Search Documents

By F. G. Tahmoush, N. J. Grant, E. P. Abrahamson

The effect of grain size on the brittle -ductile transition temperature of pure iron and three dilute Fe-W alloys has been investigated by slow bend tests. The brittle-ductile transition temperature for pure iron increased with increasing grain sizes from 8000 to 500 grains per sq mm where the transition temperature then decreased with further increase in grain size. The dilute additions of tungsten lowered the transition temperature for fine grain sizes, suppressed a reversal of the curve in the coarse grained portion, and raised the transition temperature for this region. The frequency of twin occurrence increased with increasing grain size and decreasing temperature. The object of the present investigation was to re-examine the effect of grain size on the brittle -ductile transition of pure iron and several dilute Fe-W alloys. Current literature normally presents a simple relationship between grain size and the brittle-ductile transition temperature, namely, that the transition temperature increases with increasing grain size. Heslop and etch' have studied the transition temperature of mild steel by V-notch Charpy impact tests for the grain size range between 200 and 6000 grains per sq mm. The result was a linear plot of In 1-1/2 vs brittle-ductile transition temperature, where 1 is the grain diameter. Recent experiments by sipos2 revealed the possibility of a reversal in the slope of the grain size vs transition temperature plot for pure iron; however, his investigation was limited in scope, and the data obtained were insufficient to permit a definitive curve. The present investigation was undertaken in an effort to confirm or extend the grain size effect observed in iron by Sipos. PROCEDURE All alloys were vacuum induction melted, using 99.95 pct Fe containing 0.03 pct 0 and 0.004 pct C. Four ingots were made, ranging from pure iron to iron with 0.035 pct W. The chemical composition of each alloy, after processing, is given in Table I. The four alloys were prepared as 45 lb heats and cast into 4 in. diam by 16 in. molds. They were then extruded into 3/4 in. rods at 1800oF. Specimens for chemical analysis, taken from various positions along the rods, revealed no variation in tungsten content along the length. The extruded rods were reduced to 0.156 in. diam stock by a series of cold swaging operations involving intermediate vacuum annealing treatments. This procedure yielded a final cold reduction in area ranging from 10 to 90 pct. The swaged rods were chemically cleaned, cold pressed to a cross section of 0.10 by 0.18 by 1.0 in. long (2.54 by 4.73 by 25 mm). The specimens were wrapped in iron foil and vacuum sealed (10-4 mm Hg) in quartz. Various heat treatments at temperatures from 700" to 1300oC were utilized to produce grain sizes from 8000 to 1 grain per sq mm. Grain sizes were determined by measuring the average area of grains in a polished section. In specimens with grain size greater than 20 grains per sq mm, the total number of grains in the cross section was counted and then divided by the area to yield grains per sq mm. Grain size was measured both for longitudinal and transverse cross sections. The average of the two measurements was plotted vs transition temperature. An Instron Table Model testing machine was used to determine the transition temperature of specimens tested in three point horizontal bending. The specimen was supported by two 1/4 in. dowels one in. apart. Bending was accomplished with a push rod, the end of which had an 1/8 in. radius. The head speed was 50 in. per min. Temperatures were established through the use

Jan 1, 1963

By M. J. Saarivirta

A high-purity copper-zirconium alloy system was imesti-gated. The zirconium content of the alloys studied varied from 0.003 to 0.23 pet. The solid solubility of zirconium in copper and some physical and mechanical properties of the alloys have been determined. By proper heat treatment, Cu-Zr alloy can develop a high electrical conductivity and resistance to softening at temperatures up to 500°C (930°F). This combination of desirable properties makes this alloy superior, to other com-merzcrrl copper base alloys for- use in the electrical conductor field. DEMAND for high conductivity copper alloys that retain their mechanical properties at elevated temperatures is growing rapidly. At present, copper-base alloys such as copper-silver and copper-chromium are used where these characteristics are required. As an example, commutators in electric motors are often made of these alloys. However, the life at elevated temperature of commutators made of copper-silver alloys is much shorter than the life of the same part made of copper-chromium and copper-zirconium alloys. Copper-silver alloys are subject to creep and subsequent failure when the service temperature exceeds several hundred degrees centigrade. Use of copper-chromium alloys has been known for the past several years, but little information is available in the literature concerning the properties of alloys in the copper-zirconium alloy system. Some work had been directed toward determining the solubility of zirconium in copper as well as determining properties of the Cu-Zr alloys. These investigations have revealed the superior high-temperature and electrical conductivity properties of copper-zirconium alloys over copper-chromium alloys. The United States Metals Refining Co., Carteret, N. J. has recently produced OFHC R copper-zirconium alloys for experimentation and evaluation. Because OFHC R copper contains no appreciable oxygen, no harmful oxides are formed and the full benefit of Zr as an alloying addition is obtained. This paper describes the results of this work. It contains room-temperature and some high-temperature data which have been obtained after various processing techniaues. Actual elevated temperature properties are being determined and will be reported in a separate paper. Preliminary results obtained at elevated temperatures suggest that the Cu-Zr alloy is superior to other high conductivity copper-base alloys. WORK PROCEDURE The high-purity oxygen free (OFHC R) copper-zirconium alloys with zirconium content ranging from 0.003 to 0.23 pct were cast into 4-by 4-in. wirebars by both continuous casting and conventional casting methods. Zr was added in the form of a master alloy containing 30 pct Zr and 70 pct Cu. Castings were analyzed for zirconium and nine bars containing various amounts of zirconium were selected for this study. The results of analyses and the sample numbers are given in Table I. Typical analyses of OFHC R copper are also shown. The following properties were studied: A) Solid solubility of zirconium in copper. B) Effect of zirconium on properties of copper. C) Effect of combined working and heat treating on properties of Cu-Zr alloys. The solid solubility of zirconium in copper was determined by metallographic techniques. Specimens for this phase of the investigation were hot rolled at 900oC (1650oF) to 0.250-in. rod. The rolled rods were cut into 2/3-in. long specimens and solution annealed at 950 °C (1740°F), 980°C (1795 °F). and 1020 °C (1870 °F) for 6 hr and quenched in water. In order to find the solid solubility limits at lower temperatures, the homogenized specimens were reheated at various temperatures for 1 hr and quenched. The physical and mechanical properties were determined on 0.250 in. rod, 0.132- and 0.081-in. wires. The wires were cold drawn from the 0.250-in. rods after they were solution annealed at 980 °C (1795°F) and quenched in cold water. Mechanical and electrical properties were determined on cold drawn and

