By C. H. Li, R. J. Stokes, T. L. Johnston

Dislocation half-loops, artificially introduced by sprinkling with carborundum, were subjected to stress using three-point loading. The different stages of loop expansion and multiplication were then correlated with the macroscopic stress-deflection curve. Loop expansion started at approximately one-third of the "yield stress," defined here as the motivation stress. Above one-half of the "yield stress" simple multiplication commenced while about two-thirds of the yield stress gross multiplication developed short slip-line segments. These values were not affected by the age of surfaces exposed to both dry and wet air. Slip was not detected on unsprinkled crystals below two-thirds of the "yield stress." Thus the stress to activate intrinsic sources, defined here as the activation stress, was approximately twice the motivation stress. This relationship was independent of the strain rate used. It is concluded that lattice resistance takes the form of a viscous drag rather than a static type of force. THE importance of surface condition and environment as one of the more significant factors controlling the mechanical properties of ionic solids has recently received renewed attention.1-4 In some materials, notably the alkali halides, exposing freshly cleaved specimens to the atmosphere results in a progressive hardening and embrittlement of the crystals. This has been attributed to the surface layer becoming "aged," thereby restricting the motion of dislocations in such a way that pileup and eventually fracture results. It is necessary therefore in studying the mechanical properties of ionic crystals to inquire first into the density and distribution of dislocations in the normal cleaved surface and to understand the role these dislocations play in the onset of plastic flow. Knowledge of the effect of environment on this behavior will then assist in understanding the mechanism of embrittlement on aging. In the work reported here a method is described for studying the initiation of plastic flow from dislocation sources in the surface of magnesium oxide crystals. Preliminary results are described of the influence of surface age on this behavior. EXPERIMENTAL TECHNIQUES The magnesium oxide used in this investigation was obtained from the Norton Co. and had a nominal purity of 99.5.pct. Single-crystal specimens, having dimensions typically 1/4 by 1/8 in. cross section and 1 in. in length, were prepared by cleavage over (100) planes from the parent crystal. They were deformed under three-point loading with 3/4 in. spacing between the two end supports and a constant rate of deflection at the center of 0.001 in. per min. The maximum strain rate therefore was 1.5 X 10-5 sec-1. Reasons for choosing this particular form of loading will become apparent in a later section. In addition, a number of confirmatory type tests have been performed at higher loading rates where the maximum strain rate was increased to 1 x 10-3 sec -1. Following deformation the crystals were etched to reveal the dislocation distribution. In a previous paper5 we described a satisfactory etching solution consisting of 5 parts of saturated ammonium chloride, one part of sulfuric acid, and one part distilled water. Immersion of the crystals for 1/4 hr at room temperature developed reproducible conical etch pits at the points where dislocations emerged through the surface. It should be mentioned that dislocations freshly introduced by room temperature deformation gave sharply pointed etch pits which generally distinguished them from the almost flat-bottomed pits obtained on "grown-in" dislocations. The distinction is obvious in the photomicrograph included in Fig. 5(b). Annealing crystals at 1000°C for 12 hr on the other hand gave sharper etch pits on the grown-in dislocations and the distinction was no lower -possible; a similar observation has been reported for lithium fluoride. We have succeeded furthermore in chemically polishing magnesium-oxide crystals. Boiling in fresh 85 pct ortho-phosphoric acid for only 1 min resulted in a microscopically smooth surface which could again be etched to reexamine the dislocation distribution. This boiling time was sufficient to remove the surface damage introduced by cleavage (see next section). SURFACE DISLOCATION SOURCES There are a number of ways by which dislocations may be introduced into cleaved surfaces to act later

Jan 1, 1960

By G. T. Hahn, C. N. Reid, A. Gilbert

An evaluation is made of the possible cautsal relationship between twinning and fracture in molybdenum. For both single and poly crystalline material no instance of twin-induced fracture was observed. Instead brittle fracture was found to be slip-induced at heterogeneities. For single-crystal material, the yield stvess in compression and the fracture stvess in tensiow obey a similar angular- relationship which follows approximately a 1/cos2 ? law. where 0 is the angle between the specimen axis and the nearest (100) plane. This sittlilarity between yield and fracture behavior casts doubt on the interpretations made previoltsly that a 1/cos2? relationship supports a critical normal fracture stress criterion. SINCE fracture in brittle materials takes place at stresses an order of magnitude lower than the theoretical strength of the lattice, it must be postulated that some stress-concentrating effect is operative during the fracture-initiation process. Several mechanisms have been proposed whereby the necessary stress concentrations could be produced. The well-known Cottrell mechanism1 describes a dislocation interaction which can lead to the formation of an incipient cleavage crack on a cleavage plane, and both zener2 and stroh3 have discussed models which predict the stress concentration at the intersection of a slip band with a grain boundary. When twinning occurs twin/twin intersections and twin/grain boundary intersections represent another possible means of fracture initiation. Although still controversial, the concept of twin-induced fracture is supported by a weighty mass of evidence, which has been reviewed in a recent paper.4 This investigation was conducted in order to assess the extent to which the brittleness of molybdenum can be ascribed to this cause. Emphasis was placed on seeking direct metallographic evidence for twin-induced fracture such as arrangements of twins located at the fracture origin. EXPERIMENTAL PROGRAM Materials. The experimental materials are described inTable I. From the chemical analyses and estimates of the amounts of interstitials likely to be retained in solution,5 it is concluded that all were mul-tiphased systems. X-ray diffraction experiments6 showed no evidence of preferred orientation in the polycrystalline materials. Single crystals were grown from Molybdenum X and Y using the floating-zone technique,' in a vacuum of better than 3 x 10-5 Torr. However difficulties were experienced with Molybdenum X due to violent gas evolution from the molten zone, and additional crystals (Crystals 3 to 6) were produced by annealing for 5 1/2 hr at 2300°C under a vacuum of 10-4 Torr. Techniques. A series of tension, compression, and bend tests was conducted. Tension tests were used to demonstrate brittle behavior, to measure brittle-fracture stresses, and to provide fractured specimens for metallographic inspection. Compression tests were employed in order to obtain some ductility and a measure of the yield stress. Furthermore, it was considered that compression loading would permit the study of crack nucleation in the absence of propagation. The bend tests were conducted to facilitate identification of the fracture origin, which would be expected to be at, or near, the tensile surface of the sample. Tests were carried out at temperatures between 78" and 298°K attained by means of a liquid-nitrogen evaporator of modified Wessel design.' Specimens were fashioned by mechanical grinding, and, prior to heat treatment, were electropolished at 10 v in a 3:l mixture of ethyl alcohol and sulfuric acid, using a stainless-steel cathode. Except where noted, a strain rate of 4 pct per min was used. All specimens had a gage section 0.75 in. long; diameters of 0.10 and 0.20 in. were adopted for the tension and compression specimens, respectively, the former of single shoulder design, the ends being gripped in split collets with a conical bearing surface. In the bend test, electropolished specimens measuring 0.080 by 0.25 by 1.25 in. were deformed at 78°K by four-point loading. The bending device had spans of 1 in. between the outer and 4 in between the inner fulcra; it was stressed between the compression anvils of the Instron machine at a constant deflection rate. EXPERIMENTAL RESULTS Polycrystals. Tension and Compression Tcsls. It is apparent from Fig. 1(a) that above 170°K fracture of Molybdenum X takes place at stresses equal to or greater than the compressive yield stress whereas

Jan 1, 1967

By O. C. Holbrook, George G. Bernard

A new theoretical treatment has been obtained for the behavior of pattern waterflood injection wells when closed in. Two cases are treated: Case I where oil and water are assumed to have the same properties, and Case 2 where they arc different. In applying the method, one plots log (p — p,) vs closed-in time, where p is well-bore pressure at any tims and p, is static pressure. The value of p. is determined by trial and error as that value which makes the plot linear at large time. A value for the permeability-thickness product can be determined from the intercept of this linear part, and a value of the skin factor from the injection pressure at time of closing in. Application of the method to data from water floods at three fields seems to give reasonable results. For the case of unit mobility ratio, it is proved that this new method should give the same value for permeability-thickness product as the conventional pressure build-up method. In addition, the new method gives correct values for static pressure, whereas the conventional method does not, often indicating negative static pressures. The new method may be used in cases where the surface pressure persists after closing in as well as in cases where it does not. INTRODUCTION It is of considerable interest and importance to be able to determine the characteristics of the reservoir in an area surrounding a water injection well. Thus, if we can determine early in the life of an injection well that there is a considerable "skin effect", remedial measures can be started before a full-scale pattern flood begins. Similarly, if it can be shown that a gradual buildup of skin effect is occurring with time, measures to free the water of plugging material can be taken. Determination of static pressure in the water-injection well may show that the water is entering a thief zone and not the desired reservoir. Finally, determination of the permeability of the sand around the injection well will allow estimation of the future relation between injection pressure and rate. It should be possible to determine average reservoir permeability, skin effect and static pressure from pressure fall-off data. However, at the time we began work on this subject, it was thought that no adequate theory on which to base such determinations' was available. According to the conventional method which considers the reservoir to be filled with one fluid of small compressibility (see Van Everdingen, Joers2, and Nowak2), shut-in pressure is plotted vs log where is injection time, and At is closed-in time. The physical significance of injection time, may well be questioned in this case, since in a reservoir completely filled with a single fluid (as required by this theory) and with input and output rates equal, the pressure behavior after an initial transient is independent of t,. Attempts by our Tulsa area to use this theory led to negative values of static pressure in most cases. Because of these limitations of the method discussed above, it was decided to attempt to develop a new theory of pressure behavior in water injection wells, one which would apply when there is a gas saturation, as is so often the case in water floods. In the following treatment the assumptions and basic equations are given first, then the method of application of the equations. A complete example is given to clarify details of application. All difficult mathematics has been placed in the appendices so that the reader can follow the text without difficulty. However, if he wishes only to apply the results without knowing the basis for them, he can learn how to do this from reading only the sections entitled "Plotting of Experimental Results" and "Example." ASSUMPTIONS AND BASIC EQUATIONS Statement of Problem It will be assumed that a horizontal layer of constant thickness contains in its pore system a mixture of oil, gas and water. While water is being injected into this pore- system through a well at constant rate, an oil bank is built up, gas being expelled from the space taken by the oil as shown in Fig. 1. The saturations within each

