By P. R. Celmer, Leonard R. Weisberg

THE principle of fractional crystallization has been successfully used to prepare high-purity (99.999 pct) Ga. Hoffman and Scribnerl removed single crystals of gallium solidifying in a gallium melt, while Zimmerman2 grew single crystals from the melt by the Kyropolous technique. In contrast, attempts at purifying gallium by zone refining have been less successful. ichards, reported that despite the passage of 40 zones through a gallium ingot, there still remained 5 to 70 ppm each of Cu, Fe, Ca, Mg, Si, Al, and Ag. Previously, Detwiler and Fox4 detected only one impurity, Pb, segregating in zone-refined ingots. These surprising results prompted an investigation of the factors controlling impurity segregation in gallium. Possible reasons for this were insufficient diffusion of impurities in the melt; recontamination of the melt by its oxide film which is not affected by the passage of the zone; reaction of gallium with the boat; sudden freezing of gallium following supercooling, especially since gallium easily supercools to and trapping of impurities at grain boundaries. Impurity segregation tests were carried out by directionally freezing gallium using the Bridgman rnethd, modified in that the molten gallium is lowered out of a furnace into a slush of dry ice and trichloroethylene, thus minimizing supercooling. Since the gallium is contained vertically, the oxide film is in contact only with the tail end of the melt. It was found that Teflon makes an excellent crucible for gallium since it is quite pure, non-reactive, translucent, flexible, machinable, and is not wet by gallium. The gallium crystals could be grown at various speeds, and the melt could be vigorously stirred by a Teflon rod moving through the gallium in a vertical reciprocating fashion. Single crystals could be grown by placing a solid Teflon plug at the bottom of the melt drilled out in such a way to cause the solidifying gallium to follow a winding path. Thus, even if many crystals are originally nucleated, only one grain will predominate. The grain structure of the gallium crystals was revealed by an etchant composed of equal volumes of HC1, HNO3 and HF, diluted with water to half strength. Emission spectrographic analyses were carried out on samples removed from the front and tail ends of the resulting gallium ingots. Typical results of this study are summarized in Table I. The rate of freezing in all three cases was about 1 in. per hr. It can be seen that even though stirring of the melt does help, it is even more important to grow a single crystal of Ga in order to obtain good segregation of impurities. The effect of crys-tallinity on the segregation of impurities was previously observed6 in the directional freezing of germanium; however, in this case, the effect was much less pronounced. This dependence of impurity segregation on the crystalline perfection of Ga may be related to its thermal conductivity which is the most anisotropic of all metals.7 The anisotropic thermal conductivity can cause the solid-liquid interface to be nonuniform, thus leading to trapping of impurities during freeing, and therefore reduced segregation. In conclusion, it is indicated that zone refining of gallium would be more successful if seeding and similar precautions are taken to insure single crystal growth. The authors are indebted to Mr. H. H. Whitaker for the spectrographic analyses and to Drs. B. Abeles and F. D. Rosi for helpful advice and encouragement throughout the course of this work. This research was supported by the Electronics Research Directorate, Air Research and Development Command, under Contract No. AF33(616)-5029. REFERENCES 'J. 1. IToffmon and B. T. Scribrer: I. Research h'atl. Bur. Standards, 1935, "01. 15, p. 205. 'W. Zirnmerman: Science, 1954, vol. 119, p. 41. %J. L. Richards: Nature, 1956, vol. 117, p. 182. 'D. P. Detwiler and W. M. Fox: I. Metals, 1955, "01. 7, p. 205. 5P. W. Bridgman, Proc. Am. ilcod. Sci., 1925, vul. 60, pp. 305,385,423. "S. L1. Christian: private c ommuni cation. 'K. W. Powell: roy. Sac., 1951, vol. 209, p. 525. 'W. G. Pfann: Zone Re fining, p. 20. John Wiley and Sons, Inc., New York, L058.

Jan 1, 1962

By Robert H. Richards

This is in part a review paper, indicating the various steps that have been taken in developing hindered-settling apparatus, some of the standard data that have been obtained, and some of the conclusions one is led to as to the effect of it in improving concentrating-methods and machinery, and in part it brings in some unpublished work. Causes oF Loss in ORe-ConcEntration. In making a study of the separation of valuable minerals from the waste gangue, particularly by water concentrators, it is necessary to define, first of all, what are the causes of loss that are likely to interfere with the concentration. Having made this definition, we can then study to see in what may the machines make their losses, and plan remedies for them in an intelligent way. Losses may be stated to occur as included grains, as flat or long grains, as fine free mineral, and as absolute slime. We will take these up one by one, as follows: Included Grains.—Fig. 1 shows by a set of diagrams how included grains may occur : first, where the heavy mineral grains attached to the quartz are of large size; secondly, where they are of small size; and thirdly, where very fine particles of heavy mineral are included in the quartz. We have to decide in regard to included grains whether they are rich enough to go direct to the furnace, or poor enough to throw away, or whether they lie between these two points and require recrush-ing as the only means of severing the values from the waste. This last case is the orlly one requiring special treatment at our hands. We will therefore consider that next.

