By R. K. Ham, M. L. Wayman

TD-Nickel has been broken in tension and in fatigue at voom temperature. Rod specimens failed in tension by necking, with axial cracks attributed to voids elongated in the extrusion direction. Fatigue specimens failed in shear. Thin-film electron microscopy showed that the subgrain structure of TD-Nickel was very stable, and that particle-matrix detachment was very difficult, in tension and fatigue. TD-Nickel softened slightly during fatigue but had a high fatigue ratio (0.5at 10' cycles). Fractography suggested that Stage I fatigue crack propagation is greatly extended in TD-Nickel. Td-NICKEL* is a dispersion of 2 pct by volume of thoria (ThO2) in nickel, produced by powder-metallurgical methods including compaction, sintering, and extrusion. The spherical thoria particles, which may have a mean diameter of a few hundred angstroms, are dispersed with a mean planar spacing of a few thousand angstroms. By a combination of cold working and annealing, a subgrain or cell structure of dislocations intimately associated with the dispersion can be produced.' This gives the material useful tensile properties which are extremely resistant to exposure to high temperatures.'-= At the same time, the material shows considerable ductility.3'4 At the beginning of the present work, it was considered of great interest to investigate the mechanical stability of TD-Nickel under conditions of fatigue. On the one hand, materials which derive strength from a cold-worked structure are unstable in that they are susceptible to fatigue softening: in addition, the presence of discontinuities such as the particle-matrix interfaces might be expected to assist in the initiation and propagation of fatigue cracks, in that they may provide local concentrations of internal stress and sites for the initiation of voids." On the other hand, the substantial ductility of TD-Nickel suggests that if it obeys Coffin's relation8 (or the more refined form proposed by Manson9) it should have good fatigue resistance. The initial purpose of this investigation was to assess the importance of these factors. Also, relatively little fundamental work has been done on the mechanism of fatigue in dispersion-strengthened materials. Work on overaged A1-4 pct CU10-12 revealed a very large Bauschinger effect indicative of internal stresses at the particles, and very great fatigue hardening1' presumably due to the multiple slip stimulated by these internal stresses, followed by softening which was initially due to softening in the matrix, but later might have arisen from cracking at the particle-matrix interfaces. The study of overaged Al-4 pct Cu could not settle this latter point by the electron microscopy of thin films, since the dispersion is too coarse. A previous study of the fatigue of internally oxidized copper13 was complicated by inter granular failure, attributed to oxide particles at grain bouhdaries; internal oxidation of single crystals, however, improved their fatigue properties.'3 Investigations of SAP (sintered aluminum powder) are complicated by the complex particle shapes, and the possibility of continuous internal oxide films.14 It was hoped to avoid these difficulties with TD-Nickel, which had the further advantages that it was commercially available and suitable for study by the thin-film technique. 1) MATERIALS AND EXPERIMENTAL PROCEDURE TD-Nickel was purchased from the Driver-Harris Co. as 3/9-in.-diam rod which had been extruded, swaged, and "stress-relieved" (normally at 1010°C for 1 hr). Continuous-radius fatigue specimens with a minimum diameter of -0.1 in. were ground to shape and electropolished in 40 pct phosphoric, 35 pct sul-furic, 25 pct water at 25oC, with a stainless-steel cathode, at -6 v. Fatigue tests were carried out at room temperature with a Sonntag SF-1-U machine operating in push-pull at 1800 cycles per min, and in an Instron TT-C-L modified for reversed stressing at 26 cycles per min as described elsewhere.10 Round tensile specimens were ground with 0.85-in. gage lengths of 0.135 in, diam, electropolished, and tested in a Tinius Olsen hydraulic machine. The surfaces of fatigue specimens were examined with a Reichert metallograph. Discs for electron microscopy with a Siemens Elmiskop I were spark-cut 0.01 in. thick with a modified Servomet 11 employing a tool of moving molybdenum wire, cleaned in 50 pct acetic, 30 pct nitric, 10 pct phosphoric, and 10pctsul-furic at 85oC, and thinned by the window method in the electropolishing solution at -20°C and -6 v. Two-stage replicas (parlodion, then Pt-50 pct C self-shadowed at 40 deg) were taken from fatigue fracture surfaces for electron microscopy. Plane sections parallel to the specimen axis and containing the direction of fatigue crack propagation were polished, etched with Carapella's reagent, and examined optically. Transmission Laue X-ray photographs of as-received material electropolished to a point were used to determine preferred orientation. 2) RESULTS 2.1) The Structure of As-Received Material. Grains -1 µ diam and elongated 20 to 30 u in the direction of the rod axis were observed, With' elongated "intergran-ular" voids (-4 p diam and -90 µ long and identified as such using longitudinal and transverse sections and

