By D. Mills, G. B. Craig

ZIRCONIUM has been float-zone-refined in an electron-beam furnace and the redistribution of oxygen, iron, and tungsten has been measured. The iodide zirconium used in the present experiments initially contained both oxygen and iron in the range 100 to 200 ppm by weight, and tungsten in amounts less than 10 ppm. Float-zone refining of zirconium, using induction heating, has previously been attempted by Kneip and Betterton1 and Langeron.2 Kneip and Betterton were primarily interested in the removal of iron and nickel. They achieved some purification, with respect to both these elements, in material given up to six passes at 150 mm per hr under an argon atmosphere. Langeron reported purification for a large number of elements after four completed passes in a static vacuum system operating at pressures less than 10-6 mm of Hg and with rates of zone travel between 30 and 40 mm per hr. He did not report oxygen concentrations, but stated that there was inverse segregation of this element. westlake5 has also used a minimum of four zone passes to remove iron from zirconium. No rates or conditions were given. Belk6 has shown that tungsten contamination can occur during electron-beam melting. He reported an increase from 0.01 to 0.05 pct by weight tungsten in molybdenum after four complete zone passes. The vacuum system for the electron-beam unit used in the present investigation consisted of a single-stage rotary pump backing a liquid-air-trapped oil-diffusion pump. A pressure of less than 10-8 mm of Hg was obtained with Dow-Corning 705 fluid in the diffusion pump. In order to avoid contamination of the zirconium by evaporation from the tungsten filament, a special focusing cage4 was employed. Three rates of zone travel, 114, 38, and 4 mm per hr, were investigated, with the liquid zone moving from the bottom to the top of the bar. The bars used were 3 mm diam and the total melted length was 130 mm. Oxygen was analyzed by neutron-activation analysis using a neutron flux of 10' neutrons per sq cm per sec to form the isotope N16 by the 016 (n,p) N16 reaction. The standard deviation is quoted for each oxygen determination. The iron and tungsten analyses were performed spectrographically, and the precision is estimated to be ±6 pct. Analyses for tungsten were all below the detectable limit of 10 ppm, confirming the protection given by the focusing cage. No significant redistribution of oxygen was found at the two higher rates of zone travel. The redistribution of oxygen and iron obtained after five passes at a rate of zone travel of 4 mm per hr (1.1 x 10-4 cm per sec) is recorded in Tables I and 11. Burris, Stockman, and Dillon3 have estimated the distribution of solutes during multipass zone refining. Using their curves for an effective distribution coefficient of Keff = 1.5 and 2 for oxygen and Keff = 0.3 for iron, the expected concentrations were estimated for the present material. These are shown in Tables I and 11, along with the experimentally measured values. The calculated concentrations are based on a molten-zone length of 10 pct of the total melted length, whereas in the present experiments the molten zone was approximately 5 pct of the total melted length. The effect of zone length on solute redistribution is most pronounced after a large number of zone passes. Comparison with Pfann's published data8 for solute redistribution for various Keff's and zone lengths indicates only small differences at low numbers of completed zone passes. It is evident that the expected distribution has not been realized in the case of iron. Scrapings of material deposited on the inner surfaces of the electron-focusing cage were found to be magnetic. It is, therefore, concluded that redistribution of iron is masked by evaporation. Deposition of iron inside the focusing cage was observed at all rates of zone travel. The results of the investigation may be summarized as follows: 1) Segregation of oxygen is typical for a solute with a distribution coefficient, Keff > 1. 2) No redistribution of oxygen takes place at high rates of zone travel. 3) The distribution coefficient for oxygen lies between 1.5 and 2.0. 4) Purification with respect to iron occurs mainly by evaporation. 5) The focusing cage is effective in preventing tungsten contamination.

Jan 1, 1967

By David W. James, Howard Jones, George M. Leak

Conditions are described for producing, by primary recrystallization, a matrix suitable for the growth of large grains near (110)[001] orientation in silicon iron strip by secondary recrystallizaliun in a steep temperature gradient. The orientation distribution of these large grains is expressed in terms of rotational deviations about the cross-rolling direction, the rolling direction, and the normal to the sheet, the deviational spread increasing in that order. With the aid of cowplenientary published data on the orientation dependence of growth rate, it is shown that this observation is consistent with the oriented-growth theory of recrystallization lextures. It is conclutled that growth-rate and orientation-distribution data obtained in a steep thermal gradient should be used with caution to account for isothermally Produced recrystallization textures. SEVERAL authors have reported methods of growing large grains by re crystallization of a small-grained matrix in silicon iron 1- B and pure a cr The present study was a preliminary in the growth of single crystals and bicrystals for surface relaxation," grain boundary mobility, and grain boundary diffusion studies. The method was to control the growth of a seed crystal into a suitable primary re crystallized matrix by feeding through a steep temperature gradient. The driving energy for growth derived from the grain boundary energy released as the seed crystals grew into the matrix. Thus, stability of the matrix against normal grain growth was considered to be essential for success. It was known that the manganese sulfide dispersion present in commercial silicon iron performs this function during secondary recrystallization to the (110)[001.] texture.12 Hence commercial, rather than high-purity, material was used throughout. The paper describes the growth conditions for grains large enough to be used as seed crystals for further growth into single crystals. The orientation distribution of the seed crystals is analyzed and its significance for the theory of recrystallization textures is discussed. EXPERIMENTAL PROCEDURE Strip material was supplied by the Steel Co. of Wales, Ltd. The chemical analysis in weight percent was Si, 2.90; C, 0.015; Mn, 0.059; P, 0.011; S, 0.027; Ni, 0.032; 0, 0.009; Fe, balance. A gradient furnace of similar design to one described previously4 was loaned from B.I.S.R.A. It consisted essentially of a vertical water-cooled copper slot projecting downwards into the hot zone of a molybdenum furnace. Hydrogen was passed through the furnace to protect both heating element and specimen from oxidation. Strip specimens up to 8 cm wide and 0.2 cm thick were sealed into the furnace at the mouth of the copper slot. A coating of light oil on the strip surface maintained the seal during translation of a specimen. The maximum temperature gradient in the region just below the copper slot was 500°C per cm over 1 cm, with the hottest point controlled at 1175°C. Several large grains would usually grow by secondary recrystallization from the primary matrix when a specimen was immersed in the hot zone for about 30 min. A back-reflection X-ray camera was constructed to facilitate rapid and accurate orientation determinations of the large grains produced. It was possible to reproduce a standard geometry, with regard to strip and camera, without the tedium of careful alignment on each occasion. Specimens, typically 4 cm wide and 75 cm long, were cut with the longitudinal axis parallel to the rolling direction of the original strip. The surfaces were cleaned by immersion alternately in a hot aqueous solution containing 2 pct hydrofluoric acid plus 10 pct sulfuric acid and in cold 10 pct nitric acid. The nitric acid etch was just sufficient to reveal the grain structure. Rolling and annealing treatments to prepare the matrix (discussed below) were followed by growth of seed crystals in the gradient furnace. The matrix was transformed to a single crystal by growth of a selected seed crystal connected to the matrix by a thin neck. 4,5 Growth was promoted by controlled feeding into the gradient furnace. Several single crystals of controlled orientation were grown successfully from seed crystals by twisting the interconnecting neck in a reorien-tation jig.4 EXPERIMENTAL RESULTS AND DISCUSSION Growth Conditions. A suitable matrix for growth of large grains was prepared starting from primary re-crystallized strip 1.9 mm thick. This was cold-rolled in two stages each being followed by a recrystallization anneal at 800°C for a few minutes. Such treatment gave the required growth matrix only if the two cold-reduction stages were each performed in several passes and in the following ranges: the first, 30 to 70 pct; the second, 10 to 50 pct. Immersion in the temperature gradient otherwise resulted in an equiaxed

