By A. U. Seybolt, F. J. Norton

A standard technique for heat treating small metallurgical samples where no appreciable contamination from the atmosphere can be tolerated is that of sealing small samples in evacuated fused-silica tubes. Since vitreous silica is relatively impervious to diffusion of gases, even at temperatures approaching the devitrification range, around 1100°C, this simple procedure has been very widely adopted as a standard technique in metallurgical research. Many workers have recognized that, with metals of fairly high reactivity, insulation from direct contact with the SiOz envelope is desirable in order to avoid displacement reactions of the type M + SOz-- MOz + Si(in M). It is not so generally known, however, that the 'rate of permeation of oxygen from the air through the SiOz enclosure at tem-

Jan 1, 1964

By S. T. Wlodek, John Wulff

Dense, adherent, and ductile coatings of chromium can be applied to Molybdenum by selectively freezing out the chromium solute from a supersaturated copper-or tin-rich liquid alloy. The successful exploitation of this technique depends on the control of variables common to any freezing process. Under the most favorable combimtion of supersaturation, nucleation, and mass-transfey, coatings as thick as 0.004 in. can be obtained. In exploratory experiments it was found that a coating of chromium may be applied to molybdenum by immersing the molybdenum body in a supercooled copper-chromium or tin-chromium melt and selectively freezing out the contained chromium onto the molybdenum body. Supercooling of the liquid metal plating bath can be achieved by cooling, or the maintenance of thermal or concentration gradients in the melt. The technique is similar to conventional dip-plating procedures where the sample is immersed in a molten bath of the pure plating medium, except that in these studies, the plating medium consisted of a dilute solution of chromium in liquid tin or copper. The success of this method requires that the base material to be plated be isomorphous with the coating and insoluble in the plating bath. In addition, the plating bath, while having an appreciable solubility for the coating component, must have negligible solid solubility in the solid plate. Such relationships exist in the molybdenum-chromium, chromium-tin, and chromium-copper systems. Liquid tin and copper are satisfactory as the plating solvent, because although chromium is appreciably soluble in both of these liquid metals, solid inter-solubility is almost negligible, and no compound formation occurs. The same relationships exist between molybdenum and copper or tin except that the solubility of molybdenum in liquid tin or copper is insignificant. It is this combination of solubility relationships, as well as the completely isomorphous nature of the molybdenum-chromium system, which allows the formation of a chromium coating on molybdenum by the selective freezing mechanism. Since the main deterrent to the widespread use of molybdenum for high-temperature structural applications is its poor oxidation resistance, the formation of a dense and ductile chromium coating on molybdenum may well be of commercial significance. In addition, the basic principle of coating formation by selective freezing should be applicable to other metallic or even nonmetallic systems. The precipitation of the solute from a liquid metallic solution, for the formation of a protective coating, has not been previously considered in the literature. Frequently, however, a similar phenomenon has been described in the corrosion of metallic heat exchangers by liquid metals1 wherein temperature gradients in the liquid metal heat-transfer medium result in the formation of layers or deposits of metallic residue2 in the cooler portions of the system. Impregnating techniques using liquid baths have been tried as a plating process. Semchyshen and Barr, for instance, have successfully diffused chromium into molybdenum by immersing the molybdenum specimen in a liquid tin-chromium or copper-chromium alloy. This simple holding technique fails to produce a layer of pure chromium and requires prolonged immersion to allow for the diffusion-activated enrichment of the molybdenum. During the course of this investigation, most of the phase relations published for the copper-chromium4 and molybdenum-chromium4 systems, were found reliable. It was necessary, however, to investigate the solubilities of chromium and molybdenum in liquid tin as well as the solubility of molybdenum in liquid copper. These determinations were made by a simpie weight loss technique on materials of the same purity as used in the plating studies. The results of these solubility studies are given in Tables I and I1 and indicate that although the solubility of molybdenum in liquid

