By E. M. Wise

THE properties required of gold alloys for jewelry are not well standardized, due in part to problems peculiar to certain branches of the jewelry industry, in part to the individual preference of the fabricator and to his willingness to cope with certain difficulties in manufacture, which arise with the use of certain alloys. GENERAL REQUIREMENTS In general, the properties desired may be classed as follows: 1. Color should conform to the dictates of good taste and smart style. 2. Corrosion resistance and tarnish resistance should be good. This is to a considerable extent determined by the carat. Resistance to such corrosive agents as mercuric chloride as well as certain depilatories is unreasonable to expect and difficult to meet. 3. Strength and hardness must be adequate to maintain the delicate contours of finely modeled jewelry. 4. Wear resistance must be great enough to resist abnormal wear, such as is encountered by a wedding ring in a lifetime of wear. 5. Ductility must be sufficient to permit the fabrication of drawn shells, tubes and difficult shapes. Material having a yield point of not less than 60,000 lb. per sq. in., an ultimate strength of 100,000 lb. per sq. in., and an elongation of 40 per cent. is desirable. 6. Melting point should be between 800° and 1200° C.

Jan 1, 1928

By C. A. Mitke

(Butte Meeting, August, 1913.) 1. Character of Gases which Caused Helmets to Get Out of Order. DURING September, -1911, the fire area in the Lowell mine continually increased and gases resulting from the fire came through the upcast shaft. These gases contained such a large percentage of sulphur dioxide that the men were unable to go up and down on cages, and, within a comparatively short time, repairs in the shaft were found to be necessary. Since the fire was in sulphide ores and extended into certain timbered sections, the gases contained varying amounts of SO2 CO2, and perhaps, at times, CO. The temperature in the shaft was generally about 97°, and the relative humidity from 97 to 99.5 per cent. The corrosive action of the fumes became apparent when the cables had to be changed more often than usual, the heads of lag screws .in the guides of the shaft disappeared, and the cages needed frequent repairs. It also became necessary to repair two compartments of the shaft by putting in 150 ft. of new guides between the 600 and 800 levels and lag screws in nearly all the old guides from the surface to the 800 level. 2. Ordinary Methods of Testing Helmets which were Unsatisfactory. These conditions required all work to be done by men wearing oxygen helmets. The Draeger type was tried, and was used until all repairs were completed. At first the helmets were. tested for air circulation and air tightness and the injector was tested by water gauge according to the methods recommended by the Draeger Oxygen Apparatus Co. Six arrangements, covering .these different tests, are illustrated in the catalogue and circulars of the company.

