By D. K. Deardorff, Earl T. Hayes

An improved technique is described for the accurate determination of melting points of metals in the temperature range 1500' to 2500°C. The improvements consist of gradient heating and refinements in cavity preparation to obtain true black-body conditions. The melting point of hafnium, as determined by this method, is set at 2222°±30°C. This is over 200°C higher than one of the values reported earlier. Discrepancies in the previously reported values for the melting point of hafnium are explained. The melting points of zirconium and titanium are found to be 1855O±15OC and 1668°±10°C, respectively. Reproducibility of results was ±3OC. PRIMARILY, this report is being made to correct a 1975o±25oC1 value for the melting point of hafnium, and to present an improved method for melting point determination. As a matter of interest, the technique was also applied to determining the melting point of zirconium and titanium. There is a wide difference in the melting point of hafnium as reported by competent investigators. DeBoer and Fast' reported a value of 2230°±500C, and later work of McPherson, as reported by Aden-stedt, placed the melting point at 1975o±25oC. Zwikker" calculated that the melting point was 2430°C. In resolving this discrepancy, improvements were made in the procedure for determining the melting points of refractory metals in the range 1500" to 2500°C. Special techniques are necessary to determine the melting point of these metals accurately. Since the metals oxidize in air above 900oC, the determinations must be carried out in an inert gas or vacuum. Also, every known refractory contaminates them to some extent. In addition, the attainment of true black-body conditions is always difficult. DeBoer and Fast actually determined the melting point of Hf-Zr as-deposited iodide process alloys and extrapolated to 100 pet Hf. McPherson employed a tungsten wire suspension similar to that described by Schramm, Gordon, and Kaufmann,1 and used hafnium metal produced by the iodide process. There was no apparent reason for the wide spread in melting points, since the quality of the metal was very good and the work was under the direction of highly competent investigators. Retracing some of this work revealed one understandable error in the case of hafnium, and led to development of an improved technique for determining melting points of reactive metals in the range 1500" to 2500°C. Material Crystal bar hafnium, zirconium, and titanium were used for this work, with analyses as shown in Table I. The hafnium was of the highest purity that has been prepared, though not as pure as the zirconium and titanium. At the instigation of the Pittsburgh Area Office of the AEC, a special lot of Hfo2 was purified, converted to the tetraflouride, and bomb-reduced with calcium, all at the Iowa State College Laboratories. This crude hafnium metal was then refined by the iodide process at the Foote Mineral Co. All specimens were cut with a Sic wheel, ground, pickled, and dried carefully before use. Procedure General Tungsten Suspension Method—In this method, a small specimen is suspended by a fine tungsten wire in a slender, induction-heated tungsten or tantalum cylinder, all under vacuum. The melting point is determined by heating the specimen slowly while observing it with an optical pyrometer focused upon a portion of the specimen that radiates as a black body. This means that there should be no reflected radiation, either from colder objects near the pyrometer or from hotter surfaces. The induction heater would be the only hotter object and, if it is slender enough, the specimen will attain the same temperature. Often a slender hole is drilled into the specimen as a source of black-body radiation. This was the general method used by McPherson in obtaining his value of 1975°C for the melting point of hafnium. In trying to repeat this work, it was found that the points of contact between the

