By R. R. Klimpel Discussion by C. C. Harris, L. G. Austin

C. C. Harris (Columbia University) — The authors ' have presented relationships for the random division of a magnitude into r + l parts taking account of the order of selection. Interpreting their model in comminution terms, their Eqs. 7, 9 and 11 refer to the one-dimensional case; that is, to the subdivision of a long thin rod at random. It is assumed that the fragments may be indefinitely small. Real materials, however, are limited in the degree of subdivision which can be attained through the intervention of practical restrictions. One in fine grinding is the depletion of microflaws as material becomes finer. Another is the

Jan 1, 1969

Jan 1, 1961

By Charles Prasky

ABOUT five years ago the Bureau of Mines began a study, at Minneapolis, of the various methods for beneficiating the low-grade manganese deposits of the Cuyuna range. Several samples of green carbonate slate from the Cuyuna range, containing about 7 pct Mn and about 28 pct Fe, were obtained for this study. The component minerals in the carbonate slate formation were so intimately associated that mineral dressing methods were not suitable for concentrating manganese to a ferrograde product. Although upgrading of manganese and iron minerals has been effected by flotation methods, it appears that manganese cannot be separated from iron except by chemical means. Because the flotation studies at Minneapolis were carried out simultaneously with the hydrometallurgical studies, only crude slate was available for process testing. An important economic consideration in selecting any one of the several chemical methods proposed for recovering ferrograde manganese is the availability of the chemical reagent. Fortunately, large tonnages of sulfur are available on the Cuyuna range in low-grade pyrite and pyrrhotite deposits that are readily concentrated by flotation to a suitable feed for a sulfide roasting furnace as indicated by a Bureau of Mines investigation in 195 0-1951.1 The roasted residue from the sulfide concentrates is a potential source of marketable iron oxide. Therefore, if these sulfide deposits were employed in recovering manganese, utilization of two heretofore unused mineral deposits would be accomplished. Laboratory investigations of several proposed leaching processes were made as a preliminary step in the investigation of hydrometallurgical methods for the treatment of Cuyuna carbonate slate using sulfur as a chemical reagent. From results obtained in the laboratory tests, these leaching processes did not appear entirely suitable for treating Cuyuna carbonate slate. The method developed at the North Central Experiment Station and selected for a more intensive pilot-plant investigation has been termed the differential high-temperature sulfatizing process. Essentially, this sulfatizing process consists of the following steps, described in the order in which the small-scale pilot-plant investigations were made. The first and perhaps most significant step in the process consists of a sulfate roast. Carbonate slate is roasted in an atmosphere of sulfur dioxide gas and air. The overall chemical reaction for converting manganese carbonate to a sulfate at a high temperature in a sulfur dioxide atmosphere follows MnCO8 + SO2 + 1/2 0, = MnSO4 + CO2 (H077°O = —64,180 cal per g mol) .' The need for concentrated sulfuric acid is avoided. Fine grinding is not essential. Removal of carbon dioxide from the slate during roasting produces a more porous structure and permits easier permeation by the sulfatizing gas mixture. The temperature limits for this conversion of manganese have been established as 600" and 850°C. Iron sulfate is unstable and is not formed at these temperatures; phosphorus is not converted to a water-soluble form; and polythionates are not formed. The second step in the process consists simply of a water leach of the sulfatized product. Manganese sulfate in the sulfatized product is dissolved in water. Iron, phosphorus, and calcium remain in the leach residue as water-insoluble products. The third and final step consists of the recovery of ferrograde manganese oxide from manganese sulfate leach solution. Water is evaporated from the leach solution, and impure monohydrate crystals of manganese sulfate are recovered. The moist crystals are formed into pellets or extrusions and thermally decomposed to produce a ferrograde manganese

Jan 1, 1958

By John Chipman, K. C. McCutcheon

To a very large extent the quality of a mild steel ingot is determined by the manner in which it is poured into the ingot mold and its behavior during the first few minutes after it has been poured. The formation of the solid rim of metal around the periphery of the mold, the effervescent action of the liquid steel within this solidified rim and the upward or downward movement of the metal level are indications of what is going on beneath the surface of the liquid metal, especially at the interface at which solidification occurs. Observation of this "rimming action" enables an experienced observer to predict the thickness of the sound skin of the ingot and the location and extent of cavities or "blowholes" caused by entrapment of gases. The control of rimming action at the hands of a skillful steel pourer is a vital part of the control of quality in mild steel sheet, and the behavior of the liquid steel during the rimming period is a useful criterion of the melting and refining practices employed in the open hearth. The behavior of rimming steel during solidification depends primarily upon the evolution of gases from the molten metal and it is therefore a problem of considerable interest to determine the nature and amount of the gases evolved. A number of attempts to determine either the amount or the analysis of the evolved gases have been reported. Klinger,1 in 1925, analyzed the gases extracted from rimming, semikilled and killed steel ingots and found that the chief constituent of the rimming gas was carbon monoxide. The relatively large amounts of nitrogen reported in his first few samples may have been due to incomplete removal of air from the gas-collecting mechanism. McKune2 reported similar studies of rimming ingots from which surprisingly large proportions of nitrogen and hydrogen were evolved. Ameen and Willners3 determined both the amount and composition of gases extracted from unkilled ingots with the aid of diminished pressure. . Their ingots weighed only 80 kg. (176 lb.) and apparently were solid within two or three minutes, so that their

