By A. H. Cottrel

SINCE metallurgy exists to provide strong, tough, engineering materials it must inevitably be perpetually concerned with the problem of brittle-ness. The steel-making industry was created because chemically unrefined iron is brittle. The steel-working and alloy-steel industries exist partly because hardness and ductility are mutually exclusive qualities in structurally unrefined steel. Yet, in spite of these immense industries, the brittle failure of steel ships hulls, bridges, pressure vessels, and pipelines, is still a contemporary problem. In fact, brittleness is a normal property of most solids, including metals and alloys, at low temperatures. Only face-centred cubic metals are commonly ductile at the lowest temperatures, and even here exceptions are known.'," Expensive are-melting processes. under inert gases or vacuum, have been developed to overcome brittleness in titanium, zirconium, columbium. and molybdenum. Polycrystal-line zinc, magnesium, and uranium have little ductility at room temperature. Beryllium, chromium, and tungsten have even less; similarly for antimony, bismuth, germanium, silicon, intermetallic compounds, and metallic carbides, nitrides, silicides, and borides. Oxides and other ceramics would be ideal creep-resistant materials but for their extreme brittleness when cold, and great efforts have been made to overcome this problem by mixing ceramics with metals. In fact, the traditional use of the name metallurgy for what is really the science of engineering materials is a recognition that most non-metallic solids have so far been precluded, by their extreme brittleness, from use as major structural materials in mechanical engineering. Most of what we know about brittleness in metals has come from studies of structural steel, and it is this material that shall mainly be considered. The things we have learned from it have a wider application, at least to other body-centred cubic transition metals, although the extent to which similar ideas can be applied to hexagonal metals and other materials is not yet clear. Fracture and Plastic Deformation The theoretical breaking strength of an ideal solid, about E/10 where E is Young's modulus, has been approached reasonably closely in experiments on fibres. But large specimens break at much lower stresses. For example, brittle cracks in large structural steel assemblies have been observed to spread catastrophically at speeds of 6000 ft per sec under stresses of about 10,000 psi, i.e. about E/3000. There are two sources of weakness; stress concentrations, and chemical agents in grain boundaries or on crack faces that lower the surface energy y of the material. Although we shall deal mainly only with the first of these, much of the discussion is also applicable to the second when different values of y are used. Griffith's well-known formula p = [ 2Ey/p(1 - v2)c]1/2 [1] gives the smallest tensile stress p able to propagate an atomically sharp surface crack of length c or interior crack of length 2c through a thick plate (compared with c) of elastically isotropic material of

Jan 1, 1959

By J. H. Moran, E. E. Finklea

The pressure build-up technique is a recognized method of determining permeability from conventional drillstem tests. In this paper an effort is made to extend such techniques to the interpretation of data obtained from the wireline formation tester. Such a study is necessary because of the differences, for this case, in the magnitude of the flow parameters (rate of flow, amount of recovered fluids) and in the flow geometry (flow through a perforation vs flow across the face of the wellbore, etc.) involved in the solution of the equations of flow for compressible fluids. The perforation is replaced by a spherical hole, and the effect of the borehole is neglected, so that the flow can be considered to be radial in a spherical co-ordinate system. Arguments are presented to justify this idealization. Assuming single-phase flow, general relations between pressure and flow rate are developed for a homogeneous medium. The study is then extended to permeable beds of finite thickness. It is shown that the early stages of pressure build-up tend towards spherical flow, while the later stages tend towards cylindrical flow. The thinner the bed, the more quickly flow approaches the cylindrical model. The prevalence of thin beds in practical work makes this analysis quite important. Cases involving permeability anisotropy are treated. INTRODUCTION From wireline formation tester operation, two types of data are obtained: (1) the nature and amount of recovered fluids, and (2) the pressure history recorded during the test. A number of papers have been written dealing with the interpretation of formation production on the basis of the recovered fluids.'.' In general, the methods described have been quite accurate for both high- and low-permeability formations. The present paper will deal with an analysis of the pressures observed. An analysis of the pressure build-up curves obtained in hard-rock country has already been attempted on the basis of the formula proposed by Hor-ner. Although this approach has met with success in many instances, some questions have been raised as to its validity. It is the aim of the present study to place the analysis of pressure build-up in the formation tester on a firmer basis, from which more detailed methods of interpretation can evolve. Because of the great differences between the operation of the wireline formation tester and the conventional drillstem test, modifications are necessary in the interpretation. The major difference relates to the flow geometry. Once the flow geometry has been established other features such as multiphase flow, skin effect, afterflow, etc., well described in the literature, can be introduced. It will be assumed that the mechanical operation of the formation tester is already known to the reader.6 t will suffice here merely to state that the tester provides the means for taking a relatively small sample of the fluid immediately adjacent to the borehole, and for recording the subsequent pressure response. In comparison with conventional drillstem tests, the time required for a satisfactory pressure build-up response is much shorter, because of the relatively small quantity of fluid withdrawn by the wireline tester. This feature is highly desirable in the case of low-permeability formations. For an analysis of the pressure response within the formation, three simple flow geometries are considered— linear, cylindrical and spherical. The spherical and cylindrical flow geometries are most pertinent to the formation tester; therefore, they will receive the major emphasis. Since the configuration of the borehole and the perforation made by the tester complicate the flow geometry, it is necessary to allow for them in the drawdown response. However, because of the volume of formations contributing to the pressure-response, the details of the perforation shape are unimportant in the build-up period. Since relatively small amounts of fluid are withdrawn from the formation, in contrast to a conventional drill-stem test, a study of the "depth of investigation" and the significance of drawdown as well as build-up data will be included. Because the "depth of investigation" will be shown to be rather large, the effect on the build-up curves of the finite thickness of the permeable bed is considered. It is this consideration that leads to the importance of cylindrical flow geometry. Also included is a discussion of permeability anisotropy and its effect on the interpretation of the tester results. The pressure curves recorded by the formation tester will follow two general patterns, depending upon whether the formation is of high or low permeability. Fig. I (a and b) schematically illustrates these two responses. In Fig. 1(a), the high pressure recorded during fill-up of the tool is essentially the pressure differential across the choke in the system. In Fig. l(b), the flow rate is

