By W. W. Schmittroth, A. Y. Bethune

The commercial analysis of Special High-Grade zinc usually involves the determination of lead, iron, copper and cadmium as impurities in the base metal. Over the past 20 years, as the result of metallurgical improvements in the art of producing Special High-Grade zinc metal there has taken place a gradual exclusion of almost all extraneous elements, and the few that do remain in the final product have been virtually reduced to the vanishing point. Thousands of tons of zinc are now commercially produced annually and made available to the trade, in which impurities are present only in the order of 0.0010 per cent or less and the sum total of all impurities does not exceed 0.0025 per cent. To such zinc the term "super-purity" might well be applied without undue exaggeration. The techniques used for production control and final analysis of Special High-Grade zinc by means of emission spectra in the laboratories of the electrolytic zinc plant of the Sullivan Mining Co. are based on the premise that self-electrodes are to be preferred over all other forms for the examination of the zinc in question. Furthermore, after a survey of the literature and considerable experimental work,' it was decided that the spectrographic method of internal control, the principle of which was first announced by Gerlach,2 using a modification of the high-voltage alternating-current arc source introduced by Duffendack and Thompson,3 with the calibration of each photographic plate as recommended by Wolfe,4 would yield the most accurate and reproducible results. Self-electrodes were chosen in order to make use of one of the unique advantages inherent in spectrographic analysis; namely, the rapid and almost effortless detection of elements other than those being quantified by the analyst; or conversely, the proof that the zinc is free from such impurities if no spectral line of the suspected element appears. This fact was verified for certain elements, and will be discussed later. Carbon electrodes impregnated or packed with zinc salts chemically prepared from the zinc to be assayed were avoided for a number of reasons. First, the chemical manipulation was another time-consuming step, which increased the chances for contamination. Second, none of the common zinc salts, such as the chloride, nitrate or sulphate, yielded reproducible results under our conditions, nor did the spectral line of the impurity appear as readily in the low concentrations as when using zinc metal. Third, no commercial carbon, except the very expensive, was pure enough to use with this grade of zinc and the continued time, effort and expense incurred in the purification of carbon were not desirable. The use of special High-Grade zinc self-electrodes introduces certain complications with regard to obtaining satisfactory excitation conditions, because it seems necessary to raise the temperature

Jan 1, 1949

By L. S. Richardson, N. J. Grant

Iodide-grade titanium, two oxygen alloys, and two aluminum alloys were studied by means of creep-rupture tests from 1000° to 2000°F. From the test information an evaluation was made of, 1) the relative creep-rupture strengths of the u (hexagonal-close-packed) and 0 (body-centered-cubic) forms of titanium and some of its alloys; 2) the effects of solid-solution strengthening by oxygen and aluminum on the u and 0 structures; and 3) the extent and effect of atmospheric oxygen alloying on rupture life in tests above about 1000°F. THE use of titanium alloys at temperatures above 1000° F has been considered unlikely by most investigators because of low creep strength (based on a requirement for room-temperature ductility, formability, and weldability) and low oxidation resistance. The results of this testing program do not entirely uphold this pessimism in terms of strength and oxidation resistance. The observations described below are based entirely on stress-rupture results, although some creep tests were also carried out on these alloys. Three items of primary importance are covered: 1) Stress-rupture data in the form of the Larson-Miller parameter curves for several titanium alloys at temperatures up to 2000°F; 2) The relative strengths of the hexagonal-close-packed a structure and the body-centered-cubic 0 structure; 3) The effects of solid-solution alloying on the creep-rupture properties of titaniu'm at elevated temperatures. Only two investigatons have reported the creep- rupture properties of titanium at temperatures above 1000° F. Lunsford and rant' tested iodide titanium; their values are also utilized in the paper. EXPERIMENTAL PROCEDURE After a few tests had been made in a conventional creep-rupture test machine, it became clear that some sort of atmospheric protection would be necessary for short-time tests conducted at temperatures above 1600°F, or for times greater than 100 hr at 1200°F or above. Several furnace units and test machines were constructed, the most successful of which is shown in Fig. 1. Certain experimental difficulties peculiar to titanium were encountered; for example, the use of molybdenum holders was dictated because titanium forms low melting-point eutectics with conventional high-temperature alloys containing appreciable amounts of iron, nickel, or cobalt. This same difficulty made the use of chrome l-alumel thermocouples in direct contact with a test specimen impossible, above about 1500" F. The high-temperature high-vacuum furnace shown in Fig. 1 was capable of maintaining a vacuum of better than 10"5 mm of mercury at 2000°F (pressure measured in cold part of system) and 5 X lo-' mm at room temperature. Most of the tests eonducted in vacuum were at temperatures

Jan 1, 1960

By F. R. Archibald, C. M. Nicholson

The present paper may be considered complementary to an earlier contribution on the same subject by F. R. Archibald and C. F. Jackson.1 It is particularly concerned with engineering and technological aspects of the operations at the Harleyville Alumina Plant during its period of operation from January 1945 to July 1946. The plant was built for and operated by Ancor Corporation, at Harleyville, South Carolina, as part of the government sponsored wartime program related to alumina production from domestic raw materials. The main purpose of the program was to secure technical and engineering data, based on actual plant experience, that might serve as a foundation for large scale production of alumina from raw materials other than bauxite. The Harleyville plant was directed specifically to treatment of clays found in very extensive deposits in the Carolinas and Georgia using the lime-sinter process developed by Ancor Corporation. It is considered that the purpose stated above has been served and this paper is to record and discuss some of the more important findings. The main factor in location of the plant at Harleyville was the presence in that locality of a rather remarkable deposit of high calcium limestone. The clay mining operation was centered near Aiken, S. C., and although a rail haul of ninety miles was involved there were, at the time, factors favorable to the Harleyville location offsetting, in part, the cost of transportation of clay, There are, no doubt, locations in the general area where clay and limestone deposits may be found in closer proximity hut they had not been proven up when the project was undertaken. Availability of power from the Santee-Copper development whose high tension line skirted the Property; ready access to rail and highway transportation; the promise, realized in actuality, of ample supply of soft water; and availability of labor supply were other factors of importance. Moreover, the general area has the decided advantage, for this type of operation, of a mild climate. Construction was begun in August 1943, and although stopped for a time priding review of the general situation that fall, it was resumed, albeit with less urgency, and substantially completed by the end of 1944. The total capital cost was approximately $3,460,000 The first alumina was turned out in April 1945 and from then until the plant was closed down in July 1946, the operations followed a succession of periods of production alternating with periods in which minor alterations were made in conformity with experience. Steady improvement was made and at the time Operations were discontinued it was considered that experience and the necessary engineering were in shape for removal of the remaining bottlenecks and a somewhat major revision in one section of the plant. Unfortunately this could not be carried out and it was necessary to discontinue the

