By H. J. Rahilly

Mine fires, in the Butte district, have been a source of trouble and expense for the past thirty years, for while the actual fire area in most of the mines has been comparatively small, the handling of the gas has generally been a much larger problem than the actual putting out of the fire. The chief causes of these fires have been: Defective electrical equipment, incendiarism or carelessness, and spontaneous combustion. While fires from the first two causes have been numerous, they have generally been discovered and extinguished before they became very serious. Spontaneous combustion has been the cause of most of the large fires. Sufficient heat has been generated by ground movement, high rock temperatures, and decomposition to set fire to inflammable materials (tarred ropes, canvas, dry timber, manure, and hay) left in the gobs some years ago. Also, the heat resulting from the oxidation of the fine broken sulfide ore is sometimes sufficient to set fire to the timbers. In 1906, a fire was discovered on the 1100-ft. level of the Minnie Healy mine about 400 ft. (122 m.) west of the Minnie Healy shaft, which presumably originated, in one of the upper levels, from spontaneous combustion. The fire was walled off by concrete bulkheads and a pillar of ground 100 ft. (30 m.) thick was left below and mining resumed underneath. During subsequent operations, this pillar became cracked and broken and the fire passed into the new workings. It travelled downward and spread rapidly until, in 1917, it had become necessary to wall off portions of the Tramway, Leonard, and West Colusa mines on the 1300, 1400, 1500, 1600, 1800, 1900, and 2000-ft. levels, and the tops of the 2200-ft. raises were sealed. The fire area now consists roughly of a block 1000 by 1200 ft. and from the 600-ft. to the 2200-ft. level. This block is composed largely of a series of parallel northwest-southeast nearly vertical veins and stringers that form a large orebody, with no well-defined walls but badly fractured and faulted, and known locally as "horsetail ore." These veins, or orebodies, are mined by the square-set or the rill method.

Jan 1, 1923

THE primary interest in the subject of this chapter lies in the fact that various heats of steel made to the same chemical specification do not always have the same properties. We are referring here, of course, to properties inherent in the just solidified ingot and are not considering variations in properties caused by variations in subsequent mechanical or thermal treatment. The expression "made to the same chemical specification" is used because some of the variations in properties are due to variations in chemical analysis within the specified ranges of those elements commonly specified and determined. In plain carbon steels these elements are ordinarily not more than five: carbon, manganese, silicon, phosphorus, and sulphur. In alloy steels the special alloying elements also are specified and. determined. It might be thought that variations in properties due to such variations in ordinary chemical composition are to be expected, well understood, and hence not in need of discussion in this chapter. It will be considered here, however, that this phase of the subject is not always wholly clear. Furthermore, it certainly seems profitable to seek the explanation of anomalous properties in the ordinary chemical composition of the steel before looking into less well understood variables of open-hearth practice. It is sometimes surprising to learn that some puzzling variation in properties is caused merely by a variation in the ordinary analysis of the steel. This surprise is apt to be due not to general lack of knowledge of the effects of the composition of steel upon its properties but rather to the fact that we do not happen to have been previously much concerned with the particular property under consideration. For example, if we are accustomed to using S.A.E. 1035 bars for applications which depend chiefly on the stiffness, strength, and toughness of the steel in the as-rolled condition, we might quite logically develop the conclusion that variations in carbon content from 0.30 to 0.40 per cent are not significant. Then if we later have occasion to make heat-treated bolts of the same grade of steel, we may be surprised to

