By N. A. D. Parlee, N. M. El Tayeb

Fe-V alloys with small percentages of vanadium show no deviations from Sieverts' Law up to P~, = 1 atm in the 1600º to 1750ºC region. At somewhat under 8 pct V and up to at least 20pct V, at 1604" and 1661 °C, nitrogen absorption follows Sieverts' Law at low Pn2 values, but deviates from this law beyond critical values of pn2, due to formation of a nitrzde phase of approximately VN composition. The behavior below these solubility limits can be described at all temperatures by the equations: RAO and parlee1 suggested that the nitrogen absorption curve for liquid iron alloys takes the general form shown in Fig. 1 when an alloy nitride precipitate is formed. They showed that the precipitation of 6 titanium nitride from liquid Fe-Ti alloys follows this general scheme and dealt with the general theory involved. Recently, Evans and Pehlke2 reported their research on the precipitation of aluminum nitride from liquid Fe-A1 alloys. Fountain and Chipman's recent paper3 on the precipitation of boron nitride from solid solution contains a fine example of the analogous behavior which they have been studying in the solid state. Researches on the absorption of nitrogen by liquid Fe-V alloys have been described by various authors.1,4-7 Most of this work has been confined to fairly low vanadium concentrations and rather high temperatures because of difficulties variously described as, formation of surface scums, bridging, and so forth. This behavior and the rough thermo- dynamic calculations made by chipman,8 over eleven years ago, indicated that excessively high vanadium concentrations should not be required for vanadium nitride precipitation. It seemed desirable to look for and study this precipitation in order to fill out the thermodynamically interesting nitrogen absorption data on these alloys. EXPERIMENTAL METHOD The general method used was essentially the same as employed by Rao and parlee,1 in which a Sieverts type of apparatus was used and the precipitation of the nitride detected by the "break-point" in the Sieverts' Law line, and by the visual observation of the formation of the new phase on the surface of the melt. There were, however, a few differences in apparatus and technique as described below. The oil manometer used by Rao and parlee' to measure low partial pressures of nitrogen was not employed. The present authors sought to avoid as much as possible the exposure of the liquid alloy to low total pressures of gas during the 6 to 10 hr long runs because of the heavy iron evaporation-loss errors involved. This was achieved, partly by keeping evacuation times to a minimum with fast pumping but largely by the use of two burettes, one for argon and one for nitrogen, and using them to equilibrate the alloy with mixtures of argon and nitrogen rather than nitrogen alone. Each run involved a careful sequence of operations. After melting, de-

Jan 1, 1963

By AIME AIME

IN A STATEMENT summarizing general conditions in the Federated American Engineering Societies, the executive secretary, L. W. Wallace, expresses the belief that the Federation has made substantial progress. At the annual meeting of the American Engineering Council, to be held in Washington Jan. 5 and 6, this progress will be shown by reports covering activities in many fields. "Unquestionably," says Mr. Wallace, "the Federa¬tion has made favorable and permanent contacts in Washington. Through the, activities of Congress and of the new Federal administration. we have had the opportunity to render some really constructive service. We feel, however, that the great body of engineers are not adequately informed of the organization of the Federation, of its aims and purposes and of its activities.

Jan 1, 1921

By D. F. DeSante, A. S. Tetelman

MICROCRACKS are often introduced into commercial metals during fabrication processes such as swaging, cold rolling, deep drawing, and welding. These microcracks act as strain concentrators and may be capable of causing premature catastrophic failure of a component or weld. The present investigation was undertaken to determine whether high-temperature annealing treatments may be capable of reducing or negating the detrimental effects of such existing microcracks. Internal microcracks, ranging from 0.1 to 0.85 mm in length and averaging 0.23 mm, were introduced into polycrystalline Fe-3 pct Si tensile specimens (0.155 mm grain size) by the cathodic charging of hydrogen.1'2 The typical appearance of such microcracks and their associated strain patterns (made visible by the technique of dislocation etch pitting3) is shown in Fig. 1. The stress fields of the dislocation loops formed during plastic relaxation stabilize the microcracks so that, when the internal hydrogen pressure is removed: the microcracks stay open, rather than disappear as perfectly elastic cracks would be expected to do.' As shown in Fig. 2, such stopped microcracks cause a 36 pct decrease in the macroscopic cleavage fracture strength at -196°C.

