By A. R. Marder

Fe-C alloys have been investigated at temperatures below the eutectoid transformation to determine whether the superplasticity phenomenon exists for these materials. As a result of void formation at the carbide-ferrite interfaces that led to void coalescence and premature failure, the large elongations characteristic of superplustic matem'als did not develop. It had generally been assumed that the conditions for obtaining superplasticity include: a) T/Tm =0.5, b) a strain rate sensitivity of the flow stress that results in m s 0.3, and c) fine-grain structure. Although superphsticity was not observed in the alloys studied, stress-strain rate measurements indicated that an additional condition for the existence of superplasticitv in Fe-C allovs is that the fine-wain structure be equiaxed in agveement with previous results on Zn-Al al1oys. MANY investigations have been made on the hot deformation of iron-base alloys in order to obtain an understanding of the variables that may affect high-temperature strength and ductility.'-6 However, only a few papers have studied the effect of carbon content on the high-temperature properties of iron-base alloys. Peretayat'ko and Zaikov and Wallquist and carlen4 studied the effect of carbon on strength in the y temperature range, and recently Robbins, Shepard, and sherby6 studied the influence of carbon on the torsional behavior of iron in the a and cu-plus-cemen-tite temperature ranges. In addition to studying hot deformation behavior, current investigations have also been concerned with the phenomenon of superplasticity in nonferrous materials, and, in particular, ferrous alloys. Superplasticity is identified by the increased resistance to necking that results from a high strain rate sensitivity of the flow tress. ackofenr proposed the strain rate hardening coefficient m = d log a/d log e as a measure of strain rate sensitivity and showed that m must be "-0.3 for superplasticity to exist. In addition, a fine-grained microstrcture,- a eutectic or eutectoid ornosition,- and a test temperature in the creep range (TITm > 0.5)" have also been advanced as necessary conditions for superplasticity. Although many workers""23 investigated superplasticity associated with the allotropic transformation in iron and the eutectoid transformation in steel, and recently chadler " and orrison have studied superplasticity in the a - y phase region, no one has measured the superplastic effect in the a + cementite temperature region. Therefore, the purpose of this investiga- tion was to determine the effect of carbon content, microstructure, and test temperature on the strain rate sensitivity of Fe-C alloys at temperatures below the eulectoid transformation. EXPERIMENTAL PROCEDURE Fe-C alloys with carbon contents of 0.2, 0.4, 0.6, 0.8, and 1.0 wt pct were prepared as 100 lb 54 in. ingots by vacuum-induction melting. The compositions are listed in Table I. All the ingots were soaked at 2100°F for 2 hr prior to rolling to 4 in. plate. The minimum finishing temperature for rolling was 1800°F. The plate was sheared in 10-in. lengths and tensile bars were rough-machined prior to heat treatment. The samples were heat-treated according to the schedule in Table I1 in order to obtain a fine-grained microstructure consisting of finely dispersed carbides in a matrix of small ferrite grains. All the tensile specimens were heat-treated prior to finish machining, and tensile testing was accomplished on an Instron machine in conjunction with a clamshell furnace. The buttonhead specimen configuration is shown in Fig. 1. An inert atmosphere, helium, was maintained during testing with a steel tube shroud in a bell jar arrangement. Predried helium was continually purged over the buttonhead specimens and exhausted through ceramic fiber at the bottom of the tube to keep oxidation at a minimum and to prevent

Jan 1, 1970

By Charles L. Elliot

Data on mining applications of geophysical activity in the Free World in 1964 have been made available to SME again this year by the Society of Exploration Geophysicists. Worldwide data were collected as part of an annual service to the mining industry by the Committee for Geophysical Activity of SEG. Data are taken from 245 voluntary responses (53%) to questionnaires circulated to 463 company, government and university organizations engaged in mining geophysical operations and research all over the world. WORLD ACTIVITY Worldwide manpower utilization totalled 9323 professional man-months and $14.5 million was reported spent in mining geophysical activity in 1964. This is up from 9078 man-months and $12.6 million in 1963 and 8065 man-months and $12.8 million in 1962. Worldwide geophysical activity in terms of manpower utilization and expenditures is presented in the accompanying table.

