By N. J. Grant, Hans Brunner

ThE materials used in this investigation were furnished by the Aluminum Co. of America and consisted of high-purity alurhinum (99.995 pct) and two aluminum-magnesium alloys containing approximately 2 and 5 pct Mg. The compositions of these alloys are listed in Table I. The materials were received as hot rolled 3/8-in. diam rods and were made from the same heats as the materials which were previously used in this laboratory.'j3 The rods were cold swaged to 1/4-in. diam by 1 in. long, and then had two parallel flats machined over the gage length 0.085 in. apart. The test bars were annealed for 10 min at 700° F, and strained 1 pct in tension at room temperature. They were electropolished (80 pct acetic acid; 20 pct perchloric acid, 70 pct concentration) at a temperature of 60°F at approximately 20 v. A grid, transverse or square, spaced 0.2 mm apart, was impressed by rolling a fine threaded screw (128 threads per in.) across the flat surfaces. The depth of the grooves was less than 5 p. For final annealing and grain size control the specimens were enclosed in aluminum foil and sealed in Vycor tubes. Annealing conditions varied from 1 hr at 700° F to 5 days at 1050° F, depending on the alloy content, to give for most of the specimens a final grain size of about 1 mm. This treatment was followed by electropol-ishing as described above. For the test series presented in Figs. 4 and 5 round specimens were used instead of flat ones, and fine machining marks served as marker lines instead of the impressed grid lines. Electropolishing was omitted. The major advantage is that the spacing of the machining marks is only about 1 u as compared to the 200 u of the impressed grid lines, permitting higher precision in strain measurements. Unfortunately the strain annealing necessary for grain size control also resulted in some preferred orientation of the grains. The preferred orientation of three arbitrary specimens was measured by X-ray diffraction methods and the averaged results are shown in Fig. 1. The possible effects of the preferred orientation on the test results will be discussed later. The testing temperatures were 410°, 515", 725", and 940° F, with one exception in the case of the 5.1 pct Mg alloy. Since the solubility limit of this alloy is 520°F, a test temperature of 545°F was cho-se sen instead of 515°F. The selection of the test temperature was based on two considerations: 1) at 900°F and above, extensive grain boundary migration made it more difficult to measure grain boundary sliding; 2) at 400°F and below, there was so little grain boundary sliding that it was again difficult to make precise measurements. The stress was chosen to give a creep rate of approximately 2.7 pct per hr in connection with Figs. 2

Jan 1, 1961

By G. A. Chadwick, D. Jaffrey

The morpho1ogies and orientation relationships of the phases in the Sn-Zn and A1-A13Ni eutectic systems were examined by electron microscopy and X-ray diffraction techniques. In each alloy the "transition" from the lamellar to the fibrous morphology was found to be one of scale, not of type. The minor phase in both systems exhibited certain well developed facets which were not affected by changes in the ingot solidification rate. The crystallographic relationships displayed by the pairs of phases in both systems were also insensitive to the growth rate. In the Sn-Zn alloy, the unique relationship of: growth direction - II [1201 Sn - II [01101 Zn and ribbon interface plane 11 (101) Sn 11 (7012) Zn was determined. The Al-Al3Ni alloy phases did not possess any particular orientation relationship, though the Al3Ni phase invariably grew in the [010] direction and exhibited the same set of facet planes. These results are discussed in relation to current eutectic growth theories and explanations of the "lamellar to fibrous transition". THE lamellar to fibrous transition that occurs in many eutectic alloys has been the subject of considerable speculation and experimental study. In some alloys it can be induced solely by an increase in the solidification rate,'-3 whereas in others the transition supposedly occurs only if the lamellae are forced to grow out of the overall ingot growth direction.4-6 he cause of this latter type of transition has been attributed to deviations of the lamellae from their low energy habit planes;4'5'7 fibers are produced because the sustaining force for lamellar growth (a low energy boundary) is destroyed. Implicit in these explanations is the assumption that fibers are circular in cross-section and completely lacking in low energy inter-phase interfaces. The "natural" growth rate dependent transition has been studied less thoroughly although Tiller8 has attempted a theoretical explanation of it. Tiller's arguments are not completely satisfactory9 but his suggestion that the relative undercoolings of the solid/liquid interface for lamellar and fibrous morphologies are growth rate dependent cannot be totally discounted; it is possible, for instance, that the relative interfacial undercoolings could alter and produce the observed morphology change if the orientation relationships between the phases and the associated interphase bound- ary energies were sensitive to growth rate. Salkind et al." have reported finding a change in the orientation relationships in the A1-A13Ni system accompanying the lamellar to fibrous transition, but contradictory evidence has also been reported for this3'" and another system,12 so the position remains unclear. In an attempt to clarify matters a study was made of the "lamellar to fibrous" transition in the Sn-Zn and A1-A13Ni eutectic systems; the morphologies of these two selected systems are quite similar when viewed by optical microscopy. In the present research the morphologies and morphology changes were investigated by electron microscopy. The orientation relationships existing between the eutectic phases were also determined for both morphologies in both eutectic systems. EXPERIMENTAL PROCEDURE The materials and method of alloy preparation and ingot solidification for the Sn-Zn system have been reported previously.2 In this investigation nine horizontally grown ingots of the highest purity (99.9997 pct) were used. The temperature gradient in the melt was not intentionally varied and was approximately 10°C per cm. Seven growth rates between 1.3 cm per hr and 20 cm per hr were imposed. The A1-A13Ni alloys were prepared from "Spec. Pure" nickel and 99.995 pct aluminum by melting the components in an open alumina crucible and casting the melt into the cold graphite mold. Six ingots of the Al-Al3Ni alloy were unidirectionally solidified at growth rates from 1 cm per hr to 12 cm per hr under high purity argon. A typical ingot was 20 cm long, 1 cm wide, and 0.75 cm to 1.5 cm thick. Samples taken from the bars at positions 12 cm from the nucleation end were examined by conventional orthogonal-section metallo-graphic techniques. When required, samples were mounted for X-ray diffraction analysis using the Laue back-reflection technique with a finely focussed X-ray source. The surfaces of the A1-A13Ni specimens were prepared by mechanically polishing them down to the 1 µ diamond pad stage followed by an electropolish in 80/20 methanol/perchloric acid solution at 0°C and 20 to 30 v. The Sn-Zn specimens were repeatedly polished on an alumina pad and etched in hot dilute (2 pct) nitric acid until the diffraction spots were found to be sharp. Thin films of the alloys were prepared for observation in an electron microscope by spark machining thin discs (0.03 to 0.04 in. thick) from longitudinal and lateral sections of the bars and elec-trolytically thinning them via a jet polishing technique. For the A1-A13Ni eutectic alloy, an 80/20 mixture of ethanol/perchloric acid at 40 v and 20°C was found to be satisfactory. A solution of 70/20/10 methanol/perchloric acid/butylcellosolve at 25 v and 20°C was used on the Sn-Zn alloy. For the former alloy the jet nozzles (cathodes) and the disc clamps were of aluminum;

