By W. C. Ellis, E. S. Greiner, M. E. Fine

C. H. Samans and W. R. Ham (Chicago, Ill., and Dix-field, Maine, respectively)-—For several years we have been studying transitions of this basic type in metals, alloys, glasses, etc. Usually, however, they are not so clearly marked as those which the authors have found, and hence are much more difficult to determine accurately. Since our studies indicate that most of them occur virtually unchanged (as far as temperature is concerned) regardless of the form in which the element appears, we believe that they are a characteristic of the atom. Specifically, we believe that there is an additional rotational degree of freedom possessed by the nucleus which has not been considered heretofore. This nuclear rotation is made up of several components, each related to the several quantum shells of electrons. In chromium there are four of these shells and hence four separate series of characteristic transition temperatures. The lowest temperature at which any transition occurs, based on the present state of our computations, is 125°K, 4° higher than the authors' value of 121°K. A convergence of this series, we believe, shows up at the higher temperature of 2085 °K, surprisingly close to the transformation temperature of 2103°K recently announced by N. J. Grant of M.I.T. for a body-centered to face-centered transformation in chromium. Likewise, our computations indicate a temperature of 311°K for the second transition temperature, reported by the authors as 310 °K. A convergence of this series, we believe, shows up at a higher temperature as the melting point at 2163°K. Although our work on these series must, in a sense, still be regarded as empirical, since we do not understand fully as yet just what the series mean, it is based on a reasonably firm picture. The individual constants, from which the various series are computed for each element, comes directly from the X-ray K absorption limit. Furthermore, the same basic method has accounted for transformation and melting temperatures in about 50 of the chemical elements, which is all we have tried thus far. In many cases the only known transformation is the melting point, but in others the occurrence of transformations or other transitions, equally as well marked as those of the authors, has been pointed out by others. These observations have assisted us greatly. Consequently we were very pleased to see the authors' excellent work in finding these two transitions in chromium. With these confirming data, our picture of this element is clarified considerably, so we expect that at least some of our work can be published in the near future. R. C. Ruder (E. I. du Pont de Nemours & Cu., Wilmington, Del.)—The authors' interpretation of these transitions in terms of 3d to 4s electronic structure transitions is most interesting. It would be interesting to have additional experimental evidence of such transitions from the temperature dependence of the Hall coefficient in the neighborhood of the property changes discussed in this paper. Simple theory15 suggests the Hall coefficient as a measure of the free electron (or s electron) concentration per unit volume. It has been shown that for paramagnetic'" and ferromagnetic1? metals the simple theory is in fact too simple. However, the existence of a discontinuity in the Hall coefficient would provide information which should aid both in our understanding of these transitions and the significance of the Hall coefficient in these metals. It was rather surprising that no significant paramagnetic effects were observed. In this connection the recent work of McGuire and Kriessman18 is cited. They measured the magnetic susceptibility of chromium from 20" to 1460 °C. They also observed no large change in the susceptibility although there might be a change in slope in the vicinity of the 40 °C transition. The existence of these 3d to 4s electronic transitions has been discussed in connection with the paramagnetic susceptibility behavior of nickel and nickel alloys.'"-" Assuming a correspondence principle between classical and quantum mechanical paramagnetic theory and using classical theory to calculate the effective Bohr magneton number from the Curie constant for substances obeying the Curie-Weiss law," it is found that the effective magneton number is a function of temperature. The process of calculation involves the inverse of the differential of the 1/x4 vs. temperature curve so that good and numerous data are necessary to obtain significant results. The data of Fallot23 show a discontinuous increase of about 12 pct in the effective magneton number between 850" and 900 oC, followed by a continuous increase up to the melting point. The data of Sucksmith and Pearce24 show a possible 8 pct increase. The older data of Terry25 and Weiss and Foex26 show a continuous increase. It is possible that small amounts of impurity atoms change these electronic transitions significantly. Fallot's23 data on a nickel alloy with 4.5 atomic pct Fe indicate that the discontinuity occurs around 1300 °C. Systematic investigation of the transition metals for transitions of this nature should provide information which would be very valuable for our understanding of these metals. The absence of antiferromagnetic structures in chromium has been shown by Shull27 using neutron diffraction techniques. M. E. Fine, E. S. Greiner, and W. C. Ellis (authors' reply)—The remarks by Drs. Samans and Ham are certainly very interesting, in particular those pertaining to the close agreement between the theoretically calculated values for transition temperatures in chromium and the experimental values reported by a number of investigators. This is a remarkable achievement and we shall look forward to a more detailed presentation of the method followed in their calculations. We do not believe that the transition in pure chromium near 40 °C remains temperature invariant with alloying, as was reported by Samans and Ham for a number of the substances that they studied. We have not done any work with alloys but base our belief on the results of earlier studies in which less pure chromium was included and considerably lower transition temperatures were observed. The transition tempera-

