By L. Weyher, H. L. Lovell

This discussion is restricted to a very specific application of the cyclone - its use as a hydro-cyclone in the cleaning of fine coal. It is hoped that the development of the present data will assist in the further elucidation of existing qualitative models, and also in an enhanced application of the hydrocyclone and provide a base for further research. Discussed are the mechanisms of gravity separation in hydro-cyclones, test procedures, experimental observations, and industrial applications from these studies. Within the general area of unit operations, a considerable effort has been expended in theoretical and empirical research associated with cyclone operations. The motivation involves the industrial requirement for devices and techniques to manipulate small particles at low operating costs, a situation required in coal preparation. There are good reasons why the cyclone helps to satisfy this demand, because it combines operational simplicity (no moving parts) with versatility and high throughput capacity per unit area. The cyclone is one of the most widely applied tools in the process technologies. There are areas for potential cyclone application which have been only meagerly explored or not considered at all. This discussion is restricted to a very specific application of the cyclone - its use as a hydrocyclone in the cleaning of fine coal. It represents an initial presentation of a more comprehensive report. Coal preparation can appropriately claim the hydrocyclone since most of its predominant industrial uses have originated in this area and have spread into other applications, including the broad field of ore dressing, the petroleum industry, chemical processing, nuclear engineering and food technology. There is one operational principle common in all cyclones: A fluid is tangentially introduced into a cylindrical or conical container under pressure. A predominantly irrotational flow field1 is established within the cyclone (Fig. 1). The uniqueness of this flow is indicated by the variation in tangential velocity across the cyclone radius, which reaches a maximum a short distance from the center and decays toward the cyclone wall. In contrast, the tangential velocity in a centrifuge increases uniformly toward the wall. Usually two products are discharged from the cyclone. They differ in that one discharge consists predominantly of that portion of the feed fluid which moves along the wall axially away from the feed inlet, while the other consists predominantly of fluid spiralling along the central regions of the cyclone, in an axial direction opposite to that of the wall current. Fig. 2 indicates these discharge points schematically. The latter product may be termed the vortex-product, since it is discharged with the central vortex-current. In the case of conical cyclones, the former product may be referred to as the apex-product. Although the names "over- and underflow" are widely used, many cyclones are operated from extreme angular positions thus the proposed terms are less ambiguous. The cyclone feed fluid can be laden with solid particles or nonmiscible fluid drops. Such a feed component is discharged from the cyclone, after some residence time, into the one or the other product. Yet, the orifice through which a particle will leave the cyclone is dependent upon a number of factors. These factors, in a statistical sense, determine the path of the particle within the cyclone. Thus, different separation phenomena are possible and different process results attainable by the controllable variation of the particle path. It is then, to attain a fuller understanding of this particle path, to which this study is ultimately directed. It is anticipated that the detailed study of the data being developed will allow further elucidation of existing qualitative models. However, the development of a quantitative description of cyclone operation in terms of a mechanism is not currently feasible. The flow conditions in a cyclone are not fully understood even for a pure fluid, without the added complexity of the inclusion of multiple size-density particles. It is hoped that the development of the present data will also assist in an enhanced application of the hydro-cyclone and provide a base for further research. Some practical applications drawn from the data are suggested. Cyclone operations have been classified according

Jan 1, 1967

By C. Gatlin, N. E. Garner, A. Podio

Experimental data from single chisel blows on Leuders limestone are presented. A pressure chamber, similar in design to well known microbit drilling chambers, was utilized to impose variorcs stress states on the sample. Confining pressure of zero to 10,000 psi and borehole pressures from zero to 5,000 psi have been used in the studies. Pore pressure was zero and the rock samples dry in all instances. Force-displacement records and visual examination of the craters indicate that the mode of failure depends on both confining and borehole pressure in certain ranges, ranging from brittle, through a transition, to near plastic. The mode of failure is reflected in the observed blow force and energy data, as well as the shape of force-penetration curves. INTRODUCTION A previous paper' presented initial data from the project on which this paper is the second report. While the first paper dealt with impact studies on synthetic rocks, the literature cited there is also pertinent to this paper, but will not be listed again in order to avoid needless repetition. This paper presents experimental data from single chisel impacts on limestone at certain simulated wellbore stress states. Specific variables investigated were combinations of borehole and confining pressure, crater geometry, a narrow range of impact velocity and the forces required to drive the chisel into the specimens under the varying conditions. EXPERIMENTAL PROCEDURE The same basic apparatus described in our earlier paper, except for the pressure vessel, was used in this study. Fig. 1 shows the complete experimental system. Fig. 2 shows details of the pressure cell, which is quite similar to the well known microbit drilling chamber. The confining (overburden) pressure system provides independent pressure control over the sample except for two, 21/4 in. diameter areas located on the sample ends. These two areas provide a pore pressure entrance on the bottom and a striking surface on the top where borehole pressure can be controlled. The ends are isolated from the confining pressure by O-ring seals. The borehole and pore pressures are related through the striking surface; they will be the same unless a seal is deposited on the borehole surface, either a mud cake or some other impermeable membrane. In these studies pore pressure control was not used, as the rocks were dry and unsaturated in all cases. Rock samples were prepared from 4-in. cubes as illustrated by Fig. 3. The circular disks of adhesive vinyl plastic protected the impact surface from the resin coating (Scotchcast No. 2) and were removed just prior to each test. This procedure insured a fresh uncontaminated surface for the impact. Fig. 4 shows the dimensions and loading of the sample, including the concentrations around the "borehole" periphery (O-ring seal). The rock used in this study was Leuders limestone, of Permian age (Leonard), quarried near Leuders, Tex. Geologically, Leuders limestone is a light gray, fossili-ferous limestone (oolitic foraminifera1 biosporite). Its fossil content is 80 to 90 per cent and consists primarily of calcitornellid, ostracods, pelecypods and oolites with the remaining part intraclasts. There are hematite or limo-nite rims on some of the intraclasts. The porosity is approximately 20 per cent, but the permeability is less than 1 md. There is no apparent orientation in the structure. Triaxial tests have been conducted to determine the variation of the physical properties of Leuders limestone in three orthogonal directions', and it is known to be unusually isotropic and uniform. Physical parameters for this rock are: uniaxial compressive strength = 9,700 psi; F = 32 and C = 2,700 psi; where + and C are Coulomb equation values (t = C+u tan +). Impact tests were run under the combinations of confining and borehole pressures shown in Table 1. Samples were dry with atmospheric pore pressure in all cases. Tests, in which elevated borehole pressures were applied, used a single layer of household Saran-Wrap to prevent horehole fluid invasion into the sample. This proved to be simple and reliable. The blunt wedge used in all the tests was 0.75 in. long and had an included angle of 60" with a 0.05-in. flat. In addition, a sharp 60" wedge was used for all confining pressures at zero borehole pressure. The chipper speed

