By Leo F. Reinartz

Part III of a four-part series on the history of steelmaking in the US, describes furnace developments, improvements during the last few decades, and the contribution of the AIME. THE invention of the dolomite machine was a great boon to the open-hearth furnaceman. By speeding up bottom making, it helped to increase tons per hour and decrease cost. The first homemade unit was built and operated before 1925 at the South Side works of Jones & Laughlin Steel Corp., Pittsburgh The first commercial machine, similar to those known today, was built for the Donner Steel Co., Buffalo, N. Y., in 1925. Heavy slab buckstays, 6 in. by 15 in., supplanted lighter I-beam buckstays as furnace framework in the middle 1920's. They greatly improved the rigidity of the furnace binding. Although the first sloping back wall had been in- stalled prior to 1920 on a small basic open-hearth foundry furnace at Columbus, Ohio, the impetus to install such back walls universally in ingots shops came after S. Naismith installed the first one on an open-hearth furnace at Illinois Steel Company's South works in June 1924. Before that event, back- wall life had already been improved somewhat by the use of chrome rock or metal-encased basic brick. Here again, these changes heralded major for- ward steps in furnace design, decreased costs, in- creased production, and improved safety and working conditions on the back standing of the furnace. Fuels Up to 1930, a number of different kinds of fuel were used to melt and refine steel in American open hearth furnaces. During World War I, powdered coal was used in a few plants as an open-hearth fuel, but because of the high sulfur and ash content in the coals, many operational difficulties arose. There were also dust, explosion, and accident hazards, so that after the War its use was discontinued. In some steel-manufacturing centers, natural gas was available as a fuel and gave good performance. In most steel-manufacturing centers, operators had to rely on producer gas made from bituminous coals in producer gas houses. Low-sulfur low-ash, high-fusion coals required for the manufacture of such gas were not readily available. The quality of producer gas was uncertain. The gas had to be pre-heated. Maintenance problems connected with the use of this fuel were serious. Tons per hour per month was unsatisfactory. Although petroleum had been first discovered by Edwin L. Drake at Titusville, Pa., in 1859, it was not until the early 1930's that heavy fuel oil residues for open-hearth use began to appear on the market. They were cheap; the calorific value was high, and it was not necessary to pass this fuel through the checkers to preheat it. Various plants began to use such oil as an open-hearth fuel. Others used it in combinations with tar, coke-oven, and/or blast-furnace gases. Because of its low calorific value, blast-furnace gas had to be preheated in the checkers. These fuels were cleaner and more dependable than producer gas. The dirty gas house adjacent to the open-hearth shop was no longer needed, and

Jan 1, 1961

By A. E. Jenkins, A. Jostsons

Isothermal sections of the Ti-0-H phase diagvam at 600°, 700°, and 800°C have been constructed from equilibrium hydrogen pressure measurements over a range of Ti-0-H alloys containing up to 34 at. pct 0. Oxygen reduces the hydrogen solubility at fixed hydrogen pressure but increases the terminal solubility in the a solid solutions at the a/(a + P) phase boundary. Metal-lographic studies of alloys annealed below the eutectoid temperature show that oxygen also increases the ter-ninal solubility of hydrogen in the a solid solution in equilibrium with the hydride phase. The effect of oxygen on hydrogen solubility is discussed in terms of the electronic and geometric structure of interstitial solid solutions. THE isothermal solubility of hydrogen in a Ti-0 alloys at 800°C has been measured by Hepworth and ~chuhmann' who subsequently used ternary Gibbs-Duhem integrations to calculate oxygen activities in binary Ti-0 alloys. The present study aims to extend Hepworth and Schuhmann's measurements to alloys richer in oxygen and to a range of temperatures. This paper presents the results of hydrogen equilibrium pressure/concentration measurements in Ti-0 alloys as well as observations on the effect of oxygen on the terminal solubility of hydrogen in a titanium. The thermodynamic properties of binary Ti-0 alloys, derived from these measurements, will be published separately.' EXPERIMENTAL METHODS Specimen Preparation. Ti-0 alloys were prepared from iodide-refined titanium and titanium dioxide obtained by hydrolysis of redistilled titanium tetrachlo- ride. Specimens containing up to 16 at. pct 0 were prepared by electromagnetic levitation3 whereas a conventional tungsten arc furnace with a water-cooled copper hearth was used to melt oxygen-rich alloys. The specimen homogeneity was indicated by the constancy of lattice parameters of samples from various parts of the ingot as well as by the sharpness of the reflections on X-ray powder patterns. Oxygen-rich specimens in the composition range (20 to 34 at. pct), where ordering has been ~bserved,~ were annealed for 300 hr at 600°C prior to use in hydrogen solubility measurements. Apparatus. The hydrogen pressure/concentration measurements were made with a modified Sieverts apparatus shown diagrammatically in Fig. 1. Specimens were placed in a clear silica tube and impurity pickup by direct reaction with silica was prevented by lining the heated end of the silica tube with thin molybdenum sheet. A double silica tube was required to eliminate loss of hydrogen by diffusion through silica at high temperatures and high hydrogen pressures, the space between the tubes being maintained at a hydrogen pressure equal to that above the specimen. Hydrogen was purified by diffusion through a Ag-Pd tube.= Hydrogen pressures were measured with a mercury McLeod gage in the range 0.001 to 4 Torr