Jan 1, 1961

By C. G. Dunn

This note describes a method for revealing micro-structures in tantalum through an {hkl} effect which was found during a study involving amorphous and crystalline tantalum oxides. Three steps are involved. First, an amorphous film of Ta2O5 is formed anodically1 on the surfaces of the tantalum. The amount needed depents on the thickness of the substrate tantalum; 1600Å of oxide, however, is generally satisfactory in the 1/2 -mil (12 µ) to 3-mil thickness range. The film at this point is uniform in color. Second, the anodized specimen is heated to 800°C in. vacuo during a period of a few minutes and held at temperature for 5 min. During such a treatment some oxygen leaves the oxide through dissolution into the substrate tantalum (e.g., at 10-8 Torr oxide films thinner than about 800 completely disappear on 5-mil strip). Considerable crystallization of the amorphous oxide also occurs adjacent to the metal/oxide interface but not throughout the oxide thickness. The thickness of oxide needed as a residue is not too critical; values between 500 and 1000Å (optical estimate') may be most useful. (The presence of a residual oxide layer after the heat treatment usually is not apparent; in fact, in most instances the surfaces have a metallic appearance. This can be the case also for thicker residual films needed in the detection of a crystalline oxide phase by surface X-ray diffraction—e.g., if the initial oxide film is 3000Å thick, enough crystalline oxide is formed for X-ray detection.) The third step eliminates the metallic appearance at the surface and reveals (or produces) a varied colored film of tantalum oxide. Two methods can be used and both will be illustrated. If the specimen is dipped in 48 pct HF for a few seconds, the tantalum is found to be covered with a multicolored oxide. Moreover the colors correlate with the grain structure of the substrate tantalum through an orientation dependence of the type illustrated in Fig. 1, where results of an orientation analysis by the Laue X-ray method have been plotted. Other film conditions would have provided a different set of colors for the same orientations. Any such correlation, however, provides a basis for a qualitative assessment of the distribution of orientations in a large sample. The cold-rolled structure of tantalum foil produced by a recrystallization anneal and a cold-rolling reduction of 95 pct is not easily obtained by usual metal-lographic methods.' The structure, however, is easily revealed by the present technique, Fig. 2. The alternative third step is to reanodize the specimen. The optical nature of the final anodic film depends on the presence of the crystalline oxide phase; color variations indicate optical thickness variations in the film. As the reanodization voltage is increased from zero, straw and light brown colors appear (as usual), followed now by variations in color from grain to grain depending on {hkl} orientation. Suitable end points, which are determined by voltage and time, are easily established. Fig. 3, for example, shows the grain structure developed in 5-mil tantalum strip during a 30-min re-crystallization and grap-growth anneal at 1800°C. An anodic film of 1600Å thickness was added prior to the special 800°C anneal. Reanodization was done at constant current density (near 0.2 ma per sq cm) in an aqueous solution of H3PO4 (0.01 pct) and was terminated after the initial brown colors were replaced by a deep blue at approximately 30 v. Although good grain contrast can be obtained with bright field illumination, even greater contrast for black and white micrographs may be obtained with polarized light, as in Fig. 3.

Jan 1, 1967

By E. I. Alessandrini, A. U. Seybolt

Selective oxidation (preferential oxidation of a single alloy component) can be an important oxidation mode in the case of alloys such as Si-Fe, Al-Fe, and so on, when heat-treating in atmospheres of low oxygen potential. It was the purpose of this work to identify the oxide films formed on iron containing 31/4 pct Si at low oxygen potentials, and to make some observations on the H2O/H2 ratios required to form them. EXPERIMENTAL METHOD HYDROGEN of varying water content offers a very convenient method of establishing a wide range of oxidizing power, or oxygen potential. The method chosen to provide a desired H2O/H2 ratio was to nearly saturate hydrogen at room temperature by bubbling the gas through water at room temperature, and then to wring out the excess water by passing the wet gas through a long glass spiral immersed in a refrigerated liquid at a desired dew point. After oxidation, the samples were examined by electron diffraction in order to identify any film which might be present. PREPARATION AND TREATMENT OF SAMPLES The samples were prepared from a Si-Fe alloy made in the laboratory using electrolytic iron and 96 pct ferro-silico11, vacuum-induction melted, hot-rolled then cold-rolled to 0.015-in. thickness. After the cold-rolling the samples were annealed at 1000°C. Transmission Laue X-ray patterns showed very little evidence of preferred orientation, but it is likely that a weak texture could have escaped notice. The chemical analysis was as follows: 3.34 Si, 0.01 Al, 0.001 0, 0.006 C, 0.002 N. Before each sample was oxidized, it was polished through 4/0 emery paper, cleaned and dried using benzene, carbon tetrachloride, acetone, absolute alcohol, and ether. The method of oxidizing the samples was as follows: Samples about 1/2 by 1 by 0.015 in. were held in the upper, cool part of a vertical vacuum furnace until the desired temperature was established in the furnace, Fig. 1. The sample was then lowered into the uniform hot zone where it was heated quickly to the desired temperature, and subjected to hydrogen of controlled moisture content (dew point) as mentioned previously. Temperatures from 400" to 1000°C were used, and dew points from room temperature to —78°C were explored. In general, the runs lasted about 6 hr, but a few runs were of different duration, as will be indicated later. After the predetermined period of time had elapsed, the specimens were withdrawn by the hollow stainless steel-quartz holder to a cool zone at the top of the furnace. EXPERIMENTAL RESULTS The results are summarized in Table I. Most of the electron-diffraction patterns were obtained by glancing-angle reflection, but in a few cases it was possible to strip the oxide films from the surface by a total immersion in a 3 pct bromine-methanol solution. Some of the thinner stripped films yielded quite satisfactory transmission patterns. However, both diffraction techniques yielded the same results; the patterns while most frequently showing a (low) tridymite, also showed a (low) cristobalite in some cases. A few patterns showed evidence of both phases. Because of the known nonequilibrium behavior of silica, it is not surprising that both forms of silica could coexist on one sample. It was noted that at fairly low dew points such as —40°C, there was a tendency for diffuse diffraction rings, suggesting a very small crystallite size. Also some subsequent experiments to be reported later show that thin silica films can be amorphous.

Jan 1, 1959

By J. Chipman, N. J. Grant, E. C. Roberts

An equilibrium study was made of the distribution of chromium and oxygen between liquid iron, containing less than 1 pct Cr, and simple slags of the CaO(MgO)-Si02-FeO-Cr& type in the temperature range 1526' to 1734OC. The effects of slag oxidation, temperature, and basicity were observed. IN spite of the fact that chromium is one of the most important alloying elements in steel, and exists in almost all steels as a significant residual element, little research has been done to determine its behavior in basic steelmaking processes. Considerably more work has been done under silica-saturated acid slag conditions. Korber and Oelsen,' Herasymenko,' and others have generally agreed that in acid steelmaking practice the chromium in the slag behaved as if it were present as the chrom-ous ion (CrO). Work by Hilty- ir, high chromium slags also indicated that chromium may exist as CrO. In basic slag systems no equilibrium data exist. Based on individual studies of basic open hearth and electric furnace practice, Bardenheuer," Rock-rohr,% nd HauckQ oncluded that: 1—chromium recovery increased with decreasing basicity, and 2— chromium recovery increased with increasing temperature, although the effect was small. In similar studies Yavioskii and Dzemyen' concluded that: 1— slag FeO is the most important variable, 2—the basicity of the slag has no effect on chromium recovery, and 3—slag viscosity is not high even when 20 pct Cr,O, is present. Lapitskii\ oncluded that chromium recovery improved as the basicity of the slag decreased and increased with increasing manganese in the metal. Regarding the effectiveness of CrZ08 as a base or acid in basic slags, both Kristofferseno and Trojer" reported that Cr,08 was an acidic component requiring neutralization as 2CaO-Cr,O,. Experimental Procedure The experimental apparatus and procedure used for the present research were similar in most details to those used by Winkler and Chipman" and were described in detail by them. A magnesia crucible was used, holding 60 to 80 lb of Armco iron which was decarburized with hydrogen to about 0.010 pct C. Since all the metal samples solidified without gas evolution, this carbon level was assumed not to be significant. Synthetic slags made by mixing pure oxides were used throughout the study. Temperatures were measured by means of calibrated W-Mo thermocouples and were checked by Pt-Pt-Rh thermocouples. The range of temperatures covered in this study was from 1526" to 1734°C. The chromium content of the iron was in the range 0.032 to 0.82 pct, although the bulk of the tests showed 0.04 to 0.2 pct. The slags were of the CaO(MgO)-SiO,-FeO-Cr,O, type in which the Cr,O, content was from about 2 to 20 pct, although most of the slags showed from about 2 to 10 pct. The FeO range was from about 10 to 65 pct. CaO and SiO, were in the range of about 5 to 45 pct each, yielding a rather wide range of basicity values. The first 12 heats were made without a sulphur addition, and with only 30 min allowed for slag-metal equilibrium to be reached. In previous research it had been shown that less than 30 min was adequate to achieve equilibrium in slags free of Cr2O8.11,14.15 A study of the present data indicated that some of the tests may not have reached equilibrium in this time; accordingly four additional heats were made in which at least 1 hr was permitted for equilibrium to be reached. For reaching

