By Ott F. Heizer

The mines and the mill of the Nevada-Massachusetts Co. are on the east slope of the Eugene Mountains, in Pershing County, Nevada, 8 miles northwest of Mill City, a station on the Southern Pacific R.R. and on the Victory Highway. Fig. 1. Supplies and, concentrate are transported by truck over an automobile road of easy grade. The property is at an average elevation of 5500 ft. and climatic conditions are generally favorable for continuous operation throughout the year. The ore treated is supplied by two adjoining mines, the Stank and the Humboldt. Physical and mineral characteristics of the ores produced by these two mines are substantially similar, although variations occur in hardness and mineral distribution.' The economic mineral is scheelite (CaWO4), composed, when pure, of 80.6 per cent tungstic trioxide (WO3) and 19.4 per cent lime (CaO).

Jan 1, 1935

By G. Gabra

The kinetics of acidified thiourea leaching of pyrite concentrate was investigated at temperature ranging form 20 °C to a 60 °C. The effect of various parameters on the dissolution rates are discussed. The gold extraction was found to be zero and first orders with respect to Fe (111) and thiourea concentration, respectively. The order of the reaction with respect to sulfuric acid was found to be zero. The activation energy was determined from the Arrhenius plot as 2,039 kcal mole -1 (for a freshly prepared acidic solution containing Fe (111) as the oxidant and at 800 rpm stirring speed. This relatively low activation energy value suggests that the gold extraction is controlled by a-physical phenomenon. Under optimum conditions, more than 90% of gold has been dissolved in about 30 min. and 95% in 60 min. Attempt to recover gold from thiourea solution using active carbon is also discussed.

Jan 1, 1984

By Paul Billingsley

THE purpose of this paper is a comparison, based on genesis, of the ore deposits associated with the igneous rocks of the central Montana Rockies. Considered separately, without attention to their origin, the orebodies appear to be distributed haphazard, with no fundamental laws controlling their position and character. It is believed, however, that if all the factors be weighed, this apparent confusion will to a large degree disappear. The, first essential to such a comparison is detailed knowledge of the individual mines, as to their geographic position (see Fig. 1), their mineralogical character, and in particular the derivation of their ores.1 The authors of this paper have pursued such an investigation for the past 6 years, and have accumulated a mass of evidence that enables a preliminary correlation to be attempted. It appears that the majority of ore deposits are genetically related to one or another of the igneous

Jan 4, 1917

By F. Haessner, M. Wilkens, U. Jakubowski

ThOUGH at present there is a wide range of possibilities for the quantitative determination of preferred orientations, pole figures of identical specimen material have not been determined by different methods as yet.''' In this paper a comparison of (Ill), (200), and (220) pole figures is presented which were obtained from a 95 pct cold-rolled high-purity cop- per sheet (99.9998 pct Cu), by three different methods. The three methods are: a) The combined X-ray reflection-transmission technique of plane samples by schulz3 and Decker, Asp, and Harker. 4 A Siemens texture goniometer was used. The experimental details are described elsewhere. 6 b) The X-ray reflection technique of spherical samples by Jetter and Boric.' A Siemens texture goniometer with some modifications was used. The samples were prepared by sticking 140 polished sheets together with an adhesive and machining a sphere (20 mm diam).* Additional

Jan 1, 1967

By E. F. Reed

CONSIDERABLE deep hole prospect drilling has been done in the last few years in the Globe-Miami mining district about 70 miles east of Phoenix, Arizona, and in the San Manuel-Tiger area about 50 miles south of the Globe-Miami region. More than 205,000 ft of churn drilling have been completed by the San Manuel Copper Corp. at their property in the Old Hat Mining District in southern Pinal County. The deepest hole on this property is 2850 ft; there are 49 holes deeper than 2000 ft. At the adjoining Houghton property of the Anaconda Copper Mining Co., where only one hole reached 2000-ft depth, there were 27,472 ft of churn drilling and 3436 ft of diamond drilling. Three churn drill holes were deepened by diamond drilling methods. Near Miami in the Globe-Miami district the Amico Mining Corp. drilled four holes by combined churn and rotary drilling methods, the total amounting to 13,879 ft, of which 2256 ft were drilled with a portable rotary rig. In the same district, besides doing a large amount of shallow prospect drilling, the Miami Copper Co. drilled two holes of 2560 and 3787 ft, respectively, which were completed by churn drilling methods. The rocks encountered in drilling at San Manuel and Tiger are described by Steele and Rubly in their paper on the San Manuel Prospect' and by Chapman in a report on the San Manuel Copper Deposit? The rocks are well-consolidated Gila conglomerate, quartz , monzonite, and monzonite porphyry. In some places these formations stand very well while being drilled, and three holes were drilled without casing, the deepest of which was 2200 ft. In other holes faulted and fractured ground made drilling difficult. In the Globe-Miami district the deep drilling was done in the down-faulted block of Gila conglomerate east of the Miami fault and in the underlying Pinal schist. The geology of this area is described by Ransome.3 In the Amico holes the conglomerate varied from material consisting entirely of granite boulders and fragments to a rock made up of schist fragments in a sandy matrix; in the Miami Copper Co. holes there were more granite boulders and the material was poorly consolidated. Drilling was much more difficult and expensive in the Miami area than in the San Manuel district, mainly because of the depth of the holes and the formations drilled. All the deep hole prospecting described in this paper was done with portable rigs. The churn drill rigs were of several types, of which the Bucyrus-Erie were the most popular. Bucyrus-Erie 28L, 29W, and 36L rigs were used on some of the deeper holes on the San Manuel property. A few Fort Worth spudder types were tried, and the deepest hole at San Manuel was drilled with a Fort Worth Jumbo H. The spudder type is considerably larger than most other rigs used on this work and required a larger location site. The spudders were belt-driven machines with separate power units, and time required for setting up and moving was much longer than with the more portable drills. All the churn drilling was done by contractors or with machinery leased from them. A few of the contractors had complete equipment, including most of the necessary fishing tools. Unusual and special, fishing tools were obtainable from the supply companies in the oil fields of New Mexico or in the Los Angeles area. Most of the contractors used equipment with standard API tool joints, so that much of it was interchangeable. Failure of tool joints is one of the principal causes of fishing jobs. It can be minimized if the joints are kept to the API specifications and the proper sized joints are used in the various holes. The minimum sizes that should be used with various bits are as follows: 12-in. and larger bits, 4x5-in. tool joints; 10-in. bits, 3 1/4x4 1/4-in. tool joints; 8-in. bits, 2 3/4x 3 3/4-in. tool joints; 6-in. bits, 2 1/4 x3 l/4 -in. tool joints; 4-in. bits, 1 5/8 x2 5/8-in. tool joints. Two rotary drill rigs were tried at San Manuel on the same hole, and a portable rotary drill rig was used on the Amico drilling for test coring the formation and for drilling in holes 3 and 4. Rotary drilling differs from churn drilling or cable tool drilling in that the bit is revolved by a string of drill pipe and the cuttings are removed from the hole by a thin solution of mud pumped through the drill pipe. The principal parts of a rotary rig are the power unit, a rotating table to revolve the drill pipe, hoists to raise and lower the pipe and to handle casing, and a pumping system to circulate the drilling liquid. The rig used on the Amico property at Miami was mounted on a truck. The larger rig used on the San Manuel property was hauled by several trucks and had separate turntable and pumping units. Diamond drill coring equipment was used successfully with the rotary rig in the holes on the Amico property, To allow for 2 3/8-in. drill pipe with tool joints, 3 1/2-in. core barrels and bits were used. With the standard 3 1/2-in. core barrel there was considerable difficulty in maintaining circulation with mud, so a barrel was designed with a smaller inner tube and a broad-faced bit. This allowed coarser material to circulate between the barrels. Rock bits of 5 5/8 to 3 7/8 in. were used with the rotary rig for drilling between core runs. Diamond drill equipment is much lighter than churn drill tools, so that fishing tools can usually be obtained from supply houses by air express when needed. Three churn drill holes on the Houghton property at Tiger were deepened by diamond drilling with Longyear UG Straitline gasoline-driven-machines. The open churn drill hole was cased with 2 1/2-in. black pipe. In deep hole churn drilling, casing is one of the most important items, especially in drilling in unconsolidated material like the formations drilled by

