By Joseph Fry, Ralph H. Espach

In the spring of 1943, when it was evident that the Tensleep bandstone in the Elk Basin Field, Wyoming and Montana, held a large reserve of petroleum, Bureau of Mines engineers obtained samples of oil from the bottom of nine wells and analyzed them for such physical characteristics as the volumes. of gas in solution. saturation pressures or bubble points, shrinkage in volume caused by the release of gas from solution, expansion of the oil with decrease in pressure, and other related properties. The composition of the gas in solution in the oil was studied. The pressures and temperatures existing in the reservoir and the productivity characteristics of the oil wells were determined. The data obtained indicate that the oil in the Tensleep Reservoir of the Elk Basin Field has unusually varying physiral characteristics, such as a saturation pressure of 1,250 psia and 490 cu ft of gas in solultion in a barrel of oil at the crest of the structure and a saturation pressure of 530 psia and 134 cu ft of gas in solution in a barrel of oil low on the flanks. The hydrogen sulfide content of the gas in solution in the oil varies from 18 per cent for oil on the crest to 5 per cent for oil low on the flanks of the structure. Of even greater significance is the fact that these and other variable characteristics of the reservoir oil are related to the position of the oil in the structure. Many geologists and petroleum engineers have considered that all the oil in a petroleum reservoir has rather uniform physical characteristics and that equilibrium conditions prevailed in all underground accumulations of oil and gas; that such is not always so is borne out by the results of the study by the writers. INTRODUCTION The Rocky Mountain region is one in which may be found striking examples of the unusual in oil and gas accumulations, as is evident from the following: The high helium content (7.6 per cent) of the gas in the Ouray-Leadville limestone sequence in the Rattlesnake Field, New Mexico, and gases of similar helium content in other fields; 50" to 55' API gravity distillate in solution in carbon dioxide gas and recoverable through retrograde condensation, in the North McCallum Field, Colorado; the occurrence of gas, oil, or both in closely related structures contrary to the usual concepts of gravimetric segregation: the accumulation of gas and/or oil in structures closely related to other structures that apparently are more favorable but do not contain oil or gas accumulations; the high hydrogen sulfide content (as high as 42 per cent) of the gas associated with oil in some fields in the Big Horn Basin, Wyoming; and the wide range of fluid chararteristics found in the Elk Basin reservoir. Elk Basin, an interesting old oil field that has been producing oil from the Frontier formation since 1915, is situated in a highly eroded basin resulting from the erosion of the crest of an anticline and some of the underlying softer shales. The field came back into national prominence during 1943 when it became known that it was the largest single reserve of new oil discovered in the United States that year. The Tensleep sandstone was found to contain oil in November. 1942, when a well drilled to a depth of 4,538 ft (44 ft into the Tensleep sandstone) flowed oil at the rate of 2,500 B/D. By the end of 1949, 137 oil-producing wells and five dry holes had been drilled, and approximately 32 million bbl of oil had been produced. Approximately 6,000 acres may be considered productive of oil in the Tensleep Reservoir, and estimates of the oil that will be produced average 200 million bbl. The Tensleep Reservoir has further interest because it ha-greater closure than any oil field in the Rocky Mountain region; the closure of the Elk Basin anticline is variously estimated at 5.000 to 10,000 ft. of which the top 2.00 ft of the structure contained oil. SUBSURFACE OIL SAMPLING Fig. 1 is a structural map of the Elk Basin Tensleep Reservoir, on which the nine wells used in this study and the numbers correvponding to the well designations hereafter referred to are shown. Wells 1. 2, 3, 4, and 8 were tested and sampled during October and November. 1943. and Wells 5, 6. 7, and 9 during June and July, 1944. An electromagnetic type sampler developed by the Bureau of Mines and described by Grandone and Cook' was used in obtaining the subsurface oil samples. As the wells were tubed nearly to bottom, the sampler was run as far as possible in the tubing hut never below the top perforations. The following procedure was used in testing and sampling the wells: A well was shut in for at least three days, after

Jan 1, 1951

By Zárate G. E.

Practical and statistical considerations concerned with the sampling, sample preparation and chemical analysis of precious metal ores are reviewed. The principal requirements related with the characteristics of sample cutter, sample preparation, equipment and methods are discussed. The main errors introduced in the different stages of the sampling systems are defined. The application of statistical techniques to evaluate these errors to determine the ore grade variation and to design the number of increments needed to get an accurate assay are presented. Finally, results obtained with the application of this method to gold and silver ores are analyzed and some recommendations are given.