Jan 7, 1913

By P. Chiotti, J. T. Mason

Thermal, X-ray, metallographic, and resistivity data were obtained to establish the phase diagram for the Yb-Zn system. Six intermetallic compounds and five eutectics have been identified. The compounds position at 695°C. No evidence for the compound YbZn,, was observed. Whether this compound is stabilized or inhibited by small amounts of impurities is uncertain. SEVERAL aspects of the Yb-Zn system have been reported in the literature. Much of this work deals with the crystallographic identification of some of the compounds. The YbZn compound has been reported by Iandelli and palenzonal and the YbZn, structure and thermal data for the composition range between YbZn and Yb3Znll have been reported by Michel et al. A compound of uncertain stoichiometry in the range 60 to 68 wt pct Zn with a cubic structure has been reported by Kuz'ma et aL4 The YbzZn17, YbZn,,, and YbZn13 compounds have been reported by both Kuz'ma et a1 and Iandelli and Palenzona.' YbnZn17 has also been identified by Laube. This investigation was undertaken to establish the phase diagram of this system. Ytterbium in many respects behaves as an alkaline earth rather than a rare earth metal6 and it is of interest to note the resemblance between the Yb-Zn system, the Ca-Zn,' and typical rare earth-zinc systems.g'10 MATERIALS AND EXPERIMENTAL PROCEDURES The materials used in this investigation were Ames Laboratory ytterbium and Bunker-Hill slab zinc, 99.99 pct pure. Analyses of the ytterbium showed 38 ppm Ta, 82 ppm 0, and 15 ppm N with Ca, Cu, C, Mg, Al, Si, Cr, Fe, Ni, Sc, Y, Er, Tm, and Lu all less than 50 ppm. The ytterbium was dehydrogenated by heating in tantalum under vacuum for 8 hr at 900°C. The metal was kept under argon except when being cut with shears and when being weighed. Tantalum was found to be a suitable container for alloys in the composition range between ytterbium and Yb2Zn17. With higher zinc concentrations the tantalum was penetrated by the alloy and failed after several days at temperatures of 600" to 700°C. Approximately 20 g of zinc and ytterbium metal were sealed under argon in *-in.-diam tantalum cruci- bles equipped with thermocouple wells. The crucibles were in turn sealed in stainless-steel jackets. The alloys were equilibrated in an oscillating furnace and given various heat treatments in a soaking furnace. The steel jackets were removed and differential thermal analysis data were obtained under an atmosphere of argon. The thermal analysis apparatus was calibrated against the melting points of pure zinc, aluminum, silver, and copper and found to give thermal arrests within 1°C of the accepted melting temperatures for these elements. The thermal analysis apparatus has been described in an earlier paper.g Alloys were further heat-treated as necessary and subjected to metallographic examination and X-ray diffraction analysis. Most alloys were etched with Nital (0.5 to 10 pct nitric acid in alcohol). EXPERIMENTAL RESULTS The results of the thermal analysis are summarized by the points on the phase diagram, Fig. 1. Six compounds and five eutectics were observed. The eutectic temperature and compositions in weight percent zinc are 491°C and 12 pct, 645°C and 32 pct, 687°C and 54 pct, 742°C and 67 pct, and 750°C and 77 pct. The compounds YbZn, YbZn2, Yb2Zng, Yb2Zn17, and YbZnll melt congruently at 650°, 751°, 75Z°, 754", and 755"C, respectively. The compound Yb3Znll undergoes a peritectic decomposition at 695°C. The transformation and melting temperatures for the ytterbium were observed to be 797" and 817°C. re-

Jan 1, 1969

By Linn Bradley, W. W. Strong, H. D. Egbert

Marked differences of opinion have been expressed by engineers interested in cleaning iron blast-furnace gases for use in hot-blast stoves and under boilers, in reference to the advantages of a hot-dry method over a cold-wet method. One point at issue involves the sensible heat energy in the moisture contained in the gas. Some advocates of the cold-wet methods claim that the condensation and resultant removal of the greater portion of this contained moisture by wet scrubbing, spraying or similar methods, results in a saving of some of this sensible heat energy, by reason of the fact that water vapor has a high capacity for sensible heat energy and may carry from the exit of a hot-blast stove, for example, more heat units than are sacrificed or lost when the gas is cleaned by this cold-wet method. Other advantages claimed for the latter method are: That gas burns more readily when it is free from moisture in any form; that because gas is made denser by cooling and removing the moisture it has a higher calorific value than hot gas carrying moisture; and that higher flame temperatures are obtained when the gas is cleaned by the cold-wet method. A search through the available literature fails to disclose any extensive calculations or records of conditions obtained in practice, bearing upon these phases of gas cleaning. This paper deals with these problems from the standpoint of the economy of using a gas of higher flame temperatures, of improved stove design, and of economy in the gas-cleaning department. Calculations have been made which show that by cleaning the gases by a cold-wet method the sensible heat energy of the blast-furnace gases is greatly reduced; and, in general, this loss of heat energy is far greater than that lost from the stoves or boilers due to the sensible heat capacity of the water vapor if carried away by the exit gases. By making use of the