Jan 9, 1965

By Paul M. Tyler

Higher freight rates and better methods of beneficiation now may make it more economical to open inferior deposits closer to a glass factory than to work higher-grade deposits farther away. Nature of impurities and special treatments as well as common practice of sulphuric acid leaching are described. HISTORICAL concepts of the economics of the glass-sand industry are changing rapidly. The greatly expanded demand for glass containers combined with higher freight rates on raw materials and manufactured products have induced a migration of glass factories toward densely populated centers and the creation of new standards of place value for substandard sand deposits. This migration has been facilitated by the construction of pipelines to bring cheaper natural gas and liquid fuel to large cities and may be further speeded by the adoption of modern mineral dressing methods to permit economical utilization of local raw materials. Our national resources of naturally high-grade silica sand are abundant, but most of the best deposits are situated so far from large centers of population that it now costs $3.00 to $5.00 a ton to carry the sand from the mine to the optimum site for a factory making beverage bottles, scientific and electrical glassware, and miscellaneous blown and pressed ware for local markets. It follows that on the basis of freight savings alone it may be economical to use material from inferior deposits closer to the factory even though the f.O.b. cost of mining and treatment may be much higher than at a higher grade deposit farther away. Particle-size distribution is a feature of glass-sand specifications. As long as glassmakers insisted upon having their sand principally coarser than 100-mesh, any material was automatically excluded from consideration that could not be purified without fine grinding or other drastic treatment which greatly reduces the size of the quartz grains. However, re- cent large-scale tests in Norway' showed that finely-crushed quartz used in a soda-lime-silica glass batch caused it to melt and become refined appreciably faster than when ordinary coarse (Belgian) sand was employed. Dust losses were negligible. Since the pre-war cost of sand was only 3 pct of the manufacturing cost of the glass, it was deemed economical to pay twice as much for crushed quartz because of the saving in wear and tear on the furnace walls. In the author's unverified opinion, sand ranging in size between 150 and 400-mesh would probably be superior to that in the more usual range of 20 to 100-mesh. Former objections to fine sand (other than dust) were doubtless fostered by the natural concentration of impurities in the finer sizes. Ordinarily the most objectionable, as well as the commonest, impurity from the standpoint of the manufacturer of any but the cheaper qualities of colored glass is iron. No natural sands are really pure silica. Even water-clear quartz crystals are likely to contain impurities in the form of solid solution as well as inclusions which cannot be eliminated except by chemical treatment that will break down the silica lattice. Pure white pegmatite quartz will usually analyze 0.01 pct or more of iron oxide, and ordinary vein quartz and the quartz grains in most

Jan 1, 1951

By Paul M. Tyler

Higher freight rates and better methods of beneficiation now may make it more economical to open inferior deposits closer to a glass factory than to work higher-grade deposits farther away. Nature of impurities and special treatments as well as common practice of sulphuric acid leaching are described. HISTORICAL concepts of the economics of the glass-sand industry are changing rapidly. The greatly expanded demand for glass containers combined with higher freight rates on raw materials and manufactured products have induced a migration of glass factories toward densely populated centers and the creation of new standards of place value for substandard sand deposits. This migration has been facilitated by the construction of pipelines to bring cheaper natural gas and liquid fuel to large cities and may be further speeded by the adoption of modern mineral dressing methods to permit economical utilization of local raw materials. Our national resources of naturally high-grade silica sand are abundant, but most of the best deposits are situated so far from large centers of population that it now costs $3.00 to $5.00 a ton to carry the sand from the mine to the optimum site for a factory making beverage bottles, scientific and electrical glassware, and miscellaneous blown and pressed ware for local markets. It follows that on the basis of freight savings alone it may be economical to use material from inferior deposits closer to the factory even though the f.O.b. cost of mining and treatment may be much higher than at a higher grade deposit farther away. Particle-size distribution is a feature of glass-sand specifications. As long as glassmakers insisted upon having their sand principally coarser than 100-mesh, any material was automatically excluded from consideration that could not be purified without fine grinding or other drastic treatment which greatly reduces the size of the quartz grains. However, re- cent large-scale tests in Norway' showed that finely-crushed quartz used in a soda-lime-silica glass batch caused it to melt and become refined appreciably faster than when ordinary coarse (Belgian) sand was employed. Dust losses were negligible. Since the pre-war cost of sand was only 3 pct of the manufacturing cost of the glass, it was deemed economical to pay twice as much for crushed quartz because of the saving in wear and tear on the furnace walls. In the author's unverified opinion, sand ranging in size between 150 and 400-mesh would probably be superior to that in the more usual range of 20 to 100-mesh. Former objections to fine sand (other than dust) were doubtless fostered by the natural concentration of impurities in the finer sizes. Ordinarily the most objectionable, as well as the commonest, impurity from the standpoint of the manufacturer of any but the cheaper qualities of colored glass is iron. No natural sands are really pure silica. Even water-clear quartz crystals are likely to contain impurities in the form of solid solution as well as inclusions which cannot be eliminated except by chemical treatment that will break down the silica lattice. Pure white pegmatite quartz will usually analyze 0.01 pct or more of iron oxide, and ordinary vein quartz and the quartz grains in most

Jan 1, 1951

By Richard E. McElvain, I. Cave

The selection of centrifugal pumps for mill discharge duty should be based on the total circuit concept. The practice of operating the mill circuit based on limitation of the pump can result in losses in one day which would offset the pump cost. Operating data from 25 grinding circuits have been reviewed and comparative results on added mill capacity have established advantages far beyond the less significant maintenance costs with increased circulating load and better cyclone operation. Mill discharge pumps should be selected on the following basis: i) Best available design for wear performance ii) Size to provide best economic life iii) Liner material best suited to circuit conditions Pump efficiency is a secondary consideration because power consumed by pumps is small compared to mill power input. Energy dissipated in mill pumps is contributing to comminution of ore.

