By S. J. Matas, R. F. Hehemann

The existence of two distinct forms of bainite—upper and lower bainite—in hypoeutectoid steels is confirmed by a systematic study of the structure of the product resulting from this mode of austenite decomposition. The transition between these two forms occurs at about 650° F regardless of the alloy content of the steel and their structural differences can be interpreted in terms of the kinetics of carbide precipitation from supersaturated ferrite. In the past few years, a renewed interest has been displayed in the kinetics and mechanism of the bainite reaction in steels. Several rather divergent models for the transformation mechanism have evolved from these studies,'-' however, it is difficult to evaluate these models critically on the basis of the existing experimental data. In particular, a more detailed knowledge of the structure of bainite should be helpful in providing a framework for the construction of an appropriate model. Metallographic studies7-l4 have led to a recognition of at least two distinct forms of bainite—frequently termed upper and lower bainite. Although the morphology of bainite changes with reaction tem- perature, there appears to be a relatively sharp transition between the two forms. This occurs in a narrow temperature range near 650° F. Transformation at temperatures below about 650° F results in the presence within the bainite of small plates of carbides oriented at an angle of 60 deg with respect to the direction of growth of the plate, while at higher temperatures carbides are oriented parallel to the growth direction. There is no generally accepted view regarding the significance of this structural transition. Some authors feel that carbides precipitate from austenite at all reaction temperatures1' while others claim, at least for low-temperature bainite, that carbides precipitate from supersaturated ferrite.14.15 It was recognized many years ago that the nature of the carbide in bainite depends on the reaction temperature. The carbide hase in upper bainite is unmistakenly cementite.16-19 The exact nature of the carbide in low-temperature bainite is less certain. Magnetic measurements of lower bainite reveal no cementite Curie point21'22 and dilatometric studiesz0 produce total expansions which are larger than those predicted on the basis of a ferrite-plus cementite structure. These effects have been attributed to the

Jan 1, 1962

By L. L. Swift

.It the present time there are four base metals being used for automo-tive bearing alloys. Of course there are numerous variations in the amounts of alloying elements added to each base metal and nearly all of these alloys have the conventional, if not classical, duplex structure; that is, they are composed of a hard constituent embedded in a soft matrix. The well-known theory is that the former will wear well, while the latter will be plastic enough to allow the bearing to be broken in and conform to the contours of the shaft. The requirements of the modern bearing have been most aptly described by W. M. Corse: In order to meet the engineering demands of today a good bearing metal must be able to carry the weight of the shaft and stand up under steady or suddenly applied loads, or even blows ill sorne types of service. A certain amount of plasticity is desired to compensate for minute irregularities in the shaft or bearing surface, and to permit yielding, thereby avoiding dangerous stresses in bearing and shaft and pre-venting overheating and rapid wear of parts. Less plasticity is required in a bearing tuetal if the surfaces of bearings and journals are machined accurately, aligned, and kept in alignment. It is desirable, of course, that a bearing metal have a low coeffi-cicnt of friction. Under most operating conditions the friction depends on the unit, pressure of the bcaring, the speed, the temperature, and the properties of the lubricant. A good bearing metal must have a low rate of wear to reduce the necessity for frequent replacements, and adjustment of the bearings. It must wear more rapidly, however, than the journal or shaft running on it, because replacement of the journal or shaft is more difficult and costly than replacement of the bearing.' The hardness of the bearing alloy is a property closely related to several of the foregoing. With a duplex microstructure, the measurement of hardness with any of the usual commercial devices means little. The Bierbaum method of measuring the hardness of the individual canstituents was developed to fill this need. MICROCHARACTER The Bierbaum MicroCharacter~,~ measures the scratch-hardness of a solid by pulling a weighted diamond point over the surface. The diamond point is ground so that it is the corner of a cube, and Mounted

Jan 1, 1939

By R. E. Reed, C. J. McHargue

Single crystals of aluminurn were reduced 90 pct in diameter by extrusion at 296" and 77°K. The resultant double fiber texture had a strong (111) component with a weak (001) component. The relative anzounts of these components varied with starting orientation. Decreasing the Lemperatuve of defovtnation increased the amount of (001) texture component in crystals with inilia1 orientations near (111). The starting orientation and temperature of deformation strongly affected the morphology of the (001) component. The effects of orientation and Lemperatuve upon the distribution of the (001 ) texture component in extruded aluminum single crystals were rationalized on the basis of deformation band formation and interaction. MANY papers since the early 1920s have discussed the occurrence of the double fiber texture (111) + (001) in wires and rods of deformed fcc metals. Aside from the reporting of experimental results for the various metals under a variety of fabrication conditions, emphasis has been placed on two related problems. One problem deals with the prediction of ideal end orientations based on the glide systems and flow directions. The other problem seeks the reason why different amounts of each component may be produced by the same fabrication schedule for metals apparently having the same deformation systems. Some of the difficulties in developing a satisfactory explanation have their origin in the experiments themselves. One mistake has often been the assumption of an initially randomly oriented specimen or complete ignorance of effects of starting orientation. Recent studies by Grewen and Wassermann,1 Cullity and co-workers,2' and McHargue4 have shown that the initial orientation may be the most important factor in determining the final orientation. Hence only limited comparisons of data from different studies can be made unless all conditions of the initial material are specified. Another question has been the nature of the (001) component. Hibbards suggested that any (001) present was the result of re crystallization during fabrication. Although Fleischer6 found no (001) texture in aluminum swaged at room temperature, and Dayal 7 found that component to disappear at very high reductions, a double fiber texture has usually been reported for aluminum. Vandermeer and McHargue showed that, while some (001) in aluminum may be the result of recrystallization, much of this component has its origin in the deformation process. Ahlborn and Wassermanng found the (001) component in silver deformed at low temperature not to be the product of recrystallization.