Jan 1, 1917

By R. S. Archer

SILICON is one of the most important elements in the metallurgy of aluminum. It is always present in small amounts in the ordinary grades of "pure" aluminum, and hence in all alloys made therefrom. Within the last few years binary alloys containing up to 13. per cent, of silicon have come into extensive use for castings. Silicon is also added, beyond the amount present as an impurity, in alloys containing one or more other elements such as copper, manganese, magnesium and nickel. The binary aluminum-silicon alloys are not yet heat treated to any extent in commercial practice, although, as will be shown, their properties are affected to a very considerable degree by heat treatment. There are other aluminum alloys that develop higher strength, but the special characteristics of the silicon alloys may well lead to the application of heat-treating processes on a commercial scale. The role of silicon in the heat treatment of aluminum alloys is more important than would be indicated by consideration of the binary alloys alone, because many of the alloys that are heat treated in regular commercial practice contain some silicon in addition to that derived from the aluminum ingot as an impurity. Among these may be mentioned the heat-treated 195 alloy castings, and the wrought alloys 258, Special 178 and 51S of the Aluminum Co. of America, and the German wrought alloy, Lautal. It is the purpose of this paper to present the results of experimental work and the conclusions derived therefrom regarding the heat treatment of the binary aluminum-silicon alloys. The products heat treated included forgings, chill castings and both "normal" and "modified" sand castings.

Jan 1, 1927

By Fred H. Brooks

INTRODUCTION The toughest job for any mining company, large or small, is to locate and identify a property which it feels has the potential for development and which can be tied up through location, lease or option under terms within their means. In the case of a small company, this precludes grass-roots exploration with its attendant high costs and the extended time required to develop a prospect to the point of being a project. The small mining company, therefore must limit its search to known properties which, for various reasons, have been shut down or were never thoroughly developed at the time of discovery. These types of prospects are located either through literature search, familiarity with many mining areas in general, or through contacts and submittals from a variety of sources. In order to develop a marketable presentation to any investor, the basic requirements are the same: - the property must demonstrate the potential to provide a satisfactory return on investment - the evaluation study must be thorough and professionally developed. In order to promote any mining property, it is first necessary to know what you have. INFORMATION DEVELOPMENT We normally begin with a detailed literature search of the district, assembling all available data on the basic geology, production records, and old reports of this or neighboring properties and any other information which can be found. This will aid in the general understanding of the basic geology and hopefully allow a fairly detailed knowledge of the specific occurrence. With this information one can begin to speculate on the reserve potential and develop some high and low figures for estimating purposes as to mining method, production rate, metallurgy and begin developing estimated capital and operating costs. Cashflow runs are developed for varying tonnages (high and low), estimated high and low grades of metal and at differing market prices for the product. FINANCE CONTACTS Brooks Minerals, from its inception, has been an operating company and we have been able to assemble a small but experienced operating staff. For this reason we try to put together projects and joint ventures where we can be the operator and maintain a certain degree of control. Whether due to familiarity with many colleagues in the mining industry or due to unfamiliarity with the banking houses and securities markets, the approach to raising finance has generally been to contact the established mining companies. This requires a familiarity with the corporate philosophies of these companies with respect to their development goals and financial capabilities. A common mistake is to shotgun the proposal to many companies of different sizes and goals in hopes that one might be interested. It is more beneficial, when possible, to tailor a proposal to each company, stressing the positive points where the specific proposal best meets their interests. One company may be more interested in a development program with fairly certain and conservative return potential. The property may well contain both possibilities but a lack of understanding of the individual company's method of operation could spoil the deal. In another instance, one company may look at a property as a moderate income producer over an extended life, yet a second may elect to high-grade the deposit over a shorter period in order to provide early cash flow or take advantage of a favorable market situation. MAKING THE DEAL There are as many types of deals as there