Jan 1, 1969

By M. N. Nabighian, J. R. Odekirk, D. M. Hausen

Preliminary investigations based on the concept of cross-power indicate that quantitative volume percentages of minerals, including quartz, orthoclase, plagioclase, fluorite, and chalcopyrite can be obtained by X-ray diffraction analysis. Pulverized samples are scanned from 4° to 65°, 2e, using a Norelco diffractometer, with the output recorded on a punched tape at 40 intervals per degree, 29. Errors from crystal orientation are minimized by (1) gridded surface packing, (2) sample spinning, and (3) quantitative measurement of all major diffraction peaks. Computer programming enables rapid quantitative evaluation of X-ray diffraction data. Results to date indicate that most minerals analyses can be performed within an accuracy of ±2%. Metallurgical applications include analysis of various flotation concentrates and tailings.

Jan 1, 1973

By Gilbert L. Eggert

The effects of reactor irradiation on age hardening in a Cu-2 wt pct Be alloy have been investigated in two neutron-energy ranges. During some of the irradiations, specimens were exposed to high-energy fission neutrons which passed through a boron-10 shield; during other bombardments, the boron-10 was omitted and specimens were irradiated in a reactor thermal column, or the fuel configuration was modified to increase the thermal-neutron flux at a location in the core. Differences in length, X-ray diffraction angle, and hardness indicated that low-energy neutron irradiation made a small contribution to changes in the measured properties. The influence of defects generated by knock-om with less than the Brinkman critical energy or by prompt (n,y) recoil is suggested as the cause of this effect. EXPERIMENTS designed to test the effects of reactor irradiation on the properties of age-hardening alloys have to the present time employed fluxes un-differentiated according to neutron energy. Billing-ton and Siegell in 1950 were the first to perform such an experiment and to compare the results with those obtained by thermal aging. These authors concluded that precipitation in a Cu-2 wt pct Be alloy was not enhanced by the radiation. However, 4 years later, Murray and Taylor,2 working with specimens of the same Cu-2 wt pct Be alloy, reported that an increase in density, hardness, and resistivity which followed reactor irradiation resembled changes associated with thermal aging at about 100°C. (It should be noted that these authors reported that higher aging temperatures caused a decrease in resistivity.) cupp3 reported hardness results similar to those of Murray and Taylor. Koppenaal4 showed that irradiation-enhanced precipitation and irradiation defect hardening were not simply additive but that they acted separately in an irradiated alloy. Kernohan et a1.,5 working with Ni-Be, offered evidence that beryllium was removed from solid solution by reactor irradiation and suggested that the mechanism was one of increased diffusion through the use of vacancies in the structure. piercy6 also found that more precipitate particles were formed by fission-neutron irradiation of a Cu-Co alloy which contained a small amount of particles before irradiation. He proposed that the additional particles were caused by an appreciable amount of diffusion during the final cooling of displacement spikes. The retrogression of extant precipitate particles found by Murray and Taylor2 and Boltax7 as well as piercy6 indicated that nuclei were dissolved within a high-energy spike region and, upon resolidification of the perturbed volume, new nuclei precipitate and grow by enhanced diffusion. Bleiberg et al.' and Konobeevski et al.' explained phase changes obtained by irradiating fissionable alloys in terms of retrogression and re-precipitation in regions of high-energy spikes. Parsons and Balluffi10 used electron microscopy to verify that crystallization did indeed occur in displacement spikes which were formed in amorphous germanium by fast-neutron irradiation. The concept that low-energy neutron irradiation might cause structure-sensitive property changes in semiconductors by atomic recoil associated with the (n, y) reaction was first proposed by Schweinler" and walker." This thesis was tested by Cleland and crawford" and found to be valid. Coltman et al.14 exposed a variety of pure metals to thermal-neutron irradiation at cryogenic temperatures and attributed the resulting resistivity changes to the action of defects created by (n, y) recoil. The present work was undertaken to extend the concepts of Schweinler," walker," and Coltman et al.I4 to the case of an age-hardening alloy and to determine whether or not the action of defects produced by thermal-neutron irradiation would en-hance age hardening. EXPERIMENTAL PROCEDURE Omeea West Reactor Irradiations.* Thermal-

Jan 1, 1965

Organization Place Date 1919 National Drainage Congress St. Louis, Mo. Nov. 11-13 American Mining Congress St. Louis, Mo. Nov. 1.7-21 Canadian Mining Institute Vancouver, B. C. Nov.. 26-28 American Society of Mechanical Engineers:.... New York, N. Y. Dec. 2-5 American Institute of Chemical Engineers Savannah, Ga. Dec. 3-6 Geological Society of America...; Boston, Mass. Dec. 29-31. American Society of Heating and Ventilating 1920 Engineers New York, N. Y. Jan. Mining and Metallurgical Society of America ... New York, N. Y. Jan. 13. American Institute of Min. and Met. Engineers... New York, N. Y. Feb. 16-19 American Ceramic Society Philadelphia, Pa. Feb. 23-26

