By L. C. Armstrong

A. E. ROSS*—Mr. Armstrong in his paper stated that they had experienced considerable difficulty in drilling the quartz-feldspar intergrowths. The dia-mor~d loss was excessive and the diamond bits polished quite rapidly. Mr. Davidson, who presented the paper, stated that bortx stones in the range of 20 to 30 per carat had been used in the bits on this job. I would like to suggest the use of bits employing stones in the range of 60 to 100 per carat, an average of possibly 80 per carat. If these stones had been used the bits might have lasted longer and not polished so quickly. As a basis for this suggestion I would like to point out that in northern New York State we had at least two examples where bits employing stones in the range of 80 per carat had solved a difficult problem. Bits set with stones in the range of 20 to 30 per carat had been used previously and had failed. With the finer stones, the cost per foot of drilling decreased material1y. It should also be noted from a technical standpoint that the smaller stones require higher drilling speeds than the larger stones. Greater pressures are not normally necessary, and it is the higher speed which seems to be the major factor of importance. It should also be noted that the finer stones afford a greater number or cutting surfaces for the same carat weight in a bit. Then too, the smaller stones, by virtue of their size, serve as sharper cutting edges than larger stones. There is no doubt that the diamond bit employing smaller stones costs more to set than the bit using larger stones. However, with the technique developed at the shops of Sprague and Henwood, Inc., we feel that the relatively slight additional cost required to set these bits is more than paid for by the resultant lower drilling cost. We feel that the highest quality stone available is the most economical to use when hard fine grained rock is encountered. In summary, I would suggest that it might be possible to solve the problem presented in this paper by using a diamond bit employing stones at least as small as 80 per carat of the highest grade possible and by using the diamond bit at the highest speed available with modern drilling equipment. L. C. ARMSTRONG (author's reply) —It is generally agreed that the use of smaller, high-grade diamonds and of higher drilling speeds, as suggested by Mr. Ross, may be the best approach to the solution of the problem.

Jan 1, 1950

By H. H. Uhlig

Soon after general use of stainless steels began, it was observed in practice that certain combinations of factors tended to induce corrosion by pitting. For most applications this was a serious drawback, not so much because the structural properties of the metal were impaired but because of the rapidity with which heavy sections of the alloys were penetrated by small elongated pits. These pits seemed to initiate readily in oxidizing metal salt solutions like ferric chloride and in chloride solu-tions like sea water. It was observed that in sea water pitting was more frequent in stagnant or polluted waters than in highly aerated, moving waters. The steels in these chloride solutions were observed to be sensi-tive to long contact with material such as sand grains or attached bar-nacles. At points of attachment or contact it was not uncommon to discover initiation of corrosion. Pits once begun at contact faces were observed to grow rapidly, usually elongating phenomenally in the direc-tion of gravity until the metal was perforated. Hydrochloric acid and other nonoxidizing acids, on the other hand, were observed to corrode stainless steels generally; the weight losses often were higher, but the penetration less than for the pitting type of corrosion. The causes of pitting, a type of corrosion recognized as character-istic not only of stainless steels but of many additional metals and alloys, are important in corrosion studies. A possible explanation bears prac-tical significance, for once it is known why pits begin where they do and continue to grow after initiation, intelligent direction can be given to diminishing corrosion. This can be done either by some alteration in the composition and treatment of the alloy or by some alteration in the environment. It appears foremost in importance to discover the nature of pit foci, for if initiation of pits can be discouraged their growth will be no longer a factor to be considered. In a multi-component alloy containing many impurities normal to production of such an alloy, each of which may play a part in pitting, and whose corrosion resistance is sensitive to heat-

Jan 1, 1940

By L. H. de Wald, J. Walter Scott

It is usual practice in the copper industry to use open horizontal molds for casting tough-pitch copper wire bars.' A wire bar cast in this manner is partly characterized by heavy wrinkles and a comparatively deep skin of oxide on the top of the bar, corresponding to the open side of the mold. On the theory that the rough, high-oxide surface might have an adverse effect on the rolling and drawing properties of a wire bar and might account for some of the irregularities of mill behavior, several bars which had been planed to remove the wrinkled surface were processed into wire. These bars responded to mill treatment more satisfactorily than did the regular wire bars. Realizing that machining the surface of one face of each bar would not be commercially feasible, it was decided that casting the metal into a vertical mold and cropping off the pouring end would accomplish approximately the same result. Several wire bars of commercial size (250 Ib.) were so cast and processed into wire for comparative test with bars cast in the usual horizontal molds. It is the purpose of this paper to present the results obtained from this investigation, in which commercial bar sizes and processing technique were used throughout. The results show that in general copper wire bars cast vertically are superior to those cast horizontally. Experimental Procedure A horizontally cast bar and a vertically cast bar were obtained from each of several regular reverberatory furnace heats of copper which had been refined and poled to tough-pitch metal in accordance with usual methods.' Both bars were cast from the same part of the melt and within five minutes of each other, in order to produce as nearly as possible, in each case, wire bars of identical composition.

