Search Documents

By E. J. Nielsen, P. R. Strutt

A study has been made of the progressive changes in the distribution of etch-pit structures occurring during high-temperature creep in copper + 7 wt pct Al single crystals oriented with a [113] tensile axis. The two equally stressed glide systems with the highest Schmid factor would be expected to form subboundaries of the type predicted by Kear.2 The alignments of etch-pits on sections parallel to different (111} planes consistent with these types of boundaries were not observed. However, they were consistent with planar subboundaries (on a macroscopic scale). From an analysis of Amelinckx1 it may be shown that stable cross-grid dislocation boundaries may form in the primary slip planes. These boundaries form when dislocations with a Burgers vector not in the slip plane move into the plane by combination of climb and glide. THE geometry of subboundaries formed by the interaction of dislocations of two glide systems has been analyzed by Amelinckx,1 and the particular types produced by deforming fee crystals are predicted by ear.' In this paper types of boundaries which may be formed when climb as well as glide occur are discussed as this is relevant in high-temperature creep. It is assumed in the present investigation that the etch-pits observed in Cu + 7 wt pct A1 on surfaces parallel to {111} planes delineate the sites of dislocations. Although there is no direct evidence for this previous work on a-Cu/Al single crystals by Mitchell, Chevrier, Hockey, and Mon-aghan,3 would show this assumption to be reasonable. The alignments of etch-pits which form during creep are studied on sections parallel to each {111) plane. It is then deduced that these alignments are consistent with a specific type of planar subboundary. The Cu + 7 wt pct A1 single crystals had a [113] tensile axis and Fig. 1(a) shows schematically the relation of the slip planes and slip directions (as represented by tetrahedron ABCD) with reference to the tensile axis. The two equally stressed glide systems with the maximum Schmid factor namely ß-AD and (a-BD, from the analysis of Kear,2 would be expected to form the boundaries shown in Fig. l(a) and (b), also Fig. 5(a) and (b). EXPERIMENTAL PROCEDURE The a-Cu/Al single crystals were grown and annealed in a "gettered" argon atmosphere. Chemical analysis showed the aluminum content to be uniform in each crystal and the difference between crystals was maintained to an accuracy of ± 0.25 wt pct. The initial dislocation density and mean subgrain diameter after annealing was -106 cm-2 and 250 µ, respectively. Surfaces parallel to (111) planes were produced by specially developed electrolytic machining processes. The {111} faces were next electropolished for 5 min in a solution consisting of 25 g chromium trioxide, 113 ml glacial acetic acid and 40 ml water; the applied potential was 8 v. Dislocation etch-pits were revealed using l an etchant described by 1 ml bromine, 45 ml HCl, and - 250 ml water. RESULTS In crystals strained into secondary creep at higher stresses (443 and 750 g - mm-2 at 650° C aligned rows of etch-pits parallel to slip plane traces were evident in sections parallel to the (1111, (ill), and (111) planes, see Fig. 3. As well as the longitudinal alignments in Fig. 3, well formed randomly oriented arrays indicative of an equiaxed subgrain structure are evident. At the lower stresses (100 to 230 g . mm-2) only an equiaxed structure formed during creep. The sections in Fig. 3 are from a crystal crept for 70 hr at 650°C with a CRSS of 443 g.mm-2. Two identically oriented crystals were also deformed at the same temperature and stress for 5 min and 4 hr. In the crystal crept for 5 min, the etch-pits were randomly distributed with no tendency for directional alignment, see Fig. 2(a). As shown in Fig. 2(b) aligned arrays were evident after 4 hr creep but they were not nearly so well defined as in Fig. 3. The alignments (parallel to the arrows) in Fig. 3 are consistent with the existence of boundaries in the two main slip planes a and ß. The way in which this is deduced is seen by reference to Fig. l(c), where the existence of boundaries in the a and ß planes is verified by sectioning parallel to a,ß, and d. The (111) and ß(111) planes intersect the d(111) plane along BC [101 ] and AT [011] and alignments parallel to [101] and [011] are clearly evident in Fig. 3(c) in a section parallel to the d(111) plane. Similarly the a, and ß planes in Fig. l(a) intersect each other along DC [110] and hence there will be an alignment parallel to [110 ] in sections parallel to the a-plane and the ß-plane; this is evident in Fig. 3(a) and Fig. 3(b). It is interesting to note that alignments of etch-pits consistent with the boundaries predicted by Kear2 were not observed; see Figs. l(a) and l(b). The geometry of boundaries in {111} planes as shown in Fig. l(c) is discussed later. In Fig. 4(a) the individual etch-pits are resolved and the alignments are exactly parallel to the slip trace direction [101]. However, in some areas alignments deviate away from the slip trace direction by as much as 10 to 15 deg, this is evident in Fig. 4(b), and in Fig.