Jan 1, 1938

By K. C. McCutcheson

To a very large extent the quality of a mild steel ingot is determined by the manner in which it is poured into the ingot mold and its behavior during the first few minutes after it has been poured. The formation of the solid rim of metal around the periphery of the mold, the effervescent action of the liquid steel within this solidified rim and the upward or downward movement of the metal level are indications of what is going on beneath the surface of the liquid metal, especially at the interface at which solidification occurs. Observation of this "rimming action" enables an experienced observer to predict the thickness of the sound skin of the ingot and the location and extent of cavities or "blowholes" caused by entrapment of gases. The control of rimming action at the hands of a skillful steel pourer is a vital part of the control of quality in mild steel sheet, and the behavior of the liquid steel during the rimming period is a useful criterion of the melting and refining practices employed in the open hearth. The behavior of rimming steel during solidification depends primarily upon the evolution of gases from the molten metal and it is therefore a problem of considerable interest to determine the nature and amount of the gases evolved. A number of attempts to determine either the amount or the analysis of the, evolved gases have been reported. Klinger,1 in 1925, analyzed the gases extracted from rimming, semikilled and killed steel ingots and found that the chief constituent of the rimming gas was carbon monoxide. The relatively large amounts of nitrogen reported in his first few samples may have been due to incomplete removal of air from the gas-collecting mechanism. McKune2 reported similar studies of rimming ingots from which surprisingly large proportions of nitrogen and hydrogen were evolved. Ameen and Willners3 determined both the amount and composition of gases extracted from unkilled ingots with the aid of diminished pressure. Their ingots weighed only 80 kg. (176 lb.) and apparently were solid within two or three. minutes, so that their

Jan 1, 1938

By K. C. McCutcheon, John Chipman

To a very large extent the quality of a mild steel ingot is determined by the manner in which it is poured into the ingot mold and its behavior during the first few minutes after it has been poured. The formation of the solid rim of metal around the periphery of the mold, the effervescent action of the liquid steel within this solidified rim and the upward or dounward movement of the metal level are indications of what is going on beneath the surface of the liquid metal, especially at the interface at which solidification occurs. Observation of this "rimming action" enables an experienced observer to predict the thickness of the sound skin of the ingot and the location and extent of cavities or "blowholes" caused by entrapment of gases. The control of rimming action at the hands of a skillful steel pourer is a vital part of the control of quality in mild steel sheet, and the behavior of the liquid steel during the rimming period is a useful criterion of the melting and refining practices employed in the open hearth. The behavior of rimming steel during solidification depends primarily upon the evolution of gases from the molten metal and it is therefore a problem of considerable interest to determine the nature and amount of the gases evolved. A number of attempts to determine either the amount or the analysis of the evolved gases have been reported. Klinger,' in 1925, analyzed the gases extracted from rimming, sernikilled and killed steel ingots and found that the chief constituent of the rimmining gas was carbon monoxide. The relatively large amounts of nitrogen reported in his first few samples may have been due to incomplete removal of air from the gas-collecting mechanism. McKune² reported similar studies of rimming ingots from which surprisingly large proportions of nitrogen and hydrogen were evolved. Ameen and Willners3 determined both the amount and composition of gases extracted from unkilled ingots with the aid of diminished pressure. Their ingots weighed only 80 kg. (176 lb.) and apparently were solid within two or three minutes, so that their

