By R. W. Armstrong, P. C. Jindal

The hardness dependence on grain size for polycrys-talline cartridge brass and a leaded brass has been measured by Brine11 and Rockwell B testing. In each case, the hardness, H, depends on the average grain diameter, 1, according to: H =Ho + kHl-1/2 where Ho and kH are experimental constants. Diamond pyramid hardness values have also been measured as a function of the indentation size and grain size to give additional information on the nature of the hardness test and the dependence of hardness on micro-structure. The hardness of polycrystalline brass depends on its grain size. Bassett and Davis' demonstrated this as early as 1919 by making Brinell hardness measurements on cartridge brass. Since then, the hardness of this type of material has been measured as a function of grain size by making Rockwell,2'3 Vickers,4 and Brinell5 tests. he hardness dependence on grain size has also been measured for other materials. Angus and summers6 investigated the grain size dependence of the Brinell hardness of polycrystalline copper and a Cu-4.5 pct Sn bronze. In other studies, nickel,? Armco iron,Big an Fe-0.07 pct C alloy,I0 and an 0.39 pct C-12.45 pct Cr stainless steel" have been investigated. In some of the preceding cases, the hardness results have been analyzed to show that the hardness varies with the average grain diameter, 1, according to an l-l\4, l-1/4 or I-2 dependence,11-13 The studies of the influence of grain size on hardness have not been based on any theoretical model. This may be because the hardness of a material is itself a complicated property. However, attempts have been made to correlate, experimentally and theoretically, the hardness of a material with its unidirectional stress-strain behavior.14-l6 On this basis, Hall" proposed that the polycrystal hardness dependence on grain size might follow directly from the Hall-Petch18,19 relation for the grain size dependence of the yield stress. Thus, the hardness-grain size relation was given as: H = Ho + kHl-1/2 [1] where Ho and kH were taken as experimental constants. The relation was applied to the measurements on brass,' copper,6 bronze,= and Armco iron.' More recently, this relation was shown by Armstrong and jindal20 to adequately describe the measurements on cartridge brass made by Bassett and Davis' and Babyak and Rhines.5 In this case, the relationship was taken a step further by independently relating the values of Ho and kH to the values of oyand ky, previously reported by Armstrong, Codd, Douthwaite, and petch21 from measurements of the yield stress dependence on grain size for this type of material. In the present investigation, new Brinell and Rockwell B hardness measurements have been made as a function of grain size for a cartridge brass and a leaded brass. In addition, diamond pyramid hardness values were measured as a function of the indentation size. All these results are applied to a further analysis of the hardness dependence on grain size. MATERIALS AND EXPERIMENTAL METHODS Cartridge brass and a leaded brass were selected for this investigation for two main reasons: it was anticipated 1) that these materials could be cold-worked and recrystallized to a wide range in grain size and 2) that the results to be obtained on these typical industrial materials could be usefully compared with previous investigations. The chemical analyses of the actual materials which were employed are given in Table I. The as-received 1/2- and 3/4-in.-thick plates were given various reductions in thickness by cold rolling. The rolled material was heat-treated at various temperatures between 330" and 850°C for differing time periods from 5 min to 9 hr to achieve a variation in the average grain diameter between 0.0339 and 0.000543 cm.22 During heat treatment, the brass was protected from zinc loss by packing it in chips or foils of the same composition material. Reasonably equi-axed grain structures were obtained in each case. The metallurgical grain sizes of the specimens were determined from measurements of the average linear intercept on a random line. Annealing twin interfaces were not counted along with grain boundaries. The

Jan 1, 1970

By L. D. Mullins, E. B. Elfrink, W. L. Wahl

In the past few years several articles and papers presenting results of solution gas-drive depletion calculations have appeared in the lit-erature. Such calculations are of interest to the oil industry, for investment decisions must often be made before much is known about a reservoir. At other times, an estimate of the possible benefits to be realized from alternate production methods is desirable, and theoretical depletion calculations can serve as a floor or reference level from which to work. In any case, an estimate of ultimate oil recovery based upon engineering data is commonly required. An engineer confronted with the problem of obtaining, for a specific reservoir system, an estimate of ultimate oil recovery by solution gas-drive depletion usually will be forced to perform the calculations himself. This is despite the quantity of data in the literature. Rarely will either experience or the literature provide results from a reservoir system similar in all important respects to the one under consideration, and calculated results are not so plentiful that satisfactory interpolation procedures can be devised. Performing the calculations, however, is a tedious, time-consuming task unless an electronic computer is available, and, in practice, time and manpower are not always available for this purpose. A quick, simple, consistent method was needed for reducing the uncer- tainty in estimated oil recovery from solution gas-drive reservoirs when only minimum information about the reservoir system is available. PROCEDURE Method of Calculation The usual requisite assumptions were made so that the material balance equation could be used to calculate data for the charts. The following assumptions were made: (1) the reservoir is homogeneous and isotropic; (2) oil recovery is due entirely to solution gas drive and neither a gas cap nor a water drive nor gravity drainage is present; (3) the initial reservoir pressure is the bubble-point pressure of the reservoir fluid; (4) initial total liquid saturation is 100 per cent of pore space; (5) interstitial water saturation remains at the initial value as the reservoir pressure declines from the bubble-point pressure to atmospheric pressure; (6) equilibrium gas saturation is 5 per cent of pore space; and (7) oil and gas saturations are uniformly distributed throughout the reservoir at all times. There are no saturation gradients due to a wellbore, nor is the geometry of the reservoir system considered. The material balance equation was written in the form of a differential equation' which was integrated to determine the change in oil saturation for an assigned pressure drop. Formal integration was not possible, so recourse was made to the Runge-Kutta method' of numerical integration. All computations were performed on IBM equipment. Numerical integration yielded the change in oil saturation within the reservoir as the pressure. declined from the bubble-point pressure to atmospheric pressure. The initial oil saturation minus the change in oil saturation yielded the oil saturation at atmospheric pressure. The oil originally in place was obtained by dividing the initial oil saturation by the initial formation volume factor (differential liberation) while the oil in place at atmospheric pressure was obtained by dividing the final oil saturation by the formation volume factor at atmospheric pressure. U1timate oil recovery, expressed as a percentage of the initial oil in place, was obtained by dividing the difference between the oil initially in place and the oil in place at atmospheric pressure by the oil initially in place and multiplying by 100. PVT Data Charts were based upon 135 solutions to the material balance equation. PVT properties of the reservoir fluids were variables in this equation and had to be known as functions of pressure. The required PVT data might have been obtained from either actual reservoir fluid systems or correlated data. However, correlated PVT data were developed and employed in the calculations for the following reasons: (1) it is doubtful that 135 sets of PVT data could have been obtained for the values of variables investigated in this study, and (2) results of recovery calculations from randomly obtained PVT data could not be correlated as well as rssults from selected PVT data. The PVT data used to develop the

