By E. Rudy, St. Windisch

The only complete phase diagram investigation of the Ti-W system is by Maykuth and coworkers,&apos; Fig. 1. Although previous work by Gonser2 indicated complete miscibility, later investigations3°5 essentially confirmed the diagram depicted in Fig. 1. The present study was undertaken because preliminary results on metal-rich ternary Ti-W-C alloys indicated complete solid solubility between 0 titanium and tungsten at temperatures above 1300°C—in contradiction to the presently accepted diagram. The powdered elements, as well as crystal bar titanium and tungsten sheet, were used in the preparation of the experimental alloys. The iodide titanium, obtained from Foote Mineral Co., Exton, Pa., had a total impurity content of less than 410 ppm, of which 150 ppm were interstitials (H, O, N, C). The overall purity of the titanium powder (Var-Lac-Oid Chemical Co., New York) was better than 99.7 pct. Major contaminants, in ppm, included: 0, 800; N, 10; H, 1500; Fe + Co + Ni + Cu + Zn, 50; C1, 200. The measured lattice parameters of the titanium were a = 2.94A and c = 4.68,A. The tungsten sheet and the tungsten powder (Wah Chang Corp., Albany, Ore.) contained the following impurities (in ppm, values in parentheses refer to the sheet tungsten): Mo, 50 (70); 0, 140 (110); Fe, 20 (60); Ni, 20 (not determined); N, 110 (not determined); sum of other impurities, <60 (<100). Samples from the iodide titanium bar stock and from tungsten sheet were prepared by repeated melting of the chipped materials in a nonconsumable electrode arc furnace under high-purity helium. The melted alloys were heavily cored, and homogeneity of the alloys could only be achieved after prolonged heat treatments at subsolidus temperatures. The majority of the alloys were therefore prepared by cold compacting the well-mixed powders in steel dies and pre-homogenizing the compacts for 6 hr at 1300°C in a tungsten-element furnace. The vacuum was better than 10"6 Torr, but for additional protection the sample container was wrapped in zirconium foil. Both preparation methods led to identical results. The measurements of the solidus temperatures were carried oat in the Pirani-type furnace described in a previous paper.6 Incipient melting in alloys containing between 20 and 90 at. pct W was rather difficult to detect visually, and therefore a photoelectric transducer system7 was employed to indicate the phase change. For the investigation of the solid-state equilibria, the specimens were first homogenized for 2 hr at slightly subsolidus temperatures in the Pirani fur- nace and then reequilibrated at, and rapidly cooled (-100°C per sec) from, the selected equilibrium temperatures. After the runs, the alloys were analyzed microscopically and by X-ray diffraction. With the exception of spot checks for oxygen and nitrogen in processed alloys, no other chemical analyses were performed. However, as the weight changes of the alloys during processing were within 0.05 pct and the lattice parameters of indeqendently prepared alloy series agreed within 0.0015A, it is reasonable to assume that no significant concentration shifts with respect to the nominal compositions had occurred. The measured solidus temperatures, shown together with literature data in Fig. 2, ascend smoothly from

Jan 1, 1969

By J. E. Burke

RECENT investigations have elucidated many of the phenomena of the grain growth process, but have also revealed some conflicting and unexplained results. Beck and his co-workers1,2,3 have shown that grain growth continues with continued heating at one temperature until the average grain size approaches the thickness of the specimen, Plotting the logarithm of the average grain diameter, D, against the logarithm of the annealing time, t, they find the straight line relationship given by the equation: [D=Ktn [11] with possible small deviations at short annealing times. K and n are constants at constant temperature. On the other hand, Walker4 finds that, in alpha brass, the rate of growth falls off more rapidly than indicated by Eq I after long annealing, so that an equilibrium grain size is approached. Burke5 showed, using Walker&apos;s data, that time and temperature for grain growth are apparently related through an activation energy, H, according to the relationship: [t, Hr i &apos;_ III t„ = R \T, - ~) [2]] where t1 and t2 are the annealing times necessary for the average grain size to increase from Do to D at temperatures T1 and T2 and R is the gas laws constant. In the case quoted, H had the value 60,000 cal per mol. The apparent validity of this relationship, at least up to 700°C, and the approximate value of H were later confirmed by Beck.&apos; The results obtained by Beck, Kremer, Demer and Holzworth2 for aluminum and aluminum-magnesium alloys could not be satisfied by such a relationship, since the slope of the isothermal curves increased with increasing temperature. These data indicate and Beck, Holzworth and Hu6 later demonstrated experimentally that the only apparent factor controlling the rate of grain growth at constant temperature is the grain size. While many of the phenomena have been elucidated, a reasonably quantitative explanation of the process is lacking. There exists uncertainty even as to the primary driving force for grain growth, although there is a considerable body of indirect evidence that the interfacial energy of the grain boundary is responsible.7,8,10 Making implicit use of this assumption, several authors14,15 have pointed out that grain boundaries should migrate toward their center of curvature. Harker and Parker&apos; have advanced this concept furthest, and show that one can expect grain boundary migration to occur only when the grain faces are curved, or when they meet at non-equilibrium angles. When the face is curved toward a grain A, for example, the atoms in the surface of grain B, on the other side of the boundary, are on the average more surrounded by the atoms of their lattice than the atoms on the surface of grain A. Because of thermal motion, the atoms at the interface will sometimes be attached to grain A and