By C. G. Dunn, E. F. Koch, K. T. Aust

Strain-induced grain boundary migration was studied in a series of silicon-iron (3% pct Si) bicrystals of controlled orientations. Each bicrystal was given a 7 pct cold-rolling strain rind annealed at 1100°C. The direction of boundary migration was found to depend on orientation; results for several orientations related by a common [110] axis are given. Analysis of the micrographic and X-ray data is made in terms of the residual strain-energy densities within the crystals (energy per unit volurne) and a driving force on the boundary due to an energy density difference across the boundary. Relative strain energies were obtained for the various orientations investigated. A CHROME-acetic acid electroetching method for revealing dislocation sites in silicon iron was previously applied to clarify the structural features and the energetics involved in strain-induced grain boundary migration.',' The present paper is a continuation of this study, but is primarily concerned with the influence of crystal orientation. Sperry, as reported by Beck,3 attempted to determine the factors that influence the preferred growth of one grain over another in aluminum due to strain-induced boundary migration. He found that the particular grain of a pair which work hardened more was invaded, although exceptions to this correlation were noted. The index of work hardening was determined from microhardness measurements of each grain before and after cold-rolling. In the present study, orientation itself was taken as a useful variable for studying the behavior of individual grains in a bicrystal and the direction of boundary migration, since the extent of work hardening is orientation dePendent." The effect of strain on boundary migration is evident from a consideration of driving forces. Thus, in the absence of inclusions, the driving force (per unit area of boundary) for growth of grain A into grain B when a bicrystal is strained and annealed may be expressed as follows:2

Jan 1, 1960

By J. M. Morris

The point to be made most clear in this paper is the economic value of flotation in the Benguet mill flow sheet. It is rather a statement of effect with no attempt at a technical explanation of the cause. Certain well-known, easily understood reagents, mechanisms and principles have been adapted to the conditions at Benguet, and have proved to be more successful than was demonstrated in the laboratory. The mechanical and metallurgical development of this particular operation was arrived at by trial and error, with fortunately very little error. Changes were slow, of necessity, which in the end proved a blessing in that time was afforded for observation and analysis of the disturbing factors; and as a result each change was a definite step towards higher efficiency. Many of these steps were unpredictable from laboratory work because of the varied and differing characteristics of ores met with in daily operation of the mill, which were practically impossible to reproduce on a laboratory scale. The Benguet mill receives daily ores that differ as much as if they were delivered from three different properties. There is first the surface and upper-level zone, which produces an oxidized secondary ore containing considerable iron oxide, manganese oxide and some organic matter. Formerly, most of this ore consisted of very soft fill with some hard rock mixed in. It also contained an unusual amount of iron and aluminum sulfate, which formed hydrates upon entering the alkaline cyanide solution and caused excessive frothing. When flotation was introduced in the Benguet mill the general characteristics of this upper-level ore had changed considerably, in that it was practically all newly mined, fairly hard ore. It still contained many of the same disturbing elements, but was somewhat simpler to treat than formerly. The small proportion of fines is still troublesome in flotation, and plant practice probably does not show more than 80 per cent extraction on this small portion of the ore. No definite figure on this is available, as this particular ore is delivered at irregular intervals

