By F. V. Hicks

THE similarity of mining practices in bituminous coal fields through-out America is due to the fact that certain fundamental conditions are encountered in all fields. The problems of labor, housing and mining are somewhat similar whether the mine is in Pennsylvania, Illinois, Wyoming or the State of Washington. Each field has had its particular problems, resulting in advantages or disadvantages over a competing field. This might take the form of a wage differential, a better natural condition more favorable to cheap production, or proximity to a market that allows freight rate advantages, etc. In any event, no matter how favorably situated, the mining companies that have been slow to recog-nize and accept the advantage of mechanization, clinging too long to the old hand methods, have found themselves unable to meet competition. Throughout the Wyoming coal fields, production methods have so changed in the last decade as to be almost unrecognizable to an old-time coal miner who has had no connection with the industry during; that period. The old contract system, with its peculiar labor relationship between employer and employee, based upon the long-established custom that the miner's working place was his castle, and that it was his privilege to carry on operations within that place largely in his own way and to his own liking, is a condition that has passed away. The present-day, 100 per cent mechanized mine bears but little resemblance to the old. A change -in system has naturally altered the old-time labor relationship. Contract labor has been almost entirely eliminated and a straight day-wage basis established, with certain classes of work calling for different rates, which places the entire personnel of the underground operating force more directly under the direction and supervision of the mine foreman and his assistants. The transition from the old order to the new has gradually done away with the system of penalties, personal- rights and privileges existing under the contract system, which were so controversial in the past that the average mine management was constantly involved in labor disputes in fields where organized labor was employed.

Jan 1, 1936

JESSE L. JONES,* Pittsburgh, Pa.-I would like to ask Miss Erskine if down-draft has been used in any of the foundries where heavy fumes have to be removed, instead of the overhead draft.? L. -ERSKINE.-The system of overhead draft to remove heavy fumes has been very much more successful. The entire efforts of the New Jersey Department of Labor in regard to stabilizing conditions in the foundry are the result of the physical examination of the foundryman himself on first-hand information as to the prevalence of the minor ailments and the bad timekeeping that naturally accompanies them. These ailments are a factor in not only increasing the labor turnover but in increasing the percentage of bad work as well. The physical exertion of the foundryman himself is of course an important factor. In certain standard shops the amount of energy expended runs from 11 to 13 tons of foot-pounds of energy a day. In certain shops on piece work, I found a record of the energy expended per day to run as high as 22 tons. In one shop, during the war period, the management established a bonus system, and the men increased their output from 60 to 100 molds a day. The result was an increase of some 60 per cent. in output, and an increase of 400 per cent. in defective castings. The question of the physical exertion in the unsanitary foundries, of course, is very much complicated by other factors, for which reason the department has devoted a good deal of attention to estimating what is a reasonable exertion in a sanitary, well ventilated foundry. We have met certain physical difficulties in the brass foundries that the iron foundries did not have. All that information is available through our Bureau of Industrial Information. The question of the physical energy exerted by the molder is found to have a very distinct bearing on the question of contracts, for the possibility of increasing production is balanced by the extra overhead involved. JESSE L. JONES.-I would like to ask if any evidence has been noticed of carbon-monoxid poisoning among the employees of the foundries.

Jan 4, 1919

By Bradley Stoughton

The regular, bottom-blown Bessemer converter of the present day is a modification of previous forms, and most of the latest proposed modifications of it are merely returns to former types which Ressemer discarded. That he tried almost every conceivable method of blowing iron, with tuyeres at almost every possible position or angle, is well known; and it is to be supposed that he was familiar with the advantages of each type, since he finally settled on that form which has not been improved upon hitherto, for the purposes for which converters will generally be used. Modifications have been tried along two lines: In the arrangement of tuyeres, and in the manner of carrying out the process with tuyeres still blowing vertically upward through the bath. While they have all failed in general competition with the regular modern type of vessel, some of them have found special fields in which they have held their own. The most notable example is in the steel-casting industry, and especially in that part of it concerned with the manufacture of castings which require very hot or very fluid metal, or supply a demand of constantly varying physical or chemical requirements. In this industry the small converters occupy a field between that of the crucible-process and that of the open-hearth process, arid have won a place for themselves in France, England, America, Russia and other countries, which they bid fair to retain until either a new method is discovered of producing cheaply very hot, fluid steel, or the open-hearth process is so improved that very hot steel may be made with it at lower cost of repairs to lining arid roof.

Jan 1, 1903

By A. Hultgren

PAGE Outline of Progress of Knowledge and Theories about Gas Evolution in Steel Ingots, and Its Influence on Crystallization and Segregation 2 Object of Present Investigation 16 theoretical Discussion of Process of Solidification 17 Gas Given Off from Rimming Steel during Solidification 17 Equilibrium Diagram of the Iron-carbon-oxygen Alloys 19 Solidification of Pure Iron-carbon-oxygen Alloys 25 Solidification When Carbon Monoxide Is Given Off at Constant Pressure... 25 Solidification When Gas Evolution Is Suppressed 26 Schematic Application on Solidification of Rimming-steel Ingots 27 Influence of Manganese, Sulphur and Phosphorus 28 Experimental Work 30 Liquid Steel and the Mold Gas 30 Ingots Investigated and Methods Used 33 Ingot Structure 42 Structure of Rim Zone 42 Structure of Core 49 Structures Obtained under Special Conditions of Freezing 50 Distribution of Metalloids 55 Other Observations Made 60 General Discussion of Solidification Process 63 Condition of Liquid Steel before Casting 63 Rimming Period 70 Composition of Rim Zone 93 Freezing after Top Is Closed 96 Slag Inclusions and Ingot Scum 102 Reaction between Gas in Blowholes and Surrounding Solid Steel during Cooling 103 Summary 105 Appendix-Preparation and Etching of Ingot Sections 106 References 107 IN 1934, Jernkontoret (The Swedish Ironmasters' Association) appointed a committee for the study of the structure of rimming-steel ingots and the various phenomena associated with their solidification. The members of the committee, including those who have joined it later, have been: I. Bohm, B. D. Enlund, B. Kalling, M. Tigerschiöld, 1. Wohlfahrt and the authors. The present paper? is a somewhat

