the choice of the first two words in the title of the Lecture. One sometimes hears or reads of the ((temperature of such-and-such a furnace," as if it were a single, measurable, characteristic quantity. I need hardly emphasize to any one who has ever operated a furnace or a kiln that " temperature of the furnace " is a meaningless phrase. Even if we confine our attention to the space enclosed by the roof, walls, and hearth of an open-hearth furnace, it is doubtful whether any such space has ever been so uniform in temperature that the phrase would have a meaning. In any furnace, there are many different temperatures, capable of being measured at many different places, and actually being measured for several different purposes. These pyrometric purposes, methods, and results, if given in detail, would expand this lecture into a book on the basic open-hearth process. I must therefore confine myself to a statement of the range of temperatures as they have been observed in various parts of the furnace, indicating in a general way why they are measured, and mentioning the methods that are available without attempting to describe these

Jan 1, 1949

By M. H. Caron

BASIC U. S. Patent 1,487,145 on ammonia leaching of nickel ores was issued to the author on March 18, 1924. Equivalent patents in other countries were obtained later. The Dutch Syndicate Brikcarbo became interested in the process in 1935; and a couple of years later the late Dr. H. Foster Bain sent samples of Surigao laterite iron ore to Delft and witnessed tests made there on this material for the Philippines Commonwealth. As a result, the author was asked in April 1940 by Dr. Bain to go to the Philippines to erect and take charge of a pilot plant for the process. The World War prevented carrying out this proposal. The Dorr Co. also became interested in the process at about the same period. The investigations by the Freeport Sulphur Co. on the process as applied to the Cuban nickeliferous laterites, which resulted in the Nicaro enterprise, and the results of this operation have been well described elsewhere.1,²,³,4,5 This Nicaro plant was, in operation for almost two years, and during this period produced about 10 pct of the world nickel production from laterites containing 1.35 pct nickel. This plant and its operation were war measures and, in view of this, activities were suspended in April 1947. The results obtained fully demonstrated the technical feasibility of the process and its economical aspects on a commercial scale. In this respect, it should be understood that it is probable that improvements may be made by further development, and that there are possibilities for advantageous application of the process to garnierite and similar ores with higher values in nickel than the laterite iron ores at Nicaro. While the articles cited above have given a certain amount of information, no general article containing all the important process data has been pub- lished. Since the process is of more than local interest, a fuller knowledge of the fundamental and practical factors of the method may be welcome to those interested in this new field of metals technology. The author, accordingly, takes pleasure in submitting this article to the AIME as it represents in a condensed form the results of many years of research. The brief outlines of the fundamental and other factors and the explanation of observed phenomena are presented with as little discussion of details as possible, consistent with clarity. It is a special satisfaction to the author to make some contribution of his own in return for the benefits of the many valuable publications issued by the Institute during his thirty years of membership. Ores Adapted for Ammonia Leaching: All nickel and cobalt ores which originate from weathering of peridotites or similar basic rocks having sufficient values are suitable for treatment by the ammonia leaching process after a preliminary reduction under proper conditions. The formation of these deposits was probably as follows: In the course of time the basic rocks were attacked by atmospheric agencies; MgO and SiO2 were gradually leached out, and secondary nickel minerals formed, such as garnierite, a hydrated silicate of nickel and magnesia. These secondary products are, however, not stable. They decompose in a further stage of weathering and ultimately only a relatively small residue of insoluble oxides remains, known as laterite iron ore with a small nickel content and very little cobalt. Under these mantles of laterite, richer nickel values may be found, usually indicated by the occurrence of garnierite. The more the ore is disintegrated by nature, the higher the iron content and the better the nickel extractions that may be expected therefrom. Table I shows extractions that may be expected from different types of ores, assuming treatment of -200 mesh products and that all precautions have been taken for obtaining maximum extractions. As for the distribution of the various nickel minerals and compounds that may be present, great variations may occur from locality to locality as well as vertically in a deposit. From such "run of

