By J. C. De Haven, Harry Seltz

INTERMETALLIC compounds are formed in many binary metal systems. Some compounds are stable to their melting points, and others decompose at lower transition temperatures. Even those of the first class are dissociated in the liquid state, as indicated by the continuous form of their solubility curves at their melting points'. While the lattice structures of some of these compounds' have been determined, their thermodynamic properties have not been investigated. In this paper is described the determination of the free energy and heat of formation of the compound CdSb, which is of the first class mentioned above, melting congruently at 455° C. This compound shows a rhombic structure, and the lengths of the edges of the elementary cell containing four molecules are: a = 6.52,b=8.60,c=4.16Å2 There are three possible methods of determining the free energy of formation of a compound of this type. The first method, applying the third law of thermodynamics, requires the measurement of its heat capacity preferably to liquid hydrogen temperatures, and a calorimetric determination of its heat of formation. The second method involves the study of the equilibrium of the compound in some gas reaction, such as: CdSb + CO2 = CdO + CO + Sb. From the known free energies of formation of, CdO, CO2 and CO the free energy of formation of CdSb could be calculated. The third method measures the electromotive force of a galvanic cell in which the cell

Jan 1, 1935

By D. L. Douglas

The ß decomposition of Zr-U-O alloys was studied during an interrupted quench from the a + ß region. Decomposition was more rapid than in binary Zr-U alloys of the same uranium content or qf equivalent ß composition. The rapid transformation has been ascribed to the presence of the primary a phase which provided nucleation sites and which permitted preferential partitioning of oxygen to the a phase and of uranium to the COMMERCLAL heat treatments are designed to produce certain strength and toughness character- istics by controlling the microstructure of an alloy. A desired distribution of microconstituents is achieved in practice by treating an alloy under the correct time-temperature conditions. A knowledge of the phase equilibria in any alloy system is essential in outlining heat treatments, but in addi-

Jan 1, 1961

There is a basic need for the health and safety manager to know what work he or she is to do and how to do it in a more professional way. Peter F. Drucker in The Practice of Management said, "The ignorance of the function of management, of its work, of its standards and its responsibilities is one of the most serious weaknesses of an industrial society-and it is almost universal." The biggest need in mining today is for its managers to have a thorough understanding of the management control activity.

Jan 11, 1979

By Freeman Bishop

The Bureau of Mines, beset by political woes not of its own making, is struggling to maintain equilibrium as Congress is being made the focal point for repeated charges that the Bureau has "not done a very good job" of setting up and supervising coal mine health and safety standards approved last year by the Congress. Senator Harrison Williams (D- N.J.) is the latest to enter the arena. A crusading legislator, he is now calling for "legislative overview" hearings to judge Bureau competency in matters of coal safety legislation enforcement

Jan 1, 1970

By W. R. Boehme

The laboratory test work compares various 6 x 16 mesh activated coconut carbons using a gold standard solution of 4 ppm dissolved in sodium cyanide. The carbon adsorption rate and maximum loading are measured for different feed solution ionic contaminates: silver, copper, thiocyanate, and ferrocyanide. Conclusions are drawn that among the activated coconut carbons tested, maximum loading and the effects of specific ions varied significantly. The work presented can be applied to 6 x 16 mesh carbon selection tests and specific ion monitoring for industrial carbon adsorption systems.

Jan 1, 1984

By A. J. Erickson, W. W. Atkinson

Concepts developed in a geologic data recording system at the Victoria, Nevada breccia pipe-skarn copper mine, are not fundamentally new, but represents expansion of earlier ideas. The basic philosophy is that a high quality geologic data base is necessary and should be complete, clear, standardized, neat, quantitative, and readily useable. It may be multi-colored or simply black and white. Graphic, descriptive and quantitative recording of data is essential. A format for core logging is presented and discussed, as well as a mu1tiple overlay system for recording data gathered in surface mapping.

