By JAMES SCULLY

For the last 4 years political leaders have found a new subject on which they can safely generalize wihout creating opposition. That subject is commodity prices. Since the four-fold increase in OPEC crude oil prices, public attention has focussed as never before on the subject of commodity prices. To advocate stabilizing commodity prices is akin to supporting motherhood or peace or better schooling. Everyone gives lip service to the concept that stable commodity prices are desirable. It is easier to state the principle than to achieve it. Prices that are stable in terms of one currency may be clearly unstable in terms of a different currency. This has become a troublesome matter since 1971, when the world's leading trading currencies were set free to float in relation to each other. To illustrate: consider copper prices in the interval between the end of 1974 and the end of 1977. During those 3 years, the copper price in pounds sterling on the London Metal Exchange rose by 25 per cent. During that period, however, in terms of the USA dollar equivalent, the price was unchanged. And during that period, in terms of the German mark equivalent the price shrank by 13 per cent while the Japanese yen equivalent fell by 20 per cent. Thus a price that appears stable in dollars, rose in terms of pounds sterling and fell in terms of marks and yen. Had this result been achieved as a consequence of an international effort to stabilize prices, an American would have said the effort was successful. An Englishman would have said it had failed to prevent a price rise. And a German or a Japanese consumer would have been happy to have covered his copper needs at a lower cost in terms of his own currency.

Jan 1, 1978

By AIME AIME

S ULFURIC acid made in the United States during the last four years has averaged approximately 7,000,000 tons of 50" B6 acid a year. This is double the production of the year 1913. About 66 per cent of the acid is made from sulfur, 16 per cent from pyrite, 13 per cent at copper, lead, and zinc smelters, and the remainder from miscellaneous sources it her the chamber process or the contact process, (at some plants both) is used. In 1923, the contact process accounted for nearly 30 per cent of all the sulfuric acid made in this country and since then it has been increasingly employed. It was first introduced here in 1898, and has always .proved less expensive than the chamber process for the manufacture of .acid of high concentration and purity, but the latter produces acid of low strength suitable for many industries.

Jan 1, 1929

By F. W. Glaser

Metal-carbon-boron powder mixtures were hot pressed and the resulting specimens were studied by X-ray diffraction. It was found that regardless of the starting combination of the metal, carbon, or boron powders, a metal boride phase was always the major component in these samples. In the absence of carbon the boride phase formed on hot pressing depended only on the amount of boron present. Two new phases of the system Ti-B were found. They are Ti2B and Ti2B5. The existence of a controversial face-centered cubic phase of formula TiB was confirmed. Electrical resistivities were measured for various boride phases. It was found that the diborides are generally better conductors than the monoborides of the same metal. THE carbides and borides of the transition elements have very high melting points, in the range 2500° to 4000°C, and are therefore of interest as high temperature materials. The literature on the stability or chemical reactivity of these carbides and borides is very scarce. Various investigators'-" have demonstrated a relative instability of certain carbide phases in the presence of boron or boron-containing substances. In a recent publication, Glaserl demonstrated the stability of zirconium-boride (ZrB,) in the presence of carbon at temperatures in excess of approximately 2900°C, while during a preliminary investigation of boride phases, Steinitz' concluded that the diborides are stable in the presence of carbon while the monoborides of the fourth and fifth group are not, forming diborides plus carbides instead. Nelson, Willmore, and Womeldorph" have elaborated on the reaction B,C + 2TiC = 2TiB, + 3C, which was known to occur because of a relative instability of B,C and the great tendency towards TiB, formation at relatively low temperatures (approximately 1200°C). A similar study, involving as starting materials TiO, and B,C and resulting in TiB,, was recently described by Honak4, who observed the beginning of an exothermic reaction of a Ti0,-B,C powder mixture, which, when preheated in a hydrogen atmosphere to approximately 950°C, was carried to about 1600 °C by the heat of reaction. To shed more light on reactions of this type (Metal-C-B), the final product apparently always resulting in a boride phase at the expense of a carbide phase," a systematic investigation was started * Boride phases of various metals, as reported to date, are listed in Table I. and the following is an account of some of the results that were obtained. Materials, Preparation of Samples, Testing Methods The raw materials employed for this work consisted of various carbide, boride, and metal powders. as well as of boron and graphite powders. In cases where commercial grades of carbides were considered unsuitable because of low purity or excessive amounts of graphitic carbon, such carbide powders were prepared by this laboratory. The procedure for the preparation of carbide powders (zirconium carbide, titanium carbide, tantalum carbide, and niobium carbide) consisted of mixing graphite and the respective metal hydride powders in stoichio-metric proportions and subsequent heating of such mixtures in a hydrogen atmosphere in carbon crucibles. The heating was by high frequency to temperatures ranging between 1700" and 2100°C. The resulting carbide was then comminuted and screened to the desired particle size. ZrB, and TiB, powders were produced by the electrolysis of fused salt baths, according to the method described by Andriex.. The borides of niobium, vanadium, tantalum, molybdenum, chro-ium, and iron were obtained by mixing the respective metal and boron powders in the desired proportions. Such metal-boron mixtures were heated in a high frequency furnace to form boride powders. For each metal-carbon-boron group (Tables I1 through XI) a metal, its hydride, carbide or boride were mixed with carbon, boron or boron carbide powders. The additions of carbon, boron or boron carbide powders to any of these metals or metal compounds were calculated to satisfy a particular carbide or boride phase that according to the literature (Table I) had definitely been established by X-ray diffraction work. Samples of powder mixtures were hot pressed in graphite molds that were heated by direct conduction. The specimen dimensions were approximately 2.5X1X1 cm. Hot pressing temperatures were measured optically and maintained for approximately 30 sec under a constant pressure of about 1.3 ton per sq in. Wherever possible, an attempt to obtain maximum specimen density was made by temperature variation. Electrical resistivity testing was done by measuring potentiometrically the voltage drop over a length of 1.5 cm for a current of 10 amp, at room temperature. To obtain electrical resistivities for specific carbide or boride phases, values were plotted as a function of the respective sample densities