Jan 1, 1968

By J. J. Calaman, D. H. Fleming

DURING 1950 the jet-piercing process was used commercially in the piercing of primary blast-holes in magnetic taconite at the preliminary taconite plant of .the Erie Mining Co., Aurora, Minn. The Erie Mining Co. purchased a jet-piercing machine and associated equipment in 1949, and the machine has been in operation since its installation in the summer of that year. An overall view of the pit with the JPM-1 jet-piercing machine in operation is shown in Fig. 1. During three months of 1949 and continuously since February 1950, production piercing took place under all pit conditions. By the end of October 1950, a total of 15,000 linear ft of hole had been pierced in an open pit handling an average of 1200 to 1800 tons of crude a day in one 8-hr shift. While it is recognized that this output does not approach the millions of tons a year planned for the developing Minnesota taconite projects, the machine as a unit has been operating under conditions probably more adverse than those that eventually will be encountered in the large operations. This pilot operation has permitted evaluation of the piercing problem in the full-scale taconite plant. This paper describes jet-piercing process funda- mentals, important features of the latest jet-piercing burners and machine, actual piercing results obtained, and new developments that give promise of materially increasing overall process efficiency. To produce the blasthole, jet-piercing utilizes thermal energy, as contrasted with the application of mechanical energy in churn drills and jackham-mers. The heart of the process may be termed a tailored flame produced by a rocket-type burner, thermodynamically similar in every respect to that of the giant rockets being developed for military purposes. The heat release in the combustion chamber of the burner is about 50x10' Btu per cu ft per hr as compared with 5x10' for most modern steam generators.* Combustion of liquid petroleum fuels (kerosine, diesel oil, or No. 2 fuel oil) with gaseous oxygen in the burner chamber at pressures of 100 to 200 psi results in temperatures of about 4300°F. Expansion of the hot combustion gases through divergent nozzles produces high-temperature supersonic jets having measured velocities of about 6000 fps. Impinging the flame jets on rock causes a thin surface layer to expand and break away from the base as a result of the thermally induced stresses. This spalling action is aided further in chert and quartzite by the 0.82 pct volume change resulting from the 6 to p quartz inversion at 1066"F.t The dynamic action of the jets whisks the spalled rock

Jan 1, 1952

By J. E. Burke

Recent investigations have elucidated many of the phenomena of the grain growth process, but have also revealed some conflicting and unexplained results. Beck and his co-workers 1,2,3 have shown that grain growth continues with continued heating at one temperature until the average grain size approaches the thickness of the specimen. Plotting the logarithm of the average grain diameter, D, against the logarithm of the annealing time, t, they find the straight line relationship given by the equation: D = Ktm [,] with possible small deviations at short annealing times. K and n are constants at constant temperature. On the other hand, Wa1ker4 finds that, in alpha brass) the rate of growth falls off more rapidly than indicated by Eq i after long annealing, so that an equilibrium grain size is approached. Burke5 showed, using Walker's data, that time and temperature for grain growth are apparently related through an activation energy, H, according to the relationship: ] where h and tz are the annealing times necessary for the average grain size to increase from Do to D at temperatures T1 and T2 and R is the gas laws constant. In the case quoted, H had the value 60,000 cal per mol. The apparent validity of this relationship, at least up to 700°C, and the approximate value of H were later confirmed by Beck3 The results obtained by Beck Kremer, Demer and Holzworth2 for aluminum and aluminum-magnesium alloys could not be satisfied by such a relationship, since the slope of the isothermal curves increased with increasing temperature. These data indicate and Beck, Holzworth and HuV ater demonstrated expcrimentally that the only apparent factor controlling the rate of grain growth at constant temperature is the grain size. While many of the phenomena have been elucidated, a reasonably quantitative explanation of the process is lacking. There exists uncertainty even as to the primary driving force for grain growth, although there is a considerable body of indirect evidence that the interfacial energy of the grain boundary is responsible.7,8,io Making implicit use of this assumption, several authors14,16 have pointed out that grain boundaries should migrate toward their center of curvature. Harker and Parkerg have advanced this concept furthest, and show that one can expect grain boundary migration to occur only when the grain faces are curved, or when they meet at non-equilibrium angles. When the face is curved toward a grain A, for example, the atoms in the surface of grain B, on the other side of the boundary7 are on the average more surromded by the atoms of their lattice than the atoms on the surface of grain A. Because of thermal motion, the atoms at the interface will sometimes be attached to grain A and

Jan 1, 1949

By H. E. Lee, P. C. Feddersen, D. R. Gittinger, G. W. Dunn, J. B. Schuettenhelm

The new Bunker Hill slag-treatment plant, designed ior, a capacity of 300 to 400 tons of hot slag per day, was "blown in" April 5, 1943. In the ensuing I5-months period, 157,530 tons of slag was processed, with an average recovery of over go per cent of the zinc and practically all of the lead contained. In addition to this high metal recovery, utilization of the waste heat in the gas and fume venting, the process has enabled the generation of 231,376 tons of steam at 250-lb, gauge. Over the first six months opcration the volume of slag treated averaged somewhat under 300 tons per day. Reclaimed dump slag made up only about 1 5 per cent of the plant feed. In October 1943, preparations for the smelting of additional tonnages of dump slag were completed and the plant capacity was increased to an average of about 420 tons of slag per day. During the nine-months interval since that date, monthly averages of 450 toils per operating day have been maintained several times. The new plant (Fig. I) is constructed in close proximity to blast-furnace operations. The fuming furnace and other necessary equipment are housed in an eastward extension of the existing blast-furnace building. Beyond this housed extension the dust-laden gas is conveyed about the perimeter of a large rectangle formed by the flues, cooling towers and baghouses. The course of a 10-ft. balloon flue, which transports the fuming furnace gas, describes the west and south perimeters. This flue connects with a set of cooling towers located at the southeast comer. The flue and cooling-tower system serving the deleading kiln constitute the north side and the two baghouses, serving the kiln and furnace operations, -border the east side. From these baghouses the several discharge gas flows are come biped and conveyed in to the rectangle, being vented to atmosphere by means of a fan through a centrally located zoo-ft. brick stack. In general, the plant design and operation follow quite closely that dictated by experience gained in years of slag-fuming practice by the Anaconda Copper Mining Go., at East Helena, Mont., and the Consolidated Mining and Smelting Co. of Canada, Ltd., at Trail, B.C., and more recently by the International Smelting and Refining Co. at Toocle, Utah. : Fuming operations at the East Helena and the Tooele plants are more or less identical. Trail practice differs chiefly in the methods employed for the storage of the hot feed slag and in the methods utilized for the handling and cooling of the fuming furnace gas. The new Bunker Hill fuming plant closely follows Trail procedure in the treatment of the furnace discharge gas while East Hclcna methods have been adopted for the storage of feed slag.