Jan 1, 1944

By W. C. Hagel, H. J. Beattle

DURING an earlier examination of high-temperature alloy, A-286, the presence of an unknown intermetallic compound was verified by X-ray diffraction. Owing to its prominent appearance at grain boundaries, the arbitrary name of G phase was assigned.' Low-silicon, vacuum-melted heats were found to contain no G phase, and this investigation was initiated to determine the influence of silicon on G-phase formation; additional work was undertaken to extend existing data on other intermetallic compounds and the aging reactions in this group of alloys. Taylor and Floyd2-4 observed that the Ni3Al phase (y') and the Ni8Ti phase (7)) are the only equilibrium intermetailic compounds in nickel ternary alloys containing up to 25 pct Cr and 10 pct Ti or Al. They found that y' can dissolve considerable nickel, chromium, and titanium, although the stoichio-metric composition of 7 remains fixed. Nordheim and Grant5 confirmed that age hardening of 80 pct Ni-20 pct Cr alloys of the Nimonic-80 type is due to precipitation of y', where aluminum is partially replaced by titanium. They suggest that optimum hardness and ductility result from increasing the titanium to aluminum ratio toward the end of the y' solubility range and from increasing total titanium and aluminum content to the maximum limit permitted by processing. Such information is necessary for those seeking to improve the service-temperature range and long-time structural stability of high-temperature components. Experimental Methods Compositions of materiais studied. are listed in Table I. Alloys D, E, and F possess representative A-286 analyses; silicon increases from less than 0.02 to 1.75 pct in alloys A to H; in alloys I to K, titanium decreases from 2.24 to 0.39 pct, and aluminum increases from 0.1 6 to 240 pct. Alloys A and D were solution heat treated for 4 hr at 1700°F, oil quenched and aged for 0.5, 2, 6, 12, 30, 70, 200, and 1000 hr at 1200°, 1300°, 1400°, and 1500°F. Therefore, a total of 33 specimens was required for each

Jan 1, 1958

By M. C. Udy, P. C. Rosenthal

THE use of minute boron additions to steel has been given considerable attention in recent years. Comparisons made between boron-free and boron-containing heats of otherwise identical analysis have indicated, beyond a doubt, the potent effect of boron for increasing hardenability. The actual hardenability increase has been expressed as a multiplying factor, or in terms of the percentage of other alloying elements boron might replace, The present study presents the results of a systematic survey of. the use of boron as an addition to two types of alloyed steels and as a replacement for various percentages of molybdenum in these steels, Both cast and wrought steels of the two basic compositions were prepared. Molybdenum, because of its scarcity at the time the investigation was started, was selected as the element to be replaced by boron. Attention was also given to the effects of boron on other properties of the steels, particularly their notched-bar toughness, to investigate other advantages or limitations of this element as an alloy addition. EXPERIMENTAL WORK Steels Investigated The two basic compositions used in this survey of boron as a replacement for molybdenum are given in Table I. The cast steels were higher than the wrought steels in silicon content to improve the casting quality. [ ] Each of these base steels, both cast and wrought, was made with molybdenum contents of o, 0.10, 0.20, 0.30, or 0.40 per cent, the total comprising 20 steels. In addition, each of these 20 compositions . was prepared with boron additions in amounts of 0.0015, 0.003, and o,006 per cent as ferroboron; and in amounts of 0.002 and 0.005 per cent as two com¬mercial intensifier alloys, designated alloys A and B. The boron-treated steels totaled 100, and the entire series 120, Test Procedure Each steel was melted as an individual heat in a 50-lb., magnesia-lined induction furnace. Ingot iron scrap or mixtures of ingot iron and steel scrap were used for melting stock. Deoxidation was carried out in the furnace with o.10 per cent aluminum. The aluminum addition was

Jan 1, 1946

By J. H. Hollomon, L. D. Jaffe, M. R. Norton

In the practical heat-treatment of steel the decomposition of austenite usually occurs during cooling rather than at constant temperature. Nevertheless, the course of this decomposition has generally been studied only isothermally. Isothermal studies are not only simpler experimentally, but have the great theoretical advantage that one of the variables, temperature, is constant. It is the purpose of this paper to outline the principles that govern the relations between isothermal and anisothermalt‡ decomposition of austenite, to present and systematize the available experimental information, and to indicate the gaps in the existing knowledge. Some of the experimental information is the result of new work.§ Most of it is derived from scattered data in the literature. Many of these data were obtained incidentally in the course of research on other subjects and their significance has not been pointed out and perhaps not understood. It is hoped that this paper will aid future planning of more extensive research on anisothermal decomposition. Method In order to study the relations between isothermal and anisothermal decomposition, it appears fruitful to view anisothermal decomposition as taking place at a series of constant temperatures1 (except for the martensite reaction, which does not occur isothermally to an appreciable extent). When the time the steel is at each temperature is finite, the over-all amount of the reaction is considered to be the sum of the amounts occurring at each of the successive temperatures. During continuous cooling or heating, the time the steel is at each temperature and the difference between successive temperatures can be considered to approach zero. The over-all amount of transformation will then be given by integration over the range of temperatures involved. This point of view is advantageous in that it considers anisothermal transformation to be a series of isothermal transformations. The problem thus becomes one of determining the effect of partial decomposition at any given temperature upon subsequent decomposition at another temperature. Single Anisothermal Reaction Consider a phase brought to a temperature at which it is unstable, held there until it has partially transformed, and then brought to another temperature at