Jan 1, 1968

By R. F. Mehl, J. K. Stanley

THE recrystallization of cold-worked metals is studied ordinarily by determining the temperatures required for complete recrystallization to occur within a given arbitrary time period, usually within 15 min. to 2 hr. The results obtained are conventionally assembled in a three-dimensional diagram relating this temperature to the amount of cold-work (percentage deformation) and the resultant grain size, though sometimes other modes of representation are employed.1 Such three-dimensional diagrams are not complete, for the number of variables exceeds the number represented. The process of recrystallization is characterized by a time-rate, a fact that is not portrayed upon ordinary recrystallization diagrams. It is known that recrystallization consists in the formation of new nuclei and the growth of these nuclei, a process that continues until the matrix is completely consumed and the original set of grains entirely replaced by the new. This knowledge is old.2 Truly heterogeneous reactions invariably proceed by nucleation and growth; the decomposition of eutectoid solid solutions provides an example about which much is known,3 and freezing, originally studied by Tammann, provides the classic example. Although recrystallization is not a heterogeneous reaction .within the orthodox meaning of the term, the mechanism of the process is the same. As in eutectoid inversion and freezing, it should be possible to study the rate of isothermal recrystallization as a function of time, and it should also be possible to analyze the isothermal reaction curve into the component rates of nucleation and growth that determine them.* Other methods, not employing the rates of nucleation and growth, have been used to represent the rates of such reactions, but these in general have been artificial and have not led to progress.4,5? The theory of recrystallization is not in advanced state; if recrystallization data were obtained, in terms of the rate of isothermal recrystallization, and in terms of the rate of nucleation and the rate of growth of recrystallized grains, and in particular if the temperature coefficients of these rates were measured accurately, an adequate theory should be more readily developed.27 Such an effort requires proper experimental technique, but especially requires suitable methods of mathematical analysis to convert measurements made upon a surface of polish into values for the rate of nucleation and the rate of growth and to combine these into a rate of isothermal recrystallization. These methods are now

Jan 1, 1942

By D. Walton, B. Chalmers

A preferred orientation is known to occur frequently in the columnar zone of castings. This has been attributed to a preferred direction of growth. However, no satisfactory mechanism was proposed by which the preferred direction of growth led to the preferred orientation. The purpose of this work has been to establish this mechanism. It has been found that in general the observed preferred orientations only develop when the preferred directions of growth reveal themselves by dendritic growth. A mechanism based on this premise is found to be in agreement with the experimental data obtained in the course of this work. WHEN a liquid metal is allowed to solidify in a mold, it usually freezes in three stages, distinguished from each other by the size and shape of the grains. The first zone to freeze (the chill zone near the mold wall) consists of relatively fine grains that are equiaxed in shape and random in orientation. The next zone consists of crystals that are elongated in the direction of heat flow, i.e., normal to mold wall. These crystals are much larger in cross section than the crystals of the chill zone and have a very strongly preferred orientation. This is the columnar zone. The final zone, which is absent in very pure metals, is again equiaxed and randomly oriented, but usually has a much coarser grain size than the chill zone. The purpose of this study is to describe and account for the crystal size and orientation in the columnar zone. The occurrence of a preferred orientation in the columnar zone is well known, and in 1940, Greninger' suggested that it is apparently related to dendritic growth although at that time the only data were for metals with the face-centered-cubic structure. Table I shows that the direction of dendritic growth and the crystal axis that follows the heat flow direction coincide in all cases so far studied. The term "dendritic growth" is used here to represent the branched type of morphology that is characteristic of growth into supercooled melts.' In addition to the supercooling which is necessary before nucleation will occur at the mold wall, the necessary supercooling for continued dendritic growth can be provided in a mold by heat flow into the already formed solid at an interface whose Liquidus temperature is depressed by an accumula-

Jan 1, 1960

By L. L. Swift

AT the present time there are four base metals being used for automotive bearing alloys. Of course there are numerous variations in the amounts of alloying elements added to each base metal and nearly all of these alloys have the conventional, if not classical, duplex structure; that is, they are composed of a hard constituent embedded in a soft matrix. The well-known theory is that the former will wear well, while the latter will be plastic enough to allow the bearing to be broken in and conform to the contours of the shaft. The requirements of the modern bearing have been most aptly described by W. M. Corse: In order to meet the engineering demands of today a good bearing metal must be able to carry the weight of the shaft and stand up under steady or suddenly applied loads, or even blows in some types of service. A certain amount of plasticity is desired to compensate for minute irregularities in the shaft or bearing surface, and to permit yielding, thereby avoiding dangerous stresses in bearing and shaft and preventing overheating and rapid wear of parts. Less plasticity is required in a bearing metal if the surfaces of bearings and journals are machined accurately, aligned, and kept in alignment. It is desirable, of course, that a bearing metal have a low coefficient of friction. Under most operating conditions the friction depends on the unit pressure of the bearing, the speed, the temperature, and the properties of the lubricant. A good bearing metal must have a low rate of wear to reduce the necessity for frequent replacements, and adjustment of the bearings. It must wear more rapidly, however, than the journal or shaft running on it, because replacement of the journal or shaft is more difficult and costly than replacement of the hearing., The hardness of, the bearing alloy is a property closely related to several of the foregoing. With a duplex microstructure, the measurement of hardness with any of the usual commercial devices means little. The Bierbaum method of measuring the hardness of the individual constituents was developed to, fill this need. MICROCHARACTER The Bierbaum microcharacter2.3 measures the scratch-hardness of a solid by pulling a weighted diamond point over the surface. The diamond point is ground. so that it is the corner of a cube, and mounted

