By T. Federighi, S. Ceresara, C. Panseri

The results of an exploratory investigation by means of resistivity measurements at -195ºC, on the aging characteristics of a set of Al-Mg alloys with a maximum content of 7 pct Mg, are reported. Whereas for dilute alloys (Mg < 1.5 pct) only a decrease in resistivity is observed at about 100°C (due to the elimination of quenched-in vacancies), for more concentrated alloys such a decrease is preceded by an increase in resistivity in the range between -60ºand +40°C. Following some previous suggestions, this increase is considered as good evidence for clustering of solute atoms @reprecipi-tation process). From the analysis of the results it appears that, although the process is substantially similar to that observed in other Al-rich alloys, it is characterized by a strong interaction between vacancies and zones. THE process of formation of Guinier-Preston zones, i.e., preprecipitation,1&apos;2 which occurs during the aging at about room temperature in many supersaturated aluminum-rich alloys, has been extensively investigated in the past few years by several workers.2,3 owever, a very interesting question arises when the case of Al-Mg alloys is considered: although it is very easy to supersaturate Al-Mg alloys, just in the same way as for many other aluminum alloys showing preprecipitation, only very little experimental evidence was available until a short time ago in the literature supporting the existence of "natural" aging in supersaturated Al-Mg alloys (see, for example, Refs. 4 to 6). On the other hand, as is well known, the X-ray method is not useful in this case because the X-ray scattering factors of magnesium and aluminum atoms are about the same. Recently, however, Cordier and Detert7 have stressed that during the aging at about room temperature of a supersaturated Al-Mg 10 pct alloy it is possible to detect an increase in resistivity; since, as is well known, such an increase is observed also in most alloys showing preprecipitation, the above authors have interpreted their results as evidence for the formation of magnesium-rich clusters (or Guinier-Preston zones) during the aging. In the course of or ientative investigations on preprecipitation in several aluminum-rich alloys, we also could detect a similar phenomenon in more dilute Al-Mg alloys, see Instituto Sperimentale Metalli Leggeri, Annual Report, 1959, and also Ref. 8. Since the details of our observations, although of a preliminary nature, differ from those of Cordier and Detert and allow one to draw a more advanced picture of the preprecipitation process in Al-Mg alloys, we have thought it useful to report our results in this paper and to comment on them briefly.

Jan 1, 1963

By Robert E. Green, T. Hinton

The velocities of the three possible modes of elastic-wave Propagation have been calculated for single-crystal aluminum at 1-deg intervals throughout the standard steveographic triangle. The results are presented as isospeed contours. The deviations between the direction of maximum energy propagation and specirzen axes are presented as arrows drawn within the standard triangle. The orientation factors associated with dislocation nzotion on the primary slip system only and also on all twelve slip systenzs have been calculated for all three elastic waves. The orientation factors associated with a longitudinal standing--7aue resonant specivnen hazle also been calculated. The relevance of these results to ultrasonic attenuation measurements is discussed. DUE to the widespread use of ultrasonics in the investigation of the properties of solids a number of authors15 have discussed in detail the theory of elastic-wave propagation in solids. In this paper the modes of wave propagation are evaluated according to the procedure suggested by reeen&apos; for the case of single-crystal aluminum at 1-deg intervals throughout the standard stereographic triangle. The wave speeds are presented in the form of contour diagrams within the standard triangle. The deviations between the direction of maximum energy propagation and the normals to the wave fronts are presented as arrows drawn within the standard triangle. The orientation-de pendent factors (orientation factors) associated with dislocation damping as derived in the preceding paper6 have been calculated for the case of aluminum at 1-deg intervals throughout the standard triangle. The orientation factors for dislocation motion on the primary slip system only and on all twelve slip systems are presented in the form of contour diagrams, for both the traveling- and the standing-wave conditions. The relevance of these results to ultrasonic attenuation measurements is discussed. ELASTIC-WAVE PROPAGATION Three waves can be propagated in a linear elastic homogeneous anisotropic medium. The velocity of propagation v of each of these waves in a medium of density p can be obtained from the determination of the eigenvalues and eigenvectors of the matrix equa- The A&apos;s are a series of moduli which are functions of the elastic constants cij and the direction cosines 1, m, and n of the specimen axis. In the case of cubic single crystals where there are only three nonzero elastic constants cll, c12, and C, the A&apos;s are, The solution of Eq. [I] will give the wave speeds (eigenvalues) and the direction cosines a, 0, and y of the particle displacements (eigenvectors). To obtain the direction of maximum energy flux requires the calculation of the energy-flux vector ET with com- w is the angular frequency, A, the amplitude, and v the velocity of the wave. The direction cosines a, b, and c of the energy flux vector are then given by

Jan 1, 1967

By C. M. Loeb, T. E. Norman

THE use of ball, rod and tube mills for grinding ore, cement and other materials has grown so rapidly during the past forty years that the world&apos;s annual consumption of ferrous grinding media for these mills is now estimated to be between one half million and one million tons per year. Ferrous grinding balls constitute the major portion of this tonnage. Obviously they represent sufficient value to justify thorough studies of the factor sgoverning their performance. The selection of grinding balls is governed principally by: I. Quality (wear resistance, impact resistance, soundness, and the like). 2. Sources of supply and delivered cost. 3. Grinding characteristics or efficiency in the ball mill. This paper deals principally with the quality of ferrous grinding balls. In the study of these factors certain data relative to the fundamental nature of ball wear in ball mills have been obtained. These data are also presented and discussed briefly. THE DEVELOPMENT OF A SUITABLE WEAR TEST A study of the fundamental factors governing the quality of grinding balls has been hampered seriously by the fact that a competent test has, in the past, involved the purchase of several hundred tons of balls of a specific type which were then run in one or more ball mills for a period ranging from several months to several years&apos; duration. Often, during the period of test, it became necessary to change operating conditions or the character of the ore fed to the test mill with the result that the rate of ball consumption changed and the test figures became of little value. Under such circumstances, progress in the development of better grinding balls, has been necessarily slow. Economic factors and variations in the quality of balls produced by different sources of supply generally make it necessary for each mill operator to determine for himself the most suitable type of balls for his mills. In our own ball mill grinding operations at Climax, Colo., we were faced with this problem. After we had run a few large scale wear tests at considerable expense we decided to investigate the possibilities of a small scale wear test which would be capable of testing numerous types of balls within a relatively short time. The most important requirement of any test is, of course, that it give results which can be used to predict accurately the wear in full scale operations. It was. known that Ellis and his associates1.2 had developed a method of testing grinding balls by small scale tests run at the Ontario Research Foundation. Ellis&apos; method of testing was used as a starting point in our investigations. In the course of our tests a number of modifications of the original method were found to be desirable so that, by an evolutionary procedure, a method of small scale

