By John Wulff, Steinberg Morris, Robert Kamm

In powder metallurgy it has often been observed that shrinkage may occur in one direction and growth in another during sintering. Even in long-time sintering experiments the rate of shrinkage may be different in different parts of the compact. In the fabrication of some parts requiring a constant permeability it is even questionable in some cases whether pressing from one direction should be attempted. These observations require for their interpretation a more detailed study of green or pressed density than has heretofore been available. Usually average density measurements of the whole compact are made and in some cases carefully cut sections are measured. A different approach to the problem was first mentioned by Rakowskil and also used by Balshin.2 Balshin's diagram is reproduced in Fig I and schematically shows the result of pressing three layers of metal powder with fine intervening layers of graphite. The retarding effect of the die walls and a qualitative example of the density distribution is evident. More quantitative information about the distribution of density within a cold-pressed powder compact would be useful in showing the variation in density in as as influenced by the type of poKder, shape of die, lubricatioll during the process, and other variables. Furthermore, information about the cracking of cold-pressed compacts may be obtained from an analysis of the stress distribution within a, powder compact, and some information about the stress distribution can be obtained in turn from the derlsity and strain distributions. A more detailed report on some of the present experiments appears in reference 3. Present Investigation In order to ascertain the density gradients in cold-pressed metal powders, a deformable lead grid within the powder was employed. After pressing in cylindrical di" the ejected compact was radiographed, giving a pattern of the deformed grid. From the radiograph density and deformation from point to point is readily measured. From the radiograph strain distribution and stress trajectories were also determined. The latter also permits the determination of the coefficient of friction at the die wall. This technique indicates that the densest Part of a compact pressed from one side is at the top outer circumference and the least dense region at the bottom circumfercnce near the stationary plunger. For Some heights of compacts the density at the axis is such that the lower density is at the top rather than at the bottom. SO irregular a density distribution is due primarily to die-wall friction. As the ratio - diameter to height of compact is increased the die walls play a correspondingly smaller role. More uniform density

Jan 1, 1947

By Thomas E. Leontis

INTRODUCTION THE importance of magnesium alloys in the manufacture of aircraft engines has been realized for many years. A concentrated effort has been exerted in the laboratories of the Dow Chemical Co. to develop magnesium-base alloys with improved properties at elevated temperatures whereby greater advantage can be taken of the inherent lightness of these materials. In an earlier publication,1 attention was called to the superior tensile properties and resistance to creep of cerium-containing magnesium alloys at temperatures up to 700°F. More recently, additional data on magnesium-cerium alloys have been furnished by Murphy and Payne.2 The present paper deals with the mechanical properties of sand-cast magnesium alloys containing zinc, at temperatures up to 500°F. The study includes binary Mg-Zn† alloys containing up to 10 pct zinc and several ternary and some polynary alloys based on the Mg-1Zn,†Mg-3Zn, Mg-4.4Zn, Mg-6Zn, and Mg-10Zn binaries. The compositional variation in the tensile properties, hardness, and creep at room and elevated temperatures, and in the electrical conductivity at room temperature has been determined. The results of these tests show that many zinc-containing magnesium alloys exhibit resistance to creep at elevated temperatures significantly higher than that of present commercial magnesium alloys, but lower than that of alloys of the magnesium-cerium type. In addition, they have high tensile properties at room and elevated temperatures and high conductivity. This combination of mechanical properties and conductivity indicates that these alloys should be given serious consideration for commercial applications involving exposure to temperatures higher than those to which present commercial magnesium alloys can be taken safely. LITERATURE The properties of sand-cast magnesium alloys containing zinc as a principal alloying element have not been investigated very extensively, especially at elevated temperatures. The following remarks, which are confined to sand-cast alloys, will serve as a summary of the most important references on this phase of magnesium metallurgy. The first recorded determination of the tensile strength of binary Mg-Zn alloys as a function of zinc content was reported by Aitchison.3 Similar studies, including the measurement of elongation and hardness, have been performed by Gann and Winston,4 Dumas and Rockaert,5 Haughton and Prytherch,6 and by Spitaler, the last being reported by Beck.7 A slight superiority in the tensile strength of chillcast Mg + 8 Zn alloy over the sand-cast alloy was noted by Maybrey 8 That alloys of magnesium containing 5 to 12 pct zinc

