By R. W. Gurry, L. S. Darken

The solubility of cementite in austenite is computed by thermodynamic methods from the observed solubility of graphite. It is found that the solubility of cementite is greater than that of graphite in the entire austenite temperature range. Thus the prior discrepancy between this portion of the phase diagram and the observed metastability of cementite is partially resolved. FOR several years it has been apparent that a serious discrepancy exists in certain observations pertaining to the Fe-C system. Direct experimental data indicate: 1-That the curve representing the solubility of graphite in austenite'" crosses that for cementite4 at about 945°C as shown in Fig. 1. 2— That graphite and austenite saturated therewith are stable1 relative to cementite at all temperatures between the eutectoid, about 723°C, and the eutectic, about 1153°C. These observations are mutually incompatible in view of a well-known consequence of the second law of thermodynamics, namely, that the stable phase (presumably graphite at all temperatures) has a lower solubility than the metastable phase (presumably cementite). Hence either 1 or 2 above must be in error; either the measured solubility of graphite or of cementite, or the observation as to the stability of graphite, is in error. Our present purposes are: 1—To collate the available data on cementite and prepare a table of HO — HO° and of (Fa— HO°)/T. This tabular method seems the best and most convenient way to represent the heat and free energy of formation. 2—To determine whether the measured solubilities of cementite and graphite in austenite are in accord with the above table and the measured thermodynamic properties of austenite, in order to resolve, if possible, the existing paradox of these two solubilities. Enthalpy of Cementite The enthalpy of cementite at 273 °K, H279 — HOcem, was computed by integration of the low temperature heat capacity as measured by Seltz, McDonald, and Wells" 68" to 298 °K) and as given by the Debye functions recommended by them (0" to 68°K); the result is included in Table I. At higher temperature HCem — H,,"" is given by Kelley who used the data of Naeser7 (298" to 1037°K) and of Umino8,9 (273° to 1923°K). We have recalculated Hcem — H273 cem from the data of UminoO in the following way. In the equilibrated alloy at temperature the weight fraction of cementite Pct c -Pct cr is PctC -PctCr designated f(C), and the

Jan 1, 1952

By Francis B. Foley

Fundamentally, slag control in acid open-hearth steelmaking cannot be considered from any different viewpoint than can that in basic open-hearth melting. The same laws of mass action and distribution apply in both cases, so that while most, if not all, of the recent intensive study of slag-metal reactions have been carried on in basic furnaces the principles evolved are nevertheless applicable to acid open-hearth steelmaking and it is therefore not our intention to discuss the various possible chemical reactions in the slag and between slag and metal. The points we have to carry in mind, in considering acid melting practice, are the differences in the type of steels produced and the difference in the chemistry of both the steel and the slag. The acid furnace is used to produce, let us not say "quality" steel, for, after all, a "quality" steel for one purpose is not a "quality" steel for another, but steels that require acid melting practice to be of proper "quality." Steels that are required to have high physical properties in tests taken transversely from forgings are peculiarly the product of acid furnaces. In this class may be placed various ordnance materials, notably gun forgings and projectiles and large commercial forgings requiring high transverse ductility. Forgings requiring an extremely hard surface, polished and free from imperfections, are also typical acid-steel products. Of course, such forgings can be made of basic open-hearth steel, but not with the same assurance of success. At the start, the preparation of the slag in the acid and basic furnaces differs. Lime is charged in the beginning of a basic heat to form a slag, but in the acid furnace nothing is added for the special purpose of producing a slag when the heat is melted down. The result is that the acid furnace has much less volume of slag than the basic. The slag formed upon melting down is made up almost entirely of the oxides of elements contained in the metallic charge, notably oxides of iron, manganese and silicon, the amount of silica being augmented somewhat by erosion of the furnace lining. A typical acid open-hearth slag, when the bath is completely melted, will have an analysis about as follows: CaO, 3.40 per cent; SiO2, 51.9; Fe2O3, 1.25 ; FeO, 28.86; Al2o3, 1.82; MnO, 12.22. The high iron oxide content of the slag gives it a black appearance. The metal is high in carbon and some manganese and silicon will be present, depending on the amount in the original charge, the amount of