Jan 1, 1938

By P. A. Fisher, J. B. Wilson, D. J. Whitehead, C. J. P. Ball, A. C. Jessup

The properties of a new magnesium alloy ZT1 containing 3.0 pct Th, 2.5 pct Zn, 0.7 pct Zr are described. The alloy possesses good creep and fatigue resistance up to 650°F, is free from microporosity, and is readily sand-cast. ZT1 is shown to be superior to zinc-free Mg-Th-Zr alloys. THE advent of the jet engine created a demand for a light sand-casting alloy capable of being cast into large complex shapes and capable of resisting creep at temperatures up to 500°F. This demand has been largely met by alloys of the magnesium-cerium mischmetal-zirconium types, containing about 3 pct Ce mischmetal and 0.7 pct Zr, typified by Elektron magnesium alloys MCZ and ZREI, the latter alloy also having a zinc addition of 2.5 pct. These alloys utilize the valuable properties at elevated temperatures conferred by the addition of rare earth metals to magnesium, a fact which has been known for many years and discussed by several investigators.1-1 Murphy and Payne8 showed that the addition of the powerful grain-refining element zirconium to Mg-Ce mischmetal alloys produced alloys with attractive room temperature properties combined with good creep properties and castability. With the increasing power of modern jet engines the temperatures to which some of the magnesium parts are subject are likely to exceed the safe working range of the cerium-mischmetal-containing alloys, and at the beginning of the research considerable interest had been shown by aeroplane engine designers in a magnesium sand-casting alloy suitable for service at higher temperatures, e.g., 600°F and above. At an early stage in the development of this type of alloy a check on the fatigue properties at elevated temperatures indicated that, since the fatigue limit even at 108 eversals was appreciably higher than any permissible creep stress, the main emphasis of the research could be concentrated on creep behavior. The primary aim in developing the new alloy has therefore been to attain maximum creep resistance; but due consideration has also been given to other important properties such as castability, tensile strength, and cost. It is by now well established that it is not possible to correlate creep strength with other short time mechanical properties such as are obtained in tensile

Jan 1, 1954

Alfred Stansfield, Montreal, Canada:—In Professor Howe's paper on the position of Ae3, he shows its industrial importance in determining the temperature to which steel should be heated for " grain refining." Several years ago I carried out a research on the " burning " of steel and found that while hypo-eutectoid steel should be heated to Ae3, hyper-eutectoid steel that has been very much overheated must be reheated to the curve Sa on the carbon-iron diagram, in order to redissolve the pro-eutectoid cementite and thus to obtain recrystallization and grain-refining. This treatment was necessarily only partly successful, and I should like to ask whether the conditions of heat treatment for refining overheated high-carbon steels have been ascertained. Speaking of the &'Persistence of Solidificational Segregation " Professor Howe quotes an experiment made by Mr. Stead in which a bar of 1.2 per cent. carbon steel was immersed in a large mass of molten blast-furnace slag and allowed to cool with it. The steel was heated ; above the solidus (curve An on the carbon-iron diagram), but below the liquidus (curve AB). A drop of eutectic carbon-iron alloy, rich in carbon, had liquated out and hung below the bar. This agrees exactly with my own observations on the burning of steel, but my interpretation differs somewhat from that of Professor Howe. Professor Howe considers that the fusion of a part of the metal (rich in carbon) shows that the solidificational irregularities of composition had persisted through the rolling and heat treatment of the steel, as otherwise no part of the steel would have been sufficiently fusible to melt. It does not appear to me that such an explanation is necessary. A piece of steel represented in temperature and composition by any point within the area ABa will ultimately resolve itself into a solid phase and a liquid phase in equilibrium with each other. It may appear that if the steel were absolutely uniform no fusion could take place, but, the smallest nucleus of high-carbon, fusible alloy would ultimately bring about this separation into liquid and solid phases, by diffusion of the carbon from the solid to the liquid areas. A nucleus sufficient for the purpose might be provided by an area of pro-eutectoid cementite which had not become diffused during the

Jan 1, 1914

By F. N. Rhines, A. H. Grobe

At elevated temperatures the oxide of silver is unstable in the air at atmospheric pressure, consequently no external oxide scale forms upon pure silver under conditions of high-temperature annealing. When small quantities of certain alloying elements are present in the silver, the formation of a thin external scale is possible1 and in addition there may form a subscale composed of the oxide of the solute element precipitated within the body of the silver. Norbury2 and Leroux and Raub3 have reported internal oxidation (subscaleiormation) in alloys of silver with 2, 7.5, and 30 per cent of copper. The presence of the subscale is believed to be responsible, at least in part, for the objectionable "fire mark" in Sterling silver.4 Several other alloys of silver, after oxidizing heat-treatments, are known to exhibit undesirable polishing characteristics that may be the result of internal oxidation. Except for the absence of an external scale of silver oxide, it is to be anticipated that silver alloys will prove to be very similar in their oxidation behavior to the alloys of copper, the oxidation characteristics of which have been studied in some detai1.5,6 The present research confirms this anticipation. The oxidation of a series of 20 dilute alloys of silver has been studied metallographically; some types of subscale not encountered among the copper alloys have been found. Instances of internal oxidation in alloys of most of the metals of the 1-6 and VIII groups of the periodic system are on record, but evidence of this type of oxidation in alloys of the metals of the intermediate groups is lacking. A number of the metals of the intermediate group, among them cadmium, lead, tin, and zinc, appear to provide the conditions essential to subscale formation; i.e., they form oxides with a relatively low negative free energy of formation, they dissolve other metals that form more stable oxides, and, presumably, oxygen will diffuse through them. In a study of 40 alloys of these white metals only a few cases of internal oxidation have been found. The probable reasons for this difference in behavior will be discussed presently. Experimental Procedure Silver.—The silver alloys employed in the oxidation studies were prepared in heats of 30 grams each from high-purity silver (99.993 per cent Ag)* and the purest avail-

