By Everett H. Graff, Ray H. Misener

THE Sol de Oro mine is in the province of Nazca, 487 km. southeast of Lima, and 60 km. inland from the coast at an elevation of 1200 m. above sea level. From Lima the mine may be reached in 8 hr. by automobile; 472 km. from Lima to Nazca over the paved Pan-American Highway and 15 km. from Nazca to the mine over a good graveled road. The trip from Lima can also be made in 2 hr. via the Faucett Air Lines which make two stops weekly at Nazca. The [Compania] Aurifera Nazca, owning and operating the Sol de Oro mine, was organized in Lima in 1930 by a group of prominent Peruvian mining men, including Ing. Carlos Alvarez Calderon, Dr. Alfredo Alvarez Calderón, Ing. Hector Boza, Ing. Jorge Félix Remy, Ing. Eulogio Femandini, Sr. Fernando Wiese, and Sr. Julio East. The nine claims in the Sol de Oro group owned by the company comprise an area of 52 square kilometers. Development of the property was not started until 1932 and only then under adverse conditions, owing to lack of transportation facilities. Mining machinery and other supplies could be taken as far as Ica by boat and railroad, but to transport them over the 180 km. of hot, sandy desert from Ica to the mine was a problem. There was no road in those days and only a few of the most venturesome truck drivers cared to contract the hauling. Another problem the company had to face was that of securing adequate labor. The Sol de Oro is in an agricultural region, and was forced to look to the near-by cotton plantations for men. Experienced men were imported from the "sierras," but they did not stay. The men are accustomed to high altitudes and cold climate and cannot easily acclimate themselves to the hot and arid coastal region. As a consequence the company has been forced to hire the inexperienced local laborers and train them for mining. The company has established three separate camps at the Sol de Oro property. Each is approximately one kilometer from the other and connected by auto road. The upper mine camp consists of living quarters for 300 workmen and their families, a general mine office, carpenter shop and timber-framing shed, compressor house, drill-sharpening and drill-repair shop, first-aid station, time office, school and store. At the central or "empleados" camp there is a 200-ton cyanide plant, general offices, warehouse, powerhouse, shops, laboratory, hospital, school, guest house, an 18-room hotel for the single staffmen, and 12 completely modern five-room cottages for the married staff employees. At the lower camp are living quarters for 200 workmen and their families, two general stores, a school and a small theater. Below this camp, along the river, are the company wells and pumping plant supplying water for mine, mill, and camp uses.

Jan 1, 1945

By David B. Reger

The discovery of prolific oil wells in old territory hitherto regarded as doubtful, if not worthless, and the rapid extension of a gas pool opened late in 1938 were the most interesting petroleum features in West Virginia during 1939. Oil activity in general was slow because of crude prices that were still fairly low at the end of the year, although substantially increased above those in January. Fewer oil wells were completed, but the average results were better than in 1938. Fewer gas wells, also, were completed, with greatly lessened average initial production. Many old oil and gas wells were abandoned, so that the total number of active wells has not changed appreciably. The account of operations, as gathered from trade journals and other sources, shows that 561 new wells were drilled, resulting in 101 new oil wells with 2261 bbl. of daily initial production; 366 new gas wells with 602,400,000 cu. ft. of daily open flow; and 94 dry holes. Besides these new wells, 61 old wells were drilled to deeper sands, with 12 bbl. and 13,328,000 cn. ft. of added production. On the new wells the oil average was 22.38 bbl. per well per day; and the gas average was 1,645,900 cu. ft. per well per day; the ratio of dry holes to completions was 16.76 per cent. From an exploratory standpoint one partly discredited oil area was revived by good new production, and another small oil pool may have been opened. Some of the results in gas exploration will require more drilling for true appraisal. It is certain, though, that one very considerable gas field in the sands of Mississippian age has been proved; and there is a probability of six new pools in the Middle Devonian shale. In the Oriskany sand (L. Dev.) the Elk-Poca pool has been extended considerably farther northwest into Jackson County; and farther north in Jackson County two widely separated wells, which may be pool openers, have been successfully completed. On the other hand, several important wildcats in various counties have been dry. Stratigraphically lower, some additional wells have been completed in the Newburg sand (Sil.) and one small producer has been completed in the Clinton sand (Sil.), the importance of which can scarcely be overestimated, because no Clinton production has previously been found in the state, although at least seven wells have been drilled through the sand.