By J. W. Goss, M. J. Coolbaugh

Most grouting has been done to stop water flaw in mines and for stabilizing foundations of various man-made structures, a survey of the U.S. literature reveals. Apparently Sun Manuel is one of the first mines in this country to use grout extensively underground for strengthening and stabilizing ground in drifts, shafts, and stations. A comparison with other procedures as well as details of the Sun Manuel program are covered. The employment of pressure grouting as a ground stabilizer at the San Manuel Copper Corp. mine reduces delays in both development and production, lowers costs, and makes possible safer working conditions. It specifically reduces delays in haulage operations and permits the maintenance of normal ventilation. In development work this grouting allows faster excavation by cementing together highly fractured or broken ground that otherwise would require extensive cribbing or spiling. In drift repair, it consolidates the loose or fractured rock over the timber or steel drift supports, thus decreasing the frequency of repair, lessening the hazards from falling rock, and curtailing delays due to blockage of drifts by muckpiles and repair operations. Pressure grouting is the process of pumping an accurately controlled mixture of cement and water into loose, fractured, or porous rock. The ratio of water to cement varies according to the nature of the rock encountered, from the thinnest mixture of 30 gal of water per sack of cement, used to fill very fine fissures, to very thick grout of 5 gal of water per sack of cement, used to fill large fissures or extensive areas of loose, broken rock. The pumping pressures at San Manuel vary from about 100 to 1000 psi, depending upon the compactness of the rock, while at other mines the pressures sometimes go as high as 5000 psi. In order to grout an area in which ground water is encountered, the pumping pressure of the grout must be increased by an amount equal to the pressure of the ground water. GROUTING IN DEVELOPMENT WORK The areas under development at San Manuel include many sections of loose, highly fractured rock. Prior to the advent of the grouting program, drifts, shafts, and stations in these areas could not be excavated without utilizing extensive support such as cribbing, spiling, and breast boarding. This slowed down the development work and increased the costs considerably over that required for excavating in more competent ground. Now, when a particularly bad area is contacted, the mining is temporarily stopped while the bad portion of drift or shaft is grouted. After the grouting is completed, the excavating is resumed with an approximate decrease of 50 pct in lost time and costs. Grouting in Drifts and Turnouts: The grouting procedures and patterns used in drifts and turnouts are very similar. The standard procedure for grouting such a turnout is shown in Fig. 1. After the ground is supported as well as possible with cribbing or lagging, the gaps between the back lagging and side lagging are plugged with empty cement sacks or additional timber, if necessary. The ground surrounding the proposed turnout is then grouted in two stages. In the first stage, the broken and caved rock is drilled and grouted to a depth of 5 to 10 ft, depending on the depth of the broken rock. This stage forms a grouted seal that allows higher pressures to be used at depths beyond 10 ft without developing excessive leaks at the face. After a grout hole is drilled, a 10-ft long pipe is wedged tightly into it with empty cement sacks. Grout is then pumped into the hole until the pressure reaches 200 to 300 psi, and the pipe is subsequently removed if it hasn't become cemented in. No more than one hole at a time is drilled and grouted because the grout has a tendency to go from one hole into another, plugging up the latter. Five or six holes are usually adequate for the first 10 ft of grouting. Experience has shown bentonite to be a useful admixture to the grout, particularly when it is indicated that the grout is being lost into large fissures or voids. Bentonite increases the plasticity of the grout enabling it to remain in place more easily until it has begun to set. In the second stage, the longer holes are drilled through the previously grouted rock, after which the

Jan 1, 1961

By R. W. Hertzberg, F. D. Lemkey, J. A. Ford

The technique of unidirectional solidification has been applied to the A1-AI3Ni and A1-CuAl2 ezltectic alloy systems; the controlled microstructure of A1-A3Ni consists of parallel A13Ni whiskers emhedded in an aluminum matrix while the Al-CuAl2, system solidifies as parallel alternate lamellae of aluminm and CuAl2. Mechanical tests (tension and flexure) have shown that the particle-matrix interface bond formed during unidirectional solidification allowes for efficient load transfer from the matrix to the reinforcing phase. Strength and fracture characterstics of the alloys were studied as a function of phase orientation; the tensile strength of controlled Al-Al3Ni samples was 43,000 psi (three times greater than that of as-cast specime~s). The strength of the Al-CIA2, cutectic was studied as a function of lamellae-flexure stress-axis orientation using a microbend apparatus. A twofold increase in outer fiber stress was observed as the lamellae were rotated from a position of no reinforcing (perpendicular to the stress axis) to one of maximum reinforcing (parallel to the stress axis), The brittle reinforcing constituent in each alloy (A13Ni and CuAl2) was observed to he the nucleating phase for fracture. It is to be concluded from this investigation that unidirectionally solidified eutectic alloys have a potential use as reinforcing coniposite) materials. In a recent review article, Chadwick1 has described the work of many investigators in the area of controlled solidification of binary eutectic alloys. Thus far, more than twenty eutectic alloys have been unidirectionally solidified to produce structures consisting of two phases in the form of alternating lamellae or as whiskers embedded within a continuous matrix; in either case, the phases are aligned parallel to the growth direction. In particular, Kraft and Albright2 have shown that the Al-CuA1, eutectic alloy exhibits a lamellar microstruc- ture as a result of unidirectional solidification while Lemkey, Hertzberg, and Ford3 have studied the A13Ni whisker-aluminum matrix morphology in the A1-A13Ni system. Whether these alloys could exhibit reinforcing behavior would have to depend upon the strength and volume fraction of the reinforcing phase (AI3Ni and CuA12) and the nature of the bond between the reinforcing phase and the matrix. Hertzberg and Kraft4 have shown that the interface bond between chromium whiskers and a copper matrix in unidirectionally solidified Cu-Cr is particularly good while Lemkey and Kraft5 have reported chromium-whisker tensile strengths in excess of 1,000,000 psi. However, with the chromium volume fraction being less than 2 pct, no reinforcing behavior was displayed by the Cu-Cr alloy.6 In view of the encouraging results concerning the good interfacial bond and high strength of the reinforcing phase in the Cu-Cr system and preliminary mechanical test data reported by Lemkey et al.3 for the A1-A13Ni system, the A1-CuA1, and A1-A13Ni eutectic alloys containing 50 and 10 vol pct, respectively, of the reinforcing phase give promise of possessing mechanical reinforcing behavior. Based on this premise, the objective of the investigation was to study the strength and fracture behavior exhibited by these anisotropic microstructures. EXPERIMENTAL PROCEDURE Controlled Solidification Procedure. An extensive description of the technique of unidirectional solidification has been presented elsewhere.' However, the pertinent details for each eutectic system studied are discussed below. Al-A13Ni System. Several master heats of this alloy were prepared by vacuum-induction melting in an A12O3crucible and casting in SiO2 mold or by induction melting in alumina crucibles under argon. The initial heats were prepared from 99.99 pct A1 and 99.99+ pct Ni, while later heats used 99.999+ pct A1 and 99.99+ pct Ni. Specimens of these master heats were unidirectionally solidified using induction and resistance heating sources and argon atmospheres at growth rates from 1.1 to 28.7 cm per hr. The thermal gradients in the liquid were controlled in the range of 26" to 36°C per cm for these runs. Al-CuA12 System. The master heat and controlled

Jan 1, 1965

By G. S. Tint, M. Herman, V. V. Damiano

Dislocation arrays and substructures were studied in cadmium doped zinc crystals using a newly devised etching technique. Cadmium precipitates delineating the dislocations were revealed by etching a surface closely parallel to the (0001) slip plane. Cinephotomicrography of the continuous etching process revealed the three-dimensional aspects of dislocations in the bulk crystal. Dislocation etch patterns were studied in both deformed and annealed crystals after suitable aging at room temperature. The effect of annealing was evidenced by a rearrangement of the dislocations into low-angle boundaries and hexagonal networks. ETCH pit techniques have been used extensively to study dislocations in both deformed and annealed bulk metal crystals. Ideally one hopes to obtain a one-to-one correspondence between the etch pits and the points of emergence of the dislocations at the surface. One then attempts to deduce the way in which dislocations are arranged in the bulk crystal from the arrangement of etch pits on the surface. It is clear that one can obtain only limited information of the dislocation configurations inside the crystal from etch pit studies of single surfaces. Considerably more information is obtained if one is able to follow the course of the dislocations through the crystal using progressive etching technique. Techniques of this sort were used by Gilmanl to study dislocations on the slip planes of NaCl crystals and by Damiano and Tint2 to study dislocation arrangement in zinc crystals grown from the melt. The present paper makes use of a technique first described by Tint and Damiano3 to observe and continuously record the dislocation structures which appear while a crystal surface was being progressively etched. Studies were made on cleaved (0001) surfaces to reveal the dislocations along their length on the surface closely parallel to the slip plane. The technique for revealing segments of dislocations along their length by etching is well known. Wilsdorf and Kuhlmann-wilsdorf4 revealed disloca- tions along their length in aluminum containing a few percent copper, when precipitates segregated along the dislocations. The technique was used by Low and Guard5 to study dislocation configurations on the slip plane in Fe-Si alloys containing carbon. In the present work the technique was applied to zinc containing cadmium since it was shown by Gil-man6 that a cadmium-rich phase could be made to precipitate from supersaturated solutions along dislocations in zinc. Segments of dislocations delineated by the precipitates were revealed by etching a surface prepared by cleaving the crystal. The three-dimensional nature of dislocations and substructures was thus studied from the cinephotomicro-graphic record of the continuous etching process. EXPERIMENTAL Single crystals of zinc containing the order of 0.1 pct Cd were prepared by slowly lowering a graphite crucible containing the melt through a temperature gradient of 15°C per cm at a rate of 1.5 X 10-3 cm per sec. "As grown" crystals were aged for periods of 1 month at room temperature, then cleaved in liquid nitrogen, and etched according to the procedure used by Gilman.' The etchant containing 32 g of CrO3, 6 g of hydrated Na2SO3 in 100 ml of water behaved as a chemical polish for zinc and etch pits were produced at the site of precipitates or inclusions. After the precipitates or inclusions were removed from the surface, the etch pits left behind were eventually polished smooth. This behavior enabled one to continuously observe the surface while the specimen was immersed in the etchant. Best results were obtained when the specimen surface was vertical and the reaction products of polishing were continuously removed by gravitational convection. Some crystals were heavily deformed in excess of 25 pct strain, others were lightly deformed the order of a few pct by compression such that the deformation occurred essentially by basal glide. Some crystals were etched immediately after deformation, others were allowed to age at room temperature for several weeks prior to etching. Heavily deformed crystals were annealed at various temperatures and etched on the cleavage plane immediately after annealing, others were allowed to age at room temperature for several weeks prior to etching. The etched structures of deformed and annealed structures were studied. Similar experiments were conducted on 99.9999 pct pure zone refined Tadanac zinc crystals which