By J. A. Roberson, Robert A. Rapp

From the observation of platinum wire marker movement in the oxidation of columbium at high lemperatures and low oxygen pressures, predonzinant cation diffusion in CbO, has been demonstrated. The Cu,0 molecule was used as an oxidizing species to study the nature of the porous scale and the location of the reduction site in the oxidation of colum-bium. The Cb205 scale contains microporosity and forms by alternate ionic diffusional growth and fracture. The oxidation of columbium at high temperatures and very low po, results in a relatively compact and protective Cb205 layer. THE observation of marker movements during oxidation is one means for the identification of the mobile ionic species in an oxide lattice. Previous marker experiments in the oxidation of columbium have all resulted in the markers being found on the outside surface of the Cbz05 scale. The Cr203 powder markers of Klopp et a1.,' the gold film marker of Kofstad and ~jijllesdal,' and the platinum wire marker of Cathcart et a1 .3 were found at the oxide/gas interface for oxidation temperatures ranging from 450" to 120O0C. However, in all experiments relatively high oxygen pressures were used. As discussed by Mrowec, even the interpretation of marker experiments in simple scales containing only one compound is not without ambiguities. In brief, it can be said that a marker may be found almost anywhere in the scale layer if the metal oxidizes by cation diffusion through the scale; the position of the marker depends upon morphological happenings in the scale. When considering marker movement in a polyphase scale one must proceed with extreme caution. For example, in the past (and present) work markers have never been found at the columbium-scale interface, and one might infer that the oxygen ion is mobile in CbO and CbO,. However, only trace quantities of CbO and CbOz have been present on any of the specimens, so no firm statement is justified on this basis. Despite previous experimental work, considerable doubt still exists concerning the role of the oxides CbO and CbOz in the oxidation of columbium. The identification of the mobile ionic species in CbO and CbOz from the observation of platinum wire markers was one goal of the present investigation . The linear kinetics of columbium oxidation at high temperatures (T - 1000°C) suggests that the Cbz05 scales which form on columbium are porous. From mercury absorption measurements on a Cbz05 scale formed at 500"C, Aylmore et al.' reported a minimum volume fraction of connected voids equal to 0.15. While these scales often appear to be quite porous when viewed in metallographic cross section, they are so brittle that metallographic preparation is likely to exaggerate any porosity originally present. In this investigation, porosity developed during the oxidation of pure columbium and present at the high temperature was detected by oxidizing specimens in sealed evacuated capsules containing large compacts of mixed copper and CuzO powders. wooda has demonstrated that the CuzO, or (CuzO),, molecule is volatile and that oxygen is transferred by the CuzO molecule from a Cu/CuzO mixture to materials having a greater affinity for oxygen. For each molecule of CuzO that is reduced at a sink for oxygen, two atoms of copper are deposited. Quantitatively, essentially all of the oxidation carried out by a Cu-Cu20 compact results from a displacement reaction involving the CuzO molecule. When a metal which oxidizes to form a porous scale is exposed to the CuzO vapor, the CUZO molecules are reduced in the pores leaving a deposit of metallic copper to mark the site of the reduction. This technique has the rather unique advantage that any copper-coated pores found in the scale are unambiguously related to the reduction site in the growth of the scale under consideration. Pores or cracks which form in a msition*- external to the reduction site or which occur as a result of cooling or handling of the specimen will not exhibit the copper deposit. EXPERIMENTAL PROCEDURE Marker experiments were made on columbium metal, and on pellets of CbO which had been pressed and sintered. Platinum wire markers (0.001 and

Jan 1, 1968

By J. H. Bucher

The effect oj strengthening by the precipitation of CbC on the toughness offerrilic steel (0.11 pct C, 0.74 pct Mn, 0.02 pct Cb) was stlrdierl. A g-veater degree of pvecij~itatiotz strengthning is ohtaznable by aging the so11ution-treated steel rtt velaticely Low temperature was (1050" to 1l0O3F) than at higher temperatures (I150" to 1200°F). Tlzis ),eslrlts because a finer dispersion of CbC is obtained. However, the ductile-brittle transition te~ripertltlo.e is raised approximately tlzjeee tirues as IFLIIC~ perv a given yield stress increase) by aging in the lower tempareture range, as opposer1 to the Irigher temperaturee range. This is proposed to result pl-iir~avily because different precipitation distributions ar-e associated with the different aging -treaments. For tile steel aged at 1050" and 1100 F, heavy: precipitation on disloccctions occurs resulting in a high degree of rlislocution pinningh tl~us lowevirzg- the toilguiess. in tll c(.rise of the steel aged at 1150 'a?zd 1300"F, Pvecipitatiol~ is irzove g-enerally distributed throughout the matrix rather limn preferentially on dislocations.; and Ike detlsitj, oj mobile dislocations is not sttyong-ly affected. THE most effective means of strengthening hot-rolled ferritic steels are grain refinement and precipitation hardening. It is well-known that grain refinement increases both the strength and the toughness. However, the upper limit of yield strength obtainable by grain refinement alone is about 60,000 psi,'12 i.e., without the formation of acicular structures of lower toughness. The most economical means of obtaining higher strengths is the addition of small amounts of elements such as columbium, vanadium, and titanium which form carbonitrides. These precipitates are very effective in increasing the strength, but the ductile-brittle transition temperature is is Although it is agreed upon that precipitation decreases the toughness, there has been little effort to isolate the causative aspects of embrittlement. The purposes of this research are to assess quantitatively the embrittlement associated with different precipitate distributions and morphologies, and to correlate the degree of the embrittlement with the microstruc-ture. In this manner, a more fundamental insight into the mechanism of embrittlement may be gained. The steel selected for this purpose was a low-carbon, columbium-bearing steel which, after solution treatment, was aged in various time-temperature cycles while attempting to hold all other microstructural variables constant. MATERIALS AND PROCEDURE The composition of the steel used in this investigation is given in Table I. Starting with commercially hot-rolled material 0.074 and 0.280 in. thick, tensile blanks were cut from the thinner material and sub-size Charpy blanks from the thicker stock. The steel had been rolled using a low finishing temperature and rapid cooling after hot rolling to produce grain refinement. Also, chemical-extraction analysis and electron-microscopic examination revealed that the cooling was rapid enough to suppress any significant precipitation of CbC. Therefore, the as-rolled steel is essentially in the solution-treated condition in terms of the precipitation reaction, and it was used as the base material in this investigation. The room-temperature tensile properties of the as-rolled steel aged at 1100", 1150", and 1200°F for various time intervals were determined, see Table 11. The ductile-brittle transition behavior was studied for smooth and notched tensile specimens, and longitudinal half-size (0.200 in. thick) Charpy V notch specimens aged at 1100" and 1150°F for various times, also Table 11. In addition, tensile specimens aged for single times at 1050" and 1200°F were evaluated with respect to their ductile-brittle transition. Only one 1050°F treatment was used because of the extremely slow kinetics of precipitation at this temperature and because no significant difference between 1100°F aging was observed. Only one treatment at 1200°F was used because aging at this temperature alters the shape of the grain boundary cementite particles present in this steel and complicates analysis. The design of the tensile specimens is given in Fig.1.

