By H. David Swain

On Bougainville Island in Papua New Guinea, Bougainville Copper Ltd. (BCL) has successfully applied electronic data processing (EDP) techniques to pit operations and mine planning. Though the EDP program is not complete, BCL has realized significant improvements in short and long range mine planning, and equipment and manpower utilization. About 80% of BCL's 4000 employees are Papua New Guinea nationals, and most have little education or training. The operational characteristics of the computer equipment, however, have been quickly adapted by users with low educational standards.

Jan 3, 1979

By Philip D. Wilson

OF all the metals in the war program the demand for and the production of magnesium have increased percentagewise the most. In the prewar year 1939 the production was 3350 tons. The war program, twice expanded, now provides for nearly one hundred times that amount annually. The goal announced by the War Production Board in February 1942 was 362,500 tons per year. Be- cause of the development during the year of satisfactory types of incendiary bombs other than magnesium this objective has been somewhat reduced but the capacity of the plants already built or under construction will be huge. The Aluminum and Magnesium Division of the W.P.B. has had the responsibility of planning and implementing this expansion and of providing fabricating facilities as well for this greatly increased tonnage of magnesium ingot.

Jan 1, 1943

By J. T. Dewan

An experimental setup is described whereby the responses of Neutron logging instruments have been determined opposite formations of different porosities and under various borehole conditions. The results of these tests are presented in several charts which show how the Neutron log is affected by the following factors: hole diameter, casing, cement, salinity and weight of drilling mud, and position of logging tool with respect to the wall of the hole. The responses in the case of empty holes are also shown. A chart is furthermore presented which shows the shapes of the Neutron log, as a function of logging speed and time constant, at the boundaries between two formations with different porosities. These were derived mathematically using as a basis laboratory determination of the shape of the curve under static conditions, i.e. at very low logging speed. Corrections for the readings made opposite thin beds are given by these computations. The correction is found negligible under usual logging conditions for beds thicker than about 4 ft. INTRODUCTION The Neutron log is used in borehole surveys both for the delineation of porous formations and for the quantitative estimation of their porosities.1,2,3,4,5 It is common practice to calibrate the response of the Neutron log in terms of porosity values for each given geological unit by means of empirical comparisons between the deflections of the neutron curve and the porosity values given by the core analysis in a sufficient number of wells. Usually, the plots of the porosity values vs Neutron log deflections show a definite trend. It is therefore possible to trace an average line across the plotted points. This average line constitutes a calibration curve which can be used to evaluate the porosities from the Neutron logs in the other wells drilled in the same region. Futhermore, when the porosity values are plotted on a logarithmic scale and the Neutron log deflections on a linear scale, the calibration curve is practically a straight line. Accordingly the calibration curves are often determined by simply tracing a straight line between two points corresponding to two widely different porosities. Different choices are made for these two points, depending on local conditions. For example, one point will be defined by plotting the deflection of the Neutron curve opposite a formation known to be very tight, for which an average porosity value of 1 or 2 per cent is assumed. The other point may correspond to shale sections, to which a porosity of around 40 per cent is ascribed. The information provided by the eletrical logs — in particular the Laterolog, Limestone log or Micro-Latero-log — is also very often a help in the calibration of the Neutron logs. Empirical approaches such as these make possible the derivation of fairly reliable porosity values from the Neutron logs in many cases, at least in open holes and in essentially clean formations. There are, however, several causes of uncertainty which may sometimes entail appreciable errors. On the one hand, the Neutron log readings are influenced by the borehole conditions: hole diameter, presence or absence of casing and cement, presence or absence of drilling mud, characteristics of the mud, and position of the logging instrument with respect to the wall of the hole. The amplitudes of the curves opposite thin beds are furthermore atfected by the bed thickness,