Jan 1, 1948

By Clarence E. Sims, Donald W. Williams, George A. Moore

INTRODUCTION DURING the past several years, the steel casting industry has made studies of heavy castings in which the test bar has been taken from heavy sections rather than from attached or separately cast coupons. It has been noted that the ductility properties of these heavy sections are often lower than those normally expected. Such lowered ductility is usually accompanied by a spotty test bar fracture, and the ductility values can often be greatly improved if a low-temperature aging treatment is given to the casting. A loss of ductility of this type is considered "abnormal," since it is not accompanied by an increase of tensile strength or hardness, and "temporary" when the ductility can be restored by aging. The cure of such an abnormal condition represents a real improvement in the quality of the steel, Several types of abnormal loss of ductility can be distinguished, of which those caused by excessive amounts of inclusions of undesirable type and those caused by unsuitable grain size and ingot structure are well known. The particular type of abnormal lowered ductility currently under consideration may be distinguished by the fact that the low-temperature aging treatment necessary for its relief is insufficient to cause any visible change in the microstructure as ordinarily observed. As this aging will in fact eventually occur at room temperature, the phenomenon of present interest may be given the symptomatic definition, "Temporary Abnormal Low Ductility." Some hundreds of previous investigations, largely qualitative in nature, have established, beyond reasonable doubt, that hydrogen is normally present in newly manufactured steel and that this gas, in small amounts, can cause a temporary abnormal loss of ductility. The commonly observed association of high gas content and low ductility has given strong evidence for the presumption that hydrogen-, possibly assisted by other gases, is the primary cause of the low ductility observed. Accordingly, The Steel Founders' Society of America has, since Nov. 1, 1944, sponsored investigations at Battelle Memorial Institute whose primary objective is to obtain quantitative information on the relation of the amount of hydrogen and nitrogen in steel, together with associated methods of steelmaking and treatment, to low-ductility effects and porosity. The interest of this investigation thus extends to permanent abnormal losses of ductility, such as are caused by the inclusions which sometimes result from special deoxidizing practices and possibly from metallic nitrides, but as these can be distinguished from the temporary effect of hydrogen, they have been excluded from the work reported here except when they

Jan 1, 1948

By Morris Steinberg, John Wulff, Robert Kamm

IN powder metallurgy it has often been observed that shrinkage may occur in one direction and growth in another during sintering. Even in long-time sintering experiments the rate of shrinkage may be different in different parts of the compact. In the fabrication of some parts requiring a constant permeability it is even questionable in some cases whether pressing from one direction should be attempted. These observations require for their interpretation a more detailed study of green or pressed density than has heretofore been available. Usually average density measurements of the whole compact are made and in some cases carefully cut sections are measured. A different approach to the problem was first mentioned by Rakowski1 and also used by Balshin.2 Balshin's diagram is reproduced in Fig r and schematically shows the result of pressing three layers of metal powder with fine intervening layers of graphite. The retarding effect of the die walls and a qualitative example of the density distribution is evident. More quantitative information about the distribution of density within a cold-pressed powder compact would be useful in showing the variation in density in compacts as influenced by the type of powder, shape of die, lubrication during the process, and other variables. Furthermore, information about the cracking of cold-pressed compacts may be obtained from an analysis of the stress distribution within a powder compact, and some information about the stress distribution can be obtained in turn from the density and strain distributions. A more detailed report on some of the present experiments appears in reference 3. PRESENT INVESTIGATION In order to ascertain the density gradients in cold-pressed metal powders, a deformable lead grid within the powder was employed. After pressing in cylindrical dies the ejected compact was radiographed, giving a pattern of the deformed grid. From the radiograph density and deformation from point to point is readily measured. From the radiograph strain distribution and stress trajectories were also determined. The latter also permits the determination of the coefficient of friction at the die wall. This technique indicates that the densest part of a compact pressed from one side is at the top outer circumference and the least dense region at the bottom circumference near the stationary plunger. For some heights of compacts the density at the axis is such that the lower density is at the top rather than at the bottom. So irregular a density distribution is due primarily to die-wall friction. As the ratio of diameter to height of compact is increased the die walls play a correspond¬ingly smaller role. More uniform density

Jan 1, 1947

By W. H. Hough, P. B. Leavenworth

Development during 1942 led to the discovery of 26 new fields in the Texas Gulf Coast, as compared with 27 during 1941. Of these, 19 are classed as oil fields, 4 distillate fields, and 3 gas fields. Production from the new fields amounted to 614,467 bbl. to October 1942. Producing Sections.—Discoveries in I942, compared with the previous two years, classified by producing formations, are shown in the following table: It is interesting to note the increase in Wilcox discoveries due to the extensive geophysical campaign that has been con. ducted since 1940. Drilling.—During the year 688 wells were drilled, of which 574 produced oil or gas and 114 were dry. This represents a considerable decline in activity over the previous year, when 1405 wells were drilled in the area, of which 1081 were producers and 324 failures. Jackson County continued to hold the lead, with 222 wells completed. Production.—-Despite curtailed drilling, production amounted to 118,009,451 bbl. for 1942, indicating a slight increase over the 113,726,893 bbl. produced during 1941. The statistics in Tables I and 2 include condensate and distillate as oil production, because many Gulf Coast fields produce oils with a wide variation of specific gravities, all of which are commingled in pipe lines. Table 3 shows by counties most of the activities referred to. The number of wells drilled includes only field wells; not wildcats. Outstanding Fields of 1942 The Texas Gulf Coast covered in this report has 270 more or less active oil and gas fields, including the new discoveries of 1942. Of these the most outstanding from the standpoint of production are listed in Table 4. Each of these fields produced one million barrels or more during 1942. Some of the fields where new extensions are occasionally referred to as separate fields, such as West Columbia and New West Columbia, or Thompson and South Thompson, are combined to give a more accurate outline. Two interesting facts may be noted from this list of some 26 oil fields: (I) that the Lolita field, Jackson County, is the only discovery since 1938 to produce more than one million barrels annually, although there have been 79 discoveries since Jan. I, 1940; (2) that 20 of these 26 fields produce from the Frio. New Fields ALief, Harris County.—Pure Oil Company's No. I Mike Albanese was drilled to 8637 ft. in Cook Mountain shale. After numerous tests the well was completed on Apr. 20, 1942, in a Yegua sand at 7919 to 7924 ft. for 54 bbl. of 52' gravity oil and 3,335,000 cu. ft. of gas through