Jan 1, 1948

By P. M. Aziz, I. Markson, C. S. Barrett

The abnormal after-effect in twisted wires that occurs when untwisting is interrupted by etching con be brought under control and used to study the mechanical properties of thin surface films and how they are effected by reagents and heat treatment. Results are given of studies of oxide films on high purity aluminum. IF a wire is subjected to plastic deformation by torsion and then released, it untwists in the normal after-effect, but under certain circumstances the untwisting is abruptly lessened or reversed by the application of an etchant to the wire.1,2 This abnormal after-effect may occur, for example, if there is a coherent oxide film on the surface of the wire which is removed by the etchant. Following a suggestion of A. H. Cottrell that predicted this effect, it is attributed to dislocations that had piled up beneath the oxide layer and represents the rapid release of residual stresses caused by these dislocations. When the layer is removed, the stress relief may be by escape of piled-up dislocations from the metal, or by an activation of latent sources of dislocations located at the surface, together with rebalancing of elastic stresses to compensate for the loss of stressed material, as in a residual stress analysis determination, these mechanisms acting singly or in combination.&apos; The slower the attack of the reagent, the more gradual is the stress relief and the smaller the change in strain rate when the reagent is applied. A study has been made of the factors that influence the magnitude of the normal and abnormal after-effects with the object of developing techniques suitable for a quantitative investigation of the influence of various surface films on dislocations in wires, and of the rate and extent of the attack on the films by different reagents. It was found that reasonable sensitivity and reproducibility could be achieved if a suitable choice of variables was made and if these variables were held constant through a series of experiments. The method was then applied to a study of oxide films produced and treated in different ways on the surface of high purity aluminum wires, and to a study of the damage to these films caused by various reagents. Experimental Procedure The material used throughout this work was prepared from 99.9968 pct Al. This high purity aluminum was melted, cast into 1/2 in. diameter ingots, and then swaged and drawn without intermediate annealing to 0.040 in. diameter wire. A sketch of the apparatus employed for twisting is shown in Fig. 1. The test wires were mounted into the apparatus by cementing one end of the wire to the beaker and the other to the tube with laboratory wax of high melting point. The length of the wire between the waxed joints was 4.2 & 0.2 cm. Extreme care was taken during mounting to avoid cold-working the wire. The wire was twisted through 335" in 2 to 4 sec by rotating the pinion on the gear box until the vertical post on the rotating table, which was initially touching the horizontal stop, was arrested by the stop. All the tests were conducted with apparatus and reagents at the same temperature (about 25°C). In all tests, except those where the duration of the initial torque was investigated, the torque was applied for a period of 2 min. At the end of this time the table was rotated back a few degrees away from contact with the stop and the wire allowed to untwist. The after-effects were measured by reflecting a beam of light from the mirror shown on the apparatus. After the wire had untwisted for 6 min, a reagent was carefully poured into the beaker and thereby applied to the surface of the wire.. In some tests the liquid in the beaker was removed after a few minutes and replaced by an-

Jan 1, 1954

By OTTO HERRES

TO operate the bituminous coal industry in the United States in 1929 cost $770,237,000, of which $30,739,000 was paid for purchased power and $34,947,000 for new machinery and equipment. Equipment aggregated 3,124,000 hp. A mining industry that spends $65,000,000 a year for power and machinery is likely to be fairly well mechanized, and when the machinery in use takes three million horsepower to drive it, the probabilities are that mechanization has been in progress in at least some of the mines for quite a few years. Mechanization in its broadest sense implies machine cutting, power drilling, mechanical loading, electric haulage, mechanical sizing and cleaning, and lesser applications of machinery to mining operations. But the introduction and development of mechanical loading has been the feature of coal mining recently and its extraordinary progress is causing great changes within the industry. First, let us look at the records. The quantity of coal loaded mechanically in bituminous mines was:

Jan 1, 1933

By F. D. Rosenthal, F. J. Dunkerley, G. J. Mills

Activities, free energies, and heats and entropies of mixing of liquid Pb-Zn alloys have been obtained by the electrode-potential method between 400° and 650°C. The large positive deviations observed from Raoult&apos;s law are in agreement with the phase diagram, which indicates a wide immiscibility field. A vapor-pressure method was used to extend the activity measurements to 900°C, allowing the maximum of the immiscibility gap to be estimated by thermodynamic calculation. Data on the mono-tectic and eutectic points compare favorably with previously existing work. SEVERAL long-standing methods have been in use for the study of phase diagrams from measurement of the activities of the component metals.&apos; The use of thermodynamic analysis for interpreting equilibria data is comparatively recent, however. Such analysis is usually undertaken by first evaluating the principal thermodynamic functions as, for example, the enthalpy, entropy, and free energy of the alloy constituents. These, in turn, quite often can be correlated with the interatomic potential energies and atomistics of the system, from which a clearer understanding of the causes leading to deviations from ideal behavior is gained. The present study of liquid Pb-Zn alloys is concerned with a determination of these quantities by electrode-potential and vapor-pressure measurements, using these values in calculations involving phase equilibria and to obtain a theoretical insight into an alloy system exhibiting strong positive deviations from ideal metallic solution. A considerable portion of the previously reported work is based on thermal analysis. Supplemented by optical studies of solid alloys, these techniques have revealed the essential nature of the immiscible mixtures that are formed. It is difficult, however, using the phase-