Jan 1, 1947

By Heinrich Freyn

THE American iron and steel manufacturer finds himself to-clay barely at the threshold of enormous possibilities for practicing rational economy in the use of fuels. The fuel cost is by no means the smallest of items which enter into the cost of manufacture of iron and steel products, but the great wealth of this country in high-grade fuels, together with a protective tariff, has heretofore made fuel economy relatively unimportant. In Germany, the use of raw coal for the purposes of iron and steel manufacture has been all but abandoned and large sums of money, formerly irrevocably wasted, are now being saved. When scanning the literature of this country devoted to the application of gas power, but little information will be found on a subject which, however, is destined to become of considerable importance in the United States, namely, the use of coke-oven gas for the generation of power in gas engines. This lack of information can be traced to the fact that the regenerative by-product coke oven with its large amount of surplus gas is still far from having attained in this country the universal application which it has found in Europe. This statement needs hardy any corroboration other than the evidence of statistical investigations made by E. W. Parker of the United States Geological Survey, according to which only approximately 25 per cent. of the total coke produced in this country in 1912 was made in by-product coke ovens, whereas 75 per cent. was produced in bee-hive ovens. This entailed the enormous loss of over $80,000,000 in non-recovered by-products, such as gas, tar, and ammonia, without considering the substantial loss due to the non-recovery of benzol from the coal. There are two more or less distinct fields of application of the by-product coke oven: one, to furnish as the main product metallurgical coke of specified quality, and surplus coke-oven gas as the by-product, and the other, to carbonize high-volatile coals, and thus produce as the main product large quantities of gas, high in heat value and rich in illuminants, adapted primarily for domestic heating and lighting, while domestic coke becomes the by-product.

Jan 4, 1914

By W. N. Logan

WHAT is mineral wool? This question is frequently asked by those unacquainted with its manufacture. The word "mineral" suggests that it is of mineral origin; the word "wool" suggests that it is of animal origin; but the only similarities it has to wool are its fibrous character and its white fleecyness. Mineral wool is a fiber produced by melting rock to a glasslike condition and blowing the glass into fine white, wool-like threads. A -number of the products fabricated from-mineral wool are used for some form of insulation, but mineral wool is adaptable to many other uses. It is used in the manufacture-of pipe covering designed to with; stand the high temperatures produced in steam pipes. In a similar form of insulation it is used to cover boilers and furnaces. It is used in ,the fabrication of upholstery tow for sofas and car seats: In acoustics it has many uses, such as acoustifibroblock, which is used in floors to destroy sound and vibration, and acoustic mat, which is used under carpets to destroy sound. In the insulation of houses, loose wool and granulated wool are used beneath attic floors and between the studding in frame buildings to prevent the escape of heat in winter and the entrance of heat in summer. Mineral wool is used also in fabrication of linofelt, which is a quilted form of insulation; in fibrofelt, which is an insulating board; in the fabrication of lith, which is an insulating block; in anti-fibroblock ,which is used in insulation and refrigeration; in flexfelt; in loose wool; in pressed block; in heavy oiled wool; in dark oiled block; and for many other purposes. The materials used in the manufacture of mineral wool are of two kinds. The first is a rock which contains silt, clay and silica, with smaller amounts of lime and magnesia. The second is a more highly calcareous rock which may carry a small amount of magnesia. The latter is used as flux to assist in the melting of the former. The relative proportion of the alumina-iron-silica content to the lime-magnesia content is normally as fifty to fifty but a considerable range is possible.