Jan 1, 1967

By D. L. Creighton, S. A. Hoenig

The field-emission microscope has been adapted for the study of microcrack growth during the early stages of fracture in metal wires. Cracks as small as 6 1 in length can be detected and their growth can be followed to specimen failure. The system is quite useful in searching for microcracks since only sharp-edged surface defects will emit electrons under the experimental conditions. THE conditions leading to brittle fracture were discussed a number of years ago by Griffith1 and the term Griffith Cracks is often used for the small surface cracks which are responsible for brittle fracture. Griffith's theory has been modified by stroh2 and more recent results on metals are discussed by Allen,3 pp. 123-40. At present the phenomenon is not completely understood but there is general agreement that at least in certain materials the sequence leading to brittle fracture involves several stages. The initial microcracks are present because of cooling or working stresses, Hahn et al.,3 p. 95. When a stress is applied to the specimen the cracks grow slowly until the release of stored elastic energy is large enough to accelerate the crack and provide the necessary surface energy for crack growth. At this point the growth rate appears to increase rapidly to some new equilibrium velocity, and failure occurs. Since the microcracks are usually about the size of a single metallic grain (Ref. 3, p. 99) it is not easy to find them and it is very difficult to follow their growth under stress. This paper will report on the use of a cylindrical field-emission microscope for observation of the formation and growth of microcracks. I) THE FIELD-EMISSION MICROSCOPE The field-emission microscope (FEM) has a high magnification and resolution and is almost uniquely suited for observations of microcracks. Since the FEM is relatively new as a metallurgical instrument, a short description will be given here. Normally metals at room temperature do not emit electrons; however in the presence of a strong electric-field gradient, electrons can tunnel out through the reduced potential barrier. Since this tunneling is a function of the local field gradient and the local work function, the emitted electrons can be used to produce a highly magnified image of the surface by allowing them to strike a phosphor screen. Because the electron emission is dependent upon the local field gradient, smooth surfaces emit few electrons except at very high fields. On the other hand cracks, extrusions, or other surface defects, having sharp edges, emit strongly since the field gradient is very high in the vicinity of these defects. This indicates that the FEM should be most useful for detection of microcracks on otherwise smooth surfaces. A field-emission microscope was first used by Muller4 in 1936 for observation of metal surfaces, and recent reviews have been given by Muller5 and Gomer.6 The instrument has been used for metallurgical studies in the area of surface diffusion,= recrystallization,7 and grain growth 8 (Ref. 8 is directed specifically at metallurgists). In the work of Muller4,5 and Gomer 6 the specimen was in the form of a sharp metal point at the center of a phosphor-coated glais sphere. The impact of the emitted electrons on the phosphor produced a highly magnified image of the specimens. Such a system is not practical for applying a controlled stress to the specimen and a cylindrical geometry has been used in this investigation. This allowed the application of a controlled tensile stress to the wire specimen. Normally a cylindrical FEM geometry produces magnification only in the radial direction. This is the case because a smooth wire at the center of a cylinder produces a purely radial electrical field. However, if there is a break in the smooth surface of the inner cylinder, the field near the break becomes three-dimensional and the area of the break is highly magnified. The reason for this is clear if it is recalled that the field gradient depends on the relative radii of the inner and outer cylinders; if a crack forms, its edge radii are of atomic dimensions and a very high field gradient is formed near these crack edges. Since the electrons receive most of their acceleration near the crack edge and are always traveling perpendicular to the field lines, they tend to spread out and produce the magnified image observed in the cylindrical field-emission microscope. 11) BRITTLE-FRACTURE STUDIES A) Experimental Apparatus. The geometrical arrangement chosen was that used earlier by Gifford

Jan 1, 1965

By A. H. Larson, L. G. Twidwell

The influence which Au, Ag, Sb, Bi, Sn, and Cu have, both individually and collectively, on the activity coefficient of sulfur in liquid lead at 600"C zuas studied by circulating a H2S-Hz gas wlixture over a specific lead alloy until equilibrium was attained. Subsequently, the H2S concentration in the equilibrium gas mixture and sulfur concentration in the condensed phase were deterruined. The elements gold, silver, and antinzony (above 8 at. pct) increased the activity coefficient of sulfur. Bismuth had no apparent effect. Tin (above 3 at. pct) and copper decreased the coefficient. The influence of an individual element, i, on sulfur is best reported as the interaction parameter, riS, which is defined as The values o these first-order interaction zus are: ESzu = —55.0. These interaction parameters are used to predict the activity coefficient of sulfur in six fouv-component alloys and one seven-component alloy. Comparisons are made with direct experimental determinations. INTERACTIONS in dilute solution have been studied by many investigators. Most of the experimental work has been confined to solute-solvent interactions in simple binary systems and solute-solute interactions in ternary systems. Dealy and pehlke"~ have summarized the available literature on activity coefficients at infinite dilution in nonferrous binary alloys and have calculated from published data the values for interaction parameters in dilute nonferrous alloys. Interaction parameters are a convenient means of summarizing the effect of one solute species on another in a given solvent. Only a few investigators have studied interactions of the nonmetallic element sulfur in a metallic solvent. They are as follows: Rosenqvist,~ sulfur in silver; Rosenqvist and Cox,4 sulfur in steel; chipman, sulfur in alloy steels; Alcock and Richardson,% ulfur in copper alloys; Cheng and Alcock,' sulfur in iron, cobalt, and nickel; Cheng and ~lcock,' sulfur in lead and tin. The only reported work on the Pb-S system in the dilute-solution region is that of Cheng and Alcock.' Their investigation involved a study of the solubility of sulfur in liquid lead over the temperature range 500" to 680°C. The results may be summarized by the following relationship: S (dissolved in lead) + Pb(1) = PbS(s) log at. %S = -3388/T + 3.511 Experimentally, it was found that Henry's law was valid up to the solubility limit of sulfur in lead, i.e., at 600°C up to 0.43 pct. Their investigation did not include the study of sulfur in lead alloys. More accurate calculations could be made in smelting and refining systems if activity coefficients of solute species could be accurately predicted in complex solutions. One of the objectives of this study was to compare the experimental data with the values calculated from the equations derived from models for dilute solutions proposed by wagner9 and Alcock and Richardson. A temperature of 600°C was chosen as the experimental temperature to attain reasonable reaction rates and to minimize volatilization of the condensed phase. EXPERIMENTAL Materials. The Pb, Au, Ag, Sb, Bi, Sn, and Cu used for preparation of the alloys were American Smelting and Refining Co. research-grade materials. All were 99.999+ pct purity except the antimony and tin which were 99.99+ pct. The initial alloys prepared for this study consisted of twenty-one binary alloys, eleven ternary alloys, and one six-component alloy. The constituent elements were mixed for each desired alloy and were placed in a crucible machined from spectrographically pure graphite. The crucible was placed in a vycor tube which was evacuated with a vacuum pump and gettered by titanium sponge at 800°C for 8 to 12 hr. After the gettering was completed, the chamber containing the titanium was sealed and removed. The remaining sample chamber was placed in a tube furnace at 800°C for 2 hr and quenched in cold water. The final operation consisted of homogenization of the alloy for 1 to 2 weeks at a temperature just below the solidus for the individual system. The resulting master alloys were sectioned into small pieces and a random choice made for individual equilibrations. Cobalt sulfide (Cogs8) used to control the gas atmosphere in the circulation system was prepared by passing dried HzS for 24 hr over a Co-S mixture heated to 700°C in a tube furnace. This material was then mixed with cobalt metal to give a two-phase mixture which, when heated in hydrogen to a particular temperature, produced a desired H2S/H2 gas atmosphere in the circulation system. A Cu2S-Cu mixture also used in this study was prepared in a comparable manner. Apparatus for Equilibrium Measurements. The experimental technique of this study required apparatus