Jan 1, 1982

By Harold R. Larson, John F. Elliott

The standard free energies of formation of several nzetallic sulfides have been measured by a reversible electromotive-force cell employing stabilized zir-conia as the electrolyte. The oxygen potential at the cathode was fixed by the use of pure oxygen gas at 1 atm. It was established at the anode by bringing to equilibrium the reaction between the sulfide and oxide species present. Thus, Gf: for the sulfide could be obtained from the cell potential and the standard free energies of formation of the oxides participating in the reaction. The results in calories per cam rnole for the temperature range 850" to 1100°C are: Use of the reversible electromotive-force cell having an oxide-ion electrolyte to obtain the standard free energies of formation of some of the more stable metallic sulfides offers a convenient experimental method that is very productive. It also avoids some of the problems inherent in the experimental methods' for such studies which rely on precise determination of gas compositions, particularly if these compositions lie near the limits of our capabilities for accurate chemical analyses. The reaction equilibrium between the lowest sulfide of a metal, SO2 at a fixed pressure, and an oxide of the metal has a characteristic oxygen potential. For example: and for metals whose lowest sulfide is much more stable than the oxides of the metal, the equivalent reaction might be:

Jan 1, 1968

By A. J. Lyon, J. B. Johnson, Samuel Daniels

The wrought alloys of aluminum with small amounts of copper and of magnesium have, with the development of the automotive and aircraft industries, sprung into prominence through the medium of duralumin; but the cast alloys remained in the background because their possibilities in the heat-treated condition were either not recognized or not fully investigated. In 1919, the Bureau of Standards published a preliminary survey1 of this field, which pointed out that, in general, the ultimate strength and the percentage of elongation of the alloys of aluminum with and without magnesium could be improved by so simple a treatment as heating at 932' F. (500" C.) for 2 hr., cooling in air, and aging at room temperature for several days. British investigators, too, working with chill-cast material, found that" considerable improvement in the mechanical properties of copper-aluminum alloys may be obtained from suitable heat treatment applied to castings."' Jeffries and Gibson8 made the first contribution to the literature dealing exclusively with the heat treatment of sand-cast aluminum-base alloys, describing the effect of small additions or of combinations of copper, magnesium, and iron on the response to a short heat treatment comprising heating at 932" F. in a nitrate bath for 1 hr., quenching in fish oil, and reheating at 300' F. for for 1 hr. Their results disclosed the facts that the ultimate strength and the percentage of elongation of sound alloys were usually, and quite uniformly, improved by heat treatment; that with the iron content ranging between 0.36 and 0.88 per cent. and the silicon content between 0.24 and 0.60 per cent. the effect of increasing the copper content (Tables 10