Jan 1, 1935

By Francis B. Foley

Fundamentally, slag control in acid open-hearth steelmaking cannot be considered from any different viewpoint than can that in basic open-hearth melting. The same laws of mass action and distribution apply in both cases, so that while most, if not all, of the recent intensive study of slag-metal reactions have been carried on in basic furnaces the principles evolved are nevertheless applicable to acid open-hearth steelmaking and it is therefore not our intention to discuss the various possible chemical reactions in the slag and between slag and metal. The points we have to carry in mind, in considering acid melting practice, are the differences in the type of steels produced and the difference in the chemistry of both the steel and the slag. The acid furnace is used to produce, let us not say "quality" steel, for, after all, a "quality" steel for one purpose is not a "quality" steel for another, but steels that require acid melting practice to be of proper "quality." Steels that are required to have high physical properties in tests taken transversely from forgings are peculiarly the product of acid furnaces. In this class may be placed various ordnance materials, notably gun forgings and projectiles and large commercial forgings requiring high transverse ductility. Forgings requiring an extremely hard surface, polished and free from imperfections, are also typical acid-steel products. Of course, such forgings can be made of basic open-hearth steel, but not with the same assurance of success. At the start, the preparation of the slag in the acid and basic furnaces differs. Lime is charged in the beginning of a basic heat to form a slag, but in the acid furnace nothing is added for the special purpose of producing a slag when the heat is melted down. The result is that the acid furnace has much less volume of slag than the basic. The slag formed upon melting down is made up almost entirely of the oxides of elements contained in the metallic charge, notably oxides of iron, manganese and silicon, the amount of silica being augmented somewhat by erosion of the furnace lining. A typical acid open-hearth slag, when the bath is completely melted, will have an analysis about as follows: CaO, 3.40 per cent; SiO2, 51.9; Fe2O3, 1.25 ; FeO, 28.86; Al2o3, 1.82; MnO, 12.22. The high iron oxide content of the slag gives it a black appearance. The metal is high in carbon and some manganese and silicon will be present, depending on the amount in the original charge, the amount of

Jan 1, 1935

By W. H. Gunniss

When the copper smelters were built, in Montana, all of the refractory products which were used in their construction were shipped in from Eastern factories. It was apparent that if a material suitable for the manufacture of these products could be found within the State, a saving of freight could be effected and a new industry built up. Prospecting for such materials was started and experiments were made with samples from numerous deposits. Considerable effort and funds were expended in an attempt to manufacture silica brick from Dillon quartz, a light colored sandstone that is found near Dillon, Mont., on the Oregon Shortline railroad. As a brick material the Dillon quartz was a failure, but it has proved very satisfactory as a silica cement. It is now being used in laying silica brick and for reverberatory furnace bottoms. A bed of quartzite that is particularly suited to the manufacture of high-grade silica brick was finally discovered at Browns Spur, 6 miles west of Anaconda. The material from this deposit is now being used in the manufacture of the Anaconda silica brick, which have gained a wide reputation for heat-resisting and lasting qualities. The analysis of an average sample of this quartz is: SiO2, 96.7; Fe2O3, 0.3; Al208, 2.5; CaO, 0.3 per cent. The very low percentage of fluxing ingredients makes this a most refractory material. All of the Anaconda silica brick are hand molded. Various types of brick machines have been tried, but the hand-mold process proved the best suited to the manufacture of silica brick from this material. The silica is first put through a jaw crusher and is then dumped into wet pans, where 4 per cent. of lime paste is added, to produce a bond. Without the lime the material would not be plastic enough to mold. After a few minutes' grinding in the wet pans the material is conveyed to the molder, who forces it into the molds by hand. The brick are then dumped on pallets and placed in the drier, where they are left. until dry enough to be set in the kilns. Some of the brick are re-pressed before being dried. They are burned about five days, in round down-draft kilns. It is not necessary to have as much heat in the kilns as the brick will be subjected to when in use in the furnaces. Montana refractories are used in smelters throughout the West. Prospecting for fire clays was also carried on. After experimenting with clays from several different deposits, it was found that a mixture of

Jan 1, 1914

By C. Chiou, D. P. Seraphim

The effect of clustering on the superconducting properties of Al-Zn alloys has been studied by the ballistic induction techniques. The superconducting critical temperature, T,, changes when zinc-rich clusters are formed. The change in T, depends on the concentration and may be positive or negative, but always correlates with an effective decrease in the solute concentration of the alloy. Reversion after clustering effectively returns a 5 at. pct Zn alloy to the quenched state. These methods might be use&lly extended to the Al-Mg system, where X-ray data are difficult to obtain. In very dilute Al-Zn alloys, as in other tin,' indium, aluminum,2 or tantalums base solid solutions, there is a decrease in the superconducting critical temperature, Tc, roughly proportional to the temperature independent resistivity, i.e., -0.2°K per pS2cm. With increasing solute concentration, the T, generally reaches a minimum and then increases4 to a value well above that for the pure solvent. The change of T, with solute concentration follows an empirical formulation involving two constants which correlate with the scattering cross section of the impurities. As will be shown below, the Al-Zn alloys more concentrated than 1or2at. pct do not follow the empiricism, probably because they are unstable even when rapidly quenched.5 However, it seems possible to study at least the later stages of solute clustering by precise measurements of the 1', following various thermal treatments. A few experiments on quenched alloys, aged alloys, and tests on reversion are reported here. The heat treatments selected for obtaining the quenched and aged states were mainly deduced from the work of Dash and Fine.6 For the quenched state, specimens were homogenized at 480°C, quenched to -160°C, and immediately transferred and mounted in liquid nitrogen. Measurements on the superconducting properties and residual resistivities were then made at helium temperatures, after which the specimens were aged at room temperature for 3 to 5 hr, i.e., much longer than the time required for clustering to be essentially completed. The superconducting properties and residual resistivities were once again examined. To reach the reverted state of the A1-5at. pct Zn alloy, the aged specimen was heated for 5 min at 200°C and then tested as above.

