By A. J. Lena, M. F. Hawkes

Changes in hardness, tensile properties, microstructure, electrical resistance, and X-ray diffraction effects indicate that lattice strains are necessary for the embrittlement of ferritic stainless steels when heated for relatively short times at 475°C (885°F). It is suggested that 475°C (885°F) embrittlement is due to the accelerated formation of an intermediate stage in the formation of s under the influence of these strains. FERRITIC stainless steels (low carbon alloys of iron with more than 15 pct Cr) are subject to two forms of embrittlement when heated in the temperature range of 375° to 750°C. The embrittlement which occurs after long time heating between 565" and 750°C is well understood; it is caused by the precipitation of the hard, brittle s phase. Sigma is an intermetallic compound of approximate equi-atomic composition with an extended range of formation in Fe-Cr alloys. The maximum temperature at which this form of embrittlement can occur is dependent upon chromium content; and is approximately 620°C for a 17 pct Cr steel and 730°C for a 27 pct Cr steel. The other form of embrittlement occurs after relatively short heating periods in the range of 375" to 565°C; in the higher chromium steels, hours may be sufficient as compared to months for s embrittlement. This phenomenon is not at all well understood and several controversial theories have been proposed. The rate and intensity of embrittlement increase with increasing chromium content but the maximum rate occurs at 475°C re-gardless of chromium content. As a result of this, the phenomenon has been termed 475°C (885°F) embrittlement. The effect of 475°C embrittlement on the properties of ferritic stainless steels has been thoroughly reviewed by Heger.1 The embrittlement causes a pronounced decrease in room temperature impact strength and ductility, a large increase in hardness and tensile strength, and a decrease in electrical resistivity and corrosion resistance. Microstructural changes accompanying embrittlement are minor and difficult to interpret with a general grain darkening, appearance of a lamellar precipitate, grain boundary widening, and precipitation along ferrite veins having been reported at various times. With the exception of reported line broadening, X-ray diffraction studies by conventional Debye analysis of solid samples have been of little value. BY making use of electron diffraction methods, Fisher, Dulis, and Car-roll' have recently shown the existence of a chromi-um-rich, body-centered cubic phase in 27 pct Cr steels which had been aged at 482°C (900°F) for as long as four years. Two types of theories have been advanced to account for the embrittlement. The first of these requires the precipitation of a phase not inherent in the Fe-Cr system with various investigators suggesting a carbide,3 nitride,3 phosphide,4 or oxide." Theories of this type have difficulty accounting for the influence of alloying elements on the embrittlement and for the facts that a minimum chromium content is necessary for embrittlement and the intensity of embrittlement increases with increasing chromium content. The second type of theory that has been proposed relates 475°C embrittlement to s phase formation which is inherent in the Fe-Cr system. An assumption of this kind can adequately explain the influence of alloying elements, for they exert an effect on 475°C embrittlement similar to that on s phase for-mation as can be seen in Table I. The minimum chromium content is essentially the same for both phenomena and it has been shown12,13 that s is a stable phase in the embrittling temperature range. In addition, it has been reported14,15 that pure alloys embrittle to the same extent as commercial type alloys. There are, however, several factors which have prevented complete acceptance of a s phase theory. Foremost of these is that the embrittlement can be removed by reheating for short time periods above 600°C, which in the higher chromium steels is within the stable s region. No s has ever been observed after one of these curing treatments, nor has any s been found as a result of embrittlement at 475°C. In addition, the simple precipitation of s cannot explain the time-temperature relationships for reactions between 350°and 750°C. This behavior is shown schematically in Fig. 1. Newell 16 and Ried-rich and Loib4 have shown that 475°C embrittlement follows a C-type curve as illustrated, while Short-

Jan 1, 1955

By A. J. Weinig

The method described is a modification of Schutzenberger's whereby the solution in titrations and the standards are protected from the atmosphere by a layer of kerosene. Indigo-disulfonate is the indicator and sodium hydrosulfite the standard. The method is rapid and delicate. It has been tried on a variety of mill solutions and mill men have found the method of value. THE important part that dissolved oxygen plays in the cyanide treat-ment of gold and silver ores is commonly recognized by most metallurgists and mill men.. But heretofore there has been no simple method on which the mill man could rely for determining the amount of oxygen in the various mill solutions. A few methods are adaptable to the, laboratory, such as the gasometric1 determination by actually measuring the oxygen. Winkler's2 iodometric method, and Schutzenberger's3 method, which depends on the reducing action of sodium hyposulfite on a blue solution of indigo carmine; but these are not readily adaptable to the needs of the mill man and cannot be applied to cyanide solutions without modification. The gasometric method is the most accurate but it takes too long to complete a determination. White's' method (a colorimetric method that depends on the degree of coloration imparted to a solution of pyrogallic acid in the presence of caustic soda) although much more rapid than any of the methods named, often gives misleading results on account of grading of colors of different solutions, which nearly always contain various kinds of salts. The method herein described was devised for the use of the mill man, the aim being to develop a simple, practical, accurate method. It is a modification of the Schutzenberger method and depends on the reducing