Jan 1, 1953

By J. F. Peters

The term solution loss is discussed and defined. Examples are given showing that solution loss may either have a favorable or unfavorable effect on blast furnace performance. A theory is advanced explaining the contradictions encountered during earlier studies of the problem. MANY papers have been written and numerous theories advanced concerning the chemical reactions in the iron blast furnace. Richards, discussing the utilization of fuel in the blast furnace, said: "All the carbon burnt in the furnace should be first oxidized at the tuyeres to CO and all the reduction of oxides above the tuyeres should be caused by CO, which thus becomes CO,. This dictum is not Gruner's own words, but expresses their sense, and from the point of view of the present discussion, it is the correct principle upon which to obtain the maximum generation of heat in the furnace from a given weight of fuel." Richards also said the cubic feet of wind per pound of coke does not express how efficiently a furnace is running, but it will be shown later where Howland paid much attention to this figure. Richards pointed out a shortcoming of Grun-er's discussion in that Richards claimed there is not enough CO generated in a good working blast furnace to possibly combine with the oxygen of the ore, so some of it must be reduced by solid carbon. Mathesius2 made two important contributions. First, he wrote the direct and indirect reduction equations showing the heats of formation in each case and stressed that the indirect reduction reaction produces heat while direct reduction absorbs heat. Secondly, he substantiated Richards' conclusion that there may be a deficiency of CO gas and that some direct reduction is required, but he pointed out that "direct reduction in the hearth has often been confused with direct reduction in the stack, which more correctly should be termed 'premature combustion'." Then he said that "as this carbon is consumed partly by economical (direct reduction in the hearth) and partly by wasteful reactions in ever varying proportions, it is evident that the relation of this total carbon gasified above the tuyeres to the fuel consumption of a furnace cannot possibly have a direct bearing on the economy of furnace operation. The premature combustion of carbon (CO2+C?2CO) must therefore in all cases be considered a detrimental reaction." Johnson3 discussed this whole problem. Through experience Johnson found that when departure from Gruner's ideal working is considerable, the fuel economy is poor, and when the quantity of blast goes up, the fuel economy goes up in the same proportion. Johnson said that the wind per pound of coke is a measure of fuel economy, which will be shown to be wrong. Howland4 established the fact from operating data that there was no relationship between the coke consumption of a furnace and the percentage of coke burned at the tuyeres. But some of his calculations have led to questionable conclusions, such as "it is practically impossible to obtain low coke consumption unless we keep our wind low." Howland made an important contribution when, in his concluding paragraphs, he reached certain negative decisions as to why one coke works better than another. He said the reason one coke works better than another in a blast furnace is not because: 1—there is any difference in the percentage gasified at the tuyeres, or 2—there is any difference of wind required per pound of coke. Korevaar5 propounded a new theory on combustion which disagrees with Gruner because "as far as we can see, this is sufficient proof for the invalidity of Gruner's ideal, for if it was valid, the Low coke consumption should always be accompanied by a higher percentage of carbon burned at the tuyeres. This not being the case, we must deliberately give up our belief in Gruner's ideal." The part in italics will be proved to be wrong. Martin" contended that there was not enough reducing capacity in the blast furnace unless solution loss occurs. He came to a series of conclusions, such as: 1—The greatest efficiency of the blast furnace may not be attained when the reduction is performed entirely by carbon monoxide as demanded by Gruner's definition of the ideally perfect working of the blast furnace. 2—The so-called solution loss reactions, which should more properly be termed direct reduction reactions, promote furnace efficiency. 3—In modern blast furnace practice, the carbon consumption of the process is determined primarily by the carbon needed for reduction purposes, any thermal deficiency created by the reduction process being balanced in practice by the use of blast heat. From a practical standpoint further discussion of the theory of chemical reactions is of little moment. There is however one phase of the general theory of chemical reactions which is very important and that is the combustion of coke in the blast furnace. The purpose of this paper is to show that the reaction