Jan 1, 1925

By H. Y. Hunsicker

A graphic method has been devised for three-di-mensional analysis of hot deformation and for correlating the amount and directionality of the deformation with resulting directional properties. Deformation is evaluated in terms of dimensional change ratios referred to three orthogonal axes. Since all combinations of the three ratios can be represented in a triangular coordinate field with logarithmic scales, a two-dimensional chart of extent of deformation and degree of asymetry is possible. The entire gamut of shape changes from upsetting through flat-rolling to rod-rolling is accommodated. The resulting coordinate system is a base upon which can be represented the properties of the wrought products measured in the directions of the axes employed fir evaluating the deformation. When property data are available for many types and amounts of deformation, a three-dimensional figure can be constructed, and the projection of this figure is referred to as a ''3d'' chart. Experience in using such charts to plan fabricating operations for a variety of thick-section forged and rolled products of heat-treated aluminum alloys has verified its practical value for optimizing directionality relationships. MechANICAL anisotropy of thick section products of heat-treatable aluminum alloys is recognized by producers and users of these products, and the extent of the directional differences is apparent in property tabulations included in handbooks, standards, and specifications.' Attention has also been directed to the existence of important directional differences in the resistance of these products to stress-corrosion cracking. Metallurgical structure factors responsible for these directional differences include, among other possibilities, shape and alignment of grains, voids and nonmetallic inclusions (when present), volume fraction and spatial distribution of secondary phase particles and solid-state precipitates, crystal-lographic textures, and Bauschinger effect. The contributions of the individual factors vary with alloy composition, heat-treated temper, type of working process (forging, rolling, extrusion), and the amount and directional nature of the deformation. In general, the cast ingot used as the starting material for producing these wrought products exhibits only a modest degree of directionality. A monotonic and continuous transition from this nearly isotropic state with progressive hot deformation would appear probable, assuming that the working temperature is sufficiently high to cause continuous dynamic recovery. Several years ago a project was undertaken to evaluate the effects of hot deformation and metallurgical structures on the directionality of thick wrought aluminum alloy products, and the method to be described was developed as an analytical tool in this investigation. DIRECTION NOMENCLATURE The nomenclature system adopted by industry for the three mutually perpendicular directions employed in testing aluminum alloy products includes four terms: "longitudinal", "transverse", "long transverse", and "short transverse". These terms are conventionally related to the external geometry of the product but also by implication to the deformation and resulting metallurgical structure. Occasions arise in which through use of unusual fabricating methods, intentional or otherwise, the structure does not have the usual relationship to external geometry or may be very complex because of inhomogeneity of deformation throughout the piece. The longitudinal direction is generally parallel to the primary rolling direction or to the direction of extrusion. In the case of forging, it is parallel to the direction of maximum extension (not maximum "working" or "flow", as frequently stated). The term transverse is applied to any direction perpendicular to the longitudinal direction in a product having symmetry about the longitudinal axis, and generally, although not always, the deformation to produce these forms is nearly symmetrical in the transverse plane. This term then may be applied to a round, square, hexagon, or other polygonal, symmetrical shape produced by extrusion or rolling or by forging, if produced by a simple, symmetrical drawing procedure. The type of microstructure generally associated

Jan 1, 1970

By J. E. Dutrizac, R. J. C. MacDonald, T. R. lngraham

When sintered disks of synthetic chalcopyrite (CuFeS2) were leached in acidified aqueous solutions of ferric sulfate, the following reaction stoichiometry was obtained: CuFeS2 + 2Fe2(SO4)3 = CuSO4 + 5FeSO4 + 2S Over the temperature range from 50º to 94ºC, the reaction displayed parabolic kinetics. The parabolic rate constant for the dissolution of copper is given by the equation: log.k(mg2/cm4-hr)= 11.850 - 3780/T The activation energy for the dissolution process is 17 ± 3 kcal per mole. The parabolic kinetics have been attributed to the progressive thickening of a sulfur film on the surface of the chalcopyrite. When the leaching solutions contain less than 0.01 molar Fe+3 , the Fe concentration influences the rate of leaching, probably through a mechanism involving the diffusion of ferric sulfate through the sulfur layer. At higher Fe+3 concentrations, the rate control in the leaching. reaction has been attributed to the diffusion of ferrous sulfate through the sulfur. The rate of reaction is insensitive to changes in acid concentration and in disk rotation speed. ThE reaction of acidic ferric sulfate solutions with various sulfide minerals is of practical interest for both bacterial and heap leaching. This leaching medium is generally used with low-grade ores that cannot be treated profitably by conventional means. In both bacterial leaching1-3 and heap leaching, the active agent for sulfide dissolution is ferric sulfate. Although the reactions of ferric sulfate with chalcocite, covellite, and bornite have been investigated,4*7 the kinetics of leaching chalcopyrite with ferric sulfate have not been thoroughly studied. This paper reports a study of that reaction. EXPERIMENTAL Reagent-grade sulfur was purified by the method of Bacon and FanelliB and then it was vacuum-distilled to remove any soluble magnesium salts that had been introduced during the purification procedure.9 From stoichiometric quantities of the purified sulfur and hydrogen-reduced electrolytic copper sheet (99.90 pct Cu), CuS was synthesized at 450°C in a vacuum-sealed, pyrex vessel. About 24 hr was required for the completion of the reaction. A similar procedure involving hydrogen-reduced iron wire (99.90 pct Fe) was used to synthesize FeS1.002. A 2-furnace arrangement was required. The iron was heated to 800°C while the sulfur was maintained at about 400°C. Although the reaction to consume the sulfur was rapid, the material required additional heating (1 week) in a sealed silica ampoule at 800°C before it was homogenized. X-ray powder diffraction analysis confirmed that the copper sulfide was covellite and that the iron sulfide was troilite. The composition of the iron mineral was confirmed by wet chemical analysis. The two sulfides were ground to minus 100 mesh, weighed in equimolar amounts, mixed thoroughly, and pressed into pellets at 80,000 psi. The pellets were vacuum-sealed in pyrex ampoules and then sintered for 3 days at 550°C after an initial heating at 450°C for a few hours. The pellets were then cooled, polished with 3/0 emery paper, rinsed in acetone, and stored. The material had the characteristic brassy color of chalcopyrite and was shown by X-ray diffraction to be CuFeS2. Microscopic examination of the polished surfaces revealed small inclusions of pyrite (approximately 0.5 vol pct) as the only impurity. The presence of small amounts of a second iron compound will not alter the amount of dissolved copper but might increase the amount of ferrous ion slightly. It was calculated that dissolution of all of the pyrite and 100 mg of Cu (a typical value) would change the expected ferrous concentration by only 4 pct. Microscopic examination of a pellet after leaching revealed that the pyrite was not preferentially solubilized; only those pyrite grains at the surface were attacked. Hence, the pyrite is unlikely to alter the rate of copper dissolution. The chalcopyrite disks were about 1.7 mm thick and 27 mm in diam. They were about 80 pct of theoretical density, and for this reason their true reaction area was somewhat larger than the 5.8 sq cm area presented by the polished face. The disks were cemented to lucite cylinders in such a way that only the polished face was exposed. The disks were then leached by methods previously described.6,7 RESULTS AND DISCUSSION Stoichiometry and Kinetics. The initial experiments were directed to the problem of resolving the stoichiometry of the leaching reaction. Disks of CuFeS2 were leached at 80°C for various periods of time in acidified ferric sulfate solutions that were protected from oxidation by a cover of flowing nitrogen. When the disks had been partly leached, they were removed, their soluble salts were washed out, and then they were treated with CS2 in a Soxhlet extraction apparatus. The ratio of elemental sulfur to dissolved copper thus obtained was approximately 2 to 1. After the extraction of elemental sulfur from the pellet, the residue consisted of unreacted chalcopyrite only. For runs in which an appreciable amount of copper was dissolved, the ratio of ferrous ion to cupric ion in the solution was