Jan 1, 1944

By Frank S. McKenna, Myron A. Pugacz, Clarence E. Jackson

THE notched-bar impact test has proved worth while in certain applications as a test for control of the quality or the heat- . treatment of steel. In view of the serious thought that even so simple a test as the tensile test, has evoked during the past years, it is not surprising that the notched- bar impact test should have inspired much experimental work. The correlation of the great number of data has not been successful, although steady progress has been made toward a better understanding of this test. Progress has been made, especially, in the isolation of the effects of the many variables that control the results. The stress system imposed on a specimen with a notch is so complicated and un- predictable that no simple evaluation of the test has been possible. Because of this uncertainty, many engineers hesitate to use the notched-bar impact test, and this attitude may well continue until a better understanding of the effects of the variables in the test are available. Without doubt, any additional data that may be presented should be accompanied by as complete a description of the details of test as possible, so that it may be added to the general fund of information that is to serve as the basis for the theory of the notched-bar impact test. The many factors that may control the test results have been pointed out repeatedly. The importance of the effect of the type and dimensions of the specimen has been recognized. Most of the work reported by American investigators has been limited to small- size (Charpy) specimens tested as a simple beam; two types of notches (Fig. I) have been commonly used. Considerable data have also been presented by many investigators using a small specimen tested as a cantilever beam; this commonly being called the Izod test. Here, however, a shear component of stress makes the stress system even mare complex than that present in the simple beam type of test, hence a critical analysis is difficult. Much work has also been reported by investigators using the tension type of specimen. A second variable that must be con- trolled is the testing temperature. An indication that the tests were performed at room temperature is not sufficient, since in many steels a variation of a few degrees in the actual testing temperature may be sufficient to give an entirely different range of results. Other factors. such as the com- position and condition of the material being tested and the speed of test, should also be considered. Many investigators have contributed data and theoretical discussions on the problems encountered in notched-bar test-

Jan 1, 1944

By B. M. Larsen, L. S. Darken

SOME years ago we collated all laboratory data then available to us on the distribution at equilibrium of manganese and of sulphur between metal and simple slags, and used the results in setting up an equation, which proved to be in accord with determinations of the distribution ratio of manganese and of sulphur between liquid steel and open-hearth slag, over a wide range of operating conditions. We now present an outline of our calculations and inferences on these two closely related questions, which are of especial importance because of the advisability of conserving manganese wherever possible. In general. our results show that in the open-hearth furnace equilibrium between metal and slag, with respect to both manganese and sulphur, is substantially attained during the finishing period of the heat, or in about a half hour to an hour after any additions were made. This implies that the end result will be identical whether manganese is added as alloy or metal to the liquid steel or as oxide to the slag. The proportion of total manganese retained by the steel is favored: (I) by use of the minimum amount of lime, consistent with other operating limitations, required to give a lime-silica ratio of about 2.4, which usually corresponds to a minimum practical slag volume; (2) by a high concentration in the slag of MnO relative to FeO; (3) by high operating temperature. Absorption of sulphur by the slag from the liquid metal is favored: (I) by large slag volume; (2-by a high concentration of active (or "free") lime and of manganese oxide dis) solved in the slag; (3) by low concentration of silica, iron oxide, and phosphate dissolved in the slag. DISTRIBUTION OF MANGANESE BETWEEN SLAG AND METAL AT EQUILIBRIUM On the basis that the distribution of manganese between liquid steel and slag is controlled by the reaction [FeO + Mn ;7± MnO + Fe [A] slag metal slag metal] the distribution at equilibrium, at a given temperature, is expressed by the equilibrium constant for this reaction, which is defined as [K" aFPI OFeO ? aMn] where a is the activity of the molecular species denoted by the subscript. The activity of each of the several components, although it is not known precisely, is approximately equal to the concentration of each component expressed as its mol fraction; that is, as the ratio of the number of mols of the given component to the total number of mols of all the molecular species present in the metal or slag, as the case may be. Moreover, since the activity, or concentration, of iron in the liquid metal is in fact substantially constant, the term aFe may he combined with K" to give a new constant K'. Making these changes.

Jan 1, 1942

By F. H. Wilson

Copper base alloys containing various amounts of aluminum and silicon are of considerable commercial interest. In particular the alloy containing 7 pct aluminum and 2 pet silicon shows an attractive combination of high strength with excellent, machinability. Since there is no evidence ill the literature that this ternary system has been studied since the recognition by Smith1 and Anderson2 in 1939 of the kappa phase of the binary copper-silicon system, the determination of the equilibrium phase relationships in the copper corner of the ternary diagram has been undertaken to provide a fundamental basis for understanding the behavior of these alloys. Phase boundaries have been determined by the micrographic examination of quenched samples while points on the liquidus surface have been obtained by thermal analysis. The results, of sufficient precision to serve their major purpose of providing a guide for the control of the manufacture of alloys in the region covered, are presented in a series of both isothermal and vertical sections of the diagram. Alloys StVdied For a rough survey of the copper corner of this ternary system the compositions listed in Table I (Series A) were employed. The results of examinations of these alloys indicated that the compositions listed in Table 2 (Series B) would further clarify regions of greater complexity. All alloys were prepared as 1200 g heats, the copper being melted under charcoal, and then first silicon and then aluminum were added. An excess of 0.05 pet silicon was allowed to cover deoxidation losses. Two small bars 5/8 by 1 1/4 by 5 1/4 in. were cast using Durville type casting equipment. Ailalyses were made on all alloys using material which was hot-rolled at 800 or 850°C and annealed 17 hr at 650°C. All analyses were found to be within 0.05 pet of the nominal composition. Since the precision of analysis is not much better than this, the points of both isothermal sections and vertical sections at fixed aluminum and silicon contents have been plotted at the compositions indicated by the nominal composition.

