By W. A. Backofen, G. Y. Chin, W. F. Hosford

The ductile fracturing process was studied in single-crystal and poly cvystalline aluminum deformed in tension over a temperature range from 295° to 4.2°K. At temperatures as low as 77°K, the fracture of "inclusion-free" material, including zone-refined aluminum, was by rupture (-100 pct RA). At 4.2 OK, fracture was brought on by adia-batic shear. Metallographic examination did not disclose any voids or slip-band microcracks, thus negating for inherently ductile metals any mechanism of void nucleation by vacancy condensation or of cracking due to dislocation pile-ups. In Izigh-purity aluminum not treated to be inclusion-free, fracture at temperatures as low as 45°K was of the double-cup type and a result of void formation. The reduction-of-area decreased as temperature was lowered, corresponding to the earlier appearance of voids. Such behavior was rationalized in terms of a larger increase, with decreasing temperature, in the .flow stress relative to the strength of the inclusion-matrix interface. Evidence for low-temperature adiabatic shear was found in discontinuous flow at 4.2"K, in the transition to a localized shear fracture at low temperatures, and in the suppression of shear fracture with an elastically hard pulling device. A simple analysis for the initiation of adiabatic shew permitted a general correlation of the various contributing factors. It has been pointed out that the duration of shear depends upon effective mass and elastic stiffness of the deformation system. IT has long been recognized that fracture* may Throughout this paper, the term "fracture" is taken to mean any process that results in the separation of a material into two (or more) parts. Thus rupture as it may be encountered in a tension test leading to 100 pct reduction-of-area is included in this category. occur in a ductile mode, and that the process can be of great practical as well as general interest. Much information about ductile fracture has also been accumulated over this period, but only recently has an understanding of mechanism begun to appear. Ludwik,' in 1926, first reported fracture in a tensile specimen starting with a central crack in the necked section. Since then, other studies have disclosed that such cracks may form by the coalescence of voids nucleated in this region where hydrostatic tension is highest.2-4 Rogers and Crussard et al.' have emphasized void formation and reori-entation along localized shear bands as a mode of crack propagation. pines6 has considered the tensile rod as a bundle of fibers joined by weak interfaces, which subsequently separate to allow individual fiber contraction. The notion of cavity growth and coalescence by purely plastic processes was discussed by Cottrell: who added that the tensile reduction-of-area ought not to be sensitive to temperature. On the other hand, it has been observed that the reduction-of-area is greatly increased if tests are carried out at high temperaturesa or under high hydrostatic pressure.' Fracturing anisotropy in wrought products lends support to the idea of void formation from preexisting flaws strongly aligned by earlier processing.''-l2 There is evidence that many voids result from the fracturing of inclusions or separation at the inclusion-matrix interface Another possibility is that voids grow out of pore volume produced in the initial solidification and never fully removed in later working. In general, a structure 3f particles, pores, and weak interfaces can be expected, at least in materials of engineering interest. Vacancy condensation has been suggested as an alternative mechanism of void formation for materials considered to be inclusion-free.13 Yet experience has shown that tensile reduction-of-area increases with purity, to the extreme of rupture as so often observed in single crystals. Adiabatic shear has an important bearing on ductile fracture. It occurs when the decrease of flow stress, as a result of local temperature rise from heat generated during straining, becomes larger than the increase due to strain and strain-rate hardening. As demonstrated by experiments on punching of plates,14 a large temperature rise may be brought about by rapid straining. Adiabatic flow as a result of the high strain rate reached in an ordinary tensile specimen just prior to separation may account for the cone formation in cup-and-cone fracture;14 evidence of such local heating has been presented.15 For geometrical reasons, however, pure sliding along the conical surfaces is unlikely, and separation under tensile forces is probably an important accompanying feature of the shear.7 In deformation processing operations, a high shear-strain rate may exist at boundaries between plas-

Jan 1, 1964

By H. I. Aaronson, C. Laird

Although the past results of X-ray experiments indicate that the broad faces of 0' plates are coherent with their matrix, dislocations lying in arrays have frequently been observed at these boundaries by transmission electron microscopy. Critical experiments employing the latter technique have been carried out in order to determine the origin of these dislocations. It is concluded that 8' plates are essentially coherent with the matrix at their broad faces throughout the aging temperature/time envelope studied. Virtually all of the dislocation arrays observed are deduced to have been formed by plastic deformation accompanying transformation. The proportion of dislocations arising from convexity of the plates is shown to be negligible by comparison with that from plastic deformation. At the higher aging temperatures, a[001] dislocations appeared in moderate numbers. These dislocations were traced directly, however, to the ledgewise dissolution of 0' occasioned by the formation nearby of 0 crystals. On the other hand, since there is a parametric difference normal to the broad faces of the ?' plates, mismatch dislocations do form at their edges. A previous conclusion that these dislocations have Burgers vectors of type a[001] was confirmed directly. The edges of 0' plates were observed to develop octagonal shapes when growing, but circular shapes during dissolution. 1 HIS paper presents the results of an investigation of the interfacial structures of plates of the transitional phase, 8', formed in an A1-4 pct Cu alloy. In a companion paper, Part 11, the effects of these structures upon the migration kinetics of a:?f boundaries are reported. This work is pa.rt of a general program designed to establish the basis of precipitate morphology. The present authors in Al-Ag,1 and whitton2 previously in U-C alloys, have used transmission electron microscopy to examine directly the vander Merwe3-6 networks of dislocations anticipated7 to compensate the small amount of lattice misfit normally founda at the broad faces of Widmanstatten plates. Since the broad faces of 0' plates are considered to be perfectly coherent with the corresponding habit planes in the a matrix,' no dislocations should be present at these faces. Many reports have been published, however, giving evidence to the contrary.10-18 The primary objective of this investigation was therefore to ascertain the nature of these dislocation structures. An attempt to do this is described in the first three sections of this paper. Inspection of the matching of the a and 8 ' lattices at the orientations of the 0:0' boundary corresponding to the edges of 0' plates raises the possibility that these edges may be made up of rather closely spaced edge- type misfit dislocations oriented so as to be sessile with respect to the lengthening or shortening of the plates. Since this structure should severely inhibit migration of the plate edges (Ref. 7, Part II), a situation not originally anticipated,' an experimental determination of the interfacial structure of the edges of 8' plates was clearly in order, and is reported in Section III. Those aspects of the experimental procedure applicable to both Parts I and I1 are presented in the next section. Specific procedures applicable to individual aspects of each investigation, and also the relevant surveys of the literature, are then individually reported in the appropriate sections. I) GENERAL EXPERIMENTAL PROCEDURE The material used in both parts of these studies was the same as that of a previous investigation:" strips of A1-3.93 pct Cu, 0.009 in. thick, prepared as before, solution-annealed at 548°C for 6 hr, and quenched. Details of subsequent aging, and in some cases deformation treatments, are given in the Experimental Procedure sections of the individual parts of both papers. Specimens of the heat-treated strips were electro-thinned as beforeLg and examined in a Philips EM 200 microscope equipped with a goniometer stage. A commercial hot stage, of the grid-heater type and capable of * 30-deg tilt about one axis in the plane of the specimen, was also used for kinetic studies. The usual precaution of calibrating for the additional heat supplied by the electron beam was taken.19 A 16-mm cine cam-I era mounted outside the viewing window was frequently used to record the transformations. Conventional selected-area diffraction and dark-field viewing techniques were used to identify the precipitates in the foils. Normal bright-field images corresponding to two-beam diffracting conditions or dark-field images were employed to characterize the dislocations observed at the interfaces of the precipitates. The application of these techniques to the study of an interphase boundary, and the interpretation of the images,20'21 has been fully described in a previous paper.'

Jan 1, 1969

By R. M. Hudson

The removal of nitrogen from a nitrogenized low-carbon sheet steel that contained 0.011 wt pct N was determined during heat treatment in Hz-N, mixtures. TIze process followed a first-order rate law; that is, plots of the logarithm of nitrogen content in steel were linear with the time of treatment at a given temperature. The rate of removal increased with an increase in temperature from 900" to 1300°F. By 1400°F the rate in dry hydrogen had decreased to a value intermediate between the rates at 1200" and at 1300°F; in wet (2.47 vol pct water vapor) hydrogen the rate at 1400°F was less than the rate at 1300°F and nearly the same as the rate at 1200OF. The rate at a given temperature increased as the 3/2 power of hydrogen concentration in the atmosphere. While wet atmosplzeres were generally more effective than the corresponding dry atmosplzeres, the effect of water vapor was much less pronounced than the influence of hydrogen content. NITROGEN is the principal agent in the strain aging of ferrite, the effect of carbon being secondary.' To eliminate the return of the yield point after straining and aging, it is claimed2 that the amount of nitrogen in solution in steel must be reduced to 0.0002 wt pct. Strong nitride-forming elements (titanium, vanadium, zirconium, and aluminum) can act to eliminate strain aging by combining with nitrogen. It is extremely difficult to decrease the nitrogen content in commercial steels to the low level required by conventional coil annealing because of the poor contact between the strip surface and the reactive atmosphere. However, a variety of gas-metal reactions can be effected by use of the open-coil annealing method,3 in which the metal surface is fully exposed to the atmosphere. With this possibility in mind, the Applied Research Laboratory has studied the influence of time, temperature, and atmosphere composition on the removal of nitrogen from low-carbon sheet steel. MATERIALS AND EXPERIMENTAL WORK Samples from a commercial nitrogenized low-carbon steel (0.010 in. thick) in the cold-reduced condition were used. The chemical composition of this steel is given in Table I. The gas mixtures used are listed in Table 11. The moisture content in the "wet" annealing atmospheres was controlled at a +70°F dew point (2.47 vol pct water vapor) by passing the gas mixture through a glass tube packed with a solid mixture of 10 pct anhydrous oxalic acid and 90 pct oxalic acid dihydrate held at 127°F; this technique has been described previously.4 For "dry" atmospheres, the gas mixtures were passed through a cold trap immersed in liquid nitrogen. A hinged-top Hevi-Duty electric furnace was used with a Vycor-glass furnace tube. When the furnace was at the desired temperature, the gas mixture was passed through the furnace at a flow rate between 1.1 and 1.2 cfh; coupons (size 3 by 3/4 in.) of the steel were pulled into the center of the Vycor-glass