Jan 1, 1952

By Carl F. Floe, Michael B. Bever

TRE solubility of hydrogen in molten copper-tin alloys is of both practical and theoretical interest. From a practical standpoint, data on the equilibrium solubility as a function of temperature, pressure and alloy composition are valuable for a better understanding of porosity problems in bronze castings. From the theoretical point of view the determination of the hydrogen-copper-tin equilibrium is of interest since it extends the laws governing the solution of gases in metals. This paper presents the results of an investigation of the solubility of hydrogen in representative compositions of the copper-tin system at temperatures ranging from above the liquidus to 1300°C. and at pressures from less than 50 mm. of mercury to about atmospheric. REVIEW OF PREVIOUS WORK The solubility of hydrogen in copper was determined by Sieverts and Krumbhaarl in 1910 and by Roentgen and Moeller2 in 1934. Their values are in fair agreement. In 1926 Iwasé3 reported results that were very much higher. The published data on the solubility of hydrogen in tin do not agree. Smithells4 states that no reliable data are available. According to Sieverts and Krumbhaar,5 hydrogen is insoluble in tin. Bircumshaw,6 on the other hand, found a definite solubility at 800°C. The latter's experimental procedure did not provide for stirring of the metal and in his opinion he failed to reach equilibrium. Iwasé3 again reported large solubility values. For copper alloys, Sieverts and Krumbhaar6 distinguished between alloying elements that do not markedly affect the solubility of hydrogen, elements that increase the solubility, and elements that reduce it. They named gold, tin, and aluminum as examples of this last group and reported hydrogen solubility data at 1225°C. for the copper-rich side of these alloy systems at atmospheric pressure. Without giving experimental results, they stated that the amount of hydrogen dissolved by liquid copper alloys is proportional to the square root of the pressure as in pure metals. These authors suggested that in a limited way the effect of an alloying element on the solubility of a gas is related to the constitution diagram for the alloy system. Sieverts7 also called attention to the fact that the curve of hydrogen solubility versus composition of copper-tin alloys shows a sharp change of direction at the composition of Cu3Sn and suggested that this compound persists at least to some extent in the molten state. Iwas3é reported large hydrogen solubility values for several compositions of copper- tin alloys, which appear to be in error.

Jan 1, 1944

By V. F. Leferrer

A new process for the treatment of silver crusts from desilverization of lead has been developed by Societe de Penarroya. The zinc contained in the crusts is recuperated by vacuum distillation at low temperature. The use of special retort crucibles is avoided. AT Noyelles-Godault the Parkes process (zinc addition to a silver-bearing lead melt) is used to desilverize lead bullion from the blast furnace. The crust which rises to the surface of the bath is removed and pressed by a well-known process in a press of the Howard type. The pressed crust, called zinc crust or silver crust, contains 10 pct Ag, 30 pct Zn, and 60 pct Pb. It is melted under a salt bed in a small, narrow, and deep kettle heated only in its upper part. A liquid concentrated alloy is obtained which is called T.A.C. in France (triple alliage concentr6) analyzing approximately 25 pct Ag, 65 pct Zn, 8 to 10 pct Pb, and 1 to 1.5 pct Cu. This T.A.C. is a real metallic alloy, completely deoxidized, and can be stored indefinitely. The process used at Noyelles-Godault consists in distilling this alloy in a tight furnace, under low vacuum and at low temperature, so that only the zinc distills and is condensed into liquid form. The residual silver-bearing lead is almost entirely free from zinc and oxidized dross. The vacuum dezincing equipment, see Figs. 1 and 2, consists of: 1) A furnace, constituted of a casing of steel plate lined with refractory bricks, heated internally by means of graphite resistors. The temperature of the furnace is measured by a thermocouple device and controlled by an automatic temperature regulator which acts upon the flow of the current passing through the resistors. Two doors, numbered 1 and 2 in Fig. 2, are provided for, one for charging the T.A.C., the other for tapping the high silver-bearing lead. 2) A condenser, and an ordinary room lined with good heat conductor refractory material. This condenser is provided with a graphite resistor which serves to bring to temperature when starting the furnace. A thermocouple records the temperature of the zinc melt and controls the temperature in the furnace, that is, the flow of current through the resistors, by means of the above mentioned regulator, so that the distillation rate in the furnace does not exceed that of the condensation. The condenser is connected to the vacuum pump by a filter. The whole equipment should, of course, be fluid-tight. The operation is carried out under a vacuum of about 10 mm Hg.

Jan 1, 1958

By N. A. Gokcen, M. N. Dastur

In metallurgical process industries a knowledge of true melting and casting temperatures is very essential for increasing the operating efficiency as well as improving the quality of the finished product. Optical pyrometers are widely used for the purpose because of their cheapness and ease of operation. It is an unfortunate fact, however, that this mode of measuring temperature entails a source of severe error inasmuch as with all non-black bodies, the temperature observed is always below the true temperature owing to deficient emissive power. Hence, the need for emissivity correction arises. In 1913 Bidwell1 obtained emissivity values of 0.36-0.48 for a temperature range of 1520-1800°C. He measured the true temperature of molten iron by sighting into a carbon cavity immersed in the iron under an atmosphere of hydrogen. In 1914 Burgess2 determined the emissivity of a smooth surface of liquid iron free from oxide to be 0.37 under an atmosphere of hydrogen. He claimed to have attained an accuracy of within 5°C at 1500°C with an optical pyrometer using monochromatic light. He reported that no difference appeared to exist between the emissivities of pure iron and of steels containing considerable percentages of carbon, nickel or manganese; nor was there any appreciable variation of emissivity with temperature from 1530 to 1571°C. Wensel and Roeser3 found an elnissivity value of 0.4 for temperatures above 1375°C for cast iron. The average emissivity value for carbon steels reported by Leiber,4 odd,5 Hase6 and Umino7 range from 0.4 to 0.45. Knowles and Sarjant8 made an extensive study of emissivity of molten iron and steel over a wide range of workshop and laboratory conditions. Observations of true temperature were made with immersion thermocouples, and correlated with apparent temperatures indicated by optical pyrorneter readings taken on the pouring stream as it passed over the lip of the crucible. The emissivity of Armco iron was shown to be of the order of 0.4, rising slightly with increasing temperature. But for plain carbon steels containing up to 1.0 pct carbon the emissivity was shown to fall slightly with increasing temperatures. The results of their investigation are in agreement with those of Guthmann.9 Naeser,10 Spencer," Todd5 and Hase6 in regard to the relation between emissivity and temperature for plain carbon steels. However, Goller12 has found a rise of emissivity with increasing temperature for the same steels. Results of several investigations are given in Fig 1. Measurement of True and Apparent Temperatures The necessity for an accurate optical temperature scale for liquid iron in studies of gas-metal equilibria led to this investigation. Experimental measurements were carried out in the induction furnace used by Dastur and Chipman13 in their studies of the reaction of hydrogen with oxygen in liquid iron. The furnace as modified for this work is shown in Fig 2. The atmosphere of the furnace was a mixture of purified argon with hydrogen containing a small controlled amount of water vapor. Gases were preheated by means of a platinum-10 pct rhodium resistance coil. The stream of hydrogen sweeping across the surface of niolten iron vir-

