By L. C. Uren, J. Domerco

That the diameter of a well through the oil-producing formation has an important influence on its rate of production is a principle accepted by many petroleum technologists. Knowledge of this principle extends back at least to the time when Slichter and King1 confirmed it in a study of the dynamics of flow of water through porous strata into wells. More recently, the senior author2 and his associates3 have produced qualitative experimental data confirming the principle as applied to drainage of expanding oil and gas mixtures, and suggesting that wells of large diameter, or wells having cavities about them within the reservoir rock, enjoy a material advantage in competition with wells of ordinary diameter. Apparently, however, no one has produced experimental data designed to indicate quantitatively the advantages that wells of large diameter possess in comparison with wells of normal diameter producing under comparable conditions. This paper reviews some preliminary experimental results of this kind, together with some conclusions and speculations based thereon, which further emphasize the importance of well diameter as a factor in determining the efficiency of oil recovery. Theoretical Aspects of Radial Flow of Fluids into Wells It is well understood that in a reservoir rock of uniform thickness and permeability oil and gas flow toward the wells along radial lines. The cross-section of the reservoir rock through which the fluids must move becomes ever smaller as the wall of the well is approached. The velocity of flow must therefore correspondingly increase, an effect that is accentuated by the rapid increase in volume of the fluid due to release

Jan 1, 1935

By T. M. Daulton, Chester F. Lee

The Atlin Mining District is in the northwest corner of the Province of British Columbia. Ruby Creek, where the operation to be described is situated, is 17 miles east of the town of Atlin and about 18 miles south of the south line of Yukon Territory (Fig. 1). Gold was discovered in the district in January, 1898, and the production to date from placer mines has been $4,518,000, according to the reports of the Minister of Mines for the province. Geology The essential points in the regional geology are given in the following paragraphs. Long erosion produced a plane-like surface slightly above sea level with a few peaks and ridges.' A gradual uplift followed and erosion increased, the streams cut deeper, the cuts so made being afterward increased by glaciation. The ice straightened and planed the slopes of the main valleys and widened and lowered their floors, in some cases flooring the valleys with silt, sand, gravel, and clay. As the glaciers rapidly retreated, lakes were formed. As to the origin of the gold, J. C. Gwillim says? "The Surprise granite has been carried northward toward Gladys Lake and Teslin, and the granite of the great plateau on the Taku trail was found in blocks on the opposite range across Hurricane River 10 miles north of its original position. Otherwise there is little evidence of far removed material, the boulders of the lake shore and creek beds being of local appearance. This appears to strengthen the opinion that the placer gold had its origin within the drainage basins where it is now found." In the gold-bearing creeks of the Atlin district there are two "runs"

Jan 1, 1917

By C. A. Wert, M. G. Coleman

The Zener relaxation in alloys in the a! solid-solution region of the Cu-Ni-Zn ternary system has bear investigated. Of the binary solid solutions that bound this region, Cu-Zn and Ni-Zn exhibit measurable Zener peaks whereas Cu-Ni does not. At constant atomic percent copper, the Peak height drops uni.forinly from the value in the Cu-ZTL binary to zero in CIA-Ali. The cariation of peak ternperatuve with composition is linear. At constant atomic percent zinc, the peak height in the ternary alloys goes through a large maximum as compared with the binary values. The temperature of these peaks varies smoothly with composition. The half-width of the peaks in the ter nary alloys, however, are much larger than those in the binaries. A large enhancement of the relaxation strength of the Zener relaxation in ternary Au-Ag-Zn alloys as compared to the relaxation strengths in Au-Zn and Ag-Zn binary alloys was observed by Firson and ert.' Since this effect was unexpected, the present study was devised to investigate whether enhancement of the Zener relaxation in ternary alloys is a general feature or is particular to the Au-Ag-Zn system. We have chosen the Cu-Ni-Zn alloy system for this investigation. Measurable Zener relaxations are observed in both the Cu-Zn and the Ni-Zn binary systems, but not in the Cu-Ni binary system. A large solid-solution region extends to large concentrations of zinc, making it possible to vary composition of the alloys over a wide range without crossing phase boundaries. EXPERIMENTAL PROCEDURE Two series of alloys were prepared. the first at constant atomic percent copper, the second at constant atomic percent zinc. The compositions of these alloys are shown by the circles in Fig. 1. The alloys were prepared by melting the individual components, each of which had previously been vacuum-melted, in an evacuated quartz capsule in an induction furnace at 1500 C. The capsules containing the molten alloys were quenched in water to reduce coring. Any individual melt which exceeded 0.001 pct weight loss was discarded. The ingots were swaged to a 50 pct reduction of area and annealed for 1 week in an evacuated quartz capsule to aid homogenization. The alloys were then