Jan 1, 1911

By C. W. Beattie, R. L. Solter

ALUMINUM-KILLED, low carbon steel sheets are used extensively for severe deep drawing and other difficult forming operations. They usually, but not always, have a characteristic grain structure in which the grains are elongated both in the lengthwise and in the transverse direction. As described by Burns and McCabe,&apos; a typical grain in the plane of the sheet has its two axes in that plane from 1 Y2 to 4 times as long as the axis normal to the plane of the sheet. Rickett, Kalin, and MacKenzieZ have also reported on the recrystallization behavior of such steel. The contrast in grain structures of fully processed sheets of aluminum-killed and rimmed steel is illustrated by Figs. 1 and 2. The elongated grain structure of the aluminum-killed sheet is not developed on all heats or lots of this metal, and studies of the factors controlling and influencing its formation are reported in this paper. Jeffries and Archerb tate that unstrained grains are normally equiaxed, but exceptions are common. For example, if a metal containing a material mechanically obstructing grain growth is subjected to considerable working followed by thorough annealing, it may exhibit grains consistently elongated in the direction of working. Our experiments demonstrate that aluminum-killed, low carbon steel is such a metal, and that the substance mechanically obstructing grain growth is aluminum nitride. The effectiveness of aluminum nitride in inhibiting grain growth has been found to be influenced by the degree of cold reduction, the rate of heating in annealing, the thermal history of the sample before cold reduction, and the residual aluminum content. A correlation between grain shape and austenitic grain coarsening temperature also was indicated and additional experiments demonstrated that aluminum nitride is also the principal cause for the fine grain characteristic of aluminum-killed steels. Manufacture In conventional practice, aluminum-killed sheet steel is manufactured from a low carbon steel containing approximately 0.02 to 0.07 pct residual (HC1 soluble) Al. With the exception of certain samples containing greater or lesser amounts of aluminum, the steels used in these investigations were within the following composition range: C, 0.03 to 0.06 pct; Mn, 0.28 to 0.38; S, 0.017 to 0.032; Al, 0.03 to 0.06; P, <0.01; and Si, <0.01. Properly heated ingots are rolled to slabs about 4 in. thick. After surface conditioning, the slabs are reheated to about 2300°F and hot rolled continuouslv to strip about 1/10 in. thick. The strip rolling is completed at a temperature of 1550°F or higher, and the strip is coiled, usually at a temperature near the lower critical transformation. After cooling, the strip is pickled to remove oxide, cold reduced 40 to 70 pet to final thickness, then annealed to 1250° to 1350°F in 20 to 80 ton charges, the size of which results in slow heating and cooling rates. Effect of Cold Reduction According to Sachs and Van Horn,&apos; the deformations of the individual grains in rolling are similar to those of the total volume. Thus individual grains would elongate in rolling according to the amount of cold reduction imposed. This is true theoretically, but as cold reduction increases the individual grains tend to fragment, and measured grain elongations become less than theoretical. The amount of grain elongation may be described by a numerical rating based on grain counts made by the intercept method. Specimens are polished normal to the plane of the sheet, with the polished surface extending parallel to the rolling direction. After etching, grain intercepts are counted along a 50 mm line on a micrograph of suitable magnification. In random locations parallel to the plane of the sample 20 counts are made and 20 are made in the thickness direction of the sample the average count in the thickness direction divided by the average count parallel to the plane of the sample gives a numerical rating of the grain shape called grain elongation. For example, a grain elongation of 2.00 means that the average grain is twice as long as it is thick. The average of both counts may be converted to grains per sq mm by a nomograph relating intercept counts and grain count. By the same procedure the grain elongation in the plane of the sheet but transverse to the rolling direction may be determined, using transverse metallographic samples. A comparison of theoretical and measured grain elongation was obtained on an aluminum-killed