Jan 1, 1967

By S. Nakajima, H. Okazaki

Quantitatiue studies of the deformation texture in drawn tungsten wives were made by the X-vay dif-fractottletetr. Experimental results show that the diffraction Intensities are equal to tilose pvedicted from the (1 10). fiber lexlure but the angxla), spreads of. diffraction peaks in the pole distribution curres are different for different diffraction planes and directions. For this reason a modified (110) fiber lextuve model, in which a kind of anisotropy is assumed, is proposed to explain the results. According to this model the poles lying on a line directing front the (110) to the (110) poles in the (1 10) standard stereograpllic projection should show spreads which are different from those lyitlg on a line directing from the (001) to the (001) poles, which is confirmed by the experiments. The anisolvopy and the spveads of the pole positions are large at the outer part of the wires and decrease gradually lowards the inside of the wire. The possibilily of occurrence of such anisolropy in irrelals with fcc stvuctures is discltssed. THE deformation texture of drawn tungsten wires has been assumed by different investigators to be the simple ( 110) fiber texture.' Recently, however, Leber2,3 has shown that a swaged tungsten rod has a cylindrical texture. It changes gradually to the (110) fiber texture by drawing through dies. However, even after drawing to 0.25 mm in diam, the cylindrical texture can still be found in wires together with the (110) fiber texture. This was deduced from the pole figures obtained from the longitudinal section of these wires. Use was made also of quantitative measurements of the pole distribution curves. Leber stated that the angular spread of the pole distribution curves (henceforward called dispersions) are quite different for (400) 45 deg and (400) 90 deg: the former is always larger than the latter. This inequality is accompanied by deviations of the diffraction intensities from the theoretical values for the ( 110) fiber texture. Bhandary and cullity4 have reported similar results on iron wire and explained them by assuming a cylindrical texture. Both Leber3 and Bhandary4 used only the results of the (400) reflection for the determination of the dispersion. The pole figures found by Leber3 and by Rieck5 are largely different. The model given by Leber to explain the effects is in the authors' opinion in some respects unsatisfactory, especially if one looks at other than the (400) reflections. Intensities and dispersions of diffraction peaks are conclusive factors for the determination of the fine structure in wire textures. For this reason we studied them extensively to come to a model which is more suitable to fit the facts. In the following, after giving the experimental set-up, we report about measurements of X-ray diffraction on drawn tungsten wires. Different models to describe the experimental results will be discussed. EXPERIMENTAL GO-SiO2-A12O3 doped tungsten wires drawn to 0.18 mm in diam were used for the measurements. The wires were chemically etched to various diameters down to 0.03 mm. Measurements were carried out for the different wires in order to determine the dependence of the texture on the radius. The wires were cut to pieces of 10 mm length and fixed with paste closely against each other on a flat, polished glass plate. Parallelism of the wires with the surface of the glass plate should be adequate. For the diffraction studies three different X-ray sources were applied, respectively, giving the CuK,, FeK,, and FeKp emission. The measurements were carried out with a diffrac-tometer with a GM counter. The latter was fixed to a certain diffraction angle 20hkl and the diffraction intensity was recorded as a function of the angle of rotation of the specimen around the axis, lying in the specimen surface and perpendicular to the wire axis, as shown in Fig. 1. Measurements were also done with the detector at angles slightly deviating from the diffraction maxima The measured intensities in this case were taken to be equal to the background level. The deviations were chosen as small as possible but large enough to eliminate the influence of the diffraction maxima. The useful range of the rotation angle x of the specimen is generally limited by the wavelength of the X-rays. We have: where and cp is the angle between the wire axis and the normal of the diffraction plane. Intensity measurements were made to find the necessary corrections for counting loss of the GM counter and for distortion resulting from such effects as absorption of X-rays and from inclination of the reflection plane under study with respect to the surface of the specimen. The counting loss was esti-

Jan 1, 1968

By R. L. Ash, R. R. Rollins, C. J. Konya

An investigation was performed to determine conditions for optimizing the spacing of simultaneously initiated multiple explosive columns. This was done by using models of mortar, dolomite, and Plexiglas with 10-grain mild detonating fuse as the explosive charge. It was desired to simulate blastholes with multiple primers initiated by detonating fuse or when high-velocity explosives are used in low-velocity materials. It was found that optimum spacing between multiple charges was strongly influenced by charge length. At less than optimum charge length, the spacing at which complete shearing was possible between adjacent charges decreased exponentially with a subsequent loss of broken material volume. For charges fired simultaneously, larger burdens and spacings were possible as compared to those necessary for single-crater charges. For each material studied, there was a characteristic optimum charge length and a maximum attainable spacing at any given burden. Proper selection of the spacing distance between charges is fundamental to successful blasting. Its value directly affects the cost of drilling and explosives used per unit of broken material. In addition, the choice of a spacing that is Compatible with a given set of blasting conditions aids in the control of fragmentation sizing, ground vibrations, overbreak, and throw which in turn, influence other production costs. For example, normally loaded blastholes that are spaced too closely invariably promote overbreak and usually give coarse fragmentation. Unless care is taken, airblast and violent flyrock will occur and under certain conditions cutoffs and misfires may result. Too large a spacing, on the other hand, frequently leads to conditions that form bootlegs or toes. The choice of a particular spacicg to use, however, is largely a matter of individual experience and judgment, usually based on trial and error. Very little is known or can be found in the literature with regard to how the spacing between charges is related to field conditions and charge geometry. As a general rule, the firing time sequence of adjacent charges and properties of a material are thought to have the most significant influence on the spacing distance best suited for any given field condition. For example, delayed initiation of adjacent charges usually always requires a closer spacing than when charges are fired at the same time. This should be expected if one considers that the energy normally dissipated and lost in the surrounding ground from charges fired independently would be captured and utilized for breaking material between charges when they are initiated together. Spacing can be extended also when charges are aligned with structural planes of a material, such as jointing, along which shearing is relatively easy. It is customary to relate the spacing (S) between charges to their common burden (B) in the form of a spacing ratio, or SIB. The burden normally is considered as the optimum depth or distance from any single charge perpendicular to the nearest free or open face at which the desired fragmentation and maximum crater yield are obtained. For production blasting, value of the ratio is generally considered to vary from 1 to 2, depending on conditions.1-6 When adjacent charges are fired independent of one another, the value varies from 1 to about 1.4, the closer amount being employed to square corners or produce craters having the ideal 90" apex angle. The larger ratio is the geometric balance value for craters having an apex angle of 135". The basic ideal crater forms in the plane of the charge diameter for charges fired independently are shown in Fig. 1. In the event charges are fired simultaneously, geometric balance in the plane of their charge diameters suggests that a spacing ratio near 2 would be appropriate, as illustrated by Fig. 2. In practice, however, some compromise ratio value must be selected to conform with the specific ground conditions. An example would be where the jointing planes tend to produce 60° or 120° crater angles, the appropriate geometrically balanced charge arrangement being given by Fig. 3. In this condition, the spacing ratio is 1.15, not 1 or 1.4 as suggested for the 90° cratering of independently fired adjacent charges. In view of the foregoing, it would seem logical to assume that whenever charges all having the same burden are fired at the same time, spacing distances always can be greater than those permitted by charges fired independently. In practice this is not the case, however.

Jan 1, 1970

By W. R. Hansen, F. W. Boulger

Twenty-nine laboratory steels were studied to determine the effects of composition and ferrite grain size on drop-weight and Charpy V-notch transition temperatures. The experimental steels covered the following ranges in composition.. 0.10 to 0.32 pct C, 0.30 to 1.31 pct Mn, 0.02 to 0.43 pct Si, md nil to 0.136 pct acid-soluble Al. Although most of the data were obtained on hot-rolled samples, some plates were heat-treated in order to cover a wider range in ferrite grain size. The experimental data were used for a multiple-correlation analysis conducted with the aid of an electronic computer. The study showed that carbon raises and that manganese, silicon, aluminum, and finer ferrite grains lower both drop-weight and Charpy transition temperatures. Quantitatively, variations in composition and grain size have a more marked effect on V15 Charpy transition temperatures than on the drop-weight transition temperature. Useful correlations were found between transition temperatures in drop-weight tests and those defined by seven different criteria for Charpy tests. Evidence was accumulated that the conditions ordinarily used for drop-weight tests are more severe for 1-1/4-in. -thick plate than for 5/8- to 1-in. -thickplate. PROJECT SR-151, to study quantitatively the effects of metallurgical variables on performance in the drop-weight test, was established by the Ship Structure Committee late in 1958 on recommendation of the National Academy of Sciences, National Research Council. This project was initiated as a result of the increasing use of the drop-weight (nil-ductility) test in predicting the ductile-to-brittle behavior of steel. Qualitative data indicated the drop-weight was not as sensitive to metallurgical variables as the Charpy V-notch test. Furthermore, the available information indicated that the drop-weight test did not show the superiority of killed steels over semikilled steels reflected by Charpy tests. This difference in sensitivity to brittle fracture is considered important because the drop-weight transition temperature has been reported1 to correlate better with service-temperature failures than the V-notch test does at a constant energy level. Therefore, this project was concerned with establishing quantitatively the effects of metallurgical variables in the drop-weight test. For comparison, Charpy V-notch data were obtained for the steels investigated. This paper summarizes the results of the investigation. Most of the steels used for the study were made and processed in the laboratory. However, some tests were also made on commercial killed steels available from Project SR-139 (SSC-141). During the course of the investigation, data were obtained on the effects of carbon, silicon, manganese, and aluminum on transition temperatures of drop-weight and Charpy specimens. In addition, the effects of heat treatment which changed the ferrite grain size and the transition temperatures were also investigated. Finally a few exploratory studies were made on commercial killed steels to evaluate the effects of plate thickness, grain size, and heat treatment on the performance of drop-weight specimens. EXPERIMENTAL PROCEDURES Preparation of Materials. A total of twenty-nine 500-lb induction-furnace heats were made and processed in the laboratory for the investigation. Carbon, manganese, silicon, and aluminum contents were systematically varied. Melting and rolling techniques proven satisfactory in a previous project2 were used as a guide for the current investigation. Composition. The composition of the twenty-nine laboratory heats made for this project are given in Table I. The steels are divided into three groups. The first group consists of ten aluminum-killed steels similar in composition to Class C ship-plate steel. The second group consists of ten semikilled or Class B type steels. In both of these groups the carbon and manganese contents were intentionally varied over a wide range. This wide range in composition was helpful in obtaining quantitative data from a limited number of steels. The primary purposes of these two groups of steels was to determine the effects of carbon, manganese, and deoxidation practice. In addition, one steel in each group (Steels 2-2 and 9-2) were made about 1 year after the start of the program in order to check consistency of melting practice. The third group of nine steels listed in Table I was intended for studies on the effects of silicon and aluminum. In eight of these steels carbon and manganese were held relatively constant at levels of about 0.2 and 0.8 pct, respectively, while silicon and