Jan 1, 1963

By Walter O. Snelling

In the course of some experiments more than five years ago, made for a totally different purpose than the investigation of the oil used, I placed a small quantity of a transparent yellow lubricating oil in a bomb-like vessel and heated it to a relatively high temperature. At the end of the experiment I removed the oil from the vessel and was amazed to find that instead of bearing any resemblance to the oil which I had put in, it now had the appearance of ordinary crude oil. The green color by reflected light and the rich red-brown by transmitted light were so unmistakable as to at once lead to further investigation. I subjected the material to fractional distillation, and the surprise which I experienced at the appearance of the oil, changed to amazement when I found that it yielded, on distillation, 15 per cent. of gasoline and 30 per cent. of burning oil, and that its constitution resembled crude oil quite as much as did its appearance. Furthermore, the gasoline and kerosene distillates which it yielded were of a clear water-white color, entirely without treatment with acid or alkali, and were entirely free from the odor familiar in "cracked" petroleum distillates. The result of this experiment was quite too remarkable to be credited without further confirmation, and I at once filled the vessel with some of the same oil that I had used before, and again heated to about the same temperature that I had previously used, and for the same period of time. Upon opening the vessel and removing the contents I found, not the material resembling crude oil that I had obtained before, but apparently only the same oil that I had put in, somewhat darkened in color, but nevertheless far different in appearance from the material obtained in the previous experiment. Evidently some condition existed in the first experiment that had not existed in the second test, and here began a series of tests in which I sought by the change of one variable after another to arrive at the identical conditions which must have existed in the first experiment. Only the fact that the bottle of heavy oil used in the first test was still in its place,

Jan 1, 1915

By George W. Maynard Maynard

IN this paper I desire to embody the results of some personal observations of the working of the Siemens direct process as I witnessed it for a part of three days at the works of the Siemens-Anderson Company, in Pittsburgh. This preliminary investigation was to have been followed up by one extending over a considerable period of time, and would have embraced analytical and physical tests. Circumstances over which I had no control, resulting in the temporary suspension of work, have postponed the presentation of a complete paper. If the opportunity is afforded me, I purpose doing this at a future meeting of the Institute. To those interested in the development of the process, reference is made to the papers of Dr. Siemens in the Journal of the Iron and Steel Institute for the years 1873 and 1877, and to the paper of our late lamented brother, Holley, in the 8th volume of the Transactions of our own Institute. Dr. Siemens, in the introduction to his paper "On the Manufacture of Iron and Steel by Direct Process," read before the Iron and Steel Institute in September, 1877, says: " In mixing comparatively rich iron ore in powder with about 25 per cent. of its weight of pounded coal, and in exposing this mixture for some hours to the heat of a common stove or of a smith's fire, metallic iron is formed, which, on being heated to the welding-point on the same smith's hearth, may be forged into a horseshoe of excellent quality. The admixture with the ore of some fluxing materials, such as lime or clay, will, in most cases, be of advantage to rid the iron of adherent slag." This is the keynote of the Siemens direct process. Dr. Siemens says further: "If we regard the production of wrought iron from an abstract point of view, we perceive that we have to accomplish two things, viz., the deoxidation of the ore, and the fusion of the earthy matter .mixed with it; and if we calculate the amount of carbon necessary to accomplish this end, we shall find that in using, say, hematite ore, consisting of peroxide of iron with from 10 to 15 per cent. of silica, we shall require barely 40 per cent. of carbonaceous matter per ton of iron contained in the' ore to effect its reduction, and also the fusion of the slag."

Jan 1, 1882

By C. R. Fondersmith, John Chipman

In the manufacture of rimming steel—which constitutes the bulk of the world's production of mild steel—the factors that determine the quality of the product are very closely associated with the pouring and solidification of the steel in the ingot mold. The behavior of the metal in the mold is, on the one hand, the resultant of the complex processes through which the liquid metal has passed, and, on the other, it is an indication of the probable behavior of the ingot during subsequent rolling and finishing operations. A detailed study of the mechanism of solidification of rimming ingots ought to yield information that will be useful in controlling the structure of the ingot and the quality of the ultimate product. The first step in such a study is to determine the rate at which the solid shell of the ingot forms from the liquid metal in the mold. A knowledge of the rate of solidification will make it possible to correlate observations of rimming action and gas evolution with studies of the structure, porosity, and segregation within the ingot. Thus, if the metal in the mold is observed to fall, let us say one minute after pouring, the portion of the structure associated with this fall will be located in the part of the ingot that is solidifying at that particular moment. The knowledge that the ingot solidifies to a depth of 3/4 in. in the first minute enables us to locate in the ingot the structural features corresponding to the observed fall. Conversely, the blowhole condition associated with a rising or growing ingot will be found in the part of the ingot that is solidifying at the time the phenomenon occurs. The time required for the complete solidification of an ingot has long been a matter of speculation. It is of considerable practical importance in connection with charging and heating in the soaking pits. Too rapid handling of the ingot through heating and rolling processes has been thought to be associated with excessive pipe and other internal defects, so that a further object of this investigation was to attempt to estimate the time required for complete solidification, or the minimum practical time within which the subsequent operations can be performed with the minimum hazard.