By J. C. Shyne, T. D. Gulden

The steady-state creep behavior, in compression, of indium containing a dispersion of atomized glass particles was studzed over a range of temperature, stress, and composition. The observed behavior was not consistent with a simple model of dislocation climb over dispersed particles. From room temperature to about 100°C the temperature dependence could be described by an activation energy about one and a half times that of self-dijfusion in indium while at higher temperatures a much higher ternperature dependence was observed. THE value of dispersion-hardened and precipitation-hardened alloys has long been recognized. The mechanism of hardening, however, is not completely understood, especially at elevated temperatures where dispersed particles increase creep resistance. Following the suggestion of Schoeck1 that the rate of creep in dispersion-hardened materials is controlled by dislocation climb over second-phase particles, Ansel and weertman2 derived steady-state creep equations for dispersion-hardened materials. Their derivation was based on dislocation climb over non-deformable spherical particles in a metallic matrix. For low stresses they predicted a linear relation between applied stress and steady-state creep rate. For stresses large enough to cause dislocations to pinch off around the precipitate particles, the theoretical creep rate was shown to be proportional to the fourth power of stress. For very high stresses an exponential stress dependence was predicted. In all cases the theoretical creep rate is linearly proportional to the diffusion coefficient. This provided the primary temperature-dependent factor. Subsequently, Ansel and Lenel3 reported some experimental data on SAP, a composite of aluminum and aluminum oxide, that was in good qualitative agreement with the above theories. Their experimental creep rates, however, were four orders of magnitude less than the theory predicts. This was attributed to a low density of active dislocation sources in the material; somehow the dispersed particles inactivated the dislocation sources instead of merely interferring with dislocation motion. Meyers and sherby4 have recently reported on the creep behavior of SAP. Their results were inconsistent with a simple dispersion-strengthening model and led them to conclude that a continuous network of oxide controls the high-temperature mechanical characteristics of SAP. Because of the rather complex mechanical behavior of SAP and the lack of agreement about the morphology of its oxide phase, it appeared desirable to study the creep of a dispersion-strengthened material of controlled morphology. For the present work a dispersion of spherical glass particles imbedded in a matrix of indium was chosen. The microstructure of this material was similar to the idealized uniform dispersion of hard spheres in a deforming matrix assumed by Ansel and Weertman in their theoretical treatment. SPECIMEN PREPARATION For experimental convenience, it was decided to use a low melting-point metal in this investigation. It was necessary that the metal not be oxidized readily up to its melting temperature and that it wet the second-phase particles. It was desired that the material chosen for the dispersed phase be available as a fine powder with closely controlled size and shape. The material chosen to satisfy these requirements consisted of a matrix of indium metal containing a dispersion of atomized particles of a soft soda-lime-silica glass ranging from 5 to 30 µ in diam. The glass particles had a highly regular spherical shape. The composite was made by stirring the glass powder into liquid indium maintained at a temperature just above the melting point of indium, 156°C. The creep specimens were prepared by a hot pressing operation. Five to ten g of the mixture were placed in a steel die and pressed at 125°C for 5 min under a pressure of 30,000 psi. The resulting specimens were cylinders about 3/8 in. in diam and ranged from 0.4 to 0.7 in. high. By following this procedure a uniform dispersion was obtained in the creep specimens. Typical microstructures of specimens containing twenty and forty volume percent glass powder are shown in Figs. 1 and 2. Unfortunately, grain size could not be determined by the metallo-graphic techniques used. CREEP TESTING PROCEDURE Creep tests were performed in compression under constant stress. The specimens were placed in

Jan 1, 1963

By Nicholas J. Grant, A. W. Mullendore, Paul Predecki

The Duwez technique of splat cooling in which a molten droplet of metal is accelerated and made to impact on a cold, highly conducting substrate was investigated.- An apparatus for producing "splat" was constructed employing an explosive powder charge to accelerate the molten metal. Transport of the molten metal just prior to impact with the substrate was studied by means of high-speed photography. The molten particles are small spherical droplets from about 1 to 50 µ diameter. The average cooling rates for aluminum, silver, and a gold alloy splatted on nickel substrates at room temperature were determined experimentally and were found to vary from 18 to 5 x 10' C per sec. The heat-transfer coeficients for pure aluminum and pure silver splats cooled on nickel substrates at room temperature were found to be 2.7 to 6.8 and 13.6 to 54.2 cal per sec sq cm 'C (2 to 5 x 104 and 1 to 4 x 18 Btu per hr sq ft OF), respectively. Solidification rates in pure aluminum and silver splats were calculated. "SPLAT cooling" is a term describing a technique for extremely rapid freezing and cooling of molten metals and alloys to room temperature or below. The technique was developed by Duwez et al.' in 1960, and after refinement2 consisted in transferring a few tenths of a gram of molten metal to near sonic velocity to strike a suitably placed cold copper surface. Upon impact, the metal spread into a thin nonuniform film called a splat, about 10-4 cm thick. The splat particles produced in this manner were thin enough in some areas to be suitable for transmission electron microscopy, without further treatment, and, together with X-ray data, yielded a variety of structures which would be classified as follows: 1) supersaturated solid solutions (increase in solubility limit), 2) metastable crystalline stoichiometric and non-stoichiometric intermediate phases ( in Au-20.5 at. pct Si and in Au-14 at. pct Sb, respectively), 3) amorphous alloys, 4) retained high-temperature phases, 5) alloys having equilibrium phases present, but with unusual, markedly altered structures. The crystalline phases present in splats were usually extremely fine-grained and had low dislocation densities. Present interest in splat cooling centers around a study of the unusual structures produced by the technique, their contribution to alloy theory, and the possibility of the development of new or unusual properties. In addition, the technique is being examined for the production of bulk quantities of new high-strength alloys for low- and high-temperature use. Although a number of alloy systems have already been investigated by the technique, relatively little is known about the mechanism of splat formation and the physical conditions encountered by the metal during solidification and cooling. The purpose of this work was: 1) to determine the velocity, shape, and size of the molten metal droplets just prior to impact with the cold substrate; 2) to try to estimate or measure solidification rates, heat-transfer coefficients, and cooling rates in splats. EXPERIMENTAL TECHNIQUE Splatting Apparatus and Procedure. An apparatus similar to the type originated by Duwez et a1.,2 but employing an explosive charge to accelerate the molten metal, was used. A "Ramset" fastening tool (a gun normally used for driving studs into concrete, steel, and so forth) was mounted vertically above a resistance-heated graphite crucible as shown schematically in Fig. 1. A splat product was produced by melting a few tenths of a gram of metal at the position shown in Fig. 1, and then exploding a powder charge in the breach. The shock wave thus generated traveled down the barrel into the furnace, ejecting the molten metal through the 0.06-in.-diameter hole at the bottom of the crucible. The ejected metal was impacted on a high-conductivity metallic substrate where it formed a splat. High-Speed silhouette Photography. In order to investigate the size and shape of the ejected, molten metal just prior to impact with the cold substrate, high-speed silhouette photographs were taken, and are shown in Figs. 2 and 3. These photographs were obtained with the aid of an Edger-ton, Germeshausen, and Grier microflash unit and a submicrosecond flash drive equipped with a variable time delay. Two types of triggers were

