By Tong Guangxu

INTRODUCTION Throughout the world, the caving mining methods of ore-draw under the overlying waste rock are sublevel caving in Sweden, block caving in U.S.A. and forced block caving and sublevel caving with sill-pillar in U.S.S.R. These caving methods are of high efficiency, low cost and large production (especially the block caving method) when compared to opencast mining. From the ore production of all under- ground mines, the largest annual production of underground metalliferous mines in the world is caving methods. The sublevel caving in Kiruna Iron Mine of Sweden has reached annual ore production over 20 million tons in 1974. The block caving in Climax Molybdenum Mine and San Manuel Copper Mine of U.S.A. both have produced about 40 thou- sand tons of ore per day in 1971. At the same time, the productivity of Kiruna was 12 thousand tons of ore per man-year, Climax 42.8 tons (48.3 short tons) per man-shift and San Manuel 29.01 tons (32.1 short tons) per man-shift. The main feature of this group of mining methods is the underground extraction of ore from beneath overlying caveable waste rock. Since the loss and dilution of ore are inherent (sometimes to a great extent), the control of ore-draw in these methods as com- pared with other methods is very important. Consequently, concerned Universities and Research Institutes have devoted great amounts of research on ore-draw theory and control management which has provided positive results to mine production, and has apparently promoted the development of the caving methods. During 1979 in China, metalliferous underground mines accounted for 15.22% of the total iron ore produced, while also accounting for 56% of total non-ferrous production. According to the mining methods, sub level caving in the principal underground iron mines counted for about 56.74% of total principal underground iron mine production, but only about 1% of total non-ferrous underground mine production. Relative to forced block caving and sublevel caving with sill pillar, the Chinese non-ferrous under- ground mines estimated about 35% of total non-ferrous underground mine production from these two methods, mainly from the latter. From the trend of development of underground metalliferous mines in China, the percentage of production in caving will be increased in the future, especially in block caving and forced block caving which have already been given great attention in the mining circle. In these types of mining methods the ore is drawn from the stope under a large area of overlying waste rock, which complicates the basic regulation and control of ore-draw, but provides lower loss and dilution than sublevel caving. Because of these reasons, the Kiruna Iron Mine in Sweden is intending to change its sublevel caving by testing a sublevel shrinkage caving method and considering a large area of ore-draw beneath the stope as an advantage. Therefore, the basic regulation and control management of ore-draw under a large area, as practiced in China, will be discussed in this paper. BASIC REGULATION OF ORE- DRAW FROM CAVING STOPE The aim of studying ore-draw under a large area of overlying waste rock is to se- cure a planned draw schedule that guarantees a certain plane of interface between ore and waste rock, and controls the change of its shape in spatial position for reducing ore loss and dilution during the draw process. Presently, the ellipsoid theory is comparatively near the actual attitude of ore-draw from the cave. 1. Ore Drawn Out from Single Drawpoint Laboratory testing and practical experience all show that after a certain amount of ore has been drawn out from a drawpoint, its original shape in the stope before drawing is more or less similar to an ellipsoid, hence the name "draw ellipsoid." This draw ellipsoid is cut at the bottom by a horizontal plane corresponding to the raise of the drawpoint, and its volume can be calculated by the following formula:

Jan 1, 1981

LIMA, PERU Established May, 1952 (Official year begins in June) Luncheon meetings third Wednesday monthly Ernesto A Baertl, Chairman Arthur C Hall, Chairman-Elect Raymond R Beard, First Vice-Chairman Edgardo Portaro, Second Vice-Chairman Walter E King, Secretary-Treasurer Av Santa Cruz 331 San Isidro, Lima, Peru Alberto E Brazzini, Asst Treasurer Daniel M Rodriguez, Asst Secretary, '58, Section Delegate '58, Alternate Section Delegate

