Search Documents

By A. A. Smith

The application of indium to bearings was first advocated by C. F. Smsrtl in 1938, for the purpose of inhibiting corrosion of certain bearing alloys. He found that a thin layer of indium plated on the bearing surface and subsequently diffused at elevated temperatures markedly decreased the rate of corrosion in lubricating oils containing organic? acids. Most of his work was done on cadmium-base alloys, although he showed that the treatment was also effective for copper-lead and other; alloys. Since their introduction, indium-treated bearings have found considerable use, particularly in connection with airplane motors.2 Undoubtedly the effectiveness of the indium plate in resisting corrosion depends upon its relative concentration on the bearing surface after the diffusion treatment and after prolonged use at operating temperatures. Some diffusion experiments were made on a number of base metals that had been indium plated, to determine the depth of penetration after heating for reasonably long periods of time. As only the practical aspects were desired, no attempt was made to determine actual diffusion constants. Method Two different series of experiments were carried out to study the diffusion of indium into several base metals. Cast cylinders about one-inch diameter were machined to 0.750-in. diameter, so as to remove all surface imperfections, and final finishing was done with oo sandpaper. The original diameters were very carefully measured with micrometers and then a layer of indium was electrolytically deposited on the cylinders from a sulphate bath.3 In the first series of experiments, about 0.002 in. of indium' was deposited and diffusion, was carried out at 150°C. for a period of 500 hr. in a thermostatically controlled electric oven. After the diffusion period, successive layers were machined from the specimens and analyzed spectro-graphically and chemically—the spectro-graphic examination serving as a guide to determine which layers should be chemically analyzed. Apparently there was some surface oxidation of the indium plate due to the long heat-treatment, which may have had some effect on the diffusion. A1so, the cadmium alloy showed some incipient melting, which probably was caused by the formation of a low-melting eutectic. To eliminate these factors, another series of experiments was carried out by heating in an electrically heated, automatically controlled, oil bath at lower temperature. The preparation of the specimens was the same as before except that a layer of indium 0.0001 in. thick, an amount commonly used commercially on bearings, was deposited on each of the cylinders. Diffusion was carried out at 120°C. for a period of 200

Jan 1, 1944

By A. A. Smith

The application of indium to bearings was first advocated by C. F. Smsrtl in 1938, for the purpose of inhibiting corrosion of certain bearing alloys. He found that a thin layer of indium plated on the bearing surface and subsequently diffused at elevated temperatures markedly decreased the rate of corrosion in lubricating oils containing organic? acids. Most of his work was done on cadmium-base alloys, although he showed that the treatment was also effective for copper-lead and other; alloys. Since their introduction, indium-treated bearings have found considerable use, particularly in connection with airplane motors.2 Undoubtedly the effectiveness of the indium plate in resisting corrosion depends upon its relative concentration on the bearing surface after the diffusion treatment and after prolonged use at operating temperatures. Some diffusion experiments were made on a number of base metals that had been indium plated, to determine the depth of penetration after heating for reasonably long periods of time. As only the practical aspects were desired, no attempt was made to determine actual diffusion constants. Method Two different series of experiments were carried out to study the diffusion of indium into several base metals. Cast cylinders about one-inch diameter were machined to 0.750-in. diameter, so as to remove all surface imperfections, and final finishing was done with oo sandpaper. The original diameters were very carefully measured with micrometers and then a layer of indium was electrolytically deposited on the cylinders from a sulphate bath.3 In the first series of experiments, about 0.002 in. of indium' was deposited and diffusion, was carried out at 150°C. for a period of 500 hr. in a thermostatically controlled electric oven. After the diffusion period, successive layers were machined from the specimens and analyzed spectro-graphically and chemically—the spectro-graphic examination serving as a guide to determine which layers should be chemically analyzed. Apparently there was some surface oxidation of the indium plate due to the long heat-treatment, which may have had some effect on the diffusion. A1so, the cadmium alloy showed some incipient melting, which probably was caused by the formation of a low-melting eutectic. To eliminate these factors, another series of experiments was carried out by heating in an electrically heated, automatically controlled, oil bath at lower temperature. The preparation of the specimens was the same as before except that a layer of indium 0.0001 in. thick, an amount commonly used commercially on bearings, was deposited on each of the cylinders. Diffusion was carried out at 120°C. for a period of 200