Jan 1, 1968

By M. F. Trice

PYROPHYLLITE is a hydrous aluminum silicate (Al2Si4O10(OH)2)1 that occurs in both the foliated and the massive forms. The foliated variety resembles talc in that it has a greasy feel, a pearly luster, perfect basal cleavage, and usually is white, although in some deposits apple green, gray, brown, russet, and nearly black specimens may be found. The massive deposits of pyrophyllite yield pearl gray to light tan aggregates, some of which are so friable that they may be crushed with the hands into a fine gritty powder. Frequently specimens of the massive variety are studded with crystals of radial structure. The mineral has a specific gravity of about 2.7 and a hardness of 1 on Mohs' scale.1 The chemical composition of commercial pyrophyllite reflects the mineralogy of the deposits, which, according to Stuckey,2 contain pyro-phyllite and quartz, together with chloritoid, sericite, and a few other minerals of negligible importance. The latter, he says, "are noticed in but small quantities to the extent they might occur as accessory constitu-ents of an igneous rock or as products of regional metamorphism or weathering. . . . Quartz is abundant everywhere except in the very best grades of pyrophyllite." Analyses of specimens from several deposits are listed in Table 1, showing that the silica content varies from 57 to 73 per cent and the alumina from 22 to 33 per cent. Oxides of iron and the alkaline metals are collectively present, with one exception, to an extent of about 1 to 1.5 per cent.

Jan 1, 1940

Industrial minerals enjoyed a fairly successful year in 1978, despite the sluggish economy, inflation, and environmental restrictions. A glance at US Bureau of Mines statistics shows that, in general, production of industrial minerals increased from + 1% (salt) to as much as 26% (sulfur, other than Frasch or recovered). A few industrial minerals showed a decline; fluorspar production, for example, registered a 23% decrease in 1978 from 1977 due to the closing of three domestic mines. Bromine, natural sodium sulfate, Frasch sulfur, and vermiculite also had production decreases of 2-6% in 1978.

Jan 5, 1979

By R. W. Raymond

This name is applied to the present mining law, as enacted in 1872 and since, to indicate its leading characteristic—in which it differs from all previous mining laws of this or any other country. The earlier act, passed in 1866, was practically the first attempt of Congress to deal with the question of mining titles upon the public domain. It was framed after nearly twenty years of acquiescence on the part of the Government in the self-constituted tribunals, officials, rules, and customs of the mining districts. In its recognition of these, and in several other particulars, the act of 1866 was open to serious criticisms. It is the purpose of this paper, not to trace the history of legislation on this subject, or show in detail what were the faults of the earlier law, but rather, by a discussion of certain aspects of the present law, to point out how great a revoluition it has effected in the rights of mining locators, and to indicate some of the difficulties attending its application. In the attempt to correct the vagueness of the act of 1866 an entirely new elernent was introduced into the law, bringing with it a new set of difficulties. Under the act of 1866 and the miners' customs which it followed, the lode was the thing claimed and subsequently acquired by patent. And the claim to a given number of feet on the longitudinal course of the lode was rooted in 'a discovery of any part of the lode in any part of the claim. ("Extensions" could in many districts—perhaps universally—be located and claimed on the strength of the discovery in the principal claim to which they referred; but this is a point not essential to the present discussion.) It was not necessary to find the outcrop or the upper edge of a lode in order to lay a valid location upon it. An explorer, sinking a shaft and intersecting a lode not already discovered and claimed by another, could claim by that discovery the number of feet along that lode which the local laws might permit (not exceeding the maximum set by the United States statute) whether his sur-

Jan 1, 1884

By Homer Turner

THE nature and comparative features of anthracite and bituminous coals have been discussed by the writer in two previous papers.1 Although this paper is offered as a further contribution to the subject, it seems desirable at the outset to repeat some of the descriptive matter of the early works in order to show the actual connection between various constituents of both coals and the new photomicrographs and other physical and chemical properties.

Jan 1, 1929

By Eugene F. Poncelet

GLASS squares compressed on edge by steel jaws in poor contact with them developed jagged "partial-contact" cracks caused by the formation of local tensile stresses. Compressed by steel jaws in perfect contact, they developed smooth "release cracks" during release of the pressure, caused by the formation of local tensile stresses during the release of the pressure. All these cracks were parallel to the pressure. A Microflash photograph of a disintegrating specimen under sufficient pressure reveals a network of fractures roughly normal to each other, also "release cracks" and a disintegration cloud. The Griffith theory is amended to account for the formation of a first crack. A new theory, based on the theory of thermal agitation and wave propagation, is proposed to account for the progress, velocity and forking of cracks. The network of fractures is shown to have been caused by reflection at a free boundary of pressure pulses emanating from a first crack. Postulating equal distribution of energy in the pulses emitted on either side by a crack in particles, the smaller fragments are shown to continue fracturing preferentially while some of the coarser fragments remain as residual pieces. As comminution of the smaller fragments proceeds, the solid is reduced to a collection of residual particles of smaller and smaller sizes, accounting for the disintegration cloud. EXPERIMENTAL PROCEDURE Apparatus A crushing device was built, consisting of a steel frame and two polished, hardened steel jaws to crush plate-glass samples. This device was placed between the plates of a hydraulic press (Fig. I). For centering the pressure, the upper jaw was guided vertically and provided with a rounded top. Later it was replaced by a steel jaw ground out of a 2 1/2-in. steel ball, the lower surface being ground to an optical flat (Fig. 2). Four rollers were used to eliminate side thrust. Screws and centering blocks served to center the specimen in the crushing device. Hard steel shims placed under the shoulder of the upper jaw limited the "follow through" of the jaw after failure of the specimen. Stress distribution was first examined with a polariscope mounted on an optical bench, using monochromatic light. It was found convenient to mount polaroid, quarter wave and monochromatic plates directly on the device itself. A Microflash unit* was used as light source for the photographs. A gold-paint pattern was fused on the plate-glass specimens and connected into the spark-

