By Lawrence H. Van Vlack, Otto K. Riegger, Gerald I. Madden

The microstructural variations of periclase (MgO) in the presence of oxide liquids are examined under the steelmaking variables of: 1) temperature, 2) liquid composition, and 3) FeO additions under different oxidation levels. Attention is given to the distribution of the phases, both liquid and solid, and to the growth of individual crystalline grains. Silicate liquids penetrate more extensively between individual periclase grains than do liquids containing high percentages of Fe2O3 Higher MgO solubilities in the liquid and lower MgO contents of the solid favor more rapid grain growth. The presence of a second solid phase reduces the periclase grain growth rate and increases the amount of the solid-to-solid contact within the oxide microstructures at high temperatures. The service suitability of a refractory depends on many factors. Two are of major importance and include 1) the thermal resistance to melting, and 2) the mechanical resistance to loads at service temperatures. Neither is a simple consequence of the service temperatures because service conditions will alter compositions, produce partial melting, and induee phase changes. Consequently, the equilibrium phase relationships have been rather thoroughly studied and give a knowledge of the thermal resistance to melting, but do not give full information about the mechanical properties because two refractories with the same types and quantities of phase may have different microstructures. Although variations of microstructures with time, temperature, and composition have been subjects for extensive investigation in metals, only a limited amount of comparable microstructural work has been performed for refractory materials.' This study was an attempt to evaluate some of the consequences of service parameters upon the microstructures of refractories so that bases may be established for the analyzing of high temperature mechanical properties. Periclase (MgO) was chosen as the refractory oxide; variables included those which are encountered under steelmaking conditions such as 1) temperature, 2) liquid composition, and 3) FeO additions under various oxidation levels. Specific attention was given to the distribution of the phases, both liquid and solid, and to the growth of individual crystalline grains. The most closely related work on microstructures of polyphase materials is that of Van Vlack and Rieg-ger2 on the microstructure of magnesiowüstite [(Mg,Fe)O] in the presence of silica. In that work which pertained to solid solutions with less than 40 pct MgO, most of the quantitative work was performed on FeO microstructures. The chief conclusions concerning these relatively low-melting oxide solids were as follows: 1) the rate of crystalline grain growth is inversely proportional to the grain diameter, 2) grain growth proceeds more rapidly at higher temperatures but is slightly retarded by additional liquid content, and 3) a Silicate-containing liquid penetrates as a film between the individual magnesiowüstite grains independent of time, temperature, amount of liquid, or the MgO/ FeO ratio. The above observations are in contrast to prior work3 on the microstructure of silica in the presence of iron oxide-containing liquids where the liquid does not penetrate as a complete film between solid grains. The phase relationships for the compositions of the present work are shown in Fig. 1 which is a summary of the work of several investigators.4 Of importance is the fact that CaO forms a more stable structure with SiO2 and Al2O3 than do either MgO or FeO. The oxygen potential has little effect on periclase unless iron oxide is also present. The iron oxide is ferrous at moderately low oxygen levels, changing to ferric as the Oxygen potential is increased so the spinels, magnetite, and magesioferrite are formed.5 These two phases are relatively stable in air at steelmaking temperatures. I) EXPERIMENTAL PROCEDURE ractory were made with reagent grade Oxides. The magnesium oxide used was 99 pct MgO after ignition, and the iron oxide raw material had a minimum content of 99 pet Fe2O3. The CaO, SiO2, and A12O3 were also reagent grade raw materials. After mixing, the required compositions were pressed into pellets at a minimum pressure of 5000 psi to insure compaction of the raw materials and prevent excess void content. A silicon carbide element tube furnace was used with thermocouple control for sin-

Jan 1, 1963

By W. D. Ludemann, J. E. Dor, L. A. Shepard

Recovery of the creep resistance of 99.99 pct pure Al was studied at temperatures 540°, 573°, 600°, and 611°K. Poly-crystalline specimens crept under a stress of 950 psi to a strain of 5.5 pct were allowed to recover for periods of from 1 min to 16 days under a residual stress of 4.4 psi. Increased creep rates upon reapplication of the 950 psi stress evidenced softening of the material. The activation energy for the recovery process was found to be 64,000 cal-per mol. THREE major observations have clearly revealed that the creep of polycrystalline aluminum above about 510°K is controlled by the rate of climb of jogged edge components of dislocations past the barriers impeding their motion: 1) Extensive polygonization, characteristic of climb, takes place during creep.'9' 2) The activation energy for creep equals the estimated activation for self-diffusion. 3) The stress law for creep coincides with theoretical predictions based on the climb mechanism.4,5 The decreasing rate during the primary stage of creep must be ascribed to the introduction of additional barriers to the glide of dislocations. During secondary creep the density of barriers must remain constant, the rate at which new barriers are formed being equal to the rate at which they recover. For this reason the nature of the barriers, and their rates of formation and recovery, are significant to a complete understanding of creep. It is proposed here to study the kinetics of the recovery of barriers to creep of high-purity polycrystalline aluminum in the climb range. The technique will consist of creeping a series of tensile specimens under a prescribed stress to given state following which the specimens will be recovered for various times and temperatures under approximately zero stress. The amount of recovery will be determined by comparing creep curves following the recovery. EXPERIMENTAL PROCEDURE The material used for this investigation was a 99.99 pct pure Al supplied by the Aluminum Co. of America in sheets of 0.001-in. thickness having an H-18 temper. The spectroscopic analysis of impurities gave Cu-0.004 wt pct, Fe-0.002 pct, Si-0.001 pct, others-0.000 pct. Creep specimens were machined with their tensile axes in the rolling direction of the sheets. Annealing in a molten potassium nitrate-potassium nitrite bath for 1 hr at 686K, followed by air-cooling, resulted in a grain diameter of from 0.22 to 0.27 mm. Creep machines were equipped with constant stress lever arms of the type suggested by Fullman, Carreker, and Fishher,' which maintained the applied stress to within 0.04 pct of the reported value of 950 psi. Creep strains were calculated from extensions over a 6-in. gage section to the nearest 3 X 10"5. The temperatures of testing, 540°, 573", 600°, and 611°K, were obtained by immersing the specimen and extensometer assembly in a molten KNO2-KNO3 bath. Temperatures during the periods of creeping could be maintained constant to within better than ± 1°K. Correlation of creep data at different temperatures of testing demanded the use of an appropriate temperature-compensated time 8. Previous investigations have shown that the creep of pure metals at temperatures above about 0.55 of their melting temperatures can be correlated by the functional relationship3" e=f(0), s= const. [1] where e = total plastic strain during creep f = a function that depends on stress a = stress 6 = te-Q/RT = a temperature-compensated time t = time under test Q = 35,500 cal per mol = activation energy for creep R = gas constant, and T = absolute temperature In the present series of tests all of the creep was conducted under the same stress of 950 psi. To provide identical initial conditions for the recovery all specimens were first crept to a temperature-compensated time of = 47 X 10-14 min which resulted in a creep strain of 0.055 + 0.005 regardless of the creep temperature. During recovery, a small stress (4.4 psi) was permitted to remain upon the specimens to maintain tautness in the pulling assembly and to prevent mechanical damage to the soft specimen. After each recovery period, the full stress was reapplied and