Jan 1, 1944

By A. A. Smith

THE application of indium to bearings was first advocated by C. F. Smart1 in 1938, for the purpose of inhibiting corrosion of certain bearing alloys. He found that a thin layer of indium plated on the bearing surface and subsequently diffused at elevated temperatures markedly decreased the rate of corrosion in lubricating oils containing organic acids. Most of his work was done on cadmium-base alloys, although he showed that the treatment was also effective for copper-lead and other alloys. Since their introduction, indium-treated bearings have found considerable use, particularly in connection with airplane motors.2 Undoubtedly the effectiveness of the indium plate in resisting corrosion depends upon its relative concentration on the bearing surface after the diffusion treatment and after prolonged use at operating temperatures. Some diffusion experiments were made on a number of base metals that had been indium plated, to determine the depth of penetration after heating for reasonably long periods of time. As only the practical aspects were desired, no attempt was made to determine actual diffusion constants. METHOD Two different series of experiments were carried out to study the diffusion of indium into several base metals. Cast cylinders about one-inch diameter were machined to 0.750-in. diameter, so as to remove all surface imperfections, and final finishing was done with oo sandpaper. The original diameters were very carefully measured with micrometers and then a layer of indium was electrolytically deposited on the cylinders from a sulphate bath.3 In the first series of experiments, about 0.002 in. of indium was deposited and diffusion was carried out at 150°C. for a period of 500 hr. in a thermostatically con- trolled electric oven. After the diffusion period, successive layers were machined from the specimens and analyzed spectro- graphically and chemically-the spectro- graphic examination serving as a guide to determine which layers should be chemically analyzed. Apparently there was some surface oxidation of the indium plate due to the long heat-treatment, which may have had some effect on the diffusion. Also, the cadmium alloy showed some incipient melting, which probably was caused by the formation of a low-melting eutectic. To eliminate these factors, another series of experiments was carried out by heating in an electrically heated, automatically controlled, oil bath at lower temperature. The preparation of the specimens was the same as before except that a layer of indium 0.0001 in. thick, an amount commonly used commercially on bearings, was deposited on each of the cylinders. Diffusion was carried out at l20°C. for a period of 200 hours.

Jan 1, 1944

By Fred R. Harris

INTRODUCTION MacMillan Tungsten is located in northwestern Canada on the border of Yukon and Northwest Territories at a latitude of 63º17' and altitude of 1800 m above sea level. The deposit lies within the Selwyn Mountains 10 km from the Canol Road. It is 660 km by road from Whitehorse, Yukon, and 1325 km by air from Vancouver, British Columbia. MacMil lan Tungsten is a contact metasomatic deposit in gently dipping Lower Paleozoic limestone and limestone breccia adjacent to a Cretaceous quartz monzonite stock. Four tabular tungsten skarn horizons contain total geological reserves of 30 million tons grading 0.9% WO3. DISCOVERY AND HISTORY J.F. Allan, a former AMAX geologist, located mineral claims in September, 1962, to cover the source of scheelite-bearing skarn float found in the headwaters of Cirque Lake Valley. Exploration work on the property conducted mainly between 1968 and 1973, includes geological mapping, 10,500 m of diamond drilling in 73 holes, and 735 m of underground exploration. Mil 1 tests were carried out on a 300 ton bulk sample obtained underground. Preliminary feasibility studies, collection of weather data and a variety of environment studies have been carried out since 1973. Although no production date has been set MacMillan Tungsten will undoubtedly be a major tungsten producer.

Jan 1, 1976

By M. R. Tek, F. F. Craig, J. O. Wilkes, C. S. Goddin

The waterflood performance of a water-wet, stratified system with crossflow is computed by a finite difference procedure. The effects of five dimensionless parameters on tile oil displacement efficiency, water saturation con-tour.7 and crossflow rates are evaluated in the absence of gravity forces. Crossflow due to viscous and capillary forces is shown to exert a significant effect on oil recovery in a field-scale model of a two-layered. water-wet sandstone reservoir. The crossflow is at a maximum in the vicinity of the front advancing in the more permeable layer. Under favorable mobility ratio conditions, the comparted oil recovery with crossflow always is interrnerliate between that predicted for a uniform reservoir and that for a layered reservoir with no crossflow. INTRODUCTION The important erects of reservoir heterogeneity on waterflood performance are commanding increased attention in the technical literature. Much of this attention is centered on two categories of layered reservoirs: those in which layers are non-communicating and those in which crossflow of fluids occurs between the layers. In the first category, the reservoir is assumed to consist of discrete layers, each uniform within itself and differing from the others only in such properties as thickness, porosity and absolute permeability. The performance within each layer is calculated by one-dimensional flow theory, and the performance of the total reservoir is obtained by summing individual layer performances. Capillary and gravity effects usually are not considered. Representative publications dealing with thi5 type of reservoir are those of Stiles,' Dykstra and Parsons,' Hiatt,3 Warren and Cosgrove' and Higgins and Leighton." Prediction of performance for reservoirs in the second category is considerably more difficult since viscous, capillary and gravitational forces all play important roles in causing crossflow between layers. A number of authors have investigated the simpler problem of two-dimensional displacement flow in a stratified system with a mobility ratio of unity and negligible capillary and gravity effects.'; Others have considered two-dimensional, non-steady-state flow of a single, slightly compressible fluid in a stratified reservoir. A limited number of laboratory oil displacement tests in layered models with crossflow have been reported. Miscible floods (with resultant zero capillary forces) in layered five-spot models were conducted by Dyes and Braun," who studied the effect of mobility ratio with zero gravity forces, and by Craig et al. 12 who studied the effect of gravity forces at constant mobility ratio. Waterfloods in layered five-spot models (with cross-tlow due to capillary, viscous and gravity forces) were conducted by Gaucher and Lindley,"' who showed the effect of gravity forces in causing underrunning of the injected water and by Carpenter, Bail and Bobek, 14 who demonstrated the reliability of Rapoport's" dimension-less parameters for scaling layered systems. Waterfloods in rectangular layered models were conducted by Richardson and Perkins."' who investigated the effect of velocity at constant mobility ratio and with zero gravity forces, and by Hutchinson," who studied the effects of varying mobility, layer permeability and layer thickness ratios. The differential equations which rigorously describe waterflooding in a heterogenous porous medium are non-linear and do not facilitate analytical solution. By using finite difference approximations it is possible to obtain a solution to any desired degree of accuracy. Such a solution, using an alternating direction implicit procedure (ADJP), is described by Douglas, Peaceman and Rachford.18 In the present study, a computer program using ADJP explores systematically the effects of important parameters on waterflood performance of a two-dimensional, two-layered, field-scale model of a water-wet sandstone system. Particular attention is given to evaluation of the water saturation contours and crossflow rates at the interface between layers to gain improved understanding of the crossflow mechanism. PROCEDURE BASIC: FLOW EQUATIONS The basic flow equations for two-dimensional, two-phase, immiscible, incon~pressible flow in a porous medium are:

Jan 1, 1967

By H. B. Fuqua, B. E. Thompson

The area discussed herein, commonly known as the North Texas district, embraces the following 10 counties: Archer, Baylor, Clay, Cooke, Foard, Hardeman, Knox, Montague, Wichita and Wilbarger. It is underlain by two major structural features. The northernmost portion of the district, including Cooke, Montague, northern Clay, Wichita, Wilbarger, Foard and Hardeman counties, is underlain by the system of buried mountains known as the Red River uplift, which is parallel to and closely related to the Wichita-Amarillo uplift of Oklahoma and the Texas Panhandle. While the presence of a great majority of the numerous oil fields of the area is traceable to this feature, the production in Archer, southwestern Clay and southeastern Baylor counties is due to the influence of what is known as the Cisco Arch (so called because of its influence on Cisco deposition), the axis of which extends in a northwest-southeast direction across Archer County. It has been impossible for the authors to isolate the statistics for production for each of the many small pools of this district, as such statistics are not kept by the operators except for the district as a whole, therefore Tables 1 and 2 are comparatively short. The number of wells

Jan 1, 1935

By S. Fisher Morris

The New River coal-field embraces that portion of the Appalachian coal formation which lies on the waters of the New River, principally in Fayette and Raleigh counties, West Virginia, covering a strip of territory about forty miles in length along the line of the Chesapeake and Ohio Railroad from Quinnimont to Kanawha Falls, where the New River empties into the Kanawha, the railroad following the banks of the river the whole distance. (See map.) Between Kanawha Falls and the Valley of the Ohio lies the great Kanawha region, and these two coal-fields possess a greater variety of coal than can be found in any other portion of the country, enabling them to furnish the best fuels for any of the various demands of manufacture or domestic use, the Kanawha region possessing many varieties of gas, hard splint, and cannel coal, and the New River region bituminous and semi-bitnminous, steam and coking coal. The New River, in its westward course towards the Kanawha, has cut its way entirely through the Sera1 conglomerate or No. XII of the Pennsylvania Reports, the Umbral red shales of No. XI appearing at the foot of the mountains at the eastern end of the region at Quinnimont, one of the upper ledges of the Conglomerate forming the summits; while at the western end, at Kanawha Falls, the top of the Conglomerate is nearly down to the level of the river, a portion of the " Lower Productive Measures" forming the greater portion of the mountains. These mountains rise abruptly from the banks of the river to a height of from 800 to 1200 feet, leaving only here and there narrow strips of bottom land, a few acres in extent; and as the measures consist principally of hard sandstones, shales, and conglomerates lying ill a nearly horizontal position, the mountain-sides are very precipitous, with many long and high cliffs, which, with the great height of the mountains, give the country a very rugged appearance. Along the sides of these mountains fronting on the New River and its many tributaries there are exposed the outcroppings of several veins of bituminous and. semi-bituminous coal, varying in thickness from a few inches to over four feet, five of them being workable, or

Jan 1, 1880

By Frederick M. Becket, Russell Franks

WideSpread experimentation has been conducted in recent years to devise a means of preventing intergranular corrosion in austenitic chromium-nickel steels of the 18 per cent chromium-8 per cent nickel type. Additions of titanium to these steels have been used commercially to overcome this dificulty, as advocated by Krupp of Germany, and the latest literature reference concerning improved details of this method is the article by Bain, Aborn and Rutherford.' Extensive work by the present authors has shown columbium also to be a particularly valuable agent for inhibiting intergranular corrosion. This paper does not deal with steels that are largely or wholly austenitic; it is limited to a discussion of the results obtained through the use of titanium and columbium in plain high-chromium steels. For many years titanium has been used commercially by some steelmakers as a cleanser, and to a lesser extent as a hardener, but then in greater percentages. The results of the work to be described disclose that titanium and columbium in proper Proportions act as effective softeners in the high-chromium steels. It is well known that chromium intensifies the hardening effect of carbon in steel; it imparts pronounced air-hardening properties within a rather wide range of chromium content; it provides increased ductility in steels of given strength and hardness; and it enhances resistance to corrosion and oxidation at elevated temperatures to a marked degree. However, in applications requiring a combination of some of these valuable properties great hardness is frequently a detriment rather than a merit. When the objective is a soft and ductile steel having optimurn corrosion resistance, the producer strives for a carbon content as low as commercially practicable. Despite these efforts some of the commercial high-chromium steels low in carbon present considerable difficulties during production, owing to their air-hardening properties, and in consequence the economic result is not favorable. A good example is found in the 5 to 6 per cent chromium steels employed chiefly in the oil-cracking industry. Sleels