Jan 1, 1967

"Minerals in Transition" is the timely theme of this year's SME-AIME Fall Meeting and Exhibit, to be held September 10-12 at the Salt Palace, Salt Lake City, Utah. Approximately 2000 members and guests are expected to attend the meeting, which will include 117 technical papers, presented during 27 sessions. To complement the technical program, a record number of mining manufacturers and suppliers will be on hand to exhibit the latest in equipment innovation and professional services.

Jan 8, 1975

By John Griffen

HYDRAULIC classification as explained by Rittinger and others was largely restricted to conditions wherein the free-falling velocities of the particles were conceived as governing the separations effected (see chapter 9). The laws governing classification under free-falling conditions have been summarized by Chapman and Mott as follows:

Jan 1, 1943

By John W. Vanderwilt

The unpredictable behavior of ground movement and subsidence has complicated the problems that attend the extraction of large quantities of ore. Special studies, particularly relating to coal mining, have yielded such a voluminous literature and so many involved controversial theories that a partial review would be difficult. Limited space makes any kind of a review impractical. The features to be considered cover only a relatively small part of the broad problems of ground movement and subsidence, but it is believed that this small part is critical. The practical aspects are important, since they bear directly on safety of mine workings, on recovery of ore and on dilution of ore in block caving and related systems for extracting large quantities of rock. The ground movement to be described occurs outside the vertical boundaries of a caved block in the area that is commonly referred to as being in the "zone of draw." "Draw" is a term that originated in the subsidence problems related to coal mining, and it is defined by a line drawn from the margin of the area caved underground to the most distant fracture at surface on the same side of the caved area as shown in Fig. I.' A line thus drawn is called the cave line, and its angle with respect to the horizontal is the cave angle or angle of draw. It is understood that the line is taken normal to the limit of mining, and in a vertical plane. The prevailing theories as to draw and angle of draw assume that appreciable movement occurred along the cave line, which has been described as a fracture resulting from the shearing action brought about by the weight of the overlying load. Fig. 3 shows diagrammatically the mechanics of ground movement adjacent to an area of subsidence according to the prevailing theory of draw (A, from Royce2) and, for comparison, ground movement observed in the Climax mine (B). The text in Peele's Handbook2 referring to Fig. 2 does not state the meaning of the "original position of top of workable ore" in the rectangular space above "ore in place," and the arrows are not explained. However, this presentation is most concerned with the zones outside the rectangle. According to the prevailing theory, as shown at the extreme left under A, Fig. 2, the vertical tension cracks at surface change at a shallow depth to shear fractures forming the cave line, and it is assumed that appreciable movement takes place along the cave line toward and into the subsiding caved block. The mechanics of ground movement observed in the Climax mine, as shown under B, Fig. 2, does not accord with the prevailing theory, particularly as regards the cave angle and draw. The vertical tension cracks seen at surface die out at depths of 150 to 225 ft. and shear fractures do not develop. Movement is confined at surface to a mantle of rock 50 to roo ft.

