By A. Totani, S. Nakajima, H. Okazaki

The phase diagram for the SnTe-SnSe system has been studied in the temperature range from 300° to 900°C by differential thermal and quenching techniques. The X-ray measurements were made on quenched specimens. High-temperature diffraction was also made to study the phase transition in SnSe. The system is proved to be of a eutectic type in which no intermetallic compound exists. The eutectic point is at the composition SnTeo.55 Seo.45. the eutectic temperature being 755°C. Solid solubility limits are SnTeo.6Seo.r and SnT eo. 3s Seo.6s at the eutectic temperature, and change almost linearly to SnTeo.aaSeo.lz and SnTeo.18 Seo.az as temperature decreases to 300°C. It was shown that the SnSe phase has a phase transition of the second order at about 540°C and that the transition temperature decreases with increase of the SnTe content. THERMOELECTRIC properties of tin telluride (SnTe) and tin selenide (SnSe) have been studied extensively in recent years. The variation of physical properties with composition could be of interest if these compounds form an appreciable crystalline solution. The purpose of present investigation is to confirm the formation of crystalline solution or intermetallic compound, if any, and to establish the phase diagram for this system. The crystal structure of SnTe is NaCl type with a cubic unit cell1 (a = 6.313A). The crystal of SnSe having an orthorh2mbic unit cellz (a = 11.496, b = 4.1510, and c = 4.4437A) is isomorphous with tin sulfide (SnS) which has a distorted sodium chloride structure. It has been known that SnSe has a phase at at 540°C; the transition has been assumed to be of the second order. As far as we know, only two studies on the SnTe-SnSe pseudobinary system have been reported. The conclusion obtained in these papers is that, in the composition regions near SnTe and SnSe, the system forms a crystalline solution of the SnTe structure and the SnSe structure, respectively, and that, in the intermediate region, both phases coexist. However, neither the variation of the solid solubility vs the temperature nor the liquidus and solidus were investigated. Hence present writers have attempted to determine the phase diagram of the system by differential thermal analysis (D.T.A.) and X-ray diffraction. EXPERIMENTAL Sample Preparation. Starting materials, SnTe and SnSe, were prepared by the direct fusion of commercially available high-purity (99.999 pct) elements. Stoichiometric amounts of each couple Sn-Te or Sn-Se were weighed into a clear fused silica ampule. After evacuation to a pressure below 10-3 mm Hg, the am- pule was sealed, and annealed at 900°C for 5 hr. The melt was quenched in water. X-ray analysis confirmed the formation of a single phase of SnTe or SnSe. The other samples, SnTel-,Sex were synthesized from these SnTe and SnSe by mixing them in the required ratio, followed by annealing at 900°C and quenching. These samples were used directly for D.T.A. For X-ray measurements, samples were annealed at 700°, 600°, or 500°C for 100 hr or at 300°C for 150 hr, and then quenched in water. It was found that the lattice constants of the SnTe phase annealed for 150 hr at temperatures above 500°C did not differ from those annealed for 100 hr at the same temperatures. However the X-ray phase analysis showed that at 300°C the annealing for 150 hr was necessary to attain a true equilibrium state. D.T.A. The solid-liquid equilibrium temperature was determined from D.T.A. measurements. The sample was sealed in an evacuated silica tube and molybdenum powders sealed in an another tube were used as a reference material. The sample and the reference tube were placed in a nickel block and were heated from room temperature to 900°C at a rate of 3°C per min and then cooled down at the same rate to 600°C. Thermocouples for these measurements were Pt-Pt. Rh (10 pct) and the error of temperature measurements was within + l0C. D.T.A. curves were obtained on a two-pen recorder and an automatic controller (PID type) was used for the program of heating and cooling. When temperature reaches the solidus from the low-temperature side, there appears an endothermic peak. The solidus temperature was determined by extrapolation of the straight portion of the starting flank of this peak to the base line. In a similar way, the liquidus temperature was determined from an exothermic peak on D.T.A. cooling curve. In the case of supercooling, if any, its degree can be estimated from the magnitude of the abrupt temperature rise. X-Ray . X-ray powder patterns were taken by a diffractometer using CuK, radiation. Since the SnSe crystal is cleaved easily, the powders become flaky when SnSe-rich samples are ground in an agate

Jan 1, 1969

By F. H. Buttner, H. Udin, J. Wulff

Using a modified Udin, Shaler, and Wulff technique, the surface tension of gold Udin, purified helium was found to be 1400 ± 65 dynes per cm for the temperature range 1017° to 1042°C. IN the original Udin, Shaler, and Wulff technique for measuring the surface tension of copper: variously weighted wires were allowed to extend or contract in a copper cell held at elevated temperatures in vacuum. By plotting stress vs. strain for a wire array in one test, the stress at zero strain is obtained. This is the point where the contractile forces resulting from surface tension are balanced by the applied load, according to the expression: y = e=o r [1] where y is the surface tension in dynes per cm; a,,,, the stress at zero strain in dynes per cm; and T, the radius of the wire in cm. The assumption that the wires deform viscously permits the drawing of a straight line through the points on the stress-strain plot. Justification of the assumption has received further experimental support recently.'-' The presence of grain boundaries in the wires requires a correction to the original expression used." Thus: y = d4=T [l- (dl) (ar)Y1 [2] where, n/l is the number of grain boundaries per unit length, and a, the ratio of grain boundary tension to free surface tension. Alexander, Kuczynski, and Dawson in studying the creep of gold wire in vacuum were unable to obtain reproducible values of the surface tension of gold. In plotting stress vs. strain for progressively longer times, they found that the stress at zero strain drifted with time from positive stress values to negative values. Similarly, for the surface tension of silver, reproducible values were obtained only when a purified helium atmosphere was substituted.' Evidently the evaporation rate of silver in vacuum is too high at the temperatures employed to obtain solid-gas equilibrium even in a similar metal enclosure. Thus reproducibility of results is lost. Experimental Procedure The experimental procedure was much the same as that originally developed by Udin, Shaler, and Wulff with a few modifications and improvements. For greater accuracy in strain measurements, knots gave way to cut gage marks as shown in Fig. 1. These were made with a hand-driven lathe in which razor blades serv'ed as cutting tools. Also a more precise cathetometer with a screw accurate to 0.00015 cm was used. The tests were conducted in an atmosphere of purified .helium rather than in vacuum in order to avoid possible evaporation difficulties. Five mil wire of high purity gold (99.98 pct) was used. After cutting in the gage marks, each wire of a series of about 12 was differently loaded by welding a gold ball to one end. This was done by dipping the end of the wire in a cooling gold droplet, previously melted on a charcoal block with a No. 2 acetylene torch. The other end of the wire was strung through a hole in a gold lid and twisted over the edge to hold the wires fixed and in suspension from the lid. The lid and mounted wires were then dipped in pure ethyl alcohol to dissolve any skin oils and dirt on the surface of the wires due to handling. Finally the lid was put in place on an alundum crucible lined with gold so that the wires hung freely within the gold-lined chamber. This whole assembly was next heated in a quartz nichrome wound tube furnace and heated for a few minutes at 600°C to soften the wires. After this anneal the wires were easily straightened with tweezers. The wire assembly was finally annealed 10" to 25°C above the subsequent test temperature for 2 hr. This treatment allowed the grains to grow to equilibrium size and shape. After the anneal, the lid was mounted in front of the cathetometer. The gage length was measured by sighting the 40 power microscope on the upper lip of the lower gage mark for the first reading, then traveling up to the lower lip of the upper gage mark for the final reading. This procedure was repeated four times to give an average gage length value. In this manner the annealed gage length and the final gage length could be measured to determine the strains. During all measurements, grain counts were made.