Jan 1, 1959

By William D. Klopp, Joseph R. Stephens

A substantial reduction in the 300°F ductile-to-brittle transition temperature for unalloyed chromium was achieved in alloys from systems which resemble the Cr-Re system. These alloy systems include Cr-Ru, Cr-Co, and Cr-Fe. Transition temperatures ranged from -300° F for Cr-35 at. pct Re to -75°F for 0-50 at. pct Fe. The ductile alloys have high grain gvowth rates at elevated temperatures. Also, Cr-24 at. pct Ru exhibited enhanced tensile ductility at elevated temperatures, characteristic of superplas-ticity. It is concluded that phase relations play an importarlt role in the rhenium ductilizing effect. The ductile alloys have compositions near the solubility limit in systems with a high terminal solubility and which contain an intermediate o phase. The importance of enhanced high-temperature ductility to the rhenium ductilizing effect is not well understood although both may have common basic features. CHROMIUM alloys are currently being investigated for advanced air-breathing engine applications, primarily as turbine buckets and/or stator vanes. The inherent advantages of chromium as a high-temperature structural material are well-known1 and include its high melting point relative to superalloys, moderately high modulus of elasticity, low density, good thermal shock resistance, and superior oxidation resistance as compared to the other refractory metals. Additionally, it is capable of being strengthened by conventional alloying techniques. The major disadvantage of chromium is its poor ductility at ambient temperatures, a problem which it shares with the other two Group VI-A metals, molybdenum and tungsten. For chromium, the problem is further amplified by its susceptibility to nitrogen em-brittlement during high-temperature air exposure. In cases of severe nitrogen embrittlement, the ductile-to-brittle transition temperature might exceed the steady-state operating temperature of the component. The low ductility of chromium would make stator vanes and turbine buckets prone to foreign object damage. The present work was directed towards improvement of the ductility of chromium through alloying, with the anticipation that any improvements so obtained might be additive to strengthening improvements achieved through different types of alloying. The alloying additions for ductility were selected on the basis of the similarity of their phase relations with chromium to that of Cr-Re. The reduction in the ductile-to-brittle transition temperatures of the Group VI-A metals as a result of alloying with 25 to 35 pct Re is well established.a4 the temperature range -300" to 750° F. This phenomenon is commonly referred to as the &apos;<rhenium ductilizing effect"; this term is also used to describe systems in which the ductilizing element is not rhenium. Other alloy systems which have recently been shown to exhibit the rhenium ductilizing effect include Cr-Co and c-Ru.= In order to explore the generality of this effect, alloys were selected from systems having phase relations similar to that of Cr-Re, primarily a high solubility in chromium and an intermediate o phase. The following compositions were prepared: Cr-35 and -40Re; Cr-10, -15, -18, -21, -24, and -27 pct Ru; Cr-25 and -30 pct Co; Cr-30, -40, and -50 pct Fe; Cr-45, -55, and -65 pct Mn. Seven other systems were also studied which partially resemble Cr-Re. These systems have extensive chromium solid solutions or a complex intermediate phase, not necessarily o. The compositions evaluated include the following: Cr-20 pct Ti; Cr-15, -30, and -45 pct V; Cr-2.5 pct Cb; Cr-2.5 pct Ta; Cr-20 pct Ni; Cr-6, -9, -12, and -15 pct 0s; Cr-10 pct Ir. The compositions of alloys in these systems were chosen near the solubility limit for the chromium-base solid solutions, since in the Group VI-A Re systems, the saturated alloys are the most ductile. These alloys were evaluated on the basis of hardness, fabricability, and ductile-to-brittle transition temperatures. In addition to the studies of alloying effects on ductility, an exploratory investigation was conducted on mechanical properties at high temperatures in Cr-Ru alloys EXPERIMENTAL PROCEDURE High-purity chromium prepared by the iodide deposition process was employed for all studies. An analysis of this chromium is given in Table I. Alloying elements were obtained in the following forms: Commercially pure powder — iridium, osmium, rhenium, and ruthenium. Arc-melted ingot — titanium and vanadium. Electrolytic flake — iron, manganese, and nickel. Sheet rolled from electron-bearn-melted ingot — columbium and tantalum. Electron-beam-melted ingot — cobalt. Sheet rolled from arc-melted ingot — rhenium. All alloys were initially consolidated by triple arc melting into 60-g button ingots on a water-cooled hearth using a nonconsumable tungsten electrode. The melting atmosphere was Ti-gettered Ar at a pressure of 20 torr. The ingots were drop cast into rectangular slabs and fabricated by heating at 1470" to 2800° F in argon followed by rolling in air. Bend specimens measuring 0.3 by 0.9 in. were cut from the 0.035-in. sheet parallel to the rolling direction. The specimens were annealed for 1 hr in argon, furnace cooled or water quenched, and electropolished prior to testing. Three-point loading bend tests were conducted at a crosshead speed of l-in. per min over

Jan 1, 1969

By J. E. Strassner

Oilfield emulsions are stabilized primarily by film-forming asphaltenes and resins containing organic acids and bases. Adding inorganic acids and bases radically changes the physical properties of these films and their emulsion-stabilizing properties. Interfacial films show one of three different physical characteristics when retracted in pendent drop tests. These compressed films have rigid, soap-type or minimum film properties depending on the quantity of asphaltenes and resins in the crude oil and on the pH and composition of the brine. There exists for each crude oil-brine system an optimum pH range over which the adsorbed film exhibits minimum contracted filtn properties. In this range, intmfacial tension is high — frequently near its maximum value — indicating the absence of highly surface-active specier; crude oil-brine emulsions generally show minimum stability; and surfactant requirements for breaking these emulsions are significantly reduced — sometimes no surfactant is needed. About two-thirds of the world&apos;s crude oil is produced as emulsions that must be treated (demulsified) to be marketed.&apos; Approximately three-fourths of all domestic crude oil produced must be treated. The percentage of crude requiring treatment increases as fields become older and more water is produced. Demulsification most frequently is attained through use of surfactants, heat and electric treaters. It is estimated that over 75 percent of all oilfield emulsions are broken by chemicals generally containing alkylene oxide condensates. Although acids and bases are known to affect emulsion stability:-&apos; they rarely are used in the oil field except in batch treatment of the most severe emulsions. Nevertheless, pH adjustment by using acids or bases in demulsification has some advantages over other methods. Mainly, it is cheaper. Acids and bases frequently are cheaper to use than surfactants, or can appreciably reduce the amount of surfactant required for demulsification. Secondary advantages are that less oil is lost by emulsi-fication into the aqueous phase, and that less corrosion is encountered when the optimum pH is basic. Limitations to the use of pH include (1) use in brines containing high concentrations of reactive ions, (2) closer supervision for pH control than is required for surfactants and (3) need for corrosion protection when the optimum pH is sufficiently acidic. These factors indicate that the economics of pH con trol in demulsification will be maximized when relatively large treating facilities are needed, when relatively large surfactant concentrations are required to break an emulsion, when a relatively low concentration of the aqueous phase is emulsified in the oil and when the emulsified aqueous phase contains relatively low concentrations of reactive ions. Because there are no broad guide lines for using pH control in breaking oillield emulsions (and because the limited guides available are highly specific and frequently contradictory), this paper will attempt to clarify the principles involved in using acids and bases to break emulsions. These principles also should be useful in refinery separations and in other oilfield applications where stable or unstable petroleum emulsions are involved. Principles of Emulsion Stability Oilfield emulsions generally occur as water droplets dispersed in oil (w/o) and occasionally as oil droplets in water (o/w). These emulsion droplets are usually in the 0.1- to 10-micron range. However, more coarsely dispersed water droplets frequently are present in the emulsion. Pure hydrocarbons and water will not form stable emulsii except in extreme dilutions where the large distance brtween droplets inhibits coalescence. An emulsion breaks because interfacial tension acts to minimize the surface area of the dispersed drops by coalescence. However, emulsions can be stablized for long periods of time by the presence of a third phase that adsorbs at the oil-water interface and inhibits coalescence of the dispersed phase."&apos; Emulsions generally are stabilized by (1) repulsive charges on the surfaces of the dispersed phase and (2) adsorbed films that, being preferentially wetted by the continuous phase, act as a physical barrier to inhibit contact between the dispersed droplets. Both these factors generally are important in stabilizing and in breaking o/w emulsions. However, repulsive charges are less effective in stabilizing w/o emulsions which generally are stabilized by adsorbed films.V or this reason the nature and importance of these films at oil-water interfaces were examined closely; as will be shown, pH changes were found to affect the films significantly, and this work led to laboratory tests of pH- adjustment in emulsion breaking. This paper will present evidence to show that emulsions are stabilized primarily by films that form around droplets

