Search Documents

By Frank Wartman

RECENTLY Horace Freeman1 obtained a patent on a successful method of conducting a roasting procedure described as to general features by Carl Schnabel2 almost forty years ago. Essentially, the Freeman process of roasting consists in introducing the finely powdered sulfide mineral, suspended in air or any other suitable gaseous medium, into the upper portion of a heated chamber. The stream of suspended particles is directed vertically downward. A counter-current stream of gas introduced at the bottom of the chamber flows upward. The mineral particles are oxidized as they fall through the heated atmosphere of the chamber. All air required for the oxidation may be admitted either at the top or the bottom of the chamber, or may be divided between the top and bottom inlets in any desired proportion. Heat may be recovered by passing the gases leaving the furnace through a waste-heat boiler or other form of interchanger. In speaking of the results obtained in roasting pyrite, Freeman says:3 Steam yield from the boiler exceeds 1 pound of steam per pound of pyrite con-sumed, which pays the cost of operation of the burner. The oxide produced is in the form of fused particles or hollow shells of magnetite, containing about 65 per cent of iron. It contains the gangue material ordinarily produced in flotation concentrate, of course, but it is being found that most of this can be eliminated by magnetic separa-tion, and that the sulfur content, as consistently produced, is below 0.2 percent. This material is especially interesting as a high-grade iron ore, free from phosphorus and low in sulfur. It may be sintered or briquetted. It is even more interesting as a raw material for sponge-iron production, to be directly smelted in electric furnaces without the usual cooling of the iron powder and magnetic separation between the reducing kiln and the electric furnace.

Jan 1, 1933

By R. P. Alger, C. A. Doh, M. P. Tixier

The principle, the equipment and field operation of sonic logging are described. The tfio-receiver system produces logs independent of hole size and mud. Field experience is given and forms the basis for the interpretation of the log. The derivaiion of porosity values from measured velocities is discussed, according to the type of formations (hard formations, compacted sands, and unconsolidated formations). The time-average equation proposed by M. R. J. Wyllie, A. R. Gregory and L. W. Gardner is uscd as a basis for the computation of porosity in limestones, cemented sandstones and compacted sands. Variations in the lithologic character of limestones do not seem to change the porosity calibration markedly. The compaction of sands is related to the compaction of shale adjacent to them; and, thus, the shale velocity is used for the establishtnent of empirical relations for the computation of porosity in un-consolidated formations. Various forrnu.las are tentatively presented to account for shale and fluid content. Field experience demonstrates that considerable attenuation of sonic energy takes place in unconsolidated formations, particularly when gas bearing, and in fractrured formations. Unusually large attenuation produces skipped cycles, a feature easily recognized. The application of sonic logging to structura1 studies is featured, showing its possible integration with the dipmeter. Correlation and its application to the irrterpretation of seisrmic surveys are reviewed. The paper is illustrated with field examples. Sonic logging is the recording of the time required for a sound wave to traverse a definite length of formation. Sonic travel-times are inversely proportional to the speed of sound in the various formations. The speed of sound in subsurface formations depends upon the elastic properties of the rock matrix, the porosity of the formations and their fluid content and pressure. Below the "weathered" or low-velocity layer extending from 50 to 100 ft or so below the surface, sound velocities may range from about 6,000 ft/sec in shallow shales to as much as 34,000 ft/sec in dolomites. In hard formations (well cemented and/or compacted), the sonic log reflects the amount of fluid in the formations; hence, it correlates well with their porosity. In unconsolidated formations, which are usually of fairly high porosity, the sonic log gives an approach to porosity determination, when its readings are corrected for lack of compaction, shaliness, and fluid content. In such formations the sonic log may also indicate the presence of gas and may distinguish between oil- and water-bearing beds. Field experience with the sonic log in soft formations is more limited than that in hard formations. As a result, interpretation in soft formations is not as well developed at the present time. In all types of formations the sonic log is of considerable value for correlation and for the more detailed and accurate interpretation of seismic data. EQUIPMENT AND PRINCIPLE FIELD OPERATION The basic features of the sonic log" are a two-receiver system and two available short spacings. The log is recorded on film using a standard field unit. An SP curve is run along with the sonic curve to give a more interpretable log and to establish absclute depth control for comparison with other logs run in the same well. If desired, a gamma-ray curve may be recorded simultaneously with the sonic curve. Fig. 1 shows the sonic-gamma ray combination sonde. The sonic portion consists of a sound transmitter and three receivers mounted 3, 4 and 6 ft from the transmitter. When the first and second receivers are used, a sonic log of I -ft spacing (distance between receivers) is obtainea. Use of the first and third receivers provides a 3-ft spacing. The transmitter emits pulses at the rate of l0/sec. After the transmission of a pulse the first arrival of sound energy at each receiver triggers its response system. The differ-