Jan 1, 1961

By J. D. Bateman

At Giant Yellowknife, where high grade gold-bearing orebodies are highly irregular in shape, geology has been applied extensively to the mining of ore. The classical functions of the mine geologist in the fields of exploration and mine development have been extended to guide ore extraction, ensuring "clean" mining and effectively reducing waste dilution. THE property of Giant Yellowknife Gold M.ines Ltd. is situated west of Yellowknife Bay on the north shore of Great Slave Lake, a distance of 600 air miles north of Edmonton, Alberta. The Giant claims were staked in 1935, the company was formed in 1937, and the main orebody system was disclosed by diamond drilling in 1944 following a geological study of the property by A. S. Dadson,* Consulting Geologist for the company. Production began in 1948 at the rate of 200 tons per day and, during 1950, reached a daily rate of 425 tons. During the first 3 years of operation a total of 366,000 tons was milled with an average grade of 0.79 oz of gold per ton. Work is in progress with an expansion to 700 tons per day in view. A descriptive account of the geology and gold-bearing shear zone has appeared previously.* The rock formations in the vicinity of Yellowknife Bay have been subjected to protracted pre-Cambrian tectonic deformation culminating in a series of late faults having a cumulative horizontal displacement exceeding 11 miles. The Giant property is underlain by part of an Archean sequence, several miles thick, consisting of basic volcanic flows and minor intercalated tuffs. The volcanic succession forms the west limb of a major syncline, the flows facing east, but overturned on Giant property to dip west at 65" to 75". Orebodies are confined to shear zones up to 200 ft in width, which were formed along early thrust faults. The shear zones assume fold-like attitudes, the larger of which have an amplitude of several hundred feet. The rock formations beyond the limits of the zone of shearing do not reflect the simulated folds, the axes of which are within a few degrees of the strike of the flows. The schistosity and most of the planar elements in both the shear zones and the orebodies dip west • A. S. Dadson and J. D. Bateman: Structural Geology of Camdian Ore Deposits, Can. Inst. Min. Met. Jubilee Volume (1948), PP 273-283. at angles between 65" and 75", generally corresponding to the dip of the flows. The planar elements within the shear zone system thus dip more or less constantly west whether the shear zone is flat, vertical, or expressed as east or west dipping limbs. The shear zones reflect the deformation and alteration of the basic volcanic flows into chlorite schists which, in most places, have undergone metasomatic replacement to form chlorite-sericite-carbonate schists or sericite schists. The boundaries between the shear zones and country rock, although often gradational, usually can be defined within a few feet or even inches as they are expressed by the limits of metasomatic alteration. Orebodies may occupy a small or large proportion of the shear zone and, although they generally conform to the shape of the zone, their morphology is much more complex. Ore boundaries in some instances are sharp and can be delineated with a chalk line; but more generally, a large proportion of the ore boundaries is not visually obvious and can be determined only by the perception acquired by the geological mapping of ore or study of drill cores. Ore shoots in fold-like attitudes may transect the planar elements of the shear zone at any angle; yet the schistosity within the ore shoot may be coincident with that in the enclosing shear zone. Thus it is clear that problems may arise in the delineation of mining boundaries. Ore generally consists of 20 pct or more quartz with ferruginous carbonates in sericite schist deposited in two dominant stages. The earlier stage limits of quartz with carbonate, pyrite, and very fine-grained arsenopyrite in lenses and bands. The later stage consists of quartz-carbonate lodes, in

Jan 1, 1952

By F. O. Jones

The capabilities of small proportions of divalent cations, such as calcium or magnesium, for controlling clay blocking are reported. Potentially sensitive formations can be exposed to fresh water if at least one-tenth of the salts dissolved in both the native water and invading fresh water are calcium and magnesium salts. Often, even less suffices. The behavior evidently depends upon the cation exchange properties of the clays, which favor adsorption of calcium and magnesium over sodium. Clays having sufficient adsorbed calcium and magnesium resist dispersion by water and consequent blocking of permeability. An allied phenomenon, the dependency of clay blocking on salinity contrast, is also reported. Abrupt change from highly saline to fresh water can cause blocking which may not occur if salinity is lowered slowly. A process related to osmosis is thought responsible for this behavior. Applications of findings to drilling, fracturing and water flooding are discussed. INTRODUCTION Many formations, when exposed to fresh water, can lose permeability through clay effects.',' For example, drilling-mud filtrate can cause oil permeability decreases, which persist long enough to interfere with drill-stem testing and well completion.3 Ultimate productivity may suffer when clay damage is severe, especially if drawdown pressures are low.' The injection pressures and the time required for water flooding can increase if clay blocking occurs. Earlier work indicates that clay blocking is caused by obstruction of flow channels by clays or other mineral fines dispersed by fresh water.'!" It is well known that increasing salt concentrations in water tends to prevent clay blocking. Also it is well established, although perhaps not as widely known, that the nature of the dissolved solids is also important. If, for instance, formation clays are exposed to calcium chloride solution and then exposed to weaker solutions of calcium chloride or distilled water, considerably less permeability damage results than if the clays had been exposed instead to sodium chloride solutions. The reasons for this behavior are: (1) clays are cation-exchange, or base-exchange, materials similar in this respect to zeolites or exchange resins, and (2) clays in the calcium form do not disperse easily in fresh water, whereas clays in the sodium form do. The base-exchange form of a clay is easily altered by flowing a solution through it. For example, a sodium clay can be changed to a calcium clay simply by passing a calcium chloride solution through the clay bed. There is general agreement that the reason calcium and magnesium clays do not disperse easily in fresh water is because the calcium ions do not ionize easily from the clay surfaces.' Sodium clays, however, are believed to allow the sodium ions to ionize from the clay particle surfaces. In fresh water, this allows the particle to accumulate a net negative electrical charge great enough for the particles to repel one another and, therefore, disperse more easily. The foregoing suggests that, even in the presence of a large excess of sodium, a relatively small ratio of divalent cation, such as calcium or magnesium, might serve to prevent clay dispersion. The divalent ion probably adsorbs to a disproportionately large extent, because of being adsorbed more tightly, with the result that the proportion of divalent cation on the exchange positions of the clay might then be great enough for the clays to resist dispersion. Consequently, an investigation was conducted to find how mixtures of salts in solution influence clay blocking. APPARATUS AND PROCEDURE Water permeability tests were conducted using conventional techniques. The equipment is illustrated schematically in Fig. 1. Flow rates of solutions driven through small core samples at known temperatures and pressures were measured. Regulated compressed air, usually at 10 to 15 psig, was used to drive the solutions. Core samples 0.75 in. in diameter and 1 in. long were used for the most part. Cores were saturated by evacuating and then admitting a de-aerated solution. Tight core samples were first saturated with carbon dioxide gas and then evacuated and saturated with the test solution. After saturation, 140 psig pressure was imposed for several hours. Cores were tested to insure absence of gas saturation by a Boyle's

Jan 1, 1965

By E. D. Gardner

FIFTY years ago the Utah Copper enterprise at Bingham was just getting under way. An epic in metal mining was in the making. Throughout the West the bonanza deposits were approaching exhaustion and most ore still went direct to smelter. But concentrators were shortly to be constructed for treating milling grade ores, and most important, the pilot plant for the Utah Copper enterprise was being built that year at the mouth of Bingham Canyon. The same decade was to see development at the Inspiration mine in Arizona of the most important new mining method for 50 years to come—undercut block caving. Although the average grade of ore being mined has been declining for 50 years, and wage rates and prices of supplies have been greatly increased, the mining industry has continued to grow and to prosper. Technology has advanced to a point where minerals can be mined under the most severe conditions. The hardest rock can be drilled and broken and the heaviest ground handled. Large or small, an ore-body can be mined successfully, at any desired rate of production. It is possible to pump great volumes of water and to ventilate the most extensive workings; air conditioning has made practicable the mining of ore where the rock temperatures are beyond those that can be borne by man. Mining today in the U. S. is a huge earth-moving operation. In 1953 nearly 2 billion tons of material were mined for direct use or for processing. Stripping at open-cut mines totaled about 1.7 billion cu yd. Table I gives relative tonnages of the branches of the mineral industry in 1953. In addition to the solid materials moved, 350 million tons of petroleum and 340,000 tons of gas were produced in 1953. Fifteen million tons of salt and 5 million tons of liquid sulphur were pumped from wells. An appreciable amount of copper was recovered by leaching old mine workings and dumps. Total value of minerals produced in 1953 was $14.4 billion: oil and gas $7.6 billion, coal $2.6 billion, nonmetallics $2.4 billion, and metals $1.8 billion. Formidable problems face some branches of the industry today, especially pertaining to increased output tons per manshift. The time has come when these problems should be reappraised. With current wage rates, the industry no longer can afford to pay men to do manual labor. It should be recognized, also, that the miner is a skilled worker; efforts to promote the dignity of his calling and his pride of accomplishment have yielded beneficial results. Mineral deposits occur under widely varying conditions. In most instances the degree of support needed by the roof and walls is the deciding factor in selection of an underground mining method. The degree of support needed, in turn, is governed by natural physical characteristics of the ore and its enclosing rocks. Mine operators, of course, learn to judge ground by observation, and an experienced mine boss generally can anticipate what will happen following any given mining operation. A more scientific approach, however, would be advantageous in most cases. More should be known about the strength of the ore and the enclosing rocks, more about stresses set up in the ground when ore is removed, and more about the mechanics of moving ground. Better understanding would work both ways: first, favorable rock conditions could be fully utilized for more efficient mining, and second, hazards of rock falls could be minimized, loss of ore in mining reduced, and expenses caused by ground pressures and subsidence lowered. In general, mining comprises breaking the ore or rock in place, supporting the mine workings, and transporting the ore to the surface. This latter is a materials handling problem. Ventilation, of course, must be provided, and the mines must be kept free of water. Development work at some places is the most important cost item in extracting ore. Drilling and blasting remain the usual practice for breaking ore or rock from place except, of course, at block-caving mines. The drilling and blasting practice at a mine must fit the mining method. In laying out mining procedures attention is being given to