Jan 1, 1969

By George R. Cowan

A number of studies hare been reported of the effects produced in metals subjected to deformation by shock waves with maximum pressures ranging from tens to hundreds of kilobars. On the basis of the equations for the flow of mass, momentum, and energy through a stationary shock front, the macroscopic stress-strain curve for the resulting shock deformation can be calculated within narrow limits from the experimentally determined Hugoniol curve. In relatively weak shocks which are preceded by an elastic wave, the stress rises above the clastic limit only as plastic deformation proceeds cold thus the shock has a long toe. In strong shocks that override the elastic wave a high stress is applied without prior plastic deformation. A more important effect of increasing the shock pressure is the generation of shear stresses, called supercrilical shear stresses, that exceed the strength of the perfect lattice. A change in the mechanism of deformation is expected to result from the onset of supercritical shear. The shock disordering of ordered Cu3Au in strong shocks appears to be an example of such a change. It is suggested that the formation of fine twins in copper and nickel and the formation of structures which enable visible twins to be formed in the rarefaction ware, observed in copper and presumably in disordered Cu3 Au, are related to the occurrence of supercritical shear in shock dcformation. In recent years several studies1,2 have been made of the changes in structural and mechanical properties of metals produced by the passage through the metals of strong shock-compression waves ranging from about 50 to 800 kbar pressure. Recent work involving dynamic measurements of the shock compression "Hugoniot" curves 3-8 of many metals has developed techniques and provided data required to obtain the shock pressure and the (transient! plastic deformation produced in the shock-conlpression experirnents.9 Shock deformation has been found to be much more effective than slow deformation in changing the mechanical properties of metals, when the two are compared on the basis of equal plasti strain, Holtzman and Cowan9 made quantitative estimates of the shearing stress occurring in a shock front in a metal by assuming that the shearing stress is similar to that occurring in a shock front in a viscous, heat-conducting fluid, with the addition of a yield stress. Taylor's solution9 for a weak shock was used to estimate pairs of values of shearing stress and thickness of the shock front obtained by assumed choices of the ratio of effective kinetic viscosity to thermal diffusivity. It was noted from these values that. unless the shock front is extremely thin. heat conduction has slight effect, and the shearing stress is nearly independent of the mechanism of deformation. This mechanism does, however, determine the thickness of the shock front and the rate of strain. Furthermore, since the maximum possible shearing stress occurring in shocks of moderate strength does not greatly exceed the shear stress occurring in conventional slow deformation, the mechanism of deformation is not expected to be qualitatively different. The greater effectiveness of shock deformation in changing the mechanical properties of metals can be attributed partly to the fact that dislocations, when driven by near-conventional stresses, cannot keep up with the shock front, thus necessitating a higher dislocation density than required for an equivalent slow strain. The fast uni-axial strain occurring in the thin shock front would also be expected to cause a larger number of dislocation intersections to occur. In the upper range of shock pressures that have been studied the estimated values of the shearing stress exceeded the estimated shear strength of a perfect crystal. Under these circumstances it is reasonable to expect that the mechanism of deformation might be considerably different from that involved in slow deformation. Except for the observation by smith1 of twins in shocked copper, the effects of shock waves on metals did not show any obvious or large changes in properties that would indicate the onset of a change in the mechanism of deformation. The recent investigation of the effect of shock waves on ordered and disordered specimens of Cu3Au by Beardmore, Holtzman, and ever" showed a spectacular decrease in the amount of long-range order retained by initially ordered Cu3Au when the shock pressure was raised from 290 to 370 kbar. Since Dr. Holtzman and I suspected that this behavior probably was due to the onset of a shearing stress in the shock front in Cu3Au which exceeded the limiting shear strength of the perfect crystal. it was considered appropriate to examine directly the shock-front equations for a solid. and to obtain a sound estimate of the shearing stress occurring in the front using equation of state data obtained from shock studies. In this paper an estimate is made of the