Jan 1, 1939

By J. M. Morris

The point to be made most clear in this paper is the economic value of flotation in the Benguet mill flow sheet. It is rather a statement of effect with no attempt at a technical explanation of the cause. Certain well-known, easily understood reagents, mechanisms and principles have been adapted to the conditions at Benguet, and have proved to be more successful than was demonstrated in the laboratory. The mechanical and metallurgical development of this particular operation was arrived at by trial and error, with fortunately very little error. Changes were slow, of necessity, which in the end proved a blessing in that time was afforded for observation and analysis of the disturbing factors; and as a result each change was a definite step towards higher efficiency. Many of these steps were unpredictable from laboratory work because of the varied and differing characteristics of ores met with in daily operation of the mill, which were practically impossible to reproduce on a laboratory scale. The Benguet mill receives daily ores that differ as much as if they were delivered from three different properties. There is first the surface and upper-level zone, which produces an oxidized secondary ore containing considerable iron oxide, manganese oxide and some organic matter. Formerly, most of this ore consisted of very soft fill with some hard rock mixed in. It also contained an unusual amount of iron and aluminum sulfate, which formed hydrates upon entering the alkaline cyanide solution and caused excessive frothing. When flotation was introduced in the Benguet mill the general characteristics of this upper-level ore had changed considerably, in that it was practically all newly mined, fairly hard ore. It still contained many of the same disturbing elements, but was somewhat simpler to treat than formerly. The small proportion of fines is still troublesome in flotation, and plant practice probably does not show more than 80 per cent extraction on this small portion of the ore. No definite figure on this is available, as this particular ore is delivered at irregular intervals

Jan 1, 1939

By D. R. Hay, E. Scala

STUDIES of structure-sensitive properties, especially mechanical behavior, have shown that grain and subgrain structure play an important role. The mechanical properties of tungsten, in particular, are sensitive to the nature of the intergranular structure. Substructure and dislocation networks in single-crystal and polycrystalline tungsten have been studied by Nakayama et al.' Various orders of substructure were observed ranging from a microscopic first order (grain diameter: 2 to 8 mm) to a microscopic second order (grain diameter: 50 to 300 p), and, within the latter, dislocation networks forming an even smaller order of substructure. In their single crystals, grown by arc fusion, the degree of misorientation in each order was small: 16'3OU, -11, and -10" for the first-, second-, and third-order substructure, respectively. To study the properties of polycrystalline tungsten, powder metallurgy tungsten is generally used. However, in a mechanical property investigation, the zone-melted or arc-fusion crystals are more desirable than the powder metallurgy product due to their higher purity and absence of porosity and other defects inherent in consolidation by powder metallurgy. Grain boundaries can also be produced in melted stock by working and recrystallizing. However, material with subgrain mis orientations of the order of several degrees (high-angle substructure) has not been reported previously and is the subject of this communication. Crystals were grown by electron-beam, floating-zone melting. The starting material, Sylvania Pure-tung welding rod, was given one zone pass at a traversal rate of -2 mm per min. Through control of the zone temperature, it was possible to influence the degree of crystal perfection. By maintaining the zone at a high degree of superheat, high-perfection crystals could be grown. However, at temperatures only slightly above the melting point, the zone-melted crystals contained a high-angle substructure. A sensitive control of the zone temperature was not possible due to the difficulty of estimating the temperature of the zone and of providing a constant supply of power to the sample. Therefore, an empirical method, using the shape of the molten zone as a criterion, was adopted as an indication of temperature. At high degrees of superheat, the surface tension of the molten zone decreases and a neck forms at the top of the zone, whereas at low zone temperatures the diameter of the zone remains reasonably uniform. Although it was not possible to obtain a continuous variation of misfit angle, the conditions could be directed toward the growth of either high- or low-angle substructure by maintaining only a slight neck in the zone (sufficient to establish that it was molten) or a well-necked zone, respectively. Mass spectrographic analyses of both types of material revealed no significant differences in the concentrations of their impurities. The degree of misorientation at high angles was obtained by measuring the angular spread of spots corresponding to a single reflection on a Laue back-reflection photograph. Fig. 1 shows a typical Laue back-reflection photograph of a crystal with a 3-deg spread. By measuring the angular deviation of the spots corresponding to a single reflection from the mean center of the spots around which constant angular deviation contours were drawn, an average angular spread of misfit could be calculated. The angular average was weighted by the number of spots observed in each angular interval. At angles greater than 5 to 6 deg the spots from different reflections begin to overlap, and cannot be associated with a particular reflection. Laue back-reflection photographs taken at different locations on samples .with approximately 3-deg spreads showed only a small difference in angular misorientation, less than 8' of arc, within individual specimens. The microstructure was examined using Berg-Barrett X-ray extinction contrast microscopy. Berg-Barrett photographs taken directly on the as-grown surface, Fig. 2, show an essentially equiaxed subgrain structure of -0.1 mm in average grain diameter in both high- and low-angle crystals. Fig. 2(a) is a photograph of a sample with a low misfit angle and Fig.