Jan 1, 1942

By A. H. Grobe, F. N. Rhines

At elevated temperatures the oxide of silver is unstable in the air at atmospheric pressure, consequently no external oxide scale forms upon pure silver under conditions of high-temperature annealing. When small quantities of certain alloying elements are present in the silver, the formation of a thin external scale is possible1 and in addition there may form a subscale composed of the oxide of the solute element precipitated within the body of the silver. Norbury2 and Leroux and Raub3 have reported internal oxidation (subscaleiormation) in alloys of silver with 2, 7.5, and 30 per cent of copper. The presence of the subscale is believed to be responsible, at least in part, for the objectionable "fire mark" in Sterling silver.4 Several other alloys of silver, after oxidizing heat-treatments, are known to exhibit undesirable polishing characteristics that may be the result of internal oxidation. Except for the absence of an external scale of silver oxide, it is to be anticipated that silver alloys will prove to be very similar in their oxidation behavior to the alloys of copper, the oxidation characteristics of which have been studied in some detai1.5,6 The present research confirms this anticipation. The oxidation of a series of 20 dilute alloys of silver has been studied metallographically; some types of subscale not encountered among the copper alloys have been found. Instances of internal oxidation in alloys of most of the metals of the 1-6 and VIII groups of the periodic system are on record, but evidence of this type of oxidation in alloys of the metals of the intermediate groups is lacking. A number of the metals of the intermediate group, among them cadmium, lead, tin, and zinc, appear to provide the conditions essential to subscale formation; i.e., they form oxides with a relatively low negative free energy of formation, they dissolve other metals that form more stable oxides, and, presumably, oxygen will diffuse through them. In a study of 40 alloys of these white metals only a few cases of internal oxidation have been found. The probable reasons for this difference in behavior will be discussed presently. Experimental Procedure Silver.—The silver alloys employed in the oxidation studies were prepared in heats of 30 grams each from high-purity silver (99.993 per cent Ag)* and the purest avail-

Jan 1, 1942

By Francis Foley

Small cracks in a plane normal to the axis of steels are found to be prevalent around the water hole of drill steels that have been in service for an unknown period of time. Cracks are not found on the exterior surface of the steels nor to any noteworthy extent even in the water holes of new drill steels. Undulations and serrations are found in the surface of the water hole in new steels; it is in the bottom of such defects that cracks appear to develop in used steels. The occurrence of the more serious of these cracks at the point in the steel to which it has been heated for forging or hardening is thought to account to a great extent for failures in that region. DURING the past, year, we have investigated the cause of 88 per cent, of the failures by breakage near the bit end of some 1-in. hollow, hexagon, drill steel used in a metal mine. This breakage in the region of the bit end of the steel was peculiarly interesting because we have been led to believe that breakage is most prevalent at the shank end of drill steels near the place where the steel is gripped in the chuck of the machine. Records from the mine showed, also, that the breakage was much more frequent in the short lengths of large gage than in the longer steels; this is shown graphically in Fig. 1. Because the shorter lengths of steels are usually those that have been made from broken pieces of long steels or from steels that have worn down in service, rarely being made from new stock, those who are wont to suspect steel of tiring and crystallizing in its old age through fatigue are quite apt to see in this instance an argument in favor of their idea. As usual, a careful examination of these steels reveals defects of a character hardly to be overlooked in favor of such a cause. The steel in question was rolled with a sand core and was of the usual drill steel composition: Carbon 0.85 per cent., manganese 0.60 per cent., silicon 0.25 per cent., phosphorus 0.02 per cent., and sulfur 0.02 per cent., with the exception that in some specimens there was vanadium, not exceeding 0.20 per cent.

Jan 3, 1924

By A. H. Grobe, F. N. Rhines

AT elevated temperatures the oxide of silver is unstable in the air at atmospheric pressure, consequently no external oxide scale forms upon pure silver under conditions of high-temperature annealing. When small quantities of certain alloying elements are present in the silver, the formation of a thin external scale is possible' and in addition there may form a subscale composed of the oxide of the solute element precipitated within the body of the silver. Norbury2 and Leroux and Raub3 have reported internal oxidation (subscale forma¬tion) in alloys of silver with 2, 7.5, and 30 per cent of copper. The presence of the subscale is believed to be responsible, at least in part, for the objectionable "fire mark" in Sterling silver.4 Several other alloys of silver, after oxidizing heat-treatments, are known to exhibit undesirable polishing characteristics that may be the result of internal oxidation. Except for the absence of an external scale of silver oxide, it is to be anticipated that silver alloys will prove to be very similar in their oxidation behavior to the alloys of copper, the oxidation characteristics of which have been studied in some detail5,6 The present research confirms this anticipation. The oxidation of a series of 20 dilute alloys of silver has been studied metallographically; some types of subscale not encountered among the copper alloys have been found. Instances of internal oxidation in alloys of most of the metals of the I-b and VIII groups of the periodic system are on record, but evidence of this type of oxidation in alloys of the metals of the intermediate groups is lacking. A number of the metals of the intermediate group, among them cadmium, lead, tin, and zinc, appear to provide the conditions essential to subscale formation; i.e., they form oxides with a relatively low negative free energy of formation, they dissolve other metals that form more stable oxides, and, presumably, oxygen will diffuse through them. In a study of 4o alloys of these white metals only a few cases of internal oxidation have been found. The probable reasons for this difference in behavior will be discussed presently. EXPERIMENTAL PROCEDURE Silver.-The silver alloys employed in the oxidation studies were prepared in heats of 30 grams each from high-purity silver (99.993 per cent Ag)* and the purest avail-