Jan 1, 1938

By John Chipman, K. C. McCutcheon

To a very large extent the quality of a mild steel ingot is determined by the manner in which it is poured into the ingot mold and its behavior during the first few minutes after it has been poured. The formation of the solid rim of metal around the periphery of the mold, the effervescent action of the liquid steel within this solidified rim and the upward or dounward movement of the metal level are indications of what is going on beneath the surface of the liquid metal, especially at the interface at which solidification occurs. Observation of this "rimming action" enables an experienced observer to predict the thickness of the sound skin of the ingot and the location and extent of cavities or "blowholes" caused by entrapment of gases. The control of rimming action at the hands of a skillful steel pourer is a vital part of the control of quality in mild steel sheet, and the behavior of the liquid steel during the rimming period is a useful criterion of the melting and refining practices employed in the open hearth. The behavior of rimming steel during solidification depends primarily upon the evolution of gases from the molten metal and it is therefore a problem of considerable interest to determine the nature and amount of the gases evolved. A number of attempts to determine either the amount or the analysis of the evolved gases have been reported. Klinger,' in 1925, analyzed the gases extracted from rimming, sernikilled and killed steel ingots and found that the chief constituent of the rimmining gas was carbon monoxide. The relatively large amounts of nitrogen reported in his first few samples may have been due to incomplete removal of air from the gas-collecting mechanism. McKune² reported similar studies of rimming ingots from which surprisingly large proportions of nitrogen and hydrogen were evolved. Ameen and Willners3 determined both the amount and composition of gases extracted from unkilled ingots with the aid of diminished pressure. Their ingots weighed only 80 kg. (176 lb.) and apparently were solid within two or three minutes, so that their

Jan 1, 1938

By Roussey Roussev

The use of chemical additives on grinding is of significant importance considering the high energy consumption of grinding processes. My research indicates that the dispersant approach explains the effects, in this particular case of wet grinding. Further, the dispersant approach combined with torque measurements give the possibility of clarifying the mechanisms involved when using grinding aids. I find the conclusions derived from the data obtained to be correct and useful for grinding. In general, I agree with the explanations. However, I would like to discuss several additional points that I consider to be important, and in the same time to mention some of my own results from investigations similar to those presented in the study under discussion. The "bed volume concept" and the change of slurry viscosity explain adequately the data plotted on [fig. 3], in conjunction with [Figs. 1 and 2]. However, the significant increase of the average torque in the case of 83% solid with XFS-4272 introduces the necessity of establishing the optimum of percent solid when dispersant is used. For example, the optimum percent of solid for different materials varies. One of the reasons is the material's mass density. On the other hand, it is necessary to determine the concentration of the chemical used. Because of this, it would be interesting to know how the cited concentration was selected.

Jan 1, 1983

By Herbert H. Kouns, Harlan W. Nelson, Bruce O. Buckland

GASIFICATION of coal under pressure produces a gas that may be used as the fuel in a gas turbine. The pressure produced by a gas-turbine compressor (5 to 9 atm) should allow the use of high firing rates without unreasonably high solid carry-over rates. Hot make-gas with the tars contained in it in the vapor form can be used in a gas turbine. Most of the ash can be removed through a grate, and only a small portion of the ash and any of the solid combustible material carried over by the make-gas requires separation. The gas stream from which separation is required is a small portion of the total flow of a gas-turbine plant and hence the separator size will be small. The gas stream is reducing and will not, therefore, allow separator fires to occur. The response of the producer to rapid load changes is satisfactory. Only the air rate must change substantially in synchronism with the load. The coal feed, the steam addition to the blast, and the ash-removal rate can follow the load changes with time lags in the order of minutes. The necessary control equipment is simplified by these producer characteristics. With these possibilities in mind, the Steam Turbine Division of the General Electric Co. made arrangements with Battelle Memorial Institute in January 1945 to investigate the problems of the gasification process. A number of tests were made during this investigation on an updraft producer with a grate area of 1 sq ft. The equipment used has been described and the results of the tests made between 1946 and 1950 have been reported.1 The testing with this small producer was recently completed. The concluding tests were run to determine the effectiveness of a clinker-grinding grate and the effect of the operating conditions on the amount and character of the solid carry-over. The present paper describes the producer as modified, and gives the results of the tests using three coals. Another method of using coal in gas turbines is to pulverize it and burn it directly in the combustion chambers. This plan is being tried by the Loco- motive Development Committee of the Bituminous Coal Research, Inc., whose investigation has reached the stage of tests of full-sized equipment.