Jan 1, 1963

By Pradeep K. Rohatgi, Clyde M. Adams

An analysis of heal conduction in the freezing of a solution has been performed. The case considered is the semi-infinite mass of solution, bounded by a con-stant-temperature plane with one-dimensional heat flow, Numerical cooling rate and freezing rate distributions hare been calcutated for the particular case of unidirectional freezing of aqueous solutions against. a cold copper chill. The solution at each level parallel to the chill surface is subjected to a spectra of frcezing rates; the freezing rate is inilially lour., passes through a maximum, and then decreases until solidification is camplete. Arange and maximum freeeing rates are inversely proportional to the square of distance from the chill surface. The temperature of the chill surface in contact with the solution remains constant during solidification. Experimentally, it is observed that deudrite sparing increases linearly with distance from the chill surface; in the light of heat -flow analysis this means that the dendrile spacing is imersely proportional to the square root of the maximum freezing rate. SOLIDIFICATION of liquids is accompanied by rejection of latent heat at the solid-liquid interface. The over-all rate of liquid to solid transformation is governed by the rate of heat extraction. Analysis of the heat transfer in the liquid during freezing is important since it determines the freezing rate and resulting structure. A considerable amount of work has been done on metallic systems since solidification is frequently a major step in processing metals. Unidirectional freezing from heat sinks has been treated by several investigators.1-4 Much of the work has been limited to the simpler case of substances such as pure metals which freeze isothermally at a unique transformation temperature. In this case the thickness of the solid zone y, next to a chill surface. is a parabolic function of the time. 8. where a and b are constants. Eq. |1| is a close approximation giving the progress of solidification for the case in which there is a small but finite thermal contact resistance at the interface between the freezing liquid and the chill.' It has been used with some success in connection with large steel ingots4 when the therma1 contact resistance is negligibly small (as is the case when water is brought into contact with the metal chill). The constant, b. becomes zero and Eq. [l] is then exact. even when the thermal properties of the chill and the freezing liquid depend on temperature. Analysis of unidirectional solidification of solutions is more complicated since the latent heat is evolved over a range of temperatures. Next to the all-solid zone in contact with the chill surface there is a solid plus liquid zone in which solidification takes place. Although the equations presented are considered quite general the numerical and experimental results are for freezing of aqueous solutions from a copper chill. I) EXPERIMENTAL PROCEDURE Solutions of potassium chloride, sodium chloride. and lithium chloride have been used. These solutions form a eutectic: a typical phase diagram is shown in Fig. 1. A solution at its liquid us temperature is poured into a tygon tube mounted on a relatively large copper chill. The chill is immersed in a freezing mixture of dry ice and acetone at -70°C. A thermocouple connected to a high-speed recorder was mounted near the top of the chill to measure the fluctuation in the temperature of chill surface in contact with the solution. In this system the progress of solidification can be visually observed through the tygon tube. After the specimens freeze to a desired height they are removed from the copper chill and stripped from the tygon tube. Longitudinal and transverse sections are cut from the specimen for micrographic examination. Specimens in the form of a thin slice are mounted on a transparent glass slide by freezing small drops of water around the periphery. They are then polished on a series of emery papers; the final finishing is done on a soft tissue paper. A Leitz Biological microscope was used for structural observations; photography was

Jan 1, 1968

By W. M. Robertson

The rate of crack Propagation thvough a solid meta1 in the presence of a liquid metal has been calculated. The crack is assumed to propagate by solution of the solid in the liquid under the influence of an applied stress, with volume diffusion of the dissolved solute through the liquid controlling the propagation. The calculated velocities can be tens of centimeters per second or higher. THE embrittlement of normally ductile solid metals by liquid metals has been the subject of extensive study, as summarized in the book by Rostoker, McCaughey, and arkuus.' In experimental studies of liquid-metal embrittlement it is usually concluded that the observed crack-propagation rates are too high to be accounted for by diffusion processes. Diffusion is considered to be an unimportant factor and various other mechanisms are invoked to account for the experimental observations. The similarities of liquid-metal embrittlement to stress-corrosion cracking, to hydrogen embrittlement of steel, and to low-temperature embrittlement of bcc metals are frequently used as analogies for these mechanisms.1"3 The present paper assesses how rapidly a crack could propagate by a mechanism of volume diffusion through the liquid metal. We assume that the crack propagates by solution of the solid in the liquid at the crack tip under the influence of the applied stress and diffusion of the dissolved solute away from the crack tip. The model uses only macroscopic thermodynamic, kinetic, and elastic concepts. The calculations indicate that this dissolution-diffusion mechanism can give high crack velocities. In some previous treatments4'' of crack propagation in a liquid-metal environment the fundamental step has been the breaking of atomic bonds at the crack tip. The liquid greatly decreases the energy necessary to break these bonds. The present model assumes the crack is filled with liquid metal; the presence of the liquid is essential because diffusion through the liquid is assumed to control the rate of propagation. With proper modification this model could also apply to stress corrosion in a liquid environment. THEORY Consider a crack in a homogeneous elastic continuum, ignoring all the structural details of the solid. This neglects a host of metallurgical details which can be significant in the problem of liquid-metal embrittlement;' but this simple assumption is a useful approach in evaluating the role of diffusion through the liquid. The stress distribution around the crack tip establishes a gradient in the chemical potential at the tip, which causes a diffusion flux through the liquid away from the tip. The solid-liquid interfacial tension works against crack propagation, since propagation requires creation of interfacial area. From these two considerations we derive the diffusion flux, which then yields an expression for the velocity of the crack tip. The concentration of the solute in the liquid, C, is equal to the equilibrium concentration in the presence of an unstressed, flat surface, Co, plus the excess concentration due to the stress, AC(a), plus the excess concentration due to capillarity, AC(y): We calculate AC(o) and AC(y) and then obtain the diffusion flux. Consider (Fig. 1) a long flat crack of length 2L, thickness 2r, and tip radius r, where r remains constant as the crack propagates in the positive x direction. There is no stress ay in the y direction across the flat surfaces of the crack. The magnitude of the stress at the crack tip due to the applied stress, a,, is given by the relation6 ^=^[l-2^] 12] which, for long narrow cracks, becomes The stress increases the chemical potential in proportion to the strain energy.? The excess chemical potential due to the stress, Ap(a), is given by where 52 is the atomic volume of the solid and E the Young's modulus. Inserting Eq. [3] gives Now consider the crack to be filled with a liquid metal. The excess solubility due to stress, hC(a), is given by the excess chemical potential due to capillarity, Ap(y), is given by8 where y is the solid-liquid interfacial energy, and v1 and YZ are the two principal radii of curvature of any surface point. At the crack tip, r1 = -r and vz = m, so TRANSACTIONS OF THE METALLURGICAL SOCIETY OF AIME