Jan 1, 1932

By L. D. Jaffe, M. R. Norton, J. H. Hollomon

In the practical heat-treatment of steel the decomposition of austenite usually occurs during cooling rather than at constant temperature. Nevertheless, the course of this decomposition has generally been studied only isothermally. Isothermal studies are not only simpler experimentally, but have the great theoretical advantage that one of the variables, temperature, is constant. It is the purpose of this paper to outline the principles that govern the relations between isothermal and anisothermalt‡ decomposition of austenite, to present and systematize the available experimental information, and to indicate the gaps in the existing knowledge. Some of the experimental information is the result of new work.§ Most of it is derived from scattered data in the literature. Many of these data were obtained incidentally in the course of research on other subjects and their significance has not been pointed out and perhaps not understood. It is hoped that this paper will aid future planning of more extensive research on anisothermal decomposition. Method In order to study the relations between isothermal and anisothermal decomposition, it appears fruitful to view anisothermal decomposition as taking place at a series of constant temperatures1 (except for the martensite reaction, which does not occur isothermally to an appreciable extent). When the time the steel is at each temperature is finite, the over-all amount of the reaction is considered to be the sum of the amounts occurring at each of the successive temperatures. During continuous cooling or heating, the time the steel is at each temperature and the difference between successive temperatures can be considered to approach zero. The over-all amount of transformation will then be given by integration over the range of temperatures involved. This point of view is advantageous in that it considers anisothermal transformation to be a series of isothermal transformations. The problem thus becomes one of determining the effect of partial decomposition at any given temperature upon subsequent decomposition at another temperature. Single Anisothermal Reaction Consider a phase brought to a temperature at which it is unstable, held there until it has partially transformed, and then brought to another temperature at

Jan 1, 1947

By R. L. Rickett, N. C. Fick

Despite the large volume of literature on alloys of iron and silicon,' there is little published information dealing specifically with the constitution, at various temperatures, of the alloys containing less than 0.10 per cent carl~on and from 0.5 to 4.5 per cent silicon that are used extensively in the electrical industry. Because such information was needed by those engaged in the production of these alloys in sheet and strip form, the constitution nas determined of a series of commercial silicon steels containing 0.05 to 0.08 per cent carbon and 0.20 to 4.1 per cent silicon, over the temperature range 1300° to 1500°F. These alloys were all from regular production heats and of commercial quality. The results of the tests are given in Fig. I and for comparison the constitution diagram of iron-silicon alloys with 0.01 to 0.02 per cent carbon, taken from the literature, is also presented Material and Procedure All steels were hot-rolled to a thickness of 0.060 to 0.080 in. and used in this condition. Their chemical compositions, including over-all check analysis, and "center" analysis for carbon and silicon, are given in Table I. The so-called center analysis was determined on samples pickled to remove the outer surface and leave only the center third of the gauge thickness—the portion of the sample on which metallographic ratings were based. In most, but not all, of the alloys, slightly higher carbon was found at the center than when the whole strip was sampled; the two methods of sampling show relatively little difference in silicon. Two of the steels, A and E, contain relatively high phosphorus, while I and K are somewhat higher in manganese than the others. The procedure consisted essentially of heating specimens (about 1/16 by 3/8 by 3/4 in.), protected from oxidation or change in carbon content, at a temperature in the desired range and for a selected period, after which they were quenched in iced brine; the degree of transformation that had then occurred was determined by metallographic examination. The soaking periods were selected after preliminary investigation had shown that a con-

Jan 1, 1947

By N. C. Fick, R. L. Rickett

Despite the large volume of literature on alloys of iron and silicon,' there is little published information dealing specifically with the constitution, at various temperatures, of the alloys containing less than 0.10 per cent carl~on and from 0.5 to 4.5 per cent silicon that are used extensively in the electrical industry. Because such information was needed by those engaged in the production of these alloys in sheet and strip form, the constitution nas determined of a series of commercial silicon steels containing 0.05 to 0.08 per cent carbon and 0.20 to 4.1 per cent silicon, over the temperature range 1300° to 1500°F. These alloys were all from regular production heats and of commercial quality. The results of the tests are given in Fig. I and for comparison the constitution diagram of iron-silicon alloys with 0.01 to 0.02 per cent carbon, taken from the literature, is also presented Material and Procedure All steels were hot-rolled to a thickness of 0.060 to 0.080 in. and used in this condition. Their chemical compositions, including over-all check analysis, and "center" analysis for carbon and silicon, are given in Table I. The so-called center analysis was determined on samples pickled to remove the outer surface and leave only the center third of the gauge thickness—the portion of the sample on which metallographic ratings were based. In most, but not all, of the alloys, slightly higher carbon was found at the center than when the whole strip was sampled; the two methods of sampling show relatively little difference in silicon. Two of the steels, A and E, contain relatively high phosphorus, while I and K are somewhat higher in manganese than the others. The procedure consisted essentially of heating specimens (about 1/16 by 3/8 by 3/4 in.), protected from oxidation or change in carbon content, at a temperature in the desired range and for a selected period, after which they were quenched in iced brine; the degree of transformation that had then occurred was determined by metallographic examination. The soaking periods were selected after preliminary investigation had shown that a con-