Jan 1, 1949

By F. L. Ransome

The following paper aims to present in a much condensed form the salient results of a detailed geological study of the Bisbee quadrangle, Arizona, carried on during the latter part of the year 1902. It is essentially an abstract of the final official report which will shortly appear in the series of professional papers of the U. S. Geological Survey, accompanied by maps, sections and illustrations. I. Geography. The Bisbee quadrangle, which includes the Warren mining district, lies in Cochise county in the southeastern part of Arizona. It is inclosed between the meridians 109" 45' and 110" 00' and the parallels 31" 30' and 31" 201, the latter being locally the Mexican boundarg line. The area of the quadrangle is about 170 square miles, and includes the southeastern half of the Mule Mountains, one of the smaller of the isolated ranges characteristic of this part of Arizona. The Mule Mountains, while less markedly linear than the Dragoon, Huachuca, Chiricahua, and other neighboring ranges, have a general NW-SE. trend. They may be considered as extending from the old mining town of Tombstone to the Mexican border, a distance of about 30 miles. On the northwest they are separated by the broad, flat floor of Sulphur Spring Valley from the Chiricahua Range, and on the southeast by the similar broad valley of the Rio San Pedro from the Huachuca Range. The maximum width of the range is about 12 miles, and its greatest elevation attained by Mt. Ballard, west of Bisbee, is 7,400 ft. above sea-level. An index-map, showing the geographical position of the Bisbee quadrangle, is shown in Fig. 1. The town of Bisbee (Fig. 2), with an estimated population of 6,000, is crowded into a few narrow confluent ravines near the

Jan 1, 1904

THE strike of the coal miners began on April 1, as had been expected, the entire force of unionized miners-both anthracite and bituminous-going out and making this the most widespread strike of record. Up to the present writing there has been no serious inconvenience to industry in general, the accu-mulated stocks of coal being large and the non-union mines having continued to make a substantial production. However, the union labor leaders, having concentrated their efforts toward inducing the non-union miners to go out also, met with some measure of success in certain fields and created a shortage of coking coal, which caused iron makers to bank a few furnaces. The strike of textile workers in New England spread further. Here and there, throughout the country there were sporadic troubles with the builders. Rail-way labor was the subject of continued palavers, which did not get anywhere. On the whole the events of April were in line with the forecast that this would be a year of labor troubles. In domestic politics, the soldier bonus bill, having been passed by the House, went to committee consider-ation in the Senate. Public opposition to it manifestly waxed. On the floor of the Senate the tariff bill was under consideration and is drawing nigh to passage, without there being much consideration of its probable economic consequences. It is going to be a very high tariff and there is much in it that is equivalent to subsidizing small and normally unprofitable industries at the expense of the people as a whole. Abroad affairs were more quiet, superficially at least; than they were in March. In Egypt, India and South Africa things calmed, down, so far as we know, but in Ireland there was continued turmoil. The Irish, having won their freedom to the same degree as the Canadians, have entered upon violent quarrels among themselves, more over phrases than anything .else, so far as we can see. Lloyd George obtained a spectacular vote of confidence from Parliament and thus postponed, the exigency of a general election.

Jan 5, 1922

By K. L. Meissner

It is well known that the so-called pure aluminum contains noticeable amounts of impurities, chiefly iron and silicon, and many investigators have studied the forms in which these impurities exist. Hanson and Archbutt1 state that iron exists in aluminum as FeA13 and silicon as elementary Si. The solubility of FeA13 in solid aluminum is practically zero, or at least so small that the smallest trace of this compound is always visible as a separate constituent. Under the microscope an untrained eye can hardly distinguish, without etching, the two constituents FeA13 and Si, but they can be differentiated by suitable etching reagents. Anderson2 also found the same results. At the same time, Merica, Waltenberg, and Freeman3 found a constituent of unknown composition. They found a small thermal effect, at 610" C., on the cooling curves of aluminum with small amounts of iron and silicon. The intensity of this effect increased with increasing silicon content, until an effect occurred at 576" C. due to the eutectic between aluminum and silicon. The authors ascribed the effect at 610" C. to a compound, which they call "X constituent." It was thought to be a ternary compound containing iron and silicon and could be observed under the microscope as dark particles. Dix4 has published unetched photomicrographs of an aluminum with 0.51 per cent. iron, 0.99 per cent. silicon, and 0.32 per cent. copper that shows three constituents: the dark Si (black in the figure), the lighter FeA13, which appears in half tone and crystallizes in needles, and a constituent of the same color as FeAL3 but of different crystal form, often resembling Chinese script. This last constituent, Dix thought, is a compound of Fe and Si; not the compound FeSi but a compound containing a relatively small amount of silicon. Therefore an alloy of aluminum. iron, and silicon (the copper should not be regarded in the following considerations) must contain the following four constituents: Al, FeA13, Si, and a compound of Fe and Si. This, however, does not agree with the laws of chemical equilibrium.

