The structures formed when austenite is quenched to subcritical temperatures and allowed to transform isothermally have been the subject of intensive study since the work of Davcnport and Bain.' Isothermal transformation diagrams summarizing the results of many of these studies have become widely familiar to metallurgists. Of particular interest to metallographers are the dark-etchingl acicular products of transformation formed by isothermal reaction below the temperature of maximum velocity of the austenite to pearlite reaction. These products, the bainite structures, can he formed in a wide variety of steels. However, the constitution of bainite is not well understood and divergent views have been expressed as to its mode of formation. In this investigation a combination of dilatometric, microscopic and X-ray methods has been brought to bear upon the problem in the hope of some elucidation of the bainite reaction as it occurs in hypo-eutectoid steels. Mechanism OF Bainite Formation Davenport and Bainl considered the mechanism of bainite formation to consist of two steps—an allotropic transformation followed by precipitation of carbide. The separation in time of the two processes was considered to be very slight in the upper temperature range and very marked at temperatures just above the martensite range. This concept has been restated by Vilella, Guellich and Bain2 in the form of a definition of the acicular mode of transformation as: The successive, abrupt formation of flat plates of supersaturated ferrite along certain crystallographic planes of the austenite grains; this supersaturated ferrite begins at once to reject carbide palticles, (not lamellae), at a rate depending upon temperature In effect, this is the acicular mode of transformation, even though the temperature be such as to limit the actual life of the quasi-martensite to millionths of a second. The investigation of isothermal decomposition of austenite in certain alloy steels (notably those containing chromium or molybdenum) has revealed that there may be a range of temperatures between the pearlite and bainite reactions in which the austenite decomposes at a relatively low rate.3-6 Further, it is characteristic that in the second region of fast reaction the decomposition of the austenite is incomplete by one reaction but goes to completion by a second reaction. These observations led Wever7 to a description of the bainite reaction as follows: I. The reaction takes place by initial precipi. tation of a martensitic intermediate structure. 2. In the upper temperature range this structure readily decomposes into ferrite and cementite. In the lower range carbon separates in an unknown form. 3. In the upper temperature range the precipitated carbide nucleates the precipitation
The structures formed when austenite is quenched to subcritical temperatures and allowed to transform isothermally have been the subject of intensive study since the work of Davcnport and Bain.' Isothermal transformation diagrams summarizing the results of many of these studies have become widely familiar to metallurgists. Of particular interest to metallographers are the dark-etchingl acicular products of transformation formed by isothermal reaction below the temperature of maximum velocity of the austenite to pearlite reaction. These products, the bainite structures, can he formed in a wide variety of steels. However, the constitution of bainite is not well understood and divergent views have been expressed as to its mode of formation. In this investigation a combination of dilatometric, microscopic and X-ray methods has been brought to bear upon the problem in the hope of some elucidation of the bainite reaction as it occurs in hypo-eutectoid steels. Mechanism OF Bainite Formation Davenport and Bainl considered the mechanism of bainite formation to consist of two steps—an allotropic transformation followed by precipitation of carbide. The separation in time of the two processes was considered to be very slight in the upper temperature range and very marked at temperatures just above the martensite range. This concept has been restated by Vilella, Guellich and Bain2 in the form of a definition of the acicular mode of transformation as: The successive, abrupt formation of flat plates of supersaturated ferrite along certain crystallographic planes of the austenite grains; this supersaturated ferrite begins at once to reject carbide palticles, (not lamellae), at a rate depending upon temperature In effect, this is the acicular mode of transformation, even though the temperature be such as to limit the actual life of the quasi-martensite to millionths of a second. The investigation of isothermal decomposition of austenite in certain alloy steels (notably those containing chromium or molybdenum) has revealed that there may be a range of temperatures between the pearlite and bainite reactions in which the austenite decomposes at a relatively low rate.3-6 Further, it is characteristic that in the second region of fast reaction the decomposition of the austenite is incomplete by one reaction but goes to completion by a second reaction. These observations led Wever7 to a description of the bainite reaction as follows: I. The reaction takes place by initial precipi. tation of a martensitic intermediate structure. 2. In the upper temperature range this structure readily decomposes into ferrite and cementite. In the lower range carbon separates in an unknown form. 3. In the upper temperature range the precipitated carbide nucleates the precipitation
