By R. F. Hehemann, D. J. Cometto, G. L. Houze

The w transformation in the Zr-Nb system was studied using X-ray diffraction, dilatometric, re-sistornetric, hardness, and metallographic techniques. w forms in a diffusionless, completely reaersible manner on quenching and in a diffusion-controlled manner- on aging. The temperature at which w begins to form on quenching was determined as a Junction of composition and was found to decrease with increasing solute content. w formed bv aging establishes a metastable equilibrium with an enriched ß phase. The ß/w + ß transus has been determined for this metastable equilibrium and employed to rationalize retrogression and reversion phenomena observed in these alloys. The decomposition mechanism is discussed in terms of a gradual or continuous transformation from ß to the w state. BETA- stabilizing alloying elements lower the MS temperature of the martensitic bcc (ß) to hcp (a') transformation in zirconium and titanium alloys. In certain titanium alloys, a lower symmetry modification of the martensitic structure, termed (a"), also has been reported.1,2 These martensitic transformations are suppressed when the amount of the ß-stabilizing element exceeds a critical level. However, the high-temperature ß phase cannot be quenched to room temperature without change. At alloy contents just above the critical level, |ß trans-forms to the w phase when cooled rapidly.3-6 The amount of w in quenched alloys is reduced by increasing alloy content, and this phase virtually disappears above a critical composition.5 In addition to the transformation during cooling, w also can be formed by aging ß at temperatures below approximately 500°C, and significant alloy enrichment of retained 13 accompanies the isothermal transformation.1-8 The structure of LC is closely related to that of the ß from which it forms.9-15 The bcc (ß) lattice can be generated using a hexagonal cell with three atoms located at (000) and ±(2/3, 1/3, 1/3). This cell has an axial ratio of 0.612 and is oriented with respect to the cubic cell such that (0001)H (111)C and [1120]H [101]C. Consequently, there are four possible orientations of the hexagonal cell, associated with the four (111) planes of the bee lattice. Formally w can be obtained from 0 by allowing the two atoms at the ±(2/3, 1/3, 1/3) positions to approach the coordinates ±(2/3, 1/3, 1/2) and there are four equally probable orientations of w for each 0 grain. In titanium alloys w retains the cubic axial ratio of 0.612" and hence also can be indexed as triply cubic, but this is not the case for aged Zr-Nb alloys where w is clearly hexagonal with an axial ratio of 0.622." The lattice parameters and atomic positions of w depend on thermal history and alloy content. The atomic positions (000), ±(2/3, 1/3, 1/2) provide reasonable agreement between calculated and observed diffracted intensities for w in the fully aged condition.10,14 In the quenched condition, on the other hand, the atoms appear to be displaced from the central plane12,13,15 and assume positions ±(2/3, 1/3, Z = 0.42-0.48) rather than ±(2/3, 1/3, 1/2). This results in a structure with trigonal rather than hexagonal symmetry. The readily detectable parameter and axial-ratio changes of w in Zr-Nb alloys make this system especially attractive for studying the structural changes that occur in the formation and aging of w. Particular attention in this investigation has been directed to the relationship between the structure of w in the quenched and aged conditions, and to certain aspects of the reaction kinetics. MATERIALS AND PROCEDURE Zr-5, 12, 17.5, and 25 pct Nb alloys were prepared by a double arc-melting practice, encased in stainless-steel cans and hot-rolled to 1/8-in.-thick sheet.* Charged weights have been employed for the niobium contents and interstitial analyses are reported in Table I. Dilatometric, X-ray diffraction (filtered CuK, and MoK, radiation), metallographic, and hardness techniques have been employed to follow the transformations during isothermal and quench-aging heat treatments. In quenched specimens, the electrical resistivity also was studied. Betatizing was conducted for 1 hr at 900°C. With the exception of the isothermal dilatometric studies, samples were

