By S. J. Sindeband

Prior to discussing the metallurgy of sintered chromium borides, it is pertinent to outline some of the reasoning behind this investigation and the purposes underlying the work. This study was initiated as an aproach to the ubiquitous problem of a material for service at high temperatures under oxidizing atmospheres, and it was undertaken with a view to raising the 1500°F (816°C) ceiling to 2000°F (1093°C) or better. For the reason that no small, but rather a major, lifting of the high temperature working limit was being attempted, it was felt appropriate that a completely new approach be taken to this problem. A summary of the thinking behind this approach was published recently by Schwarzkopf.' In briefest terms, it was postulated that the following requirements could be set up for a material which would have high strength at high temperatures. 1. The individual crystals of the material must exhibit high strength interatomic bonds. This automatically leads to consideration of highly refractory materials, since their high energy requirements for melting are related to the strength of their atom-to-atom bonds. 2. On the polycrystalline basis, high boundary strength, superimposed on the above consideration, would also be a necessity. Since this implies control of boundary conditions, the powder metallurgy approach would hold considerable promise. Such materials actually had been fabricated for a number of years, and the cemented carbide is the best example of these. Here a highly refractory crystal was carefully bonded and resulted in a material of extremely high strength. That this strength was maintained at high temperature is exhibited by the ability of the cemented carbide tool to hold an edge for extended periods of heavy service. Nowick and Machlin2,3 have analytically approached the problem of creep and stress-rupture properties at high temperature and developed procedures whereby these properties can be approximately predicted from the room temperature physical constants of a material. The most important single constant in the provision of high temperature strength and creep resistance is shown to be the Modulus of Rigidity. On this basis, they proposed that a fertile field for investigation would be that of materials similar to cemented carbides, which have Moduli of Rigidity that are among the highest recorded. The cemented carbide, however, does not have good corrosion resistance in oxidizing atmospheres and without protection could not be used in gas turbines and similar pieces of equipment. It would be necessary then to attempt the fabrication of an allied material based upon a hard crystal which had good corrosion resistance as well. It was upon these premises that the subject study was undertaken and at an early stage it was sponsored by the U.S. Navy, Office of Naval Research. Since then, it has been carried on under contract with this agency. Chromium boride provided a logical starting point for such research, since it was relatively hard, exhibited good corrosion resistance, and, in addition, was commercially available, since it had found application in hard-surfacing alloys with iron and nickel. That chromium boride did not provide a material that met the ultimate aim of the study results from factors which are subsequently discussed. This, however, does not detract from the basis on which the study was conceived, nor from the value of reporting the results which follow. Chromium Boride While work on chromium boride proper dates back to Moissan,4 there has been a dearth of literature on borides since 1906. Subsequent to Moissan, principal investigators of chromium boride were Tucker and Moody,5 Wede-kind and Fetzer,6 du Jassoneix,7,8,9 and Andrieux." These investigators were generally limited to studies of methods of producing chromium boride and detennining its properties. Some study, however, was devoted to the chromium-boron system by du Jassoneix,7 who did this chemically and metal-lographically. This system is not amenable to normal methods of analysis by virtue of the refractory nature of the alloys involved, and the difficulties of measurement and control of temperature conditions in their range. Dilatometric apparatus is nonexistent for operation at these temperatures. Du Jassoneix made use of apparent chemical differences between two phases observed under the microscope and reported the existence of two definite compounds, namely: Cr3B2 and CrB. These two compounds, he reported, had quite similar chemical characteristics, but were sufficiently different to enable him to separate them. The easiest method for producing chromium boride is apparently the thermite process, first applied by Wede-

Jan 1, 1950

C. A. ROSE, New York, N. Y. (written discussion *).-Without doubt the excellent results obtained at Ajo will cause surprise among metallurgists; 75 per cent. average capacity and 80 per cent. extraction during the first year of operation of a plant using a new metallurgical process are figures that speak for themselves. It is obvious that the most troublesome feature of the process is the fouling of solutions. The effects of this are most evident in the electrolytic tank house; but apparently the solutions are so heavily loaded with salts that their dissolving power is also impaired. This is indicated by the fact that copper comes into solution during washing after the leaching of the ore is completed, as shown by the decreasing ratio of acid to copper in the various washes tabulated in Table 4, and also by the fact that 4.9 per cent. of the total copper in the ore remains in the tailings in a soluble form. Even though the extraction in leaching and the ampere efficiency in electrolysis would be benefited by keeping the salts in solution at a lower concentration, it is doubtful whether it would pay to decrease these salts by discarding more electrolyte without other changes in the, process, since this would increase the amount of cement copper produced, which is already very large. If, however, it would not disturb the process otherwise, this object could be accomplished by increasing the range of electrolysis, so that solution going to the tank house would contain, say, 4 per cent. copper and 1 per cent. acid, and the solution returned to the leaching plant 1 1/2 per cent. copper and 4.8 per cent. acid, and by increasing the volume of solution to be discarded, this to be taken from the electrolyzed solution returned to the leaching plant. By this arrangement, more salts will be removed from the system per ton of cement copper produced; and if sufficient solution is discarded to keep the iron content down to 1 1/2 per cent. it would he feasible to recover the copper from