Jan 1, 1965

By R. G. Ward, D. R. Gaskell

Using the maximum bubble pressure technique, the densities of iron silicates at 1410°C have been measured blowing helium, nitrogen, and argon. By ensuring equilibrium between the melt and the blowing gas with respect to oxygen potential and by minimizing tempcrature cycling of the furnace, iron precipitation in the melt has been prevented. Thus the previously reported effect of blowing-gas composition on the densities of the melts has been eliminated. Consideration of the oxygen densities of the melts gives an indication of the structural changes accompanying composition change. The density-composition relationship of iron oxide-silica melts in contact with solid iron has been the subject of several investigations1-7 and considerable disparities exist among the various results obtained. Of these investigations, all except one5 have employed the maximum bubble pressure method. In the most recently reported of these investigations1 the density-composition relationship obtained blowing nitrogen differed from that obtained blowing argon. The measured densities obtained under nitrogen were greater than those obtained under argon, the difference being a maximum at the pure liquid iron oxide composition and decreasing with increasing silica content. This observation rationalized the disparities existing among the results of the earlier investigations, showing that two lines, one for nitrogen and the other for argon, could be drawn to fit all the earlier results. No explanation for this phenomenon could be offered. Chemical analysis of rapidly quenched samples of melt for dissolved nitrogen, and direct weighing measurements, excluded solution of nitrogen in the melt from being the cause of the increase in density. The range of blowing gases was extended by Ward and Hendersons who measured the density of liquid iron oxide bubbling helium, nitrogen, neon, argon, and krypton. The measured density was found to decrease smoothly with increasing atomic number of the bubbling gas. The work reported here is a continuation of the program initiated by Ward and Sachdev7 to study the densities in multicomponent melts in which the iron oxide-silica system is the solvent. As such it is necessary to explain or eliminate the anomalous densities of iron silicates under different atmospheres, and the present rede termination was carried out towards this end. EXPERIMENTAL The maximum bubble pressure method of density determination was again employed and the experimen- tal apparatus used was essentially the same as that used by Ward and Sachdev.7 A molybdenum-wound resistance furnace heated an ingot iron crucible of internal diameter 1 in. containing a 2-in. depth of melt. The bubbling gas was blown through a 1/4 -in.-diam mild steel tube onto the end of which was welded a 2-in. extension of 1/4 -in.-diam ingot iron rod, drilled out to 5/32 in., and chamfered to an angle of 45 deg. The blowing tube was introduced to the furnace through a sliding seal and its position was controlled by a vertically mounted micrometer screw which allowed the depth of immersion to be determined with an accuracy of ± 0.01 cm. A Pt/Pt-10 pct Rh thermocouple was located below the crucible and temperature control was effected initially by means of an on-off controller and later by a saturable core reactor. The bubble pressure was determined by measurement of a dibutyl phthalate manometer using a cathetometer. PREPARATION OF MATERIALS Iron oxide was produced by melting ferric oxide in an inductively heated iron crucible in air. The liquid was quenched by pouring onto an iron plate. Silica was prepared by dehydrating silicic acid at 650°C for 12 hr. RESULTS Before any measurements of the density of a melt were made, the density of distilled water at room temperature was measured bubbling helium and argon. Both gases gave the density as 1.00 ± 0.01 g per cu cm which showed that the density of the manometric fluid (dibutyl phthalate) was not affected by contact with the blowing gas. With the furnace controlled by an on-off temperature controller an attempt was made to measure the density of pure liquid iron oxide by bubbling argon. The furnace atmosphere gas and bubbling gas were dried over magnesium perchlorate and deoxidized over copper turnings at 600°C. It was found that the pressure required to blow a bubble at a given depth increased slowly with time, and thus it was impossible to obtain a unique value for the density of the melt. Inspection of the blowing tube after removal from the furnace showed that rings of dendritic iron had precipitated from the melt onto the immersed part of the tube. This is shown in Fig. l(a) where the various "steps" correspond to different depths of immersion. The precipitation of iron was considered to be due to one or both of two possible causes: i) The composition of the liquid iron oxide is that of the liquidus at the temperature under consideration and can be expressed by the equilibrium

Jan 1, 1968

By William E. Ford, Edward Salisbury Dana

1. Simple Hydrocarbons. Chiefly members of the Paraffin Series C,H2,+2. SCHEERERITE. In whitish monoclinic crystals. Perhaps a polymer of marsh-gas (CHI). Found in brown coal at Uznach, Switzerland. HATCHEITITE. Mountain Tallow. In thin plates, or massive. Like soft wax. Color yellowish. Indices, 1.47-1.50. Ratio of C to H = nearly 1 : 1. From the Coal-measures near Merthyr-Tydvil in Glamorganshire, England; from Galicia. PARAFE-IN. A native crystallized paraffin has been described as occurring in cavities in basaltic lava near Paterno, Sicily. Indices, 1.49-1.52. OZOCERITE. Mineral wax in part. Like wax or spermaceti in appearance and consistency. Colorless to white when pure; often leelr-green, yellowish, brownish yellow, brown. Indices, 1.51-1'54. Essentially a paraffin, and consisting chiefly of one of the higher members of the series. Occurs in beds of coal, or associated bituminous deposits, as at Slanik, Moldavia; Roumania; Boryslaw in the Carpathians. Also occurs in southern Utah on a large scale.