Jan 1, 1947

By N. C. Fick, R. L. Rickett

DESPITE the large volume of literature on alloys of iron and silicon,1 there is little published information dealing specifically with the constitution, at various temperatures, of the alloys containing less than 0.10 per cent carbon and from 0.5 to 4.5 per cent silicon that are used extensively in the electrical industry. Because such information was needed by those engaged in the production of these alloys in, sheet and strip form, the constitution was determined of a series of commercial silicon steels containing 0.05 to o.08 per cent carbon and 0.20 to 4.31 per cent silicon, over the temperature range 1300° to 2500°F. These alloys were all from regular production heats and of commercial quality. The results of, the tests are given in Fig. I and for comparison the constitution diagram of iron-silicon alloys with 0.01 to 0.02 per cent carbon, taken from the literature, is also presented. MATERIAL AND PROCEDURE All steels were hot-rolled to a thickness of 0.060 to 0.080 in. and used in this condition. Their chemical compositions, including over-all check analysis, and "center" analysis for carbon and silicon, are given in Table I. The so-called center analysis was determined on samples pickled to remove the outer surface and leave only the center third of the gauge thickness-the portion of the sample on which metallographic ratings were based. In most, but not all, of the alloys, slightly higher carbon was found at the center than when the whole strip was sampled; the two methods of sampling show relatively little difference in silicon. Two of the steels, A and E, contain relatively high phosphorus, while I and K are somewhat higher in manganese than the others. [ ] The procedure consisted essentially of heating specimens (about 1/16 by 3/8 by 3/4 in.), protected from oxidation or change in carbon content, at a temperature in the desired. range and for a selected period, after which they were quenched in iced brine; the degree of transformation that had then occurred was determined by metallographic examination. The soaking periods were selected after preliminary investigation had shown that a con-

Jan 1, 1946

By James E. York

THE honor so fairly earned and so incompletely and tardily paid to Henry Cort, the inventor of the puddling-furnace and the, rolling-mill, has been fully set forth by Mr. Charles H. Morgan,1 and needs no further emphasis here. In view of the importance of the rolling-mill in the treatment of iron and steel, the paucity of information concerning it is surprising. With the exception of a hook, written about 35 years ago, by Peter Bitter von Tunner, an Honorary Member of this Institute, and of desultory articles on simple sections, which have appeared in technical journals, I know of no pub¬lication attempting to treat this subject, although volumes have been written on the scientific theory and technical manipulations involved in other branches of the iron- and steel-industry. This strange anomaly may be due to the fact that roll-turning cannot be called a scientific business. It does not ordinarily come within the range of an educated engineer; yet it cannot be performed by an ordinary mechanic. It demands some of the qualifications of an engineer, in designing, and those of a mechanic, in execution. The men who have followed this trade have controlled the training of their successors. In many cases the technical knowledge required bas been handed down from father to son, and there has been a motive of private interest to prevent its public dissemination. Moreover, the statement of the various principles involved in the process would require, besides manual experience, a degree of scientific knowledge which roll-turners do not usually possess; and, finally, any book on the subject, in order to possess real, practical value, would have to be so fully illustrated as to make it very costly to publish. Regarding my own experience, I may say that I served a six-