Jan 1, 1930

By J. E. Hackford

IN SOME research. work carried out by the writer, certain results have bean obtained which bear on the fundamental nature and origin of coal and the relationship between coal and petroleum. Without entering into a discussion of the details of the experiments, which were conducted on petroleum and derived bitumens, there are given here, by way of definition, some of the relations that the writer has established between certain classes of bitumens of petroliferous origin. Bitumen.-A natural organic substance, gaseous, liquid, or solid, consisting of hydrocarbons and the oxy- or thionic derivatives of the same, or of a mixture of all three. Diasphaltenes.-Those portions of bitumens that are soluble, in ether or carbon disulfide, but are insoluble in a mixture of equal parts of ether and alcohol. Diasphaltenes are produced by the oxidation or thionization of petroleum oils; they have, as the name indicates, twice the molecular weight of asphaltenes, into which they are converted when subjected to moderate temperature. For example, an artificially produced diasphaltene, which was readily soluble in pentane and ether, was quite insoluble in either of these solvents after heating for three weeks at a temperature of 100° C., and was converted into an insoluble asphaltene. Asphaltenes.-Those portions of bitumen that are insoluble in ether or ether alcohol but are soluble in carbon disulfide. Asphaltites.-Those solid or semisolid natural bitumens that are composed, for the most part, of asphaltenes or diasphaltenes. A pure asphaltite1 would be composed wholly of asphaltenes and diasphaltenes, but most asphaltites contain small percentages of oil and wax, which have not yet been converted into asphaltenes; they may also contain a small percentage of kerotenes, which represent the next stage of the metamorphosis of asphaltenes. Among the naturally., occurring oxyasphaltites may be mentioned grahamite; and among the thioasphaltites, gilsonite.

Jan 8, 1920

By AIME

Annual production of more than 4,000,000 tons of 0.74 percent copper ore and coincident handling of over 5,000,000 tons of waste at the open-pit mine of Castle Dome Copper Co. near Miami, Ariz. takes a lot of power. Manufacturers have ever co-operated with mining companies in providing the required equipment to suit the problem. Power equipment suppliers have done much to make possible the economic and profitable production of copper from low-grade ores. In the future, as mining operations will necessarily handle even lower-grade ores, the ability of the manufacturer to supply the power and mechanical equipment to produce more metal at a fair and reasonable price will be the good right arm of the miner. About 27,000 tons of concentrate is produced from the 4,000,000 tons of ore.

Jan 1, 1948

By David W. Mitchell

WHILE pure magnesium does not corrode rapidly the presence of even very small quantities of certain other metals accelerates corrosion remarkably. Because magnesium is such an electropositive metal (E° = +2.34 volts)' the presence of substances that permit galvanic activity is extremely undesirable. It is stated that as little as 0.017 pct of iron in magnesium causes a marked increase in the corrosion rate.2 Magnesium and its alloys are commonly melted in iron or steel pots; consequently the commercial metal has the opportunity to pick up iron if it has that tendency. Quantitative data on the solubility of iron in magnesium are of practical as well as of academic interest. Some magnesium alloy castings tend to have large grain size unless suitable treatment is given to the liquid metal just prior to casting. One method of grain refinement consists of "superheating" the metal just prior to casting. "Superheating" is heating to a temperature 100 to 200°C above the casting temperature and holding for a short period of time. Superheated metal has a much finer grain than unsuperheated metal. A satisfactory explanation of this phenomenon has not been forthcoming. One hypothesis attributes the grain refinement in the superheated metal to precipitation of some phase that is miscible at the temperature of superheat but not miscible just below the casting temperature and which is thought to provide nucleating centers for crystallization. This phase, if the foregoing hypothesis is correct, would probably be a metal or an intermetallic compound. Of the metals likely to be found in magnesium alloys, iron is one of the most likely candidates for the role of grain refiner for iron occurs in small quantities in all commercial magnesium and magnesium alloys. A. Beck' states that magnesium, in either the liquid or the solid state, cannot dissolve iron and that iron exists as a finely divided suspension which does not settle out because of its extreme fineness. Beck also presents a micrograph showing a large iron dendrite in magnesium but does not comment on the crystallization of iron from a solution supposed to contain none. It is doubtful that dendrite formation from suspended iron would be possible. This suspension theory is the basis of patents4 covering the removal of iron from magnesium by allowing the iron particles to act as nuclei for the formation of primary magnesium crystals which can be separated by segregation. Also covered by patents is the removal of iron by the addition of another metal to form an intermetallic compound with the iron which, because of its increased particle size, is able to settle out of the molten metal. Here, too, quantitative information on the extent of iron solubility in liquid magnesium is of more than theoretical interest. M. Hansen,5 in his critical collection of the data on binary alloys, states that iron is not soluble in liquid magnesium. W. R. D. Jones6 who studied the physical properties of low iron magnesium alloys observed a