Jan 1, 1965

By E. Martinez, M. L. Hollander

Sulfurization of copper oxides was investigated using differential thermal analysis (DTA) and thermal gravimetric analysis (TGA). When mixtures of cuprous oxide and sulfur were heated, the surface of the cuprous oxide was converted to cupric sulfide at the melting point of sulfur (119°C); additional sulfuriza-tion took place when the sulfur vaporized above 200°C. Cupric oxide also reacted with sulfur to form cupric sulfide but the starting temperature was approximtely 225°C. When the cupric oxide and sulfur were physically separated, sulfurization still occurred indicating a reaction with the vapor phase of sulfur. Sulfurization was obtained in runs with cuprite, chrysocolla and basic copper carbonate. Further decomposition of cupric to cuprous sulfide was noted at somewhat higher temperatures. The DTA-TGA data made it possible to set up postulated reactions in each system. These techniques were found to be well suited for studies of this type. Because of the difficulty encountered in flotation of many metallic oxide minerals, efforts have been made to find suitable reagent combinations to sulfi-dize these minerals in the flotation circuit. Recently Bautista and Sollenberger,1 using a different approach, showed that the surfaces of many oxide minerals can be converted to sulfides by heating them with sulfur to temperatures between 150° and 225°C. This technique was effective even with chrysocolla, a mineral which is very difficult to sulfidize. The primary objective of the present study was to obtain information on the reactions between the oxide minerals and suIfur. A better understanding of the mechanisms involved might prove useful in pointing the way to improvements in the process. A secondary objective was to demonstrate the value of thermo-analysis in investigations of this type. Bollin and Kerr2 have reported the use of a modification of differential thermal analysis to study the thermal reactions which occur on heating elemental constituents in a closed system to synthesize copper sulfides and iron sulfides. Differential thermal analysis (DTA) was used to detect enthalpic changes as mixtures of minerals and sulfur were heated. The DTA indicated the temperatures at which reactions started and whether they were exothermic or endothermic. Weight change data were obtained by thermal gravimetric analysis (TGA). These data could often be used to support postulated reactions and to eliminate consideration of other possible reactions. EQUlPMENT Differential thermal analysis (DTA) involves measuring the temperature difference between the sample being tested and a thermally inert reference, generally aluminum oxide, as both are heated at a uniform rate. Series connected thermocouples in the sample and reference are used to detect the temperature differences that occur as the sample undergoes enthalpic changes.3 Crystalline transitions, fusions, vaporizations, dehydrations, decompositions and many solid state reactions can be detected. A DTA unit manufactured by the Robert L. Stone Co., Austin, Tex., was used in this investigation with a temperature rate increase of 10°C per min. The samples and reference were placed in Inconel cups with wells in the bottom into which the differential thermocouples fit, and run in a nitrogen atmosphere. Thermal gravimetric analysis (TGA) measures the changes in weight that a sample undergoes as it is heated. A Chevenard thermobalance converted electronically for graphic recording was used with a heating rate of 5°C per minute. An X-Y recorder plotted temperature on the X axis and weight changes on the Y axis. A flow of 250 ml per min of nitrogen was streamed through the furnace. Samples were placed in a porcelain crucible open at the top, unless otherwise noted. EXPERIMENTAL RESULTS Sulfur: Two sulfur samples from different sources were tested. The DTA of a high purity sulfur and a reagent grade sublimed sulfur are shown in Fig. 1. Nearly all the tests were run with the sublimed sulfur due to the difficulty in grinding and high electrostatic charge encountered with the high purity sample. Sulfur undergoes three endothermal reactions below 200°C. The first is a solid-solid crystalline transi-

Jan 1, 1964

By Masayuki Otagawa

THE mining methods adopted in Japanese mines are less known to the mining world than those of other countries, owing to the geographical remoteness, but they present many features of interest to mining engineers. The Ashio copper mine is at the village of Ashio, in Tochigiken, about 109 mi. (175 km.) from Tokyo by the Imperial Government railroad. The area of the concession owned by the Furukawa Mining Co. is 5000 acres (5023 ha.). The mine was formerly divided into three, viz.. Honzan, Kotaki, and Tsudo, which are distant 3 mi. (4.8 km.) from each other as shown in Fig. 1. However, in 1914, when the writer was general manager, the three mining plants were amalgamated into one with the result of simplifying the working projects and increasing the operat-ing efficiency. The mine was visited-by the Institute party in November, 1911, when Mr. K. Inouye was the general manager. Shortly afterward, the writer was appointed manager, and, in 1915, he was succeeded by Dr. K. Asano. At the end of 1917, Mr. K. Kibe became general manager and, after two years, was succeeded by the present manager, Mr. I. Sugimoto-. For some time Dr. J. Kojima was acting general manager. It is needless to say that the gentlemen mentioned are all members of the Institute, as is also Baron T. Furukawa, president of the company. Since the discovery of the enormous masses, called "kajika" or "bullhead" deposits; which the writer has described elsewhere,' the mining methods have been varied to meet the different conditions presented by these deposits.