Jan 8, 1924

By John P. Bernardi, Ralph B. Hall

Past and present phosphate production in the central Florida phosphate district has been predominantly from the unique Bone Valley formation. As these lucrative reserves are depleted, production will shift to the Hawthorn formation in all areas, but particularly so within the southern extension, where vast potential reserves of low grade phosphates exist. Use of existing plants can be extended for some years by mining deeper into the underlying Hawthorn formation, and by mining previously ignored peripheral areas if erratic combinations of the two formations. Hawthorn Production, as compared to the Bone valley, will be characterized by lower grade; lower tonnage yield, lower pebble percent of product, higher mining ratios, higher slimes (- 150 mesh) content, and more complex mining and beneficiation problems. Geological control and more sophisticated operational procedure; will become increasingly more important as the lower quality reserves replace Bone Valley production.

Jan 1, 1981

By Major N. R. Junner

Although manganese-garnets are rarely seen in hand specimens of the manganese ores and associated rocks, they have been detected by the writer in thin sections of all the ores and wall rocks that have been sliced, with the single exception of the Insuta deposit. Rhodonite, and an almost colorless amphibole, which appears to be manganiferous, are less common. Types of Occurrence (a) Rocks Composed of Manganese-garnet and Quartz The best known examples of this type are from near Bole and Wa in the Northern Territories of the Gold Coast, and from near Chama in the Gold Coast Colony. Normally these are fine and even-grained rocks, in which the garnets cannot be recognized in hand specimens. They are often stained with secondary manganese oxide. Thin sections examined microscopically are seen to be composed of aggregates of minute crystals of garnet in a matrix of mosaic quartz. Some manganese oxide and braumite (?) is often present, but other minerals are exceptional. The relative proportions of garnet and quartz in these rocks vary greatly and there is a complete gradation from quartz-rock to garnet-rock. (6) Rocks Composed Mainly of Manganese-garnet and Manganese Oxides Rocks of this type are known from Kalimbi Hill near Siripe, Pabini Hill near Bangwon, near Odumase and Konongo, and in the Ya Ya creek, about 5 miles east of Dunkwa. These are usually fine-grained banded dark-colored rocks, composed of abundant minute garnets in a matrix of black manganese oxide and braunite (?). A little microcrystalline is often present, and occasionally a little colorless amphibole. quartz (c) Rocks Composed of Rhodonite and Manganese-garnet Rocks of this type are not common. They are known from near Chama, and from the road between Senyong and Mangkuma. Some quartz is usually present. All these rocks resemble closely in texture and composition certain rocks from India, described by Fermorl as "gondite;" and they also resemble certain rocks described by Derby2 from the Queluz district,