By John I. Yellott

SINCE the days of Newcomen and Watt, when men first sought to turn the energy of fuels to useful purposes, coal-generated steam has supplied most of the power needed for both stationary and mobile applications. The low efficiency and large water requirements of the nineteenth century steam-power plant caused many engineers to turn their thoughts toward more direct means of converting heat into power. As far back as 1791, John Barber secured an English patent on a combination' which he might well have called a "gas turbine." He proposed to generate procducer gas from coal or charcoal, to burn it under pressure in air obtained from a reciprocating compressor, and to drive a turbine wheel with the resultant hot combustion products. With the optimism characteristic of the inventor, he hoped that the turbine would not only operate his compressor but also perform useful work. There is no record that Barber ever built his machine, but if he had done so he would have learned that useful power can result from such a combination only when both turbine and compressor are highly efficient and when the temperature of the gas entering the turbine is not far below 1000°F. Hot-air prime movers continued to attract attention, and both Stirling in England and Ericsson in America2 built reciprocating engines that operated with some success upon coal-heated air. The internal-combustion engine, burning liquid fuels, supplanted the hot-air type, and, for the first time, challenged the supremacy of both the steam cycle and its familiar fuel, coal. LIQUID FUELS COMPETE WITH COAL As the increasing use of the automobile multiplied the demand for gasoline, the supply of residual fuel increased rapidly, and heavy oil declined in price to the point where it became competitive with coal. First in the marine field and later in stationary plants in areas adjacent to refineries, oil began to be widely used. Oil's greater convenience and higher heating value per pound of weight or per cubic foot of bunker space have caused it to take over much of the marine field. The introduction of the highly efficient diesel engine, capable of burning a fuel that is cheaper than gasoline, again threatened the position of coal, for the operating costs of the diesel became directly competitive with those of coal- burning equipment. In isolated power plants and smaller marine installations, the diesel provided the medium by which oil again successfully invaded fields formerly dominated by coal. The diesel engine, provided with an

Jan 1, 1946

By H. C. George

Since 1911, when J. L. Dunn first used compressed air for repressuring depleted oil sands in southeast Ohio, the rejuvenation of many depleted oil fields has been directly due to repressuring by means of air or gas. Developments in repressuring in recent years have resulted in its successful use in the early life of some deep, high-pressure oil fields, conserving the natural gas dissolved in and associated with the oil by returning it to the producing oil sand after it has been compressed above the existing rock pressure of the reservoir. One of the most successful operations of this type is that of the Humble Oil & Refining Co., on the DeWalt salt dome at Sugarland, Texas. I quote from a personal communication with reference to this field: "Structurally, the field is dome-shaped, having a closure of approximately 350 ft. Production comes from a sandy shale interbedded with a clean sand and lying over a cap rock which is about 3400 ft. deep on top of the structure." A feature of the operation of this field is the production of the required amount of oil with the minimum of gas production. Wells on top of the dome have high gas-oil ratios, while those down structure have lower ratios, depending upon the distance of the well from the peak. To date, it has been possible to produce the oil needed from the wells circling the dome above the water zone and below the gas zone, and in this manner the average gas-oil ratio has been kept low. The gas from all separators is turned into a gas system which serves the entire field. From this system, all drilling rigs and utilities requiring gas for a fuel draw their requirements, and the remainder of the gas (about two-thirds of the production) is delivered to a compressor plant which boosts the pressure until it can be returned to the sand at the top of the dome where the rock pressure is 1400 lb, per square inch. "The Sugarland wells produce through 2-in. tubing with a 3/8-in. choke in one wing of the well-head manifold. The pressure builds up as high as 1300 lb, per square inch on the casing while on the tubing it varies from 0 to 900 lb. per square inch, depending upon the amount of gas produced with the oil."