Jan 4, 1919

By W. I. Duvall, L. D. Sadwin

Three explosives with different detonation characteristics were tested by studying their cratering ability in a granite-gneiss. The strain wave generating characteristics of these explosives were also studied in the same rock medium. Correlations between the relative performance of three explosives as evaluated by crater studies and other methods of evaluation are indicated. Numerous test methods have been employed to evaluate the output performance of explosives; for example, the underwater explosion method, the airblast method and the ballistic pendulum method.'*' For blasting applications, the study of explosion produced craters and explosion generated strain waves are the most meaningful. This laboratory has employed these techniques extensively for many years and has shown that the detonation properties of explosives and their ability to generate strain waves in rock are related and that the amplitude and shape of the strain wave is related to some of the crater parameters such as slab thickness and fly rock velocity.3'11 However, a good comparison between the relative performance of explosives as determined by the crater and strain wave methods had not been made. The purpose of this investigation was to determine if the relative performance of three explosives as determined by the crater method shows a correlation with the relative performance as determined by the strain wave method. If a good correlation exists between these two sets of relative performance, it should then be possible to relate the detonation properties of an explosive to its ability to break rock in a crater test. In most commercial blasting operations, the diameter of the blast hole remains constant even though the type of explosive may change. In general, it is the explosive volume rather than the weight which remains constant when two or more explosives of different density are compared. Therefore all tests in this investigation were conducted on a constant volume basis rather than on a constant weight basis. TEST SITE AND ROCK PROPERTIES The tests described in this paper were conducted at a granite quarry owned and operated by the Consolidated Quarries Div. of the Georgia Marble Co. at Lithonia, Ga. The tests were performed in an area where the exposed rock surface was nearly horizontal and where the general rock mass had few joints or faults. The rock has an apparent sp gr of 2.6 and a longitudinal propagation velocity of 18,000 fps. The characteristic impedance of Lithonia granite gneiss is 53(lb - sec/in3). EXPERIMENTAL PROCEDURE There are many parameters which must be considered in the study of explosion-produced craters. The role played by each variable in the explosive-rock-crater system can be determined by experimental techniques in which one parameter is varied while others are maintained constant. In this investigation, the crater geometry was studied as the depth was varied for each of three explosives. The explosive volume and rock-type were held constant for all crater tests. The experimental arrangement used in performing the crater tests is illustrated schematically in Fig. 1.

Jan 1, 1965

By Charles Hardy

?POWDER METALLURGY? is the production of semiformed or fully formed metal products by compressing metal powders. It had its beginnings in the fabrication of tungsten and molybdenum bars and wire by compression, sintering, and swaging. Powder metallurgy, although still in its infancy with other metals, has shown remarkable progress in recent years. Production of Metal Powders-The first step in any powder-metallurgy process is the production of metal particles of suitable shape and size. Mechanical processes for producing metal powders, as by crushing, stamping, or grinding, are usually not suitable, as the resulting particles may cause laminations and decreased strength in the finished articles. The principal metal powders now in use on a large scale are produced by electrolysis or by reduction of metal oxides by gases.