Jan 1, 1964

By J. E. Campbell, G. D. Calkins, N. M. Ewbank, M. Pobereskin, A. Wesner

GRINDING for size reduction affects the economics of many processes and products. It is essential as the first step in many industrial processes and is also a finishing step for materials with properties depending on particle size, such as talc, cement, and silica sand. Intermediate and fine grinding are vital operations in the U. S. cement industry, which is producing more than 250 million bbl of cement per year.' Wear of the grinding media is a large part of the grinding operation cost. Problems encountered in grinding cement are so complex that evaluation of efficiency and economy of grinding media is difficult.2 It has been especially difficult to evaluate the relative effectiveness of different types of balls because there are no good testing techniques. Many other industrial operations can be evaluated on a laboratory scale with reasonable accuracy. This does not hold true for evaluation of grinding balls. The consistent results obtained in a laboratory test under a given set of conditions are not always borne out in field application. Rough evaluations of the effectiveness of various compositions and types of grinding balls have been made in the field by using a full charge of one type in a mill and comparing the production record with another run using another type of ball. This method is time-consuming and not very precise, as the second run may not have been carried out under identical conditions. Laboratory-scale tests, on the other hand, have yielded inconclusive results, and many investigators have turned their attention to the development of a field testing technique. Field testing small sample lots of grinding balls has been impractical because it is difficult to identify and recover the test specimens from the grinding mill, and individual groups of balls that have undergone different heat treatments can not be separated.".4 To overcome these difficulties, previous investigators have identified the balls by distinctive marks, notches, and drilled holes, but this procedure has three serious drawbacks: 1) Grinding characteristics and quality of the steel balls may be affected. 2) Physical markings may be worn away in the grinding process, especially during a prolonged run. 3) Recovery from the bulk of the charge will be extremely difficult because the markings are hard to see and may be masked by a coating of the product. To circumvent these difficulties, a radioactive-tracer technique was proposed for recovery and separation of steel grinding balls and subsequent evaluation of the various compositions of the balls. The proposed technique involved five basic operations: 1) Thermal-neutron irradiation activation5 of each group of test grinding balls to a different level of specific radioactivity. 2) Addition of groups of radioactive steel-ball specimens into a ball tube mill. 3) Recovery of radioactive steel-ball specimens from the bulk of the mill charge. 4) Separation of the various groups by their specific radioactivity. 5) Evaluation of actual grinding ball wear. Before any physical tests were performed, required neutron irradiation intensity and time were calculated. Probable composition of the steels to be used was ascertained. An examination was made of the radioactive nuclides8 to be formed which would contribute measurably to the radiation level immediately after irradiation and during the test operation. The radioisotopes formed, their types of radiation, and their half lives are listed in Table I. Of these radioisotopes only iron-59 and chromium-51 were significant for the actual wear test. The intensity of radiation that could be detected by a Geiger counter when the test was completed was the basis for the minimum activation level established. The intensity of radiaton that could be safely handled at the beginning of the test was the basis for the maximum activation level, although this was not considered a major problem. Ten groups of grinding balls of various composition and/or surface or heat treatment were to be tested. One group was designated for the minimum irradiation time. The remaining groups were designated for irradiation periods that increased by increments of 33 pct from that of each preceding group. This difference was considered enough for separation and identification of the groups by comparison of specific activity. Potential Hazards: Possible radiation hazards that might be encountered during this experiment were evaluated for the three important phases: 1) the radiation hazard of placing balls and removing them from the mill, 2) contamination of the product cement by radioactive material worn from the balls, and 3) contamination of the steel by the radioactive balls left in the mill. The radiation intensity expected from the whole group of radioactive balls was calculated to be 250 milliroentgen per hr at 1 ft. This meant the balls would require special shielded packaging and warning labels on the shipping containers. In a radiation field of 250 mr per hr a man can work for 1 hr without exceeding maximum permissible weekly exposure. Since the balls could be dumped into the mill in a matter of seconds, relatively little radiation exposure was anticipated at this stage of the operation. If the weight loss in the balls was 7.7 pct per month and the cement feed through the mill was

Jan 1, 1958

By J. B. Hess, C. S. Barrett

TO reach equilibrium between different phases in cobalt-rich alloys requires prohibitively long annealing cobalt-richalloystimes when temperatures are below about 700°C. The fact that a transformation from face-centered cubic to close-packed hexagonal readily tered takes place at temperatures below this in the cobalt-rich solid solutions is not an indication that thermally activated processes occur at an appreciable rate, for the transformation is well established as martensitic in nature. Wide divergence between heating and cooling experiments and high sensitivity to prior heat treatment make it difficult to judge temperatures of equilibrium between the phases.&apos; One object of the present work was to see if the information object of on the relative stability of phases could be gained by substituting plastic deformation for thermal agitation. Procedures were worked out that led to the determination of a diffusionless type of phase diagram, which represents the temperature of of phase equal stability for phases of the same composition, and the technique was applied to the Co-Ni system. Another object of the work was to see whether or not deformation would generate frequent stacking faults when these were thin lamellae of quentstackingfaultsa phase having higher free energy than the parent phase. The alloys were prepared in 80 to 100 g melts from cobalt (with metallic impurities estimated spectrochemically as follows: Ni, 0.05 pct; Fe, 0.001 pct.; Mg, Si, Cu, Cr, Al, < 0.001 pct) and Mond Car-bony1 nickel (with Fe, 0.05 pct; Si, 0.003 pct; C, 0.61 pct.; Cu, 0.001 pct; Co, Cr not detected, < 0.01 pct). The metals were melted in pure Al2O3 crucibles. An atmosphere of argon, that had been purified by passing over hot magnesium chips, was used for the alloys that, by analysis of the portions of the ingots actually used, were found to contain 15.3, 25.7, and 35.0 pct Ni, and vacuum melting (after degassing) was used for those containing 29.4 and 31.5 pct Ni. After induction melting the alloys were allowed to solidify in the crucible, and slices % in. thick x ½ in. in diam were annealed 12 hr at 1350°C for homogenization. These same specimens were used throughout the series of experiments, with annealing treatments of 4 hr at 900°C in purified hydrogen followed by furnace cooling, alternating with the deformation and X-ray tests discussed below. Results Spontaneous transformation was observed on cooling to room temperature in all alloys containing 29.4 pct Ni or less and by cooling the 31.5 pct alloy to — 195°C but was not observed in the 35 pct alloys after cooling to —195°C. These results are in satisfactory agreement with the cooling experiments of Masimoto.4 From these data it is clear that the temperature of beginning transformation M,,, drops to 20°C with the addition of about 30 pct Ni. The test for spontaneous transformation was metallographic. Specimens were thermally polished by annealing 10 hr in hydrogen at 1350°C, then furnace cooled; if trans- formation had occurred there were relief effects visible on the thermally polished surfaces. These markings were narrow straight lines, usually resolvable at high magnification as clusters of fine lines that resembled slip lines. It was concluded that they resulted from displacements on (111) planes, for the number of directions in individual grains often reached but never exceeded four, and lines could always be found parallel to the thermally etched (111) boundaries of annealing twins. The markings were thus consistent with the idea that the transformation occurs by (111) plane displacements (Shockley partial dislocations moving on (111) planes). This was further confirmed by X-ray tests for stacking disorders. Using an oscillating crystal technique previously employed to detect strain-induced faulting in Cu-Si alloys," streaks indicative of the stacking faults were looked for and found on X-ray films of the spontaneously transformed 25.7 pct Ni alloys, as expected by analogy with Edwards and Lipson&apos;s results on pure cobalt." The streaks were much intensified after rolling at room temperature. Transformation induced by plastic strain was investigated as a function of alloy composition and temperature of deformation. A series of tests was made to determine suitable straining and X-raying techniques. Filing was found inferior to abrasion in converting cubic samples to hexagonal, and abrasion was less effective than peening in producing smooth unspotty Debye rings in the X-ray patterns. Because the diffraction lines were broad, Geiger-counter spectrometer records of filings were less sensitive in revealing small amounts of transformed material than X-ray patterns recorded on films in a small diameter camera. After these exploratory tests the following methods were adopted. Specimens that had been annealed at least 4 hr at 900°C and furnace cooled were mounted in a block of aluminum, brought to temperature, and peened thoroughly with a mullite pestle preheated to the same temperature. The specimens were then quenched to room temperature. In peening, a circular area of % in. diam was given 500 blows. A few control tests showed that an additional 1000 blows did not detectably change the proportions of the phases present. The amount of transformation was judged by X-ray reflection patterns from the peened surface, using the innermost four lines of the cubic and the hexagonal patterns with filtered CoKa radiation,