Jan 1, 1968

By M. M. Rao, P. G. Winchell

The growth rates of bainitic plates were measured at 400°C in Fe-Ni-C alloys containing 0.10 atom-fract~on nickel and 0.0012 to 0.0075 atonz-fraction carbon. The growth rates are adequately represented by where xc is nearly the atom fraction carbon of the bulk austenite and PXCy is nearly the carbon atom fractlon in the ferrlte of radiids p In equilibrium with austetzite. The form of the equation is that predicted by a model in which carbon diffusion in austernite controls the gvowth, but the numerical constatnt is two orders of magnitude below that suggested by the model. THE growth of bainitic plates in steel is often assumed to be controlled by the diffusion of carbon away from the advancing plate tip. This hypothesis predicts that the growth rate will increase as the carbon content of the austenite, xCz, is reduced toward the carbon content of the saturated ferrite comprising the plate tip, PxCY The growth rate should vary approximately as (xCg- pxCy)-1. Experimental observation of the growth behavior at low carbon levels should provide a significant test of this model. An alloying element in addition to carbon is required so that low-carbon austenite can be experimentally observed while undergoing bainitic transformation. Nickel was selected. The presence of nickel complicates the interpretation of the data in two ways: First, diffusion of nickel during the transformation would make analysis very difficult. Nickel is assumed immobile during the transformation. Second, nickel affects the solubility of carbon in ferrite and austenite in equilibrium. This effect has been evaluated.' At the completion of our experimental work Goode-now et al.2 published data in essential agreement with the observations to be reported here. Since their discussion is abbreviated and their data are scanty in the region of interest, we believe the present work is of significance. I) THE MODEL OF BAINITIC PLATE GROWTH The rate of lengthening of a plate is assumed to be controlled by the diffusion of carbon from the advancing ferrite-austenite interface into the surrounding austenite. The precipitation of carbides is assumed to be a secondary process. For ease of analysis the carbon-atom ratio,* pxCy, of austenite in equilibrium with ferrite which is convex with minimum curvature radius p, and the carbon-atom ratio, PxCY, of that ferrite in equilibrium with austenite are assumed independent of location on the ferrite-austenite interface. Since these carbon contents vary with the radius of curvature of the ferrite, p, their assumed positional independence must be held as an approximation. The consequences of these assumptions have been developed approximately by zener3 and Hillert,4 and the resulting equation for a platelet has been applied to bainite by Speich and cohen5 and Kaufman, Radcliffe, and Cohen.8 The Zener-Hillert equation* for plates is: The analysis of Hillert is supported by that of Hor-vay and cahn7 which involves no mathematical approximations but does include the assumption that the a/y interface coincides with an isoconcentration line. The solutions of Horvay and Cahn for elliptic paraboloids are replotted in Fig. 1. The shape of the paraboloid is expressed in terms of the ratio of the principal radii of curvature at its tip, A =p1/p2, which is also the ratio of the minor to the major axis of the elliptic cross section. The Zener-Hillert equation for plates is also plotted. The agreement is within a factor of two for (pxyaCr - xyC )/(xyC - PxCaY) between 0.5 and 100. This is the range of interest here and in most other work on bainite. The original form of the Zener-Hillert equation was the form given above with the right-hand side replaced by (pxCya -xCy)/(PxCya). This replacement is not appropriate here. 11) THE EXPERIMENTAL PROCEDURE Alloys were prepared and three kinds of experiments carried out. Continuous-cooling-transformation experiments were carried out on wires by measuring temperature and resistance during continuous cooling. Isothermal-transformation experiments were carried out on wires by measuring electrical resistance as a

Jan 1, 1968

By G. Bruggeman, K. G. Kreider

Grain boundary dij]usion coefficienls were measured in tungsten between 1400° and 2200° C and can be expressed by the equation sq cm per sec This activation energy confirms some eavlier estimates made .from tungsten sintering experiments. Grain boundary diffusion was found to occur in sub-bozrndavies having -misorientations of less than 10 deg. The actiuation energy for this subboundavy diffusion is equal to that for dijjusion in incoherent grain boundaries with in the limits of error. This is shown to be consistent with the dislocation model of Low-angle boundaries wheve diffusion occlcvs along- the dislocation 'YPipes" comprising -tile boundary. RECENT investigations of the sintering of tungsten powders all report activation energies which are considerably less than the activation energy for tungsten volume diffusion. Kothari' reports a value of 100 * 5 kcal per mole, Hayden and Brophy' obtained 90 kcal per mole, and Vasilos and smith3 found 110.7 kcal per mole from their sintering studies. Since most determinations of the activation energy for volume diffu-sion4-' fall between 120 and 160 kcal per mole (the true value seems most likely to be nearer 150 kcal per mole), the conclusion is drawn that the mass transport leading to densification during sintering is accomplished by grain boundary diffusion. This interpretation is consistent with various diffusion models of the sintering process. 10-12 Vasilos and Smith calculate diffusion coefficients from their data which fit the equation D * 1.36 x 10* exp(-llO,700/HD However, no direct measurements of tungsten grain boundary diffusion have been made. Furthermore, considerable disagreement exists between the directly measured values of tungsten volume diffusion.'-' In order to corroborate the inferred results of the sintering experiments concerning grain boundary diffusion and to provide accurate diffusion data essential to the analysis of the kinetics of creep, oxidation, precipitation, and so forth, the present work was undertaken to measure self-diffusion in single-crystal and polycrystalline tungsten between 1400" and 2200°C. It is within this temperature range that tungsten sintering is done, the re crystallization of tungsten occurs, and the widest application of tungsten as a high-temperature material will probably be made. EXPERIMENTAL PROCEDURE Radioactive WlE5 was produced by irradiating tungstic acid in a neutron flux of 1.2 x 1012 neutrons per sq cm per sec for 36 hr. A 2-week waiting period was allowed for the decay of w"~ also produced by the irradiation. (w"~ has a half-life of 24 hr.) The half-life of the remaining isotope was determined to be 75 days confirming the presence of w lE5 and the absence of any undesired radionuclide. Specimens 4 in. in diam and $ in. thick were cut from polycrystalline swaged tungsten rods (recrystal-lized) and from Linde single-crystal rods. Chemical analyses of these materials appear in Table I. Actually upon closer examination, the single-crystal specimens were found to consist of several subgrains separated primarily by tilt boundaries in which the misor-ientation ranged from 3 to 10 deg. Thus, it was possible to measure boundary diffusion coefficients in these low-angle subboundaries as well as in the incoherent boundaries of the polycrystalline specimens. The two faces of each specimen were ground flat and parallel within 0.0001 in. The radioactive tungstic acid was dissolved in concentrated ammonium hydroxide, placed on the ground flat of the specimen, and evaporated to dryness. The oxide was then reduced in hydrogen at 1000°C resulting in a layer of wlE5 approximately 1 p thick. The diffusion anneals were performed in vacuum in a tantalum resistance furnace. Time at temperature ranged from 10 hr at 1400°C to 2 hr at 2200°C. The penetration profile was determined by measuring the residual activity after successive removal of surface layers by grinding on metallographic polishing paper. Extreme care was exercised to insure that sections were always taken normal to the diffusion direction; this was verified repeatedly by checking that front and back surfaces of the specimen remained parallel. The activity was measured with an end-window Geiger-Mueller counter. The sides and edges of the specimen were well-shielded to eliminate possible effects due to surface diffusion. The weight of the

Jan 1, 1968

By P. L. Rittenhouse, M. L. Picklesimer

A rapid and seniquantitative method of determining prefered orientation on large numbers of. Zircaloy-2 specimens was desired. knoop microhardness measurerrzetzls were irvestigated as a solldtion to this pro6lem. The variation of Knoop microhardness measurerlerzts on selected planes as a function of 'irzdenle axis relutilje lo cryslallograplzic or fabrication divectals were used to corzstrrcl a polar coordinate hardness contour map. With use of an empirical relationslip between the single-crystal hardnesses and those of the polycrystalline material conentional pole figures could be constructed which compare favorably also obtained. To determine preferred oriention qualitatively from hardness data requires a minimum of twelve measurements per plane on three, preferattention to grain size, specimen prepartion, and in-rreinetzt, and analjlsis is of the order of- 45 to 60 rrin. THE design of structures from Zr alloys requires consideration of preferred orientation and the resulting anisotropy of mechanical properties. Rapid and semi-quantitative methods of evaluating anisotropy and of determining preferred orientation are needed for quality control and for examining the large number of test specimens required in development programs. The variation of Knoop microhardness with indenter orientation has been studied in single crystals of several hcp metals including titanium.' beryllium,' magneium, and zinc.4 The maximum hardness observed on any crystallographic plane other than the basal plane invariably occurred when the long axis of the Knoop indenter was either parallel or perpendicular to the projection of the [ OOOI.] direction on the plane of examination. When the major slip mode was (0001)(i2i0j the maximum hardness occurred at the parallel positio! but when the operating slip system was {10i0) (i210) the hardness was a maximum perpendicular to the [0001] projection. A minimum hardness was always observed at a rotation of 90 deg from the maximum. It follows that the orientation of the projection of the [0001] can be determined on any non-basal plane by making hardness measurements at a number of indenter orientations. The determination of the orientation of the [0001] projection on two non-parallel, preferably orthogonal, surfaces of the specimen will allow location of the [0001] direction in the specimen. It seems possible that such measurements could be used to examine, at least qualitatively, the preferred orientation existing in polycrystalline hcp materials. An investigation of the microhardness anisotropy in Zircaloy-2 was undertaken to ascertain whether these measurements could be used for this task. EXPERIMENTAL PROCEDURE Single crystals of Zircaloy-2 were grown by an a-8-a annealing sequence using electron-beam heating.= The orientation of the crystals was determined by a conventional back-reflection Laue technique. The crystals were then mounted on a goniometer head and the desired crystallographic faces were milled and chemically polished. Polycrystalline Zircaloy-2 specimens were prepared from fabricated sheets or plates. Inverse pole figures for these materials were obtained using the X-ray diffraction techniaue described by Jetter, McHargue, and illiams.' A Wolpert-Greis Micro-Reflex hardness-testing machine was used to make the Knoop microhardness measurements. The single-crystal and polycrystalline specimens were loaded to 0.5 and 2.0 kg, respectively. Determination of the scatter of hardness numbers as a function of applied load for several indenter orientations on several specimen surfaces showed that the loads selected were the lightest consistent with minimum scatter. Heavier loads did not appreciably decrease the scatter and produced hardness impressions too large to be conveniently measured with the equipment used. Seven crystallographic planes of the single crystals were examined, while six planes of examination were used in studying Zircaloy-2 polycrystals. The specimens were rotated 10 to 15 deg after each measurement and from four to eight impressions were made at each angle of rotation. RESULTS The two angles which were used to relate crystallographic directions and planes in the hcp cell to the planes of examination of the single crystals are shown in Fig. 1. 8 is the angle between the c axis. [0001]. and the normal, N, to the plane of examination. a is the angle between the long diagonal of the Knoop indenter and the projection of the c axis on the plane of examination. For exampIe, if P = 90 deg and a = 0 deg, the plane of examination is of the family