Jan 1, 1939

By T. E. Seidel, A. U. MacRae

The dependence of the electrical and crystalline properties of silicon containing ion implanted boron atoms have been studied as a function of the incident dose, substrate temperature, and annealing tempera-ture. Hall effect studies show that the compensation due to defects is negligible after annealing at and above 500°C for a dose of 1013 ions per sq cm. Steps occur in the isochronal annealing curve for the sheet resistance at 300°C and 800°C and the mechanisms responsible for these steps are discussed. The range of the ions at 150 kev is 3500 * 5001. Electron diffraction studies on samples implanted with 150 ker ions show the existence of damaged (polycrystalline) silicon closer to the surface than the range of the ions. Etching and subsequent annealing of etched and unetched specimens suggest that the poly crystalline silicon is closer to the surface than the bulk of the distribution of ions. THE purpose of this study is to investigate some electrical and crystalline properties of ion implanted boron in silicon. Sheet resistance, Hall measurement, depth distribution by chemical staining, thermal probe and electron diffraction have been used to study the properties of samples implanted in a random direction with ions having energy up to 150 kev. The boron-silicon system has been the subject of considerable study'-7 due to its possible application in the fabrication of electronic devices. The implanted ions produce considerable crystalline damage to the substrate crystal before they lose most of their primary energy and come to rest. Fortunately, most, if not all, of this damage can be removed by subsequent annealing or by holding the substrate at an elevated temperature during the implantation process. Sheet resistivity measurements of the p-type layers produced by boron implantation into room-temperature silicon, reveal that the annealing occurs in a two-step process: the first occurring at -300°C and the second at -800°C.' Electron-microscope and low-angle electron diffraction studies of this damaged material indicate that the bombarding ions produce an amorphous silicon region about the trajectory of each ion.' At high doses, these damaged regions overlap and an amorphous surface layer results. Furthermore, the 800°C annealing step, appears to be associated with the elimination of this gross damage. The depth distribution of the as-implanted and also the annealed samples have been studied by an angle lap and staining technique as well as by Hall measurements.3-7 We find the experimentally determined ranges of the boron are less than those calculated by the Lindhard-Scharff-Schiott theorys (hereafter referred to as the LSS theory). Our results are in essential agreement with pre- vious results. In addition, we have made Hall measurements on samples bombarded with a low dose (2 x 1013 ions per sq cm) to minimize impurity banding effects, and find that deep ionized levels influence the carrier concentration and room-temperature hole mobility until the sample is annealed at temperatures above 500°C. Above this temperature, the data corresponds to that obtained when silicon is doped with boron by conventional techniques. We have also made a depth distribution determination of the crystalline damage due to the implanted boron by using glancing angle electron diffraction techniques. It was found that the gross damage depth distribution of heavily implanted samples is closer to the surface than the depth distribution of the electrically active boron. By removing this gross damage, without affecting the distribution of the implanted boron, we have determined that the 800°C annealing stage is not exclusively due to the improvement in the crystalline perfection of the amorphous material but also appears to be associated with the annealing of some point defects. These results and their relation to previous results are discussed in the following sections. IMPLANTATIONS Boron ions were implanted into silicon samples using an accelerator capable of operating from 10 to 150

Jan 1, 1970

By B. Post, D. Moskowitz, F. W. Glaser

Lattice parameters of various hafnium compounds, two borides, a carbide and a nitride were determined. Some physical properties were measured and comparisons with the properties of the corre-sponing zirconium compounds were drawn. A LTHOUGH borides of transition metals have A been extensively investigated in recent years, there are few references in the literature to borides of hafnium. This is not surprising, in view of the extreme scarcity and great cost of the purified metal. Becker' reported the existence of a boride, carbide, and nitride of hafnium; he listed the formulas as HfB, HfC, and HfN. However, in his work no mention was made of chemical analyses of the reaction products. In this paper results of a study of various hafnium compounds, including borides, carbides, and nitrides, are reported. It was expected, of course, that these compounds would closely resemble their zirconium analogues, which have previously been extensively investigated. Three borides of zirconium are known: ZrB,² ZrB,² and ZrB212.4 In addition, one carbide, ZrC,5 and one nitride, ZrN,5 have been reported. It should be noted that ZrB and ZrB12 are stable phases only in relatively high-temperature regions, unlike ZrB2, which is stable from room temperature to its melting point." It was felt that hafnium would yield corresponding borides, carbides, and nitrides with similar stability ranges. Experimental Procedures and Results A quantity of hafnium metal that was better than 97 pct pure, with zirconium as its major impurity, was furnished by the Argonne National Laboratories. The boron powder used was approximately 96.5 pct pure. In general, the procedure involved mixing the metal and boron powders in the desired proportions, and subsequently hot pressing them. The resulting specimens were analyzed chemically and phases present were identified by X-ray diffraction methods. A Philips Norelco Geiger counter spectrometer was used for identification of components and for measurement of lattice constants. Filtered copper radiation was used for all X-ray work. Electrical resistivity and density measurements were carried out at room temperature. The stable diboride, HfB2, will be described first. Stoichiometric quantities of boron and metal were heated to approximately 2000°C during hot pressing. The reaction product was shown by X-ray diffraction methods to be isomorphous with ZrB2 (space group Dlgh; P6/mm). Values of lattice constants of HfB2 compared with those of ZrB2 are shown in Table I. The calculated density of HfB2 is 11.2 g per cc, compared with a measured (pycnometric) value of 10.5 g per cc. HfB2 specimens prepared under a wide variety of conditions (including variations in initial Hf-B ratios) showed only insignificant variations in lattice constants, indicating a very narrow range of homogeneity. Like ZrB2,7 HfB2 is an excellent electrical conductor. The resistivity at room temperature of hot-pressed samples, approximately 85 pct dense, is 12 microhm-cm. This compares favorably with the electrical resistivity of 10 mi-