Jan 2, 1922

By William Y. Holland, Roger M. Cook

In view of the increasingly widespread deterioration of concrete structures as the result of the interaction of the alkalies sodium and potassium released by hydration of portland cement and susceptible rocks and minerals in aggregates, it is believed that a paper summarizing the geographic distribution of these aggregates will be of interest to producers and users of concrete, concrete products, and concrete-making materials. THIS paper reviews the problem of alkali-aggre-gate reaction in concrete and describes the geologic and geographic occurrence and distribution of alkali-reactive sand and gravel in western United States. It includes no discussion of crushed stone or synthetic aggregates. Most deposits of sand and gravel are accumulations of particles of rocks and minerals from a variety of sources, and it is not unusual for at least one or two varieties of the rocks to contain some form of reactive material. Examination by petro-graphic methods of many sands and gravels, as well as manufactured aggregates, has shown that a comparatively high proportion of the deposits does contain, in greater or lesser degree, rocks and minerals known to be deleteriously reactive with the alkalies of cement. Fortunately the amount of reactive materials is commonly less than that necessary to cause deleterious effects in concrete. As investigation of unsound concrete structures progresses, it becomes evident that the alkali-aggre-gate reaction is even more widespread than supposed, Figs. 1 and 2. Even though some parts of the country appear at present to be immune, further investigations will probably show that the effects of alkali-aggregate reaction can be seen in many structures in these areas, although only on a small scale in most of them. Many concrete structures will, of course, have lived their useful life before disintegration from this cause is serious, and in others the alkali-aggregate reaction may never become significant even though the microscopic evidence of reaction is present. The alkali-aggregate reaction first was reported to be a cause of deterioration of concrete in 1940 when Stanton1 described expansion of concrete pavements in California. Similar expansion and deterioration of concrete was recognized during succeeding years in concrete structures located in many parts of the country, but particularly in the western states. A number of concrete laboratories2 became interested in the problem. It was soon determined that only certain combinations of aggregate and cement caused the alkali-aggregate reaction to take place, and moreover that the reaction progresses only in the presence of water. Further research proved that cements containing more than 0.60 pct total alkalies (pct Na,O + 0.658 x pct K2O), when used with aggregates containing appreciable amounts of reactive ingredients, caused the reaction to take place, usually with subsequent deterioration of the concrete. During the last few years this limitation has been adhered to in both government and private construction as the maximum allowable alkali content of cement to be used with aggregates of known alkali reactivity. Because of this limitation, it appears that deleterious reaction either has been reduced or eliminated in many recently built structures in which it probably would otherwise have occurred. Recent tests have shown that the degree of expansion obtained with any particular cement-aggre-gate combination depends not only on the alkali content of the cement but also upon the relation of this alkali content to the amount and degree of reactivity of reactive constituents in the aggregate.' In laboratory mortar bars, opal and cements with alkali content of as low as 0.2 pct (as equivalent of Na2O) have produced deleterious expansion as the result of alkali-aggregate reaction. These experiments demonstrate that aggregates containing even 0.1 pct of opal are deleteriously reactive. It was soon determined that alkali-silica gels were formed by the interaction of the alkalies of the cement and the reactive aggregate, Figs. 3 and 4. Osmotic or swelling pressures produced by the continued hydration of these gels cause expansion of the concrete with resulting cracking, warping, and dislocation. Evidence of the alkali-aggregate reaction can be seen by a petrographic study of the deteriorated concrete. Among the first structures studied by this method was Parker Dam on the Colorado River, California-Arizona. In the concrete from this dam pebbles of rhyolite, andesite, siliceous limestone, and chalcedonic chert were found to be reactive.

Jan 1, 1954

By W. S. Owen, T. Bell

The variation ox the M, temperature with nitrogen concentration has been determined experinzentally. The free-energy difference between martensite and the parent y Phase at the M, temperature,is computed for Fe-C and Fe-N alloys using recent solubility data fm the Fe-N system and new data for the variatim of the activity of the interstitial solute in the y phase with concentration. The "geometric model" is considered also, and the importance of Zener ordering is noted. It is shown that, although at any chosen concentration the M, temperature and the activity are significantly different in the two alloy systems, the free-energy duference is the same within the limits of experimental error, thus Providing further evidence of the very close similarity between the martensite transformations in Fe-C and Fe-N alloys. TO estimate the free-energy change accompanying the martensite transformation in binary interstitial alloys it is necessary to know the variation of the Ms temperature with interstitial solute concentration and some thermodynamic data. To date, only the Fe-C system has been discussed because this was the only system for which relevant experimental measurements had been made, but even in this case the data available are insufficient to permit the free-energy change to be calculated without the assumption of a thermodynamic model for the y and a solid solutions. The last comprehensive discussion of the topic was by Kaufman, Radcliffe, and Cohen in 1.960.' Since that time Ellis, Davidson, and Bodsworth2 have redeter mined the activity of carbon in y iron as a function of carbon content and Atkinson3 has measured the activity of nitrogen in Fe-N austenite. The M, temperature of Fe-N is reported in the present paper. Thus, it is now possible to assess the free-energy change accompanying the martensite transformation in Fe-N alloys on the same basis as that used to assess the change in Fe-C alloys. This comparison is of interest because it has been shown recently4 that the structure of the martensite formed in Fe-N alloys changes with nitrogen content in a manner exactly parallel to the changes in structure in the Fe-C series and that the strain associated with the distortion of the iron lattice in either the y or the a phase by a nitrogen atom is the same as that produced by a carbon atom. The work to be described tests whether or not this close similarity between the two systems extends to the thermodynamics of the martensitic transformations. THE Ms TEMPERATURES FOR Fe-N MARTENSITE Bose and Hawkes5 found the M, temperature of a eutectoid Fe-N alloy (2.35 wt pct N) to be 35°C. This single determination appears to be the only reported measurement of the M, temperature of an Fe-N alloy. In the present work a series of more than fifteen different specimens containing between 0 and 2.7 wt pct N were prepared by controlled nitriding of pure iron wire 0.010 in. diam. The iron was supplied by B.I.S.R.A. and was designated ACN2. The nitriding procedure, all aspects of which are critical, has been described in detail elsewhere.' Each specimen was quenched from the austenitizing temperature into brine at 20°C without removing the specimen from the ammonia-hydrogen atmosphere in which it was ni-trided. Alloys containing up to 0.7 wt pct N were fully martensitic. More concentrated alloys contained progressively more retained austenite. At 2.34 wt pct N the specimen was completely austenitic after quenching to 20°C. The M, temperature of specimens with M, temperature above 20°C (those containing less than 2.35 wt pct N) was determined by a thermal arrest technique. For the more concentrated alloys (2.35 to 2.70 wt pct N) the variation of electrical resistance with temperature down to -196°C was used. Unlike Fe-C alloys, Fe-N alloys cannot be reaus-tenitized in vacuum or in an inert atmosphere because excessive loss of nitrogen occurs, even in short times, at high temperatures. Consequently, the alloys were reaustenitized in the ammonia-hydrogen mixture corresponding to nitrogen equilibrium at the temperatures used. The specimens were quenched in a blast of cold hydrogen gas and the temperature, measured by a thermocouple welded to the 2.5-in.-long specimen, was recorded on a high-speed recorder. In the first experiments 0.002-in.-diam chromel-alumel wire thermocouples were used but it was found that these gave erroneous readings due to contamination by nitrogen pickup. Pt-Pt 13 pct Rh wires of 0.002 in. diam were found to be satisfactory. Further details of the experiments are available in the original thesis.7 The cooling rate was controlled between 400° and 4000°C per sec by adjusting the hydrogen pressure. At least three cooling curves were obtained for each composition. Each specimen was analyzed for nitrogen after quenching. To aid in the accurate location of the martensite arrest points a series of cooling curves of 0.010-in.-diam platinum wire were recorded and these, which did not contain an arrest, were used as comparison standards. Four specimens, each in the form of a 3-in. loop, were prepared from each of the four alloys containing more than 2.35 wt pct N. One specimen was used for nitrogen analysis, one for X-ray diffraction, and two for resistance measurements below 20°C. The latter specimens were quenched from 20°C into constant-temperature baths at selected lower temperatures.