Jan 1, 1927

By James J. Halbouty

The restraining effects of war conditions on oil-field development are well illustrated by statistics on South Texas † fields for the year 1942. Statistics also show a decline in wildcatting, but this decrease is much smaller than that shown by field activity. In comparison with results in 1941, there was a reduction of about 44 per cent in the total number of wells drilled in the area (802 in 1942 against 1452 in 1941) This 44 per cent drop represents declines of 50.4 per cent in field wells and of 17.4 per cent in rank wildcats. Field wells (exclusive of 18 wildcats that discovered fields) totaled 598; also, 204 rank wildcats were drilled (see Tables 3 and 4). The corresponding figures for 1941 are 1205 field and extension wells and 247 rank wildcats. In this connection, it should be noted that whereas in 1941 the rank wildcats made up only 17 per cent of all wells drilled in the area, their percentage of the 1942 total was 25.4 per cent. In spite of the decrease of 43 in the number of rank wildcatst drilled, there were 18 new productive areas discavered, one more than the 17 new fields found in 1941. Thus the field-discovery rate for 1942, one new field for every 11.3 wildcats drilled, compares favorably with the I to 14.5 rate of 1941. Thirteen new producing levels were opened in fields; this includes the finding of 44' gravity crude on the west flank of the Sejita field in a 5700-ft. sand, which produccs distillate higher on the structure. Interesting, and showing the general scarcity of sand discoveries, is the fact that of the 13 new sands discovered, 7 were found in Jim Wells County. The year's sand-discovery rate of one new level for every 46 field wells compares very unfavorably with the I to 19.7 rate of 1941, during which 61 new producing horizons were found. Developmeilt of new fields was on a small scale. In several instances activity in these areas was not carried beyond the drilling of the discovery well. The field discoveries of 1942, together with the type of production obtained from the discovery wells and the total number of wells (productive and dry) drilled in them, are given below: Discovery Num- Field.I County Well her Produced Wells I. Cadena....... Duval Oil 2 a. Garza......... Duval Oil I 3. Dinn......... Duval Gas I 4. Keller......... Duval Gas I 5. East.......... Tim 0 11 I 6. Green Branch . McMullen Gas 3 7. Frost. .GreenBranch........ Starr Oil I 8. Garcia........ Starr Oil 6 9. Ulrich........ Starr Oil 4 10. Lykes......... Webb Oil 2 11. McLean....... Webb Oil 9 Iz. Alamo........ Hidalgo Distillate 2 and gas 13. Penitas....... Hidalgo Distillate 2 and gas 14. Xmpnan..... Jim wells i a 15. South Premont Jim Wells Distillate i and gas 16. Quinto Creek.. Jim Wells Gas 4 17. Roth.. . :..... Jim Wells Gas I I 18. South Sinton.. San Distillate I Patricio and gas . • See Table 2 for data on discovery wells and Table I for information on these fields. • See Table 4.

Jan 1, 1943

By James J. Halbouty

The restraining effects of war conditions on oil-field development are well illustrated by statistics on South Texas † fields for the year 1942. Statistics also show a decline in wildcatting, but this decrease is much smaller than that shown by field activity. In comparison with results in 1941, there was a reduction of about 44 per cent in the total number of wells drilled in the area (802 in 1942 against 1452 in 1941) This 44 per cent drop represents declines of 50.4 per cent in field wells and of 17.4 per cent in rank wildcats. Field wells (exclusive of 18 wildcats that discovered fields) totaled 598; also, 204 rank wildcats were drilled (see Tables 3 and 4). The corresponding figures for 1941 are 1205 field and extension wells and 247 rank wildcats. In this connection, it should be noted that whereas in 1941 the rank wildcats made up only 17 per cent of all wells drilled in the area, their percentage of the 1942 total was 25.4 per cent. In spite of the decrease of 43 in the number of rank wildcatst drilled, there were 18 new productive areas discavered, one more than the 17 new fields found in 1941. Thus the field-discovery rate for 1942, one new field for every 11.3 wildcats drilled, compares favorably with the I to 14.5 rate of 1941. Thirteen new producing levels were opened in fields; this includes the finding of 44' gravity crude on the west flank of the Sejita field in a 5700-ft. sand, which produccs distillate higher on the structure. Interesting, and showing the general scarcity of sand discoveries, is the fact that of the 13 new sands discovered, 7 were found in Jim Wells County. The year's sand-discovery rate of one new level for every 46 field wells compares very unfavorably with the I to 19.7 rate of 1941, during which 61 new producing horizons were found. Developmeilt of new fields was on a small scale. In several instances activity in these areas was not carried beyond the drilling of the discovery well. The field discoveries of 1942, together with the type of production obtained from the discovery wells and the total number of wells (productive and dry) drilled in them, are given below: Discovery Num- Field.I County Well her Produced Wells I. Cadena....... Duval Oil 2 a. Garza......... Duval Oil I 3. Dinn......... Duval Gas I 4. Keller......... Duval Gas I 5. East.......... Tim 0 11 I 6. Green Branch . McMullen Gas 3 7. Frost. .GreenBranch........ Starr Oil I 8. Garcia........ Starr Oil 6 9. Ulrich........ Starr Oil 4 10. Lykes......... Webb Oil 2 11. McLean....... Webb Oil 9 Iz. Alamo........ Hidalgo Distillate 2 and gas 13. Penitas....... Hidalgo Distillate 2 and gas 14. Xmpnan..... Jim wells i a 15. South Premont Jim Wells Distillate i and gas 16. Quinto Creek.. Jim Wells Gas 4 17. Roth.. . :..... Jim Wells Gas I I 18. South Sinton.. San Distillate I Patricio and gas . • See Table 2 for data on discovery wells and Table I for information on these fields. • See Table 4.