Jan 1, 1965

By Elmars Ence, Harold Margolin

The Ti-Fe and Ti-Fe-0 systems were re-examined because of the controversy regarding the existence of Ti2Fe, and to consider all available data points to the existence of Ti,Fe. The Ti-Fe-0 system contains two ternary compounds: E, corresponding to Ti2Fe; and y. SEVERAL authors have investigated the constitution of titanium-rich alloys of the Ti-Fe system. The most extensive study of titanium-rich portions of the Ti-Fe system was by Van Thyne, Kessler, and Hansen,' who investigated this system up to 50 pet Fe and used the highest purity materials available for their alloy preparation (iodide titanium was used for alloys up to 20 pet Fe). According to Van Thyne et al., phase relationships in the region of investigation are governed by phases a,ß, and TiFe. No evidence of an intermetallic compound Ti,Fe was found. although earlier. works by Laves and Wallbaum,' and Duwez and Taylor' reported its existence. Rostoker's study on the occurrence of TilX phases" confirmed the findings of Van Thyne et al. Rostoker proposed that the compound Ti Fe found by Duwez does not exist but is actually a ternary compound, Ti1Fe3O, originated by inadvertent oxygen contamination. The partial isothermal section of the ternary Ti-Fe-0 system as reported by Rostoker' seems to confirm this explanation. In the course of phase diagram work conducted at New York University, however, certain irregularities were observed to be associated with ternary systems of the type Ti-Fe-X. The ternary phase 6, observed in the systems Ti-Fe-Mo' and Ti-Fe-V." was found to be structurally identical to the com-pound Ti2Fe as reported by Duwez and Taylor, and to Rostoker's compound Ti1,Fe2O. Since the amount of oxygen possibly present in the Ti-Fe-Mo and Ti-Fe-V systems could not account for the observed amounts of the compound, it appears that the d phase in these systems is not Ti,Fe,O. On the other hand, considering the amounts of the 6 phase, particularly in the Ti-Fe-Mo system, the location of the phase was uncertain. It was felt that the introduction of the Ti2Fe phase would alleviate some of the inconsistencies of the two systems. Because of the uncertainties relating to the phase Ti2Fe, or Ti1Fe2O, it appeared worthwhile to re-examine the Ti-Fe and Ti-Fe-O systems in the vicinity of these compounds with highly sensitive metallographic techniques and with X-ray methods. Experimental Procedure Alloy Preparation—For the study of the binary system four alloys were prepared, containing 26.9 (30 wt pct), 34.0 (37.5 wt pet), 41.2 (45 wt pet), and 56.3 (60 wt pet) atomic pet Fe, and for the ternary Ti-Fe-O system 18 alloys were prepared in the composition range of 1.6 to 16.9 atomic pet 0 and 24.3 to 55.7 atomic pet Fe. The materials used for the Ti-Fe alloys were iodide titanium (99.98 pet Ti, 0.002 pet 0) and Ferro-vac-E iron (99.95 pet Fe, 0.0052 to 0.0072 pet 0). For the Ti-Fe-O study the materials used were sponge titanium containing less than 0.06 pet 0, Ferrovnc-E iron, and Baker's analyzed TiO2. The nominal weight and atomic percentages of the ternary alloys prepared are shown in Table I. Melting—Charges of 10 to 15 g were melted in a nonconsumable arc furnace in argon atmosphere according to the technique described elsewhere.'" Since there was practically no weight loss through the various stages of melting and oxygen losses have not been observed previously, it appeared justifiable to use nominal composition for interpretation of data. Iodide titanium control buttons, of the same mass as the Ti-Fe charges, and melted under the same conditions, were used to check hardness pickup during melting. A hardness increase of 2 to 3 Vhn was found. Heat Treatment—The specimens were annealed in quartz capsules under argon. To avoid contact between the specimen and capsule material all specimens were wrapped in titanium sheet. The annealing times are given in Table 11. The attain-

Jan 1, 1957

By K. H. Kilgren

At high formation pressures the distillate produced from a gas-condensate reservoir may be black in color. In this event the dense gas phase existing above the dew point is correspondingly dark. Volumetric phase data and an analysis of a reservoir fluid exhibiting these characteristics, together with a description of the visual equilibrium cell in which these observations were made, are presented in this paper. INTRODUCTION Previously the author, like many others in the oil and gas industry perhaps, tacitly assumed that the expressions black or dark oil system, crude oil system and bubble-point system were synonymous. Crude oil reservoir fluids are bubble-point systems and yield a black or dark stock-tank oil of relatively low API gravity. Conversely, a clear or amber colored trap distillate of high API gravity is assumed indicative of a dew point system or a gas-condensate reservoir fluid. This broad classification appears satisfactory for shallow reservoirs, but as the following study demonstrates, may be misleading when applied to deep reservoirs. Theoretically, there is no reason to exclude the possibility of producing a dark, low-gravity distillate from a gas-condensate reservoir. At sufficiently high values of pressure and temperature, heavy, dark-colored hydrocarbons may exist in the vapor state of a multi-component system. If enough dark-colored components are present in the reservoir vapor phase, the resulting condensate will be dark. The reservoir fluid investigated in the present study supports this contention. Stock-tank production was black in color and measured 29" APT gravity. From outward appearances, the liquid closely resembled a medium gravity crude oil. Experimental measurements proved the reservoir fluid was in reality a gas-condensate system. Volumetric phase data for this high-pressure system and a description of the visual cell in which the study was conducted successfully are presented in this paper. THEORY Phase behavior of a reservoir fluid can be predicted accurately with reference to a pressure-temperature phase diagram. If the reservoir temperature is lower than the critical temperature of the hydrocarbon fluid in place, bubble-point behavior will be observed. If the reservoir temperature lies between the critical and cricondentherm temperature, dew point behavior and retrograde condensation will occur. For reservoir temperatures above the cri- condentherm, only a single gas phase can exist in the reservoir regardless of pressure. Providing the composition of the reservoir fluid were known, it would be possible to predict the critical temperature and estimate the phase behavior from equilibrium relationships. However, the usual practice is to obtain a sample of reservoir fluid, subject it to varying pressures at the reservoir temperature and observe the phase behavior experimentally. The latter method was used to obtain the data reported here. WELL AND TRAPPING INFORMATION A summary of pertinent data for the well from which the reservoir fluid was sampled is presented in Table 1. This well is located offshore Louisiana. Except for the pressure which substantially exceeds hydrostatic pressure, the information does not appear unusual. Prior to the sampling program, the well was produced for 22 hours at a stock tank oil rate of 139 B/D. Average trapping conditions and gauging data for the six-hour test period that followed are summarized in Table 2. Samples of the first-stage trap gas and liquid were obtained during the latter portion of the test period. Ambient temperature remained 5 to 10F below trap temperature and presented no problem for sampling. Surface wind and moderate foaming of stock-tank oil presented some difficulty in obtaining accurate stock-tank gauges. SAMPLE ANALYSIS Compositions of the gas and liquid samples are shown in Table 3. The trap gas was analyzed by isothermal chromatography which revealed only a trace of heptane in the stream. The trap liquid was initially analyzed by low-temperature fractional distillation, yielding a bottom product of heptane and heavier components. Specific gravity of this fraction was measured and the mol weight was determined by freezing point depression. The hexane and lighter overhead gas collected during distillation was