Jan 1, 1936

By Charles R. Stewart, William W. Owens

Reservoir performance predictions based on laboratory core test data assume that fluid flow is laminar for the laboratory test. A study has been made to determine the validity of this assumption for laboratory tests on various types of porosity found in producing limestone formation. Data are presented which show that turbulence and slippage can occur during laboratory tests on hetero-geneous-type porosity limestones, thus causing serious errors in measured single-phase permeabilities and two-phase relative permeability characteristics. In single-phase flow tests it is possible to eliminate turbulence and correct for slippage or to eliminate both factors by controlling test conditions. It is not always possible to control test conditions and thereby eliminate turbulence and slippage in two-phase .flow tests. A correction method is presented which can be used to calculate the true two-phase laminar flow relative permeability characteristic even though furbulence and slippage exist. .INTRODUCTION It is customary to make use of Darcy's law and modifications of this law, together with laboratory data on formation core samples to predict the performance of producing reservoirs. Such predictions are based on an assumption that fluid flow is in the laminar or streamline region for the laboratory test. It was the purpose of this inves- tigation to determine the extent to which turbulent flow may occur in laboratory fluid flow tests on hetero-geneous porosity limestones. Considering that turbulent flow conditions might exist in some laboratory fluid flow tests, additional emphasis was placed on the development of a method to correct for turbulence when laminar flow conditions could not be attained. FLUID FLOW CONCEPTS FOR POROUS MEDIA The Influence of Pore Geometry on Fluid Flow One of the more important factors influencing fluid flow in porous media is the geometry of the pore space which includes such characteristics of the pores as size, shape, distribution, roughness, uniformity, etc. In general, oil- and gas-producing formations can be divided into two broad types on the basis of pore geometry. One has been called sandstone-type porosity media, which is characterized by a small range in pore size, uniformity in shape of the pores, smooth pore surfaces and a regular and uniform distribution of pores. The other type has been called heterogeneous porosity media and is usually limited to the dolomites and limestones. This type is characterized by a wide variation in the size, shape, and distribution of the pores and rough, irregular pore surfaces. It is therefore apparent that conditions are much more favorable for turbulent flow* in heterogeneous-type porosity media than in sandstone-type porosity media. Interrelationship Between Turbulence and Gas Slippage In studying the problem of turbulent flow in laboratory tests on porous media, it is necessary to be aware of the interrelationship between slippage and turbulence for gas flow. As a result of slippage or the Klinken-berg effecta, apparent perrneabilities to gas are greater than the true value because there is no stationary layer of gas in contact with the walls of the flow channels. Gas slippage decreases as the mean free path of the gas molecules decreases. Since the mean free path of any gas decreases with increasing density, increases in static pressure result in lower apparent gas permeabilities. However, a reduction in gas permeability can also be due to turbulence. Therefore, in studying only turbulent flow in porous media, it is necessary to hold gas density, and slippage, constant or to reduce slippage to a negligible value by operating at high static pressures. Presentation of Laminar and Turbulent Flow Data A graphical relationship between permeability and a pseudo-Reynolds number, N,, will be used to show the two types of fluid flow, i.e., laminar and turbulent. The usual graphical method for such a description has been the use of friction factor-Reynolds number charts4. On such a logarithmic diagram, the laminar region appears as a straight line having a slope of 45 degrees. As the friction factor decreases and the Reynolds number increases, the turbulent region is reached and appears as a deviation from the 45-degree slope line. However, in petroleum engineering literature resistance of por-

The Anglovaal Group has released details concerning its new processes for recovering platinum group metals, stating that the Group's system, which involves batch processing and precipitation methods for these metals (PGM's), leads to faster recovery times, increased recoveries, and higher purities than the conventional process. Insofar as South Africa's Merensky Reef is concerned, the Anglovaal method of recovering palladium first (as opposed to platinum in the conventional process) enables it to use a much simpler process in the subsequent recovery of platinum and other metals. Because the processes give cleaner separations, the volume of material to be recirculated -and therefore the total volume of material in the recovery circuits- is reduced substantially.

Jan 3, 1976

By Toshimitsu Kokubo, Yoshio Yamagata, Tadao Moro, Kenji Tomita

Owing to the traffic jam in collection, and transportation of wastes, the air- and water- pollution in incineration plants, and the sanitary trouble in reclaimed land, it seems that the defective existing system of the solid waste treatment in Japan can not follow the change in quality and the increase in quantity of solid wastes. Under these situations, the objective of the municipal solid waste treatment must be to actualize the pollution-free system for environmental protection and the resources recovery system for resource- and energy- saving. From this point of view, AIST of Japan is now engaged in the research and development of the resources recovery system from municipal solid wastes. This paper reports on the outline of the development of resources recovery technology in Japan, including the AIST's project on this matter.

Jan 1, 1976

By J. B. Mackintosh

THE quantitative determination of copper, by means of electro-deposition, offers so many advantages, that it is to be preferred, when properly executed, to all other methods for ease and accuracy. The object of the present paper is to give the results of a number of experiments made during the past few months, and to indicate some sources of error, which must be avoided in order to attain the necessary accuracy. In 1867, C. Luckow, in competition for a prize offered by the directors of the Mansfield Copper Works, submitted the following

Jan 1, 1882

By C. A. Allen

FOR over three years we have been endeavoring to reduce the number of fatalities and minor accidents in Utah. The physical condition of the o? Represents the average of 4 States mentioned excluding the catastrophes indicated. FIG. 1.-NUMBER KILLED PER MILLION SHORT TONS OF COAL PRODUCED IN COLO¬RADO, NEW MEXICO, UTAH, WYOMING, AND BITUMINOUS MINES OF THE UNITED STATES, 1914 TO 1920. mines, concentrators, and smelters is good, yet the number of accidents,