Jan 1, 1985

By Robert E. Green, Edmund G. Henneke

The velocities of the three possible modes of elastic wave propagation have been calculated for single-crystal copper at 1-deg intervals throughout the standard stereographic triangle. The results are presented as isospeed contours. The deviations between the direction of maximum energy flux and specimen axes are presented as arrows drawn on stereographic projections. The orientation factors associated with dislocation motion on the primary slip system only and also on all twelve slip systems have been calculated for all three elastic waves. The orientation factors associated with a longitudinal standing wave resonant specimen have also been calculated. The results of these calculatians are compared with earlier calculations on aluminum crystals and the relevance of these results to ultrasonic attenuation measurements is discussed. GREEN and inton' have recently outlined a procedure for determining the orientation factors for dislocation damping in single crystals. The stress field associated with a given mode of elastic wave propagation is resolved on the slip systems in which it is assumed the dislocations are vibrating due to this stress field. Since, at room temperature, slip has been observed on a limited number of systems in fcc and hcp metal crystals, it is assumed that these systems are the appropriate ones to use for the resolving process. This procedure has been applied to aluminum crystals by Hinton and hreen' and to zinc crystals by Henneke and Green.3 In the present paper the modes of elastic wave propagation have been calculated for copper crystals possessing orientations at 1-deg intervals throughout the standard stereographic triangle. The deviation of the energy flux vectors from the specimen axis have been calculated for each mode. The stress field associated with each mode has been resolved on the (111)(110) slip systems in order to determine the orientation factors for dislocation damping. MODES OF ELASTIC WAVE PROPAGATION For any direction in a linear homogeneous aniso-tropic material three elastic modes can be propagated. In general, each of these modes has both longitudinal and transverse particle displacements associated with it and thus are not "pure" modes. However, there is always one component which is greatest in either a longitudinal or transverse direction and hence the mode may be referred to as quasi-longitudinal or quasi-transverse, accordingly. For certain axes of high symmetry pure modes may be propagated. The phenomenon of refraction of the energy flux vector is also exhibited by elastic wave propagation in ani-

Jan 1, 1969

By Stanley L. Lopata, Eric B. Kula

SEVERAL methods are available for determining pole figures by X-ray means.' The earlier film methods have been replaced by techniques in which the intensities are measured by Geiger counters on an X-ray diffractometerZm7. These methods utilize either flat transmission or reflection samples,214°8 cylindrical specimens,3 or spherical specimens.7 A single transmission or reflection sample will not yield information over the complete pole figure. The cylindrical specimens suggested by Nortod and the spherical specimen of Jetter and Borie7 have the advantage of allowing the whole pole figure to be obtained without any corrections to the intensity for absorption, There is a lower limit to the size of sheet which can be conveniently studied, however, and sample preparation can be rather tedious. Probably the most common method today for determining the complete pole figure is that developed by Schulz. A flat reflection sample is used for determining the pole figure from the center out to about 70". Because of the geometry of the system used, little or no correction for absorption or irradiated volume is necessary.4'6 A separate transmission sample is used for the region near the edge of the pole figure. This procedure requires two separate samples, one of which must be a thin carefully-prepared transmission sample. Furthermore, since the reflection and transmission data are in different arbitrary intensity units, a region of overlap must be obtained, and the intensity data from one set of measurements converted to units of the other. These are serious disadvantages of this method, and they point out the need for a simplified procedure. Since the reflection technique can be used for planes whose normals lie up to about 70° from the sample surface normal, it is apparent that a complete pole figure can be obtained by reflection alone if sample surfaces are cut at oblique angles to the rolling plane Specifically, if a rolled sample is cut so that the normal to the surface formed lies equidistant (54" 44') from the rolling plane normal, rolling direction, and transverse direction, then complete information for one quadrant of the pole figure can be obtained by reflection from the surface. Fig. 1 shows this oblique surface, as well as the position of the pole of this surface in the pole figure. When a surface has been cut oblique to the rolling plane, the standard polar stereographic net is inconvenient to use, and it would be more desirable to have the center of the net coincide with the pole of the oblique plane. Fig. 2 shows such a net, where the center has been offset 54' 44' to correspond to a specimen cut as in Fig. 1. This net was in effect obtained by rotating a standard polar stereographic net 54" 44' with the help of a Wulff net. With the experimental setup used. a sample can be cut from plate of 1/2-in. thickness or br Gen- erally thinner sheet is under investigation, and a composite specimen must be used. A convenient procedure has been to bond together, using epoxy resin, sufficient sheets to form a cube. These are clamped in a vise, and when dry, the whole vise is rotated and a flat surface ground at the required angle. The sample is then mounted inside a larger steel ring using Koldmount, the backside ground flat and parallel to the approximate desired thickness. The sample is then polished and etched to remove any effects of cold working during grinding. With this method only one quadrant of the pole figure is obtained. Often pole figures show symmetry around the rolling and transverse directions, and any slight asymmetry is due to scatter. Should the pole figure not be symmetrical, four oblique surfaces, corresponding to the four quadrants of the pole figure, would have to be examined. In most cases there is symmetry at least around the rolling direction, which reduces to two the number of quadrants to be investigated. For many purposes all that is required is an average polefigure for the four quadrants. This canreadilybe obtained with composite specimens of sheet material, where sheets Corresponding to each of the four quadrants can be intermixed. The four quadrants can be obtained by considering sheet in the normal position, and by rotatiolls of 180" around the sheet normal, the rolling direction, and the transverse direction. If desired, the whole thickness of the sheet can be used, yielding an average of the surface and interior textures; or the surface material can be removed from each sheet, resulting in a pole figure for the center alone. Eugene S. Meieran of the Massachusetts Institute of Technology has independently developed the same method. His results, adapted to a pole figure goniometer with a specimen spiraler, will be described in another publication.