Jan 1, 1953

By John Chipman, Wayne L. Worrell

Using recent thermodynamic data for the carbides and oxides of tantalum, columbium, and vanadium, the stable solid phases aboue 1300°K and at 1 atm CO(g) pressure in each M-C-O system have been determined. Pourbaix-Ellingham diagrams have been constructed and are used to estimate the minimum temperatures necessary to obtain these metals by carbothermic reduction under reduced pressures. TANTALUM, columbium, and vanadium react with carbon to form the M,C and MC carbide phases. The M,C carbides have narrow homogeneity ranges, but the MC phases possess considerable ranges of homogeneity.' The free energies of formation of the MC carbides were recently measured, and those of MC and M2Ccarbides have been estimated., (The notations MC and MC denote, respectively, the carbide compositions at the carbon-rich and at the metal-rich boundaries of the homogeneous MC phase.) In this paper, these carbide data are combined with thermodynamic data for the oxides to predict the stable phases in the Ta-C-O, Cb-C-O, and V-C-O systems at specified temperatures and oxygen pressures. M-C-O PHASE DIAGRAMS The solid phases in equilibrium above 1300°K for each M-C-0 system are shown in Figs. 1, 2, and 3. Above 1300°K, the vapor would consist entirely of carbon monoxide; and these phase diagrams were obtained by specifying the vapor pressure of CO(g) to be 1 atm. The temperature at which any two solid phases become unstable is specified along the two-phase equilibrium lines in each diagram. To simplify the diagrams, all solid phases in the Ta-C-O and Cb-C-O systems are represented as stoichiometric compounds. However, the homogeneity ranges of VO and VC are indicated, because they form a complete series of solid solutions.3 It also should be noted that the homogeneity range of

Jan 1, 1964

By G. F. Bolling

STUDIES of grain boundary migration in zone-refined metals have all shown that the rate of migration is greatly reduced by small added solute concentrations. However, it is apparent that a difference exists between boundary migration during normal grain growth and single boundaries migrating in a bicrystal to consume a substructure. To effect the same reduction in velocity in the two cases, much more solute is required for grain growth than for the single boundary experiments. One case is available for direct comparison; both Bolling and winegardl and Aust and utter' added silver and gold to zone-refined lead to study grain growth and single boundary migration, respectively. For comparable reductions in migration rates, about 500 times more solute was required to retard grain growth than to retard the single boundaries. A reason for this difference is suggested here. The rate of grain boundary migration is dependent on solute concentration and must therefore also depend on the solute distribution; i.e., regions of higher solute concentration encountered by a moving boundary must produce greater retardation and thus could determine any observed rate. A dislocation substructure can be the source of a nonuniform solute distribution since it can attract an excess concentration of certain solutes. In fact, it is probable that the solutes which impede grain boundary migration most would segregate most severely to a substructure for the same reasons. Thus a dislocation substructure present in a crystal being consumed could locally magnify the concentration of solute confronting an advancing grain boundary. In the single boundary experiments a low-angle substructure, within single crystals obtained by growth from the melt, was used to provide the driving force to move a grain boundary; in grain growth, no substructure of this magnitude was present. The increased solute concentration at subboundaries should be given approximately by C, = G e c,/kT, where t, is a binding energy and CO the bulk concentration. To account for the difference between the two experiments in the Pb-Ag and Pb-Au cases, C, must be the concentration impeding the single boundary migration, and a value of t, = 0.25 ev is necessary. This is reasonable, even though calculation on a purely elastic basis gives t, = 0.12 ev. because electronic effects must enter for silver and gold in lead. The compound AuPbz forms3 and the metastable compound AgrPb has been reported to nucleate at dislocations prior to the formation of the stable, silver-rich phase.4 Other observations support the hypothesis that a magnified solute concentration impedes the single boundary migration. For example, some crystals were grown by Aust and Rutter at concentrations of ~ 0.1 wt pct Sn and 2 x X at. pct Ag or Au which exhibited a cellular substructure, and in these crystals no boundary migration was observed. It is therefore evident that the higher concentrations at cell boundaries drastically inhibited migration. Inclusions would not have been responsible for this inhibition since according to recent work on cellular segregation,5 no second phase should have occurred in the segregated regions at the cell boundaries for the conditions of growth used, at least in the Pb-Sn system. In the purest lead, only the "special" boundaries observed by Aust and Rutter gave rise to the same activation energy as that obtained in grain growth. It is reasonable to suppose that the structure of special boundaries does not favor segregation at low concentrations and thus solute, or an inhomogeneity in its distribution, would have no effect. Random boundaries, on the other hand, are affected by solute and the substructure would enhance residual concentrations in the zone-refined lead, leading to a higher activation energy. It is clear, even without a detailed theory, that the apparent activation energies and exact solute dependence in the two experiments must be different as long as the non-uniform solute distribution produced by the substructure is important. Recrystallization experiments should also be susceptible to the same kind of local segregation at subboundaries or disloca tion cell walls; a suggestion similar to this has been made by Leslie et al.' Following the arguments presented here, the effects of a given solute concentration would be like those observed by Aust and Rutter if segregation occurred, and like those of grain growth otherwise. This work was partially supported by the Air Force Office of Scientific Research; Contract AF-49(638)-1029.