Jan 1, 1952

By Alexander Squire

ONE of the principal factors that have contributed to the hesitancy of design engineers to use metal-powder parts is the difficulty experienced in the determination of the mechanical properties of compacted components. Because standard test: methods cannot usually be applied in the inspection of such parts, and because adequate special test methods have not been developed, it has been considered desirable to investigate the methods that are applicable. These may then be included in specifications for metal-powder materials' and components in order that the design engineer may be assured that the subject parts possess the desired mechanical properties for satisfactory performance. It is known that direct relationships exist between usually nonmeasurable properties as tensile strength and elongation and shear strength and the angle through which compacts may be plastically deformed before fracturing. These correlations are valuable in the inspection of specific parts, but it is necessary to set up standards before they may be satisfactorily employed. Apart from the use of correlations, the number and character of the inspection methods that are applicable to almost all powder parts is limited to three-chemical analysis, density, and hardness. The last of these may or may' not be a pertinent characteristic, since the indentation hardness of many powdered-metal materials is so low as to have little significance. It is, however, occasionally desirable to use hardness measurements as an indication of the uniformity of the structure of pieces of a given type. Chemical analysis reveals very little about the physical properties of metal-powder compacts, since the unpressed powder is usually of a composition almost identical with that of the finished pieces. Density determinations are simple, to perform and have the advantage of being nondestructive in character. If the dimensions of a machine part are known (and usually they are), the average density may be determined by weighing a given number of pieces and dividing by the calculated volume of the parts. More accurate measurements may be made by the water-displacement method. , It. is recognized that mechanical properties of metal-powder materials are related to their density, but usually these relations are determined for only one type of powder, processed under a given set of conditions. Comparisons of the properties of compacts formed from different types of powders are made on the basis of compacting... pressures instead of density, and for. this reason the results obtained by using powders of different types appear widely variant.

Jan 1, 1947

By Alexander Squire

One of the principal factors that have contributed to the hesitancy of design engineers to use metal-powder parts is the difficulty experienced in the determination of the mechanical properties of compacted components. Because standard test methods cannot usually be applied in the inspection of such parts, and because adequate special test methods have not been developed, it has been considered desirable to investigate the methods that are applicable. These may then be included in specifications for metal-powder materials and components in order that the design engineer may be assured that the subject parts possess the desired mechanical properties for satisfactory performance. It is known that direct relationships exist between usually nonmeasurable properties as tensile strength and elongation and shear strength and the angle through which compacts may be plastically deformed before fracturing. These correlations are valuable in the inspection of specific parts, but it is necessary to set up standards before they may be satisfactorily employed. Apart from the use of correlations, the number and character of the inspection methods that are applicable to almost all powder parts is limited to three—chemical analysis, density, and hardness. The last of these may or may not be a pertinent characteristic, since the indentation hardness of many powdeied-metal materials is so low as to have little significance. It is, however, occasionally desirable to use hardness measurements as an indication of the uniformity of the structure of pieces of a given type. Chemical analysis reveals very little about the physical properties of metal-powder compacts, since the unpressed powder is usually of a composition almost identical with that of the finished pieces. Density determinations are simple to perform and have the advantage of being nondestructive in character. If the dimensions of a machine part are known (and usually they are), the average density may be determined by weighing a given number of pieces and dividing by the calculated volume of the parts. More accurate measurements may be made by the water-displacement method. It is recognized that mechanical properties of metal-powder materials are related to their density, but usually these relations are determined for only one type of powder, processed under a given set of conditions. Comparisons of the pioperties of compacts formed from different types of powders are made on the basis of compacting pressures instead of density, and for this reason the results obtained by using powders of different types appear widely variant.

Jan 1, 1947

By Alexander Squire

One of the principal factors that have contributed to the hesitancy of design engineers to use metal-powder parts is the difficulty experienced in the determination of the mechanical properties of compacted components. Because standard test methods cannot usually be applied in the inspection of such parts, and because adequate special test methods have not been developed, it has been considered desirable to investigate the methods that are applicable. These may then be included in specifications for metal-powder materials and components in order that the design engineer may be assured that the subject parts possess the desired mechanical properties for satisfactory performance. It is known that direct relationships exist between usually nonmeasurable properties as tensile strength and elongation and shear strength and the angle through which compacts may be plastically deformed before fracturing. These correlations are valuable in the inspection of specific parts, but it is necessary to set up standards before they may be satisfactorily employed. Apart from the use of correlations, the number and character of the inspection methods that are applicable to almost all powder parts is limited to three—chemical analysis, density, and hardness. The last of these may or may not be a pertinent characteristic, since the indentation hardness of many powdeied-metal materials is so low as to have little significance. It is, however, occasionally desirable to use hardness measurements as an indication of the uniformity of the structure of pieces of a given type. Chemical analysis reveals very little about the physical properties of metal-powder compacts, since the unpressed powder is usually of a composition almost identical with that of the finished pieces. Density determinations are simple to perform and have the advantage of being nondestructive in character. If the dimensions of a machine part are known (and usually they are), the average density may be determined by weighing a given number of pieces and dividing by the calculated volume of the parts. More accurate measurements may be made by the water-displacement method. It is recognized that mechanical properties of metal-powder materials are related to their density, but usually these relations are determined for only one type of powder, processed under a given set of conditions. Comparisons of the pioperties of compacts formed from different types of powders are made on the basis of compacting pressures instead of density, and for this reason the results obtained by using powders of different types appear widely variant.