Jan 1, 1952

By Walter Crafts, C. M. Offenhauer

IN the course of study of the heat-treatment of low-alloy steels, the behavior of alloy carbides at subcritical temperatures was found to vary from that indicated by published investigations. In order to establish the ranges of formation of carbides in low-chromium steels, a series of steels containing up to 0.60 per cent carbon and 7.5 per cent chromium has been investigated with respect to the type of carbide formed after quenching and tempering at sub-critical temperatures. The types of carbide formed as products of austenite transformation to pearlitic and pseudomartensitic structures have also been determined. There have been numerous investigations of the carbides in chromium steels and diagrams of the iron-chromium-carbon system.&apos; Westgren, Phragrnén and Ne-gresco2 identified the following carbides in chromium steels: Cementitc............ Fe3C (containing up to about 15 per cent Cr) Trigonal carbide...... Cr7C3 (containing up to about 55 per cent Fe) Cubic carbide........ Cr4C (or Cr23C6) (con- . taining up to about 25 per cent Fe) Orthorhombic carbide , cr3c2 (containing only a few per cent Fe) The most complete information on the iron-chromium-carbon system was supplied by Tofaute, Sponheuer and Bennek3 and by Tofaute, Küttner and Büttinghaus,4 By means of dilatometric and microscopic stzdies, sections of the diagram were established. This diagram showed the presence of the special carbide CI7C3 in steels containing about 2.5 per cent to 12 per cent chromium in low-carbon steels and from about 5 to 20 per cent chromium in I per cent carbon alloys from A1 to room temperature. The present investigation has shown that a carbide inversion from Fe3C to Cr7C3 occurs in chromium steels containing more than about I per cent chromium after hardening and tempering at subcritical temperatures above about 500°C. The type of carbide observed to be more stable in quenched and tempered specimens was also found to be produced by direct austenite transformation in corresponding ranges of temperature and composition. Experimental Procedure The steels used in these experiments were made in magnesia-lined crucibles in high-frequency furnaces and were poured into 2-in. ingots. The ingots were forged into I-in. round bars, and all heat-treatments were conducted on specimens of this section size. Sections of the bar stock 8 in. long were hardened in air, oil or water, depending on the composition, after heating to a temperature sufficiently high to dissolve the carbides. The low-carbon and low-chromium steels were not entirely martensitic after quenching, and contained some ferrite and pseudomartensite. No pearlite was observed in the microstructures after quenching. The quenched bars were cut into

Jan 1, 1942

By Walter Crafts, C. M. Offenhauer

IN the course of study of the heat-treatment of low-alloy steels, the behavior of alloy carbides at subcritical temperatures was found to vary from that indicated by published investigations. In order to establish the ranges of formation of carbides in low-chromium steels, a series of steels containing up to 0.60 per cent carbon and 7.5 per cent chromium has been investigated with respect to the type of carbide formed after quenching and tempering at sub-critical temperatures. The types of carbide formed as products of austenite transformation to pearlitic and pseudomartensitic structures have also been determined. There have been numerous investigations of the carbides in chromium steels and diagrams of the iron-chromium-carbon system.&apos; Westgren, Phragrnén and Ne-gresco2 identified the following carbides in chromium steels: Cementitc............ Fe3C (containing up to about 15 per cent Cr) Trigonal carbide...... Cr7C3 (containing up to about 55 per cent Fe) Cubic carbide........ Cr4C (or Cr23C6) (con- . taining up to about 25 per cent Fe) Orthorhombic carbide , cr3c2 (containing only a few per cent Fe) The most complete information on the iron-chromium-carbon system was supplied by Tofaute, Sponheuer and Bennek3 and by Tofaute, Küttner and Büttinghaus,4 By means of dilatometric and microscopic stzdies, sections of the diagram were established. This diagram showed the presence of the special carbide CI7C3 in steels containing about 2.5 per cent to 12 per cent chromium in low-carbon steels and from about 5 to 20 per cent chromium in I per cent carbon alloys from A1 to room temperature. The present investigation has shown that a carbide inversion from Fe3C to Cr7C3 occurs in chromium steels containing more than about I per cent chromium after hardening and tempering at subcritical temperatures above about 500°C. The type of carbide observed to be more stable in quenched and tempered specimens was also found to be produced by direct austenite transformation in corresponding ranges of temperature and composition. Experimental Procedure The steels used in these experiments were made in magnesia-lined crucibles in high-frequency furnaces and were poured into 2-in. ingots. The ingots were forged into I-in. round bars, and all heat-treatments were conducted on specimens of this section size. Sections of the bar stock 8 in. long were hardened in air, oil or water, depending on the composition, after heating to a temperature sufficiently high to dissolve the carbides. The low-carbon and low-chromium steels were not entirely martensitic after quenching, and contained some ferrite and pseudomartensite. No pearlite was observed in the microstructures after quenching. The quenched bars were cut into