Jan 1, 1962

By S. A. Falconer

Much attention and publicity has been given, during recent years, to grinding, classification, flotation, and thickening. The various technical papers, and symposiums held to discuss these important phases of milling, have contributed to a better understanding of the fundamental principles and operating variables involved. Another important part of milling— to the flotation operator—is a treatment step to which frequently too little attention is given—"conditioning," or the treatment the ground mineral pulp receives before it enters the flotation machines. "Conditioning" is a hackneyed and frequently misused term, commonly employed to describe the pretreatment of surfaces of minerals in ore pulps or mill products prior to froth flotation. In general, such pretreatment is for the purpose of changing the flotation characteristics of these mineral sur- faces to enable them to respond in some desired predetermined manner when subjected to flotation. Taggartl states that the function of conditioning is "either to insure selective collector coating of one mineral species while another species is not; or to take such steps as will compensate for departure therefrom." As 0. C. Ralston has stated? ... we are still faced with the fact that some mineral particles are water-avid, others air-avid, and that by properly modifying them they may be enhanced or diminished in desirable or undesirable avidity. Coatings on minerals must still be assumed to fall into three classes: (1) a coating of immiscible oil, (2) a layer of adsorbed substance, (3) a chemically produced coating. It is submitted that the process of preparing mineral surfaces for subsequent flotation treatment should take into consideration physical as well as chemical means for altering the normal flotation response of the mineral surfaces. A more descriptive word than "conditioning" is needed to designate broadly these procedures. The minerals in many ores cannot be made to respond in a normal manner to usual methods of "conditioning" with selectivity modifying reagents, until they have been cleansed, or interfering slimes and soluble salts have been removed from the ore. Therefore, it appears important to include under the general subject of "conditioning" a discussion of the purposes, methods used, and some of the advantages of these pretreatment steps. This is dealt with under the subject heading " Initial Treatment of Mineral Surfaces and Ore Pulps." Under this broader interpretation, the methods employed for treating mineral surfaces to alter their flotation characteristics may be divided into three general classes: 1. Physical methods.

Jan 1, 1950

By Donald F. Taylor

TANTALUM and columbium are newcomers in the world of metals. Many of the metals described in this volume had been known and used for centuries before either tantalum or columbium was known to exist. The scarcity of the ores and the comparative difficulty of extraction delayed their technology until specialized methods of processing could be developed. HISTORY Early in the nineteenth century, 1801, Hatchett discovered a new oxide, which he called columbium oxide, and a year later, Ekeberg announced that he had found a new element, which he named tantalum. The preparation of the metal tantalum in impure form was first announced by Berzelius in 1824, but the actual production of ductile metal did not occur until 1903, when von Bolton, of Siemens and Halske, developed a process for the production of tantalum pure enough to be drawn into electric-lamp filament wire. The use of tantalum as a filament wire began to decline when ductile tungsten was introduced in 1909. In 1921, C. W. sake, of Fansteel Metallurgical Corporation, produced the first ingot of tantalum metal in America. The first ingot of columbium was produced in 1927 in the laboratory of the same company. There are several good reasons why tantalum and columbium are often mentioned together. They occur together in their important minerals, are similar in many of their properties, and are