Jan 1, 1953

By A. Totani, S. Nakajima, H. Okazaki

The phase diagram for the SnTe-SnSe system has been studied in the temperature range from 300° to 900°C by differential thermal and quenching techniques. The X-ray measurements were made on quenched specimens. High-temperature diffraction was also made to study the phase transition in SnSe. The system is proved to be of a eutectic type in which no intermetallic compound exists. The eutectic point is at the composition SnTeo.55 Seo.45. the eutectic temperature being 755°C. Solid solubility limits are SnTeo.6Seo.r and SnT eo. 3s Seo.6s at the eutectic temperature, and change almost linearly to SnTeo.aaSeo.lz and SnTeo.18 Seo.az as temperature decreases to 300°C. It was shown that the SnSe phase has a phase transition of the second order at about 540°C and that the transition temperature decreases with increase of the SnTe content. THERMOELECTRIC properties of tin telluride (SnTe) and tin selenide (SnSe) have been studied extensively in recent years. The variation of physical properties with composition could be of interest if these compounds form an appreciable crystalline solution. The purpose of present investigation is to confirm the formation of crystalline solution or intermetallic compound, if any, and to establish the phase diagram for this system. The crystal structure of SnTe is NaCl type with a cubic unit cell1 (a = 6.313A). The crystal of SnSe having an orthorh2mbic unit cellz (a = 11.496, b = 4.1510, and c = 4.4437A) is isomorphous with tin sulfide (SnS) which has a distorted sodium chloride structure. It has been known that SnSe has a phase at at 540°C; the transition has been assumed to be of the second order. As far as we know, only two studies on the SnTe-SnSe pseudobinary system have been reported. The conclusion obtained in these papers is that, in the composition regions near SnTe and SnSe, the system forms a crystalline solution of the SnTe structure and the SnSe structure, respectively, and that, in the intermediate region, both phases coexist. However, neither the variation of the solid solubility vs the temperature nor the liquidus and solidus were investigated. Hence present writers have attempted to determine the phase diagram of the system by differential thermal analysis (D.T.A.) and X-ray diffraction. EXPERIMENTAL Sample Preparation. Starting materials, SnTe and SnSe, were prepared by the direct fusion of commercially available high-purity (99.999 pct) elements. Stoichiometric amounts of each couple Sn-Te or Sn-Se were weighed into a clear fused silica ampule. After evacuation to a pressure below 10-3 mm Hg, the am- pule was sealed, and annealed at 900°C for 5 hr. The melt was quenched in water. X-ray analysis confirmed the formation of a single phase of SnTe or SnSe. The other samples, SnTel-,Sex were synthesized from these SnTe and SnSe by mixing them in the required ratio, followed by annealing at 900°C and quenching. These samples were used directly for D.T.A. For X-ray measurements, samples were annealed at 700°, 600°, or 500°C for 100 hr or at 300°C for 150 hr, and then quenched in water. It was found that the lattice constants of the SnTe phase annealed for 150 hr at temperatures above 500°C did not differ from those annealed for 100 hr at the same temperatures. However the X-ray phase analysis showed that at 300°C the annealing for 150 hr was necessary to attain a true equilibrium state. D.T.A. The solid-liquid equilibrium temperature was determined from D.T.A. measurements. The sample was sealed in an evacuated silica tube and molybdenum powders sealed in an another tube were used as a reference material. The sample and the reference tube were placed in a nickel block and were heated from room temperature to 900°C at a rate of 3°C per min and then cooled down at the same rate to 600°C. Thermocouples for these measurements were Pt-Pt. Rh (10 pct) and the error of temperature measurements was within + l0C. D.T.A. curves were obtained on a two-pen recorder and an automatic controller (PID type) was used for the program of heating and cooling. When temperature reaches the solidus from the low-temperature side, there appears an endothermic peak. The solidus temperature was determined by extrapolation of the straight portion of the starting flank of this peak to the base line. In a similar way, the liquidus temperature was determined from an exothermic peak on D.T.A. cooling curve. In the case of supercooling, if any, its degree can be estimated from the magnitude of the abrupt temperature rise. X-Ray . X-ray powder patterns were taken by a diffractometer using CuK, radiation. Since the SnSe crystal is cleaved easily, the powders become flaky when SnSe-rich samples are ground in an agate

Jan 1, 1969

By C. F. Jenkins, G. V. Smith

Serrated plastic flow in stable austenitic alloys based on Fe/Ni has been shown to be related to the presence of carbon and/or chromium in the systems. Strength peaks and plateaus in the serrated-flow temperature region for a commercial alloy correlate with an increased dislocation content, arising, presumably, from enhanced multiplication as a result of a strong interaction between dislocations and solute atoms. The data generally support a mechanism controlled by migration of vacancies, with the energy for vacancy motion being modified by the presence of chromium. Chromium atom -dislocation interaction is responsible for effects above 500°C, whereas the defect interacting with dislocations between 200" and 500°C is suggested to be a carbon-vacancy Pair. ThE phenomenon of jerky flow, serrated flow, or the Portevin-le Chatelier (P-C) effect in austenitic stainless steels is usually attributed to substitutional at1,2 mospheres1,2 or to precipitates&apos;-4 which form at dislocations during plastic deformation. On the other hand, evidence exists which supports a direct inter-stitial-dislocation interaction mechanism for serrated flow in fcc Ni-C,5,6 Ni-H7-9 and in nickel-austenites containing carbon." The present work consists in a study of serrated plastic flow in stable austenitic al-loys. The effects of carbon and of chromium were investigated separately, and a commercial stainless steel with different levels of interstitial impurity concentration was studied in an attempt to delineate the combined effects of the alloying elements. EXPERIMENTAL TECHNIQUES a) Materials and Fabrication. A commercial AISI 330 stainless steel and several specially prepared aus-tenitic alloys have been studied. The experimental alloys were prepared by arc melting the constituents under purified argon. Analyses of the materials are given in Table I. The commercial alloy was obtained as 5/8 in. bar stock and rolled to 0.092 in. sq, with several intermediate anneals. At this stage some of the material was annealed in Pd-purified hydrogen at 1100°C to establish different levels of interstitial content. All other heat treatments were in vacuum (10-5 torr). The "pure" alloy ingots were swaged to 0.120-in. rod and annealed in Pd-purified hydrogen at 1100°C. The analyses for these conditions are also contained in Table I. Following the above treatment, the final wire sizes Table I. Chemical Analyses of Test Materials Hrin Hydrogen at Cr, Ni, Alloy 1lOO°C wt pct wt pct C, ppm* N, ppm* Type 330 As-received 14.78 33.25 430 300 Type 330 64 14.78 33.25 40 50 Type 330 200 14.78 33.25 27 21 Fe/35 Ni 72 - 35.10 <10 62 Fe/35 Ni 200 35.10 <I0 44 Fe/35 Nil15 Cr 72 14.95 34.94 <I0 61 Fe/35 Ni/15Cr 200 14.95 34.94 <10 45 Fe/35 Ni/C $ 35.OM 380 *Sensitivity: N t 5 ppm Ct10ppm. f Nominal Ni content. % A master NiC alloy was used in preparation of this material; courtesy of D.E. Sonon. were obtained by either swaging or cold drawing. The test results did not vary with these techniques. b) Specimen Preparation. Two sizes of specimen and two gripping systems were used. i) 0.070-in. wire with a chemically milled gage section: 0.75 in. long, 0.060 in. in diam. These were fastened into grips containing tapped grooves. ii) 0.050 in. wire, gage length 1.5 in. Ball bearings were welded to the ends of the wires and the gage length was taken to include all material between the welds. Socket-type grips were used with these specimens. With specimens of type ii), joining was performed in a specially constructed brass jig, under argon, and automatic timing was utilized in the procedure. No adverse effects of welding were noted. Specimens were encapsulated and solution treated for 1 hr at temperatures selected to produce the same average grain size, -50 µ. Annealing twin boundaries as well as normal crystal boundaries were counted. The temperatures used are listed in Table 11. Table 11. Specimen Size. Temperature of Heat Treatment and Resulting Grain Diameters for Test Materials Recrystallization Resulting Material Condition Temperature Grain Sue AISI 330 Not H purified 0.070 120O°C 45 to 55µ in, wire AlSl 330 H , pure, 0.070 in. 1150°C 45to55µ wire Fc/35Nil15Cr Pure, 0.070 in. wire 1000°C 45tossp Fe/Ni Pure. 0.070 in. wire 775°C 45 to 55µ Fe/Ni/C Pure, 0.050 in. wire 850°C 10 to 20p AlSl 330 Not purified, 0.050 1150CC 45to55p in. wire AlSl 330 ti, pure, 0.050 in. 1150°C 45to55p wire