Jan 1, 1984

By Kraig W. Grubaugh, Lee W. Saperstein

Rapid growth rate of surface mining for coal has caused many states to increase the rigor and complexity of their surface mining codes. The promulgation of federal surface mining standards may cause those states containing federal land to amend their codes also. Presented is an up-to-date review of these codes with tabular summaries that divide the codes into operative functions. These summaries will be of use to new operators, multiple-state operators, and state officials. Suggestions are made for industrial efforts to present workable and acceptable amendments to these codes.

Jan 1, 1978

By D. J. DeLazaro, W. Rostoker, R. E. Riley, M. Hansen

KNOWLEDGE of the isothermal transformation behavior and the TTT chart method of graphically summarizing such information has been of invaluable aid to the ferrous metallurgist in understanding and developing heat treatments intended to provide specific mechanical properties. It is to be expected that similar lines of study directed to titanium-base alloys will be as profitable. This paper summarizes, on conventional TTT charts, the isothermal transformation products and pertinent reaction rate data for binary alloys of titanium containing 1, 3, 5, 7, 9, and 11 pct Mo, respectively. The results so presented were derived from metal-lographic examination. Some X-ray diffraction work was done to clarify certain points of question. Ti-Mo System To the authors' k.nowledge, TTT charts have only been used to describe the reaction rates of eutectoidal decompositions. It would seem that the kinetics of decomposition of any unstable solid solution might be conveniently described in this manner. The equilibrium diagram of the Ti-Mo system' is shown in Fig. 1. The similarity with the Fe-Ni system will be recognized. Additions of molybdenum serve to stabilize the /3 phase to increasingly lower temperatures. The solubility of molybdenum in the a phase is restricted to less than 1 pct at 600°C. Under normal conditions. a homogeneous ,8 structure quenched to a, temperature in the a f & field will reject a of invariant composition. The rate at which this occurs depends on the degree of undercooling and the degree of supersaturation of /3. The structural character of the rejected phase may also be expected to be related to the undercooling. Materials and Experimental Methods A sponge titanium was used which has a nominal impurity content as reported in Table I. The nominal composition of the molybdenum used is also included. The alloys were prepared in 150 g melts by arc melting in an evacuated water-cooled copper crucible of the type reported in an earlier paper.' The pancake-type ingots were forged to 1/4x1/4 in. bars and homogenized for 24 hr at 1000°C in evacuated Vycor bulbs. Specimens Vi in. thick were cut from these bars for heat treatment. The heat treatment cycles followed an invariant procedure. The specimens were soaked at 1000°C for 20 min under a helium protective atmosphere prior to quenching into a lead bath held at a temperature corresponding to a chosen degree of undercooling. After a prescribed period of time at this temperature, the specimen was removed and water quenched. A series of specimens so treated for progressively longer periods served to establish the times for initiation and completion of the decomposition of the /3 phase at a particular temperature. Although heat treatment of unprotected specimens in a lead bath does permit surface contamination by lead diffusion, this method is necessary to insure sufficiently rapid quenching rates. As long as the bath treatments were of less than 1 hr duration. the contaminated surface was not unduly deep and could be removed without excessive grinding. Metal-lographically, the contaminated zone could be readily distinguished from the pure binary alloy. Transformation Characteristics of Ti-Mo Alloys Metallographic examination showed that a supersaturated p phase may decompose by one of two processes. Alloys containing 1 to 9 pct Mo, when quenched in water from the homogeneous /3 field,