Jan 1, 1970

By W. T. Lankford, Edward Saibel

During the course of an investigation of the plastic flow of aluminum aircraft sheet under combined loads, several problems arose in which analyses of the conditions leading to unstable plastic flow were needed. In order to provide these analyses, and in the hope of attaining a better understanding of the general problem of unstable plastic flow, the present study was undertaken. It is well known that unstable plastic flow is associated with a form of mechanical instabi!ity frequently observed during the plastic deformation of ductile metals. This instability is characterized by the fact that, at its onset, plastic straining mill proceed at a constant magnitude of the externally applied forces. It is further typical that the resulting unstable flow is generally accompanied by the formation of a neck, a local bulging, or some other form of heterogcneous deformation. Perhaps the most familiar example of unstable plastic flow to the metallurgist is the formation of the neck in the ordinary tension test. It is well known that in this test most metals exhibit a maximum in the externally applied load, followed by the process commonly referred to as "necking down." Instability in the simple tension test has been frequently discussed and numerous investigators1'2'3'12 have derived the criterion for instability in terms of a critical rate of strain hardening. It is the purpose of the present study to extend the criterion for unstable flow to the more general case where the body undergoing flow is subjected to combined loads. It is hoped that the problems considered will provide a more consistent picture of the general features of this important form of mechanical instability. The most practical implications of instability in plastic flow arise in connection with sheet metal forming operations. In the formation of a great many sheet metal parts, the deformations are produced primarily by stretching. If the conditions which lead to unstable flow are fulfilled in such a formation, and if the resultant instability leads to a pronounced localization of flow, then the useful limit of ductility of the material will have been reached. It i; also essential that the effects of instability be taken into consideration in any study of the plastic flow and rupture of metals under combined stresses. In general, when unstable plastic flow is initiated, straining becomes localized, the geometry of the test splecimen changes, and the state of stress in that portion of the specimen undergoing plastic flow is no longer under external control. In many past studies of the effects of combinetl Metals On flow and rupture) account has not been taken of the fact that, although a given test may be started under constant

Jan 1, 1947

By Edward Saibel, W. T. Lankford

During the course of an investigation of the plastic flow of aluminum aircraft sheet under combined loads, several problems arose in which analyses of the conditions leading to unstable plastic flow were needed. In order to provide these analyses, and in the hope of attaining a better understanding of the general problem of unstable plastic flow, the present study was undertaken. It is well known that unstable plastic flow is associated with a form of mechanical instabi!ity frequently observed during the plastic deformation of ductile metals. This instability is characterized by the fact that, at its onset, plastic straining mill proceed at a constant magnitude of the externally applied forces. It is further typical that the resulting unstable flow is generally accompanied by the formation of a neck, a local bulging, or some other form of heterogcneous deformation. Perhaps the most familiar example of unstable plastic flow to the metallurgist is the formation of the neck in the ordinary tension test. It is well known that in this test most metals exhibit a maximum in the externally applied load, followed by the process commonly referred to as "necking down." Instability in the simple tension test has been frequently discussed and numerous investigators1'2'3'12 have derived the criterion for instability in terms of a critical rate of strain hardening. It is the purpose of the present study to extend the criterion for unstable flow to the more general case where the body undergoing flow is subjected to combined loads. It is hoped that the problems considered will provide a more consistent picture of the general features of this important form of mechanical instability. The most practical implications of instability in plastic flow arise in connection with sheet metal forming operations. In the formation of a great many sheet metal parts, the deformations are produced primarily by stretching. If the conditions which lead to unstable flow are fulfilled in such a formation, and if the resultant instability leads to a pronounced localization of flow, then the useful limit of ductility of the material will have been reached. It i; also essential that the effects of instability be taken into consideration in any study of the plastic flow and rupture of metals under combined stresses. In general, when unstable plastic flow is initiated, straining becomes localized, the geometry of the test splecimen changes, and the state of stress in that portion of the specimen undergoing plastic flow is no longer under external control. In many past studies of the effects of combinetl Metals On flow and rupture) account has not been taken of the fact that, although a given test may be started under constant