Jan 1, 1949

By W. A. Anderson

Recrystallization of cold-worked metals has long been known to proceed by a process of nucleation and growth.' When a cold-worked metal is heated to a temperature at which recrystallization will ensue, nuclei of new grains, essentially strain-free, appear and grow. As the process proceeds, nuclei continue to appear and to grow, until the cold-worked matrix has been entirely consumed and recrystallization has been completed (Fig. I). Conducted isothermally, a measurement of the fraction of the matrix recrystallized plotted against time, yields an isothermal recrystallization curve, showing the time course of the recrystallization process (Fig. 2).2 Evidently, then, the rate of recrystallization is determined by the rate at which nuclei form and the rate at which they grow. The rate of nucleation N is the number of nuclei that form in unit time in unit volume of the unrecrystallized matrix, and the rate of growth G is the increase in radius of the recrystallized grain per unit time. In recent years attempts have been made to determine N and G as these vary with the well-recognized variables affecting recrystallization: time, temperature, degree of deformation, etc.1 Such studies yield information that is more fundamental than that conveyed by the conventional recrystallization diagram,' since the rate of recrvstallization is thus analyzed into its two component rates3 Methods are now available by which N and G can be measured, and analytical expressions have been developed for the interrelationships among N, G, the isothermal recrystallization curve, and the final grain size, which greatly facilitate analysis.2-4 The application of these methods has been demonstrated recently for the recrystallization of silicon ferrite.2 Data on N and G in dependence upon the recognized recrystallization variables are, however, very fragmentary;" values of N and G have been determined for some metals, but the effect of temperature, which would yield the fundamentally important activation energies, has been too little studied. Thus far there has been no detailed study of the recrystallization of any one metal in terms of X and G ovcr appreciable ranges of the variables time, temperature, degree of deformation, and original grain size. It is the purpose of the present paper to provide such a study, employing aluminum.

Jan 1, 1945

By H. H. Uhlig

Soon after general use of stainless steels began, it was observed in practice that certain combinations of factors tended to induce corrosion by pitting. For most applications this was a serious drawback, not so much because the structural properties of the metal were impaired but because of the rapidity with which heavy sections of the alloys were penetrated by small elongated pits. These pits seemed to initiate readily in oxidizing metal salt solutions like ferric chloride and in chloride solu-tions like sea water. It was observed that in sea water pitting was more frequent in stagnant or polluted waters than in highly aerated, moving waters. The steels in these chloride solutions were observed to be sensi-tive to long contact with material such as sand grains or attached bar-nacles. At points of attachment or contact it was not uncommon to discover initiation of corrosion. Pits once begun at contact faces were observed to grow rapidly, usually elongating phenomenally in the direc-tion of gravity until the metal was perforated. Hydrochloric acid and other nonoxidizing acids, on the other hand, were observed to corrode stainless steels generally; the weight losses often were higher, but the penetration less than for the pitting type of corrosion. The causes of pitting, a type of corrosion recognized as character-istic not only of stainless steels but of many additional metals and alloys, are important in corrosion studies. A possible explanation bears prac-tical significance, for once it is known why pits begin where they do and continue to grow after initiation, intelligent direction can be given to diminishing corrosion. This can be done either by some alteration in the composition and treatment of the alloy or by some alteration in the environment. It appears foremost in importance to discover the nature of pit foci, for if initiation of pits can be discouraged their growth will be no longer a factor to be considered. In a multi-component alloy containing many impurities normal to production of such an alloy, each of which may play a part in pitting, and whose corrosion resistance is sensitive to heat-

Jan 1, 1940

By D.E. Norquist, J. E. Moeller

The results of wear on marked balls, 4, 31/2, 3, and 2 in. diam are given. All balls were forged steel of practically the same chemical analysis and hardness. The results indicate that balls in a given mill for a given length of time will have equal diameter losses, regardless of size. IN order to determine the relative wear rates of several sizes of grinding balls, groups of 4, 31/2, 3, and 2 in. balls were marked individually and were charged, all at the same time, into each of two production mills grinding copper ore. The remainder, and vast majority, of the ball charge consisted of 2 in. diam, and smaller, white, cast iron balls. The original weight of each test ball was determined and recorded. Some of each group of test balls were recovered from the mills periodically, individually reidentified, and reweighed. The test balls were recovered during regular maintenance shutdowns, at approximately thirty-day intervals, so as to avoid disrupting operations. As soon as the weights had been recorded, each marked ball was recharged into the mill from which it had been taken. The test units were mechanically the same and theoretically received equal tonnages of feed. All of the test balls were of forged, alloy steel composition with only slight variations in chemistry that would not be expected to affect the physical properties. All were heat treated in the same manner to produce a high hardness, as equal as possible for all sizes and as uniform as possible from surface to center. Generally speaking, the hardness of the portion worn from the balls during the test ranged from 62 to 65 Rockwell C. The microstructure was, therefore, predominately martensitic. The method of marking the test balls consisted of forming a small, round hole, 3/16 or 1/4 in. diam, into the center of each test ball with a Thomas Metal Master disintegrator, which produces a hole in fully hardened steel without affecting the hardness of the surrounding metal. After the hole was formed, each test ball was individually weighed to the nearest gram and the weight was recorded. The balls were grouped as to size and each group assigned a code letter. The individual balls within the various groups were then assigned a number. A small copper disc was stenciled on one side with the group letter and on the other side with the individual ball number and dropped into the hole in the corresponding test ball. The hole was then plugged with a low-melting-point metal alloy, which could be melted out in boiling water. Half of the test balls in each group were charged into one mill and the other half into another mill, so that all test balls in each mill would be subject to, as nearly as possible, identical conditions for an equal length of time. Previous testing had indicated that the wear rates on balls of different sizes could not be accurately compared if weight loss, or percentage weight loss, were used as a basis for comparison. Fig. 1 is a graphic record of the average weight loss for each size group in mill No. 1, and it becomes readily apparent that the larger balls lose substantially more weight in a given length of time. Fig. 2 is a graphic record of the average percentage weight loss for each size group in mill No. 1, illustrating that the smaller balls definitely lose a greater percentage of their original weight in a given length of time. It was, therefore, decided to convert the actual weights of the test balls to diameter and follow the diameter losses periodically to see if the wear rates