Jan 1, 1942

By A. H. Grobe, F. N. Rhines

AT elevated temperatures the oxide of silver is unstable in the air at atmospheric pressure, consequently no external oxide scale forms upon pure silver under conditions of high-temperature annealing When small quantities of certain alloying elements are present in the silver, the formation of a thin external scale is possible' and in addition there may form a subscale composed of the oxide of the solute element precipitated within the body of the silver Norbury2 and Leroux and Raub3 have reported internal oxidation (subscale formation) in alloys of silver with 2, 7 5, and 30 per cent of copper The presence of the subscale is believed to be responsible, at least in part, for the objectionable "fire mark" in Sterling silver' Several other alloys of silver, after oxidizing heat-treatments, are known to exhibit undesirable polishing characteristics that may be the result of internal oxidation Except for the absence of an external scale of silver oxide, it is to be anticipated that silver alloys will prove to be very similar in their oxidation behavior to the alloys of copper, the oxidation characteristics of which have been studied in some detail 5,6 The present research confirms this anticipation The oxidation of a series of 20 dilute alloys of silver has been studied metallographically, some types of subscale not encountered among the copper alloys have been found Instances of internal oxidation in alloys of most of the metals of the I-b and VIII groups of the periodic system are on record, but evidence of this type of oxidation in alloys of the metals of the intermediate groups is lacking A number of the metals of the intermediate group, among them cadmium, lead, tin, and zinc, appear to provide the conditions essential to subscale formation, i e , they form oxides with a relatively low negative free energy of formation, they dissolve other metals that form more stable oxides, and, presumably, oxygen will diffuse through them In a study of 4o alloys of these white metals only a few cases of internal oxidation have been found The probable reasons for this difference in behavior will be discussed presently EXPERIMENTAL PROCEDURE Silver -The silver alloys employed in the oxidation studies were prepared in heats of 30 grams each from high-purity silver (99 993 per cent Ag)* and the purest avail-

Jan 1, 1942

By Frank W. Harris

The strength of hard drawn copper wire is a question of considerable importance to both manufacturer and consumer. Unlike steel and alloy wires, in which strength is governed by both chcniical and physical considerations, t,he high conductivity required for copper wire in the clcc-trical industry generally precludes the possibility of obt,aining tensile strength through the use of alloys. Consequently, this strenglh is largely a rnatter of the ~hysical structure, and all factors known to affect this structure, such as rolling temperature, die contours, lubricants, drawing speeds, etc., arc matters of prime importance. The experiments described here have becn carried out dl~ring the past year at the Baltimore plant of the American Smelting & Refining Co., in connection with a general investigat,ion of sorne of the questions mentioned above, with the object of studying thc physical ~t~ructure of hard drawn copper wire and the influence of ccrtain factors on t,hat st'ruct.ure. The work has been of an exploratory nature, rather than con~prehensivc., but it was thought that the result,s might prove of sr~fficient general interest tjo warrant their publicatlion. The bulk of the hard drawn coppcr wire used in places where strength is an important factor is rnanufacturcd to strict specification, based USU-ally in the United States on thab of t,he Arrlerican Society for Tcst'ing Materials (B-1-23). This specification calls for almost as high a, valuc of t,ensilc strength, consistent with elongation, as it is possible pract'icnlly to obtain, and only physically perfect mlaterial can be relied on to lliect such a specification. Obvious defects, such as laminat'ions protluc:etl through fins in bhe original rods or brittleness duo lo ovt~rdrawing, arc. usually recognized and need only passing refercncc. Laminatlions can be detected by twisting and untwisting the wircx several times; they will show up on the surface in the form of fins. Pig. 1 shows a very bad example of this defect. Thc wire may bc perfectly smooth before twisting hut, when such larrlinations arc3 prcstmt they will readily show up under this treatrncnt. This trouble is caliscd by sirriilar defects in the original rod produced by overfills in rolling. Fig. 2 shows the cross-section of the rod from which thc wire in Fig. 1 was drawn.

By T. C. Campbell

Copper is extracted from the Chuquicamata oxide ore by a hydro-metallurgical process. The ore is crushed to 3/8-in. sizing, and leached with a sulfuric acid electrolyte. Chlorine is precipitated. and the ferric iron reduced in the enriched electrolyte, after which the copper is recovered by electrolysis with insoluble Chilex and lead-antimony anodes, the spent electrolyte being returned to leaching. Cathodes are melted and refined in market furnaces and cast into commercial wire-bar and cake shapes. Sulfuric acid for the process is supplied by the brochantite in the ore. Water for washing the ore is advanced through the solution system and finally after cutting by electrolysis to from 6 to 16.0 grams per liter is completely stripped by the cuprous chloride method and run to waste. The cuprous chloride so obtained plus that resulting from precipitation of chlorine from strong solution is dissolved in ferrous chloride brine and the copper cemented on scrap iron. The cement so obtained is in part used to reduce ferric iron in electrolyte, and as it is of exceptional purity is also furnace refined and cast into an exceptional quality of fire-refined copper. Fig. 1 is flow sheet of the operation. The reduction plant is composed of seven divisions as follows: (1) crushing, (2) leaching, (3) tailings disposal, (4) dechloridizing, (5) sulfur dioxide treatment, (6) electrolytic tank house, (7) smelting and melting. A brief description of each of these divisions will be given. Crushing Ore that is frequently blocky and up to 5 ft. in section is crushed in four stages to 3/8-in. mesh. The first stage of crushing is called primary and the next three stages are known as secondary crushing. The first stage is accomplished with two 60-in. Superior McCully gyratory breakers by which the ore is broken to 9 in. The second coarse gyratory breakers crush the ore to 3-in. sizing. There are seven No. 10 McCully gyratories in this service, for one of which recently has been substituted a No. 7 cone crusher. The third and fourth stages of crushing are accomplished by fifty 48-in. disk crushers. In the third stage 14 disk crushers break the ore to 1 in., and in the last stage 36 disk crushers turn out the final product of 0.371-in. sizing. Reference to the flow sheets of Figs. 2 and 3