Jan 1, 1957

E. A. Loria (Product Metallurgical Engineer, Crucible Steel Co. of America, Pittsburgh)—In this interesting paper, our introductory work was quoted. We would like to call attention to our sequel paper on the experimental determination of oxygen in cupola-melted cast iron,20 which was not mentioned. Vacuum-fusion oxygen values (as well as hydrogen and nitrogen) were reported for nine heats of cast iron melted in the Battelle 10-in. cupola under normal operating practice and under oxidizing conditions. The oxygen analyses ranged from 12 to 68 pprn compared to the author's computed range of 10 to 80 ppm. The average amount of oxygen found in our irons was about 20 pprn and changes in the silicon content of the iron from 1.32 to 2.35 pct had no consistent effect on the oxygen content of the iron. The gas determination specimens were poured in split steel molds that produced a clean pin, 3/8 in. diam and 2 in. long. Because freezing was almost instantaneous, the pins were entirely white iron (nongraphitic). In the early stages of the investigation, the pins were transferred to a mercury-filled trap system immediately after pouring. This was done to collect gas evolved between pouring and analysis. However, it was found that during storage for 4 weeks gas evolution was negligible. Because the vacuum-fusion analysis was usually completed within 4 days of pouring, pins from later heats were not stored in the mercury-trap system. We found some evidence that cast iron picks up oxygen during long storage, because of rusting. Earlier work by the British Cast Iron Research Association has shown that cast irons may be stored for a long time without significant change in their oxygen content. The practical significance of this study (and our own) would be in the improvement of cast-iron quality. Has the author investigated this aspect and reached any conclusions on the effect of oxygen on the mechanical properties of cast iron? The second phase of our study was to determine the properties of the test bars poured simultaneously with the gas analysis specimens. We realize that there may be complicating factors attendant in this procedure.21 Results from many test specimens measuring chill depth, transverse flexure and deflection strength, spiral fluidity, and sensitivity to hardness of gray irons ranging from 12 to 68 pprn oxygen showed that the lowering of transverse strength was the only significant undesirable effect of high oxygen content. A statistical study of the chill test results21 showed that the iron containing 22 to 46 pprn oxygen had forced chill depths that were 2/32 in. below the expected value from their composition, and irons containing less than 16 ppm oxygen had forced chill depths averaging 1/32 in. greater than the expected chill depth. Higher oxygen contents, within the range of 12 to 68 pprn did not increase forced chill depth. With the wedge tests, there was a good linear relationship between carbon equivalent of the irons and their chill depth. The results indicated that oxygen contents below 50 ppm in the iron did not affect chill depth. With 50 to 70 ppm oxygen in the iron, oxygen appeared to have a slight graphitizing tendency. These results are in disagreement with the common belief in gray iron foundries that "oxidized irons" produce high chill depths. It would be appreciated if the author would comment on this subject. Gustaf Ostberg (author's reply)—In Fig. 1 the legend of line I should read 2 pct C, 1 pct Si. The author wishes to thank Mr. Loria for calling attention to his later work, which was published after the present paper was concluded. The range of oxygen contents quoted seems to agree well with the author's values. The lack of response to variations in silicon content is probably due to the fact that the oxygen content in most cases was below the saturation level. The absence of temperature dependence, even in the case of saturation, is understandable if the difficulty in formation and escape of the deoxidation products is taken into account.

Jan 1, 1960

By J. N. Breston, R. V. Hughes

Conclusions drawn by previous research workers with reSPect to the relation between Pressure gradients and/or velocity and oil recovery obtained by laboratory water flood tests have been in disagreement probably due to variable procedures and unnatural conditions and materials. The Bradford Laboratory of the Pennsylvania Grade Crude Oil Association as part of its secondary recovery research program has conducted nineteen water floods on two long cores of widely differing characteristics in an attempt to clarify this relationship and make it an aid in predicting flooding pressures in the field. Unlike previous research procedures the present experiments were conducted with the aim of duplicating field conditions as closely as possible by using long unextracted consolidated cores, a live crude, and natural brines for both flooding and, connate water content. Also, the pressure gradients and flooding velocities were representative of field conditions where similar sands were being flooded. Eleven floods on one core and eight floods on the other core showed increased recoveries and lower residual oil saturation with increased flood pressure gradients and flood velocities. A marked decrease in recovery was obtained from both cores at very low flood velocities. This pressure versus recovery relationship is shown to hold up to the point of water breakthrough and also up to the 100 and 1 produced water to oil ratio point. INTRODUCTION The possibility of water flooding oil sands was suggested by Carl1 of the Pennsylvania Geological Survey in 1880. It is not known when the practice was tried intentionally for the first time, but its beneficial effects were noted in the annual production rate of the Bradford field as early as 1907. The practice was illegal in Pennsylvania until 1921. Early water floods in the Bradford field usually consisted of shooting or splitting the casing secretly to permit subsurface waters to enter the producing sands under hydrostatic head. As it was noted that the benefits of water flooding seemed to be proportional to the quantity of water dumped into the well many also began to utilize surface sources after the practice became legal. It was probably during the middle 20's before many producers realized that the pressurehead of the water upon the producing sand determined the rate and quantity of water that would enter the sand. Hence, rate and quantity of production appeared to be a direct function of input pressures. By 1927 a few producers had ventured the installation of pressure pumps in order to increase water-input rates and production through the combination of hydrostatic and hydraulic pressures. The adoption of pressure flooding and the "five-spot" drilling pattern in the Bradford field were essentially simultaneous. Water-input pressures in 1930 seldom exceeded 300 p.s.i. at the well head or 1100 p.s.i. at the sand face. Since that time, water-flood producers in the Bradford-Allegany fields have gone to higher and higher pressure until today 600 p.s.i. at the well heads is called a low pressure flood. Many high pressure floods now operate at 1300-1400 p.s.i. at the well head. The limiting and advisable pressure at the sand face has been pronounced as that pressure just under what is required to lift the overburden or to cause formation parting: According to this rule any water flood operation utilizing well-head pressures nearly equal in pounds per sq. in. to 1.1 times the average depth in feet to the top of the producing sand would be considered as a high-pressure flood. Despite the higher pressure trends in the Bradford-Allegany field operations and the results of early laboratory water flooding research, the desirability and benefits of high input pressures are still questioned by many operators, particularly in midwestern water flood operations. The present paper recounts a series of 19 laboratory water floods using two long, consolidated cores of widely differing characteristics saturated with live crude and flooded with oil field brines in an effort to simulate field conditions under • various pressure gradients and flooding velocities. For both cores, higher recoveries and lower residual oil saturations were obtained at higher pressure gradients and flood velocities. This relationship is shown to hold up to the water breakthrough point and also up to the 100 to 1 produced water to oil ratio point.