Jan 1, 1956

By Byoung Whie Lee

In order to investigate the change in surface energy as a function of cold work ad environment, the contact angles between a liquid and the surface of elec-tropolislzed aluminum with various degrees of cold work were measured. Specinlens cut from aluminum rod (99.99 pct Al) were annealed at 600°C for 24 hr and then cold compressed parallel to the drawing di-rectzon of the rod in increments of approximately 10 pcl from 0 to 70 pct. The sections, taken transversely to the drawing direction, were mechanically and electro chemically polished. Contact angles between the sessile drop of distilled water, glycerin, and glycol and the specimen surface were measured optically. The differences in interfacial energy were calculated from the contact angle data. The effects of chemical washing and surface roughness of the specimen on the contact angle were also studied. The liquid contact angle was a linear function of the degree of cold working (D) ad changed markedly with differed liquids. THE plastic deformation of polycrystalline metals induces a preferred orientation in crystal structure. A preferred orientation changes the atomic density of a metal surface. This change in surface atomic density brings about the changes in surface interactions of the metals."' Also, the plastic deformation of metals raises the internal energy by increasing the stored energy.' Consequently, the total Helmholtz free energy of the metal increases and, in turn, the surface free energy of the metal. In order to study the effect of plastic deformation on solid surface phenomena, the liquid contact angle of a sessile drop made on cold compressed and elec-trochemically polished aluminum was measured. The preferred orientation in aluminum, due to uniaxial compression, is known to be [110] direction parallel to the compression axis. However, this description is only a first approximation of a rather complex orientation. In actuality, half the crystallites are more than 10 deg from this orientation, regardless of the amount of compression." For randomly oriented fcc crystals, the average surface atomic density can be calculated as follows: The number of atoms in a unit volume is 4/a3, where a is a lattice constant. Hence, the number of atoms per unit surface area is about (4/a3)2/3 = 2.52/a2 However, when the preferred orientation took place along [110] direction, the surface atomic density is as follows: The area of (110) plane of a unit cell, considering ridges and valleys, is BYOUNG WHlE LEE, Member AIME, is Research Metallurgist, Atomic Energy Research Institute of the Republic of Korea, Seoul, Korea. Manuscript submitted May 29, 1968. IMD 2 x J2- a x Ga = 6a2 Since this plane contains 4 atoms, the surface atomic density is 4i6a2 = 2.3/a2 Upon changing from random to preferred orientations, the surface atomic density decreases about 10 pct. The increase in the stored energy and the change in surface atomic density due to plastic deformation would certainly alter the surface tension of a metal. EXPERIMENT High purity aluminum rod of 6-mm diam (99.99 pct Al, obtained from Johnson, Matthey & Co., Ltd, London, England) was cut into sections approximately 1 cm long. The transverse cross section was mechanically polished. Then, the specimens were annealed in air at 600°C for 24 hr. Thus, eight annealed specimens were uniaxially compressed at room temperature from 0 to 70 pct of cold working with an increment of 10 pct. The extent of cold working was determined by the percentage of reduction in axial length to the original length. The specimens were further polished mechanically and, then, electrochemically with the Modern Battelle Type 1 electropolishing solution with a current density of 0.3 to 0.4 amp per sq cm and an electrode potential of 8 to 12 v at the solution temperature of 78" to 82°C for approxirr~ately 5 min. The Modern Whlte Diffusing Screen \t/ --------------- re Goniometer for Mercury Lamp ^-^ Sessile Drop ¦=• Condenser c=> Microscope l_*~_i bJ Mlcromster Filer with Protmcter Fig. 1—Schematic diagram of apparatus set-up for liquid contact angle measurement.

Jan 1, 1970

By A. R. Gregory

A shear wave velocity laboratory apparatus and techniques for testing rock samples under simulated subsurface conditions have been developed. In the apparatus, two electromechanical transducers operating in the frequency range 0.5 to 5.0 megahertz (MHz: megacycles per second) are mounted in contact with each end of the sample. Liquid-solid interfaces of Drakeol-aluminum are used as mode converters. In the generator transducer, there is total mode conversion from P-wave energy to plain S-wave energy. S-wave energy is converted back to P-wave energy in the motor transducer. Similar transducers without mode converters are used to measure P-wave velocities. The apparatus is designed for testing rock samples under axial or uniform loading in the pressure range 0 to 12,000 psi. The transducers have certain advantages over those used by King, 1 and the measurement techniques are influenced less by subjective elements than other methods previously reported. An electronic counter-timer having a resolution of 10 nanoseconds measures the transit time of ultrasonic pulses through the sample; elastic wave velocities of most homogeneous materials can be measured with errors of less than 1 percent. 5- and P-wave velocity measurements on Bandera sandstone and Solenholen limestone are reported for the axial pressure range 0 to 6,000 psi and for the uniform pressure range 0 to 10,000 psi. The influence of liquid pore saturants on P- and S-wave velocity is investigated and found to be in broad agreement with Biot's theory. In specific areas, the measurements do not conform to theory. Velocities of samples measured under axial and uniform loading are compared and, in general, velocities measured under uniform stress are higher than those measured under axial stress. Liquid pore fluids cause increases in Poisson's ratio and the bulk modulus but reduce the rigidity modulus, Young's modulus and the bulk compressibility. INTRODUCTION Ultrasonic pulse methods for measuring the shear wave velocity of rock samples in the laboratory have been gradually improved during the last few years. Early experimental pulse techniques reported by Hughes et al.2 and by Gregory 3 were beset by uncertainties in determining the first arrival of the shear wave (S-wave) energy. Much of this ambiguity was caused by the multiple modes propagated by piezoelectric crystals and by boundary conversions in the rock specimens. Shear wave velocity data obtained from the critical angle method, described by Schneider and Burton4 and used later by King and Fate sand by Gregory, 3,6 are of limited accuracy, and interpreting results is too complicated for routine laboratory work. The mode conversion method described by Jamieson and Hoskins7 was recently used by King 1 for measuring the S-wave velocities of dry and liquid-saturated rock samples. Glass-air interfaces acted as mode converters in the apparatus, and much of the compressional (P-wave) energy apparently was eliminated from the desired pure shear mode. A more detailed discussion of the current status of laboratory pulse methods applied to geological specimens is given in a review by Simmons.8 A new shear wave velocity laboratory apparatus has been developed for testing rock samples under elevated pressures. This apparatus employs liquid-solid interfaces as mode converters. The technique for generating pure shear waves at liquid-solid interfaces was developed from studies of critical angle methods.6 Two identical transducers are placed in contact with opposite ends of the rock sample, one transducer acting as an ultrasonic energy emitter or generator and the other acting as an ultrasonic energy receiver or motor. The P-wave energy emitted from the piezoelectric crystal in the generator transducer is converted into pure S-wave energy at the Drakeol-aluminum