Jan 1, 1967

By A. J. Griest, P. D. Frost, H. A. Robinson

The flow characteristics and uniform elongation of alpha-beta titanium alloys in the solution-treated condition were shown to be markedly affected by the solution temperature. Two classes of alpha-beta alloys were distinguished, based on the effect of solution temperature on the uniform elongation. Martensitic alpha-beta alloys, which are relatively weakly beta-stabilized, showed decreasing values of uniform elongation as the solution temperature was initially increased. However, after solution-treatment at still higher temperatures in the alpha-beta field, the uniform elongation of these alloys was again high, and often attained its maximum value. Nonmartensitic alpha-beta alloys, which are more heavily beta-stabilized, showed a continuous decrease of uniform elongation with increasing solution temperature. The behavior was rationalized in terms of the alpha-beta ratio and the alloy content of the beta existing at the solution temperature. The data indicate that in commercial practice close temperature control may be required to get maximum uniform elongotion, and hence, maximum potential formability, in solution-treated sheet. Bend-test data also were obtained for the solution-treated conditions. A MOST important objective of current titanium research is the development of age-hardenable alloys with superior formability in the solution -treated condition. Alpha-beta titanium alloys have been shown to be amenable to high-strength aging treatments after solution-treatment in the alpha-beta field.' However, heat-treatment data on the properties of solution-treated sheet, such as uniform elongation, minimum bend radius, and flow properties, which have a bearing on the potential formability, have not been widely available. This paper presents only the most significant results of a research program conducted at Battelle for the Air Force in an effort to develop sheet alloys that can be formed readily as solution-treated and subsequently aged to very high strengths. Data for 10 compositions representative of the more than 25 alloys studied in this program are presented. A primary objective of the paper is to demonstrate the pronounced dependence of the flow characteristics and uniform elongation on solution-treatment temperature. This effect is believed to be vitally important in the commercial heat-treatment of age-hardenable titanium sheet alloys. Experimental Procedures Melting and Fabrication—The nominal and actual compositions, beta transi temperatures, and rolling temperatures of 10 of the 30 alloys studied are presented in Table I. Stock :€or two of the alloys, E (Ti- 8Mn) and J (Ti-6A1-4V) was obtained from commercial heats. The remaining heats, except D and I, were double melted as 10-lb heats in a consumable-electrode furnace. Melting stock was 120 Brine11 hardness sponge. The oxygen and hydrogen analyses spotted throughout the heats indicate the range of interstitial levels resulting from the melting practice used. Heats D and I were melted as 20-lb ingots with the same grade of sponge. These ingots were cut in half and one portion used in the present evaluation. The ingots, which were about 4 in. diam and 4 in. in height, were upset forged and drawn at 1750°F to sheet bar 5/8 in. thick by 2 1/2 in. wide in such a manner that the top of the ingot corresponded to the top of the sheet bar. Slabs of the sheet bar, 5 1/2 in. in length were scalped to 1/2 in. thickness and rolled at the temperatures indicated in Table I to approximately 0.055 in. sheet. Elongation during rolling took place at 90" to the original forged length. The fabrication procedure used is described in some detail since the experimental heats showed considerable directionality in mechanical properties. The rolling procedures for the commercial heats were unknown, but were such as to produce essentially isotropic properties. All heats, as rolled, showed microstructures typical of alpha-beta alloys worked in the alpha-beta field; that is, the structures consisted of equiaxed alpha particles in a beta matrix. Heat Treatment— The effects of solution and aging heat-treatments on the properties of the alloys were evaluated uSing longitudinal and transverse tensile and bend coupons sheared from the sheet. Two or three solution-treated conditions were evaluated for each alloy. In addition, the alloys were also tested after annealing at 1200°F for 4 hr and furnace cooling. The solution-treated and annealed conditions were those in which the alloys might be expected to

Jan 1, 1959

By S. Shapiro, J. A. Ford

The crystallo graphy of several grains of the lamellar Ni-Ni3 B eutectic solidified under conditions appvoachirt equilibriun has been examined.. A preferred interlace relationship has been observed in this system which may be described as: A detailed study of this interface by means of an atomistic model reveals the interface Plane to be puckered and more accurately describable as: Analysis of the atomic configuration on these planes reveals that this interface conforms to the orientation criteria proposed for directionally solidified lanzellar eutectics. In addition, a model is proposed to help explain the growth of a "puckered" interface. DURING the past several years an increasing number of unidirectional solidification experiments on eutectic alloys have been reported in the literature. The primary emphasis, in most cases, has been the effect of growth variables on microstructure. Some authors have, however, studied the crystallographic orientations and interfacial relationships resulting from these experiments. Four crystallographic studies have been published;'-4 in each of these there is a factor which tends to prohibit the extension of the observations beyond the particular system. In the Al-CuA12 system, the approximately equal volume fractions of the phases have resulted in sorrie controversy as to which phase constitutes the matrix. In the Mg-Mg,Sn eutectic the presence of several interconnecting lamellar systems2 complicates the analysis. The two remaining eutectics. 1nSb-b and Al-Ali, are both rodlike (the latter exhibits a plate morphology at low solidification rates): the matrix in each of these alloys is the simpler (fcc) phase. Studies of nucleation in eutectic alloys indicate that the more complex constituent is the nucleating -.phase.' For the purpose of an analysis of interface crystallography it was deemed desirable to study a lamellar system in which the matrix was the more complex and, presumably. the nucleating phase. Recently it has been shown that there is a eutectic in the Ni-B system between Ni3B and i; preliminary investigation by the authors indicated that the matrix in this eutectic is the boride phase. The structure of Ni,B is reported to be orthorhombic, the compound being isostructural with cementite. This eutectic is therefore analogous to that between austenite and cementite. Furthermore, the Ni-B system is not susceptible to a competing eutectic reaction as occurs in the Fe-C alloys; nor does it exhibit a eutectoid decomposition. For these reasons the study of the interfacial relationship in the Ni-Ni3B eutectic was undertaken. PROCEDURE Ingots of nominal composition 3.5 and 3.6 wt pct B were induction-melted in boron nitride crucibles within a graphite susceptor under a boric oxide slag; a dynamic argon atmosphere was maintained over the melt to prevent rapid oxidation of the susceptor. The raw materials used were 99.97 pct Ni from Huntington Metals Division of International Nickel Co. and 99.8+ pct B chips supplied by the United Mineral and Chemical Co. The analyses of the starting materials are listed in Table I. The melt was held at 1500cC for 2 hr to insure complete reaction and allowed to cool to room temperature. The castings were chemically analyzed for boron and were metallographically examined for uniformity. The metallographic samples were mechanically polished through 0.1 p A1,0, and etched with Carapella's reagent. Each master casting was cut up to make several specimen blanks which were remelted, in boron nitride crucibles, to form ingots of 1/2 to 3/4 in. in diarn by 7 in. long. These ingots were unidirectionally solidified using a modified vertical Bridgman technique. The rate of solidification was assumed to be equal to the uniform rate at which the crucible-susceptor assembly was withdrawn from the induction coil. This rate was varied from 1.18 to 2.21 cm per hr. In order to perform these experiments it was found necessary to redetermine the eutectic composition. This was accomplished by the zone-melting technique described by Yue and lark.' An ingot of 4.5 wt pct B was zone-melted in a horizontal boron nitride boat 7-1/2 in. long with a 112-in.-square cross section. A