Jan 1, 1984

By S. Leber

Pole figures and pole distributions were used for the quantitative detevinination of the preferred orientations in swaged tungsten rods and the effect of subsequent wire drawing on the texture. In the swaged rod, the preferred orientation could best be described as a pseudo (111-112) [110] cylindrical texture. A secondary component was assigned the indices (110) [001]. Further reduction by swaging retained these cylindrical textures. Wire drawing caused lattice rotations about the wire axis, converting the cylindrical texture into a normal fiber texture. The conversion was initiated and proceeded lnost rapidly in the center of the wire. The (110) /001] component was converted into a (110) fiber texture by wire drawing. The effective rotations were about axes contained in the lransverse plane. The preferred orientation associated with tungsten wire usually has been assumed to consist of a (110) fiber texture. This implies rotational randomness around the wire axis. Leber1 has shown that rotation about the wire axis may be restricted resulting in a preferred orientation designated as a cylindrical texture. Specific crystal planes tended to remain aligned parallel to the wire surface. This texture seemed to be the result of the swaging operation used in the intermediate stages of fabrication. Bhandary and cullity2 detected similar textures in swaged iron wires. Peck and Thomas3 suggested that the preferential alignment of crystal planes parallel to the wire surface was the result of tangential flow, characteristic of swaging. Wire drawing, following swaging, twisted the crystals about axes parallel to the wire axis, converting the cylindrical texture into a normal fiber texture.4 In this investigation, quantitative techniques were used to more accurately characterize the cylindrical texture and to study its conversion into a normal fiber texture. PROCEDURE The material investigated was lamp-quality tungsten. Three ingots were rod-rolled and swaged to 112 mils diameter, and were then drawn to 10-mil wire. Samples were obtained after each drawing pass. (110) and (200) pole figures were obtained from samples prepared as shown in Fig. 1. To form the sample shown in Fig. l(a), l-in. lengths of wire were glued side by side to form a l-in. square. The composite was ground and electropolished to form a diametral reference surface. For certain specific tests, samples were prepared as shown in Fig. l(b). This composite was made from 10-mil-thick strips prepared by grinding on parallel longitudinal planes. The polished reference surface in this case was, in essence, the wire surface. The two forms of samples [~igs. l(a) and l(b)] were related by a 90-deg rotation around the wire axis. Because of ease in preparation, most data was obtained from the diametral samples. The X-ray data were obtained using a Siemen's pole-figure goniometer. These data were not corrected for absorption or defocusing effects, since only the angular locations of the intensity maxima were of interest. Regions of the pole figure more than 80 deg from the center were not investigated. Partial monochromatization was achieved by the use of unfiltered copper radiation and a krypton-filled proportional counter. No evidence of spurious white radiation effects5 could be detected. Therefore, more elaborate X-ray techniques were not required. Intensity levels were chosen to show all pertinent details of the orientation distributions. The reference plane for the pole figures was the diametral section. The orthogonal reference directions, shown in Fig. 1, were the wire axis, the radial axis per-

Jan 1, 1965

Robert H. Richards, Boston, Mass.: Mr. Goodale calls attention to the difficulty of obtaining clean tailings from the jigs which are fed by the spigots of the hydraulic separator. This difficulty is universally encountered. The Lake Superior copper mills practically overcome it by running the beds of those jigs loose, carrying into the hutch all of the available copper and some sand. These hutches are again jigged upon threesieve Collom jigs, where the treatment is very slow and gentle; and on the successive jigs lighter and lighter bedding is used. The last sieve is run thin enough to let some sand into the hutch. With these precautions most of the free copper is extracted, as well as a fair proportion of the included copper.