Jan 1, 1951

By J. W. Rutter, K. T. Aust

The temperature dependence of the rate of grain boundary migration was measured in bicrystals of zone-refined lead containing from 20 to less than 1 ppm by wezght of tin. The apparent activation energy in the temperature range from 320" to 200oC is markedly dependent upon the solute tin concentration and upon the orientation relationship of the grains adjacent to the grain boundavy. The quantitative experimental observat~ons are compared with the predictions of various theories of grain boundary migration. In previous work.&apos;?&apos; the mobility of individual grain boundaries was studied as a function of impurity concentration and type of boundary. Grain boundary migration occurred at the expense of dislocation arrays which were introduced into the specimen during solidification. Boundary mobility in zone-refined lead at 300°C was markedly decreased by small additions of tin. 0.004 wt pct being sufficient to decrease the rate of grain boundary migration by a factor of 1000. The mobility of grain boundaries having polar orientation relationships near 38 and 22 deg about <Ill>, and 28 deg about <100>, was much less sensitive to tin concentration in the range studied. As a result, these boundaries have relatively high mobilities. The present paper is a continuation of the above study. Data are now presented on the temperature dependence of the motion of individual grain boundaries in zone-refined lead as a function of solute tin concentration and orientation relationship of adjacent grains at the grain boundary. The experimental observations are compared with the predictions of a number of theories of grain boundary migration3-8 which, prior to the present experimental investigation, could not be critically evaluated. EXPERIMENTAL PROCEDURE The striation or lineage structure of melt-grown single crystals of zone-refined lead, containing various additions of tin, was utilized to provide a driving force for grain boundary migration, as previously described.1,2 Each grain boundary under study separated the striated single crystal from another grain which was introduced by localized plastic deformation and recrystallization of a small region of the sample. The speed of migration of grain boundaries in dilute alloys of tin in zone-refined lead was investigated as a function of 1) tin concentration from < 0.0001 to 0.002 wt pct, 2) temperature in the range of 200" to 320°C, and 3) orientation relationship of the adjacent grains at the grain boundary. The substructure driving energy available for grain boundary migration was estimated to be about 4000 ergs per cu cm, within a factor of two, from specimen to specimen.&apos; The specimen dimensions, and growth and alloying procedures for the preparation of striated single crystals of lead of known tin composition, were as described previously.&apos; Each bicrystal was carefully wrapped in aluminum foil, and annealed in a well-stirred salt bath consisting of 50 pct NaNO2 and 50 pct KNO3, for known periods of time at a series of constant temperatures (*2°C). The grain boundary positions, before and after each anneal, were determined by etching lightly in a solution of 5 pct nitric acid in methyl alcohol, in order to follow the motion of the boundary and determine its rate of migration. Thus, the rate of motion of the grain boundary in a single specimen was measured at various temperatures. The above procedure was carried out for each grain boundary in seventeen different bicrystal specimens.