Jan 1, 1926

By Dorsey Hager

The information given in the accompanying table is submitted as evidence confirming the application of the anticlinal theory and the value of geology in the Kansas and Oklahoma oil fields. The term anticline has been used to define a particular type of arched fold. The anticlinal theory of oil accumulation should, however, be broadened to include any structural fold of an arched type even if not a distinct anticline. A terrace may very properly come under the heading of the anticlinal theory of accumulation, as the folding is closely related to that of the anticline; in fact, in many cases is an arrested anticline, though not completely closed in all directions. Stratigraphic forms due to lensing or irregular cementation of the sands certainly cannot be considered to fall within the anticlinal theory, though the laws of accumulation may be similar. A dome is similar to an anticline and belongs to the same class. A dome is broader in proportion to its length than an anticline. Many anticlines undulate along their axes to form domes. The anticlinal theory in this discussion will then be applied to anticlines, domes and terraces. In the following list, the writer has tabulated the main oil fields of Oklahoma, and a few recently discovered fields in Kansas. The fields discovered within the past 4 years are listed with the date of their discovery. Under "How found," the writer puts "Wildcat" where a geologist has not been employed, "Geology" where it has been used, and "7" where there is doubt. In some places the geologists have claimed pools that may rightly belong to them, but their claims have been questioned, so that they belong in an unsettled category. Unless one has mapped all the old pools, it is not possible to say just how far they are dominated by structure, but from our own work, and from discussions with others, it is safe to venture that nearly all the "shallow-pool" districts, Nowata, Bartlesville, and the Eastern Osage, are controlled by structure; domes, noses, and terraces are the main structural features. The "shallow pools" of Kansas show the same relation. At Peru and at Sedan, domes are evident, though gas occurs high on the domes, and oil well down the flanks, leading some to believe