Jan 1, 1961

By F. V. Shallcross

Physical properties of thin films of CdS and CdSe formed by vacuum deposition onto glass sibstrates have been studied as a function of deposition and processing conditions. The crystallinity and surface features of CdS films were examined using electron microscopy and electron and X-ray diffraction techniques. The films were poly crystalline; the preferred orientation and crystallite size increased with film thickness, substrate temperature, and deposition time. The CdS films consisted primarily of hexagonal-phase material, in contrast to similarly prepared CdSe films which have previously been observed to contain mixtures of cubic and hexagonal phases. As-deposited CdS films showed no major dependence of Hall mobility on crystallite size or degree of preferred orientation. Hall mobility and carrier concentration in CdS and CdSe .films were measured at various temperatures; both parameters increased with temperature and yielded activation energies which depended on fabrication conditions. Surface-desorption phenomena and overcoating of the semiconductor with SiO affected the observed electrical properties significantly. THIN films of cadmium sulfide1,2 and cadmium sele-nide3,4 have been employed by various workers as semiconductors in the insulated-gate thin-film field-effect transistor, known as the TFT. These devices are most commonly made by vacuum deposition of all materials onto an amorphous substrate such as glass. A knowledge of the microstructure and electrical properties of semiconductor layers used in the thin-film transistor is essential in order to form a realistic model for the device and to improve its performance, reproducibility, and reliability. This paper will describe studies of the physical properties of vacuum-deposited CdS and CdSe films prepared under various conditions. Structural characteristics examined in- cluded phases present, crystallite size, nature of preferred orientation of crystallites, surface roughness, and structural homogeneity throughout the film thickness. Electrical properties measured were Hall mobility and conductivity and their dependence on temperature and ambient. Thin-film properties are affected by many fabrication parameters including purity and physical form of evaporant, deposition rate, film thickness, design and temperature of the evaporation crucible, geometry of the deposition chamber, nature of the residual atmosphere, composition and temperature of the substrate, and details of postdeposition processing. PREPARATION OF FILMS In this work the semiconductor films were deposited in a conventional oil-diffusion-pumped system with pressures in the 10-8 torr range. The CdS evaporant was obtained from the Eagle-Picher Co. as a high-purity coarse-grained crystalline powder; the CdSe was a high-purity sintered powder supplied by the Harshaw Chemical Co. The evaporation crucible was a resistance-heated molybdenum-wire basket coated with aluminum oxide and filled with a quartz wool plug at the top. The source to substrate distance was usually 10 cm. This region was enclosed by a Pyrex inner cylinder. The substrate was heated with an overlying Pyrex plate coated with tin oxide. The substrate temperature was controlled using a thermocouple attached to the lower side of the heater. This thermocouple was calibrated against another thermocouple attached to a dummy substrate and by observation of melting points of various metal films deposited in the system. The substrates were polished borosilicate glass plates and conventional glass microscope slides. Substrate preparation included cleaning with an ultrasonically agitated detergent bath followed by isopropanol-vapor de-greasing. Film thickness was measured interferomet-rically during and after deposition. STRUCTURE OF CdS FILMS Structural studies were performed on CdS films using electron diffraction, electron microscopy, and

Jan 1, 1967

By Charles Albert Ashburner

THE stratigraphical geology of the vicinity of Buffalo has always been of great interest on account of its bearing on the origin and history of the Niagara-river gorge, between the Falls and Lake Ontario. Recently, however, the character and thickness of the strata which underlie Buffalo have acquired more practical and economic importance on account of their relation to the possible occurrence of natural gas in commercial quantity near the Niagara river. In a paper presented at the Duluth meeting (l887), on " Petroleum and Natural Gas in New york State" (Trans., xvi., 906), I gave a brief description of the four wells which had been drilled by the Buffalo Cement Company between 1883 and that time. One of these wells is 1305 fret deep; and, at the time that my paper was finally revised for the Transactions (June, 1888), it was still an open question whether the drill in this well had reached the Niagara limestone, or had penetrated the Medina sandstones and shales, which latter are boldly exposed in a number of localities in the district, hut more particularly along the Niagara river in the vicinity of Lewiston and Qneenstown. The difficulty in this geological question at Buffalo has lain in the fact that no reliable determination could be made of the thickness of the strata included between the Corniferous limestone, immediately below which the drilling of the Buffalo gas-wells was commenced, and the Niagara limestone. On the other hand, the strata included between the latter limestone and the middle portion of the Medina sandstones and shales, have been minutely measured and studied in the Niagara gorge below the Falls by many American and European geologists. The first reliable section of these strata was constructed by Professor Eaton, and published in 1824 in his report on the Geological and Agricultural Survey of the District adjoining the Erie Canal. This section, extending from Lake Erie to Lewiston, is complete, with the exception that no thickness is given to the Salina or Onoudaga salt group,

Jan 1, 1889

By John A. Mathews

D R. CHARLES W. ELIOT, the great educator and philosopher-he of the five-foot book shelf-recently gave expression to a thought I had long been cherishing as a private opinion, when he said: "It is obvious that standardization has become a dangerous adversary of progress in both education and industry." This idea must have been more widespread than either of us knew, for some five years ago a writer of verse for one of the comic papers dealt with it at great length. I will quote only a few of his stanzas to illustrate his understanding of "A Standardized Existence" : A visitor at large, I stand Beneath a standard sky- Where everything is standardized To please the standard eye. Each tree is of a standard height, Each building is the same; Each man is uniform in height, And has a standard name. Above there is a standard star Beside a standard cloud, And a standard weather here prevails To please a standard crowd. With standard joy, and standard gain, The standard people live; And if there is one bit of pain T?is such as standards give.

Jan 1, 1926

By Robert Forsyth

As the latest plant on a large scale, the new Bessemer works of the North Chicago Rolling Mill Company, at South Chicago, presents some features of interest to steel-makers, I have ventured to lay before the Institute a short description of that plant, and some* remarks upon the practice there. At the time the South Chicago works were designed the adoption of the basic process in this country seemed imminent. Experience in Europe had demonstrated the perfect success of the process technically, and the question of its commercial value was one which, for any particular works, would have to be settled by its special advantages for procuring the necessary ores and basic materials. Under the circumstances, it was thought best at South Chicago to so arrange the plant as to allow the introdnction of the basic whenever it became advisable, and to make such other changes from the standard type of Bessemer plant as the state of the art seemed to demand and to foreshadow. As the use of metal direct from the blast furnace, while generally condemned by experts here, was in such successful practice in Europe (particularly in connection with the basic process), there was no doubt about its feasibility, while its economy in fuel and labor made it especially attractive to the Western manufacturer. It was accordingly decided to build a direct-metal plant adapted to the basic process. The ingots made were to be rolled into rails at one heat, and were to be of such size (12 inches square and long enough for three and four rails) as to be readily and quickly handled by the rolling machinery proposed. This small size of ingots, and the large number cast from each heat of 10 tons, made it necessary to provide a good deal of room in the casting-pit—much more than in any previons plant—and to put down extra facilities for handling ingots. To meet the delays incident to the basic process—to insure that one vessel should be always blowing if necessary, and to provide opportunity for current repairs to linings, etc.—it was decided that three vessels should be used, and, to properly concentrate the work of