Jan 1, 1968

By John W. Cloud

In 1877 the Pennsylvania Railroad Company removed an old bridge from its line at Duncannon, Pa., built intermediate piers and erected shorter spans of the Pratt truss type, which had previously been in use on another portion of the road. The design of this truss would not admit of diagonals larger than 19 inches diameter, and in order to stiffen the bridge somewhat steel rods were introduced for the main diagonals in the first and second panels, 19 inches and 18/8 inches diameter respectively. These rods were threaded without upsetting, and by the ordinary formulae the strains were of the same intensity upon both, viz., 16,000 pounds per square inch with the maximum loading. The other main diagonals in the truss are 19 inches diameter, and of iron. It was specified for the steel rods: Elastic limit,.......46,000 Ibs. Tensile strength,. .. ,. .. 80,000 lbs. Elongation,,.,.,. 20 per cent. The steel was procured without difficulty, and it allowed a factor of safety of 23/4 at elastic limit, while a similar factor of 2½ had for a long time been successfully used for iron. In the course of three years, from time to time, six of these steel rods broke, three of them being 18 inches in diameter, and three 19 inches in diameter. The broken rods were tested, and three of them analyzed at Altoona to ascertain the cause of failure, and what modifications should be made in the steel for such service. Examination showed that all the rods were broken in detail close under the nut. The threads were well cut and properly rounded at the root. testing the rods micrometer screws, reading to .0001" with c bell to signal the contact, were attached to the test pieces, and by this means the modulus of elasticity and elastic limit accurately obtained.

Jan 1, 1881

By F. E. Wood

Since the earliest discoveries of oil in the Rocky Mountain area the spirit of cooperation in drilling and production programs has prevailed. There has scarcely been a field which has not been developed in an orderly manner through mutual agreement between competitive operators. An appreciable saving has resulted, as many unnecessary wells have been eliminated. We have unit operation plans and agreements which were developed at an early date. Rock River, found in 1918, has been a unit operation. One of the first prorate agreements ever attempted was made in Salt Creek in 1921. Teapot, first developed in 1922, has been a unit operation; the lessee, the Government, and the lessor, one operator. South Casper Creek, found in 1918, has been developed as a unit. Rex Lake, found in 1923, is a unit operation. The list might be extended materially but it serves to indicate that the Rocky Mountain region enjoyed the fruits of unit operation at an early date. It is concluded from this unitization study in the Rocky Mountain region that there is an appreciable saving in both development and production costs as well as the elimination of waste of a natural resource. Certainly, when unit operation conserves an irreplaceable natural resource as well as capital, any legal or political impediment to its successful development will be overcome. If one company supervises the operations in one field, it appears to be a unit operation. This may not be true if the lands involved have been leased from a great number of lessors. Royalty holders create a most intense competitive operation. The Rocky Mountain region has its full quota of such diversified interests. The original study calls for consideration of two types of fields, unit and near-unit operation. This Committee has felt that if an agreement of any character has brought about a saving it is an approach to unit operation. The fields have been classified into four types: 1. Unit Operation.—Any field whereby the competitive drilling-drainage feature is or will be absent in the development and operation of the pool.