Jan 1, 1967

By S. Feuerstein, L. Rice

The effect of low pressures on the flow and fracture behavior of molybdenum is described. For poly crystalline samples, room-temperature tensile tests indicate greater ductility under 10 Torr than under intermediate pressures up to and including atmospheric pressure (760 Torr). In addition, tests conducted at 760 Torr under atmospheres of air, dry nitrogen, and purified argon exhibited no apparent difference in mechanical properties. Critical tests involving baking in situ as well as those involving single-crystal deformation further imply that the ductility effect is a pressure-dependent phenomenon related only to the fracture process. This dependency is discussed in terms of adsorption and diffusion contributions. THE effect of very low pressures on material properties has heretofore been presumed to be important only for substances possessing relatively high vapor pressures at ambient temperatures. Research has therefore been concentrated primarily on organic solids and liquids, and in some instances on metals such as zinc and cadmium. Most vacuum-effect studies' on the mechanical behavior of metals have been performed under conditions of either cyclic loading or creep rupture at elevated temperatures, i.e., over extended time periods. These studies were not restricted to high vapor pressure materials but also encompassed such metals as gold, copper, and nickel. Very little concern, however, was placed upon the importance of a vacuum environment on the mechanical behavior of metals subjected to a simple unidirectional deformation at ambient temperatures. A tension test is generally of short duration as compared to a creep test, and at room temperature vacuum effects if any would be expected to be surface-limited. In early 1963, Kramer and podlaseck2 reported a change in the bulk flow behavior of aluminum single crystals during room-temperature tension tests. The deformations were performed under pressure conditions of 760 to 3.4 X 10-8 Torr and indicated for the first time a vacuum surface effect contributing to the bulk tensile behavior of metal specimens. As a consequence, an experimental program was initiated in this Laboratory to study the effects of ultrahigh-vacuum conditions on the mechanical behavior of metals. The results of a preliminary study on poly-crystalline molybdenum3 revealed, unlike Kramer's observations of changes in the stress-strain behavior, only an increased ductility under ultrahigh vacuum. Flow behaviors were nearly identical for all tests re- gardless of pressure. This paper presents comprehensive results obtained in this area of research. 1) EXPERIMENTAL PROCEDURE Three material categories were used in this study: sintered and are-cast polycrystalline molybdenum of nominal purity 99.93+ pct and single-pass electron-beam zone-refined molybdenum single crystals having a nominal purity level of 99.99+ pct. The interstitial levels (weight percent) as determined by the Materials Testing Laboratories, Division of Magnaflux Corp., were as follows: sintered molybdenum (C— 0.005, H—0.0004, O—0.015, N—0.008); and arc-cast molybdenum (C-0.0038, H-0.0003, O-0.015, N-0.023). Single-crystal molybdenum obtained from Materials Research Corp. had a typical interstitial analysis of C-0.0015, H-0.00007, O—0.00045, and N-0.0001. Tensile specimens having a 5 mm diam by 50.8 mm length were prepared from these materials. An average grain diameter of 0.059 mm was obtained for the sintered specimens following a 4-hr, 1600°C heat treatment. Grain sizes from 0.019 to 0.149 mm were obtained in the arc-cast specimens following heat treatments from 1100° to 1600°C for 1 hr. This series of specimens was used exclusively for the grain-size effect studies. All samples were electrolytically polished in 97 pct sulfuric acid solution prior to testing. Experiments were performed at room temperature in an ion-pumped ultrahigh-vacuum system positioned in an Instron tensile machine, Fig. 1. A constant strain rate of 4.2 x 10-4 sec-1 as derived from crosshead displacement was assumed for the deformations. Starting vacuums ranged from 2 to 0.5 X 10-10 Torr. These pressure measurements were made using corrected values4 of an NRC Redhead gage. Comparative readings were also made against a G.E. triggered dis-

Jan 1, 1967

By M. M. Mebta, G. W. Dean, W. H. Somerton

With the advent of underground heating operations, interest has developed in the alteration of rock properties by high-temperature treatment. In the present work a number of sandstones were heated to temperatures in the range of 400°C to 800°C under both atmospheric and simulated reservoir pressures. Pertneabilities increased by at least 50 per cent and sonic velocities and breaking strerlgths decreased by an equivalent amount. Differential thermal expansion and other reactions of constituent min-era1 grains are the causes of these alterations. INTRODUCTION In the underground combustion of petroleum reservoirs, temperatures of the order of 600C are reported to have been reached in the combustion zone.' At this temperature rocks are subject to extensive thermal alteration. Temperatures of this magnitude and higher may also occur in subsurface formations when subjected to bottom-hole heating, thermal drilling operations, and underground nuclear explosions. Temperatures of this magnitude might also be generated by conventional rock drilling methods at points of bit-tooth contact. In earlier work, the permanent deformation of rocks resulting from heating was reported. Major structural damage of rocks occurs due to differential thermal expansion of mineral constituents. A number of mineral alterations including crystal inversions, loss of water of crystallization and dissociation, may also contribute to changes in physical structure and properties of rock. In the present work, samples of three typical sandstones were heated to several temperatures up to a maximum of 800C and then allowed to cool to room temperature. Heating was done under both atmospheric pressure and simulated reservoir pressure conditions. Physical properties of the samples were measured before and after heating and comparisons made. Measured properties included permeability, sonic velocity, breaking strength and fracture index. Changes in physical properties were compared to changes in mineralogical characteristics as determined by thin-section. X-ray diffraction and chemical tests. EQUIPMENT AND PROCEDURE Two outcrop sandstones (Bandera and Berea) and one sub-surface sandstone (St. Peter) were selected for the tests. These samples have a wide ranee in composition and physical properties as shown in Table 1. The first series of tests was made on 2-in. diameter by 5-in. long test specimens. Test specimens used in all later work were 3/4-in. diameter by 1 1/8-in. long, this being the specimen size required for heating at simulated reservoir pressures. After careful washing, the cores were oven dried at 100 ± 5C for a minimum of 24 hours before the tests were run. Test specimens were heated in an electric furnace at a constant rate of temperature increase of 3C per minute. When maximum temperature of the run was reached, the sample was allowed to soak for one hour. The furnace was then cooled to room temperature at the same rate of 3C per minute. The entire heating operation was designed for reproducibility without subjecting the test specimens to excessive thermal shock. For samples heated under simulated reservoir pressures, a pressure cell designed by Dean was used (Fig. 1).3 The core sample was inserted into a thin-walled (0.006 to 0.01-in.) copper cup which was then mounted in a high-pressure cell. Provisions were made for the application of internal pore pressure as well as confining pressure. Tests showed that the thin-walled copper cup closed tightly around the core and satisfactorily transmitted confining pressure to the core. The core was heated by placing the entire cell into the electric furnace. The heating program was the same as that used in the atmospheric pressure runs: tempera-ture rise of 3C per minute to maximum temperature of the test, soaking at maximum temperature for one hour, and cooling at a rate of approximately 3C per minute. The cell was designed to withstand 5,000 psi at 1,000C. However, since it was considered likely that repeated heating and cooling would in time weaken the steel, 2,000 psi at 850C was set as a working limit. In the present series of tests, the pore pressure was held constant at 750 psi and the confining pressure at 1.500 psi. The pressure source was a high-pressure nitrogen tank. The two pressures were controlled manually but are accurate well within ± 50 psi.