Jan 1, 1953

By A. R. Troiano, E. A. Steigerwald, F. W. Schaller

The kinetics of crack propagation in a hydrogenated high-strength steel at subzero temperatures indicated that cracking progressed in a discontinuous fashion. The delayed failure process thus involves a series of crack initiations rather than the continuous growth of a single crack. The incubation time required for the initiation of delayed failure was controlled by the diffusion of hydrogen. The activation energy for the process was 9120 cal per g-alom. As the test temperature was lowered the incubation time constituted a greater percentage of the total tinze to fracture, and al -50°F the incubation and fracture times were essentially coincident resulting in instantaneous, catastroplzic fracture. A unique feature of hydrogen embrittlement is the delayed failure process in which the material fails under the action of a sustained load even though it is capable of supporting a higher load for a finite period of time.')' Delayed failure of steel and titanium is characterized by an incubation time, preceding the initiation of a crack in a highly localized region, and the subsequent growth of the crack to ultimate failure.3-5 The kinetics of crack growth in hydro-genated high-strength steels have been studied through the use of resistance measurements and have an important bearing on the mechanism of delayed failure. Delayed failure is believed to be merely a facet of hydrogen embrittlement in which sufficient time is allowed during a test for hydrogen diffusion. The current theories employed to explain hydrogen em-brittlement can be grouped into two types. one6-8 explains the embrittlement on the basis of the pressure exerted by molecular hdrogen in lattice voids or defects while the other9-10 attributes the embrittlement to the influence of hydrogen in the lattice. The mechanism used to explain the nature of the crack kinetics in delayed failure is based on the stress-induced diffusion of hydrogen to the area of maximum triaxiality.3 When the hydrogen concentration in this region reaches a critical value, a crack is nucleated. This initial crack propagates instantaneously until stopped by the higher fracture stress of the adjacent material of lower hydrogen content. The continuation of cracking must then await the further diffusion of hydrogen to the new region of triaxiality near the base of the crack where another initiation will occur. From this mechanism it follows that crack propagation is nothing more or less than a series of initiations with limited fracture. The purpose of this investigation was to examine the kinetics of crack growth in an effort to determine whether or not the process was discontinuous. Studies of crack propagation were conducted at low temperatures to retard the diffusion of hydrogen which is presumed to be the rate controlling process in delayed failure. MATERIALS AND PROCEDURE Specimen Preparation—A commercial heat of air-craft quality SAE-AISI 4340 steel, designated as Heat G, was furnished by the Republic Steel Co. in the form of %-in. hot-rolled bars. The material had the following chemical analysis: Composition of 4340 Steel—G Heat C Mn Si Ni Cr Mo 0,395pct 0.82pct 0.29pct 1.76pct 0.85pct 0.25pct Notched tensile specimens with less than a 0.001 in. radius, Fig. 1, were used throughout the investigation. The specimens were heat treated to a 230,000 psi strength level according to the following sequence: a) Normalize bar stock at 1650°F for 1 hr, b) Stress relieve at 1200°F for 4 hr and furnace cool,

Jan 1, 1960

By L. W. Kempf

A BALANCED system of internal stress is set up in any metallic structure by plastic deformation below the annealing temperature. The internal stress induced by cold rolling or other fabricating processes is generally recognized and its magnitude is known to be, within certain limits, a function of the degree of cold deformation. The plastic deformation that may accompany rapid cooling from elevated temperatures may not materially change the form of the product. The internal stresses so induced are not, therefore, so evident and nonrecognition of their presence has at times led to engineering failures. The heat treatment of aluminum alloys is a relatively new art and little information is available regarding the magnitude of stresses induced luring the commercial heat treatment of aluminum alloy products is the industrial use of aluminum increases, it is inevitable that products of increasingly large volume be required. It has become necessary in the present commercial utilization of aluminum to heat-treat castings and forgings weighing hundreds of pounds. One of the factors governing the magnitude of internal stresses arising from rapid cooling at elevated temperatures is that of the, size of the structure being treated. Some of the other factors are: cooling rate, elastic properties of the alloy, thermal expansivity, thermal conductivity, and the presence or absence of phase changes. Practically all aluminum alloys have a high coefficient of thermal expansion and some are capable of developing relatively high