Jan 1, 1951

By W. J. Rogers, L. J. Dwiggins, R. O. Williams

THERE has been comparatively little work on the importance of strain rate and temperature as variables in the formation of deformation textures. For this reason the present work was started, the choice of compression being in part that of convenience and in part because of the absence of quantitative data in this area. These do not turn out to be important variables within the range studied which permits the results to be condensed into this note. Samples 1/4 in. in diam and 1/2 in. long were machined from 99.9 pct pure commercial aluminum and recrystallized to a fine grain size. A set of five samples were deformed between a spring-driven weight and an anvil resulting in roughly 20 pct strain each time. The strain rate varied because of decle-ration and shortening of the sample but would average about 10&apos; per min. Deformation at temperatures over the range of -76" to 150°C were obtained by heating or cooling the samples. Complete lubrication could be obtained by oil since the short time of contact did not permit its escape. The samples were compressed to a total true strain of 1.4 to 1.6. A larger sample was prepared similarly with spiral grooves in the ends to hold paraffin which provided essentially complete lubrication. This sam ple was compressed slowly at room temperature at a rate of about 2 per min to a total strain of 1.0. Cylindrical samples were carefully machined from these discs with a radial direction as an axis. They came from the center half of the samples and were roughly 1/16 in. in diam. The samples were etched down 15 pct to remove any surface effects. Diffraction data were then obtained for six different kinds of planes by the use of the Norton technique as applied to a fiber texture. Direct comparison between the raw data failed to reveal any significant difference between any of the samples and consequently the data from only one sample was completely reduced. The particular sample had been deformed at O°C The background was subtracted from the intensity data which were averaged over the four quadrants and then normalized to random. These data were then used to obtain fiber-axis distribution charts as previously described.2 For this sample the (422) plane was also run to assist in this inversion. The final result, Fig. 1, provided a comparable fit to that previously obtained from fiber data. About 85 pct of the material forms an elliptical texture around the <110> direction. The radius (at half height) is 5.5 deg along the (111) boundary and 8 deg along the (100) boundary. The remaining 15 pct forms a ridge running from this texture to near the <311> direction. The regions around the (100) and (111) planes are devoid of material. The earlier qualitative results of ~arrett~ are in complete agreement with the present results. The possibility has been dis-cused that the material around the <311> results from friction between the sample and compression plates.4 The present results are considered proof that such is not the case because of the uniformity of sample deformation and the requirement of axial symmetry before fiber-axis distribution charts can be accurately obtained. Recently results have been obtained to show that strain rate and temperature are important variables in the extrusion of aluminum.5 Perhaps the most important observation was that the partial recrystal-lization occurred even at room temperature. Strain rate was considered to be a factor only in that it produced a temperature change. There are many differences between the two experiments, the most important possibly being that their material was roughly ten times the purity of the present material. The present experiment, however, may not be as definitive as desired in this respect since it has been shown that compressed aluminum recrystallizes without a texture change6 although supplementary

Jan 1, 1961

By D. E. Norquist, J. E. Moeller

The results of wear on marked balls, 4, 31/2, 3, and 2 in. diam are given. All balls were forged steel of practically the same chemical analysis and hardness. The results indicate that balls in a given mill for a given length of time will have equal diameter losses, regardless of size. IN order to determine the relative wear rates of several sizes of grinding balls, groups of 4, 31/2, 3, and 2 in. balls were marked individually and were charged, all at the same time, into each of two production mills grinding copper ore. The remainder, and vast majority, of the ball charge consisted of 2 in. diam, and smaller, white, cast iron balls. The original weight of each test ball was determined and recorded. Some of each group of test balls were recovered from the mills periodically, individually reidentified, and reweighed. The test balls were recovered during regular maintenance shutdowns, at approximately thirty-day intervals, so as to avoid disrupting operations. As soon as the weights had been recorded, each marked ball was recharged into the mill from which it had been taken. The test units were mechanically the same and theoretically received equal tonnages of feed. All of the test balls were of forged, alloy steel composition with only slight variations in chemistry that would not be expected to affect the physical properties. All were heat treated in the same manner to produce a high hardness, as equal as possible for all sizes and as uniform as possible from surface to center. Generally speaking, the hardness of the portion worn from the balls during the test ranged from 62 to 65 Rockwell C. The microstructure was, therefore, predominately martensitic. The method of marking the test balls consisted of forming a small, round hole, 3/16 or 1/4 in. diam, into the center of each test ball with a Thomas Metal Master disintegrator, which produces a hole in fully hardened steel without affecting the hardness of the surrounding metal. After the hole was formed, each test ball was individually weighed to the nearest gram and the weight was recorded. The balls were grouped as to size and each group assigned a code letter. The individual balls within the various groups were then assigned a number. A small copper disc was stenciled on one side with the group letter and on the other side with the individual ball number and dropped into the hole in the corresponding test ball. The hole was then plugged with a low-melting-point metal alloy, which could be melted out in boiling water. Half of the test balls in each group were charged into one mill and the other half into another mill, so that all test balls in each mill would be subject to, as nearly as possible, identical conditions for an equal length of time. Previous testing had indicated that the wear rates on balls of different sizes could not be accurately compared if weight loss, or percentage weight loss, were used as a basis for comparison. Fig. 1 is a graphic record of the average weight loss for each size group in mill No. 1, and it becomes readily apparent that the larger balls lose substantially more weight in a given length of time. Fig. 2 is a graphic record of the average percentage weight loss for each size group in mill No. 1, illustrating that the smaller balls definitely lose a greater percentage of their original weight in a given length of time. It was, therefore, decided to convert the actual weights of the test balls to diameter and follow the diameter losses periodically to see if the wear rates