By C. S. Sivaramakrishnan, Manjit Singh, Rajendra Kumar
Regarding liquid nzetals structurally as a suspm-sion of clusters , having derivated solid-state coordination, in truly liquid atoms, the recently developed Kuvlar-Samarin technique of centrifuging- in liquid state enabled the determination of the cluster sizes inAl-Cu mid Pb-Sn systems. It is shown that the colutne fraction of the clusters does not exceed 9 pct and the energy of their formation in Al-Cu is about 5.5 kcal per g-atom and in Pb-Sn eutectic alloys about 25 kcal per y-atoni. STRUCTURAL investigations of liquid state have principally followed the following three courses: i) studies with X-ray, electron, or neutron diffraction; these investigations have shown that there is a certain amount of regularity in the structure of liquid metals which can be defined by a coordination number and that the structure is a derived function of that in the solid state; ii) thermodynamical investigations which are based on the concept of ideal behavior; these describe the liquid state in terms of free-energy values and other thermodynamic functions; although these investigations are of help in the study of the general effects of alloying, they do not provide any structural insight into the precise atomic distribution in liquid state; iii) measurements of surface tension and viscosity; although it is natural to expect that the viscosity is related to the structure in liquid state, these investigations have so far only provided information which can be used by the foundry technologists and has been little utilized in formulating models of the structure of liquid state. As it happens, investigators in the three groups have worked almost independently of each other and there is practically no structural correlation between the results of one group with those of another. The purpose of the present paper is to indicate that the experimentally measured parameters of these three groups of research are closely related to the structure in the liquid state. STRUCTURE OF LIQUID METALS Although atomic distribution in solid and gaseous states is rigorously known, that of the liquid state is only appreciated on the fringes. There is no universal model of atomic distribution in liquid state, but two diverse models are at present hotly contested. The first, largely expounded by ~ildebrand,' regards the liquids as condensed gas since many of their properties and much of their behavior can be adequately described by regarding them as fluids. The second mode12j3 considers that some form of near-solid as- sociation of large number of atoms exists in the liquid state. On the other hand, ~ernal' was able to predict rather precisely the radial distribution functions in liquids on the basis of statistical geometric approach which considered that liquids are "homogeneous, coherent, and essentially irregular assemblage of molecules containing no crystalline regions or holes large enough to admit another molecule". He introduced the concept of pseudonuclei in the otherwise random structure as aggregates of closely packed tetrahedra which gradually merge into irregularity and continually replace each other. To what extent the pseudonuclei can be regarded as regions of near-solid association is indefinite but Bernal suggested that the concept of pseudonuclei can be compromised with the latter model if the near-solid associations are regarded as extremely dense and not necessarily crystalline. The difficulty in projecting the structure of liquid metals arises because they exhibit duplicity of character as some of their properties are closer to those of crystalline solids and others to fluids. There is an increasing tendency to discuss the structure of liquid metals in terms of the second concept according to which the structure of liquid metals may be conceived as consisting of i) clusters of atoms where the aggregation is a close derivative of that in the crystalline state, ii) individual atoms which behave like true liquids in respect to degrees of freedom and iii) excess number of vacancies. It is noteworthy that the introduction of only 5 pct vacancies is sufficient to transform crystalline matter into the liquid state. At any instant of time thermodynamic equilibrium exists between i, ii, and iii, but the relative proportion of the clusters and random atoms is not known. That this is so can be appreciated by the fact that, when liquid metal is rapidly cooled, liquid state vacancies may condense in the form of dislocation loops and vacancies in excess of their equilibrium number in solid state. These dislocation loops have been observed in thin foils of aluminum prepared from rapid cooled aluminum. As temperature increases above melting point the number and volume fraction of clusters decrease but those of vacancies and random atoms increase. Clusters are transient in nature. In pure metals the cluster is an aggregation of the metal itself. In alloys, however, the nature of the cluster largely depends on the interaction between solvent and solute atoms. If the interaction between unlike atoms is greater than between like atoms: the clusters are then aggregates of unlike atoms. Examples of this kind of system are A1-Cu, Mg-Pb, and so forth, i.e., systems which exhibit negative departures from the Raoult's law. In systems where the interaction between unlike atoms is smaller than be-