Jan 1, 1949

By W. W. Schmittroth, A. Y. Bethune

THE commercial analysis of Special High-Grade zinc usually involves the determination of lead, iron, copper and cadmium as impurities in the base metal. Over the past 20 years, as the result of metallurgical improvements in the art of producing Special High-Grade zinc metal there has taken place a gradual exclusion of almost all extraneous elements, and the few that do remain in the final product have been virtually reduced to the vanishing point. Thousands of tons of zinc .are now commercially produced annually and made available to the trade, in which impurities are present only in the order of 0.0010 per cent or less and the sum total of all impurities does not exceed 0.0025 per cent. To such zinc the term "superpurity" might well be applied without undue exaggeration. The techniques used for production control and final analysis of Special High-Grade zinc by means of emission spectra in the laboratories of the electrolytic zinc plant of the Sullivan Mining Co. are based on the premise that self-electrodes are to be preferred over all other forms for the examination of the zinc in question. Furthermore, after a survey of the literature and considerable experimental work,1 it was decided that the spectrographic method of internal control, the principle of which was first announced by Gerlach,2 using a modification of the high-voltage alternating-current arc source introduced by Duffendack and Thompson,3 with the calibration of each photographic plate as recommended by Wolfe,4 would yield the most accurate and reproducible results. Self-electrodes were chosen in order to make use of one of the unique advantages inherent in spectrographic analysis; namely, the rapid and almost effortless detection of elements other than those being quantified by the analyst; or conversely, the proof that the zinc is free from such impurities if no spectral line of the suspected element appears. This fact was verified for certain elements, and will be discussed later. Carbon electrodes impregnated or packed with zinc salts chemically prepared from the zinc to be assayed were avoided for a number of reasons. First, the chemical manipulation was another time-consuming step, which increased the chances for contamination. Second, none of the common zinc salts, such as the chloride, nitrate or sulphate, yielded reproducible results under our conditions, nor did the spectral line of the impurity appear as readily in the low concentrations as when using zinc metal. Third, no commercial carbon, except the very expensive, was pure enough to use with this grade of zinc and the continued time, effort and expense incurred in the purification of carbon was not desirable. The use of Special High-Grade zinc self-electrodes introduces certain complications with regard to obtaining satisfactory excitation conditions, because it seems necessary to raise the temperature

Jan 1, 1946

By T&apos Kê, ing-sui

INTRODUCTION ACCORDING to the classical theory of elasticity, the elastic portion of the stress-strain curve is represented by a straight line. Such a representation implies that there is a linear relationship between strain and stress and also that strain is a single-valued function of stress and vice versa. Actually, such a one-to-one correspondence between strain and stress does not exist in real metals. A well-known example is the elastic after-effect on unloading. Another familiar example is damping or internal friction, that is, the dissipation of energy attending vibration. In an extensive review of such phenomena, Zener1,2 has proposed the term "anelasticity" to denote that property of a solid in virtue of which strain is not a unique function of stress in the non-plastic region. The phenomena arising from anelasticity are called anelastic effects. The measurements on inelastic effects are, important in many fields of metals technology. Thus, in precise instruments such as watch springs, difficulties often arise from the slight dimensional changes after fabrication. The internal friction or damping capacity of metals is often an important factor in deciding whether they are appropriate for instruments in which there are accompanying vibrations.' However, for metal scientists, the study of anelastic effects furnishes a powerful tool for understanding many properties of metals in terms of their microstructures or atomic interactions. In order to utilize the anelastic measurements to their fullest extent for acquiring such information, the experimental studies of anelasticity must be interpreted by appropriate mathematical analysis. For a great many problems, however, the necessary information often can be obtained by general qualitative arguments. From the definition of anelasticity, any physical changes occurring in a specimen as a result of the applied stress will cause anelastic effects if such physical changes are accompanied by a delayed change of elastic strain. Under these circumstances, we have the condition that strain lags behind the stress. We may mention the stress-induced transportation phenomena as examples. These include the stress-induced thermal diffusion," the stress-induced diffusion of particles,8-12. and the stress-induced viscous slip along the microelements in metals.12-15 The differential equations describing the microscopic mechanism in these phenomena lead to relations in which stress is linear with respect to strain (and/or their derivatives). Thus if we can - demonstrate that the superposition principle is valid under the circumstances in which the anelastic effects are observed, we would expect in. the macroscopic relation a linear relationship between stress and strain and their derivatives. This report is to describe a number of anelastic effects observed in alpha-iron, and an attempt is made to derive valuable information from a critical study of these

Jan 1, 1948

By T&apos Ke, ing-sui

Accoriding to the classical theory of elasticity, the elastic portion of the stress-strain curve is represented by a straight line. such a representation implies that there is a linear relationship between strain and stress and also that strain is a single-valued function of stress and vice versa. Actually, such a one-to-one correspondence between strain and stress does not exist in real metals. A well-known example is the elastic after-effect on unloading. Another familiar example is damping or internal friction, that is, the dissipation of energy attending vibration. In an extensive review of such phenomena, zener1,2 has proposed the term "anelasticity" to denote that property of a solid in virtue of which strain is not a unique function of stress in the non-plastic region. The phenomena arising from anelasticity are called anelastic effects. The measurements on anelastic effects are important in many fields of metals technology. The, in precise instruments such as watch springs, difficulties often arise from the slight dimensional changes after fabrication. The internal friction or damping capacity of metals is often an important factor in deciding whether they are appropriate for instruments in which there are accompanying vibrations.3 However, for metal scientists, the study of anelastic effects furnishes a powerful tool for understanding many properties Of meta1s in terms of their microstructures or atomic interactions. In order to utilize the anelastic measurements to their fullest extent for acquiring such information, the experimental studies Of anelasticity must be interpreted by appropriate mathematical analysis. For a great many problems, however, the necessary information often Can be Obtained by general qualitative arguments. From the definition of anelasticity, any physical changes occurring in a specimen as a result Of the applied stress will cause anelastic effects if such physical changes are accompanied by a delayed change of elastic strain. Under these circumstances, we have the condition that strain lags behind the stress. We may mention the stress-induced transportation phenomena as examples. These include the stress-induced thermal diffusion,4-7 the stress-induced diffusion of particles,8-l2 and the stress-induced viscous slip along the microelements in metals.12-15 The differential equations describing the microscopic mechanism in these phenomena lead to relations in which stress is linear with respect to strain (and/or their derivatives). Thus if we Can demonstrate that the superposition principle is valid under the circumstances in which the anelastic effects are observed, we would expect in the macroscopic relation a linear relationship between stress and strain and their derivatives. This report is to describe a number of anelastic effects observed in alpha-iron, and an attempt is made to derive valuable information from a critical study of these