Jan 1, 1955

By R. D. Schoone, J. T. Michalak

Recovery, recrystallization, and texture development of a cold-rolled aluminum-killed steel have been studied during simulated box annealing. Two different initial conditions existed prior to cold rolling: 1) essentially all of the nitrogen in solid solution and 2) most of the nitrogen precipitated as AlN. The combined effect of nitrogen and aluminum in solid solution before annealing was to inhibit recovery and sub-grain growth at temperatures above about 1000°F and to raise the recrystallization temperature range on continuous heating at 40°F per hr from 1000"-1050°F to 1065"-1085°F. For the material with nitrogen and aluminum initially in solution there was an inhibition in the nucleation of the (001) [110] texture component and an enhancement of the (111) [110] texture component. The differences in annealing behavior mzd texture development are attributed to preprecipitation clustering of aluminum and nitrogen at subboundary sites developed by prior cold working. THE annealing of cold-worked aluminum-killed steels has been the subject of numerous investigations.'-'2 These studies have been concerned with kinetics of recrystallization, with microstructure and texture development, and with the individual and combined effects of composition, thermal history prior to cold rolling, and heating rates during subsequent annealing. It has been shown that the inhibition of recrystallization, and the development of the pancake-shaped grain and recrystallization texture characteristic of aluminum-killed steels, can be associated with the precipitation of A1N particles during a recrystallization anneal involving heating rates in the range 20" to 80°F per hr. If the AIN is precipitated before cold rolling or if more rapid heating rates are employed, the cold-rolled steels recrystallize more rapidly to an equiaxed grain structure and texture comparable to that of rimmed low-carbon steel. The retardation of recrystallization, the development of the elongated grain structure, and the pronounced (111) texture have been attributed to: 1) precipitation of A1N at prior cold-worked grain boundaries to form a mechanical barrier to grain boundary migration;' 2) precipitation on the boundaries of the growing recrystal-lizing grains as well as on cold-worked grain boundaries;'" and 3) preprecipitation clustering or precipitation on subboundaries to retard recovery, nucleation, and growth. The present study was undertaken to study in more detail recrystallization and texture development during commercial box annealing of cold-rolled aluminum-killed steels. Comparison of the annealing be- havior after cold rolling, for two different conditions prior to cold rolling, was made in an attempt to define more clearly the role of aluminum and nitrogen in forming the recrystallization texture. A) MATERIAL AND PROCEDURE The material used in this investigation was a commercial low-carbon aluminum-killed steel which was hot-rolled with a finishing temperature of about 1565"F, then coiled at about 1020°F. The composition, in wt pct, was: 0.050 C, 0.30 Mn, 0.007 P, 0.019 Si, 0.03 Cu, 0.02 Ni, 0.02 Cr, 0.045 Al, and 0.004 N. Two 4.5 by 13 by 0.078 in. sections were cut from the center section of a hot-rolled panel and one of these was reheated to provide two different conditions prior to cold rolling: low AlN: as commercially hot-rolled, with aluminum and nitrogen in solid solution; and high AlN: as commercially hot-rolled, then reheated at 1300°F for 3.5 hr to precipitate most of the nitrogen as AlN. ~etallc&a~hic examination indicated that the reheating did not change grain size nor carbide distribution (some spheroidization of pearlite was noted). Texture analysis at half-thickness level showed that both sections had the same substantially random as-hot-rolled texture. The results of check chemical analysis of each sample are given in Table I. Both sections were cold-reduced 65 pct on a laboratory rolling mill to a final thickness of 0.027 in. Cold rolling, in one direction only, was in the direction of the prior hot rolling. Specimens 1.0 by 1.25 in. were cut from the cold-rolled sheets and given a simulated box anneal in an atmosphere of 2 pct HZ-98 pct He. Specimens were heated at a constant rate of 40°F per hr from room temperature to various temperatures in the range 750" to 1300°F and cooled immediately by withdrawal to the water-cooled end of a tube furnace. The temperature in the 6-in. uniform hot zone of the furnace was controlled within 3"F. Selection of the individual specimens was made to give a random distribution of annealing temperatures with respect to location in the cold-rolled sheet. At least two specimens of each condition were annealed to the same temperature and smaller specimens for light microscopy, transmission electron microscopy, and X-ray studies were prepared from each of these. Rolling-plane sections for each of these studies were taken at half thickness. Light microscopy and transmission electron micro-