Jan 1, 1943

Until a comparatively few years ago, interest in tantalum was limited almost wholly to its scientific investigation, but its extreme resistance to the action of even the strong mineral acids, its great avidity for the common gases, hydrogen, oxygen and nitrogen, and its capacity for transforming alternating to direct current are winning for it a place in our industrial life. Tantalum is not attacked by any single acid except hydrpfluoric, nor is it affected by solutions of alkalies. Aqua regia, which readily dissolves both platinum and gold, has no action on it. This resistance to the common corrosive agents is an outstanding property of tantalum and accounts for many of the applications to which it has been put. When heated, tantalum reacts readily with oxygen and nitrogen and absorbs large volumes of hydrogen, 740 volumes being taken up at a dull red heat. This capacity for absorbing gases is being utilized to an increasing extent in the manufacture of vacuum tubes, in which tantalum is used for the metal parts, especially for grid wire. It is said to be a superior metal for this purpose, particularly in power and sending tubes, because of its low secondary emission. The use of tantalum in the manufacture of electrodes, dishes, spatulas and other laboratory apparatus appears to be fairly steady. There has been some development in its use for dental instruments, surgical tools, pen points, hypodermic needles and acid-proof pumps. Recently it has been used in the manufacture of spinnerets for the rayon industry, of nozzles for the manufacture of artificial casings for sausages and of lining for plant equipment. Tantalum in Electrolysis It has been known for some time that certain substances permit the passage of an alternating current in one direction more readily than in the other. Tantalum possesses this property to a marked degree.' When an alternating current is passed through a cell with tantalum electrodes and sulfuric acid electrolyte, a thin film is soon formed at the

Jan 1, 1930

By H. J. McQueen, G. C. Kuczynski

ThE useful properties of k6-Alfenol and the thermenol alloys (summarized by J. E. Nachman and W. J. Buehler') have encouraged research into those alloys which, having compositions near 25 at. pct Al, 75 at. pct Fe, undergo an ordering transformation between 500° and 550°C. The equilibrium diagram of the iron-rich iron-aluminum alloys was first determined by Bradley and Jay.2,3 They distinguished three structures: the disordered, which is bcc; FeAl, which is simple cubic with one Fe atom and one Al atom per lattice site; and Fe3Al, which is fcc with three Fe atoms and one Al atom per lattice site. This last structure may be conceived as eight body-centered cubes with Al atoms at the centers of alternate ones, so that Al atoms have only Fe as first and second nearest neighbors. Later, Osawa and Murata4 determined the boundaries of the different superlattice regions in the iron-rich Fe-Al solid solution by dilatometric and X-ray methods. Two of the six phases, which they found between 0 and 50 at. pct Al, were never identified by other workers. A. Taylor and R. M. ones,' concurrently with and independently of this research, redetermined this diagram by measuring lattice parameters at temperature. Further reference will be made to their results. EQUILIBRIUM DIAGRAM A) Experimental Procedure—The alloys were prepared from NRC gas-free iron (99.9 pct Fe) and 99.99 pct Al. They were melted in alumina' crucubles under vacuum in an induction furnace. If the ingots were unsound or showed more than a 3 pct weight loss, they were rejected. The ingots were homogenized at 1100°C for 24 hr before hot-rolling at 700" to 900°C from 1 in. to 0.25 in. thick. It is interesting to note that alloys containing more than 28 at. pct Al were able to take an 80 pct reduction of area in the ordered FeAl region. The dilatometer specimens and specimens for chemical analysis were cut from these plates. A Leitz dilatometer was used to measure the coefficient of linear expansion as a function of temperature. The specimens were slowly cooled from 900" to 300°C where they were annealed for 10 hr before slowly cooling to room temperature. The expansion was recorded photographically as the alloys were heated and cooled at 1.5oC per min between 100" and 1000°C. The magnetic measurements determining the Curie points were performed on the dilatometer specimens in the dilatometer, by using direct current in the furnace windings both to heat the specimen at 1.5°C per min and to serve as the primary coil. The regular specimen holder was replaced by a thin alundum tube on which was wound, as a secondary, a closely spaced coil of fine copper wire. A reversal of current in the furnace windings produced, in the secondary, an emf which was proportional to the induction in the specimen, and which could be detected on a galvanometer. In this way, it was possible to determine the Curie points of alloys to within * 5°C. B) Results and Discussion—The coefficients of linear expansion, as obtained from the dilatometer curves, are plotted as a function of temperature and composition in Fig. 1. Since in many cases the heating and cooling curves were superimposed, it was decided to measure slopes of heating curves only. Definite high peaks, due to the transformations, were observed on each curve between 400" and 520°C, and, for alloys containing more than 23 at. pct Al, a second set of smaller peaks at temperatures above 660°C. The sharpness of the peaks indicates that ordering to Fe3Al is a first-order reaction. The compositions and the temperatures of these peaks are listed in Table I. When these temperatures are plotted as a function of the composition, the result is the constitution diagram presented in