Jan 1, 1943

By T. E. Leontis

The importance of magnesium alloys in the manufacture of aircraft engines has been realized for many years. A concentrated effort has been exerted in the laboratories of the Dow Chemical Co. to develop magnesium-base alloys with improved properties at elevated temperatures whereby greater advantage can be taken of the inherent lightness of these materials. In an earlier publication, attention was called to the superior tensile properties and resistance to creep of cerium-containing magnesium alloys at temperatures up to 700°F. More recently, additional data on magnesium-cerium alloys have been furnished by Murphy and Payne. The present paper deals with the mechanical properties of sand-cast magnesium alloys containing zinc, at temperatures up to 500°F. The study includes binary Mg-Znt alloys containing up to 10 pct zinc and several ternary and some polynary alloys based on the Mg-~Zn,f Mg-jZn, Mg-4.4211, Mg-6Zn, and Mg-roZn binaries. The compositional variation in the tensile properties, hardness, and creep at room and elevated temperatures, and in the electrical conductivity at room temperature has been determined. The results of these tests show that many zinc-containing magnesium alloys exhibit resistance to creep at elevated temperatures significantly higher than that of present commercial magnesium alloys, but lower than that of alloys of the magnesium-cerium type. In addition, they have high tensile properties at room and elevated temperatures and high conductivity. This combination of mechanical properties and conductivity indicates that these alloys should be given serious consideration for commercial applications involving exposure to temperatures higher than those to which present commercial magnesium alloys can be taken safely. Literature The properties of sand-cast magnesium alloys containing zinc as a principal alloying element have not been investigated very extensively, especially at elevated temperatures. The following remarks, which are confined to sand-cast alloys, will serve as a summary of the most important references on this phase of magnesium metallurgy. The first recorded determination of the tensile strength of binary Mg-Zn alloys as a function of zinc content was reported by Aitchison. Similar studies, including the measurement of elongation and hardness, have been performed by Gann and Winston,' Dumas and Rockaert, Haugh-ton and Prytherch,6 and by Spitaler, the last being reported by Beck.' A slight superiority in the tensile strength of chill-cent Mg + 8 es alloy Over the sand-cast alloy was noted by Maybrey.8 That alloys of magnesium containing 5 to 12 pct zinc

Jan 1, 1949

By H. S. Kalish, F. J. Dunkerley

Introduction and Previous Work THE determination of the low temperature tensile properties of tin and tin-lead alloys was initiated as part of an extensive research program on the phasial equilibria of tin binary systems below 13.2°C and the property changes associated therewith. A survey of the literature revealed that, although some room temperature tensile data were available for tin and a few tin-lead alloys, there existed no survey report of the low tcmPerature tensile properties of these alloys. Accordingly, the tensile data for tin and a series of pure tin alloys containing from 0.01 to 50 pet lead were measured at eleven temperatures horn — 196 to +20°C and are presented here in survey form. In addition to the importance of these tensile data as a preliminary to certain fundamental research, this information promises also to be of commercial importance because of the extensive use now being made of tin-lead solders in refrigeration and gas liquefaction equipment. Occasional failures of the solders in low temperature service have been attributed by some metallurgists to low temperature embrittlement, while others hold that failure results from the transformation of the tin-rich phase of the solder from the solid white (beta) to the powdered gray (alpha) form. From the data previously available in the literature, neither of these explanations can be completely corroborated. cohen and van Lieshout have estab-lished the beta to alpha tin transformation at 13,2°C and have shown that strain accelerates the transformation. Further, they showed that although I pct lead retarded the transformation, it was not eliminated. It will be pertinent, then, to note whether the beta to alpha transformation of the tin.rich phase will occur in a short-time tensile 'test. polanyi and schmid2 studied the tensile properties of tin single crystals at — 185°~ and report that tin is britlle at this tem-perature. In 1946, Kostenets3 reported that pure tin was brittle at —Ig6 and — 253°~, while lead remained ductile at both these temperatures. He also studied the tensile properties of tin-lead alloys containing from 10 to 75 pet lead at —253, —196 and + I~OC. The ultimate tensile strength increased more than two times in going from room temperature to — I96°C and about three times that value on further cooling to — 253 C- All the alloys were brittle at — 196'C except those containing more than 75 pct lead. Even at — 253'C, the 75 pct lead alloy retained 36 pet elongation in a 30 mm-ga. length. Creep is also an important phenomenon