Jan 1, 1949

By C. D. Allman

Specifications for coal at the Grand Lake thermal electric station read in part: "Coal will be Rom Minto Bituminous (strip operation). Maximum lump 3x3x4 ft. Very corrosive, abrasive and when damp, sticky. Coal may consist of frozen lumps of coal, snow and ice." To maintain quality control it was necessary to develop an automatic sampling system capable of: 1) sampling from one 10-ton truckload every 1½ min; 2) permitting an operator to automatically take a sample from each truckload; 3) depositing the sample in a pre-selected container, one of a possible 10; and 4) performing the sampling operations in accordance with latest ASTM specifications for sampling coal with an ash content of 35%. This paper tells how these and other problems were resolved and describes the equipment used. The New Brunswick Electric Power Commission issued detailed specification No. 5351-5009 outlining the scope of work and general requirements for a mechanical coal handling system to be installed at the Commissions Grand Lake Generating Station. The thermal station is located at Newcastle Creek, some 40 miles east of Fredericton, N.B. Canada, on the shore of Grand Lake. This particular location is immediately adjacent to the Minto strip mining coal area of New Brunswick. Contained in the specifications, but not detailed specifically was an automatic coal sampling system. The system outlined, was to be designed and specified by the individual equipment tenderers. In conjunction with the Hardinge Co., the Barber-Greene Co. designed a sampling system which was contained in the general contract proposal. The system as designed originally, however, presented certain limitations to a continuous coal handling system and was ultimately changed. However, it was only through preliminary study and design that problems created by the specifications were determined, and these problems discussed and finally negotiated with the NBEPC engineering staff created the subsequent sampling system now being installed by Barber-Greene. It must be considered that where the original specifications did not detail the mechanical equipment, it was necessary to present a system which would correspond to the intent of specification and for which Barber-Greene would be responsible as to function, but remain in a competitive position with regard to the tender considered primarily on a price basis. The system now being installed, contains basically all the components which were detailed originally, with the exception of the holding bin arrangement, which was changed to allow a continuous operation of the entire coal handling system. SPECIFICATIONS The specifications covering the sampling system follow. 4.5 Sampler: An automatic sampling system shall be installed capable of sampling one-truck load of coal every 1½ min. When the coal is dumped into the receiving hopper, the operator shall push a button and the sampler shall automatically take a sample of that particular coal when it reaches the sampler. Then the sample taken shall be crushed and reduced in quantity to a workable sample and deposited in a pre-selected container, one of a possible ten. All samples and sampling operations shall be in accordance with the latest edition of ASTM designation 492 for sampling coal with an ash content of 35%. The coal for the initial sample shall have maximum sized lumps of about 3/4 in. and the final sample shall be adjustable from 2 to 5 lb per sample and capable of passing through a sieve with 1/8-in. diam openings. It should be noted that, because of the time delay between the time the sample is requested and when it is actually taken, the operator may call for one or two additional samples from different coal before the first sample is completely refined and in the final sample can. Coal is received from a number of different suppliers on the same day, therefore, the system shall be designed so that there is no possibility of mixing or contaminating the coal from the different suppliers. All coal rejected from the sample shall be returned to the main conveyor. All chutes, hoppers, etc. shall be designed in accordance with Section 4.6 of these specifications. 4.6 Chutes, Hoppers, etc. All chutes and hoppers