Jan 1, 1954

IN the preceding chapter on thermochemistry and the reactions in and between metal and slag phases and in the following chapter on fuel combustion the main emphasis is placed on the equilibrium or "static" conditions. This equilibrium viewpoint is not concerned with the rate of change in the process or with the mechanisms or paths followed between initial and final states. The questions of just "how it works" and "how fast" belong to the kinetic aspect of any process; their answers are helpful in speeding up or slowing down and thus controlling its operation, and also in understanding its limitations. Any treatment of kinetic factors in the open hearth such as is attempted here and in Chapter 22 must at present be largely qualitative and incomplete. We are only beginning to get quantitative data on rates of reaction and diffusion at high temperatures, as indicated in Chapter 15. Empirical data in the literature on furnace operating rates do not help much to illuminate the details of gas-flow patterns and the complexities of heat flow in the many parts of the furnace system. This chapter is intended to give the reader an introduction to the problems of the flow of gases through the furnace system and the flow of heat in this system. An adequate discussion would require several times the space available here; it is possible here only to outline a few fundamentals and to indicate some of the conditions of heat and gas flow peculiar to the open hearth. Several good general treatments of these subjects may be found in the literature (see references at the end of the chapter). For the designer of open-hearth furnaces, the principles of gas flow are of paramount importance. They are also important to the operation of the process, at least to the extent of a general qualitative picture of the movement of gases in the system. MOTION OF GASES IN FURNACE DUCTS Fluid [flow] in general can vary between the extremes of laminar or streamline flow with a minimum energy loss, to irregular

Jan 1, 1964

By T. S. Plaskett

A striated structure perpendicular to the growth axis was observed by the copper-decoration tech-nique in dislocation-free, .float-zoned silicon crystals. The striations, which were spaced about 100 p apart, fitted the relationship d = f/u , where d is the spacing, f is the growth rate, and u is the crystal rotation rate. Each stria was resolved into an UNDOPED silicon crystals pulled from quartz crucibles by the Czochralski technique usually exhibit a striated structure perpendicular to the growth axis.'-' This structure has been attributed to oxygen segregation, with the oxygen being introduced from the quartz crucible. If the crucible is rotated, the level of oxygen contamination has been reported as high as 10° atoms per cu cm.10 These striations are similar to solute striations commonly observed in doped Czochralski-grown crystals. The periodic nature of the striations is caused by a periodic variation in the growth rate",12 which is attributed mainly to thermal gradients in the melt.13 A finer striated structure14 attributed to constitutional supercooling is sometimes observed between the coarse striae. The oxygen striations have been observed by infrared transmission techniques,' by the copper-decoration technique,' by X-ray diffraction microscopy,6-8 and by 9 p absorption measurements3 on crystals pulled from the melt both with and without dislocations. In this investigation float-zoned dislocation-free crystals were examined by the copper-decoration technique. The level of oxygen for float-zone material is less than 1016 atoms per cu cm the lower limit of detection by 9 p absorption measurement. EXPERIMENTAL TECHNIQUE The crystals were grown by the float-zone process with the rf heating coil outside of the quartz envelope containing the silicon. All float zoning was done under an atmosphere of purified helium. The Dash technique15 was used to grow the crystal dislocation-free. This involves growing the crystal initially with a diameter between 2 and 3 mm and at array of starlike precipitates of copper. The strucLure was not .found at the surface tor a depth of about 1.5 mm, or in a region of similar width ahead of a dislocation network. The structure is postulated to consist of vacancy clusterings or dislocation loops. very rapid rates, about 20 mm per min, for a distance of about 3 cm. The diameter of the crystal is then increased to the diameter of the source of silicon, which in this case was about 19 mm. Because of the arrangement of the apparatus, the zone was passed downward rather than upward, contrary to the standard float-zoning practice. Also, the source was rotated rather than the seed. ziegler17 has made dislocation-free crystals by a similar technique but has passed the zone upwards. The starting material was zone-refined and had a p-type resistivity of 150 ohm-cm. The major impurity was boron; the total impurity excluding the boron was reported by the supplier (Dow-Corning) to be typically less than 2 x 1013 atoms per cu cm. The crystals were examined by the Dash copper-decoration technique18'19—a method in which about 10" atoms per cu cm of copper are diffused at a temperature between 900" and 1000°C into silicon which is then quenched to room temperature. On quenching, the copper precipitates on crystalline defects which are then visible when viewed by transmission infrared microscopy. The photomicrographs shown were taken either of the infrared image tube screen or directly on infrared film. All sections prior to decorating were chemically polished and, for some sections, given a sirtlZ0 dislocation etch-pit examination. After decorating, the samples were mechanically polished. RESULTS A photomicrograph, taken in transmission of a decorated cross section, is shown in Fig. 1. The portion of the section shown is near the surface of the crystal. The entire cross section showed no dislocation etch pits after being given a Sirtl etch treatment. It is seen that the copper precipitated randomly. Each precipitate, as has been reported by others, was found to have a starlike structure.