Jan 1, 1949

By F. R. Archibald, C. M. Nicholson

THE present paper may be considered complementary to an earlier contribution on the same subject by F. R. Archibald and C. F. Jackson.1 It is particularly concerned with engineering and technological aspects of the operations at the Harleyville Alumina Plant during its period of operation from January 1945 to July 1946. The plant was built for and operated by Ancor Corporation, at Harleyville, South Carolina, as part of the government sponsored wartime program related to alumina production from domestic raw materials. The main purpose of the program was to secure technical and engineering data, based on actual plant experience, that might serve as a foundation for large scale production of alumina from raw materials other than bauxite. The Harleyville plant was directed specifically to treatment of clays found in very extensive deposits in the Carolinas and Georgia using the lime-sinter process developed by Ancor Corporation. It is considered that the purpose stated above has been served and this paper is to record and discuss some of the more important findings. The main factor in location of the plant at Harleyville was the presence in that locality of a rather remarkable deposit of high calcium limestone. The clay mining operation was centered near Aiken, S. C., and although a rail haul of ninety miles was involved there were, at the time, factors favorable to the Harleyville location offsetting, in part, the cost of transportation of clay. There are, no doubt, locations in the general area where clay and limestone deposits may be found in closer proximity but they had not been proven up when the project was undertaken. Availability of power from the Santee-Copper development whose high tension line skirted the property; ready access to rail and highway transportation; the promise, realized in actuality, of ample supply of soft water; and availability of labor supply were other factors of importance. Moreover, the general area has the decided advantage, for this type of operation, of a mild climate. Construction was begun in August 1943, and although stopped for a time pending review of the general situation that fall, it was resumed, albeit with less urgency, and substantially completed by the end of 1944. The total capital cost was approximately $3460,000. The first alumina was turned out in April 1945 and from then until the plant was closed down in July 1946, the operations followed a succession of periods of production alternating with periods in which minor alterations were made in conformity with experience. Steady improvement was made and at the time operations were discontinued it was considered that experience and the necessary engineering were in shape for removal of the remaining bottlenecks and a somewhat major revision in one section of the plant. Unfortunately this could not be carried out and it was necessary to discontinue the

Jan 1, 1948

By T&apos Ke, ing-sui

Accoriding to the classical theory of elasticity, the elastic portion of the stress-strain curve is represented by a straight line. such a representation implies that there is a linear relationship between strain and stress and also that strain is a single-valued function of stress and vice versa. Actually, such a one-to-one correspondence between strain and stress does not exist in real metals. A well-known example is the elastic after-effect on unloading. Another familiar example is damping or internal friction, that is, the dissipation of energy attending vibration. In an extensive review of such phenomena, zener1,2 has proposed the term "anelasticity" to denote that property of a solid in virtue of which strain is not a unique function of stress in the non-plastic region. The phenomena arising from anelasticity are called anelastic effects. The measurements on anelastic effects are important in many fields of metals technology. The, in precise instruments such as watch springs, difficulties often arise from the slight dimensional changes after fabrication. The internal friction or damping capacity of metals is often an important factor in deciding whether they are appropriate for instruments in which there are accompanying vibrations.3 However, for metal scientists, the study of anelastic effects furnishes a powerful tool for understanding many properties Of meta1s in terms of their microstructures or atomic interactions. In order to utilize the anelastic measurements to their fullest extent for acquiring such information, the experimental studies Of anelasticity must be interpreted by appropriate mathematical analysis. For a great many problems, however, the necessary information often Can be Obtained by general qualitative arguments. From the definition of anelasticity, any physical changes occurring in a specimen as a result Of the applied stress will cause anelastic effects if such physical changes are accompanied by a delayed change of elastic strain. Under these circumstances, we have the condition that strain lags behind the stress. We may mention the stress-induced transportation phenomena as examples. These include the stress-induced thermal diffusion,4-7 the stress-induced diffusion of particles,8-l2 and the stress-induced viscous slip along the microelements in metals.12-15 The differential equations describing the microscopic mechanism in these phenomena lead to relations in which stress is linear with respect to strain (and/or their derivatives). Thus if we Can demonstrate that the superposition principle is valid under the circumstances in which the anelastic effects are observed, we would expect in the macroscopic relation a linear relationship between stress and strain and their derivatives. This report is to describe a number of anelastic effects observed in alpha-iron, and an attempt is made to derive valuable information from a critical study of these

Jan 1, 1949

By F. Keller, J. D. Edwards

The anodic treatment of aluminum presents problems of scientific as well as of commercial interest.l-3 Of particular interest is the fact that, during the anodic oxidation process, the oxide continues to form at the metal-oxide interface under any oxide previously formed. This has led to speculation as to the mechanism involved in the formation of the relatively thick oxide coatings that are used commercially for decorative or protective purposes. Furthermore, the ability of certain types of oxide coatings to adsorb dyes and other substances has stimulated research to determine the actual structure of these adsorptive coatings. It has been found that anodic oxide coatings on aluminum are composed essentially of aluminum oxide. They are formed by the action of oxygen ions penetrating to the metal surface during the electrolytic oxidation treatment. These coatings can be formed in a number of different electrolytes, as for example, those which contain sulphuric acid, chromic acid, oxalic acid, or boric acid. These are the commonest and most useful electrolytes employed commercially. Except for certain specific conditions of formation, the coatings in general have been found to be amorphous alumina, as far as can be determined by X-ray or electron-diffraction methods. Anodic oxidation processes can be arranged in three rather general classes if they are grouped in relation to the solvent action of the electrolyte on the coating.4 In the first class, the electrolyte has little or no solvent action on the coating that is formed. In general, coatings produced under such circumstances are nonporous and non-adsorptive. In the second class, the electrolyte exerts an appreciable solvent action on the coating. These coatings are porous and adsorptive. Finally, for the third class, the electrolyte tends to dissolve the coating about as rapidly as it is formed. This action produces electrolytic brightening or anodic polishing of the aluminum surface and at most leaves only a very thin film of oxide. The nonporous and nonadsorptive type of oxide film is represented by the coatings that are formed when solutions of boric acid are employed as the electrolyte. It is especially significant that these impervious films are formed in electrolytes that exert little or no solvent action on the coating. Where a boric acid electrolyte is used, the coating tends to form rapidly, with the result that the flow of current is soon reduced to substantially zero. This indicates that the growth of the coating has stopped. As a rule, the thickness of the coating is roughly proportional to the voltage employed for formation and the coatings of this type are exceedingly thin. In an electrolyte of this type, the coating has a high resistance when the aluminum is made anode; consequently, any current that may flow (leakage current) is very

Jan 1, 1944

By F. Keller, J. D. Edwards

The anodic treatment of aluminum presents problems of scientific as well as of commercial interest.l-3 Of particular interest is the fact that, during the anodic oxidation process, the oxide continues to form at the metal-oxide interface under any oxide previously formed. This has led to speculation as to the mechanism involved in the formation of the relatively thick oxide coatings that are used commercially for decorative or protective purposes. Furthermore, the ability of certain types of oxide coatings to adsorb dyes and other substances has stimulated research to determine the actual structure of these adsorptive coatings. It has been found that anodic oxide coatings on aluminum are composed essentially of aluminum oxide. They are formed by the action of oxygen ions penetrating to the metal surface during the electrolytic oxidation treatment. These coatings can be formed in a number of different electrolytes, as for example, those which contain sulphuric acid, chromic acid, oxalic acid, or boric acid. These are the commonest and most useful electrolytes employed commercially. Except for certain specific conditions of formation, the coatings in general have been found to be amorphous alumina, as far as can be determined by X-ray or electron-diffraction methods. Anodic oxidation processes can be arranged in three rather general classes if they are grouped in relation to the solvent action of the electrolyte on the coating.4 In the first class, the electrolyte has little or no solvent action on the coating that is formed. In general, coatings produced under such circumstances are nonporous and non-adsorptive. In the second class, the electrolyte exerts an appreciable solvent action on the coating. These coatings are porous and adsorptive. Finally, for the third class, the electrolyte tends to dissolve the coating about as rapidly as it is formed. This action produces electrolytic brightening or anodic polishing of the aluminum surface and at most leaves only a very thin film of oxide. The nonporous and nonadsorptive type of oxide film is represented by the coatings that are formed when solutions of boric acid are employed as the electrolyte. It is especially significant that these impervious films are formed in electrolytes that exert little or no solvent action on the coating. Where a boric acid electrolyte is used, the coating tends to form rapidly, with the result that the flow of current is soon reduced to substantially zero. This indicates that the growth of the coating has stopped. As a rule, the thickness of the coating is roughly proportional to the voltage employed for formation and the coatings of this type are exceedingly thin. In an electrolyte of this type, the coating has a high resistance when the aluminum is made anode; consequently, any current that may flow (leakage current) is very