Jan 1, 1969

By J. W. Hickman

INTRODUCTION RECENT work by the authors1 on the oxide films formed on alloys of titanium and zirconium with nickel and copper indicated that an investigation of the oxides which form on alloys of copper and nickel might permit the relative rates of formation and diffusion of the ions of. these metals to be determined. This binary system is of further interest since the alloys which form are of the solid solution-type over-the entire range. In addition nickel is much more oxidation resistant than copper. A comparison of the free energies of formation of the simple oxides which may occur on these alloys indicates that nickel oxide should be observed over the entire time and temperature ranges of oxidation for all alloy compositions.1 In. order for nickel oxide to predominate on the surface, it is necessary that nickel ions form and diffuse to the surface. Two factors which may influence the formation of nickel oxide may be the ionic sizes, where Cu+ is 0.96Å and Ni-++ is 0.70Å, and the charges on the ions. On the basis of size, Ni++ should diffuse more readily than Cu+ while on the basis of charge, Cu+ should form more readily than Ni++. According to Uhlig2 passivity to corrosion in an alloy appears at a critical composition which for copper-nickel alloys is related to the tendency of the d band of electronic energy states to fill with electrons. This composition in the copper-nickel alloys corresponds to 40 at. Pct nickel at which composition Uhlig2 (quoting La Que&apos;s data) states that the alloy system becomes passive. Magnetic and specific heat data indicate that the d band of copper-nickel alloys is filled at 6o at. pct copper or 4o at. pct nickel. Mott and Jones3 have shown that if, on alloying nickel with copper, one considers a copper atom to be identical with a nickel atom except for an extra electron (nickel -has the-configuration: 3d8 4s2 and copper: 3 d10 4s) then at 60 at. pct copper or 4o at. pct nickel enough electrons are contributed by copper to fill the d band of the alloy. At this composition the magnetic susceptibility approximates zero according to Grew.4 Although the electron diffraction data will not determine the rates of the several reactions which may occur during oxidation, yet a determination of the structures of the surface oxides may yield information concerning the relationships, if any, which may&apos; exist between the oxide structures which form and that composition where the magnetic susceptibility approximates zero. It is quite possible, of course, that the mechanisms of the oxidation and corrosion reactions may be so widely different that no correlations between them may be possible. SURVEY OF LITERATURE The metals, copper and nickel, which are face-centered cubic, form solid solution alloys which are face-centered cubic with no superstructure for all compositions. Three oxides of nickel have been investigated structurally by X ray diffraction. Of

Jan 1, 1948

By E. A. Gulbransen, J. W. Hickman

Recent work by the authors1 on the oxide films formed on alloys of titanium and zirconium with nickel and copper indicated that an investigation of the oxides which form on alloys of copper and nickel might permit the relative rates of formation and diffusion of the ions of these metals to be determined. This binary system is of further interest since the alloys which form are of the solid solution type over the entire range. In addition nickel is much more oxidation resistant than copper. A comparison of the free energies of formation of the simple oxides which may occur on these alloys indicates that nickel oxide should be observed over the entire time and temperature ranges of oxidation for all alloy compositions~i In order for nickel oxide to predominate on the surface, it is necessary that nickel ions form and diffuse to the surface. Two factors which may influence the formation of nickel oxide may be the ionic sizes, where cu+ is o.,,6-,4 and ~i++ is o.,oh;, and the charges on the ions. On the basis of size, Ni++ should diffuse more readily than Cu+ while on the basis of charge, Cu+ should form more readily than Ni++. According to Uhlig2 passivity to corrosion in an alloy appears at a critical composition which for copper-nickel alloys is related to the tendency of the d band of electronic energy states to fill with elec-trans. This in in the copper- nickel alloys corresponds to 40 at. pct nickel at which composition Uhlig2 (quoting La Que&apos;s data) states that the alloy system becomes passive. Magnetic and specific heat data indicate that the d band of copper-nickel alloys is flied at 60 at. Pet Or or 4O at. pct nickel. Matt and Jones3 have shown that if, on alloying nickel with copper, one considers a copper atom to be identical with a nickel atom except for an extra electron (nickel has the configuration: 3ds 4s2 and copper: 3 dl0 4s) then at 60 at. pct copper or 40 at. pct nickel enough electrons are contributed by copper to fill the d band of the alloy. At this composition the magnetic susceptibility approximates zero according to Grew.4 Although the electron diffraction data will not determine the rates of the several reactions which may occur during oxidation, yet a determination of the structures of the surface oxides may yield information concerning the relationships, if any, which may exist between the oxide structures which form and that composition where the magnetic susceptibility approximates zero. It is quite possible, of course, that the mechanisms of the oxidation and corrosion reactions may be so widely different that no correlations between them may be possible. Survey OF Literature The metals, copper and nickel, which are face-centered cubic, form solid solution alloys which are face-centered cubic with no superstructure for all compositions. Three oxides of nickel have been investigated structurally by X ray diffraction. Of