Jan 1, 1948

By J. P. Hirth, G. M. Pound

The flux of evaporation J from {loo) , {111), and (110) planes of silver single crystals and from poly crystalline specimens was measured at 744°C under a high vacuum using a time average weight loss method. The evaporation coefficient a was computed from the measured flux and vapor pressure data through the relationship J = aPe/21rmkT. The evaporation coefficients for the close packed planes and the poly crystalline specimens were found to be about 0.4 providing tentative confirmation of the theoretical limiting law for evaporation of metal crystals, a = 73(P/Pe) + % . The (110) planes faceted to form (111) planes, resulting in a greater evaporating area and larger a . The evaporation morphology of the plane surfaces and the surfaces of spherical single crystals is described in some detail. RECENTLY a detailed theoretical analysis of the mechanism and kinetics of metal crystal evaporation was made.1&apos;2 A mechanism for vaporization involving the recession of monatomic ledges across a metal surface was deduced, and evaporation rate equations were derived by considering the dynamics of these ledges. In most metals, the process of evaporation is one of dissociation of atoms from ledges, surface diffusion, and desorption. The gross vaporization rate is controlled by the surface diffusion and desorption rates. It was shown that the monatomic ledges, under the action of surface diffusion gradients, tend to assume a terminal velocity and spacing. Further, it was shown that crystal edges and grain boundaries are a ready source for monatomic ledges. In the case of evaporation of large, perfect crystals with clean, low-index surfaces, the kinetic treatment1 leads to a limiting law for crystal evaporation: where J is the gross flux of vaporization, a is the evaporation coefficient, Pe the equilibrium vapor pressure, m the atomic mass, k Boltzmann&apos;s constant, T the absolute temperature, and P the actual pressure of vapor over the crystal surface. Imperfections such as grain boundaries, pores, cracks, and macroscopic steps should have the effect of causing positive departures from this limiting law. Such an imperfection is a source for monatomic ledges, which, near their origin, are closely spaced and thus give rise to higher evaporation rates there. However, under many experimental conditions,&apos; this effect should be negligible due to the relatively low concentration of imperfections. In general, a more important cause of positive departure should be screw dislocations, and the effect of these has been considered in some detai1.2,3 Monatomic ledges emanate from points where the surface is intersected by a dislocation with a screw component normal to the surface. The dynamics of ledges arising from a screw dislocation are similar to those of ledges arising from a crystal edge. There is a perturbed region near the origin where the monatomic ledges are, under certain experimental conditions, closely spaced and the

Jan 1, 1960

By C. M. Loeb, T. E. Norman

The use of ball, rod and tube mills for grinding ore, cement and other materials has grown so rapidly during the past forty years that the world&apos;s annual consumption of ferrous grinding media for these mills is now estimated to be between one half million and one million tons per year. Ferrous grinding balls constitute the major portion of this tonnage. Obviously they represent sufficient value to justify thorough studies of the factors governing their performance. The selection of grinding balls is governed principally by: I. Quality (wear resistance, impact resistance, soundness, and the like). 2. Sources of supply and delivered cost. 3. Grinding characteristics or efficiency in the ball mill. This paper deals principally with the quality of ferrous grinding balls. In the study of these factors certain data relative to the fundamental nature of ball wear in ball mills have been obtained. These data are also presented and discussed briefly. The Development of a Suitable Wear Test A study of the fundamental factors governing the quality of grinding balls has been hampered seriously by the fact that a competent test has, in the past, involved the purchase of several hundred tons of balls of a specific type which were then run in one or more ball mills for a period ranging from several months&apos; to several years&apos; duration. Often, during the period of test, it became necessary to change operating conditions or the character of the ore fed to the test mill with the result that the rate of ball consumption changed and the test figures became of little value. Under such circumstances, progress in the development of better grinding balls, has been necessarily slow. Economic factors and variations in the quality of balls produced by different sources of supply generally make it necessary for each mill operator to determine for himself the most suitable type of balls for his mills. In our own ball mill grinding operations at Climax, Colo., we were faced with this problem. After we had run a few large scale wear tests at considerable expense we decided to investigate the possibilities of a small scale wear test which would be capable of testing numerous types of balls within a relatively short time. The most important requirement of any test is, of course, that it give results which can be used to predict accurately the wear in full scale operations. It was known that Ellis and his associates1,2 had developed a method of testing grinding balls by small scale tests run at the Ontario Research Foundation. Ellis&apos; method of testing was used as a starting point in our investigations. In the course of our tests a number of modifications of the original method were found to be desirable so that, by an evolutionary procedure, a method of small scale

Jan 1, 1949

By C. M. Loeb, T. E. Norman

The use of ball, rod and tube mills for grinding ore, cement and other materials has grown so rapidly during the past forty years that the world&apos;s annual consumption of ferrous grinding media for these mills is now estimated to be between one half million and one million tons per year. Ferrous grinding balls constitute the major portion of this tonnage. Obviously they represent suficient value to justify thorough studies of the factors governing their performance. The selection of grinding balls is governed principally by: I. Quality (wear resistance, impact resistance, soundness, and the like). 2. Sources of supply and delivered cost. 3. Grinding characteristics or efficiency in the ball mill. This paper deals principally with the quality of ferrous grinding balls. In the study of these factors certain data relative to the fundamental nature of ball wear in ball mills have been obtained. These data are also presented and discussed briefly. The Development of a Suitable Wear Test A study of the fundamental factors governing the quality of grinding balls has been hampered seriously by the fact that a competent test has, in the past, involvetd the purchase of several hundred tons of halls of a specific type which were then run in one or more ball mills for a period ranging from several months&apos; to several years&apos; duration. Often, during the period of test, it became necessary to change operating conditions or the character of the ore fed to the test mill with the result that the rate of ball consumption changed and the test figures became of little value. Under such circumstances, progress in the development of better grinding balls, has been necessarily slow. Economic factors and variations in the quality of balls produced by different sources of supply generally make it necessary for each mill operator to determine for himself the most suitable type of balls for his mills. In our own ball mill grinding operations at Climax, Colo., we were faced with this problem. After we had run a few large scale wear tests at considerable expense we decided to investigate the possibilities of a small scale wear test which would be capable of testing numerous types of balls within a relatively short time. The most important requirement of any test is, of course, that it give results which can be used to predict accurately the wear in full scale operations. It was known that Ellis and his associates1&apos;2 had developed a method of testing grinding balls by small scale tests run at the Ontario Research Foundation. Ellis&apos; method of testing was used as a starting point in our investigations. In the course of our tests a number of modifications of the original method were found to be desirable so that, by an evolutionary procedure, a method of small scale