Jan 1, 1952

By M. T. Simnad, C. E. Birchenall, M. H. Davies

THE marker movements observed by Davies, Simnad, and Birchenall during the growth of magnetite on wustite have been misinterpreted. It is the purpose of this note to correct the original interpretation. In that investigation wustite specimens were prepared by oxidizing pure iron disks in water vapor until the iron was consumed. Argon was used as a carrier gas for the water vapor and on the complete conversion of the metal to its oxides ('FeO' plus a small amount (10 pct) of surface Fe3O) the water supply was bypassed and the specimens were annealed in argon alone in order to equilibrate the wustite with the overlying magnetite. After cooling, the magnetite was ground off, a crude magnetic test being employed to determine its complete removal. Radioactive silver streaks were then applied to the surface and the specimen was oxidized completely in water vapor to prevent hematite formation. After complete oxidation the markers were found to enclose about 80 pct of the magnetite with the other 20 pct lying outside the markers. This observation was interpreted to mean that oxygen transport was four times as great as iron transport during the growth of the magnetite. The conclusion would have been correct if, as in the case of wustite growing on iron, all the iron had started from one side of the marker and all the oxygen from the other side initially. Actually a material balance is required. For simplicity, take wustite to be exactly FeO, and magnetite to be Fe3O,. Then at the start of the reaction 3 FeO + O -> Fe,O., All of the iron and three-fourths of the oxygen of the final product will be within the marker inter- faces. The other fourth of the oxygen is in the gas phase outside the marker. From the experimentally determined final position of the markers simple calculation shows that one-fifth of the total iron has crossed the marker interface, while one-twentieth of the total oxygen has crossed in the reverse direction. The simplified result favors iron transport in the ratio four to one. However wiistite is not stoichiometric FeO. At 900°C, the temperature of the measurement, the composition is about FeO When the material balance for the same experimental result is repeated, assuming the product will be 1 mol of Fe3O4, it is found that 0.6 gram atoms of iron and 0.19 gram atoms of oxygen must have passed the marker in the same direction. (This is readily apparent from the reaction to form 1 mol of Fe3O4 SFeO The total oxygen supplied from the atmosphere is 0.61 gram atoms, but the iron which passes the marker interface, i.e., 0.6 gram atoms, requires 0.8 gram atoms of oxygen to convert it to Fe,O,.) If all the transport during magnetite growth is due to iron ion diffusion, then the marker would enclose about 85 pct of the final magnetite and the original measurement is in error by about 5 pct. This error is probably less than the uncertainty in locating the markers by autoradiography. The possibility also exists that the starting wustite was not quite saturated with oxygen and underwent further enrichment with consequent envelopment of the marker before magnetite caught up with the marker interface. In any case it appears that these measurements actually favor iron ion diffusion in magnetite overwhelmingly as the factor controlling its growth, although further experimental measurements are needed to eliminate the error in material balance described. Such studies are planned.

Jan 1, 1954

By D. H. Davis, I. Fatt

Oil bearing rocks, usually found at depths of 2,000 to 10,000 it, are elastically deformed by overburden pressure. Although the change in porosity with pressure in a number of example rock.: has been shown to be small, it was thought that overburden pressure might have a significant effect on permeability. This note presents results of an investigation to determine the magnitude of the change in permeabilty with pressure. In routine core analysis permeabilities are measured on rock samples which are not under overburden pressure. If permeablity measured in this way differs from permeabilities measured under overburden pressure, a systematic error is introduced into well productivity calculations. The experiments described in this report were made to determine the magnitude of the change and thus to give an estimate of the error introduced into the calculations. The error introduced by the neglect of the change in permeability when overburden pressure is removed may account for part of the difference between well productivity calculated from core analysis and the actual well productivity. The results obtained in this investigation have only quali-tative significance because of the difficulty in reproducing in the laboratory the stress conditions on the rock buried in the earth. The assumption which is usually made is that the rocks in the earth are under a uniform pressure equal to the weight per unit area of the vertical overburden column from the rock in question to the surface of the earth less the pressure of the liquid in the pores of the rock. For an overburden consisting of sandstones and shales (of assumed average specific gravity of 2.3) and for a liquid pressure equal to the pressure in a salt water column (of specific gravity 1.0) reaching from the rock to the surface, the resulting net pressure on the rock is approximately 0.56 psi per ft of depth. EXPERIMENTAL METHOD Clean, dry sandstone core plugs one in. in diameter and about three in. long were mounted in a copper foil jacket as shown in Fig. 3 or molded in a Lucite jacket as shown in Fig. 4. All cores except those labeled "2" in Fig. 1 and "8" in Fig. 2 were measured in the copper foil jacket. Cores "2" and "8" were measured in the Lucite jacket. The jacketed core was placed in a high pressure hydraulic bomb in which the liquid pressure outside the jacket could be raised to 15,000 psi. Flow lines from the core were brought out of the bomb through special fittings in the bomh head and connected to a laboratory type gas permeameter. Measurements were made with nitrogen gas; the maximum mean gas pressure in the core was 16.1 psia. RESULTS The specific permeability of sandstone decreases with in. crease in overburden pressure. Most of the decrease takes place over the range of zero to 3,000 psi overburden pressure. If the net pressure on the rock is assumed to be 0.56 psi per ft of depth as discussed above, 3,000 psi of overburden pressure is equivalent to about 5,000 ft of overburden. At 3,000 psi overburden pressure, the permeability of the eight sandstone core samples tested ranged from 59 to 89 per cent of the permeability without overburden pressure. Figs. 1 and 2 show the permeability reduction as a function of overburden pressure. The permeability of the eight cores without overburden pressure ranged from 4.35 md to 632 md; these permeabilities are listed in Figs. 1 and 2. REFERENCES 1. Carpenter and Spencer: "Measurements of Compressibility of Consolidated Oil Bearing Sands," U. S. Bureau of Mines, R.I. 3450, (1940). * * *