Jan 1, 1944

By W. G. Jeffery, James F. McDivitt

THE FRAMEWORK Consider where you, the reader, would place the emphasis m your answer to the following questions on mineral supply. Do you think of the mineral resources of developing countries in terms of the contribution which they can make to world mineral supply or in terms of the contribution they can make to development of the country? Do you look upon developing countries as a source of minerals for world industry or as a potential enormous market for minerals? If you are from a developed country it would be surprising I£ you did not emphasize the first alternative in each case, but it is also possible that simply raising the questions will call for some mental adjustments, because usually we do not think in these terms. If you are among the two-thirds of the world's population which comes from developing countries, you might well emphasize the second alternative. And to a growing extent during the reaming decades of the 20th century this is where emphasis must be placed. Increasing amounts of the world's mineral production come from countries which are in the early stages of development. Mineral consumers of the world look to these regions for continuing supplies of material to help meet their ever-growing needs; the producing countries look to mineral exports as one means of stimulating and financing their economic development-this seems a happy and fortuitous relationship. But due to the complexities of world mineral supply, it is a relationship which is fraught with potential confusion and misunderstanding. That this is so is not surprising when one considers that many of the producing countries are new countries which are urgently trying to find the path along which they can move towards development; that the direction of the path is by no means clear because various theories of economic development, as a planned and deliberate process, are relatively recent in origin and none are well understood; and that the very concept of the less developed countries (LDC's) is a relatively new one. To further complicate the situation there has never been a clear under- standing of the full role which minerals play in economic development, either in the case of those countries which are already classed as developed, or in the case of countries which are in the process of development. Before embarking on an investigation of some aspects of the relationship between minerals and developing countries, it seems wise to establish broad terms of reference, which may not be totally valid but which will at least give an initial direction for a journey with no clearly definable goal. First it can be noted that the world has been divided somewhat arbitrarily into a group of countries that are termed developed or advanced and a group of countries which

Jan 1, 1976

By F. Keller, J. D. Edwards

THE anodic treatment of aluminum presents problems of scientific as well as of commercial interest.1-3 Of particular interest is the fact that, during the anodic oxidation process, the oxide continues to form at the metal-oxide interface under any oxide previously formed. This has led to speculation as to the mechanism involved in the formation of the relatively thick oxide coatings that are used commercially for decorative or protective purposes. Furthermore, the ability of certain types of oxide coatings to adsorb dyes and other substances has stimulated research to determine the actual structure of these adsorptive coatings. It has been found that anodic oxide coatings on aluminum are composed essentially of aluminum oxide. They are formed by the action of oxygen ions penetrating to the metal surface during the electrolytic oxidation treatment. These coatings can be formed in a number of different electrolytes, as for example, those which contain sulphuric acid, chromic acid, oxalic acid, or boric acid. These are the commonest and most useful electrolytes employed commercially. Except for certain specific conditions of formation, the coatings in general have been found to be amorphous alumina, as far as can be determined by X-ray or electron-diffraction methods. Anodic oxidation processes can be arranged in three rather general classes if they are grouped in relation to the solvent action of the electrolyte on the coating.4 In the first class, the electrolyte has little or no solvent action on the coating that is formed. In general, coatings produced under such circumstances are nonporous and non- adsorptive. In the second class, the electrolyte exerts an appreciable solvent action on the coating. These coatings are porous and adsorptive. Finally, for the third class, the electrolyte tends to dissolve the coating about as rapidly as it is formed. This action produces electrolytic brightening or anodic polishing of the aluminum surface and at most leaves only a very thin film of oxide. The nonporous and nonadsorptive type of oxide film is represented by the coatings that are formed when solutions of boric acid are employed as the electrolyte. It is especially significant that these impervious films are formed in electrolytes that exert little or no solvent action on the coating. Where a boric acid electrolyte is used, the coating tends to form rapidly, with the result that the flow of current is soon reduced to substantially zero. This indicates that the growth of the coating has stopped. As a rule, the thickness of the coating is roughly proportional to the voltage employed for formation and the coatings of this type are exceedingly thin. In an electrolyte of this type, the coating has a high resistance when the aluminum is made anode; consequently, any current that may flow (leakage current) is very

Jan 1, 1944

By Charles S. Barrett

This paper is a progress report covering metallographic applications of the electron microscope that have been made during the past year at Carnegie Institute of Technology. An account is presented of the techniques that have been most satisfactory, the difficulties encountered, the resolution obtained, and the peculiarities that have been noted in the microstruc-tures. About 1200 exposures have been made during the year on the instrument, which is an RCA type B2 transmission microscope,' and a number of these have been selected to illustrate the results obtained. prints are also included showing the common types of falsities—to borrow a term from the biological field, the "artifacts." ln brief, the paper is a record of our attempt to determine the value of the electron microscope in the study of the structure of metals and alloys. In addition to comments on techniques and the quality of photomicrographs obtainable with them, the paper discusses the nature of the etch attack on a few metals, and the possible relation between the fine structure revealed by etching and the mosaic block structure of the grains, since numerous papers and reviews are available on the subject of imperfection in crystals, the comments here may be very brief; in fact, are restricted almost entirely to points having to do with recent theories relating the strength of metals to imperfections and to spacings of slip lines. Specimen Preparation and Photographs Mechanical polishing by hand was used throughout this work. Precautions that must be taken in microscopy at high magnification, which have been well explained by Vilella in his book on Metallographic Technique for Steel, are likewise important with the electron microscope. This applies particularly to the need for these polishing and etching (each successive polish becoming less severe and each etch lighter), since the fina1 etch should in general be no heavier than is used for oil-immersion optical microscopy and in many instances should be much lighter (compare Figs. 6a and 7a, 6d and 7b). An extremely light etch, of course, is incapable of cutting through a flowed layer of appreciable thickness. Unquestionably it would be very advantageous in each instance to compare the structures obtained by electrolytic polishing with those obtained by mechanical polishing, but difficulties with the electrolytic method have prevented this in the following collection of prints. The choice of etchant is important, of course; for example, picral proved superior to nital for tempered martensite. With the exception of Figs. Ib and 16, the replicas used were of silica, deposited upon polystyrene and floated from the polystyrene in ethyl bromide according to the method of Heidenreich and Peck.2 The samples were mounted in Bakelite, polished and etched, then the polished Bakelite