Jan 1, 1884

By AIME AIME

ON Thursday, Oct. 9, oil men from far and wide gathered at Beaumont, Texas to participate in a three-day celebration of the fortieth anniversary of the completion of the famous Lucas gusher well at Spindletop field just south of Beaumont, and to pay tribute to Anthony F. Lucas, for whom the Lucas Medal of the A.I.M.E. is named. In the afternoon the gathered host drove to the site of the discovery well to dedicate a 58-ft. granite monu¬ment erected on the spot where the original derrick stood. Representatives of the A.I.M.E. took a prominent part in the dedication ceremonies, giving the two principal addresses of the afternoon's program. Everette DeGolyer, past President, paid a personal tribute to Capt. Lucas, as a pioneer producer, an engineer, and a friend and well wisher of all young engineers. He gave a splendid picture of the useful and full life of Capt. Lucas who always took a great interest in the activities of the Petroleum Division of the Institute, from its inception to the time of his death.

Jan 1, 1941

By N. C. Nissen, J. A. Thomas, A. Illis, K. N. Subramanian

Successful miniplant and laboratory testwork has indicated that high purity selenium can be produced from copper refinery slimes. The recovery technique fits into existing unit operations, and the selenium recovery in the new process was close to 99%. This recovery virtually eliminated any selenium being processed through the smelting stage. In addition, miniplant tests conducted at Inco Metals Co.'s J. Roy Gordon Research Laboratory in Mississauga, Ontario, have demonstrated the reliability of the process with respect to extractions, product quality, filtration characteristics, and effluent disposal. Inco's copper refinery at Copper Cliff, Ontario, produces about 500 t/d of copper with the anode slimes fall typically averaging 0.5% of the throughput. Investigations relating to the treatment of slimes within Inco's R&D have been conducted on several occasions since 1959, when the available alternatives such as acid or alkaline pressure leaching, aqueous or high temperature chlorination, roasting, smelting, etc., were considered. Interest in slimes processing was revived recently to meet increasingly stringent environmental standards and to replace equipment of a relatively old plant.

Jan 11, 1978

By Douglas J. Harvey

The surface tension of lead-tellurium alloys (in the range 0 to 6.70 at. pct Te) ad lead-arsenic alloys (in the range 0 to 10.53 at. pct As) has been examined by the maximum bubble pressure method. The surface tension of high purity lead can be expressed over a range of temperatures (M.P. to 750°C) by the relationship = 512 — 0.133t. Arsenic and lellurium were both found to be surface active in lead. The surface excess concentration at 700°C was .found to be constant at 0.74 x 10-10 moles per sq cm for tellurium. The surface excess of arsenic at 700°C varied between 0.26 x 10-10 moles per sq cm at 0.16 at. pct to 1.5 x 10-10 moles per sq cm at 8.3 at. pet. The surface tension of lead has been investigated sporadically over the last 90 years. The first recorded study was made by Quincke1 who used a rather crude application of the drop-weight method. Hogness2 obtained the first reliable value for the surface tension of lead by measuring the pressure necessary to force the liquid metal from the end of a small capillary of known radius. Hogness gives the empirical formula: ?(surface tension)= 444 - 0.077 (l-327) which describes the relationship between surface tension and temperature ("C); This work was followed by that of Bircumshaw3 who applied the two-capillar maximum bubble pressure method of Sugden.4 The values published by Bircumshaw are in good agreement with those found by Hogness. Matuyama5 examined the surface tension of lead by the drop weight method. However, the values found are somewhat higher than those previously reported. More recent investigations by Greenaway6 and by Melford and oar' have resulted in data which are not in close agreement, but which are well within the expected range at most temperature levels. The study of the surface tension of lead alloys began with Drath and sauerwald8 who examined the lead-bismuth system. They found that the surface tension values of the alloys in this system deviated only slightly from the ideal mixture rule. Matuyarna5 examined the lead-antimony system. Bircumshaw the lead-tin, and the lead-indium system was studied by Hoar and Me1ford.10 The results of these investi- gations are summarized in Fig. 1. It may be seen that the data vary only slightly from the ideal mixture rule. As none of the metals studied and reported in the literature has a very interesting effect on the surface tension of lead,*the next logical step might be to examine the effect of metals of low solubility or nonmetals having some liquid solubility. Baes, and Kellogg11 have pointed out that the elements most likely to be surface active in liquid metals are ones of limited solubility in the liquid state and possessing weak intermolecular bonding forces in the solid state. Therefore, Group V, VI and VII nonmetals are most likely to be surface active. It was decided to examine the effect of a borderline metal, arsenic, and a nonmetal tellurium. Arsenic forms a eutectic with lead having a melting point of 290°C and a composition of 6.9 at. pct As.13 Pure arsenic sublimes when heated above 610°C. Even though alloying with lead lowers the vapor pressure, fumes containing arsenic are evolved at a very noticeable rate when lead-arsenic alloys are heated above 650°C. Tellurium raises the liquidus temperature of lead sharply to 904°C,14 the melting point of PbTe (lead-telluride). The solid solubility of tellurium in lead was determined by Greenwood and worner15 to be 0.0007 at. pct at room temperature. EXPERIMENTAL METHOD Surface Tension Measurement—The two capillary maximum bubble pressure method for measuring surface tension developed by Sugden,4 and used later