Jan 1, 1947

By Walter H. Bruckner, George B. Clark

Since the end of World War 11 interest has been increasing in the use of shaped charges in the mining industry and in other industries using explosives for blasting purposes. Shaped charges employ the principle known as the "Munroe effect," which was discovered by Charles E. Munroe more than 50 years ago (in 1888). Details of their design have been explained elsewhere.1,2,3 Fig I shows the essential features of design of two types of shaped charges (with conical and hemispherical cavities) and a schematic sketch of their action upon detonation. The following discussion deals with the behavior of the metal in the cavity liners when they are subjected to intense Pressures exerted when the explosive charge is detonated. Among the conclusions reached in research on shaped explosive charges, the following have been established conceming cavity liners:1'2 I. The optimum wall thickness of a conical cavity liner is dependent upon the apex angle of the cone as well as On the base diameter of the charge. Acute apex angles require thinner walls for optimum perfonnance and more obtuse angles require thicker walls for the same base diameter. '. Cones were more effective in forming a penetrating jet when the walls were tapered; that is, the thickness of the wall of the cone increased from the apex down. 3. The physical and mechanical properties of metals have a marked effect upon their performance as cavity-liner material. Boiling point, ductility, malleability, ten-sile strength, and hardness are among the properties that influence the effectiveness of a metal used as a cavity liner. Lead, for example, makes a wide, flat crater in steel plates. Aluminum makes a deeper crater than lead, and an aluminum alloy having a high tensile strength makes a deeper hole, but slightly smaller in diameter. Cast iron makes a deep, narrow hole. These findings, together with the following analysis under Metallographic Survey of slug, offer solutions to many of the problems involved in solving the mechanism of the formation of Munroe jets. It has been fairly well established that cavity liners collapse in a manner similar to that indicated in Fig 2, Conical liners are known to collapse upon themselves while hemispherical liners are believed to turn inside out in the process of jet formation. The first has been definitely proved by recovery of collapsed portions of cones, while liners from partly detonated charges show that hemispheres may turn inside out. Fig 3 shows a sketch of a recovered slug from a 6-in. shaped charge using a 45" cone made of cast iron. (This size of charge drilled holes up to 3 ft in depth in solid granodiorite.)

Jan 1, 1949

By Wilhelm Rohn

When a metal solidifies, gas, initially present in solution, may be concentrated at the grain boundaries, leading to brittleness, or it may form solid compounds which, if localized at the grain boundaries, impair the properties. On the other hand, the solid compounds formed sometimes distribute themselves more or less uniformly, and hence may be relatively harmless. If metallic oxides are heated under a partial oxygen pressure less than that corresponding to the dissociation pressure of the oxide in solution in the melt, they will decompose and oxygen will tend to be eliminated from the melt. This paper presents data on the partial oxygen pressures of copper and nickel oxides over a wide range of temperatures; it also presents data regarding the amount and nature of the gases evolved in the vacuum melting of a 3500-kg. charge of nickel-chromium alloy and gives test values indicating the improvement in impact values ascribed to vacuum melting. The results of commercial experience with a 4-ton vacuum melting and casting furnace indicate that this method entails an increase in cost of about 10 cents per pound of ingot over orthodox practice, which may be justified for special products and may be lowered if hot metal is charged into the vacuum furnace. DISCUSSION (Howard Scott presiding) J. H. ScafF, New York, N. Y. (written discussion).—In the section of Dr. Rohn's paper describing the effect of melting -metals in vacuo, he says, "In this way plain copper, nickel and iron may be easily purified. For example, vacuum-melted copper does not contain any oxygen and for this reason it is never sensitive to hydrogen embrittlement." This statement is contrary to the results of our experiments at the Bell Telephone Laboratories on the effect of vacuum melting on the properties of copper. Several 150-gram samples of tough-pitch copper were melted in a vacuum of the order of 1 X 10-5 to 1 X 10-6 mm. Hg for 2 hr. Portions of the ingots obtained were swaged to 0.100 in., then drawn to wire 0.050 in. in diameter for physical and

Jan 1, 1933

By W. B. Hickman, J. J. Pickell, B. F. Swanson

Many physical properties of the porous media-immiscible liquid system are dependent upon the distribution of fluids within the pores; this in turn, is primarily a function of pore structure, liquid-liquiri interfacial tcnsion and liquid-solid wetting conditions. The cnpillary pressure hysteresis process provides a means of investigating the influence of pore structure upon fluid distribution for consistent sur/acc conditions. Invcstigntiot2s indicate that residual non-wetting-phase saturations /ollozuir,g the imbibition process (i.e.,wetting phase displacing nor2-wctting phase) are dependent upon both pore structure and initial non-raetting phase saturation and suggest that residual fluid is distributed as Discontinuous ,globules, one to a few pore sizes in dimension, thrnugh the entire range 01 pore sizes originally occupied. It clppears that air-mercury capillary pressure dala adequntely rellect the distribution of fluiris in a water-oil system when strong wetting condition preliczil. An oil-air counter-current imbibition technique has also been found to provide a rapid rneans of obtaining residual-initial saturation data. In a majority of cnses, rcsidual saturations detf-rniinecl from the oil-air or air-mercury process reasonably approximate residual oil saturation following water drive of a strongly water-wet medium. INTRODUCTION A reliable estimate of recoverable reserves depends not only on the amount of original oil-in-place but also on pore geometry and distribution of fluids within the pores. A critical parameter determining the recovery from a reservoir under waterflood, for example, is the amount and distribution of residual oil within the various rock types present. The purpose of this paper is to investigate the mechanism of capillary trapping and assess its importance in laboratory measureqents of residual oil saturation. The degree of wettability of a reservoir rock is recognized as an important factor in waterflood or imbibition experiments. In this paper, however, only the water-wet case has been considered. Considerable experimental evidence1 suggests that for water-wet rocks, capillary forces predominate in tile distribution of fluids and that viscous forces in the range normallv of interest in the reservoir have a minimum influence on residual oil saturation. It follows that if the ultimate recovery is controlled by pore geometry, a unique residual non-wetting phase saturation should exist for a given set of initial conditions. Two laboratory procedures.found to be extremely useful in the study of pore structure and degree of fluid interconnection at various saturations are decribed. Although air-nercury capillary injection curves have been used2 previously to characterize the drainage case, the withdrawal or imbibition case can provide valuable supplementary data. The air-mercury process, however, has several disadvantages; it is difficult to run in a sufficiently accurate manner, mercury does not always act as a strongly non-wetting liquid and in the air-mercury process the sample is rendered unsuitable for future analyses. An alternative process is described in which air is the non-wetting phase and naptha, hentane, octane or toluene is the wetting phase. INTERFACIAL TENSION AND CAPILLARY PRESSURE Interfacial tension between immiscible fluids is due to the difference in attraction of like molecules as compared with their attraction to molecules of the neighbouring fluid. This net attraction results in a tension at the interface. To extend the interface; thus, interfacial tension s can also be thought of as free surface energy. Interfacial tension is normally expressed as dynes/cm, and interfacial energy is measured in ergs/cm2 hence, both have dimensions ml A 2 and are numerically equal.