Jan 1, 1940

By David B. Reger

The discovery of prolific oil wells in old territory hitherto regarded as doubtful, if not worthless, and the rapid extension of a gas pool opened late in 1938 were the most interesting petroleum features in West Virginia during 1939. Oil activity in general was slow because of crude prices that were still fairly low at the end of the year, although substantially increased above those in January. Fewer oil wells were completed, but the average results were better than in 1938. Fewer gas wells, also, were completed, with greatly lessened average initial production. Many old oil and gas wells were abandoned, so that the total number of active wells has not changed appreciably. The account of operations, as gathered from trade journals and other sources, shows that 561 new wells were drilled, resulting in 101 new oil wells with 2261 bbl. of daily initial production; 366 new gas wells with 602,400,000 cu. ft. of daily open flow; and 94 dry holes. Besides these new wells, 61 old wells were drilled to deeper sands, with 12 bbl. and 13,328,000 cn. ft. of added production. On the new wells the oil average was 22.38 bbl. per well per day; and the gas average was 1,645,900 cu. ft. per well per day; the ratio of dry holes to completions was 16.76 per cent. From an exploratory standpoint one partly discredited oil area was revived by good new production, and another small oil pool may have been opened. Some of the results in gas exploration will require more drilling for true appraisal. It is certain, though, that one very considerable gas field in the sands of Mississippian age has been proved; and there is a probability of six new pools in the Middle Devonian shale. In the Oriskany sand (L. Dev.) the Elk-Poca pool has been extended considerably farther northwest into Jackson County; and farther north in Jackson County two widely separated wells, which may be pool openers, have been successfully completed. On the other hand, several important wildcats in various counties have been dry. Stratigraphically lower, some additional wells have been completed in the Newburg sand (Sil.) and one small producer has been completed in the Clinton sand (Sil.), the importance of which can scarcely be overestimated, because no Clinton production has previously been found in the state, although at least seven wells have been drilled through the sand.

Jan 1, 1940

Jan 1, 1971

By Y. C. Liu, G. A. Alers

measurements of the anisotropy in Young's modulus produced in copper by rolling 95 pct reduction in thickness below room temperature have been carried out in order to study the dependence of the texture on rolling temperature. The results clearly show the transition from a copper-type texture to a brass-type texture as the temperature of rolling is lowered. The intermediate textures observed can be described very well as a simple mixture of the two terminal textures. These results cormbined with other texture measurements make possible afresh review of the experimental facts velating to rolling textures in fee metals and, as a consequence, a critical examination of the current theories is presented. PREVIOUS experiments have shown that the transition from the copper- to the brass-type rolling texture is clearly displayed and can be quantitatively analyzed by measurements of the anisotropy of Young's modulus.' Application of this method to the Cu-Zn alloy system showed that the description of the texture transition as a gradual rotation of the grains from the orientation characteristic of the copper texture to the {110}(112) texture of brass2 was inconsistent with the data. Instead, the data suggested that the texture within the transition region could be described as a simple mixture of the two terminal textures.5 Unfortunately, it was difficult to establish this point conclusively because of the inadequacy of corrections for the composition dependence of the single-crystal elastic constants. Since a rigorous establishment of the nature of this texture transition is essential to our understanding of the formation of rolling textures in fee metals, it is clearly important to undertake an investigation in which the composition dependence of the elastic constants would not enter. A suitable composition-independent texture transition is provided by the well-established variation in the rolling texture of copper with rolling temperature. This temperature-dependent texture transformation has been studied by smallman' in several fee alloys and by Müller5 and others"' in copper. They observed that the texture characteristic of copper rolled at room temperature changed to a brass-type texture when the rolling temperature was lowered to 77°K. Although it is not possible to decide unequivocally from the published pole figures whether or not the 77°K rolling texture of copper is entirely of the brass type,' this complication does not affect the main purpose of the present investigation. In addition to establishing the nature of the texture within the transition region, the modulus data should also provide a determination of the temperature at which the transition occurs as well as the temperature range over which the transition extends. This information when combined with the modulus data on Cu-Zn alloys would then provide a considerable body of new information on textures in fee metals. Since these modulus results and the data obtained from pole-figure studies must be internally consistent, it is appropriate to compile a brief summary of the experimental observations based on all available methods rather than on the pole-figure data alone as has been done in the past. The primary purpose of such a summary would be to yield a more precise definition of the experimental facts on the rolling textures of fee metals, and thus greatly facilitate our evaluation of various proposed theories in this field. The final section of this paper is devoted to this compilation of consistent, experimental facts and their application to the various theories. EXPERIMENTAL PROCEDURE Two 18-lb ingots of cathode copper of 99.99 pct purity were induction-melted under a nitrogen atmosphere in a graphite crucible and chill-cast into a steel mold. The ingots were repeatedly cold-rolled and annealed (I hr at 500°C) into slabs about 1 1/8 in. thick. Blocks 3 1/4 in. wide, 2 1/4 in. long, and 1.000 in. thick were machined from each slab. The rolling schedule used was the same as in the previous investigation1 and the final thickness of the sheet was 0.050 in. with a rolling reduction of thickness of 95 pct instead of 97.5 pct as in the previous work.' The compositions and temperatures of the cold baths used for the low-temperature rolling were as shown in Table I. After each pass the rolled strip was immediately immersed in the cold bath for about 1 min or until the bubbling of the bath had subsided. The modulus data were taken within 2 hr after the rolled strip was warmed to room temperature for the first time, so that effects due to recrystallization were minimized. The modulus specimens were in the shape of flat bars, 3 in. long, 4 in. wide, and 0.050 in. thick, cut with their long dimensions oriented at 15-deg intervals between the rolling direction and the transverse direction. The values of Young's modulus were deduced from measurements of the frequency at which these long narrow bars were set into longitudinal, resonant vibration as previously described.9 To excite the mechanical vibrations in the specimen, an electromagnetic drive similar to that employed by Thompson and lass" was used. The maximum in the amplitude of