Jan 1, 1970

F. Lynwood Garrison, Philadelphia, Pa. (communication to the Secretary): I have been specially interested in Mr. Drake&apos;s valuable contribution to our knowledge of the Chinese coalareas, as I had occasion, about a year ago, to make a reconnoissance over some of the coal-fields in the Yangtse river valley. I noticed, as he appears to have done, certain peculiarities which may eventually prove to be characteristic of the Chinese coal-measures, at least in central and northern China. The most striking feature, perhaps, is the invariable proximity of the great granite masses to those coal-deposits which have an anthracite character. In common with all other anthracite areas elsewhere, the Chinese show evidences of profound stratigraphical disturbances. The sedimentary rocks are folded, faulted and dislocated in a manner similar to those of the Pennsylvania anthracite-regions. It would seem that the intrusive granite had much to do with converting the original bituminous into present anthracite. The action of the granite was probably direct as a conveyor of heat, and indirect as dynamic force in dislocating, overturning, and compressing the coal-measures. My stay in China was unfortunately cut short, so that I was unable to collect fossils, or to give this highly interesting and important subject more than passing attention. Cholnoky* and Richthofen are practically agreed that these granite eruptions took place during the Tertiary period—probably the Eocene. This profound tectonic movement has had a most important effect upon the geological conditions in central and northern China, and will be, I am sure, a potent factor in the economic development. Evidences of disturbances and metamorphism are very abundant in the anthracite-areas of the Yangtse valley. I noticed the coal in them, as did Mr. Drake in northern China, to be often flaky and " slickensided."

Jan 1, 1902

By L. Russell, van Wert

During an investigation in which the solubility relations of the phases in Muntz metal (60 per cent. copper, 40 per cent. zinc) were under study, certain phenomena that had no immediate connection with the main problem were observed, which were thought sufficiently interesting to study further. Because of lack of time, only a preliminary survey was made of two of these; namely, the cleavage structure developed under certain conditions in a 60:40 brass and abnormal grain growth in this alloy. Cleavage Structure in Heat-treated Muntz Metal Carpenter noted many years ago that cold-working a brass of the Muntz metal type, which had been quenched previously from within the beta field, results in a partial breakdown of the supersaturated beta solution and the precipitation of the solute (the alpha solution) in the cleavage planes of the beta grains. This manner of rejection of a solute from a metastable solid solution is not peculiar to this particular alloy, for among others, it occurs in the cold-working of certain austenitic steels; for example, the austenitic nickel steels. In these ferrous alloys, cold deformation produces a partial decornposition of the austenite, with the formation of martensitic "needles" and zigzags in the austenitic poly-hedra. It is interesting to note that while the two solid solutions— austenite and quenched Muntz metal— are metastable and in their mode of decomposition behave quite alike when deformed in the cold, the metastability of each results from a different cause; viz., that of the austenite from the fact that it is a supercooled solution (its solvent. gamma iron, at ordinary temperatures is below its normal stable range whereas the metastability of the quenched Muntz metal is the result of supersaturation. When a 60:40 brass is quenched from above 800" C.—that is, from within the field where the beta phase alone is stable—this solution is retained practically intact and the alloy so cooled is found to consist almost entirely of polyhedra of this solution with only a little alpha present ordinarily at the boundaries of the beta grains—the result of a slight

Jan 1, 1929

By van Wert, L. Russell

During an investigation in which the solubility relations of the phases in Muntz metal (60 per cent. copper, 40 per cent. zinc) were under study, certain phenomena that had no immediate connection with the main problem were observed, which were thought sufficiently interesting to study further. Because of lack of time, only a preliminary survey was made of two of these; namely, the cleavage structure developed under certain conditions in a 60:40 brass and abnormal grain growth in this alloy. Cleavage Structure in Heat-treated Muntz Metal Carpenter noted many years ago that cold-working a brass of the Muntz metal type, which had been quenched previously from within the beta field, results in a partial breakdown of the supersaturated beta solution and the precipitation of the solute (the alpha solution) in the cleavage planes of the beta grains. This manner of rejection of a solute from a metastable solid solution is not peculiar to this particular alloy, for among others, it occurs in the cold-working of certain austenitic steels; for example, the austenitic nickel steels. In these ferrous alloys, cold deformation produces a partial decornposition of the austenite, with the formation of martensitic "needles" and zigzags in the austenitic poly-hedra. It is interesting to note that while the two solid solutions— austenite and quenched Muntz metal— are metastable and in their mode of decomposition behave quite alike when deformed in the cold, the metastability of each results from a different cause; viz., that of the austenite from the fact that it is a supercooled solution (its solvent. gamma iron, at ordinary temperatures is below its normal stable range whereas the metastability of the quenched Muntz metal is the result of supersaturation. When a 60:40 brass is quenched from above 800" C.—that is, from within the field where the beta phase alone is stable—this solution is retained practically intact and the alloy so cooled is found to consist almost entirely of polyhedra of this solution with only a little alpha present ordinarily at the boundaries of the beta grains—the result of a slight

Jan 1, 1929

By Ben-Zion Weiss, Melvin R. Meyerson

Chromium diffusion coatings on commercial Armco iron lead to carbide precipitation at the grain boundaries in and below the coatings. High compressive stresses are introduced into the coating and, as a result, tensile stresses are introduced into the base material below the coating. In coated samples, fatigue cracks form at the grain boundaries below the coating after only a limited portion of the total lifetime (5 to 10 pct). Residual tensile stresses and a stress concentration caused by precipitated carbides seems to be responsible for early crack nucleation. Stage I of Propagation may be divided into two substages: I-a in which the crack Propagates along grain boundaries, and I-b in which the crack propagates along slip boundaries according to a shear mode. In uncoated samples, the cracks form at slip bands after 40 to 50 pct of the total lifetime. In coated samples the Propagation process takes longer than in uncoated samples because of the moderate rate of crack extension until the crack breaks through the coating. The chromium-diffusion coating causes little if any increase in fatigue life. CHROMIUM diffusion is one of the most popular processes used to apply coatings to iron alloys. This popularity stems from the fact that the diffusion treatment is comparatively easy to carry out, and it improves certain surface properties such as corrosion and wear resistance as well as some other properties. Very little effort has been devoted to the investigation of the effect of chromium-diffusion coatings on mechanical properties and particularly on fatigue properties. Since the chromium coating usually represents a small fraction of the total volume of the base material it is generally assumed that the macro properties are dependent principally on the base material rather than the coating. Insofar as fatigue is concerned, there are indications that the fatigue life of the chromium coating is not less than that of the basic material and the fatigue properties are generally not reduced by it.&apos; But chromium diffusion causes drastic structural and chemical changes in the region of the material surface2-4 which introduce additional residual stresses. Such changes must affect fatigue crack nucleation and may sometimes affect the initial stages of propagation. Furthermore, it is conceivable that the secondary stages of the crack propagation could be influenced by some irreversible structural changes in the core of the material, which stem from the long-time heat treatment at high temperatures required to apply the coating. This paper analyses the structural and compositional changes produced in commercial Armco iron by a chromium-diffusion coating and the effect of the coating on fatigue crack initiation and propagation. EXPERIMENTAL PROCEDURES The investigations were carried out with commercial Armco iron. The chemical composition of the iron, the number of specimens tested, the grain size produced during chromizing and heat treating, and the thickness and microhardness of the chromized layers are shown in Table I. Samples were chromized by a gas diffusion process. The temperature and time of the diffusion coating process were chosen according to a previous grain growth study. It had been found that at a temperature of 970°C and a holding time of between 3 and 9 hr there are practically no changes in grain size. To describe the grain size more accurately the ASTM method5 was supplemented by a statistical analysis of the mean volume diameter as outlined by Fullman6 and The The mean volume diameter was deter- mined from D = p/2m where D is the mean volume diameter, and m is the mean reciprocal value of grain diameters as seen on the micrograph. The shape and the size of the asymmetrical sample, see Fig. 1, were chosen so as to facilitate the study of fatigue crack initiation. Before coating, the samples were machined and the surface of the groove was polished. After chromizing, the two side surfaces were machined and polished so as to retain the coating only on the top surface of the groove. Residual stress in the chromized layer was measured on the top of the grooved section of the specimen after the diffusion process. The inclined incident X-ray beam procedure was used.9&apos;10 The computations were performed with the initial assumption of a zero surface normal stress component. An electron microprobe analyzer was used to obtain the relative amounts of chromium and iron con-