Jan 1, 1930

By J. C. Detweiler

THE Jacksonville plant of Humphreys Gold Corp., operating under leases from National Lead Co. and Rutile Mining Co. of Florida, recovers rutile, ilmenite, zircon, and monazite from an ancient beach deposit containing about 2.5 pct of these minerals in combination. The location of the plant is unique, being situated about ten miles from the center of Jacksonville, Fla., surrounded by a thriving suburb. Two four-lane highways pass within 1 ½ miles of the plant. An expressway now under construction will pass over the tailing pile, within 500 ft of the mine office. The elevation at the plant site is approximately 50 ft above sea level. This is one of two mines producing titanium minerals and zircon in Florida. Another mine is also operated by Humphreys at Starke, about 50 miles southeast of Jacksonville. The Jacksonville deposit extends about six miles in a north-south direction, averaging approximately one half mile wide and twenty ft thick. Values begin at the surface over most of its length and ter-

Jan 1, 1952

By J. C. Febles

HISTORY. THE use of iron for the precipitation of copper was known at least as early as the fifteenth century. Both Paracelsus and Basil Valentine refer to it in their writings, as early as 1500 A. D. It was used in Peru for this purpose prior to 1637, and at Rio Tinto, Spain, as early as the sixteenth century. The statement has been made repeatedly that in the early history of the mining industry at Butte, the practicability of this method of recovering copper from solution was overlooked, and that enormous quantities of copper-bearing water were allowed to go to waste, the copper in which might easily have been recovered at small cost; and .that this oversight on the part of the mine operators was due to ignorance of this method of recovering copper. As a matter of fact, very little copper-bearing mineral was encountered in the mines of Butte until a depth of 400 or 500 ft. bad been reached, and in many cases much greater depths were necessary to reach the copper-bearing zone. The water encountered in the upper levels (although in most cases quite highly mineralized) contained little or no copper, and it was only after considerable areas of copper-bearing ore' had been uncovered and developed that copper sulphate began to appear in the mine water in any considerable quantity. In fact, the first water that was observed to contain copper carried it in such small amounts as to be of little or no importance. It was only after years of underground work had opened extensive areas of stopes, drifts, and other underground workings, these being subsequently filled with waste, nearly all of which contained small copper values, which became oxidized by exposure to the air and were acted upon by the slowly percolating mineral water, that the recovery of copper from mine water became commercially important.

Jan 7, 1913

By Irving M. Symonds

COMPA[N]IA Minera de Penoles, S. A., at its Avalos unit operates a lead-zinc concentrator having a capacity of about 600 short tons per day. Lead and zinc concentrates are made by flotation methods. The concentrator is at Terminal de Providencia, in the state of Zacatecas, some 70 miles south of Saltillo, Coahuila. The Pe[n]oles-Avalos railroad operating between the plant and Estacion Avalos, a distance of 6 miles, makes connections with the Coahuila and Zacatecas railroad, which in turn connects with the Nacionales de Mexico at Saltillo. The three railroads are each of different gauge, requiring the transfer of all supplies and concentrates at each junction. The mill operates on company ores, on ores from leased mines, and as a custom mill. The custom business is very small. The lead concentrates are shipped to company smelters at Monterrey, Nuevo Leon and Torréon, Coahuila. Since the European war, all zinc concentrates have been shipped to the United States. ORE TREATED The major source of ore supply is a group of four mines owned or leased by the company, some three miles south of the mill in the mountains, from which the ore is delivered to the mill by a gravity aerial tramway. Custom ore comes in by rail. The ores occur in chimneys. The upper levels contained oxidized siliceous ores of lead, copper, silver and gold, with varying amounts of zinc. These ores were direct-smelted. In the first two years of operation a good deal of the tailing loss was caused by the oxidized content of the ores milled. Much of the ore in the transition zones between the oxides and sulphides was not mined. The ores now being milled are clean, hard sulphides in a limestone gangue, with only occasional contamination of oxides. The lead and zinc sulphides are of coarse structure and are freed even above flotation sizes. The galena is usually "steel" colored, easily and quickly floated. When there is any oxidation, it is usually on the coarsest crystals. The zinc minerals vary a good deal in color; a resin sphalerite predominates but there are varying shades of brown marmatites. On an average, the zinc sulphides contain 64 per cent zinc. The only common copper mineral is chalcopyrite. Little is known of the occurrence of gold and silver. Waste minerals are mainly limestone and pyrite, both of which are barren. The ores vary from 20 to 35 per cent pyrite. Mill heads for the year 1940 and the first eight months of 1941 are given in Table I. [ ]

Jan 1, 1942

By H. S. "Pete" Fowler

SME-AIME's Planning Committee established Working Party No. 22 in September 1974. Its charge was to: "Determine and take necessary actions to have Mining Engineering included among the disciplines on the National Professional Engineering Examinations." The first national examinations in "Mining/Minerals Engineering" will be given during April 1979, in states that request questions from the National Council of Engineering Examiners (NCEE), Seneca, S.C. From a survey by NCEE, mining engineering is recognized as a specialty in professional engineering registration in 25 states. In addition, 19 states give examinations in mining engineering. At press time, Pennsylvania, West Virginia, and Virginia have indicated they will use the April 1979 exam.