By P. Somasundaran

Flotation of minerals has usually been discussed in terms of solid-liquid interfacial phenomena. This paper discusses the relative importance of phenomena such as collector adsorption at other interfaces formed between the bubble, liquid and solid. Adsorption of collector ions of various chain lengths at liquid-gas and solid-gas interfaces has been obtained. The data have been analyzed under conditions corresponding to those of flotation to show the significant role of collector adsorbed on the bubble surface in determining the bubble-mineral attachment required for flotation, and consequently to suggest consideration of this role in the development of better flotation conditions. Vacuum flotation of quartz with alkyl ammonium acetate reported in the foregoing paper1 showed that the collector chain length has an effect on flotation even at concentrations below those necessary for hemi-micelle association of the hydrocarbon chains at a solid-liquid interface. This chain length effect might be explained by the following arguments: Hydrocarbon chains find it energetically favorable to be in a medium of low dielectric constant. Considering the possibility of an iceberg structure at the solid-liquid interface, such a structure would produce a region of lower dielectric constant at the solid-liquid interface than in the liquid phase, because the dielectric constant of ice is 2 to 3,2 while that of water is 80. Depending on chain length, this difference will certainly cause even individual ions to adsorb in higher quantities at the solid-liquid interface. Another mechanism to consider is the possible formation of dimers, trimers, etc and chain length would influence this formation. But, above all, the chain length effect on flotation at concentrations of low adsorption at the solid-liquid interface could be due to the significant but often-neglected role of the collector adsorption at the bub- ble surface. Collector ions or molecules are adsorbed both at the solid-liquid interface and the liquid-gas interface. Below the concentration for hemi-micelle association at the Stern plane adjacent to the surface, the bulk of the collector ions adsorbed at the solid-liquid interface are in the diffuse part of the double layer. If such systems, where there is a gas bubble coming in contact with the solid surface, are to achieve some degree of electroneutrality, those collector ions would have to migrate from the diffuse part of the double layer to the region directly adjacent to the surface during the induction period when the bubble is making contact with the solid. The time necessary for this migration would contribute to the induction period required for creation of the solid-gas interface. It seems reasonable that the induction period could be reduced sufficiently for flotation to occur if these collector ions were carried to the surface by the bubble. In an attempt to ascertain whether or not the bubble could possibly have sufficient collector ions at its surface to meet the requirement mentioned above, the adsorption density of the collector ions at the liquid-air interface was determined. For this purpose, the surface tension of alkyl ammonium acetate solutions was determined as a function of concentration. Adsorption densities of the collector at the liquid-gas interface were calculated using the Gibbs adsorption equation: where y is the interfacial tension and ri and pi are the adsorption density and the chemical potential, respectively, of the chemical species, i. Using the convention that the adsorption density of water at the interface is zero, the following relationship is obtained for the liquid-gas interface where lg refers to liquid-gas interface and RA+ refers to the alkyl ammonium ions. For dilute solutions, rf^-wri^&rfwW [3] where C is the concentration of the collector ions in solution. l?:: can now be evaluated using Eq. 3 and surface tension measurements.

Jan 1, 1969

By F. W. Jessen, H. Kazemi

A washing technique has been developed to form a spherical cavity in massive salt. The technique is, basically, a process of controlling the fluid motion in the cavity, the concentration distribution of brine, the rate of dissolution at the walls of the cavity, and the particular settings of the wash pipe, or pipes (inlet and outlet pipe) employed. For a particular arrangement of tubing and casing, fresh water enters from the casing annulus at a position above the bottom of the tubing, and the dissolved material leaves the cavity through the tubing near the bottom of the projected hole. The initial configuration of the cavity is cylindrical, representing the drilled hole situated at the axis of the projected cavity. As washing progresses the original hole is enlarged radially (any direction perpendicular to the axis of the hole). An inert fluid (generally a hydrocarbon, natural gas, or air) which serves as a blanket is injected through the annular space between the original hole and the casing. The controlled downward motion of this blanket maintains the upper edge of the brine region that is expanding on the surface of the projected sphere. A large spherical glass container and a radial model were used to investigate the flow patterns and the concentration distribution of brine occurring during the progress of solution of the salt. Aluminum flakes and dye were injected and flow patterns were observed and recorded on motion picture film. Based on the results of these model studies and other work carried out in this laboratory, the controlled washing technique was formulated. INTRODUCTION Underground cavities leached in salt beds and salt domes have been used extensively for storing hydrocarbons. Little attention has been focused on the shape of the cavities as long as large volumes were obtained and the cavities were structurally stable. The general process involves circulating fresh water and removing brine. Two distinctly different circulating systems can be employed, each of which yields characteristically different shapes. By far the most generally accepted method of washing storage caverns in salt domes is the direct circulation system. Water is introduced through the innermost pipe of a concentric pipe system, and brine is withdrawn through the annulus. In the reverse-circulation method, water enters through the annulus and is discharged through the smallesc tubing string. The size of the operation, and hence the size of tubing and casing used, depends on such factors as cavity volume, length of hole, availability of water, disposal of brine and power requirements. Underground caverns are from 100 to 1,000 ft or more in length, and when completed vary from 40 to 100 ft in diameter, providing storage of 100,000 bbl or more. The volumes of water required per volume of salt removed vary from 6 to 7 for the reverse circulation method to 10 to 11 for the direct circulation method. Up to 80,000 BWPD are often circulated. In the direct circulation method, because water enters near the bottom of the projected cavity, solution of salt is greatest at this point, particularly in view of the fact that when the washing is begun turbulent flow undoubtedly exists in the immediate vicinity of the discharge of the inlet water. As the diameter of the hole increases, flow rates also are increased, so perhaps the condition of fluid turbulence is maintained for some time. During the later stages of leaching, when capacity of equipment may be the limiting factor in maintaining flow rates, there may still exist some turbulence adjacent to the point of influx; however, for the most part laminar flow conditions prevail. There appears, therefore, rather good evidence to indicate that the state of fluid motion is responsible for the typically shaped cavity which results from such washing — namely a cylindrical form, generally somewhat larger at the bottom than at the top. Depending on the number of so-called stages which might be employed, the walls or surfaces of the salt diminish rather uniformly from bottom to

Jan 1, 1965

By J. H. Swisher

The solubility of graphite in CaO-S2O2-Al,O3 slags was measured by equilibrating slag samples with graphite crucibles and CO gas. Carbon contents as high as 2 ut pct were obtained in CaO-saturated, CaO-A1,O3 slags, and 1.3 wt pct in slags of the composition CaO.Si0,. Although the observed conditions for Sic formation were in agreement with those predicted from thermodynamic data, CaC, was found to form at a lower temperature than predicted frotn thermodynamic data. From measurements of the equilibrium carbon content as a function of CO Partial pressure, it was found that carbide ions dissolve in CaO-A12O3 melts with a valence of minus two. The carbon content increased with CaO concentration in Ca0-Al,O3 melts and increased with SiO, content along the CaO'AlO3-CaOSi0 join in the ternary system. When solid CaC2 was added to CaO-A12O3 and CaO-SiO2-A12O3 slags, it was found that one of the oxides in the slag was reduced by the carbide (Al2O3 in the forrner and SiOz in the latter). In electric furnace steelmaking, a double-slag practice is frequently used to meet alloy specifications. Initially a flush slag, which is oxidizing in nature, is used to remove phosphorus and carbon from the steel bath. Later in the refining period, the flush slag is replaced by a highly reducing carbidic slag. When calcium carbide is formed in or added to a finishing slag, the slag is effective as a desulfurizing agent and also permits alloying elements such as chromium, vanadium, and tungsten to be added to the slag in the form of oxides. The oxides are readily reduced by calcium carbide, thereby minimizing the use of expensive ferroalloys. More work has been done on the thermodynamics of silicon carbide in slags than on calcium carbide. Baird and alor' and Kay and alor' determined the free energy of formation of Sic by measuring the partial pressure of CO in equilibrium with solid silica, silicon carbide, and graphite. Using a similar technique, they determined SiOz activities in CaO-SiOz and Ca0-Si0,-A1203 slags. Rein and chipman3 also determined the free energy of formation of Sic using slag-metal equilibrium measurements. A literature survey has uncovered only one experimental study of the behavior of CaC, in slag systems. Shanahan and cooke4 report the results of some preliminary experiments on the solubility and stability of CaC, in a CaO-A1,03 and a Ca0-Si0-A1,03 slag at a temperature of about 1500". The carbon solubility as CaC, in a slag containing 50 pct CaO and 50 pct A1203 was reported to be 0.6 pct. They also review earlier work on the binary CaO-CaC, system. A eutectic exists in this system, but various investigators disagree on the eutectic temperature and composition. eal has given an explanation for carbide furnace erruptions in terms of the thermodynamic properties of CaC,; his analysis is not based on experimental data, but on compiled data for the free energies of formation of CaC, and CO.' , These data for steel-making temperatures are all extrapolated from the results of low-temperature measurements. In the experiments described in this paper, slag samples were equilibrated with graphite crucibles and with mixtures of CO and argon or with CO gas at 1 atm total pressure for measurement of the carbon solubility. Most of the work was done on Ca0-A1203 binary slags, although in some experiments CaO-SiO, and Ca0-Si0,-A1,03 slags were used. EXPERIMENTAL Slag samples of the desired composition for the solubility measurements were obtained by blending pre-fused master slags. The master slags were prepared by fusing mixtures of reagent-grade CaC03 with either A1,03 or Si0, in a graphite crucible. The master slags were crushed, then decarburized in air in a muffle furnace at 1200O C. A schematic diagram of the apparatus is shown in Fig. 1. The source of carbon for the solubility meas-