Jan 1, 1970

By W. D. Forgeng, P. F. Wieser

MnSi alloys containing from 2 to 24 at. pct Si have been investigated by metallographic and X-ray methods. Contrary to published data, the temperature of the ß-manganese to a-manganese transformation is lowered by the addition of silicon. The existence of two additional intermediate phases E and ( is demonstrated. E, ranging in composition from 12 to 15.5 at. pct Si, forms by a peritectoid reaction between ß manganese and the second new phase, (. The latter phase is homogeneous at silicon contents from 16.2 to 18 at. pct and forms peritectically from the 0 phase and liquid. The eutectic reaction occurs between the ( phase and MnsSi rather than the ß phase and Mn3Si. As a result of this investigation, a modification of the manganese-rich section of the MnSi equilihrium diagram is proposed. The binary diagram of Mn-Si, according to Hansen,&apos; Fig. 1, exhibits in the low-silicon region (below 24 at. pct Si) a peritectic transformation at 900°C of 0 manganese + Mn3Si to a manganese as determined by R. Vogel and H. Bedarff2 as well as a thermal effect at 980°C between 16.2 and 22.6 at. pct Si reported by the same authors. The nature of the latter transformation was unknown. K. Amark, B. Boren, and A. westgren3 reported indications that possibly four more phases existed in the range of 10 to 27 at. pct Si. The present investigation deals with the phase relations in the range of 2.1 to 17.7 at. pct Si. A few spot checks were conducted up to 23.84 at. pct Si. EXPERIMENTAL PROCEDURE Small experimental heats were prepared by induction melting in a vacuum furnace using argon as a protective atmosphere. The crucible was of commercial-quality magnesia. The furnace charge consisted of silicon metal and dehydrogenated electrolytic manganese. The typical analysis for these materials is shown in Table I. The molten alloy was tapped into 2-in.-square, 7-in.-long ingots. After visual inspection, a small quantity of alloy in the middle portion of the ingot was separated for use in this investigation.MnSi alloys containing from 2 to 24 at. pct Si have been investigated by metallographic and X-ray methods. Contrary to published data, the temperature of the ß-manganese to a-manganese transformation is lowered by the addition of silicon. The existence of two additional intermediate phases E and ( is demonstrated. E, ranging in composition from 12 to 15.5 at. pct Si, forms by a peritectoid reaction between ß manganese and the second new phase, (. The latter phase is homogeneous at silicon contents from 16.2 to 18 at. pct and forms peritectically from the 0 phase and liquid. The eutectic reaction occurs between the ( phase and MnsSi rather than the ß phase and Mn3Si. As a result of this investigation, a modification of the manganese-rich section of the MnSi equilihrium diagram is proposed. The binary diagram of Mn-Si, according to Hansen,&apos; Fig. 1, exhibits in the low-silicon region (below 24 at. pct Si) a peritectic transformation at 900°C of 0 manganese + Mn3Si to a manganese as determined by R. Vogel and H. Bedarff2 as well as a thermal effect at 980°C between 16.2 and 22.6 at. pct Si reported by the same authors. The nature of the latter transformation was unknown. K. Amark, B. Boren, and A. westgren3 reported indications that possibly four more phases existed in the range of 10 to 27 at. pct Si. The present investigation deals with the phase relations in the range of 2.1 to 17.7 at. pct Si. A few spot checks were conducted up to 23.84 at. pct Si. EXPERIMENTAL PROCEDURE Small experimental heats were prepared by induction melting in a vacuum furnace using argon as a protective atmosphere. The crucible was of commercial-quality magnesia. The furnace charge consisted of silicon metal and dehydrogenated electrolytic manganese. The typical analysis for these materials is shown in Table I. The molten alloy was tapped into 2-in.-square, 7-in.-long ingots. After visual inspection, a small quantity of alloy in the middle portion of the ingot was separated for use in this investigation.

Jan 1, 1964

By Raymond L. Orr

Calorimetric measurements have been made of the heats of solution of gold axd indium in a number of liquid tin-rich alloys at a temperature of 705°K. Relative partial molar enthalpies of gold were determined as a function of dilute solute concentrations in the binary Au-Sn system and in the ternary Ag-Au-Sn and Au-In-Sn systems. Relative partial molar enthalpies of indium were determined for dilute solute concentrations in the In-Sn, Ag-In-Sn, and Au-In-Sn systems. Through application of the interaction coefficient concept introduced by Wagner and more recently extended by Lupis and Elliott, ualues have been obtained for the Au-Au, Ag-Au, Au-In, and Ag-In enthalpy interaction coefficients in liquid tin. The results are inte@reted in terms of solute atom distributions through comparisons with the predictions of dilute solution models. INTEREST in the thermodynamic behavior of dilute liquid alloys stems from two primary sources. From a practical viewpoint, it is often of importance to know or to be able to predict the effect that one solute will have on the thermodynamic properties of the other solutes in a multicomponent system. Studies of dilute solutions may also be rewarding from the theoretical point of view. Some of the difficulties arising from the more complex interactions possible in concentrated solutions are avoided, leading to easier interpretations in terms of solutibn models and bonding energies. For example, in a binary alloy the limiting values of the partial molar properties of the solute represent the case for which each solute atom is completely surrounded by atoms of the solvent, and no other interactions are possible. Solute - solute interactions in dilute solutions are conveniently treated by the interaction coefficient concept of ~agner.&apos; Using a Taylor series expansion for the logarithm of the activity coefficient, In yi, of a component, i, in a solution consisting of dilute solutes with atomic fractions xi, xj, xk, and so forth, in a solvent, s, and neglecting the second- and higher-order terms, Wagner obtained the expression: Where Wheyz is the limiting value of yi in the pure solvent, s. The interaction coefficients, e:, e:, and so forth, are defined by: Since yi is related to the excess partial molar Gibbs energy of component i by GfS = RT In yi, E: is re- ferred to as the "Gibbs energy interaction coefficient". Lupis and Elliott~ extended Wagner&apos;s treatment to the relative partial molar enthalpy, aHi, and the excess partial molar entropy, qS. They defined the enthalpy interaction coefficient as: and the excess entropy interaction coefficient as: leading to expressions similar to Eq. [I]: The three interaction coefficients are related by? The self-interaction coefficients, E:,qf,and at, represent the effects of interactions between atoms of component i in solvent s; €3, q{, and 03 represent the effects of interactions between i and j atoms in solvent s; and so forth. From the Maxwell-type relationships between partial molar quantities, it may be shown1&apos;2 that e{ = ej, r}\ =tj), and ai - crj. Experimental determination of the interaction coefficients requires extremely precise measurements of the appropriate properties as functions of solute concentrations in very dilute regions. Few such data exist for intermetallic alloys, even for binary systems, because of experimental difficulties. This is especially true with respect to enthalpy data for dilute alloys. Examination of the compilation of data for binary alloys by Hultgren, Orr, Anderson, and ~elle~~ reveals that determination of limiting values of &fii(Xi =0) often requires extrapolations to infinite dilution from xi = 0.05 to 0.10. Direct measurements of the enthalpy interaction coefficient, qi, for multicomponent systems are virtually nonexistent. This quantity is of course subject to direct calorimetric measurement, but its determination must be limited to cases where high experimental precision is possible. The heats of solution of gold and indium in liquid tin can be measured with relatively high precision, which makes determinations of 73 involving these metals as the measured solutes experimentally attractive. This paper presents the results of such determinations of the Au-Au, Ag-Au, Au-In, and Ag-In enthalpy interaction coefficients in liquid tin. MODELS FOR DILUTE-SOLUTION BEHAVIOR Random-Solution Behavior. In the quasi-chemical treatment of solutions, only nearest-neighbor bonds are considered, and a composition independent value