Jan 1, 1968

By L. K. Jetter, J. C. Ogle, C. L. McHargue

The preferred orientation developed in extruded aluminum rods has been studied as a function of extrusion temperature, extrusion speed, and position in the rod. Duplex <111> - <001> textures were developed for slow extrusion speeds at temperatures of 75° to 850° F and for fast extrusion speeds at temperatures of 75° to 450°F. The <001> texture component was shown to be primarily due to re crystallization occurring during fabrication. At fast speeds and billet temperatures of 650° to 850°F, complete recrystallization occurred and <115>or<118> textures were found. The nature of the structure has proved to be an important variable in the production and use of extruded products. Data on the flow of aluminum and aluminum alloys summarized by Smith,&apos; Hardy,&apos; and Locke3 show that the extruded product may possess a deformed, a partially recrystallized, or a completely recrystallized structure, and there may be important variations in the structure from surface to center and from front end to back end of an extrusion. This inhomogeneity in grain structure and preferred orientation affects both the mechanical properties of the extruded section and its response to subsequent heat treatment. Among the fabrication variables causing these differences are temperature, extrusion ratio, and extrusion speed. Preferred orientation which develops during the extrusion of rods is of the fiber-type and, in general, has been assumed to be similar to that developed in rods or wires fabricated by drawing through dies, rolling, or swaging.4 Because of the nature of the flow of metal being extruded, this assumption may be valid for material near the center of the rod but probably is not valid for the outer layers. In most face-centered-cubic metals a duplex fiber texture has commonly been reported in which the grains have either <Ill> or <001> directions parallel to the longitudinal axis. Sachs and fichiebold5 reported cold-drawn aluminum (99.6 pct pure) to have a single <Ill> fiber texture, and this observation was confirmed by Schmid and Wassermann.6 Hibbard, on the other hand, observed a minor <001> and a major <111> texture in 99.994 pct A1 cold drawn to 98 pct reduction in diam.7 He concluded that the <001> component resulted from a small amount of room-temperature recrystallization. Dayal8 concluded that the <001> component was an intermediate component which disappeared at high reductions in 99.5 pct pure Al. Kostron and schippers9 found duplex <111> — <001> textures in extruded 99.5 pct Al, as did Gow and cahnl0 and GOW11 for extruded rods of commercial and superpure aluminum. Similar duplex fiber textures have been reported for aluminum alloys by Kostron,= Unckel,13 and Van Horn.14 The present paper is concerned with the variation in texture with fabricating conditions and with the nature of the texture components in extruded aluminum rod (99.99 pct pure). EXPERIMENTAL PROCEDURE Ingots were chill-cast in cast-iron molds and machined to 3-in. diam by 6-in. long extrusion billets. These billets were upset to 3.125 in. diam and extruded through a flat-face 0.690-in. diam die. Quenching of the rods was accomplished by a water spray at the die face. The combinations of fabricat-