Jan 1, 1944

By W. G. Matteson

The Gulf Coastal plain of the southern United States is that area bordering for a large part, the Gulf of Mexico and extending inland and northward to the main interior highland region. It is more or less V-shaped and includes the States of Florida, extreme southern Alabama, all .of Mississippi and Louisiana, the eastern and southern half of Arkansas, and the eastern, southeastern, and southern portions of Texas. While the contents of this paper apply to. the Gulf Coastal plain in general, they are intended to refer more specifically to that portion of the plain included between the 90th and 97th meridians, and the 29th and 33d parallels, an area that may be described geographically as comprising western Mississippi, all of Louisiana, part of eastern and all of south-eastern Texas. It is within this area that numerous and prolific oil pools have been developed during the last 17 years.

Jan 2, 1918

By A. W. McReynolds

One characteristic of plastic deformation which distinguishes it from elastic strain is the essential inhomo-geneity of plastic strains. Elastic strain varies continuously through a material, and average relative displacements of initially adjacent atoms are only small fractions of their initial spacing, (strains of the order of 0.01 or less). On the other hand, plastic flow corresponds to the appearance of discontinuities in strain of the lattice, such as dislocations or slip bands, where local strain, on an atomic scale, is several orders of magnitude higher. These discontinuities are visible on a microscopic scale as the familiar slip lines (Fig 1). In spite of this obvious microscopic inhomogeneity, however, macroscopic measurements almost invariably show a smooth curve of stress vs. strain (Fig 2b) even if measurements of linear strains be made to an accuracy of one part in 107. This macroscopic homogeneity of strain indicates that the discontinuities in strain on slip planes occur in increments too small or too slow to be recorded individually, and further that they occur sufficiently independent of one another so that the small increments add at random to a smooth stress-strain curve. The present paper describes observations of plastic strain in aluminum of commercial purity and in high purity Al-Cu alloys, where there exists a strong coupling between slip in various regions of the specimen such that once initiated it spreads rapidly through a large volume. The total effect is that of relatively large, rapid, and regularly spaced steps of strain followed by periods of only elastic strain. Fig 2a illustrates the type of "stair-step" stress-strain curve which results. The properties of this cooperative slip phenomenon will be described further in the section on results: in par- ticular it will be shown that each step corresponds to the propagation of a wave of plastic deformation through the specimen. Some interpretations of the mechanism by which it occurs will be made in the following section. Although the type of plastic wave phenomena to be described has not previously been reported, there are numerous cases of related effects in the plastic yielding of metals: YIELD POINT PHENOMENA The most familiar of such effects is the "yield point" observed in low carbon steels, brass, duralurninum, and the like. It consists in the sudden termination of the elastic portion of the stress-strain curve by a large plastic strain. Since the usual tensile machine is such that yielding of the specimen relieves the load, the resulting curve is as shown in Fig 3. As the strain continues, deformation occurs at a lower stress for some time, then follows a rising curve, but with no further sudden yielding. This effect has been observed in brass by Sachs and Shojil and later by many others. Edwards, Phillips and Jones2 made extensive studies of the effect in steel, and of the role of various alloying elements. Although there seems to be fairly clear evidence that the yield point is caused by a hardening of the material by precipitation of impurities, no satisfactory explanation for the sudden yielding has been given. Winlock and Leiter3 have shown that the strain. level of the upper yield point depends strongly on the rate of loading, the yield point increasing by almost a fac- tor of two as the strain rate goes from 0.002 in. per in. per min. to 4.4 in. per in. per min. This effect would seem to imply an incubation period before yielding is initiated at a certain stress. On the other hand, by going to very slow loading rates, Edwards, Phillips and Jones2 showed that the yield point does not become lower and eventually disappear as might be expected, but, on the contrary, begins to rise at loading rates below about 25 Ib per in. per min. becoming much higher than at rapid loading rates. STRAIN AGING If, instead of continuing straining of a specimen after occurrence of a yield point, the load is removed and the specimen aged, resumption of the test results in occurrence of another yield point as shown by the dotted curve of Fig 3. The new yield stress is generally higher than the previous maximum applied stress. This hardening of the material by straining and subsequent aging is undoubtedly related to quench age-hardening resulting from the aging of a specimen quenched from high temperature. Since neither effect is observed in pure metals, it is generally accepted that quench-aging in all cases is the result of hardening by precipitation of a supersaturated alloying element, and that strain-aging is probably a similar precipitation, accelerated by disruptions of the lattice by previous strain. Pfeil4 has shown that strain-aging does not occur in iron from which all of the carbon has been removed, but that only a very small carbon content, around 0.003 pct, is necessary to cause strain-aging. In accord with this observation is recent work by Dijkstra5 in this laboratory showing that the solubility limit of carbon in iron is extremely low, less than 0.001 pct at 400°C. Edwards, Phillips and Jones2 have shown that the strain-aging effect is also removed by the addition of small quantities of elements such as Mo, Mn, Ti, and the like, which readily form carbides. Their results demonstrate the