Jan 1, 1967

By P. Shahinian, H. H. Smith, M. R. Achter

Crack growth rates are measured at elevated temperature in a resonant fatigue machine from vibration frequency decreases calibrated in terms of crack depth. Crack growth rates in Type 316 stainless steel at 500º and 800°C show a sharp increase with oxygen pressure in an intermediate pressure range and little or no change at high and low pressures. At 500°c, I torr of oxygen reduces the fatigue life by almost a factor of 100 in comparison to that in vacuum and raises the growth rate of shallow cracks by the same At At 800°C the effects are smaller. Changes in slope in the crack growth rate curves are discussed in terms of a model in which rates of surface production and of surface coverage by gas are compared. The use of a calculation method in which the surface exposure time is equal to X/v, where x is the interatomic spacing and v is the growth rate, makes it possible to obtain order of magnitude agreement at 500°C between the observed pressure and the predicted pressure at these slope changes. At 800°C oxidation becomes a .factor and the data cannot be treated by simple adsorption theory. THE decrease in the fatigue life of metals as a function of gas pressure usually follows a stepped curve with virtually all of the decrease concentrated in a sharp drop in a transition zone at intermediate pressures and little or no change at low and high ranges. A number of models, differing in the details of the mechanism, have been offered to explain the shape of the curve. Measurements of crack growth in aluminum as a function of gas pressure by Bradshaw and Wheeler' and Hordon2 demonstrated opportunities for quantitative comparison to evaluate the proposed models. Since comparable data were lacking at high temperatures, in the present work rates of crack propagation were measured in Type 316 stainless steel at 500" and 800°C as a function of oxygen pressure. Choice of this material was dictated by two considerations; it is stiff enough at these elevated temperatures to resonate with the regenerative drive on our fatigue machine and it is known to display a large effect of environment. A new method of calculation is described to predict the gas pressure at the critical point. EXPERIMENTAL PROCEDURE Because of the difficulty of measuring crack depths directly at high temperatures, an indirect method was developed based on the decrease in the resonant frequency with the growth of a crack. A reversed bending, constant amplitude fatigue machine, described previously,3 vibrates a specimen at its resonant frequency, automatically records any changes in it and shuts itself off after it has reached a preset value of frequency decrease. The record of frequency change is used to determine the rate of crack growth. Sheet type specimens of Type 316 stainless steel, Fig. 1, incorporated a sharp, shallow notch to localize the formation of a single crack. After machining, they were annealed in a vacuum of l0-6 torr either at 1066" (lot A) or 871°C (lot B) and then electropolished in an acetic-chromic acid solution. Bending strains were measured at 500" and 800°C by an optical technique4 and reported as total strain without correction for the notch. At 500°C, the 0.141 pct strain was 0.085 pct elastic and the remainder plastic. At 800°C the 0.062 pct strain was all elastic. To convert frequency decrease to crack length, calibration curves were obtained by interrupting the vibration at stated intervals of frequency decrease. The crack depth was measured microscopically at a magnification of X400 and reported as the average of the measurement on each edge. Some specimens were sectioned for crack measurement while others were returned to the machine and fatigued further. There was good agreement between the two methods. Before beginning the vibration, the vacuum chamber was first evacuated cold to 1 x 1O-6 torr, then heated to the operating temperature and held there until the pressure was again reduced to 1 x10-6 torr at which time oxygen was introduced to the desired pressure. In this investigation the vibration frequency was nominally 10 cps and a decrease of 0.6 cps was taken as the failure point. The choice of the frequency decrease to represent failure has no appreciable effect on the fatigue life because the crack is growing very fast at this point.