Jan 1, 1947

By William A. Johnson

The mathematical analysis of diffusion curves in solid metals is carried out ordinarily by analogy with the flow of heat in a continuous medium and no account is taken of the fact that the materials involved are composed of discrete particles that move discrete distances at irregular intervals. It is possible to treat the problem on the basis of simple assumed atomic mechanisms, in which case, because of the small scale of the elementary process compared to the gross effects observed experimentally, the two procedures lead to the same expression for the variation of concentration with distance. Thus, for engineering purposes, the usual methods are quite satisfactory. If, on the other hand, our purpose is to go beyond the mere collection of data, however desirable this may be, it is necessary to recognize and understand the factors that are of fundamental importance. One factor that has not hitherto been considered when dealing with solid metals is the difference in atomic weights of the isotopes of a single metal. While all the atoms of a given element are alike chemically, their weights may vary by a small but significant amount, and atoms of different weights may have different diffusion rates. With gases this variation in isotopic weight produces a change in the rate of diffusion by a factor inversely proportional to the square root of mass. While, except for the lightest gases, this is not a large effect, it is, for example, sufficient to permit a considerable concentration of one isotope at the expense of others. If metals exhibit a similar phenomenon, some modification of the analysis of the diffusion process will be required, since the different isotopes of a given metal will have different probabilities of moving and the heat-flow analogy will contain a fundamental error. This situation cannot be rectified by using a diffusion coefficient based on the average probability of moving, and it can be shown that even when the diffusion coefficient is independent of composition, the diffusion curve will not agree with the simple theory except in the rare cases where only one isotope exists; e.g., gold. If, however, the mass effect in the solid state were no larger than in the gaseous, the errors arising therefrom in the analysis of ordinary diffusion curves would be quite negligible. Nevertheless, our desire to obtain all possible information concerning the details of the diffusion process, and the possibility of diffusion in the solid state as a means for separating isotopes are cogent reasons for undertaking an experimental study to determine whether isotopes of different masses diffuse at different rates. Experimental Procedure If isotopes of different masses diffuse at different rates, the ratio of the concentration of one relative to another will vary with the distance from the diffusion inter-

Jan 1, 1946

By William A. Johnson

The mathematical analysis of diffusion curves in solid metals is carried out ordinarily by analogy with the flow of heat in a continuous medium and no account is taken of the fact that the materials involved are composed of discrete particles that move discrete distances at irregular intervals. It is possible to treat the problem on the basis of simple assumed atomic mechanisms, in which case, because of the small scale of the elementary process compared to the gross effects observed experimentally, the two procedures lead to the same expression for the variation of concentration with distance. Thus, for engineering purposes, the usual methods are quite satisfactory. If, on the other hand, our purpose is to go beyond the mere collection of data, however desirable this may be, it is necessary to recognize and understand the factors that are of fundamental importance. One factor that has not hitherto been considered when dealing with solid metals is the difference in atomic weights of the isotopes of a single metal. While all the atoms of a given element are alike chemically, their weights may vary by a small but significant amount, and atoms of different weights may have different diffusion rates. With gases this variation in isotopic weight produces a change in the rate of diffusion by a factor inversely proportional to the square root of mass. While, except for the lightest gases, this is not a large effect, it is, for example, sufficient to permit a considerable concentration of one isotope at the expense of others. If metals exhibit a similar phenomenon, some modification of the analysis of the diffusion process will be required, since the different isotopes of a given metal will have different probabilities of moving and the heat-flow analogy will contain a fundamental error. This situation cannot be rectified by using a diffusion coefficient based on the average probability of moving, and it can be shown that even when the diffusion coefficient is independent of composition, the diffusion curve will not agree with the simple theory except in the rare cases where only one isotope exists; e.g., gold. If, however, the mass effect in the solid state were no larger than in the gaseous, the errors arising therefrom in the analysis of ordinary diffusion curves would be quite negligible. Nevertheless, our desire to obtain all possible information concerning the details of the diffusion process, and the possibility of diffusion in the solid state as a means for separating isotopes are cogent reasons for undertaking an experimental study to determine whether isotopes of different masses diffuse at different rates. Experimental Procedure If isotopes of different masses diffuse at different rates, the ratio of the concentration of one relative to another will vary with the distance from the diffusion inter-

Jan 1, 1946

By William A. Johnson

THE mathematical analysis of diffusion curves in solid metals is Carried out ordinarily by analogy with the flow of heat in a continuous medium and no account is taken of the fact that the materials involved are composed of discrete particles that move discrete distances at irregular intervals. It is possible to treat the problem on the basis of simple assumed atomic mechanisms, in which case, because of the small scale of the elementary process compared to the gross effects observed experimentally, the two procedures lead to the same expression for the variation of concentration with distance. Thus, for engineering purposes, the usual methods are quite satisfactory. If, on the other hand, our purpose is to go beyond the mere collection of data, however desirable this may be, it is necessary to recognize and understand the factors that are of fundamental importance. One factor that has not hitherto been considered when dealing with solid metals is the difference in atomic weights of the isotopes of a single metal. While all the atoms of a given element are alike chemically, their weights may vary by a small but significant amount, and atoms of different weights may have different diffusion rates. With gases this variation in isotopic weight produces a change in the rate of diffusion by a factor inversely proportional to the square root of mass. While, except for the lightest gases, this is not a large effect, it is, for example, sufficient to permit a considerable concentration of one isotope at the expense of others. If metals exhibit a similar phenomenon, some modification of the analysis of the diffusion process will be required, since the different isotopes of a given metal will have different probabilities of moving and the heat-flow analogy will contain a fundamental error. This situation cannot be rectified by using a diffusion coefficient based on the average probability of moving, and it can be shown that even when the diffusion coefficient is independent of composition, the diffusion curve will not agree with the simple theory except in the rare cases where only one isotope exists; e.g., gold. If, however, the mass effect in the solid state were no larger than in the gaseous, the errors arising therefrom in the analysis of ordinary diffusion curves would be quite negligible. Nevertheless, our desire to obtain all possible information concerning the details of the diffusion process, and the possibility of diffusion in the solid state as a means for separating isotopes are cogent reasons for undertaking an experimental study to determine whether isotopes of different masses diffuse at different rates. EXPERIMENTAL PROCEDURE If isotopes of different masses diffuse at different rates, the ratio of the concentration of one relative to another will vary with the distance from the diffusion inter-