Jan 1, 1937

By G. W. Maynard

In this paper I desire to embody the results of some personal observations of the working of the Siemens direct process as I witnessed it for a part of three days at the works of the Siemens-Anderson Company, in Pittsburgh. This preliminary investigation was to have been followed up by one extending over a considerable period of time, and would have embraced analytical and physical tests. Circumstances over which I had no control, resulting in the temporay suspension of work, have postponed the presentation of a complete paper. If the opportunity is afforded me, I purpose doing this at a future meeting of the Institute. To those interested in the development of the process, reference is made to the papers of Dr. Siemens in the Journal of the Iron and Steel Institute for the years 1873 and 1877, and to the paper of our late lamented brother, Holley, in the 8th volume of the Transactions of our owu Institute. Dr. Siemens, in the introduction to his paper "On the Manufacture of Iron and Steel by Direct Process," read before the Iron and Steel Institute in september, 1877, says: " In mixing comparatively rich iron ore in powder with about 25 per cent. of its weight of pounded coal, and in exposing this mixture for some hours to the heat of a common stove or of a smith's fire, metallic iron is formed, which, on being heated to the welding-point on the same smith's hearth, may be forged into a horseshoe of excellent quality. The admixture with the ore of some fluxiug materials, such as lime or clay, will, in most cases, be of advantage to rid the iron of adherent slog." This is the keynote of the Siemens direct process. Dr. Siemens says further: " If we regard the production of wrought iron from an abstract point of view, we perceive that we have to accomplish two things, viz., the deoxidation of the ore, arid the fusion of the earthy matter mixed with it; and if we calculate the amount of carbon necessary to accomplish this end, weshall rind that in using, say, hematite ore, consisting of peroxide of iron with from 10 to 15 per cent. of silica, we shall require barely 40 per cent. of carbonsceous matter per ton of iron contained in the ore to effect its reduction, and also the fusion of the slag."

Jan 1, 1882

By William R. Webster

I have continued the investigation of the Pottstown Iron Com pany's basic Bessemer keel plates on the line referred to in my paper of last October (Trans., xxi., 766)) and have added a study of the hardening effects of sulphur, which were not taken into account at that time. The results are so encouraging that I now give them in full. For some months we have graded all the steel at these works by the table given in my former paper, and checked the grading by the forging-tests as described in the paper of Mr. Joseph Hartshorne, read at the same meeting (Trans., xxi., 748). The steel thus graded was bloomed for the plate orders. Then one slab was rolled into a plate for the order, and a tension-test was made of this plate. By the result of this tension-test we were guided in rolling the balance of the heat. Out of several hundred heats graded in this manner, 95 per cent. met the requirements of the orders in every respect, and were accepted; but these results will no doubt be improved upon, when the influence of sulphur is also considered.. The hardening effect of sulphur seems to be about 500 pounds per each .01 per cent. of increase. In the table accompanying the pres ent paper, the ultimate strength with .06.5 per cent. sulphur agrees with the old table where sulphur was not considered; that is, for all steels with less than .065 per cent. sulphur we now get lower re sults, and for those with more sulphur, higher results. Making this allowance for sulphur, the assumed ultimate strength of a 3/8-inch plate of pure iron is reduced from 38,000 pounds per square inch to 34,750 pounds. With this as a basis, I have constructed my new table, giving each of the elements, carbon, phosphorus and manganese the same hardening effect as before, to wit : Carbon is credited with a constant effect of 800 pounds per each, 0.01 per cent. Phosphorus shows greater effect in high-carbon than in low-carbon steels. For 0.07 and 0.08 C, it has about the same effect as carbon, that is, 800 pounds for each .01 P. This increases to 1500 pounds per .01 P in 0.15 C steel, or nearly twice the effect of carbon. This

Jan 1, 1894

By W. W. Cotter, W. R. Clark

WEBSTER tells us the word "extrude" means to "force, press or push out; to protrude." As applied to the metal industry, the process consists largely of forcing plastic elements (plasticity usually obtained by preheating), through dies of predetermined profiles, into constant sections of considerable length and weight. Most of the "virgin" metals are quite malleable under this process, likewise many of the commonly used "alloys" in various industries, when basic elements are proportioned or combined within the natural laws and limits of good metallurgy. Several of the foundry alloys, both ferrous and nonferrous, together with some of the heat-treatable light metal mixtures, are decidedly weak and hot short at ordinarily plastic ranges, and consequently are troublesome or quite incapable of commercial extrusion. DEVELOPMENT OF PROCESS This process was conceived some time before 1800 and during its first century was employed almost entirely in making lead pipe, plumbing fittings and coating electrical cables. As a result of contact and experience with the lead industry and presses, Alexander Dick, of London, England, is credited with first having applied the principles of extrusion to brass, and in 1894 brought out a 500-ton horizontal press powered by hydraulics. A duplicate of this unit was imported by one of the Connecticut brass mills and was in experimental operation by 1900. During the first five years of operation, this press proved the value of the method to American industry, as it immediately revolutionized and converted the manufacture of brass rod from a 15-pass cold-rolling operation, with elimination of several intermediate anneals and cleanings, to an extrusion and a finishing draw. Likewise, ornamental brass and bronze moldings formerly cast and machined were produced in one squeeze on the extruder. The extrusion operation, being entirely that of compression, deforms the material without tensile stresses and can be used on delicate mixtures under heat, which cannot be hot-worked by straight hot-rolling or roller piercing. Base slabs of clock-brass strip were early in line of development or improvement, as were the brass bronzes (Naval brass, Muntz metal, manganese bronze, and others), popular as engineering materials for bolt stock, as well as structural shapes for marine and other mild conditions of corrosion. By 1910, American engineers undertook to design tube shell extruders, but were unsuccessful. The first World War began before fabricators could procure the more substantial designs of tube extruders produced in Germany; and it was not until the middle twenties that better models of the Universal extruders (double-actioned presses), equipped with hydropneumatic accumulator systems and other modern equipment, were available in the United States.