Jan 1, 1967

By K. Tangri, M. Chaturvedi

On water-quenching from within the (a + ß) phase region Zr-2.5 Nb and Zr-2.5 Nb-0.5 Cu alloys can undergo w transfirmation. This transformation has been attributed to the enrichment of ß Zr phase, at the solution-treatment temperature, by the solute atoms. The ß—w transformation is accompanied by a hardening 01 the alloys and in the optimum condition w-bearing specimens of the ternary alloy are about 14 pct harder than those bearing only a' phase. On aging crl reverls thermally to more stable phases, which results in a considerable softening of the specirnens, as follows: w quenched -waged + ß Zr (enriched) waged - a + ß Nb The high-temperature bcc ß Zr in certain zirconium alloys can transform to a metastable w phase which has a primitive hexagonal structure. In the Zr-Nb alloy system w phase has been observed in the composition range of 7 to 15 wt pct Nb by a number of investigators.'-' In this composition range w can form by water-quenching ß Zr or by aging. known as athermal and thermal w, respectively. Hatt and Roberts' have found that thermal w has a constant c/a ratio of 0.622 +0.002 regardless of the composition and tha: the lattice parameters are of the order of a = 5.02A and c = 3.0 ?. The actual lattice parameters depend upon composition and the temperature of aging. The lattice constants of athermal w. however, depend upon alloy composition.3 The presence of w phase in zirconium alloys can cause substantial strengthening which has been attributed as probably due to the coherency between w and parent ß Zr phase. Robinson et al.' found that the presence of w can raise the strength of Zr-5.0 Nb-2.0 Sn and Zr-5.0 Mo-2.0 Sn alloys to about 170.000 psi: however. the ductility is considerably reduced. With the growing use of Zr-2.5 Nb and Zr-2.5 Nb-0.5 Cu alloys in the nuclear reactors, and the significant effect of w transformation on the mechanical properties of zirconium alloys studies were undertaken to study the w transformation in Zr-2.5 Nb and Zr-2.5 Nb-0.5 Cu alloys. This paper is concerned with the formation and reversion of w phase in these alloys. 1) MATERIALS AND EXPERIMENTAL TECHNIQUES The following two alloys were studied: 1) Zr-2.5 Nb-0.5 Cu (referred to as the ternary alloy): 2) Zr-2.5 Nb (referred to as the binary alloy). The chemical analysis of the alloys is given in Table I. The alloys, in the form of 3/8-in.-diam rods and 1/8-in.-thick sheets, were supplied by the Chalk River Nuclear Laboratories of the A.E.C.L. Initial fabrication for preparation of various specimens was carried out by cold rolling and swaging with intermediate anneals at 1000°C. All the heat treatments were carried out after the specimens were wrapped in zirconium foils and encapsulated in silica tubes under a vacuum of 5 x 10-% m of Hg. For optical metallography and hardness measurements disc specimens + in. diam by + in. thick were used. After the required heat treatments the specimens were mechanically and then chemically polished in a 45 pct HNO3, 45 pct H20. and 10 pct HF solution. The hardness measurements on the chemically polished specimens were carried out on a Vickers hardness tester using a 10-kg load. For each specimen at least fifteen indentations were made in order to obtain a representative hardness value. The phase identification and structural analysis were carried out using X-rays and electron diffraction techniques. Wires of 1.5 mm diam reduced to 0.12 mm diam by chemical etching were used for making Debye-Scherrer powder patterns using copper K-a radiations in 114.6-mm-diam camera. Thin films for transmission electron microscopy were prepared by electropolishing heat-treated a by 7 by 0.005-in.-thick strips using a modified Bollmann-Window technique. The 10 pct perchloric acid-90 pct methyl alcohol electropolishing bath was kepl at -5OCC and polishing was done at 5 to 10 v. The thinned specimens were washed in ethyl alcohol at -30" to -40°C and dried between filter papers. The thin films

Jan 1, 1970

By E. A. von Hahn, T. R. lngraham

Cementation rates ulere studied by rotating an elec-tropolished or etched copper strip in aqueous solutions, of either perchloric acid or alkaline cyanide, containing silver ions. The rates of cementation were more rapid in acidic media than in cyanide media. In both, the rates varied with the rate of rotation of the copper strip. The deposits formed in the acidic solutions were finely divided, loosely adhering powders. Those formed in the cyanide solutions were dense and adherent. The presence of the deposits influenced the cementation rates. In the acidic solutions the rate was enhanced, possibly because of the increased cathodic area. In the alkaline solutions the rates were decreased in the presence of the deposits. This has been attributed to restricting the diffusion of the copper ion from the rnetal outward into the bulk of the solution. In an earlier paper1 the authors described a kinetic study of the cementation of palladium on copper in perchloric acid solutions. That work indicated that there were two stages in the palladium cementation process. The first, more rapid stage was consistent with rate control by the diffusion of Pd11 ions to the copper surface and/or by chemical reaction at the surface. The second stage was consistent with rate control by the diffusion of copper ions from the copper surface, through the deposit, out into the main body of solution. The effect of the type of deposit on the rate of cementation is of particular interest because it may be one of the primary features involved when large quantities of metal are to be cemented from solution. No substantial investigations of the effect seem to have been made. Accordingly, an extension of the previous work was arranged to study the cementation of silver on copper. This system was selected because of the convenience of the analytical methods, the previously established technology with copper, and the fact that the system could be studied in both acidic and alkaline media. By selecting perchloric acid and alkaline cyanide solutions as the media, it was hoped that some assessment might be made of the effects, on cementation, of having the silver ion present in a virtually uncomplexed state and in a highly complexed state. EXPERIMENTAL The cementation rates were studied, as previously described,' by rotating a copper strip (1.0 by 23.2 cm) clamped to the peripheral surface of a lucite cylinder. The solutions were kept at constant temperatures (±0.05°C) under an atmosphere of purified nitrogen, and samples were taken periodically for analysis. The initial solution volume was 1000 ml and the sample volume 5 ml. The initial silver(1) ion concentrations were made low (0.5 to 1.0 x 10-4 moles per liter) to minimize the influence of the cemented deposit on rates. The solutions were prepared by dilution of suitable aliquots of silver perchlorate and silver cyanide stock solutions. Both stock solutions were prepared from purified silver powder (Johnson, Matthey, and Mallory Ltd.) with redistilled deoxygenated water, and they were kept under an atmosphere of purified nitrogen. To prepare the stock solutions, weighed amounts of silver powder were dissolved with nitric acid. For the AgC104 stock solution the silver nitrate solution was evaporated twice to near dryness with perchloric acid and then made up to volume: For the NaAg(cN)2 stock solution, the silver ions were precipitated with sodium hydroxide solution. The precipitate was filtered, washed thoroughly with redistilled water, dissolved with 1.1 times the required stoichiometric amount of sodium cyanide solution, and made up to volume. The small amounts of free perchloric acid and sodium cyanide present in the stock solutions were disregarded in the preparation of the solutions. The copper strips were cut accurately from 0.025-in. sheet (American Metal Climax OFHC brand) and annealed for 1.5 hr at 470°C in a stream of nitrogen. Analyses of the solution samples for silver and copper were done with a Techtron Model AA-3 atomic absorption spectrophotometer. Calibration standards of the same composition as the experimental solutions were prepared and analyzed simultaneously with the samples. No difficulty was experienced in the analyses, and the reproducibility was within 1 to 2 pct in both alkaline cyanide and perchloric acid solutions.