Jan 1, 1956

By John L. Lamont, Walter Crafts

STUDIES of the effect of composition of steel on hardenability by Grossmann,1 and as-quenched hardness by Field2 and by the authors,3 have made it possible to predict the results of quenching when the composition and cooling rate are known. In order to extend the application of the hardenability calculation to the quenched and tempered condition in which steel is finally used, a survey has been made of the hardness changes caused by tempering. From this study a method has been developed for the prediction of hardness and tensile strength of steel in the tempered condition. The method of calculation was developed from Rockwell C hardness tests on quenched and tempered Jominy specimens and is expressed in Rockwell C hardness units. It is of an additive type in which the degree of softening from as-quenched hardness is estimated. Tempered properties may be calculated within about plus or minus 5 Rockwell C hardness or plus or minus 15,000 lb. per sq. in. tensile strength. This degree of accuracy is less than that necessary for the control of heat-treatment, but is adequate for the comparative evaluation and selection of alloy steels. The formula indicates that tempered hardness is primarily dependent on as- quenched hardness and, as in the hardening reaction, the progress of tempering is controlled mainly by the carbon content- Alloys tend to retard softening by a secondary hardening mechanism in which the alloy appears to migrate from ferrite to the carbide phase. The factors for the effects of alloys in tempering vary so much from the effects of alloys in hardening that different steels of equivalent hardenability may, after lie heat-treatment, differ considerably in tensile strength. PROCEDURE In developing the method for calculating tempered Rockwell C hardness, simple and complex steels were tested over a range from 0.08-to 0.65 per cent carbon and up to 2.68 per cent manganese, 2.18 silicon, 3.50 chromium, 4.94 nickel, and 1.06 molybdenum. The steels were made as small induction-furnace heats at the Union Carbide and Carbon Research Laboratories, Inc. The accuracy of the method was finally checked on a variety of carbon, low-alloy and high- alloy types of heat-treating steels produced under commercial conditions. The method was based on a study of tempered Jominy bars, and its validity was tested by correlation with the center hardness and tensile strength of oil-quenched and tempered bars from ¼ to 4 in. in diameter. The method of calculation was derived from the differences in Rockwell C hardness between as-quenched and quenched and tempered Jominy specimens. Prenormalized Jominy hardenability specimens quenched from a normal temperature for austenitization were used to obtain a range of as-quenched Rockwell C

Jan 1, 1946

By W. McA. Johnson

The work of J. E. Johnson, Jr., on the effect of small amounts of oxygen in cast iron in increasing its strength and resistance to shock, is of interest from the technical and scientific standpoints. The following exposition of the theory carries Mr. Johnson's explanation further and, in my opinion, will disclose certain related phenomena and perhaps shed further light on the subject. Some facts, so novel in character as to excite incredulity, have been accepted finally by many metallurgical authorities. One of these is that oxygen to the amount of 0.060 per cent. in cast iron gives it a breaking strength of 3,500 Ib. per square inch, compared with a breaking strength of 2,500 lb. per square inch in cast iron of the same composition with respect to elements other than oxygen, but having only 0.010 per cent, oxygen. The "oxygenated" cast iron, even if made in a coke furnace, has properties equivalent to the best charcoal pig iron. Mr. Johnson has also established the fact that the variations in combined carbon cannot account for the results. By microphotographic evidence he has shown that in oxygenated cast iron the graphite particles are dense and spherical, while in well-deoxidized cast iron the graphite particles are flaky and leaf-like. It is just a matter of common sense that iron of the latter structure is much weaker than the former. The analytical and microscopical work has been done with care and there is no doubt in my mind about the accuracy of the experimental results. In this paper then, we shall consider it as accepted that small amounts (0.060 per cent.) of oxygen increase the strength of cast iron by producing a structure in which the round and solid particles of graphite are surrounded firmly by a principal matrix of ferrite. The purpose of this paper is to show that the reason why the graphite particles are round is founded on the fact that the particles of any precipitate are made denser and harder by the presence of a reagent having a solvent action on the precipitate. This can be stated as a law, although I have never seen it so given in any textbook. Let us then, for purposes of illustration, give a concrete example and develop the theory of such mechanical and chemical actions as occur: It is well known that, by a soluble sulphate, a barium salt in solution is precipitated in a dense and easily filtered body when the solution is

Jan 1, 1916

A. Scott Reid, London, Eng. (communication to the Secretary*) :—As a constructor of several glass mine-models, .I have read with much interest the description of the model of the Montana-Toriopah mine-workings by Edmund D. North.