Jan 1, 1946

By T. A. Read, M. W. Burkart

The crystal geometry of the cubic-tetragonal interface after partial transformation of an indium-thallium alloy single crystal is described and a general theory is presented. The effects of applied stresses on this transformation are interpreted and the latent heat of transformation is obtained from observations of transformation under stress. A DIFFUSIONLESS phase transformation between face-centered cubic and face-centered tetragonal structures has been reported for the indium-thallium system by Bowles, Barrett, and Guttman1, 2 The transformation takes place at approximately 105 "C at 18 atomic pct Tl and 25°C at 23 pct Tl. In their study, Bowles, Barrett, and Guttman used poly-crystalline samples whereas in the present study single crystals were used to eliminate the transformation constraints imposed by adjoining grains. The use of single crystals made possible a comprehensive study of the effect of stress on the transformation. In the course of the work, it was possible to formulate a new method of analyzing dif-fusionless transformations (presented in this paper) which permits calculation of the geometry of the interphase interface from a knowledge of the crystal structures of the initial and final phases. The specimens were prepared from chemically pure thallium and 99.97 pct In which were weighed out to produce 3 to 4 grams of alloy of the desired concentration. The metal was placed in clean fused silica tubing, then melted, degassed and sealed under vacuum. (To obtain single crystals, it was found that both degassing and extreme cleanliness were essential.) Single-crystal specimens were grown by a modified Bridgman technique.8 pecimens were removed from the tube by dissolving the quartz in concentrated hydrofluoric acid which attacks the specimen very slowly. The specimen then was polished mechanically to produce four flat surfaces, electropolished, and annealed at 140°C for 48 hr. The electropolishing solution used was that described by Bowles, Barrett, and Guttman and the polishing was carried out on both the high and low temperature phases of the alloy. The high temperature polishing was done at 110°C with a stainless steel cathode. Visual Observation of the Transformation in Single Crystals A visual study of the transformation was made on specimens which had been electropolished in the high temperature phase. The specimens were supported on the stage of a metallograph by an electrically heated holder which contained an opening for observing the specimen. Visual evidence of transformation was found in the presence of an interface which separated the two phases. The interface plane defines the boundary of the phase undergoing transformation and manifests itself by the sharp change in angle between the surface of the specimen and the incident light at the juncture of the two phases. On slow cooling, well-annealed specimens transformed from the face-centered cubic structure to the face-centered tetragonal structure by the motion of a single plane interface which traversed the specimen from one end to the other. Upon heating, the interface moved back in the reverse direction. The interface could be started, stopped, or reversed at will. A temperature hysteresis of about 31/2oC was observed in the reversal of the interface. Holding an interface stationary caused it to disappear completely in most cases, whereas in other instances the interface became less distinct depending upon its orientation. The interface could be made to reappear by changing the temperature of the specimen. The low temperature tetragonal structure exhibits only the fine markings or subbands reported by Bowles, Barrett, and Guttman and is illustrated in Fig. 1. These subbands are twin-related. Back-reflection Laue patterns show the breakup of the cubic spots into pairs of spots corresponding to the twin orientations of the tetragonal phase.

Jan 1, 1954

By Che-Yu Li, J. L. Gregg, W. F. Brehm

Oriented, oxygen-doped niobium bicrystals were tested in liquid lithium. The grain boundaries were attacked preferentially. The depth of the penetrated zone varies as (time)2. The penetration was aniso-tropic, had a high activation energy, and increased with the increased oxygen doping level. A possible model was proposed to account for the experimental observations. 1 HE grain boundary penetration of a metallic system by liquid metal has been studied by several investigators. Their results are summarized by Bishop.' Most of these works show that the penetration by liquid metal corresponds to the phenomenon of liquid metal wetting. In the case of a grain boundary, wetting will occur when twice the solid-liquid interfacial tension is smaller than the grain boundary tension resulting in the replacement of the grain boundary by two new solid-liquid interfaces. Other possibilities exist; for example, the atoms of the liquid metal may diffuse into the grain boundary region due to chemical potential gradient. The gradient can be produced by impurity segregation or simply be due to the increase in solubility in the grain boundary region. The penetrated grain boundary in these cases may remain solid at the test temperature. The Nb-Li system has been of considerable interest because of its possible technological applications. For fundamental interest it provides a possibility of studying the grain boundary penetration process which is not controlled by the wetting mechanism. The pure niobium is not attacked by the liquid lithium, but if niobium containing more than 300 to 500 ppm oxygen by weight is exposed to liquid lithium, corrosion occurs at the solid-liquid interface and preferentially at grain boundaries. Previous investigators2-' have proposed that this preferential corrosion at grain boundaries is caused by oxygen segregation there, with subsequent inward diffusion of lithium to form a Li-Nb-0 compound. These investigators also found that the corrosion could be retarded by adding 1 pct Zr to the niobium to precipitate the oxygen as ZrO2 upon proper heat treatment. However, there are no quantitative data on the kinetics of the grain boundary penetration process to test the validity of the proposed corrosion mechanism. In this work an investigation of this penetration process in oriented bicrystals was made as a function of the oxygen doping level in the bulk niobium and the grain boundary orientation. A possible model for the penetration process based on the experimental results was proposed. EXPERIMENTS Oriented niobium bicrystals were grown by arc-zone melting oriented single-crystal seeds.7 These bicrystals contained simple tilt boundary. The [001] directions in the two grains were tilted about a common [110]. The bicrystals were 31/2 in. long and 5 by 4 in. in cross section with the straight, symmetric, planar grain boundary longitudinally bisecting the crystal rod. The bicrystals were doped with oxygen by anodically depositing a layer of Nb2O on the surface in a 70 pct HNO solution at 100 v, using a stainless-steel cathode. The specimens were homogenized by annealing in evacuated quartz tubes at 127 5°C. Oxygen content of the niobium was measured from microhardness values, after DiStefano and Litmman.' Supplementary checks were made with vacuum-fusion analysis.7 Individual test specimens cut from the doped bi-crystal rods, about by by % in. in size, were tested inside double jacket sealed capsules. The inner jacket was niobium, the outer was stainless steel. The niobium inner jacket eliminated the problem of dissimilar-metal mass transfer.' The lithium (99.8 pct pure, obtained from Lithium Corp. of America) was handled only in a purified argon atmosphere in a Blickman stainless-steel glove box. After introduction of lithium, the capsules were sealed by welding. Further detailed experimental procedures are given in Ref. 7. The capsules were heat-treated in vertical Marshall resistance furnaces. Temperatures were controlled to When heating above 1100°C, it was necessary to seal the furnace work tube and flow argon through to prevent failure of the stainless-steel outer jacket of the capsule. Tests were made on 6" 2", 16" 2, and 33" i2" bicrystals at oxygen levels up to 2600 ppm by weight in the 6' and 16" crystals and with 1300 ppm oxygen in the 33' crystals. The oxygen levels were controlled to 100 ppm. Most of the quantitative data were obtained from 16" bicrystals between 800" and 1050°C. The capsules were quenched into water after the test and cut open with a water-cooled abrasive wheel. The capsules were then submerged in water, which dissolved the lithium and freed the specimen. Measurement of the depth of the penetrated zone in the grain boundary was done either on metallographically prepared surfaces or directly on the grain boundary plane after the specimen was fractured in tension in the grain boundary plane. The depth of penetration measured by both methods agreed well. Further details describing these techniques have been reported elsewhere.'p7