Jan 1, 1969

By J. L. Smith, A. L. Albee

This article presents a series of guidelines by which the geologist can evaluate the likelihood of surface faulting and its probable extent at any given site in Southern California and Nevada. The information is intended primarily for geologists concerned with establishing design criteria for proposed nuclear plants. The geologic problems involved in the location of a nuclear power plant are fundamentally no different from those for other types of installations. They fall into four main categories: foundation stability, landslides and slope stability, shaking due to earthquakes, and surface faulting. For problems in the first three categories the foundation engineer, the geologist, and the seismologist can provide criteria for plant location and design, and these problems can generally be economically handled by appropriate design measures for a project of the magnitude of a nuclear plant. However, problems in the last category — surface faulting — are more difficult to handle and require a unique evaluation. Accordingly, this paper will deal primarily with the problem of establishing design criteria for surface faulting, particularly as it affects nuclear facilities. A nuclear reactor is a power source that for greater safety is contained in a heavy, air-tight structure, just as gas, oil, water, and other power sources must be contained. Surface faulting is significant in that it may reduce the integrity of the containment by affecting critical exterior piping or by breaching of the containment. A similar significance exists relative to dams or tanks for the storage of water, gas, or oil, except that in these latter examples the breaching of the container automatically releases the fluids to do their damage. This is not necessarily the case with the rupture of a reactor containment structure because the function of the containment is totally protective, i.e., it is necessary only in the event that radioactive products are released from the reactor, and there are many other safeguards to pre- vent this release even if the containment is ruptured. At the present time, nuclear power plants must be located near large sources of water for cooling the steam generated. The construction of an industrial facility of any kind on the coast line is esthetically distasteful to most people since, unfortunately, there is not enough coast to fulfill all the needs and all the desires of all the people. In most cases where industrial facilities encroach on the lives of citizens, there is no mechanism other than zoning laws by which a person can effectively protest. But in the case of a nuclear facility, the public hearing required by the Atomic Energy Commission provides a forum for dissent, as in recent case histories, and the question of safety provides objectors with a weapon for fighting the construction of the plant. The nature of a public hearing for a nuclear plant is such that the prospective owner and operator must prove that there is no undue hazard, whereas the objectors need only demonstrate that there is a reasonable doubt. It is in this situation that geology becomes the Achilles Heel of nuclear power plant location. For his investigation, the geologist has natural exposures of rock at the ground surface and a limited number of trenches and drill holes to give him a fairly complete picture of the distribution of the various rock types. From the surficial data, he must infer three more dimensions — depth below the surface, past time, and future time. Unlike many problems faced by engineers, the geologist has only this one set of data from which to reach a conclusion — he is unable to reproduce the natural sequence of events in order to obtain another set of data for comparison. Hence, by the very deductive nature of a geologic conclusion, it is difficult to prove a geologic conclusion beyond a reasonable doubt even to other geologists — and perhaps one should say especially to other geologists because the experience and background of a geologist will strongly influence his conclusion, and no two geologists have exactly the same experience and training. The engineer and the public official would like the geologist to conclude that faulting cannot occur at a given site or to assign a numerical value to the probability of its occurrence — but no responsible geologist can do either of these things. Since government officials and others must make decisions that affect the public safety, it would seem that the geologic profession must attempt to establish criteria and

Jan 1, 1968

By A. F. Crawley

The density and viscosity of 1iquid thallium have been measured by absolute methods to temperatures of about 200° and 150°C, respectively, above the melting point. These new data reported, especially density data, do not closely confirm previous work. Density p, in g per cu Cm, is shown to vary linearly with temperaluve t, in °C, according to the equation p = 11.658 - 1.439 X l0-3t. The viscosity data obey the well-known Andrade equation nv1/3 = A exp C/vT , the constants A and C for thallium having values of 2.19 x A and 79.648, respectively. This paper reports some new data for the density and viscosity .of liquid thallium. Measurements of these fundamental physical properties were undertaken as part of a continuing research program at the Mines Branch, Department of Energy, Mines and Resources, Ottawa. Canada. A literature search has revealed that data are so scarce that there could not be a consensus on the true values of the density and viscosity of liquid thallium. To be more specific, there exists only one set of viscosity data' and only two acceptable sets of density data,273 one of which is limited in scope.3 In Liquid Metals Handbook,3 another density study is reported but indications of impurities in the thallium render the results suspect. In this situation, further careful experimentation was required to realize the true density and viscosity of thallium. EXPERIMENTAL METHODS Density. Densities were determined using a graphite pycnometer. The technique and its accuracy have been discussed in earlier papers.4'5 It is considered that experimental data can be obtained which are accurate within +0.05 pct, all sources of random and systematic errors having been evaluated. Density results for thallium were identical whether measured under an atmosphere of argon or a vacuum of 5 x 10-6 torr and, for the most part, the argon atmosphere was used. Viscosity. Viscosity measurements were made in an oscillational viscosimeter by an absolute method—the liquid metal being held in a closed graphite cylinder. Design and operation of the apparatus, constructed in this laboratory, have previously been discussed.6 For thallium, runs were made under a vacuum of about 2 x 10-6 torr. To evaluate viscosity coefficients from the various experimental parameters, the mathematical analysis of Roscoe7 was used. Measurements of the necessary parameters and the accuracy of these measurements have also been discussed.6 The cylinder dimensions were corrected for the anisotropic expansion of graphite, as discussed for density measurements.4,5 It is well-known that thallium oxidizes rapidly and hence a newly machined surface quickly tarnishes in air. The oxide film, however. is nonadherent and is easily removed by rubbing or by solution in water. Hence, immediately before use, both density and viscosity charges were immersed in water, wiped dry, and quickly transferred to the apparatus which was then rapidly evacuated. Specimens removed after determinations were only slightly tarnished and there was no other evidence that tarnishing affected the results. For example, the sharpness of the specimen edges from the containing vessels indicated complete filling by the liquid metal. Thallium of 99.999 pct purity was used in this investigation. Because of its high toxicity care was exercised in handling this material. For example, the melting procedure to prepare machinable ingots was carried out in an open, well-ventilated area, while protective gloves were always worn when handling the solid metal. RESULTS AND DISCUSSION Density. Measurements were made over a tempera-ture range of about 200°C above the melting point. The results are listed in Table I and plotted in Fig. 1. From the graph it is evident that the relation between density and temperature is linear. Such a relation has been observed before in this program for other metals and alloys475 and elsewhere by other workers. A least-squares analysis of experimental data gives the equation: pT1 = 11.658 - 1.439 x 10-3t where p = density in g per cu cm and t = temperature in "C. In Fig. 1, together with the present results, the data of Schneider and Heymer2 in the corresponding temperature range have also been plotted. Evidently, the two sets of data do not agree well, the results of Schneider and Heymer being about 0.6 pct higher. Viscosity. Viscosity data were obtained from the melting point, 303.5°C, up to 457.5"C. The data are listed in Table I and in Fig. 2 the plot of these results demonstrates a smooth curvilinear relation between