Jan 1, 1957

By Klaus Schwerdtfeger

The rules of solution of oxygen from H2O-H2-He gas and of nitrogen from N2-H2 gas in shallow melts of liquid iron were measured at 1610o and 1600o C, respectiuely. Concentration profiles were detemined in the liquid iron. Tire rate data indicate that the solution process is controlled by diffusion in the iron melt. The diffusivities for oxygen and nitrogen in liquid iron, as calculated from the present data, are DFe-o = (12 ± 3) < 10-5 sq cm per sec and DFe-N = 11 ± 2) X 10-5 sq cm per sec at the temperatures employed. AN attempt was made by Shurygin and Kryukl to measure the diffusivity of oxygen in liquid iron. In their experiments a silica disc was rotated in liquid iron containing oxygen, and the rate of formation of liquid iron silicate was measured. Assuming that the rate of dissolution of silica is controlled by diffusion of oxygen in the iron, the oxygen diffusivity was computed from the rate data giving Dfe-0 = 6.1 X 5 sq cm per sec at 1600°C. Although this value seems to be of the right order of magnitude, there is no proof of the correctness of the assumptions involved in the interpretation of these rate data. The oxygen concentration in the iron at the iron-iron silicate interface was taken to be that in equilibrium with the silica-saturated silicate melt. That is, it was assumed that no concentration gradient existed in the liquid silicate. This is a questionable assumption, unless it is proved that the thickness of the silicate layer is very much smaller than that of the diffusion boundary layer in the iron. Furthermore, Shurygin et al.1 used the Levich equation2 to interpret their rate data. This equation was derived for mass transfer between a solid disc and a single-phase liquid. The hydrodynamic and diffusion boundary layers in the iron stirred by a disc, via coupling of the silicate melt, may be appreciably different from those predicted by Levich&apos;s derivations. In the present work the diffusivities of oxygen and nitrogen in liquid iron were measured at 1610" and 1600oC, respectively. EXPERIMENTAL METHOD Iron melts contained in high-purity gas-tight alumina crucibles were reacted with H2O-H2-He gas for the determination of the oxygen diffusivity and with N2-H2 gas for the determination of nitrogen diffusivity. At the end of the reaction period, the samples were quenched in a cold H2-He gas stream at the top of the furnace. Oxygen or nitrogen contents in the iron were determined by chemical analysis. Two different types of diffusion experiments were perforxed. To determine concentration profiles, a few rate measurements were made using 4-cm-deep melts. The solidified samples were sliced into discs and each disc was analyzed for oxygen or nitrogen. In another series of experiments, oxygen or nitrogen was diffused into shallow melts (about 0.5 to 1 cm in depth) and the total sample was analyzed to obtain an average concentration of the diffusate. In most experiments, 4- to 5-mm-ID alumina crucibles were used. Some experiments were also made in smaller (3 mm) and larger (7 mm) diam crucibles. This variation in diameter caused no difference in the reaction rate, within the limits of experimental uncertainty. To promote the establishment of a stable density profile in the melt, all the samples were suspended in the lower end of the hot zone so that the top of the melt was hotter by a few degrees. Molybdenum wire resistance heating was used. The reaction tube of the furnace was a gas-tight recrystal-lized alumina tube. In most experiments the furnace was heated by an ac power supply. To check the possibility of inductive stirring, some experiments were carried out in a dc operated furnace, with essentially the same results. The temperature of the furnace was controlled automatically in the usual manner. The temperature was measured with a Pt/Pt-10 pet Rh thermocouple and is estimated to be accurate within ±5°C. The iron used was prepared by melting and vacuum-carbon deoxidizing electrolytic "Plastiron" in a zir-conia crucible. The main impurities are: Si 0.004 pct P, S <0.002 pct Cr 0.005 pct N 0.001 pct Zr 0.002 pct O 0.003 pct Mn 0.004 pct C 0.002 pct The gas composition was controlled by constant pressure head capillary flowmeters. Oxygen was removed from the gas mixture by passing it through columns of platinized asbestos (450°C) and anhydrone. Selected H2O contents were obtained by passing the purified gas through oxalic acid dihydrate-anhydrous oxalic acid mixtures held at constant temperature in a water bath. Water vapor pressure data for the oxalic acid dihydrate-anhydrous oxalic acid equilibrium were taken from the 1iterature.3 The flow rate used was about 1.5 liters per min. The whole system was checked for tightness at regular intervals.

Jan 1, 1968

By Anne Nicholson Hird, H. A. Schwartz

Of the outstanding investigators of the system iron-carbon-silicon Gontermann,1 Charpy and Cornu-Thenard,= and Honda,3 only the first touched on the chemical composition of the solid and liquid phases in equilibrium with one another. He concluded that his data did not permit a decision as to which of an indefinitely large number of pairs of compositions of liquid and solid would be found in any given case. If through the three dimensional equilibrium diagram of the iron-carbon-silicon system an isothermal plane is passed in the region of partial solidification, two lines of intersection with the liquidus and solidus, respectively, are obtained, also a point marking the alloys&apos; composition. If, in this plane, a straight line is drawn through the point, and intersecting both the liquidus and solidus isothermals, the two intersections mark a liquid and a solid alloy that may be chemically in equilibrium at the chosen temperature. From thermal data alone, Gontermann could not assign any particular direction to the line and, hence, could not determine which pair of conjugate points to choose, A separation of the liquid and solid for analysis, obviously, presents grave experimental difficulties. During the solidification of white cast iron, austenite of progressively higher carbon will separate as the temperature falls and cementite will appear suddenly at the freezing point of the eutectic. This cementite will be accompanied by a corresponding amount of austenite which, for our purpose, will be chemically inseparable from the primary austenite. We have attempted to decide on the conditions at the end of the freezing by a chemical separation applied to the solid metal.

Jan 1, 1925

By Cyril Wells, Robert F. Mehl

The purpose of this investigation was to prepare high-purity iron-carbon alloys, to determine as precisely as possible the A3(GOS), the Acm(SE), and the A1(PSK) transformation temperatures in the meta-stable iron-iron carbide system (up to 1.4 per cent C), and to study the influence of carefully controlled and constant rates of heating and cooling (1/8 to 2o C. per minute) upon the transformation temperature and upon the resulting microstructure. Apart from the general metallurgical importance attending the completion of such a task, it will be noted that highly precise transformation temperatures are of interest and importance in the thermodynamic study of this system1. Several determinations of the iron-iron carbide diagram have been made2. These suffer generally from the low purity of the alloys used, and from the application of methods of investigation of low sensitivity. Attempts to compare and weight the many data available in an effort to construct as accurate a diagram as possible have, in the main, been unsuccessful. In general, the wide differences in the results of different workers, the lack of complete analytical data, the omission of important details relating to the heat-treatment of the alloys, and the meager description of the methods of investigation applied, render such a process of averaging nearly meaningless. It may be seen from the summaries by Epstein2 and Körber and Oelsenl that variations as great as 30&apos; C. exist in the reported data on the A3 temperatures in iron-carbon alloys. Fortunately, the Aa temperature in pure iron is now known to be 910" C. ± 1° C.3 The best recent work on iron-carbon alloys is that of Esser4 on hypoeutectoid steels and that of Sato5 on both hypoeutectoid and hyper-eutectoid steels. Esser made a dilatometric and magnetic study of iron and iron-carbon alloys containing 0.06 to 0.86 per cent C, for which a high purity is claimed. Presumably the electrolytic iron was reasonably pure, but the alloys contained considerable impurities, on the average totaling 0.35 per