Jan 1, 1966

By Jonas Svensson

A new method is described for the production of cold-bonded pellets using a hydraulic binder, such as portland cement. Large-scale pilot-plant tests have proved that self-fluxing pellets of high reducibility and good handling strength can be made by the method. Blast-furnace trials have shown that the pellets are an acceptable burden material, comparable with self-fluxing sinter or heat-hardened pellets. Economic factors of commercial-scale production are discussed. The Grangcold Pellet Process—for which patents have been applied or already granted in a number of coun-tries—uses a hydraulic adhesive such as portland cement, slag cements, pozzolanic cements, etc., for the production of cold-bonded pellets. The idea of using a hydraulic binder for the agglomeration of iron-ore fines is not new. Portland cement was proposed as an adhesive for cold-bonded iron-ore briquettes in patents granted more than 50 years ago.' In a report on the briquetting of iron-ore fines, published in Stahl und Eisen in 1959; it is stated that briquettes bonded with portland cement are used on a small scale at an ironwork in Germany. According to the report, the briquettes showed excellent strength in the blast furnace although their general use was made impossible because they required a long hardening time, during which they are sticky, soft, and difficult to store and handle. The Grangcold Pellet Process has overcome this particular disadvantage by mixing the balls with a suitable amount of the balling concentrate before storing them. The pellets are embedded in the concentrated during storing in such a way that they are isolated from each other and thus prevented from sticking together to form clusters. Thanks to the embedding concentrate, the pellets are subjected to a more or less uniform pressure from all sides which does not deform them. Thus, the mixture can be stored in a stockpile or in a bin until the pellets have hardened sufficiently. The concentrate is separated from the pellets by means of screening. The concentrate is returned to the balling operation and the pellets are either shipped to the blast furnace or stored for final hardening. The binder preferred for the Grangcold Pellett Process is portland-cement clinker, ground without the admixture of gypsum in order to avoid sulfur in the pellets as far as possible. Usually a 10% binder content is used. Two-thirds of the portland-cement clinker consist of lime and the rest is silica, alumina, and ferric oxide. Thus, self-fluxing or overbasic pellets are produced with this binder if the amount of silica in the concentrate used does not exceed 4%. The Grangcold Pellet Process was developed by the mineral Processing Laboratory of the Granges Co. Work started in 1963 with batch-scale tests. In 1966, a small pilot plant was put into operation in which 1800 tons of pellets were produced using 10% of rapid-hardening portland cement as a binder. Favorable results from a blast-furnace test with this batch led to the decision to erect a larger pilot plant which went into production in the summer of 1967. Since then, approximately 100,000 tons of cold-bonded pellets have been produced, mostly with 10% gypsum-free portland cement as a binder. Several full-scale blast-furnace trials have been performed with the pellets. The results of the trials indicate that the Grangcold pellets constitute a satisfactory blast-furnace feed. An industrial plant for the production of Grangcold pellets with a rated capacity of 1.5 million tpy is now under construction at the Granges Co.'s mine at Grangesberg. The plant will come into operation in the summer of 1970. Results from Laboratory Work Pellets made from iron-ore concentrate bonded with portland cement harden slowly and their handling is very critical until they have hardened enough to loose their stickiness. It is therefore especially important to study the progress of the hardening action and the factors influencing it. This is best achieved by investigating the relationship between the compressive strength of the cement-bonded pellets and the curing time under varied conditions. The general course of this relation-

Jan 1, 1971

By R. D. West

Miscible displacenzent recovers all oil in the area contacted by the injected .fluid, whereas water or immiscible gas drives usually leave substantial amounts of oil as residual. However, the Door mobility ratios associated with a gas-driven miscible displacement cause the sweep pattern efficiency to be much lower than that obtained with water flooding. One way in which the sweep eficiency in a miscible displacement process can be increased is by decreasing the mobility behind the flooding front. This can be achieved by injecting water along with the gas which drives the miscible slug. This water reduces the relative permeability to gas in this area and thus lowers the total mobility. The main operating conditions for the simultaneous injection -vrocess are that a zone of gas exists between the miscible slug and the leading edge of the water and that a su,@cient amount of gas be injected with the water to form the pas volume which is being left in the water zone. Laboratory model studies have shown that the ultimate sweep pattern efficiency can be as high as 90 per cent for a five-spot flooding system. If gar alone is used as the driving medium an ultimate sweep-out efficiency of about 60 per cent would be obtained in the same system. I INTRODUCTION The miscible displacement processes are a step towards total oil recovery. Conventional gas or water drives usually leave 25 to 5.0 per cent of the oil as residual in the swept portion of the reservoir. This residual can be eliminated if the oil is driven by a fluid with which it is miscible. At some reservoir conditions natural gas will become miscible with the oil. This is the "high pressure gas process".' More often, the oil does not contain enough light hydrocarbons to cause the gas to become miscible with the oil at reasonable pressures. In these cases a small band of fluid which is miscible both with the oil and gas must be kept between them2. Less than 2 per cent of the reservoir volume of the slug material is needed to keep the displacement miscible. Both processes work in the same manner, recovering all of the oil in the portion of the reservoir contacted by the injected fluids. The only difference is the manner in which the miscibility between the oil and the injected gas is obtained. Previous publications have contained detailed descriptions of these processes.1,2,3,4 However, total displacement of the oil in the swept region does not guarantee an efficient recovery process. The amount of oil to be recovered is also determined by the fraction of the reservoir contacted by the flood. This fraction is largely determined by the mobilities of the fluids. (The fluid mobility is the permeability of the rock to that fluid divided by the fluid's viscosity, k/p). This. dependence of the fraction swept on the mobility ratio has been shown in previous studies. Fig. 1 shows the ultimate fraction swept in a five-spot system as a function of the mobility ratio. The small drawings show the location of the areas left unswept for two different mobility ratios. The ultimate fraction of the reservoir swept is here considered to be attained when the producing stream contains less than 5 per cent oil at reservoir conditions. THE GAS-DRIVEN MISCIBLE DISPLACEMENT Since there is no oil left in the swept region after miscible displacement the mobility in this region is very high. It is often 50 times the mobility in the unswept regions. This means that the fraction of the reservoir contacted by the injected fluid will be less for a gas-driven miscible displacement than for a conventional water or gas drive. For a five-spot injection system, water would contact the entire reservoir volume, and the low pressure gas would contact about 90 per cent of this volume, while a gas-driven miscible displacement would only contact about 65 per cent of the reservoir. This poor sweep efficiency often offsets the benefits obtained through miscible displacement. Fig. 2 shows what the recovery curves for the three processes might look like for a five-spot system. The curves show the fraction of the in-place oil recovered as a function of reser-