Jan 1, 1950

By Frank Harwood Riddle

Products made from the ores of the sillimanite group, and synthetic substitutes for them, have unique properties, and service tests prove that they are playing, and will continue to play, a major part in improvements in metallurgical processes. Also, they are examples of how comparatively useless, rare, or "museum" minerals have been made available in commercial quantities. Until research developed uses for them, the minerals had been observed only in small, scattered masses, or crystals. Improvements in ceramic processes and compositions have come about very gradually. In the last 10 or 15 years, several outstanding developments have been made. Of greatest interest to the mining and metallurgical engineers are those affecting the composition, necessitating the mining of new minerals, and improvements in ceramic products used in metallurgical processes. Sillimanite and Mullite Sillimanite (Al2O3.SiO2), then known as Fibrolite, according to Dana,' was first reported in 1792. In 1796, cyanite (Al2O3.SiO2) was first described.2 In 1873, Behrens published results of his microscopic study8 of porcelain. He showed that it contained what appeared to be crystals, which dissolved less readily than quartz and glass in hydrofluoric acid. Hussak4 described the presence of needlelike crystals as occurring in some instances in small amounts in certain porcelains. In 1908, Plenske and Zoellner both studied porcelain structure.5 Plenske observed that "sillimanite" might be present in masses of exceedingly minute grains which apparently were amorphous. Zoellner advanced the theory that the needlelike crystals were formed by a molecular change in the clay,

Jan 1, 1932

By B. C. Burgess

IN the first edition of this volume,44 feldspar was introduced as "the I commonest mineral of the crystalline rocks," usually in small grains associated with other minerals and commercially produced only from pegrnatites. Now other crystalline rocks, such as alaskites and granites, have become present or potential sources of feldspar. In addition, feldspar has encountered very vigorous competition from such substitutes as nepheline syenite and aplite. COMPOSITION AND PROPERTIES The feldspars form a group of which the principal species are orthoclase, microcline, albite, and anorthite. These are aluminum silicates of potassium, sodium and calcium. There are also a barium feldspar, celsian, and barium orthoclase feldspar, hyalophane, rarely found and of no commercial importance. None of the minerals in the feldspar group are found pure or nearly pure. The potash feldspars, orthoclase and microcline, nearly always contain some albite (soda microcline, an- orthoclase); the soda feldspars usually contain some anorthite (lime feldspar). There is a series of soda-lime feldspars known as plagioclase in which the albite and anorthite molecules replace each other in varying proportions from albite through oligoclase, andesine, labradorite, and bytownite to anorthite. Theoretical chemical composition of the principal feldspars is given in Table 1. The Whiteware Division of the American Ceramic Society sub- mitted a list of definitions of ceramic terms, in April 1947, for use in technical literature. For feldspar it gives: "A group of igneous minerals consisting chiefly of the aluminum silicates of potash, soda and lime, in which one base generally predominates." Commercial feldspars are intergrowths of at least two species of feldspar, which occur associated with one or more accessory minerals such as quartz, muscovite, biotite, garnet and tourmaline as well as with small but varying proportions of the decomposition product, kaolinite. An intergrowth of quartz and feldspar frequently contains