Jan 1, 1960

By M. E. Wadsworth, T. L. MacKay

Sintered UO, samples were leached in sulfuric acid solutions of various concentrations. A pressurized system was used so that it was possible to investigate the kinetics of the reaction to 270°C with oxygen overpressures as high as 900 psi. The rate was observed to be a function of the concentration of hydrogen ions and directly proportional to the partial pressure of oxygen. Evidences are presented which indicate that a UO2 surface site reacts with a molecule of water to form a hydroxyl complex which in turn can dissociate with the characteristics of a weak acid. A rate determining step has been proposed which involves the reaction between an oxygen molecule and the hydroxyl complex on the surface of UO,. ThE 2 principal methods for uranium dissolution are carbonate and acid leaching. The sulfuric acid leach is the more popular and is used for the treatment of the majority of the ores of Africa, Canada, and the United States. Low recoveries in basic leach circuits led investigators at the University of British columbia1 to study leaching of uranium ores in pressurized vessels. Early in the study of dissolution of uranium it was found that only uranium in the hexava-lent state could be leached in acid or basic circuits. Therefore, the use of oxygen over-pressure in an autoclave offered an interesting approach to solving the low recovery problems of carbonate leaching. UO, was used in this study because it could be obtained in high purity and also because it is representative of the most refractory of the primary uranium minerals. A pressurized system was used to provide a means whereby important temperature and pressure parameters could be varied for the evaluation of the kinetic processes. The mechanism for the dissolution of UO2 should be similar for any of the uraninite type minerals. At the present all of the kinetic studies that have been conducted have been in carbonate media. Peters and Halpern2 carried out a kinetic study of the leaching of pitchblende. Their specimens were pitchblende ores selected on the basis of high grade and homogeneity. Pearson and wadsworth3 conducted a kinetic study of the dissolution of UO2 in carbonate solutions with results very similar to those obtained by Peters and Halpern. EXPERIMENTAL The UO2 as received* was found by spectroscopic *Mallinckrodt reagent, supplied by the Atomic Energy Commission. analysis to have a purity of 99.94 pct 0.03. It was ground in a mechanical agate mortar and screened through a 400-mesh sieve. Thin flat disks of UO2 were prepared by pressing the sized powder in a specially constructed die at a total pressure of approximately 25 tons per sq in. The pressed disks were approximately 0.25 cm thick, 1.6 cm diam, and 3.5 g in weight. As pressed, the samples were approximately 65 pct of theoretical density. It was essential that a binder such as poly-vinyl alcohol be added before pressing to prevent formation of cracks when fired. It was found by trial and error that pressed disks sintered close to 1870°C in a hydrogen atmosphere, reach densities between 91 and 91.5 pct of the theoretical density. At this density the samples had no measurable porosity based upon a 2-hr emersion in boiling water. An X-ray examination of these sintered UO2 disks showed them to be identical with the original UO2 received. Reaction of UO2 with the alundum furnace core was prevented by placing molybdenum between the samples and the core according to the method of Corwin and Eyerly.4 Leaching studies were carried out in a specially designed autoclave, the details of which have been presented e1sewhere.6 The main features of the equipment as applied to a kinetic study are: 1) solution samples may be removed during the course of a single run; and 2) temperature and agitation are carefully controlled. Two-ml samples removed from the autoclave during the course of a run were analyzed for U3O8 content with a Beckman model DK-2 spectrophotometer by the method of

Jan 1, 1959

By Wm. D. Owsley, R. E. Moeller

In the petroleum industry, the process known as oil well cementing is the equivalent of pressure grouting in the mining and construction industries. The science of oil well cementing has been known and practiced for many years. At the present time it has been brought to a high degree of perfection in the handling of many different types of jobs, all of which are known as oil well cementing. In order to understand more easily these processes, we will discuss briefly several different types of oil well cementing jobs, the purposes for which they are performed, and the methods of their accomplishment. It is believed that some of .these procedures, in a modified form, can be applied to pressure grouting projects in general. Originally, oil well cementing consisted of placing a neat cement slurry about a steel casing set in a bore hole. Cement is used about these casings to protect them from the corrosive effects of ground waters, to protect the oil and gas zones from encroachment of undesired water from other levels, to prevent the blowing out of high pressure oil and gas zones from shallow levels, and to strengthen generally and support the casing being placed in the bore hole. After the bore hole is completed to the desired depth, casing is run into the well, pumps are attached to this casing and circulation of the mud fluid in the hole is established; this circulation being from the inside of the casing into the annulus about the casing, and thence back to the surface. Next, a cement slurry is mixed and pumped into the inside of the casing string, A plug, which acts as a piston within the casing, is placed above the cement slurry. This is to separate the top of the cement slurry from mud or water which is used to shove the cement down through the casing and out into the annulus. This plug further serves the purpose of shutting off against a baffle in the bottom end of the casing string, thus stopping the flow of cement out of the casing and leaving the shoe, or lower end of the casing, surrounded by cement and also filling the annulus there above. Casing strings cemented in the above described manner may vary in length from a few feet of large diameter pipe to very long lengths of smaller pipe. As of the present date the longest string of casing which has yet been cemented is some 16,600 ft deep. As a general rule, the deeper the well and the more cement slurry used, the higher the pressures which are required to place the slurry. In parts of West Texas, it is not uncommon to use 4000 sacks to cement a single string of casing in place. Machinery used to mix the cement and place it into the casing is mounted on heavy duty, powerfully equipped trucks which are capable of negotiating any type of highway or country roads. These trucks