Jan 1, 1962

By Milton E. Wadsworth, T. D. Chatwin

Bulk density variations can usually be minimized by properly mixing the material before moisture measurement. The measuring of moisture on material being with- drawn directly from storage bins requires some form of bulk density correction. In Bethlehem's pellet plants continuous automatic bulk density correction and uniform feed-rate control are obtained with Bethlehem's patented Bin Level Control System. With this sys- tem a single probe, suspended or inserted in the bin, senses whether material is at the proper level in the bin and automatically regulates filter speed to control the filter-cake discharge rate to maintain this level. The level of concentrate in the filter-cake bin can thereby be controlled to within ± 1/2 in. of the point of contact between the concentrate and the probe. Material thickness on the conveyor does not have to be controlled accurately and mix compositions can vary widely as long as they do not contain variable amounts of water-soluble electrolytes. In sinter plants, errors caused by changes in normal feed rate and bed height are minimized by counter-weights that permit the free-floating to maintain a uniform contact pressure on the mix. Large changes in mix resistance can be taken care of either by resetting the control point or by adjusting the calibration control.

Jan 9, 1968

By Julian Kennedy

When it was decided to erect these furnaces the company also decided to use the Cowper type of stoves. It was, however, desirable to improve upon the plan of the stoves then in operation, to avoid, if possible, some defects which had shown themselves in them. The stoves now in use at Furnaces " A," " B," and " C " are of the well-known type of Cowper stove, having a circular combustionchamber placed at one side of the stove, and a regencrator with crescent-shaped section, resting at the bottom oil cast-iron glatings, which are supported in turn by cast-iron girders, the products of combustion passing up the chamber, down through the flues of the regenerator, and thence to the chimney. The objection to this shape of stove, that the gases would not pass down the parts of regenerator lying beside and behind the combustion-chamber—the horns of the crescent, as it were,—did not apply to the newer form of stoves, with combustion-chamber having a straight wall next to the regenerator; but. there were other defects, the principal ones bring the small size of the openings through the regenerator and the material used for supporting it. The small passages (4" X 4") soon choked up, and when a part of them became entirely closed, not only was the effective heating surface greatly diminished, but as the remaining opening were not sufficient to absorb the heat

Jan 1, 1882

By Ferid Kromer

This paper is the first in a series which will describe geology, mining methods, and production costs of some, of Turkey's more important minerals. In this paper the economically significant minerals-chromite, meerschaum, and magnesite-of the Tagtepe district are described. The cost data presented are believed by the author to be the first made public on Turkish chromite mining.