Jan 1, 1960

By Robert H. Hafner, Irvin R. Kramer

In recent years considerable interest has been shown in surface-alloyed metals, particnlarly those of chromium (chromized steels), which have excellent corrosion resistance under a variety of severe conditions, and may undergo bending and flanging operations without spalling. An early method1 employed to produce a high-chromium case on steel was developed by Kelley in 1921. It consisted of heating a low-carbon steel in intimate contact with powdered chromium in the presence of hydrogen at temperatures sufficiently high to permit diffusion of chromium into the steel. The usefulness of this process was limited because the extremely high tem- peratures of 1200º to 1400ºC. (2200° to 2550°F.) caused excessive grain growth and warpage. Louenstein and Ulmer2 packed iron castings in ferrochromium and com- mon salt, and heated for approximately three hours at 930º to 1040°C. (1700º to 1900ºF.). A recent and more practical method of depositing chromium on steel surfaces has been developed in Germany by Daeves, Becker and Steinberg3-8 and in Russia by Izgaryshev and Sarkisov.9 This process consists of passing gaseous chromium chloride over the steel to be chromized at temperatures of 900º to 1000ºC., or packing them in a porous, ceramic material that previously had been saturated with chromium chloride. They reported obtaining a Chromized layer, 0.004 in. thick, on low-carbon steels. Later, Daeves4 established a relationship between the carbon content

Jan 1, 1943

By Robert H. Hafner, Irvin R. Kramer

IN recent years considerable interest has been shown in surface-alloyed metals, particularly those of chromium (chromized steels), which have excellent corrosion [ ] resistance under a variety of severe conditions, and may undergo bending and flanging operations without spalling. An early method1 employed to produce a high-chromium case on steel was developed by Kelley in 1921. It consisted of heating a low-carbon steel in intimate contact with powdered chromium in the presence of hydrogen at temperatures sufficiently high to permit diffusion of chromium into the steel. The usefulness of this process was limited because the extremely high temperatures of 1200° to 1400°C. (2200° to 2550°°F,) caused excessive grain growth and warpage, Louenstein and Ulmer2 packed iron castings in ferrochromium and com- [ ] mon salt, and heated for approximately three hours at 930° to 1040°C. (1700° to 1900°F,). A recent and more practical method of depositing chromium on steel surfaces has been developed in Germany by Daeves, Becker and Steinberg3-8 and in Russia by Izgaryshev and Sarkisov.9 This process consists of passing gaseous chromium chloride over the steel to be chromized at temperatures of 900° to 1000°C., or packing them in a porous, ceramic material that previously had been saturated with chromium chloride. They reported obtaining a chromized layer, 0.004 in, thick, on low-carbon steels. Later, Daeves4 established a relationship between the carbon content

Jan 1, 1942

By Robert H. Hafner, Irvin R. Kramer

In recent years considerable interest has been shown in surface-alloyed metals, particnlarly those of chromium (chromized steels), which have excellent corrosion resistance under a variety of severe conditions, and may undergo bending and flanging operations without spalling. An early method1 employed to produce a high-chromium case on steel was developed by Kelley in 1921. It consisted of heating a low-carbon steel in intimate contact with powdered chromium in the presence of hydrogen at temperatures sufficiently high to permit diffusion of chromium into the steel. The usefulness of this process was limited because the extremely high tem- peratures of 1200º to 1400ºC. (2200° to 2550°F.) caused excessive grain growth and warpage. Louenstein and Ulmer2 packed iron castings in ferrochromium and com- mon salt, and heated for approximately three hours at 930º to 1040°C. (1700º to 1900ºF.). A recent and more practical method of depositing chromium on steel surfaces has been developed in Germany by Daeves, Becker and Steinberg3-8 and in Russia by Izgaryshev and Sarkisov.9 This process consists of passing gaseous chromium chloride over the steel to be chromized at temperatures of 900º to 1000ºC., or packing them in a porous, ceramic material that previously had been saturated with chromium chloride. They reported obtaining a Chromized layer, 0.004 in. thick, on low-carbon steels. Later, Daeves4 established a relationship between the carbon content