Jan 1, 1949

By T. B. Counselman

Probably the earliest concentration of iron ore in this country was carried on in the northeastern magnetite areas. Magnetic concentration was relatively simple and gave a concentrate that, after agglomeration, and in spite of being high in phosphorus because of the dry concentrating methods then in use, was satisfactory blast-furnace feed. Production from the northeastern magnetite area languished after the discovery and development of the Lake Superior ores, where there was seemingly an unlimited tonnage of high-grade ore, first the Michigan ores, and subsequently the still larger deposits of Minnesota. For years only the higher grade, direct shipping ores of the Lake Superior district were mined. Those of Michigan, and of the Vermilion Range in Minnesota, were hard ores and came principally from underground mines. The softer ores of the Mesabi came partly from underground mines, but mostly from the enormous deposits that could be worked by open-pit methods. The costs of ore from these open-pit deposits, even with the high initial cost of stripping, were so low that the underground mines of the Mesabi could hardly compete. The so-called Old Range ores, of Michigan and of the Vermilion. Range of Minnesota, were hard and lumpy, and opened UP the burden in the blast furnace, therefore making possible harder driving with greater output. Also, some of these ores were of such grade and physical characteristics that they were suitable for charge ore in the open hearth. These ores, therefore, commanded a price premium, and could compete with the softer, finer, but cheaper, Mesabi ores. The big tonnage reserves, however, are on the Mesabi. and it is these big open-pit deposits that constitute our stock pile of iron ore, from which we are drawing so heavily during this war period. On the western end of the Mesabi the ore was found to be high in silica, and not suitable as furnace feed. As early as 1902, attempts were made to concentrate this so-called wash ore and by 1910 the first washing plant was put into operation. The Process was very simple, consisting essentially of a sizing and washing operation, with scalping screens, logwashers, and tables, which later were replaced by classifiers. Ore particles finer than 100 mesh were deliberately wasted, because these fines were undesirable in the furnace. Fortunately, these tailings were impounded, and already are being reworked. Before long some of the low-grade ores began to require more elaborate treatment than the simple washing operation and, tables having been discarded because of their low capacity, in favor of classifiers, jigs were next introduced. These were able to discard coarser pieces of tailing than classifiers. jigs are in active use today, various improvements having been made in their design and application. Various other machines and methods of concentration have been tried from time to time, and have in turn been discarded for more improved processes. The latest and most important process that has been

Jan 1, 1947

By T. B. Counselman

Probably the earliest concentration of iron ore in this country was carried on in the northeastern magnetite areas. Magnetic concentration was relatively simple and gave a concentrate that, after agglomeration, and in spite of being high in phosphorus because of the dry concentrating methods then in use, was satisfactory blast-furnace feed. Production from the northeastern magnetite area languished after the discovery and development of the Lake Superior ores, where there was seemingly an unlimited tonnage of high-grade ore, first the Michigan ores, and subsequently the still larger deposits of Minnesota. For years only the higher grade, direct shipping ores of the Lake Superior district were mined. Those of Michigan, and of the Vermilion Range in Minnesota, were hard ores and came principally from underground mines. The softer ores of the Mesabi came partly from underground mines, but mostly from the enormous deposits that could be worked by open-pit methods. The costs of ore from these open-pit deposits, even with the high initial cost of stripping, were so low that the underground mines of the Mesabi could hardly compete. The so-called Old Range ores, of Michigan and of the Vermilion. Range of Minnesota, were hard and lumpy, and opened UP the burden in the blast furnace, therefore making possible harder driving with greater output. Also, some of these ores were of such grade and physical characteristics that they were suitable for charge ore in the open hearth. These ores, therefore, commanded a price premium, and could compete with the softer, finer, but cheaper, Mesabi ores. The big tonnage reserves, however, are on the Mesabi. and it is these big open-pit deposits that constitute our stock pile of iron ore, from which we are drawing so heavily during this war period. On the western end of the Mesabi the ore was found to be high in silica, and not suitable as furnace feed. As early as 1902, attempts were made to concentrate this so-called wash ore and by 1910 the first washing plant was put into operation. The Process was very simple, consisting essentially of a sizing and washing operation, with scalping screens, logwashers, and tables, which later were replaced by classifiers. Ore particles finer than 100 mesh were deliberately wasted, because these fines were undesirable in the furnace. Fortunately, these tailings were impounded, and already are being reworked. Before long some of the low-grade ores began to require more elaborate treatment than the simple washing operation and, tables having been discarded because of their low capacity, in favor of classifiers, jigs were next introduced. These were able to discard coarser pieces of tailing than classifiers. jigs are in active use today, various improvements having been made in their design and application. Various other machines and methods of concentration have been tried from time to time, and have in turn been discarded for more improved processes. The latest and most important process that has been