Jan 1, 1934

By Walter H. Munk

Generation of Waves by storms, and the transformation of waves in shallow water by local bottom topography are briefly reviewed. A detailed description of water motion in waves explains the nature and distribution of wave forces. A numerical example dealing with forces and moments against vertical piles summarizes the principles involved. Introduction The oil industry is moving into the open waters of the Gulf of Mexico. The design and construction of offshore drilling rigs present a number of difficult problems, among them problems involving the action of waves on fixed and floating structures. This paper deals with our present knowledge of ocean waves as it pertains to these problems, and the principles involved in computing wave forces against fixed structures. It is hoped that the more difficult case pertaining to floating structures can be discussed at a later time. None of the engincering aspects of the problem are entered upon in this paper, yet an understanding of the principles presented here should be helpful in the solution of practical problems. Waves are capable of exerting almost unbelievable forces. During a gale, waves at the harbor entrance of Amsterdam Canal in Holland lifted a 20-ton concrete block, which was resting on the bottom in 12ft of water, and deposited it on top of a pier which was 5 ft above the high water mark. At Wick Breakwater in Scotland, a mass of large stones in cement and bound together with iron rods, weighing 1350 tons, was broken loose and moved bodily! But one need not go to Holland or Scotland to find evidence of damage that waves are capable of inflicting (Fig I and 2). What is the mechanism by which waves are capable of exerting such enormous forces? To answer this, we must consider briefly the nature of wave motion. When a wind blows over a wheat field, waves appear to travel across the field, whereas the wheat itself remains rooted, slowly swinging back and forth. Similarly, in the case of water waves, the waveform travels swiftly over the water surface, whereas the water particles oscillate back and forth, but scarcely advance. The speed of the wave form is called wave velocity, the speed of the water particles is called orbital velocity. This fundamental difference between wave velocity and orbital velocity was already recognized by Leonardo da Vinci. Orbital velocity is generally much slower than wave velocity except for a breaking wave, a case which is of particular importance in the application to engineering problems. Forces exerted by the waves on obstacles

Jan 1, 1949

By Leslie Burris, J. C. Hesson

The diffusivity of uranium in liquid cadmium has been measured as a function of temperature by the capillary -bath technique. The diffusivity measurements were made at 4509 500°, 575º, and 650°C, over which temperature range the diffusivity of uranium varied from 1.3 to 2.3 x 10-5 sq cm per sec. The diffusivity of uranium in cadmium was less than that predicted by the Einstein-Stokes equation. VERY little information is available on the diffusivity of uranium in liquid metals. Bonillal has reported a single measurement of the diffusivity of uranium in bismuth. Measurement of the diffusivity of uranium in cadmium was undertaken, not only to supply data in an area in which a dearth of information exists, but also because of a need for this physical property measurement in connection with mass transfer studies now underway in the U-Cd system at Argonne National Laboratory. The capillary-bath method used in this work has been successfully used by other workers2"4 to obtain diffusivities in liquid metal systems. Although considerable experimental technique is required to obtain reliable diffusivity measurements, the basic information required is only that of temperature, capillary tube length, the initial and final compositions of the alloy in the capillary tube, and the composition of the bath into which the solute element is diffusing. From these measurements, diffusivities may be calculated using Fick's law. The diffusivity equations are presented in the Appendix. Equations which are often used to predict diffusivities in dilute solutions5 are the Einstein-Stokes equation: D= (kT)/(6pµr) and the Eyring equation: D = (?,kT/?y?zp), where D= diffusivity (sq cm per sec), k = Boltzman's constant, T= temperature ("K), p = viscosity (poises), r = radius of diffusing molecule or species (cm), and A,, Ay, and A, are the diameters of the diffusing molecule in the three axial directions. For round molecules, the Eyring equation gives values which are 37r times larger than the Einstein-Stokes equation. In this work, the experimental values were compared to the Einstein-Stokes equation. Experimental values of diffusivities in liquid metal systems usually lie between those predicted by the Einstein-Stokes and Eyring equations. The viscosity values for cadmium were obtained from the Liquid Metals Handbook.6 EXPERIMENTAL APPARATUS AND PROCEDURE The general procedure employed consisted of rapidly immersing in a molten cadmium bath containing a negligible amount of uranium a capillary