Jan 1, 1967

By M. E. Wadsworth, T. L. MacKay

Sintered UO, samples were leached in sulfuric acid solutions of various concentrations. A pressurized system was used so that it was possible to investigate the kinetics of the reaction to 270°C with oxygen overpressures as high as 900 psi. The rate was observed to be a function of the concentration of hydrogen ions and directly proportional to the partial pressure of oxygen. Evidences are presented which indicate that a UO2 surface site reacts with a molecule of water to form a hydroxyl complex which in turn can dissociate with the characteristics of a weak acid. A rate determining step has been proposed which involves the reaction between an oxygen molecule and the hydroxyl complex on the surface of UO,. ThE 2 principal methods for uranium dissolution are carbonate and acid leaching. The sulfuric acid leach is the more popular and is used for the treatment of the majority of the ores of Africa, Canada, and the United States. Low recoveries in basic leach circuits led investigators at the University of British columbia1 to study leaching of uranium ores in pressurized vessels. Early in the study of dissolution of uranium it was found that only uranium in the hexava-lent state could be leached in acid or basic circuits. Therefore, the use of oxygen over-pressure in an autoclave offered an interesting approach to solving the low recovery problems of carbonate leaching. UO, was used in this study because it could be obtained in high purity and also because it is representative of the most refractory of the primary uranium minerals. A pressurized system was used to provide a means whereby important temperature and pressure parameters could be varied for the evaluation of the kinetic processes. The mechanism for the dissolution of UO2 should be similar for any of the uraninite type minerals. At the present all of the kinetic studies that have been conducted have been in carbonate media. Peters and Halpern2 carried out a kinetic study of the leaching of pitchblende. Their specimens were pitchblende ores selected on the basis of high grade and homogeneity. Pearson and wadsworth3 conducted a kinetic study of the dissolution of UO2 in carbonate solutions with results very similar to those obtained by Peters and Halpern. EXPERIMENTAL The UO2 as received* was found by spectroscopic *Mallinckrodt reagent, supplied by the Atomic Energy Commission. analysis to have a purity of 99.94 pct 0.03. It was ground in a mechanical agate mortar and screened through a 400-mesh sieve. Thin flat disks of UO2 were prepared by pressing the sized powder in a specially constructed die at a total pressure of approximately 25 tons per sq in. The pressed disks were approximately 0.25 cm thick, 1.6 cm diam, and 3.5 g in weight. As pressed, the samples were approximately 65 pct of theoretical density. It was essential that a binder such as poly-vinyl alcohol be added before pressing to prevent formation of cracks when fired. It was found by trial and error that pressed disks sintered close to 1870°C in a hydrogen atmosphere, reach densities between 91 and 91.5 pct of the theoretical density. At this density the samples had no measurable porosity based upon a 2-hr emersion in boiling water. An X-ray examination of these sintered UO2 disks showed them to be identical with the original UO2 received. Reaction of UO2 with the alundum furnace core was prevented by placing molybdenum between the samples and the core according to the method of Corwin and Eyerly.4 Leaching studies were carried out in a specially designed autoclave, the details of which have been presented e1sewhere.6 The main features of the equipment as applied to a kinetic study are: 1) solution samples may be removed during the course of a single run; and 2) temperature and agitation are carefully controlled. Two-ml samples removed from the autoclave during the course of a run were analyzed for U3O8 content with a Beckman model DK-2 spectrophotometer by the method of

Jan 1, 1959

By Ronald K. Linde

Metastable Ag-Cu solid solutions at two compositions beyond the maximum limits of solubility obtainable by quenching from the solid state were obtained by rapid quenching from the liquid state. The process of transformation of the metastable solid solutions into the equilibrium phases was studied by means of X-ray diffraction intensity measurements and electrical-resistance measurements; metallographic examination was also performed. Results are compared with those for an alloy quenched from the solid state at a composition which exists as a solid solution at elevated temperatures. Activation energies for the trans-formation were computed to be 33,600 * 2500 and 33,100 * 2000 cal per g mole for the 60.1 and 75.0 at. pct Ag;Cu compositions, respectively THE kinetics of precipitation in supersaturated solid solutions obtained by quenching from high temperature has been thoroughly studied in many alloys, and detailed investigations of the early stages of nucleation and subsequent growth of the equilibrium phases have been carried out. All of these studies have been made on alloys quenched from the solid state, however, and it is the purpose of this paper to present some of the results on the kinetics of transformation of metastable solid solutions in Ag-Cu binary alloys whose compositions lie outside of the solid-state limits of solubility. Limits of solubility in the solid state can be increased by rapid quenching from the liquid state. This was first demonstrated by Falkenhagen and Hofmann, who obtained appreciable increases in solubility limits of the elements of the first transition series in aluminum by rapid cooling of liquid alloys through contact with a copper mold maintained at liquid nitrogen temperature.' The same basic idea of cooling a liquid alloy by conduction onto a substrate rather than by convection of a gas or liquid (conventional quenching) has been recently revived and extended to very high rates of cooling by Duwez and his collaborators. The new technique was first applied to Ag-Cu alloys because the existence of a eutectic in this system is not predicted by the Hume-Rothery rules of alloy phase formation. Rapid quenching from the liquid state resulted in metastable solid solutions at all concentrations. The kinetics of decomposition of these metastable solid solutions containing 60.1 at. pct Ag;Cu (eutectic composition) and 75.0 at. pct Ag;Cu is the subject of the present paper. EXPERIMENTAL TECHNIQUES Alloys were made in 10- to 20-g heats using silver of purity 99.99 pet and copper of purity >99.999 pct. Components were weighed accurately to 0.1 mg and melted by induction heating in an alumina crucible under an atmosphere of hydrogen. Weight losses amounted to less than 0.02 ~ct in all cases. Rapid cooling from the liquid state was achieved in an apparatus of the type described by Pietrokowsky. 3 In this technique a freely falling drop of molten alloy is caught between a stationary anvil and a fast moving piston, both anvil and piston being lined with copper. The resulting foils were approximately circular (about 2 cm in diam) and from about 50 to 150 u in thickness, depending on the pressure driving the piston. Metallographic samples were prepared for polishing by edge-mounting foils in Quickmount. The mostef-fective etching procedure was found to be: 10 parts NH4OH (concentrated), 1 part H2O2 (30 pct), 5 parts H2O, swab for 5 to 10 sec. The transformation of the metastable alloys to equilibrium was followed by X-ray diffraction and electrical-resistivity measurements. The peak intensity and the integrated intensity of suitable Bragg reflections of the metastable and stable solid solutions were studied with a Norelco dif-fractometer, using nickel-filtered copper KO radiation. The peaks were step-scanned at intervals of 0.05 deg. Using either a Kelvin bridge or a null circuit with a Leeds and Northrup K-2 potentiometer, the changes in electrical resistance due to phase transformation were measured for specimens cut into strips about 20 mm long and 4 mm wide. All resistivity measurements were carried out at liquid-nitrogen temperature. The isothermal heat treatment was accomplished by sealing the samples in argon-filled aluminum containers with stainless-steel O-rings. Containers were then suspended in wax baths with temperatures in the