Jan 1, 1922

By R. Ruka, E. A. Gulbransen

ONE of the interesting questions in the understanding of the reaction of iron with oxygen is the kinetics and the mechanism of the crystal structure changes occurring in the formation and breakdown of the oxide film. In a recent work' the electron diffraction method was applied to the study of the solid phase reactions occurring internally in the oxide film on iron above 570°C and under vacuum conditions. The higher oxides which form under oxidizing conditions are reduced internally by the diffusion of iron into the oxide leaving the bulk of the oxide FeO (wüstite). This paper will ask and consider three questions. These are: (1) What is the nature of the depressed transformation temperature for the Fe3O4 + Fe ? 4Fe0 reaction in very thin oxide films?; (2) What is the mechanism of the forward transformation of Fe3O4 to FeO at or near 570°C?; and (3) What is the nature and mechanism of the slow reverse transformation of FeO to Fe3O4 and Fe below 570°C?. The composition of the oxide as well as its electrical, magnetic, mechanical, and chemical properties depends upon the kinetics of these reactions. Literature Survey The composition of the oxide film on pure iron at temperatures up to 570°C has been studied extensively by the electron diffraction method. Nelson,' Jackson and Quarrell,3 and Gulbransen and Hick-man4 have shown that Fe3O4 and a-Fe2O8 are formed in the temperature range of 225" to 570°C, while y-Fe,O, is most likely formed below 225°C for long oxidation times. In very thin films FeO (wüstite) is found to form at temperatures as low as 400°C, and its existence depends essentially upon the extent of initial oxidation. FeO is not found in the formation of thick films below 570°C. On the other hand X-ray5 and micrographic8 studies show that Fe3O4 may exist as the main com-ponent in thick films up to 650°C, well above the equilibrium temperature for the reaction Fe3O4 + Fe ? 4FeO. The kinetics of the forward and reverse trans-formations of the reaction Fe3O4 + Fe ? 4FeO have not been studied in oxide films. However, analysis of the data of Gulbransen and Hickman4 on the heat-ing and cooling of iron oxide films of known thick-nesses in high vacua shows that the forward reac-tion proceeds rapidly even for a 4000 A film at temperatures of 575" to 600°C. The reverse reaction or decomposition of wüstite (FeO) occurs at tem-peratures below 450°C. Thus, there appears to be a slow process in the decomposition which is in marked contrast to the rapid forward reaction. The decomposition of a bulk sample of FeO free from the metal has been studied extensively by Chaudron, Benard and coworkers using the micro-graphic, X-ray diffraction, and thermomagnetic methods. Chaudron7,8 first observed that the de-composition of FeO (wüstite) below 570°C occurs by the reaction 4FeO ? Fe3O4 + Fe. Later work by Chaudron and Forestier5 showed that the rate of de-

Jan 1, 1951

By A. H. Grobe, F. N. Rhines

AT elevated temperatures the oxide of silver is unstable in the air at atmospheric pressure, consequently no external oxide scale forms upon pure silver under conditions of high-temperature annealing. When small quantities of certain alloying elements are present in the silver, the formation of a thin external scale is possible' and in addition there may form a subscale composed of the oxide of the solute element precipitated within the body of the silver. Norbury2 and Leroux and Raub3 have reported internal oxidation (subscale forma¬tion) in alloys of silver with 2, 7.5, and 30 per cent of copper. The presence of the subscale is believed to be responsible, at least in part, for the objectionable "fire mark" in Sterling silver.4 Several other alloys of silver, after oxidizing heat-treatments, are known to exhibit undesirable polishing characteristics that may be the result of internal oxidation. Except for the absence of an external scale of silver oxide, it is to be anticipated that silver alloys will prove to be very similar in their oxidation behavior to the alloys of copper, the oxidation characteristics of which have been studied in some detail5,6 The present research confirms this anticipation. The oxidation of a series of 20 dilute alloys of silver has been studied metallographically; some types of subscale not encountered among the copper alloys have been found. Instances of internal oxidation in alloys of most of the metals of the I-b and VIII groups of the periodic system are on record, but evidence of this type of oxidation in alloys of the metals of the intermediate groups is lacking. A number of the metals of the intermediate group, among them cadmium, lead, tin, and zinc, appear to provide the conditions essential to subscale formation; i.e., they form oxides with a relatively low negative free energy of formation, they dissolve other metals that form more stable oxides, and, presumably, oxygen will diffuse through them. In a study of 4o alloys of these white metals only a few cases of internal oxidation have been found. The probable reasons for this difference in behavior will be discussed presently. EXPERIMENTAL PROCEDURE Silver.-The silver alloys employed in the oxidation studies were prepared in heats of 30 grams each from high-purity silver (99.993 per cent Ag)* and the purest avail-