Jan 1, 1948

By D. T. Peters

To better understand the Co-Mo interaction in maraging steels, the precipitate reversion behavior of two alloys closely related to the 18 Ni-250 grade has been studied. The reversion experiment is carried out by aging at a low temperature, T1 (preaging temperature), for some period of time and then aging at a higher temperature, T2, called the reversion tetnperature. Aging and reversion tmzperatures used were in the range 679 to 1050°F. Reversion is marked by an increase in resistivity and a decrease in hardness. It teas found that some reversion took place at all cornbinations of T1 and T2 but that pronounced rei3ersion resulfed for an Fe-18 pct Ni-5 pct Mo-8 pcl Co alloy exposed to preagz'ng' temperatures at or below 850°F. A similar alloy not containing cobalt exhibited no such discontinuity in reversion behazior with TI. The results are interpreted in terms of two types of molybdenum-rich precipitates, one nucleated at dislocations and the other in the matrix. The increased supersaturation resulting from the presence oj- cobalt evidently provides sufficient energy to nucleate the matrix phase. Anotnalies in the temperature dependence of the resistivity decrease and peak hurdness in the Fe-18 pct Ni-5 pct Mo-8 pct Co alloy as a junction of aging temperature noted in an earlier study are explained on this basis. SEVERAL investigatorsl-9 have studied the details of the precipitation-hardening reaction of the maraging steels. The great majority of conclusions have been drawn from transmission electron microscopy. Although much has been learned by this method, alternate techniques which will give information earlier in the aging process are needed for a more complete understanding of the series of precipitation steps probably involved in the aging reaction. Peters and cupp'' have recently shown, by measurements of the kinetics of precipitation, that an 18 pct Ni-Co-Mo maraging steel shows a distinct change in precipitation behavior at aging temperatures below 850°F. The results were interpreted in terms of the existence of two types of precipitates at low aging temperatures. Only one precipitate type is present at higher aging temperatures. The low-temperature precipitate was found to be a particularly effective strengthener. No evidence for the additional low-temperature precipitate was found in the 18 pct Ni-5 pct Mo ternary alloy. The object of this investigation was to study further the characteristics of the two types of precipitates and the interaction between cobalt and molybdenum characterizing this system. Some preliminary experiments indicated a difference in reversion behavior in specimens aged above and below 850°F. This suggested that knowledge of the reversion behavior might shed some light on these two questions. Hardy and Heal11 have defined reversion as the loss of hardness, electrical conductivity, or other properties caused by heating for a very short time at temperatures above the aging temperature. The precipitate reversion referred to in this paper is entirely distinct from "austenite reversion" often referred to in maraging steel literature. This latter phenomenon could more accurately be called the diffusion-controlled formation of austenite. Much has been written about reversion in several of the aluminum-base binary and ternary alloys.'2-16 Two explanations for reversion have been advanced. Based on the classical nucleation theory of Volmer-Weber-Becker-Doring,17 Konobeevski18 suggested that reversion was due to the size of the precipitate particles

Jan 1, 1968

By Geo. H. Ashley

The following paper is intended to be suggestive only, and to open the way for discussion and further observation. Its preparation was requested only two days before the time limit set for the submission of the papers comprising this symposium. Thus no time existed for detailed studies, so it is largely a memorandum of such facts as have come incidentally to the notice of the writer in the study of coal in the field. The field study of sulfur in coal has received very little special attention or description from coal student's. The presence of sulfur concretions is noted in hundreds of descriptions, and certain benches of a coal bed may be described as "sulfury" or the presence and position of sulfur bands may be noted in coal sections in connection with sampling. It may be accepted that some sulfur is present in all coal. The amount varies greatly in different regions, in different beds, and in the same bed in different areas. The anthracite of Rhode Island comes the nearest of any coal known to the writer of being free from sulfur, several analyses of that coal showing less than 0.1 per cent. Subbitumi-nous coals in Colorado in a few places have close to 0.2 per cent. of sulfur on the dry-coal basis and in other states subbituminous coals approach this lower limit. Bituminous coals seldom run under 0.4 per cent. of sulfur on the dry basis, though in a few places dry bituminous coals in Colorado and Washington have between 0.3 and 0.4 per cent. The better known bituminous coals have almost everywhere over 0.4 per cent. The best of the Pocahontas and New River coals run close to 0.4 per cent., but there is very little commercial coal in Pennsylvania, Ohio, Indiana, Illinois, Kentucky, or the other states, that runs under 0.5 per cent. on the dry basis. From these minimum figures, the amount will range up to 5 or 6 per cent. or higher if visible sulfur is not excluded. It must be remembered that the usual analysis of a coal bed is not intended to give the total proportion of sulfur in the bed but the amount in the coal after the removal of the more obvious and larger sulfur masses. Professor Parr has already pointed out that, chemically, sulfur occurs in several forms: as pyrite, organic sulfur, sulfates, and possibly as un-combined sulfur. Sulfur in the form of sulfates is commonly the obvious result of the weathering of pyrite and may be found in the coal within .

Jan 1, 1920

Volumes 57 and 58 of the Transactions were mailed together during the third week of August to all members whose dues for 1918 had been paid on Aug. 1. Any member whose copies fail to reach him within a reasonable time is requested to notify the Secretary. Volume 59 is on the press, and will be ready for distribution early in October.