Jan 1, 1950

By William E. Brewster

Dating back some five years ago, various foundries made inquiries as to the probable total carbon content in a given specification and grade of pig iron. Up to that time we had no data, and except for a few occasional determinations of total carbon, no attempt had ever been made to set up routine determinations of total carbon. In fact, at that time, a cast analysis was considered sufficient, without examining at further length into possible variations of analysis between ladles of the same cast. In view of the various inquiries as to total carbon, we sampled all piles of all grades of pig iron, making complete analyses. Finding some variation in carbon content, we secured more samples and plotted the carbon content with respect to silicon in each grade of iron except for the higher phosphorus foundry iron, where it was necessary to divide the group into twenty-point phosphorus ranges. This is easily understood, owing to the falling off of carbon content with the increase in phosphorus content, silicon in each case being the same. In addition, these curves clearly demonstrate the lowering of the carbon content as the silicon is increased. In order to insure accuracy and reliable determinations the following method of sampling and analysis was employed: Two pigs selected from each end of the car, each car containing iron from one 50-ton ladle, are drilled with a 5/6-in. drill all the way through from top to bottom in the center of one section of the pig. The drillings are collected and transferred to an 80-mesh sieve; the portion passing through and the portion retained are placed in separate envelopes and labeled accordingly. The amount of sample in each envelope is weighed to obtain the proportionate amount of coarse and fine drillings, then a 1/2 factor weight of sample (1.3636 grams) made up of proportionate

Jan 1, 1936

By William E. Brewster

Dating back some five years ago, various foundries made inquiries as to the probable total carbon content in a given specification and grade of pig iron. Up to that time we had no data, and except for a few occasional determinations of total carbon, no attempt had ever been made to set up routine determinations of total carbon. In fact, at that time, a cast analysis was considered sufficient, without examining at further length into possible variations of analysis between ladles of the same cast. In view of the various inquiries as to total carbon, we sampled all piles of all grades of pig iron, making complete analyses. Finding some variation in carbon content, we secured more samples and plotted the carbon content with respect to silicon in each grade of iron except for the higher phosphorus foundry iron, where it was necessary to divide the group into twenty-point phosphorus ranges. This is easily understood, owing to the falling off of carbon content with the increase in phosphorus content, silicon in each case being the same. In addition, these curves clearly demonstrate the lowering of the carbon content as the silicon is increased. In order to insure accuracy and reliable determinations the following method of sampling and analysis was employed: Two pigs selected from each end of the car, each car containing iron from one 50-ton ladle, are drilled with a 5/6-in. drill all the way through from top to bottom in the center of one section of the pig. The drillings are collected and transferred to an 80-mesh sieve; the portion passing through and the portion retained are placed in separate envelopes and labeled accordingly. The amount of sample in each envelope is weighed to obtain the proportionate amount of coarse and fine drillings, then a 1/2 factor weight of sample (1.3636 grams) made up of proportionate