Jan 1, 1960

By J. C. Scully

In June, 1965, Sanderson and scully5 reported at the Conference on Environment Sensitive Mechanical Properties of Materials at the Research Institute for Advanced Studies at Baltimore that thin foils of titanium could be prepared by chemical polishing in a mixture of 44 pct HF and 73 pct HNO3 in the volumetric ratio 2:3. The technique is simpler than that since reported by Rice and Orava. As-received annealed titanium (containing 0.8 pct Fe and 30 ppm H) in the form of sheet 0.05 cm thick is placed in the solution and moved up and down. The reaction is violent but suitable foils are obtained very easily and consistently. A typical micrograph is shown in Fig. 3. The small precipitates were not identified. Yamane and ueda6 observed many spotlike features which they referred to as small dislocation loops. While their spots may be due to the reaction of the warm foil with the air as suggested by Rice and Orava, the precipitates in Fig. 3 are also found when foils of titanium are prepared by electro-polishing at low temperatures and subsequently examined in the electron microscope without any inter- mediate warming. Furthermore, they are not a surface effect. It is necessary to add that alloys of titanium cannot be so easily thinned by the chemical polishing solution described above since it contaminates the a, phase with hydrogen and produces y hydride. These matters are described at length in a paper7 and their relevance to stress corrosion is considered elsewhere.&apos;-* Author&apos;s Reply The authors are grateful to Dr. Scully for bringing to our attention his hitherto unpublished technique for thinning unalloyed titanium, and deeply regret the unintended apparent duplication. The chemical thinning solution (7 parts HNO3 and 3 parts HF, by volume) reported by us is the same as that with which, for some period in the past, we had experienced success in the preparation of foils from single and polycrystalline niobium. Its subsequent effective application to titanium was a logical step, which, clearly independently of Scully, was conceived by Mr. Rice, to whom full credit is due. A few comments are warranted concerning some of the details of the preceding Discussion. It is evident to the discerning reader that the two thinning techniques under consideration are chemically almost identical, and in that sense are equally "simple". The chemical aspect is, of course, the one of primary importance in both communications. Thereafter, the relative simplicity is dictated by the mechanics of the actual thinning operation selected by the individual investigator. Our standard dimpling, or dishing, procedure was chosen with a view toward providing, for the electron transparent areas of the sample, the maximum protection from extraneous deformation during handling. That the long, straight dislocations visible in Scully&apos;s electron micrograph of a seemingly recovered structure closely resemble handling dislocations would tend to indicate the merit of our adopted technique. Features similar to those which Scully has attributed to precipitates, without any apparent diffraction contrast confirmation, were not observed in any of our clean foils taken from annealed or deformed specimens. This was admittedly somewhat surprising since the 3700 ppm (nominal) Fe in the A-70 commercial-grade titanium examined should have given rise to TiFe precipitates. Presumably these existed but were un-resolvable. Curiously, Scully&apos;s "precipitate1&apos; density is fairly high although the iron content quoted was less than one-fourth of that in our material. One is forced to conclude from the evidence that prior thermal and mechanical treatments are responsible for the two different types of structure observed.