Jan 1, 1949

By C. E. Sims, G. A. Moore, D. W. Williams

During the past several years, the steel casting industry has made studies of heavy castings in which the test bar has been taken from heavy sections rather than from attached or separately cast coupons. It has been noted that the ductility properties of these heavy sections are often lower than those normally expected. Such lowered ductility is usually accompanied by a spotty test bar fracture, and the ductility values can often be greatly improved if a low-temperature aging treatment is given to the casting. A loss of ductility of this type is considered "abnormal," since it is not accompanied by an increase of tensile strength or hardness, and "temporary" when the ductility can be restored by aging. The cure of such an abnormal condition represents a real improvement in the quality of the steel. Several types of abnormal loss of duetility can be distinguished, of which those caused by excessive amounts of inclusions of undesirable type and those caused by unsuitable grain size and inget structure are well known. The particular type of abnormal lowered ductility currently under consideration may be distinguished by the fact that the low-temperature aging treatment necessary for its relief is insufficient to cause any visible change in the micro-structure as ordinarily observed. As this aging will in fact eventually occur at room temperature, the phenomenon of present interest may be given the symptomatic definition, ''Temporary Abnormal Low Ductility." Some hundreds of previous investigations, largely qualitative in nature, have established, beyond reasonable doubt, that hydrogen is normally present in newly manufactured steel and that this gas, in small amounts, can cause a temporary abnormal loss of ductility. The commonly observed association of high gas content and low ductility has given strong evidence for the presumption that hydrogen, possibly assisted by other gases, is the primary cause of the low ductility observed. Accordingly, The Steel Founders' Society of America has, since Nov. 1, 1944, sponsored investigations at Battelle Memorial Institute whose primary objective is to obtain quantitative information on the relation of the amount of hydrogen and nitrogen in steel, together with associated methods of steelmaking and treatment, to low-duetility effects and porosity. The interest of this investigation thus extends to permanent abnormal losses of ductility, such as are caused by the inclusions which sometimes result from special deoxidizing practices and possibly from metallic nitrides, but as these can he distinguished from the temporary effect of hydrogen, they have been excluded from the work reported here except when they

Jan 1, 1949

By Thomas Fraser

UP to the present, there has been no large coal-producing industry in any of the South American countries. Since colonial times, the great mineral and agricultural wealth of that continent has led the people to activities other than the development of manufacturing industries based on coal; and climatic conditions are such that there has been very little demand for solid domestic fuel. However, there are extensive and widely distributed reserves of coal in South America that would make the development of a modern coal industry feasible. That factor is of the utmost significance now, when it is believed that the South American countries are entering the pioneer phase of a broad industrial development. Coal Fields Great areas of coal-bearing formations of Cretaceous and Tertiary ages occur generally throughout the Andean uplift and extend into the coastal range of the Caribbean region far east of Caracas. Thus the west coast countries have adequate reserves of coal, which include a wide range of types and classes. In the eastern part of South America, east of the Cordillera, as in North America, the coal measures are of Carboniferous and Permocarboniferous ages. The principal known deposits in this area are in the southern States of Brazil. Permocarboniferous coals ranging in rank from lignitic to anthracitic are found in the States of Rio Grande do Sul, Santa Catarina, Parana and Sao Paulo. In the great.interior plateau of Brazil, south of the Amazon River, are extensive areas of Carboniferous strata that may contain coal deposits. There are widely scattered reports of findings of coal in' wells and stream beds in northern Piaui and Goias. In the Rio Fresco Valley, explorers have observed outcrops of two beds of anthracite and have brought to Rio de Janeiro samples from these beds. The Fresco is a tributary of the Xingu River that enters the Amazon from the south, but coal could not be shipped by water since the Rio Fresco area is in the upper part of the Xingu Valley, and there is a formidable series of rapids between that area and the lower level of the Amazon River basin. It is doubtful if coal deposits in this general area will be of economic importance for many years to come. Fig. 1 shows the general location of known coal fields of South America that have been explored sufficiently to indicate the presence of workable reserves. The coal deposits of the Andean region are similar in occurrence and general characteristics, as well as in age, to the coals of the Rocky Mountain region of North America. Although the coal fields obviously

Jan 1, 1952

By Frank L. Nason

The complete statistics of zinc-ore production in the United States for 1916 are not yet available. The following figures are, therefore, only approximate. The total production of concentrates for this year, including New Jersey and Tennessee, amounts to 1,280,000 tons. Of this tonnage, five mines produced approximately 536,000 tons, or about 42 per cent. The remaining concentrates came mainly from the "Valley States," Missouri, Wisconsin, Kansas, Oklahoma, and Arkansas. The 1,280,000 tons of concentrates represent about 25,000,000 tons of crude or run-of-mine ore. Of the five mines producing the 42 per cent., the dimensions of three are approximately 25 by 1500 by 2000 ft. (7.6 by 457 by 610 m.) or more: Four of the five mines are undoubtedly veins in the common acceptance of the term. They are located in great vein systems. The mines of "Valley States" have not, so far, been classed as veins; simply as "secondary deposits." The origin of these secondary deposits has been a warmly debated subject. Many geologists contend that they are the results of leaching from overlying and adjacent rocks carrying but traces of zinc, these traces leached out and deposited in favorable places. If this theory is correct, deposition is strictly limited to shallow depths. No volume of ore comparable to that of "true fissure veins" is to be expeeted. Just what this means to the future of zinc mining in these States is here indicated. The total zinc-bearing areas of these States amount to about 9124 sq. miles (23,631 sq. km.). Assuming that 10 per cent. of this total will be more or less productive, there are 912 sq. miles (2,362 sq. km.) of "mineral" ground. The average depth of the operated mines is something like 100 ft. or less. In Bulletin 606, U. S. Geological Survey (1915), p. 202, Siebenthal makes the following statement: "The writer is informed by William Waugh, one of the drillers of the Stone City well, that cuttings from other wells which he drilled in the vicinity of Pittsburgh, Kan., have shown galena and sphalerite taken from a depth of 591 ft. (180.14 m.) and that the showing of ore at some places would be considered good enough to justify the sinking of a shaft had it been found in the Joplin district and at shallower depths." Leaving out of the question the prohibitive cost of such a shaft, there is