Jan 1, 1936

By R. G. Treuting

Germanium single crystals strained in tension at 600°C slip on the {Ill} plane and, macroscopically at least, in the <110> direction. Deformation is in homogeneous: various localized rotations are observed, as is a banding consistent with secondary slip banding. The structure after deformation is polygonized with a domain size of about 2x1O-3 cm. In relaxation tests, an incubation period prior to flow is observed, of duration inversely related to temperature and applied stress. Under continuous loading, there is a sharp first yield point. A critical resolved shear stress therefore must be cited with respect both to temperature and to rate of loading. At 600°C, when loading proceeds at 2900 psi per min, it is 1310 psi. The yield point phenomenon is suggestive of Cottrell&apos;s solute atom atmosphere theory and five points of qualitative agreement with this theory are found. PLASTICITY of germanium at elevated temperatures has been reported by Gallagher,&apos; who ascribed it to slip on {Ill) planes and described some associated effects. Preliminary experiments with single crystals of silicon and germanium loaded as simple beams confirmed {ill) as the slip plane of both materials.V his was demonstrated by the standard technique employing traces on two surfaces of known angle on a deformed crystal of known orientation.3 These experiments did not fix the slip direction, since more than one glide system operated. Uniaxial tensile straining is preferred for this purpose in order to restrict slip to one predominant system and to provide an unequivocal determination of the orientation change with respect to the stress axis. Experimental Method Specimens were diamond-sawed from germanium crystals containing about 5x10-5 wt pct Sb prepared by the zone-leveling process described by Pfann and Olsen;4 these specimens measured about 81/2 in. long, 0.20 in. wide, and were of various thicknesses from 0.035 to 0.060 in. Prior to testing, a specimen was coated over 1 in. or more of length at each end with Apiezon wax, chemically polished (in a solution of 15 ml HF, 25 ml HNO,, 15 ml CH3COOH, and 3 to 4 drops Br2), and dewaxed in warm xylene. A brief re-etching after scribing through a complete wax coating with vernier dividers provided gage marks at 0.200 in. intervals on the polished surface. A specimen with grips soft soldered to the ends was passed through the furnace tube and the grips pinned to the tensile machine in series with a stress gage. The Schopper testing machine is best described by reference to the illustration on p. 107 of Schmid and Boas5 and is operated with the pendulum arm locked, fixing the upper head. Load is applied through the screw-driven lower head, manually or by reduced speed motor. The furnace is 21/2 in. long surrounding a 4x7/16 in. ID quartz tube and was positioned about the specimen to permit free motion. The inert or reducing atmosphere required was sufficiently provided by a flow of helium introduced at the center of the furnace tube, with the tube ends loosely plugged with asbestos paper. Surface corrosion was slight. The stress gage employs a Be-Cu strip with SR-4 units incorporated in a simple bridge network with provision for balancing and calibrating. The bridge output on loading is fed through a Leeds and North-rup dc amplifier to a Speedomax 10 mv recorder, and calibration is obtained by dead loading. Experiments of two types have been conducted. Most have been in relaxation at constant elongation. One stress-strain curve has been taken with the machine continuously driven. Following extension of a specimen, Laue X-ray photographs were taken to obtain the orientation change between deformed and undeformed regions, recorded on a single film by translating the specimen in a plane normal to the beam between exposures. Sequences of such multiple exposures were made on some specimens to include the entire orientation range on one film. Slip Direction To obtain a maximum orientation change with a single slip system, crystals of very closely <110> axial orientation were used. The classic determination of slip direction rests on establishing that direc-

Jan 1, 1956

By B. M. Larsen, T. E. Brower

Introduction and Summary By "thermochemical factors" we refer to those variables which affect the net heat which must be put into the bath in order to make a heat of steel from any given set of charge materials. This is admittedly only one phase of the production rate problem. The whole problem includes also consideration of rate of charging, flame radiation intensity, rate of optimum fuel input obtainable without undue damage to the furnace structure and any variations in conditions such as stirring, slag volume or viscosity which affect the rate at which heat can flow down and away from those exposed surfaces where the heat is first received from the flame. Because a given type of charge in a shop is often considered as being nearly constant in both physical and chemical characteristics from one heat to another, and because such a state of affairs may be thought of as resulting in a reasonably constant net heat requirement, this requirement is usually neglected as an invariable, inevitable matter, about which nothing can be done. With normally variable charge, and variable percentages of limestone and cold pig, however, the net heat requirement can be subject to very appreciable change; it may also be affected by such things as the currently popular procedure of blowing oxygen into the bath. To bring the general problem of production rate into better perspective, therefore, it seems worthwhile to try to evaluate the net bath heat requirement and the amount by which it may change through variation in different factors. Because our calculated values of net heat are admittedly uncertain, we have tried to check them in part by statistical data on actual production rates over rather large groups of commercial heats. The results of calculation of net heat requirements in a wide range of actual commercial practices may first be summarized briefly. We find a wide range between the extremes of different practices, as would be expected, with duplex practice (essentially blown metal plus hot metal) having essentially a zero net heat requirement, an all-cold charge practice somewhat over I million Btu per ton of steel and a high hot metal practice about 0.75 million Btu per ton. Over the commercial range of scrap plus hot metal practice, increasing the percentage of hot metal from 40 to 78 pct, with other factors nearly constant, decreased the net heat by only some 5-10 pct. The net heat is increased by about 1.2 pct for each I pct of the metallic charge present as cold pig. Calculated values of oxygen supplied by air varied from about 25 up to 60 lb per ton of steel, and in a 60 pct hot metal practice, an increase from 32 to 52 Ib oxygen from air decreased the calculated net heat from 0.88 to 0.74 million Btu per ton. Use of pure cold oxygen to substitute for about one half of the total charge ore (about 28 Ib oxygen replacing 145 Ib ore per ton of steel) decreased the