Jan 1, 1952

By Irwin Politziner F. M. Townsend, L. S. Reid

Recently published data indicate that the water vapor content of a gas, as determined by dew point measurement, is inaccurate when the gas has been dehydrated with diethylene glycol. Water vapor contents and dew point measurements of gases dehydrated with triethylene glycol have been obtained in this investigation in order to determine the magnitude of a similar error, if one exists. Experimental data show a very low concentration of triethylene glycol vapor in gases dehydrated at atmospheric ternperatures and pressures ranging from 500 to 2,500 psia and that the accuracy of dew point measurements is not impaired by the presence of triethylene glycol vapor. INTRODUCTION Nearly all natural gas transported by pipe line to northern and eastern markets must be dehydrated to a low residual moisture content in order to assure maximum transmission efficiency and continuous delivery under peak load conditions. Without dehydration, water vapor often condenses in pipe lines in quantities sufficient to restrict the flow3 and. under low atmospheric temperature conditions, gas hydrates may form and plug gathering. transmission and distribution facilities. Gas may be dehydrated to pipe line specifications by a number of methods. The most widely used methods are (1) adsorption of water vapor on a solid dessicant such as activated bauxite, alumina or silica gel,' (2) by absorption of water vapor by either diethylene or triethylene glycol-water solutions of high glycol concentration,11,13 and (3) by simultaneous expansion-refrigeration of very high pressure gas in which gas hydrates are purposely formed and then quickly decomposed.'"" Of these three fundamental methods, the adsorption and absorption processes provide the bulk of the dehydrated gas moving to market at the present time. The expansion-refrigeration process. a relatively new development, is gaining in favor because of its simplicity but is sharply limited in its application by available differentials between source and gathering system pressures. Where gas sale or purchase contracts contain a maximum water vapor content specification, the water vapor content is usually determined by measuring the dew point of the gas at system pressure. Knowing he dew point temperature and the system pressure, the water vapor content of the gas is determined from a graphical correlation of saturation, or dew point, temperature us the water vapor content of the gas which is customarily expressed as pounds of water vapor per million cubic feet of gas measured at 14.7 psia and 60°F. Dew points are usually measured with the U. S. Bureau of Mines Dew Point Tester. shown in Fig. 1, which is well suited for use at temperatures lower than 120°F and at pressurei; ranging from atmospheric to 3,000 psi. A number of correlations of dew point temperatures vs water vapor content are available,3,5,15 the most recent of which is that by McCarthy et al.4 Where natural gas is dehydrated by absorhing contact with concentrated diethylene glycol-water solutions. considerable difficulty is experienced in observing water dew points due to condensation of liquid hydrocarbon and glycol films on the mirrored surface of the dew point tester. Riesenfeld and Frazierl2 report that the dew point method for determining the water vapor content of a dietllylene glycol-treated natural gas is in error due to the glycol content of the condensate formed on the tester mirror, and that the water vapor content of the gas tested is actually lower than that indicated by the standard' dew point-water vapor content correlation. Extensive experience in testing gases dehydrated by concentrated triethylene glycol-water solutions lias not revesled difficulties of the nature cited above for diethylene glycol. Water dew points are clear and sharp and condensation of

Jan 1, 1951

By Ed L. Reed

INTRODUCTION The most efficient development of a mine plan for in-situ leach (solution) mining must be based upon an understanding and application of the basic hydrologic characteristics of the aquifer containing the mineral values. Similar knowledge of the overlying and underlying aquifers is also required. This paper summarizes the hydrologic properties of a ground water system and describes some of the more important conclusions that can be drawn from a detailed hydrologic study. Basic to an in-situ leach mining operation is the flow of fluids through porous rock from place to place. The degree to which these movements of fluids can be predicted and controlled determines to a large extent the efficiency of the ore recovery operation. HYDROLOGIC CHARACTERISTICS The principal hydrologic characteristics of a porous medium (sand, intercrystalline or vuggy limestone, fractured basalt, etc.) influencing fluid flow are: Porosity Permeability Thickness Transmissivity Storage Coefficient Water Table or Piezometric Surface Hydraulic Gradient Briefly these parameters can be defined as follows: Porosity: the void space in a unit volume of rock. Permeability: the ease with which fluid will flow through a porous medium. Thickness: the height of the formation which contributes flow to a well. Transmissivity the product of permeability and thickness. Storage Coefficient. the volume of water released from the reservoir per unit drop in head. Water Table or Piezometric Surface: the level at which water will stand in a well: the top of the zone of saturation in a gravity aquifer; the height to which water will rise above the confining bed in an artesian system. Hydraulic Gradient the direction and rate of dip of the water table or piezometric surface. A properly designed pumping test will provide numbers for transmissivity, storage coefficient and the water table or piezometric surface. Drilling records or bore hole logs provide aquifer thickness data from which permeability can be calculated. Ground elevations applied to measured depths to water enable one to calculate the direction and rate of dip of the water table or piezometric surface. Porosity can be determined from core analyses or density logs; it can be estimated from grain size distribution curves in sands or sandstones and from, microscopic examination of drill cuttings derived from carbonate aquifers. CHARACTERISTICS OF FLUID FLOW The characteristics of fluid flow that are vital to an understanding of leach mining include: Velocity Direction Flow Path Radius of Influence The velocity of fluid flow is of paramount importance in planning and managing a leach mine operation. Velocity is directly proportional to the permeability and hydraulic gradient and indirectly proportional to the effective porosity The permeability determined from a pumping test is an average value for the interval stressed; therefore, the velocity calculated from data derived from a pumping test represents average conditions. Under actual conditions discrete portions of the aquifer open to the screen may have permeabilities several times as high as the average and minimum permeabilities only a fraction as much. An injection front will be irregular to the extent that the reservoir rocks are heterogeneous An important consideration is the direct relationship of velocity to head. A reservoir which would provide a velocity of 0.05 feet per day under conditions of equilibrium would allow fluid flow of 36 feet per day under typical leaching operations, i.e. 12-foot injection head, 12-foot pumping level and 50 foot five-spot pattern. The direction of fluid flow is also vital both inside and outside the mine area. In the pattern area the direction of flow is determined by the geometry of the well field and can be approximated by mathematical modeling techniques. Outside the well field, the direction of flow is influenced by both natural conditions and the degree to which production and injection volumes are balanced. Flow directions (and velocities) are critical to an understanding of leachate excursions and their control.