Jan 1, 1962

By D. R. Hanson

The acoustic vibrational spectra of impacted rock slabs were examined at the Denver Research Center, US Bureau of Mines, in an attempt to characterize the behavior of partially detached mine roof rocks. The ultimate goal of this study was to develop a technique or instrument that could provide a quick, accurate, quantifiable measure of mine roof stability. The power spectra of unstable rock slabs were found to contain more energy in the range of 200 to 1000 Hz than solid rock. Comparison of the power contained between 500 and 1000 Hz with that between 3000 and 3500 Hz provided a quantitative measure of rock stability. A lightweight prototype field instrument was designed, constructed, and field tested. This battery-powered instrument computes the power contained in the two frequency bands, compares their magnitude, and displays a number related to the stability of the block tested. Field tests showed the instrument provided reliable measurements of block stability even under conditions of noise that would have seriously degraded the accuracy of the standard methods of roof sounding.

Jan 1, 1986

By Elmer W. Pehrson

Minerals have played a prominent role in the affairs of man and nations since time immemorial but with the advent of the industrial revolution, expanding use of the products of the mineral kingdom became synonymous with the material progress of mankind. Individuals and business groups have recognized this fact so have been aggressive in searching for and utilizing mineral resources, with notable success. Indeed, their achievements are primarily responsible for the present Machine Age. On the other hand, until recently the body politic has failed to grasp fully the essentiality of minerals although, at times, access to mineral supplies has been an important factor in the political maneuvers of nations. This chapter is concerned primarily with the broader political and economic relationships of mineral resources to the world economy, and with the internal and external actions of nations in the field of minerals. Many factors that condition the mineral economy of regions and the world as a whole, influence the internal and external affairs of individual nations. The more important of these are: 1. The nature of man's dependence on minerals. 2. The problems resulting from the unique characteristics of mineral occurrence. 3. Geopolitical concepts. 4. Minerals and world power. Actions of individual nations affecting their mineral economy seek two basic objectives: 1. Attainment and maintenance of prosperity. 2. Military security. Other objectives may be cited but on careful analysis they become integral parts or extreme phases of the two points noted above. For example, the twentieth century aggressions of the USSR, Germany, Italy, and Japan might be considered as direct bids for world power but they also can be interpreted as exaggerated or mistaken efforts toward military security and peacetime prosperity. Similarly, trade barriers, nationalization of industries, foreign exchange manipulations, taxation, monopolistic prac-

Jan 1, 1964

By Herman Poole

WHEN finely divided ferrous sulphide, FeS, is roasted at a moderate, carefully regulated temperature, the iron and sulphur are oxidized, the first products being probably ferrous oxide and sulphurous acid. In the presence of oxygen of the air the ferrous oxide soon becomes ferric oxide and in the presence of oxygen and the ferric oxide the sulphurous acid oxidizes to sulphuric acid. These facts are well known, having been established by Plattner many years ago. As a further reaction, some of the sulphuric acid parts with a portion of its oxygen to oxidize more ferrous oxide to ferric oxide, and a portion of it escapes uncombined or else unites with the iron oxides to form sulphates. Ferrous sulphate is usually soon oxidized to ferric sulphate and if the heat becomes sufficient this is then decomposed into sulphuric acid and ferric oxide. As a result of these reactions a mass of more or less pure ferric oxide is formed which is generally made porous by the escaping gases and, if rabbled properly, practically all the sulphur is expelled. If ferric sulphide or ordinary pyrites, FeS2, is roasted, a portion of the sulphur sublimes and usually burns to form sulphurous or sulphuric acid, although at times and under favorable conditions some of the sulphur is driven off uncombined and can be collected as such. Under ordinary methods of roasting, however, only a small portion escapes combustion. By the combustion of the sulphur an increase of heat is de¬veloped and, as a consequence, the reactions mentioned take place more rapidly and actively-more sulphuric acid is formed and the oxidation is more complete-nearly all the iron being left as ferric oxide with practically no sulphate or ferrous oxide. When the iron sulphide is in lumps the roasting proceeds generally as with fines, but with some changes due to mass. The