Jan 1, 1949

By G. H. Matheson, J. M. W. Mackenzie

The flotation rate of coal has been studied using a continuous laboratory flotation cell and a multiple exposure photographic technique. The effects of particle size, reagent additions and cell turbulence on the flotation rate of coal have been investigated. The results have been analyzed in terms of current theories of particle bubble encounter and adhesion. The rupture forces which occur during particle bubble encounter have been shown to have an important effect on the flotation rate of coarse coal particles. The flotation of coal is a time dependent process, and in order to obtain a complete understanding of the operation it is necessary to determine the kinetics of the process. In coal flotation, the flotation rate and the associated values of cell productivity in terms of tons per kilowatt-hour and tons per cubic foot of cell volume are of greater importance than in most other mineral flotation operations. The reasons for this are associated with the low unit value of coal and the relatively high cost of coal flotation compared with other coal cleaning processes. An important aspect of coal flotation kinetics is the design of coal flotation cells. The cells used in many coal cleaning operations are often replicas of those used for the treatment of sulfide ores and are not necessarily suitable for the treatment of coal washing pulps, which usually contain a higher percentage of coarse and floatable material than the sulfide pulps for which the cells were designed. This disadvantage of many coal flotation cells has been recognized by Russian engineers who, by the addition of baffles to their subaeration coal flotation cells have increased the cell capacity by 100%. Investigation of the variables which influence flotation kinetics and cell productivity are, therefore, important to the coal industry where flotation is the only accepted method of cleaning the fine (-1/2mm) coal. The kinetics of the flotation process have been investigated in detail by Schumann10 who developed a continuous flotation cell which permitted the study of flotation under steady state conditions. This technique has been used by Gaudin et a1.,6 Brown and Smith and recently by Jowett and Savfi.7 The latter authors have developed a refined mathematical treatment for interpreting the results of continuous laboratory tests. Attempts have also been made to study flotation kinetics using conventional batch testing techniques. The experimental difficulties, however, and the problems of determining the order of the flotation rate process have made this technique of dubious value. A summary of the proposed rate equations for batch testing and the difficulties associated with this technique is given by Brown and Smith. 2 The experimental techniques described above are concerned with the rate of production of froth product. However, several authors, notably Sutherland, 11 Bogdanov1 and Philippoff, 9 have analyzed flotation

Jan 1, 1963

By George A. Grandy, D. W. Fuerstenau

Simulation of nonlinear grinding systems is discussed in the context of the size-discretized batch-grinding model. A linear approximation of environment-dependent (or nonlinear) selection functions is postulated for systems which exhibit feed grinding orders less than unity. For this, a convex linear combination of zero and first-order selection function forms is used to obtain an analytical solution that can be used for simulation. An example in which marked nonlinear behavior occurs is rod-mill grinding. Accordingly, a series of grinding experiments was carried out in a batch laboratory rod mill to test these techniques; agreement between experiment and the model was found to be very good. Recently, significant progress has been made in the simulation of linear grinding systems by using a population balance mathematical model. Herbst and Fuer-stenaul presented a parameter estimation scheme that can be used with the size-discretized batch-grinding model, and Gumtz and Fuerstenau3 have extended these techniques to the simulation of locked-cycle grinding. Grandy et aL." summarized the simulation of linear systems and noted important alternate solutions to the batch-grinding equation. Kelsall et a1.&apos;-" discussed the dynamic simulation of linear batch grinding, as well as linear open and closed-circuit grinding. In all of these, the key word is linear, which certainly restricts the engineer trying to simulate a variety of grinding systems. This paper discusses an approach for the simulation of non-linear grinding systems, particularly those which exhibit grinding orders less than unity. Experimentally, dry rod-mill grinding is used to evaluate the technique presented. Batch Grinding Model The size-discretized batch-grinding model has been discussed in detail by Mika et al.&apos;.&apos; and by Herbst and Fuerstenau,&apos; and therefore, will only be briefly developed here. The model is formulated by making a differential mass balance of each size fraction in such a manner that the equation parameters are precisely defined in terms of selection and breakage functions,&apos; which can be either calculated&apos;.&apos; or estimated1 from experimental data. The model is phenomenological because it averages all stress-application events in the system and, therefore, does not distinguish the manner in which individual particles are stressed.&apos; For this average environment, the resistance of all particles in a size fraction to breakage is defined by that size-frac-tion&apos;s selection function; and when fracture occurs from an average event, the breakage product size distribution is defined again by that size-fraction&apos;s breakage function. The model is deterministic and is derived in terms of a continuous time variable and a discretized size variable,&apos; i.e., the n mass fractions associated with the n defined size intervals (see Table 1 for nomenclature).

Jan 1, 1971

By C. M. Loeb, T. E. Norman

The use of ball, rod and tube mills for grinding ore, cement and other materials has grown so rapidly during the past forty years that the world&apos;s annual consumption of ferrous grinding media for these mills is now estimated to be between one half million and one million tons per year. Ferrous grinding balls constitute the major portion of this tonnage. Obviously they represent suficient value to justify thorough studies of the factors governing their performance. The selection of grinding balls is governed principally by: I. Quality (wear resistance, impact resistance, soundness, and the like). 2. Sources of supply and delivered cost. 3. Grinding characteristics or efficiency in the ball mill. This paper deals principally with the quality of ferrous grinding balls. In the study of these factors certain data relative to the fundamental nature of ball wear in ball mills have been obtained. These data are also presented and discussed briefly. The Development of a Suitable Wear Test A study of the fundamental factors governing the quality of grinding balls has been hampered seriously by the fact that a competent test has, in the past, involvetd the purchase of several hundred tons of halls of a specific type which were then run in one or more ball mills for a period ranging from several months&apos; to several years&apos; duration. Often, during the period of test, it became necessary to change operating conditions or the character of the ore fed to the test mill with the result that the rate of ball consumption changed and the test figures became of little value. Under such circumstances, progress in the development of better grinding balls, has been necessarily slow. Economic factors and variations in the quality of balls produced by different sources of supply generally make it necessary for each mill operator to determine for himself the most suitable type of balls for his mills. In our own ball mill grinding operations at Climax, Colo., we were faced with this problem. After we had run a few large scale wear tests at considerable expense we decided to investigate the possibilities of a small scale wear test which would be capable of testing numerous types of balls within a relatively short time. The most important requirement of any test is, of course, that it give results which can be used to predict accurately the wear in full scale operations. It was known that Ellis and his associates1&apos;2 had developed a method of testing grinding balls by small scale tests run at the Ontario Research Foundation. Ellis&apos; method of testing was used as a starting point in our investigations. In the course of our tests a number of modifications of the original method were found to be desirable so that, by an evolutionary procedure, a method of small scale