Jan 1, 1897

By Robert H. Dickson

Limestone replacement and contact metamorphic orebodies are 80 irregular that sampling and estimating are far less. exact than in more regular types of deposits; both the mineralized masses and the lenses of ore within them are extremely irregular. So much development work is required to find the ore that the expense of blocking out great tonnages is prohibitive; furthermore, the rock near these orebodies is so heavy that drifts or raises cannot be kept open for many years without excessive repairs. As a result, few mines in limestone have more than three years supply of ore in sight. As most of the ore, is developed by stoping— not by drifting, raising, or drilling—estimates of ore developed do not indicate the total amount of ore that may be expected; they simply indicate the relative condition of the mines. But even if they are to do this, they must be made according to a fixed plan, intelligently carried out. The estimates of ore in the Calumet & Arizona Copper mines, Warren District, Ariz., have been of much value to those who plan the mining and development work. This paper describes the methods of sampling and estimating used in these mines. Sampling Samples are taken in various ways and depend on the condition of the working and the purpose for which the sample is to be used. Drifts, crosscuts, and raises are sampled by channels or by taking a grab off each mine car as it is filled. Stopes are usually sampled by drill holes or by taking a representative sample off each mine car; the latter, or chute, sample is by far the best sample. All workings are studied periodically by an engineer, who makes graphic and detail notes of the geologic structure, as shown in Fig. 1. The daily car tally and assay of each particular working is added to the same sheet opposite the material it represents. These sheets make a permanent record, showing the exact boundaries as well as the grade of ore in all workings.

Jan 1, 1925

Prof. Henry M. Howe, New York, N. Y. (communication to the Secretary*):—The results presented in Mr. Mathewson's paper are of very great interest. Perhaps the most interesting is that shown in Table I. and Fig. 1, in which the arsenic decreases in 10 min. from 0.22 to 0.07 per cent. This is such a large decrease that it is to be hoped that Mr. Mathewson will verify it by repeating his tests with a matte of similar composition. This is particularly to be desired, because the simultaneous removal of sulphur appears to be very small. All three blows further agree in showing that the removal of arsenic is in the very early part of the blow. The fact that the removal of arsenic then ceases abruptly cannot be explained completely by the fact that the arsenic has fallen so low as by its lowness to resist further removal, because in the first blow the arsenic becomes stationary at 0.06 per cent., whereas in the third blow it does not become stationary until it has fallen to 0.034 per cent. The abrupt ending of the removal of arsenic is more likely to find its explanation in the composition of the slag, and it is to be hoped that Mr. Mathewson will supplement these extremely valuable data with others in which the composition of the slag at the same time shall be given. The sudden rise of arsenic toward the end of the third blow I suppose must be referred to an error in sampling or analysis.

Jan 1, 1908

In the Texas Panhandle 277 oil wells and 60 gas wells were completed during 1942, as compared with 647 oil and 52 gas wells completed in 1941. Fourteen dry holes were drilled in the Texas Panhandle in 1942, of which five were wildcats, resulting in four failures and one gas-field discovery in Sherman County; the latter being Hazy-Herrington-Marsh No. I Bivins completed for 5,600,000 cu. it. ol gas from 2989 to 3226 feet. During the year 1942 the Texas Panhandle produced, by counties, the following quantities of oil:

Jan 1, 1943

In the Texas Panhandle 277 oil wells and 60 gas wells were completed during 1942, as compared with 647 oil and 52 gas wells completed in 1941. Fourteen dry holes were drilled in the Texas Panhandle in 1942, of which five were wildcats, resulting in four failures and one gas-field discovery in Sherman County; the latter being Hazy-Herrington-Marsh No. I Bivins completed for 5,600,000 cu. it. ol gas from 2989 to 3226 feet. During the year 1942 the Texas Panhandle produced, by counties, the following quantities of oil:

Jan 1, 1943

By Robert F. Mehl

THE gamma-alpha transformation in iron and iron-rich alloys is of such practical and theoretical importance that many papers have been published upon the subject relating to critical temperatures, transforma-tion rates and accompanying property changes. Although crystallo-graphic studies are of less immediate practical usefulness, the opportunities which these offer to furnish data, on the basic atomic movements which characterize the transformation are not to be neglected1. The early work on the crystallography of this transformation has been reviewed in the fourth paper of this series2 since then several important papers have appeared. Our present, knowledge may be briefly summarized as follows. Kurdjumow and Sachs, working with a 1.4 per cent carbon steel3, established the orientation relationships subsisting between the face-cen-tered gamma and the metastable tetragonal lattices in freshly quenched martensite, and between the face-centered gamma and the body-Centered alpha lattices in tampered martensite. The orientation relationship observed in the latter case may be stated in terms of planes and directions observed to lie parallel in the two lattices: { 111 }Y//{110}a [110]Y//[111]a