Jan 9, 1918

By E. B. Branson

Introduction to Geology, by E. B. Branson, W. A. Tarr, and W. D. Keller, revised-by Carl C. Branson. McGraw-Hill, 1952. $5.50.-Dealing with physical and historical geology, the book has been revised from an earlier edition. An attempt has been made to eliminate unnecessary detail in discussing processes and history. Revisions bring technical and statistical data up-to-date, and follow suggestions by teachers who used earlier editions. The book carries an eye witness account of the severe earthquake in Assam, India, in 1950 and the story of Paricutin and other major examples of volcanism. Charts summarize chemical weathering, and the results of metamorphisms. The book also contains many new illustrations, including aerial photographs. A History of Phelps Dodge 1834-1950, by Robert Glass Cleland. Alfred A. Knopf, 1952. $4.00.-The book traces the growth of Phelps Dodge from the day Anson Greene Phelps opened a small saddle shop in Hartford, Conn., to the present day. As the country grew, so did Phelps Dodge. The company took part in large affairs from its very beginning. It bought and sold, exported and imported, built factories and railroads, and widened its scope of operations economically and geographically. Entrance of Phelps Dodge into copper mining and the gradual giving up of other interests in favor of the new venture is traced.

Jan 1, 1952

By Mark J. Klein, A. H. Clauer

The Snoek peak induced by solute nitrogen in chromium was studied. A rapid quenching rate is required to maintain nitvogen in solution in sufficient concentrations to be detectable by internal-friction techniques. An expression for the tertninal solubility, c, of nitrogen in weight pevcent is log,,c = -4130/T + 1.05. The diffusion of nitrogen in zhromium determined by internal friction is SNOEK&apos;S theory1 of the stress-induced ordering of interstitial solute elements in the bcc lattice has been used to deduce information on the behavior of interstitials in a number of bcc metals. Under the proper conditions, internal-friction studies of "Snoek peaks" permit a determination of diffu-sivities, solubilities, and precipitation kinetics of interstitial elements. Internal-friction studies of this type have been reviewed by Nowick,&apos; Wert,= Powers and Doyle,4 and others. The behavior of interstitial atoms in Group V-A metals and iron has been rather extensively studied in this way, and results are reasonably self-consistent. However, the study of interstitial elements using internal friction in the Group VI-A metals—tungsten, molybdenum, and chromium—is much less clear. Thus far, internal-friction studies have revealed a peak in tungsten tentatively attributed to carbon5 and a peak in chromium associated with nitrogen. In chromium, Bungardt and Preisendanz6 observed a peak at 180°C for a frequency of -1 cps which they associated with nitrogen. More recently, de Morton7 determined the diffusivity of nitrogen in chromium from studies of a nitrogen peak at 160°c for a frequency of -1 cps and from elastic aftereffect measurements. The objective of this investigation was to study the nitrogen peak in greater detail, to obtain information on the behavior of nitrogen in chromium. This information is of interest because nitrogen is known to have an embrittling effect on chromium. However, efforts to deduce the role played by nitrogen in influencing the mechanical behavior of chromium are handicapped by lack of information on its behavior and distribution in chromium. EXPERIMENTAL PROCEDURES The chromium wires used in these studies were drawn from arc-melted iodide-chromium stock that had been extruded, swaged, and centerless-ground to 0.25 in.-diameter rods. Internal-friction measurements were made in an evacuated torsional pendulum similar to the one described by Kê,8 utilizing wires 0.048 to 0.030 in. in diameter. A series of analyses of the fabricated wires showed that the major impurities were approximately 100 ppm Fe and a combined interstitial content of 50 to 100 ppm C, O, N, and H. A typical interstitial analysis of the wires after processing is 15 ppm C, 2 ppm H, 50 ppm O, and < 5 ppm N. Interstitial concentrations were determined by vacuum-fusion, combustion-conductimetric, and micro-Kjeldahl analyses. In general, vacuum-fusion analysis yielded a lower nitrogen concentration than did micro-Kjeldahl analysis. For consistency, the nitrogen concentrations reported in this investigation were determined by the former method. Heat treatments were carried out by encapsulating the specimens in quartz tubes containing argon. The fabricated wires were annealed at 1150°C for 1 hr to produce uniform recrystallized grain size of about 0.015 mm. Nitrogen and carbon were added to the fabricated wires by encapsulating them in a quartz tube containing ammonia or methane, and annealing them at 1150°C for 48 hr. In some instances, carbon was also introduced by coating the wires with carbon black prior to annealing.