Jan 1, 1967

By Barry D. Lichter, Pierre Sommelet

High-temperature heat contents of InSb, GaSb, and AlSb were measured over the temperature range 400" to 1450°K using a diphenyl ether drop calorimeter. Smoothed ualues of the thermal properties, H$ - H:9s, have been derived and are tabulated at even temperature intervals. The heats of fusion of the three compounds were determined as, respectively, 5707 *100, 7780 * 100, and 9800 5 3011 cal per g-atorn at the determined melting points of 797" l°, 985" * , and 1330" * 5°K. The calculated entropies of fusion are, respectively, 7.16 0.12, 7.90 * 0.11, and 7.37 * 0.23 cal per deg per g-atotn. The heat capacities increase substantially on tnelting in contrast to the behauior of structurally related germanium and silicon. Deriations from the Kopp-Neumann rule are negative for solid compounds and positive for the liquid phases. Previously obsevrrd "post melting" in InSb is confirmed. The high-temperature thermal properties of 111-V compounds are presently not well-established, despite the technical importance of these semiconducting cbmpounds. Uncertainties in available heats of fusion and heat contents have seriously hampered thermo-chemical evaluations' and thermodynamic analyses of phase equilibria2"" in these systems. This paper reports results of high-temperature heat content investigations of InSb, GaSb, and AlSb measured in the range 400" to 1450°K employing a diphenyl ether drop calorimeter. Similar measurements for InAs and GaAs will be reported in a following publication.~ EXPERIMENTAL PROCEDURES Samples. High-purity samples of the compounds InSb and GaSb were supplied in the form of crushed crystal fragments by Dr. Carl Thurmond of the Bell Telephone Laboratories and in the form of single crystals by Dr. A. Strauss of the M.I.T. Lincoln Laboratory. Single-crystal samples of semiconductor-grade AlSb were supplied by Dr. W. P. Allred of the Bell and Howell Research Center. Chemical analyses indicated that all compounds were stoichiometric to *0.1 at. pct, which is within the experimental uncertainties of the analyses. Samples were crushed, weighed, and encapsulated in evacuated, thin-walled, fused silica capsules. The capsules were nearly identical in external shape, 2 cm by 2 cm diam, but varied in weight due to differences in wall thickness. One sample of AlSb was contained in a thin-walled, high-purity alumina cup encapsulated in silica and used for heat content determinations of liquid AlSb. The capsule materials showed no visual evidence of reaction with any of the compounds. The sample and capsule weights are given in Table I. Calorimeter. A Bunsen-type calorimeter, similar in design to a previously described instrument6 but employing diphenyl ether (C6H5)'0 as the calorimetric substance, was used for measurements of heat contents above 300.0°K, the melting point of diphenyl ether. Heat input to the calorimeter caused isothermal melting of diphenyl ether, and the resulting increase in volume was measured by displacement of mercury from the calorimeter into a 200 cm horizontal, calibrated capillary, 1.25 * 0.01 mm diam, or into a weighed beaker. The advantages of diphenyl ether over water have been previously pointed out7 and include: i) an increase by a factor of 3.5 in sensitivity as measured by the ratio of the volume change to the enthalpy change on fusion, ii) the smaller required extrapolation from the melting point to the standard temperature of 298.17"K, and iii) the positive volume change on fusion of diphenyl ether in contrast to the contraction which occurs on fusion of ice. Diphenyl ether was purified by fractional crystallization to 99.95 mol pct as determined from the melting point depression with fraction crystallized. During assembly of the calorimeter, the ether was repeatedly outgassed under high vacuum to remove dissolved air. The calorimeter receiving vessel consisted of an 8-in.-long by 1:-in.-diam copper tube with twelve horizontal 3-in.-diam radiator "fins" for dissipating heat to the surrounding mantle of diphenyl ether. Before forming the mantle the chamber surrounding the receiving vessel contained 3300 cu cm of liquid diphenyl ether above 250 cu cm of mercury which was

Jan 1, 1970

By J. B. Cohen, O. F. Kimball

Aging of specimens of Au-20 at. pct Ni and Au-40 at. pct Ni has been followed with electron microscopy, resistance, magnetic measurements, and X-ray diffraction. The periodic structures observed by electron microscopy in Au-Ni alloys by Fisher and Embury are shown to be due to nickel-rich prepre-cipitates. Assuming this alloy system undergoes spinodal decomposition, our observations and available data on thermodynamic properties and elastic constants indicate that the gradient energy coefficient in this system is of the order of 10-5 ergs cm-1 . Shifts of X-ray peaks in this system have been found to be due primarily to residual stresses, not faulting. A large effect of applied stress during aging was detected by X-rays and electron microscopy for the Au-20 at. pct Ni alloy. The presence of a preprecipitation stage during aging of gold-rich Au-Ni alloys for short times below 300°C has been indicated by several previous investigations. Changes in electrical resistivity,1"3 elastic modulus,4 superparamagnetisrn,5 positions of X-ray diffraction peaks,6 and hardness7 have been studied. Electron diffraction and microscopic studies by Fukano8 and Fisher and Embury9 respectively showed that the precipitation process resulted in the formation of periodic composition fluctuations—perhaps spinodal decomposition. MOSS10 detected a satellite with X-rays in quenched specimens, but the wavelength was much smallerthan that found by Fukano. Recently Woodilla and Averbac11 detected a modulation similar to that found by Moss, but with electron diffraction. They suggested that the microstructures observed by Fisher and Embury may be simply due to a Moir'e effect from a back deposit of gold during electropolishing. Satellites in electron diffraction can be enhanced by small bends or tilts of a foil. Even if this were not the case, asymmetric satellites, as are found in Au-Ni are difficult to analyze. They are principally influenced by the large differences in atomic size in this system, and obtaining information on the associated composition fluctuations depends on assumptions as to whether or not there are isolated clusters or composition "waves", and in the latter case whether or not the entire specimen has decomposed. Assuming that decomposition was complete in alloys aged at low temperatures, Woodilla and Averbach suggested that the satellites indicated a composition which varied about the average value by only± 5 pct, much less than that predicted from the phase limits, Fig. 1; they attributed this small variation to a cessation of the reaction caused by the loss of mobile vacancies. In Ref. 12 it was shown that vacancies are trapped by the preprecipitate in this system. Furthermore, after reversion, aging proceeds at a much slower rate than immediately after a quench from the solution temperature,5'11,13 indicating the importance of vacancies in the kinetics. In some senses Au-Ni is a favorable system for studying preprecipitation and reversion mechanisms because of the simplicity of the equilibrium diagram14 and the availability of good thermodynamic15 and diffusion data.16,l7 The calculations necessary to relate the decomposition process to classical nucleation and growth or to spinodal decomposition, as well as those necessary for understanding reversion mechanisms, can, therefore, be made. As an example, the position of the chemical spinodal, calculated from the thermo-dynamic data of Sellars and Maak15 with the method described by Rundman and Hilliard,18 is included in Fig. 1. It is compared to the chemical spinodal calculated from the equilibrium miscibility gap by Cook and Hilliard's method.l9 Included is the coherent spinodal suggested by Golding and MOSS," using measured elastic constants for their calculations and the same ther-modynamic data. The spinodal estimated by Woodilla and Averbach,11 by determining the temperature limits for the observation of the satellites discussed above, is also given. Actually this last curve is open to question on the following grounds: As a phase boundary is approached the spacing of particles or the wavelength

Jan 1, 1970

By D. A. Elgillani, M. C. Fuerstenau

With either sulfonate or oleate as collector, quartz responds to flotation with moderate additions of calcium only at moderately high pH, where some portion of the activator has hydrolyzed to caOH+ . Calculations of the concentrations of various ionic and precipitated species of calcium and collectors suggest that the products of [(CaOH+) (RSO3)] and [(CaOH+)(01-)] determine whether flotation is obtained under specific conditions. Ion products on the order of 10-12 were calculated for both the sulfonate and oleate systems. The activating effect of calcium ion in nonmetallic flotation systems is of considerable interest because of the normal presence of calcium in natural water. As a result, this phenomenon has received quite some attention in the past. Kraeber and Boppel1 showed that quartz could be activated by calcium above pH 10 with sulfonate as collector. The feasibility of selectively separating quartz from hematite with calcium activation at relatively high pH was demonstrated by Clemmer, Clemmons, Rampacek, Williams, and stacy.2 Cooke and Digre3 showed with a bubble pick-up method that the minimum quantity of calcium ion required as activator for complete pick-up of particles occurs at pH 11.5 for an addition of 20 mg per liter sodium oleate. They also showed that larger additions of calcium (10-fold increase per unit decrease of pH) must be added for complete bubble pick-up as the pH is reduced. Schuhmann and Prakash,4 using a vacuum flotation technique, found that quartz could be floated with moderate additions of calcium chloride and oleic acid at neutral pH, providing the metal ion was present in stoichiometric excess over the quantity needed to form the normal soap with oleic acid. They also reported that calcium will function as an activator only in basic media. More recently, Eigeles and volova5 have shown that essentially complete flotation of quartz is obtained with 6 x 10-4 mole per liter calcium chloride and 1.7 x 10-5 mole per liter sodium oleate at pH 11.6. while no flotation is obtained at about pH 10.9 and below. The importance of adsorption of activator and collector at the air-liquid interface is also demonstrated in these systems. The important role that metal ion hydrolysis assumes in quartz activation systems was also demonstrated recently.6-8 A detailed investigation of metal activation in sulfonate flotation of quartz was undertaken in one system7 and yielded a number of interesting and important observations. Quantification of the data of this system7 to the extent desired was not possible, though, because certain species could neither be ignored nor accounted for accurately. These difficulties can be circumvented when calcium is involved as activator. This detailed analysis was undertaken to obtain a more quantitative explanation of calcium and metal ion activation in quartz flotation. EXPERIMENTAL MATERIALS AND METHODS Sodium alkyl aryl sulfonate9 mol wt 450, and pure potassium oleate were used as collectors. All other reagents used were reagent grade in quality, i.e., n-amyl alcohol as frother, KOH for pH adjustment, and calcium chloride. Conductivity water, made by passing distilled water through an ion exchange column, was used in the investigation. Quartz was prepared by leaching the sized sample (48 x 150 mesh) with HC1 until no iron could be detected in the leach liquor. The experimental equipment and procedure were the same as that described previously.6,10 EXPERIMENTAL RESULTS As the presence of precipitates was noted in all of the systems to which ca++ and collector were added, experiments were undertaken to determine the solubility products of calcium sulfonate and calcium oleate using a nephelometer. With this technique, collector is titrated into a known solution, which in this case was 5 x 10-5 mole per liter CaCl2 at pH 5.5. Upon precipitation of the calcium-col lector salt, e.g., calcium oleate, light is scattered and detected