Jan 1, 1953

By Robert J. White

Strong's equation for calculating bottom-hole pressure reduction due to gas cutting of drilling mud is corrected, resulting in a simpler equation which is easier to use. Use of the equation is illustrated by examples. It is shown that reduction of weight of a 10 lb/gal mud by 50 per cent at the surface due to gas cutting produces only n 3 per cent decrease in hydrostatic head at the bottom of a 5,000-ft well. It is also shown that at the surface 5 volumes of air per volume of mud are required to reduce the apparent mud weight from 8.5 to 6.5 lh/gal in a 3,000-ft well. Illustrative graphs are included to show the effect of various degrees of gas cutting on apparent mud weight at depths of 2,000, .5,000 and 10,000 ft and to show variation of apparent mud weight, with depth for a 100 lb/cu ft (13.37 lb/gal) mud gas cut to 90 lb/cu ft (12.03 lb/gal) at the surface. INTRODUCTION In 1938, Strong' published the following equation for calculating reduction in bottom-hole pressure due to gas cutting of drilling mud h = 1/D [p + pn/100 In p + p(1-n/100)/p(1- n-100)] where: h = depth in feet P = pressure in atmospheres at depth h due to mud column only D = hydrostatic pressure in atmospheres of a col-umn of uncut mud 1 ft high p = back pressure at well-head (in atmospheres) n/100 = fraction by volume of gas in mud at well-head at back pres-sure p This equation was recently found to contain an error due to an incor-rect expression for variation of vol-ume fraction of gas with pressure. Values calculated by the original equation are close to the correct values for small percentages of gas for which it was derived but become increasingly erroneous as the gas content increases and are completely unusable at the very high gas con-tents employed in aerated mud. DERIVATION The nomenclature used is the same as in Strong's paper. The pres-sure dP exerted by a lamina of thickness dh at a depth h ft is ex-pressed by Eq. 1 where x = volume fraction of gas at depth h dP = D (l - x)dh . . . (1) When we express x in terms of the wellhead per cent gas n, the well-head pressure p and the pressure P at depth h, the result is Eq. 2. x = (np/p+p)/(100-n) + (np/P + p) When this is substituted in Eq. 1 and rearranged to separate the var-iables the result is dh = 1/D [dp + np/100-n dp/(P + p]. Integration between appropriate lim-its results in or if the wellhead is open so that p = 1 atm and we rearrange Eq. 4, the result is loss in head = hD — P = n/100-n In (P + 1) ...(5) Eq. 5 can be solved easily by successive approximation using hD as a first approximation for P on the right-hand side and calculating a first value for loss in head. This can then be used to get a new value of P using the left-hand side of the equation. Values converge very rap-idly even for quite large values of per cent by volume gas n. EXAMPLES The effect on bottom-hole pressure of 50 per cent gas cutting of the mud in a 5,000-ft well using 10 Ib/ gal mud will be calculated, we have: h = 5,000 ft 10 X 7.48 144 X 14.7 = 0.0353 atm/ft hD = 176.5 atm n = 50 Substituting these values in Eq. 5 and using hD as a first approxima-tion of P on the right, we have, approximate loss in head = 50/50 In (176.5 + 1) = 2.30 log 177.5 = 5.17 atm. We calculate a new value of P as follows:

Jan 1, 1958

By Klaus Detert

Fifteen and 18 pct Ni maraging steel and several binavy and ternary alloys of the iron-rich corner of the Fe-Co-Ni system have been studied. After annealing in the austenite range, these alloys were deformed slightly by cold rolling and subsequently aged. Compavison of experimental measurements at various processing stages indicates that small degrees of deforn~ation (5 to 10 pct reduction in thickness) do not influence hardness and strength or the aging kinetics. Electrical resistivity and ductility are somewhat redu]ced and the coercive force is substantially lower when compared to identical samples which were not deformed. The results are explained in terms of retained austenite which transforms into martensite with the small amount of deformation. RECENTLY there has been increasing interest in maraging steel for applications in electric power generators requiring a high ratio of power to weight.' Fifteen pct Ni maraging steel has been investigated to evaluate its properties and performance for application as high-strength magnetic rotor steel,' and a thorough investigation of the precipitation and transformation processes in this alloy has been conducted in this laboratory.3 The influence of deformation, which preceded the aging treatment, was also studied. It was found that a small deformation in the order of 5 pct has a rather striking effect in reducing the coercive force. Other interesting effects on the properties caused by such deformation have led to the more detailed studies reported herein. EXPERIMENTAL METHOD The methods used to produce the samples from 15 pct Ni maraging steel have been described elsewhere.3 The general procedure of hot forging and cold rolling to sheet has been followed. The composition is included in Table I which also contains the composition of the 18 pct Ni maraging steel grade 250 studied. More data about the material and the processing of the 18 pct Ni maraging steel have been recently reported.4 The experimental alloys of binary and ternary Fe-Ni-Co alloys were made by levitation melting in an argon atmosphere and casting into rod-shaped ingots 7 mm thick weighing 20 g. From these ingots 25-mm-long rods were machined to study the phase transformation by a dilatometer. These rods were then cold-rolled to strips, 2.4 mm thick. Annealing for austenitizing was done in tube furnaces in an argon or helium atmosphere followed by cooling in the water-cooled portion of the tube. Aging was done in a salt bath containing a neutral blend of Alkali nitrates and nitrites. Vickers hardness was measured using a load of 50 kg for 15 sec. Tensile tests were carried out on a hard beam tensile tester at a strain rate of 5 X lo-' per sec using flat samples with a gage length of 37.5 mm and a cross section of 1.25 by 6.25 mm. Estimated sensitivity was 5 K x strain and 0.35 kg per sq mm stress. Magnetic saturation was determined on small cylindrical samples, 2.5 mm in length and diameter, by measuring the force exerted by the gradient of a magnetic field of 1000 oe per cm in a mean field of 11,500 oe. The measured values could be reproduced within *1 pct. Coercive force was measured by a precision-type magnetic field probe in a magnetic coil as described by Foerster.5 The magnetizing field was 1300 oe. The samples were 5 cm long, 1 cm wide, and 2.4 mm thick. he coercive force was measured to within +0.1 oe. Electrical resistivity was measured by using a potentiometer on flat strips with a gage length of 100 mm and a cross section of 2.5 by 0.5 mm. The accuracy of the measurement was 0.1 pct but the reproducibility of the measured specific resistivity among different samples was in the order of 1 pct. The method used to prepare the samples for electron transmission has been reported elsewhere.3 RESULTS Fig. 1 shows the influence of deformation after annealing on the resistivity, hardness, and coercivity. The samples were annealed for 30 min at 1000"C,