Sep 1, 1905

By E. Martinez

Samples of chrysocolla, a hydrated copper silicate, from several sources were submitted to differential thermal analysis (DTA) and thermal gravimetric analysis (TGA). Pure samples of chrysocolla are difficult to obtain, but comparison of the thermograms revealed that certain reactions occurred in all the samples and it is believed that these are due to chrysocolla. Endothermic reactions occurred at 50' to 175°C, 350° to 650°C, and 980° to 1100°C each of which caused a weight loss. The first was due to loss of absorbed water, the second to a dehydroxyla-tion, and the last to conversion of cupric oxide to cuprous oxide. In addition, two exotherms were detected at 685° to 695°C and 935° to 950°C. Infrared spectra of heated samples indicated the exotherms were due to changes in the Si-O bonds leading to the formation of cristobalite. The results suggest that thermoanalysis may be a more sensitive and reliable method for detection and identification of chrysocolla than X-ray diffraction, infrared spectroscopy, or optical techniques. The recovery of copper from oxide ores has been the subject of much research in recent years. One of the principal oxide copper minerals is chrysocolla, a hydrated copper silicate. The information available indicates that it has widely varying properties depending on the origin of the sample. Chrysocolla usually is found associated with cuprite, malachite, azurite, and native copper. Most of these other minerals are recoverable by present day flotation practice, but chrysocolla is lost in the tailings.1,2 Reagent combinations that are successful in laboratory chrysocolla flotation with ore from one source have been found to be ineffective with another. 3 The copper segregation process offers an altemative to beneficiation of oxide copper ores.4'5 The process is of particular interest in processing ores that cannot be treated by conventional hydrometal-lurgical methods because of high acid consumption.6 Fuller understanding of the properties of chryso- colla may prove of value in the search for improvements in both the flotation and segregation processes. Chrysocolla samples from Arizona, Nevada, Chile, Australia, and South Africa were studied by differential thermal analysis (DTA) and thermal gravimetric analysis (TGA). In addition, a sample from Miami, Ariz., was submitted to X-ray diffraction, infrared spectrophotometry, and surface area determination. EQUlPMENT Differential thermal analysis (DTA) detects, amplifies, and records exothermic-endothermic reactions occurring in a sample as its temperature is raised at a constant rate, usually 10°C per minute. A unit made by the Robert L. Stone Co. was used in this study. The tests can be run if desired with a gas streaming through the sample. A thermobalance records weight losses or gains in a sample as its temperature is raised at a uniform rate. The gravimetric analyses (TGA) were run on a Chevenard thermobalance converted electronically for graphic recording. A heating rate of 5°C per minute up to 1100°C was used in these tests. A Perkin Elmer Infrared Spectrophotometer, Model 221, was used with sodium chloride optics obtaining IR spectra in the 2 to 15 region. A pressed pellet technique with potassium bromide was used in preparing the samples. DESCRIPTION OF SAMPLES Chrysocolla is found in the oxidation zones of copper deposits commonly associated with malachite, azurite, and limonite. It is described as varying in composition and in color from bluish green to brown or black. Inclusions of other minerals are usual so chemical analysis of chrysocolla samples may be suspect. However, it is considered by many to be a solid solution of CuO, SiO2 and H2O with a general formula of CuO.SiO2.2H2O or 2CuO.2SiO2. 3H20. Chukhrov7 has described a sample from the Urals as CU3,5(OH)2 (A1Si3) O10.nH2O and stated that chrysocolla is a montmorillonite-type mineral. On the basis of X-ray analyses, DTA, and infrared spectra of chrysocolla from the Inspiration Mine, Ariz., Sun8 concluded that there was no substantial evidence to classify it as a montmorillonite mineral. Chrysocolla samples from many sources throughout the world were used in this investigation. The following is a brief description of each:

Jan 1, 1963

By D. B. Myers

The consistent upward trend in crude oil production prevailing in California throughout the greater part of 1929, was effectively checked in November by a curtailment program instituted by mutual agreement between operators in four of the major fields. This program artificially reduced daily production to approximately the same daily figure as prevailed in December, 1928. The large amount of deep drilling during the later part of 1928 and during 1929 has established a potential, however, which is far in excess of refinery needs in the state. Low prices for crude oil which prevailed in California during 1928 continued during 1929. General curtailment continued in the older fields in San Joaquin Valley. The number of wildcat and exploratory wells drilled throughout California was materially increased, but no major field was discovered unless the recent bringing in of the Ohio Oil Co.'s Recreation Gun Club No. 1 well, near Venice in Los Angeles Basin, during the closing days of 1929 results in such a field. Significant developments during 1929 were: (1) The discovery of three deeper zones in the Santa Fe Springs field known as the O'Connell, Clarke, and Hathaway; (2) Kettleman Hills development and unanimous agreement to restrict production; (3) developments along the Santa Barbara Coast and the drilling of tideland permits; (4) extensions of some of the older producing areas in the San Joaquin Valley; (5) the Lawndale and Santa Barbara Mesa structures, the former discovered in Los Angeles Basin in 1928, the latter in Santa Barbara County in 1929, proved to be failures; (6) intensive exploration throughout the state and the drilling of a large number of deep wildcat wells; (7) discovery of oil by the Ohio Oil Co. in the Los Angeles Basin at Venice; (8) Long Beach and Ventura Avenue fields maintained steady production throughout the year. As a natural sequence to the discovery of high-gravity oil fields in Kettleman Hills and at Elwood in 1928, a tremendous amount of exploratory work was done in 1929 in areas underlain by rocks of lower Miocene age, particularly along the Santa Barbara Coast area, the San Joaquin Valley, and the Salinas Valley, where the Vaqueros and Temblor sands were considered to hold possibilities for production.