Jan 1, 1949

By J. L. Lamont, W. Crafts

Studies of the effect of composition of steel on hardenability by Grossmann,&apos; and as-quenched hardness by Field2 and by the authors, have made it possible to predict the results of quenching when the composition and cooling rate are known In order to extend the application of the hardenability calculation to the quenched and tempered condition in which steel is finally used, a survey has been made of the hardness changes caused by tempering. From this study a method has been developed for the prediction of hardness and tensile strength of steel in the tempered condition. The method of calculation was developed from Rockwell C hardness tests on quenched and tempered Jominy specimens and is expressed in Rockwell C hardness units. It is of an additive type in which the degree of softening from as-quenched hardness is estimated. Tem-pred properties may be calculated within about plus or minus 5 Rockwell C hardness or plus or minus 15,000 lb. per sq, in. tensile strength. This degree of accuracy is less than that necessary for the control of heat-treatment, but is adequate for the comparative evaluation and selection of alloy steels. The formula indicates that tempered hardness is primarily dependent on as-quenched hardness and, as in the hardening reaction, the progress of tempering is controlled mainly by the carbon content. Alloys tend to retard softening by a secondary hardening mechanism in which the alloy appears to migrate from ferrite to the carbide phase. The factors for the effects of alloys in tempering vary so much from the effects of alloys in hardening that different steels of equivalent hardenability may, after like heat-treatment, differ considerably in tensile strength. Procedure In developing the method for calculating tempered Rockwell C hardness, simple and complex steels were tested over a range from 0.08 to 0&apos;65 per cent carbon and up to 2.68 per cent manganese, 2.18 silicon, 3.50 chromium, 4.94 nickel, and 1.06 molybdenum. The steels were made as small induction-furnace heats at the Union Carbide and Carbon Research Laboratories, Inc&apos; The accuracy of the method was finally checked on a variety of carbon, low-alloy and high-alloy types of heat-treating steels produced under commercial conditions. The method was based on a study of tempered Jominy bars, and its validity was tested by correlation with the center hardness and tensile strength of oil-quenched and tempered bars from 1/2 to 4 in. in diameter. The method of calculation was derived from the differences in Rockwell C hardness between as-quenched and quenched and tempered Jominy specimens. Prenormalized Jominy hardenability speci-menS quenched from a normal temperature for austenitizatios were used to obtain a range of as-quenched Rockwell C

Jan 1, 1948

By W. Crafts, J. L. Lamont

Studies of the effect of composition of steel on hardenability by Grossmann,&apos; and as-quenched hardness by Field2 and by the authors, have made it possible to predict the results of quenching when the composition and cooling rate are known In order to extend the application of the hardenability calculation to the quenched and tempered condition in which steel is finally used, a survey has been made of the hardness changes caused by tempering. From this study a method has been developed for the prediction of hardness and tensile strength of steel in the tempered condition. The method of calculation was developed from Rockwell C hardness tests on quenched and tempered Jominy specimens and is expressed in Rockwell C hardness units. It is of an additive type in which the degree of softening from as-quenched hardness is estimated. Tem-pred properties may be calculated within about plus or minus 5 Rockwell C hardness or plus or minus 15,000 lb. per sq, in. tensile strength. This degree of accuracy is less than that necessary for the control of heat-treatment, but is adequate for the comparative evaluation and selection of alloy steels. The formula indicates that tempered hardness is primarily dependent on as-quenched hardness and, as in the hardening reaction, the progress of tempering is controlled mainly by the carbon content. Alloys tend to retard softening by a secondary hardening mechanism in which the alloy appears to migrate from ferrite to the carbide phase. The factors for the effects of alloys in tempering vary so much from the effects of alloys in hardening that different steels of equivalent hardenability may, after like heat-treatment, differ considerably in tensile strength. Procedure In developing the method for calculating tempered Rockwell C hardness, simple and complex steels were tested over a range from 0.08 to 0&apos;65 per cent carbon and up to 2.68 per cent manganese, 2.18 silicon, 3.50 chromium, 4.94 nickel, and 1.06 molybdenum. The steels were made as small induction-furnace heats at the Union Carbide and Carbon Research Laboratories, Inc&apos; The accuracy of the method was finally checked on a variety of carbon, low-alloy and high-alloy types of heat-treating steels produced under commercial conditions. The method was based on a study of tempered Jominy bars, and its validity was tested by correlation with the center hardness and tensile strength of oil-quenched and tempered bars from 1/2 to 4 in. in diameter. The method of calculation was derived from the differences in Rockwell C hardness between as-quenched and quenched and tempered Jominy specimens. Prenormalized Jominy hardenability speci-menS quenched from a normal temperature for austenitizatios were used to obtain a range of as-quenched Rockwell C

Jan 1, 1948

By Stanley D. Michaelson, Norman Weisis

The purpose of beneficiation is to increase the economic value of an ore by elimination of waste rock or by separation of minerals that require separate reduction, without destroying the physical and chemical identity of the minerals. Flotation has replaced older methods of beneficiation to a very great ex- tent, nearly entirely in the case of the copper, lead, and zinc minerals and less completely in the case of such other minerals as iron, coal, and titanium. Flotation is also used to recover barite, fluorspar, feldspar, cement rock, spodumene, vermiculite, silica, beryl, and potash in the nonmetallic field, and cobalt, vanadium, germanium, antimony, mercury, molybdenum, manganese, nickel, gold and silver, cadmium, and bismuth for metals. The rapid growth of flotation to pre-eminence cannot be attributed to its low cost, because gravity, magnetic, and electrical methods may in some cases cost only half as much. But for ores containing finely disseminated minerals, these other methods are successful only in exceptional cases, for example the magnetic taconites or titanium-bearing sands. For low grade ores with coarse texture or spotty mineralization the advantages of low-cost gravity methods and highly efficient flotation are often combined, as in the beneficiation of coal and some ores of lead and zinc, phosphate, tungsten, and manganese. When an ore is responsive to either flotation or non-flotation concentration, or to combinations of the two, the choice depends upon cost of the process only when dealing with ores of low value; in other cases it is dictated by either the process efficiency or the product specification. Generally speaking, flotatio.1 is so efficient as compared with other methods of concentration that process cost is rarely an important factor in its selection. It is said, "The metal in the mill tailing has already been mined." Once the mining cost has been paid it doesn&apos;t increase total costs very much to do a thorough job of milling. With the exception of the few types of ores that are not amenable to flotation, the chief reason for preferring electrical and gravity methods to flotation may lie in the specification of the product. Flotation demands fine grinding, and specifications may not permit this with many nonmetallic ores or coal. Another reason is the size of investment-where capital is hard to obtain or the life of the property is short, the justification for a flotation plant may not exist, and one must be content to skim off the cream. y not exist, and one must be content to skim off the cream. Gravity processes often cost less than flotation because a large part of the waste rockcan be rejected without costly grinding, no chemicals are required,