Jan 1, 1951

By M. T. Hepworth, T. P. Papazoglou

Hydrogen diffusion in hcp and bcc titanium in the temperature range 610° to 900°C was measured by reacting cylindrical specimens of high-purity titanium at constant temperature with small constant pressures of hydrogen of the order of a few Torr. In the range 0 to 6.7 at. pct H in hcp titanium, the diffusion coefficient D in sq cm per sec is given by: where T is in °K and R in cal per g-atom OK. Only three measurements of diffusivity in bcc titanium were made: at 900&apos; : the diffusivity in ß titanium was found to be 1.8 x 10-4 sq crn per sec. McQUILLAN1 has studied the constitution of the Ti-H system and reported the concentration of hydrogen as a function of pressure of hydrogen and temperature. He found hydrogen absorption was reversible and rapid at temperatures above 500°C in both crystallographic modifications, the a (hcp) phase and the ß (bcc) phase, with the latter phase stabilized by hydrogen additions. Wasilewski and Kehl 2 measured the diffusivity of hydrogen in hcp and bcc Ti-H alloys. For bcc alloys, they reacted cylindrical specimens of titanium with hydrogen gas at 1 atm pressure. They measured the rate of absorption of hydrogen isothermally on specimens ranging from zero hydrogen content when above the transformation temperature to hydrogen contents sufficient to stabilize the bcc phase when below the transformation temperature. By integrating Fick&apos;s second law for a cylindrical geometry, assuming a diffusion coefficient independent of composition, they calculated diffusivities as a function of temperature. In the range 650" to 1000°C their results in bcc titanium yielded the expression: where D is in sq cm per sec, T in OK, and R the gas constant in cal per g-atom-OK. Their studies on the hcp a phase were conducted by exposing long cylindrical titanium specimens to hydrogen at a sufficiently high pressure to establish a surface layer of fl phase 80 to 120 u thick for the duration of an isothermal experiment. Concentration profiles were then determined by hydrogen analysis from chips obtained upon machining quenched specimens. The diffusivity of hydrogen was then calculated yielding the expression: The present investigation was undertaken principally to redetermine the diffusivity data on a titanium by a direct absorption from the gas phase at sufficiently low hydrogen pressures to avoid the presence of a surface bcc phase and also to check the diffusivity data at low hydrogen concentrations in the bcc stmcture. EXPERIMENTAL PROCEDURE High-purity electrolytic sponge titanium (99.9 pct) of BHN 91 was arc-melted, forged, rolled, and machined into cylinders of final hardness, upon annealing, of BHN 92. Cylindrical specimens of two sets of dimensions were used: 1.524 by 2.931 cm and 1.905 by 3.663 cm diam and length, respectively. The experimental apparatus used for annealing specimens and for admitting known amounts of hydrogen at constant pressure is shown in Fig. 1. In a typical experiment, a specimen was lightly abraded with fine-grain silicon carbide, washed with water and detergent, and then thoroughly degreased with reagent-grade tri-chlorethylene and acetone. The specimen was suspended by a Chrome1 wire in the center of a quartz furnace tube, without contact with the tube, and heated to 925°C (as measured by a thermocouple adjacent to the specimen, outside the tube) for a period of at least 4 hr under a vacuum of from 10-6 to -7 Torr as measured by an ionization gage. The furnace temperature was then adjusted to the temperature chosen for the particular diffusion study and the specimen allowed to equilibrate thermally. Hydrogen was then ad-

Jan 1, 1969

By P. M. Aziz, I. Markson, C. S. Barrett

The abnormal after-effect in twisted wires that occurs when untwisting is interrupted by etching con be brought under control and used to study the mechanical properties of thin surface films and how they are effected by reagents and heat treatment. Results are given of studies of oxide films on high purity aluminum. IF a wire is subjected to plastic deformation by torsion and then released, it untwists in the normal after-effect, but under certain circumstances the untwisting is abruptly lessened or reversed by the application of an etchant to the wire.1,2 This abnormal after-effect may occur, for example, if there is a coherent oxide film on the surface of the wire which is removed by the etchant. Following a suggestion of A. H. Cottrell that predicted this effect, it is attributed to dislocations that had piled up beneath the oxide layer and represents the rapid release of residual stresses caused by these dislocations. When the layer is removed, the stress relief may be by escape of piled-up dislocations from the metal, or by an activation of latent sources of dislocations located at the surface, together with rebalancing of elastic stresses to compensate for the loss of stressed material, as in a residual stress analysis determination, these mechanisms acting singly or in combination.&apos; The slower the attack of the reagent, the more gradual is the stress relief and the smaller the change in strain rate when the reagent is applied. A study has been made of the factors that influence the magnitude of the normal and abnormal after-effects with the object of developing techniques suitable for a quantitative investigation of the influence of various surface films on dislocations in wires, and of the rate and extent of the attack on the films by different reagents. It was found that reasonable sensitivity and reproducibility could be achieved if a suitable choice of variables was made and if these variables were held constant through a series of experiments. The method was then applied to a study of oxide films produced and treated in different ways on the surface of high purity aluminum wires, and to a study of the damage to these films caused by various reagents. Experimental Procedure The material used throughout this work was prepared from 99.9968 pct Al. This high purity aluminum was melted, cast into 1/2 in. diameter ingots, and then swaged and drawn without intermediate annealing to 0.040 in. diameter wire. A sketch of the apparatus employed for twisting is shown in Fig. 1. The test wires were mounted into the apparatus by cementing one end of the wire to the beaker and the other to the tube with laboratory wax of high melting point. The length of the wire between the waxed joints was 4.2 & 0.2 cm. Extreme care was taken during mounting to avoid cold-working the wire. The wire was twisted through 335" in 2 to 4 sec by rotating the pinion on the gear box until the vertical post on the rotating table, which was initially touching the horizontal stop, was arrested by the stop. All the tests were conducted with apparatus and reagents at the same temperature (about 25°C). In all tests, except those where the duration of the initial torque was investigated, the torque was applied for a period of 2 min. At the end of this time the table was rotated back a few degrees away from contact with the stop and the wire allowed to untwist. The after-effects were measured by reflecting a beam of light from the mirror shown on the apparatus. After the wire had untwisted for 6 min, a reagent was carefully poured into the beaker and thereby applied to the surface of the wire.. In some tests the liquid in the beaker was removed after a few minutes and replaced by an-