Jan 1, 1969

By A. L. Bailey, B. A. Landry

All who are even generally aware of the tremendous rate of increase in coal washing operations must realize the growing importance of the float-and-sink test. I believe it is conservative to estimate that, in the past decade, the dollar volume of float-and-sink testing has increased tenfold. It is a simple matter of economy, then, to examine the factors that determine the cost of adequate float-and-sink testing. When the Coal Preparation Section of the Bureau of Mines entered upon a greatly expanded program of such work in connection with the synthetic liquid fuels investigations, it seemed advisable to examine these factors experimentally. The principal consideration that differentiates float-and-sink test sampling from general purpose sampling, is that the original particle size must be preserved. Therefore, the total cost of the test will be directly affected by any standard that might be proposed to limit sample bulk reduction at any given particle size. For this reason, the relationship of sample size to variability of results was the first factor to be studied experimentally. Of course, the matter is rendered complex by the circumstance that the float-and-sink test, not a simple analytical measurement but a process test, comprehends a number of more-or-less independent items of fundamental data; and as shown in the report, the' variability of the samples differs with respect to these different items. This condition and the wide variety of situations in which float-and-sink test data are used, in combination with other factors, to study complex process operations, indicate the difficulty of setting up fixed standards for float-and-sink sampling and testing. At this stage at least, it is the intent rather to obtain experimental data on the principal Factors involved so that the reader may arrive more intelligently at a procedure adapted to his problem. The authors of this paper have presented experimental data showing the relationship between size of sample and particle size for different variability tolerances with respect to percentage of sink. In further studies, data are being collected to appraise also the variability of the samples with respect to float-ash content and size consist. The scope of this work will be broadened to cover particle sizes up to 4 in., and a third series of tests has yielded similar data for a much cleaner type of raw coal. Thus, the further studies will make available a fairly comprehensive meas- ure of variability with respect to size consist, percentage of sink, percentage of middlings, and percentage of ash in the float, for three coals ranging from 3.87 to 17.68 pct in refuse content (heavy sink material) and from 4.18 to 17.52 pct in middlings. Introduction At present there are no published standards for float-and-sink test sampling. During the rapid expansion of float-and-sink test work, varying procedures have been based on adaptations of the ASTM standards for sampling coal for analyses. For this reason, a special study of gross sample reduction has been undertaken to determine the limits for this step in the operation where no reduction in particle size is to be made before testing. Float-and-sink tests are made whenever a thorough study of coal characteristics is desired. The tests may be made on samples from coal-cleaning units such as jigs or tables, or coal samples may be tested which are taken from a loading boom, railroad car, or the coal seam itself. The resultant gross sample may be large and pose a problem of sample reduction. The question is, then, how much can the sample be reduced and still fall within preassigned limits of accuracy of the original gross sample of coal? Coal from channel samples may be crushed to liberate impurities and then separated into various gravity fractions from which washability curves are drawn; from these curves, it is possible to determine the cleaning characteristics of the coal. However, coal samples from coal-cleaning units cannot be