Jan 1, 1970

By Klaus Schwerdtfeger, Hans-Jürgen Engell

Activities of silicon in Ni-Si melts have beelz determined in the temperature range 1480° to 1610°C from electromotive-force measurements involving the cells The data obtained are used to derive the activities of nickel and the integal free energies of mixing. Entropies of mixing are calculated from the free energies of mixing as obtained in the present study and the heats of mixing as available in the literature. ACTIVITIES in Fe-Si and Co-Si melts have been determined recently by the authors&apos; using galvanic cells consisting of alloy, an oxygen electrode, and an oxide melt as electrolyte. The present paper deals with activities in Ni-Si melts as measured with the same technique. A schematic diagram of the cell is shown in Fig. 1. The alloy and the electrolyte consisting of CaO and SiO2 are contained together in a silica-glass crucible. During the experiment the silica glass crystallizes to cristobalite on the surface of the crucible. Nickel contents of the electrolyte are very small (<0.1 pct as checked with chemical analysis), because of the noble character of nickel in comparison with silicon. A tapered silica tube is connected to the crucible through which a platinum or molybdenum wire is inserted, as shown in Fig. 1. A platinum tube reaches the surface of the CaO-SiO2 electrolyte from above. The platinum tube is provided with four holes on its side, through which oxygen of 1 atm pressure is blown over the electrolyte. The cell reaction is given by the equation Si(metal) + O2(gas) = SiO2(electrolyte) [3] and the galvanic electromotive force of the cell is given by the formula

Jan 1, 1965

By A. T. Yu

As the first loads of Noamundi iron ore rumbled into the new 54-in. Gyratory Crusher on March 30, 1968, one of India&apos;s largest and most modern iron ore processing complexes began operations. The completion of the $13 million mining and processing complex brought to a successful conclusion the second chapter of a phased expansion program initiated in 1958 by India&apos;s gigantic Tata Iron and Steel Co. The completed complex will yield annually 2.5 million tons of washed, sized ore and sinter fines destined for Tata&apos;s furnaces at Jamshedpur. Hewitt-Robins Div. of Litton Industries was awarded the turnkey project on the basis of world- wide competitive bids. Eighty miles southwest of the city of Jamshedpur, Noamundi lies on an approximate geographic grid of 22º-5&apos; latitude north and 85º-30&apos; longitude east. The mine is approximately 600 ft above sea level.