Jan 1, 1945

By J. Gordon Parr, D. H. Polonis

High purity alloys of titanium and iron, made by a technique of levitation melting, have been investigated with particular reference to martensite formation and decomposition in the hypoeutectoid range. A preliminary study has been made of the occurrence of the phase corresponding to the structure Ti2Fe. MANY of the previous investigations of Fe-Ti alloys have been made using Kroll sponge as a source of titanium; and the subsequent heat treatments to which alloys have been subjected has, on occasion, led to further contamination. Worrier,',' who suggested a part of the equilibrium diagram for the binary system, and Wallbaum and coworkers,3-5 who worked largely with iron-rich alloys, all used Kroll sponge. Van Thyne, Kessler, and Hansen,6 in their determination of the equilibrium diagram, used iodide titanium for alloys up to 30 pct Fe. Duwez,7 who measured the M. temperature of titanium binary alloys with many solute elements, used iodide titanium in all cases except in his work on Ti-Fe alloys for which he used Kroll sponge. The investigation of the supposed phase Ti2Fe by Rostoker8 nvolved the use of iodide titanium. A section of the constitutional diagram, after Van Thyne et al., is reproduced in Fig. 1. Frequently too much stress is placed on the effect of contaminants in equilibrium and nonequilibrium systems, but there is no doubt that titanium alloys are extremely susceptible to interstitial atoms. Consequently, the main purpose of the work to be described was to determine those features of phase transformations in pure Ti-Fe alloys that were considered of importance in commercial heat treatments. For, although commercial alloys may not be of high purity, the investigation of a system uncomplicated by traces of impurity is a desirable starting point. Another incidental feature, the occurrence of Ti2Fe, was also investigated. The entire study was carried out using powders obtained from alloy ingots, for diffusion reactions are often more rapid in small particles than in bulk specimens. The frequently adopted practice of ascertaining phase constitutions by X-ray analysis of powders, and relating these to the microstructures and mechanical properties of bulk specimens, is considered by the authors to be open to criticism. In the martensite reactions in the Fe-Mn system, for example, it has been shown- hat similar phase distributions in solid and powder may result in different hardness values and appearance under the microscope; and it is possible that similar anomalies might occur in the Ti-Fe system. Consequently, in order to

Jan 1, 1955

By John Chipman

DESPITE the rapidity of chemical reactions at steelmaking temperatures, deoxidation reactions cannot be expected to reach equilibrium immediately after addition of a deoxidizing agent. A considerable period of time may be required merely to obtain complete mixing of the deoxidizing element throughout the volume of steel to which it is added. Evidence in the literature indicates that in some cases the time is long compared with that allowed for completion of the experiment or for teeming of the heat. The great turbulence observed during the filling of the ladle is no guarantee of complete dispersion on a fine scale throughout the heat. During the process there are initially certain volume elements which are high in deoxidizer and others which retain substantially their original oxygen content. Mixing consists of the subdivision and ultimate destruction of these liquid segregates through the process of shear and elimination of concentration gradients by diffusion. The shear process does not continue indefinitely and a quiescent state may be reached in the ladle before all volume elements of divergent deoxidizer and oxygen content are completely eliminated. In furnace deoxidation the time required for complete mixing may be very long unless continuous stirring is employed.' In Fig. 1, let the circle represent one small volume element of aluminum-rich metal surrounded by oxygen-rich steel in which no stirring movement remains. Further mixing requires inward diffusion of oxygen and outward diffusion of aluminum, resulting in precipitation of A12O3 in the diffusion zone. It is important to note that such a precipitate may itself interfere with the diffusion process. Moreover, if the precipitate forms as a film with even minimal mechanical strength, it may interfere not only with diffusion but with shear as well, thus stabilizing compositional differences in volume elements of greater than microscopic size. A film surrounding such a volume element would have little or no ability to rise or to sink unless it enclosed a liquid whose density differed from that of the ambient. Consider now the effect on the overall composition of the melt. Fig. 2 represents the A1-O equilibrium at the temperature of the bath. High-aluminum elements of composition X may exist alongside high-oxygen elements of composition Y in such proportions that the average composition 2 has a much higher A1-O product than that corresponding to equilibrium. The A1-O product supposedly corresponding to equilibrium at 1600 °C was found by Wentrup and Hieber2 to be 10-10, by Hilty and crafts3 to be 2 X 10-9 and by Gokcen and chipman4 to be 2 x 10-14. Only the last named investigators approached equilibrium by means