Jan 5, 1922

By S. T. Wlodek

The scale md subscale reaction products were identified and their rates of formation were studied in air over the range 1600" to 2000°F (871 " to 1149°C) for periods of up to 400 hr and for hoth the solution-annealed and aged conditions. The effect of prior sltrface preparation on suhscale oxidation was also studied The general oxidation behavior of both Ni-Cr-Mo-Al-Ti type alloys was similar. A surface film of a, Al2O3, forms immediately on exposure Subsequent oxidation continued at a linear rate (QL = 55 * 5 kcal per mole) as colonies of Cr2O3 nucleated at the A12O3/gas interface Further oxidation proceeded at a paraholic rate zvhiclz could he fitted to two successive rate constants. During paraholic oxidation, and depending on temperature, the scale consisted of Cr2O3, NiCr2O4 , and TiO2 with traces of NiO. In the case of Rene 41, the activation energy of both paraholic processes was 66 * 3 kcal per mole suggesting that diffusion of cations tlzrozrgh Cr2O3 was the rate -determining process. An unusual decrease in the oxidation of Udimet 700 at 1900°F where a spinel of Ni(A1,Crh0, zuas the predominant reaction product prevented the accurate assignment of activation energies for this composition. In both alloys internal oxidation of Al2O3 commenced shortly after parabolic scaling was observed. Prolonged exposure prod7tced intemal oxidation of TiN, and in Udimet 700 a complex Mo-Ni nitride was also found. At 1900oF, the subscale reactions in Udimet 700 undergo an inversion which parallels the decrease in surface oxidation; internal oxidation ceases hut is replaced by the formation of "spherodized" 3.' colonies. Surface-preparation techniqtles which introduce appreciable working, such as coarse surface grinding or grit blasting. increase the amount of alloy depletion and internal oxidation in Reni 41. The reverse is true of Udimet 700 for which electropolished or mechanically polished specimens show much more subscale oxidation than strongly worked stirfaces. The strongest commercial nickel-base alloys presently available are generic to the Ni-Cr-Mo-A1-Ti base which exploits the precipitation of Ni3(A1,Ti) as the main strengthening mechanism, while relying on solid-solution strengthening by molybdenum and chromium reinforced by the pre- cipitation of carbides to attain maximum properties. This study characterizes the oxidation behavior of Rene 41, the strongest alloy of the Ni-Cr-A1-Ti type commercially available in sheet form, and Udimet 700, whose higher aluminum and titanium content allows it to exhibit one of the more attractive combinations of high-temperature properties available in a wrought product. The scaling processes of complex, type nickel-base alloys have received relatively little attention. Malamand and vidal as well as Poulignier et al.2'3 have determined the composition gradients across the metal/oxide interface produced by high-temperature oxidation and considered the effect of surface perature, Limited weight-gain data has also been published by Fere 5 for alloys of this type and Radavich6 has identified the reaction products on Udimet 500 and Inco 702 after oxidation at 1832°F. Reference can, of course, be made to the excellent reviews of Kubaschewski and Hopkins7 or Ignatov and Shamgunova8 for a summary of the data available on the oxidation of binary and ternary alloy systems which are related to the more complex alloys considered here. EXPERIMENTAL The analyses of the different commercial heats studied are given in Table I. Using the experimental procedures previously established,9 continuous weight-gain data were obtained on both heats of Rene 41 sheet (A and B) and 150-mil-thick slices of cast Udimet 700. Subscale oxidation reactions were followed by static exposure of cylindrical specimens obtained from swaged Rene 41 (Heat C) and Udimet 700 (Heats E and F). In brief, continuous weight-gain tests were performed on specimens with a surface area of 10 to 12 sq cm. These were abraded through 600 grit Sic paper, electropolished to 2p rms in an electrolyte of 10 pct H2So4 in ethanol, and lightly etched in 10 pct HCl in ethanol before final washing and rinsing in ethanol. All continuous weight-gain data were obtained in dried (-70°F dew point) flowing (1 liter per min) air to an accuracy of +0.1 mg. Subscale oxidation processes were followed by the metallographic examination of 0.5-in-diam by 1.0-in.-long specimens. After an initial center-less grinding, various additional surface treatments were employed to determine the effect of surface preparation on subscale oxidation processes. Before exposure in zirconia crucibles, all samples were lightly etched in 10 pct HCl-ethanol, washed in ethanol, and dried. The depth of internal oxidation was measured to ±0.00025 in. on unetched specimens mounted so as to provide a taper mag-