Jan 1, 1949

By E. P. Abrahamson

The effect of transition element binary solid solution additions upon the re crystallization temperature of nickel has been investigated. All additions raised the re crystallization temperature. Both the rate of change of re crystallization temperature with at. pet solute and the limit of initial linearity are found to correlate with the free atom ground state outer electron configuration of the solute element. A comparison of all of the correlations for the transition elements studied has yielded a set of empirical relations, which allows the prediction of the effect of dilute binary transition elements on the recrystallization temperature of other transition elements. The work of Abrahamson, et al.1-7 on dilute binary solution alloys indicated a correlation between the free atom ground state electron configuration of the solute and both the brittle-ductile transition and re-crystallization temperature. Further, it has been shown3,4 that the limit of initial linearity may also be correlated with the solute electron configuration. Since previous studies have dealt with bee and hexagonal base elements, this study is made to note what effect, if any, the fee base structure might have. Nickel also serves to give a solvent configuration which will allow the comparison of all of the transition element solvents. Olsen8 has studied the effect of some trace elements upon the recrystallization of nickel. He included only Ti, Zr, W, Mn, and Co of the transition elements. The differences in change of recrystallization temperature were attributed to the solute atom size and to the solubility of the solute in nickel. PROCEDURE All alloys were made using 99.9 + pet Ni with 0.003 C, 0.015 Fe, 0.007 0, and 0.0007 H. The solute elements were 99.9 + pet pure. According to the published binary phase diagrams9 and metallo-graphic examinations at X750, all solute elements were in solid solution. The alloys were arc melted and remelted four times in the form of cubic 200-g buttons under an argon atmosphere. They were then hot forged at 800oC to 0.750 in. diam, machined to 0.60 in., vacuum annealed for 1 hr at 700°c, swaged to 0.40 in. and annealed at 700oC for 1 hr in vacuum. The grain size was checked and found to be 77 * 20 grains per sq mm. The specimens were then swaged to 0.187 in., yielding 76 ± 1 pet cold work. All alloys were then chemically analyzed for the solute addition. The interstitial contents remained at the values of the starting material when checked on random alloy specimens. The swaged rod was cut into 8.25 in. lengths and heat treated in a gradient furnace for 1 hr. The gradient was maintained at 250" to 850°C over an eight inch length, recorded by twelve thermocouples. Control was ± 3oC, accomplished at the hot end. The recrystallization was determined metallo-graphically over the entire specimen. The criterion chosen was that point on the specimen showing the first recrystallized grain at a constant magnification, X200. Specimens were repeated, and the agreement was found to be generally ± 3oC.

Jan 1, 1962

By Robert C. Linares

Cubic zinc sulfide has been grown from molten salt solutions substantially below the hexagonal-cubic phase transition of 1020°C. Crystals free of birefringence have been grown from molten lead chloride at temperatures from 500° to 800°C. Factors affecting the optical transmission and the birefringence are discussed. CUBIC zinc sulfide is of interest for electrooptic devices and as an optical coating material. However, it cannot readily be produced as large crystals which are free of birefringence. The birefringence arises from the fact that the cubic ZnS is usually grown as the high-temperature hexagonal phase and is transformed to the lower cubic phase by annealing.&apos; This results in stacking faults, stress, and birefringence. A requirement for the growth of cubic ZnS is that it be grown below the phase transition of 1020°C.2 Crystals of cubic ZnS have been grown below 1020°C by the hydrothermal,3 flux,4 and vapor transport5 techniques. However, these all appear to have limitations in size or quality of material produced. It was felt that a new flux method might have a good chance of overcoming some of the previous problems. Mita6 reported the growth of hexagonal ZnS from molten NaCl and wilke7 reported the growth of iron sulfides from molten lead chloride solution, indicating that molten chlorides make good solvents for sulfides. An investigation of a number of possible molten chlorides as solvents showed that molten PbCl2 has an appreciable solubility for zinc sulfide and that crystals can be grown at temperatures from 500° to 800°C. EXPERIMENTAL Crystal growth was performed in open or sealed Vycor or fused silica tubes, in an argon atmosphere or vacuum. There were no deleterious effects due to using vacuum; however, a sealed essentially isothermal system must be used to prevent vapor transport mechanisms from dominating. This will be discussed later in detail. Noble metal containers were not usable as they were severely attacked by these melts. The materials used were: reagent-grade PbC12, reagent-grade ZnS, optical-coating-grade ZnS, and Irtran 2 (ZnS). Crystal growth was accomplished by both slow cooling techniques and gradient growth techniques. In the slow cooling techniques, 15 g of ZnS and 100 g of PbCl2 were used. The components were placed in the silica tube, heated at 800°C for 2 hr, and then slowly cooled (l° to 10° C per hr) to 500°C. The furnace was constructed so that the tube could be inverted, thus allowing the liquid to drain off the crystals at the end of the run. The gradient runs were made by placing the above mixtures in a silica tube at 550° to 600°c, Fig. 1. A temperature gradient was maintained such that the floating mass of undissolved sulfide was 10° to 50°C warmer than the bottom of the tube. Growth occurred on spontaneously nucleated sites at the cooler bottom. RESULTS When using high cooling rates (5° to 10°C per hr), crystals form in thin sheets perpendicular to the {111} face. Crystals 5 by 5 by 1.2 mm, Fig. 2, have been ob-

Jan 1, 1969

HAVING previously described the metals to you, before I proceed any farther I do not wish to fail to tell you, as I promised to do in the first chapter on metals, what I have learned through experience concerning the semiminerals, although this may seem to you outside our proposed subject. Since these are not produced by Nature as all rock or all metal they are called semiminerals by speculative physicians. Many kinds of these are found; those that resemble rocks are earthy, very difficult to liquefy, and much more adapted for adorning paintings than for anything else. Those that liquefy with fire, like sulphur, antimony, marcasite, [22] calamine, zaffre, manganese, and others, resemble the metals almost like brothers. Some others are more watery so that they dissolve in water, although they are fairly dense, and are obtained and reduced to their, perfection by means of water. These are the salts, vitriol, rock alum, and saltpeter. To these, as a watery thing, belongs also quicksilver, as it is commonly called because of its motion. Although it appears. not only liquid, but very liquid, this is not at all similar in its effects to any of the above. Indeed, it retains its same being until its very form is consumed. Since the reasons for its effects are almost impossible to investigate, I do not intend to speak of them here or to enter now this maze of speculation, because I wish to make definitely clear to you what this quicksilver really is. Therefore, leaving aside opinions and disputes, I shall take only those of the said semiminerals that I know are useful. First we shall see the method by which the semiminerals can be found and then how they are to be extracted from their matrices. These, perhaps, have no less need of effort and industry than the metals since they are substances completely hidden in the rocks or in the earth. For this reason some of these that are sought are made use of by means of fusion after they have been mined from their mother mountains, and some others need to be disposed by a certain maturative corruption, now with moisture and coldness, now with dryness and heat, as with waters, rains, frosts, or long baking in the sun, with fire, or even with a strong reheating within themselves. Most of them can finally be brought to the desired end by means of solution with water and fire.