Jan 1, 1965

By J. E. Metcalfe

Proceedings of the Fourth Empire Mining and Metallurgical Congress, Great Britain 1949. Part II published at the Offices of the Congress in London, England, 1139 pp. The price of these proceedings is £ 2. The parts may be purchased separately at a cost of £ 1 each.-Part I of this book covers a report of the organizing committee, the inaugural meeting and presidential address, banquet at Guildhall, welcome by Sir Richard Livingstone at Oxford. and final session. Technical session and papers are also covered in Part I. Part II covers such topics as coal, present-day trends in mineral dressing and metallurgy. Mining Engineer&apos;s Survey Manual. By J. E. Metcalfe. Published for "Mine & Quarry Engineering" by Electrical Press, London, 1951. 341 pp., illus., charts, diagrs., tables, 8 ¾ x 5 1/ in., cloth, 30s., available from Percival Marshall & Co., Ltd., London, and British Book Centre, 122 East 55th St., New York 22, N. Y. Beginning with a brief treatment of surveying fundamentals and a discussion of the correlation of surface and underground surveys, this practical manual continues with descriptions of surveying practice both above and below ground including stopes, inclined shafts; etc. Space is devoted to sampling and valuation, geological considerations, and descriptions of modern surveying instruments. The organization of survey operations is covered in the last chapter.

Jan 1, 1952

By P. M. Aziz, I. Markson, C. S. Barrett

The abnormal after-effect in twisted wires that occurs when untwisting is interrupted by etching con be brought under control and used to study the mechanical properties of thin surface films and how they are effected by reagents and heat treatment. Results are given of studies of oxide films on high purity aluminum. IF a wire is subjected to plastic deformation by torsion and then released, it untwists in the normal after-effect, but under certain circumstances the untwisting is abruptly lessened or reversed by the application of an etchant to the wire.1,2 This abnormal after-effect may occur, for example, if there is a coherent oxide film on the surface of the wire which is removed by the etchant. Following a suggestion of A. H. Cottrell that predicted this effect, it is attributed to dislocations that had piled up beneath the oxide layer and represents the rapid release of residual stresses caused by these dislocations. When the layer is removed, the stress relief may be by escape of piled-up dislocations from the metal, or by an activation of latent sources of dislocations located at the surface, together with rebalancing of elastic stresses to compensate for the loss of stressed material, as in a residual stress analysis determination, these mechanisms acting singly or in combination.&apos; The slower the attack of the reagent, the more gradual is the stress relief and the smaller the change in strain rate when the reagent is applied. A study has been made of the factors that influence the magnitude of the normal and abnormal after-effects with the object of developing techniques suitable for a quantitative investigation of the influence of various surface films on dislocations in wires, and of the rate and extent of the attack on the films by different reagents. It was found that reasonable sensitivity and reproducibility could be achieved if a suitable choice of variables was made and if these variables were held constant through a series of experiments. The method was then applied to a study of oxide films produced and treated in different ways on the surface of high purity aluminum wires, and to a study of the damage to these films caused by various reagents. Experimental Procedure The material used throughout this work was prepared from 99.9968 pct Al. This high purity aluminum was melted, cast into 1/2 in. diameter ingots, and then swaged and drawn without intermediate annealing to 0.040 in. diameter wire. A sketch of the apparatus employed for twisting is shown in Fig. 1. The test wires were mounted into the apparatus by cementing one end of the wire to the beaker and the other to the tube with laboratory wax of high melting point. The length of the wire between the waxed joints was 4.2 & 0.2 cm. Extreme care was taken during mounting to avoid cold-working the wire. The wire was twisted through 335" in 2 to 4 sec by rotating the pinion on the gear box until the vertical post on the rotating table, which was initially touching the horizontal stop, was arrested by the stop. All the tests were conducted with apparatus and reagents at the same temperature (about 25°C). In all tests, except those where the duration of the initial torque was investigated, the torque was applied for a period of 2 min. At the end of this time the table was rotated back a few degrees away from contact with the stop and the wire allowed to untwist. The after-effects were measured by reflecting a beam of light from the mirror shown on the apparatus. After the wire had untwisted for 6 min, a reagent was carefully poured into the beaker and thereby applied to the surface of the wire.. In some tests the liquid in the beaker was removed after a few minutes and replaced by an-