Jan 11, 1968

By E. J. MCOAUSTLAND

THE behavior of steel after overstrain and at moderate temperatures is fairly well known. It has been made the subject of much investigation, and our knowledge is clear and definite on many points. The ultimate raising of the elastic limit, after moderate overstrain, and the consequent lowering of the ductility, seem to be well established. It is also well understood that the immediate effect of overstrain is to lower the elastic limit, possibly to zero, but that if not interfered with, this limit will subsequently rise higher than before. The "tests after moderate temperature," reported in this paper, were undertaken to verify the above statements for the particular steel under investigation, and also to determine, if possible, the total time required for complete recovery from this state of overstrain. The behavior of overstrained steel at temperatures at or below 32° F. is not so well known. Tests made by Prof E. G. Coker, at McGill University,&apos; show that steel, overstrained and subjected to cold, will remain in a state of overstrain for an indefinite period. I am not aware of any other published results of tests along this particular line. The effect of time and temperature on the recovery of steel from overstrain was made in 1902-3 the subject of sortie investigation in the laboratories of the College of Civil Engineering of Cornell University. A general plan was outlined in connection with the regular courses of instruction in testing of materials; but the press of routine work and the demands of the schedules on the time of the students were so great as to presage long delay in the completion of the work. Not much had been accomplished up to 1904-05, when Messrs. E. C.

May 1, 1906

By L. O. Howard

THE practice of using acid-lined converters at the plant of the Old Dominion Copper Mining & Smelting Co. was discontinued early in January, 1913, and they were replaced by basic-lined converters. The new equipment consists of one electrically operated 12-ft. upright converter stand and two basic-lined shells for same. These shells are provided with twenty-four 1 1/4-in. tuyères. The mouths are 5 ft. in diameter. Owing to the fact that there is no bedding system or other large storage capacity between the mine and the smelter, the furnaces must handle as fast as produced ore and concentrates, which may vary considerably from day to day, both in tonnage and copper content. Consequently the converter is often crowded to its utmost capacity by the frequent fluctuations in the daily matte supply. From the foregoing, it will be seen that in no way can the converter be favored by running light charges or by transferring to it from other stands in operation. Neither can it regularly be allowed to cool between blows, and only occasionally can it be run at as low a temperature as might be wished. No copper precipitate or other foreign material high in copper is available to help out the tonnage. Repairs and alterations or the removal of defective tuyères must wait until such time as a slight falling off in the matte supply-allows the converting operations to ease up. These variable conditions all combine to interfere with the systematic operating of the converter.

Jan 7, 1914

(Under this heading will be published notes sent to the Secretary of the Institute by members or other persons introduced by members.) Member, graduate Columbia School of Mines, age 35, married, best of health, dependable, desires position as manager or scout for reliable interests. Experience covers responsible positions incident to the mining and milling of gold-silver, copper, lead, and zinc ores, and the examination of base and rare-metal deposits in United States and Mexico. Salary $3600. Available April 1. No. 453. Member, mining engineer, technical training, age 32, assayer, engineer and superintendent of porphyry copper development, churn drilling and shaft sinking. Examination of prospects and development of gold prospects. Considerable flotation experience. No. 454. Young Columbia graduate, conscientious worker, with experience in inorganic analysis, surveying, draughting, and wit. post-graduate training in geology, desires position wt. prospects. Minimum salary considered, $130 in U. S. and $150 in Mexico. At present employed. Draft exempt. No. 455.

Jan 5, 1918

By D. H. Gurinsky, D. G. Schweitzer

The empirical equilibrium constantsd the heat of reaction for the reduction have been determined from 300° to 500°C. The mechanisms of the oxidation of uranium and magnesium from dilute bismuth solutions have been investigated. The kinetics of some of the reactions were affected by air adsorbed on the uranium oxides. THE Liquid Metal Fuel Reactor studied at Brook-haven National Laboratory uses a solution of uranium in bismuth as the fuel. Corrosion and stability problems require that the fuel solution contain corrosion inhibitors and deoxidants. Of the additives tested, magnesium has been found to be the best deoxidant and zirconium the best corrosion inhibitor in bismuth. Some experiments1 indicate that magnesium may play a secondary role in increasing the effectiveness of zirconium in inhibiting corrosion. The work reported here was intended to determine the relative concentrations of Mg and U required to prevent oxidation of the uranium fuel in the event of an air leak. In addition, an attempt was made to identify some of the mechanisms of the oxidation and reduction reactions occurring in the liquid bismuth solutions. EXPERIMENTAL Apparatus and Procedure—The equipment shown in Fig. 1 was designed so that the reaction kinetics could be studied as functions of temperature, melt composition, pressure, and flow rate. At the start of a run, the 10-liter bell jar (F) is removed by opening the bottom Dresser fitting (L), and the bismuth and additives are placed in a pyrex crystallizing dish (I). The bell jar is replaced, the system is evacuated to 10-5 to 10-6 mm Hg and then the heater (J) is turned on. When the selected temperature is reached, the oxidizing gas is admitted to the system to the desired pressure as read on the manometer (D). Gas is introduced through the slide tube (Q) which has a pyrex frit (R) sealed to its bottom. Stirring is accomplished by immersing the end of the tube in the melt. To maintain a constant pressure under flow the input and evacuation rates must be equalized. To obtain this condition stopcock (C) is closed and flowmeters (B) are matched. The reaction is "stopped" by closing the inlet flowmeter and quickly evacuating the system. To obtain a liquid metal sample, the system is evacuated with the sampler positioned near the surface of the liquid. The sampler, Fig. 2, is then immersed until its thermocouple reading matches thermocouple (G) Fig. 1. The system is then pressurized with helium which forces the solution through the frit. Twenty to 30 min elapsed between the time the system was evacuated and sampled. During evacuation and pressurization of the system, the temperature variations did not exceed ± 5°C. While bubbling occurred the temperature remained constant to within 1/2 oC. The volume of the equipment was determined by adding a known volume of air at atmospheric pressure to the evacuated system and noting the resulting pressure.