Jan 1, 1964

By R. A. Pallanch

Probably one of the most perplexing problems with which a mill operator contends is the proper evaluation of his mill results. True, he accurately determines his recoveries of metals and grades of products monthly, weekly, and often daily. These figures do not of themselves directly translate to mill economics. When one figure is unusually good there may be an offsetting circumstance. The advantage of high lead or zinc concentrate grade may be offset by poorer recovery; high lead recovery may be offset by poorer zinc recovery, or vice versa; and so on. Besides, grades or recoveries may not of themselves mean more than a reflection of the grade and character of the ore during the period under study. What the operator sorely needs is some one measuring stick that tells him when he has achieved his greatest return, regardless of grades or recoveries—for if he knows his methods and practices are yielding the optimum return he need no longer concern himself with the assays of products and tailings, or the corresponding distribution of metal values. At first blush it would appear that the obvious answer to this is the actual money return to the mill. Paradoxical as it may seem, however, money return does not make a dependable yardstick any more than do grades and recoveries, as ore condi- tions would vary enough to bring about greater money return during periods when the actual metallurgical work is not as good. The mill operator, of course, should always aim for the greatest return on the ore, once it is in the mill bins, with proper attention always to mill treatment cost. The need of a proper yardstick becomes more imperative with the increasing complexity of the problem. In the case of a simple, single-product operation on a fairly uniform ore, in which only one metal is of significant importance, the need is not great, as grade and recovery pretty well tell their own story. At the other extreme is the operation that makes three or four separate marketable products from a complex mixture of heterogeneous ores that vary tremendously in individual metal contents and ratios, degree of oxidation, and other characteristics, and in which gold, silver, copper, lead and zinc are all significant values. Economic Recovery The first attempt at obtaining a proper single yardstick for a fairly complex ore with which I am familiar is the use of the ''Economic Recovery" term at the lead-zinc flotation mill of the Sunnyside Mining and Milling Co., Eureka, Colorado. This method had been applied there early in Sunnyside flotation-mill history (not later than 1920) and credit for the innovation I believe belongs to Messrs. Kuryla and Marquand. The term "Economic Re-

Jan 1, 1949

By Albert L. Toenges

C. P. HEINER*—I would like to ask Mr. Toenges about the highest rank coal. I did not get that clearly. What kind of coal is that? A. L. TOENGES (author's reply)— The coal in the Matanuska field ranges from high volatile "B" bituminus to anthracite. It all depends on which direction you go in the Matanuska field. C. P. HEINER—Is it a large reserve. A. L. TOENGES—That is what we hope. That is what we are trying to find out. B. W. DYER*—In those strip beds, I wonder how far back the coal would weather ? A. L. TOENGES—I never noticed particularly. B. W. DYER—The weathering does not extend back like it does in this country ? A. L. TOENGES—No, it does not. B. W. DYER—Is that due to the freezing ? A. L. TOENGES—Probably so. B. W. DYER—In this country, you would expect nothing but weathered coal. R. H. SWALLOW*—Along that line, you mentioned some of the seams were on fire. Did you ever know how far back they burned, or was it hard to tell ? A. L. TOENGES—The fires occurred in the mine. That one you refer to was from an inside fire.

Jan 1, 1950

By H. R. Barnhurst

IT would be a difficult matter to trace from the beginning the very few improvements made in the burning of fuels prior to 1860. Doubtless the crossing of the sticks of wood in building a, wood fire early appealed to our savage ancestry as a means of expediting its effectiveness for their crude culinary purposes. Stones and andirons came later in assisting the admission of air to the under part of the fuel bed, while beacons and cressets utilized metal bars as supports for the same purpose. It is probable that Tubal Cain owed his success to the use of bellows making possible the use of mixed fuel and charge upon a hearth. With the development of working in east iron, grate bars cane in, and they are still with us doing duty in every household and almost every art where heat is a factor. Little was done beyond these crude methods prior to 1860. With the advancement of knowledge came the fuel-gas producer, a. natural child of the retorts employed in supplying illuminating gas. It is only within the last 15 years that the conclusion became general that complicated systems for saving heat would not remedy deficiencies in its primary development, and within that tine there has been great advancement in the means of producing initially fire of high efficiency, so that to clay we are moving rapidly toward loth high development and high absorption, with the resultant of high efficiencies. In studying the subject of the availability of pulverized coal as a fuel, it may occur to ask, why has this not come up earlier? This question would be naturally prompted by recalling the fact that Thomas Crompton's English patents upon his methods were issued to Min nearly 40 years ago. A conclusive answer to this, however, is that Crompton at that time had very crude facilities for raking what was at best a, very imperfect pulverization of the coal, and the expense of preparation was very great. He does not seem to have been aware of the advantage of a thorough drying of the coal in the