Jan 1, 1979

By Bernard S. Borie

THE U-A1 binary system has been studied by Kaufmann and Gordon.' They have shown that three intermetallic compounds occur in the system: UAl², UAl², and a third compound tentatively identified as UA15. UA1³ is simple cubic, a, = 4.26A. Its unit cell contains one formula weight, and it is iso-morphous with AuCu³. UA1² is face-centered cubic, a, = 7.72A, with eight formula weights per unit cell. Rundle and Wilson have shown that it is iso-morphous with Cu²Mg.² A Debye-Scherrer pattern of the Al-rich compound indicated a more complex structure than either UA1² or UA1³. The following is a report of an investigation of the crystal structure of this compound and a determination of its stoi-chiometric formula. A melt of uranium (99.9 pct pure) and aluminum (99.9 pct pure) was prepared which contained about 25 pct U by weight. It was cooled from 950" to 650°C at a rate of 500" per hr and then taken from the furnace and air cooled. An X-ray diffraction pattern of the ingot showed only lines of aluminum and the Al-rich compound. Filings from the ingot were reacted with a solution of sodium hydroxide, producing a fine black powder, the diffraction pattern of which showed no traces of aluminum. A comparison of the Debye-Scherrer pattern of our sample with the data published by Kaufmann and Gordon1 showed that it is identical with the Al-rich phase which they reported. Single crystals were obtained by cooling the melt more slowly (about 50°C per hr). After reaction with sodium hydroxide, the crystals appeared as small black needles attached to the ingot surface. Cell Size, Space Group, and Uranium Positions A series of Weissenberg photographs for rotation about two of the crystallographic axes, taken with copper radiation filtered through nickel foil, revealed an orthorhombic cell of dimensions: a = 4.41 ± 0.02A b = 6.27 ± 0.02A c = 13.71 ± 0.03A Reflections of the type hkl were observed only if: h + k + I = 2n, of the type hkO only if: h = 2n and k = 2n, of the type h01 only if: h + 1 = 2n, and of the type Okl only if: k + 1=2n. Hence, the cell is body-centered with an 001 glide plane. The evidence for the existence of the glide plane is the observed extinction of 23 possible re- flections of the type hkO with at least one index odd. There are only two space groups consistent with these data: C"" — I2ma and D28 2h — Imma.³ he possible sets of atomic positions for these space groups are: 12ma: (0 0 0; ½ ½ ½) + 4: (a) x 0 %; x % % (b) x ¼ z; x ¾ Z 8: (c) x y z; x y z; x, ½ + y, Z x, M - y, z Imma: (0 0 0; ½ ½ ½) + 4: (a) 0 0 0; 0 ½ 0 (b) 0 0 ½; 0 ½ ½ (c) ¼ ¼ ¼; ¾ ¼ ¼ (d) ¼ ¾ ¾ ; ¾ ¾ % (e) 0 ¾ Z; 0 ¾ z 8: (f) x 0 0; x 0 0; x 1/2 0; x ½ 0 (g) ¼ Y ¼; ¾ Y ¾; ¾ y ¼; 1 y ¼ (h) 0 y z; 0; ;; 0, ½ + y, z; 0, l/2 - Y, Z (i) x 1/4 z; x ¾ z; ¼ z; x ¾ z 16: (j) xy z; x y z; x y z; x y z; x, ½ + y, Z; x,½ - y, z; x, ½ - y, z; 11 1, + y,Z Though density measurements on different samples were found to vary somewhat, they were all within the range 5.7 * 0.3 g per cu cm. If it is assumed that the unit cell contains four formula weights of UAl,, it is 6.5 g per cu cm. If there were as many as eight uranium atoms per unit cell, the

Jan 1, 1952

By W. J. Rogers, L. J. Dwiggins, R. O. Williams

THERE has been comparatively little work on the importance of strain rate and temperature as variables in the formation of deformation textures. For this reason the present work was started, the choice of compression being in part that of convenience and in part because of the absence of quantitative data in this area. These do not turn out to be important variables within the range studied which permits the results to be condensed into this note. Samples 1/4 in. in diam and 1/2 in. long were machined from 99.9 pct pure commercial aluminum and recrystallized to a fine grain size. A set of five samples were deformed between a spring-driven weight and an anvil resulting in roughly 20 pct strain each time. The strain rate varied because of decle-ration and shortening of the sample but would average about 10&apos; per min. Deformation at temperatures over the range of -76" to 150°C were obtained by heating or cooling the samples. Complete lubrication could be obtained by oil since the short time of contact did not permit its escape. The samples were compressed to a total true strain of 1.4 to 1.6. A larger sample was prepared similarly with spiral grooves in the ends to hold paraffin which provided essentially complete lubrication. This sam ple was compressed slowly at room temperature at a rate of about 2 per min to a total strain of 1.0. Cylindrical samples were carefully machined from these discs with a radial direction as an axis. They came from the center half of the samples and were roughly 1/16 in. in diam. The samples were etched down 15 pct to remove any surface effects. Diffraction data were then obtained for six different kinds of planes by the use of the Norton technique as applied to a fiber texture. Direct comparison between the raw data failed to reveal any significant difference between any of the samples and consequently the data from only one sample was completely reduced. The particular sample had been deformed at O°C The background was subtracted from the intensity data which were averaged over the four quadrants and then normalized to random. These data were then used to obtain fiber-axis distribution charts as previously described.2 For this sample the (422) plane was also run to assist in this inversion. The final result, Fig. 1, provided a comparable fit to that previously obtained from fiber data. About 85 pct of the material forms an elliptical texture around the <110> direction. The radius (at half height) is 5.5 deg along the (111) boundary and 8 deg along the (100) boundary. The remaining 15 pct forms a ridge running from this texture to near the <311> direction. The regions around the (100) and (111) planes are devoid of material. The earlier qualitative results of ~arrett~ are in complete agreement with the present results. The possibility has been dis-cused that the material around the <311> results from friction between the sample and compression plates.4 The present results are considered proof that such is not the case because of the uniformity of sample deformation and the requirement of axial symmetry before fiber-axis distribution charts can be accurately obtained. Recently results have been obtained to show that strain rate and temperature are important variables in the extrusion of aluminum.5 Perhaps the most important observation was that the partial recrystal-lization occurred even at room temperature. Strain rate was considered to be a factor only in that it produced a temperature change. There are many differences between the two experiments, the most important possibly being that their material was roughly ten times the purity of the present material. The present experiment, however, may not be as definitive as desired in this respect since it has been shown that compressed aluminum recrystallizes without a texture change6 although supplementary