Jan 1, 1947

By J. J. Gilman

Zinc monocrystals, when compressed nearly parallel to their basal planes (within 20), deform in a new way; and certain deformation markings, called "-bands," are typical of this new mode. Characteristics of these bands are described. Mechanical behavior of low angle zinc monocrystals was investigated in some detail. Recrystallization did not occur upon annealing of banded specimens that were free of deformation twins. -Bands do not seem to be the result of nonbasal slip, but rather, a result of a microbuckling mechanism. u-Bands differ qualitatively and quantitatively from ortho kink bands. A dislocation model, consistent with some of the features of u-bands, is described. THE plastic deformation of zinc monocrystals with slip planes (0001) nearly parallel to the stress axis was studied in this investigation. In a previous investigation, it was shown that some low angle zinc crystals (those with slip planes making angles of more than about 2.5+1° with the compression axis), deform by ortho kinking while others (those with slip planes making angles of less than 2.5+1° with the compression axis) deform in a new way.&apos; This new mode of deformation will be described in some detail here. Some of its striking features are: 1—it operates only for compressive stresses, 2—its temperature dependence is anomalous, and 3—it exhibits a new type of "yield-point" behavior. The mode of deformation to be discussed is not new in the sense that no previous evidence of its existence had been reported. The markings that it creates on the cleavage surfaces of zinc crystals have been described by several investigators.&apos;" However, this is the first time that it has been made to operate under controlled conditions so that its response to mechanical variables, temperature, and aging treatments could be investigated and its geometry completely described. Apparently. Jillson&apos; as well as Holden3 and Pratt" believed that the small bands they observed were simply small versions of ortho kink bands. In fact, two of these authors3,6 "alled the markings "micro kink bands." In spite of the precedence, it is felt that this term is not entirely suitable because these bands do not have the same genesis as kink bands, and they are qualitatively different in structure. As will be indicated by later discussion, the bands seem to be related to the tensile deformation bands observed in aluminum. The present author has chosen to call the bands "micro deformation bands," or simply ",ubands," and the deformation process, &apos;&apos;p-banding." Experimental Methods Crystals were grown from 99.999+ pct Zn obtained from the New Jersey Zinc Co. The details of the technique are given elsewhere." It should suffice to say that the crystals were seeded for orientation control, and precision pyrex tubes were used for molding them. About 40 crystals were used, yielding some 130 specimens. Fig. 1 illustrates the typical form of the specimens and shows how the orientation angles are defined. The crystal specimens were usually 1 3/4 in. long and about 150 mil in diameter. The angle between the slip or cleavage plane (0001) and the specimen axis is designated by xo, while a is the angle between the maximum slope of the (0001) plane and the nearest close-packed direction [1210], vary ing from 0°to 30°. The crystals were cut into specimens with a jeweler&apos;s saw and the ends were squared by filing (specimens held in V-block). Crystals of this orientation are stiff toward bending, so this procedure introduced only deformation localized at the ends. Then the specimens were polished either chemically in 50 pct HNO³ or electrolytically in 20 pct chromic acid. The mechanical tests were made with an Instron testing machine. This machine weighs by means of electric strain gages on elastic bars and is quite stiff, since the full-load deflection of its load cells is at most 0.002 in. Most of the testing was done at a