Jan 10, 1913

By H. R. Barnhurst

It would be a difficult matter to trace from the beginning the very few improvements made in the burning of fuels prior to 1860. Donbtless the crossing of the sticks of wood in building a mood fire early appealed to our savage ancestry as a means of expediting its effectiveness for their crude culinary purposes. Stones and andirons came later in assisting the admission of air to the under part of the fuel bed, while beacons and cressets, utilized metal bars as supports for the same purpose. It is probable that Tuba1 Cain owed his success to the use of bellows making possible the use of mixed fuel and charge upon a hearth. With the development of working in cast iron, grate bars came in, and they are still with us doing duty in every household and almost every art where heat is a factor. Little was done beyond these crude methods prior to 1860. With the advancement of knowledge came the fuel-gas producer, a natural child of the retorts employed in supplying illuminating gas. It is only within the last 15 years that the conclusion became general that complicated systems for saving heat would not remedy deli-. ciencies in its primary development, and within that time there has been great advancement in the means of producing initially a fire of high effciency, so that to-day we are moving rapidly toward both high development and high absorption, with the resultant of high efficiencies. In studying the subject of the availability of pulverized coal as a fuel, it may occur to ask, why has this not come up earlier? This, question would be naturally prompted by recalling the fact that Thomas Crompton's English patents upon his methods were issued to him nearly 40 years ago. A conclusive answer to this, however, is that Crompton at that time had very crude facilities for making what was at best a very imperfect pulverization of the coal, arid the expense of preparation mas very great. He does not seem to have been aware of the advantage of a thorough drying of the coal in the

Jan 1, 1914

By E. F. Adkins, R. W. Douglas

The variation of the spectral emissivity of osmium and ruthenium with temperature can be expressed by the following relations: DURING a study of the sintering characteristics of osmium and ruthenium, discrepancies in the previously accepted melting points of the metals were noted. The melting temperatures had not been measured at the time of the work, but were estimated in the literature as 2700°C for osmium and 2450°C for ruthenium.' A recent investigation by Baird2 has shown the melting temperatures of osmium and ruthenium are 3000" and 2250° C, respectively. In the present work, osmium bars sintered at temperatures as high as 2900° C showed no evidence of melting, whereas ruthenium showed definite evidence of melting at temperatures as low as 2250°C. In view of the apparent discrepancies, the melting temperatures of both metals were determined. The spectral emissivities of both metals were determined as an aid to studies of the sintering characteristics of these metals. MATERIALS AND PROCEDURES The materials used in these studies were metal powders supplied by Englehard Industries, Inc., through the courtesy of The International Nickel Co. Analytical data from three laboratories, although not in complete agreement as to the purity of the material or the major impurity elements, indicated that the maximum impurity levels were 0.5 and 1.0 wt pct in osmium and ruthenium, respectively. The metal powders were pressed to 1/4 by 1/4 by 6-in. bars at 20Tsi using carbon tetrachloride as a lubricant. The pressed bars were presintered 1 hr at 1200°C after heating 1 hr at 400°C. The presintered densities of the several bars of the metals ranged from 65 to 80 pct of ideal density. Specimens were self-resistance heated in a vacuum sintering bell. Temperatures were measured with an L&N, disappearing filament optical pyrometer. True temperatures were read at the base of an 0.30-in.-diam, 0.150-in. deep hole drilled into the center of a presintered bar. Apparent temperatures were read from the surface of the bar adjacent to the hole. MELTING POINT DETERMINATION The melting temperature of the metals was determined as the temperature at which a slight additional increase in current through the specimen resulted in a reduced temperature at the base of the hole. The apparent reduction in temperature is a result of the liquid metal filling the hole, thus altering the black-body conditions. The melting points of osmium and ruthenium, based on three deter-

Jan 1, 1962

By W. E. Remmers

The fact that gray iron increases in volume, cracks and distorts upon repeated heating and cooling is rather conlmon knowledge. In ingot molds, Diesel engine pistons, carburizing boxes, continuous furnace parts, grate bars, stoker parts, and all castings that are subjected repeatedly to high and low temperatures, the phenomenon of growth presents a vital problem. Ingot molds distort and produce cracks which result in seams or laps and later appear as defects in the finished product. The heads of Diesel pistons frequently fail by cracking in a stellar shape. This is attributed usually to the result of permanent growth. Distortion and change of dimension of furnace parts frequently renders them entirely unusable. In chain grate stokers, mechanical difficulties frequently are caused by the growth of the links. In proper operation these links should never attain a temperature sufficiently high to start growth; nevertheless, some have grown in. on an 8-in. length when improperly operated. Even though the phenomenon is generally known there still exists a deficiency in the explanation of the mechanism of this growth. The field of investigators of this subject has a decided variation in opinion concerning the causes. The problem is of sufficient importance therefore to warrant further consideration. Review of Published Work Since the published work, particularly the European, contains much detail, only the outstanding results and conclusions of the investigators will be reviewed. The pioneering investigations of Outerbridge in 1904 and 1905 brought forth the conclusion that growth was not a function of chemical or crystallographic changes but was a result of the formation of fine hair cracks. These cracks are supposedly due to a nonuniformity of thermal expansion and contraction which ruptures the structure of the material. More recently Benedicks and Lofquist presented a purely mechanical theory, which is similar to that of Outerbridge. These investigators believe the temperature gradient from the outside to the center of the cast piece causes a contraction of the outer layers on passing