Jan 1, 1967

By D. A. Munro, G. P. Contractor

Fourteen 50-lb laboratory melts were investigated to determine the effect of uranium on the tenpering characteristics of loo-carbon (0.06 to 0.1 pct C) steels. It was found that uranium additions, particularly in the range 0.30 to 0.45 pct, enhanced the hardness and both ultimate and yield strength of the experivzental steels in the quenched and tempered condition. The structural and morphological chazges indicated that uranium retarded tempering of the tnartensite, thereby hindering the normal formation of polygonal ferrite formed in the late stages of tempering. The effect of this was to make possible the re-tension of the acicilar ferritic structure in the uranium-bearing' steels. The iraniuin-bearing steels also showed IVidnzanstatten-type growth of ferrite plates and had large prior austenite grains containing assenzblies of fine ferrite grains, mainly acicular in geometry. The fine-grained ferrite structure and the presence of more numerous and apparently smaller precipitates in the uranium-bearing steels are thought to he principally responsible for the itnproved tensile strength and hardness of the experinzental uranium-bearing steels. At ternperirzg temperatures above 455% (850'F) the ferrite in the higher-uraniun steels nzaintained acicularity and, hence, its strength and resistance to tempering. Uranium did not produce a secondary hardening peak. However, it retarded softening during the third stage of tempering because of its effect of inhibiting the grouth of cementite particles and of retaining the acicularity of ferrite plates. The resistance to coalescence accounted for the slow grocth of the ferrite grains in the uranium-modified steels and, hence, fov the persistence of the acicular ferrite structure. IT had been found previously1 that uranium additions up to about 0.45 pct had no significant effect on the tensile properties of low-carbon steel (0.06 to 0.10 pct C) in the as-rolled and normalized conditions, Fig. 1. On the other hand, it was observed that uranium in excess of about 0.30 pct had an embrittling effect as revealed by Charpy V-notch impact results. It was also noted that, as the uranium content increased, the morphology of pearlite changed from lamellar to feathery and the ferrite grains showed an etching effect resembling striated or dashed markings, suggestive of precipitation. The sharp drop in the impact properties shown in Fig. 2 warranted an assumption that the uranium content of about 0.30 to 0.45 pct may produce some secondary hardening reaction on tempering, analogous to that associated with a Cr-Mo-V steel, which shows very poor CVN toughness at the secondary hardness peak in the tempering curve.1' With this background and the reported findings of Hasegawa and noda that low-carbon uranium-treated steel showed signs of secondary hardening, the present investigation was undertaken to determine the effect of uranium additions on the mechanical properties of 0.10 pct C steels. No attempts were made to investigate in detail the mechanisms of hardening, although some suggestions based on the experiments are made. MATERIALS AND PROCEDURES A series of 50-lb induction-furnace melts was made using AISI 1008 rimming steel billets as the melting stock. The melting, forging, and rolling techniques proven satisfactory in previous projects'-3 were employed as a guide for this investigation. The steel was deoxidized with aluminum (2 lb per ton) prior to the addition of high-purity uranium. The analysis of each melt is given in Table I. Properties were evaluated as a function of heat treatment and are presented in terms of hardness and tensile strength vs tempering temperatures. The variation of hardness with the tempering temperature was studied on the quenched and tempered specimens, some of which measured 0.50 by 0.25 in. diam and the others 0.40-in. cubes. Before quenching, the specimens were vacuum-sealed in glass tubes and normalized at 900°C (1650°F) for 20 min. Following this treatment, the sealed specimens were hardened by austenitizing at 955°C (1750°F) for 20 min and water quenching, and then tempered for 1 hr in the range 150 to 730°C

Jan 1, 1967

By F. M. Smith, R. H. Moore, J. R. Morrey

Electrodiffusion in y cerium reported by Henrie has been confirmed and a Preliminary estimate made of the relative rates of electrodiffusion of iron, cobalt, and nickel. These diffuse to the anode at rates decreasing in that order. In addition, copper and manganese exhibit slow, but detectable, diffusion to the anode and molybdenum exhibits detectable diffusion to the cathode. The electrodiffusion of carbon, .zirconium, antimony, magnesium , and silicon in y cerium could not be detected. Iron and cobalt diffuse in y cerium at rates proportional to the current density and with no apparent dependence on temperature. Decreasing polarization of iron and cobalt with increasing temperature, which cancels the expected rate increase, would account for this behavior. The electrodiffusion rate of iron in y uranium and in E plutonium has been measured. Diffusion of iron is anode-directed. Tin was found to diffuse to the cathode, in y uranium, at an appreciable rate. In all of these solvent metals, negative ions diffuse to the anode and positive ions to the cathode. The potential field effect appears to account satisfactorily for these results. FROM early experimental work summarized by Jost1 and Seith,2 the driving force for electrodiffusion was attributed to the potential field acting on ions in a metal. More recently, Heuman,3 Wever,4 and Huntington5 have shown that momentum interchange between conduction electrons and mobile entities in the metal contributes to electrodiffusion. Electron momentum interchange is anodically directed and the direction of diffusion resulting from the field force is dependent upon the charge on the diffusing entity. These two effects may either reinforce or oppose each other. Glinchuk6 has pointed out that momentum transfer in defect conductors should be cathode-directed and this appears to be the case as demonstrated by wever's4 work on iron. Barnett's7 work, on the other hand, indicates that, even in defect conductors, electrons show a negative E/m ratio when accelerated with respect to the lattice and should lead to anode-directed momentum transfer. In discussing this problem, Wever and seith8 suggest that defect electrons interact preferentially with activated ions so as to allow a net movement toward the cathode while still maintaining an electron momentum transfer in the anode direction. Williams and Huffine9 and Henriel0 have demonstrated that electrodiffusion may be useful for purification of yttrium and cerium. In yttrium, Williams and Huffine note that movement of several metallic impurities toward the anode is in keeping with observations in most other metallic systems and indicates that yttrium remains a normal electronic conductor at least to 1230°C. Close inspection of their data shows, however, that oxygen, nitrogen, and the transition elements diffused toward the anode, while nontransition elements diffused toward the cathode. This suggests that potential field effects may have been appreciable. The present work was concerned with the applicability of electrodiffusion as a technique for purification of plutonium, but, because of the obvious hazard inherent in work with this metal, experiments to develop the technique were carried out using cerium and uranium. The results of electrodiffusion measurements on these metals and on plutonium are reported here. EXPERIMENTAL The metal specimens prepared for this work were 6 in. long, 1/4 to 1/2 in. wide, and 1/16 to 3/32 in. thick. The uranium specimens were machined from a bar which analyzed 310 ppm Fe and the electrodiffusion of iron was followed by spectrographic and by chemical analysis. Cerium and plutonium specimens were cut from sheet rolled from ingots obtained from molten salt-metal equilibrations during which radioactive tracers were introduced. The electrodiffusion of the tracers was subsequently determined by counting methods. The specimens were electrolyzed between nickel electrodes containing resistance heaters used to equalize the specimen and electrode temperatures, thereby reducing thermal gradients. The temperature of the electrodes adjacent to the ends of the specimen was measured with chromel-alumel thermocouples which were connected to the heater controls. The surface temperature of the specimen at a point midway between the electrodes was measured with a sapphire rod pyrometer, the output of which controlled the dc power supply. This assembly was enclosed within an evacuable chamber containing a quartz viewing window. The temperature of the specimen over its entire length could be scanned with a portable pyrometer through