Jan 1, 1949

By E. T. Turkdogan

This paper deals with an analysis of the conditions leading to the formation of blowholes and surface and subsurface defects in cast low-carbon steels. The theoretical analysis of the problem is based on the concept of the occurrence of deoxidation reactions during cooling of liquid steel and during its solidification. The reaction equilibrium data are given on deoxidation of steel by carbon, silicon, and manganese. The details of the calculations are given on the simultaneous deoxidation of steel by silico-manganese additions to produce a desired level of deoxidation at certain residual concentrations. Based on an idealized model, an attempt is made to calculate the enrichment of solutes in the solidifying liquid entrapped within the interdendritic cells which are known to be less than 200 µ thick. Formulae are derived for the calculation of the change in the residual oxygen content of the enriched liquid steel, controlled by Si/Mn deoxidation. It is shown that for every particular initial silicon, manganese, and oxygen concentration in steel (as residuals in liquid solution at the beginning of solidification) there is a particular carbon concentration below which carbon monoxide, leading to blowholes or pinholes, is not expected to form. There are a number of independent variables which have a decisive influence on the formation of blowholes. For example, it is shown that the position of the curve depicting the critical relation between initial silicon and carbon content for suppression of the evolution of carbon monoxide) can be shifted to lower silicon or higher carbon levels by: increasing manganese content; decreasing oxygen, hydrogen, or nitrogen content; or increasing external pressure on the solidifying mass. FOR the production of sound castings it is essential to prevent the formation of interdendritic worm-holes or pinholes brought about by gas evolution during solidification. Another major problem encountered in solidification of ingots is the formation of surface defects. These problems are thought to be closely associated with the deoxidation reaction occurring in liquid steel during cooling and subsequent solidification. As the liquid becomes richer in impurities during dendritic solidification of steel, a series of reactions may occur in the liquid phase trapped within the branches of growing dendrite platelets. Because of the strong interaction between dissolved oxygen and impurities in liquid steel, the reactions most likely to occur are of the deoxidation type. However, inherent to the extreme complexity of the problem in question, numerous simplifying assump-

Jan 1, 1965

By G. Willard Quick, John R. Freeman

Jan 1, 1930

By J. C. Bradbury

The year of the Centennial is upon us. Not only is AIME marking its 100th birthday, but the cement industry is also celebrating 100 years of activity (see article by Roy Grancher, page 48). Fort Dodge, Iowa, and gypsum also tried to get into the act but missed by one year. Frank Apple-yard's gypsum article (page 53) informs us that the Fort Dodge area has been producing gypsum continuously for 99 years. That would seem to make AIME and the industrial minerals doddering oldsters. Not so-our Institute shows more energy than ever, and the word for industrial minerals is growth. These are the mineral resources of the future, the raw materials for the abundant life to come

Jan 1, 1971

By H. A. Wriedt

Zinc-vapor pressures in equilibrium with bcc solutions of zinc and iron at 703.5", 757", 793", and 900°C were measured by an isopiestic method. Thermody-na?nic properties of zinc in these solutions were derived directly and those of iron with a Gibbs-Duhem integration. Zirzc and iron exhibit large, positive, and moderately temperature-sensitive deviations from ideality. Excess enthalpies and Gibbs energies are positive in the ranges studied. It has been establzshed in relating published phase equilibria to the Gibbs energies of forming solid solutions that positive departures from ideality also exist in the fcc solutions. Tlze stability, as defined by Darken, of the bcc solutions is small but positive at 703.5"C. Its decrease with decreasing temperature indicates that a miscibility gap may exist in the stable or metastable bcc solutions at lower temperatures. The changes of thertnodynanlic properties relatable to changes in magnetic state are minor compared to other changes due to alloying. The accuracy with which the relation between lattice parameter and composition of the bcc solutions is known has been improved. Zinc increases the lattice parameter of a iron by O.ZOZA per unit atom action zinc to at least NZn = 0.25. TO our knowledge, only Ciganl has previously investigated thermodynamic properties of the bcc solutions of the Fe-Zn system. He measured zinc-vapor pressures in the temperature range from about 320" to 360°C by an effusion technique. We have measured the vapor pressures of zinc in equilibrium with bcc solutions of zinc and iron at 703.5", 757", 793", and 900°C by an isopiestic technique. This investigation and the pursuant thermodynamic computations are part of a program for studying several properties of these solid solutions. In the appendix we report a remeasurement of the relation at room temperature between the lattice parameter and zinc content. Related work not reported herein embraces measuring the diffusivity2 of zinc in ferrite at 700" to 900°C and the Curie point temperature3 as functions of composition. EXPERIMENTAL METHOD AND APPARATUS Purified iron at a series of constant temperatures was saturated with zinc at a series of constant zinc-vapor pressures, the range of conditions being so limited that the equilibrated solid solutions were ferri-tic. The equilibration was conducted in long capsules, Fig. 1, that had been evacuated, gettered with titanium, and sealed. The purified iron, part of a vacuum-melted ingot of electrolytic-iron stock (Glidden Co. 1044-grade), had the impurity contents listed in Table I. It was used in the form of millings about 0.001 in. thick. A zinc of 99.999 pct purity (United Mineral and Chemical Corp.) and later one of 99.9999 pct purity (Cominco Products, Inc.) were used, with no observed difference in results. Sufficient zinc was placed in the capsule (separate from the iron and kept at a different temperature) to supply the vapor phase and the iron alloy, while leaving a pool of pure liquid zinc throughout the run. The imposed temperature of the residual zinc pool fixed the vapor pressure of zinc throughout the capsule; condensation was avoided at other locations by making this the lowest temperature in the capsule. Two common complications of nonisothermal systems were, we believe, effectively absent from ours: first, molecular species other than monatomic have no appreciable concentration in zinc vapor at 700" to 900~~: second, the development of zinc-pressure differentials in the capsules was suppressed by use of relatively large-diameter tubing and the absence of diluents in the zinc vapor other than desorbed impurities. The specimens and zinc pool were located at two isothermal zones (each ranging within 1°C over several inches) of a wire-wound, 37-in.-long vertical-tube furnace. The required temperature distribution was achieved by external adjustment of the currents in three electrically isolated windings. The temperatures of the isothermal zones were controlled independently by ther-