Jan 1, 1931

By D. G. Westlake

The electrical resistance of a series of V-H alloys (0 to 3.5 at. pct H) has been measured over the temperature range G° to 360°. Interstitial impurities made contributions to the residual resistivity, but not the ideal resistivity. The contribution of hydrogen in solid solution is expressed by Ap = 1.12 microhm-cm per at. pct H; but the contribution of precipitated hydride was negligible. A portion of the so1vu.s for the V-H phase diagram is presented. The solubility limit is given by In N (at. pct H) = (5.828 i 0.009) - (2933 i 44)/RT. Comparison of critical temperatures joy hydride precipitation and published critical temperatures for hydrogen embrittlement suggests the two are related. ThiS study was initiated as part of an investigation of the mechanism by which small concentrations of hydrogen embrittle the hydride-forming metals at low temperatures. It has already been shown that, in the case of hcp zirconium, a reduction in ductility accompanies the strengthening resulting from precipitation of a finely dispersed hydride phase.''' Our attempts to detect a similar precipitation of a second phase at low temperatures in V-H alloys by transmission electron microscopy have been thwarted because we have been unable to prepare thin foils that are representative of the bulk material with respect to hydrogen concentrati~n.~'~ The present investigation establishes the solvus of the V-H system at subambient temperatures. Subsequently, we hope to be able to determine whether the embrittlement temperature is related to the critical temperature for precipitation of the hydride in a given V-H alloy. veleckis5 has proposed a partial phase diagram for the V-H system based on extrapolations of the pressure-composition relations he measured at higher temperatures. Kofstad and wallace' conducted a similar study of single-phase alloys but did not attempt to establish the phase diagram. Zanowick and wallace' and ~aeland' have studied a portion of the phase diagram by X-ray diffraction, but they investigated no alloys in the hydrogen concentration range 0 to 3 at. pct, the range of interest to us. EXPERIMENTAL PROCEDURE The vanadium was obtained from the Bureau of Mines, Boulder City, Nev., in the form of electrolytic crystals. The analyses supplied with them listed 230 ppm by weight metallic impurities, 20 ppm C, 100 ppm N, and 290 ppm 0. The crystals were electron-beam-melted into an ingot that was rolled to 0.64 mm. Strips, 60 mm long and 4.2 mm wide, were cut from the sheet, and both rolled surfaces were ground on wet 600-grit Sic paper to produce specimens 0.4 mm thick. They were wrapped in molybdenum foil, vacuum-encapsulated in quartz, and annealed 4 hr at 1273°K. The specimens were annealed in a dynamic vacuum of 2X lo-' Torr for 30 min at 1073°K for dehydrogenation, and charged with the desired quantity of hydrogen by allowing reaction with hydrogen gas at 1073°K for 2 hr and cooling at 100°K per hr. Purified hydrogen was obtained by thermal decomposition of UH3. Sixteen specimens were studied: two contained no hydrogen and the others had hydrogen concentrations between 0.5 and 3.5 at. pct (hydrogen analyses were done by vacuum extraction at 1073°K). Electrical resistances were measured by the four-terminal-resistor method on an apparatus similar to the one described by Horak.~ The specimen holder was designed so that both current and potential leads made spring-loaded mechanical contact with the specimen. The potential leads were 30 mm apart, and the current leads were 55 mm apart. The current was 0.10000 amp. We used the following baths for the indicated temperature ranges: liquid nitrogen, 77°K; Freon 12, 120" to 230°K; Freon 11, 230" to 290°K; and ethanol, 290" to 340°K. Temperatures lower than 77°K were achieved by allowing the specimen to warm up after removal from liquid helium. Temperatures above 77°K were measured by a calibrated copper-constantan thermocouple (soldered to the specimen holder) and below 77°K by a calibrated carbon resistor. The temperature of the bath changed less than 0.l0K between duplicate measurements of the resistance. RESULTS AND DISCUSSION Typical plots of resistivity p vs temperature T are shown in Fig. 1. In the interest of clarity, only five curves are presented and the data points have been