Jan 1, 1969

By F. E. Werner, B. L. Averbach, Morris Cohen

THAT bainite formed near the M, temperature bears a striking r esemblance to martensite tempered at the same temperature has been shown by the electron microscope.' By means of electron diffraction,' it has been established that carbide and cementite are present in bainite formed at 500°F (260°C); these carbides are also found in martensite tempered at 500°F (260°C).' The investigation reported here is concerned with an X-ray study of the matrix phases in lower bainite and tempered martensite. These phases have turned out to be dissimilar in structure; the matrix of bainite is body-centered-cubic while that of tempered martensite is body-centered-tetragonal. A vacuum-melted Fe-C alloy containing 1.43 pct C was studied. Specimens of 16 in. diam were sealed in evacuated silica tubing and austenitized at 2300°F (1260°C) for 24 hr. One specimen was quenched into a salt bath at 410°+7 °F (210°+4°C), held for 16 hr, and cooled to room temperature. The structure consisted of about 90 to 95 pct bainite, the re: mainder being martensite and retained austenite. A second specimen was quenched from the austen-itizing temperature into iced brine and then into liquid nitrogen. It consisted of about 90 pct martensite and 10 pct retained austenite. The latter specimen was tempered for 10 hr at 410°+2°F (210°+1°C). The specimens were then fractured along prior austenite grain boundaries (grain size about 2 mm diam) by light tapping with a hammer. Single aus-tenite grains, mostly transformed, were etched to about 0.5 mm diam and mounted in a Unicam single crystal goniometer, which allowed both rotation and oscillation of the sample. Lattice parameters were measured by the technique of Kurdjumov and Lyssak. This method takes advantage of the fact that martensite and lower bainite are related to austenite by the Kurdjumov-sachs orientation relationships Thus, the (002) and the (200) (020) reflections can be recorded separately, permitting the c and a parameters to be determined without interference from overlapping reflections. According to these findings, the matrix phase in bainite is body-centered-cubic and, within experimental error, has the same lattice parameter as ferrite (2.866A). On the other hand, martensite, tempered as above, retains some tetragonality, with a c/a ratio of 1.005t0.002. Most workers in the past have assumed that bainite is generated from austenite as a supersaturated phase, but the nature of this product has not been established. The question arises as to whether bainite initially has a tetragonal structure and then tempers to cubic, or if it forms directly as a cubic structure. If it forms with a tetragonal lattice, it might well be expected to temper to the cubic phase at about the same rate as tetragonal martensite. The martensitic specimen used here was given approximately the same tempering exposure, 10 hr at 410°F, as suffered by the greater part of the bainite during the isothermal transformation. About 50 pct bainite was formed in 6 hr at 410°F. On tempering at this temperature, martensite reduces its tetragonality within a few minutes to a value corresponding to 0.30 pct C.' Further decomposition proceeds slowly, and after 10 hr the c/a ratio is still appreciable, i.e., 1.005. Thus, even if the bainite were to form as a tetragonal phase with a tetragonality corresponding to only 0.30 pct C, which might be assumed to coexist with e carbide, it would not be expected to become cubic in this time. It seems very likely, therefore, that bainite forms irom austenite as a body-centered-cubic phase and does not pass through a tetragonal transition. The carbon content of the cubic phase has not been determined, but it could easily be as high as 0.1 pct, within the experimental uncertainty of the lattice-parameter measurements. It has been postulated that retained austenite decomposes on tempering into the same product as martensite tempered at the same temperature. There is now considerable doubt on this point. The isothermal transformation product of both primary and retained austenite at the temperature in question here is bainite," and the present findings show that bainite and tempered martensite do not have the same matrix. Acknowledgments The authors would like to acknowledge the financial support of the Instrumentation Laboratory, Massachusetts Institute of Technology, and the United States Air Force.

Jan 1, 1957

By Y. Nakada, U. F. Kocks, B. Chalrners

THE orientation dependence of work hardening has previously been studied over the entire range, i.e., including special orientations of high symmetry, in aluminum1-3 and silver.* The differences between various orientations are substantial, and the trend is the same in all fcc crystals. However, there are quantitative differences in behavior between aluminum and silver at room temperature, particularly in the (100) orientation. While many experiments on gold have been reported,5'9 none included the special orientations. We therefore undertook tension tests on gold crystals of the axial orientations (100),(110), (Ill), (211), and, as a representative of single slip, one whose Schmid factor was 0.5 (hereafter referred to as m = 0.5). Single crystals of dimensions 1/4 by .1/4 by 6 in. were grown from the melt1' at a rate of 4 in. per hr, using gold of 99.99 pct purity obtained from Handy and Harman. A growth rate of 1/8 in. per hr, or a purity of 99.999 pct,ll produced no difference in results. The crystals were annealed at 1000°C in air for 24 hr and furnace-cooled down to room temperature, after which they were electro-polished in a solution of potassium cyanide (40 g), potassium ferrocyanide (10 g), soda (20 g), and enough distilled water to make 1 liter of solution, at a current density of 0.02 amp per sq mm. After 2 or 3 hr, a very smooth surface was obtained by this method. Nine m = 0.5, two (loo), one (110), three (Ill), and one (211; crystals were tested at room temperature in a floor-model Instron machine at a tensile strain rate of 0.5 pct per min. The accuracy of the stress measurement was k10 g per sq mm up to 500 g per sq mm, k2 pct for higher stresses. The strain measurement was accurate to t2 pct. The scatter of stress at a given strain among the crystals of the same orientation was small, *5 pct being the largest. The representative stress-strain curves for various orientations are shown in Fig. 1. Table I summarizes the work-hardening parameters as used by seeger.12 Results of other investigators are also included in this table for comparison. There are no previous data for the corner orientations. Values for m = 0.5 crystals agree fairly well with those of Berner. Tm is defined as the stress at which the stress-strain curve begins to deviate from linearity of Stage 11. However, in practice this is a very difficult value to estimate because each investigator has a different idea of linearity. Therefore, the comparison with the values of other investigators may not be valid. In the present experiment, (100) crystals had the highest 111, followed by (111) crystals. The work-hardening rate in Stage I1 was highest for the (111) crystal followed by the (100) crystals. Our value for 0x1 of m = 0.5 orientation agrees very well with those of other investigators. 1) Single-Slip orientation (m = 0.5). These crystals were oriented so that the primary-slip vector was contained in one side face. The dimension perpendicular to this side should then not change if single slip indeed takes place. Within the accuracy of measurement, this dimension did not change during the deformation. Since the accuracy is k0.2 pct, the amount of secondary slip is less than 0.7 pct of the slip on the primary-slip system at 30 pct tensile strain. This is in conformity with the results obtained by Kocks" for aluminum crystals. The tensile axis moved toward (211) during the deformation. Slip bands, Fig. 2(a), were very fine and closely spaced. Some deformation bands were observed. There were no clear-cut cross-slip traces such as the ones observed on aluminum m = 0.5 crystals. 2) (111) Crystals. The orientation of the tensile axis was stable during the deformation. From this observation, one can deduce that at least three slip systems must have operated, and probably all six because the remaining three all have cross-slip relation to one of the first three.' It was very difficult to observe the slip markings. Consequently, we could not confirm by this method that six systems were operative during the deformation. At high strains (above 50 pct shear strain), this orientation had the highest stress-strain curve. At 80