Jan 1, 1962

By R. F. Hinds

A pressurizing system was designed and built to apply a radial pressure of 5.000 psi to rock samples. Samples of the Bradford, Weir and Kirkwood sandstones were subjected to radial pressures parallel and perpendicular to the bedding in the system and the changes in conductivity, porosity and permeability were deter-mined. Asymptotic decreases in conductivity, porosity and Klinkenberg permeability were observed over the 0- to 3,500-psi range. From these data, the increase of formation factor over the same range was calculated. The cementation exponent expressed in the Archie equation was found to increase with pressu,re. The rate of change varied from formation to formation. Only small differences were observed for samples taken parallel to the bedding as comnared to those taken perpendicular to it except for the Bradford sand. Above 3,500 psi the data are not good enough to tell if the properties continue to fall-off asymptotically or in a different manner. A possible explanation for the probable litnit of the asymptotic rate around 3,500 to 4,500 psi is that this represents the maximum pressure which the formations have unrdergone during their geological life as a result of burial. INTRODUCTION For many years measurements have been made in the laboratory of the properties of oil-bearing sandstones with little consideration being given to whether these properties had been changed when the samples were moved from their original position in the ground to the laboratory. Relatively little has been reported in the literature on the effect of pressure on the properties of sandstones. The changes in permeability for eight typical consolidated oil-bearing sandstone samples with overburden pressure (0- to 15,000-psi range) was presented by Fatt and Davis&apos; in graphical form. In 1953 Fatt&apos; also reported the relationship between porosity and overburden pressure for four typical consolidated oil-bearing sandstone samples (0- to 5,000-psi range). Fatt later described the changes of formation factor and porosity of 20 typical oil-bearing sandstone samples with overburden pressure changes (0- to 5,000-psi range) giving the values of the coefficients and exponents in the Archie&apos; equation, and the more general Winsauer equation&apos;, where C, k and m are empirical constants, F is the formation factor, and + is the porosity. During the experiments of this investigation the core was contained in a neoprene rubber sleeve as shown in Fig. 1. It was held between two steel end members which were mounted in a steel cylinder. The unassembled pressure cylinder with its component parts is shown in Fig. 2. The core was insulated from the two steel end members by a Teflon sleeve with a small hole in the

By William C. Harrigan, William D. Nix

Dynamic measurements of Young&apos;s modulus have been made for poly crystalline Ni-W alloys from room temperature to 800°C. The alloys studied range in composition from pure nickel to Ni-10 at. pct W. The results indicate that Young&apos;s modulus decreases linearly with temperature above the Curie temperature. The rate of change of Young&apos;s Modulus with temperature mas found to range from 104 psi per "C for pure nickel to 0.82 x 104 psi per °C for Mi-10 pct W. At all temperatures the elastic modulus decreases with increcrsing tungsten content up to 1 at. pct W, and increases as the tungsten content is increased above that level. Young&apos;s modulus decreases slightly as the carbon content is increased from 0.002 to 0.09 wt pct C THE knowledge of the elastic modulus of metals and alloys is important for a number of reasons. The first and most obvious reason comes from the need to predict elastic deflections under given loading conditions. A second and somewhat more subtle reason comes from the fact that the elastic properties of an alloy must be known before a proper account of the mechanisms of plastic deformation can be made. This is especially true for high-temperature creep of crystalline solids. Sherby and his coworkers have shown that the high-temperature steady-state creep rates of crystalline solids are inversely related to the elastic modulus1,2 and that the temperature dependence of the elastic modulus must be taken into account if reliable determinations of the activation energy for creep are to be made. In addition, measurements of the elastic constants of solid solutions are needed to allow one to assess the modulus interaction contribution to solid-solution Strengthening.3-5 Pelloux and Grant6 have demonstrated that substantial solid-solution strengthening at room temperature and elevated temperatures occurs when refractory metal solute atoms are added to nickel. While the high-temperature elastic properties of pure nickel have been measured by a number of authors,7-10 the elastic properties of nickel-based refractory metal alloys have not been determined. The purpose of this paper is to report on measurements of Young&apos;s modulus of polycrystalline Ni-W alloys at elevated temperatures. It is expected that these measurements will be valuable to studies of the mechanical properties of nickel-based refractory metal solid solutions. I) EXPERIMENTAL Young&apos;s moduli of polycrystalline samples were determined by a dynamic method in order to reduce high- temperature anelastic and plastic relaxations. The samples were forced in transverse free-free vibration; that is, both ends of the sample were unrestrained and the vibration was transverse to the long axis. The fundamental resonant frequency was determined by the Forster method.11 The analysis of this type of vibration which was formulated by Rayleigh,12 Timo-chenko,13 and pickett,14 and reviewed by Fine," leads where fn is the resonant frequency of the nth mode, r is the radius of the circular cross section. L is the specimen length, ßn is 1.5056 for free-free vibration in the fundamental mode of vibration, 6 is the mass density, and E is Young&apos;s modulus in the axial direction. This equation can be transformed into: E = 9.17605 x 10-6(L/D)E/Lf2 [2] where E is Young&apos;s modulus in psi, L is the length in inches, d is the diameter in inches, W is the weight in grams, and f is the resonance frequency in cps. Eq. [2] was further modified in order to take account of the thermal expansion of the samples. The resulting correct term is: where the thermal expansion coefficients for nickel and tungsten, respectively. Xw is the atom fraction of tungsten in the sample and T is the temperature in "C. The treatment of the thermal expansion coefficient as a linear function of composition seems sufficiently accurate since an error of 25 pct in the expansion coefficient will result in only a 0.3 pct error in the modulus at 1000°C. A) Apparatus. The equipment for this investigation has been described by Lytton et al.16 Several modifications of the equipment have been made. The most significant change involved replacing the detector crystal transducer with a magnetic transducer. A phonographic magnetic transducer was employed as a sensing device since the contact pressure necessary to produce a stable signal is much less than that for a crystal transducer. This magnetic transducer is also not affected by conditions of high temperature and vacuum which are present in these experiments. The vacuum was 10-5 torr at room temperature and about 5 x 10-4 torr at 900°C. This was sufficient to prevent surface contamination of the samples during the tests. The samples were heated in an elliptical furnace with a quartz lamp at one focal line and the sample at the other, as described by Lytton et a1.16 The temperature of the sample was measured by monitoring the

Jan 1, 1969

By A. T. Miesch, L. B. Riley

Distribution of minor elements in sandstone-type uranium deposits of the Colorado Plateau is being studied by the USGS on behalf of the A EC. A primary objective has been to provide basic data which could be useful in geo-chemical exploration for new deposits. The basic statistical measures — similar to those used in sedimentary petrology—are described. The underlying principle is that the frequency distributions fit or approach the log-normal form. Since 1952 the U. S. Geological Survey on behalf of the U. S. Atomic Energy Commission has conducted a study of the distribution of minor elements in sands tone-type uranium deposits of the Colorado Plateau. A primary objective in this study has been to provide basic data which could be useful in geo-chemical exploration for new deposits. Among the basic data considered important are estimates of the abundance and habit of each element in the ore and in the host rocks. It has been found that a few basic statistical techniques, and variations of these techniques, are useful in this type of study. Some of the basic techniques have been used to advantage by researchers in geochemistry and in other fields of geology, especially sedimentary petrology; others have been used to only a limited extent. Among the latter is the linear correlation coefficient, which has proved useful in assessing the element associations in a particular rock type without analysing individual mineral separates. In computing the basic statistical measures a scale has been used which is, in some ways, similar to the phi ($) scale used by sedimentary petrol-ogists in grain-size studies.&apos; FREQUENCY DISTRIBUTIONS It has been recognized for some time that the results of analyses for a given minor element in a suite of samples of rocks or ores yield frequency distribution curves which are approximately normal when the curves are plotted on logarithmic or geometric scales. In other words, the analytical results give an approximate lognormal frequency distribution. A classical example is given by D. G. Krige2 in the study of the distribution of gold values from a mine on the Witwatersrand. Another example is shown in Fig. 1, the distribution of barium concentrations in samples of uranium ore from the Chinle formation. The geochemical data are analogous to grain-size data gathered by the sedimentary petrologist. Both types of data, after simple logarithmic transformations, may be treated by conventional statistical methods based on the normal distribution. This is not to say that other types of transformations may not serve equally well or better for particular element distributions.3 Spectrographers and other analysts are quite aware of the dependence of their precision on the concentration of the element present.4 For example, in the part per million range the variation may