Jan 1, 1942

By Walter Crafts, C. M. Offenhauer

IN the course of study of the heat-treatment of low-alloy steels, the behavior of alloy carbides at subcritical temperatures was found to vary from that indicated by published investigations. In order to establish the ranges of formation of carbides in low-chromium steels, a series of steels containing up to 0.60 per cent carbon and 7.5 per cent chromium has been investigated with respect to the type of carbide formed after quenching and tempering at subcritical temperatures. The types of carbide formed as products of austenite transformation to pearlitic and pseudomartensitic structures have also been determined. There have been numerous investigations of the carbides in chromium steels and diagrams of the iron-chromium-carbon system.1 Westgren, Phragmén and Negresco2 identified the following carbides in chromium steels: [Cementite Fe3C (containing up to about 15 per cent Cr) Trigonal carbide Cr7C3 (containing up to about 55 per cent Fe) Cubic carbide Cr4C (or Cr23C3) (containing up to about 25 per cent Fe) Orthorhombic carbide . Cr3C2 (containing only a few per cent Fe)] The most complete information on the iron-chromium-carbon system was supplied by Tofaute, Sponheuer and Bennek3 and by Tofaute, Küttner and Büttinghaus.4 By means of dilatometric and microscopic studies, sections of the diagram were established. This diagram showed the presence of the special carbide Cr7Ca in steels containing about 2.5 per cent to 12 per cent chromium in low-carbon steels and from about 5 to 20 per cent chromium in r per cent carbon alloys from A1 to room temperature. The present investigation has shown that a carbide inversion from Fe3C to Cr7Ca occurs in chromium steels containing more than about 1 per cent chromium after hardening and tempering at subcritical temperatures above about 500°C. The type of carbide observed to be more stable in quenched and tempered specimens was also found to be produced by direct austenite transformation in corresponding ranges of temperature and composition. EXPERIMENTAL PROCEDURE The steels used in these experiments were made in magnesia-lined crucibles in high-frequency furnaces and were poured into 2-in. ingots. The ingots were forged into 1-in. round bars, and all heat-treatments were conducted on specimens of this section .size. Sections of the bar stock 8 in. long were hardened in air, oil or water depending on the composition, after heating to a temperature sufficiently high to dissolve the carbides. The low-carbon and low-chromium steels were not entirely martensitic after quenching, and contained some ferrite and pseudomartensite. No pearlite was observed in the microstructures after auenchine. The quenched bars were cut into

Jan 1, 1942

Meeting, of Jan. 22, 1915.-Dr. Albert R. Ledoux was unanimously nominated-by the Board as one of the representatives of this Institute upon the Engineering Foundation Board. The following Tellers to count the votes for officers and directors on Feb. 16, 1915, were appointed: David H. Browne; Arthur S. Dwight, and Bradley Stoughton; and the following Tellers to count the ballots, on the amendments to the Constitution: Arthur L. Walker, Max Roesler, and Burr A. Robinson. Karl Eilers was appointed a member of the Library Board of the United, Engineering Society, representing this Institute in place of C. R. Corning, ;resigned. The Pick and Hammer Club of the University of Oklahoma was established as an Affiliated Student Society. The sum of $150 was appropriated to the Columbia Local Section. The sum of $29.50 was appropriated to the Chicago Local Section.

Jan 3, 1915

By Thomas M. Drown, P. W. Shimer

THE precipitation of phosphoric with titanic acid, by boiling an iron solution which had been reduced to the ferrous condition by sulphuretted hydrogen or sulphurous acid, was first noticed by E. H. Bogardus in 1874.* Since that time, as far as we are aware, not much has been published on the relation- of these two acids to each other, and to silicic acid, in the ordinary course of analysis of iron ores. The following investigation may perhaps aid in clearing up some of the obscure points in the analysis of titaniferous ores. THE DETERMINATION OP PHOSPHORUS. From two to five grams of the finely powdered ore are weighed into a beaker and treated with about 50 c.c. of hydrochloric acid (sp. gr. 1.12), evaporated to dryness, and heated in an air-bath for * American Journal of Science, III, 8, p. 334.