Jan 1, 1930

By J. R. Cahoon, H. W. Paxton

The mechanical properties of unidirectionally solidified A1(rich)-Mg and A1(rich)-Cu castings containing up to 15 wt pct solute have been determined with re -spect to the volume fraction of interdendritic eutectic. Pioperties were determined in the directions pumllel and Perpendicular to that of solidification; the volume fraction of eutectic was varied between the "as-cast" and equilibrizcm amounts by approperiate heat treatment following solidification. The principles of fiber strengthened composites and dispersion strengthened materials are adapted to explain the mechanical properties of these castings. It is generally accepted that castings often have inferior mechanical properties when con~pared to wrought products. However, there is little quantitative data available concerning the factors which make apparently sound castings weak and/or brittle. The relative ease and inexpensiveness of the casting process have always been attractive and, therefore, an understanding of the factors which contribute to the mechanical properties of castings would seem desirable. Such an understanding may lead to an improvement in the mechanical properties to an extent where castings would become competitive in applications where presently only wrought products are considered to have the requisite properties. Such an understanding could also improve the reliability of present cast products. Much of the recent research on castings has centered about determining the extent of segregation in cast alloys. Macrosegregation, particularly inverse segregation, has been studied in some detail 1-8 and a considerable understanding of microsegregation has been obtained.9'10 The effect of solidification rate on dendrite spacing and on the amount of interdendritic eutectic in binary alloys has been established, particularly for Al(rich)-Cu alloys.""0 However, the extension of these ideas to relate the amount of interdendritic eutectic, concentration gradients, micro-segregation, dendrite spacings, and so forth, to the rnechanical properties has been limited. Dean and spear" have related the mechanical properties of an Al-Si-Mg alloy, A356-T62, to the dendrite spacing and have shown that the mechanical properties improve with decreasing dendrite spacing. Passmore et al.12 have shown that annealing at high temperature improves the mechanical properties of Al(rich)-Cu al- loys and Archer and Kempf 13 have shown that an Al-1 pct Mg-1.75 pct Si alloy behaves in a similar manner. Ahearn and Quigley 14 have shown that high temperature homogenization also enhances the mechanical properties of an SAE 4330 steel. However, in the above investigations, no underlying reasons were suggested for the improvement in mechanical properties. The purpose of the present investigation is to relate the mechanical properties of castings to some of the solichfication variables and to derive some equations by which calculations of the mechanical properties may be attempted. In particular, the effect of the amount of interdendritic eutectic and the effect of stress direction with respect to that of solidification on the mechanical properties will be considered. The Al(rich)-Mg and Al(rich)-Cu binary alloy systems were chosen for study. The A1-Mg system was chosen because its constitutional relationships are such that large volunles of eutectic (up to 24 vol pct) may be obtained in the as-cast condition and then be completely dissolved by subsequent heat treatment at about 440°C. This allows a comprehensive study relating the mechanical properties of castings to the amount of interdendritic eutectic. Also the Al(rich)-Mg eutectic is almost a single phase 15 which should make the experimental results more amenable to theoretical interpretation and calculation. The A1-Cu system was chosen for study because of the large amount of related information available concerning segregation, dendrite spacing, and so forth. Unidirectionally solidified castings were used throughout the investigation so that the effect of solidification direction with respect to the direction of applied stress could be determined. THEORETICAL It is well known that upon solidification of binary alloy castings, the nonequilibrium amount of eutectic which forms is given by 10 where fe o is the weight fraction of eutectic, Cs is the solid solubility of solute at the eutectic temperature, k is the equilibrium partition coefficient, and C, is the average composition of the alloy. In the development of Eq. [I], it is assumed that the effects of inverse segregation and diffusion in the solid are negligible, and that no porosity is present. If the casting is homogenized at a high temperature for a long period of time, some (or all) of the eutectic is dissolved and the amount of eutectic for this "equilibrium" condition may be calculated directly from the constitutional diagram. By appropriate intermediate annealing, the

Jan 1, 1970

By Fred C. Bond

MANY grindability tests have been made in the Allis-Chalmers laboratory since the tabulated results were last published.1 The lists of standard ball-mill and standard rod-mill grindability tests are brought up to date in this paper, and considerable new material is added. This includes a tabulation of open-circuit grinding tests, with impact and compression-crushing tests. The standard ball-mill grindability tests (Table I) were made in a standard laboratory ball mill, 12 by 12 in. inside, running at 70 rpm, with a charge of 285 iron balls ranging from 1 1/2 to 3/4 in. in diameter and weighing 20,125 grams. Seven hundred cubic centimeters of minus 6-mesh stage-crushed dry feed was used, and the circulating load was maintained constant at 250 pct by adjusting the number of mill revolutions for each grinding period. Tests were made at all mesh sizes from 28 to 200, and the grindability is the number of net grams of screen undersize produced per revolution. The table includes 479 tests. It has been calculated that the ball mill does 52.3 joules of useful work on the ore per revolution2 with 93 joules input to the mill. The standard rod-mill grindability tests (Table 2) were made in a laboratory tilting rod mill, 12 in. in diameter by 24 in. long inside, with a wave-type lining, running at 46 rpm. The grinding charge consisted of six 1 1/4-in. diameter and two 1 3/4-in. diameter steel rods, all 21 in. long and weighing 33,380 grams. The mill was rotated level for eight revolutions, then tilted up 5° for one revolution, down 5° for one revolution, and returned to level for eight revolutions. It was discharged by tilting downward at 45° for 30 revolutions. Feed consisted of 1250 cc of minus 1/2-in. stone and the circulating load was maintained constant at 100 pct by adjusting the number of mill revolutions for each grinding period. Tests were made at all mesh sizes from 3 to 65, and the rod-mill grindability is the number of net grams of screen undersize produced per revolution. The table includes 105 tests. The impact and compression-crushing tests (Table 3) are given in a table that is an extension of a previous publication3 in which the method of testing was described in detail. Two equal hammers weighing about 30 lb each were arranged to strike simultaneous blows on opposite sides of the test specimen. Broken pieces of rock passing a 3-in. square and retained on a 2-in. square were set up with the smallest dimension between the hammers, and this distance was measured. The height of the hammers was increased slightly before each blow until the specimen broke, and the foot-pounds per inch of thickness was calculated. Ten pieces