Jan 1, 1942

By A. H. Grobe, F. N. Rhines

AT elevated temperatures the oxide of silver is unstable in the air at atmospheric pressure, consequently no external oxide scale forms upon pure silver under conditions of high-temperature annealing When small quantities of certain alloying elements are present in the silver, the formation of a thin external scale is possible' and in addition there may form a subscale composed of the oxide of the solute element precipitated within the body of the silver Norbury2 and Leroux and Raub3 have reported internal oxidation (subscale formation) in alloys of silver with 2, 7 5, and 30 per cent of copper The presence of the subscale is believed to be responsible, at least in part, for the objectionable "fire mark" in Sterling silver' Several other alloys of silver, after oxidizing heat-treatments, are known to exhibit undesirable polishing characteristics that may be the result of internal oxidation Except for the absence of an external scale of silver oxide, it is to be anticipated that silver alloys will prove to be very similar in their oxidation behavior to the alloys of copper, the oxidation characteristics of which have been studied in some detail 5,6 The present research confirms this anticipation The oxidation of a series of 20 dilute alloys of silver has been studied metallographically, some types of subscale not encountered among the copper alloys have been found Instances of internal oxidation in alloys of most of the metals of the I-b and VIII groups of the periodic system are on record, but evidence of this type of oxidation in alloys of the metals of the intermediate groups is lacking A number of the metals of the intermediate group, among them cadmium, lead, tin, and zinc, appear to provide the conditions essential to subscale formation, i e , they form oxides with a relatively low negative free energy of formation, they dissolve other metals that form more stable oxides, and, presumably, oxygen will diffuse through them In a study of 4o alloys of these white metals only a few cases of internal oxidation have been found The probable reasons for this difference in behavior will be discussed presently EXPERIMENTAL PROCEDURE Silver -The silver alloys employed in the oxidation studies were prepared in heats of 30 grams each from high-purity silver (99 993 per cent Ag)* and the purest avail-

Jan 1, 1942

By M. Murakami, Y. Murakami, O. Kawano

The formation and growth of Guinier-Preston zones in Al-Zn alloys containing 4.4, 6.8, 9.7, and 12.4 at. pct zn have been studied by the X-ray small-angle scattering method. Particular attention was paid to the effects of small amounts of third elements silver, silicon, and magnesium on the formation and growth of G.P. zones. It was noticed that an appreciable number of G.P. zones were formed during the course of rapid cooling and that the size, volume fraction, and number of these G.P. zones were influenced by the existence of the third elements. During subsequent aging it was also found that the addition of both silver and silicon lowered the temperature for the growth of G.P. zones, whereas the addition of magnesium raised it. These results were explained in terms of the mutual interactions among zinc atoms, vacancies, and the third elements. A number of studies on the formation and growth of Guinier-Preston zones in Al-Zn alloys have been reported.1-4 Panseri and Federighii have found that the initial stages of zone growth take place at temperatures as low as around -100°C. For investigation of the mechanism of the initial stages of zone growth, growth studies must be carried out at low temperatures. In order to investigate the possibility of the formation of G.P. zones by the nucleation mechanism or the spinodal decomposition during quenching which was reported by Rundman and Hilliard,5 the examination of the as-quenched structure must be performed. In this paper the investigation of the early stages of the formation and growth were determined by means of the X-ray small-angle scattering method. With this technique, change of X-ray scattering intensities was measured while quenched specimens were heated slowly from liquid-nitrogen temperature to room temperature. At as-quenched state and after heated to room temperature, investigation of zone size, volume fraction, and zone number per unit volume was carried out. Measurements on these specimens yielded information on the early stages of zone formation and growth. Measurements were made also on specimens quenched to and aged at room temperature. From these measurements the previously reported model6 for the later stages of growth is confirmed; namely, the larger zones grow at the expense of smaller ones. Three elements, silver, silicon, and magnesium, were chosen as the third elements for the following reasons: Silver. In the binary A1-Ag alloy the spherical disordered 77' zones were observed immediately after quenching.7 Therefore, in the Al-Zn-Ag alloys, it is suggested that silver atoms might induce cluster formation during quenching. Also, since the migration energy of the zinc atoms was found to be raised by the addition of silver atoms,' silver atoms may have a great effect of the zinc diffusion, especially during low-temperature agings. Silicon. The effects of the addition of silicon atoms were found to be marked, especially at low-tempera-ture aging. In the binary Zn-Si system, no mutual solid solubilities between silicon and zinc9 and no in-termetallic compounds10 are reported to exist. Shashkov and Buynov11 investigated the behavior of silicon atoms in Al-Zn alloys and showed that silicon was not in the G.P. zones. The interaction between silicon atoms and vacancies is strong enough to increase the quenched-in vacancy concentration.* Magnesium. Magnesium atoms are reported to trap quenched-in vacancies and after much longer aging times these trapped vacancies will become free and act as diffusion carriers.13 Therefore at intermediate aging times, the diffusion of zinc atoms in Al-Zn-Mg alloys will be slower than in the binary Al-Zn alloys, whereas at longer times zinc diffusion will become faster. EXPERIMENTAL PROCEDURE The alloys used in this investigation had compositions of 4.4, 6.8, 9.7, and 12.4 at. pct Zn with or without 0.1 and 0.5 at. pct Ag, Si, or Mg. The alloys were prepared from high-purity aluminum, zinc, silver, silicon, and magnesium, with each metal having a purity better than 99.99 pct. The analyzed composition of the specimens is given in Table I. The measurements of the X-ray small-angle scattering were carried out with foils of 0.20 mm thick. The change of the scattering intensity was always measured at the fixed scattering angle of 20 = 2/3 deg. This angle exists nearly on the position of the intensity maximum. The value of the interparticle interference function14 which has large effect in this range of angles may not change abruptly in the case of the spherical shape of small zones. Therefore, from the above considerations, it is concluded that an increase of the intensity measured at this constant angle corresponds to an increase of the average radius and volume fraction of G.P. zones. The specimens were homogenized at 500°, 450°, and 300°C for 1 hr in an air furnace. For the study of the formation and growth at low temperatures, the foil