Jan 1, 1955

By D. Harker, W. E. Seymour

CERTAIN alloys of iron and nickel, when rolled and annealed, possess a preferred crystal orientation: (001) in the rolling plane and [loo] in the rolling direction, when recrystallized at 850" to 1050°C after approximately 98 pct cold reduction. Since the preferred orientation makes a direction of easiest magnetization coincide with the rolling direction, these alloys, especially a 50 pct iron in nickel alloy, have found wide application in the electrical industry' for choke coils and special types of transformers. The rate of the recrystallization reaction was studied at temperatures ranging from 500° to 600°C. The heat of activation for the reaction was calculated from the observed rates, and crystal orientation determinations were made before and after re-crystallization. A vacuum melted iron-nickel alloy* analyzing 49.6 pct nickel, 0.018 pct carbon, and 0.30 pct manganese was used for the experiments. The alloy was cold-rolled 98 pct into strips 1/2 in. wide by 0.002 in. thick. Specimens 1 in. long were sealed under a vacuum (approximately 10-8 mm Hg) in 1/2 in. ID pyrex glass tubes. For heat treatment these tubes were fastened to Nicrohm wires and submerged in a molten salt bath controlled to ±2°C. (The maximum measurement error was within 3°C.) The time at temperature was varied logarithmically from one sample to another, and runs were made at 500°, 525", 550" and 575°C. A molten lead bath was used for a run at 600°C which was controlled to the same accuracy. To determine the extent of recrystallization after a particular time at a given temperature, a method was used suggested by the work of Decker, Asp, and Harker.3,4 This method employs an X-ray spectrometer whereby X rays are diffracted from crystallites whose diffracting atom planes are parallel to the rolling plane of the specimen. The intensities of the diffracted rays are measured by a Geiger counter. The counter can be rotated through a range of angle, and can be motor driven through this range at a speed of 2" per min. The measured intensities are plotted vs. angle by a potentiometer recorder. In a 50 pct iron-nickel alloy it was found that only (200) reflections were obtained from the rolling plane with recrystallized material, and that only (220) reflections were obtained from the rolling plane with unrecrystallized material. No other reflections were obtained under these conditions over a range of Bragg angle of 0 to 45" using either type of specimen. As a consequence, the intensity of the (200) reflections from the rolling plane was taken to indicate the amount of recrystallized ma-terial present in a specimen, and the corresponding intensity of the (220) reflections was taken to indicate the amount of unrecrystallized material present. To insure flatness and proper alignment of the reflecting specimen in the spectrometer, the sample was laid in a slot 1/2 in. wide x 0.001 in. deep which was machined in a 3/4x2x1/2 in. steel carrier. The specimen then was taped down with cellophane tape. This steel cradle was mounted vertically in the specimen holder of the spectrometer so that the bottom edge of the carrier rested against a horizontal shoulder. Intensity data used in plotting the percent of recrystallized material vs. time at temperature were obtained by directly counting the diffracted beam of nickel filtered copper Ka radiation used throughout the work. The X-ray spectrometer was employed also in obtaining pole figure data to be used for orientation determinations. At the beginning of this investigation a transmission pole figure holder was used." As a thickness of 0.002 in. of this alloy was found to be opaque to the copper Ka radiation, it was necessary to reduce the thickness of the pole figure specimen. A cold-worked sample was etched in a 50 pct HCl solution for 5 min and was found to transmit a

Jan 1, 1951

By N. Tiner

THE mechanical properties of magnesium-alloy castings are greatly improved by grain refinement, and at present considerable attention is being paid to methods of obtaining fine-grained castings. One method of achieving this end is the use of proper melting and superheating techniques. These have been employed commercially to a great extent, but no comprehensive study of the subject appears to have been published at present. Numerous investigations found in the literature include some reference to superheating techniques, 1-4 and Achenbach, Nipper and Piwowarsky,5 based principally on thermal analysis, ascribe the grain-refining action of superheating to the influence of solid foreign particles or dissolved gases present in the melt upon the course of crystallization. The primary purpose of this paper is to present the principal facts concerning the effect of superheating on grain size of magnesium alloys. Attempts are also made to explain the experimental results in terms of a general hypothesis. The investigations are limited chiefly to common commercial casting alloys. In order to carry on this work, it was necessary to determine the factors influencing grain size and to develop a proper technique for the preparation of samples. The preliminary tests made by the author indicated that the grain size of magnesium alloys resulting from the solidification of a melt is determined by alloy composition, presence of impurities, rate of cooling during solidification, thermal history of the melt and to some extent the structure of the charge used. The rate of cooling is in turn dependent upon the mass of the melt, pouring temperature, and dimensions, properties and temperature of the mold into which the melt is poured. The final grain size of the alloys is still further modified by heat-treatment subsequent to casting. It is not within the scope of the present paper to discuss all of these factors, and it would suffice to note here that when equal amounts of magnesium alloys are prepared from the same alloying materials, melted in graphite crucibles under the same thermal conditions, then cast into graphite molds at a constant temperature, the .resultant solids have the same grain size. By maintaining all other factors constant, it is thus possible to vary thermal conditions of a melt and to examine the grain size of resultant castings. PREPARATION OF SAMPLES AND GRAIN-SIZE TESTING The alloys investigated in this paper were taken from ingots made by Permanente Metals Corporation or prepared by the author with pure carbothermic magnesium and necessary alloying elements. Melting was carried out under a flux in a graphite crucible heated uniformly by an

Jan 1, 1945

By George W. Sargent

For the experiments here described a rod was used, 0.75 in. in diameter, and rolled from one ingot. Analyses of the ingot and rod showed them to have the following composition respectively: C. Mu. Si. P. 8. Percent. Percent. Percent. Percent. Percent. Ingot,. .. 1.150 0.328 0.223 0.020 0.016 Rod,. .. 1.033 0.327 0.223 0.020 0.016 Pieces 4 in. long were heated to various temperatures in a closed porcelain tube, within a gas furnace, and allowed to cool with the same; they were then turned, threaded, and subjected to physical tests in a Riehlé testing-machine. The elastic limit was determined by the drop of the beam. The elongation was measured in two inches. From the threaded ends of the testrpieces, disks were cut, and prepared by combined polishing and etching, using parchment stretched over a wooden block and moistened with a 2-per cent. solution of ammonium nitrate. The structure, as thus developed, and the fractures, were magnified and photographed. A cooling-curve was constructed, and the critical point was located at 675º-680º C. A thermo-electric pyrometer was used to make the measurements of temperature. The micro-constituents of steel have been so frequently and thoroughly described by others that I need only say here that the theoretical micro-structural constituents of this steel were : pearlite, 95 ; ferrite, 0 ; cementite, 5 per cent. The quenched metal would be expected to consist almost entirely of martensite—provided, however, the quenching be done at or near the proper temperature. Rapid quenching from a high temperature would give rise to austenite.