Jan 1, 1910

By M. J. Sinnott

WITH the advent of nodular iron as an engineering material, considerable interest has been shown in developing this material for various applications. Generally the strength, hardness, or ductility are the more common properties used for design purposes but occasionally applications involving a knowledge of the thermal conductivity of the material is required. A search of the literature showed, rather surprisingly, that relatively little work has been done on this property for all types of cast iron. Insufficient data are available on thermal and electrical conductivities to develop the Weidemann-Franz ratio, or the Lorentz relationship, for estimation purposes. There are no data on nodular irons and the published data on malleable irons are quite sketchy. For these reasons the conductivity of the group of nodular irons listed in Table I were measured. Irons I to IV were made in such a fashion as to maintain the carbon and alloy content essentially the same while varying the silicon content. Test specimens were cut from the mid-section of 4-in. keel castings. Iron V is a commercial casting of nodular iron. The test specimen of this iron was cut from the center of a large cast billet 3x10x26 in. All alloys were tested in the as-cast condition. A microstructural examination showed that each iron had spheroidal graphite but the size and distribution varied with the silicon content of the iron. The spheroid size decreased while the number of graphite nodules increased as the silicon content of the iron was increased. The matrix structures of each iron consisted of pearlite and ferrite with the proportions varying from predominantly pearlite in the low-silicon iron to mostly ferrite in the high-silicon iron. The commercial heat, iron V, was predominantly pearlite probably because of its higher manganese and phosphorus content. Two methods for measuring the thermal conductivity were used. The first was a modification of the techniques described by Powell and Hickman and Van Dusen and Shelton,² the second method was a simpler technique described by Jakob and Hawkins." Since the agreement of both methods as tested on two sets of duplicate samples was excellent, the simpler experimental technique was used. The results of the measurements are given in Table II along with a summary of the microstructural constituents. These conductivity data indicate that as the percentage of silicon increases there is a corresponding decrease in the thermal conductivity even though the structure is changing from pearlitic to ferritic. Such a change in microstructure is usually accompanied by an increase in conductivity. A third factor involved in the behavior of these irons is the size and distribution of the graphite nodules. The relative amounts of graphite do not change greatly but the size and distribution do. Generally graphite improves the conductivity but in the present case such an effect is probably masked by the alloying effect from the silicon and its dispersion through the matrix. The thermal conductivity of the nodular irons studied is less than that of regular foundry irons by some 10 to 30 pct and is less than that of regular malleable irons.' The cause of the decreased conductivity is probably the more highly alloyed fer-rites obtained in these irons and the changed mode of distribution of the graphite as compared to the regular foundry irons. References R. W. Powell and M. J. Hickman: Journal Iron and Steel Inst. (1946) 154, No. 2, p. 99. 'M. S. Van Dusen and S. M. Shelton: U. S. Bur. Standards Journal of Research, RP668 (1934) 12, p. 429. ³M. Jakob and G. A. Hawkins: Elements of Heat Transfer and Insulation. 2nd Ed. (1950) New York. John Wiley and Sons. ' J. W. Donaldson: Journal Iron and Steel Inst. (1933) 128, No. 2, p. 255.

Jan 1, 1954

Frank Williams, Johnstown, Pa. (Communicatioll to the Secretary): As the manager of the company which manufactured the " American " magnesite and the silica-brick mentioned by Mr. Pennock, I beg to say that he was quite right in placing a mark of interrogation after " American " (page 268). While the users of magnesite in this country are at a disadvantage as to cost by reason of not having any large bodies of sufficiently pure material at hand, the manufacturing concern referred to has secured an advantage as to quality by a mixture of the different foreign magnesites, which vary considerably in their composition and physical structure. The American (?) magilesite tested was a sample of the next

Jan 1, 1897

By W. R. Hicks, J. E. Pollock, E. Camp

In the oil-refining industry, steel comprises by far the greatest proportion of the materials used in construction work, but with an enormous number of alloy steels and nonferrous alloys available, and a greater knowledge of their properties and corrosion resistance, a substitution first in the "hot spots" and then in locations of moderately severe corrosive conditions will be made as the greater expense can be justified. In new construction work, advantage is taken of the experience already gained and appropriate materials used, whether for high temperatures and pressures demanding additional strength or for corrosive conditions. The locations, however, where equipment in operation constantly requires replacement will soon become evident, as will the necessity for replacement in more resistant materials, if considerable down-time is to be avoided. In what direction and how far to go in the matter of alloys then becomes a question of the highest importance. Obviously, any replacement with more costly material must be justified economically by the promise of longer life, thereby saving both material and installation costs besides the reduction of loss of production. Where the equipment is overcapacity and a regular schedule of cleaning periods is in force, the last item frequently must be ruled out and justification made on the basis of the first two only. Installation of material that will outlast the remainder of the equipment and have no recovery value must also be avoided; this is particularly important in temporary construction or in old equipment that will soon become obsolete. Test Methods Either one of two methods or a combination of both, in the absence of reliable data in similar services, may be adopted to determine to what extent replacement with other, and perhaps more expensive, materials is justified. A unit may be constructed incorporating different metals or alloys so that comparative service may be obtained under the same service conditions; this has been applied in many instances, such as condenser and tank construction, but the opportunities for inspection may be few and