Jan 1, 1937

By Alexander R. Troiano, Eugene P. Klier

Since the very early work on quenched structures, where the products of the martensite transformation had been recognizedl this transformation has provoked much interest and study. Theoretically it was desirable to account for the extreme changes in physical properties resulting from the formation of martensite, as that information might lead to results of practical importance. Desirable information, therefore, was on the kinetics of transformation from austenite to martensite as well as on the physical constitution of the martensite. It has been known for years that certain steels quenched to room temperature will contain persistent austenite as well as martensite. Other important and now well-established features of the martensite reaction are the Progress of the reaction on cooling only and the independence of Ar" with cooling velocities exceeding the critical velocity. These facts have been experimentally determined by various methods and investigators. Notable among the early investigators were Tammann and Scheill and Wever and Engel.2 Unfor- tunately, all investigators did not fully interpret their results, which, coupled with several investigations that yielde. conflicting resultsl caused a state of confusion that was not clarified until quite recently. X-ray investigations of martensite in steels3-6 indicate it to be a supersaturated solid solution of carbon in alpha iron. This supersaturation is evident from the appearance of a body-centered tetragonal structure with the addition of sufficient carbon. The dimensions of this tetragonal structure are a linear function of the carbon content within the limits of accuracy of the determinations. Slight tempering of tetragonal martensite leads to the destructi,, of the tetragonal structure, which is converted to a body-centered cubic strutture. This phenomenon has precipitated a controversy concerning the nature and mechanism of the tempering of martensite The facts in the case have been outlined by Epstein7 and more recently by Antia, Fletcher, and Cohen.8 The significance of Ar" on theoretical grounds is not clear, however, although considerable study has been devoted to its determination. The precise position of Art' aS a function of carbon content was first stated by Greninger and Troiano9 for steels covering a range of approximately 0.7 to 1.8 per cent carbon. The effect of alloying elements on Ar" has recently been the subject matter of investigation by various methods.

Jan 1, 1945

PRODUCTION of nonmetallic mineral raw materials used by the fertilizer, ceramic, chemical, and construction industries and many others, was greater during 1953 than in any previous year. Production of fertilizer minerals was the highest in history despite somewhat decreased consumption in the second half of the year. Marketable phosphate rock production increased 10 pct to an estimated total of 13.1 million LT, valued at $78.5 million, and potash production was estimated at 1.8 million tons of K2O equivalent, valued at over $60 million. Crude gypsum output exceeded the 1952 total and approached the record of 8.66 million tons mined in 1951, with indications that 1953 will show a new all-time high. Gains and losses among gypsum products were irregular, with major gains in plate- glass and terra-cotta plasters, sanded building plasters and miscellaneous building plasters, and principal declines in base-coat plasters, prepared finishes and tile. Lath and wallboard outputs were each about 20 pct higher than in 1952.