Jan 1, 1965

H. RIES, Ithaca, N. Y.-The part of Mr. Fiske's paper that interests me especially is that portion dealing with the raw materials, and the tests that were applied to the raw materials in order to determine their value in advance, if possible, because that, I believe, is a step in the right direction. For a number of years I have done my best to persuade different consumers of clay to develop standard methods for testing raw materials. We have in this country a large variety of clays which can be used for a great many different purposes, but in many cases the consumers either have no standard methods for determining the value of those clays in. advance, or if they have they do not publish them; consequently it often puts the clay miner at a disadvantage. If, for example, manufacturers of different types of refractory materials would state publicly just what physical tests their raw materials have to meet, it would, I believe, help them to find more easily the materials that they are looking for, and the clay producer would also be benefited. It would also encourage him to have his clays tested in advance, so that samples could be accompanied by certificates of physical tests that would be of convenience to the manufacturer. At the present time, in this country there are certain types of clay which seem to be rather scarce. There apparently are not many deposits of clay that are exactly suited for the manufacture of zinc refractories. So, too, there are not many deposits of clay that are suited for the manufacture of glass-pots, or the blocks for glass tank furnaces, or clays that can be used for graphite crucibles. Now, in many cases, no standard series of tests has been developed. I am also gratified to see that Mr. Fiske considers the tensile strength. tests of value. Some years ago the American Ceramic Society appointed a committee to draw up a series of recommendations covering standard tests. These recommendations were especially for the use of State geologists and the U., .S. Geological, Survey. Among the tests that were considered was the tensile-strength test, which Mr. Fiske has mentioned in his paper. Unfortunately, a majority of the committee turned it down, and the test was therefore not officially approved, but two of us, who formed the minority, believed in it. Since then the other members of the Committee have come to see that that is an important test to make and Mr. Fiske has emphasized it in his paper.

Jan 1, 1918

By Alfred V. de Forest

WE are now assembled in this hall for the eighteenth lecture in honor of the memory of our greatest American metallurgist, Henry Marion Howe. Many of his most intimate contemporaries, led, as was fitting, by Professor Sauveur, have described his vital accomplishments in three fields: as a leader in technical industrial development; in theoretical research; and finally as a teacher and source of inspiration for nearly two generations of students. In 1914 Professor Howe had retired from active teaching, but maintained his laboratory at Columbia University under the care of Arthur G. Levy, with whom he published many of the papers that later were incorporated into his last book, "The Metallography of Steel and Cast Iron." My position at the time was that of personal assistant to Professor Campbell-no pay, no duties, but the great privilege of preparing specimens, taking pictures and attending to some of the current consulting work. Whenever possible, I visited Howe's laboratory to chat with Levy and gather ideas about the wonderful field of metallography-in which I was a rank amateur, rescued by the quiet enthusiasm of Donald Smith of Princeton from an instructorship in civil engineering. Levy let me act as a fly on the wall during the Professor's occasional visits. Busy as he was, Professor Howe took the time and trouble to encourage my interest, as he had done for hundreds of others. He told me how he went about gathering his own information speculating as to causes, considering experiments, and verifying his conclusions. I ventured to mention some tests I had run on the irregular stretching of wires of different metals. He read the small volume I had prepared of ill-assorted facts and fancies and remarked: "Nobody cares for your theories or the history of your tests. Describe what you found as briefly as possible and perhaps I can help you to publish." Curiously enough, among my discards were some autographically recorded load-versus-electrical-resistance measurements. Taken with inadequate knowledge and equipment, these curves did not reproduce consistently, but if the relationship between strain and resistance had then been explored, the latest type of strain gauge might have been in useful service for the past 25 years. Professor Howe was a gifted teacher, perhaps because he was primarily an ardent and assiduous student. His own eagerness to learn and his willingness to revise and extend his opinions constantly encouraged those of his environment to be diligent and painstaking in the pursuit of knowledge. In honoring his memory, I also wish to bring to mind the kindly, humorous and quiet Levy, and join his name again, as it was for too brief a space in the past, with that of many-sided Henry Marion Howe. FACTORS OF IMPACT STRENGTH The subject chosen for the Howe Memorial Lecture by Dr. Gillett last year