Jan 1, 1968

By Y. L. Yao

THE NaT1-type compound may be considered as the penetration of two diamond lattices in such a way that a superstructure of the bcc lattice is formed. Examples of the NaT1-type compound of lithium are LiZn, LiCd, LiA1, LiIn, and LiGa. Except for LiZn and LiCd, each molecule of these equiatomic compounds contains a total of four valence electrons. In LiZn and LiCd it was suspected (for example, see Ref. 1) that the fourth electron was withdrawn from the 18-shell of zinc or cadmium. An incomplete 18-shell would have to show strong paramagnetism. In 1955 Klemm and Fricke2 determined the magnetic susceptibility of LiZn, LiCd, LiA1, and LiIn (also NaTl and NaIn). The molar susceptibility of the outer electrons of LiZn and LiCd was found to be not strongly but weakly positive; that of LiAl and LiIn not negative but weakly positive. Thus they questioned the hypothesis about LiZn and LiCd in particular and the description of the NaT1-type structure in general. However, they did not determine the magnetic susceptibility of LiGa. This note is to report results for all five compounds of lithium. The starting materials are 99.9 pct pure lithium sticks containing less than 0.005 pct Na. 99.9 pct Zn, 99.9 pct Cd, 99.99 pct Al, 99.999 pct In, and 99.999 pct Ga. Weighed amounts of two components were wrapped in tantalum foil and placed in a graphite crucible. It was found that the tantalum sheath minimized the vaporization losses of lithium during melting. The sheath was easily stripped from the alloy rod and the tantalum in the alloy was barely detectable (less than 0.01 wt pct). The melting was performed in a resistance furnace under an argon atmosphere. Alloy specimens were annealed for 1 hr at 400°C in vacuum. The magnetic susceptibility at room temperature was determined by the Faraday Method, using the procedures previously described.' The results are shown in Table I. The interpolated values at 50 at. pct of Li and the average values at 48 to 52 at. pct of Li at 20°C determined by Klemm and Fricke2 are also shown. It is seen that the present value for LiZn and LiCd is slightly more positive but the present value for LiAl and LiIn is slightly less positive than their corresponding values. Also, it is noted there is an abrupt decrease of susceptibility of LiAl from 51.2 to 52.5 at. pct of Li. Klemm and Fricke2 found that the total susceptibility of LiZn, LiCd, LiA1, and LiIn is almost independent of temperature. slater4 gave a working expression for the diamagnetism of the atomic core as follows:

Jan 1, 1964

By W. A. Wood, W. H. Reimann

A study is made of the creep that can be induced in armco iron at room temperature by superposing small amplitudes of alternating torsion on a tensile creep load. It is shown that the creep differs from that in comparable tests on copper in being trmsient only. At the same time, though transient, the creep can produce extensions of some 10 pct under creep loads less than the tensile yield stress of the material. The creep can be largely suppressed b$ applying cyclic strain of suitable amplitude before applying the creep load and the metal thereby stabilized. At room temperature, plastic flow in a metal under steady load is normally limited by strain-hardening processes. However, if a small cyclic stress is superposed on the steady load these processes may be more or less neutralized and, as shown in recent investigations,'-4 plastic flow may continue. In this way annealed copper, for example, can be induced to creep continuously to fracture under loads as small as 1 tsi. Dislocation mechanisms possibly responsible for this room-temperature creep have been usefully reviewed by Feltner.But discussion so far has been based mainly on creep as it is found in close-packed metals initially in the annealed state, and their behavior may not be general. In fact, recent work shows that the form of creep in annealed copper is different from that even in cold-worked copper;7 the creep thus depends on the dislocation pattern already in a metal as well as on the metal itself. This paper describes the creep in annealed armco iron, tested in the same way as the above-mentioned copper. One object was to see how creep in a typical bcc metal compared with that in the annealed close-packed metals. Another object was to utilize the fact that a bcc metal like iron has a more pronounced elastic range than close-packed metals like copper and to find to what extent the creep load or superposed cyclic stress had to exceed their re-