Jan 1, 1937

By R. W. Heckel, R. L. DeGregorio

The DeHoff method of determining the size distribution of ellipsoid-shaped, second-phase particles has been applied to the spheroidization of cementite in a eutectoid steel. The surface area of Precipitates determined from the various size fractions in the distribution was correlated with surface-area measurements based on the number of intersected interfaces on a random lest line. The precipitate particles were found to be oblate ellipsoids with an axial ratio of about 0.90. The size distributions were found to be log-normal. A method is proposed whereby the shrinkage of small particles and growth of large ones can be determined from the experimental data. The experimental data are compared to previously proposed mathematical models describing diffusion-controlled kinetics and various types of interface-controlled kinetics. The experimental growth and shrinkage rates are considerably slower than those predicted by diffusion-controlled kinetics. The best fit is obtained for a model describing interface-controlled kinetics limited by the rate of formation of cementite at the growing interfaces where the interfacial reaction rate is proportional to the solute thermodynamic activity gradient across the surface. THE subject of spheroidization of second-phase particles has been considered previously by other investigators. Livingston1 has studied the precipitation of the cobalt-rich phase from copper alloys containing 0.7 to 3.2 wt pet Co. His results indicate that the average particle size increases as the cube root of the heat treatment time in accord with diffusion-controlled kinetics.&apos;-&apos; Komatsu and rant&apos; in their studies of the growth of SiO2 in a dispersion-strengthened copper-silica alloy found that the initial growth of SiO2 proceeded by diffusion-controlled growth and later stages were limited by interface-controlled growth. The values of the activation energy obtained for the interface- controlled process led them to the conclusion that the process was limited by the dissociation of SiO2 at the shrinking interface. The transition from diffusion-controlled growth to interface-controlled growth was characterized by a particle size which varied with the heat-treatment temperature. It is also interesting to note that the particle-size distribution as found by Komatsu and Grant exhibits log-normal behavior when replotted on log-probability coordinates. Dromsky, Lenel, and Ansell9 have observed the growth of Al2O3 particles having a mean free path of about 1.5 to 13 µ. Their photomicrographs indicate that the Al2O3 particle sizes were larger than those observed by Komatsu and Grant. Dromsky, Lenel, and Ansell concluded that the Al2O3 coarsened by an interface-controlled growth mechanism limited by the solution of A12O3 at the shrinking interfaces. Bannyh, Modin, and Modin10 have studied the spheroidization of a eutectoid steel (0.83 wt pet C). Their spheroidization (tempering) treatments were carried out in the range from 210o to 700°C for times between 1.5 sec and 20 hr. Measurements of mean particle size as a function of time indicated a cube root of time dependence of size at 700°C, in agreement with previous analyses of diffusion-controlled kinetics.2°7 At lower temperatures, the time dependence was less than the one-third power. It is important to note that, although mathematical models of growth* considering particle-size distribution have been available, measurements of only mean particle size have been carried out. DeHoff11 has presented a quantitative metallography technique which is applicable to the determination of the size distribution of ellipsoids of constant shape. This method is applicable to both oblate and prolate ellipsoids of all ratios of minor to major axis and is based upon an extension of Saltykov&apos;s analysis12 of the distribution of spheres of varying size. DeHoff&apos;s analysis is based upon measurements of the minor axis of the particles on a random plane of polish in a unit area. This method provides a measure of the number of ellipsoids in various size ranges per unit area. As pointed out by DeHoff, such measurements may be used to obtain surface area and total precipitate volume data. Thus, the accuracy of the distribution analysis may be checked by comparison of the surface and volume

Jan 1, 1965

By C. G. Black

The purpose of this paper is to present data obtained from an investigation conducted on the grindability of coal by the American Society for Testing Materials Tentative Standard ball-mill method. This investigation has been conducted over a period of a year, during which time several hundred tests were run on a wide selection of different coals coming from Pennsylvania, Ohio, West Virginia and Kentucky. The data herewith presented tend to show that the tentative standard ball-mill method might give results that are misleading and that a volume measure might be more indicative of the true grindability of materials of varying specific gravity. A means whereby the time element might be reduced has been studied and other phases of this work such as preparation of samples, mechanical screening, reporting results and duplicating tests have been investigated. It is hoped that all criticism offered in this paper will be taken as constructive, with the purpose ill mind of perfecting the method now tentative to show the true conditions 2nd of making optional the manner in which certain parts of the test might be conducted to meet diversified laboratory conditions. Weight and Volume The results of grindability on extraneous material from the coal scam obtained with the present tentative standard ball mill method indicate easier grinding of these materials as compared to most coals. Varying amounts of these impurities in the coal therefore may cause a raising of the grindability index and may lead to the erroneous conclusion that coals containing large amounts of these foreign materials are easier to grind. For a true comparison of grindability, it would seem necessary to grind to the same particle weight. If material were sized in a commercial mill by means of an air current set at a velocity to remove 1.60 sp. gr. float coal ground to 80 per cent minus 200 mesh, any 1.60 sink particles would be left behind, and in order to remove this 1.60 sink material by the same current it would be necessary to grind finer and produce a