Jan 1, 1969

By R. T. Hukki, P. Voutilainen

This paper describes a new apparatus for continuous wet fine-screening. Its preferred size range seems to be from 0.1 to 1 mm. The supercritical trommel screen is a short cylindrical trommel of wedge-bar type construction operated at a speed greater than the calculated theoretical critical speed and at a speed lower than the speed at which particles introduced into it will centrifuge. The paper describes results obtained with the prototype supercritical trommel screen in pilot plant scale. The results point to a high capacity and simultaneously to a high sharpness of screening. Finally, an analysis is presented of the forces acting in screening on a supercritical trommel screen. In the era of high speed, high capacity processing of raw materials the conventional slowly rotating trommel screen is often considered a relic from the times passed. A typical trommel screen is the cylindrical trommel rotated about a horizontal or slanting axis at a relatively low speed. Its screening characteristics are well known. Trommel screens of various types of construction, methods of operation, performances and other characteristics have been described in detail by Taggart.1 The theoretical critical speed of a trommel screen is defined by the same well known equation as that applied for grinding mills: where ncritical = the numerical value of the theoretical critical speed in rpm, D 1 = the inside diameter of the trommel in feet, and D2 = the inside diameter of the trommel in meters. ncritical corresponds also to the centrifuging speed provided that the coefficient of friction f between the trommel surface and the outer layer of the charge is = 1.0. In a general case: From Eq. 2 it is seen that in all cases where f < 1.0 the centrifuging speed of the trommel is greater than the theoretical critical speed. The supercritical trommel screen concerns screening operations within that speed range which is between the theoretical critical speed defined by Eq. 1 and the centrifuging speed defined by Eq. 2, under conditions such that the coefficient of friction f<1.0. It is reported by Taggartl that the optimum speed of a conventional cylindrical trommel screen 36 in. in diam was experimentally found to be about 16 rpm. From Eq. 1, the critical speed of this trommel is 44.2 tpm. The indicated optimum speed corresponds to (16/44.2) x 100% = 36.2% of the theoretical critical speed. The optimum speed range based on information available seems to vary from 33% up to 45% of the theoretical critical value. The trommel screen operated at a supercritical speed: operates at a speed greater than the calculated theoretical critical speed; operates at a speed lower than the speed at which the charge introduced into it will centrifuge; operates within the supercritical speed range in such a way that the coarse fraction of the charge must slide in respect to the inside surface of the trommel; the outer layer of the said fraction next to the screen tends to proceed in the same direction as any selected point on the trommel surface, but now at a lower speed, and indeed at a subcritical speed; allows to a certain degree adjustment of the maximum determining particle size x of the fine product simply by a variation of the speed of the trommel within the supercritical speed range. With increasing trommel speed, finer and finer material only will get the opportunity to find its way into the fine product while the screen opening remains constant. In conventional practice, the low speed trommel is generally used for sizing of coarse and medium coarse material, but seldom for fine screening. The characteristic feature of the product passed through the conventional trommel is that the determining size x of the biggest particle is barely smaller than the nominal size of screen opening. The supercritical trommel screen, on the other hand, is best suited for sizing of relatively fine material. Furthermore, the characteristic determining size x of the biggest particle in the fine product can be substantially smaller than the nominal width of the screen opening or slot. In the trommel screen best suited for the applications

Jan 1, 1965

By G. S. Cole, G. F. Bolling

ThE exact type of fluid flow which occurs in a solidifying ingot is important in determining subsequent grain structure. This has been shown in studies of natural Convection" and of forced stirring or other disturbances of the melt."16 We shall explicitly argue that a complement to the existing natural flow in an ingot should be more effective than other types of flow in promoting the columnar-to-equiaxed transition. The ultimate effects of fluid flow upon structure is one of the topics of solidification that we have investigated in the alloy system Pb-Sb, under conditions simulating casting. In Fig. 1, the essential features of a bidirectional growth apparatus are shown; horizontal freezing from water-cooled faces within a low-thermal-conductivity lavite boat is a reasonable simulation of an ingot section. Details such as the furnace and thermocouples are omitted in order to show the location of four permanent. magnets, each with a pole separation of 21 in. providing a central field of about 1000 Gauss. When coupled with a dc current imposed through appropriate connections made at the cooled faces, a flow of fluid is produced as shown schematically. This technique described by Pfann and ~orsi" is ideal for our purpose since the flow indicated is the same as that we observe to occur naturally in this system. Components of 99.999 pct purity were used for study and all due precautions were taken in alloy preparation to avoid contaminants. Sections of the specimens were taken to ensure results representative of the interior as well as the surface of specimens. All proportions of equiaxed and columnar regions were measured by tracing the etched grain structures onto graph paper and simply counting squares. Four alloys were examined at superheats of 40" * 5°C and 100" * 9°C. Preliminary tests had shown that no appreciable enhancement of structure was obtained with magnetic field alone, so that this condition is not reported; it should nevertheless be noted that other configurations of magnetic field will reduce convection and thus enhance columnar growth.&apos;8 For the tests reported the magnetic field was applied to a specimen by bringing the four preassembled magnets to a position 2 mm from an outer tube immediately after the ingot was poured. The dc current of 30 amps passed through the sample throughout the entire solidification cycle, resulting in a power dissipation of 9 w per sq cm of interface. This may be compared to the evolution of latent heat of approximately 18 w per sq cm. Table I contains the results of this experiment in terms of the total area ratio, equiaxed/columnar grains, as a function of the field interactions, solute concentrations, and superheats employed. The total structure of the ingot is seen to be most influenced when both the field and current are applied simultaneously; when current acts separately, little effect may be noted in spite of the heat supplied. In addition, the change in structure from the no field-no current case to the field-current condition is more pronounced at the higher superheat, and the higher the concentration of antimony. An example of the grain refinement, as well as the increased equiaxed zone, is shown in Fig. 2. It is now important to prove that there is indeed an increase in fluid flow due to the presence of the field-current interaction; this is done by temperature measurements in the liquid metal. Let us consider a bidirectional casting in which heat is applied to and removed from the system, in such a way that rate of solidification is zero.* When a sensitive thermocouple