Jan 11, 1919

By J. P. Murphy, T. E. Leontis

DURING the last few years, the trend in the aircraft and automotive industries has been toward higher and higher operating engine temperatures. This has created considerable interest in the effect of temperature on the properties of alloys. In the magnesium field, it has been recognized for many years that the addition of cerium imparts high strength and good resistance to creep at elevated temperatures. Beck,1 in his treatise on-magnesium, has summarized the work of German investigators. This includes the unpublished data of Menking, showing the increase in strength and hardness of extruded alloys containing 2 to 20 per cent Ce at temperatures from 200 to 300°C. (68° to 572°F.) and the results of Vosskühler, who demonstrated the improved resistance to creep of alloys containing 6 per cent Ce plus 2 per cent Mn and 0.5 per cent Ce plus 2 per cent Mn at 150°C. (302°F.). Wellinger and Keil2 have also reported the creep properties of a forged magnesium-cerium-manganese alloy at 200° and 250°C. (392° and 482°F.). Haughton and Prytherch have determined the tensile properties of various forged magnesium alloys containing cerium, cerium plus manganese, cerium plus calcium, cerium plus nickel, cerium plus nickel plus manganese, and cerium plus cobalt plus manganese at temperatures up to 290°C. (554°F.). Magnesium-cerium alloys have been used in some commercial applications. It is reported that an alloy containing 3 per cent Ce plus 0.5 per cent Mn plus 0.5 per cent Ca is being used on a forged impeller in Great Britain. Two forged parts made from an alloy with a nominal composition of 5 per cent Ce and 2 percent Mn have been found on the German .BMW-801D aircraft engine. These two forgings consist of a supercharger impeller and a rear cam-follower guide. In this country, several types of pistons have been made experimentally in both .the cast and the forged conditions from an alloy containing 6 per cent Ce plus 2 per, cent Mn and in the cast condition from an alloy of magnesium plus 10 per cent Ce. The cast pistons have been tested in various types of internal-combustion engines, with promising results. This paper presents the results of an extensive investigation on the properties of various cerium-containing magnesium alloys in both the cast and the forged conditions. Data are presented to show the beneficial effects of increasing amounts of cerium on the mechanical properties of magnesium at elevated temperatures. The effects of heat-treatment on the properties of these alloys and the attendant changes in the microstructure are discussed. The

Jan 1, 1946

By Robert C. Berggren

THE hot-milling process for reconditioning rock-drill bits is not new. It has been employed by a few mines for years and in the past decade it has been widely adopted, as its advantages have become better known. Because of the extensive commercial development in England and Canada of machines to operate on this principle, general acceptance has been largely in the British possessions and until recently has been chiefly in the field of conventional steel. In the past two years there has been a definite trend toward hot-milling of detachable bits in Canada, [t] but only in the past year has any considerable attempt been made to build special machines for this type of work. Generally a machine designed for conventional steel has been used and special holders employed to manipulate the bit. As early as 1934 at least one operator in the United States had adapted hot-milling to conventional steel with a substantial saving in resharpening costs.1 Several other operators have taken it up but there has been no widespread adoption of the method in this country by users of conventional steel. This may be partly explained by the fact that until recently no American manufacturer produced this equipment and operators have been obliged to build their own hot-millers or import them. Several years ago a few machines were built in Seattle, Washington, and operated in some mines in the northwest, but, for reasons not generally known, the effort was abandoned. THE PROCESS Hot-milling performs the function of re-dressing the bit at a forging temperature of about 1650°F., by the removal of metal from the flutes with a milling cutter, followed by a similar cut from the bit gauge. Conventional bits are thus treated following the usual forging operation in a sharpener, and usually in the same heat.