Jan 1, 1936

By C. G. Black

The purpose of this paper is to present data obtained from an investigation conducted on the grindability of coal by the American Society for Testing Materials Tentative Standard ball-mill method. This investigation has been conducted over a period of a year, during which time several hundred tests were run on a wide selection of different coals coming from Pennsylvania, Ohio, West Virginia and Kentucky. The data herewith presented tend to show that the tentative standard ball-mill method might give results that are misleading and that a volume measure might be more indicative of the true grindability of materials of varying specific gravity. A means whereby the time element might be reduced has been studied and other phases of this work such as preparation of samples, mechanical screening, reporting results and duplicating tests have been investigated. It is hoped that all criticism offered in this paper will be taken as constructive, with the purpose ill mind of perfecting the method now tentative to show the true conditions 2nd of making optional the manner in which certain parts of the test might be conducted to meet diversified laboratory conditions. Weight and Volume The results of grindability on extraneous material from the coal scam obtained with the present tentative standard ball mill method indicate easier grinding of these materials as compared to most coals. Varying amounts of these impurities in the coal therefore may cause a raising of the grindability index and may lead to the erroneous conclusion that coals containing large amounts of these foreign materials are easier to grind. For a true comparison of grindability, it would seem necessary to grind to the same particle weight. If material were sized in a commercial mill by means of an air current set at a velocity to remove 1.60 sp. gr. float coal ground to 80 per cent minus 200 mesh, any 1.60 sink particles would be left behind, and in order to remove this 1.60 sink material by the same current it would be necessary to grind finer and produce a

Jan 1, 1936

By O. B. Bucklen, J. P. Matoney, P. G. Meikle, R. L. Terry

INTRODUCTION The trend in the coal industry for many years has been to make every- thing "bigger and faster." This also holds true for loading and storage facilities. Where once a 1 million st per yr (910,000 mt/yr) mine was rare, 3-5 million st per yr (2,730,000-4,550,000 mt/yr) mines are not uncommon today in the bituminous industry. This great increase in production, made possible through mechanization, requires greatly improved loading facilities just to get the coal away from the mine. Also, there is a trend to- ward combining production from more than one mine and cleaning it in a single preparation plant. In addition to increased loading capacity, this frequently necessitates raw-coal storage and blending facilities. The development of the unit train with its attendant economics has contributed more than any other factor to the widespread construction of storage and high-speed loading facilities. In the export market, the construction of ever larger coal colliers has added to the need for faster and larger loading facilities. In this climate of rapidly changing technology, any written ac-

Jan 1, 1979

By R. F. Frantz, T. P. McNulty

The upper-level mineralization of the din Buttes, Arizona copper orebody consists primarily of dilute copper silicate impregnation in fault clay and throughout the altered limestone hostrock. Cuprite and native copper are minor with true chrysocolla rare. Owing to the high calcium carbonate and to the hydrogen ion exchange capacity of the clays, acid leaching would be economical only with cheap acid available. Leaching of the silicate copper with reagents other than sulfuric acid is slow and incomplete unless the ore is first heated to disorder the mineralized grains and to reduce partially the contained copper. Following heat treatment, 70 to 90 percent of the nonsulfide copper can be dissolved in aqueous anrmonium carbonate. Recovery of a pregnant solution by counter-current decantation is effective provided ammonium carbonate solution is added to the washing stages in order to oppose adsorption of dissolved copper by clays in the residue. Thermal stripping of the pregnant solution permits recovery of ammonia and carbon dioxide while precipitating copper either as oxide or carbonate. The research program was carried from batch tests through continuous miniplant operation to a five-month campaign in a 20 TPD continuous pilot plant. Pilot plant results, the relationships among key varibles, and a detailed flowsheet are given.

Jan 1, 1973

By DIFTIGIHT E. WOODBRIDGE

(Glen Summit Meeting, June, 1911,) DURING April, May, and June, 1910, I was in charge of an examination of the greater part of the Moa iron-ore area in Oriente Province, Cuba, on the north coast, near the east end of the island. My instructions, on arrival at the properties, were to check former estimates of tonnages and grades, and to re-examine the ore comprised in claims covering 44,727 acres. This work included .the running of lines dividing the properties into co-ordinate planes, the boring of many thousand feet of holes spaced at the intersections of these co-ordinates, the taking of samples of the ore penetrated, the analysis of these samples for their various constituent minerals, and the determination of the results as to tonnages, depths, and grades, both for individual properties and for the entire group. Each section of every one of the thousand holes drilled was to be compensated for depth and grade with every other, a series of simple arithmetical calculations of no slight magnitude, the mere mechanical labor of which consumed much time, but finally resulted in giving a complete average of all the essential facts for the entire area of 18,000 hectares. Had it not been for the more than willing, active, and able co-operation of the officers of the Spanish-American Iron Co., from Charles F. Rand, President, and Jennings S. Cox, General Manager, down to the most humble water-carrier, the work would have consumed far more time than it did. Papers prepared by others, and to which my present paper may be considered an addendum, elucidate, more fully than I could hope to do, the origin and geological character of these ores. I will confine myself to the situation, method and expense of exploration, and to probable courses of development and mining, with some attention to the cost of the ore delivered in the United States.