Jan 11, 1978

By F. D. Rosi

IN the production of single crystals by the Bridg-man method of solidification from the melt in vacuum at a crucible lowering rate of 0.25 in. per hr, a cellular structure was frequently observed in copper and copper-base alloys at the terminal surface of the as-cast crystals (i.e., the surface representing the last portion of the crystal to solidify). The geometrical form of this structure varied from crystal to crystal, but, in general, could be classified as either hexagonal or quadrilateral. Fig. 1 shows examples of this cellular structure, which is similar to that reported by Buergerl and, more recently, by Pond and Kessler&apos; and Rutter and Chalmers. In the micrographs of Figs. lb and c, the cubic structure in the alloy crystals is obscured somewhat by excessive surface evaporation in the final stages of solidification. X-ray orientation studies indicate that the traces outlining the various geometrical forms correspond to octahedral planes, which are the planes of greatest reticular density in the face-centered cubic lattice. It would appear from this that the view first propounded by Bravais,4 that the surface energies and normal growth velocities of the different crystal planes are inversely proportional to their reticular densities, applies to this cellular structure, since those surviving are the planes of greatest atomic density. Thus, the observed variation in the geometrical form of this structure in crystals of different orientation is readily understandable from the distribution of the (111) planes in the standard {111}, (1101, and (1001 stereographic projections. Depending upon whether the crystal axis (i.e., the direction of crystallization) coincides with a <111>, <111>, or <100> direction, the cellular structure viewed from a surface perpendicular to the crystal axis will consist of a network of regular hexagons, skewed hexagons (with interfacial angles of 110" and 125"), or cubes, respectively. It follows, moreover, that off-orientations from these principal directions will yield modifications of these three basic geometric configurations. In this connection, it is interesting to note that the bounding planes of the hexagonal structure observed in tin by Rutter and Chalmers3 showed no preferred orientation.

Jan 1, 1954

By H. W. Smith

This paper presents a review of developments to date in computer control practice, based in large part on Canadian experience. The basic problem examined is that of stabilizing control; matters considered are control strategies, hardware and software aspects of system implementation, reliability, human factors, and economic results.

Jan 1, 1976

By H. J. R. Way

The work to be described was undertaken at various periods from 1937 to 1939 on the Busia gold field, in the eastern province of Uganda. It was decided to examine the possibility of reef prospection by the resistivity method, for it was not known how far the usually disintegrated nature of most reefs in the ubiquitous laterite near the surface would obscure indications obtained by resistivity traverses. The work at the commencement was therefore largely experimental, but the results obtained thereby were satisfactory, and a survey was started at the Government closed area at Amonikakine. With the limited time and resources at the writer&apos;s disposal, it was not possible to complete the survey to his satisfaction or to follow up exhaustively all the geophysical indications, but some of the results of the experimental work and the survey were of sufficient interest to be worth recording; in particular the relation between the width of reef, electrode separation and shape of the curve, and the interference effect of constant separation curves over zones of float are significant and useful. Three new veins were located, but only one contained sufficient gold to warrant detailed prospection. This was called the Geophysical reef, and was uncovered over a strike distance of 1140 ft., and there are indications that it extends over a distance of 1990 ft. These results and the recom- mendations consequent therefrom were embodied in a special report to the Uganda Geological Survey. History OF the Field The Busia field is in the southeastern corner of Uganda near the Kenya-Uganda border, and is about 17 miles north of the northeastern corner of Lake Victoria. Gold was first discovered in the area in the stream beds by Davies1,2 in 1932. Subsequently numerous small alluvial claims were worked by prospectors and the area was prospected for reef by a company for periods varying from three to nine months, but was finally abandoned, as the results were considered unfavorable. Further prospecting by the Geological Survey in 1935-1936 under Davies8 and later under the writer4 uncovered three reefs with sufficient gold values to be of economic interest. These were finally taken over by a company known as Borderland Syndicate, which still owns the area, and from September 1937 to the end of 1941 about 13,000 oz. of gold was extracted from reefs of the area proved by the Geological Survey. Opencast mining operations are still proceeding (February 1943). The Amonikakine area lies to the immediate north of that of Borderland Syndicate. A certain amount of prospecting had been done when the writer started work there. As a result of his report, this area was taken over by another syndicate, but little further work was accomplished before it ceased operating because of difficulties of wartime working.

Jan 1, 1946

By H. J. R. Way

The work to be described was undertaken at various periods from 1937 to 1939 on the Busia gold field, in the eastern province of Uganda. It was decided to examine the possibility of reef prospection by the resistivity method, for it was not known how far the usually disintegrated nature of most reefs in the ubiquitous laterite near the surface would obscure indications obtained by resistivity traverses. The work at the commencement was therefore largely experimental, but the results obtained thereby were satisfactory, and a survey was started at the Government closed area at Amonikakine. With the limited time and resources at the writer&apos;s disposal, it was not possible to complete the survey to his satisfaction or to follow up exhaustively all the geophysical indications, but some of the results of the experimental work and the survey were of sufficient interest to be worth recording; in particular the relation between the width of reef, electrode separation and shape of the curve, and the interference effect of constant separation curves over zones of float are significant and useful. Three new veins were located, but only one contained sufficient gold to warrant detailed prospection. This was called the Geophysical reef, and was uncovered over a strike distance of 1140 ft., and there are indications that it extends over a distance of 1990 ft. These results and the recom- mendations consequent therefrom were embodied in a special report to the Uganda Geological Survey. History OF the Field The Busia field is in the southeastern corner of Uganda near the Kenya-Uganda border, and is about 17 miles north of the northeastern corner of Lake Victoria. Gold was first discovered in the area in the stream beds by Davies1,2 in 1932. Subsequently numerous small alluvial claims were worked by prospectors and the area was prospected for reef by a company for periods varying from three to nine months, but was finally abandoned, as the results were considered unfavorable. Further prospecting by the Geological Survey in 1935-1936 under Davies8 and later under the writer4 uncovered three reefs with sufficient gold values to be of economic interest. These were finally taken over by a company known as Borderland Syndicate, which still owns the area, and from September 1937 to the end of 1941 about 13,000 oz. of gold was extracted from reefs of the area proved by the Geological Survey. Opencast mining operations are still proceeding (February 1943). The Amonikakine area lies to the immediate north of that of Borderland Syndicate. A certain amount of prospecting had been done when the writer started work there. As a result of his report, this area was taken over by another syndicate, but little further work was accomplished before it ceased operating because of difficulties of wartime working.