Jan 1, 1963

By John M. Kelly

This report covers the development, exploratory drilling, and production of oil and gas in New Mexico during 1945. The statistical information was gathered from state regulatory agencies and other sources believed to be reliable; it is presented here in combined form for general information only, and the author assumes no responsibility for its accuracy or completeness.

Jan 1, 1946

By J. Szekely, Robert G. Lee

Calculations are presented for the prediction of the combined radiative-convective heat loss from molten steel held in a ladle, covered by initially molten slag. A mathematical formulation is given and numerical solutions are presented of the resultant partial differential equation. It is shown that a slag layer of about 2 to 3 in. thick would prevent any significant heat loss from the top metal surface for Periods of up to 1 hr. For thinner slag layers (or in the absence of the protective slag) appreciable heat losses would occur; plots given in the paper allow the quantitative evaluation of the fall in the metal temperature due to this heat loss. The ironmaking-steel processing operation involves several intermediate steps where the molten metal is held or transfered in ladles. The quantitative assessment of the heat losses occurring under these conditions is of considerable importance in process design considerations since the temperature of the metal may have to meet rigid specifications in any given part of the processing sequence. While the metal is held in a ladle, heat is lost by two mechanisms: i) by conduction into the ladle walls; ii) by radiation and convection from the top surface. Calculations relating to the conductive heat loss, are readily made and information may be found in the literature both on data pertaining to metallurgical situations and on the techniques that are available for performing additional computations.'-3 The evaluation of the combined convective-radiative heat loss is less straightforward, especially when there exists a protective slag layer covering the metal. In this latter case, as the top slag surface loses heat partial solidification may occur and the latent heat thus given up by the slag may represent an effective barrier to the heat loss from the metal. A semiquantitative assessment of the role played by the slag in preventing heat loss from the metal has been made in a previous paper,4 where it was shown that a slag layer 6 in. thick would act as a near-perfect insulator for periods of up to 2 hr. However, this first paper reported on an essentially preliminary investigation that considered only one slag layer thickness; furthermore, the boundary conditions used for the calculations were somewhat restrictive since no allowance was made for changes in the metal temperature. The purpose of this second paper is to extend the scope of the preliminary investigation previously reported by: i) considering several slag layer thicknesses; ii) allowing for variations in the metal temperature; and finally iii) by performing calculations on the net loss from the metal rather than from the slag surface. FORMULATION Consider a slag phase extending from y = 0 to y = L1, covering a metal phase that occupies the region extending from y = Ll to y = L, as illustrated in Fig. 1. Denote the slag and metal temperatures by TS and Tm and assume that initially both slag and metal are molten, having a uniform temperature Ti. At time = zero the surface represented by the y = 0 plane (top slag surface) is brought into contact with cold air, the temperature of which is given as T Thus for time > zero, heat will be transfered from the slag to the air by natural convection and thermal radiation; as a result of this heat loss the slag temperature will fall and after some time a solid phase is formed and a solidification boundary (more realistically described as a zone) will move progressively from y = 0 toward y = L1. Once the region of temperature gradients, moving ahead of the solidification zone, reach the slag-metal interface (y = L1) there will be a net transfer of heat from the metal through the slag to the cold air, across the y = 0 plane. In the formulation of moving boundary problems, involving phase changes that require computer solution, it is convenient to represent both phases by a single equation, making allowance for the latent heat of solidification by assigning an appropriate temperature dependence to the specific heat content. Thus the energy equation for the whole of the slag may be written as follows:

Jan 1, 1969

By E. S. Machlin

The wzodel of Blandin and Diplunt;, generalized to include a phase factor, is applied to the carbon-carbon interaction in iron. Darken&apos;s "energetic" model is generalized to include not only first neighbor interactions but further neighbor interactions as well. On the bases of these generalized models relations are derived for the activity of carbon in both austenite and ferrite in terms of the carbon-carbon Pair interaction energies. A single function then yields the pair interaction energies consistent with the experimental activities of carbon in both ferrite and austenite. Thus, a simple explanation is given for the observation that the nearest-neighbor interaction between carbon is repulsive in austenite and attractive in ferrite. Certain consequences of this approach are explored. OnE object of the present paper is to attempt to take into account the consequences of electrostatic contributions to the carbon-carbon pair interaction energy for carbon as a solute in iron. Friedel&apos; has shown that oscillations in electrostatic potential are to be expected about a solute atom in a metallic solution. Blandin and 6lant6&apos; have shown that such oscillations yield an interaction energy between pairs of solute atoms that obeys the relation: W{ = A cos(2ftFri + 4>)/(kFri)3 [l] where kF = Fermi wave vector, ri = distance between solute atoms comprising the pair7 <p = phase factor dependent only on electronic nature of solute and solvent, A = coefficient dependent only on electronic nature of solute and solvent. Machlin3 found that Eq. [I] accurately described the pair interaction energy derived from short-range order measurements based on field ion microscope observations of dilute alloys of platinum. He also found that the value of the phase factor $ derived from residual resistivity measurements agreed well with that obtained from the analysis of the short-range order data. Harrison and paskin4 were able to predict the long-range ordering energy of 0 brass using Relation [I] and residual resistivity values to predict the value of the phase factor $. Machlin5 has repeated their analysis and applied it to the prediction of the long-range ordering energy in AgZn and AgCd with excellent agreement between prediction and experiment. Both A and $ are independent of the crystal structure. The Fermi wave vector depends uniquely upon the conduction electron concentration per unit volume in the spherical approximation of the Fermi surface. Thus, Eq. [I] is expected to apply to both fer- rite and austenite with only one set of values of A and $. Mossbauer studies6 yield the result that iron has one 4s electron. We shall make an assumption found to hold previously for platinum3&apos;7 and nikel, which is that only the s electrons are involved in shielding the perturbing potential of carbon. With this assumption, kF = 1.35 A-l. Although A and $ may be obtained from certain mdels&apos;&apos;&apos; we shall take A and $ to be empirical constants in the spirit of Kohn and osko.&apos; Thus, Eq. [I] involves two adjustible parameters. Consequently, two independent relations in A and $I are required in order to evaluate them for carbon as a solute in iron. We may use a recent analysis of Aaronson, Domain, and poundg who showed that Darken&apos;s energetic model,1° as well as others, can be used to describe the activity-temperature data for carbon in iron in both the aus-tenitic and ferritic phases. Darken&apos;s model takes into account only first neighbor pair interactions. For our needs, all neighbor pairs need to be taken into account. It is convenient to generalize Darken&apos;s model. The result for the partition function for austenite is: over the temperature range 800" to 1200°C and where the uncertainty corresponds to one standard deviation. Eq. [4] effectively yields only one relation. Another relation is required to obtain unique values for A and $. One property of Eq. [4] is that it is independent of crystal structure. Hence, data for a iron can be used to obtain another relation. To arrive at this relation we must generalize Eqs. [2] and [3] so that they may be applied to the bcc a iron. The result is that:

Jan 1, 1969

By Dale A. Vaughan, Oliver M. Stewart, Charles M. Schwartz

A. U. Seybolt (General Electric Research Laboratory)—The authors should be commended for adding some important information to our knowledge of the solubility of interstitial elements in metals. It is becoming increasingly evident that the effect of even traces of such elements have very far-reaching effects upon the mechanical properties of the body centered cubic metals. Those who have worked in this area know that the accurate determination of the small solid solubility limits in systems of the type reported by the authors is a quite difficult task, and it is therefore not surprising that frequently the results of different workers are not in agreement. It is instructive, and usually helpful, to plot the solubility results on log weight or atomic percent -1/T coordinates to find out if a straight line is obtained. A straight line is expected because in systems displaying solubilities of the order of 1 to 3 at. pet or less, Henry&apos;s law is usually obeyed—or at least well enough obeyed so that the deviation from linearity is not very appreciable. If Henry&apos;s law is obeyed, one canthen use the Van&apos;t Hoff Equation in the form In N = ?H/RT + C, where N is mole fraction, at. pet, or wt pet for small values, and AH is the partial molal heat of solution of the solute. R and T have the usual significance, and C is an integration constant. If one plots the reported nitrogen solubility values as indicated above, the three points fall reasonably well on a straight line. The oxygen values for the two upper temperatures fall very closely to the nitrogen values as shown in the authors&apos; Fig. 15. However, the value at 500°C departs widely from the straight line established by the data at 1500" and 1000°C. It is, of course, true that one cannot place too much emphasis on the significance of a line established by only three points, but in the absence of reasons for anticipating deviations, data exhibiting wide departures from linearity should at least be examined closely. Fig. 16 shows the log at. pct -1/T plots for the authors Ta-O and Ta-Ndata including a solid circle point at 500°C and 1.8 at. pet for Ta-O, which is simply extrapolated from the two higher temperature points. In addition, the data of R. P. Elliott9 for Nb-O are shown. These points were picked off his curve and are not very exact, but as can be seen they line up well on a straight line. It is interesting, and probably significant, that the slope of Elliott&apos;s results is not far from those of Vaughn, et al. This is probably to be expected because one would anticipate that the partial molal heats of solution of oxyten in these two very similar metals should be not too far apart. AH for Ta-O is about -1900 cal per mol, while for Nb-O it is near -2300 cal per mol. Hence, this lends some support to the thesis that the point at 500°C for Ta-O is much too high. The data of Gebhardt and Preisedanz10 are also plotted, and it is seen that their data while lying on a linear plot, have an appreciably steeper slope. The possible reasons for this will not be discussed here except to point out that their pressure-composition data show anomalies which suggest that they may have been dealing with a different equilibrium from that being discussed. There is another consideration which would also suggest that the solubility at 500°C is lower than shown. The solubility values were obtained by the classic method of first establishing a lattice parameter-composition curve. This the authors did, and there is probably little doubt that it is quite accurate. Such a plot is generally almost error-free because it has a self-correcting feature in that any deviation from linearity makes a data point immediately suspect, and subject to confirmation. Unfortunately, this is not true with respect to the actual solubility values. These are obtained ordinarily by taking an alloy containing more solute than is soluble at some temperature and then thermally

Jan 1, 1962

By Harold M. Mooney

WHEN apparent resistivity data are taken with the symmetrical Wenner 4-electrode spread, a fixed center position is used and readings are taken for values of electrode separation. Basic data consist of apparent resistivity plotted against separation of adjacent electrodes . The interpreter attempts to infer geologic structure, such as the depth to discontinuities and the nature of subsurface earth materials. An earlier paper&apos; described methods for interpreting resistivity data. All of these involve a severe assumption, namely that the earth in the region of interest consists of horizontal layers, electrically homogeneous and isotropic. The actual earth never satisfies this assumption exactly and may deviate from it so much that none of the above methods can be applied. Attempts in three directions have been made to modify the assumption so that it approaches known geologic complexity more closely. First, curves have been calculated for dipping discontinuities. Stern&apos; and Aldredge hose a few widely separated dip angles. Trudu confined his attention to small dips. Berel&apos;kovskiy and Zubanov computed gradient curves for widely separated dip angles. Unz as given the most complete solution, with a brief attempt to treat the three-layer case. Second, anisotropy can be taken into account. It seems geologically probable that layered materials have different vertical and horizontal conductivities. Cagniard, Maillet, and Pirson et up methods for finding an equivalent hypothetical isotropic medium. Standard interpretation methods can be applied to this, and the actual medium can then be deduced. Belluigi&apos;" discounts the practical importance of anisotropy; Geneslay and Rouget do not agree with his conclusion. Third, the effect of variable resistivity in a layer can be considered. Keck and Colby" examine the mathematics of an exponential increase in a surface layer. Several authors, for example, Stevenson,&apos;&apos; consider a continuous variation of resistivity with depth. The present paper deals with a linear variation of resistivity in a surface layer. Geologically, surface variations should be expected. Unconsolidated materials such as glacial drift show marked irregularities over short distances. The effects of weathering change with depth. The moisture content of material above the water table may vary from a dry sand to a saturated clay, and both of these will be changed by rainfall. Figs. 1 to 6 present apparent resistivity curves to show the effect of a variable surface layer. In all cases resistivity varies linearly with depth down to a depth of one unit. Material beneath this depth has constant resistivity. Electrode separation is plotted in depth units. Insets on each figure show the corresponding cross-sections, plotting true resistivity against depth. To illustrate, consider curve A of Fig. 1. The true resistivity of material at the surface of the earth is taken as 0.4 units. Resistivity increases with depth, reaching a value of 1.0 at 0.5 depth units and 1.6 at 1.0 depth units. Below a depth of 1.0, all the material has very low resistivity (zero, for purposes of calculation). Curve A in the main part of Fig. 1 shows how apparent resistivity varies for this case as the electrode spacing is increased. To illustrate further, curve E of Fig. 4 corresponds to true resistivity of 1.2 units at the surface, 1.0 at a depth of 0.5 units, 0.8 at a depth of 1.0, and 1.5 for all depths greater than 1.0. Apparent resistivity curves have been plotted logarithmically so that the shape of the curves becomes independent of the units, giving the curves wide validity. A certain drift-covered area, for example, shows a gradual decrease of resistivity from 230 ohm-meters at the surface to 150 ohm-meters at the bedrock surface, 275 ft down; bedrock resistivity is 800 ohm-meters. Curve E of Fig. 5 indicates that true resistivity decreases from 1.2 units at the surface to 0.8 at a depth of 1.0, then increases abruptly to a constant value of 4.0 units. Since resistivity and depth ratios are the same, this can be used to predict the field curve. For Fig. 5, multiply true resistivity and apparent resistivity by

Jan 1, 1955

By Elton A. Youngberg

The Holden mine operated by the Chelan Division of the Howe Sound Co. is on the east slope of the Cascade Range in north central Washington on the south slope of Railroad Creek valley at an elevation of 3500 ft. The mine may be reached by a 40 mile boat trip from the town of Chelan which is at the southern tip of Lake Chelan, to Lucerne at the mouth of Railroad Creek and an 11. mile bus ride up Railroad Creek to Holden. A11 freight and concentrate is moved over this route to Chelan Falls on the Columbia River which is on the railroad four miles below the town of Chelan. The mine is now producing 2000 tons of gold, copper, and zinc ore per day which is treated in the Holden mill. Gold-copper and zinc concentrates are made, the first of which is shipped to Tacoma, Wash., and the latter to Kellogg, Idaho, for smelting. Ore is broken by long-hole blasting using the Noranda system which has been modified to meet local conditions. Until recently, blastholes have been drilled by diamond drills. Now a partial substitution of percussion drill holes, drilled with tungsten carbide insert bits, is being made. Geology The ore body occurs as a replacement deposit in a highly metamorphosed series of sedimentary rocks, mainly gneiss and schists, in a shear zone several hundred feet in width and of undetermined length. Commercial ore has been found in mineable widths of 25 to 100 ft for approximately 2500 ft along its strike. The commercial minerals are chalcopyrite, sphalerite, and gold. During the period of mineralization considerable silicifica-tion took place giving the ore an abrasive drilling characteristic. Following the period of mineralization, numerous dikes were introduced into the ore body. The earlier ones were of granite composition having a width of a few inches up to 80 ft. These were followed by much younger, fine grained basic dikes which usually do not exceed 2 ft in width. Development of Percussion Blasthole Drilling Equipment Test work with the 1½-in. tungsten carbide bit was carried on in development headings for several months early in 1947. The short life of the bits, because of gauge loss caused by the abrasive nature of the rock, prevented its adoption for this use. However fast drilling speed and ability to drill a long uniform hole suggested its use for drilling blastholes in competition with diamond drills as diamond costs were steadily increasing and exper-ienced drillers were difficult to obtain. The 1½-in. bit was the largest available at the time initial test work was started with sectional steel. The 1½-in. hole limited the diameter of the steel thread and coupling which could be used. Type F couplings were first used but because of the small thread section excessive breakage of the steel was experienced. Type H couplings were tried next. In order to use this coupling which is 15/8 in. in outside diameter, it was reduced to 1 3/8 in. giving 1/8 in. clearance between the coupling and the hole. Rod breakage at the thread was substantially reduced but some coupling breakage was experienced, however the overall performance was considered satisfactory (see Fig 1 for illustration of coupling and thread). Early test work with the 1½ in. bit indicated machines of piston diameters larger than 255 in. would cause inserts to loosen or break. It was found however that the additional weight of the sectional steel cushioned the blow enough to prevent bit failures when 3-in. Leyners were used. Rods used with the 1½-in. bits were 7/8 in. q. o. for sectional steel and 1 in. q. o. for all chuck pieces. In May 1948, 2-in. tungsten carbide bits became available and test work was immediately started. The 2-in. hole approximated the AX (1 15/16 in.) diamond drill hole which was being used exclusively for blastholes and permitted their substitution for diamond drill holes in a ring without alteration of pattern, burden, or explosives. The 2-in. bit also gave room in the hole for larger couplings and permitted the use of heavier rods and 3½-in. machines, increasing the