Jan 1, 1902

By H. N. Treaftis, J. W. Cahn

THE previous determinations of the solvus of tin in solid lead disagree with one another by as much as 40°C or almost 10 at. pct. Even determinations that appear to be careful differ considerably in both the solubility and its temperature coefficient. Recent kinetic workl -3 on the rate of precipitation of tin from lead-tin alloys and thermodynamic work4 on the heat of solution of tin in lead have given some insight into the time necessary to reach equilibrium in this system. As this time is longer than that used in almost all previous determinations of the solvus, these determinations are questionable. Since the interpretation of recent kinetic results requires accurate values of the equilibrium solubility the present work was undertaken. DISCUSSION OF PREVIOUS RESULTS The methods used in previous studies may be placed into three classes: 1) Several alloys covering a range of compositions are allowed to reach "equilibrium" at a certain temperature.5-7 Some property, such as the X-ray lattice parameter of the lead-rich phase or the re- sistivity of the alloy, is then measured as a function of composition. The solubility limit for that temperature is taken to be that composition at which a discontinuity in the property occurs. However, the recent kinetic work has shown that tin precipitates in two stages. The first stage is rapid but leaves the lead still supersaturated. The second stage is very slow, and it seems from the equilibration times quoted by the investigators of the solvus that the end of the first stage of precipitation was usually mistaken for equilibrium. This is especially true at temperatures below 100°C where the first reaction is still quite rapid (from minutes to months), but where the second stage is so slow that very long holding times are required to reach equilibrium. Alternatively micrographic work8 on several alloys of different compositions seems to have given good results if done carefully. 2) The beginning of precipitation in a homogenized alloy is measured as it cools slowly8-10. Since reactions in solids undercool easily, such determinations will always give too low a temperature for the solvus. 3) Some property of an alloy is measured as a function of temperature while the alloy is above the solvus.5,9,11 The range of temperature can usually be extended slightly into the two phase region. Then the alloy is precipitated at a much lower temperature and slowly reheated. The solvus is taken to be the lowest temperature where the property of the reheated alloy is equal to that previously determined for the homogeneous alloy. Usually one also expects a discontinuity at the solvus in the temperature variation of the property for the reheated alloy. The difficulty in this method is the sluggishness of the dissolution process, and this method may give too high a solvus temperature. EXPERIMENTAL The phase boundary or solvus temperature was determined by a modification of method 3 for a series of chemically analyzed high-purity alloys, ranging from 5.1 to 26.4 at. pct Sn. The resistance, as a function of temperature, of a sample of homogenized alloy (which could easily be undercooled) was compared with the equilibrium resistance which that alloy sample attained after precipitation at room temperature followed by long isothermal anneals at various temperatures. Before each anneal the sample was rehomogenized and reprecipitated. The solvus temperature could be located to within 1°C as the intersection of the resistance vs temperature curves for the homogenized and equilibrium alloys. No attempt was made to locate the phase boundary more accurately since the limiting factor was the precision with which the alloys could be analyzed. This precision was ±0.1 wt pct Sn and corresponds to an error of 1 deg in temperature. This use of isothermal anneals differs from some of the previous investigations in which method 3 was used with baths of slowly rising temperatures. It was found early in the investigation that solvus temperatures tended to be high if the latter method was used even at extremely slow heating rates. For example a

Jan 1, 1961

By H. P. Leighly, F. C. Perkins

THERE have been several statements in the literature about the difficulty of producing single crystals of high-purity (99.99pct) by the strain-anneal method. Consequently, investigators tend to employ low-purity aluminum for their single-crystal experiments, or else resort to the Bridgman or other techniques which depend on solidification for the production of single crystals. The following paragraphs describe a solid-state method for the manufacture of single crystals of high-purity aluminum which should provide crystals with greater perfection than those formed by solidification. The starting material for this method of producing single crystals was secured from the Aluminum Corp. of America and has a purity of 99.99 pct, the balance being trace amounts of impurities. Specimens approximately 1 by 4 in. are sheared from sheet having a nominal 0.050 in. thickness. The specimens are given a preliminary anneal at 640°C for approximately 3 hr in order to remove fabrication strains and to produce an average grain size of about 1/4-in. diam. The specimens are then etched in Tucker's etchant (45 pct HC1, 15 pct HNO3, 15 pct HF and 25 pct H2O) to remove the oxide film. Critical strain is applied by wrapping each specimen about a 1 3/4 in. round and subsequently straightening it against a flat surface. The high-purity aluminum sheet is sufficiently soft that this operation can be accomplished by ordinary finger pressure. The specimens are immediately annealed again at 640°C for 3 hr and reetched for examination. Ordinarily, considerable growth of certain of the grains will have occurred, and occasionally a single crystal will be produced on the first attempt. The procedure of alternately straining, annealing and etching is repeated until the majority of a batch of specimens contains usable crystal sizes. Typical examples are illustrated in Fig. 1. The greatest changes in crystal sizes are produced in the initial treatments. As the average crystal sizes get coarser in the later treatments, the sever- ity of the strain must be increased in order to produce grain boundary- migration. This increase in severity is effected by decreasing the diameter of the round used for straining (to 1 1/2 in., for example) and/or wrapping the specimens about the round twice, with opposite faces in contact with the round, before flattening. Usually the strain treatments described are not severe enough to produce nucleation in coarse grain high-purity aluminum. The growth of grains occurs by strain-induced grain-boundary migration. It has been observed that the grain boundaries move most readily during the first hour or so of each annealing treatment and that the rate of movement decreases with extended holding times at temperature. Prolonged annealing treatments are therefore not usually beneficial. Similarly, the rate of growth of each crystal appears to depend upon the orientation of the crystal with relation to those of its neighbors. Frequently island grains are formed after the initial heat treatment as the result of slow grain-boundary migration. These sometime become stationary during later heat treatments. Twin orientation interfaces are frequently developed during annealing. These imperfections can usually be removed by increasing the severity of strain to produce actual nucleation of new grains of more favorable orientation at the imperfection interfaces. The largest single crystals produced in our laboratory by the above method measured 4 by 1 by 0.050 in. Examination of Laue back-reflection patterns from a limited area of the specimens, gave no evidence of polygonization. Probably there is some indication of polygonization in the original grain area provided a more sensitive technique is used for detection. Experiments to produce wider specimens were less successful, possibly because wider sheets increase the complexity of the strains induced by deformation and promote widespread nucleation. Grain boundary migration occurs preferentially in a direction parallel to the longitudinal axis of the specimen. The choice of specimen geometry with respect to the rolling direction of the sheet appears to be immaterial in regard to the production of single crystals.