Jan 1, 1946

By Carle R. Hayward

This work was first undertaken in the metallurgical laboratory of the Massachusetts Institute of Technology in 1907 by L. A. Dickinson, E. Phelps, and V. S. Rood, under the author&apos;s direction. They attempted to determine the diagram for the system Cu2S-MiS, but several inexplicable results were obtained. The following year, P. H. Mayer with Mr. Dickinson carried on some experiments with nickel sulphide and found that the molten material slowly lost sulphur until it reached a composition corresponding to the compound Ni3S2, established by Bornemann.l At this point the composition remained stable. The freezing points of the mixtures gradually fell off with the loss of sulphur. Since the above facts seemed to explain the erratic results obtained in the first experiments, Mr. Mayer with F. Jaeger attempted in 1910 to establish a correct equilibrium diagram for the Cu2S-Ni3S2 series. They prepared pure Cu2S and Ni3S2 and determined the cooling curves for various mixtures. The fusions were made in a platinum resistance furnace and the temperatures were measured with a platinum-iridium thermocouple connected with a Sullivan galvanometer. The curve was established for mixtures containing more than 40 per cent. Cu2S, but they were unable to determine certainly the direction of the curve beyond that point. Nothing further was attempted with this series until the present year, when the work was carried to a successful conclusion with the assistance of A. Butts, Jr., and E. H. Weil. The results of this work are given in the following pages. Preparation of Cu2S.—A piece of cathode&apos; copper from the Buffalo plant of the Calumet & Hecla Co. was cut into shavings by a shaper and converted into sulphide by heating in boiling sulphur. A porcelain casserole was used for the purpose, the heat being furnished by a Bunsen burner. It was found that after boiling in the sulphur for an hour the copper shavings were completely converted into sulphide. The liquid sulphur was then poured off, leaving the solid sulphide in the casserole in

Jan 1, 1915

By William B. Stephenson

The paper describes efficient and effective methods of automatically controlling sand pump installations. Particular reference is made to liquid-level controls actuating variable speed pump-driving units. Included is a discussion of various combinations of equipment, with schematic drawings. HERETOFORE many sand pump installations in the mining and metallurgical field involved guesswork as to the size of the pump and then simply direct-connecting it to a constant speed motor which was often large enough to do twice the work required. Considerable thought was given to mill location in an effort to avoid as much pumping as possible. Hillside design of mills with gravity flow of tailing was much to be desired. Power costs were low, construction was relatively cheap, and labor in many places meant nothing in comparison to the values derived from the ores being treated. Today most of these conditions are reversed. Ores are becoming more complex with lower values per ton of ore treated. Power is more expensive, construction is higher, and labor definitely takes a very important place in the profit and loss statement. Each piece of equipment incorporated in the design of a new mill is selected to provide highest efficiency based on careful metallurgical analysis of the ore to be treated both in good and poor markets. Each is designed with its flexibility in mind and with provision for adjustments in its performance to meet actual conditions in the operation of the mill. Sand pumps have taken an important position in mill design. Operators the world over are relying more and more on the performance of a sand pump in the efficient operating of their plant. Many ordinary jobs are being done today with pumps driven through adjustable pitch diameter V belt drives in order that changes in pump speed can be made easily to meet actual operating conditions. Operating costs have long since proved the folly of operating a pump at too high a speed for the volume and head to be overcome. Metallurgical results have shown the benefits derived from a smooth flow as contrasted with a surging flow from an uncontrolled pump. Construction costs have risen to such an extent that surge bins and other means formerly employed must be omitted from today&apos;s flowsheet. Several installations of considerable size and involving the use of automatic pump speed control have proved the adaptability of such controls since they were placed in service in recent years. In the following presentation each system discussed and illustrated schematically has been installed in one or more instances and has proved itself reliable and definitely economical from the standpoint of capital investment, operation and maintenance. Variable Volume-Head Speed Control: Probably the most popular, effective and efficient automatic control setup for sand pumping installations is the one shown schematically in fig. 1. Commonly used