Jan 1, 1934

By L. W. McKeehan

THE occurrence of twins in large ferrite crystals, made by a new process, was reported in a recent note. This paper describes a typical case of such twinning and suggests, on the basis of the observed facts, why smooth slip-planes are rarely observed in this metal. METHOD OF PREPARATION The material In which the crystals here dealt with were grown was made from 1/8 -in. Armco iron welding rod containing C, 0.04; S, 0.037; P, 0.003; Si, 0.008, and Mn, 0.02 per cent. This rod was cold drawn into wire about 1 mm. dia. A piece of this wire was supported vertically and was locally heated in hydrogen at atmospheric pressure to about 1400° C. by an alternating current (60 cycles per sec.) of about 35 amp., passed through it between a pair of travelling contacts about 8 cm. apart. The rate of travel for the case in hand was 12 cm. per hr. After some 30 cm. of the length of the wire had been heated and cooled in this manner the whole wire was immersed for a few seconds in dilute nitric acid, not restrained by alcohol. Etching was continued until, as nearly as could be judged by eye, the original smooth cylindrical surface of the wire was no longer capable of specular reflection.

Jan 1, 1927

IN the preceding chapter on thermochemistry and the reactions in and between metal and slag phases and in the following chapter on fuel combustion the main emphasis is placed on the equilibrium or "static" conditions. This equilibrium viewpoint is not concerned with the rate of change in the process or with the mechanisms or paths followed between initial and final states. The questions of just "how it works" and "how fast" belong to the kinetic aspect of any process; their answers are helpful in speeding up or slowing down and thus controlling its operation, and also in understanding its limitations. Any treatment of kinetic factors in the open hearth such as is attempted here and in Chapter 22 must at present be largely qualitative and incomplete. We are only beginning to get quantitative data on rates of reaction and diffusion at high temperatures, as indicated in Chapter 15. Empirical data in the literature on furnace operating rates do not help much to illuminate the details of gas-flow patterns and the complexities of heat flow in the many parts of the furnace system. This chapter is intended to give the reader an introduction to the problems of the flow of gases through the furnace system and the flow of heat in this system. An adequate discussion would require several times the space available here; it is possible here only to outline a few fundamentals and to indicate some of the conditions of heat and gas flow peculiar to the open hearth. Several good general treatments of these subjects may be found in the literature (see references at the end of the chapter). For the designer of open-hearth furnaces, the principles of gas flow are of paramount importance. They are also important to the operation of the process, at least to the extent of a general qualitative picture of the movement of gases in the system. MOTION OF GASES IN FURNACE DUCTS Fluid flow in general can vary between the extremes of laminar or streamline flow with a minimum energy loss, to irregular

Jan 1, 1951

By John Chipman

HE lecture on 'Thermodynamic Properties of Blast Furnace Slagso prepared in 1959 and published two years later required revision in one particular before it appeared in print. The activity of SiO, was deter mined through studies of the equilibrium: SiO, (in slag) 2C (graphite) = (in Fe) 2C0 (1 atm) The ratio for each experimental temperature was found from the heat of formation of cris-tobalite, the entropies and heat capacities of the re-actants, by virtue of the third law of thermodynamics. Discrepancies between several kinds of data led to investigations regarding other equilibria involving SiO, on the suspicion that there might be an error in the third-law value of its free energy. In particular the equilibrium: was restudied by Kay and Taylor who Confirmed the earlier results of Baird and Tayloron which their SiO, activities depended. The free energy of Sic was also rechecked4 independently. These and other equilibrium measurements led to the conclusion6 that the free energy of SiO, at high temperatures is in error and requires a correction of about -5 kcal. The exact source of the error is uncertain; it could lie either in the entropy of SiO, or in its heat of formation, but it more probably lies in the latter. Adjustment of this free energy lowers the ratio by a factor of approximately 4. Accordingly it will be necessary to multiply by this factor all of the SiO, activities determined by this method.',B Referring to the lecture cited, this correction should be applied in Figs. 8, 9, 10, 19, and 20. It applies also to the experimental data of Fig. 13, bringing these as well as those on the ternary system into good agreement with the work of Taylor and associates. At the same time it eliminates the discrepancy shown in Fig. 11, lowering both lines until the upper