Jan 1, 1961

By C. R. Simcoe, T. J. Koppenaal

The effect of direct and alternating currents on the quench aging behavior in an Al-4 pct Cu alloy has been investigated by use of resistivity measurements. The reaction rate increases with direct current density in the investigated range of 1000 to 3000 amps per sq cm. Alternating current of a specific frequency is observed to decrease the reaction rate by a factor of about two. ErDMANN-JESNITZER et al.,1,2 investigated the effect of direct and alternating current on the quench and strain aging behavior of low-carbon iron. In both cases they observed that direct current accelerates the aging reaction and that an alternating current can completely inhibit the aging process. The purpose of the present research was to investigate these phenomena in the quench aging behavior of an Al-4 pct Cu alloy and to determine the correlation, if any, between the increase in the observed reaction rate and possible heating effects accompanying the aging with direct current. EXPERIMENTAL PROCEDURE The aluminum-base alloy used in this investigation contained 3.98 wt pct Cu (1.72 at. pct) with impurities of 0.003 pct Si, 0.002 pct Fe, and 0.001 pct Mg. The alloy was rolled into a ribbon about 0.36 mm thick and 3.7 mm wide. The ribbon was split end from end with the ends being used as electrical contacts and the central unsplit section, about 5.3 cm in length, serving as the specimen. Solution treatment was accomplished by quenching from a salt bath at 520° ± 2°C into water at 25° ±0.5°C; the specimen was immediately transferred to a liquid nitrogen bath. All aging was done at 75° ± 0.2°C in a rapidly stirred ethylene glycol bath. Resistivity measurements were made by the double potentio-metric method employing a standard resistor; for purposes of convenience, the resistance measurements were made at 77°K. The transfer of the specimen from the aging bath to a liquid nitrogen dewar was accomplished in less than 1 sec. The aging kinteics were studied with the specimen being aged under the influence of direct current, alternating current, and without any type of current. The amount of heating caused by direct currents was investigated by soldering a thermocouple on the specimen surface and measuring the temperature change after applying various current densities. The temperature was observed to increase (from 75°C, the aging temperature) about 0.8°, 3.0°, and 8.5°C with direct currents of 1000, 2000, and 3000 amp per sq cm, respectively. When employing alternating current, the circuit was monitored with an oscilloscope and adjustments made to produce a normal sine-wave pattern. RESULTS Prior investigations3&apos;4 in the aging characteristics of A1-4 wt pct Cu have shown that the resistivity initially increases, reaches a maximum, and then decreases to values significantly lower than the as-quenched resistivity. This type of behavior is seen in Fig. 1 which shows the resistivity at 77°K as a function of aging time at 75°C observed in this investigation. At this aging temperature, the resistivity maximum is seen to occur in about 1 to 1-1/2 min and it further decreases to the as-quenched value in about 24 min. The behavior observed with the application of direct currents of 1000, 2000, and 3000 amp per sq cm during aging is shown in Fig. 2. With increasing current densities, (+) ?pmax decreases and the rate of the aging process increases. The time necessary to reach the as-quenched resistivity value decreases from 24 min for aging without current to about 16, 10, and 7 min for aging with 1000, 2000, and 3000 amp per sq cm direct current, respectively. Fig. 3 shows the results obtained when two changes were made during the aging with 2000 amp per sq cm

Jan 1, 1963

By T. A. Read, M. W. Burkart

The crystal geometry of the cubic-tetragonal interface after partial transformation of an indium-thallium alloy single crystal is described and a general theory is presented. The effects of applied stresses on this transformation are interpreted and the latent heat of transformation is obtained from observations of transformation under stress. A DIFFUSIONLESS phase transformation between face-centered cubic and face-centered tetragonal structures has been reported for the indium-thallium system by Bowles, Barrett, and Guttman1, 2 The transformation takes place at approximately 105 "C at 18 atomic pct Tl and 25°C at 23 pct Tl. In their study, Bowles, Barrett, and Guttman used poly-crystalline samples whereas in the present study single crystals were used to eliminate the transformation constraints imposed by adjoining grains. The use of single crystals made possible a comprehensive study of the effect of stress on the transformation. In the course of the work, it was possible to formulate a new method of analyzing dif-fusionless transformations (presented in this paper) which permits calculation of the geometry of the interphase interface from a knowledge of the crystal structures of the initial and final phases. The specimens were prepared from chemically pure thallium and 99.97 pct In which were weighed out to produce 3 to 4 grams of alloy of the desired concentration. The metal was placed in clean fused silica tubing, then melted, degassed and sealed under vacuum. (To obtain single crystals, it was found that both degassing and extreme cleanliness were essential.) Single-crystal specimens were grown by a modified Bridgman technique.8 pecimens were removed from the tube by dissolving the quartz in concentrated hydrofluoric acid which attacks the specimen very slowly. The specimen then was polished mechanically to produce four flat surfaces, electropolished, and annealed at 140°C for 48 hr. The electropolishing solution used was that described by Bowles, Barrett, and Guttman and the polishing was carried out on both the high and low temperature phases of the alloy. The high temperature polishing was done at 110°C with a stainless steel cathode. Visual Observation of the Transformation in Single Crystals A visual study of the transformation was made on specimens which had been electropolished in the high temperature phase. The specimens were supported on the stage of a metallograph by an electrically heated holder which contained an opening for observing the specimen. Visual evidence of transformation was found in the presence of an interface which separated the two phases. The interface plane defines the boundary of the phase undergoing transformation and manifests itself by the sharp change in angle between the surface of the specimen and the incident light at the juncture of the two phases. On slow cooling, well-annealed specimens transformed from the face-centered cubic structure to the face-centered tetragonal structure by the motion of a single plane interface which traversed the specimen from one end to the other. Upon heating, the interface moved back in the reverse direction. The interface could be started, stopped, or reversed at will. A temperature hysteresis of about 31/2oC was observed in the reversal of the interface. Holding an interface stationary caused it to disappear completely in most cases, whereas in other instances the interface became less distinct depending upon its orientation. The interface could be made to reappear by changing the temperature of the specimen. The low temperature tetragonal structure exhibits only the fine markings or subbands reported by Bowles, Barrett, and Guttman and is illustrated in Fig. 1. These subbands are twin-related. Back-reflection Laue patterns show the breakup of the cubic spots into pairs of spots corresponding to the twin orientations of the tetragonal phase.