Jan 1, 1961

By R. I. Jaffee, F. C. Holden, H. R. Ogden

ECENT papers dealing with the properties of unalloyed iodide titanium have been directed primarily at the determination of base-line properties for alloy investigations. Early work was limited to a few tests because of the limited availability of iodide titanium at the time. In the results of papers by Campbell et al.,1 Gonser and Litton,2 Jaffee and Campbell,3 inlay and Snyder,4 and Jaffee, Ogden, and Maykuth, data on mechanical properties are presented for unalloyed iodide titanium in the annealed and cold-worked conditions. Data are presented in this paper which show the effects of heat treatment on the structure and mechanical properties of commercially produced iodide titanium. Correlation is made between microstruc-tural variables and the mechanical properties. Experimental Procedures Melting Stock: The melting stock used was as-deposited iodide titanium, produced by New Jersey Zinc Co. The furnished analysis showed the following range of impurities: N, 0.004 to 0.008 pct; Mn, 0.005 to 0.013; Fe, 0.0035 to 0.025; Al, 0.013 to 0.015; Mo, 0.0015; Pb, 0.0045 to 0.0065; Cu, 0.0015 to 0.002; Sn, 0.001 to 0.01; Mg, 0.0015 to 0.002; and Ni, 0.003. Hydrogen content as determined by vacuum-fusion analysis was 0.0091 wt pct (0.44 atomic pct) after arc melting and fabrication. Nitrogen analysis on the arc-melted and fabricated titanium showed a content of less than 0.002 pct N. The average hardness of the furnished stock was Rf 70, or approximately 85 VHN. Melting Procedure: The as-deposited rods were rolled, sheared, and degreased in preparation for arc melting. The charge was arc-melted with a tungsten electrode in a water-cooled copper crucible under a positive pressure of high purity (99.96 pct) argon. The final ingot was approximately 2 in. in diameter and showed no increase in hardness over that of the initial stock. Fabrication: Heating for fabrication was done in air. It was begun by forging the ingot into a 3/4 in. diam rod, at an initial temperature of 1600°F. Scale was removed by sandblasting. The rod was then swaged to 1/4 in. diam at room temperature through a series of 20 dies, with approximately 10 pct reduction in area between each die. An anneal of 1 hr at 850 °C in air was given after the 1/2 in. die, such that the final cold reduction was 75 pct. Sections cut from this rod were used for test and microstructure specimens. Heat Treatment: Heat treatments were carried out in resistance tube furnaces with stainless-steel linings, under an atmosphere of gettered argon. As further protection against contamination, the specimens were packed in titanium turnings in a titanium sleeve. Control experiments have shown negligible hardness increases with this method, indicating that contamination from oxygen and nitrogen is slight. Three cooling rates were employed in this work; these have been designated as water quenching, argon cooling (to simulate air cooling under a controlled atmosphere), and furnace cooling. The cooling rate for an argon cool is 100°C per min for the first minute, with an average cooling rate of 35°C per min over a 15-min period. A furnace cool requires about 10 hr, with an average cooling rate of 3.6oC per min during the first hour, and an average cooling rate of 1.2°C per min over the 10-hr period. Microimpact Test: The specimen adopted was based on the cylindrical Izod Type Y specimen (ASTM, E23-41T). All dimensions were reduced to half scale, including the notch radius. Specifications are shown in Fig. 1. The specimen is held vertically in an adapter and broken as a cantilever beam. Impact tests were run on a constant-velocity (11.34 ft per sec) Tinius Olsen impact testing machine with a total available energy of 100 in.-lb. Tests were made to determine the correlation between this microimpact and the standard V-notch Charpy impact test. Curves showing impact energy as a function of temperature for both impact tests are plotted in Fig. 2. Transition temperatures, when they occur, are about the same for both impact tests. All three titanium-rich materials have the same conversion factor, 10. Tensile Testing: Tensile tests were conducted on Baldwin-Southwark testing machines using the 600, 2400, or 3000 1b range. Specifications for the test specimen were taken from the 1948 edition of the ASM Metals Handbook, and are shown in Fig. 1. Strain measurements were made using an SR-4 resistance gage (Type A-7) cemented to the reduced section in conjunction with a lever-type extenso-meter. Readings on the SR-4 strain indicator were