Jan 1, 1944

By Charles S. Barrett

This paper is a progress report covering metallographic applications of the electron microscope that have been made during the past year at Carnegie Institute of Technology. An account is presented of the techniques that have been most satisfactory, the difficulties encountered, the resolution obtained, and the peculiarities that have been noted in the microstruc-tures. About 1200 exposures have been made during the year on the instrument, which is an RCA type B2 transmission microscope,' and a number of these have been selected to illustrate the results obtained. prints are also included showing the common types of falsities—to borrow a term from the biological field, the "artifacts." ln brief, the paper is a record of our attempt to determine the value of the electron microscope in the study of the structure of metals and alloys. In addition to comments on techniques and the quality of photomicrographs obtainable with them, the paper discusses the nature of the etch attack on a few metals, and the possible relation between the fine structure revealed by etching and the mosaic block structure of the grains, since numerous papers and reviews are available on the subject of imperfection in crystals, the comments here may be very brief; in fact, are restricted almost entirely to points having to do with recent theories relating the strength of metals to imperfections and to spacings of slip lines. Specimen Preparation and Photographs Mechanical polishing by hand was used throughout this work. Precautions that must be taken in microscopy at high magnification, which have been well explained by Vilella in his book on Metallographic Technique for Steel, are likewise important with the electron microscope. This applies particularly to the need for these polishing and etching (each successive polish becoming less severe and each etch lighter), since the fina1 etch should in general be no heavier than is used for oil-immersion optical microscopy and in many instances should be much lighter (compare Figs. 6a and 7a, 6d and 7b). An extremely light etch, of course, is incapable of cutting through a flowed layer of appreciable thickness. Unquestionably it would be very advantageous in each instance to compare the structures obtained by electrolytic polishing with those obtained by mechanical polishing, but difficulties with the electrolytic method have prevented this in the following collection of prints. The choice of etchant is important, of course; for example, picral proved superior to nital for tempered martensite. With the exception of Figs. Ib and 16, the replicas used were of silica, deposited upon polystyrene and floated from the polystyrene in ethyl bromide according to the method of Heidenreich and Peck.2 The samples were mounted in Bakelite, polished and etched, then the polished Bakelite

Jan 1, 1944

By A. W. Schlechten, Ernest J. Breton Jr.

Experiments on the separation of copper and zinc ions by selective action of ion exchange resins showed the carboxylic type to be more effective than the sulphonic resins. The latter demonstrated a greater capacity over a wider pH range. Data show the effectiveness of resins as a means of concentration. IN recent years the restrictions of stream pollution laws and the high price of metals have created an interest in ion exchange as a means for metal recovery. Some applications have proved successful. In Germany during World War 11, 17 tons of copper per day were recovered from rayon mill wastes by means of ion exchange resins;' and for some time in this country a large ion exchange unit has been in operation for the recovery of copper from rayon waste water. The possibilities of applying ion exchange to the recovery of metals occurring in plating rinse water is particularly promising. In most of these applications only the metal being recovered occurs in the waste. The ion exchange resins act merely as a means of concentrating the metals to a point where they can be recirculated. It would be highly desirable to use ion exchange as a means of not only concentrating but also of separating metals. With the exception of the impressive separations accomplished in connection with the atomic energy program, very little has been done on metal separations.' Therefore, an investigation was undertaken at the Missouri School of Mines and Metallurgy to determine if either of the two main types of ion exchange resins could be used to separate metal ions in solution. The selective removal of copper ions from a mixture of copper and zinc on carboxylic and sulphonic-type resins was investigated as a function of flow rate, pH, copper-zinc ratio, and concentration. It was shown that zinc can be separated from copper and that very large ratios of concentration can be obtained using ion exchange resins. Since ion exchange is relatively new to the field of metallurgy, a brief review of the subject will be included. Theory of Ion Exchange A comprehensive theory for ion exchange has not been developed as yet, but the mechanisms are analogous to metathetical reactions: R Na + Cu++ *=? K(SO3)2 Cu + 2Na+ R is the designation for the ion exchange resin. If a copper solution is passed over a resin bed in the sodium form, two ions of sodium will be released for every ion of copper removed. For the most part this reaction follows the laws of mass action and of electrical neutrality. Consequently, if an excess of sodium ions is passed over a bed containing copper, the reactions will be reversed, and the resin will be regenerated to its original form. A few empirical rules governing the exchange reaction have been set forth: 1—In general ions with a high valence will replace ions with a lower valence. 2—Ions having higher activity coefficients have a higher replacement potential. 3—In a series of mono-valent ions, those with the smallest radii of hydra-tion will tend to replace those having larger radii of hydration. 4—Where ions are similar in most respects, those with the higher atomic weight sometimes will take precedence. This last rule is not as definite as some of the others. These rules apply to rather dilute solutions at moderate temperatures and assume all ions to be present in about equal concentrations. Higher concentrations and temperatures may in some cases reverse the normal exchange reactions. Ion exchange materials are unique in that their efficiency increases as the concentration of the solution decreases. For many exchangers, most efficient operation is obtained at concentrations in the order of one thousandths of a percent. Most applications, though, are made in solutions containing considerably higher concentrations than this. Coste9 as shown that ion exchange resins will remove aluminum and iron effectively' from solutions of up to 10 pct chromic acid. Ion Exchange Resins Ion exchange resins are insoluble, porous, resinous structures to which active groups have been attached. Active groups such as (—SO,,)- and (COO)- pick up cations; hence structures saturated with groups such as these are called cation exchangers. Structures saturated with groups such as (—NH,)' which pick up anions, are referred to as anion exchangers. The resinous structure of necessity is resistant to strong acids, bases, oxidizing, and reducing agents, and most of the common organic solvents. An idea of the stability can be gaged from the fact that resins last for many years under constant use without detectable chemical or physical breakdown. The ion exchange reaction is not confined to the surface of these synthetic resins. Its porous structure permits active groups in the center of a particle as well as those on the surface to remove ions. A high capacity resin such as Amberlite IR-120 will remove up to 3.3 lb Cu per cu ft of resin. In this investigation several approaches to the problem of separating copper from zinc by ion exchange were considered. First, if a reagent could be found which would complex one of these metals and not the other, then by passing this reagent through a bed of exchanger containing copper and zinc, the