Jan 1, 1954

By C. S. Smith, Chih-Chung Wang

TURNBULL and his collaborators1,2 have developed the theory of homogeneous nucleation as applied, inter alia, to solidification of liquid metals. Vonnegut³ and Turnbull4 have shown that if a liquid metal is subdivided into small droplets a vast majority of them will undercool very considerably before solidification, generally to as low as about 0.8 of the freezing temperature on the absolute scale. The nuclei effective at small degrees of supercooling in bulk metal seem to be internal or surface heterogeneities, relatively small in number. If the metal is subdivided, those droplets that happen to contain such nuclei will solidify at a temperature not greatly below the true freezing point, but only a small part of the whole volume will be affected and the majority of the drops will under-cool to the much lower temperature at which homo- geneous nucleation occurs as a result of fluctuations. It occurred to one of the authors that an appropriate subdivision to give effective freedom from random nuclei is produced during the solidification of many alloys that contain a minor amount of a phase of low melting point, and that one might then expect marked undercooling of the distributed phase. Experimental: The alloys selected for initial study were copper with minor amounts of lead and bismuth, and aluminum with tin. In all these alloys, the major component freezes at a temperature not much below that of the pure metal, and there is little further change in constitution on cooling until the lower melting point constituent freezes in an almost pure state. Cooling curves were taken using the controlled heat flow method permitting approximate specific heats to be obtained. Chromel-alumel thermocouples were used, with the standard emf tables, since extreme precision was not needed. The crucible (3/4 in. id, 5/16 in. wall) was made of B & W K-20 insulating brick. It held about 10 cc of the alloy being investigated. The cooling rate was 2.5" to 2.9°C per min under a controlled temperature difference of 20°. Approximate specific heats were computed from the inverse rate curves together with data from a blank run and from a standard run with a copper cylinder of known heat capacity. The alloys for investigation were made from high-purity metals (99.99+pct) and cast into graphite molds. The castings were machined to fit the crucible and to provide a hole for the inner thermocouple. Cooling curves were taken after heating to a temperature about 50" above the melting point of the minor, lower melting-point, constituent. Results The lead phase in an alloy of copper with 5 pct lead did not undercool more than 3" below the melting point of lead (327°C) either as cast or after annealing to produce a new dispersion of the liquid phase. A copper-zinc-lead alloy with 23.75 pct zinc and 5 pct lead undercooled more but showed no thermal effect below 319°C. A cast alloy of copper with 5 pct bismuth undercooled to 249°C (M.P. bismuth 27l °C), but once solidification started it was completed at the same temperature. This was anticipated, since the bismuth forms a nearly continuous phase between the grains of copper, and a solid crystal nucleated anywhere would rapidly* con- sume the entire network of liquid, unless the physical continuity of the liquid were broken through volume changes, inadequate fluidity, or gas evolution. Similar arguments apply in the case of copper-lead alloys, where the lead-rich liquid forms a network along grain edges, though not grain faces. In both cases there would be a few isolated particles

Jan 1, 1951

By H. C. Chang, N. J. Grant

Creep of very coarse grained high purity aluminum was studied at 400°, 700°, and 1100°F at initial stresses of 50 to 1200 psi. Local strain measurements were made across the grain boundaries and in different regions of various grains during creep, thereby permitting the drawing of component creep curves. The relative amounts of elongation as measured across a grain boundary and in the grains adjacent to the boundary depend on the temperature of testing. The significance of creep curve equations and activation energies is discussed. THIS paper presents some of the results of a research program devoted to the study of the mechanism of creep in high purity aluminum. Previous publications have dealt with the cyclic processes of alternating grain boundary sliding and migration, and the deformation in the grains caused by these processes;&apos; the direction and the driving force of grain boundary sliding and migration;&apos; the deformation in the grains and the restricting effects of the grain boundaries on this deformation." These previous papers were based mainly on either microscopic observations or X-ray data, or both. Sometimes creep curves across two closely spaced reference marks (about 0.6 to 0.7 mm apart) were also presented with a view to correlating the elongation values with the optical observations in general, and with certain deformation processes in particular. These curves shall henceforth be referred to as component creep curves. No attempts were made, however, to compare either the component creep curves which were obtained in different regions of a specimen, or those obtained from different specimens subjected to different creep test conditions. It is the purpose of this paper to present these component creep curves. Among the factors influencing the behaviors of these curves, those studied were stress, temperature, and grain arrangements in the specimens. It is proposed to show how greatly the deformation can vary from grain to grain and within an individual grain in a coarse grained specimen. The experimental technique and procedure have been presented.&apos; It remains necessary to emphasize that the reference marks were produced by pressing a thin sewing needle into the surface of the specimen before the final annealing at 900°F for 24 hr and at 1150°F for 12 hr. The cold work around the needle indentations was therefore removed. The depth of these holes after electropolishing the annealed specimens was about 0.01 mm. This depth and area were negligible in comparison with the thickness of the specimens, 2.3 mm, and hence would not affect the creep behavior. Results Fig. 1 shows a development diagram of specimen P-8. The dots on the surface locate the needle point reference marks used to obtain the component creep curves. A curve obtained between two dots across a grain boundary measures not only the boundary deformation but also the deformation associated with boundary sliding occurring in the grains in the region between these indents. The original distance between two reference marks was about 0.6 to 0.7 mm. The maximum error of measurement was 0.01 mm, or in terms of percentage elongation, of the order of & 1.5 pct. Whereas the component creep curves shown in the figures to follow were drawn as a gross average of the points, in view of the fineness of some of the steps of grain boundary sliding and migration, as shown in the previous publications,¹,2 it appears logical to expect that some of the finer cycles of movement have not been delineated for the strain sensitivity of the measuring system. It seems justifiable to say that the curves are not as smooth as shown. 700°F Tests: Fig. 2 shows component creep curves across four of the grain boundaries in specimen P-8, tested at 700°F and 85 psi. These curves clearly show alternate cycles of increasing and decreasing

Jan 1, 1954

By L. S. Reid, Irwin Politziner F. M. Townsend

Recently published data indicate that the water vapor content of a gas, as determined by dew point measurement, is inaccurate when the gas has been dehydrated with diethylene glycol. Water vapor contents and dew point measurements of gases dehydrated with triethylene glycol have been obtained in this investigation in order to determine the magnitude of a similar error, if one exists. Experimental data show a very low concentration of triethylene glycol vapor in gases dehydrated at atmospheric ternperatures and pressures ranging from 500 to 2,500 psia and that the accuracy of dew point measurements is not impaired by the presence of triethylene glycol vapor. INTRODUCTION Nearly all natural gas transported by pipe line to northern and eastern markets must be dehydrated to a low residual moisture content in order to assure maximum transmission efficiency and continuous delivery under peak load conditions. Without dehydration, water vapor often condenses in pipe lines in quantities sufficient to restrict the flow3 and. under low atmospheric temperature conditions, gas hydrates may form and plug gathering. transmission and distribution facilities. Gas may be dehydrated to pipe line specifications by a number of methods. The most widely used methods are (1) adsorption of water vapor on a solid dessicant such as activated bauxite, alumina or silica gel,&apos; (2) by absorption of water vapor by either diethylene or triethylene glycol-water solutions of high glycol concentration,11,13 and (3) by simultaneous expansion-refrigeration of very high pressure gas in which gas hydrates are purposely formed and then quickly decomposed.&apos;"" Of these three fundamental methods, the adsorption and absorption processes provide the bulk of the dehydrated gas moving to market at the present time. The expansion-refrigeration process. a relatively new development, is gaining in favor because of its simplicity but is sharply limited in its application by available differentials between source and gathering system pressures. Where gas sale or purchase contracts contain a maximum water vapor content specification, the water vapor content is usually determined by measuring the dew point of the gas at system pressure. Knowing he dew point temperature and the system pressure, the water vapor content of the gas is determined from a graphical correlation of saturation, or dew point, temperature us the water vapor content of the gas which is customarily expressed as pounds of water vapor per million cubic feet of gas measured at 14.7 psia and 60°F. Dew points are usually measured with the U. S. Bureau of Mines Dew Point Tester. shown in Fig. 1, which is well suited for use at temperatures lower than 120°F and at pressurei; ranging from atmospheric to 3,000 psi. A number of correlations of dew point temperatures vs water vapor content are available,3,5,15 the most recent of which is that by McCarthy et al.4 Where natural gas is dehydrated by absorhing contact with concentrated diethylene glycol-water solutions. considerable difficulty is experienced in observing water dew points due to condensation of liquid hydrocarbon and glycol films on the mirrored surface of the dew point tester. Riesenfeld and Frazierl2 report that the dew point method for determining the water vapor content of a dietllylene glycol-treated natural gas is in error due to the glycol content of the condensate formed on the tester mirror, and that the water vapor content of the gas tested is actually lower than that indicated by the standard&apos; dew point-water vapor content correlation. Extensive experience in testing gases dehydrated by concentrated triethylene glycol-water solutions lias not revesled difficulties of the nature cited above for diethylene glycol. Water dew points are clear and sharp and condensation of