Jan 1, 1917

By J. R. Szedon, T. L. Chu, G. A. Gruber

Amorphous adherent filnzs of silicon dioxide have been deposited on silicon substrates by the oxidation of silane at temperatures ranging from 650 to 1050C. Various diluents (argon, nitrogen, hydrogen) were used to suppress the formation of SiO2 in the gas phase. Deposition rates of the oxide were determined over the temperature range in question as functions of' re-actant flow rates. Etch rate studies were used for a cursory comparison of structural properties of deposited and thermally grown oxides. From electrical evaluation of metal-insulator-silicon capacitors it was determined that the interface charge density of deposited films is similar go that of dry-oxygen-grown films in the 850° to 1050 C temperature range. Deposited films exhibit several ionic instability effects which differ in detail from those reported for thermal oxides. Stable passivating films of silicon nitride over deposited oxides appear to be practical for use in silicon planar device fabrication. Such films can be prepared under temperature conditions which have less effect on substrate impurity distributions than in the case of grown oxides. AMORPHOUS silicon dioxide (silica) is compatible with silicon in electrical properties and is the most widely used dielectric in silicon devices at present. Silica films can be prepared by the oxidation of silicon or deposited on silicon or other substrate surfaces by chemical reactions or vacuum techniques. The ability of thermally grown silicon dioxide films to passivate silicon surfaces forms one of the practical bases of the planar device technology. Properly produced and treated films of grown SiO 2 can have low densities of interface charge (-1 X 10" charges per sq cm) and can be stable as regards fast migrating ionic sgecies. 1 To maintain these properties, even with an otherwise hermetically sealed ambient, the Sia layers must be at least l000 A thick. Such thicknesses require oxidation in dry oxygen for periods of 7.8 hr at 900°C or 2 hr at 1000°C. Although oxidation in steam or wet oxygen can reduce these times to 17 and 5 min, the resulting oxides must be annealed to produce acceptable levels of interface charge., Oxidation or annealing involving moderate to high temperatures for extended periods of time can be undesirable. Under some conditions, there can be changes in the distribution of impurities within the underlying substrate. A chemical deposition technique using gaseous am-bients is particularly attractive and flexible for preparing oxide films. With a wide range of deposition rates available, films can be produced under condi- tions of time and temperature less detrimental to impurity distributions in the silicon than in the case of thermal oxidation. The pyrolysis of alkoxysilanes, the hydrolysis of silicon halides, and various modifications of these reactions are most commonly used for the deposition of silica films.3 Silica films obtained in this manner are likely to be contaminated by the by-products of the reaction, organic impurities, or hydrogen halides. The use of the oxidation of silane for the deposition process has been reported recently.4 The deposition of silica films on single-crystal silicon substrates by the oxidation of silane in a gas flow system has been studied in this work. The deposition variables studied were the crystallographic orientation of the substrate surface, the substrate temperature, and the nature of the diluent gas. The electrical charge behavior of Si-SiO2-A1 structures prepared under various conditions was investigated by capacitance-voltage (C-V) measurements of metal-insulator-semiconductor (MIS) capacitors. The experimental approaches and results are discussed in this paper. 1) DEPOSITION OF SILICA FILMS The overall reaction for the oxidation of silane is: The equilibrium constants of this reaction in the temperature range 500° to 1500°K, calculated from the JANAF thermochemical data,= are shown in Fig. 1. In addition to the large equilibrium constants, the oxidation of silane is also kinetically feasible at room temperature and above. However, the strong reactivity of silane toward oxygen tends to promote the nucleation of silica in the gas phase through homogeneous reactions, and the deposition of this silica on the substrate would yield nonadherent material. The formation of silica in the gas phase can be reduced by using low partial pressures of the reactants. Argon, hydrogen, and nitrogen were used as diluents in this work. 1.1) Experimental. The deposition of silica films by the oxidation of silane was carried out in a gas flow system using an apparatus shown schematically in Fig. 2. Appropriate flow meters and valves were used to control the flow of various reactants, i.e., argon, hydrogen, nitrogen, oxygen, and silane. Semiconductor-grade silane, argon of 99.999 pct minimum purity, oxygen of 99.95 pct minimum purity, and nitrogen of 99.997 pct minimum purity, all purchased from the Matheson Co., were used without further purification. In several instances, a silicon nitride film was deposited over the silica film. This was achieved by the nitridation of silane with ammonia using anhydrous ammonia of better than 99.99 pct purity supplied by the Matheson CO.' The reactant mixture of the desired composition was passed through a Millipore filter into a horizontal water-cooled fused silica tube of 55 mm

Jan 1, 1969

By F. H. Rhines

Page Foreword. By F. N. Rhines............................525 Design Factors for the Metal Forms with Which Powder Metallurgy May Compete. By Fred P. Peters...................... ......527 Discussion..................................530 Powder Metallargy as Applied to Machine Parts. By A. J. LanghamMer........531 Discussion......................... . Pole Pieces for Electric Motors from Iron Powder. By F. V. Lenel...........535 Discussion....................... . Bearings from Metal Powders. By W. R. Toeplitz.................542 Discussion.........................'.........549 Brushes and Allied Powder-metal Parts. By R. R. Hoffman . .............'550 Electrical Contacts Manufactured from Metal Powders. By E. I. Larsen........554 Sintered Magnets. By C. B. Fulton........................557 Friction Articles from Metal Powders. By C. T. Cox..................565 Discussion..................................567 Certain Characteristics of Silver-base Powder Metallurgical Products. By I?. R. Hensel and E. I. Larsen........................ ....569 Discussion............................... . . . . 579 Some Properties of Sintered and Hot-pressed Copper-tin Powder Compacts. By C. G. Goetzel..................................580 Discussion..................................593 The Sintering of Metal Powders—Copper. By C. J. Bier and J. F. O'Keefe......596 Some Experiments on the Effect of Pressure on Metal-powder Compacts. By Jerome F. Kuzmick..................................612 Discussion.................................. 630