Mar 1, 1911

By J. T. Norton, J. G. McMullin

The ternary system of gold-silver-copper is characterized by a solid solubility gap and a two phase region in which copper-poor and silver-poor phases coexist. At about 30 pct gold, the two phases become mutually soluble at temperatures below the melting temperature. As the gold content is increased, the solubility temperature of the alloys decreases until at about 80 pct gold, the two phases are soluble down to the lowest temperature at which the alloys will recrystallize. Although the general form of the two phase region is known, its boundaries do not seem to have been investigated extensively. In an X ray diffraction study, Masing and Kloiberl have outlined the boundaries of this two phase field at 400 and 750°C. Using only microscopic techniques, Pickus and Pickus2 determined a vertical section of the ternary diagram showing the 14 kt alloys (58.3 pct gold). These two reports are riot in complete agreement. It has been shown3 that some of the ternary alloys are susceptible to age hardening and that the hardening is caused by the separation of a homogeneous alloy into two phases at the aging temperature. While the gold-copper binary system is an outstanding example of super lattice formation, Hultgren4 has shown that a few per cent of silver added to gold-copper destroys the tendency for ordering. Because of the age hardening possibilities of these alloys, it seemed advisable to investigate the boundaries of the two phase field more in detail using an X ray diffraction method, so as to permit a better understanding of the aging phenomena and enable predictions as to the behavior of other alloys to be made. This is especially true for the 18 kt alloys (75.0 pct Au) at the lower temperatures since they are known to exhibit age hardening. Twelve ternary alloys were prepared having the compositions shown in Table 1 and graphically in Fig 1. The gold used was fine gold bars supplied by Handy and Harmon. The silver was a bar of high purity silver from the U. S. Bureau of Standards. The copper was a bar of vacuum-treated, high conductivity copper from the National Research Corporation. The pure metals in the form of powder were weighed out in proper proportions and melted in graphite in a high frequency induction vacuum furnace. They were heated to 1100°C and slowly cooled. The ingots were then removed from the crucible, inverted, returned to the crucible and remelted. This remelting procedure was intended to reduce segregation in the ingots. After remelting, the ingots were checked for weight loss. The weight loss in each ten gram ingot was held to less than 25 mg. The remelted ingots were cold rolled and then given a homogenizing heat treatment of 16 hr at 760°C to remove any remaining segregation. Powder specimens were prepared by cutting the ingots with a fine file, one half the required amount of powder being taken from each end of the ingots. When the X ray diffraction pattern showed any difference in lattice constant between the ends of the ingot, the ingot was remelted and given an additional homogenization treatment. All powder samples were sealed in evacuated pyrex tubes for heat treatment. Ordinary pyrex proved satisfactory for temperatures up to 650°C but above that temperature it was necessary to use a special high temperature pyrex glass. Annealing at temperatures below 500°C was done in a salt bath whereas for temperatures of 500°C and above an electric muffle furnace was used. In both furnaces the temperature control was ± 5°C. In all annealing treatments samples of cold worked powder were placed in a furnace which was already at temperature. In this manner the specimens recrystallized directly to the equilibrium structure for that temperature. Time at temperature was selected so as to allow complete recrystallization, but very little grain growth. Specimens were quenched from the annealing temperatures by breaking the pyrex tubes in cold water. X ray diffraction photograms were made of all the heat treated powders using copper radiation and a Phragmen

Jan 1, 1950

By Henry A. Stiff, J. P. Hammond, A. B. Westerman, H. C. 195-000-000-014 Cross, and Lawrence E. Davis

The phases in Cr-Fe-Mo alloys have been investigated with homo-genization, aging temperature, composition range, and alloy addition as variables. Metallography, three X-ray methods, and hardness were used as methods of study. The behavior of s, M23,C8, and Z phase are reported for cornpasition range 60 pct Cr-15 to 25 pct Fe-15 to 25 pct Mo-<0.005 to 0.36 pct C with aging at 1400º to 2000°F. With 2 pct Ti, Tic and TiC-TiC are formed; with nitrogen Cr2N. THE recently developed class of chromium-base heat-resistant alloys shows appreciably higher strength than commercially used high temperature alloys. However, further developmental work is required to impart needed shock resistance and some degree of room-temperature ductility to these alloys. Extensive exploratory work on chromium-base alloys was begun in a program initiated by the War Metallurgy Committee of the National Defense Research Council at the Climax Molybdenum Co. in the early part of 1942.&apos; Alloys were sought for gas-turbine blades for use at 1600°F. A minimum of 5 pct elongation in the stress-rupture test was a requirement. From the Climax work, ternary alloys of chromium, iron, and molybdenum appeared to show the greatest promise as materials for gas-turbine blades. The composition line in the ternary diagram joining the 60 pct Cr-15 pct Fe-25 pct Mo and 60 pct Cr-25 pct Fe-15 pct Mo alloys was indicated as representing the most useful combination of strength and ductility.&apos; Strength increased while ductility decreased as molybdenum was raised in this composition range.&apos; The 60 pct Cr-15 pct Fe-25 pct Mo type alloy was thought to have the most suitable properties for gas-turbine blades.&apos; Concurrent with the study reported here, other investigations were being made on Cr-Fe-Mo alloys. The liquidus temperatures on a series of low carbon, ternary alloys were being determined, and isothermal sections drawn at 2370°, 2010°, and 1650°F (1300°, 1100°, and 900°C).2 Also, various methods of preparation and some mechanical and physical properties of chromium-base alloys, particularly the 60 pct Cr-15 pct Fe-25 pct Mo type, were being investigated., At the inception of the present program, only a limited study had been made of etchants for developing the microstructures of chromium-base alloys; X-ray analysis of the microconstituents had not been made. A review of the literature revealed that no phase-diagram work had been reported on the Cr-Fe-Mo system. Scope of Work The work on chromium-base alloys includes the following: 1—The development of etching methods for differentiating between the microconstituents; 2—The identification of microconstituents by X-ray diffraction methods; and 3—A comprehensive metallographic and hardness study after various heat treatments. The phases were studied by three standard X-ray techniques: 1—The block-sample focusing-camera method; 2—The powder-diffraction method on elec-trolytically separated residues; and 3—The powder-diffraction method on cold-worked aggregate samples. The results by the first two methods were correlated with the metallographic data. The third method was used largely to study conditions approaching equilibrium, since cold working prior to heat treating accelerated precipitation. Seven types of alloys were investigated: 50 pct Cr-50 pct Fe, 40 pct Cr-40 pct Fe-20 pct Mo, 55 pct