Jan 1, 1882

By P. N. Richards, M. K. Ormay

The present Paper extends the previous work on cold reduced, low carbon steels to preferred orientations developed after various heat treatments. In recrystal-lized rimmed steel, cube-on-comer orientations increased with cold reductions up to 80 pct. Above that {111}<112> and a partial fiber texture with (1,6,11) in the rolling direction dominated. During grain growth, cube-on-corner orientations have been observed to grow at the expense of {210}<00l>. In re-crystallized Si-Fe (111) (112) and cube-on-edge type orientations are dominant near the surface and the (1,6,11) texture near the midplane for reductions up to 60 pct. With larger reductions {111)}<112> and the (1,6,11) texture are dominant. In cross rolled capped steel a relationship of 30 deg rotation was observed between the (100)[011] of the rolling texture and the main orientations after re crystallization. Most orientations present in recrystallized specimens can be related to components of the rolling texture by one of the following rotations: a) 25 to 35 deg about a (110) b) 55 deg about a (110) C) 30 deg about a (Ill) THE orientation texture of recrystallized steel is of interest where the product is to be deep drawn, because preferred orientation is related to anisotropy of mechanical properties such as the plastic strain ratio (r value);1,2 and in electrical steel applications where a high concentration of [loo] directions in the plane of the sheet improves the magnetic properties of the material. It is interesting to note that both these aims are to a large extent achieved commercially, even though the orientation texture of cold rolled steel does not show large variation3 and the recrystallized orientations are generally given as being related to the as rolled orientations mostly by 25 to 35 deg rotations about common (110) directions.4-6 There is, as yet, no single completely accepted theory on recrystallization. The three mechanisms that have been investigated and discussed are: a) Oriented growth b) Oriented nucleation c) Oriented nucleation, selective growth Largely from the observations of the recrystalliza-tion process by means of the electron microscope,7-11 there is now considerable evidence that the "nucleus" of the recrystallized grain is produced by the coalescence of a few subgrains to form a larger composite subgrain, which finally grows by high angle boundary migration into the deformed matrix. From the intensive work on the recrystallization of rolled single crystals of iron, Fe-A1 and Fe-Si al-loys4-" he following observations have been made: 1) The change in orientation during primary recrys-tallization can usually be described as a rotation of 25 to 36 deg about one of the (110) directions. 2) The (110) axes of rotation often coincide with poles of active (110) slip planes. 3) If several orientations are present in the cold rolled structure, the (110) axis of rotation will preferably be a (110) direction that is common to two or more of the orientations. 4) With larger amounts of cold reduction (70 pct or more) departure from these observations became more frequent. 5) After larger cold reductions, rotations on re-crystallization about (111) and (100) directions have been observed. K. Detert12 infers that a rotation relationship of 55 deg about (110) directions is also possible, by stating that the recrystallized orientation {111}<112> can form from the orientation {100}<011> of cold reduced partial fiber texture A.3 The observation by Michalak and schoone13 that (lll)[l10] formed during recrys-tallization in fully killed steel containing (111)[112],— as well as (001)[ 110] which is related to the {111}<011> by a 55 deg rotation about <110>-implies a possible 30 deg rotation relationship about the common [Ill]. Heyer, McCabe, and Elias14 have recrystallized rimmed steel after various amounts of cold reduction, by a rapid and by a slow heating cycle and found that the preferred orientations strengthened with increased cold reduction. The most pronounced orientation up to about 70 pct cold reduction was found to be {1 11}< 110>, after 80 pct cold reduction both {111}<110> and {111}<112>, after 85 and 90 pct cold reduction, {111}<112>, and after 97.5 pct cold reduction it was {111}<112> and (100)(012). In the present work, the orientation textures of the recrystallized specimens are examined under various conditions of steel composition, amount and method of cold reduction, and method of recrystallization. The relationships between the preferred orientations of the as rolled and recrystallized specimens, and the conditions for the formation of the various orientations during recrystallization are investigated.

Jan 1, 1970

By Arthur Tauber, Horst Kedesdy

FERRITES are sintered metallic oxides of the spinel structure type1 and belong to the class of soft ferromagnetic materials. Similar to a ceramic, they can be formed and fired to a dense body, exhibiting a high electrical volume resistivity ranging from 102 to 102 ohm-cm as compared with 10-6 ohmcm for some of the metallic magnetic materials. This high resistivity, with resulting low eddy current losses, finds special application at high frequencies. The dispersive susceptibility of ferrites at microwave frequencies has also led to many applications in this field. Where high resistivity with high permeability is desirable, ferrites are used in low frequency applications. During the last few years ferrites exhibiting rectangular hysteresis loops have been developed for computer and magnetic memory systems. The general formula for ferrites is MeFe2O4 where Me is a divalent metal ion such as Ni, Zn, Mg, Mn, Cu, Cd, and Fe. Only two of these ferrites are nonferromagnetic, namely, those with Zn and Cd. Solid solutions can be formed between different ferrites, and it is of interest to note that solid solutions of a ferromagnetic ferrite with a nonferromagnetic ferrite yield much better magnetic materials than the basic ferrite body. In general, it can be said that the solid solution formation between ferrites has widened the field of ferrite synthesis and has led to methods of preparing materials with a large variety of magnetic properties.

Jan 7, 1957

By Martin F. Milligan

THIS short discussion of the effects of deoxidation on the mechanical properties of cast steels is intended to serve as general introduction to the subject of this afternoon&apos;s session. The subject is covered in detail in Mr. Carter&apos;s excellent paper. My material has been collected from the works of various investigators, several of whom are present today. For a definition of deoxidation, as applied to steel-furnace melting practice, we can best go to Briggs&apos; book, "The Metallurgy of Steel Castings." Briggs says that deoxidation "includes all the phenomena in the final preparation of steel that would permit it to solidify free from gas cavities and from dissolved oxygen of all kinds." Various practices are used by welters to produce these end results.