Jan 2, 1954

By L. A. Geoffrion, R. H. Perkins, J. C. Biery

Densities of cerium metal and several lour-melting binary cerium alloys were measured over the range 25° to 800°C. A rolumeter, using NaK as working fluid, was used to obtain the data. The cerium, Ce-Co, Ce-Ni, and Ce-Cu alloys all exhibited an increase in density on melting, while a Ce-Mn alloy expanded on melting. FOR the proper design of a nuclear reactor, the change in density of the fuel with temperature must be known. This is especially important in a system utilizing molten fuel, such as LAMPRE (Los Alamos Molten Plutonium Reactor Experiment), since a relatively large change in density usually occurs during the solid-liquid transition. The fuel for LAMPRE is a Pu-2.5 wt pct Fe alloy with a melting temperature of 410°C. However, limitations in reactor design with this fuel have led to consideration of other plutonium-containing alloys for use in future generations of this type of reactor. Several ternary alloys containing plutonium and cerium as two components have satisfactorily low melting points. The system that at the present time appears to be most acceptable is Pu-Ce-Co; it exhibits little change in melting temperature with wide variation in plutonium concentration. Other alloys that have received some consideration contain nickel, copper, and manganese as the third constituent. The proposed fuel alloys are difficult to handle experimentally in the 25" to 800°C temperature range since they oxidize readily, react with many solvents, and contain a poisonous fissionable material. In addition, in this temperature range the alloys pass through the solid-liquid transition. Several techniques are available for measuring the densities and volume coefficients of expansion of solids or liquids. However, the only apparatus that appears suitable for measuring expansion coefficients over this temperature range and through the phase transition is a volumeter. In a volumeter, the indicating medium must be essentially inert to and insoluble in the material being studied. It must also possess a low vapor pressure over the operating temperature range, and its coefficient of expansion must be accurately known. One material that is satisfactory in nearly all of these respects is the alloy Na-78 wt pct K, which melts at -10°C and has a vapor pressure of 860 mm Hg at 800°C. This relatively high vapor pressure at 800°C requires an overpressure of an inert gas to prevent boiling. While a volumeter is capable of determining accurately the volume coefficients of expansion of materials, it cannot be used for absolute density measurements. Therefore, a density determination at a known temperature must be coupled with the volumeter measurements to give all the desired data. The weight-loss technique using immersion in bromobenzene at room temperature proved to be satisfactory. The preliminary work that was done on this experimental program involved developing and calibrating the equipment, and measuring the densities and volume coefficients of expansion of cerium and some low-melting binary cerium alloys. The complications that are caused with the introduction of plutonium into the system were avoided until the equipment was proved to be satisfactory and until experience was gained in its operation. It is this first phase of the experimental work that is described in this report. DESCRIPTION OF EQUIPMENT AND OPERATING PROCEDURE The NaK volumeter is shown schematically in Fig. 1. Basically, the equipment consists of two weld-sealed stainless-steel containers of nearly identical volume. One container holds a tantalum crucible and the specimen being measured; the other contains a tantalum crucible and a tantalum specimen used as a control reference material. To avoid temperature gradients, the bombs are located in a copper block inside the furnace. Stainless-steel capillaries of equal length and volume connect each stainless-steel container to a glass viewing capillary. The stainless-steel containers, stainless-steel capillaries, and a portion of the glass capillaries are filled with NaK (22 wt pct Na-78 wt pct K). The NaK/gas interface in the glass capillary is viewed with a cathetometer which is accurate to *0.5 mm. The cathetometer readings are used to calculate the volume changes of the samples during a run. This volumeter is basically the same as that described by F. Knight in Plutonium 1960. 2 However, changes in equipment design and operating procedure were made to eliminate some major operating difficulties. These changes are summarized below. 1) In filling the manometer with NaK, gas was frequently entrained in the system. Evacuation of the system before filling failed to eliminate the en-

Jan 1, 1965

By J. J. Kanter

A. I. Blank.*-—Mr. Kanter has spoken of failures from causes other than creep itself in metals that are subjected to creep stresses. Would it be possible for the author to enlarge on this very important matter of "cataclysmic types of failures? " J. J. Kanter.—Of course, it is always a delicate matter to discuss specific failures. I would prefer to keep the present discussion on fundamentals and principles. H. L. Burghof.*—Mr. Kanter, I should like to ask what you consider the responsibility of the designer in avoiding stress concentrations that would lead to these types of failures? J. J. Kanter.—lt was my feeling in looking over the papers of this symposium that they were significantly lacking in consideration of what happens to the metals when strained under conditions that lead to rupture. Often creep tests are run that produce only a fractional percentage of the deformation, in several thousand hours. That kind of information gives the designer no assurance whatever that cracks will not result in his structure at points where stress concentrations, and therefore deformation concentrations, exist. I think anyone in this day and age who presents a paper on creep should incorporate with those studies a thorough investigation of creep rupture if it is expected to make an impression upon the design engineer.