May 1, 1906

By Carle R. Hayward

This work was first undertaken in the metallurgical laboratory of the Massachusetts Institute of Technology in 1907 by L. A. Dickinson, E. Phelps, and V. S. Rood, under the author's direction. They attempted to determine the diagram for the system Cu2S-MiS, but several inexplicable results were obtained. The following year, P. H. Mayer with Mr. Dickinson carried on some experiments with nickel sulphide and found that the molten material slowly lost sulphur until it reached a composition corresponding to the compound Ni3S2, established by Bornemann.l At this point the composition remained stable. The freezing points of the mixtures gradually fell off with the loss of sulphur. Since the above facts seemed to explain the erratic results obtained in the first experiments, Mr. Mayer with F. Jaeger attempted in 1910 to establish a correct equilibrium diagram for the Cu2S-Ni3S2 series. They prepared pure Cu2S and Ni3S2 and determined the cooling curves for various mixtures. The fusions were made in a platinum resistance furnace and the temperatures were measured with a platinum-iridium thermocouple connected with a Sullivan galvanometer. The curve was established for mixtures containing more than 40 per cent. Cu2S, but they were unable to determine certainly the direction of the curve beyond that point. Nothing further was attempted with this series until the present year, when the work was carried to a successful conclusion with the assistance of A. Butts, Jr., and E. H. Weil. The results of this work are given in the following pages. Preparation of Cu2S.—A piece of cathode' copper from the Buffalo plant of the Calumet & Hecla Co. was cut into shavings by a shaper and converted into sulphide by heating in boiling sulphur. A porcelain casserole was used for the purpose, the heat being furnished by a Bunsen burner. It was found that after boiling in the sulphur for an hour the copper shavings were completely converted into sulphide. The liquid sulphur was then poured off, leaving the solid sulphide in the casserole in

Jan 1, 1915

By T. L. Joseph

The extent to which hot metal from the blast furnace affects open-hearth practice and the quality of steel produced has been discussed widely. Open-hearth operators have attributed difficulties experienced in making satisfactory steel to characteristics of the pig iron not disclosed by ordinary analysis. The commonest criticism of the iron has been that it is "physically cold" or "dirty." Often when the blast furnaces are working irregularly the quality of the iron is questioned. A cold hearth, slipping and hanging, the use in the past of unsintered flue dust, and the use of ores difficult to smelt have been associated with the production of iron of poor quality. The difficulty of the situation is that we have no proven yardstick for quality aside from ordinary analysis. Uniformity in analysis is recognized as being important, but the difficulty of changing the open-hearth practice when the iron analysis varies widely may not always be fully appreciated. Although the problem of correlating the characteristics of steel with those of pig iron is admittedly obscure, the effort of producers of quality steel to investigate all factors that may have a bearing on the final product is justified. This report contains data on the oxides in several hundred casts of basic iron produced in a furnace during the course of normal operation on Lake ores. Incidental to the study of the oxides in the iron, it was desirable to follow closely the temperature of the iron. The effect of temperature of the iron upon the silicon and sulphur present is discussed. A general relation between the basicity of the slag and the sulphur in the metal was developed. The amount and composition of oxides in the hot metal and in the steel bath during various intervals between melt-down and tap are discussed. Heats of rimmed steel, killed steel, and semikilled steel were investigated. The hot metal on individual heats was either all taken from a mixer or consisted partly of direct metal and partly of metal from the mixer. Samples of the iron for oxide determinations were

Jan 1, 1937

By T. D. Yensen

It is safe to say that of all the different materials that go to make up electrical machinery, iron is the most important. Upon its magnetic and electrical quality depends not only the efficiency of the machine but, to a very large extent, the cost. Aside from the mechanical strength, there are three characteristics of iron that are of importance in this connection, viz., magnetic hysteresis, electrical resistance, and magnetic permeability. In the homopolar machine, where the magnetic flux is unidirectional, permeability is the only important factor, but in all other machines the flux is reversed in one or more parts and causes losses due to hysteresis and eddy currents. The eddy-current loss depends largely upon the electrical resistance of the iron; the higher the resistance the lower the loss, under otherwise identical conditions. These hysteresis and eddy-current losses cause heating of the machine, and as they depend upon the magnetic density in the iron, this density must be regulated so that the heating shall not be excessive. If the hysteresis and eddy-current losses and the permeability of the magnetic circuit will permit an increase in the magnetic density, or, in other words, a decrease in the amount of iron, this in turn will mean a decrease in the amount of copper needed, with a consequent decrease in the copper loss. It is thus seen that, indirectly as well as directly, the above characteristics have an important bearing on both the efficiency and the cost of electrical machinery. In general, it may be said that iron for electrical machinery should have the following characteristics: (1) low hysteresis loss, (2) high electrical resistance, and (3) high permeability. These are the characteristics that investigators have been striving to attain since electrical machinery first came into use. Until the beginning of the present century, Swedish charcoal iron was regarded as the best grade of iron for magnetic purposes, and even now it ranks high among the various grades used. About that time Sir Robert Hadfield1 produced a number of iron alloys that revolution-