Jan 1, 1968

By A. S. Yue, A. G. Guy

A study was made of the effects of a prolonged flux of zinc atoms through the a solid solution of zinc in copper. The experimental arrangement consisted essentially of a copper disk about 0.01 in. thick, at one of whose surfaces a gaseous atmosphere containing zinc atoms was maintained, and at the other surface a gaseous atmosphere with a minimum of zinc atoms was maintained. During prolonged theothersurfaceexposure at high temperatures the zinc content of the copper disk gradually built up to the steady-state concentration distribution and then remained at this value. The concentration-distribution curves for various conditions were determined by chemical analyses. The results showed that the condition of steady-state diffusion was achieved. The diffusion coefficients calculated from the experimental data, although not of high precision, agreed with the values obtained by other workers using unsteady-state methods. Relatively slight porosity developed in the specimens in the course of diffusion. A LTHOUGH most diffusion studies have been made under unsteady-state conditions, it is known' that the steady-state method is often superior with respect to the directness and accuracy of interpretation of the data. Steady-state diffusion of gases through metal diaphragms is well known. Also, Harris' and Smith" have used the steady-state method in studying the diffusion of carbon in aus-tenite. The accepted mechanism in this system involves the motion of the interstitial carbon atoms in the rigid framework of the lattice of iron atoms. Thus, there is little difficulty in visualizing the steady flow of the small carbon atoms through the austenite. The situation in substitutional diffusion is quite different. Here the atoms are comparable in size, and it is not evident how a steady flow of one of the atoms through the solid solution might be achieved. At the time the present research was started, it was known that a previous exploratory attempt to produce steady-state diffusion in a substitutional alloy, the Au-Ag system,' had been unsuccessful and had indicated that perhaps there were basic difficulties that could not be ovei-come. Therefore, the present research began as a study of the effect of a prolonged flux of metal atoms through a substitutional solid solution. Eventua.lly, it was possible to produce actual steady-state diffusion in the system chosen for study, the a Cu-Zn alloys. Experimental Procedure The aim in the experiments was to maintain a high zinc content, about 30 pet, at one surface of a copper sheet, and to maintain a low zinc content, near 0 pet, at the opposite surface. The zinc would then diffuse into and through the copper, first building up to the steady-state concentration distribution and then maintaining this distribution. The three types of specimens that were used are shown in Fig. 1. In type A specimens the copper disk through which diffusion occurred was welded to the top of a cylindrical molybdenum tube, the bottom of which also was sealed by welding. At the diffusion temperature the brass chips in the molybdenum container were the source of the zinc vapor which maintained the lower surface of the copper disk at 30 pet Zn. The upper surface was maintained at 0 pet Zn by the vacuum in which type A, and also type B, specimens were diffused. Since the molybdenum container was impervious to zinc vapor, it was intended that the only path of escape for the vapor from the brass chips would be through the thin copper diffusion disk. However, it was found that small leaks often developed at the welded joints during the diffusion treatment, and in most specimens some of the zinc was lost in this manner. Although even small losses of this kind were a serious handicap in attempting to determine the flux through the disk, they did not prevent the maintenance of satisfactory boundary conditions for the attainment of the steady-state condition. Type B specimens differed from type A in having a weight of about 300 g supported on the copper disk by 15 to 20 short quartz rods. This change was made when it was observed that the copper disk was being bowed upward by the difference in the pressures acting on its two surfaces. Since the grain-boundary cracking which occurred in the bowed specimens could be attributed largely to the accompanying creep,3 it was desirable to minimize this effect. The counterweight was effective in significantly decreasing both bowing of the disk and cracking at grain boundaries. Type C specimens differed considerably from the others in that the low-zinc atmosphere at one sur-