Jan 1, 1968

By A. Vignes, J. P. Sabatier

A study of ternary diffusion at 1315°C in the Fe-Co-Ni system covering the entire ternary phase diagram has been carried out. Experimental values of the four interdiffusion coefficients DFeNico,DFeCoCo, DFeCoNi were computed at 33 points of the ternary diagram. The limiting values of these coefficients on the three sides of the ternary diizgram have also been determined. This set of data is presented as a contour map on the ternary isotherm for each of the four coefficients. Assuming that the Fe-Co-Ni system can be considered as ideal, the phenomenological coefficients Lk ij (with k = Fe) have been computed and the Onsager reciprocal relutions verified. It is shown that, in the Fe-Co-Ni system, the diffusion process can also be described by only two interdiffusion coefficients DFeFe and DCoNiFe, the second cross diffusion coefficient DCoFeNi being equal to zero and the second direct difusion coefficient being given by The values of the cross interdiffusion coefficients and of the Onsager coefficients are explained in terms of atomic mobilities of the three components with the help of a kinetic calculation due to Lane and Kirkaldy.8 It is shown that all the results are explained if the tracer difusion coefficients of the three components are such that DFe > DNi ~ DCo in complete agreement with experimental data on the three binary systems. DIFFUSION in a ternary alloy system is basically and significantly different from diffusion in binary alloys. In binary diffusion, there is just one independent composition variable and only one coefficient Dij is needed to describe the interdiffusion process. In ternary diffusion, we must allow for cross interaction between two independent species, and four interdiffusion coefficients are necessary to describe the transport process. Kirkaldy et al.1,2 have determined interdiffusion coefficients in the systems, Cu-Mn-A1 and Zn-Cu-Al. Guy and Leroy4 have reported intrinsic diffusion coefficients for the r phase at 1300°C of Co-Ni-Cr alloys as a function of composition using the analysis of Philibert and Guy.3 Interdiffusion coefficients were measured at three different compositions at 850°C in the single phase copper-rich corner of the Cu-Zn-Mn system by Dayananda and race.5 Zie-bold and Ogilvie6 have determined interdiffusion coefficients in the single-phase field of the Cu-Ag-Au system at 725°C. Preliminary results on diffusion at 1136°C in the system Fe-Co-Ni have been reported.7 In this study, data are reported on a more complete determination of interdiffusion coefficients in the Fe-Co-Ni system in the entire ternary at 1315°C. There is complete solid solubility with the fcc structures at 1315ºC, and this system can be considered as nearly ideal. This approximation allows the computation of the Onsager phenomenological coefficients. These values can then be used to test a kinetic calculation of the Onsager L coefficients in ternary substitutional solid solutions due to Lane and Kirkaldy.8

Jan 1, 1970

By J. W. Freeman, R. F. Decker

A microstructural investigation was pursued to establish the mechanism of the pronounced benefits of traces of boron and zirconium on creep properties of a 55 Ni-20 Cr-15 (20-4 MO-3 Ti-3 A1 alloy at 1600°F. The mechanism of improvement of creep properties was found to be a pronounced stabilizing effect of traces of boron and zirconium on the grain boundaries of the alloy. The alloy with low boron and zirconium was subject to rapzd agglomeration of M23 C6 and in the grain boundaries, followed by depletion of y &apos; and intergranular microcracking at the grain boundaries transverse to applied stress. Brittle fracture then occurred by linking of microcracks. However, additions of zirconium, boron, and boron plus zirconium decreased this tendency in that order, allowing longer creep exposure and higher creep defor.mations before fracture occurred. VERY little information has been published describing the mechanism by which trace amounts of boron or zirconium improve the creep properties of complex nickel-base heat-resistant alloys, although the effect is now well recognized.1-4 Because the phenomenon is so important to properties and the effects are so striking, a study was made of the mechanism in a 55 Ni-20 Cr-15 Co-4 Mo-3 Ti-3 A1 alloy. It was believed that such a mechanistic approach would increase knowledge in theory of alloying and give a more basic understanding of alloy design to resist creep. The basic premise of the study was that boron or zirconium would alter the microstructural characteristics controlling creep and fracture to the extent that the effects could be identified by light and electron microscopy and by electron diffraction techniques. Characteristic of the microstructure of the Ti + Al-bearing nickel-base alloys is the dispersed precipitation of the intermetallic compound Ni,(Al, Ti), the ? &apos; phase, which is generally con- sidered to be the major source of high creep resistance.5-7 In addition, carbide phases have been identified8-10 and these can alter creep properties markedly.11 Since both the ?&apos; and carbide transformations have been found to control properties, careful attention was paid to the effect of boron and zirconium on these transformations.

Jan 1, 1961

Official Program

Jan 8, 1950

Discussion of the paper of H. R. Barnhurst, presented at the New York Meeting, October, 1913, and printed in Bulletin No. 82, October, 1913, pp. 2523 to 2532. H. R. BARNHURST :-I would say that in that experimental furnace we were trying to adopt the proper form for burning low-volatile coal. I was enabled on one occasion to burn coke having 15 per cent. ash. Tailings, or washings from the preparation of coal for by-product coke ovens, which came to me 52 per cent. ash, were burned without any trouble. So that ash really might be regarded as not burning, but simply diluting the fuel that was there, without doing any particular harm except that we had to put in more of the material to get the same quantity of heat. With anthracite, I burned coal right along with from 24 to 27 per cent. ash, but it took a furnace of peculiar form in which the products of combustion had to be diverted to the point of entrance of the fuel. With an ordinary furnace the fuel is deflagrated by its surroundings as soon as it enters the furnace. In a cement furnace this action is secured by the hot clinker passing clown, and the walls of the kiln are heated upon contact with it, revolving as they do&apos;, so that deflagration occurs very quickly in a cement kiln. Deflagration would occur very quickly in an open-hearth furnace also. There is no trouble in burning anthracite coal under those conditions for three or four days successively. It should be very well dried and thoroughly pulverized. Aside from that, there is no trouble. WILLIAM A. EVANS,* Boston, Mass. :-In a 52 per cent. ash, or any high-ash coal, what disposition is made of the ash ? MR. BARNHURST :-Most of it went out through the flues. Some of it remained in the boiler and a quantity remained in the furnace. We raked it out and carried it away. MR. EVANS :-Do you experience the forming of stags in flues with such coal as that?