Jan 1, 1952

By J. A. Jaekel, W. C. Aitkenhead

Uranium deposits in the Spokane Indian Reservation, as well as those around Mt. Spokane, are essentially low grade, much of the ore containing less than 0.2 pct U3O8. The Mining Experiment Station of the Division of Industrial Research, State College of Washington, has been engaged in intensive research on the amenability of these low grade ores to froth flotation. The results: successful flotation of autinite, chief mineral constituent. At the outset of this work the goal was a concentrate of 1 pct U3O8 with a 90 pct recovery from ores containing less than 0.2 pct U3O8. Most of the work has been done on argillite ore from the Midnight mine on the Spokane Indian Reservation. The goal has not been attained using this ore, but samples of the granite ore from Mt. Spokane yielded successful results. For example, a concentrate containing 11.2 pcl U3O8 was produced from a Mt. Spokane high grade ore containing 1.27 pct U3O8 with a recovery of 97.8 pct. Another Mt. Spokane ore yielded a concentrate of 5.0 pct U3O8 from an ore containing 0.13 pct U3O8. with a recovery of 85 pct. This same ore gave a recovery of 93.5 pct when the grade of concentrate was reduced to 2.0 pct. It has been concluded that a successful method for floating autunite has been developed and that the mediocre results from the Midnight argillite ore are probably caused by the presence of some other uranium mineral or minerals less amenable to these reagents. The experimenters tested a third type of Washington ore, found on the Northwest Uranium Mines Inc. property on the Spokane Indian Reservation. This is a conglomerate of pebbles and small boulders of partially decomposed granite and is shot through with autunite. Its characteristics lie between those of the Midnight ore and the granite ore from the Spokane district. It responds better than the ore from Midnight but not as well as that from Mt. Spokane. As the fatty acids are the only type of collectors showing promise, investigation has been concerned with these acids and the optimum conditions for their use. The first method for treating the argillite ore from the Spokane Indian Reservation made use of Cyanamid's R-708 as a collector, a tall oil product described as a substitute for oleic acid. Although the investigators proved that R-708 is a collector for autunite when mixtures of autunite and silica sand are used, results on the ore were mediocre. Tests of other fatty acids revealed that the solid fatty acids of the saturated series are collectors for autunite and that their collecting power increases with the length of the carbon chain. The even carbon members of the whole series were tested from the 10 carbon acid (capric) to the 22 carbon acid (be-henic). The least expensive collector, stearic acid (18 carbon), proved to be a good one, so this was used in most of the tests. In first attempts with stearic acid, the collector was dissolved in various hydrocarbons and the solutions were added to the flotation cell. Cyclohexane, gasoline, fuel oil, kerosene, and other solvents were tried. Small amounts of high grade concentrates could be brought up, but recoveries were low. Finally emulsions of stearic acid were tried. It was discovered that stearic acid alone has little collecting power except when conditioning is carried out at high temperature. When hydrocarbon solvents were also present, it proved to be an excellent collector. An example of one emulsion that proved satisfactory for some ores is given as follows: 1 part stearic acid by weight, 1 part sodium oleate by weight, 1.2 parts kerosene by weight, 100 parts water. In some successful tests part of the stearic acid was replaced by oleic acid. The emulsions were made by agitating the stearic acid and sodium oleate together with hot water, then adding the kerosene and agitating while cooling. In the five tests reported in Table 1, 650 g of ore were ground with 650 cc water in a laboratory rod mill. The pulp was filtered to eliminate excess water and the ground ore transferred to a stainless steel beaker for conditioning at high pulp density. In most of the tests sodium hydroxide was added to the conditioner during agitation, then the collector emulsion, and finally the sodium silicate. The amount of alkali was adjusted to give a pH of 8.5 to 9.0 in the flotation cell. After conditioning the pulp was transferred to a laboratory flotation cell and the test completed in a normal manner. It is interesting to note that a deposit of high grade concentrate forms on the conditioning agitator and in the conditioning vessel, and at times on the agitator of the flotation cell itself. A few grams of concentrate running as high as 4 pct U3O8 were recovered from the conditioner when Midnight ore containing less than 0.2 pct U3O8 was treated. In the examples given in Table I this conditioner concentrate is calculated as part of the total concentrate. The authors have not yet fully explored the possi-

Jan 1, 1960

By C. E. Schwab

A lead-zinc orebody, in fairly strong quartzite and with a dip of 35" to 60°, is block-caved by use of scrams in a stair-step pattern up the ore footwall. Scram linings to handle coarse muck and permit the use of folding scrapers are developed by the use of end-grain wooden blocks to reduce maintenance and keep operating cost to a minimum. THE Bunker Hill mine, since its discovery in 1885, has steadily produced a high grade of lead-silver-zinc ore. By the end of 1952 over 21,000,000 tons of this high-grade ore had been produced by square-set mining, and reserves in the mine continue to be very satisfactory both as to quantity and grade. For many years prior to 1941, mine production and mill capacity had been 1200 tons of feed per day. Closely adjacent to the mill, and stored behind dikes, coarse jig tailings had been impounded during the time preceding the advent of fine grinding and selective flotation. When manpower became short in 1941 and sink-and-float preconcentration was proved successful, mill capacity was increased to 1800 tons per day to treat these jig tailings economically. By 1946, because the supply of jig tailings was limited, underground exploration was started to discover and prove ore reserves of low-grade material which could be mined by an appropriate bulk mining method. During the years of square-set mining many possible areas of low-grade mineralization had been observed. One chosen for the first exploration work was sufficiently remote from active mining areas so that subsidence, if an ore-body were proved, would cause no problem. Also, old adits and workings were still open and in good enough condition so that exploration in the mineralized zone could be started with a minimum of preparatory work. In 1948 an orebody was proved of sufficient tonnage, of a grade about 2 pct Zn, 0.5 oz Ag, and 1.0 pct Pb. It was decided to use block-caving, the only appropriate mining method by which this grade of ore could be economically recovered. Exploration for additional reserves in other areas of the mine is continuing, but ultimate results are not known at this time. With more sink-and-float capacity, larger ball mills, and more flotation machines, mill capacity was increased to 3000 tons per day, permitting the mining of ore in the square-set area at a maximum rate not usually achieved, because of the scarcity of labor. Increased mill capacity also permits block caving and the mining of jig tailings at variable rates to keep mill feed up to 3000 tons per day. Fortunately the three types of feed are amenable to the same mill circuit and reagents for recovery of Pb and Zn. For example, during the first 10 months of 1952 square sets produced 827 tons per day, block-caving 1421 tons per day, and jig tailings 643 tons per day, an average daily production of 2891 tons for all three products. Exploration had proved the existence of an ore-body 1000 ft long and 165 ft wide in horizontal section, see Fig. 1. Company engineers were concerned only with the vertical extension, about 300 ft, from an old level to the surface. Much of this almost outcropped, Fig. 2. The ore lies in the hanging wall of a major fault of the Bunker Hill mine, standing at 65" in one end of the zone and separated from the fault by a wedge of waste, see Fig. 3. This wedge pinches out near the center of the zone, at which point the ore dips 45", lying nearly on the fault, Fig. 4. The remaining portion lies on the fault and conforms to the fault dip of 35", Fig. 5. Open-pit mining for the top of the ore was considered, but since the ore zone dipped into and under the mountains, adverse waste-to-ore ratios precluded use of this method. The ore occurs in massive quartzite of sufficient strength to support untimbered drifts, crosscuts, and raises. Zones of weakness in the quartzite are bedding, jointing, and small faults or slips. The mineralization, which occurs as small stringers of sphalerite and galena as well as pyrite, creates another line of weakness. The mineral veins or veinlets in themselves are high-grade. Their size and regularity and the amount of barren quartzite by which they are separated determined the limits of mineable ore, which are all assay limits except for the one determined by the major fault. Block 1 Without any background of caving in this type of quartzite, engineers selected the first block on the very steep end of the zone. Compelling reasons prompted this decision. The steep portion of the ore in Block 1 was of the lowest grade, so that if difficulties were encountered no very valuable ore would be lost, while the experience gained might be applied in mining the remaining blocks. A block 200x200 ft was laid out, with four scrams spaced 50 ft apart for drawing and placed at a right angle to the strike. Finger raises were placed in a 25-ft interval grid pattern, with flat undercutting done by crosscuts at the undercut level 25 ft above