Jan 1, 1941

By Lucien Eaton

VENTILATION in the iron mines of the Lake Superior region in nearly all cases is natural; that is, it is induced by the difference in elevation between different outlets in the mine and by the difference in temperature of the air in the mine and that outside. This difference in temperature is frequently augmented by placing a steampipe in the upcast shaft; but aside from this, artificial aids to ventilation have been rare until - recent years. In some of the older mines, as at the Cliffs Shaft mine at Ishpeming, Mich., in the 80's, fans have been used when there was only one opening to surface, but their use was abandoned as soon as a natural circulation of air started. In recent years, the Newport mine at Ironwood, Mich., was the first to use positive mechanical ventilation. The installation was not large enough, however, to give definite results, reliance being placed largely on natural ventilation. With the coming of warm weather in the spring of 1914, the necessity of positive mechanical ventilation at the Lake mine of the Cleveland-Cliffs Iron Co. at Ishpeming, Mich., became evident. The workings of the Lake mine are under the bed of old Lake Angeline, which was pumped out in 1894, and the mine had been in operation for 6 years prior to that date making a total of 26 years of continuous operation. The total production, up to 1914, amounted to over 8,000,000 tons. The ore was first mined by square-set rooms and pillars, but this was later changed to top slicing and caving. Both methods required the use of large amounts of timber, probably 80,000,000 board feet in all, practically all of which remained in the timber mat. The slow oxidation of this timber was one of the principal causes leading to the installation of mechanical ventilation. The mine was served by only one working shaft, called No. 4, a second outlet being provided by a raise to the surface from the old workings on the south side of the mine. This raise was the "down cast;" but it was very small and the drifts and raises leading to it were too small and crooked to permit an adequate amount of air to enter the mine, especially during the warmer weather. Measure-

Jan 8, 1920

By Frank Firmstone

The material described below was made at Furnace No. 2, Longdale, Va., Oct. 28, 1907, during a sudden derangement of working, in the course of which the furnace became entirely bridged over and for some time no solid material whatever descended into the hearth. This caused the hearth to become so completely emptied that, at the tuyere-level, a pricker put in at one tuyere could be seen by looking in at the opposite one. The tap-hole was opened and the iron got out with some difficulty. It ran sluggishly, throwing many sparks, but was not too thick to run into the chill-molds. Naturally, the product was assumed to be white iron, which is almost always produced under similar circumstances; but on removal front the molds it proved to be very strong and tough, although full of blow-holes. Most of these blow-holes bad bright, unoxidized walls. The iron could be drilled by using a "special steel" drill, the drillings curling up similarly to those of steel. An analysis by P. W. Shimer of this unusual product gave: Si, 0.019; P, 0.228; S, 0,39; Mn, 0.042; C, 2.366; and graphite, 0:000 per cent. A cast of iron made just before the disturbance contained P, 0.98, and Mn, 1 per cent. The peculiar product seems to have been decarburized in the hearth and, at the same time, to have lost much phosphorus and manganese, either by the action of the blast in the empty hearth, or, more probably, by. contact with the cinder rich in iron which was formed at the time. Unfortunately, no specimen of the cinder was preserved, so its composition cannot be given. It seems very remarkable that, with the furnace in bad condition, the temperature should be high enough to keep such

Sep 1, 1908

By E. S. Machlin

The possibility that formation of voids under creep-rupture conditions may take place by the condensation of vacancies has been investigated theoretically. It has been concluded that nucleation of voids under creep-rupture conditions by vacancy condensation is highly improbable. However, growth of pre-existant voids by vacancy condensation is probable. A number of predictions made in this theory have been verified by the data. It has been predicted and checked that the product of rupture life and steady-state creep rate for preannealed metals and single phase alloys is an approximately invariant quantity, independent of stress, temperature, and atomic number for a given type structure. The direction of the effect of cold work on this product has been predicted and found in agreement with experiment. A number of experiments to evaluate the vacancy condensation mechanism further are described. SEVERAL papers have appeared recently which speculate on the origin of voids formed at grain boundaries under stress.' ' The object of this paper is to examine quantitatively the proposition that the voids produced in a creep test are a result of vacancy condensation. A result of this paper is a theory of creep-rupture. Void Nucleation Application of standard nucleation theory" to the problem of void nucleation leads to the following conclusions: 1—Homogeneous nucleation of voids requires a supersaturation ratio (concentration of vacancies in supersaturated to that in saturated solution) of 400 for a reasonable surface energy of 1000 erg per cm-and 1.4 for the improbably low surface energy of 10 erg per cm. 2—Heterogeneous nucleation of voids at plane interfaces between two phases requires a supersaturation ratio of 2.5 for a typical contact angle of 145 3-—Void nucleation about a solid particle may be accomplished at a supersaturation ratio of 1.17 for a typical value of work of adhesion? of 60 erg per The work of adhesion is the surface work 10 replace two solid-vauor surfaces by a solid-solid interface. enr ' between an oxide and a metal in the presence of a surface active element such as sulphur. Estimates of the supersaturation ratio at which voids are produced in diffusion experiments yield a maximum of 1.01. Inasmuch as the foregoing mechanisms of void nucleation probably will not operate at this level—too low a surface energy is required—the investigatol. is led to the conclusion that voids must already exist. That is, nucleation of voids probably does not occur. Rather, existing submicroscopic voids grow out to visible size. Already existing voids might be produced during solidification or working. Supercritical sized parlicles which contain cracks may act as heterogeneous void nuclei. Gas pockets may act as void nuclei. Experiments are desired to determine the nature of the heterogeneous void nuclei which grow out to voids in both diffusion and creep experiments. Void Growth Void growth might occur in at least two possible ways, depending upon whether the already existing void nuclei are at grain boundaries or within the grains. In the case of a spherical void far from a crystal boundary, vacancies are generated during creep as a consequence of the migration of suitable dislocation jogs' and are also annihilated at sinks. Under these conditions, a steady-state concentration of vacancies is built up in the crystal, defined by the condition that for any differential volume the rate of generation of vacancies in that volume equals the rate of annihilation of those vacancies." This equality would lead to the development of a gradient of vacancy concentration radially outward from the void surface up to a radius where the vacancy lifetime becomes equal for all directions of vacancy migration. The distance over which this vacancy concentration gradient extends equals about 2vD,T* where D, is the vacancy diffusivity and T:' the vacancy lifetime in a crystal outside the gradient in a zone of constant vacancy concentration. The vacancies generated in the region over which the gradient exists will annihilate more often at the void than elsewhere. Approximately a little over one-half the vacancies generated in the gradient zone will annihilate at the void. Hence, the growth rate of the void is given by on where R is the radius of void in centimeters, is the atomic volume, and R is the rate of generation of vacancies, number per centimeter" per second. R D and T* may be estimated in terms of other physical parameters." In particular, R = n.j e/b [3] where n is the average number of vacancy produc-