Jan 1, 1963

By R. V. Hughes, J. N. Breston

Conclusions drawn by previous research workers with reSPect to the relation between Pressure gradients and/or velocity and oil recovery obtained by laboratory water flood tests have been in disagreement probably due to variable procedures and unnatural conditions and materials. The Bradford Laboratory of the Pennsylvania Grade Crude Oil Association as part of its secondary recovery research program has conducted nineteen water floods on two long cores of widely differing characteristics in an attempt to clarify this relationship and make it an aid in predicting flooding pressures in the field. Unlike previous research procedures the present experiments were conducted with the aim of duplicating field conditions as closely as possible by using long unextracted consolidated cores, a live crude, and natural brines for both flooding and, connate water content. Also, the pressure gradients and flooding velocities were representative of field conditions where similar sands were being flooded. Eleven floods on one core and eight floods on the other core showed increased recoveries and lower residual oil saturation with increased flood pressure gradients and flood velocities. A marked decrease in recovery was obtained from both cores at very low flood velocities. This pressure versus recovery relationship is shown to hold up to the point of water breakthrough and also up to the 100 and 1 produced water to oil ratio point. INTRODUCTION The possibility of water flooding oil sands was suggested by Carl1 of the Pennsylvania Geological Survey in 1880. It is not known when the practice was tried intentionally for the first time, but its beneficial effects were noted in the annual production rate of the Bradford field as early as 1907. The practice was illegal in Pennsylvania until 1921. Early water floods in the Bradford field usually consisted of shooting or splitting the casing secretly to permit subsurface waters to enter the producing sands under hydrostatic head. As it was noted that the benefits of water flooding seemed to be proportional to the quantity of water dumped into the well many also began to utilize surface sources after the practice became legal. It was probably during the middle 20's before many producers realized that the pressurehead of the water upon the producing sand determined the rate and quantity of water that would enter the sand. Hence, rate and quantity of production appeared to be a direct function of input pressures. By 1927 a few producers had ventured the installation of pressure pumps in order to increase water-input rates and production through the combination of hydrostatic and hydraulic pressures. The adoption of pressure flooding and the "five-spot" drilling pattern in the Bradford field were essentially simultaneous. Water-input pressures in 1930 seldom exceeded 300 p.s.i. at the well head or 1100 p.s.i. at the sand face. Since that time, water-flood producers in the Bradford-Allegany fields have gone to higher and higher pressure until today 600 p.s.i. at the well heads is called a low pressure flood. Many high pressure floods now operate at 1300-1400 p.s.i. at the well head. The limiting and advisable pressure at the sand face has been pronounced as that pressure just under what is required to lift the overburden or to cause formation parting: According to this rule any water flood operation utilizing well-head pressures nearly equal in pounds per sq. in. to 1.1 times the average depth in feet to the top of the producing sand would be considered as a high-pressure flood. Despite the higher pressure trends in the Bradford-Allegany field operations and the results of early laboratory water flooding research, the desirability and benefits of high input pressures are still questioned by many operators, particularly in midwestern water flood operations. The present paper recounts a series of 19 laboratory water floods using two long, consolidated cores of widely differing characteristics saturated with live crude and flooded with oil field brines in an effort to simulate field conditions under • various pressure gradients and flooding velocities. For both cores, higher recoveries and lower residual oil saturations were obtained at higher pressure gradients and flood velocities. This relationship is shown to hold up to the water breakthrough point and also up to the 100 to 1 produced water to oil ratio point.