Jan 1, 1953

By R. I. Jaffee, F. C. Holden, H. R. Ogden

ECENT papers dealing with the properties of unalloyed iodide titanium have been directed primarily at the determination of base-line properties for alloy investigations. Early work was limited to a few tests because of the limited availability of iodide titanium at the time. In the results of papers by Campbell et al.,1 Gonser and Litton,2 Jaffee and Campbell,3 inlay and Snyder,4 and Jaffee, Ogden, and Maykuth, data on mechanical properties are presented for unalloyed iodide titanium in the annealed and cold-worked conditions. Data are presented in this paper which show the effects of heat treatment on the structure and mechanical properties of commercially produced iodide titanium. Correlation is made between microstruc-tural variables and the mechanical properties. Experimental Procedures Melting Stock: The melting stock used was as-deposited iodide titanium, produced by New Jersey Zinc Co. The furnished analysis showed the following range of impurities: N, 0.004 to 0.008 pct; Mn, 0.005 to 0.013; Fe, 0.0035 to 0.025; Al, 0.013 to 0.015; Mo, 0.0015; Pb, 0.0045 to 0.0065; Cu, 0.0015 to 0.002; Sn, 0.001 to 0.01; Mg, 0.0015 to 0.002; and Ni, 0.003. Hydrogen content as determined by vacuum-fusion analysis was 0.0091 wt pct (0.44 atomic pct) after arc melting and fabrication. Nitrogen analysis on the arc-melted and fabricated titanium showed a content of less than 0.002 pct N. The average hardness of the furnished stock was Rf 70, or approximately 85 VHN. Melting Procedure: The as-deposited rods were rolled, sheared, and degreased in preparation for arc melting. The charge was arc-melted with a tungsten electrode in a water-cooled copper crucible under a positive pressure of high purity (99.96 pct) argon. The final ingot was approximately 2 in. in diameter and showed no increase in hardness over that of the initial stock. Fabrication: Heating for fabrication was done in air. It was begun by forging the ingot into a 3/4 in. diam rod, at an initial temperature of 1600°F. Scale was removed by sandblasting. The rod was then swaged to 1/4 in. diam at room temperature through a series of 20 dies, with approximately 10 pct reduction in area between each die. An anneal of 1 hr at 850 °C in air was given after the 1/2 in. die, such that the final cold reduction was 75 pct. Sections cut from this rod were used for test and microstructure specimens. Heat Treatment: Heat treatments were carried out in resistance tube furnaces with stainless-steel linings, under an atmosphere of gettered argon. As further protection against contamination, the specimens were packed in titanium turnings in a titanium sleeve. Control experiments have shown negligible hardness increases with this method, indicating that contamination from oxygen and nitrogen is slight. Three cooling rates were employed in this work; these have been designated as water quenching, argon cooling (to simulate air cooling under a controlled atmosphere), and furnace cooling. The cooling rate for an argon cool is 100°C per min for the first minute, with an average cooling rate of 35°C per min over a 15-min period. A furnace cool requires about 10 hr, with an average cooling rate of 3.6oC per min during the first hour, and an average cooling rate of 1.2°C per min over the 10-hr period. Microimpact Test: The specimen adopted was based on the cylindrical Izod Type Y specimen (ASTM, E23-41T). All dimensions were reduced to half scale, including the notch radius. Specifications are shown in Fig. 1. The specimen is held vertically in an adapter and broken as a cantilever beam. Impact tests were run on a constant-velocity (11.34 ft per sec) Tinius Olsen impact testing machine with a total available energy of 100 in.-lb. Tests were made to determine the correlation between this microimpact and the standard V-notch Charpy impact test. Curves showing impact energy as a function of temperature for both impact tests are plotted in Fig. 2. Transition temperatures, when they occur, are about the same for both impact tests. All three titanium-rich materials have the same conversion factor, 10. Tensile Testing: Tensile tests were conducted on Baldwin-Southwark testing machines using the 600, 2400, or 3000 1b range. Specifications for the test specimen were taken from the 1948 edition of the ASM Metals Handbook, and are shown in Fig. 1. Strain measurements were made using an SR-4 resistance gage (Type A-7) cemented to the reduced section in conjunction with a lever-type extenso-meter. Readings on the SR-4 strain indicator were