Jan 1, 1954

By J. R. Szedon, T. L. Chu, G. A. Gruber

Amorphous adherent filnzs of silicon dioxide have been deposited on silicon substrates by the oxidation of silane at temperatures ranging from 650 to 1050C. Various diluents (argon, nitrogen, hydrogen) were used to suppress the formation of SiO2 in the gas phase. Deposition rates of the oxide were determined over the temperature range in question as functions of' re-actant flow rates. Etch rate studies were used for a cursory comparison of structural properties of deposited and thermally grown oxides. From electrical evaluation of metal-insulator-silicon capacitors it was determined that the interface charge density of deposited films is similar go that of dry-oxygen-grown films in the 850° to 1050 C temperature range. Deposited films exhibit several ionic instability effects which differ in detail from those reported for thermal oxides. Stable passivating films of silicon nitride over deposited oxides appear to be practical for use in silicon planar device fabrication. Such films can be prepared under temperature conditions which have less effect on substrate impurity distributions than in the case of grown oxides. AMORPHOUS silicon dioxide (silica) is compatible with silicon in electrical properties and is the most widely used dielectric in silicon devices at present. Silica films can be prepared by the oxidation of silicon or deposited on silicon or other substrate surfaces by chemical reactions or vacuum techniques. The ability of thermally grown silicon dioxide films to passivate silicon surfaces forms one of the practical bases of the planar device technology. Properly produced and treated films of grown SiO 2 can have low densities of interface charge (-1 X 10" charges per sq cm) and can be stable as regards fast migrating ionic sgecies. 1 To maintain these properties, even with an otherwise hermetically sealed ambient, the Sia layers must be at least l000 A thick. Such thicknesses require oxidation in dry oxygen for periods of 7.8 hr at 900°C or 2 hr at 1000°C. Although oxidation in steam or wet oxygen can reduce these times to 17 and 5 min, the resulting oxides must be annealed to produce acceptable levels of interface charge., Oxidation or annealing involving moderate to high temperatures for extended periods of time can be undesirable. Under some conditions, there can be changes in the distribution of impurities within the underlying substrate. A chemical deposition technique using gaseous am-bients is particularly attractive and flexible for preparing oxide films. With a wide range of deposition rates available, films can be produced under condi- tions of time and temperature less detrimental to impurity distributions in the silicon than in the case of thermal oxidation. The pyrolysis of alkoxysilanes, the hydrolysis of silicon halides, and various modifications of these reactions are most commonly used for the deposition of silica films.3 Silica films obtained in this manner are likely to be contaminated by the by-products of the reaction, organic impurities, or hydrogen halides. The use of the oxidation of silane for the deposition process has been reported recently.4 The deposition of silica films on single-crystal silicon substrates by the oxidation of silane in a gas flow system has been studied in this work. The deposition variables studied were the crystallographic orientation of the substrate surface, the substrate temperature, and the nature of the diluent gas. The electrical charge behavior of Si-SiO2-A1 structures prepared under various conditions was investigated by capacitance-voltage (C-V) measurements of metal-insulator-semiconductor (MIS) capacitors. The experimental approaches and results are discussed in this paper. 1) DEPOSITION OF SILICA FILMS The overall reaction for the oxidation of silane is: The equilibrium constants of this reaction in the temperature range 500° to 1500°K, calculated from the JANAF thermochemical data,= are shown in Fig. 1. In addition to the large equilibrium constants, the oxidation of silane is also kinetically feasible at room temperature and above. However, the strong reactivity of silane toward oxygen tends to promote the nucleation of silica in the gas phase through homogeneous reactions, and the deposition of this silica on the substrate would yield nonadherent material. The formation of silica in the gas phase can be reduced by using low partial pressures of the reactants. Argon, hydrogen, and nitrogen were used as diluents in this work. 1.1) Experimental. The deposition of silica films by the oxidation of silane was carried out in a gas flow system using an apparatus shown schematically in Fig. 2. Appropriate flow meters and valves were used to control the flow of various reactants, i.e., argon, hydrogen, nitrogen, oxygen, and silane. Semiconductor-grade silane, argon of 99.999 pct minimum purity, oxygen of 99.95 pct minimum purity, and nitrogen of 99.997 pct minimum purity, all purchased from the Matheson Co., were used without further purification. In several instances, a silicon nitride film was deposited over the silica film. This was achieved by the nitridation of silane with ammonia using anhydrous ammonia of better than 99.99 pct purity supplied by the Matheson CO.' The reactant mixture of the desired composition was passed through a Millipore filter into a horizontal water-cooled fused silica tube of 55 mm