Jan 1, 1931

By William Hutton Blauvelt

The type of gas producer in which the ashes are fluxed and run off as slag was among the very earliest made. Ebelmen built the first one in 1840 at Audincourt, France, only a year after the installation of the first gas producer of which we have record. Charcoal was used as the fuel, with blast-furnace slag and clay as flux. My interest in this type of producer began when as a boy I saw the fluxing producer at Chester, N. J., which was invented by W. J. Taylor, and described by him in 1881.' This producer was invented independently by Mr. Taylor to meet the difficulties he experienced in making producer gas for roasting sulphurous iron ores. It will be of interest to review briefly his description of his producer. It was built like a small blast furnace, having a hearth 24 in. in diameter and 24 in. high. The bosh angle was 25' from the vertical; the diameter at the bosh 4 ft. and at the top 3 ft.; the total height 12 ft. The producer contained one water-cooled tuyere 12 in. above the bottom, with a 1.5-in. nozzle. Depth of the coal above the tuyere, 6 ft. Mr. Taylor mixed the coal with from 30 to 40 per cent. of basic blast-furnace slag to flux the ash. Occasionally some limestone was also used, but never limestone alone, as the use of the furnace cinder gave a larger volume of slag and made it easier to maintain a proper fluidity. The producer was blown with a small Weimer blowing engine, delivering 300 ft. of air per minute, at from 1 to 1.5 lb. pressure. The slag was tapped every 2 hr. and was black and glassy in appearance. Broken or egg size anthracite was used. The fine sizes of anthracite could not be made to work. Mr. Taylor expressed the belief that bituminous coal could be used if not too fine, but no experiments were made with this coal. Runs were made of four weeks' duration, with no stops or changes. Mr. Taylor reported the following advantages: 1. Excellent gas, very uniform in quality. The high fuel bed permitted no air to pass unconsumed, and the gas was almost entirely free from carbonic acid.

Jan 1, 1914

By Paul Weaver

DURING 1932 the amount of geophysical surveying carried out as a part of oil-field development in¬creased, particularly in the Gulf Coast of Texas and Louisiana. Here the most intensive geophysical activity was displayed in the discovery of domes and prospects several years ago, after which there was a period of relative inactivity. This year many of the leases required development and geophysical methods were used to obtain pictures of the detailed structures. These were almost exclusively gravity and reflection-seismograph surveys and for the first time this latter method was generally used by oil operators to construct subsurface contours. The total number of geophysical troops in this territory increased from 16 to 40 during the year.

Jan 1, 1933

By Rudolph Emmel

THE mines operated by the South American Development Co. are located in the Zaruma mining district of southwestern Ecuador. They are near the old mining town of Zaruma, which is the only important city in the canton of the same name. The district is situated in the upper end of a valley lying between two spurs of the Cordillera, one of which may be considered the Coast Range and the other an intermediate range. The mining camp proper, known as Portovelo, and the plant are 2.4 km. south of Zaruma, on the north bank of the Amarillo River, a tributary of the Tumbes River, which flows southwestward through Peru to the Pacific. Portovelo is difficult of access; it is reached from Guayaquil by means of river steamers and muleback. Embarking at Guayaquil, the route is down the Guayas River, across the Jambeli Canal, and up the Santa Rosa River to Santa Rosa, a distance of 177 km. From Santa Rosa, the road or trail follows the Santa Rosa River, then across the summit of the Coast Range into Portovelo, a distance of 74 km.-a two-day trip on muleback. The mining property of the South American Development Co. comprises 297 lode claims and 142 placer claims. The combined lode claims cover an area, roughly rectangular in shape, 9000 m. long from north to south by 4000 m. wide; the northern edge of the rectangle is about 3000 m. north of the central plaza of Zaruma. Mineral lands in Ecuador are held by virtue of an annual tax per claim paid to the central government, no surface rights being included.

Jan 1, 1925

By JOHN R. SUMAN

IT appears now that the conflict with the totalitarian states will be a long-drawn-out struggle. The course of this war up to now indicates that this may well be the first major conflict where man power has not been the vital and determining factor. Mechanized warfare has made it possible for relatively small, well-equipped groups to outmaneuver and defeat large armies which lack the necessary modern equipment. Under these circumstances, ultimate victory becomes a matter of resources and productive ability. The important question is not how many soldiers can he put into the field, but the volume and speed in producing the armaments essential to ensure a victory. The resources available to the opposing nations and the efficiency of their systems of enterprise and production will be primary factors in determining the ultimate outcome. Germany had a head start of eight years in the armament race, and it is not easy to overcome such an advantage overnight.