Jan 1, 1970

By J. H. Rose

The arrangement of the reverberatory furnace and the two waste-heat boilers at the Magma Copper Company's smelter at Superior, Ariz., is shown in Fig. 1. The inside dimensions of the furnace at the slag line are: length, 96 ft.; width, 22 ft. The boilers are Erie City vertical type with a rated capacity of 700 hp. The 3-in. boiler tubes are arranged in two banks with a vertical baffle between. The banks are 30 tubes wide by 9 tubes deep—a total of 540 tubes.

Jan 1, 1934

By N. V. Melnikov, L. N. Marchenko

The latest theoretical and experimental study of physical processes initiated by explosions in solid media have made it possible to obtain a deeper insight into the mechanism of the energy transfer to ambient rock from char es of explosives interspersed with various air gaps. As shown in (17, high explosive action causes excessive fragmentation of medium in the vicinity of the charge, while expansion of the process into the massif is negligible. A theoretical outline of a more rational application of explosion energy was given with a view of obtaining more uniform fragmentation of rock convenient for loading and transportation. The proposed idea proven by experimental study consisted of the possibility of explosion control based on redistribution of explosion energy. Practical realization of the above idea was proposed (1) involving charges with air gaps for rock fragmentation. Since the Rolla Symposium on Mining Research (USA, 1961) (2), borehole charges with air gaps have become common practice. This method of rock blasting is applied in open cast and underground mines working the hardest and viscous, hard, medium hard and soft rocks (ore, quartzites, granites, 1 imes tones, sandstones, coals, etc.) as well as at enterprises for extraction of building materials and raw chemical minerals of any strength. Application of charges with air gaps results in an increase of the degree and uniformity of fragmentation (up to 94 percent of the blasted rock mass consists of fragments not exceeding 400 mm), the average fragment size decreases by 1.5-2 times and the amount of lumps is reduced by 2-10 times (in some cases there are no lumps at all ). Besides, the amount of operation for filling boreholes with tamping material is reduced, the specific consumption of explosives

Jan 1, 1971

By Alexander Squire

A brief study of the effects of material and processing variations upon the tensile properties of steel formed from mixtures of iron and carbon was made in order to provide information regarding the properties obtainable in iron-carbon compacts as influenced by forming pressure, sintering temperature, and graphite particle size. Sintered steels formed from mixtures of iron and graphite have been studied by Stern,' who investigated the effect of various percentages of graphite on compacts formed from electrolytic iron that were repressed and heat-treated after sintering. A further study, by Stern and Greenberg,l is concerned with the heat-treatment of steels formed by the car-burization of iron compacts, and Margolies3 has reported work on the simultaneous sintering and carburization of iron-powder parts. Glauch4 investigated the effect of various types of graphite on the properties of iron-carbon powder alloys but did not determine the effect of different particle sizes of the same graphite alloyed with different types of powder. In the investigation reported in this paper, powders typical of those produced by electrolytic deposition and the decar-burization of shotted steel scrap were used. The powders were mixed by tumbling in a jar mill with graphite powder ground to an average particle diameter of 2, 4, 6, and 16 microns (as determined by microscopic measurement). The properties of the iron and graphite powders are presented in tabular form as Table I. In order to obtain the maximum information from a minimum number of test specimens, the study was divided into two sections with one set of specimens treated identically in each section as a basis for comparison. In the first section, iron powder produced by the shotting and subsequent decarburization of scrap steel was mixed with 2-micron graphite powder, pressed at 50,000, 100,-000, and 200,000 psi, and sintered in hydrogen at 1200°C for the periods of time ranging from 15 to 120 minutes. In the second section of the investigation, electrolytic iron powder was mixed with graphite of an average particle diameter of 2, 4, 6, and 16 microns, pressed at 100,000 psi, and sintered at temperatures ranging from 1000° to r200°C'. for periods of time of 30 to 180 minutes. By following this procedure an indication of the effect of the following variables upon the density and tensile properties of iron-carbon powder compacts was obtained: (I) forming pressure, (2) sintering time, (3) particle size of graphite powder, (4) sintering temperature, (4) type of iron powder.