Jan 1, 1918

By D. C. Hilty, W. Crafts

The solubility of oxygen in iron containing aluminum has been determined at 1550°, 1600°, and 1650°C and found to be much higher than predicted from theoretical considerations, possibly due to equilibria with an iron-aluminum spinel phase rather than pure AI,O.. The presence of manganese greatly increased the deoxidizing power of aluminum. DEOXIDATION and inclusion formation in steel have proved to be elusive phenomena that are difficult to control in spite of much effort to understand and evaluate the reactions. Study of the problem indicated that more accurate data on the solubility of oxygen in iron containing deoxidizers were essential to further progress, and an empirical determination of oxygen solubilities has been initiated at the Union Carbide and Carbon Research Laboratories, Inc. The investigation has included the effects of aluminum, silicon, manganese, and combinations of these elements at 1550°, 1600°, and 1650°C. The equipment and experimental procedure as well as the results of a study of the effects of aluminum are described below. In general, it was found that the solubility of oxygen in iron containing aluminum is much higher than predicted, possibly because of the formation of complex nonmetallic phases, and that manganese greatly increases the deoxidizing power of aluminum. The generally accepted deoxidation curves for 1600°C are summarized in fig. 1, from "Basic Open Hearth Steelmaking"'. These curves are assumed to represent the solubility of oxygen in the presence of deoxidizers and should indicate the limits of mis-cibility gaps in the phase diagrams of the systems that control the formation and character of non-metallic inclusions as described by Benedicks and Lofquist'. They were derived mainly by application of the methods of thermodynamics to the available experimental observations, and by calculations based on the thermal constants of the pure substances when experimental data were lacking. Among the more notable researches contributing to the development of knowledge of oxygen solubilities are those of Korber and Oelsen8, 4, C. H. Herty, Jr. and associates5,6, Krings and Schackmann7, Went-rup and Hieber8 Schenck and Briiggeman9, Vacher and Hamilton'" and Chipman and co-authors 1,11,12,13 Practically, the deoxidation curves are of limited value in predicting oxygen content and rationalizing deoxidation practices. The reasons for this inadequacy appear to be error from inaccurate data, oversimplifying assumptions, interacting effects of combined deoxidizers, and possibly unknown extra-equilibrium and side reactions. Although inclusion formation is a very complex reaction it must be re-

Jan 1, 1951

By G. Sachs, E. J. Ripling, S. I. Liu, J. J. Lynch

It is a generally recognized fact that by repeated straining the fracture stress of any metal is reduced to a fraction of its value for static loading. The value of this fatigue strength depends upon numerous factors, such as the states of strain and stress, the limits of straining, and the number of repeated loadings or cycles The large volume of previous investigations on fatigue is concerned entirely with large numbers of cycles, say exceeding 10,000 and up to 500,000,000. However, the changes in fracture stress and fracture strain occurring after a small number of repeated loadings have attracted little attention. Apparently the only investigations of this type are those byLudwik4.5 who subjected steel, copper, and aluminum wire to repeated torsion. In each test the torque was varied between identical values in the two directions of twisting. Depending upon the magnitude of the moment, fracturing occurred after a number of cycles, up to 10,000. The results of Ludwik's tests will be discussed later Such torsion does not readily yield actual stress and strain values. Therefore a pre- liminary study was made of the effects of repeated direct stresses, that is, tension and compression stresses. Because such tests are considerably more tedious than torsion tests, only high stresses were used in the preliminary work, yielding definite changes in metal properties after a few cycles. It was found in these tests that strains could be controlled more readily than stresses in the investigated range of high stresses. This paper, consequently, deals with the effects of strains of equal magnitude but different signs. The metal was first prestrained in static tension by a certain amount then subjected to compression to yield the same amount of strain after unloading. This loading cycle was repeated up to a maximum of seven times. After various cycles, the stress-strain curves in tension were determined, up to fracturing. As material for these tests, the aluniinum alloy 24ST was selected because it exhibits a comparatively small amount of necking in the tension rest This alloy permitted, therefore rather accurate cont.rol at the high strains necessary to produce fatigue failures at less than seven cycles. The results of this invest~gation appear sufliciently interesting to extend the method of attack in various directions It is intended to study (11 the effects of cycles up to a tew thousands and (2) the effects of strains of different magnitude in tension and compression respectively 'The latter variable also includes a. a special case the effects of compressive strains.