Jan 1, 1964

By Erwin S. Sperry

The presence of small amounts of tellurium in certain binds of copper, and its exceptionally deleterious* influence in producing red-shortness of this metal, led the author to conduct a few experiments on the influence of tellurium on the properties of brass. While these experiments were not intended to be exhaustive, they demonstrate that, as far as the rolling of brass is concerned, tellurium, unless it occurs in far greater amounts than exist in refined copper, cannot be called an injurious impurity. In comparatively large amounts it appears to impart cold-shortness to high-brass. Tellurium, the rare element that it is considered to be, has recently been extracted on a large scale from the slimes of an American electrolytic copper-works. They have, in attempts to discover some commercial use for it, sent it out promiscuously and gratuitously in quantities which would lead the young chemical student to fancy that a rare element exists only in name. Through the courtesy of Mr. R. L. Whitehead, of Baltimore, the author was able to obtain somewhat over 2 lbs.,? and use it in quantities which, at the market price, would be prohibitive. In order to add specific quantities of tellurium to brass, a rich alloy of copper and tellurium was previously made. The method was as follows, viz.: Nine and one-half lbs. of Lake copper were melted un-. der charcoal in a new plumbago crucible, and then pound of tellurium was added in small portions at a time. The mixture was stirred with a plumbago-stirrer and poured into

Jan 1, 1903

By F. F. Craig

The authors have done a commendable job in combining a number of recognized waterflood performance prediction methods into one composite method. The availability of a FORTRAN program for this composite method should encourage its widespread industry use. Pan American has had a computer program developed along similar lines for a number of years,' and it has received more use than any other reservoir prediction method. In three important stages of a pattern waterflood, the authors fail to consider fully the effects of water-oil mobility ratio on performance. This is discussed in the following paragraphs and modifications of the prediction method are suggested. During the early stages of a waterflood in a partially depleted formation, the injected water and its preceding oil bank move out radially from the injection wells. As pointed out in the author's paper the method of Yuster and Calhoun2 or predicting the water injection rate during this period assumes that the mobilities of the water and oil are equal. In his book, Muskat3 resents a modification of the Yuster-Calhoun approach that considers fully the influence of water-oil mobility ratio. In Muskat's method, the prediction of the injection rate-injected volume-time relationship is expressed in readily programmed dimension-less unts. At and following fillup the five-spot pattern consists of a water-invaded pattern with the remainder of the pattern containing only oil and connate water. In the paper, Eq. 18 is used to calculate the water injection rate at fillup. This equation considers that the entire pattern is invaded by water. To properly consider both the incomplete areal sweep of water and the water-oil mobility ratio, Eq. 18 should read:

Jan 1, 1969

By W. F. Hergert, L. H. Banning

Experimental production of Al-Si alloys, containing from 33 to 55 pct Al, by direct reduction of aluminum silicates in a three-phase arc furnace is described. Advantages of a smelting technique utilizing hogged wood waste as part of the reductant and for temperature control are discussed. WORK on the problem of producing aluminum by smelting has been in progress since the middle of the eighteenth century. Early work met with little success and in 1782 Lavoisier, an eminent French chemist, expressed the belief that alumina could not be reduced by carbon. It was almost a century later when the Cowles brothers developed a process for the production of aluminum alloys by reducing alumina coincident with the reduction of other metal oxides. In practice, the other metal oxide was usually copper. In 1907 it was first shown that alumina alone could be reduced by carbon at a temperature of 2200°C. The metal produced was volatilized and lost or recombined with the oxides of carbon formed in the reaction.' For a number of years after the Cowles brothers abandoned production of Cu-A1 alloys because their product was not commercially competitive with the aluminum produced by the Hall process, there was little interest in thermal reduction processes. After World War I interest in such processes was renewed and a number of patents were issued on processes for the production of A1-Si alloys.' , "he function of the silicon in these processes was the same as the function of the copper in the Cowles brothers process, namely, to prevent the reduced aluminum from recombining with the oxides of carbon and to promote absorption of the aluminum vapors set free at the high temperature required for the reduction reaction. The advantage of using silicon in place of copper for this function is that silicon has a higher boiling point (2600"C) than copper (2310"C) and its oxides, combined with aluminum oxides, occur in nature in almost unlimited quantities. No A1-Si alloys have been produced commercially in the United States, as far as is known. However, considerable experimental smelting of aluminum silicate materials has been done by the TVA at Wilson Dam, Ala.' The most extensive development and commercialization of the electrothermal production of A1-Si alloys took place in Germany before and during World War II.V he furnaces used in the