Jan 1, 1945

By G. K. Dumbauld, B. E. Morgan

Kesults of laboratory investigations of the effects of drilling muds on oil well cements are presented which show that relatively large quantities of untreated muds do not seriously interfere with the setting of cement slurries, but that relalively small quantities of treated muds seriously retard the setting of cement slurries. Laboratory results also indicate that the harmful effects of contamination with treated muds can he counteracted by the addition of activated charcoal to cements. Also described is the successful use of cement containing activated charcoal for the placement of plugs in oPel hole after previous attempts with ordinary cement had been unsuccessful. INTRODUCTION The contamination of cement slurry by dilution with drilling mud has long been considered a cause of failure in oil well cementing. The cement slurry must displace the drilling mud from the annulus between the casing and the walls of the borehole. and it is probable that some mixing of the slurry and the mud occurs even under the most nearly ideal displacement conditions. Hole enlargement, failure to center the casing in the hole, and formation of gel structure in the drilling mud increase the probability of contamination. In some cementing operations, such as the placement of a cement plug in open hole, considerable mixing of the mud and slurry is likely. Many cement failures which can be attributed logically to no cause other than contamination of the cement slurry by the mud attest the need of a better understanding of this problem. Considerable attention was given to the problem of mud contamination of cements about 20 years ago.The effects of field mud upon cement slurries prepared with different amounts of mix water were investigated thoroughly, and the data obtained were invaluable in determining the causes of the high percentage of failure in oil-well cementing at that time and in bringing about improved cementing results. Since then, many aspects of the problem have changed, due primarily to advancements in cement and drilling mud technology. Today, several types of portland cement are used in well cementing and numerous chemical additives are used in drilling muds. An excellent report on the effects of drilling mud additives on oil-well cements was issued during 1951 by the American Petroleum Institute. Data in the report revealed that many mud additives, notably organic materials in relatively small amounts, produce a marked effect on the properties of cements. Prior to this time, little information has been available on the effects of chemicals commonly used in the treatment of drilling muds upon the properties of cements. Another aspect of the problem of mud contamination of cements, which has received no attention heretofore, is the possibility of producing a cement having properties unaffected by a reasonable amount of mud contamination. In view of the need for additional information on the contamination of present-day cements by currently-used drilling Muds, the investigation described herein was initiated Several years ago with a two-fold purpose: first, to determine the capacity of cement slurries to tolerate contamination by both untreated and treated muds without loss of ability to set and develop strength within a reasonable time; and, second, to investigate the possibility of enhancing the ability of cement slurries to withstand mud contamination by incorporating additives in the cement. The data for this study were obtained by mixing drilling mud with cement slurry and testing the resulting slurry-mud mixture for rate of set and development of strength. Also, several materials were tested for their possible improvement of the property of cement slurry to withstand mud contamination; these materials were tested in both contaminated and uncontaminated cement slurries.

Jan 1, 1952

By I. R. Kramer

The delay time for single crystals of iron, zinc, and pre-strained aluminum was measured under conditions of high-speed deformation. The delay time of aluminum was found to be affected by the orientation of the crystal. Under the dynamic conditions employed, tile calculated "activated volume" term appears to be very small for the three metals studied. IN a previous paper,1 it was shown that under dynamic testing conditions at 78° K, there was a delayed yield in single crystals of aluminum and copper which had been cold-worked prior to testing. The experimental results also indicated that the delay-time effect was not due to the interaction of dislocations with impurity atoms or vacancies, but rather to a dislocation-dislocation interaction since aluminum which has not been prestrained shows no delay-time phenomenon. In this paper, some data are reported on the effects of orientation on the delay time of aluminum single crystals; the delay time of zinc single crystals saturated with nitrogen and the delay time of iron single crystals also were measured. EXPERIMENTAL PROCEDURE Aluminum (99.997 pct) and zinc (99.999 pct) crystals, 1/2 in. in diam and 8 in. long were grown by the Bridgman technique. The iron single crystal was supplied by Dr. R. Maddin. The zinc crystals containing nitrogen were prepared by melting high-purity zinc in a graphite crucible and the nitrogen was introduced by additions of ammonium chloride. The liquid zinc was then drawn up into glass tubes of 1/2 in. diam and allowed to solidify. The rods were cooled to room temperature before the transfer to the mold for conversion into single crystals. The orientation of all specimens was determined by the Laue' back-reflection technique, Fig. 2 and Table I. To prepare for the delay-time measurements, the crystals were cut with a fine jewelers saw and the ends carefully machined. The specimens then were electrolytic ally polished to remove the cold-worked metal, mounted in a special fixture and hand-lapped. As a final step, the crystals were annealed in evacuated tubes. Specimens of aluminum crystals, Nos. 24 and 26, were compressed 0.5 and 2 pct, respectively, in the direction of the later impact. The zinc specimens were aged at 50°C for 15 min, In the case of iron, only two specimens could be obtained. To obtain sufficient data, it was necessary to resort to a reaging treatment. After each delay-time test, the specimens were aged at 65° C for 100 min. This treatment, according to Clark,2 is sufficient to restore the original delay time. It is believed that although the specimens were plastically deformed approximately 10-4 pct, after each test the delay-time values are reliable. The delay-time measurements were made in an apparatus similar to that described previously.' Single crystals approximately 1 in. long and having a diameter of 1/2 in. were placed in a pendulum which consisted of a bar 1/2 in. in diam and 8 ft long, designed with a crystal holder to accommodate the specimen at low temperatures. The crystal was held at a position 2 ft from the front part of the pendulum. This portion of the apparatus was supported on a fine molybdenum wire. A projectile bar of the same diameter and length comprised the other portion of the apparatus. This bar was supported on