Jan 1, 1945

By D. J. Blickwede

PRESENT knowledge of the effects of time and temperature upon stabilization of the austenite-martensite reaction in steel is fairly complete,1-3 but at the time the work described herein was initiated there was no information about the effects of alloy elements on the phenomenon. However, it has been assumed on theoretical grounds that alloy elements, particularly carbide formers, may have a significant effect on stabilization.' The present work was undertaken to provide information about the effect of two common elements, nickel and molybdenum, on stabilization in hypereutectoid and hypoeutectoid steels. Seven induction-furnace melted, 1.2 pct C steels ' with a variation of nickel from 0 to 6 pct and of molybdenum from 0 to 1.0 pct were used for most of the experiments. Along with these a series of 0.4 pct C steels containing 0 to 6 pct Ni were also studied. The chemical compositions of the steels are listed in Table I. Stabilization in these forged, hot-rolled, annealed, and centerless ground steels was measured by aging brine-quenched specimens (aus-tenite temperature, 1800°F) at 95" and 150°F and then determining the change in specific volume produced by subsequent cooling from room temperature to —320°F.³ In presenting the results the decrease in the change in specific volume, ?V, after various stabilization times is used. This is given by ?V -= ?VO - ?V1 where AVO is the change in specific volume on quenching directly to —320°F and aV, is the change in specific volume on quenching to —320°F after stabilizing for time t. In other words, ?V is a direct measure of the amount of martensite that is lost to the subzero quench as a result of stabilization and hence is greater, the longer the aging time or the higher the aging temperature. The results are shown in Fig. 1. The scatter of the data, which are not shown for clarity and brevity, was sufficient to make the relative location of the curves on the ?V axis inaccurate within ±2x10-5 cc per g. However, some generalities appear which are of interest. Effect of Nickel In the 0.4 pct C steels, up to 3 pct Ni has little, if any, effect on the rate or amount of austenite stabilized at 95°F, Fig. la. Increasing nickel from 3 to 6 pct almost doubles the amount of austenite stabilized in a given time. In the 1.2 pct C steels aged at 95°F, increasing the nickel from 1 to 3 pct appears to decrease the amount of stabilization, and a further increase to 6 pct Ni completely eliminates stabilization as shown in Fig. lb (M, of 6 pct Ni steel was below room temperature). The same behavior was exhibited by these steels stabilized at 1500°F, especially after aging for periods longer than 5 hr, Fig. lc. Thus it appears that up to 1 pct Ni has little effect on stabilization at low or high carbon levels. More than 1 pct Ni increases stabilization at low carbon contents and decreases it at high carbon contents. Ward, Jepson, and Rait5 have found that at inter-

Jan 1, 1954

Jan 1, 1931

By S. P. Rothwell

ABOUT thirty miles north of, the city of Belleville (which is situated on a branch of Lake Ontario), and in the township of Marmora, Ontario,: there is found a. belt of gold-bearing quartz veins, which present geological, mineralogical, and economic features of great interest to the profession. The district in which these veins are found is characterized as a rolling country, with low rounded bills of syenitic granite, overlain on the flanks of the hills by Silurian limestones, which lie in nearly horizontal beds, and in some places are so fine in texture as to afford lithographic stone of a fair quality. The gold-bearing veins run north and south through this belt of syenitic granite, and are quartz-filled true fissures, with micaccous or talcoid slates forming the walls of and horses in the veins. This

Jan 1, 1881

By William P. Blake

THE importance to the growing steel industry of the United States of a domestic supply of ferro-manganese or "spiegel" of a high grade, induces me to bring to your notice some details of the method by which a superior article is produced in the Austro-Hungarian Empire. At Reschitza, Hungary, and probably at Laibach also (the Krainische Industrie Gesellschaft), ferro-manganese is made in a blast-furnace, with charcoal as fuel, and limestone as the flux. The ore is a ferruginous mixture, containing about 37 per cent. of sesquioxide of manganese. It is silicious, and somewhat resembles, in its appearance, the manganese ore from Red Island, in the Bay of San Francisco, California. It contains about 29 per cent. of silica and some alumina, shown by the subjoined analysis