Jan 1, 1940

THE Johnson award for 1926 was given to T. L. Joseph for his experimental work on blast-furnace operation. When the Bureau of Mines undertook its experimental blast-furnace investigation in 1919, a number of operators and metallurgists were doubtful as to the practicability of small-scale tests. Several pre-vious attempts, outside the Bureau, to operate small furnaces had been unsuccessful. However, pig iron was produced in three and four-ton furnaces during the first half of the nineteenth century. The operation of a small furnace did not therefore seem an impossible task. This point of view, together with a realization of the importance of problems connected with the pro-duction of pig iron, prompted the Bureau to undertake this work. Such problems as the feasibility of using charcoal briquets as a fuel, the application of oxygen enriched blast, and the use of new ores and raw ma-terials, in general, can be investigated only at consider-able cost on full sized furnaces, while with an experimental furnace they can be conducted at a com-paratively ;small, cost. The results of small-scale tests are sufficient to determine whether the problem. War-rants the expenditure required for a trial on a com-mercial scale. The accompanying photographs and chart show the various stages of the experimental furnace development. Some idea of the size and shape of furnaces which were tested can be had from the development chart. In oper-ating furnaces A to F, a series of changes were made to increase hearth temperature. Perhaps the most im-portant change was the position of the tuyeres with respect to the bottom of the hearth. The height of the tuyeres above the hearth was gradually increased and the hearth diameter decreased. It was shown by this series of furnaces that metal and slag are the chief source of heat supply to the crucible. For this reason there is a minimum rate at which these materials can be brought into the hearth of a small furnace if it is to function properly. The rate of slag "and metal fall are determined by the burden on the furnace and the rate of blowing. Due to lack of funds necessary to provide ample blowing equipment, hot blast stoves, essential mechani-cal features, and to meet operating expenses, it. was necessary to work with much smaller furnaces, such as G to K shown in the chart. The particular object of these tests was to study the extent to which reactions could be speeded up by decreasing the size of the stock. One decided change, noticed at the beginning of this series of tests, was the effect which coke size had on the production of a strongly reducing gas. Furnace G, 22 in. high, operating on coke crushed to pass 10 mesh, made a gas richer in carbon monoxide than did fur-naces A to F, operating on run-of-the-oven coke.

Jan 3, 1927

By F. R. Hensel

Up to the present time few attempts have been made to produce hard nonmagnetic materials by heat treatment of austenitic steels. The usual result has been to cause them to pass into the martensitic stage, thus destroying to a great extent the typical austenitic properties, since this involves a transition of a portion of the iron from a face-centered to a body-centered type of atomic arrangement. High-strength nonmagnetic materials such as might be provided by properly hardening austenite are required in the electrical industry for different machine parts. In Europe nonmagnetic retainer rings for restraining the end-turns of the rotor windings in turbo-alternators have been developed as a special application of high-strength austenite. In testing1 a 28,000-kva. three-phase Siemens turbogenerator running at 3000 r.p.m. at full load current, the losses in the short-circuit test were 450 kw. for the magnetic ring and 286 kw. for the nonmagnetic, and the difference should be attributable to the magnetic ring. The differences in temperatures during the same test are given in Table 1 and these show the advantage of a nonmagnetic over a magnetic retainer ring. Hardening in this case was obtained by cold working, such as hammering, rolling or some means for stretching the steel while at a temperature near 500" C. One means for stretching2 is to rotate the forged or rolled ring in a centrifugal machine so as to develop within it stress higher than