Jan 1, 1949

By K. Tangri, B. Swaroop

Simultaneous measurements of lattice (elastic) strain by X-ray line shift method and total strain with an electrical strain gage have been carried out on polycrystalli,ne nickel with the help of a specially designed tensometer attachment for the X-ray dif-fractometer. During the initial stages of deformation, the rate of increase in lattice strain closely follows the total strain until the plastic strain sets in. From then onwards, the two strains deviate from each other and with further increase in afiplied stress the rate of increase of lattice strain eventually decreases. Depending upon the mode of unloading, both compressive and tensile strains have been observed in nickel deformed up to 0.29 pct strain. These results have been explained on the basis of the effects of clustering of dislocations and also the production and behavior of point defects during loading and unloading, respectively. POLYCRYSTALS deformed plastically in a uniaxial tension test show residual lattice strains (hereafter referred to as RLS), which broaden the X-ray line profiles and shift their peak positions.''4 It is known that uniform straining of a crystal lattice (macrostrain) produced movement of ddfraction line peaks, whereas nonuniform straining (microstrain) causes line broadening.= Though the nature and origin of RLS in deformed metals is not yet clearly understood, these are believed to be due to the presence of some form of a locked-up stress system. Several possible detailed interpretations6'" of the stress system have been proposed by various workers and common to all these interpretations is the assumption that different parts of the aggregate have different tensile yield stresses; e.g., that a part A yields under a lower applied stress than a part B. Therefore, during the deformation process, the elastic strain in A will be less than that in B, and, after completion of deformation, B will tend to contract further than A but will be prevented from doing so by the restraining influence of A. Thus, when equilibrium is reached, A will be in compression while B is in tension. Although there is general agreement on the correctness of this argument, controversy still exists as to the exact nature of the parts A and B in a deformed metal. In an alternative approach to the creation of parts A and B, many other investigators have assumed that the RLS observed in unloaded specimens are in some way connected with the lack of proportionality between lattice strain and applied stress in the region above the yield stress." cullity13 has prepared a schematic summary of the results of previous workers, mainly Smith and Wood,2'11 which suggests that, above the elastic limit, the lattice strain may increase less rapidly with respect to strain, or may even decrease with increase in applied stress. If the applied stress is then decreased, the lattice strain would decrease along a line parallel to the loading line in the elastic region and thus produce a compressive residual lattice strain after unloading. At equilibrium, to balance these compressive stresses? there would have to be regions under tensile stress which may well be the grain boundaries or the substructure walls formed during deformation. The present investigation was undertaken to gain a better understanding of the nature and origin of RLS and also to experimentally verify the salient features of this hypothesis. EXPERIMENTAL Stress and strain determinations were made with a specially constructed tensometer attachment for the X-ray diffractometer, Fig. 1: which permits the following measurements simultaneously on a sheet specimen under uniaxial tension at various stress levels during loading and unloading: a) lattice strains, E=. in a direction perpendicular to the direction of pulling (x direction) from shifts in X-ray line peak positions; b) the total strain, ex, in the direction of pulling. with the help of an electrical strain gage affixed to the back of the specimen directly below the area irradiated by X-rays: and c) the applied stress, with the help of a load cell which consisted of a calibrated stainless-steel sample of dimensions identical to those of the specimen under investigation, and to which it was coupled. Because of its high stacking fault energy.I4 nickel

Jan 1, 1970

By J. A. Pusateri, M. A. Orehoski, N. R. Arant

Plant studies on commercial-size ingots and laboratory experiments with induction furnace heats have demonstrated that the major source of ingot cracks is associated with two conditions arising during top-pouring practice: 1—solidification during pouring, and 2—turbulence created by the impact of the stream. Methods of controlling the two factors were effective in eliminating or significantly reducing ingot cracks. BECAUSE the process of removing surface defects from hot-rolled product is so costly, the steel industry is striving constantly to develop methods of preventing, or at least decreasing, the occurrence of surface defects. Investigations have revealed steel-making and processing variables related to major surface defects, and controlling these variables has led to improvements in surface quality. However, the fundamental causes of major surface defects, such as ingot cracks, have not been determined; consequently such defects persist. At the Research and Development Laboratory of the United States Steel Corp. in Pittsburgh, a seam research program was initiated to determine the fundamental causes of certain major defects. As a part of the program, ingot cracks in killed, finegrained C1020 steel were selected for study. A cost survey indicated that, of the steels produced in sizable tonnages, carbon steels in the range of 0.18 to 0.23 pct C content require the most conditioning. Since this is particularly true of C1020, any im-provement of surface quality that might be effected from the study would be beneficial. Also, since the frequency of ingot cracks is exceedingly high for this grade, the steel would provide an excellent opportunity for a thorough study of the ingot-crack-ing problem. Why steels in this carbon range tend to exhibit more ingot cracks than do other steels was not considered in the investigation; the mechanism of ingot-crack formation was of paramount importance. Also, only the top-pouring practice was considered in the investigation, because this pouring procedure is used more extensively than others. In this study, ingot cracks are defined. as deep surface defects that sometimes are observed in an ingot prior to rolling but usually are observed during the initial stages of rolling on the primary mills. These defects may occur at any angle to the rolling direction but are most prominent in the transverse or nearly transverse direction. The appearance of ingot cracks on the rolled product varies with respect to their angle of formation and with the extent of rolling after their first occurrence. Ingot cracks are also termed "deep seams," "arrowheads," "irregular cracks," and "transverse cracks." Fig. 1 shows ingot cracks in a rolled bloom. This report summarizes: l—the exploratory investigation of commercial-size ingots; 2—the labor-atory investigations related to determining the source of ingot cracks and developing corrective methods; and 3—the plant evaluations of laboratory methods of decreasing ingot cracks. Exploration of lngot Cracks in Commercial Ingots Materials and Experimental Work: At the Du-quesne Works of the United States Steel Corp., five heats of killed, fine-grained C1020 steel were selected for the exploratory phase of the seam-research program. The heats were made by open-hearth practices that are considered most conducive to good surface quality. They were top-poured into 22x25 in. big-end-up hot-topped molds. One as-cast ingot and four other ingots rolled to the following cross-sectional sizes were set aside from each heat: 16x20 in.; 9 1/2x10 in.; 5x5 in.; and 2x2 in. The processing of the heats, from the time of charging in the open hearth furnaces to the end of the rolling operation on the primary mill, was observed carefully and recorded. The cast ingot and the four rolled ingots from each heat were examined for surface defects. The cast ingots were split longitudinally near the vertical center plane to expose the ingot structure beneath badly cracked regions. Also, a series of transverse sections was cut at about 1 in. intervals in a badly cracked area of one ingot. All sections were ground, polished, examined by sulphur printing and deep etching, and photographed. The rolled ingots