Jan 1, 1947

By Alexander Squire

A brief study of the effects of material and processing variations upon the tensile properties of steel formed from mixtures of iron and carbon was made in order to provide information regarding the properties obtainable in iron-carbon compacts as influenced by forming pressure, sintering temperature, and graphite particle size. Sintered steels formed from mixtures of iron and graphite have been studied by Stern,' who investigated the effect of various percentages of graphite on compacts formed from electrolytic iron that were repressed and heat-treated after sintering. A further study, by Stern and Greenberg,l is concerned with the heat-treatment of steels formed by the car-burization of iron compacts, and Margolies3 has reported work on the simultaneous sintering and carburization of iron-powder parts. Glauch4 investigated the effect of various types of graphite on the properties of iron-carbon powder alloys but did not determine the effect of different particle sizes of the same graphite alloyed with different types of powder. In the investigation reported in this paper, powders typical of those produced by electrolytic deposition and the decar-burization of shotted steel scrap were used. The powders were mixed by tumbling in a jar mill with graphite powder ground to an average particle diameter of 2, 4, 6, and 16 microns (as determined by microscopic measurement). The properties of the iron and graphite powders are presented in tabular form as Table I. In order to obtain the maximum information from a minimum number of test specimens, the study was divided into two sections with one set of specimens treated identically in each section as a basis for comparison. In the first section, iron powder produced by the shotting and subsequent decarburization of scrap steel was mixed with 2-micron graphite powder, pressed at 50,000, 100,-000, and 200,000 psi, and sintered in hydrogen at 1200°C for the periods of time ranging from 15 to 120 minutes. In the second section of the investigation, electrolytic iron powder was mixed with graphite of an average particle diameter of 2, 4, 6, and 16 microns, pressed at 100,000 psi, and sintered at temperatures ranging from 1000° to r200°C'. for periods of time of 30 to 180 minutes. By following this procedure an indication of the effect of the following variables upon the density and tensile properties of iron-carbon powder compacts was obtained: (I) forming pressure, (2) sintering time, (3) particle size of graphite powder, (4) sintering temperature, (4) type of iron powder.

Jan 1, 1947

By Alexander Squire

A BRIEF study of the effects of material and processing variations upon the tensile properties of steel formed from mixtures of iron and carbon was made in order to provide information regarding the .properties obtainable in iron-carbon compacts as influenced by forming pressure, sintering temperature, and graphite particle size. Sintered steels formed from mixtures of iron and graphite have been studied by Stern,1 who investigated the effect of various percentages of graphite on compacts formed from electrolytic iron that were repressed and heat-treated after sintering. A further study, by Stern and Greenberg,2 is concerned with the heat-treatment of steels formed by the carburization of iron compacts, and Margolies3 has reported work on the simultaneous sintering and carburization of iron-powder parts. Glauch4 investigated the effect of various types of graphite on the properties of iron-carbon powder alloys but did not determine the effect of different particle sizes of the same graphite alloyed with different types of powder. In the investigation reported in this paper, powders typical of those produced by electrolytic deposition and the decarburization of shotted steel scrap were used. The powders were mixed by tumbling in a jar mill with graphite powder ground to an average particle diameter of 2, 4, 6, and 16 microns (as determined by microscopic measurement). The properties of the iron and graphite powders are presented in tabular form as Table I. In order to obtain the maximum information from a minimum number of test specimens, the study was divided into two sections with one set of specimens treated identically in each section as a basis for comparison. In the first section, iron powder produced by the shotting and subsequent decarburization of scrap steel was mixed with 2-micron graphite powder, pressed at 50,000, 100,000, and 200,000 psi, and sintered in hydrogen at 1200°C for the periods of time ranging from 15 to 120 minutes. In the second section of the investigation, electrolytic iron powder was mixed with graphite of an average particle diameter of 2, 4, 6, and i6 microns, pressed at 100,000 psi, and sintered at temperatures ranging from 1000° to 1200°C. for periods of time of 30 to 180 minutes. By following this procedure an indication of the effect of the following variables upon the density and tensile properties of iron-carbon powder compacts was obtained: (I) forming pressure, (2) sintering time, (3) particle size of graphite powder, (4) sintering temperature, (4) type of iron powder.

Jan 1, 1947

Organization Place Date International Mining Convention (Auspices, Van- 1919 couver Chamber of Mines) Vancouver, B. C. Jan. 8-10 American Institute of Consulting Engineers, Inc... New York, N. Y. Jan. 13 American Society of Civil Engineers New York, N. Y. Jan. 15-16 Institute of Chemical Engineers Chicago, 111. Jan. 15-18 American Wood Preservers Association St. Louis, Mo. Jan. 28-30 American Society of Heating and Ventilating Engineers New York, N. Y. Jan. 28-30 Automotive Engineers New York, N. Y. Feb. 4-6

Jan 1, 1919

By H. R. Hoffman

SINCE slag is a necessary product of the reactive oxygen additions necessary to the present-clay quality steelmaking, the study of the control of its volume is being attempted. With other varying factors that may affect the volume of slag kept as nearly constant as possible, the object of this investigation is to determine what effect the one factor of varying the amounts of iron-ore additions and the time of the additions may have upon the volume of slag in producing an acid electric steel heat.