Jan 1, 1964

By R. W. Ludt, C. C. DeWitt

The use of froth flotation for the separation of minerals has become one of the most important of ore dressing processes. Its particular adaptability to the enrichment of low grade ores has made the process an important factor in the national economy. The methods have been extended to the recovery of a great number of minerals. Among the few minerals which have resisted efforts toward industrial flotation is chrysocolla, a hydrated partly colloidal copper silicate. Chrysocolla, being a product of natural oxidation, has been found to occur in small quantities with many ores which are recovered by flotation methods. In present practice, these small quantities of copper silicate pass off with the tailings and are lost. The advantages to be gained by a satisfactory process for the recovery of chrysocolla is apparent. Any application of principles which points a way toward the satisfactory industrial flotation process for copper silicate would be of advantage. This paper presents an attack on this problem. Two methods for the recovery of chrysocolla have been developed by the United States Bureau of Mines.1,2 They have been successful on a laboratory scale but have been seriously restricted in industrial application by critical requirements in the procedure. In one of the Bureau of Mines methods,' the ore is activated with sodium or hydrogen sulphide in an aqueous solution at a pH of 4. Amy1 xanthate is then used as a collector with pine oil as a frother in the flotation process. An excess of sulphide acts as a depressant and the state of optimum conditions is difficult to control industrially. In the second Bureau of Mines method,2 soap is used as the collector at a pH of between 8 and 9. The diffi- culties with this process are that soap is not a specific collector, that heavy metal or alkaline earth ions cause the formation of insoluble soaps, and that a more acid solution causes the formation of a free acid which does not act as a collector for chrysocolla. The problem of recovering chrysocolla by flotation involves the selection of a suitable collector. The collector molecule must be composed of an active polar group that has an attraction for chrysocolla, and of a hydrocarbon chain. Certain dyes have been shown to have an attraction for certain minerals. Suida3 found that hydrated silicates are colored by basic dyes. Dittler4 showed that chrysocolla, among other colloidal minerals of acid reaction, preferentially takes up such basic dyes as fuchsin B, methylene blue, and methyl green. Endell5 gave information to show that the colloidal material in clay may be determined by its selective adsorption of fuchsin. A simple experiment, likewise, illustrates the difference in the adsorptive power of chrysocolla and of silica for the basic triphenyl methane dyes. When a mixture of chrysocolla and silica is immersed in a very dilute dye solution, less than 5 ppm, the chryso-colla is rapidly dyed and the silica is dyed more slowly. The difference is substantial but one of degree. Dean2 showed that the dyes, crystal violet and toluidine blue, are taken up by quartz in an adsorption type process. The difference in the adsorptive power, however, offers the means by which a new collector may act. To form such a collector, a hydrocarbon chain must be attached to the dye molecule. This involves a process of organic synthesis. Butyl, hexyl, and octyl hydrocarbon chains were selected for substitution in the malachite green molecule. For the purpose of identification, the alkyl-substituted dyes formed are called: butyl-malachite green; hexyl- malachite green; and octyl-malachite green. An outline of the procedure for their synthesis is given in the appendix. It is generally recognized in the preparation of this type of dye that the chemical structure of some of the dye molecules varies. However, a uniform formula is attributed to the dye. Such a procedure has been followed in specifying the structure of these alkyl-substi-tuted malachite green dyes. The structure is given on the basis of their properties as an homologous series of dyes, on their method of preparation, and on the purity of intermediates used. Structure of substituted alkyl malachite green is: C6H4 N(CH3)2 p-R C6H4 CH C6H4 N(CH)2 Procedure The flotation cell is a Bureau of Mines 100-g, batch unit provided with an air inlet at the bottom above which is a variable speed agitator. The agi-

Jan 1, 1950

An extra-tough rubber is the answer to many maintenance problems.

Jan 8, 1951

By J. Downie, H. A. Kendall, G. H. F. Gardner

Some cases of the motion of two miscible fluids in uniform linear models are discussed. There is no bulk flow through the models, and the convection currents are caused solely by density gradients. Horizontal, vertical and inclined positions of the models are treated separately. Analytical formulas for the motion of a narrow transition zone between the fluids are obtained and compared with measurements, and the limitations are discussed. Observations of the ultimate stabilizing effect of diffusion on the motion me compared with the theory. It is shown that fluid motion in an inclined model with a constant rate of bulk flow can be directly deduced from the cases discussed, provided the viscosity ratio is small. INTRODUCTION In some reservoirs, convection currents caused by variations in the fluid densities may be significant. For practical purposes it may be desirable either to minimize the effect, particularly in miscible displacement, or to maximize the effect as in some schemes for the production of heavy crude oils by combustion. Experiments by Craig, et al,l have shown the effectiveness of gravity in reducing the efficiency of a miscible displacement when the mixed zone between the displacing and displaced fluids is narrow compared with the height of the system. The presence of a board transition zone from one fluid to the other has been shown by Perkins, et al,2 to nullify considerably the influence of a difference in density. Indeed, the theoretical discussion given by Perrine3 has shown that when the transition zone exceeds a certain critical length the efficiency approaches 100 per cent. Many additional results 495 have been published on miscible and immiscible displacements which show the importance of density difference and also mobility ratio. The aim of the present paper is to discuss some cases of gravity segregation of miscible fluids in linear models such as are often used in the laboratory to evaluate recovery processes, and to supply additional experimental evidence in support of the conclusions. An attempt is made to calculate simply the magnitude of the fluid motion caused by density pdients and mobility ratios, and to quantify the modifications in the fluid motion produced by the combined effect of molecular and convective dispersion. However, it should be pointed out that the uniform permeability of the models and the use of only a single pair of fluids (whereas several pairs of fluids may be employed in a recovery scheme) severely restricts direct conclusions about natural reservoirs. For conciseness, the motion generated by density gradients is emphasized for the case of no bulk flow through the models. This is not a drastic limitation because, as shown in Appendix A, a fluid motion with a constant bulk flow through any linear model is equivalent to a fluid motion with no bulk flow in the same model inclined at a different angle to the horizontal, provided only that the density is a linear function of the viscosity of the fluid mixture. HORIZONTAL MODEL In this case the model is assumed to have a rectangular cross-section with a horizontal breadth b, vertical height and a great length L. Throughout.the paper it will be assumed that x-axis points along the length, the y-axis along the width and the z-axis along the height. Thus, in the present case the x, y plane is horizontal. Initially, the transition zone between the fluids is assumed to be thin and parallel to the y, z plane. An example of this situation in a practical problem arises in a scheme for using air for cushion gas in the storage of fuel gas in aquifers. 6 With the passage of time the denser fluid sinks and spreads along the bottom of the model while the lighter fluid rises. The interface extends from the top plane of the model to the bottom. Experiments have shown that for practical purposes this interface may be treated as a plane surface at all times. The surface is significantly curved, however, for viscosity ratios greater than about 10. Other complications arise with large viscosity ratios because of the nonlinear dependence of the viscosity on the composition of the mixture, so that the simple results given here are restricted to fairly low viscosity ratios.

By P. Bardzil, J. Gurland

An experimental study of the variation of transverse-rupture strength with composition Anexperimentaland grain studysize has shown that the strength reaches a maximum for values of the mean free path between carbide particles of 0.3 to 0.6 microns. The fracture oforiginates in and proceeds through the carbide grains mainly. Impact strength and hardness also were recorded. MOST of the physical properties of sintered carbides vary linearly with composition. The transverse-rupture strength, however, shows a unique behavior. As the amount of binder metal is varied from 6 to 25 pct by weight, the strength at first increases; then, between 15 and 20 pct Co, it reaches a maximum of nearly 400,000 psi, and finally decreases with further additions of binder metal. This behavior of the transverse-rupture strength has been reported, among others, by Englel and Sandford and Trent.' The significance of these observations has not been discussed in the literature. That it may be of more than specific importance is indicated by the very similar variation of strength with composition encountered in other systems sintered in the presence of a liquid phase, such as Tic-Ni3 and Fe-Cu.' Experimental Details All compacts were prepared and sintered according to normal industrial practice. The average diameter of WC grains and the mean free path between grains were measured on metallographically prepared samples by a method of linear and planar analysis sing the relations where d is the average diameter of dispersed grains; Nl is the number of noncontiguous grains intersected on a metallographic plane by a line of unit length; N, is the number of noncontiguous grains per unit area; P is the mean free path between grains of dispersed phase; and f is the volume fraction of dispersed phase. Approximately 1000 grains were counted on each sample. For each composition d2 was plotted against P, the resulting straight lines serving as a check on the measurements. The distribution curves of the WC powders of different average diameters were homologous, and no attempt was made to influence the grain size by blending powders, adjusting the sintering conditions, or otherwise altering the particle size distribution. Densities were measured by differential weighings in air and water. The degree of densification did not vary consistently with either composition or grain size. The density is influenced by slight amounts of impurities, specifically by 0.1 to 0.2 pct Fe which enters the powders during ball milling. As an illus- -tration of the experimental variations, a number of measured densities are listed in Table I. They are expressed in percentage of theoretical density, as calculated from the published X-ray densities of WC and Co.' For the purpose of determining the transverse-rupture strength, rectangular test specimens (3/16x 3/8x3/4 in.) were broken by loading at the center of a 9/16 in. span. The average strength of five or more samples is reported for each composition and grain size. The compacts were ground on two parallel surfaces only. The load was applied at an average rate of 6,800 psi per sec. Since the elongation after fracture of the alloys is very small, it was assumed that the compacts deform elastically to failure and the fracture stress was calculated by the conventional beam formula. The data for one alloy are presented in Table II as an example of the results and scattering ranges encountered. The precision of the test, as measured by the average difference between duplicates, is of the order of 15,000 psi. The results are strictly comparable only to compacts prepared and tested in the manner described and of similar chemical composition and grain size characteristics. Unnotched Charpy specimens were used for impact testing. Each point represents the average of 3 to 20 samples, the larger number being used in an attempt to determine the influence of grain size. Considerable scatter was encountered, the range from lowest to highest value often amounting to 30 pct of the impact strength. The hardness is reported as a Ra reading, using a 60 kg load with diamond brale indenter. Compositions are given in weight percent.