Jan 1, 1969

By L. T. Larson, M. L. Picklesimer

The relationship between the apparent angle of rotation of monochromatic plane polarized light and the tilt of the basal pole from the surface normal has been experimentally determined for zirconium over the wavelength range of 500 to 655 mp. This relationship allows the determination of the spatial orientation of the basal pole of an individual grain in a polycvystal-ling zivrconium specimen to within ±3 deg by three simple tneasurements with a polarized-light metallurgical microscope. The method of measurement is discussed in detail. THE optical anisotropy of materials having noncubic crystal structures has long been used to reveal features by polarized-light microscopy. Petrographers have used measurements of certain optical properties to identify and classify transparent or translucent minerals. More recent work (i.e., Cameron1) has extended such measurements to opaque minerals in reflected light. Few attempts have been made to make similar measurements on noncubic metals. Couling and pearsall2 have reported that a sensitive tint plate can be used in a polarized-light metallurgical microscope to determine the position of the basal-plane trace in a grain of polycrystalline magnesium. Reed-Hill3 has reported that the same technique can be used for zirconium. We have found that the precision of measurement can be increased to about ±0.5 deg by using a Nakamura plate4,5 to determine the exact extinction position after the sensitive tint plate has been used to locate approximately the basal-plane trace. This report describes a method for measurement of another optical property, the apparent angle of rotation. This measurement permits determination of the angle between the basal pole of a grain of a hcp metal and the normal to the surface of the specimen. When the two measurements are combined, the orientation of the basal pole in space can be determined from three simple measurements on a single surface. One to two hundred such determinations will permit plotting of a basal-pole figure for the polycrystalline material with reasonable accuracy. When normally incident, monochromatic, plane-polarized light is reflected from the surface of an optically anisotropic material, the light may be converted to elliptically polarized light, the plane of vibration may be rotated, or both may occur. The el- lipticity, the angle of rotation, and the reflectivity can be related to the indices of refraction and the absorption coefficients of the material.6,7 Ellipticity values can be determined with an elliptical compensator, but not with the ease and precision desirable for the present purposes. Measurement of the angle of rotation requires only the determination of the angle from the crossed position (90 deg to the polarizer) that the analyzer must be rotated to obtain extinction when the trace of the optical axis in the surface is at 45 deg to the vibration direction of the polarizer. The angle of rotation of the analyzer is approximately 6/5 that of the true angle of rotation of the light as reflected from the specimen because there is a small amount of additional rotation produced during the passage of the reflected light through the mirror of the microscope. Since we are presently interested only in determining the tilt of the basal pole, the angle of rotation of the analyzer (the apparent angle of rotation of the light, i.e., uncorrected) can be used. Precision of the measurement can be increased substantially by the use of a Nakamura plate4,5 in determining the extinction position. In an optically uniaxial material (hcp or tetragonal crystal structure) the angle of rotation depends only on the optical properties of the material and the orientation of the optical axis of the grain relative to the plane of incidence of the plane-polarized light.7,8 Thus, in a metal such as zirconium, the apparent angle of rotation at the 45-deg position in any given wavelength of light is a direct measure of the tilt of the basal pole from the normal to the surface. If the optical properties vary with wavelength, the apparent angle of rotation for any given tilt of the basal pole will vary. None of the required information exists in the literature for zirconium nor for any other non-cubic metal. MEASUREMENTS ON SINGLE-CRYSTAL ZIRCONIUM A single-crystal sphere of zirconium 9/16 in. in diam was spark-cut from a single-crystal rod grown from iodide bar by an electron-beam zone-melting process.9 The damaged surface was removed by chemical polishing in a 45/45/10 mixture (by vol) of water, concentrated HNO3, and HF (48 pct) and then electropolishing at 50 v in a bath1' of methyl alcohol and perchloric acid (95/5 by vol) at -70-C. The single-crystal sphere was mounted in a five-axis goniometer stage having a removable eucentric X-ray diffraction goniometer head for the two inner orientation axes. The basal pole of the single-crysta sphere was aligned parallel to a third axis of the goniometer stage by using the sensitive tint method to determine the basal-plane trace at several rotational positions of the sphere. The alignment was then checked by removing the sphere and eucentric gonio-

Jan 1, 1967

By B. F. Oliver, C. W. Haworth

Pure tin and Sn-0.5pct Pb ingots have been frozen unidirectionally from the base. For quiescent melts that were initially undercooled, a transition from lower eqlciaxed structure to an upper columnar structure is found in the alloy ingots. Columnar to equi-axed back to columnar transitions are observed in superheated alloy ingots, but no such equiaxed band is observed impure tin. The reproducible equiaxed band is associated with a thermal undercooling followed by a recalescence. This undercooling is <5"C, whereas the critical (maximum obtainable) under-cooling for both the pure tin and the alloys used is -20°C. A similar undercooling is observed at the same position in the pure tin ingots, although in this case no clear transition in structure can be seen. The structure of the pure tin ingots is either entirely columnar or mixed columnar-equiaxed. A consideration of the detailed thermal history of the ingots indicates that the ingot macrostructures are determined by the occurrence of a local therlnal undercooling in conjunction with nuclei multiplication and transport mechanisrris. GENERALLY it is found that a pure metal ingot solidifies so as to produce an entirely columnar structure. Frequently an alloy ingot is found to have a columnar outer zone and an equiaxed central portion. Early systematic work to examine the factors controlling the formation of the equiaxed structure was reported by Northcott&apos; who showed that, for copper alloys frozen unidirectionally with a given ingot practice, the alloying element influenced the length of columnar crystals and the extent of the equiaxed structure. Northcott showed that alloys with a wider freezing range more readily produced the equiaxed structure. The nucleation process can be important in producing equiaxed structures; frequently an alloy which readily solidifies with an entirely columnar structure will produce an entirely equiaxed structure when a nucleating agent is added to the melt.&apos; The formation of the equiaxed structure was attributed by Winegard and chalmers3 to the presence of constitutional supercooling; that is, a region of liquid in front of the growing solid could have a temperature below its equilibrium liquidus temperature. Thus, with a small enough temperature gradient in the liquid, it was suggested that the presence of constitutional supercooling may be sufficient to bring about the nuclea-tion necessary for the formation of an equiaxed structure. Although this explanation is plausible, and may be relevant in many ingots, Walker has described an experiment&apos; for which constitutional supercooling seems to be an unlikely cause of nucleation. A Ni-20 pct Cu alloy, repeatedly undercooled more than 50"C, was crystallized and found to show the typical colum-nar-equiaxed structure. The separation between the liquidus and the solidus for the alloy is 40°C. Thus, in this experiment the nucleation required for the formation of the equiaxed structure must have come about in some other way than by the nucleation catalysis constitutional supercooling hypothesis. Chalmers has suggested more recently5 that nuclei (in a typical ingot) are present immediately after pouring and are prevented from redissolving by the constitutional supercooling effect. More recently Uhlman, Seward, Jackson, and ~unt&apos; have shown direct evidence using ice and organic materials that freeze dendritically that the "remelt mechanism" may be an extremely effective crystal multiplication process during the freezing of ingots under conditions involving dendritic growth. JSlia" experimentally demonstrated the detachment of dendrite arms. chernov14 has analyzed the dendrite arm detachment process as a coarsening phenomena driven by the minimization of interphase area. Katta-mis and ~lemings" working with undercooled steel melts give evidence supporting this mechanism. Mechanisms of dendrite arm detachment such as those assisted by convection are believed to be the origin of the macrostructures obtained in this study. This study makes no attempt to distinguish the relative contributions of these mechanisms. The object of the present work was to obtain accurate temperature measurements during the solidification of an ingot and to correlate these measurements with the formation of equiaxed grains in the resulting ingot structures. Similar previous work is very limited. The measurements carried out by Northcott are neither sufficiently extensive nor sufficiently accurate for any interpretation. Plaskett and winegard7 carried out experiments on A1-Mg alloys in which they observed values of the temperature gradient, G, in the liquid and rate of freezing, R (for a given alloy solute content Co), at the transition from a columnar to an equiaxed structure. They reported that equiaxed crystals were produced at values of G/G approximately proportional to the solidus composition. Similar experiments using Pb-Sn alloys carried out by £111011" showed a linear relation between G/R and the solidus composition. However, the thermocouples were in the mold wall rather than in the melt and, in one case, ingot surfaces were examined. There is ambiguity in the meaning of the values of G and R measured in all these experiments. APPARATUS AND EXPERIMENTAL PROCEDURE Alloys were prepared by induction melting 99.999 pct Sn and 99.999 pct Pb to form a Sn-0.5 wt pct Pb alloy in air in a graphite crucible and casting into a cylindrical graphite mold 6 in. long, 1 in. in diarn , and with a & in. wall thickness. This mold was mounted on a copper base through which cooling water could be

Jan 1, 1968