Jan 1, 1968

By C. J. Ramsburg

The construction and operation of by product coke-oven plants in America are essential to strong national defense and of the greatest importance to many widely diversified undertakings as well as to safety and health. Carbonization Process Coal used under a boiler or in a locomotive is consumed by combustion. Coal used in a by-product oven is distilled or carbonized, meaning that heat is applied to the coal, out of contact with air, causing a distillation that removes the volatile matter in the coal in the form of gas and vapor, leaving coke as a final product. From the gas and vapor distilled from the coal, many valuable substances can be secured, known as by-products. Hence the name "by-product oven." The simplest example of this principle can be shown by means of an ordinary clay pipe. If powdered coal is placed in the bowl of the pipe, the opening of the bowl is plugged with clay, and the bowl placed in a flame, the bowl will become hot, transferring the heat through the wall of the bowl to the coal within. When this coal attains a temperature of about 750°F., gas will begin to pour out of the pipe stem, and this gas may be lighted. A black liquid also will exude from the stem of the pipe, This is tar mixed with certain other products. What remains in the bowl after distillation is coke. A coke oven corresponds to the bowl of the pipe. A modern oven of the latest type is a refractory brick chamber approximately 42 ft. long and 14 ft. high, averaging 18 in. in width. The oven is filled with coal through closable charging holes in the oven top. Each end of the oven consists entirely of a self-sealing door, the removal of which permits the finished coke to be discharged by means of a power-operated pusher machine. The ovens are built in batteries, and the heating is effected by gas burned in vertical flues in the oven walls, each set of flues heating the walls of two adjacent ovens. Such ovens carbonize a charge of approximately 18 tons of coal in 18 hr., or have a daily throughput of 24 tons per oven, producing about 17 tons of coke. In times of need, the output may be increased by raising the temperature of flues, thus shortening the coking time. There is one great essential difference in principle between distillation in a clay pipe and in a coke oven. In the 18-in. oven, the distillation proceeds from two parallel walls held at a high temperature (over zooo°F.) and instead of all the coal being heated at once, the distillation is a progressive one creeping inward. The average travel of this heating is 35 in. per hour from each vertical wall, and as the volatile products are formed progressively they must push away from the interior toward the wall through the previously formed hot coke, then up the walls and Over the top of the coal charge, finally escaping through the outlet pipe. This results in a cracking of the components into many different and valuable substances not formed when the carbonizing temperature is low.

Jan 1, 1942

By C. J. Ramsburg

The construction and operation of by product coke-oven plants in America are essential to strong national defense and of the greatest importance to many widely diversified undertakings as well as to safety and health. Carbonization Process Coal used under a boiler or in a locomotive is consumed by combustion. Coal used in a by-product oven is distilled or carbonized, meaning that heat is applied to the coal, out of contact with air, causing a distillation that removes the volatile matter in the coal in the form of gas and vapor, leaving coke as a final product. From the gas and vapor distilled from the coal, many valuable substances can be secured, known as by-products. Hence the name "by-product oven." The simplest example of this principle can be shown by means of an ordinary clay pipe. If powdered coal is placed in the bowl of the pipe, the opening of the bowl is plugged with clay, and the bowl placed in a flame, the bowl will become hot, transferring the heat through the wall of the bowl to the coal within. When this coal attains a temperature of about 750°F., gas will begin to pour out of the pipe stem, and this gas may be lighted. A black liquid also will exude from the stem of the pipe, This is tar mixed with certain other products. What remains in the bowl after distillation is coke. A coke oven corresponds to the bowl of the pipe. A modern oven of the latest type is a refractory brick chamber approximately 42 ft. long and 14 ft. high, averaging 18 in. in width. The oven is filled with coal through closable charging holes in the oven top. Each end of the oven consists entirely of a self-sealing door, the removal of which permits the finished coke to be discharged by means of a power-operated pusher machine. The ovens are built in batteries, and the heating is effected by gas burned in vertical flues in the oven walls, each set of flues heating the walls of two adjacent ovens. Such ovens carbonize a charge of approximately 18 tons of coal in 18 hr., or have a daily throughput of 24 tons per oven, producing about 17 tons of coke. In times of need, the output may be increased by raising the temperature of flues, thus shortening the coking time. There is one great essential difference in principle between distillation in a clay pipe and in a coke oven. In the 18-in. oven, the distillation proceeds from two parallel walls held at a high temperature (over zooo°F.) and instead of all the coal being heated at once, the distillation is a progressive one creeping inward. The average travel of this heating is 35 in. per hour from each vertical wall, and as the volatile products are formed progressively they must push away from the interior toward the wall through the previously formed hot coke, then up the walls and Over the top of the coal charge, finally escaping through the outlet pipe. This results in a cracking of the components into many different and valuable substances not formed when the carbonizing temperature is low.

Jan 1, 1942

By J. H. Polhems, R. B. Brackin, D. B. Grove

P. L. Jones (Sink and Float Corp., New York)—The comparisons between galena and ferrosilicon medium should be applied only to the specific sink-float process used at Mascot since no evidence is presented that allows the comparison to be extended generally to galena medium as now used in other forms of sink-float. It is stated that flotation recovery of galena medium was tried but was unsuccessful and therefore the elaborate gravity system of medium recovery was applied. The expense of the gravity system at Mascot was one of the reasons for changing to ferrosilicon. However two important sink-float plants treating a combined total of over 13,000 tons of ore per day are using flotation to clean galena medium most successfully and are obtaining medium recoveries comparable with those reported in the paper for ferrosilicon. Slightly increased zinc recovery is claimed due to the change-over but it is to be noted that at the time of the change a decreased density differential was obtained in the separator. With galena a differential

Jan 1, 1952