Jan 1, 1931

By H. H. Podgurski, H. E. Knechtel

Annealed Fe-Al alloys do not react readily to form AlN when held at 500ºC in NH3-H2 gas mixtures, but do so upon the introduction of dislocatims. Nuclea-tion of the nitride phase occurs on dislocation sites. In turn, the growth of the aluminum nitride particles causes the ferrite phase to yield plastically, generating more dislocations for the nucleation process. The nitride phase extracted from an Fe-2 pct A1 alloy nitrogenated at 500°C was identified as stoichio-metric aluminum nitride with a hexagonal crystal lattice. THIS investigation reveals the role that dislocations play in initiating and sustaining the nitriding reaction in Fe-A1 alloys. As early as 1931 the work of Meyer and Hobrock1 suggested that the initiation of the nitriding reaction could involve a nucleation controlled process. Recently Bohnenka2 depicted the gas-phase nitriding process below 600°C as one of mixed control limited by nitrogen penetration through the surface, by nitrogen diffusion, by aluminum diffusion, and by nucleation of the nitride phase, Fig. l(a). In our research in a comparable alloy (0.57 pct Al) at 575ºC, we have observed a nitrogenation which we feel is better described by Fig. l(b). In the case of a 2 pct-A1 alloy partially nitrided at 500°C we propose the profiles shown in Fig. l(c). For a complete and accurate description of the process, a concentration profile of the dislocation density in the test specimen would be needed. EXPERIMENTAL Nitrogenization was conducted between 500" and 575°C in a variety of NH3-H2 gas mixtures on three Fe-A1 alloys: 1) zone-refined iron + 0.16 i 0.2 pct Al—levita-tion melt, 2) zone-refined iron + 0.57 0.02 pct Al— levitation melt, 3) plastiron + 2 pct Al—melted by induction heating. To demonstrate the effect of dislocations on reactivity, both cold-worked and annealed samples were investigated. All nitrogenation rate studies were conducted gravimetrically with a gold-plated invar balance4 contained in a gas-flow system. To avoid contamination of the specimens in the reaction zone of the system, the reaction chamber was constructed of high-purity dense alumina. The activity of nitrogen was fixed by specific NH3-H2 gas mixtures whose compositions were continually monitored by calibrated thermal conductivity gages and checked by chemical analysis. Variations of ± 0.1 pct NH3 could easily be detected by both methods. Throughout this paper the activity of nitrogen is defined as PN3 /PH23/2 , where PNH3, and Ph2 are partial pressures in atmospheres. Electron transmission, density measurements, and chemical analyses were made on specimens before and after nitrogenating in order to reveal structural and chemical changes. Similar studies as well as X-ray diffraction studies were conducted on nitride extractions from the nitrogenated 2 pct-A1 alloy. These extractions were obtained by the use of an anhydrous bromine-methyl acetate solution which dissolves the iron and leaves the insoluble nitrides as a residue. Hardness profiles were obtained on cross-sections of partially nitrided specimens to demonstrate the extent of nitriding through the thickness of the specimens. RESULTS AND DISCUSSION The nitrogen activity in the NH3-H2, atmospheres was never allowed to reach a level capable of producing iron nitride (Fe4N). Hence, the term nitriding as used in this paper refers only to the formation of aluminum nitride whereas nitrogenation refers to the total uptake of nitrogen regardless of how it is distributed throughout the alloy. The weight increases observed during the initial stage of a nitrogenating treatment are due primarily to the solution of nitrogen in the ferrite phase, particularly when starting with annealed specimens. Because this initial nitrogenation rate in the case of the 0.57 pct A1 alloy, see Figs. 2 and 3(a), was most rapid the weight change that occurred thereafter might be attributed to the nitriding reaction with the exception of a small weight increment due to the irreversible pickup of oxygen by aluminum. The oxygen (<70 ppm) came from traces of H2O and 0, in the hydrogen and ammonia gases. On the basis of discrepancies between total weight increase and the increase in the nitrogen content of the sample as determined by chemical analysis, it was estimated and later established by activation analysis, that as much as 200 ppm of oxygen were taken up by a fully nitrided Fe-0.57 pct A1 specimen at 575°C. Most of the oxygen could have been picked up from the nitriding atmosphere on the surface of the samples during cooling to room temperature. Even 50 ppm of water in the gas phase will become oxidizing to iron before the sample has cooled to room temperature. The lack of reactivity* of these alloys in the annealed

Jan 1, 1970

By Nelson Severinghaus

Mineral fillers have been defined as inert materials that are included in a composition for some useful purpose. Because this definition and the scope of this review are not specific-indeed, exceptions abound-accurate total statistics are unavailable. One source estimates the total production in the United States in 1979 at 11.3 Mt (12.5 million st) valued at $534 million, averaging $49.19 per ton. Included are a broad group of minerals-asbestos, barite, bentonite, ground limestone and dolomite, clays, diatomite, feldspar, micas, silica, talc. Additional references will be made to synthetic mineral-derived fillers such as aluminum hydrate, precipitated calcium carbonate, and pyrogenic and precipitated silicas and silicates. A section on related uses at the end of this chapter covers absorbents and filters. Mineral fillers can be included in compounds to accomplish a variety of final results. Hardness, brittleness, impact strength, compressive strength, softening point, fire resistance, surface texture, electrical conductivity, and a host of other physical characteristics may be modified by the inclusion of fillers. These effects are the result of properties of the fillers, including chemical activity, hardness, particle size, shape and distribution, surface structure, color, density, and refractive index. To facilitate an overview of the mineral filler industry, this chapter will review the general usage of fillers, the inherent characteristics that intensify their utilization, and similarly their manufactured characteristics. Major using industries will then be examined in detail. Specific information on deposits and processing for industrial minerals will be found in the appropriate commodity chapter. All of these same minerals have additional significant uses based on their chemical composition or other characteristics. References will be found in other use chapters and summarized in commodity chapters. The chart in Table 1, updated from the 4th edition of Industrial Minerals and Rocks, illustrates the major mineral fillers (both natural and manufactured) and their more important end uses. Use of Mineral Fillers Archaeologists have found that more than 5000 years ago, bitumen used for mortar and waterproofing contained mineral contaminants that acted as fillers. Since that time man has added mineral products to compounds to improve certain characteristics. Perhaps the most common objective of filler usage is reduction of cost of the end product. Certainly the inclusion of a filler that costs 2¢ per 0.45 kg (lb) will reduce the cost of a plastic product whose resin costs 50¢ per 0.45 kg (lb). But the decision to use a specific filler is not that simple. It may "soak up" binder, making a compound more viscous and perhaps preventing its flow into a mold as an injection molding compound, but similarly will give good anti-sag characteristics to putty, caulking compound, or undercoating. Fillers may be incorporated to modify: 1) Cost 2) Physical characteristics 3) Flow characteristics 4) Fire resistance 5) Density 6) Heat conductivity 7) Color or brightness and opacity 8) Hardness, brittleness, impact strength 9) Deformity, viscosity, softening point 10) Processing problems 11) Electrical conductivity 12) Surface texture 13) Thermal expansion characteristics 14) Abrasion resistance