Jan 1, 1935

By J. E. Pollock, W. R. Hicks, E. Camp

In the oil-refining industry, steel comprises by far the greatest proportion of the materials used in construction work, but with an enormous number of alloy steels and nonferrous alloys available, and a greater knowledge of their properties and corrosion resistance, a substitution first in the "hot spots" and then in locations of moderately severe corrosive conditions will be made as the greater expense can be justified. In new construction work, advantage is taken of the experience already gained and appropriate materials used, whether for high temperatures and pressures demanding additional strength or for corrosive conditions. The locations, however, where equipment in operation constantly requires replacement will soon become evident, as will the necessity for replacement in more resistant materials, if considerable down-time is to be avoided. In what direction and how far to go in the matter of alloys then becomes a question of the highest importance. Obviously, any replacement with more costly material must be justified economically by the promise of longer life, thereby saving both material and installation costs besides the reduction of loss of production. Where the equipment is overcapacity and a regular schedule of cleaning periods is in force, the last item frequently must be ruled out and justification made on the basis of the first two only. Installation of material that will outlast the remainder of the equipment and have no recovery value must also be avoided; this is particularly important in temporary construction or in old equipment that will soon become obsolete. Test Methods Either one of two methods or a combination of both, in the absence of reliable data in similar services, may be adopted to determine to what extent replacement with other, and perhaps more expensive, materials is justified. A unit may be constructed incorporating different metals or alloys so that comparative service may be obtained under the same service conditions; this has been applied in many instances, such as condenser and tank construction, but the opportunities for inspection may be few and

Jan 1, 1935

By W. K. Hartley

INTRODUCTION AND HISTORY The Kimberley Division of De Beers Consolidated Mines Limited includes four underground mines in Kimberley viz. Dutoitspan, Bultfontein, De Beers and Wesselton Mine and two outside mines, viz. Finsch, an opencast operation and Koffie- fontein, an underground operation. Figure 1 is a map of the Kimberley district showing the location of these mines. Finsch is 150km west of Kimberley and Koffiefontein is 80km south of Kimberley. The head office of the De Beers Company is in Kimberley. The diamond sorting and trading companies for diamonds produced in South Africa are also in Kimberley. Diamonds were first discovered in the Kimberley area at Hopetown in 1866 on the banks of the Orange River. This, and later finds, triggered the start of the great "Diamond Rush". In 1870 the Jagersfontein (now closed) and Dutoitspan pipes were discovered, followed by those at Bultfontein, De Beers and Kimberley Mine (now closed) in 1871, Koffiefontein in 1880 and Wesselton in 1891. Finsch Mine was a more recent discovery in 1961. Finsch, due to go underground in 1986, and Koffiefontein, are fully self-contained with their own treatment plants, housing, services etc. The four Kimberley mines deliver ore by conveyor to a central treatment plant and use joint ser- vices. ,+lining is presently carried out mainly by Block Caving which has replaced the earlier Chambering method. De Beers Mine, on a limited scale, and Wesselton Mine have recently started to use Sub-Level Caving, and both Bultfontein and Du- toitspan are scheduled to use the same method at a later date. The combined ore tonnage produced by the Kimberley Mines is 17 400 tons per day, Koffiefontein 12 000 tons per day and Finsch Mine 17 000 tons per day. THE EVOLUTION OF MINING METHODS Initially, the open-cast mining was carried out to as great a depth as safety would permit. In the early stages of open-cast mining, the Kimberlite was removed in horizontal slices from levels 13m to 20m apart. The rock broken in the workings was raised to the surface by means of endless rope haulage inclines. As lower levels were attained these rope haulages were replaced by aerial hoists, inclined shaft haulages or inclined skip-ways. These methods were dependent upon the strength of the unsupported pipe walls, which became increasingly unstable with depth and a system was adopted whereby the ground mined in open excavations was tipped down passes to tunnels connecting with vertical hoisting shafts sunk in the country rock. As work in the open pit became more and more impracticable due to extensive falls of ground, this system was replaced by a combination of open-cast and underground mining, and eventually by wholly underground methods. Chambering With the advent of underground mining, a system known as "Chambering" (or "Inclined Chambering") was evolved. It was essentially a combination of shrinkage stoping and caving, whereby advantage was taken of the high pressure exerted by the loose rock that had accumulated in the open excavations due to the collapse of the pipe walls. This mining method was introduced around 1890 and was successfully employed, with little change, up to the early nineteen seventies. In this system each mine was served by a main hoisting shaft situated about 300m in the country rock. Main haulage cross cuts were driven from the shaft to the pipe at 200m (600ft) vertical intervals. A sub-vertical shaft, situated close to the pipe provided access to the working levels. Chamber levels were established from the sub-vertical shaft at 13m (40ft) intervals. See figure 2. On each of these levels successive 6,8m wide “cuts" were mined out across the pipe, from one rock contact to the other, and extended vertically to the footwall of the level above. Every 6,8m cut was made up of a chamber and a "back-pillart1, each approximately 3,401 wide. The chamber was mined by overhand shrinkage stoping. The levels were carried "en echelon", with each chamber on a level approximately three cuts ahead of the chamber on the level