Jan 1, 1942

By M. S. Burton, G. V. Smith, A. Rosen

The kinetics of re crystallization and the effect of recovery on recrystallization of pure iron were investigated within the temperature range of 517" to 632 OC. Grain growth and activation energies were also studied. Two stages can be distinguished during recrystallization; the first is gvowth-controlled and the second is nucleation-controlled. The extent to which the first stage succeeds before the second stage begins depends on both temperature of recrystallization and temperature of recovery. The softening of cold-worked metals and alloys due to transformation of the deformed crystals to strain-free equiaxed grains during annealing is well-known, and early inestiators established that recrystallization kinetics is strongly influenced by minute quantities of impurities. Generally, it is believed that impurities decrease the rate of recrystallization and the rate of grain growth. To understand the basic phenomena of recrystallization, investigations should be on pure materials. Most of the research on high-purity materials has been on metals having the fee Bcc materials, and especially high-purity iron, have been studied only in recent years. It is known that recovery may influence recrystalliation;" however, no general description of the influence, applicable to all materials, has been presented. This paper presents results of a study of the recrystallization kinetics of high-purity iron, after 60 pct cold deformation by drawing, with particular reference to the influence of recovery on the rates of recrystallization and grain growth. From observations of these rates, conclusions are drawn concerning nucleation. MATERIAL AND EXPERIMENTAL PROCEDURE Preparation of Material. High-purity iron, prepared by zone refining of vacuum-melted electroiytic iron at Battelle Memorial Institute under sponsorship of the American Iron and Steel Institute, was used in this study. Table I gives the reported chemical analysis of the material, taken at a point near the last molten zone and thereby rep- resenting the maximum impurity level for the entire bar. Prismatic specimens, approximately 10 x 10 X 50 mm, were sawed from the 50-mm-diam bar, perpendicular to the zone-refining direction, and turned to cylindrical shape. These specimens were sealed in quartz capsules under vacuum, approximately 10"e mm Hg, austenitized at 930° C for 15 min, slowly cooled, removed from the capsules, and cold-worked in air by swaging to approximately 20-pct reduction of area. The encapsulating, austenitizing, and swaging operations were repeated two additional times, after which the samples were encapsulated, austenitized, and cold-drawn to 60-pct reduction of area. A further vacuum anneal at 630°C for 120 min and cold drawing to 60-pct reduction of area produced wire 2.8 mm in diameter. The drawn wire was electropolished to remove deformed material on the surface, after which it was sawed into 4-mm-long specimens for the recrystallization study. Microscopical examination before the final cold reduction revealed equiaxed grain structure with very fine grains in a thin layer near the surfaces of the specimen and nearly uniform ASTM 3-4 grain size in the center. Recrystallization Heat Treatment. a) Direct Recrystallization of Cold-Worked The 60 pct cold drawn iron specimens were recrystallized at five temperatures, 517, 556, 590°, 612, and 632C, in a lead bath covered with graphite (the temperature was controlled to 1°C). Specimens were treated for twelve different times at each temperature, and all were water-quenched after heat &eatment. b) Recrystallization Following Preliminary Recovery Heat Treatment. After cold working, specimens were sealed into quartz capsules under vacuum, 105 mm Hg, and recovery-annealed at 362", 400", and 440°C for 20 hr prior to recrystallization. No evidence of recrystallization was found