Jan 1, 1934

By A. C. JR. Boyle

I. INTRODUCTION THE geological field work of the Bully Hill district, upon which this paper is based, was begun July 1, 1908, and covered a period of three months. The time was found too short for a complete report and the district was again visited in the early part of July, 1912,. from which time detailed study of the locality continued until September of the same year. This paper is the result of observations made in the mines in the immediate vicinity of Winthrop, Shasta county, Cal., during these two periods of study. The preparation of this report has been greatly facilitated by various courtesies rendered the writer by D. M. Riordan, President of the Bully Hill Copper Mining & Smelting Co., and by John B. Keating and Herbert R. Hanley, managing officers actively in charge at the mines. The elaboration and further study of the notes and collections were carried on in the laboratories of the Departments of Geology and Mining at Columbia University, and the writer takes pleasure also at this point in expressing his acknowledgments to Profs. James F. Kemp, A. W. Grabau, Charles P. Berkey, and William Campbell, for advice and assistance. In order that one may appreciate at first reading the significance of some of the details which follow, and for the sake of clearness, a brief outline of the geological relationships is here given, together with certain conclusions which have been reached regarding the genesis. of the ores and the gypsum masses. In the Bully Hill mining district an associated series of Triassic lavas and tuffs, chiefly andesites, is preceded as well as followed by sediments. The entire system is tilted so that the original bedding planes dip in general to the southeast. The surrounding region has been greatly disturbed, and in the immediate vicinity of the mines close folding of the later sediments and extreme shearing of the igneous rocks locally is a striking feature. Into the nearly vertical shear zones have been intruded post-Triassic dikes of various rock types in the following order: alaskite-porphyry and andesite-porphyry. Outside the area under consideration diorite dikes are known, but they will not receive attention further than to note that' they, probably, represent a differentiation product of the same magma from which the other two dikes came. In this connection all the dikes have an important bearing on the origin of the ores and of the gypsum found in the mines.

Jan 1, 1914

By David Turnbull

STAFF: Editor, Gerhard Derge Carnegie Institute of Technology Schenley Park Pittsburgh 13, Pa. Editorial Assistant, M. A. Redmerski Production Editor, Otto T. Johnson THE METALLURGICAL SOCIETY: J. S. Smart, Jr., President; C. C. Long, Past-President; K. L. Fetters, Vice President; T. D. Jones, Treasurer; R. W, Shearman, Secretary. PUBLICATIONS COMMITTEE OF THE METALLURGICAL SOCIETY: C. L. McCabe, Chairman; H. L. Bishop, K. L. Fetters, J. J. Harwood, W. A. Krivsky, F. C. Langenberg, R. E. Lund, W. O. Philbrook, L. L. Seigle, R. L. Smith, and F. L. Vogel. Review and selection of monuscripts is under the supervision of the following Publications Committees: Extractive Metallurgy Division: C. L. McCabe, Chairman; R. E. Lund, Vice-Chairman; D. H. Baker, Jr., W. A. Krivsky, R. A. Lewis, Paul Queneau, A. S. Russell, R. E. Shinkoskey, W, W. Stephens, and M. E. Wadsworth. Institute of Metals Division: L. L. Seigle, Chairman, Paul A. Beck, I. I. Bessen, J. 0. Better-ton, Jr., J. B. Clark, R. S. Davis, A. E. Dwight, R. W. Fountain, R. B. Gordon, C. D. Graham, Jr., R. W. Guard, J. C. Gurland, E. L. Harmon, J. J. Heger, A. A. Hendricksan, M. Herman, J. N. Hobstetter, H. H. Johnson, Jr., R. R. Nash, T- N. Rhodin, R. H. Richman, W. Ros-toker, P. G. Shewmon, C. W. Spencer, L.SIifkin, J. K. Stanley, C. D. Starr, and H. C. Stumpf. Iron and Steel Division: H. L. Bishop, Chairman; R. E. Boni, F. C. Langenberg, J. B. Wagstaff, and T. V. Wainwright. Published bimonthly by the American Institute of Mining, Metallurgical, and Petroleum Engineers, Inc., 29 West 39th Street, New York 18, N. Y. Telephone: PEnnsylvania 6-9220. Subscription $20 per year for non-AIME members in United States and North, South, and Central America; $25, foreign; $5 for AIME members. Single copies, $4.00, single copies foreign, $5.00. The AIME is not responsible for any statement made or opinion expressed in its publications . . . Copyright 1961 by the American Institute of Mining, Metallurgical, and Petroleum Engineers, Inc. . . . Registered cable address, AIME New York .. . Indexed in Engineering Index, Industrial Arts Index, and Chemical Abstracts . . . Second class postage paid at New York, N. Y., and Ann Arbor, Mich. Volume 221, Number 3.