Jan 1, 1963

By M. J. Sinnot, J. C. Shyne

Low-frequency mechanical damping measurements were made to investigate internal friction in Fe-A1 alloys. The atomic ordering of the Fe-A1 system strongly influenced the stress-induced ordering internal friction. Magnetoelastic damping was also encounteyed and was shown to be reduced by the application of a static stress. THIS paper describes some damping experiments made on alloys of Fe and Al. Stress-induced ordering internal friction was measured with samples containing from 9.8 to 31.3 at. pct Al. Aluminum is soluble in a-Fe to about 50 at. pct and forms at least two long-range ordered structures, Fe3Al and Feu.' Stress-induced ordering internal friction is known to occur in many substitutional solid solutions, but few measurements of this damping effect have been made with alloy systems that have pronounced ordering tendencies. LeClair and Lomer developed expressions relating the relaxation strength of the damping process to the degree of atomic ordering and predicted that stress-induced ordering internal friction would be zero with complete ordering.' This concept was confirmed experimentally by Lulay and Wert using the system cd-Mg It is also consistent with the weak stress-induced ordering peaks observed in P -brass by Artman and in 16 wt pct Al Fe-Al by bert.' It was expected, therefore that the ordering characteristics of the system Fe-Al would strongly influence the stress-induced ordering internal friction exhibited by the experimental alloys. SAMPLE PREPARATION The alloys used in this investigation were induction melted under vacuum using high-purity melting stock. The iron was electrolytically refined Plastiron 101 which contained 99.85 wt pct Fe. The aluminum was a special 99.95 pct pure grade supplied by Alcoa. The only other raw material was spectrographically pure graphite which was used in small quantities as a deoxidant. The amount of carbon used was slightly in excess of the amount required to completely deoxidize the melt; this resulted in residual carbon contents of 0.01 to 0.02 pct in the finished alloys. The vacuum cast 2 1/2-in. diam ingots were hot rolled to 5/8-in. diam round bars. Portions of these bars were hot swaged and hot drawn to 0.050-in. diam wire. Straight pieces of the hot drawn wire were slowly heated to a temperature of 1300°C in a He atmosphere. After holding for 4 hr, the samples were allowed to cool in the furnace. This annealing treatment resulted in grain growth in the samples, the final grain size being about the same as the wire diameter. The grain boundaries were oriented perpendicularly to the wire axis, giving a bamboo grain structure. The existence of a preferred orientation could not be detected in these coarse grained samples. If the samples had a fiber structure, this probably would have been the same in all samples because of similar processing, thus the influence of crystal orientation on the relaxation strength would have been similar in all samples. The aluminum contents of the alloys are listed in Table I. EQUIPMENT The principle of the torsion pendulum was used for the internal friction measuring device. The

Jan 1, 1961

By Roland Blanchard

Recent discovery at Mount Isa of copper mineralization in commercial amount at a depth of 1000 ft., coinciding with downward termination of ore at about the same depth within the larger silver-lead-zinc lenses that have been the standby of Mount Isa's production to date, has been cited as an example in support of mineral zoning. A previous paper by the author and Graham Hall1 furnished a detailed description of the geology of the ore at Mount Isa as exposed up to that time, but necessarily dealt mainly with the silver-lead-zinc mineralization. Most of the geologic facts that constitute the first half of the present paper were set forth in the previous one in much greater detail, with full supporting evidence for the facts cited. The large amount of underground development (approximately 20 miles) and the extensive exploration carried out by diamond drilling (100,000 ft.) at Mount Isa, added to extensive microscope work conducted over a period of years, both by the company's staff and by others, had made possible the calculation within fairly close limits of mineralogical composition of the principal mineralized block of ground down to 1000-ft. depth, and had established closely the mineral succession, with reasons for deposition of the various minerals in the patterns now occupied by them. The geologic facts as outlined in the previous paper remain as stated; but because substantial development within the new copper ore body and further exploratory diamond drilling within the new silver-lead-zinc area (Racecourse) have taken place since that paper was written, statements and figures relating to those two areas in the present paper supersede those furnished in the previous one. The recent work likewise has established more clearly the paragenetic relationship between the chalco-pyrite and galena. Evidence confirming the relationship is furnished in the present paper. The facts of ore occurrence at Mount Isa show Accepted Zonal Succession Silver sulphantimonides Galena Sphalerite Tetrahedrite Arsenical sulphides Chalcopyrite Pyrrhotite Mount Isa Succession I In the main but prob- Silver sulphantimonides ably not wholly Tetrahedrite I contemporaneous Galena Pyrrhotite Sphalerite Arsenical sulphides They show further: (I) that instead of the silver-lead minerals yielding to increased zinc in depth, the zinc yields to increased silver-lead; (2) no dovetailing of the silver-lead-zinc sulphides into chalcopyrite takes place; (3) despite the large amount of pyrrhotite deposited in the district (estimated at upward of 100,000,000 tons), its deposition took place under moderately low temperature conditions; (4) no evidence has been found for increase in temperature of deposition, with depth, to deepest exploration in ore (1475 ft.). The anomalous condition at Mount Jsa, both as to the unorthodox mineral succession and the largely unorthodox patteru of mineral distribution, is explained in the present paper,

Jan 1, 1949

By Roland Blanchard

Recent discovery at Mount Isa of copper mineralization in commercial amount at a depth of 1000 ft., coinciding with downward termination of ore at about the same depth within the larger silver-lead-zinc lenses that have been the standby of Mount Isa's production to date, has been cited as an example in support of mineral zoning. A previous paper by the author and Graham Hall1 furnished a detailed description of the geology of the ore at Mount Isa as exposed up to that time, but necessarily dealt mainly with the silver-lead-zinc mineralization. Most of the geologic facts that constitute the first half of the present paper were set forth in the previous one in much greater detail, with full supporting evidence for the facts cited. The large amount of underground development (approximately 20 miles) and the extensive exploration carried out by diamond drilling (100,000 ft.) at Mount Isa, added to extensive microscope work conducted over a period of years, both by the company's staff and by others, had made possible the calculation within fairly close limits of mineralogical composition of the principal mineralized block of ground down to 1000-ft. depth, and had established closely the mineral succession, with reasons for deposition of the various minerals in the patterns now occupied by them. The geologic facts as outlined in the previous paper remain as stated; but because substantial development within the new copper ore body and further exploratory diamond drilling within the new silver-lead-zinc area (Racecourse) have taken place since that paper was written, statements and figures relating to those two areas in the present paper supersede those furnished in the previous one. The recent work likewise has established more clearly the paragenetic relationship between the chalco-pyrite and galena. Evidence confirming the relationship is furnished in the present paper. The facts of ore occurrence at Mount Isa show Accepted Zonal Succession Silver sulphantimonides Galena Sphalerite Tetrahedrite Arsenical sulphides Chalcopyrite Pyrrhotite Mount Isa Succession I In the main but prob- Silver sulphantimonides ably not wholly Tetrahedrite I contemporaneous Galena Pyrrhotite Sphalerite Arsenical sulphides They show further: (I) that instead of the silver-lead minerals yielding to increased zinc in depth, the zinc yields to increased silver-lead; (2) no dovetailing of the silver-lead-zinc sulphides into chalcopyrite takes place; (3) despite the large amount of pyrrhotite deposited in the district (estimated at upward of 100,000,000 tons), its deposition took place under moderately low temperature conditions; (4) no evidence has been found for increase in temperature of deposition, with depth, to deepest exploration in ore (1475 ft.). The anomalous condition at Mount Jsa, both as to the unorthodox mineral succession and the largely unorthodox patteru of mineral distribution, is explained in the present paper,