Jan 1, 1970

By N. A. D. Parlee, I. D. Shah

THIS communication reports the results of some work done on the effect of gold, palladium, and platinum on the liquid-gas-solid equilibrium in the Ag-O system,1,2 see Fig. 1. Recently several investigators3, 4, 5 have reported the effects of gold, palladium, platinum, and copper on the solubility of oxygen in liquid silver. This communication represents only a portion of the work done here on the solubility of oxygen in liquid silver and liquid Ag-Au, Ag-Pd, and Ag-Pt alloyss—the greater part having already been reprted. The apparatus, materials, and procedures used were similar to those of earlier work.' l The main precautions observed in obtaining these freezing points at constant temperature and PO2 = 1 atm were as follows: 1) The points were approached very slowly from higher temperatures. 2) In the very near vicinity of the L-G-S equilibrium point precautions were taken to see that the melt was in equilibrium with oxygen at one atm. Equilibrium was considered to have been attained when no more absorption of oxygen was observed in the last 15 min at a fixed temperature. 3) In the case of these alloys, the freezing point of the melt at 1 atm of oxygen and the equilibrium amount of oxygen absorbed by the liquid "infinitesimally" above this point were determined by lowering the temperature in very, very small steps, equilibrating at

Jan 1, 1969

By J. H. Frye, C. P. Sun

A Frimary substitutional solid solution is a solution that has the same crystalline structure as the solvent metal, and in which solute atoms have replaced, solvent atoms at random on the host lattice. This replacement usually results in an increase in hardness as measured by conventional penetration tests. The factors controlling this hardness increase have been investigated in some detail for copper and silver alloys.1-5 It has been shown that at least four factors are involved: (1) concentration of solute, (2) row of the periodic table from which the solute is taken, (3) increase in lattice parameter of the solvent produced by the solute, and (4) work-hardening produced by penetration of the hardness indenter.2,4 The last factor is of the utmost importance. An investigation of the available data2,4 leads to the conclusion that the solutes that produce large hardness increases in copper or silver do so principally because they increase the rate of work-hardening. Furthermore, it is doubtful whether any solute produces appreciable hardening in the absence of plastic deformation and hence work-hardening. Thus it is clear that an understanding of the effect of solutes on rate of work-hardening is essential to an understanding of the hardness of solid solutions. This effect of solutes is also important in forming operations such as rolling or deep drawing. The presence of elements that confer rapid rates of work-hardening will increase power consumption and may well decrease the amount of deformation possible between anneals. This paper is the report of an investigation of the factors that control rates of work-hardening in copper and silver solid solutions. The silver and copper alloys considered are those in which all solutes are from the B subgroups or second short period of the periodic table. Experience with hardness, with structure of alloys, and with electrical conductivity has proved that results of a fundamental nature are most likely to be obtained if alloys are made up on the basis of the positions of the constituent elements in the periodic table. In previous work, Meyer analysis data on high-purity copper and silver solid solutions were obtained through careful measurements with fully calibrated equipment and these data were corrected to correspond to a standard grain size. From these corrected Meyer analysis data rates of work-hardening have now been calculated. Calculation of Rates as Work- HARDENING The Meyer analyses, on which this study of rates of work-hardening is based, consisted in determining impression

Jan 1, 1944

By J. H. Frye, C. P. Sun

A Frimary substitutional solid solution is a solution that has the same crystalline structure as the solvent metal, and in which solute atoms have replaced, solvent atoms at random on the host lattice. This replacement usually results in an increase in hardness as measured by conventional penetration tests. The factors controlling this hardness increase have been investigated in some detail for copper and silver alloys.1-5 It has been shown that at least four factors are involved: (1) concentration of solute, (2) row of the periodic table from which the solute is taken, (3) increase in lattice parameter of the solvent produced by the solute, and (4) work-hardening produced by penetration of the hardness indenter.2,4 The last factor is of the utmost importance. An investigation of the available data2,4 leads to the conclusion that the solutes that produce large hardness increases in copper or silver do so principally because they increase the rate of work-hardening. Furthermore, it is doubtful whether any solute produces appreciable hardening in the absence of plastic deformation and hence work-hardening. Thus it is clear that an understanding of the effect of solutes on rate of work-hardening is essential to an understanding of the hardness of solid solutions. This effect of solutes is also important in forming operations such as rolling or deep drawing. The presence of elements that confer rapid rates of work-hardening will increase power consumption and may well decrease the amount of deformation possible between anneals. This paper is the report of an investigation of the factors that control rates of work-hardening in copper and silver solid solutions. The silver and copper alloys considered are those in which all solutes are from the B subgroups or second short period of the periodic table. Experience with hardness, with structure of alloys, and with electrical conductivity has proved that results of a fundamental nature are most likely to be obtained if alloys are made up on the basis of the positions of the constituent elements in the periodic table. In previous work, Meyer analysis data on high-purity copper and silver solid solutions were obtained through careful measurements with fully calibrated equipment and these data were corrected to correspond to a standard grain size. From these corrected Meyer analysis data rates of work-hardening have now been calculated. Calculation of Rates as Work- HARDENING The Meyer analyses, on which this study of rates of work-hardening is based, consisted in determining impression

Jan 1, 1944

By H. O. Pickard

The Hoover and Mason Phosphate Co. made extensive tests with a rig manufactured by the Paris Manufacturing CO. as shown in Fig I. It is powered by a 20-hp Wisconsin air-cooled gasoline engine, through a single reduction gear and flexible coupling. The machine operates a 4-in. auger with a detachable cutting head, as shown in Fig I. The auger length is 3 ft 4 in. and the cutting head averages 7 in. The unit has a drilling capacity of 100 ft and can drill an average prospect hole in less than 15 min. The weight of the motor is used for the thrust feed for driving the auger and head down, aided by the spiral shape of the auger. The rate of downward motion—i.e., the feed—is regulated by a handwheel. The string of tools is withdrawn from the hole by a gear train controlled by a hand-operated clutch. In fairly dry strata, not of the consistency of mud, the action of the auger