Jan 1, 1942

By R. G. Davies

The activation energy for steady state creep above -500°C is observed to be independent of the applied stress although it varies from -67 kcal per mole at 2 at. pct Si to -100 kcal per mole at 11 at. pct Si due to changes in crystallographic order. The magnitude of the activation energy, by comparison with Fe-A1 alloys, indicates FeSi type of order in certain alloys. X-ray results confirmed the presence of FeSi type of order. It is proposed that dislocation climb is the rate controlling mechanism for all the alloys. It has been demonstrated that when a diffusion mechanism is the rate controlling process, the formation of a superlattice in brass,1 Fe3A1,2 Ni3Fe,3-5 and Feco6 1) increases the creep resistance, and 2) increases the activation energy for steady state creep. Furthermore, a study of creep in Fe-15 to 20 at. pct A1 alloys7 has revealed that as the alloy composition approaches the long-range order field, there is an increase in the activation energy for steady state creep which is thought to be due to an increase in short range order. Fe-A1 and Fe-Si alloys are similar in that they both form the DO3 superlattice in which aluminum or silicon atoms have only iron atoms as first and second nearest neighbors. There are, however, two important differences between the alloy systems: 1) The superlattice formation at -350°C commences at -10 at. pct si8 as compared to -20 at. pct Al,9 and 2) Fe-A1 alloys form a FeAl (B2 type) super-lattice where aluminum atoms have all iron first nearest neighbors even at 22 at. pct Al, but so far no similar FeSi superlattice has been observed. With the similarity between Fe-A1 and Fe-Si alloys in mind, alloys of iron with 2 to 11 at. pct Si were examined for variations with composition of the activation energy for steady state creep and of creep strength. The temperature range of greatest interest was above 1/2 TM (TM is the absolute melting temperature) where it is usually observed that diffusion is the rate controlling process. A subsidiary X-ray investigation of the Fe-Si system was undertaken in an attempt to define the position of the order-disorder boundary as a function of cooling rate. EXPERIMENTAL DETAILS a) Creep. Specimens whose gage length was 1.5 in. and with a cross-section 0.04 by 0.08 in. were strained in tension by a lever-arm arrangement, and the load was adjusted between each creep test to maintain constant stress. The apparatus and mode of operation have been fully described in a previous publication.7 As each test produced a creep strain of 0.25 pct, the variation in stress during the test was negligible. Creep strain was measured at the end of one of the alloy steel grips by a displacement transducer with the out-of-balance potential being recorded on a variable speed recorder. The full-scale deflection of the recorder could be varied in steps to give limits of sensitivity of between 0.1 and 0.001 pct creep strain. The alloys, Table I, were made available by the Metallurgical Department, National Physical Laboratory (N.P.L.), england,10 and by the Research Department, General Electric Co. (G.E.), Schenectady, N.Y. They were hot worked at -850°C, warm worked at 550° to 650°C, and recrystallized in vacuum at -750°C to give a grain diameter of -0.1 mm. All the alloys had a very low impurity content; those from the N.P.L., for which a complete analysis is available,&apos;&apos; show carbon less than 0.026 pct, manganese less than 0.006 pct, and oxygen plus nitrogen less than 0.0024 pct. b) X-ray Procedure. A General Electric XRD-5 X-ray set with a focussing lithium fluoride mono-chromator in the diffracted beam, and a pulse height analyzer to eliminate harmonic wavelengths of the cobalt radiation, was used to investigate the structure of several very fine grained (grain diameter <.01 mm) Fe-Si alloys after the following heat treatments: 1) Quenched from 700°C, 2) slow cooled from 650°C (-40°C per hr), and 3) very slowly cooled from 400° to 100°C (10°C per hr with a 24 hr anneal every 100°C). The method of obtaining the diffraction pattern over the range of 20 from 15 to 45 deg was to count for at least 100 sec every l/3 deg with a slit subtending 1 deg in 20 at the focus; the probable counting error was less than 2 pct.

Jan 1, 1963

By AIME AIME

BY the end of 1943, the United States will be able to produce aluminum at a rate of 1,150,000 tons a year. How much aluminum is 1,150,000 tons? It is sufficient to replace every railroad passenger car in this country three times a year. Or, it would put a thirty-piece aluminum cooking utensil set in every one of America&apos;s 34,000,000 homes with enough metal left over to make 5,000,000 miles of aluminum transmission cable, such as was used in the electrification of much of rural America. Expansion of aluminum production capacity for the war program has occurred in three steps: (1) expansion by private industry; (2) the letting of contracts by the Defense Plant Corp. for the construction of additional aluminum plants which may remain after the war to compete with existing facilities; and (3) the more recently announced D.P.C. program for the building of emergency plants to make aluminum, using stand-by power available in large metropolitan centers power of relatively higher cost, making it questionable whether such plants, now gravely needed, will be able to compete in a peacetime economy.