Jan 1, 1967

By Garth M. Crosby

Hugh E. McKinstry (Professor of Geology, Laboratory of Mining Geology, Harvard University, Cambridge, Mass.) Pre-Cambrian age for the Coeur d&apos;Alene mineralization, as indicated by isotope studies and recently discussed by Silverman, Long, and Kulp&apos; would explain some features of the mineralogy of the district that have long been a puzzle. In the Silver Belt, especially in the Sunshine mine, lead-zinc min erali zation passes downward into tetrahedrite ore. Although commercially speaking this is a rich silver zone, the silver is, quantitatively, a mere impurity amounting to a small fraction of 1 pct. In effect the zonal change is from lead-zinc down into copper mineralization—-the usual zonal change that occurs in many districts. In the Burke-Mullan portion of the district, on the other hand, lead-zinc ore does not pass downward into copper mineralization of the Sunshine type. Instead, pyrrhotite appears in depth while the tenor in lead and zinc declines. The change occurs at increasingly greater depth away from the Gem stocks, deepening irregularly by some 3000 ft within two to four miles. As noted by Crosby, biotite, grunerite, and garnet appear in the deep zone. The marked difference between this apparent zonal change and the more nomal change to a copper zone is quite explainable if already existing pre-Cambrian veins have been locally metamorphosed by a Tertiary intrusive. The chief obstacle to this explanation is the evidence that mineralization cuts Laramide intrusives, but evidence on this point is conflicting as indicated by Crosby&apos;s observations and summary. This is not the first instance of a problem in determining the time-relationship of mineralization to a spatially associated intrusive. At the Noranda mine veins of chalcopyrite extend into a diabase dike which apparently cuts the ore, although Price2 concludes that the ore is later. However, at the Normetal mine diabase of a similar dike is thought3 to intrude the orebody but is cut by stringers of chalcopyrite. In the Sullivan Mine, B. C.,4 galena follows a fracture in a larnprophyre dike which, itself, cuts the main orebody. In the Sudbury district dikes of olivine diabase are clearly younger than the nickel ore, yet where they cut the Creighton orebody they contain stringers of chalcopyrite. In the laboratory, Hawley5 has developed veinlets of sulfide (chalcopyrite) it] silicate gangue by heating specimens of ore in a stream of H2S at 410 °C. From this and other evidernce. it seems clear that sulfides can be transferred from one site to another — at least through short distances — at temperatures well below their melting points. It would seem then that even if sulfide Mineralization in the Gem stocks can be shown unequ ivocably to be later than the intrusive the possibility of "remobiliza tion" need not be more than local. Thus the zonal relationships are quite in accord with a pre-Cambrian age for original deposition of the lead, zinc, copper, silver, and uranium in the Coeur d&apos;Alene district. REFERENCES 1. A. Silverman, A. Long, and J. L. Kulp: Discussion of: The Gem Stocks and Adjacent Orebodies, Coeur d&apos;Alene District, Idaho. Mining Engineering, May 1960, pp. 470-471; AME Trans., 1960, vol. 217, p. 117. 2. Peter Price: Geol. & O. D. at the Home Mine, Noranda, Quebec. Can. Inst. M & M Bull 263, 1934, p. 108; also,Trans. CIMM 1939, pp. 108-140. 3. w. L. Brown Nometal Mine in structural Geology of Canadian Ore Deposits, Montreal, 1948, p. 690. 4. C. O. Swanson and H. C. Gunning: Geology of the Sullivan Mine. Can. Inst. Mining & Met. Trans. vol. 48, 1945, p. 653. 5. J. E. Hawley: Heat Effects on Sulphides and Possible Applications. Univ. Toronto Studies, Geol. Ser. No. 46, 1941, p. 34.

Jan 1, 1961

By Charles W. Goodale

In the course of the preparation of my paper on " The Occurrence and Treatment of the Argentiferous Manganese Ores of Tombstone District, Arizona" (Dam., xvii., 767), my attention was called to two patents which have been issued for the use of a diaphragm at the upper end of a Howell furnace, whose importance merits more than a passing reference. Mr. J. K. Pardee invented and first put into use in the Algon quin mill, at Philipsburg, Mon., in 1880, a (&apos;new&apos; and useful im provement in rotary ore-roasting furnaces," which was intended "to increase the capacity, effectiveness and working economies of such furnaces." The following description and accompanying figures are taken from the patent papers, dated December 21st, 1880: Fig. 1 is a side elevation of the feed-end of the Howell rotary furnace, with parts broken away, the better to exhibit my invention. Fig. 2 is an end elevation of the same. Fig. 3 is an end elevation of the same, showing a modification of my invention. In operating a furnace of this kind, of the capacity of one ton of ore an hour, it was found that for the best work the two fire-places (one at each end of the revolv ing cylinder) consumed about ten cords of wood every twenty-four hours, and that about twenty-fonr tons of silver-ore were introduced through the feed-pipe. It was also found that of the amount of ore, fully one-third did not go through the revolv ing cylinder, but went into the dust-chanibers about the feed-end of the furnace or cylinder, and this ore going into the dust-chambers was found not to be sufficiently chloridized for amalgamation, but had to be re-roasted. I then caused to be made, out of boiler-plate iron, a segment of a circle, the height of which was about one third of the diameter of. the cylinder or furnace, the circumference of the circle being smaller than the circumference of the furnace, so that about a half-inch space would be left between the plate and the furnace, when said plate or segment was in position. This segment or plate of iron was then fastened to the bottom of the feed pipe, as shown in the drawings, wherein A represents the revolving cylinder or furnace; B, the fire-place and dust-chambers at the feed-end of said furnace; C, the inclined feed-pipe, and D, the diaphragm, partition, or plate fixed within said furnace, A. With the diaphragm or plate, D, in the position shown, the furnace was run for about a month, and it was found that with the furnace in best working condition only four cords of wood every twenty-four hours were consumed, that no fire was required at the feed-end of the furnace, that not one-twelfth of the ore

Jan 1, 1890

By Charles Wurms, Robert Steinitz

DURING an investigation to determine the compatibility of several metals with tungsten, the degree of reaction between tungsten and lead was determined. A literature survey showed considerable disagreement between the results of various earlier investigators. Information presented by M. Hansen1 states that, according to S. Inouye,2 tungsten has very poor resistance against attack by molten lead, even at the low temperature near the melting point of lead. A phase diagram in the same reference indicates a solubility of 30 wt pct W in molten lead at 1300°C. Contrary evidence was shown by Parkman and shepard3 in their investigation of materials for use in heat transfer systems containing liquid lead alloys; they performed experiments at 980°C for times up to 50 hr without noticing any appreciable attack on the tungsten. Tungsten sheet was immersed in molten lead contained in Vycor tubes evacuated to at least 10-4 mm Hg. R. Bernard4 and R. I. Jaffee5 also indicate that no reaction occurs between molten lead and tungsten. However, no experimental data were included in these reports. In order to settle the question of the solubility of tungsten in molten lead, tungsten powder with an average Fisher subsieve particle size of 6µ was pressed in a double-acting die at 6 tsi to small compacts. They were then sintered in an atmosphere of hydrogen for 2 hr at 1700°C, resulting in a sintered density of 64 pct of theoretical with final dimensions of 0.260 in. in height and 0.245 in. in diameter. For all tests, the tungsten pellets were immersed in molten lead. Table I is a summary of the experimental procedures showing atmospheres, temperatures, and times. The first experiments were performed at 650°C; at this temperature, the liquid lead should wet the porous tungsten better than at its melting point, and penetrate into the pores. The lead was heated in a graphite crucible with a graphite cover. No protective atmosphere was used, as it was expected that the formation of CO would be sufficient to prevent oxidation. This, however, proved to be wrong, and all tungsten samples showed a slight oxide film after treatment. The tungsten samples were immersed in the molten lead for times of 5 min, 10 min, 1/2 hr, 1 hr, and 2 hr. After this time, the melt was poured into a form and the