Jan 1, 1968

By B. C. Allen

Liquid surface tensions of copper and 18 Group IV-A to VIII transition metals (Ti, Zr, Hf, V, Cb, Ta, Mo, W, Re, Ru, Rh, Pd, Os, Ir, Pt, Fe, Ni. Co) have been measured by the static pendant-drop and dynamic drop-weight methods on the same rod sample. The drops were formed by electron-bombardment heating in high vacuum. Application of necessary corrections enabled determination of surface tensions to k2 pct and agreement between methods to * 1 to 4 pct for all the metals studied. Evidence is presented that the liquid surface was well screened by metal vapor, suggesting negligible adsorption of gaseous impurities and that the surface tensions measured are characteristic of the metals involved. Correlations between liquid surface tension and melting point, molar volume, heat of vaporization, and atomic number are presented and discussed. Temperature coefficients of surface tension were calculated using Eötvös' law. SURFACE tension and interface energies of metals are the result of incomplete atomic coordination resulting in a force perpendicular to the boundary, tending to minimize its area. These energies are important in many phases of metallurgy, including microstructure, sintering, joining, electronic emission, and lubrication, which in turn affect many physical and mechanical properties of metals. Liquid surface tension refers to the interface between the liquid and its own vapor or nonreactive atmosphere, and is considered a physical property of the liquid. Since equilibrium shapes can be readily obtained with liquids, the units of surface tension (force per length) and interface energy (energy per area) are interchangeable. Thermo-dynamically, the surface tension ?LV is given by the change in free energy F with surface area A at constant pressure P, temperature T, and composition N: for commercially important refractory metals, vanadium, columbium, tantalum,13,14 molybdenum,14 and tungsten,l5 and none for the rare platinum-group metals and rhenium. Measuring the surface tensions of transition metals is difficult because of their high reactivity and melting points. Of the many techniques available,16-18 the pendant-drop 19-21 and drop-weight methods17,22 are considered superior because they can be modified to eliminate persistent sources of contamination such as supports and capillaries necessary in the popular sessile drop, capillary rise, and maximum-bubble-pressure techniques. The necessary modification is to melt a drop on the tip of a vertical rod, which provides support through a solid of the same composition.13,15 The object of the work was to study the surface-tension behavior of copper and transition metals, having reasonably low vapor pressures. Liquid surface tension of each pure metal was systematically determined by using a combination of the static pendant-drop and dynamic drop-weight methods on the same rod. Liquid drops were formed by electron-bombardment heating in high vacuum. EXPERIMENTAL WORK As indicated in Table I, the metals studied were high purity and generally were obtained in rod form. The exceptions were titanium and zirconium, which were machined from crystal bars, and molybdenum (tot 11, osmium, and ruthenium, which were sintered and arc cast into rods. All the metals were ground or swaged to desired sizes between 1- and 7-mm diam, and centerless ground round and smooth to a finish better than 50 µ in., rms. Each rod was thoroughly cleaned with steel wool, degreased, acid etched, and dried. In a typical run, the rod was vertically clamped in a modified floating-zone electron-bombardment furnace designed after Calverley23 and Carlson.24 The specimen was outgassed and maintained positive at several kilovolts in a dynamic vacuum of 10-5 to 10-7 mm. The bottom end was enclosed by a tantalum pillbox and heated by electrons emitted from a hot concentric tungsten filament mounted on a movable bracket. The bombardment power was slowly raised until melting was observed. Power requirements ranged from 30 w for copper to 1300 w for 4-mm tungsten. The stabilized and out-gassed drop of near-maximum size was photographed at 4. 1X on panchromatic film at desired time inter-

Jan 1, 1963

By Kenneth A. Moon

An exact statistical treatment of a one-dimensional model is used as a basis for evoluating the reliability of certain simplified expressions for the activity of the solute in interstitial solutions, including one obtained from the exact expression by setting the repulsive interaction equal to infinity. The latter approximation is found to be satisfactory at low and moderate concentration if the repulsive interaction is large, even though not infinite. A similar expression (identical if the co-odination number is two) is derived from the quasichemical expression of Lacher, and is recommended as the best available expression for the excess configurational entropy of interstitial solutions with excluded sites. Some reasonable models are discussed, and the nature of the saturated solutions is determined by inspection. Some of the models reduce to the one -dimensional case. An analysis is given of the excess partial entropy of hydrogen in V-H; Nb-H; and To-H solutions. MOST treatments of the statistical thermodynamics of interstitial solid solutions have followed the classic paper1 of Lacher in making the simplifying assumption that the configurational entropy of the solution is ideal. However, it is becoming increasingly apparent that there are many interstitial solutions with very large so lute-solute repulsions, and for these the assumption of ideal entropy is not valid or useful. It is important to realize that with substitutional solutions large repulsions between the component atoms must lead to phase separation, whereas in interstitial solutions the free energy of the solution is not drastically increased by large solute-solute repulsions until intrinsic saturation is reached at the concentration where further solute would be forced to enter a site in which it would experience the repulsive effect of one or more solute atoms already present. In the limiting case of an infinitely large repulsive interaction, the excess free energy would be attributable entirely to excess entropy, the enthalpy of mixing being zero. AS will be shown below, even if the repulsions are less than infinite, a treatment based on an assumption of infinite repulsions may be very satisfactory up to moderately high concentrations of the interstitial component. Often in solutions where large repulsive interactions exist, there are also small interactions — often attractive—between solute atoms in configurations other than that corresponding to the large repulsion. In such cases the excess free energy will consist of an excess entropy term attributable to the large repulsive interactions, and an enthalpy term corresponding to the other small interactions. Nomenclature to differentiate succinctly between important cases would be a convenience. In this paper the nomenclature shown in Table I will be used. In Table I, and in the preceeding discussion, excess quantities are defined in terms of standard states which are pure solid solvent and pure (possibly hypothetical) solid saturated phase of the structure in question. In practice, it is more convenient to choose the interstitial element as a component, and its conventional standard state. This will add a composition-independent term to the excess entropy and the enthalpy. The earliest paper known to the present author which treats the thermodynamics of athermal interstitial solutions was given by schei12 in 1951, but the statistical derivations in that paper are open to criticism. Speiser and Spretnak were the first to give a correct statistical treatment,3 limited, however, to concentrations sufficiently low that the number of empty sites excluded from occupancy by more than one filled site is negligible. The purpose of the present paper is to extend the statistical treatment to more concentrated solutions, and to examine the magnitude of the errors introduced by assuming that the repulsive interactions are infinite when in fact they must be finite. THE QUASICHEMICAL APPROXIMATION Fortunately, a standard method already exists for taking into account the effect of large interactions upon the entropy of mixing. This is the quasi-chemical method, in which the probability of existence of a given pair of solute atoms in a certain proximate configuration is assumed to be proportional to exp(-w/kT), where w is the energy increase of the solution when the two atoms are moved from isolated locations in the solution to the configuration in question. A quasichemical treatment of interstitial solutions was given in 1937 in a widely neglected paper by Lacher.4 The result comes out