Jan 1, 1949

By H. S. Munroe

As elaborate discussion under this heading formed a chapter in one of the reports made by Professor Raymond as Commissioner of Mining Statistics." In a subsequent report? was printed a paper., by Mr. William Main, Jr., of Columbia, South Carolina, containing a theoretical investigation into the effect of the velocity of impact on the effective ditty of stamps. A visit to the Lake Superior copper region last summer suggested an inquiry into the relative efficiency and economy of the enormous steam stamps of the copper-mills, as compared with the results obtained with the cam and tappet stamps commonly used in the West. The atmospheric stomp used at the Phoenix Mill promised to add interest to the inquiry, as giving an example of unusually high speed, this stamp making 160 drops per minute. In introducing his subject Dr. Raymond makes the following remarks, which are quite apropos of the present investigation: "In considering the economical application of stamping machinery, we meet, at the beginning, with serious difficulties in obtaining accurate data for comparison. The weight and fall of stamps vary as the shoes and dies wear out; and this may lead to a change of speed also. Moreover, defects in engines, boilers, or machinery for the transmission of power, may occasion serious losses, which cannot fairly be charged to the arrangements of the stamps proper. Again, the capacity of stamp-mills is directly dependent, in some degree, upon the nature and extent of discharge, fineness of screens, and other peculiarities of the battery. Finally the hardness and tenacity of the rock crushed varies so much that comparisons between different localities cannot be implicitly trusted. The safest experiments are those made in the same mill, by changing first one arid then another condition of working; but this is seldom possible for such

Jan 1, 1881

By Len Ramp

CHROMITE deposits in southwestern Oregon occur along definite zones or horizons in sill-like ultramafic intrusions. These horizons are here referred to as ore zones and are distinguishable only by relatively Shin and scattered, discontinuous chromite occurrences. The zones are tabular in shape but are usually folded and faulted by the intensive post-intrusion deformation the ultramafic rocks have undergone. A single zone may contain disseminated, nodular, banded, or pods of massive chromite. The typical chromite deposit is composed of a series of thin lens-shaped bodies that lie along a definite plane and generally show evidence of magmatic flow with their long dimensions aligned in the direction of flow. A body of chromite often pinches down to a narrow wisp only a fraction of an inch thick. This thin streak of chromite may point to or be connected with another body of chromite. In some deposits the orebodies have a definite rake. The depth at which chromite may be found can be predicted by its position in a folded intrusive, provided that adequate structural evidence is available. Although the ore shoots are characteristically discontinuous, there is theoretically no limit to the depth at which chromite may be found. Origin: All the chromite deposits examined in southwestern Oregon are of magmatic origin, that is, the chromite was an original constituent of the peridotite magma and became segregated in varying degree from the magma to form the ore de- posits. Examples of early, intermediate, and late magmatic chromite have been recognized in the area. Crystallization of the principal minerals (olivine, pyroxene, and chromite) was apparently near completion at the time of intrusion of the peridotite magma. The magma acted as a viscous crystal mush stringing out aggregates of pyroxene and chromite in the direction of flow. These streaky accumulations are termed schlieren.