Jan 1, 1962

By Robert Archer

Two new alloys of the "strong alloy" class having improved fabricating qualities are described; also methods of producing alloys of the duralumin type with greater strength and hardness than previously obtained, are given. IT is about fifteen years since the development in Germany, largely by Alfred Wilm, of the aluminum alloy called duralumin. In this alloy, combining as it does the tensile strength of mild steel with the lightness and corrosion resistance of aluminum, a distinctly new material was presented to the engineering world. Despite the evident usefulness of this material, however, its commercial development has been slow, due in part to the difficulties involved in its fabrication. In view of the potentially great utility of strong aluminum alloys, it seemed desirable to find means of producing such alloys with better fabricating properties, and work was undertaken with this object in the laboratories of the Aluminum Company of America several years ago. This work has resulted in the production of two new types of aluminum alloy of the "strong alloy" class, having distinctly improved fabricating qualities. The knowledge gained has also made it possible to produce alloys of the duralumin type with greater strength and hardness than previously obtained. There have thus been made available some new engineering materials which it is the object of this paper to describe. These alloys, including duralumin, are fundamentally wrought alloys. Castings of the same compositions, heat-treated in the same manner give inferior physical properties, particularly as to ductility. The statements made subsequently concerning properties and heat treatment apply to material that has received sufficient working to thoroughly break down the cast structure. The material referred to has; in general, undergone a reduction in section of at least 80 per cent. by mechanical working. It may be mentioned in passing that other compositions have been found that are suitable for the production of the maximum physical properties in heat-treated castings.

Jan 2, 1925

By J. B. Berkowitz-Mattuck, R. Hopper, L. Kaufman, E. V. Clougherty

MARNOCH has reported on the attractive high-temperature oxidation resistance of Hf-Ta alloys.' In view of current interest in these alloys, three Hf-Ta alloys were tested in the present study. These included a Hf-27Ta alloy and a Hf-20Ta-2Mo alloy which were supplied by Marquardt Corp. and a Hf-20Ta-Zr alloy provided by Illinois Institute of Technology Research Institute.' The microstructure of these alloys was heated inductively in a glass vacuum system; the oxidizing gas, helium carrier plus a known partial pressure of oxygen (35-102 Torr), was continually passed over the sample at temperature for a given time period. The concentration of oxygen in the gas stream was continuously measured by a differential thermal conductivity technique2 so that the rate of oxygen picked up by the sample could be obtained. The flow rates were 0.1 to 0.2 ft per sec in the vicinity of the specimen. The concentration of oxygen did not fall below 50 pct of the input level in any of the experiments. In several cases a single sample was exposed consecutively at a series of increasing temperature levels. In a second system at ManLabs, cylindrical specimens were exposed to flowing air in a z irconia tube which was heated by radiation from a carbon tube resistance furnace. The specimen was heated from room temperature to the test temperature in flowing argon, then oxidized in air flowing at 0.1 to 0.2 ft per sec. Following exposure, the air was displaced by argon and the specimen was cooled. Postoxidation metallography was performed on every sample. The depth of conversion of the metal matrix to oxide was measured as shown in Fig. 1. The conversion depth was obtained by measuring the oxygen-contaminated metallic zone (which is bounded by a dense outer oxide and a subscale oxide region), subtracting its dimensions from the original dimensions, and dividing by two. Preferential oxidation of