Jan 1, 1950

By AIME AIME

ED DIX, after studying both mechanical and electrical engineering at Cornell, started out to be an electrical engineer, then taught material testing at Cornell, and decided to become a metallurgist. He was successively employed by the Morse Chain Co. as metallographist, by the Baltimore Copper Smelting and Rolling Co., as chief of the testing department of the Bureau of Aircraft Production, as assistant engineer of tests of the Aluminum Castings Co., and as chief of the metals branch, engineering division, U. S. Air Service. Since 1923 he has been with the Aluminum Co. of America, now as chief metallurgist.

Jan 1, 1936

By Donald Towse

Geothermal energy can substitute for and compete with other fuels, but until now it has been used only in special situations where it costs much less than alternate fuels. Geothermal heat is expected to be developed where it can: (1) compete with alternate fuels, (2) replace scarce fuels, (3) be more environmentally acceptable, or (4) is especially adapted to local needs. Economic problems in development include the often high capital costs of wells and gathering systems and the long lead-times required for electric generating plants. The large investment and long payout times for large industrial uses adversely affect the economics.

Jan 1, 1977

By P. Somasundaran, D. W. Fuerstenau

Adsorption isotherms for dodecyl sulfonate on alumina were determined at 45°C and 25°C and the data was used for calculating the partial molar heat and entropy of adsorbed ions under various concentrations. Changes in OH and AS observed at certain concentrations agree with the postulate of interaction of surfactant ions to form two-dimensional aggregates at the solid-liquid interface. Values of the total OH and AS for the aggregation process calculated using the Clausius-Clapeyron equation is used to interpret the interactions of surfactant ions with each other as well as with the solvent molecules.

Jan 1, 1973

By A. L. Holley

IN order to put sufficient work on steel ingots for rails, they must be reduced from about 12 inches square. As this cannot be done at one heat, they are first drawn down to about 7 inches square, and then reheated and rolled into rails. This first reduction or " blooming," is usually done in this country in a 30-inch 3-high rolling-mill, with movable rolls, so as to get several reductions in each set of grooves. The first of these mills has been running at the Troy Steel-works above a year, with great success. Another at the Cambria Iron-

Jan 1, 1873

By Alexander L. Holley

IN order to put sufficient work on steel ingots for rails, they must be reduced from about 12 inches square. As this cannot be done at one heat, they are first drawn down to about 7 inches square, and then reheated and rolled into rails. This first reduction or " blooming," is usually done in this country in a 30-inch 3-high rolling-mill, with movable rolls, so as to get several reductions in each set of grooves. The first of these mills has been running at the Troy Steel-works above a year, with great success. Another at the Cambria Iron

By F. A. Kjellin

The problem of smelting steel by electricity attracted years ago the attention of inventors, and as early as 1879 C. W. Siemens constructed his first furnace for the smelting of metals, especially steel. His furnace was of the arc type in which the voltaic arc was formed between a carbon electrode and the metallic content of a crucible, the length of the arc being regulated by an electromagnetic device. This electric furnace, as well as others of similar construction, has the inconvenience that the source of the heat—the voltaic arc—possesses a temperature of 3,700' C., which is much

Jan 1, 1904

By J. W. Spretnak, R. Speiser, A. M. Adair

THERE are sufficient arguments and evidence to indicate that boron should be adsorbed to existing austenite grain boundaries during the austen-itizing treatment. Accordingly, it is possible that boron contributes to the hardenability of heat-treatable steels by the reduction of the interf acial energy of austenite grain boundaries, at which sites are nucleated heterogeneously the decomposition products of austenite. Such a reduction in interfacial energy would reduce the total energy that can be borrowed in these heterogeneous nudeation processes and thus retard the initiation of transformation. This investigation was undertaken in an attempt to determine the effect of boron on this interfacial