Jan 1, 1981

By E. A. Lowe, C. C. Walden, D. W. Duncan, P. C. Trussell

The industrial importance of bacteriological leaching is finding increasing application in the treatment of low-grade ore and of exhausted mines. Another possible application of bio-leaching is in the extraction of ore concentrates, although here the first uses will likely be for ores that are refractory to conventional metallurgy. Biological leaching studies, which have been in progress for over ten years in this laboratory, are directed towards the more rapid and complete leaching of metals from their sulfides, particularly of copper, zinc, and nickel. The program involves not only laboratory studies, but pilot-plant operations and liaison with mining companies which are underwriting the cost of the investigations. Although the bacterial oxidation of mineral sulfides to the corresponding water-soluble sulfates has been occurring naturally for many centuries, the first documented recovery of solubilized metal from pregnant solution was at the Rio Tinto operation in Spain. At this location leaching variables were studied extensively in an empirical manner some years before the causative bacteria were first isolated from other leaching situations. Documentation of the presence of bacteria in leach waters of the Rio Tinto, Spain, operation was not confirmed until 1962.3 On this continent leaching was pioneered in the early

Jan 1, 1968

By W. D. Smith

It has been 5 years since the writer left the Philippine Islands and while in that country his chief work did not lie in this field, though he has visited all but one of the localities mentioned in this article. The principal field studies relating to oil were M de by his colleague, Mr. Wallace E. Pratt. The writer's investigations ealt with the general stratigraphy and paleontology of the Philippines. with the exception of the investigations made by Mr. Pratt and the writer very little information on this subject is available. A number of geologists in the employ of large oil companies have visited the Islands from time to time but, following the general rule, the public has scarcely ever been permitted to learn anything of the results. The writer is indebted to the Bureau of Insular Affairs, Washington, for late information regarding recent legislation in the Islands relating to petroleum. All the known oil seeps, petroleum residues, such as ozocerite, and natural-gas emanations are associated with Tertiary sediments. The chief seeps and most promising prospects are located as follows: 1. Bondoc Peninsula (lower end), Tayabas Province, Southeast Luzon. 2. The west coast of the island of Cebü from Alegria north to, and perhaps beyond, Toledo. 3. Central Mindanao not far from Lake Lanao. 4. The ozocerite veins on the Island of Leyte in the northwestern part in the vicinity of the town of Villaba. 5. Natural gas from some deep wells in Tertiary shale formations on the eastern flank of the Cordillera and extending out under the plain on the island of Panay. The first mention in geological literature, to the writer's knowledge, of gas or petroleum in the Philippines is found in the description of the Island of Panay by the Spanish geologist, Abella, in the year 1890. In 1898, an oil well was being dug on the estate of Smith Bell & Co., an English concern, near the town of Toledo on the west coast of Cebu. In