Jan 1, 1950

By F. C. Kelley, L. L. Wyman

In order to clarify and amplify the existing data concerning the action of the cementing material in cemented tungsten carbide alloys, the authors have initiated this investigation of the entire range of cobalt-tungsten carbide alloys. Inasmuch as the ultimate objective is relative to what actually goes on during the sintering of cemented tungsten carbide materials, this work was necessarily restricted to heat treatments similar to those used in actual production of these materials. In the course of numerous experiments, the authors have noted several conditions that indicated that there was a solubility to be considered. Among these factors are the following: 1. Many of the alloys showed a much larger amount of binding constituent to be present than could possibly be accounted for by the cobalt content. 2. In many areas, grains of the carbide constituent are much larger than the particles of carbide originally added. In addition, these grains are of very regular contour. 2a. In samples of cemented tungsten carbide which had been fused in the atomic hydrogen torch in the presence of excess binder constituent, immense grains are formed, and their shapes are very regular. This is also true when the cemented tungsten carbide of 13 per cent. Co content is fused alone in the atomic hydrogen torch. Contrary to general expectation, chemical analysis of this material, after fusion in the atomic hydrogen torch, checks the analysis of unfused material. 3. In making the cemented tungsten carbide materials by the process of exerting the pressure at the time of heating a certain portion of the ' contents squeezed out of the mold. Chemical analysis has shown that this material contains approximately 12 to 20 per cent. of tungsten. The microstructure shows a cored dendritic structure interlaced with eutectic network, and some graphite, as shown in Fig. 1. 4. Thermal analysis of these materials has consistently indicated an arrest point close to 1350" C.

Jan 1, 1931

The Library of the above-named Societies is open from 9 A.M. to 10 P.M., except on holidays. It contains about 70,000 volumes and 90,000 pamphlets, including sets of technical periodicals and the publications of scientific and technical societies. Members of the Institute, with few exceptions, are forced to spend a portion of their time in localities isolated from sources of information. To these the Library, through its Library Service Bureau, can render valuable service through correspondence; letters requesting information will receive especial attention. The Library is prepared to furnish references and photographic copies of articles on mining and metallurgical subjects; to determine the existence of mining maps, and to furnish general information on the geology and mineral resources of all countries. All communications should be made as definite as possible so that the information received may be what is, desired and not include collateral natter which may not be of interest. The time spent in-searching for such collateral matter will be saved, and the information will be sent more, promptly and-in more usable shape.

Jan 2, 1917

The Library of the above-named Societies is open from 9 A.M. to 10 P.M., except on holidays. It contains about 70,000 volumes and 90,000 pamphlets, including sets of technical periodicals and the publications of scientific and technical societies. Members of the Institute, with few exceptions, are forced to spend a portion of their time in localities isolated from sources of information. To these the Library, through its Library Service Bureau, can render valuable service through correspondence; letters requesting information will receive especial attention. The Library is prepared to furnish references and photographic copies of articles on mining and metallurgical subjects; to determine the existence of mining maps, and to furnish general information on the geology and mineral resources of all countries. All communications should be made as definite as possible so that the information received may be what is desired and not include collateral. matter which may not be of interest. The time spent in searching for such collateral matter will be saved, and the information will be sent more promptly and in more usable shape.

Jan 3, 1917

The Library of the above-named Societies is open from 9 A.M. to 10 P.M., except on holidays. It contains about 70,000 volumes and 90,000 pamphlets, including sets of technical periodicals and the publications of scientific and technical societies. Members of the Institute, with few exceptions, are forced to spend a portion of their time in localities isolated from sources of information. To these the Library, through its Library Service Bureau, can render valuable service through correspondence; letters requesting information will receive especial attention. The Library is prepared to furnish references and photographic copies of articles on mining and metallurgical subjects; to determine the existence of mining maps, and to furnish general information on the geology and mineral resources of all countries. All communications should be made as definite as possible so that the information received may be what is .desired and not include collateral matter which may not be of interest. The time spent in searching for such collateral matter will be saved, and the information will be sent more promptly and in more usable shape.