Jan 1, 1956

By W. W. Odell

Once it was believed that anthracite or coke were the only fuels generally available and suitable for the generation of water gas, particularly so when this gas was made in the generators of standard carburetted water-gas sets such as are commonly used in the manufacture of city gas. During the past 8 years, practice has changed considerably and it is now common to find gas plants operating without anthracite or coke and using bituminous coal in the generator. This change in fuel has appreciably increased the marketability and sales of certain coal producers&apos; products; accordingly it is of interest to coal operators and others to know the reason for this change, the present trend in practice and the adaptability of various coals for generation of water gas. This paper briefly discusses these conditions and some of the factors relating thereto. Bituminous Coal not Ideal but Cheaper than Coke In spite of many changes which have been made in both process and generating apparatus for using bituminous coal as generator fuel more efficiently, in general it is not an ideal fuel for this purpose. It is supplanting coke because it costs less; it is so much cheaper per ton delivered at the gas works that water gas made therefrom costs less per unit-volume than that made from coke, even though the quantity of generator fuel consumed per therm (100,000 B. t. u.) of gas made is greater with coal. This is the reason why so many city gas plants, as well as others, are using bituminous coal instead of coke. Conditions Favoring Change from Coke to Coal The conditions which have made it possible and feasible, as well as economical, to supplant coke with coal may be summarized as follows: (1) Changes in methods of operating and alteration in generating apparatus; (2) lowering of the calorific standards for city gas, and (3) availability

Jan 1, 1927

By C. B. Post, D. G. Schoffstall

A determinatioil of the hydrogen content of molten steel by means of the Vacuum-extraction method, as reported here, consists in first casting a sample of the bath in a bomb, so that the gases evolved during solidification are trapped for analysis. A portion of the cast steel sample is then prepared and heated at a temperature of 600" to 800°C. under high vacuum, and the gaser given off during this vacuum extraction (which are shown to be hydrogen), are collected and measured. Analysis of the gases evolved on solidification and the gases in the solid sample enables an accurate determination of hydrogen in the molten steel. Fig. I shows the bomb and accessories that have been found suitable for trapping the gases evolved on solidification. The bomb is made of scamless steel pipe, approximately 7 in. long by 136 in. i.d., and welded at the bottom. An ordinary pipe cap has a vacuuni-type metal stopcock threaded and brazed in its upper end. This pipe cap fits onto the bomb by means of machined threads. A flange is brazed to the pipe at the point where the cap starts to tighten up, and a rubber gasket is placed between the flange and cap. Heavy vacuum grease is used between the flange and gasket and the gasket and cap. The weight of the complete bomb and it? interval volume is known before the sample is cast. In practice, a sample of about 400 grams of steel is poured into the bomb, the funnel quickly swung out of the way, the bomb cap spun down the threads and tightened against the gasket, and the bomb set in a pail of water to keep the gasket and vacuum grease cool. It is estimated that at least 80 per cent 01 the gases evolved from the liquid sample during solidification are trapped in the bomb."