Jan 1, 1949

By B. M. Larsen, T. E. Brower

Introduction and Summary By "thermochemical factors" we refer to those variables which affect the net heat which must be put into the bath in order to make a heat of steel from any given set of charge materials. This is admittedly only one phase of the production rate problem. The whole problem includes also consideration of rate of charging, flame radiation intensity, rate of optimum fuel input obtainable without undue damage to the furnace structure and any variations in conditions such as stirring, slag volume or viscosity which affect the rate at which heat can flow down and away from those exposed surfaces where the heat is first received from the flame. Because a given type of charge in a shop is often considered as being nearly constant in both physical and chemical characteristics from one heat to another, and because such a state of affairs may be thought of as resulting in a reasonably constant net heat requirement, this requirement is usually neglected as an invariable, inevitable matter, about which nothing can be done. With normally variable charge, and variable percentages of limestone and cold pig, however, the net heat requirement can be subject to very appreciable change; it may also be affected by such things as the currently popular procedure of blowing oxygen into the bath. To bring the general problem of production rate into better perspective, therefore, it seems worthwhile to try to evaluate the net bath heat requirement and the amount by which it may change through variation in different factors. Because our calculated values of net heat are admittedly uncertain, we have tried to check them in part by statistical data on actual production rates over rather large groups of commercial heats. The results of calculation of net heat requirements in a wide range of actual commercial practices may first be summarized briefly. We find a wide range between the extremes of different practices, as would be expected, with duplex practice (essentially blown metal plus hot metal) having essentially a zero net heat requirement, an all-cold charge practice somewhat over I million Btu per ton of steel and a high hot metal practice about 0.75 million Btu per ton. Over the commercial range of scrap plus hot metal practice, increasing the percentage of hot metal from 40 to 78 pct, with other factors nearly constant, decreased the net heat by only some 5-10 pct. The net heat is increased by about 1.2 pct for each I pct of the metallic charge present as cold pig. Calculated values of oxygen supplied by air varied from about 25 up to 60 lb per ton of steel, and in a 60 pct hot metal practice, an increase from 32 to 52 Ib oxygen from air decreased the calculated net heat from 0.88 to 0.74 million Btu per ton. Use of pure cold oxygen to substitute for about one half of the total charge ore (about 28 Ib oxygen replacing 145 Ib ore per ton of steel) decreased the

Jan 1, 1949

By B. M. Larsen, T. E. Brower

INTRODUCTION AND SUMMARY BY "thermochemical factors" we refer to those variables which affect the net heat which must be put into the bath in order to make a heat of steel from any given set of charge materials. This is admittedly only one phase of the production rate problem. The whole problem includes also consideration of rate of charging, flame radiation intensity, rate of optimum fuel input obtainable without undue damage to the furnace structure and any variations in conditions such as stirring, slag volume or viscosity which affect the rate at which heat can flow down and away from those exposed surfaces where the heat is first received from the flame. Because a given type of charge in a shop is often considered as being nearly constant in both physical and chemical characteristics from one heat to another, and because such a state of affairs may be thought of as resulting in a reasonably constant net heat requirement, this requirement is usually neglected as an invariable, inevitable matter, about which nothing can be done. With normally variable charge, and variable percentages of limestone and cold pig, however, the net heat requirement can be subject to very appreciable change; it may also be affected by such things as the currently popular procedure of blowing oxygen into the bath, To bring the general problem of production rate into better perspective, therefore, it seems worthwhile to try to evaluate the net bath heat requirement and the amount by which it may change through variation in different factors. Because our calculated values of net heat are admittedly uncertain, we have tried to check them in part by statistical data on actual production rates over rather large groups of commercial heats. The results of calculation of net heat requirements in a wide range of actual commercial practices may first be summarized briefly. We find a wide range between the extremes of different practices, as would be expected, with duplex practice (essentially blown metal plus hot metal) having essentially a zero net heat requirement, an all-cold charge practice somewhat over 1 million Btu per ton of steel and a high hot metal practice about 0.75 million Btu per ton. Over the commercial range of scrap plus hot metal practice, increasing the percentage of hot metal from 40 to 78 pct, with other factors nearly constant, decreased the net heat by only some 5-10 pct, The net heat is increased by about 1.2 pct for each I pct of the metallic charge present as cold pig. Calculated values of oxygen supplied by air varied from about 25 up to 60 lb per ton of steel, and in a 60 pct hot metal practice, an increase from 32 to 52 lb oxygen from air decreased the calculated net heat from 0.88 to 0.74 million Btu per ton. Use of pure cold oxygen to substitute for about one half of the total charge ore (about 28 lb oxygen replacing 145 lb ore per ton of steel) decreased the

Jan 1, 1948

By J. D. Bateman

At Giant Yellowknife, where high grade gold-bearing orebodies are highly irregular in shape, geology has been applied extensively to the mining of ore. The classical functions of the mine geologist in the fields of exploration and mine development have been extended to guide ore extraction, ensuring "clean" mining and effectively reducing waste dilution. THE property of Giant Yellowknife Gold M.ines Ltd. is situated west of Yellowknife Bay on the north shore of Great Slave Lake, a distance of 600 air miles north of Edmonton, Alberta. The Giant claims were staked in 1935, the company was formed in 1937, and the main orebody system was disclosed by diamond drilling in 1944 following a geological study of the property by A. S. Dadson,* Consulting Geologist for the company. Production began in 1948 at the rate of 200 tons per day and, during 1950, reached a daily rate of 425 tons. During the first 3 years of operation a total of 366,000 tons was milled with an average grade of 0.79 oz of gold per ton. Work is in progress with an expansion to 700 tons per day in view. A descriptive account of the geology and gold-bearing shear zone has appeared previously.* The rock formations in the vicinity of Yellowknife Bay have been subjected to protracted pre-Cambrian tectonic deformation culminating in a series of late faults having a cumulative horizontal displacement exceeding 11 miles. The Giant property is underlain by part of an Archean sequence, several miles thick, consisting of basic volcanic flows and minor intercalated tuffs. The volcanic succession forms the west limb of a major syncline, the flows facing east, but overturned on Giant property to dip west at 65" to 75". Orebodies are confined to shear zones up to 200 ft in width, which were formed along early thrust faults. The shear zones assume fold-like attitudes, the larger of which have an amplitude of several hundred feet. The rock formations beyond the limits of the zone of shearing do not reflect the simulated folds, the axes of which are within a few degrees of the strike of the flows. The schistosity and most of the planar elements in both the shear zones and the orebodies dip west • A. S. Dadson and J. D. Bateman: Structural Geology of Camdian Ore Deposits, Can. Inst. Min. Met. Jubilee Volume (1948), PP 273-283. at angles between 65" and 75", generally corresponding to the dip of the flows. The planar elements within the shear zone system thus dip more or less constantly west whether the shear zone is flat, vertical, or expressed as east or west dipping limbs. The shear zones reflect the deformation and alteration of the basic volcanic flows into chlorite schists which, in most places, have undergone metasomatic replacement to form chlorite-sericite-carbonate schists or sericite schists. The boundaries between the shear zones and country rock, although often gradational, usually can be defined within a few feet or even inches as they are expressed by the limits of metasomatic alteration. Orebodies may occupy a small or large proportion of the shear zone and, although they generally conform to the shape of the zone, their morphology is much more complex. Ore boundaries in some instances are sharp and can be delineated with a chalk line; but more generally, a large proportion of the ore boundaries is not visually obvious and can be determined only by the perception acquired by the geological mapping of ore or study of drill cores. Ore shoots in fold-like attitudes may transect the planar elements of the shear zone at any angle; yet the schistosity within the ore shoot may be coincident with that in the enclosing shear zone. Thus it is clear that problems may arise in the delineation of mining boundaries. Ore generally consists of 20 pct or more quartz with ferruginous carbonates in sericite schist deposited in two dominant stages. The earlier stage limits of quartz with carbonate, pyrite, and very fine-grained arsenopyrite in lenses and bands. The later stage consists of quartz-carbonate lodes, in