Jan 1, 1983

By B. Ramaswami

INTERNAL oxidation occurs readily in silver due to the rapid diffusion of oxygen in silver.&apos; It has a marked effect on creep in polycrystalline silver2 and raises the critical resolved shear stress in single crystals of silver.3 However, the effect of oxygen on the work-hardening parameters of silver is not known. It is the aim of this paper to describe the effect of internal oxidation on the work-hardening characteristics of single crystals of silver and an Ag-0.1 at. pct A1 alloy. The materials used were: 99.99 pct Ag from Handy and Harman and 99.993+ pct A1 from Alcoa. Single crystals, 6 mm by 6 mm in cross section of silver and Ag-0.1 at. pct A1 of mo.5 orientation, i.e., the orientation with the Schmidt factor m = 0.5. were grown by the Chalmers technique.4 One set of specimens, referred to herein as oxidized specimens, was annealed at 940°C for 24 hr in a muffle furnace, in air, and furnace-cooled to room temperature. Another set of specimens, referred to as nonoxidized specimens, was annealed in oxygen-free helium at 940°C for 24 hr and furnace-cooled over a period of 7 hr to room temperature. The annealed single crystals were tested at room temperature in a floor-model Instron testing machine. The results are presented in Figs. 1 and 2. A

Jan 1, 1965

By Arnulf Muan, R. E. Johnson

Equilibrium CO2 /CO ratios of a gas phase coexisting with selected oxide phase assemblages of the system CaO-"Fe0"-SiOz and vnetallic iron have been determined at 1080°C. The data obtained are used to calculate activity-conzposition relations for metasili-cute, orthosilicate, and CaO- "FeO" solid solutions, and to determine a new value for the free energy of formation of C&S&0,. The metasilicate solution is practically ideal, whereas large deviations from ideality exist in the othe,r two solid solutions. BECAUSE of the geochemical and metallurgical importance of the oxides CaO, "FeO", and SiOz, the system CaO-"FeO"-SiO2 has been the subject of several experimental studies during the past 30 years. Following the delineation of phase relations at liquidus temperatures by a group of investigators at the Geophysical Laboratory of the Carnegie Institution of Washington in 1933,1 Chipman and associates in the early forties2,3 determined activities of FeO in liquids of this system. Since that time, many attempts have been made to interpret the data of Chipman et al. in terms of the constitution of the silicate liquids and the interaction parameters among the various constituents of the system (see for instance papers by Richardson4 and by Flood and coworkers5). One of the assumptions made in some of these interpretations4 is that the binary silicate systems CaSiO3-FeSiO3 and CazSi04-Fe2SiO4 mix ideally in the solid state. The objective of the present study is to provide experimental data on activity-com position relations in solid solutions of the system CaO-"FeO"-SiO2. Such data will contribute toward an understanding of the thermodynamics of silicate solid-solution phases in general, and will serve specifically to confirm or refute some of the assumptions made in interpreting liquid slag behavior. PREVIOUS WORK Phase relations in the system CaO-"FeO"-SiO2 in contact with metallic iron were determined by Bowen, Schairer, and Posnjak,1 and additional phase-equilibrium data for this system have been presented by Allen and snow.&apos; A reproduction of the most up-to-date phase diagram for this system is shown in Fig. 1.7&apos;8 Of particular interest in the present investigation are the relations among the various crystalline phases slightly below the lowest solidus temperature in the system, as shown in Fig. 2. The present work will be concerned primarily with some of the composition