Jan 1, 1949

By A. H. Geisler, R. F. Mehl, C. S. Barrett

The complicated nature of the property changes that accompany age-hardening has made it necessary to reconsider and to elaborate the simple dispersion theory.l It has been apparent for some time that more direct information is needed concerning the atomic mechanism of precipitation from solid solution if the theory of age-hardening is to be developed past a purely qualitative stage.‡ Fortunately, in recent years information has been developed which allows us to trace in detail the lattice changes accompanying the process of precipitation from solid solution. This information relates chiefly to the sequence of the several stages of lattice alteration by which the matrix lattice is transformed to the equilibrium precipitate lattice, and permits reasonable inferences to he drawn concerning the states of internal strain that accompany these stages. This information is most complete for the solid solution of copper in aluminum. The equilibrium precipitate is the 0 phase, "CuAl2." This forms in plates, parallel to the {100} matrix planes. The atom pattern and atom spacing on the plane in 0 lying parallel to this plane are roughly similar to those opposite it in the matrix.3 The formation of 0, however, is preceded by the formation of a transition lattice 0': which again lies parallel to the matrix {100} plane, but in this case the matching of atom pattern and spacing across the matrix-precipitate interface is nearly periect; thus there is lattice coherency across the interface and the interface is a plane of separation in only a very limited sense.'8 Particles of 0' may be recognized microscopically and form a well-defined Wid-manstatten figure.* The 0' lattice is recognized by the occurrence of diffraction lines on powder photo-grams or of spots on Laue photograms which may be analyzed in the usual ways to determine the lattice type and the lattice spacings. Very recent research 6, 7, 1 has shown, however, that streaks occur on the Laue photogram at an earlier point in time during the aging process. These streaks have been attributed to a preferential clustering of copper atoms into small platelike elements of only a few atoms in thickness and a lew hundred atoms in diameter, probably of the composition of " CuA12," which may be designated as Guinier-Preston zones or aggregates.1 It is difficult if not impossible to determine the lattice type and lattice spacing in these aggregates. It is possible1 that these aggregates are in fact ?' in a high State of dispersion; the inclination to argue this is strong, as we shall see later. Never-

Jan 1, 1941

By R. F. Mehl, C. S. Barrett, A. H. Geisler

THE complicated nature of the property changes that accompany age-hardening has made it necessary to reconsider and to elaborate the simple dispersion theory.1 It has been apparent for some time that more direct information is needed concerning the atomic mechanism of precipitation from solid solution if the theory of age-hardening is to be developed past a purely qualitative stage.‡ Fortunately, in recent years information has been developed which allows us to trace in detail the lattice changes accompanying the process of precipitation from solid solution. This information relates chiefly to the sequence of the several stages of lattice alteration by which the matrix lattice is transformed to the equilibrium precipitate lattice, and permits reasonable inferences to be drawn concerning the states of internal strain that accompany these stages. This information is most complete for the solid solution of copper in aluminum. The equilibrium precipitate is the ?' phase," CuA12." This forms in plates, parallel to the {100} matrix planes. The atom pattern and atom spacing on the plane in ?' lying parallel to this plane are roughly similar to those opposite it in the matrix.' The formation of ?', however, is preceded by the formation of a transition lattice ?', which again lies parallel to the matrix {100} plane, but in this case the matching of atom pattern and spacing across the matrix-precipitate interface is nearly perfect; thus there is lattice coherency across the interface and the interface is a plane of separation in only a very limited sense.4-8 Particles of ?' may be recognized microscopically and form a well-defined Widmanstätten figure.* The ?' lattice is recognized by the occurrence of diffraction lines on powder photograms or of spots on Laue photograms which may be analyzed in the usual ways to determine the lattice type and the lattice spacings. Very recent research 6.7,1 has shown, however, that streaks occur on the Laue photogram at an earlier point in time during the aging process. These streaks have been attributed to a preferential clustering of copper atoms into small platelike elements of only a few atoms in thickness and a few hundred atoms in diameter, probably of the composition of "CuA12," which may be designated as Guinier-Preston zones or aggregates.1 It is difficult if not impossible to determine the lattice type and lattice spacing in these aggregates. It is possible1 that these aggregates are in fact merely ?' in a high state of dispersion; the inclination to argue this is strong, as we shall see later. Never-

Jan 1, 1941

W. 0. HOTCHKISS, * Madison, Wis.-It was fortunate, in a way, that this subject of income taxation came up during the war when the government could appeal, on the basis of patriotism, to men of large, business experience to undertake the work of formulating this matter and practically donate their services. At any other time the government would have been unable to secure the necessary number of men of like ability. There is one thing that must not be forgotten. In all cases, except the very largest and most important, the application of this income tax law to a mine is going to be made by clerks whose salaries are fixed by a Congress that appropriated a half billion of dollars for a war purpose and provided that $4000 should be the highest salary paid in the adminis-tration of that great sum. The Congress of the United States unfor-tunately seems almost entirely unaware of the fact that men of ability and experience are worth money and must be paid adequately if proper public service is to be secured. While the formulation of the broad plans for administering the law have been in the hands of. men of unusual ability, we have the future to guard, and, if possible, the mining industry should see to it that the Internal Revenue Department is permitted by Congress to pay salaries that will enable it to secure men of the ability and experience necessary to insure proper consideration of the industry. Another fact to which I would call attention is the difference between the business and the economic, or economists', points of view as to what a mine is. The economists have properly, from their point of view, classed a mine as a wasting asset, but the average metal mine is not a wasting asset if it is a real mine. The economists are correct in a broad sense in that every ton of ore taken out diminishes the orebody by that amount. When it comes to the consideration of an individual mine from the business standpoint, the future of that mine rests on unfore-seeable events-the discovery of new orebodies or the development of old bodies beyond the point of probable expectations. Every going mine must develop new ore each year to replace that extracted, and, .during all but the last one or two years of its activity, actually does so. Instead of being a "wasting asset" such a mine, from the practical stand-point which must control valuation, is an "increasing asset." From