Jan 1, 1921

By Mark R. Lamb

THE various methods of treating pulp in air-agitation tanks offer problems for experiment and study which are fascinating as well as practical. The usual method heretofore has been to fill each tank in turn, agitate the mixture the required period and then discharge the treated pulp into a storage-tank, from which it. is drawn to the filter as required. A later method is to run the pulp from the tube-mill, classifier, thickener, or settler into the first of a set of tanks, and thence continuously or in series through the remaining tanks, finally drawing off the pulp to a continuous filter, or to a pulp-storage tank if the filter is of the intermittent type. It is this method which I propose to discuss here in a preliminary way, with the idea of going exhaustively into the examination of the results of a series of experiments in a later paper. It may be of interest to note that the design of a cyanide-plant has recently been completed in which the estimated cost of the agitation-tanks, storage-tanks, and pumps was 30 per cent higher for the charge-agitation arrangement than for the series plan. The first question in studying the series method is, "What is the actual period of treatment undergone by the pulp?? One first supposes that by chance some of the pulp may get through with little or no treatment, while other portions may stay in the tanks a needlessly long period. The former is not probable or even possible, and the latter is, practically, true to only a limited extent. The greater the number of tanks the greater is the percentage of chance that all the pulp will be treated equally. Without going into the mathematical analysis of the problem (which is of little value, since it is based on problematical premises), its important terms may be clearly grasped by thinking of, or " visualizing," the conditions when,

Jan 1, 1910

By Jerome Strauss

IN his review of developments in 1943, Gilbert Seil, Chairman of this Committee on Reduction of the Ferroalloy Ores, tabulated the consumption of the alloying metals in relation to the steel production of that year. In the year just closed the approximate tonnage was of the same order, differing only to a minor degree or suffering some correction with more precise figuses available, as indicated in the following estimates: Consumption Metals in Tons Steel 92,000,000* Manganese 700,000 Silicon 200,000 Chromium 200,000 Nickel 75,000 Molybdenum 20,000 Tungsten 8,000 Vanadium 1,700 Titanium 1.600 Boron 10 `Production figure. The technologic studies instituted during 1942 and carried forward with such great vigor during 1943 continued into 1944 although in some instances were brought to a close either by completion of the specific development

Jan 1, 1945

By R. S. Hadi, L. Svarovsky

SUMMARY This is a report of a new development in on-line particle size measurement of fine powders in dust-laden gases. A continuous sample of the solids-air suspension is drawn from the process stream via a sampling probe by means of an air operated ejector into a cyclonic separator whereby the sample is subjected to a particle size dependent separation process and split into two streams, "overflow" and "underflow". The overflow stream carries most of the fines at a relatively low concentration and the underflow stream carries the coarse particles at a relatively higher concentration. The concentration of solids in the two streams is detected by electrostatic noise level technique which utilises the electrostatic charge accumulated on the solid particles due to their high velocity in the turbulent air stream, for the mass concentration measurement. The ratio of the solids concentration of the fines stream to that of the coarse stream is then correlated against the average particle size in the main process stream by a calibration curve. The in-plant tests clearly indicate that this relatively simple instrument offers good sensitivity in the size range from 2 to 6 µm, and is capable of giving a continuous indication of average particle size for process control purposes. Although the instrument was developed for a particular application, it may be used in other situations where fine powders are conveyed in gas streams. British and foreign patents are applied for.

Jan 1, 1980

By John Tyssowski

In 1925, Harry Howard Stout, then metallurgist for Phelps Dodge Corporation, while investigating the cleaning of cathode copper by various gases at elevated temperatures below the melting point of the metal, observed in the laboratory that particles of pure copper heated in a closed tube filled with hydrogen seemingly "stuck together." By further investigation he found that there was actual crystal growth across the boundaries of the particles of pure metal; in other words, there was a complete new crystal realignment and growth throughout the newly formed copper mass. It was coalescence, not adhesion; the several particles had become one unit. From this discovery has been developed the coalescence process, whereby copper of cathode purity is squirted out in semifabricated form from an extrusion press, by the application of about 3000 tons pressure on a 10-in. piston. Stout decided that cathode copper produced by electrolytic deposition was the logical source of the pure copper required for the coalescence process, but as there was no way of reducing the ordinary tough commercial cathodes to the small particles required he was confronted by a serious problem at the outset. Under his direction, this problem was solved by William H. Osborn and Harry Howard Stout, Jr. They developed the process and technique for producing cathode copper in brittle, friable form, and to them must be given the greater part of the credit for this phase of the development program as well as for that relating to the gas cleaning of the cathode particles. Concurrently, the three metallurgists worked on the problem of effecting a complete union of the cathode particles. Adequate washing was all that was needed to free the particles from electrolyte solution and slimes. A press was designed to produce briquettes of the proper porosity and density, and a method was devised of removing surface oxidation from the particles of cathode, by treatment in an atmosphere of deoxidizing gas at an elevated temperature. The temperature was determined at which the surface cleansing and preheating could be done in one operation, and for this a charging and preheating furnace in which there is maintained a positive pressure of deoxidizing gas atmosphere was designed. And finally, a method of feeding the heated briquettes of deoxidized cathode copper into an extrusion press without contamination from the air was evolved. For the final stage, a press was required because not only heat but pressure was required to obtain complete growth of the new crystals between the cathode particles as well as the elimination of all voids or non-coalesced areas. All essential stages of the process are protected by patents or patent applications in the United States and principal foreign countries, and the copper is produced on a commercial scale.