Jan 1, 1962

GENERAL GEOLOGIC DESCRIPTION The Escalante silver deposit located in southwestern Utah is an epithermal vein system consisting of a hanging wall and footwall vein, straight along strike and dipping about 1.2 rad (70°). The veins consist of banded quartz and calcite fissure fillings between volcanic wall rock that are silicified for some distance outward from the vein. The walls of the veins are sharp and the silver values are irratically distributed through the various bands within the vein. Only very low grade values are to be found in the wall rock on either side. The portion of the veins above the water table have been somewhat leached, with some secondary enrichment below. The mineralogical zonation is variable due to a fluctuating water table through geologic time. SAMPLE MANAGEMENT AND COMPOSITE ASSAYS Sample data for the deposit was obtained from over 50 diamond drill holes, from channel samples cut at intervals across a drift, and from scattered surface trenches along the out- crop of the hanging wall vein. Fig. 13-1 is a surface plan map showing the vein outcrop and some diamond drill locations. Two cross sections through the vein are shown in Figs. 1 3-2 and 13-3. Nearly all of the diamond drill core of vein material was assayed in 0.3-m (I-ft) lengths, from which weighted composite assays were manually calculated for the horizontal thickness of the vein. The centers of the composited samples were plotted in north and east coordinates and by elevation, and locations and assay

Jan 1, 1980

By J. A. Harrison

The physical composition of coal and the distribution of its physical constituents will partially determine the efficiency of the process chosen for coal preparation. Distribution and concentration of coal macerals will, to a degree, be controlled by preparation processes. A number of preparation processes have been evaluated to determine this interrelation. These evaluations will help provide information needed for the production of coal that meets definite petrographic composition specifications. etrographic composition and degree of coalifica-tion of coal can determine the choice of cleaning processes and equipment used in coal preparation. The purpose of this paper is to present data on studies of the preparation processes of breakage, sizing, cleaning, and blending and to show the effect coal&apos;s petrographic composition has on these processes. Herrin (No. 6) and Danville (No. 7) Coals from Illinois were used in these tests. Nomenclature used herein is that approved in the Glossary of the International Committee for Coal Petrology,&apos; based primarily on the Stopes-Heerlen system of classification2 and used in coal petrography laboratories throughout the world. BREAKAGE TESTS Breakage tests of Illinois coals related to petrographic composition have been conducted at various times at the Illinois State Geological Survey. These tests have been classified under two headings -impact tests and compression tests. Impact tests, as the name implies, consisted of breaking the coal by a sharp, sudden force. Impact tests were further divided into fall tests and block tests. Compression tests consisted of applying a constant pressure on a piece of coal until the coal fractured.

Jan 1, 1963

By T. Toda, R. Maddin

A study has been made of the microstructure and mechanical properties of splat-cooled aluminum-base gold alloys with gold concentration from 0.25 to 5.0 wt pct. These alloys have been quenched from the liquid state by a torsion-catapult technique, which has made it possible to pepare specimens suitable for mechanical property measwements. From the electron micrographs it has been shown that the solid solubility of gold in aluminum can be extended to 2.5 wt pct (0.35 at. pct) by splat-cooling, while the maximum equilibrium solubility is known to be less than 0.3 wt pct (0.04 at. pct). The very fine grain size (several tenths of a micron), the extended solid solubility, and the fine dispersion of a second phase (AuAl2) contribute concurrently to a substantial strengthening effect. In Al-5 wt pct Au splat-cooled specimens of less than 50 thickness, the yield strength is 17 kg per sq mm or 6 times as large as the strength of bulk specimens. For the Al-1.0 to 2.5 wt pct Au solid solution obtained by splat-cooling, the yield strength reaches 7.5 kg per sq mm after an aging treatment (for 10 hr at 200°C), while it is 3.7 kg per sq mm for the corresponding bulk specimens. A great deal of research has been done in recent years on the structure and the properties of metals and alloys rapidly quenched from the liquid state.&apos; The term "splat-cool" has been used with the meaning of a rapid quenching from the liquid state., The splat-cooling techniques have produced large numbers of new structures, which are expressed in terms of metastable phases,3 concentrated solid solutions,4 amorphous phases,5&apos;6 new phases,7 and so forth. Nearly all previous studies have concentrated on the physical properties; i.e., crystallography, structure, electrical resistivity, magnetism, and so forth, of the splat-cooled metals and alloys. The mechanical strength of splat-cooled metals and alloys has hardly been investigated except for some recent work by MOSS&apos; on A1-V alloys. The principle common to all experimental techniques developed to obtain very rapid quenching rates is based on the heat transfer by conduction. Liquid must be in good thermal contact with a substrate of high heat conductivity. Both of the published devices known as the "gun" and the "piston and anvil" techniques suffer from certain shortcomings. For example, the specimen obtained by the gun technique is very small and flaky, and hence inadequate for mechanical properties measurements. On the other hand if the material is forced to yield a continuous speci- men by the piston and anvil technique, it is probable that some plastic deformation occurs during the quench. A novel method for rapid quenching of a liquid metal or alloy, the "torsion-catapult", has been devised by Roberge and Herman9 at the University of Pennsylvania. In the apparatus the melt is thrown out of a curved furnace by a catapult and impinges on a copper substrate. The apparatus has the advantage of producing a continuous foil which is relatively large in size and of a quality suitable for the measurements of mechanical properties. The quenching rate is estimated to be of the order of l05 to l06 ºC per sec, (comparable to rates achieved by the piston and anvil technique). In selecting an alloy to be studied we were made aware of the fact that gold was believed to be "insoluble" in in and consequently age hardening in the A1-Au system appeared to be interesting. Quite recently Heirnendahl13-15 revealed that the solid solubility, as determined by transmission electron microscopy, was 0.3 wt pct Au at 640°C and 0.25 wt pct Au at 600°C, decreasing with decreasing temperature. In an A1-0.2 pct Au alloy after quenching from a solution treating temperature of 600°C the yield stress was 2 kg per sq mm, and it increased up to 6 kg per sq mm after aging for 1 to 10 hr at 200°C. The precipitation occurred in the form of platelike particles mainly on (100) matrix planes. The intermediate phase n&apos;, the equilibrium phase n (AuAl2), and lattice relationships between both precipitates and the matrix were also investigated by electron microscopy. One of the purposes of the present research is to determine whether or not the solid solubility in this system, in which gold has a very small solubility in