Jan 1, 1965

By J. H. Waxweiler, L. C. Ikenberry, R. J. Bendure

Carbon which is present as insoluble carbides in austenitic stainless steels can be measured quantitatively by dissolving the steel in iodine-methanol and analyzing the residue for carbon. Severe sen-sitization was observed in Type 302 due to precipitation of only 0.003 pet carbon. Both cold work and the presence of delta ferrite caused a marked acceleration in rate of carbide precipitation. Carbide precipitation rates in 17-7 PH were stzulied for the austenite conditioning and also the aging heat treatment. CARBON and its compounds exercise a major influence on the properties of stainless steels and their response to thermal treatment. Sensitization in 18-8 type stainless steels has been the subject of numerous investigations throughout the years. Bain, Aborn, and utherford," and Binder, Brown, Frankss all studied the effects of heating austenitic stainless steels in the temperature range of 1000° to 1500°F. The primary purpose of most of these studies was the investigation of susceptibility to in-tergranular attack in acids due to these sensitizing heat treatments. Intergranular precipitation of carbides was always associated with intergranular attack but it was recognized2 that severe attack could occur with but minute quantities of precipitated carbide. Mahla and ielsen utilized the electron microscope to make a significant contribution in illustrating the appearance and method of growth of chromium carbides during sensitizing heat treatments. However, as they stated, their studies of residues could not be used to obtain a quantitative measurement of the amount of carbon which was actually precipitated. The aim of the present investigation was to devise a relatively fast, simple method for the quantitative measurement of carbides in stainless steel. EXPERIMENTAL WORK The initial investigations were made to determine the best means of separating carbides from the matrix. A number of dissolving media were tried using both chemical and electrolytic attack. Qualitative examination of the extracted residues by X-ray diffraction indicated that solution in iodine-methanol would furnish a good means of separation. Consequently, further work was pursued along this line. The method is quite simple. The sample in the form of millings or nibblings is dissolved in iodine-methanol solution at room temperature (6-g iodine, 25-ml methanol per g of sample). The insoluble residue containing the carbides is separated by suction filtration through an ultra-fine glass filter disc. This is a very fine filter medium that will retain particles as small as 0.1 to 0.2 p in diameter. After washing with methanol and drying, the filter disc and residue are placed in a conventional combustion carbon-tube furnace and the carbon determined gravimetrically. Using this technique it was found that reproducible insoluble carbon values were obtained. However, since such small amounts of insoluble carbon were obtained on Type 302 after sensitizatipn at 1250°F and 1500°F, the values were confirmed by a second method. In the second method the sample was dissolved with copper potassium chloride and filtered through a millipore paper. This treatment dissolves the matrix but leaves undissolved practically all of the carbon irrespective of how it is present in the steel. The amount of insoluble carbon present as chromium carbide is determined by calculation from the analysis of the residue for chromium and iron. The derivation of the formula used for this calculation is discussed later. The values obtained by the indirect copper-potassium-chloride method were in agreement with those obtained by the iodine-methano1 method. See Table I. It should be pointed out that the sensitivity of the direct combustion method is not too high when the amount of carbide present is small. This is due primarily to inherent blanks and to analytical errors such as weighing. For this reason it cannot be stated with any degree of certainty that there is a significant difference between values of 0.002 and 0.005 pct. Having confirmed that the iodine-methanol extraction gave a quantitative measurement of the precipitated carbides in Type 302, exploratory tests were conducted on Armco 17-7 PH stainless steel. Samples from commercial Heat 54807 were solution annealed at 2000°F, water quenched and heated at 1250" and 1500°F, and water quenched. The analysis of Heat 54808 is as follows:

Jan 1, 1962

By C. W. Arnold, H. L. Stone, D. L. Luffel

The purpose of this research is to determine (I) the efficiency of small banks of enriched gar driven by methane in displacing oil from a porous medium and (2) the effects of variation in bank size and composition of that efficiency. Most of the experiments were conducted in a sand-packed tube 20-ft long and 1/2-in. in diameter. The hydrocarbon system generally used was methane, butane and decane at 2,500 psia and 160°F. The results of these experiments indicate that, in the regions contacted by the gas, a small bank of an oil-miscible gas driven by methane can displace all of the oil in a piston-like manner. If the enriched gas is of such composition as to remain immiscible with the oil, displacement of oil is less efficient than for the miscible case, and the gas bank travels through the sand with a velocity less than that of the driving gas. These data along with theories discussed imply that smaller banks and less total gas are required when the enriched gas and oil are miscible. INTRODUCTION Widespread application of enriched-gas drive to the recovery of oil rests upon a key factor — the use of limited quantities, or "banks", of enriched gas. At the present time, the value of liquefied petroleum gas or other enriching agents discourages their use in a continuous injection technique, or even in a large bank, except in a few isolated reservoirs. If small banks of enriched gas driven by methane were as effective in displacing oil as is continuous injection, the enriched-gas drive process might be applied to a larger number of reservoirs. Previous research on the mechanics of the enriched-gas drive process reported by Stone and Crurnpl and by Kehn, Pyndus and Gaskell has utilized continuous injection of enriched gas. This work has shown that two types of displacements occur. With gases containing sufficient intermediates. the oil is displaced misciblv and complete recovery is obtained from the regions swept. When gases are used which contain insufficient intermediate hydrocarbon for miscible displacement, oil is displaced immiscibly. In the latter type, selective solution of the intermediate hydrocarbons causes a swelling and reduction in viscosity of the oil and leads to an increased recovery over that obtained by dry-gas (methane) drive. The size of the enriched-gas bank necessary for efficient displacement of oil is determined by those factors which cause deterioration of the bank. A differentiation may be made between those factors which operate on a microscopic scale and those which act on a macroscopic scale. On the smaller scale, the enriched gas mixes in the direction of flow by diffusion and convection with the fluids immediately preceding and following it. On the larger scale, the gas may by-pass the oil by flowing through permeable streaks, by overriding the oil because of density difference, or by fingering because of unfavorable viscosity ratios. In such cases, the enriching material tends to mix with the oil both laterally and in the direction of flow. The increase in effective area available for diffusion and dispersion of the enriching components leads to a faster degradation of the bank and a need for a larger bank than is necessary for those cases in which no by-passing occurs. The effects of such macroscopic factors in the deterioration of enriched-gas banks have been reported in a separate paper by Blackwell, Terry and Rayne. The present study was confined to the factors which operate on the smaller scale, in particular to the behavior of banks of enriched gas in sands uniformly swept by the gas. Experiments were designed to answer the following questions. 1. Can small banks of enriched gas driven by methane be used to secure oil recoveries comparable to those obtained by continuous injection of enriched gas? 2. What is the optimum bank size (the minimum bank size necessary to obtain a recovery comparable to that obtained by continuous injection of the same enriched gas)? 3. How many total pore volumes of gas must be injected to obtain the maximum recovery when the optimum bank size is used? 4. What is the effect of varying the number of enriching components in a gas bank? This report describes the experimental investigations and discusses the results in terms of their significance to reservoir behavior.

By N. J. Themelis, P. Spira

The efficiency of the reverberatory furnace operation in producing. slags of 1020 copper content depends on the mixing and flow conditions in the bath. Radioactize-tmcer tests have indicated the jkaction of bath volume engaged inflow and the mixing conditions in the bath. The factors controlling the flow pattern of slag have been classified as laminar transfer flow, natrsral convection, and flou, due to the rapid addition or removal of slag.. Similarity criteria for model studies have been developed. The pyrometallurgical processing of copper begins with the smelting of either flotation concentrates, or direct-smelting ores which have been partially roasted to calcines. These materials are generally smelted in a reverberatory furnace, Fig. 1, and separate into two liquid phases, a sulfide matte and an iron silicate slag. he matte is tapped and subsequently reduced to metallic copper in a converter, while the reverberatory slag is usually discarded without any further treatment. Molten slag from the converting operation is returned intermittently to the reverberatory in order to recover its high copper content (1 to 3 pct Cu). The reverberatory furnace is about 115 ft long by 30 ft wide. In general, the solid charge is fed at intervals through openings along the sides of the roof and forms sloping banks from which the molten materials trickle down into the bath; the charge banks extend over a length of about 70 ft from the firing wall. The depth of the slag and matte layers varies from smelter to smelter; in the Noranda furnaces, the slag depth is 24 to 30 in., while the depth of matte at the taphole is about 20 in. Apart from smelting, the functions of the reverberatory are to recover most of the copper content in the converter slag by physical and chemical interaction with the furnace bath, and to provide adequate time for optimum separation between matte and slag. The efficiency of these operations depends on the mixing and flow conditions in the bath and is reflected on the copper losses in the slag. In the present study, the reverberatory furnace is considered as an open-channel chemical reactor and the driving forces for material transport through the bath are examined by means of flow and mathematical models. FLOW CONDITIONS IN THE REVERBERATORY FURNACE To facilitate the study of mixing conditions in continuous-flow reactors, two idealized patterns of flow have been accepted by workers in this field.' The term "backmix" flow is used to describe complete and instantaneous mixing in the reactor (perfect mixing); all particles have the same chance of leaving the system, independently of their time of entrance, and the fluid is uniform in composition throughout the vessel. On the other hand, "plug" flow, or "piston" flow, assumes that a fluid element moves through the reactor without overtaking or mixing with fluid entering at an earlier or later time. In addition to the two idealized patterns of flow, "deadwater" flow accounts for that portion of the fluid which is moving so slowly that it may be assumed to be stagnant. According to the definition by evensppiel,' the cut-off point between active and stagnant fluid may be taken as material which stays in the vessel for a period twice the mean residence time. The flow patterns in real vessels may be approximated by a combination of the above flows. Thus, the vessel is assumed to consist of interconnected flow regions with various modes of flow existing between them. The flow pattern may be determined directly from the flow paths of fluid through the essel. -However, the difficulty of obtaining and interpreting such information has led to the alternate approach of determining the residence time distribution of fluid elements by means of stimulus-response studies. The stimulus is provided by introducing a tracer in the inlet stream and the response by the record of the change in tracer concentration in the exit stream from the reactor. Such tests have been conducted in glass tank furnaces using either chemical7"9 or radioactive tracers1'-'' and, in one case, experiments have been reported for a metallurgical furnace.'"

Jan 1, 1967