Jan 1, 1962

By Walter Showak

The published phase diagrams for the copper-zirconium system1,2 indicate that the solid solubility of zirconium in copper is not accurately known. Studies made on relatively impure alloys by Pogodin, Shumova, and Kugucheva3 yielded a maximum solubility value of 1 wt pct Zr at the eutectic temperature. Allibone and sykes5 reported that an as-cast 0.2 wt pct Zr alloy is single phase at room temperature. Limited results obtained by Raub and Enge14 indicated that zirconium solubility in copper is less than 0.13 wt pct Zr at 940°C. Tn 1960, on the basis of a microstructural examination of several copper-rich Cu-Zr alloys, saarivirta6 placed the maximum solubility of zirconium in copper at 0.15 wt pct at the eutectic temperature, 980°C. The present note describes results obtained during a re-investigation of the Cu-Zr system for the purpose of accurately establishing the solidus and solvus curves and the eutectic temperature in copper-rich alloys. High-purity copper (99.99 pet) and zirconium (99.64 pet) consolidated reactor grade sponge were used to prepare several alloys, containing up to 2 wt pct Zr, by induction melting in graphite crucibles in vacuum and chill casting into a split steel mold. The melting procedure consisted of first melting the copper charge and then adding the bulk zirconium wrapped in pure copper foil. Chemical analyses were made of both the cold-rolled alloy ingots after homogenization at 925°C for 450 hr in evacuated quartz capsules and of small specimens which had been used in the phase diagram studies. 'The carbon content of each alloy was also determined and was found to be less than 0.001 wt pct in every case. Metallographic and electrical resistivity measurements were used as the primary methods for this investigation, although some thermal analysis studies were also performed. Heat treatments of all the alloys were carried out with the specimens wrapped in molybdenum or alloy foil (of the same composition as the specimen) and sealed in quartz tubes either in vacuum or under a purified helium atmosphere. Following high-temperature anneals for long periods of time, slight depletion of zirconium from the specimen surface was observed. Therefore, careful preparation of samples for microscopic examination and chemical analysis of the samples themselves was necessary to check the composition of samples used in determining phase boundaries. Points on the solvus curve were determined on quenched specimens by both isothermal reaction after solution heat treatment at 950°C for 8 hr and by isothermal annealing of alloy specimens at successively higher temperatures for times ranging from 24 to 500 hr. Liquation studies for positioning of the solidus and eutectic temperatures were performed by holding a pre-

Jan 1, 1962

By Reuben B. Ellestad, Fremont F. Clarke

Lithium chemical plant extraction methods are discussed with reference to 1) base exchange with alkali sulphates; 2) processing based on roasting with lime; 3) miscellaneous methods; and 4) application of the Lithium Corp. process to extraction of lithium from run-of-mine, low grade spodumene ore, or concentrates. IN the early days of the lithium industry most of the production was from lepidolite, zinnwaldite, and amblygonite. Nearly all the early extraction processes described in the literature involve heating the finely ground mineral with sulphuric or hydrochloric acid. On subsequent water leaching most of the bases present in the mineral (especially aluminum) are dissolved as sulphates. As a result, the leach solution required extensive chemical purification before the lithium could be precipitated as carbonate. Following the remarkable growth of the lithium industry to its present size, zinnwaldite and amblygonite ores must be considered of minor importance only. Attention is now focused on spodumene, abundant enough in North America to be a major source of supply, and there are important supplies of lepidolite and petalite in Africa. The extraction processes described below all apply to spodumene, although several will also operate on other lithium minerals, such as petalite. Base Exchange with Alkali Sulphates: A distinct advance was made with the disclosures of Wadman and von Girsewalt. In these methods the finely ground silicate ore (spodumene or lepidolite) is intimately mixed with an excess of alkali sulphate (usually K2SO4) in at least a 1 to 1 proportion, and the mixture was heated to a relatively high temperature. Base exchange results, with the formation of lithium sulphate. A water leach dissolves the lithium sulphate, together with the excess potassium sulphate. Successful operation of this type of process requires very thorough grinding and mixing, as well as careful temperature control. The use of K2SO4 is objectionable from cost considerations since purification of lithium carbonate requires the use of potassium carbonate, if the K2SO4 is to be recovered and recycled. The lower solubility of K2SO4 as compared with Na2S04 is also objectionable, since it limits the concentration of the Li2SO4 solution to be precipitated by K2SO4. Early laboratory-scale investigation of this process by Lithium Corp. was not encouraging. Other related base exchange processes are those of Lindblad, Wallden, and Sivander3 and Sivander, Gard, Villestad, and Wallen4. The former covers the reaction of lithium silicate minerals with a sodium sulphate solution, at 100" to 300°C (under pressure), while the latter involves the extraction of silicate minerals with molten sodium sulphate. Both these processes would seem to be difficult and expensive to operate.