Jan 1, 1963

By F. A. Schaufelberger

Early work on chemical precipitation of metals from metal salt solutions is reviewed. The chemistry and thermodynamics of precipitating copper, nickel, cobalt, and cadmium metals by reaction with hydrogen are discussed. Mechanisms of metal precipitation, nu-cleation, growth, and agglomeration are reviewed, as well as some solubility phenomena of cleation,gases and solids at elevated temperatures. Experimental data presented deal mainly with the reaction of copper sulfate solution with Hz. METAL can be recovered from a leach solution either indirectly by precipitation as a compound that is later reduced or directly by electrolysis, cementation, or chemical reduction, for example, with hydrogen. The widely used electrowinning processes suffer from the inefficiency of converting fuel to low voltage dc and from low current efficiency when complete recovery is attempted. With the batch hydrogen reduction methods outlined here, a unit of fuel converted to hydrogen in modern gas reform plants will make two to three times as much metal as can be obtained with electrolysis. With continuous hydrogen reduction, four to six times as much metal is obtained. Precipitation by reducing a metal salt solution with H, has been known for almost 100 years.' Commercial use of the process, however, awaited the research and development program initiated by Chemical Construction Corp. Within the last few years this program has brought about construction of commercial plants, listed on p. 701. Ideal hydrogen reduction will precipitate a pure metal from a solution obtained by commercial leaching methods at a rapid rate without excessive temperatures and pressures. The metal precipitate will be of desired size and density, less than a percent left in the vessel being deposited on the wetted parts. The present discussion will outline Chemical Construction Corp.'s early development program and will discuss the chemistry and mechanics of reducing copper, nickel, cobalt, and cadmium from solution by H2. Work on selective reduction of nickel from cobalt has been described earlier.2 The article is not concerned with precipitation of copper by disproportionation of cuprous solutions where yield is limited" to 50 pet.* It does not discuss use of gaseous reducing agents other than hydrogen, such as SCV which may lead to contamination with sulfur, or CO," which is considerably more expensive than hydrogen and produces a gaseous reaction product, CO2.† The article does not include use of other nongaseous reducing agents: which are far more expensive than CO. Also, notes on the history, engineering design, and performance of commercial plants have been given elsewhere." It will be shown that a pure metal can be precipitated by reduction with hydrogen from solutions obtained by commercial leaching methods when the solution cohposition is controlled and proper acidity, proper metal ion concentration through controlled complex formation and hydrolysis, and adequate agitation for suspension of metal and for transfer of reducing gas are maintained. Reasonable temperatures and pressures are used which are less excessive than those used by previous workers, although they are maintained at above equilibrium values because of process kinetics.' It has also been found necessary to induce nuclea-tion and to control growth and agglomeration in order to get a powder product of suitable physical properties. Review of the Literature Muller, Schlecht, and Schubardt of I. G. Farbenm claimed a successive reduction of silver, copper, nickel, cobalt, and zinc from ammoniacal solution by applying progressively higher temperatures and hydrogen pressures. Metals produced by this technique were not pure, since no attempt was made to adjust the solution composition between the different reductions. It is doubtful that the zinc product contained any metallic zinc. The major contribution to the literature" was made by the Ipatiews,12 who prepared platinum, iridium, copper, nickel, cobalt, lead, tin, arsenic. antimony, and bismuth at often extreme conditions, up to the critical temperature of water (373"C), at 1500 to 7500 psi, for as long as several days. Even cadmium and zinc were claimed to have been observed in trace quantities precipitated together with basic salts. In the early experiments solutions were not stirred. Extensive formation of oxides and basic salts occurred. probably long before sufficient hydrogen could be supplied in the unstirred liquid to decrease the metal concentration in solution by reduction. The importance of hydrogen pressure was

Jan 1, 1957

By B. C. H. Steele, C. B. Alcock

In choosing solid oxide electrolytes for use in the measurement of thermodynamic quantities at high temperatures, the two most important criteria are the values of the partial ionic and electronic conduc tizities. Measurements of these conducticities have been made for some Group IVA oxides and solid solutions of these oxides with CaO, Y2O3, and La2O3. The total conductivities as a function of temperature. oxygen partial pressure, and composition were determined, as well as the electromotive forces of cells in which the oxygen partial Pressures of the electrodes were between 10-7 and 10-29 atm at 1000°C. Additional factors that influence the experimental arrangements, such as the operating temperature, the appropviate cell atmosphere, and electrode kinetics, are also discussed. IT has long been recognized that galvanic cells incorporating solid electrolytes can possess many advantages for the measurement of high-temperature thermodynamic data. Unfortunately, the electrical-transport properties have only been established for a few solid electrolytes, although attempts have been made, and are still being made, to use such materials as porcelain' and magnesia.' Kuikkola and Wagner have discussed3 and demonstrated4 various applications of solid electrolytes, and, in particular, their work stimulated the electrochemical measurement of oxygen activities using cells incorporating the solid oxide electrolyte, Zr0.85Ca0.15O1.85 The excellent characteristics of this oxide electrolyte have been confirmed by the investigations of Kingery et al.5 (oxygen ion diffusion), Carter and Rhodes6 (zirconium and calcium ion diffusion), and Weissbart and Ruka7 (electronic transference number). However the observations of Peters and Mobius,8 later confirmed by Schmalzried,9 indicated that the electronic component of zirconia-based electrolytes could become significant at low oxygen chemical potentials. Under these conditions, thoria-based electrolytes have obvious advantages arising from their superior thermodynamic stability. It was known that certain thoria solid solutions possessed defect fluorite structures containing anionic vacancies (cf. Zro.85Cao.l50O1. 85), although data on their electrical properties were conflicting. Kiukkola and wagner4 concluded that thoria-based electrolytes exhibited appreciable electronic conductivity, whereas Peters and Mobius8 mentioned that the electronic conductivity only became important at high oxygen partial pressures, but gave no further details. In addition, both Kiukkola and wagner4 and Peters and Mann'" had determined the oxygen chemical potentials associated with the Fe-FeO, Co-COO, Ni-NiO, and Cu-Cu2O equilibria, and it was not known whether discrepancies in their results could be attributed to the different cell design, or the thoria-based electrolyte used by Peters and Mann. These uncertainties have been resolved during the present investigation into the measurement of low oxygen chemical potentials, and transport properties of the relevant oxide electrolytes are presented and discussed. Other experimental difficulties associated with low oxygen chemical potential measurements are also described, with particular reference to the Nb-O system. 1. THEORETICAL CONSIDERATIONS Oxide systems of potential use as solid electrolytes possess a large energy gap between the valence and conduction bands. Little is known about the defects present in these wide-gap metal oxides as a function of impurity content and deviations from stoichiom-etry, or the mechanisms by which electronic charges move in these solids. For these materials it is convenient to represent the measured conductivity as the the sum of three terms: where a, is the conductivity due to positive hole conduction (p type), and oe is the electronic conductivity due to electron conduction (n type). U there is a large concentration of ionic vacancies fixed by composition then the ionic contribution will not be a function of oxygen pressure. Although the possibility of a pressure-independent electronic component also cannot be ignored, it is likely that such a term would only become significant at very high temperatures, and in general the positive hole conduction will increase with increasing oxygen pressure, and the electron conduction will increase with decreasing oxygen pressure. It follows that the total conductivity is related to oxygen partial pressure as follows:

Jan 1, 1965

By W. F. Domis, F. von Gemmingen, R. W. Whitmore, F. Garofalo

Constant-load creep-rupture tests at 1100°, 1300° and 1500°F were made on a Type-316, 18 Cr-8 Ni-ZMo, austenitic stainless steel to determine the relationship between ruptzire life and other aspects of creep behavior, The test program was designed on a statistical basis to check the variability of various creep properties and to determine emprically the dependence of minimutn creep rate and ruptzire life on initial stress, The dependence of the rupture life, tn, on the initial stress, a,, is found to be related to the stress dependence of the wrinimum creep rate, i,, and secondary creep strain, The instabilities or breaks found in the conventionual log - logt, plots can be traced to either a change in the linear dependence of log i, on log a, or to a change in secondary creep strain. In the alloy tested, rupture is found to be predowmanantly of the inter crystalline type, For this material, the secondary creep strain is -found to depend on the nature of the grain boundary precipitate, which affects grain boundary migration. It has been shown for a variety of metals and al tested at elevated temperatures under creep conditions that the empirical relationship exists between rupture life, tr, and minimum creep rate, i,. This relationship, in which C and a are in some cases independent of stress or temperature, shows in a general way that creep rupture depends on creep behavior prior to tertiary creep stage. To determine more fully the factors which control creep rupture requires, therefore, more knowledge of the relationship between rupture and creep behavior. To obtain such information, constant-load creep-rupture tests have been made on a Type-316, 18 Cr-8 Ni-2 Mo, austenitic stainless steel at 11000, 1300°, and 1500°F. These tests were designed on a statistical basis to determine the variability of the various creep properties measured and to determine empirically the stress dependence of minimum creep rate and rupture life. As a result of this work, various empirical relations have been established defining more closely the factor, C, in the relation between rupture life and minimum creep rate. This factor is found to be proportional to the amount of strain during secondary creep. The variation of secondary creep strain with rupture life and temperature is determined and its effect on rupture behavior discussed. The variability in minimum creep rate and rupture life is also dis- cussed and the dependence of these quantities on initial stress is interpreted. TEST MATERIAL AND TEST PROCEDURES The material tested is an austenitic stainless steel, AISI Type 316, of the following composition: C, 0.07 pct; Mn, 1.94 pct; P, 0.01 pct; S, 0.021 pct; Si, 0.38 pct; Cr, 18 pct; Ni, 11.4 pct; Mo, 2.15 pct; All 0.003 pct and N, 0.043 pct. The material was received as a hot-rolled 0.5-in. diam bar which was sectioned into 3.25 in. long blanks. Each blank was heat treated by holding 1/2 hr at 2000° F followed by water quenching. A 3/8-in. coupon was removed from each heat-treated blank and the microstructure was examined, the grain size determined, and the hardness measured. The microstructure was found to be uniform from blank to blank and the grain size was found to range from 4 to 6 ASTM numbers. Hardness, measured using a 20-kg load, varied between 127 and 148 Vpn. Tensile creep-rupture specimens having a 0.25 in. diam within a 1.5-in. reduced section were machined from the heat-treated blanks. Constant-load tests were made on these specimens at 1100°, 1300°, and 1500 F. Six specimens were tested at each stress level. Three creep-rupture machines were employed for tests at each temperature, two specimens being tested in each machine for each stress level. To minimize any effect due to local inhomogeneities along the length of the as-received bar the specimens were randomized before test. Each specimen was tested to rupture and in most cases an autographic extension-time curve was obtained. For very low stress levels at 1500°F no auto-