Jan 1, 1952

United Engineering Trustees, Inc. TAMES L HEAD, &apos;50 E C MEAOHER, &apos;52 R M ROOSEVELT, &apos;49 The Engineering Foundation F F COLCORD, &apos;50 E A PRENTIS, JR , &apos;48 R M ROOSEVELT, &apos;49

Jan 1, 1952

By A. M. Gaudin

This year the American Institute of Mining, Metallurgical and Petroleum Engineers has chosen to give me its Robert H. Richards Award, a distinction which is widely regarded as the highest honor in the field of mineral engineering. I am deeply moved by this tribute, which suggests not only regard for my service to the profession but also the affectionate esteem of my fellow mineral engineers. You have made me happy at the prospect of the permanent association of my name with that of Robert Hallowell Richards and of the distinguished recipients of the award, Arthur Fay Taggart, Frank R. Milliken, John F. Myers, Edward William Englemann, C. Harry Benedict, Edward W. Davis and Arthur W. Fahrenwald. I wish to thank you all for an honor so generously bestowed. Professor Richards is known to us all as a legendary figure, and we can read about him in the Richards Memorial Volume of our Transactions. Some of us have even had the good fortune of knowing him. I count myself among those lucky few. In its intangible attributes the Award recalls those things for which Professor Richards stood: for Science in Art, for thoroughness, for meticulous accuracy, for bold imaginativeness, most of all for professional integrity. Now, as in his day, these attributes are central to an engineer&apos;s creed. They are appropriately needed in a formulation of a definition of the mineral engineering profession.

Jan 6, 1957

By William Brewster

DATING back some five years ago, various foundries made inquiries as to the probable total carbon content in a given specification and grade of pig iron. Up to that time we had no data, and except for a few occasional determinations of total carbon, no attempt had ever been made to set up routine determinations of total carbon. In fact, at that time, a cast analysis was considered sufficient, without examining at further length into possible variations of analysis between ladles of the same cast. In view of the various inquiries as to total carbon, we sampled all piles of all grades of pig iron, making complete analyses. Finding some variation in carbon content, we secured more samples and plotted the carbon content with respect to silicon in each grade of iron except for the higher phosphorus foundry iron, where it was necessary to divide the group into twenty-point phosphorus ranges. This is easily understood, owing to the falling off of carbon content with the increase in phosphorus con-tent, silicon in each case being the same. In addition, these curves clearly demonstrate the lowering of the carbon content as the silicon is increased. In order to insure accuracy and reliable determinations the following method of sampling and analysis was employed: Two pigs selected from each end of the car, each car containing iron from one 50-ton ladle, are drilled with a 5/16-in. drill all the way through from top to bottom in the center of one section of the pig. The drillings are collected and transferred to an 80-mesh sieve; the portion passing through and the portion retained are placed in separate envelopes and labeled accordingly. The amount of sample in each envelope is weighed to obtain the proportionate amount of coarse and fine drillings, then a factor weight of sample (1.3636 grams) made up of proportionate