Jan 1, 1967

By D. T. Peters, S. Floreen

The age hardening behavior of an Fe-8Ni-13Mo alloy was studied after the matrix had been varied to produce either ferrite, cold u~orked ferrite, or nzassive nzartensite. The aging behavior of the cold worked ferrite and murtensite structures were very similar. The martensite aging kinetics were much different from those observed in earlier studies of aging of maraging steels, even though the martensite wzatri.r had the same dislocation structure as those found in maraging steels. The results suggest that the previously observed precipitation kinetics of maraging steels ?nay have been controlled by the nucleation be-haviov, which in turn were dictated by the alloy compositions and the resultant identities of the precipitating phases. IT is well known that the rate of precipitation from solid solution depends not only on the degree of super-saturation, but also on the density and distribution of dislocations in the matrix structure. These imperfections often act as nucleation sites, and may also enhance atomic mobility. &apos;Thus, the presence of dislocations is important since the type and distribution of precipitates may be determined by them. The precipitate density and morphology in turn affects the mechanical properties of the alloy. A number of studies have been devoted to the precipitation characteristics in various types of maraging steels.&apos;-" These are iron-base alloys containing 10 to 25 pct Ni along with other substitutional elements such as Mo, Ti, Al, and so forth, that are used to produce age hardening. The carbon contents of these steels are quite low, and carbide precipitation is not believed to play any significant role in the aging reactions. After solution annealing and cooling these alloys generally transfclrm to a bcc lath or massive martensite structure characterized by elongated martensite platelets that are separated from each other by low angle boundaries, and that contain a very high dislocation den~it~.~~~~~~~~-~~ Age hardening is then conducted at temperatures on the order of 800" to 1000°F to produce substitutional element precipitation within the massive martensite matrix. Most of the aging studies to date have revealed several common traits in these alloys, regardless of the particular identity of the precipitation elements. Generally hardening has been found to be extremely rapid, with incubation times that approach zero. The agng kinetics, at least up to the time when reversion of the martensite matrix to austenite begins to predominate, frequently follow a AX/~~ = ktn type law, where x is hardness or electrical resistivity, t is the time, and k and n are constants. The values of n are frequently on the order of 0.2 to 0.5, which are well below the idealized values of n based on diffusion controlled precipitate growth models. Finally, the observed activation energy values are typically on the order of 30 kcal per mole, and thus are well below the nominal value of about 60 kcal per mole found for substitutional element diffusion in ferrite. The common explanation of these observations is that the precipitation kinetics are controlled by the massive martensite matrix structure. Thus, the absence of any noticeable incubation time has been attributed, after ~ahn," to the fact that the precipitate nucleation on dislocations may occur without a finite activation energy barrier. The low values of the activation energy are generally assumed to be due to enhanced diffusivity in the highly faulted structure. If this explanation that the precipitation kinetics are dominated by the matrix structure is correct then one should observe a distinct difference in lunetics between aging in a martensitic matrix and aging the same alloy when it has a ferritic matrix. Such a comparison cannot be made with conventional maraging compositions, but could be made with the alloy used in the present study. In addition, the ferritic structure of the present alloy could be cold worked to produce a high dislocation density so that one could determine whether ferrite in this condition would age similarly to martensite. EXPERIMENTAL PROCEDURE The composition of the alloy used in this study was 8.1 pct Ni, 13.0 pct Mo, 0.10 pct Al, 0.13 pct Ti, 0.012 pct C, bal Fe. The alloy was prepared as a 40 lb vacuum induction melt. The heat was homogenized and hot forged at 2100°F to 2 by 2 in. bar, and then hot rolled at 1900°F to $ in. bar stock. The aging lunetics were followed by Rockwell C hardness and electrical resistivity measurements. Samples for hardness testing were prepared as small strips approximately 2 by $ by 4 in. thick. Electrical resistivity was studied on cylindrical samples approximately 2 in. long by 0.1 in. diam. The method for making the alloy either martensitic or ferritic was based on the fact that the alloy showed a closed y loop type of phase diagram. At high temperatures, above approximately 24003F, the alloy was entirely ferritic. Small samples on the order of the dimensions described above remained entirely ferritic after iced-brine quenching from this temperature. In practice, a heat treatment of 1 hr in an inert atmosphere at 2500°F followed by water quenching was used to produce the ferritic microstructure. These samples were quite coarse grained and usually en-

Jan 1, 1970

By Brian F. Dyson

The surface tensions at 1550°C of some Fe-S alloys (in the range 0.008 to 0.052 wt pct S), Fe-Sn alloys (0.31 to 48.4 wt pct Sn), Fe-P alloys (0.038 to 2.38 wt pct P), Fe-Cu alloys (2.15 to 22.8 wt pct Cu), and Fe-1 pct C-S alloys (0.005 to 0.076 wt pct S) along with the surface tension of the base iron have been measured by the sessile-drop method. A mean value of 1754 dynes per cm was found for the surface tension of the base iron. Sulfur was found to be highly surface-active, the surface-tension results being in quantitative agreement with existing data. Tin and copper were found to be less surface-active than sulfur while phosphoms was completely nonsurface-active. The surface tensions of Fe-1 pct C-S alloys were found to be lower than those of the Fe-S alloys containing the same sulfur content. This was shown to be a mmzifestation of the increase in the thermodynamic activity of suZfur by carbon. It is only in recent years that attempts have been made to measure the surface tension of liquid iron of known high purity.1-3 Earlier measurements4-7 were made on liquid iron containing variable amounts of what are now known to be surface -active solutes. The exact value of the surface tension of liquid iron is still, however, open to some doubt. Halden and Kingery&apos; reported a value of 1720k 34 dynes per cm at 1570°C, Kozakevitch and Urbain8 gave 1790k 25 dynes per cm at 1550°C, while Van-Tszin-Tan et al. obtained a value of 1865k 37 dynes per cm at 1550°C. The first systematic investigation into the effect of controlled solute additions on the surface tension of iron was made by Halden and Kingery.&apos; They showed that sulfur and oxygen were highly surface-active, whereas nitrogen was only slightly active, and carbon inactive. A subsequent investigation by Kingery indicated that two other group-6B elements, selenium and tellurium, were also surface-active. This highly surface-active nature of sulfur and oxygen has recently been substantiated by Kozakevitch and Urbainla and Van-Tszin-Tan et al. l1 Kozakevitch and Urbainl2 have also conducted an experimental survey of the effects of a number of metals on the surface tension of liquid iron. Their surface-active nature was, in all cases, less than that of the group 6B elements. The present investigation was undertaken to study in more detail the surface tensions of dilute Fe-S alloys and to measure the surface tensions of binary alloys of iron containing phosphorus, copper, and tin. The effect of sulfur additions on the surface tension of Fe-1 pct C alloys was also determined. EXPERIMENTAL PROCEDURE The sessile-drop method was employed in the present investigation. An apparatus was built similar in principle to that described by Humenik and Kingery.lS It consisted of a horizontal silica tube, which could be evacuated to pressures less than 10-5 torr, with its central portion surrounded by a water jacket within which was a high-frequency coil. This generated heat in a tantalum susceptor placed inside the silica tube, which in turn radiated heat to the specimen mounted on a recrystallized alumina plaque. Temperatures were measured by an optical pyrometer and photographs of the molten drop were taken on a fixed-focus plate camera giving a magnification of X2. Surface-tension values were determined from the resultant drop using the method described by Baes and Kellogg.l4 The high vapor pressure of molten iron made it necessary to conduct all the experiments under a 1/4 atm of argon (greater than 99.995 pct purity). The analysis of the base iron used in the investigation is given in Table I. Each sample was approximately 3 g in weight and had a hemispherical base to ensure a uniform advancing contact angle on melting. The iron alloys were prepared individually in the sessile-drop apparatus by drilling a hole in the top of each sample and adding the required amount of solute, the drops being analyzed after the experiment. This method of preparation had the advantage of ensuring a consistent minimal contamination by oxygen due to refractory attack and also allowed surface tension to be measured at the same time. Every precaution was taken to ensure that the specimen was not contaminated by grease when it was introduced into the apparatus, the samples being cleaned in acid, dried in alcohol, and rinsed in petroleum ether. All handling was done with tweezers. Once the specimen had been placed inside the susceptor, the furnace was evacuated and the Sample leveled. The furnace was then degassed at approximately 1000"C before the argon was introduced. In every case the surface tension was determined at 1550" C.