Jan 1, 1968

By Robert C. Berggan

The hot-milling process for reconditioning rock-drill bits is not new. It has been employed by a few mines for years and in the past decade it has been widely adopted, as its advantages have become better known. Because of the extensive commercial development in England and Canada of machines to operate on this principle, general acceptance has been largely in the British possessions and until recently has been chiefly in the field of conventional steel. In the past two years there has been a definite trend toward hot-milling of detachable bits in Canada, but only in the past year has any considerable attempt been made to build special machines for this type of work. Generally a machine designed for conventional steel has been used and special holders employed to manipulate the bit. As early as 1934 at least one operator in the United States had adapted hot-milling to conventional steel with a substantial saving in resharpening costs.1 Several other operators have taken it up but there has been no widespread adoption of the method in this country by users of conventional steel. This may be partly explained by the fact that until recently no American manufacturer produced this equipment and operators have been obliged to build their own hot-millers or import them. Several years ago a few machines were built in Seattle, Washington, and operated in some mines in the northwest, but, for reasons not generally known, the effort was abandoned. The Process Hot-milling performs the function of re-dressing the bit at a forging temperature of about 1650°F., by the removal of metal from the flutes with a milling cutter, followed by a similar cut from the bit gauge. Conventional bits are thus treated following the usual forging operation in a sharpener, and usually in the same heat.

Jan 1, 1940

By Robert C. Berggan

The hot-milling process for reconditioning rock-drill bits is not new. It has been employed by a few mines for years and in the past decade it has been widely adopted, as its advantages have become better known. Because of the extensive commercial development in England and Canada of machines to operate on this principle, general acceptance has been largely in the British possessions and until recently has been chiefly in the field of conventional steel. In the past two years there has been a definite trend toward hot-milling of detachable bits in Canada, but only in the past year has any considerable attempt been made to build special machines for this type of work. Generally a machine designed for conventional steel has been used and special holders employed to manipulate the bit. As early as 1934 at least one operator in the United States had adapted hot-milling to conventional steel with a substantial saving in resharpening costs.1 Several other operators have taken it up but there has been no widespread adoption of the method in this country by users of conventional steel. This may be partly explained by the fact that until recently no American manufacturer produced this equipment and operators have been obliged to build their own hot-millers or import them. Several years ago a few machines were built in Seattle, Washington, and operated in some mines in the northwest, but, for reasons not generally known, the effort was abandoned. The Process Hot-milling performs the function of re-dressing the bit at a forging temperature of about 1650°F., by the removal of metal from the flutes with a milling cutter, followed by a similar cut from the bit gauge. Conventional bits are thus treated following the usual forging operation in a sharpener, and usually in the same heat.

Jan 1, 1940

By J. W. Harshbarger, E. L. Montgomery

The region of metallic ore deposits in northern Chile, southern Peru, western Bolivia, and northwestern Argentina occurs in arid zones at altitudes as high as 6 km (19,700 ft). Because surface water supplies are meager, new mines require unexploited sources of water. Prolific ground water aquifers occur in salar basins in this region of the Andean Highlands. Exploration water wells have been constructed and aquifer characteristics have been tested in eight salar basins. Results indicate ground water quality is good. Aquifer transmissivity and storage computed from results of pumping tests indicate maximum capacities of more than 170 L/sec (2700 gpm) for individual production water wells. Results of investigations conducted by the authors demonstrate that ground water reservoirs in the Andean Highlands comprise a source of large quantities of water for the mineral industry.

Jan 1, 1986

By W. V. Youdelis, W. H. Bear, G. Cochrane

HERETOFORE, there has been very little study of the effects of various metallurgical factors on the behavior of thermoelectric materials, the need for which is evident if optimum processing and design of thermoelectric devices is to be realized. Accordingly, we have undertaken such an investigation on the thermoelectric materials bismuth and Bi-Sb alloy and in this paper present some preliminary results which merit consideration, in particular the relatively high thermoelectric power and figure of merit values obtained for the Bi-12Sb (at. pct) alloy powder compacts. The thermoelectric parameters for ingot and powder compact specimens are determined and the results are compared with published data for single crystals. Preparation of Materials. The bismuth and antimony used in this investigation are six nines pure. Melting and casting of the ingots was carried out in air for expediency, since most oxidation unavoidably occurs during the preparation of the powder by filing of the ingots. Chill cast ingots of pure bismuth were prepared by pouring the melt into split copper chill molds, and unidirectionally solidified ingots of bismuth and Bi-Sb alloy were obtained by slow directional cooling in pyrex tubes. All melts remained bright during melting and casting, indicating minimum oxidation. Powder for the powder compact samples was obtained by filing the ingots with a fine and coarse file to give a variation in the particle size of the compacts. The particles in the fine powder compacts varied in size from approximately 28 pct less than