By D. S. Flett, A. W. Fletcher

Equilibrium studies on the extraction of nickel and cobalt with kerosine solutions of naphthenic acid have shown that an exchange extraction reaction occurs at pH 5.5. The nickel/cobalt separation factor is constant at 1.8 for constant total metal molarity and varying nickel/cobalt ratios. The separation factor decreases with increasing total metal molarity in the organic phase beyond 0.2 M and also decreases with increasing temperature. From the equilibrium data, it has been possible to derive a mathematical model for the separation of nickel from cobalt by exchange extraction in multistage systems. Experimental data from a continuously operated multistage mixer/settler apparatus has shown a reasonable correspondence with computer-calculated data. The effective separation of nickel and cobalt in sulfate solution remains a problem in hydrometallurgy and the hope that this would be solved by solvent extraction has not yet been fulfilled. With chloride solutions, advantage may be taken of the ability of cobalt to form anionic complexes with the chloride ion. It can then be readily separated from nickel, which does not form stable chloro complexes, by extraction with a suitable long chain amine. However, in hydro metallurgical operations, sulfate solutions are generally obtained in which no extractable anionic species are present. Thus, the possibility of using cationic extractants must be considered, and in this paper attention is directed to the use of carboxylic acids. The method of separation studied has been termed exchange extraction, which involves replacement of a metal in the organic phase with a more acidic metal in the aqueous phase. Thus, (BR2).+ (Az+)aqt=(AR,).+ (B2+)aq (I) where metal A is more acidic than metal B, R represents the acidic radical derived from the acid RH, and the subscripts e and aq refer to the organic and aqueous phases, respectively. Ashbrook and Ritcey' have used this method for the separation of cobalt from nickel using the sodium salt of di-2 ethyl hexyl phosphoric acid, which preferentially extracts cobalt. Some nickel is coextracted, and this is removed by exchange with cobalt ions in the feed solution by suitable countercurrent operation in a pulsed column. Much work has been carried out by a number of workers in Russia on the general use of exchange extraction for the separation of metal ions using car-boxylic acids. Gindin et aL a have demonstrated that this technique could be applied to the separation of nickel from cobalt using a C--C. carboxylic acid and have applied the technique to the production of high purity cobalt solutions for electrolysis. Further worka was concerned with the development of a process for the separation of nickel from cobalt in a pulsed column. This system permitted the separation of iron and copper from nickel and cobalt in one system. The procedure involved center feeding with acid backwashing at the top and alkali addition lower down the column. Thus the system operated under a pH gradient and the metals were distributed in the column in the order of their basicities. A similar application was studied by Gel'perin et al,4,5 for the removal of copper and iron impurities from a nickel anolyte by means of a C10-C,12 fatty acid fraction. Ginden et al,' and Fletcher and Wilson' have studied the effect of pH on the extraction of a number of metals with carboxylic acids. These studies showed that metals such as iron, copper, lead, zinc, nickel cobalt, and manganese are extracted at pH values close to the pH of hydroxide precipitation. Nickel is extracted at a slightly lower pH than cobalt and thus the nickel/cobalt separation factor has a value not much greater than 1. More basic work on complex identification has been reported by Fletcher and Flett: by Tanaka; and Jay-cock and Jones." These studies have suggested that at low loadings in the organic phase, the nickel and cobalt carboxylates appear to be dimeric and solvated by free carboxylic acid molecules. As the concentration of metal in the organic phase increases, the complex changes and larger polymeric species are formed. In order to permit assessment of the potential of carboxylic acids as extraction reagents for separation of

Jan 1, 1971

By W. K. Godfrey

The highest compressive strength cement has the highest bond strength in tests in which the cement is subjected to a confining pressure. After perforating, the bond strength is reduced to nearly zero when the pipe is supported by weak cement. Perforating does not affect the bond strength, however, when the pipe is supported by strong cement. Pipe supported by weak cement is damaged by perforating with expendable capsule jets, but is not damaged by perforating with the hollow carrier gun. High strength cements are recommended for oil wells that are to be perforated. Introduction The purpose of this work is to determine the effect of jet perforating on the bonding strength of oilwell cement at simulated down-hole conditions. Bond strength is a good criterion for determining the effectiveness of cement in performing its main function, i.e., that of isolating zones. According to the literature on the subject, the optimum cement strength for perforating is low and should not exceed 2,000 psi compressive strength. This conclusion was based on the appearance of bullet and jet perforations in neat and gel cements largely done in the absence of a confining pressure more than 15 years ago. Discussion Literature A relatively weak cement has been recommended in the literature as having optimum properties for perforating. In 1947, Oliphant and Farris tested bullet perforating of neat cements at various curing times.' Some of the tests were made at down-hole conditions. They reported that the optimum cement strength for perforating was about 2,000 psi compressive strength. Enlarged holes occurred when strength was too low, and the cement shattered and cracked when the strength was too high. In 1951, Morgan and Dumbauld tested bullet and jet perforating of neat and gel cements at surface conditions.' They reported that optimum cement has a compressive strength less than 2,000 psi. In their tests at atmospheric pressure, high strength cement shattered and cracked when perforated. Thus, the optimum cement strength was based on the appearance of neat and gel cement after perforating. In 1953, Clark showed a relation between cement strength and fluid shutoff.' He concluded that a 500 psi compressive strength is required for good fluid shutoff and that maximum bonding ability is developed at approximately 1,000 psi compressive strength. In 1964, Bell and Shore invalidated most of the conclu sions by the previous authors when they demonstrated that atmospheric pressure tests cannot be used to determine casing deformation and damage that will result from perforating under down-hole conditions.' They showed that the higher the hydrostatic pressure, the more restricted will be the expansion of gases generated by the charge. Less casing deformation and damage occurs under down-hole conditions than at atmospheric pressure. In recent work, Bearden et al. reported that jet perforating at surface pressure with the hollow carrier gun caused the cement sheath to shatter and crack.' The perforating, however, did not seriously affect the pressure required to leak past the casing cement bond. Only three cementing mixtures were tested, and presumably they had strengths in excess of 2.000 psi. Bearden et al. also reported that the hydraulic bonding strength increased as the compressive strength increased. Their hydraulic test showed that approximately 1,000 psi pressure is sufficient to break the casing cement bond for a well aged neat Portland cement sheath. Unfortunately, the tests were not run with a confining pressure, so Bearden et al. were merely measuring the strength of their outer 8%-in. casing. In our investigation, we measured the hydraulic bond strength of cement to pipe under a confining pressure and found that the bond strength was not limited to 1,000 psi. Cement Bond The bond strength is a good criterion for measuring the effectiveness of cement in performing its main function, that of preventing interzonal communication of fluids behind the casing. Measuring bond strength after perforating should be a good quantitative method of determining optimum cement properties, and should be a better method than that used by previous investigators,11 ' who simply observed the appearance of the cement after perforating.