Jan 1, 1945

By A. U. Seybolt, J. L. Walter

The effects of the addition of 0.5 pct ThO2 (by volume) on the grain structure and texture of heavily rolled tungsten sheet were studied. Powder metallurgy ingots were rolled to sheet, 0.001 in. thick, and samples were annealed at temperatures from 1200" to 2500°C. The heating rate to the anneal temperature was varied from 3°C per min to 6500°C per min. The orientations of the largest grains were determined by X-ray diffraction. The disposition and loss of the ThO2 particles were determined by electron transmission microscopy and the activation energy for remozlal of the thorium was measured by mass spec-troscopy. Heating rates below about 800 C per min produced large, highly elongated grains. Higher heating rates produced much smaller, less elongated grains. The grain structure and texture of the slowly heated samples were identical to the structures and textures of heavily rolled tungsten foil conventionally doped with aluminum, silicon, and potassium but the recrystallization temperature was about 200°C lower. There was stringer-like dispersion of larger ThO2, particles superimposed on a uniform dispersion of fine particles. The particles increased in size and decreased in number with time at temperature. The loss of particles was accompanied by formation of grain boundary voids and surface pits. The activation energy for removal of the ThO2 was about 40 kcal per mole. THE addition of small amounts of aluminum, silicon, and potassium to tungsten has a profound effect on the grain structure of heavily rolled sheet1 or drawn wire."4 Thus, "doped" tungsten sheet, rolled to 0.001 in. and recrystallized, develops a structure consisting of large, highly elongated grains of a specific preferred orientation.&apos; It has been shown that the elongated grain structure was caused by a dispersion of particles, identified as mullite (Al6si2O13),1,4 in strings parallel to the rolling direction in sheet or to the wire axis. Identical results were obtained for iron which was doped with glass and rolled to 99 pct reduction of thickness and recrystallized.5 Again, the glass particles were disposed in strings parallel to the rolling direction. The strings retarded boundary migration in the lateral direction but grain growth was able to proceed relatively unhindered along the direction parallel to the strings.1,5 In both the doped tungsten and the glass-doped iron, the particles were highly plastic during the high-temperature deformation. Since mullite melts at about 1800°C and the glass employed melts at about 810ºC, the particles were probably molten during the recrystallization anneals (above 1800°C for the doped tungsten and 850°C for the glass-doped iron). There are indications in the literature that particles not plastic at hot-working temperatures (up to about 1550°C for tungsten) may also impart elongated grain structures by primary recrystallization of worked alloys. Examples are dispersions of tantalum carbide in chromium,6 and ThO2 in nickel where elongation ratios of recrystallization grains of up to 20:l were obtained.7 Strings of ThO2 particles in W-ThO2 wire have been seen by Rieck.8 In view of the available evidence, it was of interest to extend the previous studies of doped tungsten and glass-doped iron to include W-ThO2 sheet materials. Of specific interest was the grain structure, preferred orientation, recrystallization temperature, and disposition of the thoria particles. EXPERIMENTAL PROCEDURE A) Material Preparation. About 380 g of blue tungsten oxide (approximate composition WO3) was wet with a sufficient amount of aqueous solution of Th(N03)4 to provide 0.5 vol pct ThO2. The wet mixture was stirred to distribute the doping material uniformly throughout the powder. Stirring was continued while the mixture was heated until it was completely dry. The dried, doped mixture was then reduced to tungsten powder by heating at 850°C for 2 hr in a stream of dry hydrogen. The doped tungsten powder was hydropressed in a rubber sack at pressures of 50,000 psi to produce an ingot approximately 2 cm diam by about 5 cm long. Next, the pressed cylinder was heated in hydrogen for 2 hr at 1350°C to render it strong enough for machining. The cylinder was machined to a square cross section of 1.6 by 1.6 cm with rounded corners. Finally, the bar was heated for 2 hr at 2150°C in hydrogen to provide a sufficiently dense mate rial to withstand the hot-rolling operation. Prior to rolling, the ingot was reduced in thickness by about 20 pct by forging at 1550°C. This served to increase the density of the material and to widen it slightly for better rolling characteristics. The forged ingot was then rolled at 1550°C to a reduction of 45 pct of thickness, following which the rolling temperature was reduced to 1300°C and the slab rolled, with several reheats, to 0.050 in. Further reduction was accomplished at 800°C in tungsten sheet packs to a total reduction of about 99.85 pct. B) Annealing Treatment and Observation of Structure. Small samples of the rolled foil were annealed in one of two ways. Some of the samples were suspended in a covered tungsten can and annealed at temperatures from 1200" to 2200°C for various times in vacuum of l0-7 to 10-6 mm Hg. The can was heated by induction and temperatures were determined by optical pyrometry