Jan 1, 1943

By M. B. Bever, A. B. Michael

The solidification of aluminum-rich aluminum-copper alloys was investigated for different solidification rates. The measured amounts of nonequilibrium eutectic were compared with the amounts calculated on the assumption of no diffusion in the solid. The morphology of the eutectic was studied and dendritic spacings were measured. Compositions of the cored primary solid solutions were determined by quantitative autoradiography after activation of the solute copper by neutron irradiation. CONSIDERABLE progress has been made in recent years toward an understanding of the solidification of metals. This is especially true for the factors involved in nucleation, the controlled growth of metal crystals from melts, and various aspects of the freezing of ingots and castings. Many features of the solidification process, however, are not understood adequately and much further work is required. In the research reported here the solidification of a series of aluminum-rich aluminum-copper alloys was investigated. Different degrees of deviation from the idealized case of equilibrium solidification were attained by varying the rate of solidification. Thermal analysis and microscopic examination were supplemented by lineal analysis and autoradiography. The latter required the use of radioactive tracers and was adapted to the quantitative determination on a microscale of concentrations of copper dissolved in aluminum. The tracers were produced in situ by activating the copper with neutrons. These techniques permitted a correlated interpretation of the temperature-time history, the amounts of nonequilibrium eutectic and the general morphology of the alloys, and yielded quantitative data on microsegregation. Nonequilibrium Solidification In the general case of the solidification of a solid solution in accordance with the phase diagram, the composition of the coexisting liquid and solid must change continuously. This change requires diffusion, which at best remains incomplete in the solid during solidification. The resulting inhomogeneity of the solid solution crystals is well-known as coring, dendritic segregation, or microsegregation. The generally accepted analysis of coring assumes that, 1—no diffusion occurs in the solid, 2—diffusion is complete in the liquid, and 3—the composition of the solid formed on cooling through any infinitesimal temperature interval is given by the solidus of the phase diagram. On this basis, In this equation m designates mass, x designates the concentration of solute and the subscripts L and S refer to the liquid and solid phases, respectively; the subscript o indicates the initial state, in which the liquid is identical with the entire system. Eq. 1 or its equivalent has been derived repeatedly&apos;-7 and an analogous equation, known as Rayleigh&apos;s equation, has been used for distillation. The assumptions on which Eq. 1 is based do not include an infinitely fast cooling rate as sometimes stated. In fact, Olsen and Hultgren %ave shown by experiment that very high solidification rates suppress coring, presumably by preventing diffusion in the liquid and by the effect undercooling has on the composition of the nucleus. Coring thus occurs at rates of cooling which are too fast for a close approach to equilibrium in the solid and too slow to suppress diffusion in the liquid and to cause marked undercooling. If the liquidus and solidus approximate straight lines, Eq. 1 simplifies to The fraction of liquid present at any temperature during nonequilibrium solidification can be calculated from Eqs. 1 or 2. By the lever relation it is

Jan 1, 1955

By G. S. Tint, M. Herman, V. V. Damiano

Dislocation arrays and substructures were studied in cadmium doped zinc crystals using a newly devised etching technique. Cadmium precipitates delineating the dislocations were revealed by etching a surface closely parallel to the (0001) slip plane. Cinephotomicrography of the continuous etching process revealed the three-dimensional aspects of dislocations in the bulk crystal. Dislocation etch patterns were studied in both deformed and annealed crystals after suitable aging at room temperature. The effect of annealing was evidenced by a rearrangement of the dislocations into low-angle boundaries and hexagonal networks. ETCH pit techniques have been used extensively to study dislocations in both deformed and annealed bulk metal crystals. Ideally one hopes to obtain a one-to-one correspondence between the etch pits and the points of emergence of the dislocations at the surface. One then attempts to deduce the way in which dislocations are arranged in the bulk crystal from the arrangement of etch pits on the surface. It is clear that one can obtain only limited information of the dislocation configurations inside the crystal from etch pit studies of single surfaces. Considerably more information is obtained if one is able to follow the course of the dislocations through the crystal using progressive etching technique. Techniques of this sort were used by Gilmanl to study dislocations on the slip planes of NaCl crystals and by Damiano and Tint2 to study dislocation arrangement in zinc crystals grown from the melt. The present paper makes use of a technique first described by Tint and Damiano3 to observe and continuously record the dislocation structures which appear while a crystal surface was being progressively etched. Studies were made on cleaved (0001) surfaces to reveal the dislocations along their length on the surface closely parallel to the slip plane. The technique for revealing segments of dislocations along their length by etching is well known. Wilsdorf and Kuhlmann-wilsdorf4 revealed disloca- tions along their length in aluminum containing a few percent copper, when precipitates segregated along the dislocations. The technique was used by Low and Guard5 to study dislocation configurations on the slip plane in Fe-Si alloys containing carbon. In the present work the technique was applied to zinc containing cadmium since it was shown by Gil-man6 that a cadmium-rich phase could be made to precipitate from supersaturated solutions along dislocations in zinc. Segments of dislocations delineated by the precipitates were revealed by etching a surface prepared by cleaving the crystal. The three-dimensional nature of dislocations and substructures was thus studied from the cinephotomicro-graphic record of the continuous etching process. EXPERIMENTAL Single crystals of zinc containing the order of 0.1 pct Cd were prepared by slowly lowering a graphite crucible containing the melt through a temperature gradient of 15°C per cm at a rate of 1.5 X 10-3 cm per sec. "As grown" crystals were aged for periods of 1 month at room temperature, then cleaved in liquid nitrogen, and etched according to the procedure used by Gilman.&apos; The etchant containing 32 g of CrO3, 6 g of hydrated Na2SO3 in 100 ml of water behaved as a chemical polish for zinc and etch pits were produced at the site of precipitates or inclusions. After the precipitates or inclusions were removed from the surface, the etch pits left behind were eventually polished smooth. This behavior enabled one to continuously observe the surface while the specimen was immersed in the etchant. Best results were obtained when the specimen surface was vertical and the reaction products of polishing were continuously removed by gravitational convection. Some crystals were heavily deformed in excess of 25 pct strain, others were lightly deformed the order of a few pct by compression such that the deformation occurred essentially by basal glide. Some crystals were etched immediately after deformation, others were allowed to age at room temperature for several weeks prior to etching. Heavily deformed crystals were annealed at various temperatures and etched on the cleavage plane immediately after annealing, others were allowed to age at room temperature for several weeks prior to etching. The etched structures of deformed and annealed structures were studied. Similar experiments were conducted on 99.9999 pct pure zone refined Tadanac zinc crystals which