Jan 1, 1943

By Robert H. Hafner, Irvin R. Kramer

IN recent years considerable interest has been shown in surface-alloyed metals, particularly those of chromium (chromized steels), which have excellent corrosion [ ] resistance under a variety of severe conditions, and may undergo bending and flanging operations without spalling. An early method' employed to produce a high-chromium case on steel was developed by Kelley in 1921. It consisted of heating a low-carbon steel in intimate contact with powdered chromium in the presence of hydrogen at temperatures sufficiently high to permit diffusion of chromium into the steel. The usefulness of this process was limited because the extremely high temperatures of 1200° to 1400°C. (2200° to 2550 F.) caused excessive grain growth and warpage. Louenstein and Ulmer2 packed iron castings in ferrochromium and com- [ ] mon salt, and heated for approximately three hours at 930° to 1040°C. (1700° to 1900°F.). A recent and more practical method of depositing chromium on steel surfaces has been developed in Germany by Daeves, Becker and Steinberg3-8 and in Russia by Izgaryshev and Sarkisov.9 This process consists of passing gaseous chromium chloride over the steel to be chromized at temperatures of 900° to 1000°C., or packing them in a porous, ceramic material that previously had been saturated with chromium chloride. They reported obtaining a chromized layer, 0.004 in. thick, on low-carbon steels. Later, Daeves4 established a relationship between the carbon content

Jan 1, 1942

By J. P. Matoney, E. J. Sandy, D. A. Dahlstorm

INTRODUCTION Before an understandable discussion concerning coal dewatering processes can be initiated, it is necessary to define some terms of usage. The many different meanings and interpretations of terms preclude development of standard definitions so the terms defined in this chapter should be regarded primarily as working terms intended to facilitate communication.

Jan 1, 1979

By C. P. Karr

For several years, the Bureau of Standards has been working in cooperation with an Advisory Committee on non-ferrous metals on various phases of the production and testing of zinc bronzes. The work has dealt especially with the type of metal known as "Admiralty bronze" in England and as "Government bronze" in this country and consisting of 88 copper, 10 tin, and 2 zinc. Several reports have been made on this subject and these should be considered in connection with this paper.' First Series of Five Foundry Tests A very brief summary of the first series of five foundry tests has been made12 but for the sake of clearness the results are given here in different form. The five foundries cooperating in this investigation were: Ohio Brass Co., Mansfield, Ohio; Titanium Alloy Mfg. Co., Niagara Falls, N. Y.; Packard Motor Car Co., Detroit, Mich.; National Cash Register Co., Dayton, Ohio; Bureau of Standards, Washington, D. C. The object of the work was to determine whether uniform results could be obtained with this alloy in different foundries working under definite instructions. One of the participating foundries prepared, from virgin metal, a stock of ingots of the composition 88 copper, 10 tin, 2 zinc, and at the same time poured nine test bars from this melt of virgin metal. The results of the physical tests of these bars are shown in Table 1. Examination of this table shows that the highest and most nearly uniform results were obtained when the virgin metal was cast flat in chill molds and the lowest and- most variable results were encountered when it was cast, vertical in green-sand molds. In this, as in all other tables, the mean deviation was obtained by the usual method of taking the average of the differences of the individual values from the average values.

Jan 1, 1921

AS IS evident from the discussion in previous chapters, the methods by which an open-hearth heat may be made are numerous, but any heat, in the ingot form, may be classified as one of three types, depending upon the degree of deoxidation to which the metal is subjected. These are rimmed, semikilled, and killed, and desirable ingot structures, from the standpoint of distribution of porosity, are illustrated in Fig. 63. These are the most useful types of ingot structure [ ] and represent three stages in the continuous series from "wild" to "dead killed" (see Fig. 23, page 46) ; some of the variations of each type are discussed later in the chapter. The choice of ingot structure and of finishing practice used to produce the desired metal action in the molds is determined by consideration of: 1. Specified final analysis. As an example, the production of rimmed steels is mostly limited to carbon contents below 0.30 per cent and manganese contents below 0.60 per cent; on the other hand the production of low-carbon killed steel requires greater care.