Jan 1, 1956

By J. G. Savins

Certain types of macromolecules added to water and salt solutions flowing in turbulent motion can reduce the pressure gradient. Alternatively, the volumetric capacity of a pipe for these fluids is increased by the presence of these materials. Examples presented show that the drag reduction can become significant. Thus, the presence of 0.28 per cent of a gum derivative in a solution of sodium chloride flowing at 200 gal/min in a 1.89-in. pipe yields a pressure drop which is 0.44 of the single-phase drop measured under the same conditions of turbulent flow; the addition of 0.1 per cent of a vinyl derivative to a I-in. water line yields a throughput capacity which is 1.78 of the single-phase capacity at the same pressure drop. It is further shown that these phenomena are distinctly different from previous observations with other classes of non-Newtonian systems. There a simple lowering of friction factors below the levels predicted from the resistance laws for Newtonian fluids is associated with a suppression of turbulent motion. A rational physical explanation for drag reduction is advanced. Briefly, the proposed mechanism is a storage by the molecular elastic elements of the macromolecules in solution of the kinetic energy of the turbulent motion. INTRODUCTION This study was inspired by a recent review of some paradoxical drag reduction phenomena in turbulent pipe f1ow.I Under very moderate conditions of turbulent flow, the pressure gradient necessary to pump solutions containing certain specific kinds of polymers, fibers and metallic soaps may become appreciably lower than that required* to pump the solvent, i.e., water or a low-viscosity hydrocarbon, under identical flow rates in the same conduit. As shown by our review, this phenomenon of drag reduction in turbulent duct flow was first noted during the second world war, apparently arising in connection with the development of flame warfare weapons. Since that time several papers illustrating this phenomenon have appeared: Toms, Oldroyd,3 Agoston et al., Bundrant and Matthews, Robertson and Mason,6 Ousterhout and Hall,7 Daily and Bugliarello~ Lummus, Anderson, and Fox. 9 That there are practical applications for techniques which increase discharge or decrease the pressure necessary to transport a liquid through a pipeline is illustrated in the patents which have issued which take advantage of this peculiar phenomenon, e.g., Mysels,l0 Dever, Harbour, and Seifert.11 One also finds fragmentary evidence of this effect in the data pertaining to a few of the polymeric solutions studied by Shaver12 and Dodge.13 However, these investigators were concerned with the development of friction factor vs Reynolds number correlations for a variety of non-Newtonian solutions and suspensions, rather than in a study of drag reduction-. A similar kind of drag reduction effect has been observed in gases. Sproull, for example, reports that adding dust to air flowing in turbulent motion through a pipe results in a lowering of the pressure gradient at identical flow rates. There are also military applications for reducing the drag on hydrodynamic vehicles. For example, the possibility of injecting a rheologically complex fluid into the boundary layers of bodies to reduce the skin friction has been investigated by Fabulal5 and Granville.16 Along somewhat different lines are the drag reduction studies of Kramer.17118 He has shown that skin friction can be reduced by covering the surface of a vehicle with a flexible skin. The effect is apparently due to the boundary layer being stabilized by the presence of the skin. Drag reduction by means of coexisting gas and liquid boundary layers, e.g., film boiling and continuous gas injection, has been proposed by Bradfield, Barkdoll, and Byrne,19 Cess and Sparrow,20'21 Sparrow, Jonsson, and Eckert.22 Here the skin friction occurs between a vapor and a surface rather than between a liquid and a surface. There are several references in the literature to friction-factor correlations for non-Newtonian solutions and suspensions: Shaver and Merri11,23 Dodge and Metzner, Clapp,25 and Thomas.26

Jan 1, 1965

By P. Somasundaran, D. W. Fuerstenau

The length of the collector is found to influence the flotation of the mineral even at incipient conditions, which are below the concentration at which interaction at the solid-liquid interface begins to take place to form hemi-micelles. To study this dependence, concentration for incipient flotation of quartz was determined as a function of pH with collectors of various chain lengths. The observed effect of chain length on flotation is ascribed to that of collector adsorbed on the bubble surface. In previous studies, it was shown that at low concentrations the alkyl collector ions adsorb at the solid-liquid interface as individuals.''2 At higher concentrations, the collector ions adsorbed at the solid-liquid interface associate with each other to form two-dimensional aggregates called hemi-micelles. Above the hemi-micelle concentration, the length of the hydrocarbon chain is extremely important since the hydrocarbons are in effect removed from water during the association, making the energetic conditions more favorable for adsorption at the interface. Because of this enhanced adsorption, one observes a very rapid increase in flotation associated with the hemi-micelle formation at the solid-liquid interface. However, a dependence of flotation on the chain length at concentrations below that required for hemi-micelle association was also observed,' and this cannot be explained by the above mechanism which postulated hydrocarbon chain interactions only at the solid-liquid interface. This prompted an investigation into other possible reactions of the hydrocarbon chains and an examination of the conditions at the bubble surface involved in the flotation system and how these observations might explain the reactions at the solid-gas interface which cause the particle-bubble attachment required for flotation. To obtain more information on chain length effects, flotation, under incipient conditions, was tested by vacuum flotation techniques. The collector-concen-tration-pH relationships for flotation of quartz with alkyl ammonium acetate collectors was delineated by observing the pH at which quartz particles begin to float to the liquid surface. By investigating flotation as a function of pH, it was also possible to study the effect of neutral molecules on incipient flotation conditions, since the aminium ions hydrolyze to amine molecules at higher pH values. EXPERIMENTAL WORK Brazilian quartz specimens were crushed and sized, and the 270 x 400 mesh fraction was used for flotation studies. The samples were leached with concentrated hydrochloric acid until no coloration of the acid occurred. The leached material was washed free of chloride ions and stored in distilled water. The vacuum flotation technique developed by Schuhmann and prakash3 was used to determine the critical pH-concentration curves. This method, which can be used to delineate conditions for incipient flotation, is fairly simple and rapid. About 0.5 gm of 270 x 400 mesh quartz was placed in a 100 ml graduated cylinder which was then filled to the 100 ml mark with the collector solution made from high-purity alkyl ammonium acetate salts. The water used for the test was conductivity water saturated with air that had been passed through a cleansing train consisting of Drierite, Ascarite, a water wash bottle, and a trap. After the pH was adjusted, the cylinder was then conditioned for thirty minutes. In the tests where an acid pH was desired, sufficient acid was added before the collector solution to avoid any effect due to slow desorption of collector from the quartz surface. After conditioning, vacuum was applied to the system and the flotation or nonflotation of the quartz was noted. The pH at which the quartz particles began to float to the liquid-gas interface was taken as the critical PH. Critical pH curves were thus determined for different concentrations of the various collectors. Hallimond tube flotation data were taken from the authors' previous publication1 for correlation with that from the vacuum flotation. RESULTS AND DISCUSSION The results of vacuum flotation studies for determining critical pH-concentration curves, i.e., curves which delineate conditions for incipient flotation, are shown in Fig. I. In generaI, all the curves exhibit an upper and lower pH limit between which flotation will

Jan 1, 1969