Jan 1, 1962

By Henry Ferguson

THIS paper is a preliminary statement, intended to present the more important results of the recent studies of the ore deposits of the Alleghany district in advance of the publication of the complete report, now in preparation. The Alleghany district (Fig. 1) has been a producer of gold since the early days of California gold mining. As in other California gold camps, placers yielded the bulk of the earlier production, but during the last 30 years lode deposits have been the only important source of output. The district differs from other California gold-quartz districts in that nearly all the production is from small shoots of high-grade ore. The mining camps of Alleghany and Forest are on the western flank of the Sierra Nevada range about 20 miles west of the crest. The gently sloping lava-covered plateau which controls the upland topography has been trenched by deep canyons of the westward flowing streams, which are cut to depths of as much as 2000 ft. below the crests of the ridges. The district is about 18 miles from Nevada City but the automobile road which connects the two places is 31 miles long. The senior writer first visited the district in 1913 and published a short description of the lode deposits.1 The increasing importance of the district made further study desirable. A detailed topographic map was therefore made by W. B. Upton, Jr., of the U. S. Geological Survey, in the spring of 1924, and the senior writer spent parts of the field seasons of 1924 and 1925 in the district. For the second field season the Geological Survey was fortunate in securing the services of R. W. Gannett, who had already done geologic work in the district for several of the mining companies. Owing to the death of Mr. Gannett in October, 1925, just before the close of his field work, the work of preparation of the entire report fell to Mr. Ferguson. He takes this opportunity of acknowledging how deeply he is indebted to Mr. Gannett for his excellent work in the field, and his realization of how greatly the completion of the report on the district has suffered from lack of Mr. Gannett's assistance in the office. In October, 1.928, after the completion of the first draft of the manuscript, Mr. Ferguson made a short visit to the district.

Jan 1, 1929

By R. F. Mehl, C. E. Birchenall

R. E. Hoffman and D. Turnbull—The authors have presented evidence which they have interpreted as indicating that the rate of self diffusion is not intrinsically more rapid at grain boundaries than within the grain. Grain-size effects which apparently exist are attributed rather to impurities concentrated at the grain boundaries. In view of our own experiments and the existing evidence, we believe that the support for this hypothesis is not convincing. We have in progress an investigation in which the rate of self diffusion of silver is being measured over an extended temperature range in both single-crystal and polycrystalline specimens. The results of the single-crystal experiments and some preliminary data on fine-grained polycrystalline specimens have already been reported:' and it is anticipated that a complete report will be published in the near future. The self-diffusion coefficient of large-grained polycrystalline silver (1 grain per sq mm) has previously been measured by Johnson" between 730" and 940°C. The diffusion coefficients which we have measured in single crystals (210 plane normal to diffusion direction) agree within experimental error with values calculated from an extrapolation of Johnson's curve down to temperatures as low as 500 °C. However, it has been demonstrated that the overall self-diffusion rate in fine-grained polycrystalline specimens (initial grain size of 0.003 cm) becomes measurably larger than the overall rate in a single crystal at a temperature of 600°C, and the discrepancy between the two rates becomes greater as the temperature is further decreased. In fact, it has been possible to obtain satisfactory penetration curves for polycrystalline specimens using the sectioning technique at temperatures as low as 400°C. At this temperature, the penetration is 50 to 100 times greater in the polycrystalline specimens than in a single crystal. Fisher" has developed an analysis whereby the ratio of the rate of the unit diffusion process at the grain boundary to the corresponding rate within the grain can be calculated from the penetration curves and an assumption as to the width of a grain boundary. This analysis applied to our data indicates that the unit process at the grain boundary is faster by a factor of 10' at 475°C when the grain boundary width is taken to be 5. The silver used in most of these experiments was obtained from the Handy and Harmon Co. and listed as 99.97 pct pure. Preliminary experiments on 99.999 pct silver from the Jarrel-Asch Co. indicate a grain-size effect of the same order of magnitude as in the less pure silver. Nominally, these purities are as good, at least, as that of the carbonyl iron used by the authors, but of course if an impurity effect does exist its magnitude might be very dependent upon the nature of both major and minor constituents. The authors have cited the work of other investigators who have found no grain-size effects. Neither Steigman, Shockley and Nix" nor Maier and Nelson8 were able to correlate self-diffusion coefficients of copper with grain size. However, all their measurements were performed at or above 750°C; and on the basis of our work with silver, no grain-size effect would be expected at temperatures above about 0.7 of the absolute melting temperature unless the grain size were exceedingly small. Likewise, in the investigation of the self diffusion of lead by Seith and Keil,14 the lowest temperature at which the diffusion coefficient was measured in polycrystalline specimens was 207°C, which is still sufficiently high so that the lack of a grain-size effect is not surprising. Finally, in those experiments on iron from which they concluded that there was no grain size effect, Drs. Birchenall and Mehl seem to have no information as to the actual grain sizes immediately prior to and following the diffusion anneal. Without this information, we believe that their own experiments offer little support for their hypothesis. F. S. Buffington, I. D. Bakalar, and M. Cohen—The results given in this paper agree in order of magnitude with those tentatively reported by us.27 However, significant differences exist in the two sets of data, and it may be well to make an explicit comparison. The diffusion studies at M.I.T. were conducted on somewhat higher purity iron (99.98 pct Fe) than the grades used by the authors, but this is undoubtedly not the answer. Fig. 4 shows the diffusion results of both laboratories for the gamma phase, omitting the authors' data on the commercial steels, while fig. 5 presents a similar comparison for the alpha phase. The divergence is much more marked in the latter case than in the former. In connection with the M.I.T. determinations, all of the runs in the gamma range and those above 800 °C in the alpha range were conducted with specimens having a relatively thick (0.002 cm) electrodeposit of radioactive iron. This practice minimizes any possible error due to extraneous diffusion that may occur during the heating to and cooling from the operating temperature. An exact solution of Fick's law for these boundary conditions was used in calculating the diffusion coefficients. At a later time, three runs were made below 800°C, using very thin electrodeposits similar to those of the authors, and the points fell considerably below the values expected from the extrapolation of the results based on the specimens with the thick deposits (compare dash-dot line in fig. 5). However, in the runs with the thin deposits, deviations of 100 pct were found between the individual specimens, whereas the maximum deviation with the thick deposits was less than 25 pct. Accordingly, it is not known at the moment whether the M.I.T. points below 800 °C should be given as much weight as those above 800°C. If this were done, the frequency factor would be of the order of 400 cm2 per sec, which is quite high. In other metals, the frequency factor for self diffusion lies between about 0.1 and 10 cm2 per sec. As the points below