Jan 1, 1954

By E. H. Jr. Dix

OF all the alloying elements used in commercial aluminum alloys, copper stands out as by far the most important, and it is perhaps for this reason that the constitution of the aluminum-copper system has received the attention of a number of experimenters covering a period of approximately 20 years. It would be expected that during this time the equilibrium relations had been thoroughly and exactly worked out. In a general way this is true, but there is a surprising lack of agreement in the details of the high aluminum end of the diagram, particularly in regard to the solid solubility of copper in aluminum, which has been given variously as 2 per cent. to 5 per cent. at the eutectic temperature. The importance of this is much greater than might at first appear to one unfamiliar with modern commercial aluminum alloys. This is true because, with one exception, the susceptibility of the strong alloys to heat treatment depends, in part at least, upon the solid solubility relations of copper in aluminum. In 1919, Merica, Waltenberg, and Freeman1 published the first detailed information on these solubility relations. They found that the solubility of copper decreases with falling temperature from about 4 per cent. at 5.25° C. to about 1 per cent. at 300° C. and is apparently still diminishing at lower temperatures. In 1921 there was published a brief account of the results obtained in the National Physical Laboratory, Teddington, England.2 This laboratory, however, reported that 5 per cent. of copper is soluble in aluminum at 540° C., and that this amount decreases to about 3 per cent. at 20° C.

Jan 2, 1926

By R. Floyd Farris

A method is presented for determining minimum waiting-on-cement time, which takes into account the differences that exist between types and brands of cements and such individual well conditions as depth, temperature, and pressure. The basis for the method was determined by laboratory tests. Being a laboratory development, several steps were required to prove its merit. The first step consisted of laboratory tests designed to determine the minimum cement strength required in wells. Basis was found for setting a minimum value of 8 Ib. per sq. in. tensile strength. Next, it was shown by laboratory tests that the time to 8 Ib. per sq. in. tensile strength may be expressed as a function of consistometer stirring time to loo "poises," the approximate relation being "the time to 8 Ib. per sq. in. tensile strength equals the time to I00 &apos;poises&apos; times three." Next, it was shown that the time of maximum temperature development in cement slurries, due to heat of hydration, is also related to consistometer stirring time to loo poises, but only by a factor of approximately two. It was shown also that the shut-in casing pressure will build up after cement is placed and register a maximum pressure at approximately the same time the slurry down the hole attains maximum temperature. From this and the relationships listed above, the general rule was established that minimum waiting-on-cement time (time to 8 Ib. per sq. in.) after casing cement jobs in any well is equal to the time when the shut-in casing pressure reaches a maximum, as measured from the initial mixing of cement, times a factor of 1.5. Cement plugs drilled in the field at the time prescribed by this formula were found to drill "firm to hard," thus confirming the laboratory tests. These tests prove that many of the present regulations for waiting on cement require a longer time than is absolutely necessary. Use of the method herein proposed offers the possibility of a saving of $1200 per well. Introduction The length of time allowed for cement to set after casing is determined either by state-wide rules, field rules, or self-imposed rules written into drilling contracts. In general, the time is dictated by experience and common practice. However, owing to differences in opinion and in experience of the various groups involved, waiting-on-cement time often varies from one area to the next. For example, an operator in an area where no rules exist may drill out of surface pipe at 24 to 36 hr., while another operator in another area may wait 48 hr. or more to comply with state or field rules, although the depth of the well, hole size, type of cement, and other data are identical. An even greater difference in practices will be found by making similar comparisons with respect to oil-string cement jobs. Differences in waiting-on-cement times of 36 to 48 hr. are common. Further complicating the picture is the rather common practice of allowing more waiting time for cement to set at the greater depths than is allowed at the shallow depths. This practice has existed for years in spite of the common knowl-edge1,2,3 that the temperature of the earth at the usual setting depths of surface

Jan 1, 1946

By S. Shapiro, G. Krauss

RECENT investigations1 3 of the products of marten-sitic transformation in Fe-Ni and Fe-Ni-C alloys have made use of light microscopy to describe mar-tensitic fine structure. The application of conventional metallographic techniques to this problem was possible because of the similarity of distributions of parallel striations developed by etching polished surfaces to distributions of transformation twins which are positively identified in thin films by transmission electron microscopy. The surface striations frequently are not well-defined, and could also be due to, for example, rows of etch pits which are not resolved by the light microscope. This note describes the etching effects revealed by examination of surface replicas of mar-tensite in the electron microscope. The application of a replica technique both extends the observations of fine structure made with the light microscope and allows the results of conventional metallography to be used with more confidence. Samples of an Fe-33 wt pct Ni alloy were used for this study because of the detailed knowledge of the fine structure of martensite which has been developed&apos;-4 for alloys of about this composition. Samples transformed to martensite at -120°C, and transformed samples heated to 340°C to effect a small amount of reversal of martensite to austenite, were examined. Surfaces were first prepared for replication by elec-tropolishing in a chromium oxide-acetic acid electrolyte at a current density of 0.1 amp per sq cm and a temperature of 15°C or a perchloric acid-acetic acid electrolyte at a current density of approximately 2 amps per sq cm and a temperature of 15°C. The polished surfaces were then etched for 4 to 7 sec by immersion in a solution of equal parts HC1, HNO,, and H20. Application of the etchant for this period of time produced discrete attack of certain features without loss of resolution due to overlapping of areas most susceptible to etching. The etched surfaces were replicated by 1) preshadowing with Pt-Pd alloy at an angle of 20 to 30 deg, 2) depositing a thin carbon film, and 3) stripping the film and shadowing material by immersion in a 5 pct nital solution. Two types of etching effects were observed by examination of the surface replicas in the electron microscope: l) continuous striations centered at the bottom of long grooves or the tops of pyramidal elevations on the sample surface, and 2) high densities of fine etch pits. Examples of both types of features are shown in Figs. 1 to 4. The striations are in each case continuous and have the same characteristic configurations as do transformation twins in martensite. Fig. 1 shows that the density of grooves decreases toward the edge of a martensite plate and Fig. 2 shows a region where the striations are of varying length. Similar examples of transformation twin arrangements determined by transmission electron microscopy of thinned foils of martensite have been shown in the literature,&apos;~ and, based on these similarities, the striations and their associated grooves or mounds are considered to be evidence for the presence of transformation twins. The transf~rmation twins in martensite are on the order of l00 A thick, much too fine for resolution by the light microscope. It appears that orientation-dependent etching of the matrix martensite about the twins results in grooves or surface elevations which