Jan 1, 1950

By W. D. Ludemann, J. E. Dor, L. A. Shepard

Recovery of the creep resistance of 99.99 pct pure Al was studied at temperatures 540°, 573°, 600°, and 611°K. Poly-crystalline specimens crept under a stress of 950 psi to a strain of 5.5 pct were allowed to recover for periods of from 1 min to 16 days under a residual stress of 4.4 psi. Increased creep rates upon reapplication of the 950 psi stress evidenced softening of the material. The activation energy for the recovery process was found to be 64,000 cal-per mol. THREE major observations have clearly revealed that the creep of polycrystalline aluminum above about 510°K is controlled by the rate of climb of jogged edge components of dislocations past the barriers impeding their motion: 1) Extensive polygonization, characteristic of climb, takes place during creep.&apos;9&apos; 2) The activation energy for creep equals the estimated activation for self-diffusion. 3) The stress law for creep coincides with theoretical predictions based on the climb mechanism.4,5 The decreasing rate during the primary stage of creep must be ascribed to the introduction of additional barriers to the glide of dislocations. During secondary creep the density of barriers must remain constant, the rate at which new barriers are formed being equal to the rate at which they recover. For this reason the nature of the barriers, and their rates of formation and recovery, are significant to a complete understanding of creep. It is proposed here to study the kinetics of the recovery of barriers to creep of high-purity polycrystalline aluminum in the climb range. The technique will consist of creeping a series of tensile specimens under a prescribed stress to given state following which the specimens will be recovered for various times and temperatures under approximately zero stress. The amount of recovery will be determined by comparing creep curves following the recovery. EXPERIMENTAL PROCEDURE The material used for this investigation was a 99.99 pct pure Al supplied by the Aluminum Co. of America in sheets of 0.001-in. thickness having an H-18 temper. The spectroscopic analysis of impurities gave Cu-0.004 wt pct, Fe-0.002 pct, Si-0.001 pct, others-0.000 pct. Creep specimens were machined with their tensile axes in the rolling direction of the sheets. Annealing in a molten potassium nitrate-potassium nitrite bath for 1 hr at 686K, followed by air-cooling, resulted in a grain diameter of from 0.22 to 0.27 mm. Creep machines were equipped with constant stress lever arms of the type suggested by Fullman, Carreker, and Fishher,&apos; which maintained the applied stress to within 0.04 pct of the reported value of 950 psi. Creep strains were calculated from extensions over a 6-in. gage section to the nearest 3 X 10"5. The temperatures of testing, 540°, 573", 600°, and 611°K, were obtained by immersing the specimen and extensometer assembly in a molten KNO2-KNO3 bath. Temperatures during the periods of creeping could be maintained constant to within better than ± 1°K. Correlation of creep data at different temperatures of testing demanded the use of an appropriate temperature-compensated time 8. Previous investigations have shown that the creep of pure metals at temperatures above about 0.55 of their melting temperatures can be correlated by the functional relationship3" e=f(0), s= const. [1] where e = total plastic strain during creep f = a function that depends on stress a = stress 6 = te-Q/RT = a temperature-compensated time t = time under test Q = 35,500 cal per mol = activation energy for creep R = gas constant, and T = absolute temperature In the present series of tests all of the creep was conducted under the same stress of 950 psi. To provide identical initial conditions for the recovery all specimens were first crept to a temperature-compensated time of = 47 X 10-14 min which resulted in a creep strain of 0.055 + 0.005 regardless of the creep temperature. During recovery, a small stress (4.4 psi) was permitted to remain upon the specimens to maintain tautness in the pulling assembly and to prevent mechanical damage to the soft specimen. After each recovery period, the full stress was reapplied and

Jan 1, 1961

By G. J. Heuer, J. N. Dew, G. C. Clark

The effect on well behavior of partial permeability barriers, changes in producing rates and well spacings have been calculated through use of a radial, unsteady-state, two-phase-flow mathematical model. This model allows for variations in permeabilities and porosities with distance from the wellbore. The numerical methods necessary to solve the problem require use of a highspeed digital computer, in this case an IBM 704. In each instance, pressure and saturation gradients, gas-oil ratios and recoveries around a well producing by solution-gas drive have been calculated as a function of time and distance from the wellbore. Comparisons are made to show the effect of changes in producing rate and of varying permeability near the wellbore and out in the formation on the production and pressure history of the well. The effect of different well spacings on producing rate and ultimate recovery is considered. Although the mathematical description of the reservoir is simplified in comparison to an actual reservoir, the results do give some insight into the difficult problem of spacing and proration in a heterogeneous solution-gas-drive reservoir. Results show that for the cases considered spacing has little effect on ultimate recovery and that permeability barriers removed from the well decrease producing rate for a period of time but have only a small effect on ultimate production. INTRODUCTION The effect of spacing and producing rate on the production characteristics and ultimate recovery of a well producing by the solution-gas-drive mechanism have been topics of interest to the oil industry for many years and the subject of many hearings before state regulatory bodies. The problem is very complicated because of the difficulty of simulating in the laboratory a reservoir producing by the solution-gas-drive mechanism under anything like normal field conditions. This paper gives the initial results of a study aimed at determining the effect of these factors on production from reservoirs simulated by a mathematical model. Two-phase, unsteady-state equations are used to calculate pressures, saturations, and rates of oil and gas flow as a function of time and distance from the wellbore. The model is radial, and reservoir properties may be varied with distance from the wellbore. A decrease in permeability at a given distance results in a low-permeability ring concentric with the wellbore through which all the fluids from more distant portions of the reservoir must flow. The current mathematical model allows for variation of permeability, porosity and saturations as a function of distance from the well. Any desired drainage radius for the well may be selected. Drainage radii of 745 and 1,053 ft, which correspond to 40- and 80-acre spacing, were chosen for the calculations which follow. A large amount of the input data has been held constant. No investigation was made into the effect of changes in fluid properties and relative permeability characteristics on oil and gas production behavior. Fluid properties and relative permeabilities are essentially those of the White Mesa portion of the Greater Aneth area in southeastern Utah. A recently concluded hearing before the Utah Oil and Gas Conservation Commission to determine spacing for the field aroused interest in the possible effect of permeability constrictions located some distance from the well on production and recovery. This interest stimulated the present study. In this paper, no attempt has been made to simulate any field production characteristics exactly. Only the solution-gas-drive mechanism has been investigated, and production by liquid expansion has not been considered. This investigation is exploratory in nature but does give some insight into the problems of spacing and proration in a solution-gas-drive field having permeability variations. THE MATHEMATICAL MODEL The mathematical model is similar to that proposed by West, Garvin and Sheldon.&apos; Approximately the same techniques have been used in arriving at a solution. The equations are nonlinear, partial differential equations which have been known for some time. The particular equations used for this study neglect the effects of capillary pressure and gravitational forces. The advent of modern digital computing equipment has made their solution practical. Basically, the method solves for pressure, saturations, and oil and gas flow rates as a function of distance and time. In our model, distance to the