Jan 1, 1968

By H. D. Merchant

NUMEROUS publications have examined hot hardness of metals and alloys. Some have studied creep in long-time hardness tests, few of which, however, were tested under a spherical indentor. 1-3 The results of Mulhearn and Tabor' indicate a parabolic-type creep for indium and lead, whereas Moore and Tabor2 how a logarithmic-type creep for indium. Similar semilog relationships between hardness and time have been found by Goffard and wheeler3 for magnesium, aluminum, and their alloys. In this note, the elevated-temperature hardness of some complex alloys, shown in Table I, was examined to discover whether any basic information about the deformation behavior of the alloys could be obtained. One of the alloys, H-13 alloy steel, was tested for short-time creep tests to examine the hardness-time relationship at various temperatures. A standard Brinell Hardness Tester, mounted with an appropriate furnace and 99 pct A12O3 poly-crystalline indentor, was employed for the purpose. The alloys were tested at temperatures from room to 1400°F for 30 sec under 1500-kg load. The creep studies were conducted for about 8500 sec at 7l°, 500°, 1000°, and 1200°F. For constants A and B, a relationship of the type H = Aexp(-BT) [ll was obtained for all alloys between hardness, H, and temperature, T. In the semilogarithmic plot, the data points for each alloy were arranged into two groups, each group on a straight line with a specific set of A and B values. These results are in agreement with many such observations on hot hardness, notably those of Westbrook for pure metals,4 The thermal softening coefficient, B, and transition temperature, Tt, for various alloys are shown in Table I. The change in slope around the transition temperature suggests an apparent change in the mechanism of deformation, probably from the shear (below Tt) to the diffusion type of mechanism. At the temperatures above Tt, for constants A' and B, a relationship of the type was obtained between H and T, Fig. 1. The nature of the equation, where R is gas constant, suggests the possibility of a thermally activated mechanism of deformation above Tt. The constant B' may hence be defined as the apparent activation energy of indentation. The B' values of various alloys are shown in Table I. A plot of B vs B' gives a curvilinear relation shown in Fig. 2. The indentation-creep data for H-13 alloy steel is shown in Fig. 3. At 71" and 500°F, the creep initially follows the logarithmic time law. However, the indentation size stabilizes after 7 sec at 71°F, and after 10 sec at 500°F. Further increase in loading time has no effect on indentation size. The creep of 1000° and 1200°F follows the logarithmic time law for the first 1000 sec, after which the

Jan 1, 1964

By Frank Firmstone, Kenneth Robertson

Peculiar crusts having appeared on certain irons made at Glendon and Pequest, which, in our experience, were entirely new, some analyses of them were made; and these analyses, together with an account of the manner of appearance of the crusts, are herewith submitted to the Institute. At Pequest the ores mere: & Peters, from Ringwood, N. J.; + roasted sulphurous ore, from Charlotteburgh, N. J.; and + red ore (decomposed magnetite), from Chester, N. J. The fuel was 7/8 Lehigh anthracite and + Connellsville coke, and the limestone a dolomite from Andover, N. J. The resulting iron varied in silicon from 0 84 per cent. in No. 1 foundry to 0.51 per cent. in gray forge; in phosphorus, from 0.81 per cent. to 0.55 per cent.; sulphur, 0.035 per cent.; manganese, 0.375 per cent. It was highly "chilling" in its properties, and very strong. In running, it invariably appeared to be of a lower grade than it really was; the higher grades scintillating as much as hard iron usually does. After getting into the moulds, and beginning to cool, a black crust began to show itself, seeming to exude from the pigs, till finally, when the iron was cold enough to break, it completely covered the face of the pigs. At this time it was dense black, but after some exposure to the air it ac .