Jan 12, 1913

Jan 1, 1970

By F. V. Lenel, M. V. Rose, A. B. Backensto

WHEN aluminum-flake powders are compacted and hot pressed and the resulting compacts are extruded or hot forged, a group of materials with unique properties is obtained. Not only do they exhibit high room-temperature strength of the order of some of the aluminum alloys, but they maintain this strength even after prolonged heat treatment at temperatures up to 900°F. Moreover, their strength decreases much less with increasing temperature than that of aluminum alloys of comparable room-temperature properties. Irmann,&apos;" who discovered and first described this group of materials, which was called SAP, showed that the room-temperature mechanical properties of the extrusions are a function of the oxide content of the powders and therefore the oxide content of the extrusions. The higher the oxide content, the higher are their tensile strength, yield strength, and hardness, and the lower their ductility. Lyle" investigated the relationship between mechanical properties at elevated temperature and oxide content in the course of the development work of the Aluminum Co. of America on materials, called APMP, similar to those developed in Switzerland. He found that at 600 °F, just as at room temperatures, tensile strength and yield strength increase and elongation decreases with oxide content. A careful study of his data (Fig. 3, loc. cit.) shows, however, that the scatter is more pronounced than at room temperature. Gregory and Grant&apos;s data on the creep5 and stress-ruptureb roperties of the one commercial grade of the Swiss SAP and the various grades of APMP indicate that creep strength and stress to rupture also generally increase with increasing oxide .content. Ever since this new group of materials was discovered, attempts have been made to explain the mechanism by which they obtain their high room-temperature and particularly their elevated-temperature strength. In most of the attempts the new material was considered as a dispersion of aluminum oxide particles in a matrix of aluminum. Ir-mann, Von Zeerleder, and Rohner&apos; applied a theory on dispersion strengthening developed by Rohners to the flake-powder extrusions. According to this theory the elastic limit S, of a dispersion would depend upon the average distance between the dispersed particles L according to the equation: 2 E ¦ a where E is the modulus of elasticity and a the distance between nearest neighbors in the lattice of the matrix material. Irmann and co-workers assumed

Jan 1, 1958

By F. N. Rhines, A. H. Grobe

At elevated temperatures the oxide of silver is unstable in the air at atmospheric pressure, consequently no external oxide scale forms upon pure silver under conditions of high-temperature annealing. When small quantities of certain alloying elements are present in the silver, the formation of a thin external scale is possible1 and in addition there may form a subscale composed of the oxide of the solute element precipitated within the body of the silver. Norbury2 and Leroux and Raub3 have reported internal oxidation (subscaleiormation) in alloys of silver with 2, 7.5, and 30 per cent of copper. The presence of the subscale is believed to be responsible, at least in part, for the objectionable "fire mark" in Sterling silver.4 Several other alloys of silver, after oxidizing heat-treatments, are known to exhibit undesirable polishing characteristics that may be the result of internal oxidation. Except for the absence of an external scale of silver oxide, it is to be anticipated that silver alloys will prove to be very similar in their oxidation behavior to the alloys of copper, the oxidation characteristics of which have been studied in some detai1.5,6 The present research confirms this anticipation. The oxidation of a series of 20 dilute alloys of silver has been studied metallographically; some types of subscale not encountered among the copper alloys have been found. Instances of internal oxidation in alloys of most of the metals of the 1-6 and VIII groups of the periodic system are on record, but evidence of this type of oxidation in alloys of the metals of the intermediate groups is lacking. A number of the metals of the intermediate group, among them cadmium, lead, tin, and zinc, appear to provide the conditions essential to subscale formation; i.e., they form oxides with a relatively low negative free energy of formation, they dissolve other metals that form more stable oxides, and, presumably, oxygen will diffuse through them. In a study of 40 alloys of these white metals only a few cases of internal oxidation have been found. The probable reasons for this difference in behavior will be discussed presently. Experimental Procedure Silver.—The silver alloys employed in the oxidation studies were prepared in heats of 30 grams each from high-purity silver (99.993 per cent Ag)* and the purest avail-