Jan 1, 1951

By William B. Stephenson

The paper describes efficient and effective methods of automatically controlling sand pump installations. Particular reference is made to liquid-level controls actuating variable speed pump-driving units. Included is a discussion of various combinations of equipment, with schematic drawings. HERETOFORE many sand pump installations in the mining and metallurgical field involved guesswork as to the size of the pump and then simply direct-connecting it to a constant speed motor which was often large enough to do twice the work required. Considerable thought was given to mill location in an effort to avoid as much pumping as possible. Hillside design of mills with gravity flow of tailing was much to be desired. Power costs were low, construction was relatively cheap, and labor in many places meant nothing in comparison to the values derived from the ores being treated. Today most of these conditions are reversed. Ores are becoming more complex with lower values per ton of ore treated. Power is more expensive, construction is higher, and labor definitely takes a very important place in the profit and loss statement. Each piece of equipment incorporated in the design of a new mill is selected to provide highest efficiency based on careful metallurgical analysis of the ore to be treated both in good and poor markets. Each is designed with its flexibility in mind and with provision for adjustments in its performance to meet actual conditions in the operation of the mill. Sand pumps have taken an important position in mill design. Operators the world over are relying more and more on the performance of a sand pump in the efficient operating of their plant. Many ordinary jobs are being done today with pumps driven through adjustable pitch diameter V belt drives in order that changes in pump speed can be made easily to meet actual operating conditions. Operating costs have long since proved the folly of operating a pump at too high a speed for the volume and head to be overcome. Metallurgical results have shown the benefits derived from a smooth flow as contrasted with a surging flow from an uncontrolled pump. Construction costs have risen to such an extent that surge bins and other means formerly employed must be omitted from today&apos;s flowsheet. Several installations of considerable size and involving the use of automatic pump speed control have proved the adaptability of such controls since they were placed in service in recent years. In the following presentation each system discussed and illustrated schematically has been installed in one or more instances and has proved itself reliable and definitely economical from the standpoint of capital investment, operation and maintenance. Variable Volume-Head Speed Control: Probably the most popular, effective and efficient automatic control setup for sand pumping installations is the one shown schematically in fig. 1. Commonly used

Jan 1, 1951

By P. Hudock

Thin films of PbS and CdS have been deposited on insulutiug- sapphire substrates by euzploying a subliwzation technique rising near-equilibriurum conditions in ultrahigh vacuum. Oriented polycrystalline PbS and CdS films on sapphire have mobilities approachitzg values characteristic of bulk crystals. In the case of CdS, special purification procedures were crucial in obtaining high-mobility films. By performing the depositiotz of a compound within a small chamber heated to a UNiform temperature within a Vacuum systerrz, it is possible to approach equiilibrium cod-tions r.~litl~irs the chamber. In this way; the sublimation and condensation proceed under near equilibrium co?zditions, and it was found that the properties of dePosited corrzpounds were similar to those of the source material. Oriented PbS films on sapphire have a roor?l- temperature unobility of 700 sq cm per v sec and a T-5/2 temperature dependence characteristic of bulk crrystnls. CdS layers on sapphive Izazse a resistivity ~uhich is corrlpamble to the resistivity of the souvce crystals over a range of four ordem of rrlagnitude. Irz contrast, Ihe resistivity of CdS films prepared by conventional evaporation depends largely upon the substrate terrzperat~ire and postheating treatrrletlt, vather than upon the properties of&apos; the solirce rrraterial. In the case oj the CdS films the achievment of high carrier mobility required the cargful exclusion of cont~~~~ii~unts from the films. The steps taken to accomplish this included presublimation of the source material, performance of the deposition at a backg-m~ozd pressure less than 10-8 Torr, and a solvent extraction with liquid cadminum, similar to that described by Aven and woodbury. The deposition of ,films under near-equilibrium conditions is being op-plied to other classes oj COmpounds. II should he of 1:allce ,tor llle deposition of nny matevial that decomposes in the vapor state. THIN films of PbS and CdS have been deposited on insulating sapphire substrates by employing a sublimation technique using near-equilibrium conditions in ultrahigh vacuum. Oriented polycrystalline PbS and CdS films on sapphire have Hall mobilities approaching values characteristic of bulk crystals. In the case of CdS, special purification procedures were crucial in obtaining high-mobility films. Depositions were performed in a small quartz sublimation cell shown in Fig. 1 that contained the compound and the single-crystal sapphire substrate. The substrates were etched in tapered solutions of hot phosphoric acid, rinsed in deionized water, dried, and transferred to the cell under dry nitrogen. Graphite crucibles and substrates were used in experiments where it was necessary to provide an inert test vehicle for the analytical determination of impurities in the source crystals and deposited films. The crucibles and substrates were machined out of spectrographic-grade graphite having less than 1 ppm of impurities. A quartz mask was sometimes used to define a pattern which could be used for Hall and resistivity measurements. Close spacing between the compound and substrate was maintained to insure better transport of each component from the source material.

Jan 1, 1968

By G. A. Vissac

In continental Europe the feldspar jig is used almost exclusively for cleaning the fine sizes of coal; it operates with an artificial bed, made up generally of pieces of feldspar or of any other hard and heavy rock with good cleavages. A primitive form of this machine requiring close supervision was used in this country years ago, but output was small. The modern machines are generally air-pulsated Baum-type jigs, with capacities up to 150 tph, and treat sizes from 3/s in. to 0, usually previously dedusted or deslimed. These jigs are equipped with very accurate and sensitive automatic controls insuring satisfactory operation even at low separating gravity and with feeds irregular in quality and quantity. This paper will deal more particularly with coal cleaning separation, but the technical studies apply equally to all minerals.

Jul 1, 1955