Jan 1, 1956

By William R. Webster

At the Richmond mecting in February, 1901, I presented for discussion the proposed rail-specifications of Committee No. 1 of the American Section of the International Association for Testing Materials, with a review of their work, and other matters relating to the heat-treatment and chemical composition of steel (Trans., xxxi., 455). In order to bring out the views of our members on the important points referred to, I offered for discussion the following questions and comments (trans., xxxi., 972): " 1. The advantages to be gained by using more metal in the flanges and web of the heavier sections of rails.

Jan 1, 1903

By T. S. Govindan

The first step in energy conservation in any industrial plant involves implementing many of the day-to-day "housekeeping" items, such as fixing leaks, turning out lights, etc. When this step has been accomplished, additional opportunities require a detailed analysis of the energy systems, evaluation of risks and costs, and assignment of priorities. Examples of conservation schemes drawn from the experience of Du Pont's Energy Management Consulting Services will be discussed. The utility of heat balances for kilns and dryers in minerals processing will be outlined. The input needed from management for the success of conservation efforts will be discussed.

Jan 1, 1981

By Horace C. Knerr

It has been shown that the resistance to corrosion of duralumin sheet is greatly influenced by the quenching medium used in heat treatment, or, more specifically, by the rate of cooling during quenching. The severity of corrosive attack after exposure to salt-water spray increases in .the following order: The tensile strength, yield point and elongation are only slightly affected by the quenching medium, as shown in Table 1. Tensile test requirements: yield stress, 25,000 lb. per sq. in. minimum; ultimate stress, 55,000 lb. per sq. in. minimum; elongation in 2 in., 18 per cent. minimum.

Jan 1, 1931

By Edward B. Durham

At the Richmond mecting in February, 1901, I presented for discussion the proposed rail-specifications of Committee No. 1 of the American Section of the International Association for Testing Materials, with a review of their work, and other matters relating to the heat-treatment and chemical composition of steel (Trans., xxxi., 455). In order to bring out the views of our members on the important points referred to, I offered for discussion the following questions and comments (trans., xxxi., 972): " 1. The advantages to be gained by using more metal in the flanges and web of the heavier sections of rails.

Jan 1, 1903

By W. D. Forgeng, B. F. Decker

IT has been known for almost a century' that silicon and nitrogen combine when heated to a high temperature. Three nitrides have been reported, SiN, Si3N,, and Si,N, containing 33.3, 40.0 and 42.9 pct nitrogen by weight, respectively. The existence of SisN, is well established but that of Si,N, and SiN is doubtful. The first systematic study of the reaction between silicon and nitrogen was made in 1910 by Weiss and Engelhart" who determined the rate at which silicon absorbed nitrogen at temperatures from 1250°C to

Jan 1, 1959

By Jan M. Mutmansky, Gordon H. Walrod, Y. J. Wang

The approach proposed in this paper is, as stated by the authors, an update of methods well discussed in the literature. The authors are to be congratulated for their excellent effort in quantifying a difficult problem with realistic cost data. Economic analysis of the components of a mine ventilation system is complicated by both the dynamic nature of the system and the uncertainty as to the time when system changes occur. We wish to address three specific areas of this paper which require further consideration: shaft designed air capacity, shaft location, and economic criteria used within the analysis

Jan 11, 1979

By O. Hyvärinen

The treatment of anode slimes at Outokumpu Pori Copper Refinery comprises the following process stages: copper leaching by air oxidation, nickel removal by digesting slimes in concentrated sulphuric acid at 200 °C, and dissolving of the formed nickel sulphate into water, roasting of the slimes in controlled gas atmosphere at 600 °C for selenium removal, smelting of slimes in a Doré furnace, electrolytic refining of silver, sulphuric acid and aqua regia leaching of slimes from the silver cells followed by the reduction of gold and platinum metals. The paper discusses operational experiences and recent developments of the process.

Jan 1, 1984