Jan 1, 1963

By A. J. Mortlock

Cobalt and nickel have been diffused at tracer concentrations in gold at several temperatures in the range from approximately 700° to 950°C. The diffusion penetration profiles were determined by a serial sectioning technique in which the gold is first anodized and then the anodic layer is dissolved in acid. In this ulay sections as thin as 250A could be removed reproduci-bly. In all cases, the region close to the specimen surface was characterized by irregular behavior in the sense that the logarithm of concentration was not linear in the square of the penetration distance. In sotne cases, there zuas an indication of the operation of very slow dijfusion in this region, while in others the apparent diffusion coejj&apos;icient was negative. Possible reasons for this anomalous behavior are briefly discussed. In recent years it has been found that the region close to the surface of a metal can sometimes exhibit anomalously slow diffusion characteristics relative to the interior of the metal. One of the best examples of this fact is the work of Styris and omizuka,&apos; who showed that the apparent diffusion coefficient for zinc in the region withi: about 1 p of the free surface of copper was about ,,,, that at deeper penetrations. This result is particularly interesting, because it is free from the possibly complicating effects of low solubility of the diffusing tracer in the solvent metal. In the case of diffusion under conditions of low solubilitjr, interpretaticn of the results in terms of lattice diffusion is difficult because of the enhanced short-circuiting produced by segregation to dislocations.2&apos;3 Measurements by Duhl et 1. suggest that cobalt diffusing in gold may also show a near-surface effect of this type. Once again the solubility is high, so that this result could be of great interest. However, the technique used for analyzing the diffusion penetration zones by Duhl, viz. the counting of residual gamma activity in the specimen following sectioning, appears to have indicated a near-surface effect in a parallel experiment on the self-diffusion of gold reported at the same time. The latter result is known to be spurious, since Kidson5 has demonstrated that self-diffusion in gold does not show this effect. Duhl et 01. also reported some measurements on the diffusion of nickel in gold, but failed to give any data for the near-surface region. As the solubility of nickel in gold is high, such data would also be of special interest. We, therefore, decided to conduct another set of experiments on the diffusion of nickel and cobalt in gold, using a sectioning technique that allows the individual sections to be assayed for solute content and thus gives direct determinations of penetration profiles. Also, by sectioning with an anodizing/stripping tech- nique, very thin layers can be removed and the region close to the surface studied in detail. MATERIALS The gold specimens were supplied as single crystal disks $ in. in diam by a in. high by Monocrystals Co. of Cleveland, Ohio. The gold itself was of spectro-scopic purity, i.e., better than 99.99 pct pure. METHOD Specimen Preparation. One flat end face of each gold crystal was spark planed with a Servomet spark erosion machine set for minimum spark energy. Following this treatment the crystals were preannealed for 2 to 4 days at temperatures of either 400" or 700°C. The three crystals preannealed at 700°C showed signs of recrystallization. The spark-planed end face of each crystal was then coated with the appropriate amount of 63i or 60 radioactive tracer. This deposit was laid down in a simple plating bath containing the as-supplied solution of the radioactive isotope as well as sufficient ammonium oxalate to saturate the solution. Some ammonium oxalate remained undissolved on the floor of the bath for this purpose. During plating further additions of ammonium oxalate were sometimes required to allow the plating to continue satisfactorily, perhaps due to passivation of the undissolved oxalate already present. The thickness of the deposited layer was determined by comparison of the apparent surface activity of the plated specimen with that of a similar specimen having a weighable deposit of the isotope on its end face. Correction for self-absorption of the radiation was made in this calculation. Annealing. The deposited crystals were annealed in a hydrogen atmosphere in sealed silica tubes. During this heat treatment they were supported, active face down, on optically flat silica plates. The temperature was measured with calibrated Pt vs Pt-10 pct Rh thermocouples, and the tabulated values can be taken to be correct to Z°C. All the crystals showed evidence of recrystallization following these heat treatments, suggesting that initially they may not have been good single crystals or had suffered strain during delivery. Concentration Profile Analysis. After annealing, the crystals were sectioned by the anodizing-stripping technique.6 The anodizing involved suspension of the specimen with its cylindrical axis horiz6ntal by a gold wire in a 200-ml beaker containing 1 M Hg304. A cathode in the form of a strip of gold sheet, 2 in. wide and positioned to be in contact with the curved side of the beaker, completely encircled the specimen. An anodizing current of 30 ma, corresponding to a current density of 5 ma per sq cm on the surface of the specimen, was passed for times ranging from 5 to 150 min depending on the thickness of gold to be removed; the solution was stirred continuously during this process. Following this treatment, the specimen

Jan 1, 1969

By R. P. Agarwala, M. S. Anand

Using residual activity technique, the diffusion of palladium, silver, cadmium, indium, and tin in alunzinum has been studied in the temperature range of 400" to 630°C. The diffusivities (in units of square centimeters per second) have been expressed as: IMPURITY diffusion in aluminum,1-9 silverand lead5 for cases of low solid solubility of the impurity in the host metal has yielded frequency factors in the range of l0-6 to l0-9 sq cm per sec whereas the activation energy is practically half the self-diffusion activation energy value. From the observed values of frequency factor, activation energy, and entropy of activation, it has been suggested&apos; that these solutes are not diffusing by vacancy or interstitial mechanisms but by a mechanism which should be consistent with such low values of the diffusion parameters (Do and Q). However in spite of extensive work on these types of systems, the mechanism of diffusion is still not well understood. The present investigation on the diffusion of palladium, silver, cadmium, indium, and tin in aluminum has been carried out to throw further light on the diffusion mechanism in systems, where the solid solubility is very low (except for the case of silver). The results are discussed on the basis of solid solubility and the structural changes involved owing to the presence of the solutes in aluminum solid solution. An attempt has also been made to apply the existing theories of charge5-8 and size8 difference between the solute and the solvent. EXPERIMENTAL PROCEDURE Specimens (1/2 in. diam by 3/8 in. high) were machined out of pure aluminum (99.995 wt pct) rod obtained from Johnson Mattheys. They were sealed under vacuum in quartz tubes and annealed at 620° C for several hours; the grains thus developed were sufficiently large to eliminate the possibility of diffusion along the grain boundaries. The flat ends were prepared carefully after polishing as described previously,10 Radioactive nitrates of cadmium, indium, and tin and chloride of palladium containing, respectively, cd115, 1n114, sn113, and pd103 were dissolved in distilled water and mixed with 30 pct acetone. By means of a micropipet a drop of this solution was placed on a smoothly polished and lightly etched surface of the specimen. Due care was taken to see that the solution spread uniformly on the surface of specimen without trickling down its sides. Radioactive silver was elec-trodeposited using a AgCN-KCN bath. The amount of sample deposited in all the cases was not more than 0.1 µ thick. The samples were then sealed in quartz tubes in vacuum. The cadmium samples were sealed in a purified argon atmosphere to avoid evaporation. The samples were then diffusion-annealed. The temperature of annealing varied between 400° and 630°C and was controlled to ±5°C. On heating to -400°C,the deposits of cadmium, indium, and tin, which were of the order of 0.1 p in thickness, were converted to their respective oxides. The contribution of oxygen present in the lattice of aluminum due to these oxides has been calculated and found to be less than 10 ppm in all cases. Oxide method has already been used by other workers11&apos;12 in diffusion studies without any controversy on the issue. However, in some of these investigations, metallic deposition was also tried. The diffusivities calculated from these measurements were found to agree very well with the diffusivities obtained by using the oxide method. Thus it is assumed that the measured diffusivities represent true diffusion coefficients. Since palladous chloride decomposes at about 500°C, the deposited samples which were to be diffusion-annealed below 500°C were heated in vacuum for a very short time at 500°C to allow the decomposition of palladous chloride to palladium metal. Time taken in decomposition of nitrates to oxides and chloride to metal was negligibly small as compared to the period of the diffusion anneals. The residual activity technique13 was used to study the diffusion profiles where thin layers from the specimen surface were removed by grinding it parallel to a flat surface on a 600-grade carborundum paper. The specimen was washed, dried, and weighed, the differ -ence of the weight being the measure of the thickness of the layer removed. After each such abrasion and weighing, the total residual activity on the surface of the specimens was measured by counting 0.656, 0.94,

Jan 1, 1968

By A. H. Larson, L. G. Twidwell

The influence which Au, Ag, Sb, Bi, Sn, and Cu have, both individually and collectively, on the activity coefficient of sulfur in liquid lead at 600"C zuas studied by circulating a H2S-Hz gas wlixture over a specific lead alloy until equilibrium was attained. Subsequently, the H2S concentration in the equilibrium gas mixture and sulfur concentration in the condensed phase were deterruined. The elements gold, silver, and antinzony (above 8 at. pct) increased the activity coefficient of sulfur. Bismuth had no apparent effect. Tin (above 3 at. pct) and copper decreased the coefficient. The influence of an individual element, i, on sulfur is best reported as the interaction parameter, riS, which is defined as The values o these first-order interaction zus are: ESzu = —55.0. These interaction parameters are used to predict the activity coefficient of sulfur in six fouv-component alloys and one seven-component alloy. Comparisons are made with direct experimental determinations. INTERACTIONS in dilute solution have been studied by many investigators. Most of the experimental work has been confined to solute-solvent interactions in simple binary systems and solute-solute interactions in ternary systems. Dealy and pehlke"~ have summarized the available literature on activity coefficients at infinite dilution in nonferrous binary alloys and have calculated from published data the values for interaction parameters in dilute nonferrous alloys. Interaction parameters are a convenient means of summarizing the effect of one solute species on another in a given solvent. Only a few investigators have studied interactions of the nonmetallic element sulfur in a metallic solvent. They are as follows: Rosenqvist,~ sulfur in silver; Rosenqvist and Cox,4 sulfur in steel; chipman, sulfur in alloy steels; Alcock and Richardson,% ulfur in copper alloys; Cheng and Alcock,&apos; sulfur in iron, cobalt, and nickel; Cheng and ~lcock,&apos; sulfur in lead and tin. The only reported work on the Pb-S system in the dilute-solution region is that of Cheng and Alcock.&apos; Their investigation involved a study of the solubility of sulfur in liquid lead over the temperature range 500" to 680°C. The results may be summarized by the following relationship: S (dissolved in lead) + Pb(1) = PbS(s) log at. %S = -3388/T + 3.511 Experimentally, it was found that Henry&apos;s law was valid up to the solubility limit of sulfur in lead, i.e., at 600°C up to 0.43 pct. Their investigation did not include the study of sulfur in lead alloys. More accurate calculations could be made in smelting and refining systems if activity coefficients of solute species could be accurately predicted in complex solutions. One of the objectives of this study was to compare the experimental data with the values calculated from the equations derived from models for dilute solutions proposed by wagner9 and Alcock and Richardson. A temperature of 600°C was chosen as the experimental temperature to attain reasonable reaction rates and to minimize volatilization of the condensed phase. EXPERIMENTAL Materials. The Pb, Au, Ag, Sb, Bi, Sn, and Cu used for preparation of the alloys were American Smelting and Refining Co. research-grade materials. All were 99.999+ pct purity except the antimony and tin which were 99.99+ pct. The initial alloys prepared for this study consisted of twenty-one binary alloys, eleven ternary alloys, and one six-component alloy. The constituent elements were mixed for each desired alloy and were placed in a crucible machined from spectrographically pure graphite. The crucible was placed in a vycor tube which was evacuated with a vacuum pump and gettered by titanium sponge at 800°C for 8 to 12 hr. After the gettering was completed, the chamber containing the titanium was sealed and removed. The remaining sample chamber was placed in a tube furnace at 800°C for 2 hr and quenched in cold water. The final operation consisted of homogenization of the alloy for 1 to 2 weeks at a temperature just below the solidus for the individual system. The resulting master alloys were sectioned into small pieces and a random choice made for individual equilibrations. Cobalt sulfide (Cogs8) used to control the gas atmosphere in the circulation system was prepared by passing dried HzS for 24 hr over a Co-S mixture heated to 700°C in a tube furnace. This material was then mixed with cobalt metal to give a two-phase mixture which, when heated in hydrogen to a particular temperature, produced a desired H2S/H2 gas atmosphere in the circulation system. A Cu2S-Cu mixture also used in this study was prepared in a comparable manner. Apparatus for Equilibrium Measurements. The experimental technique of this study required apparatus