Jan 1, 1947

By C. C. Harris

A critical literature review leads to a descriptive model of tumbling mill operation based upon energy partition concepts and the necessary requirements for particle fracture. As grinding proceeds into the ultra-fine region, conditions which are of little significance during normal operations gradually become controlling. These involve increasing resistance to fracture and an increasing tendency to aggregate as particles become smaller, and a growing fraction of the power input being consumed fruitlessly. The result is that fineness asymptotes to a maximum value as comminution proceeds indefinitely; thus where t is time, p and n are experimentally determined parameters, and Ø is a measure of fineness, which is presumed to be proportional to specific surface area, or proportional to the reciprocal of the size modulus (provided that the distribution modulus remains constant with time), or both. Ø, is the asymptotic value of Ø and is a measure of the grind limit. A method for its graphical determination is given. In a previous paper1 the physical and mathematical principles requisite to a study of the role of energy in comminution were reviewed. The micro-process of comminution — or the comminution event — can be investigated in terms of (a) the magnitude of the force-field localized around the individual particles which gives rise to the stresses generated in the particles, which in turn induces their fracture, and (b) the distribution of fragment sizes, should the event prove fruitful. The entire fragmentation operation can be considered to be the totality of its individual events, and in order to obtain a single independent variable of the process it is necessary to transform and sum the local stresses in terms of energy.1 This energy, however, will account for only a fraction of the energy input to the comminution process, the actual magnitude depending upon the kind of mill and several related factors. From the comminution viewpoint the primary function of a mill is that of stressing as many as possible of the individual particles of the charge to failure, with the maximum economy of energy expenditure. This is difficult indeed to achieve, for stressing a particle does not always break it, while the overwhelming portion of the energy input is involved with various internal mill processes which — almost incidentally — determine the magnitude, frequency, and manner in which the forces are applied to the particles. Essentially, these processes depend upon the mill dimensions, loading and speed, and they may be little affected whether fracture occurs or not. These processes must be delineated if a complete description of the role of energy in comminution is to be given; the energy account sheet1 (Fig. 1) in showing how the energy is partitioned for the requirements of the several functions it performs, provides a framework for the development of a model of the comminution process. Actual numerical values for the variables appearing in Fig. 1 will depend upon the mill, materials, and operating conditions. A possible general relationship between the variables will be suggested in this paper. Before proceeding further, a cautionary note must be issued. It was pointed out in an earlier paper&apos; that while energy input is not changed by increasing the power and decreasing the time in the same proportion, and vice versa, the results of the process in terms of particle fineness may be different. Thus, although energy is chosen as the independent variable of a comminution process, it is not absolutely independent, and care must be exercised to ensure that it is used within its range of valid application. Time has the necessary independence, and it will be used in place of energy where it is appropriate. The residence time in a mill is usually of the order of minutes. Under these conditions the particles are subjected to "... a relatively constant fracture producing environment".2 However, under the more rigorous conditions of greatly extended time, which pertain in ultra-fine grinding, indications are that the fracture producing environment no longer remains constant; this is the major subject of this paper. At this extreme limit the mill is probably taxed to its utmost, and at the same time the bulk material properties are becoming closer to ideal, while the physico chemical effects associated with surfaces, edges and corners are multiplying. (The edge length per unit volume is proportional to the square of the specific

Jan 1, 1968

By M. G. Nicholas

The influence of deformation, relative movement and surface cleanliness on the strength of room -temperature "interparticle" bonds between copper surfaces has been studied. No bonding resulted when clean surfaces were merely pressed together, even under pressures of 50,000 psi. Bonding resulted, however, when clean surfaces were simultaneously pressed and moved relative to each other, some bonding occurring no matter how small the pressure or relative movement. Exposure of the clean surfaces to various chemicals inhibited bonding, none at all being produced by small relative movements. The size of the movements which first produce bonding between exposed surfaces depends on the nature of the chemical, being less than 0.002 in. for cleansing reagents and greater than 0.004 in. for lubricants, water and hydrogen sulfide. It is concluded from the experimental data that the prime requirement for bonding is the dispersal of surface films such as oxides and adsorbed contaminants. THE formation of interparticle bonds during the room-temperature compaction of powder metallurgy components greatly increases the ease of handling in subsequent production operations prior to sintering. The strength of unsintered compacts follows the same general trends as their density and hardness, but quantitative data are extremely Scarce. Quantitative correlation of the data on the overall strength of a compact with that of the individual interparticle bonds is virtually impossible due to the extremely complex geometry of powder compacts. Qualitatively, however, the strengths of unsintered compacts can be correlated with variations in parameters known to influence the extent of cold bonding, and hence interparticle bonding, such as surface cleanliness, relative movement, and deformation of the mating surfaces. Kuzmic and seelig4 found that contamination of powder particle surfaces with lubricants reduced the strength of unsintered iron and copper compacts. Interparticle shear has been shown to promote bonding by Train and Hersey7 while Gregory has shown that die rotation is beneficial. Eilender and schwalbe6 concluded that most bonding occurred during the early stages of pressing iron powder compacts when interparticle shear is one of the principal processes occurring. mile there can be little doubt that these and other factors, such as particle size and shape, affect the extent of interparticle bonding produced by compaction, evaluation of the influence of individual factors is not easy. Particle deformation and relative movement, for example, occur simultaneously during compaction, making any precise measurement of their relative influences difficult. Because of these and other difficulties encountered in studying interparticle bonding in actual powder compacts, the approach adopted in this study was to