Jan 1, 1968

Trans. Pamphlet Volume Number Title Author Meeting and Page* 1033 Relation of Air Presaure to Drilling H. W. Seamon New York 66, 743. 766 Speeds of Hammer Drills . Feb. 1921 1034 Time Factor in Depletion of Mines J. W. Roberts New York 66, 711 Feb., 1921 1035 Calculation of Ore Tonnage and Grade J. E. Harding New York 66, 117, 122 from Drill-hole Samples Feb., 1921 1038 Diacuasion of Papers Presented in 1920 1041 Run-off and Mine Drainage H. N. Eavenson New York 66. 624. 630 Feb.. 1921 1043 The Health of the Underground Worker A. J. Lanza New York Feb, 1921 1045 Dust-ventilation Studies in Metal D. Harrington New York 66, 272, 288 Mines Feb., 1921 1046 Discussion of Papers Presented at New York Meeting, 1921 1072 Breakage and Heat Treatment of Rock- B. F. Tillson New York 66. 758 drill Steel Feb., 1921 1073 Discussion of Papers Presented at New York Meeting, 1921 1076-M Analysis of Some Drill-ateel Teats F. B. Foley New York 66,789 Feb.. 1921 1077-M Application of Magnetic Analysis to C. W. Burrows New York 66, -796 Rock Drills Feb., 1921 1078-M Heat Treatment of Rock-drill Steel G. H. Gilman New York 66.779 Feb., 1921 1080 What is the Ideal Drill Steel? F. H. kingdon New York 66, 807 Feb.. 1921 1081 Rock Drill-Steels, etc. W. T. Ober New York 66,814 Feb.. 1921 1082-C Underground Mine Development, Its J. B. Dilworth Wilkes-Barre 66,715, 761 Definition and Valuation Sent.. 1921 1081 Drill Steel from Hollow Ingots P. A. E. Armstrong New York 66,809 Feb., 1921 1068 Authors' Replies to Recent Discussion 1092 Heat Treatment of Rock Drill Steel A.E.Perkins New York 66,811 Feb., 1921 1096-M Octagonal Ventilation Shaft of Davis- J. L. Bruce Wilkes-Barre 66. 252, 608 Daly Copper Co. Sept., 1921 1100-C Determination of Electrical Equip- G. Bright Wilkes-Barre 66,580,606 ment for a Mine Hoist Sept., 1921

Jan 1, 1927

THE refining period of an open-hearth heat blends imperceptibly into the finishing period, during which final adjustments are made in slag composition, in bath action and temperature, and in composition of the steel, in order to prepare it for casting into ingots. Operations must be governed by the consideration that alterations in the character of the heat during the finishing period must be held to a minimum. In a broad sense, the finishing and deoxidation period of a heat may be said to be- gin when the action of the last ore addition has ceased, and to end when the teeming of the ingots is completed. INGOT STRUCTLIRES A survey of the relative advantages and disadvantages of different types of ingot structure is required because deoxidation treatments during the finishing period control the amount of gas evolved during solidification and consequently determine the type of ingot structure. Four classes of ingots are recognized, de- pending upon the degree of deoxidation to which the steel has been subjected. These types are killed, semikilled, capped, and rimmed; typical examples of their structures are represented by ingots 1, 2, 5, and 7, respectively, of Fig 9-1. The actual ingots from which these cross sections were sketched were all poured to the same height (indicated by the dotted lines) in the same type and size of bottle-top molds. The eight drawings of the figure represent selected types of ingot structure in a continuous series from "dead killed" to "wild," resulting from variations in the total quantity of gas evolved, from none at all to copious amounts, during solidification of the steel in the mold. Killed and semikilled steels are adjacent at the "quiescent" end of the ingot structure series where only small amounts of gas are evolved. The term "quiescent" describes the action of the molten metal during and subsequent to the teeming of killed and semikilled steels. Capped and rimmed steels are adjacent at the