Jan 8, 1957

By J. Sibakin, R. D. Hindson

In order to devise a practicable soaking pit schedule for use at The Steel Co. of Canada Ltd.'s Hamilton Works, soaking pit heating temperatures, sooking times, pit capacity, and safe maximum mill drafts were correlated with fluctuations in the current or load of the bloom mill driving motor. Other variables such as total delays in the pit, rolling schedules, mill delays, and track times were also investigated. IN order to show an easily applied and accurate means of establishing soaking pit heating temperatures, soaking times, pit capacity, and safe maximum mill drafts, these various factors are correlated herein with fluctuations in the current or load of the bloom mill driving motor. Rolling practices have a considerable influence on the production capacity of a blooming mill. The maximum values of the torque, in particular, are of importance, since even instantaneous current peaks lead to the tripping of the motor by the overload relay and result in loss of mill time. The establishment of safe maximum drafts and accelerations for ingots of different sizes and of a soaking pit practice which would ensure a consistent and satisfactory plasticity of the metal is of considerable importance for increasing the efficiency of both the blooming mill and the soaking pits. The Bloom Mill Dept. of the Hamilton Works, The Steel Co. of Canada Ltd., is equipped with one 44 in. mill driven by a 7000 hp motor with the setting of the overload relay at 22.0 ka. The speed of rotation of the motor is regulated after the Ward-Leonard system. There are three basic speeds of 9.5, 28, and 47 rpm and a further possibility of increasing the speed by weakening the field. This last possibility is hardly ever used during practical operations. The rolling program of the blooming mill is varied, both in the size of the ingots to be handled and in the steel grades. The total tonnage handled by the mill is about 2,000,000 ingot tons per year. At the time of the investigation, the Bloom Mill Dept. was equipped with 22 soaking pits (6 regenerative, 14 bottom-fired, and 2 one-way top-fired pits) with a total bottom area of 2770 sq ft. The pits are fired with a blast furnace-coke oven gas mixture having a calorific value of 155 Btu per cu ft. The foregoing figures show that the production program was such as to impose the necessity of a most efficient usage of the available equipment. For this purpose, the operations of the 44 in. mill and of the soaking pits were investigated, and the results of the investigation were used as a basis for a revised soaking pit schedule and drafting practice. The plasticity of an ingot of a certain chemical composition when being rolled is determined mainly by the following factors: I—the ingot size, both thickness and width; 2—the length of the gas soak; and 3—the surface temperature. The first two factors determine the uniformity of the temperature distribution over the cross-section of an ingot. The third factor introduces the level of the heating of an ingot. The torque produced by an ingot being rolled is determined by the area of the metal displaced, its plasticity, and acceleration values. On the other hand, with shunt motors the torque is determined by the current. This can be assumed to be correct with only a small degree of error for compound motors with a relatively small effect of the series windings as long as the velocity is not regulated by weakening the field. Since the spread is relatively unimportant when compared to the width of an ingot and since it is also reduced several times during rolling by edging passes, the draft alone and not the area of the metal displaced may be taken into consideration with ingots of a similar size. It is therefore possible to determine the main features of the heating and drafting of an ingot by measuring the current and acceleration of the mill motor. After the acceleration has been taken into account, the amount of current will be an indication of how the motor responds to a heating and/or drafting practice and these practices can be adjusted in order to get the desired result. As peak currents are more likely when heavier ingots are rolled, the rolling of plate and slab ingots was investigated. Conditions prevailing when smaller ingots are rolled can be deduced from the results obtained on heavier ingots. All measurements were made when plain carbon grades under 0.15 pct C were rolled. The motor current, the voltage across the armature, and the rpm were recorded simultaneously on synchronized charts, Fig. 1, which moved with the speed of 6 in. per min. Each draft was recorded by a special observer. The rpm curve made it possible to establish the acceleration at any given moment. For purposes of correlation, the maximum current during a pass and the corresponding acceleration were used. The charts made it possible to establish the position of the roller's lever at any given moment as well as the total time of a pass. The slab ingots were divided into three groups (28x35, 28x45, and 27Mx53 in. ingots) and each group was investigated separately. Since they account for most of the current peaks, only flat passes were used for purposes of correlation, a total of 1373 having been investigated.

Jan 1, 1956

By T. L. Joseph

Charcoal was the predominant blast-furnace fuel until 1838, when it was found, by the operation of a 2-ton experimental furnace, that anthracite could also be used. This information was a stimulus to the iron industry, particularly in eastern Pennsylvania where anthracite was available at low cost. The production of anthracite pig iron increased steadily and, in 1855, its tonnage exceeded that of charcoal iron. Of the 680 furnaces in operation in 1874, the 226 using anthracite produced nearly one-half the total tonnage. In 1869, the production of coke furnaces exceeded that of charcoal furnaces and, in 1875, coke surpassed anthracite as a metallurgical fuel. In 1907, the output of anthracite pig dropped well below a million tons and its present significance is largely historical. In recent years, the production of coke has gone hand in hand with the production of pig iron and it has gradually attained the position it now occupies as a universal blast-furnace fuel. Charcoal, however, has great merit as a blast-furnace fuel chief1y because of its freedom from ash and sulfur. The harmful effect of the latter and the necessity of keeping the percentage of this element in pig iron at a minimum are well recognized. Other contaminating elements can be reduced to specified limits in the steel-making process, but the control of sulfur belongs essentially to the blast furnace. The purpose of this paper is to point out the distribution of this impurity in blast-furnace materials and to indicate how its presence alters the composition, quantity, and free-running or critical temperature of the slag, and the relation between these factors, fuel economy, and the cost of iron. Sulfur Distribution in MateRials Table 1 shows the distribution of sulfur in charcoal practice. Similar figures taken from coke practice are given in Table 2. These data were

Jan 1, 1925

By Charles R. Fettke

The permeability of an oil or gas sand is its capacity for transmitting fluids, either liquids or gases, under pressure. The permeability of a sand depends upon the size and shape of the openings in it and the extent to which these communicate with one another, as well as upon the ratio of their volume to the total volume of the sand. The apparatus employed and the method of procedure used by the authors in conducting the permeability tests have been described in a previous pub1ication.l For the tests described here 1/2-in. cubes were used. They were set in the lower end of a 1-in. union, inserted in a square hole cut in a hard rubber stopper which fitted into the lower end of the union. In the tests with air, volumes were measured with a wet American gas meter of 100 cu. ft. capacity. In those with water, distilled water at room temperature was employed, unless otherwise noted. DescRiption of Sands Tested The tests described in this paper were performed upon 18 samples representing typical oil and gas sands from 7 localities in northwestern Pennsylvania. For purposes of identification, the cores from which the samples came have been designated by capital letters, the sequence of the samples in the cores by numerals, and the individual cubes by small letters. All cubes from the same samples came from adjacent portions parallel to the bedding. Core A of the Bradford sand came from the north central part of the Bradford field, from an area where water-flooding operations have proved highly successful. Core B of the same sand was obtained from the southern part of the field. This core contained a so-called "loose streak," 7.5 ft. thick, in the middle portion of which B2 is a representative sample. The "loose streak" has given trouble in water-flooding but responded favorably to an air-drive, using a pressure of 300 lb. The natural production was increased approximately five times over a period of three years in which the air-drive was in operation. Core C, also of the Brad-