Jan 1, 1963

By Lucius W. Mayer

The iron-mines of the Ilsede Hütte Co. are at a town called Peine, about 20 miles east of the city of Hanover, on the railroad to Brunswick (Braunschweig). Hanover, the capital of the province, is a military city, of approximately 250,000 inhabitants, and Brunswick, 33 miles to the westward, has half this number. The mines here described are located in a hamlet called Bülten. The Ilsede Hütte Co. operates two mines, 1.5 miles apart, in this district, Gruber Bülten Adenstadt and Gruber Lengede Bodenstadt. It also operates an iron-mine north of Hanover, known as Eiserhaven, and one in the Harz mountains, the Georg Friedrich, at Grauhof. At Bülten a coarse conglomerate, a, Figs. 1 and 2, contains nodules of limonite, cemented together by calcium phosphate. The ore contains Fe, 25 to 45; Mn, 3 to 4; P, 0.6 to 1.4; S, 0.02 to 0.09; and CaCO3, 40 per cent. Directly above the conglomerate is limestone, b, followed by a mixture of clay and sand, c. Below the conglomerate is a hard clay floor, d. The ore-body, from 10 to, 12 km. long, and from 3 to 4 km. wide, has a maximum thickness of 20 m. It clips approximately 10° S.E., and strikes N. 45° E. Diamond-drill prospecting shows that the thickness diminishes to 1 m. as the end of the deposit is approached to the northward. At this point the deposit is 250 m. below the surface. In Fig. 2, the arrow, A, indicates the general direction of the work along the face, a, which is carried forward in a straight line for its entire length. At B, a train is approaching, which has come from the bench-track, shown at G, by a circuitous route, and is dumping the overburden behind the face, in the space left by the excavated rock. Formerly the work at this mine was essentially open-cut, the deposit having a very strong outcrop. Figs. 1 and 2 show also

Sep 1, 1908

By Barry N. Whittaker

INTRODUCTION Considerable progress has been achieved with long- wall mining in recent years especially in enabling increased rates and levels of output to be gained, higher standards of safety and increased usage of advanced technological developments. Longwall mining also has major long term advantages, prominent amongst which is general minimisation of the effects of pillars and room intersections giving rise to future instability problems as can be the case with room and pillar mining operations. The fact that longwall mining is not presently limited by depth below surface inclination of seams or thickness of seam to be worked strengthens its position as the most popular underground mining method for extracting coal seams in Europe. Its wider application in North America and Australia can give rise to significant economic benefits coupled with higher levels of safety and recovery of coal. This present paper reviews recent progress achieved and draws attention to the more important factors influencing longwall mine design and layout. LONGWALL STRATA PRESSURE ABUTMENTS A longwall gives rise to major redistribution of strata pressures. The roof behind a longwall is normally allowed to cave and permit subsidence of the overlying strata and eventually giving rise to a trough depression at the surface. Consequently, reestablishment of strata loading within the caved region behind the longwall depends upon effective caving and subsequent recompaction. This requires sufficient depth pressure and/or adequate width of extraction in relation to the depth to achieve breaking of overlying roof beds necessary to reload the extracted region. Figure 1 shows results of an analysis carried out by Whittaker and Singh (1979) indicating the pattern of redistribution of vertical stress around a longwall in the plane of the seam. The analysis represents the average depth of longwall working in the UK, and was performed using a stress balance assumption of compatibility before and after mining. The main stress abutments are indicated by (1) the front abutment strata pressure zone which travels with the longwall, and (2) the flank abutment strata pressure zone which

Jan 1, 1982

By Newell G. Alford

Forecasts of future timber consumption in soft-coal mining are handicapped by the lack of adequate experience records for estimating properly the timber requirements of the industry. Data were obtained from plants where records are kept or from operators who collected the information and to these were added composite figures for the continental United States in 1905 and 19191 and for central and western Pennsylvania and for Illinois in 1922.2 The result, representing slightly over 928,000,000 net tons, is shown in Table 1. Some of the companies furnishing data were unable to segregate the timber into classes of use but for those who did, Table 2 shows the board feet of posts and cross ban used per ton of coal mined and the percentage of the total timber consumed that was used in roof support. The wide variation in amounts of timber per ton of coal mined is the result of