Jan 1, 1962

By R. J. Quigg, G. S. Doble

Commercial stress -relieved TD Nickel bar was shown to retain room- and elevated-temperature tensile strength after exposure up to 2501°F. Cold swaging increased both room -temperature and 2000°F tensile strength. After annealing at 2500°F the strengthening due to swaging was retained at 2000°F hilt eliminated at room temperature. Annealing produced changes in hardness and X-ray half peak width indicating the presence of recovery processes as 1071° as 1000°F but no recrystallization of swaged material was noted at any temperature. In contrast to swaging, rolling induced a recrystal-lized structure after annealing. The tensile strength of this recrystallized structure was comparable to the cold-worked condition. High-temperature tensile properties of as -received bar were highly anisotropic with the transverse tensile strength being one fifth the longitudinal value. The aniso-/ropy is affected by working direction and may he partially reversed by changing the direction of metal flow. The divergence in tensile strength, beginning above 550°F or- approximate one third the absolute melting point, is strain-rate dependent. T D Nickel is a commercial dispersion-hardened alloy containing 2 vol pct thoria. The dispersion, consisting of spherical particles 0.030 to 0.050 in diameter with an interparticle spacing of less than 1 is reported to maintain stable properties up to 2400°F.1 This stability of second phase results in maintenance of elevated-temperature strength at higher temperatures and longer times than normal nickel-base superalloys.2 The purpose of this paper is to describe the effect of various mechanical working operations on the strength and microstructural stability of TD Nickel bar. MATERIAL AND PROCEDURES All material used in this study was commercial TD Nickel bar. This material is produced by a chemical process which results in a nickel powder containing a dispersion of thoria particles. The powder is then pressed, sintered, extruded, and subsequently worked to bar stock. Three starting materials from three separate lots were used: as-extruded bar. 1-in.-diam stress-relieved bar, and 1/2-in.-diam stress-relieved bar. Since TD Nickel bar stock is cold-worked without a recrystalliza-tion anneal, the accumulated deformation or degree of cold work in these materials increases as the bar diameter decreases. Some of the 1/2-in.-diam bar was swaged to 1/4 in. diameter at room temperature in order to produce an as-worked condition for comparison with the stress-relieved stock. Tensile testing was performed on an Instron Tensile Tester at a constant crosshead speed of 0.020 in. per min. The 0.2 pct offset yield strength was measured from the load-crosshead movement plot. Specimen gage dimensions were 0.080 in. in diameter by 0.40 in. in length, producing a strain rate of approximately 0.050 min-1. Specimens were tested in air and heated within a resistance-wound furnace controlled to ±5°F. A 15-min soak at temperature was employed before testing. Samples were heat-treated in air and specimens machined after exposure with sufficient material removed to eliminate any surface contamination. X-ray line breadth was determined from a diffractometer scan of a transverse face of a bar using copper K, radiation. Metallographic preparation utilized standard mechanical polishing with Carapella&apos;s etch. Specimens for electron microscopy were electropolished in a 1:7 sulfuric/methaol solution and chromium-shadowed collodion replicas prepared. RESULTS AND DISCUSSION I) Effect of Elevated-Temperature Exposure on the properties of TD Nickel. The effect of various elevated-temperature exposures on the room-temperature tensile strength of TD Nickel is shown in Table I. In the unexposed condition the tensile strength, reduction in area, and hardness all increase with increasing accumulated deformation while the elongation decreases. After exposure at 2500°F the strength of all three materials decreases to about 65,000 psi and the elongations increase slightly. The apparent increase in strength of the 1-in. bar after a 2000°F treatment is probably experimental scatter. These results indicate that the room-temperature strengthening due to additional deformation is annealed out upon elevated-temperature exposure. In contrast to the room-temperature data, the 2000°F tensile strengths increase in order of increasing deformation even after exposure. Although some loss of strength occurs after exposure, much of the effect of working is still maintained at 2000°F. The room-temperature hardness after various