Jan 1, 1956

By M. T. Worley

This paper reports investigative work conducted to develop a method of estimating the groundwater influx from a homogeneous permeable formation into a vertical mine shaft during sinking. A method of analysis was developed using data obtained from pumping tests and a modification of the Theis non-equilibrium interpretation technique. Excess influx of groundwater into mine shafts has long been one of the more important problems encountered in the development of a mining property. Much work has been done on methods of preventing such influx and on pumping schemes to control inflow if preventive measures fail. The fundamental aspects of the problem, on the other hand, seem to have been neglected. The purpose of this paper is to review the fundamentals of groundwater flow and to propose a rapid method of analyzing hydrologic data in order to estimate influx from a homogeneous permeable formation into a mine shaft. Such an estimate of the quantity of water to be encountered is of value in planning grouting, pumping and other programs designed to control that influx. It is emphasized that the proposed method of analysis should be regarded only as a tool to be used in evaluating the problem before investing the capital necessary to begin development of a property. FUNDAMENTALS OF GROUNDWATER FLOW In order to effectively approach the problem of estimating influx into a mine shaft, a knowledge of the fundamentals of fluid flow through a porous medium is necessary. Darcy, in 1856, developed an empirical relationship to explain the flow of water through sand filters. This relationship V = k (dh/dl), is the basis for all other flow formulae. It has been shown that Darcy's relation is a solution of the Laplace equation and thus is analagous to other natural phenomena such as heat flow. Theis, using the analogy of heat flow by conduction, developed an expression for determining the transient or time-dependent groundwater flow through a homogeneous, isotropic medium. The resulting equation Was also derived by Jacob using hydrologic considerations alone.' The individual terms in the equation are described in Table I. It is important to understand the assumptions upon which this equation is based. 1) The medium through which the fluid flows is infinite in areal extent, homogeneous and isotropic. 2) The well into which the fluid discharges completely penetrates the medium. 3) The characteristics of the medium remain constant at all times. 4) The initial pressure surface is horizontal. 5) The confining media are impervious and horizontal. 6) Fluid is removed from storage instantaneously by a decline in pressure. 7) The diameter of the discharge well is infinitesimal with respect to the drainage radius of the medium.

Jan 1, 1962

By S. Beatty

RECENT experimental results' on the superconductive properties of vanadium indicate that the magnetic behavior of the metal is greatly affected by internal strains caused by mechanical work, and particularly by oxygen and nitrogen impurities. These result in an increase in the hardness of the metal such that metallurgists' have used hardness as a measure of the impurities. An increase in the impurities should also be reflected in a change of lattice parameter with increasing impurity content. The lattice parameter of vanadium prepared by the thermal decomposition of the iodide has been determined by two workers. Neuburger3 obtained a value of a, =3.0338 ± 0.0003A for the body-centered cubic lattice by means of the powder method. The work of Katelaar is referred to by van Arkel4 in which a value of a0 = 3.025 is given. Four samples were used for this investigation. Sample A, the vanadium of the highest purity in the group, was obtained by means of the thermal decomposition of vanadium diiodide and deposited on a 3 mil diam tungsten filament in the form of crystals. The second sample, labeled B, was obtained by the calcium reduction of the pentaoxide at a sufficiently high temperature to give a melt. A third sample, C, was obtained in the same manner as B but remelted in a pure argon atmosphere. The last sample, D, was prepared by the calcium reduction method and the fine powdered vanadium was then sintered by means of applied heat and pressure. Samples A, B, and C were thus essentially free of mechanical strain in their preparation. Sample D was annealed in a high vacuum at 800°C. The samples were prepared for X-ray diffraction analysis such that all additional strain by cold work or by contamination with oxygen and nitrogen was kept at a minimum. Powder obtained from filings was deemed unsuitable since this would require annealing to get rid of the cold work. A heat treatment up to 1000°C at 10-6 m pressure might still increase the impurity content by means of adsorbed oxygen from residual gas in the vacuum chamber. The most satisfactory samples were prepared for back-reflection film techniques. Samples were cut to size, etched with hydrobromic acid, and mounted in Bakelite. They were then lightly polished on 3-0 paper and lightly etched. Chemical and Hardness Analysis of Samples Spectrographic analyses were made of the four samples and indicated similar metallic impurities for the group. The major metallic impurity in each sample was iron, which was less than 0.01 pct. The sum of the other metallic impurities was approximately 0.1 pct. The carbon content was assumed low by virtue of the methods of sample preparation. The principal impurity difference between the samples was in the oxygen and nitrogen content.

Jan 1, 1953

By W. A. Mudge

ONE of the most prominent features of our present-day industrial development is the ever-increasing demand put upon materials of con-struction. Engineering ingenuity, within the past 25 years, has been unusually active, and in some fields at least engineers frankly say that engineering design has progressed as far as the limitations imposed by the properties of the present materials of construction will permit. Consequently, they are today demanding improvement in their working materials and seeking new ones, through the aid; of which the present limitations of design may be overcome. The activity of this search is evident in all fields, but it is particularly so in that of structural materials required to be resistant to corrosion. The corrosion resistance of metals and alloys is never absolute and all-inclusive; a particular alloy will withstand some corrosive conditions well and fail utterly tinder others. Furthermore; other properties, physical and mechanical, required in-conjunction with corrosion resistance vary considerably for different commercial applications. One wants a soft, ductile sheet metal resistant to atmospheric corrosion; another, a high-strength- alloy resistant to sulfuric acid. The last decade has witnessed active and definite progress in the development of high-strength, corrosion-resisting alloys. In June, 1924, a symposium by the American Society for Testing Materials, on Corro-sion-Resistant, Heat-resistant and Electrical-resistance Alloys, disclosed no less than 60 commercial alloys the properties of which were described as being suitable for industrial service where corrosion resistance