Jan 1, 1970

By d&apos, K. Mukherjee, C. R. Antonio, R. J. Maciag, G. J. Fischer

Tensile data indicate that over the range of strain rates 10-5 to 10-1 sec-1 and in the temperature range 298° to 743°K the flow stress at a given temperature may be expressed as: C0 = Cem where m changes abruptly at a critical strain rate of 10-2 sec-1. The Zener-Hollomon parameter was tested and found to be invalid except at temperatures exceeding 700° K. Values of AH calculated for temperatures above 700°K ranged from 30 to 47.5 kcal per g-mole. ThE flow characteristics of aluminum and aluminum alloys as a function of temperature and strain rate have been of interest to various experimenters for many years. Trozera et al.1 determined tensile flow curves for pure aluminum and concluded that the combined effect of temperature and strain rate on the flow stress could be related using the Zener-Hollomon parameter. More recently, Hockett2 proposed a relationship between compressive flow stress, temperature, and true strain rate which could be represented by a surface. Holt et al.3 studied strain rate effects on flow stress in a number of aluminum alloys at room temperature. It was determined that there is a critical strain rate above which a strain rate effect is observed. It was also reported that the strain rate sensitivity was significant in aluminum alloys in the "0" condition only. In a recent review paper McQueen4 has considered a number of mathematical expressions which have been used to describe the relationship between stress, strain rate, and temperature. These expressions have been applied to the flow characteristics of a number of different metals and alloys including aluminum. In the present work the strain rate sensitivity of 7075-0 aluminum was determined in the temperature range of 298° to 743°K. The tensile flow stress at 0.2 pct offset was obtained over a nominal strain rate range of 10-5 to 10-1 sec-1. EXPERIMENTAL Threaded tensile specimens were cut from a single heat of 7075-T6 aluminum. The composition of this heat is given in Table I. The test bars had a gage section 1.5 in. long by 0.250 in. diam and conformed to ASTM specification E-8-57T. After machining, the bars were annealed at 413° ± 10°C for 2 hr. They were then cooled to 260°C in 3 hr, and finally air cooled to room temperature. This treatment is commonly used to produce the "0" condition. Load-time curves at constant crosshead speeds were obtained at various temperatures using an Instron testing machine. Crosshead speeds ranged from 0.002 to 40 in. per min. A three-zone resistance tube furnace was used for the elevated-temperature tests. Temperatures were measured at three points along the gage length by means of suitably placed thermocouples. Each tensile bar was held at temperature for 30 min prior to testing and the maximum temperature variation along the gage length was kept below 1°C. In all, 275 samples were tested and each data point plotted is an average of at least two tests. In many cases the point represents up to six tests. RESULTS AND DISCUSSION Values of the flow stress at 0.2 pct offset at six different temperatures are plotted vs strain rate on log-log coordinates in Fig. 1. Over discrete ranges of strain rate, the data for each temperature fit the expression:

Jan 1, 1969

By H. S. Choi, I. Iwasaki

The effect of temperature as a parameter in ore flotation has not been systematically studied, although for some ores it has been known for many years that selectivity and grade of concentrates can be improved by conditioning or flotation at moderately or substantially elevated temperatures. In 1934 Coghill and Clemmer&apos; stated that "elevated temperature seems to make hard water more tolerable" in soap flotation, and a cursory examination of the literature indicates that some earlier investigators were aware of beneficial results obtained by floating above room or mill-water temperatures. Tartaron,2 Mitchell et aL.,3 and particularly Hamilton et al.&apos; have shown that high pulp temperatures give high recovery and selectivity in soap flotation of fluorite from a variety of gangue minerals. As a result of the work of these and of other investigators, high-temperature flotation has been successfully applied to industrial flotation of fluorite. Falconer" stated: "The use of high temperature conditioning (above 35°C and preferably above 60°C) in connection with the soap flotation of nonsulphide ores, as covered in B. Kalinowski&apos;s French Patent No. 847,-215, Dec. 7, 1938, is claimed to provide more intense activation, better separation of values from gangue, and reduction in quantity of reagents." The various investigations quoted above clearly demonstrate the improvements to be realized by increasing the temperature at which fluorite is floated, and it is surprising that little or no information has been published on systematic investigation of the same method as applied to other ores. The present article describes comparative results obtained at room temperature and at elevated temperatures by otherwise conventional flotation of iron ores, by single-mineral flotation in the Hallimond tube, and by contact-angle measurements. It is not the purpose of this article to evaluate the commercial feasibility of high-temperature flotation of iron ores, although preliminary calculations show that the cost should not be excessive and that the gains to be realized may well outweigh the extra cost of heating the pulp. LABORATORY FLOTATION TESTS Experimental: All flotation tests reported in this article that use a laboratory Fagergren cell were made on ore A (either containing the primary slimes or deslimed at 20µ as specified) following the preparatory procedures described elsewhere- or this particular ore. Ore A contained hematite, goethite (limonite), quartz, chert, and minor quantities of magnetite. Confirmatory tests made on other ores show that the same general principles apply to ores of similar mineralogy and structure. Conditioning was performed by adding the collector, as a soap, to the vigorously stirred and heated pulp. Conditioning time was 5 min, the pulp contained 60 pct solids, and the equivalent of 0.5 Ib of fatty acid was added per ton of original (unde-slimed) ore. The pH of the pulps ranged from 6.8 to 7.1 (25°C measurement) during conditioning. The pH was adjusted in the flotation cell by addition of either NaOH or H2SO4, the values reported being those of the pulp cooled to 25°C. During conditioning and flotation the pulp temperatures were controlled within l° to 2° by immersion of Variac-controlled Calrod elements in the conditioning beaker and in the cell, and by the use of water, heated to the appropriate temperature, for transferring pulp, adjusting pulp volume, and washing. Selectivity indexes have been calculated on the same basis as those reported in the article by Cooke, Iwasaki, and Choi." Results: Table I gives the results obtained by floating deslimed ore A with pure oleic acid at 25" and 50°C, and Fig. 1 shows the selectivity indexes plotted against pH of flotation. Inspection of Table I

Jan 1, 1961