Jan 1, 1964

By C. B. Post, G. V. Luerssen

It is generally recognized that non-metallic inclusions in steel come from two principal sources. First are the chemical reactions in the furnace, or in subsequent deoxidation, resulting in slag which does not free itself from the metal. Much information has been published concerning these chemical reactions and their control through proper attention to slag viscosity, composition of deoxidizers, and other qualities. The studies of this subject by C. H. Herty, Jr. and others through the medium of physical chemistry have yielded much information for the steelmaker. The second source is erosion of ladle refractories, such as lining brick, stoppers, nozzles and runners, causing entrapped particles of globules of fluxed silicate material. In contrast with the large amount of information available on the first source, relatively little has been published on the subject of erosion which, in the case of basic electric melted steel, is the principal source of nonmetallics. This is probably due to the fact that the problem was assumed to be one of simple mechanical erosion, which could be solved primarily by modification of ladle practices. Good improvements have been made by elimination of slurries in the ladle, better ladle and runner refractories, and more attention to pouring temperatures. It is doubtful, however, that this problem has been recognized in its true light since it is not one of simple mechanical erosion but rather one of chemical reaction between the metal and the refractories; and in this sense is as much a problem of physical chemistry as the reactions involved in the actual steelmaking process. The influence of ladle refractories on the resulting cleanness of steels was early recognized by A. McCancel who examined large inclusions in steels made by both acid and basic practices. His chemical analyses showed the large influence exerted by the manganese content of the steel on erosion of the ladle and nozzles used in those days. The presence of MnO in such inclusions led McCance to the hypothesis that both basic and acid steels react chemically with the ladle refractories so that small globules of fluxed refractories are carried in the stream into the molds. This early work of McCance was checked by one of the present authors on basic electric bearing-steel, and it was found that on steels containing as low as 0.40 pct manganese the fluxed surface of the ladle lining after delivering such a heat showed as high as 25 pct MnO by actual analysis. Furthermore, by lowering the manganese content of the steel to 0.20 pct, ladle erosion was decreased with a corresponding decrease in silicate inclusions in the steel. Limitations placed on the manganese content for the required inherent properties made it impossible to pursue this line further, and subsequent attention was concentrated on improved ladle refractories, care in keeping the ladle clean and free from loose refractories up to the time of tapping, and pouring the steel at optimum temperature. Our study of the chemical reactions at the metal-brick interface between steel and ladle refractories was revived in 1939 as a result of an experimental observation made on the cleanness of alloy steels of the SAE types. This observation showed that the relative cleanness of such steels made in basic electric arc furnaces of 12 ton capacity and poured in ingots ranging from 1100 to 2200 lb weight was determined to a large extent by the ratio of the manganese and silicon contents, provided other steelmaking variables such as tapping temperature, pouring temperature, pouring time, amount of aluminum added for grain size control, and degree of deoxidation in the furnace were kept reasonably constant. Detailed studies made on the deoxidation and slag practice during the refining period of basic electric furnace practice showed that these two variables exerted some influence on the resulting cleanness of steel in the form of bars and forgings. The important variable, the manganese-silicon balance, was not apparent until heats were made in succession by the best furnace practice kept under fairly rigid metallurgical control. Another observation pertinent to this work concerned the similarity in the microscope of slag particles causing magnaflux or step-down indications in subsequent rolled bars, and the patches of slag frequently seen on the surface of ingots. These patches are generally believed to come from the glassy metal-brick interface in the ladle and represent an entrapment of such glass (both from the ladle brick and nozzle) in the metal as it flows over the refractories in the neighborhood of the nozzle. These glassy particles are carried down into the mold with the liquid steel, and gradually coalesce into a slag "button" which floats on the surface of the steel as it rises in the molds. Periodically the button is washed to the side of the ingot where it is trapped between the surface of the ingot and the mold, later appearing as a slag patch on the surface of the ingot after stripping. Even though most of the small glassy particles coalesce into a slag button while the ingot is being poured, it is logical to suspect this step in the steelmaking process as being a source of slag lines large enough to cause trouble