Jan 12, 1919

By H. S. Kalish, F. J. Dunkerley

INTRODUCTION AND PREVIOUS WORK THE determination of the low temperature tensile properties of tin and tin-lead alloys was initiated as part of an extensive research program on the phasial equilibria of tin binary systems below 13.2°C and the property changes associated therewith. A survey of the literature revealed that, although some room temperature tensile data were available for tin and a few tin-lead alloys, there existed no survey report of the low temperature tensile properties of these alloys. Accordingly, the tensile data for tin and a series of pure tin alloys containing from 0.01 to 50 pct lead were measured at eleven temperatures from -196 to +20°C and are presented here in survey form. In addition to the importance of these tensile data as a preliminary to certain fundamental research, this information promises also to be of commercial importance because of the 'extensive use now being made of tin-lead solders in refrigeration and gas liquefaction equipment. Occasional failures of the solders in low temperature service have been attributed by some metallurgists to low temperature mbrittlement, while others hold that failure results from the transformation of the tin-rich phase of the solder from the solid white (beta) to the powdered gray (alpha) form. From the data previously available in the literature, neither of these explanations can be completely corroborated. Cohen and van Lieshout1 have established the beta to alpha tin transformation at 13.2°C and have shown that strain accelerates the transformation. Further, they showed that although I pct lead retarded the transformation, it was not eliminated. It will be pertinent, then, to note whether the beta to alpha transformation of the tin-rich phase will occur in a short-time tensile test. Polanyi and Schmid2 studied the tensile . properties of tin single crystals at -185°C and report that tin is brittle at-this temperature. In 1946, Kostenets3 reported that pure tin was brittle at -196 and -253°C, while lead remained ductile at both these temperatures. He also studied the tensile properties of tin-lead alloys containing from 10 to 75 pct lead at -253, -196 and +17°C. The ultimate tensile strength increased more than two times in going from room temperature to -196°C and about three times that value on further cooling to -253°C. All the alloys were brittle at -6°C except those containing more than 75 pct lead. Even at -253°C, the 75 pct lead alloy retained 36 pct elonga¬tion in a 30 mm-ga. length. Creep is also an important phenomenon

Jan 1, 1948

By Dr. O’Neil Thomas J., Donald W. Gentry

"We can easily represent things as we wish them to be..” -Aesop INTRODUCTION The first eight chapters of this book have primarily addressed the concepts and fundamentals associated with project valuation, particularly as they apply to mining-related projects. Specific emphasis was placed on the engineering and economic parameters and estimates necessary for quantifying line items in pro forma income statements and the subsequent calculation of net annual cash flows. Given these estimates of relative benefits, costs, and annual cash flows for a project, it then becomes necessary to convert these estimates into measures of relative desirability or attractiveness. The criteria and techniques typically utilized to determine project acceptability or desirability are, then, the topics of discussion in this chapter. Before proceeding it may be advantageous to put the problem of project evaluation into proper perspective by reiterating some of the fundamental concepts developed in Chapter 1. The basic premise set forth in this book is that the objective of the firm should be to maximize its value to its owners (stockholders' wealth). This value or wealth is represented by the market price of the firm's common stock; consequently, the primary objective of the firm can be restated as one of maximizing the value (price) of the firm's common stock in the marketplace over the long term. This price, in effect, is an indicator or index of the market's perception of the company's progress and a reflection of the investment, financing, and dividend decisions made by corporate management. These three major decisions are inter- related and jointly impact the market price of the firm's stock. Therefore, if the objective of maximizing the value of the firm to its stockholders is to be achieved, an optimal combination of the three decisions will be necessary. It is important to emphasize that maximizing stockholder wealth is not the same as profit maximization or even the maximization of earnings per share. Corporate managers making decisions based on the objectives of maximizing profits and/or earnings per share must recognize that these objectives do not consider: (I) the timing or duration of expected returns, (2) the business and financial risks of the promised earnings, or (3) the dividend policy of the firm. Obviously all of these factors are of concern to the company's stockholders and will have an effect on the market value or price of the firm's common stock. Maximizing market price per share, or wealth maximization, is therefore the appropriate corporate objective and