Jan 1, 1935

By H. E. Stauss

THE time-to-fracture test has been applied to pure platinum and to two alloys of platinum under the special conditions of small cross-sectional area of the specimens and of a test temperature above the annealing temperature. While the results are similar in character to those secured with large specimens of steel at temperatures below the annealing temperatures, two differences are noted: (I) an upward inflection in the curves for log stress vs. log time for the alloys, and (2) a sharp break in the curve for log stress vs. log time for pure platinum when single crystals filled the wire. The experiments showed that: (I) platinum and 10 per cent rhodium-platinum maintained their strengths at 1100°C. better than did 10 per cent iridium- platinum, and (2) the rhodium-platinum after a time exceeded the iridium-platinum in strength at 1100°C. Platinum alloys in their service at high temperatures encounter conditions some- what similar to those that exist in the usual form of the time-to-fracture "l test with steel. This paper is intended primarily to present results obtained by a "time-to- fracture" test under conditions approximating actual service for platinum (at the temperature 1100°C. under oxidizing conditions) with three materials, pure platinum (99.99 per cent), a platinum alloy with lo per cent iridium, and a platinum alloy with 10 per cent rhodium. The experimental procedure differed from that previously used in this type of measurement in that the samples were of small diameter (0.010 in.), were fully annealed, and were tested at a temperature definitely above their annealing points (600°C., 1000°C. and 1050°C., respectively, for 60 per cent cold reduction and 15 min. heating time2,3). The experimental arrangement was similar to that previously described,4 using as heating unit a small, horizontal, platinum- wound furnace, ½ by 12 in., maintained at constant temperature by an automatic controller. The samples were 0.010-in. wires, which had been annealed at 1200°C. by drawing them slowly through the furnace. The time-to-fracture was measured electrically. Elongation was not determined because of the difficulties inherent in the experimental arrangement. Life-that is, the time-to-fracture-was considered the important property in these first tests. No attempt was made to measure the reduction in area, but the types of fracture were noted qualitatively; in the text they are referred to as (I) the normal, plastic, or necked fracture, (2) the knife-edge fracture, and (3) the brittle or intercrystalline fracture with small reduction of area. Results for different constant applied stresses are plotted in Fig. I. In all cases at least two trials were made for each stress, although they cannot always be indicated separately on the curves. The breaking stresses drop very rapidly to a small frac-

Jan 1, 1943

By A. W. Schlechten, A. H. Larson

Equilibrium H2S/H2 ratios were determined as functions of temperature (500o to 900°C) and composition in a hydrogen-circulation apparatus. Within the composition range studied there exists a two-phase region of "Zr3S4" and "ZrS2". The upper composition limit of this two-phase region is hounded by a disulfide phase and is practically constant over the temperature range investigated. The lower composition limit of this two-phase region is bounded a "Zr3S4 " phase and varies appreciably with tem- perature. The upper composition limit of the homogeneous region of the disulfide phase is not definitely determined, but it appears to he bounded by the stoichiometric composition of ZrS2. The lower composition limit of the homogeneous region of the Zr3S4 phase could not he determined due to the extremely low values of the equilibrium H2S/H2 ratios. Various thermodynamic quantities are evaluated from the data. PUBLISHED free-energy data for the Zr-S system are practically nonexistent. Strotzer, Biltz, and Meisel1 measured the sulfur pressures for the reaction 2ZrS2(s) + S2(g) = ZrS3(s) in the temperature range 783" to 874°C. The average heat of reaction calculated from the temperature dependence of the sulfur pressure is -47 keal. It should be noted, however, that according to these investigators, the two-phase region as determined by sulfur pressure constancy under isothermal conditions extended from approximately ZrS2, 3 to ZrS2.7. From consideration of X-ray data they concluded that the homogeneous regions of the disulfide and trisulfide phases are ZrS1.8-2.0 and ZrS2.8-3.2, respectively. Hahn and coworkers2 have made a structure study of the zirconium sulfide phases. They summarized the zirconium sulfide phases as follows: the compounds ZrS3 and ZrS2 with narrow homogeneous regions, a "Zr3S4" phase with a homogeneous region roughly within the limits of ZrSl.5 and ZrSo.9, the compounds ZrS and Zr4S3, and a "Zr3S2" phase with a homogeneous region within the limits ZrSo.8 and ZrSo.5. It is noted that the compounds ZrS and Zr4S3 are only formed in the gaseous state through sublimation of a phase which has the approximate composition of the compound. This paper describes the determination of the stability of the zirconium sulfide phases by a hydrogen-reduction method in which hydrogen is circulated over the heated sulfide until equilibrium is attained. The resulting H2S-H2 mixture is then analyzed. Partial molar free energies, enthalpies,

Jan 1, 1964