Jan 1, 1959

By W. G. Matteson

I. Introduction...................................................... 436 (a) Extent of the Gulf Coastal Plain. (b) History of Important Gulf Coast Oil Pools. 1. Corsicans, Tex. 2. Spindletop, Tex. 3. Sour Lake, Tex. 4. Jennings, La. 5. Saratoga, Tex. 6. Batson, Tex. 7. Humble, Tex. 8. Caddo, La. 9. Vinton, La. 10. Naborton, La. 11. Red River, La. 12. Edgerly, La. 13. Goose Creek, Tex. 14. Damon Mound, Tex. 15. New Iberia, La. (c) Favorable Features of the Gulf Coast Pools. 11. General Topography and Physiography of the Gulf Coastal Plain.....440 111. General Stratigraphy of the Gulf Coastal Plain West of the 90th Meridian......................................................441 IV. Structural Types and their Characteristics.........................446 (a) hnticlinal Structure. (b) Structure of Salt Domes. 1. Domes of the Coast Prairie. 2. Domes of the Wold Region. 3. Recapitulation of Dome Structural Characteristics. V. Methods of Surveying and Prospecting............................. 454 VI. The Development of Salt Domes................- .................458 VII. Origin of Salt Domes...............4.............................461 (a) The Volcanic-plug Theory of Hager. (b) The Contemporaneous Sedimentation Theory of Norton. (c) The Theory of Upward Pressure Exerted by the Force of Growing Crystals, as Developed by Harris. VIII. Source of the Oil in the Gulf Coastal Pools.........................465 IX. Petrolific Value of the Salt Domes of the Wold Region..............467 X. Future Outlook.................................................. 467

Jan 1, 1918

By George J. Clark

One of the major problems of operation in the anthracite industry is the disposal and handling of refuse—not because of its complexity but because of the quantity and type of material involved. It is the purpose of this paper to describe the kinds of refuse, methods of disposal, quantities of material to be handled and equipment used, together with present day application at specific operations in the Northern, Eastern Middle, Western Middle and Southern anthracite fields. For the purpose of this paper, refuse is considered to be any material that has no present or foreseeable future value and that must be handled and disposed of in the process of mining and preparing anthracite for market. Included in this classification are tunnel rock, mine rock, cleaner plant refuse, breaker refuse, old timber, ashes and silt. Disposal Methods Old timber is disposed of either by burning or by depositing on the refuse bank. Burning is preferred because timber on the refuse bank is a potential fire hazard. Ashes are deposited on a separate bank, mixed with other refuse, or flushed into old mine workings. In many places, the latter practice has caused considerable difficulty in preparation of coal mined from these areas. In depositing ashes on the surface, it is wise to refrain from mixing them with material containing coal as such contamination may prevent reclamation of the coal in future years. Tunnel work, mine rock, cleaner plant and breaker refuse compose the bulk of the material to be disposed of and handled, and are referred to collectively as "refuse" in this paper. Waste material in or adjacent to the coal beds may be removed at the working face wherever possible. This can be done in flat or lightly pitching beds, and in the Northern field represents a sizable percentage of this type of refuse handled. In the other three coal fields, this method of disposal cannot often be used. Refuse not removed at the working face is taken to the surface and generally is deposited on banks; occasionally it is crushed and flushed into old mine workings. Breaker refuse often is used for constructing berms for silt-retention basins. Disposal Problems The problem of handling refuse is different for each operation, owing to topographical conditions, quantity of material to be handled, anticipated requirements and types of equipment in use elsewhere at the operation. Preparation plants with limited refuse-disposal areas, excessive grades to reach the required elevation and long hauls to disposal areas not readily accessible require the selection of equipment to best meet the conditions. The quantity of refuse to be handled from a given amount of raw material varies considerably throughout the four fields. In mine coal, this varies from a low

Jan 1, 1949

By W. L. Saunders

IMPORTANCE OF ROCK DRILLING. IT has been estimated that the value of the mineral products of the United States is about $2,000,000,000 a year; that about $25,000,000 is expended. annually for explosives and that about double this sum is paid in wages where blasting is done. The value of the mineral products does not adequately express the importance of the industry involved in the excavation of rock and ore because of the enormous sums of money expended in tunnel driving, in quarries, and in open-cut excavation generally. We know that the Catskill Aqueduct in the neighborhood of New York, which is now nearing completion, has cost some $165,000,000 and that about one-third of this may be rated as rock excavation. These illustrations are given in order to call attention to the great importance of an industry the extension and development of which in our industrial life depend so much upon the economics of rock drilling. Reference has been made to the new Catskill Aqueduct. There are three aqueducts leading into New York, each built at periods separated by some 20 years of time. 'The first one, known as the Old Aqueduct, conveys the waters of the Croton river to New York City in a manner which reminds one of the old Roman aqueducts, the ruins of which are still in evidence. The engineers who laid out these old conduits sought to direct their lines around the hills and into the valleys, at all times avoiding the rock. When it was necessary to cross a river or a deep ravine, a bridge or causeway was constructed. High Bridge, over the Harlem river, is an arched masonry viaduct differing in no essential features from the aqueducts of the Romans. When the second Croton Aqueduct was built, about the year 1890, the art of drilling rock had been so far perfected, and the use of explosives, through the invention of dynamite, had become ,so general, that this waterway was planned and executed on straight lines, following rather than avoiding the rock. The second Croton Aqueduct is a tunnel through rock, about 32 miles in length; material gneiss, almost as hard as granite. Its construction was made practicable by sinking