Jan 1, 1944

By C. P. Karr

FOR several years, the Bureau of Standards has been working in cooperation with an Advisory Committee on non-ferrous metals on various phases of the production and testing of zinc bronzes. The work has dealt, especially with the type of metal known as "Admiralty bronze" in England and as "Government bronze" in this country and consisting of 88 copper, 10 tin, and 2 zinc. Several reports have been made on this subject and these should be considered in connection with this paper.1 FIRST SERIES OF FIVE FOUNDRY TESTS A very brief summary of the first series of five foundry tests has been made,2 but for the sake of clearness the results are given here in different form. The five foundries cooperating in this investigation were: Ohio Brass Co., Mansfield, Ohio; Titanium Alloy Mfg. Co., Niagara Falls, N. Y.; Packard Motor Car Co., Syracuse, N. Y.; National Cash Register Co., Dayton, Ohio; Bureau of Standards, Washington, D. C. The object of the work was to determine whether uniform results could be obtained with this alloy in different foundries working under definite instructions. One of the participating foundries prepared, from virgin metal, a stock of ingots of the composition 88 copper, 10 tin, 2 zinc, and at the same time poured nine test bars from this melt of virgin metal. The results of the physical tests of these bars are shown in Table 1. Examination of this table shows that the highest and most nearly uniform results were obtained when the virgin metal was cast flat in chill molds and the lowest and most variable results were encountered when it was cast vertical in green-sand molds. In this, as in all other tables, the mean

Jan 9, 1919

By Augustus J. Bowie

THE discovery of the auriferous cement gravel deposits in and near Deadwood Gulch, Lawrence County, Dakota Territory, in 1876, created a mining excitement, and rush to the Black Hills. Numerous ten and twenty-stamp mills were built on Deadwood Gulch ; Central City and the town of Deadwood sprang into existence, and became the centres of the mining industry of the Hills. Gold quartz deposits were subsequently discovered and located on a so-called mineral belt, extending from Whitewood Creek on the south, to Deadwood Gulch on the north. A northerly group of these quartz locations was purchased in December, 1877, by parties in San Francisco,, who formed a company, incorporated under the name of the Father de Smet Consolidated Gold Mining Company. This company immediately commenced the work of exploration. The deposits were proved to be extensive, and easily mined, but it was found that the ore, on an average, would not. yield more than $10.00 per ton* of 2000 pounds. At this time the cost of supplies and materials in the Hills was high. Miners' wages were $3.50 per diem, and custom mills charged $6:00. per ton. The successful working of mines on "the belt" necessitated cheap milling. The ores being of so low grade,† this could be accomplished only with large and economically running mills. To insure the greatest possible economy, the Father,& Smet mill * Up to December 31st, 1879; the de Smet mine had produced bullion of the value of $718,211.68 from 76,155 tons of ore, being an average value of $9.41 per ton. During the year ending December 31st, 1879, the mine produced 46,344 tons, which yielded $425,360.42, or $9.18 per ton. The total gross cost of working for the corresponding period, including deadwork, exchange, legal expenses, fete., wits $219,914.82. The yield of the mine for the year 1880 (Engineering and Mining Journal, February 5th, 1881), was $600,011, with total expenses of mining and milling, of $313,108. † The first 4083 tons extracted from the de Smet mine, were selected, yielding $62,783.97. The next 25,728 tons produced $230,067.24. The total 29,811 tons were weighed, and worked at custom mills. The yield of the first 409 tons from tine Golden Terra Mine was $11.44 per-ton.

Jan 1, 1882

By H. A. Schwartz, W. Kenneth Bock

IN this paper it is shown that when the tensile strength of a given steel in various states of heat-treatment is plotted against its elongation, a straight line results. The equation of this straight line can be computed with considerable accuracy from its chemical composition. The appropriate equations are given. The logarithm of the slope of the tensile-strength locus is shown to be proportional to the cumulative effect of the total alloy addition and the position of the line to be directly proportional to the cumulative effect of the alloy content. It is further pointed out that heat-treatment is more effective than composition in determining yield ratio. The latter enters mainly by its effect on hardenability, which is briefly discussed. Reduction of area and Brinell number are given some incidental attention. The data are applicable only to steels that have been normalized and/or quenched. The steels, if normalized, may or may not have been tempered. If quenched they must have been tempered at or above 400°C. (750°F.).