Jan 1, 1956

By Milo W. Krejci

The plant and quarries of the Inland Portland Cement Co. are located at Metaline Palls, Wash., about 128 miles north of Spokane, on the Pend Oreille river, and within 10 miles of the Canadian border. The plant is one of a chain of cement plants controlled by the Lehigh Portland Cement Co., of Allentown, Pa. Work on this plant was commenced in June, 1910, and was completed in April, 1911, but on account of some delays in the construction of the power plant, the works were not put into operation until August, 1911. Since then it has been in continuous operation and has furnished the Inland Empire with a high grade of cement. Fig. 1 is a view and Fig. 2 is a plan of the works. Water Power Development.—The source of the water supply for the hydro-electric plant of the Inland Portland Cement Co. is Sullivan lake, a body of water approximately 5.5 miles long and' 0.5 mile wide, situated in the Kaniksu Forest Reserve. A wooden crib dam was installed so as to raise the elevation of the lake 25 ft., and the additional storage capacity was taken up by the diversion of Sullivan creek into the lake by means of a wooden flume, 0.25 mile long, 6 by 8 ft. in cross-section, and a ditch 1,200 ft. long. The water from the lake follows the natural water course to an intermediate storage reservoir, which was created by the construction of an earthen dam. This pond was used in connection with the saw mill which was installed at this point. Besides the earth dam, there was also built a crib, at the point shown in the sketch map, Fig. 3. This crib dam is 35 ft. high. From this point the excess water follows the natural course of Sullivan creek to the Pend Oreille river. The water is taken from this intermediage storage by means of a 6 by 8 ft. wooden flume approximately 13,000 ft. long. This flume is built up on the side hill, piling being driven most of the way on

Jan 1, 1914

By John M. Dealy, Robert D. Pehlke

This note presents a summary of the available literature on activity coefficients at infinite dilution in binary metallic solutions, Table I. These data should prove useful in not only examining the therm-odynamic properties of binary metallic solutions, but also in predicting the activity of a component in a complex alloy. The relationship proposed by wagner1 for expressing the activity coefficient in dilute solution is of the form:

Jan 1, 1963

By M. V. Nevitt

THE Cr,O-type, or P-tungsten, structure having the space group (Oh2— Pm,n) is one of the most widely occurring structures found among the intermediate phases involving transition metals. Including the phases reported here for the first time, the total number of these A,B phases now known is 39. Greenfield and Beck' have correlated the lattice parameters of these phases with the Goldschmidt radius of the close-packed chains of A atoms. Laves' discussed the apparent size of the A and B atoms in this structure. Gel1er" proposed a scheme for reproducing the lattice constants of the phases by the use of a list of effective C.N. 12 radii for the component elements. Reported here is a survey of the A,B combinations which appeared favorable for the stability of the Cr,O-type phase but which, at the time the investigation was begun, either had not been reported upon or had conflicting reports as to the existence of the structure. Seventy systems were investigated, and 8 Cr,,O-type structures were found. Six of these also were reported by other investigators in the interval between the start of this investigation and its completion. This survey yielded information as to the influence of the relative sizes of the A and B atoms on the stability of the phase and, for the various families of Cr,O-type phases, the effects of the sizes of the A and B atoms on the lattice constant. Likewise, a somewhat clearer picture of the connection between the position of the A and B elements in the Periodic Table and their Cr,O-type phase-forming tendencies has become apparent. Experimental Procedure Alloys were prepared in the form of arc-melted 3-gram buttons in all cases where the vapor pressure of neither component was high enough to cause