Jan 1, 1936

By Bailey Willis

It is proposed to present some of the results of observation of the geologists of the Appalachian division during the past seven years, and of experimental study during the past three years, on the subject of structural geology in the Appalachian Province. The article must be brief, even at the risk of obscurity; but a more complete and fully illustrated paper will appear in the Thirteenth Annual Report of the United States Geological Survey. Certain Facts. The following facts are first to be taken account of: From the Cambrian age to the Carboniferous there existed a conti nent stretching southeast from the present range of the Blue Ridge, covering what is now eastern Pennsylvania, New Jersey, eastern Vir ginia, North and South Carolina and eastern Georgia, with some un known part of the present Atlantic ocean-bed. Northwest from this continent lay a sea, reaching to the west and north of the Mississippi. Sedimentary deposits derived from the land accumulated with or ganic remains, in the sea; the greater part fell in a narrow zone along the shore, the remainder spread in a comparatively thin sheet over the bottom of the Mediterranean of North America. The resulting strata measure, near Mauch Chunk, Pa., 30,000 feet; over much of Pennsylvania, 20,000 to 25,000 feet; over eastern Tennessee, Georgia and Alabama, but 10,000 to 15,000 feet. The stratified mass, considered with reference to its broad physical char acters, consists of three members: A base of shale and sandstone ; a middle of limestone, 2500 to 6000 feet thick—a stratum probably not equalled in the world for uniformity of character and massive ness; and a top of shale and sandstone, 5000 to 23,000 feet thick. This mass has been folded. In a zone 900 miles long and 50 to 125 miles wide, the strata exhibit such attitudes and relations as could result only from a force of compression acting from north west or from southeast, or from both directions. Our problem is :

Jan 1, 1893

By J. J. Arps

This paper is a study of the effect of temperature on the electrical resistivity of sodium chloride solutions based on the published resistivity and density data in the International Critical Tables. This temperature effect is of considerable importance in quantitative interpretation of electric logs, where it is frequently necessary to correct mud resistivities measured under surface conditions to temperatures existing at the bottom of the bore hole. An empirical approximation formula was developed for this conversion which has proved to be very useful and seems to provide results well within the range of accuracy of the data involved. This approximation formula states: sistivities of sodium chloride solutions at temperatures of t and t degrees Fahrenheit, respectively. INTRODUCTION Research by various investigators during the past 20 years has clarified the physical principles of the phenomena which cause the natural or spontaneous electric potential in rotary drilled bore holes. The basic relationship which is most commonly used reads: in which the SP deflection, as measured from the shale base line, is expressed in millivolts. K is a constant, which appears to vary between 50 and 110; the low value applying to shaly sands, whereas the higher values are more common in carbonate rocks. A good average value for K = 70. for which value there is considerable theoretical justification." In order to calculate the resistivity of the connate water R and to estimate its "equivalent salinity" (as NaCl) from an electric log by means of this SP relationship from a knowledge of the static self potential and of the resistiv- ity of the mud filtrate R it is necessary to first correct the resistivity of the mud filtrate measured under surface conditions to the resistivity of this same mud filtrate in the well bore at a different temperature. In order to make this temperature conversion for the mud filtrate the variation of the electrical resistivity of sodium chloride solutions with temperature is commonly used. Since some discrepancies were found in the charts ordinarily used for this purpose, it was felt desirable to make a new study of this relationship based on the published measurement data. Because of the fundamental nature of these relationships and as an aid to other workers in this field, an attempt has been made in this study to show every step in the calculations. CONDUCTIVITY VS MOL CONCENTRATION The most complete published reference on the temperature relationship of sodium chloride solutions of different concentrations is provided in the International Critical Tables.&apos; The basic measurement data on the electrical conductivity of aqueous sodium chloride solutions, at different temperatures, as given in these tables, are reproduced in Table 1. The electrical conductivity values in this Table 1 are expressed as 10&apos; times the specific conductivity k in ohm-&apos;cm&apos;l per unit of concentration in milligram mols per liter of solution C, or: RESISTIVITY VS MOL CONCENTRATION These conductivity values from Table 1 were first converted to the corresponding electrical resistivity values (R) , expressed in ohm-meters, as is conven-

Jan 1, 1953

E. T. Dumble, Houston, Texas (communication to the Secretary) : During the field-season of 1890 I had occasion to examine some of the salines of eastern Texas. As the result of my stridy of them I came to the conclusion that, together with the oil of Hardin county (since extended to Beaumont by the work of Capt. Lucas) and the rock-salt and gypsum-deposits of the coast country, extending southward to the Rio Grande, these were simply a continuation of similar deposits in Louisiana described by Hilgard, Hopkins, and others; and I recommended the sinking of wells wberever they were found.

Jan 1, 1902

By E. C. Harder, D. F. Hewitt

Since early in 1916, when it became apparent that the steel industry of the United States could not depend for the duration of the war on several important foreign sources of manganese and might have to depend entirely on domestic ores, the U. S. Geological Survey, with the assistance of several cooperating organizations, has made a comprehensive investigation of domestic manganese resources. The work has included field studies in a number of states well as annual, quarterly, and monthly canvasses among operators concerning current and future production. In order that the interested public might have access to the important results of the studies, preliminary reports concerning the field work as well as periodic summaries of production were issued as promptly as possible. Although numerous summaries of production l2, l3, l4 have been prepared from time to time for the use of the several boards and committees responsible for the conduct of the war, it has been thought for some months that those engaged in the industry, as well as others, might be interested in a preliminary summary of the accumulated geologic and production data. The cessation of hostilities, in November, 1918, probably detracts from the usefulness of much of the material that is here presented, but apart from the historic interest in the performance of an important industry in war time, there is a possibility that some of the conclusions may be helpful to those who continue to exploit domestic deposits, as well as to those who wish to measure the country&apos;s independence in mineral supplies. Appropriate final geologic reports are being prepared by the geologists who did the field work. The present authors, having done but a small part of the recent field work, acknowledge with great appreciation the use of preliminary and unpublished reports and the cordial informal cooperation of the following geologists in the preparation of this paper: F. L. Ransome, G. W. Stose, F. C. Schrader, J. T. Pardee, E. L. Jones, Jr., H. D. Miser, Laurence LaForge, J. B. Umpleby, Arthur Keith, F. J. Katz, and E. S. Larsen, of the U. S. Geological Survey. Field work in Virginia was carried out in cooperation with the Virginia Geological Survey, T. L. Watson, State Geologist; in Georgia, with the Georgia