Jan 1, 1954

By John Chipman, Raymond L. Orr

Recently reported high -temperatlnre thermal data have been incorporated in a reuieu&apos; of the therinody-r~ar,zic propesties of iron. The recent data permit mot corlsisterlt and reliuble choices to be made for many of the pvoperties, resnlling in bettev eslablished tabrtlations of the thermodynamic functions. Values of Cp, h°t- - H°298. s°t - S2sa, and (G°T -H298/T are tabulated for -the solid and liquid phases of iron in both stable and melastable regions. Consistency of the tabulations has been maintained to the precision necessr~vg to yield the Gibbs energy change belween the bcc (a, 8) and fcc (y) phases of iron at temperatures pertinenl to alloy studies. THE importance of the metal iron has stimulated many investigations of its thermodynamic properties at elevated temperatures. Reviews and summaries of the data have appeared from time to time. Among these the 1951 paper of Darken and smith&apos; deserves highest recognition for the quality of its criticism and for the precision and thermodynamic consistency of its tabulations. These and the more recent table of Kaufman, Clougherty, and weiss2 reproduce the Gibbs energy of the (a, 6)--Y transformation with sufficient sensitivity for alloy studies. Other recent compilations of equal validity3-&apos; make no attempt to do this. Since this Gibbs energy change is not greater than 22 cal per g-atom over the temperature range 1100° to 1800°K, it is obviously desirable to tabulate values of (G°t - H298)/T to four places of decimals even though the absolute accuracy would not warrant such precision. The necessity for reconsideration of the problem is emphasized by the recent publication of several important researches on the enthalpy and heat capacity of iron. The older work is well-covered in the reviews cited and will be mentioned here only when actually employed in the tabulations. GAMMA IRON Transition temperatures are taken from the selec -tions of Elliott and Gleiser,5 based on the work of Boulanger7 and earlier workers. For the a-y (A3) transition at 1184°K we retain the value 215 cal per g-atom adopted by Darken and smith.&apos; It has received confirmation in the recent work of Dench and Kubaschewski,&apos; and of Braun8 using adiabatic calori-metry, and of Wallace, Sidles, and Danielson10 using a pulse heating technique. The enthalpy data of Olette and ferrier" and of Anderson and Hultgren12 at higher and lower temperatures may be extended to 1184°K to give the following values which are adjusted to the required value of ? 1184 Ha,1184 Ha 298 = 8030 cal per g-atom [11 hr,1184-ha298 = 8245 cal per g-atom [2]

Jan 1, 1968

By Richard H. Sibson

Changes in seismic style along the San Andreas fault system appear to correlate with strike-parallel variations in regional heat flow. Large earthquake ruptures are associated with colder segments of the fault zone, while comparatively high levels of microearthquake activity and small to moderate shocks occur along the hotter segments, often in association with aseismic creep. Such behavior is consistent with geotherm and strain rate dependent profiles of shear resistance versus depth, constructed for quartz-bearing rocks. These profiles suggest that the transition from frictional to quasi-plastic behavior with depth should increase by a few kilometers passing from the hotter to the colder portions of the fault zone, giving rise to long-wavelength concentrations of distortional strain energy near the base of the seismogenic zone in the cold segments. Some support for this hypothesis comes from the observed deepening of microseismic activity passing northwest and southeast from the central Californian active region to the currently locked, ~400 Ian segments of the San Andreas fault that ruptured in 1906 and 1857.

Jan 1, 1982

By A. D. McMaster, M. L. Gimpl, N. Fuschillo

Low-power, high-speed, radiation-resistant, monolithic thin-film integrated circuits require thin-film resistors of high sheet resistance which are compatible with the processing requirements for monolithic silicon devices. For this purpose the structure and electrical resistance as a function of temperature were investigated for Nichrome-silicon monoxide cermet films on passivated single-crystal silicon substrates. A suitable material was found to be a mixture of 50 vol pct Nichrome-50 vol pct silicon monoxide. This mixture, when evaporated onto 300°C substrates. showed a low temperature coefficient up to 400°C, at both 270 and 1100 ohms per square. Resistors deposited on room-temperature, 300°, and 500°C substrates were heat-treated at 600°C in air for short periods of H- seed, low-power, radiation-re sis tant, monolithic thin-film integrated circuits&apos;-3 require thin-film resistors of high sheet resistance and low temperature coefficients of resistance which are compatible with the processing requirements for monolithic silicon active devices. The present investigation is directed towards the replacement of the Nichrome in the sandwich-type SO2-Nichrome-SiO resistors, currently used for DTL monolithic thin-film integrated circuits, with codeposited Nichrome-SiO cermet resistors. These Nichrome-SiO resistors are provided with an overcoat of SiO and are deposited onto thermally oxidized silicon wafers used in monolithic mi-crocircuit technology. The cermet resistors are shown to provide a lower temperature coefficient of time totaling up to 45 min. Electron nzicrogvaphs and diffraction patterns were taken of the as - deposited and heat-treated films. These results were then compared with electrical-resistance measurements for each condition. The room-temperature and 300°C substrate films showed a large decrease in resistance. The 500°C substrate film remained stable throughout the entire cycle. Electron-microscopy results show that the increased stability after heating to 600°C is largely due to crystallization of the films which begins in the vicinity of 400°C. The slight oxidation of the films when heated in air had a negligible effect on the resistance. The resistance of the film was a function of the substructure. resistance and a more versatile compatibility with silicon monolithic processing. Previous work3, on chromium-SiO coevaporated cermet resistors on glass and ceramic substrates without overcoats of SiO has been reported. For the present application, the thin films should possess the following ideal requirements: a) a temperature coefficient of resistance as near zero as possible up to 300°C; b) have a sheet resistance higher than 200 ohms per sq to conserve space on the chip; c) be easy to evaporate; d) be oxidiation- and radiation-resistant; e) show long-time stability at 100°C; } be stable in N2 atmospheres up to 600°C for short periods of time (5 to 45 min). Requirements a to e are well-known. The last requirement was optional and was due to a mask elimi-