Jan 1, 1957

By D. J. DeLazaro, W. Rostoker, R. E. Riley, M. Hansen

At very low concentrations, carbon dissolves interstitially in molybdenum resulting in a linear expansion of lattice parameter with increase of carbon in solid solution. Geometrical consideration of the relative size of carbon atom to size of interstice approximately predicts the observed volume expansion. THE element carbon, occurring in molybdenum, either as an unavoidable impurity, or purposely added, markedly affects the mechanical properties of molybdenum. Several investigators1-" have noted the occurrence of molybdenum carbide at the grain boundaries of cast molybdenum, and Fischer and Rengstorff' have shown that this intergranular constituent can induce intergranular brittleness. The appreciable change, with temperature, of the solid solubility of carbon in molybdenum, found by Few and Manning," suggests other important effects upon mechanical properties. Finally the relative atom diameters of carbon and molybdenum (the ratio of atom diameters is 0.59) are indicative, by analogy with iron (ratio of carbon atom diameter to iron atom diameter is 0.65), of a possible interstitial solid solution. If carbon dissolves intersti-tially in molybdenum, anelastic effects and age-hardening effects, similar to those observed in other body-centered cubic metals, could be expected. However, from the work of Sykes, Van Horn, and Tucker," it might be inferred that carbon forms only a substitutional solid solution with molybdenum. These considerations made it desirable to study the effect of carbon on the lattice parameter of molybdenum in greater detail than heretofore. All heat treating was done in a high temperature furnace7 built specifically for heat treatment of molybdenum. The temperatures and times of heat treatment were determined from the a solubility limit for the Mo-C system." These heat treatments were carried out in argon which was purified with respect to N, and H.!0." Purification of the argon was accomplished by passing the argon over hot (750°C) titanium and then through a magnesium perchlorate drying tower. As many as six samples were run concurrently and quenched at different times without interrupting the furnace cycle. Both the purity of the furnace atmosphere and ability to quench samples from any temperature up to 4000 °F were of prime importance in the successful heat treatment of samples for the lattice parameter investigation. Carbon Analysis The Leco Combustion apparatus was used for carbon analysis. This apparatus is capable of an accuracy of & 0.003 pct for a 1 g sample in the range below 0.10 pct. However, it is felt the degree of accuracy is somewhat better than this limit in view of the consistency evident by cross checking a number of determinations. The Battelle Analytical Laboratory consistently reported check results to within k 0.001 pct C. X-ray Measurements The molybdenum wire specimens (20 mils) were carefully filed down to about 12 mils and then etched with nitric acid to 8 mils. Carbon analyses were made on specimens before reduction in size; however, since there was no evidence of surface carburization, it is probable that the carbon was uniformly distributed throughout the sample. The resultant specimens were strain free and small enough to minimize the error in the lattice parameter determinations due to X-ray absorption. Diffraction patterns were obtained with a Debye-Scherrer powder camera 114.59 mm in diam utilizing the Straumanis type asymmetrical film mounting. Nickel-filtered copper. Ka radiation and zirconium-filtered molybdenum Ka radiation were used. Line positions on the film were measured with a traveling microscope equipped with a vernier scale permitting measurement to 0.001 cm. The average of five readings was used to determine the position of each line. The lattice parameter for each specimen was determined from the data by the extrapolation method of Bradley and Jay, Y.e., the intercept at 90" of the straight line obtained by plotting the apparent lat-

Jan 1, 1953

By Frederick Laist

F. N. FLYNN, Clifton, Ariz.-I would like to ask Mr. Mathewson what percentage of his leaching liquor is wasted at this time? It has a bearing on the question in connection with the New Cornelia, and I think it is a very important question. E. P. MATHEWSON, Anaconda, Mont.-I am not sure what the percentage is now, but we don't discard the strong liquors. Something like 25 per cent. of the wash water taken out each day is sent over a special set of scrap iron tanks, and the copper recovered there. We had a little trouble at first. We did not proceed to use the sponge iron for the reason that the plant we originally contemplated was abandoned for flotation. Our original idea was to use a leaching process on all the tailings of the mill, but we found it would take a great deal of time to build a plant; and the cost of operating the plant we estimated to be about the same and the recovery the same. It was a question of time with us, and we decided to adopt flotation. That changed our plans. We now have the leaching plant, treating the tailings of the old dump, and the flotation applied to the current tailings. The sponge iron was figured for the large plant. We can get all the scrap iron necessary for the small plant-plenty from the scrap produced in the main plant of the smelter.