Jan 1, 1954

By Ramesh Malhotra, Hubert E. (Deceased) Risser

THE WORLD Coal, as a source of energy and as a source of coke for the smelting of iron ore, has contributed significantly to the development of every major industrial nation of the world A number of other materials-oil, natural gas, wood, waste materials, water, and, in some applications, nuclear materials -can be used satisfactorily for the generation of heat and energy, but no generally acceptable and economic substitute has been found to supplant coke in iron ore smelting in conventional blast furnaces. In the development of many nations, coal provided the initial source of energy for industrialization Although coal provided more than 60% of the world&apos;s energy each year between 1902 and 1929, oil and natural gas have surpassed it as a source of energy in more recent years (Ref. 38, pp. 439, 441). Despite the rapid rise in importance of other fuels, a considerable amount of the total energy consumed is still supplied by coal. In 1972, coal supplied 32.1 % of the total world energy (Ref. 49, pp. 2-3). To produce this energy, 2.4 billion metric tons of coal were consumed-a 16.0% increase over the amount consumed in 1962. A further worldwide increase in the amount of coal used to supply energy is projected. According to Dr. Karlheinz Bund (Ref. 37, p 145), by the year 2000 world coal consumption could amount to 5 billion mt. Coal Resources and Production The world&apos;s coal resources are estimated to be about 10,872 billion mt. Of this amount, 1,297 billion mt are classified as measured reserves (Ref. 50, p. 57). In Table 13.A.1 the estimates of measured reserves and total resources, recent production, and the ratio of measured reserves to production of major coal-producing countries are shown. About 90% of the world&apos;s total coal resources are estimated to be in the USSR, the United States, and China. The United States ranks second in the world in coal resources, but in measured reserves, it ranks first. Because of the difference in rate at which available coal resources are being exploited, the ratio of measured reserves to actual production varies widely among areas and countries. France and East Germany have the lowest reserve to production ratios, 49.5 and 60.1, respectively. In Mexico, where currently less than 5 million mtpy of coal are produced, the ratio is 1257 For all countries producing more than 200 million mtpy of coal (except East Germany), the ratio ranges from 350 to 670. For the United States, the ratio is 669.7. In Table 13.A.2, distribution of the world&apos;s coal resources by area is shown. More than 97% of the total resources lie in the northern hemisphere, with Asia, including European USSR, having 63.4%. Only 1.9% of the total coal resources are estimat-

Jan 1, 1976

By D. W. Mitchell

While pure magnesium does not corrode rapidly the presence of even very small quantities of certain other metals accelerates corrosion remarkably. Because magnesium is such an electropositive metal (E° = +2.34 volts)&apos; the presence of substances that permit galvanic activity is extremely undesirable. It is stated that as little as 0.017 pct of iron in magnesium causes a marked increase in the corrosion rate.2 Magnesium and its alloys are commonly melted in iron or steel pots; consequently the commercial metal has the opportunity to pick up iron if it has that tendency. Quantitative data on the solubility of iron in magnesium are of practical as well as of academic interest. Some magnesium alloy castings tend to have large grain size unless suitable treatment is given to the liquid metal just prior to casting. One method of grain refinement consists of "superheating" the metal just prior to casting. "Superhcating" is heating to a temperature 100 to 200°C above the casting temperature and holding for a short period of time. Superheated metal has a much finer grain than unsuperheated metal. A satisfactory explanation of this phenomenon has not been forthcoming. One hypothesis attributes the grain refinement in the superheated metal to precipitation of some phase that is mis-cible at the temperature of superheat but not miscible just below the casting temperature and which is thought to provide nucleating centers for crystallization. This phase, if the foregoing hypothesis is correct, would probably be a metal or an intermetal-lic compound. Of the metals likely to be found in magnesium alloys, iron is one of the most likely candidates for the role of grain refiner for iron occurs in small quantities in all commercial magnesium and magnesium alloys. A. Beck³ states that magnesium, in either the liquid or the solid state, cannot dissolve iron and that iron exists as a finely divided suspension which does not settle out because of its extreme fineness. Beck also presents a micrograph showing a large iron dendrite in magnesium but does not comment on the crystallization of iron from a solution supposed to contain none. It is doubtful that dendrite formation from suspended iron -would be possible. This suspension theory is the basis of patents4 covering the removal of iron from magnesium by allowing the iron particles to act as nuclei for the formation of primary magnesium crystals which can be separated by segregation. Also covered by patents is the removal of iron by the addition of another metal to form an intermetallic compound with the iron which, because of its increased particle size, is able to settle out of the molten metal. Here, too, quantitative information on the extent of iron solubility in liquid magnesium is of more than theoretical interest. M. Hansen,5 in his critical collection of the data on binary alloys, states that iron is not soluble in liquid magnesium. W. R. D. Jones% ho studied the physical properties of low iron magnesium alloys observed a 57°