Jan 1, 1951

By T. L. Joseph

S. T. Killian (Johnstown, Pa.)—This is one of the finest papers I have read. Tying in stoichiometric calculations with furnace performance and practice is a step which had to be taken sooner or later. The noteworthy difference between Dr. Joseph&apos;s type of calculations and regular blast furnace calculations is that the Ib mol system is used as a basis. With the Ib mol system, weights, volumes, and chemical reactions can all be expressed in the same equation. In the paper, wind, ore, flux, and fuel are all expressed as lb or lb mols. Probably Dr. Joseph does not realize it, but the vague word coke appears only twice in the entire paper. Lb of C and Ib mols of C are followed through reactions but the word coke appears only as 1560 lb coke per ton of pig and 1700 lb of coke per ton of iron. Obviously in order to understand furnace reactions, the coke should be expressed as lb or lb mols of C. Furnaces can also be compared more easily. In some respects the paper is too thorough and too complete. The effects of the metalloids reduced into the iron upon the top gases represents a difference of less than 3 pct of the CO formed in the bosh. Due to the completeness of the calculations in relation to the CO/CO2 ratio, this was included and was necessary. However, the exclusion might have enabled more furnace men to follow the lb mol system of calculations through the blast furnace to a better degree. By considering only irons of similar analysis, this part of the calculations might have been omitted. However, if this had been done, total rewriting of the paper later would have been necessary in order to make the work complete as it is now. It also would not have been nearly as authoritative. In the paper, there appears the reaction: H2O + CO ? CO2 + H2 [I] Dr. Joseph states that he did not take this reaction into consideration in any calculations pertaining directly to the paper. The piobable reason- for this is that although it contains all the main reacting top gases except N2, it is rather inflexible since it is monomolecular in relation to each of the reacting gases and does not tie in with the gasification of C. Actually the reactions: H2O + C ? CO + H2 [2] 2H2O + C ? CO2 + H2 [31 and the solution loss reaction: CO2 + c ? 2c0 [41 tend to assume an equilibrium through the reaction: H2O + CO ? CO2 + H2 [I] which should be considered a balancing or equilibrium reaction. Reactions 2, 3 and 4 permit furnace conditions to balance with the CO/CO2 ratio and H2 formation. They tie in with the solution loss. Reaction 1 unites them chemically. Probably the best calculation to make at this time would be to try to find the relative importance of the CO2 from the flux and the H2 in the dilution on an actual furnace gas analysis. For this purpose the Dob-scha-Carnegie-Illinois paper—"Effect of Sized and Sintered Mesabi Iron Ores On Blast Furnace Performance" is chosen. This paper was presented before the blast furnace section of the AIME in 1948. This represents the best large scale furnace operation available to me. Unfortunately the changes were brought about by beneficiation of the burden and not by changes on one burden. In choosing the basis for the calculation in relation to the furnace, 100 mols of dry top sgas is chosen. This leaves something to be desired inasmuch as the nitrogen basis is changing but I believe it will be better understood than any other type and it is the easiest to use.

Jan 1, 1952

By E. S. Mardock, Robert E. Bush

The object of this paper is to report recent developments in the quantitative interpretation of radioactivity logs. The use of reference lines is described in the application of the new zero radioactivity reference line for the determination of neutron derived porosities is discussed. Illustrated examples are shown of logs from the reef limestone of the North Snyder Field and from the Lansing-Kansas City limestone of central Kansas. A method of using an interrelation factor calculated from the neutron and gamma ray curves, called the neutron Productivity number, for the estimation of productivity from sandstone formations is discussed. When used in a relative manner the neutron productivity number has aided in Predicting whether a given zone will produce gas or liquid or whether it is too shaly to produce. Examples of logs from wells in the Freites District, Venezuela, and in East Texas are shown to illustrate the application of the neutron productivitv number. INTRODUCTION The petroleum industry was introduced to some of the preliminary results of investigations into the quantitative interpretation of radioactivity logs in October, 1949." It was stated at that time that the methods presented were entirely relative because they involved the use of reference points obtained from the radioactivity log, i.e., shale reference lines, dense zone reference lines, or a combination of both shale and dense zone reference lines. These relative methods offered many advantages to the industry in interpreting radioactivity logs in terms of porosity with particular application to limestone and dolomite reservoirs. However, these relative methods did not offer the wide range of applicability desired because the esta1)lishment of reliable reference points from shale in some areas were difficult. It was recognized that a more reliable mean; of establishing reference lines was vitally needed. Such a method is now available through the introduction of an instrumeutal zero device. It is the purpose of this paper to discuss the application of this new zero reference to the quantitative interpretation of radioactivity logs. Previously all applications of quantitative interpretations of radioactivity logs have been made in limestone reservoirs with little or no emphasis placed on sandstone reservoirs. A brief resumé of investigations into the quantitative interpretation of radioactivity logs in sandstone reservoirs is presented here. This discussion deals primarily with the interrelation of the gamma ray and neutron curves and the response of the latter to the density of the fluids filling the pore space in relatively homogeneous sandstones of uniform porosity. The authors believe that the methods presented herein are only applicable locally to specific fields and reservoirs, and that they probably do not offer a wide range of applicability. However, tile authors believe that the wider use of the new instrumental zero references in sand areas will reveal more information about the specific response of the gamma ray and neutron curves to changes in lithology and saturation. Two applications of quantitative interpretation using the new instrumental zero references are presented. Examples are given which show the comparison of logs and porosity in the limestones and dolomites of West Texas and Kansas. Logs of wells in &apos;Venezuela and East Texas are compared with the drill stem test data, production data, etc.. to illurtrate the interrelation of the gamma ray and neutron curve: and the rise of methods involving these interrelations to determine certain saturation variables. THE QUANTITATIVE APPLICATION OF RADIOACTIVITY LOGS TO LIMESTONE AND DOLOMITE RESERVOIRS Tile theoretical basis for the gamma ray and neutron curves has been discussed elsewhere.9 he method of recording the logs and apparatus involved has also been thoroughly covered and will not be discussed here.&apos;."".&apos;" It has been shown that the neutron curve responds exponentially to liquid filled porosity over the 1 1/2 to 35 per cent