Jan 1, 1984

By R. F. Mehl, C. S. Barrett, A. H. Geisler

The complicated nature of the property changes that accompany age-hardening has made it necessary to reconsider and to elaborate the simple dispersion theory.l It has been apparent for some time that more direct information is needed concerning the atomic mechanism of precipitation from solid solution if the theory of age-hardening is to be developed past a purely qualitative stage.‡ Fortunately, in recent years information has been developed which allows us to trace in detail the lattice changes accompanying the process of precipitation from solid solution. This information relates chiefly to the sequence of the several stages of lattice alteration by which the matrix lattice is transformed to the equilibrium precipitate lattice, and permits reasonable inferences to he drawn concerning the states of internal strain that accompany these stages. This information is most complete for the solid solution of copper in aluminum. The equilibrium precipitate is the 0 phase, "CuAl2." This forms in plates, parallel to the {100} matrix planes. The atom pattern and atom spacing on the plane in 0 lying parallel to this plane are roughly similar to those opposite it in the matrix.3 The formation of 0, however, is preceded by the formation of a transition lattice 0': which again lies parallel to the matrix {100} plane, but in this case the matching of atom pattern and spacing across the matrix-precipitate interface is nearly periect; thus there is lattice coherency across the interface and the interface is a plane of separation in only a very limited sense.'8 Particles of 0' may be recognized microscopically and form a well-defined Wid-manstatten figure.* The 0' lattice is recognized by the occurrence of diffraction lines on powder photo-grams or of spots on Laue photograms which may be analyzed in the usual ways to determine the lattice type and the lattice spacings. Very recent research 6, 7, 1 has shown, however, that streaks occur on the Laue photogram at an earlier point in time during the aging process. These streaks have been attributed to a preferential clustering of copper atoms into small platelike elements of only a few atoms in thickness and a lew hundred atoms in diameter, probably of the composition of " CuA12," which may be designated as Guinier-Preston zones or aggregates.1 It is difficult if not impossible to determine the lattice type and lattice spacing in these aggregates. It is possible1 that these aggregates are in fact ?' in a high State of dispersion; the inclination to argue this is strong, as we shall see later. Never-

Jan 1, 1941

By G. E. Agar, P. L. De Bruyn

Flotation is an important example of a chemical process by which one solid may be separated from other solids in a mixture. In contrast to other chemical processes such as leaching and smelting, separation of solids by flotation is characterized by the establishment of contact among three phases. In froth flotation these three phases are the solid to be floated, an aqueous electrolyte solution, and a gas, usually air. The gaseous phase may be re- placed by an organic liquid phase or this organic liquid phase may be added deliberately as a fourth phase. To gain an understanding of the flotation sys- tem, it is therefore necessary to study the chemical and physical properties of surfaces and to establish the effect of changes in composition of the bulk phases on the nature of the three interfaces, solid-gas, solid-liquid and liquid- gas. With very few exceptions inorganic solids are completely wetted by the aqueous phase so that the first step in flotation is to replace partially the solid-liquid interface by a solid-gas interface. This displacement process is accomplished by the addition of suitable reagents to the aqueous phase. The resultant surface reaction leaves the solid surface with a hydrophobic film. Although the primary objective of these reagent additions is to alter the solid surface, chemical reactions between the added chemical species and those species derived from the dissolution of the solids are unavoidable. For a quantitative description of such reactions and for the determination of the feasibility of a proposed reaction, we rely on available thermodynamic data. The application of thermodynamic principles to flotation systems has contributed much to our understanding of flotation. The changes in thermodynamic properties such as free energy and chemical potential are accessible to experimental determination, and a knowledge of their magnitude allows us to develop and predict a chemical mechanism oy which a solid becomes floatable. In this chapter it will be assumed that the reader has a working knowledge of the general principles of thermodynamics and solution chemistry. A complete discussion of the physical chemistry of flotation must include a treatment of solubility relations, complex ionic equilibria, reaction potential, and the elements of electrochemistry, especially those dealing with reversible electrical cells. The principles related to all of these features of the flotation system will not be discussed in this chapter. The discussion will be concerned with the thermodynamics and electrochemistry of surfaces and the electrical double layer model of the interface.

Jan 1, 1962

By C. E. Brown, D. C. Helms, O. W. Shimer

The early history and progress of anthracite stripping, from the first known operation at Summit Hill in 1821 through 1917, was covered in 1917 in a paper by J. B. Warriner,1 then chief engineer, now president of the Lehigh Navigation Coal Co., and stripping methods between 1917 and 1931 were the subject of a paper in 1931 by H. H. Otto,2 of the Hudson Coal Company. . The present paper is confined to methods used today on pitching beds in the western middle and southern anthracite fields. The anthracite industry, not unlike other large industries, had been affected for more than a decade by the adverse economic conditions of the country. High development and operating costs and the competition of other fuels caused some collieries to be closed temporarily, while others were permanently abandoned. In order to obtain a larger tonnage at a lower development cost, a larger stripping program was put into effect by many companies. In 1932, stripping operations accounted for 3½ million tons, or 7 per cent of the total anthracite production of the year, and in the next 10 years this increased until more than double that amount, or over 14 per cent of the total production, was from stripping operations. These figures represent the total production of the entire anthracite region; unfortunately, the figures have not been separated from the different fields. There are some operations in the southern and middle western fields where the tonnage obtained from stripping amounts to more than 30 per cent of the total colliery production. Stripping operations on pitching beds present difficult problems. Owing to the various geological formations, a different situation is encountered in nearly every stripping pit; and because of the proximity of an overlying bed, it is very often necessary to load the entire overburden into trucks and haul it out of the pit to the dump area, although back filling and casting is done whenever possible. Beds in the areas described in this paper pitch from 20" to 90 and some are on the invert in many sharp folds and faults. Planning The more successful strippings have had adequate engineering analysis. Some work is being done without much preliminary planning, but many strippings would have failed completely if close supervision by the engineering department had not been . maintained. Locations of stripping areas are determined as follows: I. By constructing cross sections over the areas and drilling sufficient diamond-drill or well drill holes to study the strata and to determine the location, thickness

Jan 1, 1944