Jan 1, 1944

By E. O. Kirkendall

The investigation reported herein was undertaken to obtain data to supplement those presented in an earlier paper,l particularly for longer times at a higher temperature. This information may further develop our knowledge of the mechanism of diffusion in substitutional solid solutions. Diffusion of solute atoms interstitially dissolved is not difficult to visualize: it can take place without much disturbance of the solvent atoms. The mechanism of diffusion of solute atoms substitutionally dissolved is not so easily understood. Many theories have been advanced. Rosen-hain,2,3 Frenkel,4 Smekal,5 Langmuir,3,6 Steigman, Shockley and Nix,' and Johnson8 all proposed theories to explain diffusion. Langmuir's proposed mechanism consisted of a simple cyclic interchange of atoms involving an interchange in lattice positions of four or more atoms. This mechanism, accepted by the author at the time of his previous publication,1 and apparently quite generally accepted, required a net exchange in positions of both solute and solvent atoms in equal numbers. In other words, the rate of diffusion of the solvent and solute atoms would be the same. That this cyclic interchange in lattice positions of solute and solvent atoms in equal numbers is the only true mechanism of diffusion is denied by the evidence presented in this paper. Experimental Procedure This modification of similar procedure1 will be outlined briefly. The method consisted of the following steps: I. A pure Muntz metal (60.6 per cent Cu, 0.1 per cent total impurities) that was almost all beta brass at 780°C. was chosen. 2. The brass was turned between centers in a lathe to a diameter of 0.5965 inches. 3. After the brass was cleaned, it was electroplated with pure copper to a diameter of about one inch. 4. The sample was heated slowly to 400°C. under reduced pressure and held at that temperature for 4 hr. to remove occluded gases. It was then cooled to room temperature. 5. The sample was heated to 780°C. ± 3°C. and held at that temperature for different lengths of time; then quenched. Samples were cut off each time after quenching. Metallographic samples 1/4 in. thick were removed at I hr., 6 hr., 24 hr., 96 hr. and 701 hr. After 96 and 701 hr. samples of about I in. were removed for X-ray analysis. 6. The metallographic samples were polished on the cross section and photomicrographs were taken. 7. The I-in. samples were polished and etched on both ends. With the aid of a microscope each was carefully mounted in a four-jaw chuck in a lathe, so that they could be accurately bored for an arbor. 8. Turnings were taken for each X-ray sample. After each set of turnings, the sample was heated in an oil bath for about 1/2 hr. at 300°C. It was then etched in 25

Jan 1, 1942

By E. O. Kirkendall

The investigation reported herein was undertaken to obtain data to supplement those presented in an earlier paper,l particularly for longer times at a higher temperature. This information may further develop our knowledge of the mechanism of diffusion in substitutional solid solutions. Diffusion of solute atoms interstitially dissolved is not difficult to visualize: it can take place without much disturbance of the solvent atoms. The mechanism of diffusion of solute atoms substitutionally dissolved is not so easily understood. Many theories have been advanced. Rosen-hain,2,3 Frenkel,4 Smekal,5 Langmuir,3,6 Steigman, Shockley and Nix,' and Johnson8 all proposed theories to explain diffusion. Langmuir's proposed mechanism consisted of a simple cyclic interchange of atoms involving an interchange in lattice positions of four or more atoms. This mechanism, accepted by the author at the time of his previous publication,1 and apparently quite generally accepted, required a net exchange in positions of both solute and solvent atoms in equal numbers. In other words, the rate of diffusion of the solvent and solute atoms would be the same. That this cyclic interchange in lattice positions of solute and solvent atoms in equal numbers is the only true mechanism of diffusion is denied by the evidence presented in this paper. Experimental Procedure This modification of similar procedure1 will be outlined briefly. The method consisted of the following steps: I. A pure Muntz metal (60.6 per cent Cu, 0.1 per cent total impurities) that was almost all beta brass at 780°C. was chosen. 2. The brass was turned between centers in a lathe to a diameter of 0.5965 inches. 3. After the brass was cleaned, it was electroplated with pure copper to a diameter of about one inch. 4. The sample was heated slowly to 400°C. under reduced pressure and held at that temperature for 4 hr. to remove occluded gases. It was then cooled to room temperature. 5. The sample was heated to 780°C. ± 3°C. and held at that temperature for different lengths of time; then quenched. Samples were cut off each time after quenching. Metallographic samples 1/4 in. thick were removed at I hr., 6 hr., 24 hr., 96 hr. and 701 hr. After 96 and 701 hr. samples of about I in. were removed for X-ray analysis. 6. The metallographic samples were polished on the cross section and photomicrographs were taken. 7. The I-in. samples were polished and etched on both ends. With the aid of a microscope each was carefully mounted in a four-jaw chuck in a lathe, so that they could be accurately bored for an arbor. 8. Turnings were taken for each X-ray sample. After each set of turnings, the sample was heated in an oil bath for about 1/2 hr. at 300°C. It was then etched in 25

Jan 1, 1942