Jan 1, 1941

By John Tyssowski

In 1925, Harry Howard Stout, then metallurgist for Phelps Dodge Corporation, while investigating the cleaning of cathode copper by various gases at elevated temperatures below the melting point of the metal, observed in the laboratory that particles of pure copper heated in a closed tube filled with hydrogen seemingly "stuck together." By further investigation he found that there was actual crystal growth across the boundaries of the particles of pure metal; in other words, there was a complete new crystal realignment and growth throughout the newly formed copper mass. It was coalescence, not adhesion; the several particles had become one unit. From this discovery has been developed the coalescence process, whereby copper of cathode purity is squirted out in semifabricated form from an extrusion press, by the application of about 3000 tons pressure on a 10-in. piston. Stout decided that cathode copper produced by electrolytic deposition was the logical source of the pure copper required for the coalescence process, but as there was no way of reducing the ordinary tough commercial cathodes to the small particles required he was confronted by a serious problem at the outset. Under his direction, this problem was solved by William H. Osborn and Harry Howard Stout, Jr. They developed the process and technique for producing cathode copper in brittle, friable form, and to them must be given the greater part of the credit for this phase of the development program as well as for that relating to the gas cleaning of the cathode particles. Concurrently, the three metallurgists worked on the problem of effecting a complete union of the cathode particles. Adequate washing was all that was needed to free the particles from electrolyte solution and slimes. A press was designed to produce briquettes of the proper porosity and density, and a method was devised of removing surface oxidation from the particles of cathode, by treatment in an atmosphere of deoxidizing gas at an elevated temperature. The temperature was determined at which the surface cleansing and preheating could be done in one operation, and for this a charging and preheating furnace in which there is maintained a positive pressure of deoxidizing gas atmosphere was designed. And finally, a method of feeding the heated briquettes of deoxidized cathode copper into an extrusion press without contamination from the air was evolved. For the final stage, a press was required because not only heat but pressure was required to obtain complete growth of the new crystals between the cathode particles as well as the elimination of all voids or non-coalesced areas. All essential stages of the process are protected by patents or patent applications in the United States and principal foreign countries, and the copper is produced on a commercial scale.

Jan 1, 1941

By W. A. Wood, H. L. Wain, R. I. Garrod

The mechanical behavior of recrystallized chromil~m of high purity has been studied, principally in torsion and to a lesser extent in tension, at temperatures between —196oand 350oC. Depending upon the conditions of test, the material may show brittle or ductile behavior or an intermediate or subduc-tile state having some of the characteristics of each. This latter state existed at temperatures between approximately ±50°C and was characterized by a) extensive creep at stresses well below the normal fracture stress, b) nonelastic loading/unloading effects during creep, c) strain softening under cyclic loading, and d) final failure of a brittle type. Suggestions are made on the dislocation processes and interactions which give rise to subductile behavior The ductile-brittle transition in bee metals has been studied mainly by tension and bend tests. These methods, however, favor crack propagation which may follow too closely on initiation for detailed study of the transition itself. For work of this nature, therefore, other modes of deformation less favorable to crack propagation may be preferable. This paper describes a study of the ductile-brittle transition in chromium which is based mainly on torsional testing although a few subsidiary experiments were made in tension. It appears to reveal at the transition an intermediate state that cannot properly be described as either brittle or ductile. Torsional tests on chromium have been made by other workers1 but not, as here, primarily for study of this intermediate state. EXPERIMENTAL The chromium, in the form of swaged rod, was prepared by techniques already described.' The particular material used was one in which the main impurities were 0.03 wt pet 0 and 0.006 wt pet N and one in which transition from ductile to brittle states in torsion conveniently fell at about room temperature. For torsion, test specimens were from 5/16-in.-diam rod to provide test portions 1-1/4 in. long by 7/32 in. diam, a twist of 1 deg thereby corresponding throughout this paper to 0.0015 surface shear. The specimens before test were annealed for 2 hr at 1200°C in vacuo, which left them with a re-crystallized grain size of about 0.01 mm, and then electropolished. They were tested under dead-weight loading in an apparatus in which they could be surrounded by a furnace or cooling chamber, tests in practice being made at various temperatures between -196" and +350°C. For tension tests, cylindrical specimens were prepared in a similar manner and tested at room temperature under dead-weight loading. RESULTS (TORSION) Subductile State. The state described above as intermediate between brittle and ductile may be perhaps best defined by reference to torque/twist curves at various temperatures. These are grouped in Fig. 1. Below about -50°C the material was brittle, in the sense that it exhibited little plastic deformation under stress and fractured by cleavage along planes of maximum resolved tension, which in torsion produces the well-known helical type of fracture. The deformation is typified by the curves for -196" and -150°C in Fig. 1; it shows a slight but progressive deviation from linearity above a certain torque, here about 50 lb-in., until fracture occurs at about 95 lb-in. A feature to which it is desired specially to call attention is that under none of the loads did the specimens show significant creep.