Jan 1, 1949

By H. A. Hoffman

Competition from an all-flotation plant, with demonstrated economies and efficiencies, plus a change in smelting contract and introduction of improved cyclones lead to conversion from gravity-flotation. Detailed descriptions are given of equipment installed and procedures used at St. Joseph Lead&apos;s Federal mill. Future plans include further quality control by instrumentation in all aspects of the mill operation. Also planned are improvements in materials handling systems. Competitive conditions will continue to dictate improvements and changes in the mill flowsheet. The advent of all-flotation mills in the Lead Belt was introduced by the Indian Creek mill in late 1953. This modern and efficient plant then became a pattern for the other mills in this area to re-evaluate their circuits in an effort to develop flowsheets that would improve operating conditions and metallurgy. The Indian Creek mill demonstrated that all-flotation would require considerably less operating and maintenance labor than the combination of tabling and flotation that was common in the Lead Belt at that time. Two significant changes occurred in recent years to allow all-flotation to be seriously considered in other Lead Belt mills. One was a change in the smelting contract which did not require gravity concentrate. Another was the development of cyclones which provided classification of the flotation feed in a very small space. Since the Federal mill was the largest concentrating plant in the Lead Belt it was felt that the greatest savings could be made by investigating the all-flotation possibilities at this mill. Interest was stimulated by the milling and ore dressing Depts. to determine if this mill would be converted without undue cost, provided the metallurgy could be improved. Accordingly, laboratory tests were initiated to learn what metallurgical benefit could be derived. Numerous tests were run which indicated that grinding to all-flotation would improve the tailing by as much as 0.02 pct Pb. This was quite significant when multiplied by the tonnage of ore treated. Projecting the added cost of power for extra grinding and flotation, and the additional flotation reagents required, plus additional new equipment that would have to be purchased, it would still add up to a considerable saving. The all-flotation mill would reduce man power by some 30 pct, and make a metallurgical improvement. Operating costs could be reduced bv 2$ per ton. The metallurgical improvement would amount to 4$ per ton, for a total of 6$ per ton of ore milled. An estimate of the cost of the conversion was set at $250,000. With the savings as estimated this could be paid off in about two years. On paper it therefore seemed attractive enough to justify a mill test. MILL TESTING One section of the Federal mill was made available for use as a separate test circuit. Cyclones and density controllers were borrowed from the Viburnum and Indian Creek mills. Denver flotation cells were obtained from the Desloge mill that was then shut down. Two 10-cell groups of Fagergren flotation machines, consisting of eight roughers and two cleaners in each bank, were segregated from the remainder of the plant. The 9x12-ft rod mill was continued as a primary grinding mill. The two 6%x12-ft mills on this section were converted from rods to balls, and the speed increased to 22.0 rpm. Cyclones were installed to close the circuit of these ball mills. The ground pulp from each of the ball mills was fed separately to its own bank of flotation cells so that two completely separated test circuits could be run in parallel. This test circuit operated on a three-shift basis from Dec. 22, 1959 to Mar. 21, 1960. The first few weeks were occupied in developing conditions for proper metallurgy and trouble-free operations. Results were rather erratic but as the ore dressing laboratory and the mill operators became more familiar with conditions they were able to obtain expected results, which could be duplicated day after day. The last five weeks of testing indicated the best results and are tabulated in Table I. During the first two weeks a Denver unit cell was used on No. 1 flotation circuit. Even though it recovered almost one half of

Jan 1, 1962

By J. E. Hackford

In some research work carried out by the writer, certain results have been obtained which bear on the fundamental nature and origin of coal and the relationship between coal and petroleum. Without entering into a discussion of the details of the experiments, which were conducted on petroleum and derived bitumens, there are given here, by way of definition, some of the relations that the writer has established between certain classes of bitumens of petroliferous origin. Bitumen.—-A natural organic substance, gaseous, liquid, or solid, consisting of hydrocarbons and the oxy-or thionic derivatives of the same, or of a mixture of all three. Diaspha1tenes.—-Those portions of bitumens that are soluble in ether or carbon disulfide, but are insoluble in a mixture of equal parts of ether and alcohol. Diasphaltenes are produced by the oxidation or thionization of petroleum oils; they have, as the name indicates, twice the molecular weight of asphaltenes, into which they are converted when subjected to moderate temperature. For example, an artificially produced diasphaltene, which was readily soluble in pentane and ether, was quite insoluble in either of these solvents after heating for three weeks at a temperature of 100" C., and was converted into an insoluble asphaltene. Aspha1tenes.—Those portions of bitumen that are insoluble in ether or ether alcohol but are soluble in carbon disulfide. Aspha1tites.—Those solid or semisolid natural bitumens that are composed, for the most part, of asphaltenes or diasphaltenes. A pure asphaltitel would be composed wholly of asphaltenes and diasphaltenes, but most asphaltites contain small percentages of oil and wax, which have not yet been converted into asphaltenes; they may also contain A small percent.age of kerotenes, which represent the next stage of the metamorphosis of asphaltenes. Among the naturally occurring oxyasphaltites may be mentioned grahamite; and among the thioasphaltites, gilsonite.