Jan 12, 1916

By T. F. Archbold, R. E. Grace

The use of interference colors is the simplest experimental way to determine the approximate film thicknesses of oxides formed on liquid metals. A large amount of data under various conditions can be obtained easily and quickly. The oxidation of liquid lead has been studied by several investigators,1-5 but all of these studies have been on thick oxide scales. The purpose of- this work was to investigate the range 0 to 2000A film thickness. By using electron diffraction, Jenkins concluded that the surface of the film on molten lead is yellow orthorhombic PbO with the (110) planes parallel to the surface. This was confirmed by Shimaoka and Yamai7 who also used electron diffraction from the melting point of lead to 730°C. The rate of oxidation of pure liquid lead in air was measured in the temperature range 453" to 643°C by observing the rate of formation of interference colors on static lead baths. Approximately 170 g of lead (99.999 pct) was placed in a refractory dish having a working surface of 13.8 sq cm. This crucible was placed in a deep-well resistance furnace open to the atmosphere. The times at which the various interference colors appeared, after wiping the molten metal surface clean, were determined at 453", 533°, 600°, and 643°C. Elapsed times were determined with a stopwatch and all colors were estimated by eye. Bath temperatures

Jan 1, 1959

By T. L. Joseph

A study is made of the amount of solution loss necessary to maintain the reducing power of the gas stream in the blast furnace. Curves are presented to show the effect of solution loss, moisture in the blast, and carbon dioxide from the flux on the nitrogen in the THE blast furnace process is based upon the counter flow of gases and solids. As CO, N, and H, flow upward from the combustion zones, oxygen is acquired from the descending charge. In the reduction of iron ore, a portion of CO is converted to CO, and similarly a portion of H, is converted to water vapor. The inert N,, from the air used in combustion, passes through the furnace with little change. Its concentration is, however, decreased by reactions such as direct reduction and solution loss which increase the volume of CO in the gas stream; Similarly the evolution of C02 from the limestone also dilutes the nitrogen. he purpose of this paper is to illustrate an idealized and simplified method of studying furnace processes by following changes in the gas phase between the tuyeres and the stock line. A more specific objective is to evaluate the effect of solution loss upon the CO/CO, ratio in that region of the furnace in which FeO is reduced to metallic iron. This last stage of reduction requires relatively high CO/CO, ratios to exceed the equilibrium requirements. Solution loss or the reaction of COZ with C to produce CO has a pronounced effect upon the ratio of the carbon gases and is necessary to maintain the reducing power of the gas stream if the consumption of coke is low. It will be explained later that indirect reduction followed by solution loss is stoichiometri-cally equivalent to direct reduction. Calculations will be made to show how the composition of the gas in the region of the mantle varies with coke consumption and with different amounts of solution loss. Such calculations show the condi- tions under which gasification of C with oxygen in the charge is needed to maintain the reducing power of the gas. Equilibrium conditions for FeO and the carbon gases will be used to establish a minimum CO/CO, ratio below which reduction will not proceed. The manner in which carbon is gasified in the furnace, at the tuyeres with oxygen in the air or above the tuyeres with oxygen from the charge, will be a basic feature of all calculations. It is hoped that greater interest in the use of top gas as a means of following furnace reactions will be aroused by the calculations and generalized curves which are presented. Bosh Gas Equations Subject to some alteration by the amount of moisture in the blast and by direct reduction, the gas leaving the combustion zones of a blast furnace has a definite composition. Because a relatively small amount of oxygen is acquired from the charge in the bosh and in the crucible, the products of combustion undergo little change until they enter the shaft. Bosh gas is, therefore, essentially the products of combustion of carbon in a deep fuel bed with air. The relative weights and volumes of reacting materials are expressed by the equation: 2~ + 0? + 3.76N, = 2C0 $ 3.76NZ [I] Air Bosh Gas -air = 79% N? = 3.76) 21% 02 Starting with a known mass of C consumed largely by air, Eq 1, but partly by water vapor, Eq 2, the volume and C + H2O = CO $ H? [21 composition of the bosh gas can be calculated and subsequent changes followed as reactions take place at various elevations in the furnace. As shown in