Jan 1, 1961

By D. H. Forbes, I. B. Cadoff, H. M. Manasevit

Single-crystal silicon films have been obtained on several natural crystal faces of BeO using the thermal decomposition of silane and the hydrogen reduction of silicon tetrachloride. From an analysis of X-ray diffraction data it was determined that the following film-substrate orientation relationships exist: (111) Si 11(0001) BeO, (111) Si 11(1011) BeO, (100) Si 11f1010) BeO. and (110) Si 11(1010) BeO. An analysis of the crystallographic relationships between the film and substrate indicates that a match occurs between the silicon atoms in the film and the berylliuni ion sites in the substrate. This correspondence is in agreement with previous work on the deposition of silicon on sapphire.1-3 silicon on spinel: and tungsten on sapphire. The high resistivity, thermal conductivity, and radiation resistance of beryllium oxide make it an important substrate material for the deposition of thin films of silicon or other semiconductors. The importance of semiconductor-insulator composites to the field of integrated microelectronics has been well-documented in the case of silicon on sapphire.'-' The successful growth of large-area single-crystal silicon on an insulator, sapphire, was first reported in 1963.1,2 Since that time studies have been made of the crystallographic relationships between the deposited film and the sapphire substrate. On the basis of the observed relationships, a model has been proposed relative to the crystallographic requirements for epitaxy between the semiconductor film and the metal oxide substrate.3 It is proposed in this model that epitaxy is the result of a match between atoms of the deposited film and the metal ion sites of the substrate plane. This match is not limited to a 1 to 1 correspondence between sites in the two lattices. Sub- sequent studies of the deposition of silicon on spinel4 and tungsten on sapphire5 have yielded data which support this model. On the basis of this previous work it was felt that silicon on BeO should also fit this model. In the present study, the choice of substrate orientation was limited to the natural faces of synthetic BeO crystals. Of the faces available, the (0001) plane seemed the most favorable for epitaxial growth. EXPERIMENTAL PROCEDURE Silicon films were deposited from silane and silicon tetrachloride in the apparatus shown in Fig. 1. The hydrogen ambient gas was purified by passage either through a DEOXO unit, molecular sieves, and a liquid nitrogen cold trap, or through a heated Pd-Ag thimble. The gas was then mixed with the silicon source materiai and passed over the substrate which lies on a spacer above an inductively heated silicon pedestal. The following deposition conditions were used: a hydrogen flow rate of 3 liters per min with silane and silicon tetrachloride concentrations of 0.2 mole pct and a pedestal temperature of 1175" * 5°C as observed with an optical pyrometer assuming an emissivity of 1.0. Deposition was preceded by a 15- to 30-min hydrogen-etch period conducted at a temperature of 1275°C (obs). Adherent silicon films from 2 to 10 u were grown on the various BeO faces. The substrates were synthetically grown beryllium oxide single crystals ranging from 5 to 10 mm in

Jan 1, 1967

By M. C. Smith, W. V. Green, D. M. Olsen

The creep-rupture behavior of commercial powder-metallurgy molybdenum rod is reported in the temperature range 1600" to 250O°C, at stresses up to 9000 psi and times up to 1 month. The effects of temperature, stress, and grain growth are discussed. Rupture time is fitted to the Larson-Miller parameter and compared to lower-temperature and higher-stress results reported by pugh.1 BECAUSE of its high melting point, molybdenum should retain useful strength to relatively high temperatures. Combined with its ready availability in the United States, this makes it attractive for many applications in missiles, rockets, and so forth—wherever its susceptibility to oxidation can be tolerated or overcome. The mechanical properties of molybdenum rod in the temperature range —200" to 1540°C have been reported by pugh,' Bechtold,' Parke,3 and Carriker and Guard.4 Madden and chen5 have measured the tensile properties of molybdenum single crystals in vacuum up to about 2500°C. As one further step in evaluating its mechanical usefulness, the constant-load creep-rupture properties of commercial powder-metallurgy molybdenum rod have been investigated in the range 1600" to 2500°C. MATERIAL TESTED Creep specimens were machined from 1/2-in. round commercial molybdenum rod, manufactured from powder by pressing, sintering, and swaging. Spectrochemical analysis of the rod showed "traces" (less than 0.01 pct) of silicon, aluminum, chromium, iron, and zirconium, and "faint traces" (less than 0.001 pct) of manganese, magnesium, cobalt, and nickel. Carbon content was 130 to 200 ppm, nitrogen was 110 to 180 ppm, and oxygen 30 to 35 ppm. A typical microstructure of the as-received rod is shown in Fig. 1. Room temperature tensile properties for five specimens strained at about 0.015 in. per in. per min are shown in Table I. CREEP SPECIMENS USED The specimens used for creep-rupture testing are illustrated in Fig. 2. The 1/4-in.-diam gage section was 3/4 in. long, and terminated at shoulders 5 mils high. These shoulders served as fiducial marks for optical strain measurements. Surface finish on the gage section was 16pin. r.m.s. One specimen, for a "long-time" test described below, was modified by dividing the 3/4-in. gage length into three 1/4-in. long sections with individual diameters of 0.250, 0.230, and 0.210 in., each terminating in a pair of fiducial shoulders. TESTING PROCEDURE The constant-load creep-testing machine used has been described by Smith, Olson, and Brown.6 In it the specimen is held vertically on the axis of a cylindrical tantalum or tungsten heater tube by threaded molybdenum or tungsten grips. Both specimen and grips are heated by radiation from the heater-tube, which is heated by its own electrical resistance. The bottom specimen grip is held at its lower end by a clevis pin. The testing load is applied to the specimen through the upper grip by means of hanging weights, a constant force-multiplication lever system, and a pull rod sealed to the chamber lid by a bellows. The incandescent specimen is viewed by an external optical system through slots in the heater-tube and radiation shielding, and an enlarged image of it is projected on a ground-glass screen. Gage-length measurements are made on this image with a pair of cathetometers. Thorium oxide coatings were applied to the threaded ends of most specimens, to prevent diffusion-welding of specimens to grips during testing. Without such a coating welding usually occurred, and grips were often broken by subsequent efforts to remove the tested specimens.