Jan 1, 1924

By C. R. Boyd

The sulphuretted ores of Carroll and Grayson Counties, Va., Ore Knob, Ashe County, N. C., and Ducktown, Tenn., in their general position, are in the prolongation of the same massive deposits. The existence of the extensive ore-bodies has been well-established, not only in a practical way, but by the careful research of a number of men of science, including Dr. T. S. Hunt, Professor Kerr, Dr. Genth, Rogers, Safford, Professor Egleston, Dr. H. E. Colton, the writer, and others, and described in one or more of the volumes of our Transactions, as well as in other publications. The greater quantity of&apos; these ores being pyrrhotite, although much of them carry nonmagnetic disulphide, their reduction on the gronnd will probably lead to better results than an attempt to mine and ship them to distant places; and their use as sulphuric acid producers, to be employed in the cheap manufacture of valuable fertilizers, will be chiefly the subject of this paper. The great deposits of Carroll County, Va., are now nearer to railway transportation than any of the others, being six to eight miles from the Cripple Creek extension of the Norfolk and Western Railway, now being constructed, the grading of which is in an advanced state of completion. I am not able to state what are the present prospects of an early completion of the contemplated line of railway to Ducktown. For a long while, during the time those deposits were mined and reduced for their copper, the works were forty miles from any railway ; and the same may be said of Ore Knob, N. C. The deposits in Carroll and Grayson Counties, Va., being now the most accessible to cheap transportation, will naturally claim the greater part of our attention ; though it may be pertinent to remark, just here, that the ores of Ducktown, like those of Carroll and Grayson, Va., exist in the undecomposed levels as iron and copper sulphurets, much of which is a non-magnetic disulphide, as stated, with occasional exhibits of sulphides, such as covellite, erubescite, etc. There are, now and then, small quantities of silver, lead, and zinc,

Jan 1, 1886

By C. R. Ince

The term "differential flotation" is used to denote a flotation operation in which separation is effected between two or more minerals of the same class; e. g., lead sulfide from zinc sulfide, pyrite from blende, chalco-pyrite from pyrite, chalcopyrite from blende. At present, so far as published work shows, there seem to be two theories as to the mechanics of differential flotation. The earlier and more generally accepted theory is that the so-called depressing agents alter the surface of one or more of the sulfides in the ore, either by chemical action or adsorption, so that it is no longer amenable to flotation, but that these depressed sulfides can be revived, after the unaffected sulfide has been floated, by reagents which react chemically with the altered surface and make it amenable to flotation. More recently, Professor Taggartl has advanced the theory that slime adsorption is an important factor in differential flotation. He believes that, with the proper use of a class of agents, which he calls dispersion agents and which include practically all the depressing agents, one can cause the slime to adsorb differentially on sulfide surfaces. A gangue-slime coated sulfide surface will act as a gangue particle and will not float. If, subsequently, an agent that will remove the gangue-slime coating is added, the sulfide again assumes its original surface and can be floated as an ordinary sulfide. This is the basis of the slime theory of differential flotation. Timber Butte mill at Butte, Mont., is a typical lead-zinc flotation concentrator. Neihart ore, chosen for investigation in this work, is one of the custom ores treated at that mill. Practice at Timber Butte mill in February, 1928, was as follows: A combined lead-zinc concentrate was first made using 0.2 Ib. per ton on the ore of potassium xanthate and 0.03 lb. per ton of Cleveland Cliffs oil after 1.5 lb. per ton of lime and 1 lb. per ton of calcium chloride has been added just before the ball mill. The concentrate was then thickened to 70 per cent. solids. Potassium cyanide to the amount of 0.3 lb. per ton and zinc sulfate in the quantity of 0.5 Ib. per ton were added to the thickened pulp and the whole

Jan 1, 1930

Lawrence Addicks, Perth Amboy, N. J. (communication to the Secretary*): The excellent series of photo-micrographs given in this paper shows clearly the relation between micro-structure and cuprous oxide in refined copper. The authors suggest that this method of examillation might be substituted for the " button " method now used to control the refining of cop

Jan 1, 1904

By Linn M. Farish

The reported production of petroleum in the Dominion of Canada for 1930 was 1,555,199 bbl., an increase of 455,373 bbl. over 1929. Alberta accounted for nearly all the production with Ontario and New Brunswick, the other two productive provinces, contributing less than 1 per cent, of the total. The completion of about 25 producing wells in Alberta was more than sufficient to offset the decline of the older wells in that province and the small decline in Ontario. The production of about 5000 bbl. in New Brunswick represents a restricted output to meet the market demand. Table 1 shows the production by provinces for the past 10 years. The consumption of natural gas for all purposes in Canada reached a new record of practically 40,000,000,000 cu. ft. in 1930, which was a considerable increase over 1929. The estimated value of the gas output was $10,500,000, against a little over $5,000,000 for the total petroleum production. Gas wells in Alberta accounted for over 75 per cent. of the total, with Ontario second and New Brunswick a poor third. The outlook for 1931 is for very little change in production of either gas or oil in Ontario and New Brunswick but for a substantial increase in both in Alberta.

Jan 1, 1931