Jan 1, 1969

By M. C. Flemings, F. R. Mollard

Two-phase Pb-Sn alloys, ranging in compositiotz from 12 to 26 at. pct Pb, were unidirectionally solidified in a convection-fvee system, with thermal gradients in the liquid of up to 480°C per cm. Plane front solidification Loas achieved in all alloys at sufficiently steep gradient and slow growth rate. Conditions causing breakdown of the interface to a cellular or dendritic structure were roughly as predicted by a sinlple constitutional supercooling criterion. Structures of alloys of near-eutectic composition, solidified with plane front, exhibited a lamellar structure; the alloys furthest from the eutectic exhibited a rod-like morphology. Assumptions used in a previous paper for calculations of solute redistribution in two-phase plane front growth are shown to be reasonable for Pb-Sn alloys. Results of calculations are in good agveement with experiment. These show that variations in growth rate during solidification of the composite produce marked changes in average composition of the solid. IN a previous paper, Part I,' conditions necessary for plane front solidification of two-phase alloys were discussed and calculations given on solute redistribution in this type of solidification. This paper, Part 11, describes experiments on Pb-Sn alloys, designed to check the assumptions of the analyses presented, and to demonstrate their applicability to a given alloy system (Pb-Sn). APPARATUS AND PROCEDURE General. A vertical crystal growing unit was built for the study as described below, and "normal solidification" employed throughout (i.e., the ingot was completely melted except for a portion near the bottom end and then solidification initiated). The furnace was designed to permit achieving very low interface velocities, and steep gradients, in essential absence of convection; it is sketched in Figs. 1 and 2. Simple heat flow considerations indicated choice of a small-diameter specimen (ingot) to achieve high thermal gradients; ingot size chosen was 0.3 cm in diam. The ingots were held inside silica tubes 0.06 cm wall thickness. The requirement for an essentially convection-free system was met by use of the vertical furnace with the heat source over the heat sink, as well as by use of the small diameter ingots. In addition, by selection of tin-rich Pb-Sn alloys, the diffusion boundary layer (lead-rich) was denser than the bulk liquid and would not cause convection. The only apparent driving force for convection in this system was the small transverse temperature gradient resulting from heat flow into the samples from the furnace. Such convection must have been small, however, since 1) no temperature fluctuations in the melt were noted in the recordings, which would have indicated turbulent convection, and 2) experimental results obtained and described below could not have been achieved in presence of significant convection. Ingot Preparation. Pb-Sn alloys ranging from 12 to 26 at. pct Pb were prepared from high-purity lead and tin (99.9999 pct pure metal). Each alloy was prepared by first melting the pure metals in the proper ratio in air, in a Pyrex container. The melt was then stirred thoroughly with a graphite rod and cast into a preheated graphite mold. Ingots were then prepared from these castings for use in the actual experiments; each ingot consisted of a rod of alloy, 15 cm long in a 25-cm-long transparent fused-silica tube, 0.3 cm ID and 0.06 cm wall thickness. One chromel-alumel thermocouple, made with 0.004-in.-diam wire and protected by a two-hole alumina tube, was inserted into each ingot. The 1.5 cm of the thermocouple nearest the bead were protruding from the alumina tube and were coated with a very thin layer of boron nitride paste which provided electrical insulation while allowing good heat conduction. The electrically welded junction size was about that of each wire and the cross section of the two wires represented about 0.3 pct of the sample cross section. Including the coating, the thermocouple cross section still represented less than 0.5 pct of the ingot cross

Jan 1, 1968

By N. A. Gjostein

The formal descnption of the decay of an isolated scratch can be written in terms of an appropriate Fourier integral. With the application of certain approximations, this description leads to the second-moment analysis developed by King and Mullins. It is shown that the second-moment analysis does not adequately describe the behavior of a decaying, isolated scratch, and that it is difficult to obtain internally consistent values of the surface self-diffusion coefficient, D,,from this analysis. This inconsistency arises from contributions of higher-order moments to the decay process. Two new analytical methods, based on the Fourier integval representation of a scratch profile, have been developed for determining values of D, from the decay kinetics of isolated scratches. In the profile-matching method, a given initial profile is resolved into its Fourier components, the components are allowed to decay exponentially over an annealing time interval, At, and finally they are synthesized to form a decayed profile. The predicted profile is adjusted to fit the experimental profile by varying only the parameter, D,At; the contribution from volume diffusion is directly taken into account and the integrals involved in the Fourier analysis are evaluated by numerical integration on an electronic computer. In the kinetic method, the widths, W, of a series of predicted profiles are determined for various volume-diffusion contributions, and the results are plotted in the form W vs DSAt. For a fixed ratio of surface to volume diffusivities, R, these plots are linear; the slope of the lines increases as R decreases. A simi-lar analysis can be performed on the depths of the predicted profiles. In this case, plots of (l/df3 vs D,At are found to be nonlinear. The proper value of Ds is found by superimposing the data for the experimental widths and depths on Plots of this kind and adjusting Ds until a fit is obtained with the line having the appropriate value oj R. An analysis of the slopes of these plots for R —= (surface diffusion only) reveals that they do not give the correct value, 2276, for width tf second-moment standard profile. This finding allows one to modify the second-moment analysis in such a way as to obtain internally consistent values of Ds. ThERE are several processes, involving a flow of matter along a surface, due to gradients in curvature of the surface, that may be used to determine the surface self-diffusion coefficient, Ds. These processes are commonly known as 1) thermal grooving, 2) single and 3) multiple scratch decay, 4) blunting of field-emitter tips, and 5) sintering. In this series of papers, the first three of these processes are examined in detail in an attempt to subject the phenomenological theories governing these processes to a critical test and, furthermore, to make a critical comparison of the values of D, obtained from these techniques. Although the thermal grooving technique has been established'' as a reliable method for determining D, , this has not been the case for the process of scratch flattening. Mullins and coworkers374 have proposed phenomenological laws governing the growth of the width and the decay of the amplitude of an isolated scratch, but only in one study5 has the width-growth law been supported by experimental evidence. In paper I of this series detailed experimental evidence is presented that points up the deficiencies of the second-moment analysis; the origins of these deficiencies are also discussed. Following this development, some new analytical procedures, based on representing the scratch profile by Fourier integrals, are presented as a means of obtaining reliable values of D, from the kinetics of the scratch-flattening process. Further applications of the Fourier integral approach are reported in papers 11' and 111,~ where the method has been useful in interpreting the anisotropy of flattening rates of isolated scratches (paper 11) and in describing the multiple scratch decay process (paper 111). THEORY OF SCRATCH DECAY Following ~ullins" approach we consider an arbitrarily shaped scratch profile, Fig. 6, at some time, t. The profile is designated by a function z(x,t) which can be expressed in terms of a Fourier integral as follows:

Jan 1, 1967

By T. S. Spicer

The relationship of coal characteristics to the principal types of firing equipment has been known to the coal combustion engineer, but is not as familiar a subject for purchasing agents, salesmen, consumers, and executives of coal-producing and consuming companies. This general survey of characteristics determined by standard laboratory tests, of major types of combustion techniques, and of the relationships between the two is directed toward the latter audience. It will also serve as a review for those actively engaged in the combustion of coal. Although the relationship of coal characteristics to the principal types of firing equipment is well known to the experienced coal combustion engineer, apparently there is need for a summary article on this subject. The author has received numerous requests for such a paper from purchasing agents, coal salesmen, coal customers and executives of coal-producing and consuming companies. Consequently, the scope of this paper will be directed to this audience, with the hope that it may serve also as a review to others actively engaged in the combustion of coal. The magnitude of this subject is so great that only a brief general treatise is possible. The author realizes that because there are so many special cases and exceptions to the generalities which follow, he is in jeopardy of contradicting himself. It is the hope, however, that the many references cited will prove valuable to those who wish to study the details excluded by necessity, due to space and time limitations. Hence, the characteristics of coals as determined by standard laboratory tests will be discussed; the major types of combustion techniques reviewed; and then the characteristics and firing will be related. CHARACTERISTICS OF UNITED STATES COALS The coals of the United States range from lignite to anthracite and each has its own general characteristics. The extensive coal fields of the U. S. are shown in Fig. 1 and the estimated reserve according to rank for each state is illustrated in Fig. 2. Coals may be classified according to rank as shown by Table I from the ASTM Standards on Coal and Coke, D-338-38.1 The basis of this classification is ac- cording to fixed carbon and heating value (Btu per pound) calculated to a mineral-matter-free basis. The high-rank coals are classified according to fixed carbon on the dry basis; and the low-rank coals according to Btu on the moist basis. Agglomerating and slacking (weathering) indices are used to differentiate between certain adjacent groups. While rank is not itself a characteristic it does signify certain characteristics that accompany a class of fuel. Anthracite, for example, immediately implies a hard, free-burning, smokeless coal of low volatile matter, usually having an ash of high fusibility. Coals may also be classified according to grade as described by ASTM Designation D-398-37.1 This quality classification is determined by size, calorific value, ash, ash-softening temperature, and sulfur. This type of classification is not used as extensively by the industry as the rank classification. Fig. 3 shows the heat value of different ranks compared to proximate analyses. Coals may also be classified by sizes, as shown in Tables IIA and IIB, and sizes can be on both top and bottom limits. If this is done, then the coal is called double screened; otherwise, either top or bottom sizes can be specified as a limit. Bituminous coal sizing varies from field to field and depends upon the market demand. The common sizes and their main uses are outlined in Table IIA. Anthracite is usually available in many sizes at the colliery, and Table IIB summarizes standard sizes and names. Although rank, grade, and size designations help identify and describe a coal in question, there still remain other characteristics such as indicated by moisture, free swelling index, grindability tests, etc. A bituminous coal information chart Table III) suggested for use in studying the available coals in a region, lists origin and chemical and physical characteristics. Even this more comprehensive list does not completely spell out all the characteristics of a heterogenous material like coal. For example,

Jan 1, 1961

By NILS DANIELSEN

THE name of Swedish charcoal iron will probably bring to the memory of many old consumers an extremely tough and ductile iron which was formerly used in considerable quantities for common blacksmith purposes. To-day very little of this iron goes to such kind of work. Swedish charcoal iron is merely a speciality which is chosen whenever its remark¬able properties can be utilized. By giving a rough sketch of the manufacturing process of Swedish charcoal iron, the character of the iron, its weak as well as its strong points will more easily be understood. Swedish charcoal iron is a wrought iron also known in the United States under the name of Norway iron and Swedish Lancashire iron. The name Norway iron seems to have been attached to the product for the reason that in the earlier days it was generally brought into the States by Norwegian ships. However no iron of this kind is now made in Norway. The reason for the name Swedish Lancashire iron is that the manufac¬turing process emanated from Lancashier in England, the method being generally adopted in Sweden in the years 1831-1850. Today this iron is, with the exception of one plant in the United States, made in no place in the world outside of Sweden.

Jan 1, 1924

By J. R. Thoenen

IN five years mineral wool has grown to a thirty-million-dollar industry from one whose output was valued, in 1933, at $1,700,000. Ten years ago, in 1928, there were only seven producing companies, with an annual output of but 50,000 tons. By 1936 fifty or more companies were producing half a million tons. The industry is still growing vigorously and will profit from the expected activity in building in 1339, for two-thirds of this material is used for building insulation and to assist in fire-retarding, in both new and old homes. It is as useful in the South, to protect against heat, as in the North, to keep out the cold, if one may speak nontechnically. It is a concomitant of air conditioning, that new addition to the American standard of living that began in theatres, department stores, and railroad dining cars, and is rapidly progressing down to small homes. Here, then, is an industry that is only beginning to have a present, and one with an almost certain important future; one that depends upon mining and the by-products of mining for all of its raw materials; one that every progressive mining man should know something about.

Jan 1, 1939

By T. A. Rickard

A severely technical article, however well written, can not be an agreeable form of literature. It suffers from the defects of its qualities. One defect is a congestion of language, due to a multiplicity of adjectival nouns. The sentences are packed with words of unpleasing sound, charged with complex ideas, crowding one another so closely that the phraseology moves like an ice-pack in Bering Sea or a log-drive in a river; the undercurrent of meaning may continue to move, but the surface is obstructed. This verbal congestion is made evident by ugly compoundings, many of which are adopted by the technical writer in the mistaken belief that they give directness to his statements. For example: A unanimously approved scheme "A scheme unanimously approved" The continuous temperature record "The continuous record of temperature" To stimulate interest in synthetic plant construction "To stimulate interest in the construction of synthetic plants " In smelters reverberatory-furnace firing with powdered coal has been practised for a decade. "In smelting, the firing of reverberatory furnaces with powdered coal has been practised for a decade. " A tar consumption of one pound per ton "A consumption of tar at the rate of one pound per ton'

Jan 1, 1931

By RUSSELL C. FLEMING

THE important advances that have been made of recent years in mining and milling methods and in mechanical equipment at mines need no re- telling, but there has been a remarkable growth in one type of equipment which has gone nearly unnoticed. That is the increasing use of storage-battery locomotives underground. Since the war the number of these locomotives and their field of use have increased tremendously; their growing acceptance represents an al- most complete reversal of opinion from an earlier period when they were generally looked upon as in- adequate for the strain of mine service. At the time when storage-battery powered units were first making their bid for recognition, the use of power in haulage had already passed through several phases; hand tramming, rope haulage, compressed air locomotives, even gasoline locomotives, had all been used, ending finally in the general adoption of the electric trolley locomotive for practically all power-haulage requirements. It was, and is, conceded that the trolley loco- motive met more adequately the varied and severe conditions of mine service than any previous type of haul- age unit. Subsequent developments have had to endure comparison and surpass in performance that type of haulage before changes would be considered.

Jan 1, 1930

By D. H. NETLAND

DURING the year 1907 an investigation of the Clinton formation in New York has been carried out under the direction of the State Geologist, and a full account of the results has been prepared for publication.1 The more important economic features of the report are summarized in the present paper. Previous knowledge of this, the type, section of the Clinton has been contributed mostly by Hall and Vanuxem in their reports for the Natural History Survey of New York, which were issued in their final form in 1842-43. Brief accounts of the ore-occurrences have been given by B. T. Putnam,2 J. C. Smock,3 A. H. Chester,4 and E. C. Eckel.5 Prof. C. H. Smyth, Jr.,6has discussed the origin of the Clinton ores in two papers, which, so far as the local occurrences are concerned, have removed all doubt that may have existed on that subject. Distribution of the Clinton Formation. The Clinton strata in New York State are restricted to a single belt, Which extends from the eastern central part to the Niagara river, which it crosses, and thence continues for some distance into the province of Ontario. The New York

Mar 1, 1909