Jan 6, 1917

The Library of the above-named Societies is open from 9 A.M. to 10 P.M., except on holidays. It contains about 70,000 volumes and 90,000 pamphlets, including sets of technical periodicals and the publications of - scientific and technical societies members of the Institute, with few exceptions, are forced to spend a portion of their time 'in localities isolated from sources of information. To these the Library, through its Library Service Bureau, can render - valuable service through correspondence; letters requesting information will receive especial attention. The Library is prepared to furnish references and photographic copies of articles on mining and metallurgical subjects; to determine the existence of mining maps, and to furnish genera1 information on the geology and mineral resources of all countries. All communications should be made as definite as possible so that the information received may be what is desired and not include collateral matter which may not be of interest. The time spent in searching for such collateral matter will be saved, and the information will be sent more promptly and in more usable shape.

Jan 10, 1916

The Library of the above-named Societies is open frond 9 A.M. to 10 P.M., except on holidays. It contains about 70,000 volumes and 90,000 pamphlets, including sets of technical periodicals and the publications of scientific and technical societies. Members of the Institute, with few exceptions, are forced to spend a portion of their time in localities isolated front sources of information. To these the Library, through Its Library Service Bureau, can render valuable service through correspondence; letters requesting information will receive especial attention. The Library is prepared to furnish references and photographic copies of articles on mining and metallurgical subjects; to determine the existence of mining neaps, and to furnish general information on the geology and mineral resources of all countries. All communications should he made as definite as possible so that the information received may be what is desired and not include collateral matter which may not be of interest. The time spent in searching for such collateral matter will be saved, and the information will be, sent more promptly and in more usable shape.

Jan 1, 1917

The Library of the above-named Societies is open from 9 A.M. to 10 P.M., except on holidays. It contains about 70,000 volumes and 90,000 pamphlets, including sets of technical periodicals and the publications of scientific and technical societies. Members of the Institute, with few exceptions, are forced to spend a portion of their time in localities isolated from sources of information. To these the Library, through its Library Service Bureau, can render valuable service through correspondence; letters requesting information will receive especial attention. The Library is prepared to furnish references and photographic copies of articles on mining and metallurgical subjects; to determine the existence of mining maps, and to furnish general information on the geology and mineral resources of all countries. All communications should be made as definite as possible so that the, information received may be what is desired and not include collateral matter which may, not be of interest. The time spent in searching for such collateral matter will be saved, and the information will be sent more promptly and in more usable shape.

Jan 4, 1917

The Library of the above-named Societies is open from 9 A.M. to 10 P.M., except on holidays. It contains about 70,000 volumes and 90,000 pamphlets, including sets of technical periodicals and the publications of scientific and technical societies. Members of the Institute, with few exceptions, are forced to spend a portion of their time in localities isolated from sources of information. To these the Library, through its Library Service Bureau, can render valuable service through correspondence; letters requesting information will receive especial attention. The Library is prepared to furnish references and photographic copies of articles on milling and metallurgical subjects; to determine the existence of mining maps, arid to furnish general information on the geology and mineral resources of all countries. All communications should be made as definite as possible so that the information received may be what is desired and not include collateral matter which may not be of interest. The time spent in searching for such collateral matter will be saved, and the information will be sent more promptly and in more usable shape.

Jan 10, 1916

The Library of the above-named Societies is open from 9 A.M. to 10 P.M., except on holidays. It contains about 70,000 volumes and 90,000 pamphlets, including sets of technical periodicals and the publications of scientific and technical societies. Members of the Institute, with few exceptions, are forced to spend a portion of their time in localities isolated from sources of information. To these the Library, through its Library Service Bureau, can render valuable service through correspondence; letters requesting information will receive especial attention. The Library is prepared to furnish references and photographic copies of articles on mining and metallurgical subjects; to determine the existence of mining maps, and to furnish general information on the geology and mineral resources of all countries. All communications should be made as definite as possible so that the information received may be what is desired and not include collateral matter which may not be of interest. The time spent in searching for such collateral matter will be saved, and the information will be sent more promptly and in more usable shape.

Jan 12, 1916