Jan 1, 1967

By J. O. Brittain, E. P. Lautenschlager, D. A. Kiewit

Compression tests were run in the temperature range of 700° to 900°C ox 0&apos; phase NiAl intermetal-lic alloys of several grain sizes. At these temperatures the minimum strengths were observed at the stoichiometric composition. While significant increases in strength occurved in both the low-nickel (vacancy) and high-nickel (substitutional) regions, the highest strengths were found in the high-nickel region. During deformation serrated flow was sometimes observed in the low-nickel alloys. After deformation transgranular cvacking and deformation striations were observed in all compositions tested. AS part of a general investigation of the properties of NiAl inter metallic compounds, a preliminary study of the role of point defects upon plasticity was made by high-temperature compression tests on ß&apos; NiAl specimens of several grain sizes and compositions. ß&apos; NiAl is an intermetallic compound having a CsCl structure and a rather wide range of composition from A1-45 at. pct to 60 at. pct Ni.1 According to Bradley and Taylor2 and to cooper,&apos; it possesses a defect lattice in which departures from stoichiometry in the direction of decreased nickel content lead to the presence of vacant nickel sites (although Cooper&apos;s work indicates that a small amount of substitution also occurs) whereas departures on the high-nickel side lead to substitution of nickel on aluminum sites. NiAl forms congru-ently from the melt at approximately 1650°C,1 and thus has a higher melting point than either of its component elements. Up to this time, although this and other high-melting intermetallic compounds have been suggested for elevated-temperature usage,4 only the hardness4 and a few tensile-strength measurements5 have been reported for NiAl at high temperatures. In the present investigation the effects of composition upon the compressive-strength properties in a range of 700° to 900°C have been measured for NiAl of several grain sizes. EXPERIMENTAL PROCEDURES The alloys were made as described elsewhere6 from an A1-46.8 at. pct Ni master alloy furnished by the International Nickel Co. with additions of high-purity nickel and aluminum. The charges were vacuum-induction-melted in A12O3 crucibles with small amounts of helium added to the atmosphere to suppress vaporization. They were cooled slowly from the melting temperature to achieve uniform grain size. In order to refine the as-grown grain size a special rolling technique was developed. Alloys were packed into 0.10-in. wall-type 302 stainless-steel tubes which were partially filled with magnesium oxide to prevent bonding between the alloy and the steel jacket. The ends of the tubes were closed by hot forging, and the packets were then hot-rolled. The alloys with greater than 50 at. pct Ni were rolled at 1100°C, but it was found necessary to increase the temperature to 1350° C before alloys with less than 50 at. pct Ni would roll without cracking. With these temperatures, reductions as high as 48 pct were achieved in a single pass. The rolled alloys will hereafter be referred to as "fine grained" whereas the as-grown material will be designated "coarse-grained&apos;&apos;. The compression specimens were made by cutting square cross-sectional pieces, approximately 3/16 by 3/16 by 1/2 in., with a water-cooled diamond cut-off wheel from the as-grown or the rolled alloys. Specimens were ground to their final dimensions by polishing through 3/0 grit silicon carbide papers. The final shape was a rectangular parallelepiped of square cross section having a height-to-width ratio of 3:1. Compression testing was carried out in a compression rig of our own design mounted on an In-stron Floor Model. The specimen chamber could be heated to 1000°C and was controlled within ±2°C. The compression rig was enclosed within a bell jar and was maintained at a 50 µ of mercury vacuum throughout the duration of the test. The test cham -ber was heated from room to test temperature within 15 min. Specimens were then held at the test temperature 30 min prior to testing. Previous experiments indicated that no grain growth would occur within this time. An Instron Variable Crosshead speed unit was used to adjust for small variations in specimen lengths in order to have a constant initial strain rate, €, for all specimens of a group. For the fine-grained specimens the strain rate was changed rapidly at constant temperature by a factor of 10 with the speed lever on the Instron. For a given € the compression data was analyzed in terms of true plastic strain (E) and true compressive stress (0).

Jan 1, 1965

By G. P. Airey, R. F. Mehl, T. A. Hughes

The coarsening of cementite particles in a ferrite matrix has been studied in a series of steels with 0.15 pct C only and 0.15 pct C plus 1 pct Ni, Mn, and Cr, respectively. Two initial states were employed: quenched nartensite, and quenched and cold-rolled martensite. A series of tempering temperatures between 500&apos; and 700" and tempering times of up to 190 hr were used. The structures were studied by replica and transmission electron microscopy. Particle size distribution curves were determined. From the average size value coarsening curves were obtained. These were plotted in accordance with the Wagner analysis assuming diffusion control. A discussion of the significance of the results is given. L HE reactions occuring upon the tempering of martensite have long engaged the attention of metallurgists. The latter stages, when cementite particles coarsen in a ferrite matrix, have been studied both qualitatively and quantitatively. Studies of such coarsening processes have recently been spurred by the publication of the Lifshitz-Wagner theory1, and the extension of this to the a Fe-Fe3C system by Oriani3 and by Li, Blakely, and einold. Following Wagner the coarsening process is often designated as "Ostwald Ripening". The only quantitative data on the rate of coarsening, except for the work of Hyam and uttin,&apos; in the a Fe-Fe3C system are those of Bannyh, Modin, and odin&apos; for a commercial eutectoid steel and those of Heckel and ereorio" using a pure eutectoid steel. The data of Bannyh, Modin, and Modin have been employed by 0riani3 to derive the a Fe-FeE interface energy. The reaction is one of the most important ones in steel and is worthy of detailed study. This is the purpose of the present study. Laboratory heats were prepared; these were steels with approximately 0.15 pct C, selected so that the num ber of carbide particles would be relatively small and thus so that the overlapping diffusion fluxes would be minimized, presumably a desirable circumstance.&apos;-3 In addition to Fe-C alloys, comparable heats containing 1 pct of Ni, Mn, and Cr, respectively, were included with a view of appraising the effect of alloying elements. This report includes an account of the micro-structures observed, primarily with the electron microscope, and of kinetic data and their interpretation. MATERIALS AND TREATMENT The alloys were prepared from electrolytic iron ("Plastiron") and high-purity graphite; these were melted in a zirconia crucible using a vacuum furnace. The alloy steels were made by adding electrolytic nickel, electrolytic manganese, and "vacuum grade" chromium, respectively, under a partial pressure of argon. Each melt was poured into a mold within the vacuum furnace and cooled in the mold. The ingots were 2 in. in diam. and 8 to 10 in. long. The analysis of the alloys is given in Table I. These ingots were hot-rolled to strip 0.1 in. thick, then cold-rolled to 0.05 in. and each alloy split into two batches. One batch was austenitized at 1200 for 1 min, quenched in cold brine, then cold-rolled to 0.02 in.; samples given this treatment are hereinafter designated as "worked". The other batch was cold-rolled to 0.025 in., austenitized at 1200" for 1 min, and quenched in cold brine; such samples are hereinafter designated as "quenched". These two batches were then tempered, as below. The purpose of the treatment given the first batch was to provide an initial structure of cold-worked martensite, with the expectation that the additional defect structure created by cold work would encourage a higher rate of nucleation of cementite on tempering and hence a more uniform distribution of cementite particles. Individual specimens were sealed in evacuated quartz or Pyrex tubes, then tempered in a muffle furnace. The temperature control was better than 3&apos;C at 700. Tempering treatments wer: performed at 400°, 500°, 550°, 600°, 65o°, and 700C for time periods between 15 min and 190 hr. PREPARATION OF SPECIMENS Specimens for optical and replicalelectron microscopy were mounted, polished conventionally, and etched with 2 pct nital. For electron microscopy, single-stage "formvar" replicas were made, dry-stripped and rotary-shadowed with chromium at an angle of 30 deg. Carbide extraction replicas were prepared from electropolished specimens usirig the method described by Smith and uttin.&apos; Thin foils for electron transmission microscopy were prepared by chemical thinning in an H202-HF bath prior to electropolishing in a chromium trioxide-acetic acid solution. The most

Jan 1, 1969