Jan 1, 1965

By Stanley C. Herold

TWENTY-FIVE years ago no distinction was made between water wells and oil wells except in the nature of the fluid produced. Water wells usually showed no decline in their rate of production; when oil wells showed decline something in the manner of handling them was considered wrong. Both water and oil were believed to be subject to the same physical laws in their underground movement toward the wells. Today a sharp distinction is made between them. Whereas water exists alone in the porous formations at depth, oil is usually accompanied by gas. This mixture does not behave as a liquid alone. It is a frothy, seething mass of foam which approaches and enters the wells. Different physical laws come into play. Twenty-five years ago attention was directed entirely to the well itself; today the well is accepted as a mere hole in the ground, a hole to be equipped properly for efficient service, yet without any value whatever unless it is backed up by a sufficiently prolific reservoir. Then, we were concerned with wells alone, 3000 ft. in depth; now commercial wells and their reservoirs are 10.000 ft. deep. Petroleum engineering concepts have necessarily therefore undergone a change in this last quarter century. What are they today?

Jan 1, 1937

By AIME AIME

In the present number of Mining and Metallurgy, issued on the fiftieth anniversary of the founding of the Institute, it appears appropriate to chronicle a few of the interesting incidents respecting its early life. We are fortunate in being able to cull the following notes from unpublished manuscripts of Doctor Raymond and Doctor Drinker, than whom no other members could have written with greater exactness and fidelity. THE seventh decade of the 19th century may be said to have marked an. era in the history of the world. Industrially and .commercially it was marked by the wide application and utilization of discoveries already made, which came to their full effect at this period in steamships, railways, telegraph and cable lines; the standardization of parts in machines, from watches to locomotives; the use of &apos;dynamite, antiseptic surgery, the open-hearth steel process, the compressed-air rock-drill, the electric generator, and the Gatling gun. Through the opening of the Suez canal in 1870 the maritime trade of the world was revolutionized, sailing vessels were supplanted by steamers, while ocean cables and ocean "tramps" brought about far more rapid movement of commerce than had before been experienced. Politically, this period was marked by the sudden birth of the German empire and the beginning of that intensive internal development of the national resources of that empire in preparation for colonial extension and war, the amazing result of which has been made evident by the recent world conflict. In the United States, the significance of this decade was peculiarly important. The re-admission to the union of Virginia, Mississippi, Texas and Georgia in

Jan 1, 1921

By B. D. Lichter

In a previous paper, Oelsen, Schuermann, and Hey-nertl pointed out the possibility of obtaining complete thermodynamic functions for alloy systems from calorimetric measurements alone. Specifically, if the heat content of a heterogeneous, multicomponent system is known as a function of temperature and composition, then it is possible to derive the heats, entropies, and free energies of formation of liquid phases and of solid intermediate phases of fixed composition. The authors present equations and graphical techniques applicable to eutectic systems and systems with intermediate phases without solid solubility at lower temperatures. eijering has considered possible extension of the treatment to systems with complete solid-state miscibility at lower temperatures; however, experimental difficulties practically restrict the method to systems with very limited miscibility in the solid state. The purpose of this note is to present an alternative derivation of the heats and entropies of formation of liquid phases and of solid intermediate phases from heat-content measurements alone. Fig. 1 shows three types of phase diagram to which the analysis may be applied. If the heat content is determined as a function of composition x, at temperature T, we have quite generally and the heat of mixing of the liquid is obtained directly from heat-content measurements. If the temperature T lies in a two-phase region (solid-liquid) then

Jan 1, 1967

By George C. Bateman

I HAVE been introduced in the dual capacity of president of the Canadian Institute and Metals Controller for Canada. There are three particular points of similarity between these two positions. They are both temporary ; they both have to do with the mining industry ; and by a peculiar coincidence they both pay me exactly the same salary. It is difficult to appreciate the background of our present situation without knowing the really tremendous changes that have taken place since the last war. I sometimes think that even among ourselves we are likely to forget the extent to which our great mining industry has been expanded. In 1914 Canada&apos;s gold production amounted to only $16,000,000 and the suggestion was seriously ad¬vanced in Ottawa that the gold mines should be allowed to close down so that their men might be used in more important work. Today with a production at the rate of over $200,000,000 a year no one in Canada would venture such a suggestion because the output of our gold mines is the greatest single factor in producing dollar exchange, badly needed for the purchase of munitions and to maintain Canada&apos;s unbroken record of always meeting its obligations. Even with the severe restrictions now in effect against the importation of nonessentials, our imports for war purposes from the United States are resulting in the biggest adverse trade balance in our history. With us, gold mining ranks as an essential industry.

Jan 1, 1941