Jan 1, 1954

By D. C. Hilty

It has long been known that in melting high-chromium steels, some of the carbon might be oxidized out of the melt without excessive simultaneous oxidation of chromium, and that higher temperatures favor retention of chromium. The advent of oxygen injection as a tool for rapid decarburization of a steel bath permits significantly higher bath temperatures, and it was quickly recognized that the use of oxygen injection facilitated the oxidation of carbon to low levels in the presence of relatively high residual chromium contents. Up to the present time, however, specific data pertaining to the chro-mium-carbon-temperature relations in chromium steel refining have not been available. Individual steelmakers have evolved practices more or less empirically, but there has been very little real basis for predicting how effective any given practice can be in permitting maximum oxidation of carbon with minimum loss of chromium. The current investigation, therefore, was undertaken in an effort to establish the fundamental carbon-chromium relationship in molten iron under oxidizing conditions. As reported below, the equilibrium constant and the influence of temperature on that constant have been derived for the iron-chromium-carbon-oxygen reaction in the range of chromium steel compositions with what appears to be a fair degree of precision. The practical application of the result will be obvious. Experimental Procedure The laboratory investigation was carried out on chromium steel heats melted in a magnesia crucible in a 100-lb capacity induction furnace at the Union Carbide and Carbon Re- search Laboratories. The charges for the heats consisted of Armco iron, low-carbon chromium metal, and high-carbon chromium metal, the relative proportions of which were calculated so that the various heats would contain from approximately 0.06 pct carbon and 8 pct chromium to 0.40 pct carbon and 30 pct chromium at melt-down. When the charges were melted, the bath temperatures were raised to the desired level, and the heats were then decarburized by successive injections of oxygen at the slag-metal interface through a ½-in. diam silica tube at a pressure of 30 psi. The duration of the oxygen injections was from 30 sec to 2 min. at intervals of approximately 5 to 30 min. It did not appear that length or frequency of the injection periods had any significant effect on the results; cansequently, no effort was made to hold them constant and they were controlled only as was expedient to the general working of the heats. Between successive injections, the heats were sampled by means of a copper suction-tube sampler that yields a sound, rapidly-solidified sample representative of the composition of the molten metal at the temperature of sampling. This sampling device is a modification of the one described by Taylor and Chipman.1 An attempt was made to vary bath temperatures between samples, but it quickly became evident that, unless the variations were small or unless the new temperature was maintained for a minimum of 15 min. during which an injection of oxygen was made in order to accelerate the reactions, a very wide departure from equilibrium resulted. For most of the runs, therefore, temperature was maintained relatively constant at approximately 1750 or 1820°C. A few reliable observations at other temperatures, however, were obtained. Temperature Measurement The high temperatures involved in this investigation were measured by the radiation method, utilizing a Ray-O-Tube focused on the closed end of a refractory tube immersed in the metal bath. The immersion tubes employed were high-purity alumina tubes specially prepared by the Tona-wanda Laboratory of The Linde Air Products Co. These tubes were quite sturdy under reasonable mechanical stress at high temperature. They were unusually resistant to thermal shock, and chemical attack on them by the melts was slow. With care, it was found possible to keep these tubes continuously immersed in a heat for as long as 5 hr at temperatures up to 1850°C, before failure by fluxing occurred. The Ray-O-Tube—alumina tube assemblage was similar to those supplied commercially for lower temperature applications. In operation, the alumina tube was slowly immersed in the molten metal to a depth of approximately 5 in., and the device was then clamped solidly to a supporting jig where it remained for the duration of the run. A photograph of the equipment, in operation with Ray-O-Tube in place and oxygen injection in progress, is shown in Fig 1. When in position in a heat, the instrument was calibrated by means of an immersion thermocouple and an optical pyrometer. For calibration through the range of temperatures from 1500 to 1650°C, a platinum -platinum + 10 pct rhodium thermocouple in a silica tube was immersed alongside the alumina tube. Output of the Ray-O-Tube in millivolts and the

Jan 1, 1950

By T. S. Lovering

GEOCHEMICAL prospecting extends the age-old method of searching out lodes with a gold pan and rationalizes the prospector&apos;s hunch that certain plants are associated with ore. It uses sensitive but cheap and rapid analytical methods to find the diagnostic chemical variations related to hidden mineral deposits. Exploration geologists can gain tremendous assistance from this new tool, although its optimum use is not simple. To bring out the geochemical pattern that reveals the presence of a hidden ore deposit with a minimum number of samples requires a combination of shrewdness, chemical knowledge, and exploration geology. The use of sensitive analytical methods for prospecting had its start in the 1930&apos;s in northern Europe, where Scandinavian and Russian geologists had some success in these early efforts. Very little geochemical prospecting was carried on in the United States at this time, and no sustained interest was manifest until the close of World War 11, when geochemical investigations were started by the Mineral Deposits Branch of the U. S. Geological Survey. The purpose of these investigations was to apply geochemical principles and techniques to surface exploration for mineral deposits. Both the research on analytical methods and the routine trace analyses for field investigations were at first conducted by a single group, but it later became apparent that the trace analyses could be done by men of less experience than that required for successful research on methods. For the past several years there have been two groups of chemists, and although their functions overlap, three of the chemists are chiefly concerned with research, while four to six other men make the trace analyses for field projects. The chemical investigations, as well as the field projects of the Geochemical Exploration Section, concern only those phases of the subject that are appropriate to a government organization; every effort is made to help private industry, but not to compete with it, in finding orebodies. The chief aim of the Section, therefore, is to develop new analytical techniques and publish the results promptly, to carry out field investigations of the fundamental principles of geochemical dispersion, and to field test promising- techniques under controlled conditions. Some routine geochemical exploration work is carried on in connection with DMEA loans, and in district studies where the project chief wishes geochemical information on certain areas for his report. It should be emphasized, however, that geologists of the Geochemical Exploration Section are primarily concerned with fundamental principles underlying the distribution, migration, and concentration of elements in the earth&apos;s crust. To facilitate the use of geochemical methods the USGS has published much information on its methods of analysis and has provided opportunities from time to time for qualified professional personnel to study these methods, to work in the USGS laboratory, or to attend demonstrations of the analytical techniques at the Denver Federal Center. Typical of the research carried on are the problems now being investigated: 1) Development of rapid and sensitive analytical methods suitable to the determination of traces of metals and other minor elements in various materials, such as rock, soils, plants, and water. At the present time attention is being concentrated on U, Bi, Cr, and Hg, and satisfactory rapid trace analytical methods are virtually perfected for U and Bi. Good methods are also available for: Cu, Zn, Pb, Ni, Co, As, Sb, W, Mo, Ag, Nb, Ge, V, Ti, Fe, Mn, S, and P. 2) The relation of geochemical anomalies in plant materials to the geochemical distribution of elements in soils surrounding the plant. 3) A study of the dispersion halos in transported sedimentary cover such as glacial drift and alluvium over known orebodies. 4) A study of the behavior of ore metals in the weathering cycle. 5) A study of the behavior of the ore metals during magmatic differentiation. This requires a study of the distribution of minor metals in fresh igneous rocks and their component minerals in a well established differentiation series and in adjacent country rock. 6) A study of the dispersion of metals in primary halos in the wall rock surrounding orebodies. 7) Regional and local studies of the metal content of surface and groundwater in mineralized and barren areas. Many field projects of the Mineral Deposits Branch also require the services of USGS chemists during their investigation of the geochemical environment of ore deposits. From the work that has been done certain general principles have emerged. Concentrations of an element that are above the general or background value of barren material are called positive geochemical anomalies or simply an anomaly, whereas values less than background are called negative anomalies. The anomalies most commonly investigated in geochemical prospecting are those formed at the earth&apos;s surface by agents of weathering, erosion, or surficial transportation, but more and more attention is being given to primary anomalies found