Jan 1, 1964

By R. F. Burdyn

The inadequate use of centrifugation to economically recover solids from weighted drilling fluids reflects the need for better equipment and techniques for this putpose. Laboratory studies in the development of an improved separator are described in which an operating equation is derived and tested. Results show that the concentric cylinder geometry employed effectively separates bnrite from a suspension and that the operating equation provides a good approxinmtion for scale-up. INTRODUCTION Our current drilling technology frequently requires a high-density drilling fluid obtained by addition of barite. In the course of drilling, formation solids which are too fine to be removed either by screening or settling become suspended in the drilling fluid and gradually the volume of solids in the mud increases. The volume fraction of solids must be limited (if a satisfactory set of rheological parameters are to be maintained). A centrifugal separatorprovidesan economical way of accomplishing this. The barite recovery process can be considered as a separation of two solids. One, the light solids, composed of formation and added solids, has a specific gravity of 2.6 to 2.7; the other, barite, has a specific gravity of 4.2 to 4.3. This density difference, plus the fact that the average light-solids particle size is much smaller than the average barite particle size, permits separation by a centrifuge. In drilling fluids some of the coarse particles of the light-solids-range will settle faster than fine particles of the barite-particle range. As a result a complete separation of the two species is not possible. since the object of the process is not merely recovering the maximum amount of barite but includes as well removing the maximum amount of light solids, an optimum barite recovery efficiency exists. From a practical standpoint this optimum cannot be determined in the field for each drilling fluid system, and in practice the separation is less than optimum, with some sacrifice of barite. Drilling technology has included centrifugal separators for barite recovery for more than a decade. Results have been reported by a number of investigators indicating that the process is practical and economica1. l-4 The decision to use a centrifuge is based on economics in which direct cost savings and the indirect benefits in rig time derived from improvement of the drilling fluid are important factors. One would expect that centrifugal separation of barite from drilling fluids would significantly affect barite consumption; however, this is not the case. The Minerals Yearbook shows an annual domestic barite consumption in the drilling industry of nearly 1 million tons.5 By rough estimate there are perhaps 80 separators presently in field use. Assuming half of these in use at any one time, operating an average of four hours per day, at recovery rates averaging 3,000 Ib of barite per hour, total annual recovery is about 90,000 tons. This is less than 10 per cent of he total barite used. I conservatively estimate that barite consumption in drilling operations can be reduced by 30 per cent through greater utilization of centrifugal separators. To encourage more widespread acceptance of centrifugal separators in the drilling industry, improved equipment and techniques would be very desirable. The present paper, covering theory and results obtained from a laboratory model, is the first in a series on he development of an improved mud separator for field use. THE CONCENTRIC CYLINDER GEOMETRY AS A SEPARATING DEVICE Consider the geometry shown in Fig. 1, consisting of two concentric cylinders separated by an annular space. These are arranged so that the outer cylinder is fixed and the inner one can be rotated about its axis on shafts sealed against the ends of the outer cylinder. If the outer cylinder is fitted with openings at either end, the inner

Jan 1, 1966

By Harold M. Mooney

WHEN apparent resistivity data are taken with the symmetrical Wenner 4-electrode spread, a fixed center position is used and readings are taken for values of electrode separation. Basic data consist of apparent resistivity plotted against separation of adjacent electrodes. The interpreter attempts to infer geologic structure, such as the depth to discontinuities and the nature of subsurface earth materials. An earlier paper1 described methods for interpreting resistivity data. All of these involve a severe assumption, namely that the earth in the region of interest consists of horizontal layers, electrically homogeneous and isotropic. The actual earth never satisfies this assumption exactly and may deviate from it so much that none of the above methods can be applied. Attempts in three directions have been made to modify the assumption so that it approaches known geologic complexity more closely.

Jan 12, 1954

The world's largest steam-driven mine hoist, built by Nordberg Manufacturing Co. a half century ago, has become a major tourist attraction in Michigan's Upper Peninsula. The hoist, designed by company founder Bruno V. Nordberg, is located in the Quincy Mine Number Two, just north of Hancock. Nordberg began construction of the mammoth machine before World War I, but delayed completion until after the war. The hoist became operational in 1920 and continued running until the mine was shut down in 1931.

Jan 9, 1968