Jan 1, 1942

By A. H. Grobe, F. N. Rhines

At elevated temperatures the oxide of silver is unstable in the air at atmospheric pressure, consequently no external oxide scale forms upon pure silver under conditions of high-temperature annealing. When small quantities of certain alloying elements are present in the silver, the formation of a thin external scale is possible1 and in addition there may form a subscale composed of the oxide of the solute element precipitated within the body of the silver. Norbury2 and Leroux and Raub3 have reported internal oxidation (subscaleiormation) in alloys of silver with 2, 7.5, and 30 per cent of copper. The presence of the subscale is believed to be responsible, at least in part, for the objectionable "fire mark" in Sterling silver.4 Several other alloys of silver, after oxidizing heat-treatments, are known to exhibit undesirable polishing characteristics that may be the result of internal oxidation. Except for the absence of an external scale of silver oxide, it is to be anticipated that silver alloys will prove to be very similar in their oxidation behavior to the alloys of copper, the oxidation characteristics of which have been studied in some detai1.5,6 The present research confirms this anticipation. The oxidation of a series of 20 dilute alloys of silver has been studied metallographically; some types of subscale not encountered among the copper alloys have been found. Instances of internal oxidation in alloys of most of the metals of the 1-6 and VIII groups of the periodic system are on record, but evidence of this type of oxidation in alloys of the metals of the intermediate groups is lacking. A number of the metals of the intermediate group, among them cadmium, lead, tin, and zinc, appear to provide the conditions essential to subscale formation; i.e., they form oxides with a relatively low negative free energy of formation, they dissolve other metals that form more stable oxides, and, presumably, oxygen will diffuse through them. In a study of 40 alloys of these white metals only a few cases of internal oxidation have been found. The probable reasons for this difference in behavior will be discussed presently. Experimental Procedure Silver.—The silver alloys employed in the oxidation studies were prepared in heats of 30 grams each from high-purity silver (99.993 per cent Ag)* and the purest avail-

Jan 1, 1942

By A. H. Grobe, F. N. Rhines

AT elevated temperatures the oxide of silver is unstable in the air at atmospheric pressure, consequently no external oxide scale forms upon pure silver under conditions of high-temperature annealing When small quantities of certain alloying elements are present in the silver, the formation of a thin external scale is possible&apos; and in addition there may form a subscale composed of the oxide of the solute element precipitated within the body of the silver Norbury2 and Leroux and Raub3 have reported internal oxidation (subscale formation) in alloys of silver with 2, 7 5, and 30 per cent of copper The presence of the subscale is believed to be responsible, at least in part, for the objectionable "fire mark" in Sterling silver&apos; Several other alloys of silver, after oxidizing heat-treatments, are known to exhibit undesirable polishing characteristics that may be the result of internal oxidation Except for the absence of an external scale of silver oxide, it is to be anticipated that silver alloys will prove to be very similar in their oxidation behavior to the alloys of copper, the oxidation characteristics of which have been studied in some detail 5,6 The present research confirms this anticipation The oxidation of a series of 20 dilute alloys of silver has been studied metallographically, some types of subscale not encountered among the copper alloys have been found Instances of internal oxidation in alloys of most of the metals of the I-b and VIII groups of the periodic system are on record, but evidence of this type of oxidation in alloys of the metals of the intermediate groups is lacking A number of the metals of the intermediate group, among them cadmium, lead, tin, and zinc, appear to provide the conditions essential to subscale formation, i e , they form oxides with a relatively low negative free energy of formation, they dissolve other metals that form more stable oxides, and, presumably, oxygen will diffuse through them In a study of 4o alloys of these white metals only a few cases of internal oxidation have been found The probable reasons for this difference in behavior will be discussed presently EXPERIMENTAL PROCEDURE Silver -The silver alloys employed in the oxidation studies were prepared in heats of 30 grams each from high-purity silver (99 993 per cent Ag)* and the purest avail-