Jan 1, 1951

By Paul A. Beck

THE occurrence of the (100) [lOO] or "cube" texture upon annealing of cold-rolled copper has been much investigated.' The conditions favorable for its formation were found to be a high final annealing temperaturez or long annealing time," a high reduction of area in cold rolling prior to the final anneal,' and a small penultimate grain size." The effects of penultimate grain size and of rolling reduction were found by Cook and Richards4 to be interrelated in such a way that any combination of them giving lower than a certain value of the final average thickness of the grains in the rolled material leads to a fairly complete cube texture with a given final annealing time and temperature. Also, according to the same authors, at a higher final annealing temperature a larger average rolled grain thickness, i.e., a lower final rolling reduction, is sufficient than at a lower temperature. These somewhat involved conditions can be understood readily on the basis of recent results obtained at this laboratory. Hsun Hu was able to show recently by means of quantitative pole figure determinations that the rolling texture of tough pitch copper, which is almost identical with that of 2s aluminum: may be described roughly as a scatter around four symmetrical "ideal" orientations not very far from (123) [112]. In the case of aluminum, annealing leads to retain-ment of the rolling texture with some decrease of the scatter around the four "ideal" orientations, and to the appearance of a new texture component, namely the cube texture." A microscopic technique, revealing grain orientations by means of oxide film and polarized light, showed that the retainment of the rolling texture is achieved through two different mechanisms operating simultaneously, namely "re-crystallization in situ," and the formation of strain-free grains in orientations different from their local surroundings, but identical with that of another component of the rolling texture. Thus, a local area in the rolled material, having approximately the orientation of one of the four "ideal" components of the texture, partly retains its orientation during annealing, while recovering from its cold-worked condition, and it is partially absorbed at the same time by invading strain-free grains of an orientation approximately corresponding to that of another "ideal" texture component. The reorientation here, as well as in the formation of the strain-free grains of "cube" orientation, may be described as a [Ill] rotation of about 40°, see Fig. 1 of ref. 6. The preferential growth of grains in such orientations is a result of the high mobility of grain boundaries corresponding to this relative orientation.' " It appears very likely that in copper the mechanism of the structural changes during annealing is similar to that observed in aluminum (except for the much greater frequency of formation of annealing twins in copper). In both metals the new grains of cube orientation have a great advantage over the new grains with orientations close to one of the four components of the rolling texture. This advantage stems from their symmetrical orientation with respect to all four retained rolling texture components of the matrix; they are oriented favorably for growth at the expense of all of these four orientations. As a result, the growth of the "cube grains" is favored over the growth of the others, as soon as the new grains have grown large enough to be in contact with portions of the matrix containing elements of more than one, and preferably of all four component textures. It is clear that this critical size is smaller and, therefore, attained earlier in the annealing process if the structural units, such as grains and kink bands, representing the four matrix orientations are smaller, i. e., if the average thickness of the rolled grains is smaller. Hence, for a given annealing time and temperature, a smaller penultimate grain size and a higher rolling reduction both tend to increase that fraction of the annealing period during which the above condition is satisfied. Consequently, the percentage volume of material assuming the cube orientation increases. The same is true also for increasing time and temperature of annealing when the penultimate grain size and the final rolling reduction are constant, since the average size attained by the new grains during annealing increases with the annealing time and temperature. For the same reason, at higher annealing temperatures a given volume percentage of cube texture can be obtained with larger rolled grain thickness (larger penultimate grain size, or smaller rolling reduction) than at lower annealing temperatures. The well-known conspicuous sharpness of the cube texture may be interpreted as a result of the fact that selective growth of only those grains is favored that have an orientation closely symmetrical with respect to all four components of the deformation texture and exhibit, therefore, a high boundary mobility in contact with each. The effect of alloying elements in suppressing the cube texture, as described by Dahl and Pawlek,' appears to be associated with a change in the rolling texture. For face-centered cubic metals, such as copper, which do exhibit the cube texture upon annealing, the rolling texture is always of the type described above, i. e., scattered around four "ideal orientations" of approximately (123) [112]. The addition of certain alloying elements, such as about 5 pct Zn or 0.05 pct P in copper, has the as yet unexplained effect of changing the rolling texture into the (110) 11121 type. This texture consists of two fairly sharply developed, twin related components. In such cases, as in 70-30 brass and in silver, the annealing texture again is related to the rolling texture by a [lll] rotation of about 30°, however, because of the different rolling texture to start from, it has no cube texture component. At higher temperatures, both in brassm and in silver," grain growth leads to a further change in texture: A [lll] rotation of the same amount, but in reversed direction, back to the original rolling texture.

Jan 1, 1952