Jan 1, 1964

By J. R. Hornaday, A. E. Morris, N. A. Parlee, D. C. Carmichael

Rates of absorption and effusion of hydrogen in solid iron were measurede by a Sieverts type of apparatus. With clean a iron these rates are diffusion controlled down to 420°C and are represented by the equation D = 6.70 x e-'100' crn2 sec-I Certain surface impurities can affect these rates at all temper-atuves. Thin oxide films lower, the apparent diffusivity of annealed iron markedly. Cold-worked iron (75 pct) annealed at 430°C has practically the same solubility and diffusivity as anealed iron. THE mechanism of absorption and evolution of hydrogen in solid iron alloys is not fully understood despite the large number of investigations on the subject. While there appear to be many instances of simple solid-state diffusion control of rate, there are many cases where investigators have either concluded that surface reactions are rate controlling or that some "nondiffusible" hydrogen resides in discontinuities. The purposes of this research were 1) to develop a sound method for studying this absorption and evolution behavior, 2) to examine it in pure annealed iron, and 3) to determine the effects of important variables, such as cold work, surface condition, and composition. This paper relates the progress toward these objectives. Much of the present knowledge of the movement of hydrogen through iron alloys comes from permeability studies which involve the measurement of the rate of passage (under steady state conditions) through membranes of the order of 1 mm in thickness. This method is open to question on various grounds. If surface reactions are involved, two different surfaces operating under two different conditions must be considered. The presence of defects in the membrane even of microscopic dimensions may lead to erroneous results. A few people have studied evolution of hydrogen into vacuum, under carefully controlled (unsteady state) conditions, and some of the best diffusivity data come from these sources. Most of these methods measure rates of evolution only and thus do not make a rigorous test for reversibility of behavior. It appeared that an "unsteady state" method that would permit the measurement of both rates of evolution and absorption under controlled temperature, pressure, and other conditions would offer several advantages. Accordingly the modified Sieverts apparatus described below was designed and built. APPARATUS This apparatus is shown in Fig. 1. The sample bulb is detailed in Fig. 2. Hydrogen of 99.5 pct purity and argon of 99.99 pct purity were used. The hydrogen was deoxidized and dried by means of a Deoxo unit followed by a "Dri-erite" tower. The argon was only dried. The gas burette was graduated in tenths of a cubic centimeter, and, with the aid of a travelling magnifier, readings could be estimated to the nearest 0.01 cc. The level of mercury in the burette was adjusted by means of a leveling bulb operated by a fine screw adjustment. An electrical system, consisting of two slightly separated platinum electrodes inserted in one leg of the manometer and a small light bulb was used to obtain rapid accurate adjustment of the pressure. The capillary tubing of the Vycor sample bulb was 3 mm bore as was all tubing back to the gas burette. The samples were discs made from vacuum-melted Ferrovac-E iron of greater than

Jan 1, 1961

By John Mills

THREE case histories from professions other than engineering will serve to introduce ideas basic to this discussion. Case (1) Date, about 1900. A young man, B. D. from a three-year graduate course in a prominent divinity school, was for two years a successful pastor of a small church; then friction over theological matters arose with a fundamentalist deacon of the "Bible belt" type. He resigned, returned to his university for a four-year medical course, interned for two more, and thereafter was successful and apparently happy as a physician. We may assume that he was converted in early adolescence and vowed himself to service as a minister. Acceptance of his announced career by parents, friends, and teachers plus his own determination confirmed his choice until illiberal criticism threatened his usefulness and he awoke to the fact that his inner needs were not along the direction in which inertia and his conscience had constrained him.

Jan 1, 1947