Jan 1, 1967

By D. J. Pye

Certain high molecular weight synthetic polymers in very dilute solutions decrease water mobility in porous media 5 to 20 times more than would be expected from the solution viscosity. This indicates that increasing water viscosity to reduce adverse mobility ratios in water floods is economically feasible in many situations. Laboratory results are consistent with accepted theory with respect to improved areal sweep, permeability distribution and displacement efficiencies as would be predicted from the solution mobility measured in the core. The laboratory results have been confirmed by field pilot floods which recovered 80 per cent and 100 per cent more oil than comparative water-flood pilots in fields containing 16 cp and 130 cp oil respectively. Economic analyses based on pilot data indicate the method to be profitable. INTRODUCTION The desirability of improving the water-oil mobility ratio in waterflood-ing operations has long been appreciated, especially for high viscosity crudes. Methods of reducing the oil viscosity by application of heat, gas resaturation and miscible drives have met with some success. Conversely, it has been generally conceded that increasing the water viscosity would also be effective, but the amount of thickening agent required to effect an appreciable increase in viscosity is discouragingly high. The use of such materials as glycerin, sugar, or glycols is completely out of the question economically, so that considerable attention has been given to the use of the much more efficient synthetic water-soluble polymers as viscosity improvers; but even these materials are not economically attractive. If increased water viscosity could be economically realized, marked improvements in areal sweep efficiency, as discussed by Caudle and Wittel and others, would be realized in field operations. Similarly, the improved mobility ratio would bring about increased recoveries by correcting permeability distribution problems as discussed by Stiles2 and Dykstra and Parsons,&apos; and improvements in displacement efficiency would be obtained as recognized by Buckley and Leverett4 and Welge.5 LABORATORY STUDIES THE RESISTANCE EFFECT In the course of research to develop a more efficient water-soluble polymer viscosity builder, we discovered that a very few types of water-soluble polymers exhibited a most unusual and very interesting property not previously observed. Among the earliest materials showing such activity were polymers containing acry-lamide. Fig. 1 shows a typical plot of the solution viscosity vs concentration for one of these polymer solutions as determined in an Ostwald viscometer. As usual, such a plot is an approximate straight line on semi-logarithmic paper. Now, an inspection of Darcy&apos;s law, shows that a viscosity value can also be determined in a formation sample if the pressure, flow rate and permeability are known. If the core permeability is previously determined with wa- ter or brine, then the viscosity of another aqueous fluid may be determined from the equation. The viscosities so determined for glycerin (glycol or polyvinyl alcohol solutions, for example) agree with the viscometer determinations. However, in the case of the water-soluble polymer solutions in which we are interested, the viscosities measured in the formation sample depart very markedly from the viscometer values. A typical relationship for a polymer solution is also shown in Fig. 1. This unusual departure from the expected response is referred to as a resistance property of the polymer and is quantified as "resistance factor". Since the resistance factor R can best be determined in a core under study, the term has been defined on the basis of the ratio of the brine mobility to the polymer solution mobility at residual oil saturation so that:

Jan 1, 1965

By P. Dayal, L. S. Darken

THE migration of carbon in austenite under the influence of an electric current has been observed qualitatively several times.14 Lebedev and Guterman5 recently have reported quantitative measurements; their method consisted of welding a low-carbon to a high-carbon wire, passing current, and later estimating the carbon distribution metal-lographically. We believe the method reported in this paper is superior in principle since electrolytic migration and ordinary diffusion are not necessarily coupled as in the weld method; also for the first time the extent of migration is determined by combustion analysis for carbon. A uniform tubular specimen (S.A.E. 1045 or 1095) was mounted as illustrated in the figures. the whole assembly being in an atmosphere of purified nitrogen. Direct current (129 to 226 amp at 0.65 to 1.0 v) served as source both of heat and of potential gradient for carbon migration. The duration of experiment was 7.5 to 12 hr, during which time the temperature was controlled (±10°C) manually. The experimental conditions are indicated in the first five columns of table I. With this experimental arrangement, the temperature initially has a maximum value at the central plane. Also, in this vicinity (by virtue of the symmetry), the carbon entering any volume element is equal in quantity to that leaving; the loss or accumulation of carbon occurs near the electrodes since the carbon moves uniformly near the center and is "frozen" at the cold ends. Hence, providing the time of experiment is not sufficiently long to seriously influence the conditions at the central plane, carbon crosses this plane only under the influence of the electrical potential gradient and not under the influence of temperature or concentration gradient. The amount of carbon which has crossed this plane was determined by combustion analysis of the two halves of the specimen. The results of these analyses are shown in the sixth and seventh columns of table I. It will be noted that substantial amounts of carbon migrated from the anode portion to the cathode portion (except at 920°C, which temperature was too low to exhibit the effect in the allotted time). In spite of precau-tions taken, considerable decarburization occurred as may be seen by comparing cols. 8 and 5. In three cases (indicated by asterisks in table I) the specimen was ground on one side, polished, and examined metallographically before analysis. One specimen was normalized and re-examined. Micrographs of selected areas in specimens 4 and 6 are shown in figs. 1 and 2, respectively. Evidence of carbon migration from the anode toward the cathode is quite apparent. Fig. 2 shows abundant graphite as well as cementite in a region near the cathode. The temperature of this zone is estimated at about 800°C. In fig. 1, particularly in the micrograph on the extreme right (the right side of which is of unaltered carbon content), there is evidence of slight depletion of carbon in the immediate vicinity of the cathode as contrasted to the general increase in carbon of the cathode half of the specimen. Although this may be attributed in part to decarbur-ization, it is believed that it is occasioned also by thermal diffusion—migration (of carbon) from a cool to a hot zone4—a phenomenon superimposed upon the electrical migration. Evidence of carbon migration was visible particu-larly during the course of the high-temperature,

Jan 1, 1951