Jan 1, 1916

By Henry Fay

The erosion of guns is a complex problem which can be solved only by a detailed study of all the factors involved. In the present paper it is proposed to submit the results of observations and experiments which have extended over several years. Certain facts have been established and preliminary reports have been published.' Conclusions have been reached since then which, it is believed, are worth presenting for the purpose of promoting discussion, and with the hope that ultimately the whole truth will be known. The particular phase of the problem which will be presented here is the hardening of the inner surface of the gun tube. It has been known for a long time that after firing a large caliber gun for some time, the surface of the metal becomes hard and brittle, cracks, and wears away.2 The character of this phenomenon may be learned by an examination of some results which are typical, obtained from a detailed study of a 12-in. gun. The gun was trepanned and rings representing various sections of the gun were cut out for examination. The first ring represented the metal at the muzzle end, and the other rings were removed at approximately 120, 240, 325 and 337 in., respectively, toward the breech end. The appearance of the surface of the metal in the different sections is shown in Fig. 1. The greatest amount of wear and maximum amount of hard surface layer was found in section marked E, which is nearest the powder chamber and at the beginning of the rifing; the maximum amount of cracking in D; the maximum amount of copper deposition in C. Section B showed heat cracks on both lands and grooves, and section A showed heat cracks on the driving edge of the lands only. There was much flow of metal in both sections E and D, and there was progressively less effect noticeable toward the muzzle end. The polished cross-section of these same pieces is shown in Fig. 2. The extent of the erosion is greatest nearest the powder chamber, and diminishes toward the muzzle end.

Jan 1, 1917

By John H. Hall

The Frémont test for measuring the energy consumed in breaking a notched bar of steel is not so well known in this country as it deserves to be. The test specimen used in this test is about # by 6 by about 16 in., notched with a hack saw on the lower side to cause the piece to break at a fixed point. A weight of 10 kg. falling 4 m., and provided with a knife or chisel which strikes the specimen, breaks the test piece by impact. The residual force in the falling weight after it has broken the specimen is recorded by a suitable device, and the difference between the total energy and the residual energy of the weight (in kilogrammeters) is the force consumed in breaking the specimen. An experience of several years with the Frémont testing machine has shown its great value in readily detecting brittleness not revealed by tensile testing or slow bending testing. In this paper it is proposed to discuss (1) the supersensitiveness of the test as applied to cast steel and (2) its value in revealing the effect of heat treatment under certain conditions. In testing coupons cut from castings heat treated by quenching and annealing, attention was drawn to the wide variations in the value of the Frémont test of specimens cut from different parts of the coupon. The latter was of the form and dimensions shown in Fig. 1, and Fremont test pieces were cut from two parts of this coupon, marked A and B in that figure. The results of the tests are shown below, tests A and B in each instance being from the same coupon: A. B. A. B. Coupon. Kilogram- Kilogram- Coupon. Kilogram- Kilogram- meters. meters. meters. meters. 1,........ 12.0 12.5 9,........ 27.5 32.5 2,........ 11.0 32.5 10,........17.5 31.0 3,........ 11.5 30.0 11,........ 14.5 31.0 4,........ 20.0 33.0 12,........ 15.0 27.5 5,........ 17.5 33.0 13,........ 19.0 30.0 6,........ 17.5 20.0 14,........ 17.5 25.5 7,........ 17.5 13.0 15,........15.0 30.0 8,........ 10.0 30.0