Jan 1, 1884

By Ernest Gayford

This is a nontechnical paper on flotation, subdivided under three general headings: (I) Definition of flotation; (2) what flotation is now doing in Utah; and (3) what is the future of flotation? Definition T. A. Rickard defines flotation' as "the act or state of floating," from the French flottaison, water-line and flotter, to float. The dictionary defines flotation as "the science of floating bodies." The flotation process is a method of concentrating ores by frothing. Weinig and Palmer,2 define flotation as follows: What is the flotation process? Briefly, it consists in the agitation of finely divided ore in water containing bubbles of air or gas, a small amount of oil and, usually, other reagents, soluble and insoluble; under these conditions the small particles of native metals, sulfides, arsenides, antimonides, selenides and tellurides show a tendency to attach themselves to the films of the bubbles, and are thus carried to the surface of the water. The oxidized gangue minerals, such as quartz, feldspar, limestone, hematite, etc., show much less affinity for the bubbles, are easily wetted by the water, and either remain in suspension in the water, or sink to the bottom of the vessel. If the bubbles are sufficiently stable they can be removed, carrying their load of sulfide-mineral particles with them. Thus there can be effected a separation of the two classes of minerals from each other, assuming that the grinding has been sufficient to unlock all of the particles of different composition. The separation does not depend upon differences in specific gravity of the various minerals; in fact, the sulfides are usually heavier than the oxides, and some of the heaviest sulfide minerals are the easiest to float. A particle of mineral may be so large, however, that its weight will counteract its affinity for the film of the bubble. In most cases the ore must be fine enough to pass a screen having at least 48 meshes to the linear inch. Taggart3 defines flotation as follows: Flotation is a method of wet concentration of ores in which separation of mineral from gangue is effected by causing the mineral to float at or above the surface of a body of liquid pulp while the gangue becomes or remains submerged. The method

Jan 1, 1928

By Ernest Gayford

THIS is a nontechnical paper on flotation, subdivided under three general headings: (1) Definition of flotation; (2) what flotation is now doing in Utah; and (3) what is the future of flotation? . DEFINITION T. A. Rickard defines flotation1 as "the act or state of floating," from the French flottaison, water-line and fitter, to float. The dictionary defines flotation as "the science of floating bodies." The flotation process is a method of concentrating ores by frothing. Weinig and Palmer 2 define flotation as follows: What is the flotation process? Briefly, it consists in the agitation of finely divided ore in water containing bubbles of air or gas, a small amount of oil and, usually, other reagents, soluble and insoluble; under these conditions the small parti- cles of native metals, sulfides, arsenides, antimonides, selenides and tellurides show a tendency to attach themselves to the 6lms of the bubbles, and are thus carried to the surface of the water. The oxidized gangue minerals, such as quartz, feldspar, limestone, hematite, etc., show much less affinity for the bubbles, are easily wetted by the water, and either remain in suspension in the water, or sink to the bottom of the vessel. If the bubbles are sufficiently stable they can be removed, carrying their load of sulfide-mineral particles with them. Thus there can be effected a separation of the two classes of minerals from each other, assuming that the grinding has been sufficient to unlock all of the particles of different composition. The separation does not depend upon differences in specific gravity of the various minerals; in fact, the sulfides are usually heavier than the oxides, and some of the heaviest sulfide minerals are the easiest to float. A particle of mineral may be so large, however, that its weight will counteract its affinity for the film of the bubble. In most cases the ore must be fine enough to pass a screen having at least 48 meshes to the linear inch. Taggart defines flotation as follows : Flotation is a method of wet concentration of ores in which separation of mineral from gangue is effected by causing the mineral to float at or above the surface of a body of liquid pulp while the gangue becomes or remains submerged. The method

Jan 1, 1928

[RALPH ADAIR Ore Dressing Consultant Bull Mtn. Rd., Asheville, N. C. Phone 4-1693 JAMES A. BARR Consulting Engineer Mt. Pleasant, Tennessee Washington, D.C. BEHRE DOLBEAR & COMPANY Consulting Mining Engineers and Geologists 11 Broadway New York 4, N. Y. I. R. BERENT Engineering Consultants and Contractors Mineral Exploration, Mine Evaluation, Mine Designs and Mine Management 156, Ataturk Bulvarl-Ankara, Turkey BLANDFORD C. BURGESS Registered Professional Engineer Mining Consultant Monticello, Georgia GLENVILLE A. COLLINS Mining Engineer Uranium examinations Cable "Coins" 8 Howard-Canfleld Bldg. Santa Barbara, Calif. COWIN & CO. Mining Engineers and Contractors Consulting Shaft & Slope Sinking Appraisal Mine Development Reports Mine Plant Construction I- 18th St. S. W. B'ham, Ala., Phone 56-5566]

Jan 1, 1952