Jan 1, 1970

By J. T. Norton, N. J. Grant, A. R. Chaudhuri

MOST of the recent work to establish the mech-anism of creep in metals at high temperatures has utilized aluminum as the experimental material. It was thought desirable to initiate an investigation of a hexagonal close-packed metal, because of the relatively simple slip system, and compare the observed deformation characteristics with those that have been observed for the face-centerd cubic metals. High-purity magnesium was chosen for this purpose, first, because its strength and other mechanical properties are similar to those of aluminum in the same temperature range, and second, because the existing equipment was ideally suited to observe magnesium during creep. It is proposed in this paper to present a pictorial and qualitative account of the changes that high-purity magnesium undergoes during creep at 500°F. The characteristics of deformation of aluminum described below have been observed by various workers and accounts of these may be obtained from the papers of Chang and Grant.&apos;- These characteristics are: slip, subgrain formation, grain boundary sliding and migration, fold formation, deformation bands, and kink bands. It is well known that in a flat magnesium specimen, slip on the basal plane (0001) in the [1120] direction results in the formation of straight bands on the surface of the specimen. Schmid and co-workers&apos; have shown that this system is operative in the temperature range of -185" to 300°C (-300° to 572°F). They have also shown that a second system, slip on the pyramidal planes {1071} or {1012} in the [1120] direction, is operative at temperatures higher than 225°C (437°F). Between 225° and 300°C (437" to 572°F), therefore, deformation by both these systems is expected. Bakarian and Mathewson5 confirmed the occurrence of pyramidal slip on the {1011} plane and found that it resulted in irregular markings on the surfaces of their specimens. Burke and Hibbard6 obtained evidence of pyramidal slip in single crystals of magnesium deformed at room temperature. Bakarian and Mathewson5 suggested that the irregular appearance of these bands was due to slip on both of the pyramidal planes occurring simultaneously but in the same direction, the close angular relationship between the planes making this process possible. Furthermore, since neither of these planes is close enough to the basal plane, slip on the latter does not exhibit the irregular appearance of slip bands resulting from pyramidal slip. Experimental Procedure High-purity magnesium, supplied by the Dow Chemical Co., was used in these experiments. The analysis was as follows: Al, 0.0002 pct; Mn, 0.0018; Fe, 0.0024; Cu, 0.0002; Sn, 0.001; Ca, 0.01; Ni, 0.0003; Zn, 0.01; Pb, 0.0005; Si, 0.001; and Mg, 99.972. The magnesium was supplied in the form of 1/2 in. diam rods. The specimens had an overall length of 21/4 in., the round ends being threaded to fit the specimen holders. The previously round 3/16 in. diam gage section of the specimen had two parallel flats machined on opposite sides for microscopic observation, yielding a test zone having the dimensions of lx3/16x7/64 in. The specimens were electrolytically polished (without prior mechanical polishing of the machined flats), in a solution composed of 375 ml of ortho-phosphoric acid and 625 ml of ethyl alcohol.&apos; The cathode was a stainless steel sheet bent so that the specimen was completely surrounded. The voltage for successful polishing was 1.5 v at 100 to 300 milli-amp current. Electropolishing for about 45 min sufficed to obtain a good metallographic surface on the specimens after they had been machined. The creep tests were performed under constant load, and two types of equipment were used. In the first, designed by Servi and Grant,V he specimens were beam-loaded, and a furnace could be lowered to surround the specimen. As the microstructural changes could not be observed during the course of the test, the tests had to be interrupted periodically by removing the specimen for microscopic examination. The second unit was a high temperature microscopy furnace designed by Chang and Grant.&apos; The furnace was fitted with an optically flat quartz window having area dimensions 1.25x0.5 in., so that the whole test portion could be viewed through it at magnifications up to x240. The metallurgical microscope had three mutually perpendicular axes of motion, and, in addition, it was possible to measure angular displacements by rotation of the eyepiece. It was thus possible to make precise observations of the specimen during creep, and micrographs could be taken by attaching a camera to the eyepiece of the microscope. The average grain size of the specimens that were tested was about 1 to 3 mm. This grain size could

Jan 1, 1954