Jan 1, 1950

By W. F. Netzeband

Jan 1, 1927

By J. Gordon Parr, A. J. Goldak

OgdEN et al.1 and Bumps et al.2 suggested that the solubility of aluminum in a titanium extended to 30 pct.* Sagcl,3 Clark and Terry,4 Anderko et al.,5 Ence and Margolin6 and Saulnier and croutzelles,7 subsequently proposed the existence of an intermetallic compound in the region of 25 pct Al. Although Anderko et al.5 suggested that the structure of this phase, Ti3Al, was of the DO,, (Ni3Sn) type, their conclusion was based only upon the results of a powder photograph that included reflections from ? = 0 to ?= 27° (CuK),some of which were reported to be indistinct. Ence and Margolin,6 referring to a 25 pct alloy (but without indicating whether the figure referred to weight or atomic pct) stated: "The structure of Ti2Al is isomorphous with Ti3Sn DO19, as pointed out by Pietrokowsky". But the point was not proven, because Ence and Margolin did not report values of calculated intensities of Ti2Al with the DO,, structure. In fact, the observed intensities they reported are in poor agreement with the values we calculate for DO19 (see Table I). Saulnier and croutzelle7 concluded, on the basis of electron micrography and microdiffraction studies, that the structure of the 25 pct A1 alloy was ordered hexagonal. Our purpose has been to unequivocally determine the Ti3Al structure. Alloys containing 25 pct Al were prepared from iodide titanium and spectrographic standard aluminum by levitation melting. The levitation chamber was evacuated to 10-6 mm Hg before filling with 99.999 + pct A. After casting, the alloy was chilled to liquid air temperature and crushed to -200 mesh in a percussion mortar. The powder, wrapped in molybdenum foil, was annealed (by induction heating) at 1000 "C for 2 hr in the argon atmosphere of the levitation chamber. No sublimate was seen on the foil or elsewhere, and therefore the assumption is

Jan 1, 1962

By C. P. Miller

In order to determine the usefulness of geochemical and biogeochemical prospecting for nickel, ten localities representing several types of nickel occurrences were selected as sites from which to collect plant and soil samples. This report covers the investigations in two of the areas. After a brief geologic description of the areas, the author presents details of the experimental tests and resulting data. Conclusions drawn from the studies led to several general guides for further prospecting. In a study of the usefulness of geochemical and biogeochemical prospecting for nickel made about three years ago, approximately ten localities, representing several different types of nickel occurrences, were sampled and about 1500 samples of plant and soil were collected. This report will cover briefly the data and results for two areas, and a summary of guides for prospecting. DESCRIPTION OF AREAS SAMPLED One locality is the Red Flats nickel prospect in Curry County, Ore., about six miles southeast of Goldbeach, and the other is the Little Rocky Creek prospect in Stillwater County, southcentral Montana, just southeast of the Benbow chromite mine. The Oregon area is a lateritic-type nickel deposit formed on a nickel-rich serpentinite peridotite complex, similar to the Josephine intrusion in southwestern Oregon. The Montana area is a nickel prospect in norite, peridotite, and related rocks of the Stillwater igneous complex. The Stillwater complex is a series of layered basic and ultrabasic rocks, with a layer of norite-gabbro at the base and a series of peridotites and gabbros above. The nickel in the Oregon deposit occurs in both the peridotite and the overlying soil. A deep lateritic soil is developed locally on the peridotite and serpentinite and constitutes the ore. The average nickel content of the lateritic soil is less than 1 pct, whereas the nickel content of the weathered peridotite is about 1 to 1.5 pct. The nickel occurs as garnierite (Mg, Fe, Ni, Mn)3 (OH)4 (SiA1)2O5 in the soil and in the olivine and pyroxene in the peridotite where it probably substitutes for Fe2+ or Mg2+ in the silicate lattices. Nickel is found in three distinct ways in the Still-water rocks: 1) it is in the olivine and pyroxene minerals in norite, harzburgite, etc.; 2) it occurs as widely disseminated grains of pentlandite-pyr-rhotite, which tend to be concentrated in the lower norite band; and 3) it occurs as discrete bodies of pentlandite-pyrrhotite and chalcopyrite which are localized in the norite zone, close to the contact with the underlying rocks. The nickel content of the norite is probably less than 1 pct, and the nickel content of the pods and lenses within the norite is about 1 pct. PROSPECTING APPROACH Although the areas are different geologically, the approach in prospecting them is fundamentally the same. The procedure is twofold: 1) a rapid reconnaissance survey to outline an area of high nickel content, and 2) a more detailed survey to outline zones of possible ore grade within the area of high nickel. The possible ore at Red Flats is concentrated in the lateritic soil, whereas at Little Rocky Creek it is in the sulfide pods. Both types are surrounded by an area of relatively high nickel content. CHEMICAL ANALYSIS Chemical analyses of nickel were made by a di-methylglyoxime colorimetric test, similar to the standard test for nickel, utilizing concentrated sul-furic acid for extraction. The lower limit of detection for nickel in soil by the method used was about 10 ppm and for nickel in plants about 5 ppm. The relative deviation was about 25 pct. SOIL PROSPECTING General Statements: A summary of the approximate average parts per million of nickel in soil, as compiled from the literature and from my study, is given in Table I. Selected references are given at the end of the paper. Few of the investigators reported the type of extraction or analysis, so the data given may not be strictly comparable to mine, which were made with a sulfuric acid extraction. Any nickel concentration greater than these average values might be considered anomalous, although each area must be studied in relation to the surrounding rocks. Method of Soil Sampling: The soil samples were taken in a zone from 1 in. to 1 ft below the humus layer, and within a 15-ft radius around a station.