Jan 1, 1947

By Joseph D. Weeks

Manganese has, until recently, been most highly esteemed as a good thing to keep out of steel. Its value in the process of mannfacture has been fully recognized, but after it has played its part in the crucible or the converter, then the less of it the better. It is true that the mission of this metal and its influence upon the character of steel has been a source of much controversy. Our own Holley, in one of his special reports on ferromanganese: I, states that ''it has been suspected by some, and believed by a few, while it is still denied by many, that manganese as an ingredient in steel has not only a body-giving and toughening influence, but a positive neutralizing influence upon any excess of hardening or cold-shortening substances, as phosphorus." In another paper on the same subject he states that " it should appear from such facts as we have that manganese toughens" the structural steels, "increases their soundness and prevents red-shortness." Notwithstanding these rather guarded assertions as to its value, the general belief, it will be found, is with Dr. Siemens, that manganese is " merely a cloak to hide impurities," and its presence in steel has been endured, not welcomed. But whatever may have been the difference in opinion as to the

Jan 1, 1885

By E. T. Hunter

Surrounded by the 13,000-ft high peaks of the San Juan Mountains in southwestern Colo., the town of Silverton is the site of the extensive development operations initiated 20 months ago by Standard Metals Corp. Appropriately termed the Silverton Project, Standard's operation has now passed the half-way point in its program to reopen two mines that were once sizeable producers of copper, lead, and zinc ores.

Jan 1, 1961

By G. M. Schwartz, D. M. Davidson

THE Duluth gabbro outcrops containing sulphides of copper, nickel, and iron are located on both sides of State Highway No. 1 an airline distance of 8.5 miles southeast of Ely in northeastern Minnesota. The region of known sulphide occurrences includes parts of sections 5, T. 61 N., R. 11 W., and parts of sections 25, 26, 32, 33, and 34, T. 62 N., R. 11 W. These sections, given in Fig. 1, are all in Lake County, Minnesota. Part of the area, which lies entirely within the Superior National Forest, is shown on the topographic map of the Ely quadrangle. The original discovery was made in 1948 when a small pit was opened in weathered gabbro rubble for use on a forest access road. A shear zone had caused unusual decomposition in this glaciated area, and the resulting copper stain was noted by Fred S. Childers, Sr., an Ely prospector, who began searching the outcrops along the base of the intrusive. He was joined in further exploration by Roger V. Whiteside of Duluth. In the summer of 1951 a small diamond drill was moved into the area and a hole 188 ft deep was drilled, passing through 11 ft of glacial drift into sulphide-bearing gabbro. This paper is a preliminary report on the geology of the newly discovered ore. The Duluth gabbro is one of the largest known basic intrusives and may be defined as a lopolith.' It extends northeastward from the city of Duluth as a great crescent-shaped mass that intersects the shore of Lake Superior again near Hovland, 130 miles to the northeast, see Fig. 2. The distance around the outside of the crescent is nearly 170 miles. The form of the intrusive is simple at Duluth where it ends abruptly north of the St. Louis River; at the east end, however, the gabbro splits into two elongated, sill-like masses separated mainly by lava flows and characterized by minor irregularities. The outcrop reaches a maximum width in the central part where it is about 30 miles across, and a maximum thickness of about 50,000 ft. It may be significant that the sulphides occur at the base of the thickest part. The lopolith has segregated into rock types ranging from peridotite to granite. The most abundant types are olivine gabbro, gabbro, troctolite, anortho-site, and granite. Of lesser importance quantitatively are peridotite, norite, pyroxenite, magnetite gabbro, and titaniferous magnetite. Grout estimates that two-thirds of the gabbro at Duluth is olivine gabbro. Variations in the percentages of plagio-clase, augite, olivine, and magnetite-ilmenite constitute the only essential differences found among the basic rock types. The predominant mineral is plagioclase, mainly labradorite. Plagioclase and olivine seem to have crystallized early, and the olivine rich rocks, usually troctolite, are found in the lower part. Segregations of titaniferous magnetite are abundant near the base of the gabbro along the eastern part and also occur far above the base. These have recently been described in detail by Grout.' Near the top, segregation has produced a gradation to granite, or "red rock," as it is known locally. This consists of quartz, red feldspar, and hornblende. The red rock forms a zone with a maximum width of nearly 5 miles but is quantitatively unimportant from Duluth northward for 35 miles. In Cook county, where the gabbro splits, each of the two sill-like masses has a red rock top somewhat thicker in proportion to the gabbro below than in the main central mass. The intrusive ranges from coarse to medium in grain size and from granitoid to diabasic in texture. Throughout much of the Duluth gabbro in Minnesota banding and foliation are well developed, as Grout has emphasized.V he bands are mainly a result of variation in the percentage of minerals, as in troctolite with alternating bands high in olivine and in plagioclase. A few bands may consist largely of one mineral, as is true of some segregations of magnetite. Many of the banded rocks show a clearly developed parallelism of platy plagioclase crystals, and both banding and foliation are believed to conform to the floor of the lopolith. Throughout its extent in Minnesota the Duluth gabbro dips east and south toward Lake Superior. It is generally believed to extend beneath Lake Superior and is found as a smaller mass exposed along the north side of the Gogebic district in Wisconsin and Michigan. The dip at and near the base ranges along most of its length from 20 to 40°, but at places the internal banding dips even more steeply. The dip of the upper part is much less, and if it is assumed that the flows along the north shore of Lake Superior are a dependable indication, it does not exceed 15". The formations shown in Table I which are intruded by the gabbro range from Keewatin to Middle Keweenawan in age. They present a significant picture. At the top, the gabbro and its accompanying