Jan 1, 1962

By N. S. Stoloff, M. Gensamer

The effects of temperature, grain size, and magnesium content on the strength and ductility of cadmium were studied in the range -269° to 23 °C. A sharp drop in ductility between -140° and -190°C marked a transition in fracture mode from ductile shear to inter gvanular fracture. The addition of up to 15.35 wt pct Mg in solid solution raised the transition temperature, and for two compositions produced basal cleavages. The relatively high ductility of unalloyed cadmium at cryogenic temperatures is attributed to temperature independence of the yield stress and the absence of dislocation locking. ALTHOUGH numerous studies have been made of the mechanical properties of cadmium single crystals,1-5 no comprehensive investigation of deformation and fracture in polycrystalline cadmium has been carried out. This investigation was initiated to determine the mechanisms of deformation and fracture in polycrystalline cadmium, and to attempt to correlate these mechanisms with the behavior of other metals of hexagonal close-packed structure. A second objective of this work was to determine whether the slip systems and mode of fracture of polycrystalline cadmium could be altered by reduction of the axial ratio, which is 1.886, through alloying. Dorn and co-workers' have been able to induce prismatic slip in magnesium through alloying to reduce the axial ratio. Single crystals of cadmium are so highly ductile that glide strains of 400 pct are observed at room temperature, and 80 pct at -269°c.l Failure in every reported case is by necking down and shearing off of the crystal. Cleavage in cadmium single crystals has never been observed. Magnusson and aldwin reported a ductile to brittle transition for polycrystalline cadmium at about —160 C for specimens tested at a strain rate of 0.05 in. per in. per min in tension. However, even at -196° substantial ductility was retained. The transition temperature was strain rate dependent, impact loading at 19,000 in. per in. per min raising the transition temperature to about -85°C while leaving the low temperature ductility unchanged. No information was given on microstructures or fracture mode, nor were stress-strain characteristics reported. In the present investigation, tensile tests were carried out on polycrystalline cadmium and solid solution Cd-Mg alloys to determine flow stresses, work-hardening behavior, fracture strength, and fracture ductility. Variables employed included temperature, alloy content (and c/a ratio), and grain size.Some compression data also have been obtained for comparison purposes. I) EXPERIMENTAL PROCEDURES A) Polycrystalline Cadmium. Two purities of cadmium were employed in this investigation. Cadmium of 99.95 pct purity was supplied by Belmont Smelting and Refining Co. Cadmium of 99.99+ pct purity was supplied by American Smelting and Refining Co. Threaded cylindrical tensile specimens were machined to give approximately a 1/2 in. long straight gage section with a reduced diameter of about 0.110 in. Specimens were heat treated in evacuated pyrex capsules in the range 140" to 290°C to produce desired grain sizes. All specimens were polished in a solution containing 320 g Cr03 and 20 g NaS04 in 1000 cc of H20. Occasionally this solution caused staining of the specimen, in which case a further polish with a solution of one part HN03 and two parts H202 in two parts ethyl alcohol was employed.' Tensile testing was carried out on a screw-driven Instron machine, at a constant rate of crosshead movement, which for most tests was 0.01 in. per in. per min. Load vs time, and therefore load vs total strain, were recorded. Temperatures from -196" to -40°C were obtained by passing nitrogen gas through a copper coil immersed in liquid nitrogen, and then feeding the gas into a jacket around the specimen. Tests at -269°C were carried out in a helium cryostat, at a crosshead rate of 0.1 in. per in. per min, with specimens of 1 in. gage length. Compression specimens were tested in a jig similar to one designed by ilman. The jig was mounted on the under side of the Instron crosshead. Load was transmitted by means of a rod connected to a movable part of the jig at one end, and the load cell at the other end. A downward movement of the crosshead applied a compressive load to the specimen.

Jan 1, 1963

By Peter Greenfield, Paul A. Beck

Thirty binary systems of vanadium and chromium group transition elements with second and third long period transition elements were explored in regard to the intermediate phases formed. It was found that the phases predominating in these systems are s, AB type with ordered a-tungsten or C8 structure, close-packed-hexagonal with small unit cell dimensions and, finally, phases isomorphous with 1-manganese. IN recent years, considerable information has become available concerning the intermediate phases in binary systems of the transition elements. Thus, the s phase has been found to occur in most of the binary systems of vanadium, chromium, and molybdenum with the group of elements manganese, iron, cobalt, and nickel.' It was observed that, while the rr phases formed by chromium with manganese, iron, or cobalt possess a considerable temperature range of stability, particularly in the Cr-Co system, the corresponding s phases with molybdenum are limited to a temperature range of less than 400" above about 1200°C. Goldschmidt' reported v phases of tungsten with iron and cobalt, and these are apparently stable only at (and above?) 1400°C." Exploratory work in this laboratory with Fe-W and Co-W alloys of approximately 60 atomic pct W annealed at 1300°C did not produce X-ray patterns suggesting the presence of a phase. It appears then that the phases of iron and cobalt with the chromium group elements decrease in stability as the two components are chosen from long periods further removed from each other. From the available information, it might be concluded that the controlling factor is the increasing difference in atomic radii between the components. In contrast to the a phase, the phases formed by iron and cobalt with chromium group elements' are stable only when the latter have large atomic radii (molybdenum and tungsten); the corresponding phases with chromium do not occur. When the difference in atomic size becomes still larger (r,/r,, approaching the ideal value of 1.225), the u and p phases are replaced by Laves phases (AB,), as in the alloys of iron and cobalt with columbium," tantalum." and titanium."-" However, atomic size certainly cannot be the sole determining factor, since, for instance, in contrast to the very stable (Mo, Co)p phase, no such phase occurs in the Mo-Ni system even though the atomic diameters of cobalt and nickel are nearly the same. Similarly, chromium and cobalt form a a phase in a wide temperature range," but the corresponding s phase in the Cr-Ni system is missing. It has been shown that the composition of the u phase in various binary and ternary systems of transition elements in the first long period may be correlated in a fairly quantitative manner with the number of electron vacancies. The influence of electronic structure is probably present also in binary and ternary phases' and to some extent, apparently, even in Laves phases." " Although the absence of phases in the Cr-Ni and Mo-Ni systems has not as yet been explained on the basis of electronic structure, it appears reasonable to suspect a connection. One of the great difficulties in arriving at well founded rules in regard to the alloying behavior of transition elements lies in the lack of reliable information concerning the details of their electronic structure in the metallic and alloy form. The theoretical penetration of this field appears to be beset by very considerable difficulties, even when the complications due to alloy formation are disregarded. Another great source of uncertainty is the scarcity of phase diagram information even for binary systems of the transition elements so that only a very limited basis is provided for generalizations as to the occurrence of intermediate phases. For instance, very few binary phase diagrams of second and third long period transition element systems have so far been published. The present work was undertaken in order to survey the various types of intermediate phases occurring in 30 binary systems of elements of the group vanadium, columbium, tantalum, chromium, molybdenum, and tungsten with the elements rhenium, ruthenium, rhodium, palladium, and platinum. For most of these binary systems phase diagrams are very incompletely or not at all known, as will be further reviewed.*