Jan 1, 1960

By B. E. Cornish

Most technical and statistical data published on pyrophyllite relating to production figures, uses, markets and sales, have in the past traditionally linked the mineral with talc and soapstone. This is due to several common superficial physical properties resulting in substitute uses and applications. However, these minerals are not similar in chemical composition and do not generally occur in a similar geological environment. Pyrophyllite now stands on its own in the marketplace-particularly in ceramic applications-due to the combination of excellent heat shock and creep resistance properties of the mineral. The increase in pyrophyllite use in the field of ceramics indicates the continuing realization of these marked unique properties. Several new fields of ceramic applications, previously the preserve of high-alumina materials, have been developed on the intrinsic properties of pyrophyllite. Pyrophyllite is an aluminum silicate with the molecular formula of AI2O34SiO2H2O. It would be more appropriate to group pyrophyllite with such materials as kyanite, diaspore, andalusite, and certain high-alumina clays in relation to its general applications (Stuckey, 1928). These materials all have good beat shock resistance properties at high temperatures and are widely used for the manufacture of refractories. For those reasons they are interchangeable in some applications. Pyrophyllite also has many uses in nonceramic applications, the most important to date being as a substitute for talc in fillers. The major pyrophyllite mining operations are located in the US, Japan, Korea, Canada, and Australia, where the mineral is widely used as a raw material for general ceramic, mineral filler, and dilutant applications. Commercial Applications Pyrophyllite was first used in the last century for lining stoves and fireplaces, and also in the carving and polishing of ornamental objects. The rise in industrial demand for new products and applications resulted in the introduction of pyrophyllite as an alternative, mainly for talc and soapstone. Industrial filler applications followed for paint, paper, cosmetics, rubber, pesticides, crayons and pencils, and bleaching soap. The first use of pyrophyllite in ceramic applications was prior to World War II, in the manufacture of ceramic cladding tiles in the US. This was followed by the production of kiln furniture refractories and whiteware when pyrophyllite was offered by suppliers in North Carolina as an alternative to some local clays. The largest tonnages of pyrophyllite used today are in refractory linings in steel ladles in Japan, as seen in Table 1. The consumption of pyrophyllite in Japan is second only to clay and chamotte among refractory raw materials used. Recently this technology has been adopted in Australia. Japanese and Australian practice has resulted in appreciable technical and economic benefits, particularly when pyrophyllite is used in combination with zircon. The potential growth for this application is substantial if US and European steelmakers follow. Investigation and research into the properties of pyrophyllite determined the following main advantages of pyrophyllite-based ceramics: high corrosion resistance for molten iron, steel, and slags; good heat shock resistance; good indices of deformation under load and hot creep resistance (refractories); and increase in mechanical strength of whiteware products promoted by a better distribution of mullite in finished products (also obtained at lower firing temperatures than normally required in production of triaxial ceramics). White cement

Jan 1, 1983

By Robert T. MacMillan

Of all the mineral substances utilized by man, salt or sodium chloride has one of the longest and most varied histories. Because all animal life is descended from marine organisms, sodium and chlorine became necessary to life, and as sodium chloride meets requirements most readily, common salt has been essential to human and animal diets from earliest times. As civilization progressed, man learned to evaporate sea water and brines of saline lakes and springs to obtain salt, and gradually ceased to depend on the flesh of animals and the occasional salt outcrops or "salt licks" they frequented. He also learned that salt had a multitude of uses, particularly as a preservative of meat and other foods. The importance of salt in the minds of early men may be readily seen from many allusions in the Bible and other ancient writings. Expressions such as "not worth his salt," and "the salt of the earth" are deeply embedded in the English language. Salt has symbolized friendship, fidelity, purity, and hospitality. It has been used as currency; had religious significance; caused wars; and has been a favorite commodity for taxation. The English word "salary" stems from the Latin word for salt, in which Roman soldiers received part of their pay. Although salt today retains its dietary importance, it has thousands of other uses. Of each 100 pounds produced in the United States less than three pounds is for table use. The other 97 pounds goes for agricultural, industrial, and chemical uses. Fortunately, reserves of salt are enormous and reasonably well distributed on the face of the earth. The sea is an inexhaustible source of salt which may be had at prices which vary with climate and other factors. In addition, large underground salt deposits and many salt lakes, springs and playas are scattered throughout the world. Most countries have access to a salt supply, although some are more favored than others. Properties Crystallized sodium chloride or common salt is known as halite. Its molecular weight is 58.454 and it contains, by weight, 39.34 pct sodium and 60.66 pct chlorine. Alternate positions in the cubic lattice are occupied, respectively, by negative chloride and positive sodium ions; the crystal form is isometric. Crystallization from water produces concentric shells, and when broken, a crystal shows conchoidal fracture. Salt has a hardness of 2.5; its specific gravity ranges from 2.1 to 2.6 for rock salt and is 2.165 for the pure crystal. The refractive index is 1.554; it melts at 800.8 ± 0.5°C and boils at 1413°C. Its heat of fusion is 123.59 cal/ gram. Salt is transparent or translucent and highly diathermous. It is colorless when pure and has a vitreous luster. Salt containing traces of iron oxides has varying shades of yellow, orange, brown, pink, or red. The peculiar shade of red sometimes found in that produced by solar evaporation of sea water has been attributed to tiny organisms. Blue mottlings sometimes seen in halite crystals have been attributed to colloidal sodium. Salt is soluble in water to the extent of 35.7 parts per 100 parts of water at 0°C and 39.8 parts per 100 of water at 100°C. The small difference in solubility with increasing temperature is important in the economics of producing salt by evaporating brine. Salt has a negative heat of solution which is 1.281 kg-cal/ mole at 18°C in 200 moles of water.

Jan 1, 1960

By N. K. Chen, R. Maddin

Single crystals of molybdenum were extended at temperatures from 1300° to 2500°C. It was found that with increasing temperatures, the yield becomes more pronounced and the number of slip bands for equal amounts of elongation decreases. Slip at high temperatures fragments the structure. OTHER than the investigations on sodium and potassium by Andrade and Tsien,&apos; the researches of Steijn and Brick&apos; on a iron single crystals at low temperatures are about the only studies of the influence of temperature on glide of body-centered cubic single crystals. The effect of test temperature on glide has been rather widely investigated with hexagonal crystals" and less widely with face-centered cubic crystals. ~~ a result of these studies it can be said that, in general, the onset of plastic flow as measured by the initial rate of strain hardening becomes more abrupt with increasing temperature, and the value of the yield decreases with increasing temperature. Strain hardening, however, is markedly affected by changes in temperature except at very low and very high temperatures where the strain hardening rate becames constant. In the present investigation it is shown that temperature affects the glide of molybdenum single crystals in much the same manner as crystals of other classes, it., for comparable strains the number of slip bands decreases with increasing temperature; shear along the slip bands increases with increasing temperature; the yield becomes more pronounced with increasing temperature of test; and the strain hardening approaches a constant at very high temperatures. In addition, it is shown that, in agreement with the work of Tsien and Chow, Qlip occurs on (110) planes in <Ill> directions. It is further shown that slip at high temperatures fragments the structure into either irregular sized cells or bent atomic planes which are roughly aligned in crystallographic directions. Experimental Procedure Single crystals 3 mm in diameter by about 25 mm long were prepared using the technique previously described.&apos; The furnace in which the crystals were grown served as the extension apparatus for the tension tests. It consisted of a 4 in. water-cooled brass tube 20 in. long which was continuously evacuated at the bottom. Two water-cooled copper electrodes held the specimen by means of spherical collets secured in place in the electrodes by set screws. These electrodes served also to transmit power and stress to the specimen. The lower electrode was clamped to a stand, while the upper electrode was fastened to one side of a lever arm flexibly supported at the top through a slightly offset pinion. A metal bellows operating elastically was attached to the upper electrode to affect a vacuum seal and allow freedom of motion. The level of the arm was adjusted by rotating a graduated nut. Rotation of the electrode was prevented by a key fitted into a groove. After the specimen was mounted and the vacuum secured, the lever arm was adjusted so that the bellows was at its relaxed position. This insured that the total weight of the specimen, the upper electrode, and the downpull of the vacuum were balanced by the horizontal beam. Since the specimen was heated by its own resistance, expansion of the specimen proceeded freely by this arrangement. During the time of heating the specimen, the beam was maintained in a horizontal position by turning the nut at the top. By graduating the lever arm and using a known dead weight on the lever arm to supply a tensile stress, the graduated nut could be read to 0.0001 in. extension. Since