Jan 1, 1967

By F. M. d’Heurle

Films of molybdenum have been prepared by sputtering onto oxidized silicon substrates. The resistivity. lattice parameter, orientation, and grain size were studied as a function of substrate temperature and substrate bias. Under normal sputtering conditions, the resistivity of the films was found to be quite high (600 x 10 ohm-crn). However, with the use of the negative substrate bias of 100 v and a substrate temperature of 350°C, films weve produced with a resistivity of ahout twice that of bulk molybdenum. The lattice parameters measured in a direction nornzal to the surface of the films weve found to be gveatev than the bulk value. This was interpreted as being at least partly due to the presence of compressive stresses. The effects of annealing in an Ar-H atmosphere were studied in terms of diffraction line width, lattice parameter, and resistivity. BECAUSE of its relatively low bulk resistivity (5.6 x 106 ohm-cm)&apos; molybdenum is potentially interesting as a thin-film conductor in integrated circuits. An additional feature which makes it attractive for this purpose is its low coefficient of expansion (5.6 x KT6 per "c),&apos; which is fairly well matched to that of silicon (3.2 x 10 per c). It is possible to deposit molybdenum films by evaporation but generally films produced in this manner have a high resistivity. In order to achieve resistivities close to bulk value, Holmwood and Glang found it necessary to operate in a vacuum of about 107 Torr and to maintain the substrates at 600 C during film deposition. Sputtered molybdenum films have been examined by Belser et a1.7 and, recently, by Glang et al.&apos; This paper describes the results of an attempt to extend some of that work and examine the effects of annealing and getter sputtering on the physical and structural properties of the films produced. SPUTTERING APPARATUS AND PROCEDURE The apparatus used for most of the film sputtering work described here consisted of two "fingers" serving as anode and cathode, respectively, which were mounted within an 18-in.-diam glass chamber. A liquid nitrogen-trapped 6-in. diffusion-pump system was used to achieve a vacuum of about 1 x 107 Torr within the chamber prior to sputtering. The essential features of the equipment are shown in Fig. 1. Cathode and anode fingers are stainless-steel tubes isolated from the top and bottom plates by Teflon collars. In order to limit the discharge to the space between anode and cathode, each finger is surrounded by an aluminum hield, at ground potential, having an internal diameter 18 in. larger than the outside diameter of the finger. The cathode and anode fingers are 6 and 4 in. in diam, respectively. A 116-in.-thick sheet of molybdenum is brazed with a 10 pct Pd, 58 pct Ag, 32 pct Cu alloy to a copper disc which is mounted by means of screws and a large 0 ring onto the lower end of the cathode finger. The disc is cooled during sputtering by water circulation inside the finger. The use of several feet of plastic tubing for the water input and outputg reduces leakage to ground to less than 1 ma when the cathode potential is raised to 5 kv. The upper end of the anode finger is terminated by a brazed-on copper block. A variety of specimen holders can be easily mounted on the upper face of this block. Substrate heating or cooling is achieved by use of an appropriate unit attached to the lower face of the same block. Heating is achieved by means of cartridge-type heaters and cooling by copper coils fed with forming gas under pressure. The inner chamber of the specimen finger constitutes a small vacuum chamber of its own which is evacuated by an auxiliary mechanical pump in order to limit heating element oxidation and heat transfer by convection currents. An advantage of the finger arrangement is the absence of cooling and heating coils and wires within the main chamber. The stain less-steel shutter is useful to establish a discharge for cleaning the cathode at the beginning of each sputtering run. Water cooling of the shutter reduces heating and the out-gassing of impurities which might condense on the nearby substrates. Unless otherwise specified, the substrates used in these experiments were 1-in.-diam oxidized silicon wafe:s, 0.007 in. thick, having an oxide thickness of 6000A. The substrate holders were large copper discs onto the surface of which a number of molybdenum discs, 116 in. thick and 78 in. in diam, were brazed. The wafers were clamped to the molybdenum discs

Jan 1, 1967

By D. A. Woodford

A number of observations have now been reported where the steady-state creep rate is apparently linearly dependent on the applied stress at high temperature and low stresses. This results in a creep rate greater than that predicted by extrapolation of high-stress data and has obvious practical implications. However, some of these observations are open to question. For example, the analysis by Harris and Partridge17 of the data of Greenfield et a1.18 was dependent on strain rates which, according to the original authors, were too low to be measured. Dr. Bernstein appears to have demonstrated a linear stress dependence at low stresses in two zirconium alloys. There are, however, a number of discrepancies in his treatment of the data and the subsequent theoretical analysis which require clarification. 1) It is incorrectly stated that steady-state conditions are revealed by a slope of unity on a plot of log i vs log (time). This objection is trivial if the author meant to say a slope of zero, although it is unclear how subsequent extrapolation was made to determine the steady-state creep rates at low stresses for the zircaloy-2. If the plot used was actually log c vs log (time), it is unlikely that a slope of unity would represent a constant creep rate. A plot of log (c - co) vs log (time), where c0 is the extrapolated intercept sf the steady-state creep rate on the strain axis, would have a slope of unity during steady-state creep. However, eo cannot be determined unless is is already known. 2) The author chooses to interpret his results based on the equation: where A, and B, are structure-sensitive parameters, Ql and Q, are the activation energies for the particular creep process, and n describes the sensitivity of the creep rate on stress. The first term represents a slip creep process and the second a diffusion creep process. However, it is stated later that "two distinct processes acting in parallel are involved". Eq. [I] surely represents two processes in series since each reacts to the total applied stress and t, is the sum of the individual creep rates. If the processes are acting in parallel, then the effective stress in each would be less than the applied stress. The component stresses would be given by sl + s2 = a but it is not clear how the magnitude of either, or the corresponding stress exponent, could be determined.

Jan 1, 1969