Jan 1, 1955

By Shiro Ban-ya, John Chipman

The effects of many alloying eletnents on the acticity coefficient of sulfur in liquid iron have-been studied by the equilibriutn in the reaction Sfin Fe) + Hz = HzS at 1550°C'. Results are expressed in terms of a concentration variable for a nonmetallic or for a substitutional metallic solute. Activity coefficient of sulfur, defined as increased by B, Al, C, Si, Ge, Sn, P, As, Sb, Mo, W, Co, and PI. It is decreased by Cu,Au, Ti. Zr, V, h'b, Ta, Cr, ,23n, and Ni. Irulues oj. the interaction coejficient 0i = 6 In are labulated. The same interactions are expressed also in terms of atom fraction and of weight percent. The thermodynamic properties of sulfur in liquid iron have been fairly well established. Our recent paper1 reported new determinations of activity coefficient up an atom fraction of 0.12 and equations based on a careful review of all published data. The effects of alloying elements on the activity of sulfur have been studied by several investigators,2"11 especially by Morris and Williams for silicon,' by Morris and Buehl for carbon,~ and by Sherman and Chipman for manganese. phosphorus, and al~minum.~ However, the effects of some important alloying elements remain to be determined. The purpose of this investigation was to determine the effects of many alloying elements on the activity of sulfur in Fe-S-j ternary systems. EXPERIMENTAL METHOD This study was based on experimental determination of equilibrium in the reaction at 1550°C: The same apparatus and procedure as described in our previous paper have been retained, and the same corrections were applied for dissociation of H2S. The alumina crucibles used in the experiments consisted of four separate compartments. In a given experimental run. kach of three alumina crucibles held four different samples of about 3 g each which reached equilibrium in the same gas atmosphere and temperature. The charges were made up of electrolytic iron, pure iron sulfide, and desired alloying elements, which were pure metal or master alloys made in the laboratory. The weighed samples were held for 4 to 12 hr in the prepared atmosphere at 1550°C. They were then low- ered to be cooled as quickly as possible. The quenched metal beads were crushed to avoid the errors of segregation in the ingot. The sulfur content was determined gravimetrically and alloy content by appropriate chemical analysis. CALCULATIONS The apparent equilibrium constants of Eq. [I] are expressed as follows from the corrected gas ratios and sulfur concentrations: The term K" is the observed equilibrium constant in any given ternary solution, K' is the value for the Fe-S binary solution. and the limiting value of K' in the infinitely dilute solution is designated by K, which is the true equilibrium constant in Eq. [I]. In the thermodynamic treatment of nonmetallic elements in a metallic solution, it has been suggested1' that the lattice ratio has certain advantages over other variables to express the concentration of solute. In interstitial solid solutions the lattice ratio zj is proportional to the ratio of filled interstitial sites to those which remain unfilled. The equations derived for the activity of the solute using zj as the concentration variable are found also to be applicable to liquid solutions containing nonmetallic solutes when the nonmetal is treated as if it were interstitial. For this purpose we adopt the following definitions: The quantity vj which is negative for interstitial solutes is taken as -1 for nonmetallic and +1 for metallic solutes. For purposes of calculation however ; j may be assigned a value which results in a linear relation such as shown in Figs. 1 to 15. The activity coefficient of sulfur, Qs, and equilibrium constant. K(z). are defined as follows: According to a Taylor series expansion. the logarithm of the activity coefficient of sulfur in Fe-S-j ternary system is: However, the value of 6 In */6zi remains constant through a broad range of dilute solutions and the terms of higher order are negligibly small. As a consequence, Eq. [6] is simplified as follows:

Jan 1, 1970

By U. F. Kocks

The flow stress in some latent slip systems of aluminum and silver crystals after various deformations in single slip was investigated by transverse compression and supplemented by experiments on overshoot of the compression axis and the stability of corner orientations. Work hardening was found to be remarkably isotropic, the ratio of the flow stress in the latent system to that in the primary system being between 1.0 and 1.3. The strain-rate dependence was not significantly larger in the latent system. This low anisotropy suggests that specific dislocation interactions are not the direct cause of work hardening. Either the obstacles are essentially impenetrable so that only their distance enters, or a fairly random distribution of dislocations of all systems is. in fact. formed during single slip. The latter seems to he excluded by the observations on the strain-mte dependence and on the amount of secondary strain. The amount of seconzdary strains occurring in single slip was determined by shape-change mensurements and by a new method connected with the latent-hardening experiments. It is definitely less than 1/300 times the strain in the primary svstem. WORK hardening is due to dislocation interactions; this is a hypothesis, and possibly the only one, on which all present work-harden ing theories agree. About a dozen specific interactions have been considered, and it is unlikely that any essential one has been missed. Different work-hardening theories differ to a large extent in the specific interactions which are deemed most important. The presence or absence of any particular interaction, and its degree, depend on the geometrical relationships between the two dislocations interacting. Let us enumerate some examples. Two dislocations may react, with a varying reaction energy, to form a third dislocation, and this reaction product may be sessile or glissile. Two dislocations may intersect and a jog may be formed on both, on one of them, or on neither; this jog may be sessile17Z or glissile and it may, if moved nonconservatively, lead to the production of vacancies or interstitials. Finally, a dislocation may bypass another one and thus interact only with its stress field. All these interactions depend on the specific relation between the Burgers vectors and line directions of the two dislocations. Any dislocation generated during plastic deformation of fcc crystals belongs to one of twelve slip systems. Taking any one dislocation, its relationship to each of the other eleven can fall, by symmetry, into one of only five classes. These relationships are enumerated in Fig. 1 and Table I. Each slip system is represented in the stereo-graphic projection by two triangles, namely those in one of which the specimen axis would have to lie if the specimen were to deform in single slip on this slip system in a given sense, in a tension test. Let us represent the primary slip system by the shaded triangles. The other slip systems are classified only with respect to their relationship to this primary system. The code letters (initials of established names* in German) are explained in Table I. Three specific interactions are also listed in cases where they may be strong: the product of a reaction, the formation of jogs in either system, and the elastic bypass stress. The last column relates to the types of experiments reported in this paper and summarizes their results. To decide experimentally between the relative importance of the various interactions one would like to produce a group of dislocations in one slip system and then measure the stress necessary to force another group of dislocations of a specific second system through them. Hopefully, one can produce the first set of dislocations by plastically deforming the specimen in single slip. Then one can try to achieve single slip in a specific, previously latent system and measure its flow stress. If it is different from the virgin flow stress, there has been "latent hardening". Some types of latent-hardening experiments will be discussed in the next section. The strain-rate and temperature dependence of the flow stress is an indication of the importance of dislocation intersections. By extending an investigation of this dependence to the latent systems, one can determine how much more important forest contributions are here. seeger3 has used the as-