Jan 1, 1955

By R. Ruka, E. A. Gulbransen

ONE of the interesting questions in the understanding of the reaction of iron with oxygen is the kinetics and the mechanism of the crystal structure changes occurring in the formation and breakdown of the oxide film. In a recent work&apos; the electron diffraction method was applied to the study of the solid phase reactions occurring internally in the oxide film on iron above 570°C and under vacuum conditions. The higher oxides which form under oxidizing conditions are reduced internally by the diffusion of iron into the oxide leaving the bulk of the oxide FeO (wüstite). This paper will ask and consider three questions. These are: (1) What is the nature of the depressed transformation temperature for the Fe3O4 + Fe ? 4Fe0 reaction in very thin oxide films?; (2) What is the mechanism of the forward transformation of Fe3O4 to FeO at or near 570°C?; and (3) What is the nature and mechanism of the slow reverse transformation of FeO to Fe3O4 and Fe below 570°C?. The composition of the oxide as well as its electrical, magnetic, mechanical, and chemical properties depends upon the kinetics of these reactions. Literature Survey The composition of the oxide film on pure iron at temperatures up to 570°C has been studied extensively by the electron diffraction method. Nelson,&apos; Jackson and Quarrell,3 and Gulbransen and Hick-man4 have shown that Fe3O4 and a-Fe2O8 are formed in the temperature range of 225" to 570°C, while y-Fe,O, is most likely formed below 225°C for long oxidation times. In very thin films FeO (wüstite) is found to form at temperatures as low as 400°C, and its existence depends essentially upon the extent of initial oxidation. FeO is not found in the formation of thick films below 570°C. On the other hand X-ray5 and micrographic8 studies show that Fe3O4 may exist as the main com-ponent in thick films up to 650°C, well above the equilibrium temperature for the reaction Fe3O4 + Fe ? 4FeO. The kinetics of the forward and reverse trans-formations of the reaction Fe3O4 + Fe ? 4FeO have not been studied in oxide films. However, analysis of the data of Gulbransen and Hickman4 on the heat-ing and cooling of iron oxide films of known thick-nesses in high vacua shows that the forward reac-tion proceeds rapidly even for a 4000 A film at temperatures of 575" to 600°C. The reverse reaction or decomposition of wüstite (FeO) occurs at tem-peratures below 450°C. Thus, there appears to be a slow process in the decomposition which is in marked contrast to the rapid forward reaction. The decomposition of a bulk sample of FeO free from the metal has been studied extensively by Chaudron, Benard and coworkers using the micro-graphic, X-ray diffraction, and thermomagnetic methods. Chaudron7,8 first observed that the de-composition of FeO (wüstite) below 570°C occurs by the reaction 4FeO ? Fe3O4 + Fe. Later work by Chaudron and Forestier5 showed that the rate of de-

Jan 1, 1951

By D. Weinstein

Yieldilzg in annealed arc-cast molybdenunz in torsion was studied as a function of strain rate and tem-perature. The temperature dependence of the yield point for different strain rates was used to calculate a heat of activation for the yield point. The heat of activation was not a constant but was approximately a linear function of the stress at yield. It is proposed that the rate effect in yielding is determined in part by a site place-change of C (or other interstitial atom) in the metal. THE low-temperature embrittlement phenomenon in metals and alloys has been known to exist for a long time. Although a transition from ductile to brit-tle behavior has been observed in some close-packed hexagonal metals1 and a face-centered cubic alloy, the most common class of metals exhibiting this be-havior has a body-centered cubic lattice structure. For example, a ductile to brittle transition has been observed in iron,3 molybdenum,4 chromium,5 colum-bium,6 and tungsten.7 In the present investigation, molybdenum specimens were tested in torsion over a wide range of temperatures at three widely separated strain rates, and the temperature for onset of embrittlement was determined. Characteristic of body-centered cubic metals and closely associated with plastic deformation is the appearance of a sharp upper and lower yield point. Theoretical explanation of the yield point in iron and low-carbon steel is due to Cottrell,8 who attributes the phenomenon to the pinning of dislocations by the formation of impurity atmospheres around the dislocations. These atmospheres tend to lock the dislocations and make them more difficult to move. The stress required to move a dislocation and thereby cause plastic deformation is greatly increased, and thus an upper yield point is observed. In addition, theoretical analysis,9 as well as experimental observations, show that the upper yield point is strongly a function of temperature. The upper yield point is observed to decrease with an increase in testing temperature, and above a certain temperature (-700° K in iron) it no longer appears. This is consistent with the concept that thermal vibrations will help free a dislocation from its atmosphere, so that the external stress required to free a dislocation from its pinning atmosphere decreases with increasing temperature. Furthermore, with increasing temperature the equilibrium concentration of impurity atoms around a dislocation decreases exponentially with the result that the dislocation is less firmly pinned. In Cottrell&apos;s theory of yield point a static model is visualized in which the pinning atmospheres, particularly interstitial atoms, are immobile, and the dislocations are anchored to stationary positions in the lattice. However, experiments1,7 show the upper yield point to be time-dependent or a function of the rate of straining, a high strain rate causing a high upper yield point. Present theory does not adequately account for the rate dependence of the yield point, and the exact function of the interstitial atom is not under stood. Nevertheless, observation of the temperature dependence and rate dependence strongly suggests that the upper yield point phenomenon is due to the interaction between dislocations and pinning atoms, and that a diffusion mechanism is important in determining the yield point.

Jan 1, 1962

By Wendell S. Williams

Single crystals of TIC doped with boron at high temperat~ires develop second-phase inclusions. The inclusions are in the form of lamellae lying parallel to {l 11 } planes of the Tic matrix and can be vevealed by etching [100] cleavage faces of the boron-doped Tic crystals. measurements of the critical resolved shear stress. t, of TIC crystals containing such inclusions showed that the ropid drop in t wilh increasing temperatu.ve found for pure Tic was greatly reduced. At 1600°C, the inclusion containing crystals had a value of t five limes that of pure Tic. The hardening effect also was found to inhibit hot pressing of TiC powders containing boron impurity. Thermochemical and crys-tallographic arguments suggest that the inclusions are TiB2. The boron content of the hardened carbide is a few tenths of 1 pct. TITANIUM carbide is noted for its high room-temperature hardness. However, measurements of the critical resolved shear stress, T, of single crystals of Tic at high temperatures have shown that t decreases exponentially with increasing temperature.&apos; This temperature dependence of t is attributed to thermally activated dislocation mobility limited by a large Peierls stress.&apos; In turn, this large Peierls stress is believed to be a consequence of strong co-valent and ionic binding in Tic. The rapid drop in 7 with increasing temperature, characteristic of pure Tic, is lessened by the introduction of second-phase inclusions. Exposure of Tic to boron at high temperatures produces such inclusions. A report of the influence of boron on t in Tic is presented, followed by a discussion of the nature and formation of boron-containing inclusions in Tic which are believed to be responsible for the hardening effect. I) CRITICAL RESOLVED SHEAR STRESS OF BORON-DOPED Tic CRYSTALS Tic single crystal boules grown by Union Carbide Corp., Linde Division, were doped with boron by placing them in a carbon crucible packed with boron powder and heating in a vacuum furnace to 2000°C for 1 hr. Samples 1 by 1 by 3 mm were cleaved from these doped boules. High-temperature compression tests&apos; were made on these samples to determine the critical resolved shear stress as a function of temperature . The rapid drop in critical resolved shear stress found for pure Tic crystals&apos; did not occur: tests indicated that the boron-doped crystals at 1600°C had values of T equal to those of pure Tic crystals heated to only 1100°C, Fig. 1. No difference in the shape of the individual stress-strain curves was produced by the boron doping, but the stress scale was multiplied by a large factor. The hardening effect of boron in Tic probably extends to temperatures lower than those used in the present work (1100°C minimum). At room temperature, however, the influence of boron is difficult to determine because the stress required for gross plastic flow in pure Tic is SO high that in practice fracture cccurs first. Microhardness is the only test that can give an indication of the yield stress in Tic at room temperature. such measurements were made5 on boron-doped Tic; the matrix had a hardness value