Jan 1, 1956

By N. I. Fisher, J. Shepherd

A rapid method of determining natural fracture trends in collieries has been developed. The method will yield information that is precise enough to permit fracture domain boundaries to be delineated in a coal seam. Instead of a survey of cleat trends in a colliery taking several man-weeks or even man-months, a reconnaissance survey can be carried out in only a few man-days. At each of a sequence of sampling sites along a traverse, five measurements of trend are recorded for each set of fracture directions. A sequential plot of the medians of each fracture set is then made manually underground or by a computer in the mine office. Changes in fracture pattern can be detected easily in colliery development work if a geologist visits advancing faces regularly, and forecasts can be made about the likelihood of forthcoming faults and dykes. A full description of this method is given in Shepherd and Fisher (1981). The concept of mapping fractures rapidly in a colliery is based on using a geological traverse (Compton, 1962), along which observations can be made at chosen, regular intervals. The technique has been widely used for surface mapping across outcrops and in follow-up work in photogeological studies (Hepworth and Kennerley, 1970). In these cases, the geologist surveys the traverse line as mapping proceeds. In a colliery, however, ready-made traverse lines already exist in panels and along main roadways, often in several directions. It is thus possible to traverse a colliery in different directions and record the fracture trends at intervals, generating a reconnaissance fracture map. This can also be done on a continuing basis as mine development takes place. Generally, a sampling traverse should be longer than 0.5 km with sampling sites at relatively close-spaced intervals along the traverse. For example, in room-and-pillar mines pillars are commonly formed on 40-m centers and the sampling sites can then be arranged at 20-m intervals [(Fig. 1)]. The sites might have to be closer together for mines known to have bad mining conditions. The predominant fracture trend is normally the face cleat and the subordinate trend is the butt cleat (McCulloch et al.. 1974). Various changes can occur in the cleat or joint pattern: the face and butt sets may disappear or an entirely new set or sets may appear. Therefore, it is best to record all prominent fracture sets. Sometimes there is only one; in other cases there may be as many as three or more. An odd number of measurements of each fracture set are made (generally five or more) to enable the median value to be determined easily. The median value can be plotted underground using graph paper or a computer plot can be made in the laboratory or mine office [(Fig. 2)]. The sequential linked median (SLIME) plot draws the median trend for each sampling site as a unit line segment. The segments from successive sampling sites can be connected together to form a long chain [(Fig. 2A)]. The needle plot, on the other hand, draws a straight line to represent the traverse and then plots out the median trend for each sampling site [(Fig. 2B)]. The SLIME plot is better for visual display, as it highlights small irregularities and gross changes in trend. However, some work is required to relate the individual segments to their site location along a traverse. In this respect, the needle plot is more convenient because each segment -can be plotted-at a point corresponding to its location. Also, there is precise match-up if needle plots of face and butt cleat are compared. A description and listing of the SLIME program is given by White et al. (1981). An example of the use of this method is given for Wallsend Borehole colliery in New South Wales (Australia) [(Fig. 2)], where domains II and IV are associated with mining hazards. Domain II is coincident with a normal fault of 2.6-m throw, and domain IV with a basic dyke 12 m thick. These hazards were approached driving in a southwesterly direction, and a pronounced change in trend of the cleat to a northwesterly direction occurred at a distance of approximately 45 m from each one. The northwestern joint trend is parallel to that of the dyke and fault, and it occurs at a higher frequency close to these structures. The association of a particular joint set with faults has been found elsewhere (Shepherd and Creasey, 1979). The two minor cleat direction changes within domain V are narrow joint zones that are less than 5 m wide. The fracture trends derived from a SLIME traverse can be verified by collecting larger quantities of data at selected sites, as shown in the balloon density (rose) plots depicted in [Fig. 2C]. We are grateful for the financial support provided by Thiess Bros. Pty. Ltd. and the National Energy Research, Development, and Demonstration Program administered by the Commonwealth Department of National Development and Energy. R.W. Miller Holdings Ltd. and Thiess Bros. Pty. Ltd. are thanked for their permission to publish data from their collieries.

Jan 1, 1982

By Frank C. Kelton

It is perhaps not widely realized that extraction and saturation processes carried out on oil well core samples alter the properties of these samples to varying degrees. On the other hand it is felt by some that quick-freezing of core samples increases their permeability and porosity significantly. Accordingly, laboratory tests were carried out on 49 pairs of horizontally adjacent samples in order to differentiate between the effect of quick-freezing per se on permeability and porosity of the samples, as distinguished from the effect of the identical saturation treatment on permeability and porosity of the companion samples. Also, additional field data were obtained on comparison of frozen vs unfrozen companion samples. LABORATORY INVESTIGATION OF FREEZING us SATURATION EFFECTS Procedure The samples used in these tests were two-cm cubes cut in horizontally adjacent pairs from cores from eight Gulf Coast and Mid-Continent wells, which cores had not previously been frozen. These samples were extracted with carbon tetrachloride, dried, and air permeabilities run in the conventional manner. They were then evacuated and saturated with brine of 25,000 ppm sodium chloride content, and porosities determined by gain in weight. The samples were partially desaturated by evaporation down to an average brine saturation of 68 per cent. One sample from each pair was quick-frozen by covering with dry ice after wrapping in a single layer of paper, and allowed to remain frozen for about two hours; the companion sample from each pair was not frozen. After thawing the frozen sample, all samples were immersed in tap water overnight in order to leach out most of the brine. Air permeabilities were re-run, and the samples were again saturated with brine to determine a second porosity value. For purposes of averaging of data, the samples were grouped according to four permeability ranges, from 0 to 10, 10 to 100, 100 to 1,000, and 1,000 to 3,840 md. Average permeability and porosity changes for the frozen vs the unfrozen adjacent samples are shown in Table 1. Discussion As may be seen from Table 1, the averages of the per cent permeability increases for the quick-frozen samples ranged from 3.8 to 12.9 per cent among the four permeability groups. The average changes among the four groups of unfrozen companion samples ranged from a decrease of 0.2 per cent to an increase of 9.3 per cent. There was no particular correlation of these changes with magnitude of permeability; however, the increase for each group of frozen samples paralleled the increase for the corresponding unfrozen samples. The differences between the two sets of values are believed to be a valid indication of the effect of the quick-freezing in itself, since the treatment of the two samples in each pair was identical except for freezing. The permeability changes which are strictly the result of the quick-freezing are shown in the sixth column of Table 1. These range from a decrease of 0.9 per cent to an increase of 4.0 per cent; the overall weighted average is 1.2 per cent, as compared to an average increase of 6.8 per cent caused by the saturation treatment of the samples not frozen. The average porosity changes are in general smaller than the changes in permeability, and range from a decrease of 2.3 per cent to an increase of 3.3 per cent. The overall weighted average change ascribed to the quick-freezing is 1.0 per cent of porosity. Many factors can contribute to the changes in permeability and porosity observed when subjecting cores to the simple processes used in these tests. Such are: hydration and swelling of clay, adsorption of ions, changes in surface structure and wettability, expansion and compression effects due to ice formation, shrinking and cracking, leaching of salts and colloids, displacement of particles resulting in either blocking or enlarging of pore openings. Whatever particular mechanisms are involved. however, it is apparent not only from this study but also from other investigations in the literature&apos; not directly concerned with quick-freezing, that the effects produced by commonly used extraction, saturation and drying techniques may be of considerable magnitude The results of this study indicate that for the particular samples and techniques used, such effects are of the order of five to six times the effect of quick-freezing. insofar as changes in permeability are concerned. It may be argued that these samples might not include extremely shaly material where the effect of freezing upon permeability may be much greater. However, had such material been available for these tests, it would undoubtedly have been very susceptible also to alteration by the extraction and saturation treatment used. To investigate this point further, the individual sample data were re-grouped according to the magnitude of the average per cent permeability increases for the pairs of samples, irrespective of permeability. The results

Jan 1, 1953