Jan 1, 1942

By George S. Rice

A problem of possible subsidence of the surface from mining operations, which might have had disastrous results, arose in 1913 at the Brier Hill mine, of the Penn Iron Mining Co., near Norway, Mich., now managed by Pickands, Mather & Co. for the Bethlehem Steel Co. A double track and sidings of the Chicago & North Western Railroad passed over part of the mine, and if subsidence had reached the surface it might have affected the stability of the tracks. The chief purpose of this paper is to record the facts disclosed by investigations of underground movement from 1913 to 1919, when the tracks were moved, and subsequently at intervals, as engineering data of value from mining carried on below the tracks in the steeply pitching lenses. A secondary purpose of this paper is to describe a novel method for determining the rate of speed of upward breaking above the mine excavations. This method was found effective and might be used elsewhere under similar conditions. The mine workings under consideration were developed from the Brier Hill shaft, which was circular, concrete-lined, 14 ft. in diameter and about 900 ft. deep. They extended about 800 ft. westward from the shaft, and nearly parallel to a corresponding length of the railroad tracks. The highest part of these workings was at a depth of 400 ft. below the tracks (Figs. 1 to 12). The mining company had the right to remove the ore, the railroad assuming that the surface would be supported. Finally, without legal controversy, an amicable adjustment was reached as to what should be done to lessen or obviate the hazard of subsidence. Method oF Mining Before the problem became acute, the mining company, to decrease the possibility of subsidence, had been mining the part of the orebody that lay under the tracks by a room-and-pillar system, back-filling with

Jan 1, 1934

By L. G. Truby

DISCUSSION By Rhrt G. Nisle, Phillips Petroleum Co., Barthesville, Okla. The subject paper presents the results of a reservoir behavior analyzer study of the pressure-production performance of five Ellenburger pools in West Texas. These five pools are Wheeler, TXL, Andector, Embar, and Martin. This laboratory has also made reservoir behavior analyzer studies in this area and arrived at substantially the same conclusions. Although the principal results of the studies made in this laboratory are confirmed by the results in the subject paper, there are certain points of difference. The points of difference are (1) the subject paper includes the Martin pool in the common aquifer, whereas our studies indicate that it is not, and (2) the subject paper concludes that the effective aquifer is considerably smaller than that derived from studies made in this laboratory. In terms of reservoir analyzer data, our rejection of Martin is based on the inability to obtain a satisfactory match of the pressure curve when Martin is considered as lying within the common aquifer. A satisfactory match was possible, however, when Martin was run as an isolated pool. This indicates that the pressure disturbance resulting from production at Martin had not reached Embar, Andector, TXL, or Wheeler at the time of our study. A similar situation exists relative to Dollarhide. In tern of geological data, our rejection of Martin is based on the presence of a faulted zone between Martin and Embar. This condition is indicated in Fig. 4 and again in Fig. 10 of the subject report. If a permeable connection between Martin and the other fields does exist, it is probably by way of a detour around this fault. The second point of difference between the two studies is illustrated by a comparison of Fig. 4 of the subject paper with Eg. A. Fig. A is obtained from an internal report on one of the studies made by this laboratory. It will be noted that the area indicated in Fig. 4 is roughly that marked "Pool Unit" in Fig. A. The additional portion of the aquifer shown in Fig. A was simulated on the reservoir analyzer by means of the water drive network. A satisfactory pressure match could not be obtained without this additional network. The differences involved here stem from a more fundamental consideration concerning reservoir analyzer operating techniques. The true source of these differences in reported results cannot at this time be determined because of the incompleteness of the subject paper. It is not stated, for instance, whether the pressure match was induced by altering the field resistance or the field capacitance, or both. Changing analyzer

Jan 1, 1953

By S. Skowronski

PURPOSE OF INVESTIGATION Since cuprous chloride melts at 418° C., boils at 954° C. to 1033° C.,1 and is known to be volatile at a much lower temperature, the presence of chlorine in any form in or on copper to be melted has always been looked upon by copper refiners as a possible source of-serious copper loss. Although this fact has been known for some time, the copper literature contains little or no information regarding it and the field seems .never to have been properly investigated from a metallurgical standpoint. According to Greenawalt,2 cupric chloride, CuCl2, when ignited gives cuprous chloride; therefore cuprous chloride is always formed when copper enters into reaction with chlorine at a high temperature. Cuprous chloride melts somewhat below a dull red heat, and does not volatilize in closed vessels, even if strongly heated, but if heated in the air it goes off as a white vapor. Hofman3 gives the melting point of cuprous chloride

Jan 2, 1919