Jan 1, 1914

By Cyril Wells, Robert F. Mehl

The purpose of this investigation was to prepare high-purity iron-carbon alloys, to determine as precisely as possible the A3(GOS), the Acm(SE), and the A1(PSK) transformation temperatures in the meta-stable iron-iron carbide system (up to 1.4 per cent C), and to study the influence of carefully controlled and constant rates of heating and cooling (1/8 to 2o C. per minute) upon the transformation temperature and upon the resulting microstructure. Apart from the general metallurgical importance attending the completion of such a task, it will be noted that highly precise transformation temperatures are of interest and importance in the thermodynamic study of this system1. Several determinations of the iron-iron carbide diagram have been made2. These suffer generally from the low purity of the alloys used, and from the application of methods of investigation of low sensitivity. Attempts to compare and weight the many data available in an effort to construct as accurate a diagram as possible have, in the main, been unsuccessful. In general, the wide differences in the results of different workers, the lack of complete analytical data, the omission of important details relating to the heat-treatment of the alloys, and the meager description of the methods of investigation applied, render such a process of averaging nearly meaningless. It may be seen from the summaries by Epstein2 and Körber and Oelsenl that variations as great as 30' C. exist in the reported data on the A3 temperatures in iron-carbon alloys. Fortunately, the Aa temperature in pure iron is now known to be 910" C. ± 1° C.3 The best recent work on iron-carbon alloys is that of Esser4 on hypoeutectoid steels and that of Sato5 on both hypoeutectoid and hyper-eutectoid steels. Esser made a dilatometric and magnetic study of iron and iron-carbon alloys containing 0.06 to 0.86 per cent C, for which a high purity is claimed. Presumably the electrolytic iron was reasonably pure, but the alloys contained considerable impurities, on the average totaling 0.35 per

Jan 1, 1937

By Leonard Greenburg

The American literature in the field of dust sampling and analysis has been growing rapidly since 1915. Studies made since that time clearly indicate that there are three fundamental factors that determine the production of lung pathology due to dust inhalation. These are the duration of exposure, the chemical and mineralogic nature of the dust and the concentration of the potentially harmful dust. In the estimation of the amount of the potentially hazardous dust there are essentially three problems involved: (I) a determination of the size of the hazardous dust; (2) determination of the most satisfactory apparatus and technique of sampling, and (3) the most satisfactory method of analysis. A complete study of the literature shows that industrial dust varies ill size from ultramicroscopic particles to those larger than lop in diameter and that relatively few particles are found over 5u in diameter. Approximately 10 to 25 per cent are less than 0.811 in diameter and the median size as a rule is found to lie between 1.25 and 1.75 microns. From the point of view of lung pathology the particle sizes of most importance lie between 0.5 and 5u. Of all the instruments for sampling dust the Impinger apparatus is the only one that will sample a larger body of air satisfactorily with small control errors and high efficiency in both low and high concentrations of dust. The Owens apparatus has the advantage of being more portable and somewhat easier to use but it does riot permit of the sampling of large volumes of air. It has a low efficiency in high concentrations of dust and does not permit dust weights to be obtained. From the point of dust-counting technique the author points out that in 1922 considerable experimentation with dark field and oblique illumination resulted in the conclusion that such methods were not readily duplicated from day to day and therefore yielded somewhat erratic results. Changes in the amount of illumination produced variations of several hundred per cent in dust counts obtained with dark ground

Jan 1, 1934

Air-sand Process of Cleaning Coal Discussion of paper by THOMAS FRASER and H. F. YANCEY, presented at the New York Meeting, 1926, and issued, as Pamphlet No. 1561-F, with MINING AND METALLURGY, February, 1926. T. DEVENNY, Edgarton, W. Va.-How near the size of the sand can the coal to be treated be brought? Do you use an 8-mesh coal on that cleaner? J. J. RUTLEDGE, Baltimore, Md.-From the little I have seen of the apparatus in operation, I should say 8-mesh. In my experience in metalmine concentration work, trying to separate different minerals on one jig, sometimes I have succeeded and sometimes not. This apparatus has appealed to me; something of this kind should be useful with the silicates and carbonates of zinc. I think this apparatus has possibilities in metal mining. Recently in our coal field a screen has been introduced for cleaning coal; it is giving excellent service. When I asked the inventor why he did not take it to the metal mines, he said there was a good and sufficient reason, in a patent way. There may be reasons why it would not be applicable for metal mining; but the simplicity of it appeals to me and I cannot see why it could not be so used. T. FRASER (written discussion).-We feel that 8-mesh would be about -the minimum size of coal practicable to treat by the air-sand process. This would depend partly upon the friability of the coal. The more nearly the lower size limits of the coal- approaches the size of the sand, the more .time will be required in screening the sand out of the cleaned coal, which would mean a little more chance of breakage. In regard to the treatment of ores; this would necessitate the use of some heavier mediums than ordinary silica sand, or some other means of making the separation at a higher specific gravity than is required for coal. We are now working on a method of obtaining this effect for the preparation of anthracite coal without resorting to the use of heavier and more expensive material than common sand.

Jan 1, 1927