Jan 1, 1962

Since this paper was written, some changes have taken place, materially reducing the cost of iron-making as estimated in the text. These are chiefly reductions in the prices of ore and fuel. The charcoal used is now made in bee-hive ovens, and the price is con-

Jan 1, 1895

By Richard H. Sibson

Changes in seismic style along the San Andreas fault system appear to correlate with strike-parallel variations in regional heat flow. Large earthquake ruptures are associated with colder segments of the fault zone, while comparatively high levels of microearthquake activity and small to moderate shocks occur along the hotter segments, often in association with aseismic creep. Such behavior is consistent with geotherm and strain rate dependent profiles of shear resistance versus depth, constructed for quartz-bearing rocks. These profiles suggest that the transition from frictional to quasi-plastic behavior with depth should increase by a few kilometers passing from the hotter to the colder portions of the fault zone, giving rise to long-wavelength concentrations of distortional strain energy near the base of the seismogenic zone in the cold segments. Some support for this hypothesis comes from the observed deepening of microseismic activity passing northwest and southeast from the central Californian active region to the currently locked, ~400 Ian segments of the San Andreas fault that ruptured in 1906 and 1857.

Jan 1, 1982

By Harold M. Mooney

The most significant trends appear to be an increased use of electromagnetic and geochemical methods. The most promising instrumental developments are airborne electromagnetic equipment, a magnetometer based on nuclear resonance, and reflection seismic equipment operable to depths less than 100 ft. Work in progress may lead to a one-man magnetometer capable of high precision and continuous recording.

Jan 3, 1955

By Fred A. Anderson, George B. Wallace, Edward J. Slebir

Auburn Dam will be a thin, double-curvature concrete arch dam about 685 ft high. With a crest length of about 4000 ft, it will be the world's longest single-arch dam. The site is located on the North Fork of the American River about 40 miles northeast of Sacramento, Calif. Construction is scheduled to get under way in 1970. In planning for the design and construction of Auburn Dam (see artist's conception), the foundation material, with its various discontinuities, is being investigated and the structural characteristics of the rock mass evaluated. The investigation and testing programs will aid in defining the pertinent geologic features and their individual and cumulative influence on the foundation. The work includes geologic surface mapping, surface trenching, core drilling, geophysics, tunneling, excavating shafts and raises, performing in-situ tests, and conducting laboratory tests on core and block samples. Competent amphibolite is the predominant material in the foundation, but significant bodies of chloritic, talcose, and metasedimentary rocks, a strongly developed jointing pattern, faults, and shear zones also affect the deformability of the rock mass. A comprehensive rock mechanics program, closely coordinated with geologic investigations as well as the engineering studies, therefore is required The rock mechanics work is a combination of many analytical studies and experimental investigations. The experimental work includes laboratory tests on core samples from holes drilled for geological studies of the entire foundation and in-situ tests performed in selected areas. The laboratory testing program evaluates the general properties of all important rock types and aids in correlating many of the key structural features encountered within the foundation. To derive maximum benefit from the field tests, they are conducted in materials which represent a

Jan 1, 1970

By D. E. Wolfson, D. A. Reynolds, F. W. Smith

IN 1948 the U. S. Bureau of Mines began a three- phase program to evaluate the extent and quality of U. S. coking coal: 1) a factual appraisal of known recoverable reserves in beds of mineable thickness, 2) a study of preparation characteristics, and 3) a study of carbonization properties. A previous paper presented the methods used in assessing reserves.' Although this investigation is only partly completed, data on coking properties of the Pittsburgh district coals are now available. The results are presented in this article. When coals are selected for manufacture of metallurgical coke more factors must be considered than for any other major use, as no basic industry requires coal of such high quality and uniformity. This is particularly true in the Pittsburgh district, where blast furnace practice is based on use of cokes from high quality coals. Although it is true that inferior coals are carbonized in other industrial areas, both here and abroad, the Pittsburgh coals are the best economically obtainable in the required tonnages, even though they are not the most desirable for metallurgical use.

Jan 3, 1957