Jan 1, 1967

By C. H. Samans, G. F. Tisinai, J. K. Stanley

The times at which the first detectable amount of a phase forms at temperatures between 900° and 1800°F were determined. Both X-ray diffraction and metallography were used to detect a in highly strained filings; metallography alone to detect it in annealed bulk samples of six different types of stainless steels. The a phase was found to form in accordance with the C-type reaction curve in both austenitic and ferritic alloys. In filings of types 304, 347, and 446, a formed in a few hours, and in types 316, 309, and 310, it formed in a matter of minutes at temperatures corresponding to the knee of the C-curve. Only in the bulk type 309 steel, after 500 hr, and in the bulk type 310 steel, after as short a time as 25 hr at temperature, was n detected; in both instances at approximately the same optimum temperature as in the filings. The annealing temperature affected a phase nucleation only for the filings of type 304 and 347 steels, and for the bulk samples of type 309 and 310 steels. KNOWLEDGE of both the rate of nucleation and the rate of growth of the new phase is required for a complete description of metallurgical rate phenomena. However, data on the time for nucleation alone may frequently be useful in evaluating the tendency of commercial stainlcss steels to form s under various conditions. Very little correlated information of this type is available in the literature. Shortsleeve and Nicholson&apos; indicate that s forms in ferritic 24, 27 and 30 pet Cr steels according to a C-type of reaction curve, and Emmanuel&apos;s&apos; data for austenitic type 310 steel also suggest this type of solid state reaction. In addition, significant, though fragmentary, information has been given by Binder, Dulis and Smith,4 Payson and Savage,.; Guarneri, Miller, and Vawter,8 rerichs and Clark,7 Wilder,5 Lismer, Pryce, and Andrews,&apos; Smith, Dulis, and Link,10 Dulis, Smith, and Houston," and Henry, Cordovi, and Fischer." The bearing of these data on this work is covered in the discussion. The purpose of this paper is to present such correlated data on s formation in AISI type 304 (18 pct Cr-8 pet Ni), 347 (18 pet Cr-10 pet Ni-Cb), 316 (18 pet Cr-12 pet Ni-2 pet Mo), 309 (25 pet Cr-12 pet Ni), 310 (25 pet Cr-20 pet Ni), and 446 (27 pet Cr) stainless steels. Materials and Test Methods X-ray diffraction and metallographic methods were used to determine the first appearance of the s phase in cold worked filings and in annealed bulk samples of seven steels, under various combinations of time and temperature. The rate of growth of the s particles was not determined. Commercial heats of six AISI steels and a low carbon laboratory experimental heat containing about 28 pet Cr were studied. Analyses are given in Table I. Because cold work greatly accelerates the nucleation of s particles, the relative rates of s nucleation in mechanically strained samples, i.e., filings through 120 mesh, were determined for direct comparison with those in annealed bulk alloys of the same composition.

Jan 1, 1957

By Matti J. Saarivirta

The relative machinabilities of the precipitation-hardenable Cu-0.9 pct Cr, Cu-0.25 pct Zr, and Cu-0.9 pct Cr-0.25 pct Zr alloys are improved from 18 to 80 pct by 0.75 to 1.25 pct Pb. The Lead also improves the tensile strength, hardness, ad resistance to softening of the Cu-Cr and Cu-Cr-Zr alloys. When the alloy containing 0.7 to 2.2 pct Cr, 0.10 to 0.25 pct Zr, 0.75 to 1.25 pct Pb, and balance copper is solution-annealed at 1000°C (1830°F) and then aged at 525°C (Y75°F), tensile strength of 65,000 psi, 16 pct elongation, 62Rb hardness, and 84 to 87pct IACS electrical conductivity are obtained. The copper base Cu-Cr, Cu-Zr, and Cu-Cr-Zr alloys have high electrical and thermal conductivities, high strength and resistance to softening at elevated temperatures, but their machinability is poor, i.e., close to that of the pure copper. In the manufacture of various components such as welding electrodes or electrical and thermal conductors it is ofter desirable that the alloy have good machinability for high production rates and long tool life. Thus, alloys that combine these properties may be used not only for existing applications, but for new ones where good machinability is a requirement. This investigation was undertaken to improve machinability without impairing other desirable characteristics of the Cu-Cr, Cu-Zr, and Cu-Cr-Zr alloys. These commercial alloys contain about 0.4 to 1.2 pct Cr, 0.10 to 0.25 pct Zr, and balance copper. Lead was selected as an element that should improve the machinability and possibly other characteristics of the alloy. WORK PROCEDURE This investigation began with a study of the effect of lead on the hardness, tensile strength, electrical conductivity, and machinability of the binary alloy containing 0.10 to 1.30 pct Cr and balance copper. This was followed by an investigation of the effect of lead on the Cu-0.1 to 0.4 pct Zr and Cu-Cr-Zr alloys. The alloys were made from initially oxygen-free copper and for comparison some castings were made from phosphorus-deoxidized Lake Copper. Commercially pure chromium, zirconium, and lead were used for alloying. In melting the chromium was added to molten copper at 1400°C (2550°F), the heat held for 15 min at temperature, and the temperature then lowered to 1350°C (2460°F) when the other elements were added. The alloys were held for 15 min at this temperature and cast into a cast-iron mold. One-kilogram, 3-in.-diam castings were made. An argon cover was maintained during melting and casting to prevent oxidation. The chemical compositions of the alloys are shown in Table I. The micro structure and properties of the alloys were studied in the cast and wrought conditions prior to and after various solution-annealing and heat-treating cycles. The relative machinability was determined as a function of the lead content and compared with the free-machining Cu-lpct Pb alloy. To determine the machinability, 13/16-in.-diam cast specimens were cut by a machine hack saw using a constant cutting speed of 50 fpm, a fixed feed force, and a new blade for each alloy specimen. Molybdenum highspeed steel saw blades, 0.032 in. thick with 14 teeth per in., were used in all tests. No cutting fluid was used. Five tests were made on each specimen and the average elapsed time per test was taken as a measure of the relative machinability for that alloy. The variation of cutting time for each alloy was less than 110 pct.

Jan 1, 1969