Jan 1, 1921

By H. T. Sumsion, A. U. Seybolt

The results of an investigation of vanadium-rich V-O solid solutions are presented, indicating the structure and lattice parameters of two solutions, a and ß, and their approximate temperature-composition existence. The a solution is the terminal body-centered cubic one, and contains up to 3.2 atomic pct 0. The ß solution has an ordered body-centered tetragonal structure, is formed at 1270°C, and exists from about 15 to 22 atomic pct 0. From the evidence available, the various phase boundaries have no appreciable temperature dependence. Evidence has been found for a polymorphic transformation in pure vanadium at 1550°C. IN an earlier investigation&apos; dealing with the preparation of pure vanadium by calcium reduction of the oxide, it was found that small amounts of oxygen drastically reduced the ductility of the metal. Because this effect was so marked, it was decided to make a study of the solubility of oxygen in solid vanadium. This report deals principally with this solubility and the nature of the phase relationships in the vanadium-rich region, particularly at temperatures below 1300 °C. However, during the investigation enough data on the V-0 system were obtained to make it appear worthwhile to present a tentative phase diagram up to the composition VO. The only significant prior work found on this system are the contributions of Klemm and Grimm,&apos; and Mathewson et al.3 Klemm and Grimm prepared a wide range of V-O compositions by powder techniques including the compositions VO.l, VO.2, VO.3 and VO4 (9.1, 16.8, 23, and 28.6 atomic pct 0, respectively). The first three compositions were found to consist of a body-centered tetragonal solid solution, while the last also showed lines of VO (NaCl structure). They found that the parameter c, increased and the parameter a, decreased with increasing concentration of oxygen. For their composition VO.27, or about 16.8 atomic pct O, they cite the values a, = 2.948A, c, = 3.53A, and c/a = 1.2. Klemm and Grimm made no attempt to determine the solid solubility limit nor to construct a phase diagram. They did, however, give some data on the homogeneity range of VO, and they proposed a structure for the body-centered tetragonal solid solution; these points will be taken up later. Materials and Preparation of Samples The vanadium used in this investigation was prepared in the laboratory by the method previously mentioned.&apos; A typical analysis is as follows: Fe, 0.007 pct; Si, 0.02; Ca, 0.06; C, 0.224; O2, 0.044; N,, 0.0017; H2, 0.003; and V, 99.34 ±0.3 (assay). The vanadium assay is probably low by about the error given. The impurities total about 0.36 which, if subtracted from 100, gives a purity of about 99.6. At the time material was being prepared for this work no suitable technique was available for melting vanadium without appreciable contamination. The procedure adopted therefore was to cut the calcium-reduced regulii into slices which were then rolled to strip about 0.025 in. thick for oxygen diffusion. Pieces of rolled vanadium of approximately 0.025xY4xl in. and weighing about 0.3 g were suspended in a vertical fused-silica tube which was part of an ordinary gas absorption apparatus. The silica tube was heated by an electric resistance-tube furnace which could be raised around the silica tube or lowered away from it as desired. This apparatus had no novel features which require detailed description. Other than the silica tube and furnace, it consisted of a glass system evacuated by a liquid nitrogen trapped mercury diffusion pump, a mercury-operated gas burette, a McLeod and a Pirani gage, and a mercury manometer. It was also equipped with suitably located stopcocks for isolating various parts of the system; the vacuum ordinarily attained was between 10" and 10-6 mm of mercury. Oxygen generated by decomposing MnO2 was passed through anhydrous magnesium perchlo-rate before introducing it into the gas burette and thence to the absorption chamber.

Jan 1, 1954

By M. L. Samuels

In a recent paper the authors1 discussed the reactions to tempering of hypereutectoid steels quenched from 1000&apos; C., as revealed by studies on changes in hardness, electrical resistivity, coercive force and metallo-graphic charaeteristics. The data, which related specifically to tempering temperatures of 550°, 650" and 710" C., for varying periods up to 125 hr., permitted the following important conclusions: 1. The rate of softening of the steels at the temperatures examined differed markedly although the steels were of "similar" general chemical composition. 2. The temperature of maximum softening spread over a range from about 650" C, to the eutectoid inversion. 3. The divergence in behavior was ascribed, at least in part, to a profound difference in tendency to graphitization on annealing at sub-eutectoid temperatures. 4. The mode of spheroidization of the cementite, as revealed by metallographic studies, also varied considerably in the different steels. The purpose of the present investigation is to pursue further the study of the difference in behavior of the steels on tempering over a wider range of temperature. To this end the following features have received particular attention: 1. Comparison of temperatures of maximum softening of the various steels when the quenched samples were tempered for 5 hi. and for 75 hr. followed by furnace cooling and by quenching in water. 2. Deterrnirlation of the effect of quenching temperature, prior to tempering, on the rate of softening. Quenching temperatures of 1000" and 850" C. were used in the investigations. 3. Examination of the microstructures obtained with the various heat-treatments employed.

Jan 1, 1938

By M. L. Samuels

In a recent paper the authors1 discussed the reactions to tempering of hypereutectoid steels quenched from 1000&apos; C., as revealed by studies on changes in hardness, electrical resistivity, coercive force and metallo-graphic charaeteristics. The data, which related specifically to tempering temperatures of 550°, 650" and 710" C., for varying periods up to 125 hr., permitted the following important conclusions: 1. The rate of softening of the steels at the temperatures examined differed markedly although the steels were of "similar" general chemical composition. 2. The temperature of maximum softening spread over a range from about 650" C, to the eutectoid inversion. 3. The divergence in behavior was ascribed, at least in part, to a profound difference in tendency to graphitization on annealing at sub-eutectoid temperatures. 4. The mode of spheroidization of the cementite, as revealed by metallographic studies, also varied considerably in the different steels. The purpose of the present investigation is to pursue further the study of the difference in behavior of the steels on tempering over a wider range of temperature. To this end the following features have received particular attention: 1. Comparison of temperatures of maximum softening of the various steels when the quenched samples were tempered for 5 hi. and for 75 hr. followed by furnace cooling and by quenching in water. 2. Deterrnirlation of the effect of quenching temperature, prior to tempering, on the rate of softening. Quenching temperatures of 1000" and 850" C. were used in the investigations. 3. Examination of the microstructures obtained with the various heat-treatments employed.

Jan 1, 1938