By J. E. Owen

A model of a porous body is presented in which the pore space consists of a system of voids and interconnecting tubes. Relationships between porosity and resistivity formation factor are determined partly by calculation, partly by experiment. Con triction effects characteristic of the model are shown to be sufficient to account for high formation factors. It is shown that constriction may be combined with moderate amounts of tortuosity to give model pore systems exhibiting to a first approximation porosity and resistivity properties similiar to those of natural porous bodies. INTRODUCTION The relationship between the electric resistivity of a fluid-filled porous body and the geometry of its pore space is so complex that the calculation of the resistivity of a natural porous rock is a practical impossibility. Both the resistivity of a body and its porosity are measurable quantities, however, and previous successes at relating them have been reached by an empirical approach. Efforts at obtaining theoretically derived formulae relating them have generally been unsatisfactory. One of the reasons for this may lie in the pore geometry that has been assumed. THE TORTUOSITY CONCEPT A Parameter called the formation factor is useful in dis-cussing the resistivity of a fluid-filled porous body. This parameter is the ratio of the resistivity of a fluid saturated porous body to the resistivity of the saturating fluid. Formation factors are often available from measurements on cores or from electric logs, and many attempts have been made to correlate formation factors and porosities of geological formations. Whenever a successful correlation is found, the engineer working with electrical logs has a useful tool for the determination of porsities of pay section?. One of the more successful formulae applicable to these correlations is the familiar equation empirically obtained by Archie.&apos; which F is the formation factor. $ is the porosity, and rn is an exponent called the cementation factor. When the for- mula applies, the cementation factor usually is found to be between 1.3 and 2.2. The values for formation factors experimentally obtained are often higher than simple pore geometry would lead one to expect. In an effort to account for such high values certain formulae have been derived based on a so-called "tortuosity concept." In deriving these formulae a synthetic porous body is usually assumed in which the solid material is an electrical non-conductor. and in which the pore system consists of three sets of fluid-filled tubes of uniform diameter connecting opposite faces of the body which, for convenience, is considered to be cubical in shape. The three sets of tubes account for the whole of the effective porosity of the body, and usually, it is specified that they do not interconnect. By considering that the pore tubes are not straight but tortuous, their resistance to the flow of electric currents can be made as high as needed to explain high formation factors. Such an explanation has some basis in fact, but it appears that the tortuosity concept is often incorrectly applied when other factors are largely responsible for observed high resistivities. Recently, Wyllie and Spangler have recognized that tortuosity as calculated by conventional formulae has little if any physical significance.&apos; RESISTIVITY AND THE CONSTRICTION CONCEPT Any explanation of high formation factors which depends solely on tortuosity of uniform pore paths necessarily ignores the effect that variations in the cross-sectional area of the conducting paths have on the resistivity of a body. Although, as previously pointed out, the calculation of such paths for an actual body is impossible, it will he shown that a synthetic pore network can be devised which will yield to analysis, and lead to results in agreement with the experimental data represented by Equation (1). The porous body to be considered is assumed to be homogeneous and isotropic or, for present purposes, identical in its characteristics in the three directions parallel to its coordinate axes. It will he assumed to be built of identical unit cubes, each of which contains a single pore network connecting all faces of the unit cube. A unit of such a pore network is shown

Jan 1, 1952

By F. O. Jones

The capabilities of small proportions of divalent cations, such as calcium or magnesium, for controlling clay blocking are reported. Potentially sensitive formations can be exposed to fresh water if at least one-tenth of the salts dissolved in both the native water and invading fresh water are calcium and magnesium salts. Often, even less suffices. The behavior evidently depends upon the cation exchange properties of the clays, which favor adsorption of calcium and magnesium over sodium. Clays having sufficient adsorbed calcium and magnesium resist dispersion by water and consequent blocking of permeability. An allied phenomenon, the dependency of clay blocking on salinity contrast, is also reported. Abrupt change from highly saline to fresh water can cause blocking which may not occur if salinity is lowered slowly. A process related to osmosis is thought responsible for this behavior. Applications of findings to drilling, fracturing and water flooding are discussed. INTRODUCTION Many formations, when exposed to fresh water, can lose permeability through clay effects.&apos;,&apos; For example, drilling-mud filtrate can cause oil permeability decreases, which persist long enough to interfere with drill-stem testing and well completion.3 Ultimate productivity may suffer when clay damage is severe, especially if drawdown pressures are low.&apos; The injection pressures and the time required for water flooding can increase if clay blocking occurs. Earlier work indicates that clay blocking is caused by obstruction of flow channels by clays or other mineral fines dispersed by fresh water.&apos;!" It is well known that increasing salt concentrations in water tends to prevent clay blocking. Also it is well established, although perhaps not as widely known, that the nature of the dissolved solids is also important. If, for instance, formation clays are exposed to calcium chloride solution and then exposed to weaker solutions of calcium chloride or distilled water, considerably less permeability damage results than if the clays had been exposed instead to sodium chloride solutions. The reasons for this behavior are: (1) clays are cation-exchange, or base-exchange, materials similar in this respect to zeolites or exchange resins, and (2) clays in the calcium form do not disperse easily in fresh water, whereas clays in the sodium form do. The base-exchange form of a clay is easily altered by flowing a solution through it. For example, a sodium clay can be changed to a calcium clay simply by passing a calcium chloride solution through the clay bed. There is general agreement that the reason calcium and magnesium clays do not disperse easily in fresh water is because the calcium ions do not ionize easily from the clay surfaces.&apos; Sodium clays, however, are believed to allow the sodium ions to ionize from the clay particle surfaces. In fresh water, this allows the particle to accumulate a net negative electrical charge great enough for the particles to repel one another and, therefore, disperse more easily. The foregoing suggests that, even in the presence of a large excess of sodium, a relatively small ratio of divalent cation, such as calcium or magnesium, might serve to prevent clay dispersion. The divalent ion probably adsorbs to a disproportionately large extent, because of being adsorbed more tightly, with the result that the proportion of divalent cation on the exchange positions of the clay might then be great enough for the clays to resist dispersion. Consequently, an investigation was conducted to find how mixtures of salts in solution influence clay blocking. APPARATUS AND PROCEDURE Water permeability tests were conducted using conventional techniques. The equipment is illustrated schematically in Fig. 1. Flow rates of solutions driven through small core samples at known temperatures and pressures were measured. Regulated compressed air, usually at 10 to 15 psig, was used to drive the solutions. Core samples 0.75 in. in diameter and 1 in. long were used for the most part. Cores were saturated by evacuating and then admitting a de-aerated solution. Tight core samples were first saturated with carbon dioxide gas and then evacuated and saturated with the test solution. After saturation, 140 psig pressure was imposed for several hours. Cores were tested to insure absence of gas saturation by a Boyle&apos;s

Jan 1, 1965

By D. E. Wolfson, D. A. Reynolds, F. W. Smith

IN 1948 the U. S. Bureau of Mines began a three-phase program to evaluate the extent and quality of U. S. coking coal: 1) a factual appraisal of known recoverable reserves in beds of mineable thickness, 2) a study of preparation characteristics, and 3) a study of carbonization properties. A previous paper presented the methods used in assessing reserves.&apos; Although this investigation is only partly completed, data on coking properties of the Pittsburgh district coals are now available. The results are presented in this article. When coals are selected for manufacture of metallurgical coke more factors must be considered than for any other major use, as no basic industry requires coal of such high quality and uniformity. This is particularly true in the Pittsburgh district, where blast furnace practice is based on use of cokes from high quality coals. Although it is true that inferior coals are carbonized in other industrial areas, both here and abroad, the Pittsburgh coals are the best economically obtainable in the required tonnages, even though they are not the most desirable for metallurgical use. In the general evaluation of suitability of coals for coke making, particular attention is given to: 1) reserve, 2) ash and sulfur content, 3) inherent properties of forming strong, well fused coke, 4) expanding characteristics, and 5) blending properties. Items 1 and 2 are covered in detail in the first two phases of the survey, and coking behavior is considered in items 3 through 5. Problems is Coal Evaluation: Although not all coal beds of immediate or potential use to the coking industry in the Pittsburgh area have been tested for their coking properties, enough tests have been made to permit certain generalized statements. Virtually all the coals that will be used in this district are from the Appalachian region, and except for high oxygen coals from outcrops or stripping operations, they are coking coals. Hence the evaluation problem is not so much that of distinguishing between coking and noncoking coals as attempting to measure quantitatively differences in the coking and expanding properties of the better coking coals. Quantitative differentiation between good coking coals, is complex, since differences in their coking abilities are frequently of about the same magnitude as the precision of the test. Small-scale tests are generally unsuitable for measuring these slight differences, and there has been gradual acceptance of pilot-scale tests. Test Methods Employed: All the data reported here were obtained in two units known as the Bureau of Mines-American Gas Association (BM-AGA) carbonization apparatus and the sole-heated expansion oven. The BM-AGA unit, which consists essentially of a cylindrical steel retort about 18 in. diam and 26 in. high, carbonizes enough coal (180 lb) to allow evaluation of the coke by standard methods of the American Society for Testing Materials. The BM-AGA carbonization procedure and methods of testing the gas, liquid, and solid products have been described.&apos; Expanding characteristics of the coals were determined in the sole-heated expansion oven," wherein the coal charge, heated from the bottom only, is carbonized under a constant applied force and the linear expansion or contraction is measured. Although results in this oven have never been quantitatively correlated with the expansion behavior of coals in conventional slot ovens, they are useful in assessing expansion behavior. In this report discussion will be confined to results obtained from these pilot-scale units, although the following data are available for most coals: proximate and ultimate analyses, free swelling index, agglutinating value, and plasticity. Sources of Coals Tested: In selection of coals for coke manufacture, economic considerations are as important as quality, and each coke plant balances these two factors to meet requirements of the most satisfactory coke at lowest price. Although these economic factors may in some instances outbalance small differences in coke quality, they are usually specific to each coke plant and cannot be given in any general statement. Recognizing that coal and plant operating costs are beyond the scope of the survey, the USBM evaluates the coking quality of various coals without regard to their competitive economic status. For the purpose of this article, coals of interest to the Pittsburgh district are arbitrarily defined as