Jan 1, 1953

By G. M. Schwartz, D. M. Davidson

THE Duluth gabbro outcrops containing sulphides of copper, nickel, and iron are located on both sides of State Highway No. 1 an airline distance of 8.5 miles southeast of Ely in northeastern Minnesota. The region of known sulphide occurrences includes parts of sections 5, T. 61 N., R. 11 W., and parts of sections 25, 26, 32, 33, and 34, T. 62 N., R. 11 W. These sections, given in Fig. 1, are all in Lake County, Minnesota. Part of the area, which lies entirely within the Superior National Forest, is shown on the topographic map of the Ely quadrangle. The original discovery was made in 1948 when a small pit was opened in weathered gabbro rubble for use on a forest access road. A shear zone had caused unusual decomposition in this glaciated area, and the resulting copper stain was noted by Fred S. Childers, Sr., an Ely prospector, who began searching the outcrops along the base of the intrusive. He was joined in further exploration by Roger V. Whiteside of Duluth. In the summer of 1951 a small diamond drill was moved into the area and a hole 188 ft deep was drilled, passing through 11 ft of glacial drift into sulphide-bearing gabbro. This paper is a preliminary report on the geology of the newly discovered ore. The Duluth gabbro is one of the largest known basic intrusives and may be defined as a lopolith.' It extends northeastward from the city of Duluth as a great crescent-shaped mass that intersects the shore of Lake Superior again near Hovland, 130 miles to the northeast, see Fig. 2. The distance around the outside of the crescent is nearly 170 miles. The form of the intrusive is simple at Duluth where it ends abruptly north of the St. Louis River; at the east end, however, the gabbro splits into two elongated, sill-like masses separated mainly by lava flows and characterized by minor irregularities. The outcrop reaches a maximum width in the central part where it is about 30 miles across, and a maximum thickness of about 50,000 ft. It may be significant that the sulphides occur at the base of the thickest part. The lopolith has segregated into rock types ranging from peridotite to granite. The most abundant types are olivine gabbro, gabbro, troctolite, anortho-site, and granite. Of lesser importance quantitatively are peridotite, norite, pyroxenite, magnetite gabbro, and titaniferous magnetite. Grout estimates that two-thirds of the gabbro at Duluth is olivine gabbro. Variations in the percentages of plagio-clase, augite, olivine, and magnetite-ilmenite constitute the only essential differences found among the basic rock types. The predominant mineral is plagioclase, mainly labradorite. Plagioclase and olivine seem to have crystallized early, and the olivine rich rocks, usually troctolite, are found in the lower part. Segregations of titaniferous magnetite are abundant near the base of the gabbro along the eastern part and also occur far above the base. These have recently been described in detail by Grout.' Near the top, segregation has produced a gradation to granite, or "red rock," as it is known locally. This consists of quartz, red feldspar, and hornblende. The red rock forms a zone with a maximum width of nearly 5 miles but is quantitatively unimportant from Duluth northward for 35 miles. In Cook county, where the gabbro splits, each of the two sill-like masses has a red rock top somewhat thicker in proportion to the gabbro below than in the main central mass. The intrusive ranges from coarse to medium in grain size and from granitoid to diabasic in texture. Throughout much of the Duluth gabbro in Minnesota banding and foliation are well developed, as Grout has emphasized.V he bands are mainly a result of variation in the percentage of minerals, as in troctolite with alternating bands high in olivine and in plagioclase. A few bands may consist largely of one mineral, as is true of some segregations of magnetite. Many of the banded rocks show a clearly developed parallelism of platy plagioclase crystals, and both banding and foliation are believed to conform to the floor of the lopolith. Throughout its extent in Minnesota the Duluth gabbro dips east and south toward Lake Superior. It is generally believed to extend beneath Lake Superior and is found as a smaller mass exposed along the north side of the Gogebic district in Wisconsin and Michigan. The dip at and near the base ranges along most of its length from 20 to 40°, but at places the internal banding dips even more steeply. The dip of the upper part is much less, and if it is assumed that the flows along the north shore of Lake Superior are a dependable indication, it does not exceed 15". The formations shown in Table I which are intruded by the gabbro range from Keewatin to Middle Keweenawan in age. They present a significant picture. At the top, the gabbro and its accompanying

Jan 1, 1953