Jan 1, 1931

By F. W. Jessen, John C. Miller

In many areas where carbonate rocks form important parts of the stratigraphic sequence, stratigraphers have experienced varying degrees of difficulty in differentiating and correlating limestone and dolomite units in both surface and subsurface work. With early Paleozoic rocks of the Mid-Continent, insoluble residues yield a remarkable amount of strati-graphic data and relatively good correlations may be carried over broad distances.' Unfortunately, neither such information nor electric logs and radioactive logs have been particularly helpful in interpreting the limestone sections of the Permian Basin of West Texas. This is because: (1) the variations in the sections may be very slight; (2) no completely satisfactory method of interpretation has been developed; and (3) the measurements themselves are not sensitive enough for small variations. Also, such logs are influenced by the fluid content. Paleontology and micro-paleontology remain the ultimate arbiters. As a routine tool, however, paleontol-ogical examination is slow and tedious. Chemical analysis may be used, but this, too, is extremely slow. Although rocks are not classified according to chemical composition, there is considerable variation with rock types. Correlation by chemical composition has two advantages, first, the characteristics determined are subject to minimum human error and interpretation, and secondly, the lithologic changes are not masked by fluid content as in the case of electric and radioactive logs. Some fossils concentrate certain elements which tentatively might be used to date rock units.' Rapid chemical analysis by spec-trographic means could be used as an adjunct to other means employed in correlation work, or might, in itself, present a suitable method. PURPOSE OF THIS INVESTIGATION Sloss and Cooke' have published data concerning spectrographic analysis of limestone rocks specifically for purposes of direct correlation of a single formation. These authors found satisfactory evidence that differences in percentage of four elements (Mg, Fe, Al, and Sr) in the Mississippian limestones of northern Montana were useful in carrying out correlation of this formation over a distance of approximately 50 miles. It was concluded from the preliminary work that the spectrochemical method offered possibilities of solution of some problems of correlation heretofore not possible. Since the work of Sloss and Cooke' was confined to one particular limestone zone, extension of the use of the method to examine two or more geologic formations would aid materially in the over-all problem of correlation of such rocks. Equipment is now available commercially with which very rapid spectrographic analyses may be made, and hence the problem was to determine whether the variations existing in the minor constituents of limestones were sufficient for use in possible correlation. Qualitative and semi-quantitative investigations were made to determine whether significant changes in the chemical condition occurred. It was a further purpose to investigate the geologic time-boundaries to see whether significant chemical variation could be found corresponding to the paleontological breaks. It was desirable to attempt correlation of a thick section of limestone or dolomite rock and to have as much information as possible on the section. Furthermore, it was felt that examination of formations more difficult to correlate by other means would enhance the value of the method should definite points of correlation be found. Samples were chosen from the Chapman-McFarlin Cogdell No. 25 well in the Cogdell field, Kent County, Tex., and from the General Crude Oil Co., Coleman No. 193-2 well in the Salt Creek field, Kent County, Tex. These fields belong to the famous series of "Canyon" reef fields of West Texas. Cores from the above wells were available from the United States Geological Survey, Austin, Tex. THE SPECTROGRAPHIC METHOD The choice of procedure to be followed in this investigation was based on the anticipated requirements peculiar to the problem. Since the problem was primarily to investigate the possibilities of applying the spec-trograph to problems of correlation in thick carbonate sections, a precise quantitative analysis did not appear necessary. A qualitative analysis to show the possible absence of presence of any element, or a semi-quantitative analysis of the elements present to show the relative changes in magnitude of selected elements was required. Both types of analysis were employed. The two most widely applied methods of semi-quantitative estimates are those of Harvey and of Slavin4,5 though various other procedures have been described.6 while the Harvey method has been modified by Addink,7 this refinement did not seem necessary to the present problem. Essentially, the procedure employed is a variation of the total energy method of Slavin with two exceptions: (1) stressing matrix effect, and (2) using densitometer measurements. As measured by a densito-

Jan 1, 1956

By W. C. Ellis

For the purpose of developing combinations of higher strength and conductivity than are obtainable by heat treatment alone in the age-hardening copper alloys, an investigation has been made of the effects of combinations of heat treatment and strain hardening on the properties in question. The investigation was limited to a study of the alloys containing nickel and silicon; nickel, silicon and cadmium; and cobalt and silicon. The experiments made in the course of the study are described in this paper in three groups: 1. The effect of hard drawing subsequent to heat treatment on the mechanical and electrical properties of the alloys. 2. The effect of low-temperature aging on the properties of heat-treated and hard-drawn alloys. 3. The effect of strain on the rate of aging of quenched nickel-silicon-copper alloys.

Jan 1, 1931