Jan 1, 1952

By Harry K. Ihrig

The hot-working of iron and steel is an art dating back to antiquity, but until about 25 years ago, relatively few alloying elements were used, and these were present only in small percentages. With the exception of sulphur, the amounts of other elements in steels did not markedly affect their hot-workability. The references in the literature on the effect of other elements on the hot-workability of steel are usually reports of failure of these steels in forging or rolling.1-8 With the increased use of alloying elements, and their use in larger amounts, it was observed that many of the new steels were red short in certain critical ranges or at all hot-working temperatures. The stainless steels are particularly difficult to hot-work. The determining of the correct conditions for piercing, rolling and forging of these alloys by experimentation in the mill often results in large losses of these expensive metals. It also is found that the hot-workability limits of many types vary from heat to heat, and hence poor results are obtained on changing to a new heat after a previous one has rolled satisfactorily. To determine the effect on hot-workability of iron to which various elements have been added, it was necessary to devise a method that could be used on small quantities of metal. In such a method, the minimum number of variables should be present, and the procedure should be simple, quick and correlatable with large-scale hot-working operations. Sauveur,9 in the first Henry Marion Howe lecture in 1924, described the effect of carbon on the ductility of steels in torsion near their critical points. He found that carbon increases the plasticity of gamma iron. In the 1930 Campbell Memorial lecture,10 he gives the effect of carbon, chromium, and chromium and nickel on the ductility of steels under 2000°F. in torsion. Ellis11 has studied the malleability of steels at various elevated temperatures by means of a single-blow drop-hammer test. In this test the percentage decrease in height of standard cylinders is taken as a measure of their malleability. He has shown that in the low-alloy steels studied, carbon has a greater effect than nickel, chromium and vanadium. In 1938 the first tests were run on a new quantitative hot-workability test in the laboratories of the Globe Steel Tubes CO. Thum12 mentioned it in 1940. An illustration of the apparatus was published in January 1942.'' The effect of a few alloying elements on the hot-workability of metals was shown in a description of the test in 1944.14 Description of Test Method The method adopted after a trial of several others is a rapid twisting of bars to failure in a furnace. The standard-size bar was chosen as 9/16 in. It is prepared from larger pieces by forging and cold-

Jan 1, 1947

By Harry K. Ihrig

The hot-working of iron and steel is an art dating back to antiquity, but until about 25 years ago, relatively few alloying elements were used, and these were present only in small percentages. With the exception of sulphur, the amounts of other elements in steels did not markedly affect their hot-workability. The references in the literature on the effect of other elements on the hot-workability of steel are usually reports of failure of these steels in forging or rolling.1-8 With the increased use of alloying elements, and their use in larger amounts, it was observed that many of the new steels were red short in certain critical ranges or at all hot-working temperatures. The stainless steels are particularly difficult to hot-work. The determining of the correct conditions for piercing, rolling and forging of these alloys by experimentation in the mill often results in large losses of these expensive metals. It also is found that the hot-workability limits of many types vary from heat to heat, and hence poor results are obtained on changing to a new heat after a previous one has rolled satisfactorily. To determine the effect on hot-workability of iron to which various elements have been added, it was necessary to devise a method that could be used on small quantities of metal. In such a method, the minimum number of variables should be present, and the procedure should be simple, quick and correlatable with large-scale hot-working operations. Sauveur,9 in the first Henry Marion Howe lecture in 1924, described the effect of carbon on the ductility of steels in torsion near their critical points. He found that carbon increases the plasticity of gamma iron. In the 1930 Campbell Memorial lecture,10 he gives the effect of carbon, chromium, and chromium and nickel on the ductility of steels under 2000°F. in torsion. Ellis11 has studied the malleability of steels at various elevated temperatures by means of a single-blow drop-hammer test. In this test the percentage decrease in height of standard cylinders is taken as a measure of their malleability. He has shown that in the low-alloy steels studied, carbon has a greater effect than nickel, chromium and vanadium. In 1938 the first tests were run on a new quantitative hot-workability test in the laboratories of the Globe Steel Tubes CO. Thum12 mentioned it in 1940. An illustration of the apparatus was published in January 1942.'' The effect of a few alloying elements on the hot-workability of metals was shown in a description of the test in 1944.14 Description of Test Method The method adopted after a trial of several others is a rapid twisting of bars to failure in a furnace. The standard-size bar was chosen as 9/16 in. It is prepared from larger pieces by forging and cold-

Jan 1, 1947

By C. H. Mathewson, W. R. Hibbard, Robert Maddin

A satisfactory mathematical relationship between shear, elongation and change of orientation in the axial straining of a single crystalline rod or wire may be based on a simple model in which blocks, representing glide lamellae, glide over one another and rotate so as to maintain the original fixed position of the axis as the wire elongates.' Obviously such a model gives no information concerning strain-hardening or the atomic adjustments at the sliding surfaces and their influence on the internal structure of the blocks. Moreover such an operation could be conducted with rigid blocks only by using self-aligning grips or a flexible attachment which would permit the adjacent blocks to freely assume their changing orientations. There are many unsolved problems (see Andrade2) concerning the manner in which nature departs from the simple model in permitting the essentials of slip, rotation and elongation to occur along with strain-hardening and the appearance of glide lamellae of various dimensions and special characteristics, not fully appreciated at the present time. This paper describes part of an extensive investigation on the development and characteristics of glide ellipses in single crystalline alpha brass rods and is especially concerned with the observation of cross-slip in crystals oriented wholly within the range of slip on a single system according to the generalizations first presented by Taylor and Elam in 1923.³ Experimental Procedure Half-inch rods of alpha brass (nominally 70 pet Cu, 30 pet Zn)* were converted into single crystals by melting and gradual solidification in a graphite mold according to the Bridgman method.4 In order to remove any coring, the crystals were homogenized at 800°C for 16 hr and tested by etching with a 50 pet nitric acid solution. The back-reflection Laue technique as described by Greninger6 was used for determining the orientations of the crystals. Standard stereographic operations were employed to locate the specimen axis in a triangle of the Taylor and Elam3 projection so that the slip plane and direction could be predicted. The lineage structure reported by Buer-ger6 was present in the crystals used in this investigation. However, only crystals were used in which the internal differences in orientation did not exceed two degrees. Very little is known concerning the effect of the presence of a lineage structure on the detailed mechanism of plastic deformation.

Jan 1, 1949