Jan 1, 1947

By William Lodding

In leaching ores at atmospheric pressure it is often desirable to apply high reagent concentration, long exposure time, and elevated temperature. All of these conditions tend to increase the treatment cost. In conventional leaching, direct or countercurrent, the leaching fluid is needed to transport the solids through the process. This requires relatively large volumes of fluid and limits the reagent concentration economically feasible. The relatively high dilution also increases fuel cost if leaching is to be done above ambient temperature. Heating of water is expensive.

Jan 3, 1967

By H. A. Wilhelm, P. Chiotti, G. A. Tracy

A summary of analytical, X-ray, thermal, and metallographic data obtained in the study of the Mg-U system is presented. No intermetallic compounds are formed by these two elements, and their mutual solubility is limited at temperatures up to 1255°C. The compositions of the liquids which coexist at 1135°C under a pressure of 3 atm are 0.14*0.05 wt pet U in magnesium, and 0.004 wt pet Mg in uranium. The solubility of uranium in magnesium decreases to 0.0510.03 wt pet at 675OC, and to about 0.0005 wt pet at 650°C. Due to the reactivity of both uranium and magnesium toward crucible materials, the choice of a suitable crucible presented a problem. Crucibles made from high purity magnesia to which 10 wt pet MgF2 was added to reduce porosity proved to be satisfactory. Some observations made with the use of other crucibles are given. THIS investigation was made to establish the phase diagram for the Mg-U system. Ahmann,' formerly of the Ames Laboratory, did some work on the system. He used several methods in an attempt to prepare Mg-U alloys. One of the methods involved the reduction of UF, with a large excess of magnesium. In these experiments, the magnesium wet the surface of the uranium, but there was no evidence for compound formation. The maximum solubility of magnesium in uranium was indicated to be 0.01 wt pet. In another set of experiments, uranium chips as well as uranium powder were heated in contact with molten magnesium in a graphite crucible for periods of time up to 48 hr. A reaction layer was found at the Mg-U interface in several instances. X-ray analysis of the layer material showed the presence of UC and some additional unidentified lines which were interpreted as indicating the possibility of an intermetallic compound of uranium and magnesium. These studies indicated the maximum content of magnesium in uranium to be 0.043 wt pet. One sample of magnesium which had been heated at 1025°C in contact with excess uranium was found by chemical analysis to contain 0.275 wt pet U. Rules, based on empirical or semi theoretical considerations, which attempt to predict the alloying behavior of metals have been presented in the literature. Although these rules are not infallible, they nevertheless serve as useful guides. Using them, several generalizations can be made concerning the Mg-U system. According to Hume-Rothery's' atomic

Jan 1, 1957

Electro-mechanical actuator, self-protected for mechanical and electrical overload, is developed by RACO. Tubular housing consists of squirrel cage motor with hollow rotor shaft and inner threads in the rotor. Features stroke distance of 2-72 in. and wide range of trust (20 lb-10 tons). (100) Agglomeration systems, offered by Ferro-Tech, incorporate pelletizing, briquetting and extrusion systems to agglomerate materials too fine to convey, load or feed to a process. Equipment includes disc and drum pelletizers, briquetter presses, compactors, extruders, pugmills and mixers, dryers, coolers, feeders and conveyors. (101)

Jan 9, 1973

By L. W. Casteel

This is a story of progress through research, invention and innovation-progress that made a small mine in Missouri into a large and prosperous corporation. The St. Joseph Lead Co. was founded in Borne Terre, Missouri, in 1864. At that time, the mine consisted of a narrow trench eight feet deep; the mill was a hand-operated jig; and the smelter, a charcoal oven with a sloping hearth. During the first year, production was suspended for two months because of an invasion by the Confederate army. There have been few interruptions since that time.

Jan 7, 1964

By AIME AIME

T HE Institute of Metals Division and the Iron and Steel Division will meet jointly at the Stevens Hotel, Chicago, during the week of the American Metals Congress, Sept. 22-26. The Iron and Steel Di- vision of the American Society of Mechanical Engineers, the American Society for Steel Treating and the American Welding Society meet at the same time. but the sessions have been arranged to conflict as little as possible. A rich program of papers and plant visits has been arranged for the members and guests of the two Institute Divisions. The annual dinner and a pro- gram of entertainment are being arranged by the Woman's Auxiliary of the Chicago Section. Members are urged to register immediately up011 arrival and to make dinner and plant visit reservations at the same time.

Jan 1, 1930