Jan 1, 1951

By Milton F. Goodrich

The idea of using water-only cyclones to scalp clean coal from the feed to other devices has recently been gaining in popularity. 1,2,6 An indication of this popularity is that water-only cyclone scalping is already employed in a few commercial plants. Water-only cyclones scalp the feed to a heavy media vessel in the Warwick plant,3 to Deister tables in the Rowland plant,4 and to a heavy media cyclone circuit in the Amherst Coal Company&apos;s McGregor plant.5 Despite this trend, we found surprisingly little information in the literature on the performance of water-only cyclone scalping. Therefore, we undertook a study of its technical merits, limiting our investigation to a water-only cyclone scalper in conjunction with heavy-media cyclones. We felt this to be a reasonable combination of equipment, since both processes operate well on the same size coal. First, we developed simple mathematical relationships revealing general characteristics of the system. Next, we compared the clean coal yield and quality obtainable by the system on four different coals with that obtainable by heavymedia cyclone circuit alone and water-only cyclones middlings recirculation circuit alone. This was done by using computer program to simulate the operation of the three systems. Finally, we considered the effect that implementation of the system would have on a typical preparation plant circuit. The System The system chosen for study [(shown schematically in Fig. 1)] comprises two stages: a primary stage (PI) consisting of water-only cyclones, and a secondary stage (P2) consisting of heavy media cyclones. The water-only cyclones separate raw coal at a low specific gravity, producing a relatively small amount of high quality clean coal and a refuse containing much good coal. This refuse is then recleaned in the secondary stage, where the sharper separation of heavy media cyclones, operated at a higher specific gravity, reclaims additional clean coal. Finally, the clean coal from both stages is combined as the system&apos;s clean coal, while the refuse from the secondary stage becomes the system&apos;s refuse output. Theoretical Analysis Two assumptions lie behind the following theoretical analysis. The first assumption is that partition curves can represent not only the performance of each stage but also the performance of the system as a whole. These curves show partition number as a function of specific gravity, where partition number is either the percent or fraction of a raw coal with a given specific gravity reporting to clean coal. The second assumption is that these curves are independent of the raw coal characteristics. At any specific gravity the system&apos;s partition number is solely a function of the partition numbers of each stage. For convenience, we use the following variables in describing this relationship: g = specific gravity, PS(g) = the partition number of the system at specific gravity g, P1(g) = the partition number of the primary stage at specific gravity g, P2(g) = the partition number of the secondary stage at a specific gravity g. For this system, we can show algebraically that the relationship is: [Ps (g) = PI (g) + (1- P1(g)) P2 (9)(1)] With this equation the system&apos;s partition curve can be determined if the partition curves of each stage are known. By definition, the partition numbers P1(g) and P2(g) must each be less than, or equal to, one. Placing these constraints on Eq. (1), we arrive at the relations: [Ps(g) % P1(g) and Ps(g) % P2(g)(2)] Thus, at any specific gravity the system&apos;s partition number is always greater than that of both stages. [Figure 2] shows typical partition curves. Curve I represents the primary stage, which consists of water-only cyclones operating at a separating gravity of 1.3. (The separating gravity or the

Jan 1, 1979

By W. M. Myers

Certain minerals possess inherent color and other properties that make them suitable for the pigmentation of paints, mortar, plaster, concrete, face brick, and other materials. Their production is one of the most ancient of mineral industries and their use by primitive man is well known. These natural pigments have some economic factors in their favor, particularly wide geographic distribution, low cost of production, ease of preparation, chemical stability, and permanence in use so that they continue to form the basis of a small but useful industry. When used in paints such pigments act as a filler and supply body and opacity in addition to color. Natural mineral pigments are prepared for the market by the comparatively simple operations of washing, grinding, blending, and calcining. Any one, or all of these processes may be applied to a single pigment. The development of synthetic pigments and the use of byproduct materials have introduced competition with the products of nature and are having a growing influence on the economic position of the mined minerals. Development of the Industry The industry developed to commercial stature in Pennsylvania largely because of the presence of beds of ocher extending from Easton in a southwesterly direction toward Reading, and a variety of small iron mines in the region. The mining of paint ores in the Lehigh Valley was active as early as 1850 and shortly after the Civil War the establishment of mills expanded production and led to the development of new products and eventually the manufacture of synthetic pigments. Pennsylvania continues to maintain it.s leadership as a producer of mineral colors. Production is recorded also in New Jersey, Illinois, Virginia, Ohio, and Georgia. Iron as a Pigment Iron in various compounds is the most important pigment in nature. The iron pigments are characterized by stability, light fastness, good covering power, high index of refraction, and economy in production. Ferrous compounds display a typical green coloration. This has not been employed as a commercial pigment to any great extent except incidentally in such greenstones as have been used in construction, or crushed and sized for application as a granule to roofing. Ferric oxides are characteristically red and form an important group of industrial pignents. Hydrated ferric oxides exhibit various shades of yellow and are present in such familiar pigments as ocher and sienna. The addition of small amounts of manganese oxide or carbon as organic matter to the yellows produces the brown umbers. Magnetite is one of the few black minerals that grinds to a black powder. The mineral pigments vary from earth colors of low intensity and great dilution of iron content to almost pure iron compounds with high tinting strength and correspondingly greater value. There has been some relationship between the mining of iron ores and the production of mineral pigments; although the production of colors is not carried on appreciably as a byproduct of iron mining. A number of mineral pigment producers, particularly in the eastern states, have operated mines which in the past were small producers of hematite, bog ore, or carbonate ore. The knowledge of the location of the deposit and its possibilities as a producer of pigment are due to its past history as a producer of metallic ore. Many iron compounds may be changed in color by calcination, the end product being Fe2O3, a stable red oxide. The yellow hydrated oxides may be changed to red. The gray carbonate, found in Carbon County, Pa., calcines to a fine red product. Ferrous sulphate (copperas) often available in tonnage as a byproduct of the steel industry, breaks down under heat or chemical action leaving a residual red oxide. Pigments produced by calcination or dissassociation of compounds possess the advantage of fine particle size and ease of grinding. Mineral Pigments MINERAL BLACKS Many black minerals grind to a light colored powder. This characteristic is familiar to the mineralogist as the white streak produced by a black

Jan 1, 1950