Jan 1, 1948

By H. O. Pickard

The Hoover and Mason Phosphate Co. made extensive tests with a rig manufactured by the Paris Manufacturing CO. as shown in Fig I. It is powered by a 20-hp Wisconsin air-cooled gasoline engine, through a single reduction gear and flexible coupling. The machine operates a 4-in. auger with a detachable cutting head, as shown in Fig I. The auger length is 3 ft 4 in. and the cutting head averages 7 in. The unit has a drilling capacity of 100 ft and can drill an average prospect hole in less than 15 min. The weight of the motor is used for the thrust feed for driving the auger and head down, aided by the spiral shape of the auger. The rate of downward motion—i.e., the feed—is regulated by a handwheel. The string of tools is withdrawn from the hole by a gear train controlled by a hand-operated clutch. In fairly dry strata, not of the consistency of mud, the action of the auger

Jan 1, 1948

By M. G. Arthur

This paper is a theoretical analysis of fingering of water and coning of water and gas in homogeneous sand. Investigation of this idealized case illustrates the relative magnitude of the factors involved in actual conditions. The body of the report presents equations, example calculations, and charts that facilitate solution of such problems. Derivation of the equations introduced in this paper and a discussion of previously published equations are included in the appendix. Introduction Production of water from oil wells as a result of the pressure gradients established by flow of fluids through oil-~roducing sands is a common occurrence, which influences the cost of oil production, the degree of depletion and the efficiency of expulsion of oil from naturally occurring reservoirs. Control of water production and encroachment are important both in primary and secondary phases of of exploitation in order to produce oil and gas at lowest cost and in order to achieve the greatest ultimate recovery of the oil in the reservoir. Although many actual oil reservoirs present a multitude of variables that influence fingering and coning of water and gas, an inspection of the relationship and magnitude of the forces involved in the case of a homogeneous sand may indicate satisfactory methods of controlling water production. Application of equations relating the variables may indicate the geometric type of drainage that exists in a particular reservoir or in the vicinity of a particular well. A homogeneous sand body is assumed within the portion of the reservoir influenced by the well. Two geometric types of drainage are considered theoretically. The first is water fingering into an oil sand that is relatively thin compared with the lateral extent of the sand. This sand may represent the entire oil-producing reservoir or it may represent one interval in an oil reservoir, which is separated from other producing intervals by competent lithologic barriers to flow of fluids. For the condition of complete penetration of a well in such a sand body, it may be assumed that no flow occurs across bedding planes. A mathematical relation is developed between the limit of approach of a water finger to the well without being drawn into the well and the corresponding operating pressure drawdown. The second condition considered is that of water or gas entry into an oil well as the result of coning through bedding planes. The theory and graphical solution developed by Muskat' for the limit of approach of a water or gas cone to a well, without its entry into the well, related to the corresponding maximum pressure drawdown, is reviewed and amplified, Charts are presented, which facilitate graphical solution of the problem. A method is presented for the extension of this type of graphical solution to the case where gas and water coning occurs simultaneously~

Jan 1, 1944

By M. G. Arthur

This paper is a theoretical analysis of fingering of water and coning of water and gas in homogeneous sand. Investigation of this idealized case illustrates the relative magnitude of the factors involved in actual conditions. The body of the report presents equations, example calculations, and charts that facilitate solution of such problems. Derivation of the equations introduced in this paper and a discussion of previously published equations are included in the appendix. Introduction Production of water from oil wells as a result of the pressure gradients established by flow of fluids through oil-~roducing sands is a common occurrence, which influences the cost of oil production, the degree of depletion and the efficiency of expulsion of oil from naturally occurring reservoirs. Control of water production and encroachment are important both in primary and secondary phases of of exploitation in order to produce oil and gas at lowest cost and in order to achieve the greatest ultimate recovery of the oil in the reservoir. Although many actual oil reservoirs present a multitude of variables that influence fingering and coning of water and gas, an inspection of the relationship and magnitude of the forces involved in the case of a homogeneous sand may indicate satisfactory methods of controlling water production. Application of equations relating the variables may indicate the geometric type of drainage that exists in a particular reservoir or in the vicinity of a particular well. A homogeneous sand body is assumed within the portion of the reservoir influenced by the well. Two geometric types of drainage are considered theoretically. The first is water fingering into an oil sand that is relatively thin compared with the lateral extent of the sand. This sand may represent the entire oil-producing reservoir or it may represent one interval in an oil reservoir, which is separated from other producing intervals by competent lithologic barriers to flow of fluids. For the condition of complete penetration of a well in such a sand body, it may be assumed that no flow occurs across bedding planes. A mathematical relation is developed between the limit of approach of a water finger to the well without being drawn into the well and the corresponding operating pressure drawdown. The second condition considered is that of water or gas entry into an oil well as the result of coning through bedding planes. The theory and graphical solution developed by Muskat' for the limit of approach of a water or gas cone to a well, without its entry into the well, related to the corresponding maximum pressure drawdown, is reviewed and amplified, Charts are presented, which facilitate graphical solution of the problem. A method is presented for the extension of this type of graphical solution to the case where gas and water coning occurs simultaneously~

Jan 1, 1944

By C. H. Mathewson

CHARACTER OF THE WORK IN HAND IN planning the present experiments, we have made a particular effort to secure that adjustment of working conditions which would render the forthcoming tests most serviceable by way of indicating the comparative properties of the three different commercial grades of copper used. More specifically, we have endeavored to obtain certain definite information with respect to the relative behavior under test of ordinary electrolytic copper and furnace-refined lake copper containing (a) a moderate percentage of arsenic and (b) a rather large percentage of arsenic, in addition to the usual content of silver and other impurities. These comparisons were made systematic and comprehensive by testing throughout a series of (eight) reductions running from 0 to 70 per cent. in the case of cold-rolled metal, and throughout a series of (15) temperatures running from 100° C. to 1,000° C. in the case of annealed metal. In other words, a survey of properties similar to that made by Grard,1 in the case of electrolytic copper, was here repeated (with modifications) and extended to two other commercial varieties of copper.