Jan 1, 1970

By J. H. Dewey, J. McCreedy

Ontario Division of The International Nickel Company of Canada, Limited, operates five under- ground mines and one open pit on the rim of the Sudbury basin. In 1962, the total underground ore production was over 10 million tons which was mined mainly by blasthole and caving methods with the remainder by cut-and-fill, square set and undercut-and-fill techniques. Because of the large expenditures required annually for explosives, a great deal of study has been devoted toward cost reduction in this field. The large saving effected by ammonium nitrate-fuel oil combination at the open pits, along with reports of its success in underground mining in Sweden, generated much interest in the possibility of its use as a replacement for high explosives in the underground operations at Inco. In June, 1960, a research engineer was assigned to this project, and preliminary investigations soon indicated substantial savings and important safety advantages. The final results of the program were successful beyond any expectations and ANFO is now used exclusively in all Inco mining operations in Ontario except shaft sinking.

Jan 11, 1964

By A. G. Guy

In a special type of electrodiffusion experiment the entire specimen is at constant temperature. The vacancies are then created at one end of the specimen and flow to the other end where they are destroyed. The energy required to operate the corresponding sources and sinks results in a super saturation of vacancies at one end of the specimen and an under -saturation at the other end. This gradient in vacancy concentration produces a chemical-diffusion flux, J(D), of vacancies in addition to the flux, J(E), caused by the electric current. Using the experimental data of Ch. Herzig,5 it is shown that a super saturation of 1 pct can cause J(D) to be about 25 pct of J(E), and thus account for the anomalous behavior of short specimens. THERE are advantages in a phenomenological treatment as contrasted to an atomistic one. For example, there are many reactions involving the element copper that are quantitatively and usefully understood from a phenomenological viewpoint, even though electron theory is not yet able to predict whether copper should be fcc or cph.&apos; Similarly, the lack of a complete atomic theory of vacancies need not prevent the development of a treatment based on thermodynamics and chemical kinetics. In the following discussion, models will be used for the vacancies and for the mechanisms by which they move or are created or destroyed, but the phenomenological treatments are not dependent on the details of these models. The important product of a phenomenological analysis is an equation that describes the relation among the measurable quantities determining the behavior of the system. Based on such an equation, experiments can be performed to study these quantities in detail. Eventually atomic theory will supply an adequate theoretical base for the phenomena in question. A chemical species whose chemical potential was invariant during reactions in binary and ternary systems of varying composition would indeed be an anomaly. Yet this is the role that has frequently been assigned to the vacancies in pure metals, in dilute solutions, and even in ordinary alloys. The weight of available evidence supports the view that supersatu-rations of vacancies are on the order of 1 pct in usual diffusion processes.&apos; Although it may seem strange that such a small deviation from equilibrium could significantly affect the thermodynamic properties of the vacancies, it is well known that the driving force for an ordinary chemical reaction is the departure of the components from their equilibrium state. Similarly, the reaction of vacancies that results in the formation of pores in various types of diffusion3 can reasonably be attributed to the supersaturation of vacancies. In the present paper, it will be shown that small degrees of supersaturation can significantly affect the kinetics of the diffusion process itself. ISOTHERMAL ELECTRODIFFUSION Two different experimental techniques are convenient for studying the behavior of vacancies in a pure metal in the presence of an electric field. Gilder and Lazarus4 studied self-electrodiffusion in a gold specimen in which only the central portion was at high temperatures. In this case the significant vacancy sources operate inside the specimen in the presence of a temperature gradient. In the laboratory of Th. Heumann a method has been devised for studying self-electrodiffusion at constant temperature.5 In principle, there is then no effect of thermodiffusion. It will now be shown why in this case the significant ATungsten disks \^^ ^^ ^Gold disks^^ ^^"T>.... "TTZA ? Up Iy&apos;7 markers ///// ////// initial plane p I y/y/y of joining \I 7//// V7//A_________I_________V//// -I 0 +I Distance from center of specimen (a) -— Direction of flow of electrons —Direction of flw of vacancies %yy} Matano I z~irkendall /%W, vy/A inlerfacej "interface ///// -} HfiK- +/ 0 Distance from center of specimen (6) Fig. 1—-Schematic illustration of the essential features of isothermal self-electrodiffusion. (a) Initial condition of specimen. (b) Condition of specimen after electrodiffusion.

Jan 1, 1970