Jan 1, 1957

By J. E. Steiner, J. M. Hodge, M. A. Orehoski

Ingots of four steels (1045, 1080, Ni-Mo-V, and Ni-Cr-Mo-V) were cast at pressures varying from about 1 to 760 mm of mercury, so as to obtain a range of hydrogen contents in each steel. The susceptibility of these steels to flaking was evaluated by cooling hot-rolled blooms at a range of cooling rates, varying from water quenching to slag cooling, and studying the occurrence of flaking as a function of cooling rate. The steels exhibited differences in susceptibility to flaking, and a tlzreshold value for hydrogen content for each steel was found, below which the susceptibility was very low and above which the susceptibility increased markedly with increasing hydrogen content. Mechanical property evaluations, metallogvaplzic exantinations, and X-my diffraction determinations o,t retained austenite were made on samples from the blooms. A mechanism of flaking which is consistent with the observed behaviors, the effects of hvdrogen content, and the differences in susceptibility among the steels investigated is postulated, based on the results of mechanical property evaluations and metallographic and X-ray diffraction studies. ThE important role of hydrogen as a factor in the occurrence of "flakes" or "hair-line cracks" in steel has now been established by many investigations. These have included investigations by steel producers and forging manufacturers, to whom the prevention of flaking is a very real and serious problem, and many research studies aimed primarily at establishing the mechanism of this behavior Several investigators3 have reported that steels cast at reduced pressures (absolute pressures of about 1 mm) not only are low in hydrogen content but are essentially insensitive to the formation of flakes. These investigations have shown that a general relationship exists between hydrogen content and susceptibility to flaking. The difficulty of obtaining suitable samples of steels of a given composition with the desired range of hydrogen contents, particularly in the relatively large sections in which flaking most commonly occurs, has been the principal obstacle to quantitative evaluations of these relationships. Steels with intermediate hydrogen contents between 1 ppm, and the 4ppm or higher of air-cast steels are generally not available in commercially produced steels. Laboratory procedures, in which the hydrogen is introduced into solid steel samples by heating in a hydrogen atmosphere under pressure, generally involve a limitation in the size of the sample which can be treated, and thus are not representative of the behaviors in large sections. The availability of a facility at the South Chicago Works of U.S. Steel, in which several ingots could be cast from a single heat of steel at total air pressures ranging from 0.25 to 760 mm of Hg, has made it possible to overcome this obstacle and to obtain ingots of a given steel covering the intermediate range of hydrogen contents desired. These ingots, furthermore, are of a size suitable for the production of product with section sizes large enough to be representative of the products in which flaking most commonly occurs in commercial production. In these experiments, this facility was used to study the relationships between hydrogen content and the susceptibility to flaking of four steels, two plain carbon steels at 0.45 and 0.80 pct C and two low-carbon alloy steels representing a medium and a rather high hardenability level. These flaking studies were supplemented by evaluations of mechanical properties and by metallographic studies on samples from the blooms, in order to obtain pertinent information on the factors other than hydrogen content which influence the susceptibilities of these steels to flaking. Based on the results of these tests, a mechanism for the initiation and propagation of the flaking cracks, which is consistent with the observed behaviors, is postulated. MATERIALS AND EXPERIMENTAL WORK Steelmaking and Conversion. To provide material for the investigation, five 29- by 35-in., hot-topped, big-end-up ingots were cast from each of four 80-ton, basic electric-furnace heats of four different steels (a 1045 steel, a 1080 steel, a Ni-Mo-V steel, and a Ni-Cr-Mo-V steel). A double-slag practice was used on all steels and the two plain carbon steels were Si-A1 deoxidized with an addition of 2 lb of A1 per ton, while the Ni-Mo-V and Ni-Cr-Mo-V steels were deoxidized only with silicon and

Jan 1, 1964

By J. L. Lytton

The flow-stress recovery of high-purity aluminurn following a 10 pct tensile prestrain was studied in terms of a fractional flow-stress recovery parameter fr. The flow-stress recovery behavior was related to the dislocation arrangements using transmissiort electron rnicvoscopy. During recovery at 120° and 160°C, nearly stable strength levels were attained, the strength level for 120°C recovery being greater than that for 160°C. This stabilization of flow stress was related to the formation of meta-stable dislocation networks bounding nearly perfect cells. Both network formation and the annealing of dislocation loops were found to be recovery mechanisms, and the stronger metastable strength level joy 120°C recovery was related to a smaller average cell size. Analysis of the networks was consistent with the reaction of sets of dislocations with a/2 (110) Burgers vector to give product Burgers DURING isothermal annealing of cold-worked metals, a degree of softening occurs without re-crystallization, and the processes responsible for this change are termed recovery processes. During recovery annealing, the dislocations generated during cold work become rearranged into low-energy configurations, and as much as 50 pct of the stored energy is released."' The relationship between this rearrangement of dislocations and mechanical behavior is of considerable importance, since the dislocation substructures formed during recovery provide a significant degree of low-temperature strength3j4 and can favorably alter the course of primary creep at high temperatures.4 The purpose of the present study was to relate the flow-stress recovery behavior of high-purity aluminum to the substructural modifications that occur. Electron transmission microscopy was therefore employed for direct observation of dislocation substructures at various stages of recovery following 10 pct prestrain. Several investigators5-' have proposed that dislocations can become rearranged or lost during the preparation of thin foils. It was found early in the present study that the dislocation structures in the thicker regions of the foils changed in a systematic way during the course of recovery. Therefore, it is unlikely that substantial losses or rearrangements occurred during thinning. This point will be discussed in more detail later. The results of various investigators indicate that recovery processes in fcc metals can result in release of 50 pct or more of the total energy stored in the as-prestrained metal, this percentage decreasing with increasing prestrain.' Alloying elements or impurities tend to increase this percentage. The release of stored energy of fcc metals during recovery appears to occur by 1) annealing of point defects if the deformation occurred at sufficiently low temperaturesg and 2) rearrangement of dislocations into low-energy Configurations.1,2In bcc metals, the annealing of dislocation loops has also been observed during recovery after prestrain,10-12 and it has been proposed that this is a recovery mechanism for unidirectionally strained fcc metals.' The density of dislocations in bcc metals has not been observed to decrease appreciably during recovery,10 although the formation of regular dislocation networks has been observed. has shown that the formation of such networks can result in elimination of long-range stresses and can lead to significant release of stored energy without dislocation annihilation. It might thus be expected that network formation is a significant recovery mechanism in fcc metals, although extensive network formation has apparently not been reported in controlled recovery experiments. The formation of sub-boundaries in aluminum has been observed by various investigators13'17 during recovery studies of aluminum, but the structure of these boundaries was not resolved. In this regard, it is significant to note that Bailey and Hirsch,' using transmission electron microscopy, detected no network or sub-boundary formation during recovery of 99.99 pct Ag. Furthermore, Clarebrough et al.2 found no such rearrangements during recovery of copper. EXPERIMENTAL PROCEDURE The high-purity aluminum used in this investigation was obtained in the form of 0.125-in.-thick sheet. Spectrographic analysis revealed that the sheet was 99.995 pct A1 with the following weight-percent impurities: 0.001 Cu, 0.002 Fe, 0.001 Si, and 0.0004 Mg. The as-received sheet was in the heavily cold-rolled condition. The as-received sheet was cold-rolled at room temperature to 0.040-in.-thick sheet in the longitudinal direction, which was the original rolling

Jan 1, 1965

By Robert M. Weidenhammer

For years before the war, Coal had the reputation of being a sick industry. Currently it is operating at peak production and succeeding pretty well in keeping out of the red. But, says Mr. Weidenhammer, it will have a relapse as soon as the war ends unless (1) working capital can be built up; (2) it gets the support of the people and Congress; and (3) a truly long-range national fuel policy is formulated.

Jan 1, 1943

By E. Ray Webb

A interest to geologists and to mining and petroleum engineers is a laboratory method for determining the dip and strike of sub- surface structures, as well as the direction of fault planes traversing them. The information is derived by making use of the magnetic properties of borehole cores which must show visible representations of bedding or fault planes. Complete knowledge of these factors aids greatly in the successful exploitation of both ore and petroleum deposits.

Jan 1, 1940