Jan 1, 1961

By Donald M. Liddell

ALTHOUGH the midday lunches of business associations have been re-echoing the phrases that re- search would lead us out of the depression and that the last place to economize is on research, nevertheless most executives apparently concluded that it was their neighbor who ought not to economize in research, and that in their own plants what had been discovered in 1929-30 was sufficient to lead them out of the wilderness. At any rate, I have discovered much less that seems worth noting, and compared with 1931, the report volume of the committee members is off about 40 per cent, and compared with 1929, about 80 per cent. Evidently there is some hookup with the +tee1 industry as to output, and the Report Reading Committee should investigate this and the relative use of commas and periods.

Jan 1, 1933

By R. S. McClellan

In order to meet the ever-increasing demand by consumers for uniformity of ground talc, a new method of blending its finished product has been developed by Gouverneur Talc Company, Inc., at its plant near Gouverneur, N. Y. The method has been in use for a sufficient length of time to be now judged a success. The Gouverneur district is the leading talc producing area of the world, inasmuch as more tonnage is produced there than from any other state in the U.S. or, so far as is known, from any other locality in the world. Almost all of the output goes into industrial uses, with ceramics and paint being the principal consuming industries. The physical and chemical specifications imposed by these industries are stringent and the trend, as in most industries, is toward ever increasing severity. The blending method described herein has aided Gouverneur Talc to keep up with this trend.

Jan 3, 1961

By Albert Sauveur

THE following experiments were conducted in order to study the influence of the rate of cooling through and below solidification on the dendritic structure (macrostructure) and microstructure of some hypoeutectoid steel. The steel selected was of commercial grade and had the following composition: C, 0.40 per cent.; Mn, 0.85; Si, 0.70; P, 0.099; S, 0.043. After melting in vacuum in an Arsem furnace, the various samples were allowed to solidify and to cool to room temperature as indicated in Fig. 1. Samples were thus obtained representing all possible combinations of slow and fast cooling through the various ranges of temperatures indicated, namely: (1), zone of solidification or primary crystallization, (2) zone of granulation, and (3) zone of secondary crystallization. The location of the different temperature zones in the iron-carbon equilibrium diagram is shown in Fig. 2. The authors adopted. Belaiew's notations. The designations of the various samples readily indicate their treatment, as will be apparent from Table 1.

Jan 1, 1930

Diesel powered machines are doing some specific operations in the cyclic order required by the technical process. The dynamics of this process in certain conditions has an essential influence on environmental health conditions in the working area. The main purpose of this paper is to show, using computer simulation, how the movement (dynamic) of diesel vehicles effects environmental health standards and also how to determine the required air quantity for ventilation.