Jan 7, 1916

By C. G. Rhodes, D. Kramer

The kinetics of precipitation of transient a phase during the transformation in U-16 wt pct Mo between 400° and 550°C were studied using quantitative metallography and electrica1 resistiuity measurements. The volume percent of a phase goes through a maximum in time, corresponding to a critical degree of progress of y' formation. prior to its re-solution after prolonged annealing. The fastest rate of a precipitation oc-cuvs at 500°C with a concomittant lowest peak of 9.5 vol pct a. At 450°C, 14 vol pct a, greatest fov any temperature, was observed after 24 hr witlz an associated slowest rate of formation. a precipitation at 400°C ceases after approximately 160 hr and the amount of a present remains unchanged after long times at temperature; no y' was observed metallographically at this temperature. IN the U-Mo system at 16 wt pct Mo, an ordering reaction takes place below 600°C, see Fig. 1, whereupon the random bcc solid solution, y, transforms to the ordered bct phase, y'."2 The new unit cell is constructed of three old unit cells somewhat distorted. While attempting to study the kinetics of this transformation it was observed that an unexpected phase was precipitating out early during the transformation anneal reaching appreciable amounts before disappearing after long times. The y' appeared in the presence of this new phase and after long times constituted the whole sample. Owing to the high optical activity of this unexpected phase under polarized light, it was suspected to be the a phase. Subsequent X-ray powder pictures confirmed this belief. The kinetics of a phase formation and disappearance is the subject of this paper. EXPERIMENTAL PROCEDURE A) Alloy Preparation. Alloys for this study were prepared by vacuum induction melting normal reactor grade uranium and 99.5 wt pct Mo pellets in thoria crucibles. Two ingots were prepared, and sections of the top and bottom of each ingot were chemically analyzed for uranium and molybdenum content. The results of the analyses appear in Table I. B) Metallography. Samples of 16M were wrapped in tantalum foil, sealed in evacuated (5 X 10"6 mm of Hg) quartz capisules, and annealed at 1110"C prior to being transferred directly to the transformation temperature. They were examined metallographically after increasing times to determine the progress of the transformation at 400°, 450°, 500°, and 550°C. The samples were prepared for metallographic examination by mechanical polishing with diamond paste and electrolytic polishing with a solution of glacial acetic acid and chromic acid. Since the y' phase is tetragonal, its presence can be detected by viewing the sample in polarized light. To increase the contrast between y' plates, the samples were electro-etched in a 10 pct oxalic acid solution. To reveal a phase in bright field (it can be seen in polarized light in the "as-polished" state), the samples were electro-etched in a solution of citric acid and nitric acid. To determine the vol pct a phase, a variation of the one dimensional systematic point count method as described by Hilliard and cahn3 was used. The

Jan 1, 1962

By T. Szaplonczay, D. E. Light

The auto-oxidation of sulfur dioxide to form sulfuric acid in commercially produced barren and recycle liquors, containing 1.66 and 4.56 gpl Fe respectively, from Elliot Lake was studied. A gas mixture, containing 3.5% SO2 and air was introduced into these liquors through a frit at a rate of 6.0g SO2 per hour per liter of solution. The barren and recycle were heated to 60°C. At the end of the first 24 hours of the process the concentrations of acid produced were 158 and 220 gpl H2SO4 for the barren and recycle respectively. Corresponding conversion efficiencies were 70 and 83%. In the period from 24 to 36 hours the rate of acid production decreased so that the H2SO4 concentrations at the end of 36 hours were 180 gpl for the barren and 260 gpl for the recycle; average conversions for the initial 36 hours were 55 and 68% respectively. Many investigators1'2'3 have considered the oxidation of sulfur dioxide to form sulfuric acid in aqueous solutions containing metallic ions. A summary of the work performed on this subject prior to 1946 has been presented by Keyes4 who described the auto-oxidation process as follows. Keyes also suggested that in this second reaction ferric ion serves as a catalyst for the conversion of sulfur dioxide to sulfuric acid. Neytzell-de Wilde and Taverner5 have reported on the use of auto-oxidation to produce a 4 to 5% sulfuric acid solution for use in a cyclic leach process at South African uranium plants. This paper describes investigations carried out to determine the feasibility of using the auto-oxidation process to produce sulfuric acid solutions of as high concentration as possible using commercially produced uranium plant barren and recycle liquors from the Elliot Lake region of Ontario. These liquors contained 1.66 and 4.56 gpl respectively of iron, chiefly in the ferrous state. This investigation is of particular interest to the uranium producers in Elliot Lake where the ores contain 3 to 4% sulfur, as sulfides. Flotation of these sulfides and roasting of same to produce SO, bearing gases have been successfully demonstrated using conventional methods.6'7 Barren and recycle solutions, as described previously, are also produced in large tonnages by these uranium producers. The experimental method and apparatus used to examine the auto-oxidation process will be described first. Then the tests carried out on laboratory prepared aqueous solutions containing ferric sulfate to determine optimum conditions will be presented. The next section will describe the tests using the commercial barren and recycle liquors. A final section will summarize the conclusions of the work. EXPERIMENTAL APPARATUS AND PROCEDURES Two types of solutions were used in the tests, a laboratory prepared aqueous solution containing definite amounts of ferric sulfate, and commercially produced iron bearing solution obtained from a uranium leaching plant in the Elliot Lake area. Two liters of a solution to be examined were placed in a 3 in. diam by 30 in. long glass cylinder with a cross-sectional area of 7 sq in. A mixture of air, and SO2 supplied from a lecture bottle for convenience, was introduced into the bottom of the vessel through a standard 30 mm glass frit, 700 sq mm in area. The temperature of the apparatus was controlled by a heating tape and variable transformer. Exhaust gases were vented to atmosphere. At the end of the test period the gas flow was shut off and the solution was analysed for H2SO4, Fe ++, and Fe +++, by conventional means. Four variables were examined using the laboratory prepared aqueous solution of ferric sulfate. First, the effect of SO2 concentration, from 1 to 1076, in the feed gas mixture was considered. Second, the temper-