Jan 1, 1876

By Robert Phelps

A STUDY of solid solutions has long been a source of interest because of the conditions -controlling their formation. X-ray investigations so far have been conducted with the idea that there were two types of solid solutions. In the first type, an atom of the solute was supposed to replace an atom of the solvent in the crystal lattice. In the second type, an atom of the solute was supposed to lie in one of the interstices between the atoms of the solvent. These pictures both require that the sizes of the atoms must play an important part in the process of solution. It is the purpose of the present investigation to study the mechanism of solid solution, using pure silver as the. solvent, and pure aluminum as the solute. X-ray measurements show that these elements have the same "shape" of atomic domains (they both crystallize as face-centered cubes) and that their atomic diameters differ by less than one per cent.1 The results of the present investigation point toward a chemical rather than a physical picture of the nature of solid solution, and make the older' pictures merely special cases of a more general picture. The new theory has the advantage, too, that it offers a rational explanation of certain phenomena which hitherto have been only interesting detached facts. The aluminum-silver system which was, chosen for this study has been studied by various methods by several workers. By means of thermal analysis Gautier2 and Petrenko3 have determined the phase diagram. Hansen4 studied the aluminum-rich alloys by means of thermal and microscopic analyses. , He showed that at high temperatures silver dissolved in aluminum to the extent of 47 per cent by weight at 5600 C. But this solubility decreased to 1 per cent at 200° C. Westgren and Bradley5made an extensive X-ray study of these alloys. They used the change in the lattice parameter of silver as a criterion of the solution

Jan 1, 1932

By S. A. Ford

I would like to call the attention of our Bessemer steel manufacturers to a few facts in regard to the action of the manganese in the spiegel with the oxide of iron in the blown iron. The oxygen is united with the iron as a magnetic oxide, as Gautier asserts, and this oxide is reduced to a protoxide by one atom of the manganese uniting with one atom of the oxygen of the magnetic oxide of iron. This oxide of manganese and the protoxide of iron thus formed unite with the silica which has been formed by the oxidation of the silicon in the pig iron. Mr. Snelus and others

Jan 1, 1881

By I. R. Kramer

Single crystals of aluminum were pulled in tension in a solution of paraffin oil and stearic acid. The critical resolved shear stress did not change with the concentration of the stearic acid solution; however, the extents and slopes of Stages I and II were affected greatly. The observations lend evidence that the weakening effect of surface-active agents is controlled by the rate of desorption of the metal soap formed by the reaction of the surface-active agent and the metal surface. IT has been shown by various investigators1-" that surface-active agents markedly affect the mechanical properties of single crystals. (A surface-active agent, for the purpose of this report, is defined as a long-chain organic molecule which contains one or more polar groups. Usually, however, investigations have considered only molecules having one polar group.) In general, when single crystals are deformed in some solutions containing surface-active agents, the creep rate, Fig. 1, is increased and the yield strength is decreased. The fatigue strength has been reported to be affected also.ll Rehbinder and his asociatesl' explained the "weakening" effect of surface-active agents in terms of physical adsorption. They assumed that a large pressure was created in microcracks which existed on the surface of the crystal." Harper and Cottrell,' from their study of the effects of surface conditions, found that the deformation characteristics of zinc single crystals were not altered by a solution containing a surface-active agent unless the surface of the specimen had an oxidized surface. They concluded that the role of the polar molecule was to remove the strengthening effect of the oxide coating. Later, And-radeetBpresented additional evidence which appeared to agree with this conclusion. In contrast, Klinken-berg et al.7 reported data which confirmed the results of Rehbinder. Using zinc and cadmium crystals which had been cleaned by electrolytic polishing, a large increase in the creep rate was observed when Lle specimens were tested in a 1 pct oleic acid-paraffin oil solution. They also reported that the creep rate

Jan 1, 1962

By Theodore B. Comstock

The paper of Mr. S. F. Emmons on the structural relations of ore-deposits, presented at the Boston meeting in February last, having been, as I am informed, unavoidably delayed in publication, was not distributed in the preliminary edition to members until immediately before the sheets of Volume XVI. of the Transactions, containing it, were sent to press. Consequently, I saw it for the first time too late to offer any comments which might have accompanied it in that volume. This is my justification for present-

Jan 1, 1889