Jan 1, 1985

By H. A. Wriedt

At 500°C (932°F) the range of y' iron nitride is from 5. 77 + 0.03 wt pct N (in coexistence with a iron) to 5.88 * 0.03 wt pct N (in coexistence with E iron nitride). Stoichiometric "Fe,N" (5.900 wt pct N) is near the upper extreme of possible compositiom. The depe-dence of nitrogen activity (expressed as pnh,/Ph,) on nitrogen content is described satisfactorily by a "Langmuir" isotherm: At even the highest nitrogen concentrations, less than 0.18 pct of' the nitrogen atoms present are impositions of disorder. Past investigations1-4 of the Fe-N system have left only details of the thermodynamic behavior of the y' nitride, "Fe,N9', to be studied. The present investigation was made to establish more precisely than hitherto the limits of composition and the relation between composition and nitrogen activity at 500°C. EXPERIMENTAL TECHNIQUE The compositions of nitrides in equilibrium with various NH, + Hz mixtures at 500°C were determined from the weights gained by 0.02-in.-thick (4.0 to 4.5 g) strips of purified iron* when the nitrides were formed A description of the gas generation and furnace system has been published.5 Cracking and blistering during conversion of the original solid iron at 550°C injected considerable porosity into the strips without causing their disintegration. The time for complete conversion was significantly lowered by periodically reducing partly nitrided specimens in hydrogen and then reexposing them to the nitriding gas. Gas mixtures producing single-phase were used in the equilibrations at 500°C. Equilibrium was regarded as existing when the specimen weight was not detect-ably affected by further exposure to the same conditions. The gas compositions and nitrogen activities at which y' transformed to a iron (lower activity limit) and to E iron nitride (upper activity limit) were redetermined during the investigation. A specimen was equilibrated in an NH, + Hz mixture at 500°C and then exposed to a s1ightly different gas. When equi- librium had been reestablished the gas was again changed slightly. At each stage of this repeated process, while the specimen was reacting with the gas, the variation of its weight with time was observed. The onset of phase transition was marked by an abrupt change in the amount and rate of weight gain or loss. The specimens were weighed outside the furnace, in air and at room temperature, on a balance with 0.05 mg precision. When it was found that the specimens were oxidizing at a significant rate during the weighing, a series of timed weighings was made with each specimen, starting 1 min after its exposure to air. RESULTS AND ANALYSIS The gain in specimen weight from oxidation during weighing was linear in the logarithm of time between 1 min and about 2 hr, Fig. 1, later becoming linear in the cube root of time. In the logarithmic period, nitride specimens oxidized two to three times as fast as

Jan 1, 1970

By Albert Sauveur

As director of the Division of Metallurgy of the Technical Section of the Air Service, American Expeditionary Forces, from August, 1917, to January, 1919, I devoted much time to the study of the steels best suited to the construction of aircraft. It became apparent at a very early stage of my investigation that the practice of builders varied greatly in regard to the number of different steels to be used, to the kinds of steels, and to their treatment. Some manufacturers employed as many as fifteen steels while the builder of one of the newest motors, favorably passed upon in the United States, assured me that two or, at the most, three kinds of steel were all he needed to produce satisfactory results. In the matter of treatment, the manufacturers were also greatly at variance. Some treated their steel with considerable refinement while others paid but scant attention to this feature. Some manufacturers case-hardened many parts, while others used the case-hardening process sparingly, if at all. Nickel-chromium steels were used at some works for case-hardening while at other plants this treatment was applied exclusively to carbon steels. Air-hardening nickel-chromium steel was used extensively by some and not at all by others. Considerable variance existed likewise in regard to the steels used for admission and exhaust valves. The conclusion was obvious, that no two manufacturers of airplane motors held like opinions as to the steels to be used or as to the treatment they should receive. Was it to be inferred from this that the many committees and associations that had been created, in part at least, for the standardization of aircraft steels had failed to make proper recommendations or that the manufacturers had ignored their recommendations ? Confining our inquiry to the committees and associations that had dealt with this question in England, France, and the United States, it was found that in Great Britain the British Engineering Standards Committee, now the British Engineering Standards Association, had devoted much time to the problem of satisfactory standards for aircraft steels. In April, 1918, this Association presented a set of specifications described as "British Standard Specifications for Aircraft Steels for Government Purchases in the United States of America." They included twenty-one different steels and, as the title indicates, were drawn for the

Jan 1, 1920

By W. C. PAGE

AS the pioneer operation treating the mixed lead- zinc-iron ores from the district tributary to the Salt Lake Valley, the International Smelting Co.'s plant has offered an extremely interesting and instructive opportunity to study some phases of this problem. Basically, there were two main reason for our attempting to work out a successful operation for the separation and concentration of the values contained in the rather widespread deposits of these so- called lead-zinc ores. In the first place, the time was ripe and demanded some method of curtailing the economic waste resulting from the costs of past and present practice of smelting ores of this character, or rather, those ores which could stand the charges inherent with smelting them. Secondly, but rather primarily with us, we believe that such a solution would greatly in- crease in general the production of lead in the district tributary to the Salt Lake Valley. It is generally known that there were and are three relatively large lead smelting plants in the Salt Lake Valley and the decreasing production of correspondingly clean lead ores was not efficient to justify the existence of all three. We could not hope for better lead smelting metallurgy nor more efficient business management than was being practised, so the only prospect was to at- tempt to work out some way to increase the primary production and thus widen the scope of operations.

Jan 1, 1926