Jan 1, 1959

By G. M. Schwartz, J. N. Gundersen

Utilization of magnetite-bearing taconite from the great Mesabi range of Minnesota is fast becoming a major industry in the state. The planning and early development stages of taconite processing projects have been de-scribed1-3 and an excellent discussion has appeared recently4 concerning the current mining, crushing, concentrating, and pelletizing techniques of the Reserve Mining Co., whose operations lie entirely within the Eastern Mesabi district. The present paper will deal only with some of the geological aspects of taconite utilization in the district, with emphasis placed upon some of the common mineralogical and textural features of the tacon-ites currently being mined or stripped and how these factors generally affect the potential recovery of the iron from the metamorphosed Biwabik iron-formation. The generalized geologic setting of the Eastern Mesabi district is presented in Fig. 1. The small circles on the geologic map, adapted from Grout and Broderick,3 mark the location of drill holes that were available for inspection during this study through the courtesy of Reserve Mining and Erie Mining Cos. The cores from these holes were divided into stratigraphic units and examined for their mineral content. Typical mineral associations and grain fabrics were also determined from hundreds of thin and polished sections. Available metallurgical tests made it possible to determine the probable response of a given variety of taconite to magnetic concentration. The longitudinal section of Fig. 1, projected along the strike of the iron formation, presents the simple stratigraphy of the area. It also shows the uniformly thick nature of the iron formation members in the district as well as a somewhat abrupt thickening of the formation to the west of the probable fault. The stratigraphy of these precambrian rocks has been described5-' elsewhere and need only be briefly reviewed. Historically, the oldest rocks unit, the Giants Range granite (Algoman) was covered by the Animikie group of sediments (Middle Huronian?), consisting of the Pokegama, Biwabik, and Virginia formations. Outcrops of the Pokegama quartzite are locally distributed along the northern limit of the Biwabik iron formation, but they are too limited to depict on the geologic map of Fig. 1. The effects of the intrusion of several small diabase sills within the Virginia and Biwabik formations are obscure because all of these rocks have been subsequently highly metamorphosed, mainly by the Duluth gabbro. The emplacement of the transgressing Duluth gabbro (Middle Keweenawan) and that of numerous peg-matitic veins in the iron formation8 has resulted in extensive contact and metasomatic metamorphism which has locally reconstituted the previously existing minerals of the Biwabik formation, in large part quartz and magnetite, into a wide variety of silicate mineral assemblages9 that have a profound effect upon the re coverability of the remaining magnetite. The entire region has subsequently been eroded and largely buried beneath Pleistocene glacial deposits. Structurally, the strike of the gently dipping Animikie group generally parallels the elongate outcrop pattern of the Biwabik iron formation on the map of Fig. 1. The Animikie group most commonly dips from 5" to 15" to the south-southeast. In this area, the Duluth gabbro pluton is somewhat sill-like, dipping about 30" to the southeast. Projecting these present structures upward, it seems probable that the gabbro once extended over the underlying Animikie group in the Eastern Mesabi district. SELECTION AND PRESENTATION OF DATA Because of the locally intense metamorphic activity in the district, mineralogical variations within the magnetite-bearing taconites are commonly abrupt, both vertically and laterally. Consequently it is difficult to select a single hole or small group of holes whose cores will be entirely representative of all of the district. Two holes have been selected, however, that in a general way represent mineralogical and textural variations that are likely to be encountered in both the eastern and western parts of the district. These recently drilled holes were chosen for discussion because it was possible to log the core and then to place the sample intervals at stratigraphic boundaries prior to preparation of the core for magnetic tube tests.

Jan 1, 1961

By George Espey, George Sachs, G. B. Kasik

IT has been reported frequently that the hardness and strength vary over the cross section of cold-worked, particularly cold-drawn, material. Brass rod and wire usually have been found to possess a maximum strength and hardness near the surface.1,2 According to Sachs,' the center fiber has about the same strength as a wire stretched by the same amount in a tensile-test machine, the strength increasing toward the surface (Fig. I). These differences are particularly large for wire given a small reduction on drawing through a die with a wide opening. However, with increasing reduction and hardness, a tendency to form a thin soft surface skin becomes apparent. On the contrary, copper wire has usually been found to possess a soft surface skin3-5 and it has been reported by Harris3 that during the cold-drawing of hot-rolled wire the surface layer becomes increasingly softer than the core, while the layer of maximum strength moves toward the core, it being found near the surface at first. The increase of strength and hardness from the core to the skin is readily explained by the observation that, in addition to the stretching, the layers of a rod or wire are sheared more the closer they are to the surface.1,6-8 However, the presence of a soft surface layer can be attributed only to an annealing effect. The source of such a softening might be the extremely high temperature that originates from the friction between

Jan 1, 1942

By G. B. Kasik, George Sachs, George Espey

IT has been reported frequently that the hardness and strength vary over the cross section of cold-worked, particularly cold-drawn, material. Brass rod and wire usually have been found to possess a maximum strength and hardness near the surface.1,2 According to Sachs,' the center fiber has about the same strength as a wire stretched by the same amount in a tensile-test machine, the strength increasing toward the surface (Fig. I). These differences are particularly large for wire given a small reduction on drawing through a die with a wide opening. However, with increasing reduction and hardness, a tendency to form a thin soft surface skin becomes apparent. On the contrary, copper wire has usually been found to possess a soft surface skin3-5 and it has been reported by Harris3 that during the cold-drawing of hot-rolled wire the surface layer becomes increasingly softer than the core, while the layer of maximum strength moves toward the core, it being found near the surface at first. The increase of strength and hardness from the core to the skin is readily explained by the observation that, in addition to the stretching, the layers of a rod or wire are sheared more the closer they are to the surface.1,6-8 However, the presence of a soft surface layer can be attributed only to an annealing effect. The source of such a softening might be the extremely high temperature that originates from the friction between