Jan 9, 1913

By Manuel Eissler

The material presented in this paper is an abstract of a thesis submitted by the writer to the faculty of the Massachusetts Institute of Technology, as part requirement for the degree of Master of Science. The investigation was undertaken at the suggestion of Prof. H. 0. Hofman, and it was conducted, under his direction, in the laboratories of the Mining Department of the Institute. The purpose of the work was, first, to study some of the reactions that have been considered as a part of the mechanism of the chloridiz-ing roast, and second, to study the conditions under which nickel oxide and copper oxide may be chloridized. While the production of chlorine gas by various reactions during the chloridizing roast may not be primarily useful in the chloridation of metal oxides and compounds, it nevertheless serves a useful purpose in preventing the dissociation and decomposition of chlorides once they have been formed; for example, the dissociation of cupric chloride into cuprous chloride and chlorine. Therefore it was thought that a study of some chlorine-producing reactions would prove of interest, and the first series of experiments dealt with this phase of the subject. he object of the latter part of the work was to show the possibility of treating heavy sulphide ores, such as those of Sudbury, Ontario, containing much iron and small amounts of copper and nickel, by chloridizing and removing the copper, leaving an iron-nickel oxide product suitable for smelting in the blast furnace for nickel-bearing pig iron. The chloridizing of the copper would, of course, be preceded by a roast for the removal of sulphur, the sulphur oxides being available for the manufacture of sulphuric acid, if under the local conditions this product would be of commercial value. Reactions of the Chloridizing Roast Reaction of Sodium Chloride, Sulphur Trioxide, and Oxygen.—The first reaction studied was that involving the production of chlorine

Jan 1, 1915

By J. S. Kirkaldy, D. H. Weichert, G. R. Purdy

Two-phase diffusion couples have been used to simulate the growth of proeutectoid ferrite in ternary Fe-C-Mn austenites. It has been shown, theoretically and expermentally, that the results fall into two classes: a high-super saturation class in which the major role of manganese additions is to influence the boundary conditions for carbon diffusion; and a low-supersaturation class in which the partition of manganese is required. In the latter case, a drastic inhibition of the reaction rate is to be expected. As an aid to the kinetic analysis, a portion of the iron-rich comer of the Fe-C-Mn constitution diagvam has been determined. The conclusions drawn from this work have a direct bearing on the kinetics of the grain boundary ferrite precipitation reaction and thus yield insight into the manner in which alloying elements can influence the rate of austenite-decomposition reactions. THE role of alloying elements in the austenite-decomposition reactions has provoked considerable interest, since it is apparent that an understanding of this phenomenon will yield insight into the harden-ability problem. In the present investigation, attention is focused upon the proeutectoid-ferrite transformation in the system Fe-C-Mn, and upon the manner in which manganese additions affect the growth rate of ferrite. When hypoeutectoid austenite is supersaturated, the ferrite first formed usually exhibits two distinct types of morphology. At low super saturations, grain boundary layers grow into the austenite grains with an approximately planar interface, and usually possess at least one incoherent phase boundary. At high supersaturations, Widmanstiitten plates appear, which bear an orientation relationship' to the parent austenite. In this case, there is a chance of partial lattice matching along the sides of the plates and an attendant semicoherent interface structure. Purdy and Kirkaldy2 have used a two-phase binary Fe-C diffusion couple to demonstrate that carbon volume diffusion controls the incoherent reaction, while Rouze and rube,' using thermionic-emission microscopy, have shown that the thickening of Widmanstatten ferrite plates is appreciably slower than expected for carbon-diffusion control. This suggests that the plates are bounded by partially coherent, low-mobility interfaces. The redistribution of alloying elements during transformation has been the object of studies by Aaronson4 and owmman,5 who have shown that no alloy partition occurs during ferrite precipitation in the systems Fe-C-Cr and Fe-C-Mo, respectively. More recently, Aaronson et al.6 have shown that some manganese partition occurs at low super-saturations in the system Fe-C-Mn, but that no partition occurs at higher super saturations. Pickle-simer et al.7 observed that no manganese partition occurred during the early stages of the pearlite transformation in a manganese steel, and concluded that volume diffusion of the alloying element is not the rate-deter mining factor. The diffusion coefficients pertinent to this investigation have been measured by Wells, Batz, and Mehl8 (carbon in austenite), R. P. smith9 (carbon in ferrite), Wells and Mehl 10 (manganese in austenite), and Kirkaldy and Purdy11 (diffusion of carbon on a manganese gradient in austenite). Kurdjumov 12 has shown that the diffusivity of substitutional elements in ternary austenites up-quenched from martensite may be greatly enhanced, due, apparently, to the presence of a persistent defect structure. The recent work of Krauss 19 showing high densities of tangled dislocations in reversed Fe-Ni martensite is in agreement with this conception. THEORETICAL Diffusion in ternary or higher-order systems may be described with the aid of Onsager's extenbion of Fick's first law,14 in which the flux of each of the n components is assumed to be a linear function of all concentration gradients:

Jan 1, 1964