Jan 1, 1963

By R. M. Brick

THE Institute of Metals Division Lecture in 1936, given by R. F. Mehl, on diffusion in solid metals1, was introduced with the statement that "the phenomena of diffusion are intimately related to many basic prob-lems of the metallic state, but in addition to this the process of diffusion is of first importance practically." In view of the scope of that lecture, it does not seem necessary to review the importance, history or present status of diffusion problems. One aspect of the subject of diffusion that has received little attention became of some immediate importance in the course of a study on segrega-tion. When a solid solution alloy freezes, the familiar mechanism of solidification requires that the first nuclei formed be low in solute con-centration, with a resultant normal segregation or coring effect during freezing. Theoretically, diffusion of solute atoms during solidification should result in a homogeneous solid solution. Actually, of course, it is impossible in most binary alloys to obtain a cooling rate that will permit diffusion to eliminate coring in the freezing dendrites. For a given alloy, the extent of diffusion attained up to the point of final solidification will determine the degree of enrichment in solute atoms of the final liquid phase. The flow of this liquid into dendritic contraction channels and the solute concentration of the liquid seem to be the determining factors as to whether the final gross segregation is normal, inverse or absent. The purpose of the present study of diffusion was to determine to some extent the separate diffusion rates of copper and magnesium into pure aluminum with a view to clarifying previous results on segregation in these alloys; i.e., the fact that under similar freezing conditions alumimum-copper alloys segregate inversely and aluminum-magnesium alloys segre-gate normally. Of concomitant interest were the questions of the homogenization times required for segregated ingots or partially melted, i.e., "burnt," structures, and the solution heat-treatment times required for cast, hardenable aluminum-copper and aluminum-magnesium alloys, for worked and annealed structures, and so forth.

Jan 1, 1937

By H. Rumfelt

Strip mining in the domestic coal industry is contributing a greater proportion bf overall production than at any time in the past. U.S. Bureau of Mines statistics show that the percentage of total production mined in 1958 by stripping methods increased to more than 30 pct, up from 22 pct in 1951. The tendency to favor strip and open pit mining exists in other mining activities, but such trends are not as clearly outlined as in the coal industry. Significantly, the depth of overburden in coal properties considered suitable for stripping is also increasing. A depth of 50 to 60 ft of overburden was once considered to be about the maximum amount that could be handled economically. Today, a depth of 80 to 100 ft is frequently taken into consideration for simple overcasting operations (i.e., excavating overburden and dumping it in the spoil position where it remains indefinitely).

Jan 5, 1961

By H. H. Campbell

The following paper deals almost exclusively with the results of practice at the works of the Pennsylvania Steel Company at Steelton, Pa. From the records of the furnaces at this plant, both acid and basic, large and small, are drawn the data for the various demon strations, and on a long and intimate experience with their opera tions are founded many theories and generalizations. It may seem that universal laws should not be built upon a basis so restricted ; but in reality the condition is the strongest guarantee of validity. Each table investigates some- certain variable, and by virtue of the common origin of the factors, we have good ground for assuming the corresponding agents to be equal. The examples may or may not be instances of good practice, and may be open to criticism if regarded solely as exponents of • metallurgical success. But it must be remembered that the lists are not made up of selected specimens, nor are they chosen to show su perior results; they are gathered to investigate, by strict scientific methods, the formula? of the operation. In such work no untoward results should be eliminated, save those which bear upon their face the stamp of experimental error. If the worst members be omitted, then the best must also be omitted. Only by using every available case can an honest attempt be made to deduce a true average. It is recog nized, however, that with the most careful selection it is difficult, if not impossible, to collect data representing universal conditions. In each table the records tell of a special practice, and all conclusions drawn from them are true only within the limits between which the equations have been integrated. Not assuming the prerogative of speaking for American melters in all the opinions herein expressed, nor acting as a camera in por traying an ephemeral state of national metallurgical development,

Jan 1, 1894

By W. B. Gogarty

With the use of polymer solutions in secondary recovery operations, the need has developed to understand the mobility control mechanism. This study investigated mobility control by considering both permeability and rheological effects. Experiments used a high molecular weight, partially hydrolyzed polyacrylamide polymer. Flow studies took place in reservoir and Berea cores having zero oil saturation. Effective size of the polymer flow unit was inferred from Nuclepore filter tests. Clay studies indicated the particle size capable of decreasing the core permeability. Flushed permeabilities measured the approximate core permeabilities with flowing polymer solutions. These permeabilities were considerably lower than original values. With mobility data and the flushed permeability, maximum effective viscosities were determined for polymer solution flow in a core. Effective viscosities showed that rheological properties play an important part in mobility control with polymer solutions. The study showed that permeabilities decrease and stabilize with polymer flow. At the lower permeabilities, high shear rates exist in the cores. Because of the pseudoplastic character of the polymer solution, the high shear rates caused low effective viscosities. This condition pointed to the inefficient use of the potentially high viscosity of the polymer solution at low shear rates. INTRODUCTION In the oil industry, a great deal of interest is being shown in the use of polymer solutions for secondary recovery and a number of polymer floods are being performed in the United States.1 Some of these floods have become commercial while others have been reported as failures. A number of floods are still in progress and remain to be evaluated. With the advent of polymer flooding, the need developed to understand the mobility control mechanism in porous media. Rheologically, the polymer solutions behave as pseudoplastic fluids. Investigators have studied the rheology for this type of non-Newtonian fluid in porous media?-6 Results have also been reported on the ability of polymer solutions to decrease mobility.7-10 Some investigators indicated that polymer solutions show a different rheological behavior in cores than on the viscometer.7,8 This study is representative of an initiatory investigation on mobility control with polymer solutions. Some effects are considered on a qualitative basis. Mobility control is considered from the standpoint of both permeability and rheology and, to the extent possible, permeability and rheological effects are considered separately. Results show that mobility control occurs from a reduced permeability caused by polymer retention and an effective viscosity determined by the average shear rate in the core. In this respect, rheological behavior is as important in mobility control as permeability. PROCEDURES A high molecular weight, partially hydrolyzed, polyacrylamide polymer was used in the investigation. Solutions of various concentrations were made with this polymer in different types of water. Some solutions used distilled water and others used tap water. The tap water contained approximately 500 ppm dissolved solids. As used in this paper, concentrations in ppm refer to parts by weight solute to one million parts by weight of solvent. In the tap water, calcium and magnesium accounted for from 60 to 80 ppm of the solids, the remainder being mostly sodium chloride. All solutions contained a bactericide, and anti-oxidants and antiprecipitants were added to the tap water. Capillary and concentric-cylinder* viscometers determined the rheological properties of solutions. The capillary viscometer is described elsewhere.6 Berea and reservoir sandstone were used as core materials for this investigation. Cores were 1 in. in diameter by approximately 2 to 3 in. long. Prior to mounting, the Berea cores were heat-treated for 3 hours at 850F. This treatment decreased the water-sensitivity of the clays in the cores. The reservoir cores were cleaned with solvent and