Jan 1, 1958

By Laurance S. Reid, Joe A. Porter

Gas dehydration plays an important part in the production of natural gas. Effective dehydration prevents formation of gas hydrates and the accumulation of water in transmission Systems,2,6,7 insuring uninterrupted gas deliveries at maximum efficiency under the most adverse weather conditions. At the present time, most gas companies require a maximum water vapor content of seven lb per million standard cu ft of gas. so that virtually all gas tendered for sale must he dehydrated to meet this specification. For a number of years it has been common practice to produce gas and gather it at a common point for dehydration prior to discharge into the transmission system.1,3,11,16,17 However, higher transmission line pressures, long gathering lines and relatively low ground temperatures have made it necessary to dehydrate gas at. or near. individual. wells in order to gather gas from a number of newly developed fields without unusual difficulty. Where gas has been dehydrated at pressures ranging from 300 to 800 psi in the past. future trends indicate that these processes may be operated at pressures as high as 2,000 psi. Economics of gas dehydration are of great importance, partitularly where facilities must he provided to process relatively small quantities of gas, such as the production from an individual well. Although the adsorption of water vapor from gas on a granular sorbent material such as activated bauxite, activated alumina, or one of the alumina-silica gels is highly effective and produces virtually "bone dry" gas, the cost of a small unit of this type is substantially greater than that of an absorption process which, through proper selection of the absorbing liquid, will dehydrate the gas sufficiently to meet pipe line specifications. For this reason, a great deal of emphacis has been placed on the development of small, inexpensive dehydration units8,24 and the search for more effective absorb. ent liquids has been intensified. A wide variety of methods for dehydrating gas are known&apos; and many of these have been used in industry. Earlier applications of the absorption process employed concentrated solutions of calcium and lithium chlorides as the absorbent. The severe corrosion problems inherent in handling these solutions and the relatively small dew point depressions obtained caused early abandonment in favor of, or conversion to. diethylene glycol when it was found that aqueous solutions of this organic liquid were more hygroscopic than the brines and were non-corrosive. Processes employing diethylene glycol-water solutions are widely used for gas dehydration at pressures ranging as high as 1,200 psi.13,14,15 At nominal pressures a dew point depression of 45° to 50°F may be be and the data of Russell et al." indicate that a minimum dew point is obtained from the effluent gas at a pressure of approximately 1,200 psi when the gas is in equilibrium contact with a 95 per cent by weight diethylene glycol solution. In a number of instances the dew point depression obtained with diethylene glycol-water solutions is not sufficient to produce a specification product without cooling the inlet gas. In a recent search for a better absorhent, triethylene glycol was used in a small commercial dehydration unit and subjected to rather exhaustive field tests.&apos; The data obtained were encouraging and indicated that, at pressures ranging from 300 to 500 psi, triethylene glycol porduced a substantially greater dew point depression than diethylene glycol. These results led to an investigation of the system natural gas-water-triethylene glycol in an effort to obtain vapor-liquid equilibrium data, to determine pressure limitations, and to develop other data pertinent to the design of gas dehydration processes. A review of the literature has failed to reveal any data which permit reasonably accurate calculation of the vapor-liquid equilibrium conditions for a solution of water and triethylene glycol in contact with natural gas at high pressure. Since these constituents form a non-ideal system, the Poynting equation18,21 or the usual combination of Raoult&apos;s and Dalton&apos;s laws19,20,22 would not be valid. Correction of Raoult&apos;s and Dalton&apos;s laws by the use of activity coefficients2&apos; is not feasible for available data are insufficient for the prediction of the actual increase in the ratio of the activity of one component in the vapor phase to its activity in the liquid. Therefore. experi-

Jan 1, 1950

By J. P. Hirth, A. H. Clauer

A simple graphical method is presented for the determination of climb forces on dislocations exerted by uniaxial stresses. In conjunction with standard stereographic projections, the technique is applicable for any crystal system. Climb forces on glide dislocations in bcc crystals are determined as an application. In connection with a study1 of elevated temperature creep of molybdenum single crystals, a detailed analysis of the climb force on a dislocation was necessary. In general, such forces can be calculated for an arbitrary dislocation segment from the Peach-Koehler equation2 (or one of its variants3"6) where Fk are the components of the force per unit length of dislocation line, ?i of the unit sense vector tangent to the line, ojl of the stress tensor, bl of the dislocation Burgers vector, and is the Einstein permutation operator with components ?123 = ?231 = ?321 = —?132 = — ?321 = —?—213 = unity, and all other components zero. It is understood in the suffix notation of Eq. [I.] that repeated indices are to be summed over 1, 2, and 3. For the most general coordinate system, the matrix manipulations required to solve Eq. [I] are fairly complex. However, a simplification can be achieved by specifying a coordinate system based on the dislocation in question. The pertinent system involves cartesian coordinates xi, x;, xi, with attendant unit vectors e&apos;i; ei being parallel to the Burgers vector b, and e&apos;3; being parallel to the climb directions (b x ?), i.e., normal to the slip plane. In this coordnate system b = (bi, 0, 0) and ? = (?&apos;1,?&apos;2, 0). Hence, Eq. [I] yields for the climb force per unit length F3 = ?&apos;2s&apos;11b&apos;1—?&apos;1s&apos;12b&apos;1 [2] The first term on the right side of Eq. [2] is the climb force on the edge component of the dislocation, while the second is the (cross-slip) force normal to the glide plane acting on the screw component. Thus, the problem of determining the climb force reduces to that of resolving the stress components —il and s&apos;12 in the xi coordinate system. Several authors7- l0 have shown, for the glide case, that such stress resolution can be performed most readily by graphical methods. Therefore, we present a similar method for the climb case. Of the suggested methods, we follow that of Hartley and Hirth,9 which can be performed directly with a standard stereographic projection for the crystal system in question. We treat the case of simple tension, or compression, this being the most common creep test in which climb is important. A set of cartesian coordinates (x1, x2, x3) is fixed with x3 parallel to the specimen axis. This set is connected to the x&apos;i set by the factors defined in Table I. A perspective view of the coordinate systems relating them to the glide ellipse, is given in Fig. 1, while a stereographic projection of the coordinate systems is presented in Fig. 2. The transformation matrix connecting the xi and xi coordinates is x&apos;i =aijXj [3] where an a11 a13 aij = a21 a22 a23 a31 a23 [4] s The corresponding transformation for the stresses is i [5] The only nonzero component of okl for the simple tension case is s33,. Hence, using Eqs. [4] and 151, we find that Eq. [2] becomes F3 = b&apos;1s33 sin2 cos ?[cos ? sin a - sin ? cos a] [6] = m1b&apos;1s033 sin a- rn2b&apos;s33 cos a where sin a = 5: and cos a = ?i, with a the angle measured from b to ?, i.e., a polar angle in the x1, x2 plane. The same equation with a sign change applies for compression. A graphical plot of the "Schmid" factor m1, relating to the climb force on the edge component, is presented in the stereographic projection of Fig. 3. In this projection the glide plane normal points toward the top of the page and the glide direction points normal to the plane of the page. To use the graph, one

Jan 1, 1970