Jan 1, 1964

By L. S. Darken, H. A. Wriedt

An investigation has been made of nitrogen absorption by the lattice defects in a low-carbon steel afte~ Plastic deformation. Specimens in which defects were distributed by various combinations of cold rolling and vacuum heat treatment were equilibrated with controlled ammonia + hydrogen mixtures at 300° to 450°C to study the relation between the solubility and the thermodynamic activity of nitrogen. The results are interpreted in terms of nitrogen being absorbed upon two different types of defect sites, called A sites and B sites. The concentrations of these sites are calculated for specimens with various histories of straining and annealing; and the thermodynamic relations descrihing the equilibrium distribution of nitrogen among the A, B, and ordinary interstitial sites in ferrite are evaluated as follows: THE generalization that the solute atoms in a solid solution interact with imperfections in the solvent lattice is now universally recognized and the subject of an extensive literature. All types of imperfections—point, line, or surface—exhibit these interactions, but the relative importance of each type depends upon its concentration, the strength of its interaction with the particular solute atom, and whether the interaction is attractive or repulsive. The strength and sign of the interaction vary with the vectorial displacement of the solute atom from the imperfection in the crystal. The concentration of lattice defects increases during plastic deformation and the effect of the imperfections upon the solute atoms is usually perceived only after cold work or irradiation. Two experimental methods have previously been used to observe the effects of interaction between nitrogen atoms and lattice imperfections in a iron. Internal friction, which was first used for this purpose by Dijkstra,1 has been applied more often than the electrical-resistivity method of Cottrell and Churchman.2 The method of the present investigation has not been used before.* Uniform specimens of steel with a metastable defect structure are produced by cold rolling and subsequent heat treatment below the recrystallization temperature. Variations in the defect structure are obtained by varying the amount of strain and the heat-treatment conditions. The specimens are then saturated with nitrogen at moderately elevated temperatures in ammonia + hydrogen mixtures having various thermodynamic activities of nitrogen below saturation with Fe4N. From the nitrogen contents of analyzed samples, the metastable equilibria of interactions between the defects and nitrogen can be established and the concentration of sites for nitrogen atoms in the lattice defects calculated. A steel was used in the present experiments instead of purified iron or iron alloys because the amount of nitrogen absorbed at defects is larger in the steel over a much wider range of experimental conditions and could therefore be measured more accurately. The effect of alloy composition is discussed in Part II of this paper; it is sufficient to say here that impurities and phase heterogeneity in ferritic alloys favor the generation and/or retention of larger defect concentrations during plastic deformation and annealing at 300° to 500°C. MATERIALS AND EXPERIMENTAL PROCEDURE The experimental specimens were prepared from stock of a low-carbon steel, which will be called "X steel" here, with the composition: C, 0.12 pct; Mn, 0.43 pct; P, 0.010 pct; S, 0.034 pct; Si, 0.007 pct; As, 0.086 pct; Cu, 0.022 pct; Ni, 0.009 pct; Cr, 0.003 pct. The stock was all from a single ingot made by the basic open-hearth process, which was hot-rolled to strip 0.080 in. thick.. This hot-rolled strip, given the code designation "XH", was the starting material for preparing a series of cold-rolled sheets. The latter are designated "XC27",

Jan 1, 1965

By R. E. Reed, C. J. McHargue

Single crystals of aluminurn were reduced 90 pct in diameter by extrusion at 296" and 77°K. The resultant double fiber texture had a strong (111) component with a weak (001) component. The relative anzounts of these components varied with starting orientation. Decreasing the Lemperatuve of defovtnation increased the amount of (001) texture component in crystals with inilia1 orientations near (111). The starting orientation and temperature of deformation strongly affected the morphology of the (001) component. The effects of orientation and Lemperatuve upon the distribution of the (001 ) texture component in extruded aluminum single crystals were rationalized on the basis of deformation band formation and interaction. MANY papers since the early 1920s have discussed the occurrence of the double fiber texture (111) + (001) in wires and rods of deformed fcc metals. Aside from the reporting of experimental results for the various metals under a variety of fabrication conditions, emphasis has been placed on two related problems. One problem deals with the prediction of ideal end orientations based on the glide systems and flow directions. The other problem seeks the reason why different amounts of each component may be produced by the same fabrication schedule for metals apparently having the same deformation systems. Some of the difficulties in developing a satisfactory explanation have their origin in the experiments themselves. One mistake has often been the assumption of an initially randomly oriented specimen or complete ignorance of effects of starting orientation. Recent studies by Grewen and Wassermann,1 Cullity and co-workers,2' and McHargue4 have shown that the initial orientation may be the most important factor in determining the final orientation. Hence only limited comparisons of data from different studies can be made unless all conditions of the initial material are specified. Another question has been the nature of the (001) component. Hibbards suggested that any (001) present was the result of re crystallization during fabrication. Although Fleischer6 found no (001) texture in aluminum swaged at room temperature, and Dayal 7 found that component to disappear at very high reductions, a double fiber texture has usually been reported for aluminum. Vandermeer and McHargue showed that, while some (001) in aluminum may be the result of recrystallization, much of this component has its origin in the deformation process. Ahlborn and Wassermanng found the (001) component in silver deformed at low temperature not to be the product of recrystallization.

Jan 1, 1968