Jan 1, 1942

By George Ashley

IT has been said that the Pittsburgh bed is the most valuable single mineral deposit yet known to man. The figures in Table 1 are presented in substantiation of that claim. TABLE 1.-Pittsburgh Coal Bed to Dec. 31, 1934 Estimated Recov- State Thousands of ( Value erable Reserves Tons Mined (1935), Thousands of Tons Pennsylvania 3,144,000 $4,922,000 7,500,000 Ohio 493,391 843,699 3,000,000 West Virginia 650,000 1,027,000 5,500,000 Maryland 183,224 254,681 20,000 Totals 4,470,615 $7,047,380 16,020,000 PRODUCTION AND VALUE In order that the figures of Table 1 may have any weight, a statement must be made to show how they were arrived at. Because, to the writer's knowledge, no accurate separate figures ever have been kept of the production and value of the Pittsburgh coal bed, the states will be considered separately.

Jan 1, 1936

By Arthur C. Simmons

Oil production and activity in northern and central Pennsylvania was slightly less in 1939 than in the previous year, but owing to higher average prices 1939 was undoubtedly a better business year. The last quarter showed markedly increased activities throughout all of the Pennsylvania fields. Production, Stocks and Price Storage of Pennsylvania crude oil at pipe lines and refineries totaled 5,413,000 bbl. on Dec. 31, 1938, and declined during the year 1,124,000 bbl. to a total of 4,319,000 bbl. at the end of 1939. The stocks of crude at the end of the year represent the lowest point reached in Pennsylvania-grade crude storage in recent years. Stocks increased slightly during April, May and June, but decreased during all other months of 1939. The Bradford field production within the state of Pennsylvania averaged 35,340 bbl. per day throughout 1939, which represents a decrease of 1419 bbl. a day from the 1938 average. The production in central and southern Pennsylvania increased 1176 bbl. per day, averaging 12,159 bbl. throughout 1939. Table 1 includes annual production for the part of Bradford field situated within the state of Pennsylvania, for central and southern Pennsylvania, and for the entire state of Pennsylvania. A definite segregation of production between the Bradford field and central and southern Pennsylvania is slightly ambiguous because a portion of the oil from the newly discovered Music Mountain pool is included statistically in each area. In all probability the entire increase and some small addition to the production from southern Pennsylvania can be attributed to oil produced from the Music Mountain pool. Within the Bradford field, six price changes occurred throughout the year. At the beginning of 1939 the price of Bradford crude oil was $1.80 per barrel, whereas by the end of the year it had risen to $2.50. The weighted average price for Bradford crude during 1939 was $2.059 per barrel.

Jan 1, 1940

By Arthur C. Simmons

Oil production and activity in northern and central Pennsylvania was slightly less in 1939 than in the previous year, but owing to higher average prices 1939 was undoubtedly a better business year. The last quarter showed markedly increased activities throughout all of the Pennsylvania fields. Production, Stocks and Price Storage of Pennsylvania crude oil at pipe lines and refineries totaled 5,413,000 bbl. on Dec. 31, 1938, and declined during the year 1,124,000 bbl. to a total of 4,319,000 bbl. at the end of 1939. The stocks of crude at the end of the year represent the lowest point reached in Pennsylvania-grade crude storage in recent years. Stocks increased slightly during April, May and June, but decreased during all other months of 1939. The Bradford field production within the state of Pennsylvania averaged 35,340 bbl. per day throughout 1939, which represents a decrease of 1419 bbl. a day from the 1938 average. The production in central and southern Pennsylvania increased 1176 bbl. per day, averaging 12,159 bbl. throughout 1939. Table 1 includes annual production for the part of Bradford field situated within the state of Pennsylvania, for central and southern Pennsylvania, and for the entire state of Pennsylvania. A definite segregation of production between the Bradford field and central and southern Pennsylvania is slightly ambiguous because a portion of the oil from the newly discovered Music Mountain pool is included statistically in each area. In all probability the entire increase and some small addition to the production from southern Pennsylvania can be attributed to oil produced from the Music Mountain pool. Within the Bradford field, six price changes occurred throughout the year. At the beginning of 1939 the price of Bradford crude oil was $1.80 per barrel, whereas by the end of the year it had risen to $2.50. The weighted average price for Bradford crude during 1939 was $2.059 per barrel.

Jan 1, 1940