Jan 1, 1920

By J. W. Snavely

WITH all the advantages of handling bulk materials by means of belt conveyor also go some problems, one of the most persistent being that of cleaning. When sticky materials are being carried; the build-up of material on the return idler rolls results in difficulty of belt training. Much attention has been given to the problem of cleaning conveyor belts, and a great variety of cleaning devices have been developed. Even the best involve troublesome maintenance, and none can completely remove the fine particles imbedded in the belt cover, which cause rapid wear of the return idler rolls, and at the same time, of the belt cover as well. One of the major rubber companies has been promoting a two-way belt system, in which the conveyor belt is given two successive 90" twists at each end to enable it to carry material in both directions simultaneously. For many years the flat belt transmission industry has installed quarter-turn and half-turn twists in countless numbers of instances. While quarter-turn and half-turn twists in transmission belts is a familiar application, the 180" twist apparently has never been previously attempted with a conveyor belt. About a year ago, two officials of the National Iron Co. of Duluth, Lester and Lewis Erickson, proposed twisting the return run of a conveyor belt on an installation that they were designing for one of the major iron ore producers. Since then the soundness of the idea has been demonstrated, both in theory and by practical test, with the result that the installation of two conveyor belts involving the twisting of the return run is now under way. These two installations are designed to have the return run of the conveyor belt twisted 180" as it leaves the snub pulley at the head drive. The clean underside of the belt is thus placed against the idlers on the return run as well as on the carrying run. Just before it enters the tail pulley, the belt will be twisted an additional 180°, restoring it to its normal position. Because this twisting of the return run of a conveyor belt is a radical departure from accepted practice, an elaborate and extensive test was conducted early in 1950 to demonstrate that this twisting of the return run could be done successfully, also to establish application data for accomplishing this twisting, and to determine if any special equipment would be required. In studying this concept of twisting the return run of a conveyor belt, a number of problems need to be solved, primarily the ones brought about by deliberately introducing an unequal distribution of stress across the conveyor belt and controlling that maldistribution of stress, while confining it to the return run portion. The tension conditions existing in the return run of a conveyor belt are clear to all designers. First, the return run carries the initial or slack side tension of the conveyor belt, the tension that must be supplied to the return run to provide proper frictional contact between the belt and the driving pulley so that the necessary power can be transmitted from the driving pulley to the belt without slippage. This slack side tension is supplied to the belt by means of takeups, either of the gravity type, which can be vertical or horizontal, or by means of the screw type. With inclined or declined belt conveyors the slope tension also must be considered, which is the tension imposed by the weight of the belt hanging from the top pulley. This slope tension frequently can furnish part or even all of the initial tension required. The maximum value of the slope tension will be at the top pulley, and it decreases in direct proportion to the length. In addition to the foregoing, it frequently is desirable to impose arbitrarily additional slack side tension to provide sufficient tension at the loading point at the tail, so that the belt will adequately support its load between the carrying idlers. Design Conditions for Twisting A number of design conditions exist, which must be satisfied successfully to accomplish the twisting of the return run without exceeding normal working limits in any portion of the conveyor belt. It is obvious that the belt edge, in its relation to the center of the belt, must stretch in making a twist, because as the twist is accomplished, the belt edge travels through a longer path than does the center of the belt. It is further obvious that if the edge of the belt is stretched, a redistribution of stress in the belt is required to allow this edge stretching. Moreover, this stress will be unequal across the width of the belt, having a maximum value at the edges, with a minimum value at the- center of the belt. With correct initial tension in the return run of a conveyor belt, the existing slack side tension will be unequally distributed when a twist is introduced. A condition then exists in which the edge stresses,

Jan 1, 1952

By E. P: Mathewson

Discussion of the paper of E. P: Mathewson, presented at the Butte Meeting, August, 1913, and printed in Bulletin No. 78, June, 1913, pp. 1033 to 1037. PROF. JOSEPH W. RICHARDS, South Bethlehem, Pa. :-Speaking to the question of the development of the basic lining, and speaking from a somewhat considerable study of the history of the process, ,I think Mr. Mathewson&apos;s conclusion (in the last paragraph. of his paper) is perfectly justified and is very fairly stated. Messrs. Smith and Pierce worked at developing their process for many years ; copper men had been trying their level best to get away from the silica lining of the converters and had uniformly failed. On one page of Mr. Mathewson&apos;s paper we read that at the old works of the Anaconda Company, at Anaconda, the experiments " were abandoned on the score of cost and lack of advantages." On the next page, after describing the work of Messrs. Smith and Pierce, we have the statement that the Anaconda Company lined a shell with mangnesite brick and the ?results were excellent." I think Mr. Mathewson&apos;s statement that to Smith and Pierce belongs the credit of developing a long-discredited idea, is correct. C. D,. DEMOND, Anaconda, Mont. :-It seems to me that the matter of the lining is important; my impression is that they used tar in their basic lining and that did not seem to be at all successful at Anaconda, but silicate of soda was very successful. MR. RICHARDS :-I did not know that they- had abandoned the use of tar. MR. DEMOND :-I said I thought that was the practice. At Anaconda that was not at all satisfactory in the basic linings. Silicate of soda was very satisfactory and is so.

Jan 11, 1913