Jan 1, 1964

By G. S. Cole

The temperature has been measured ahead of stationary solid-liquid interfaces under conditions approximating luzidirectional heat flow and therefore unidirectional solidification. Natural convection flow patterns may be deduced from the temperature distributions , temperature fluctuations, and shape of the interface. Fluid flow increases with the height and the rate of heat transfev through the interface and this is further manifested by a deviation of the interface from aflat vertical plane. The influence of fluid flow on solute inhomogeneity during alloy crystal growth can be inferred from the observed temperature distributions. A buoyancy force exists in the liquid ahead of a vertical solid-liquid interface, caused by a difference in density between cold fluid near the interface and warmer fluid in the bulk liquid. When the viscous and inertia forces in the melt exceed this buoyancy force, a flow of fluid takes place, termed natural or free thermal convection. Natural convection in purely liquid systems has been extensively studied for many years. 1"u On the other hand, fluid flow during horizontal crystal growth has oniy recently been the subject of experimental investigation."-25 The requirements for horizontal crystal growth differ from other heat flow systems. The small aspect ratio (ratio of height of cold wall to length of fluid) has never been considered. The uniform furnace gradient which supplies heat radially (and not necessarily symmetrically) differs from previous boundary conditions of uniform heat flux at the cold and hot ends. And most important of all an isothermal s/l interface is present which can adjust its shape and position to conform to heat and fluid flow. All of these boundary conditions involve complexities which cannot be readily solved analytically. Preliminary observation has demonstrated the penera1 shape of the natural convective flow pattern in transparent media.20'24'25 The flow is circulatory, directed toward the interface at the surface of the liquid, down and away from the interface at the bottom, and then up at the hot end of the melt. During crystal growth such a flow may interact with the solute boundary layer at the s/l interface to affect solute incorporation.M'1B|28'i!T Evidence has also been presented recently to show that thermal convective flow will affect the structure of ca~tin~s.~~-~~ The rate of heat transfer (conduction plus convection) in a given fluid system is a function of the temperature difference between the hot end of the liquid and the s/l interface and the height of the interface. At the lowest values of these variables* all heat is *It has been shown' that adverse temperature gradients as low as O.OOS°C oer cm are sufficient to cause convection. transferred by conduction. When the temperature difference or interface height are increased, laminar fluid flow commences and heat transport takes place by laminar convection as well as by conduction; turbulent heat transfer takes place at higher values of these variables. In the transition region between laminar and turbulent flow, boundary layer separation takes place; fluctuations in temperature are also noted and increase in amplitude and frequency as turbulence becomes dominant. In this paper, fluid flow patterns in the melt ahead of a stationary interface are deduced from observations of temperature distribution and fluctuations, heat flow rate, and interface shape. The fluid flow ahead of advancing interfaces and the effect of such flow on solute incorporation may be inferred from these measurements on stationary interfaces. Observations during enforced fluid motion will also be considered. EXPERIMENTAL PROCEDURE The metal was contained in a lava boat 10 cm in length, 1+ cm in width, and 2 cm in height, as shown in Fig. 1. A water-cooled, molybdenum block heat-sink is at one end of the boat; surrounding this assembly is a slotted stainless-steel tube noninductively wound with a nichrome heating element. Temperature was measured by 38-gage Chrome1 vs Alumel thermocouples sheathed in 0.05-cm-diam graphite-coated stainless-steel tubing, which were moved longitudinally and vertically through the melt by means of a two-dimensional motorized micrometer stage. In some experiments the thermocouple junction was exposed, but in the majority of experiments the junction was welded to the sheath tip; no significant difference

Jan 1, 1968

By J. E. Hilliard, J. W. Cahn

calculation has been made of the standard deviations to be expected in the measurement of volume fractions by areal analysis, lineal analysis and four point-counting Procedures. The effect of experimetztal errors is not included. Our conclusion is that a point count using a two-dimensional grid will be the most efficient method of volume fraction analvsis providing the grid spacing IS coarse enough. The predicted standard deviation for such an analysis is shown to he in good agreement with that determined experimentally. A metallurgist wishing to estimate a structural property by means of quantitative metallography is often faced with a choice between several different procedures. In such a case, he will naturally wish to know: a) Which procedure is the most efficient in the sense of requiring the least effort for a given precision? b) For a given procedure, what are the conditions for maximum efficiency? c) Under these conditions, how many measurements are required to attain a given precision? It is our aim in this paper to provide at least partial answers to these queries as they relate to the estimation of volume fractions from measurements on a random two-dimensional section of an opaque specimen. The commonly used techniques1,2 for volume-fraction analyses are based on one or more of the following principles: i) For an areal or Delesse3 analysis: That the areal fraction of a three-dimensional feature intercepted by a random plane provides an unbiased estimate of the volume fraction of that feature. ii) For a lineal or Rosiwal4 analysis: That the fractional intercept on a line passing at random through a two-or three-dimensional feature provides an unbiased estimate of, respectively, the areal or volume fraction of that feature. iii) For a point-count analysis: That the fractional number of randomly or regularly dispersed points falling within the boundaries of a two-dimensional feature on a plane, or within the boundaries of a three-dimensional feature in a volume, provides an unbiased estimate of, respectively, the areal or volume fraction of that feature. The absence of bias referred to in these principles does not, of course, imply that the results of an analysis will be free of error, but only that the expected result is equal to the true one. Application of the foregoing principles provide the following six possible experimental procedures: a) An Areal Analysis—This involves the measurement with a planimeter (or other means) of the area of a constitutent intercepted by the plane of polish b) A Two-Dimensional Random Point Count—Apos-sible experimental procedure for this analysis is to superimpose a sheet of transparent graph paper on a micrograph, and then use a table of random numbers to select coordinates for the points. c) A Two-Dimensiotuzl Systematic Point Count-Similar to b) except that the points are distributed in a prescribed manner, usually at the corners of a lattice superimposed on a micrograph or the screen of a projection microscope. d)A Lineal Analysis—A measurement of the fractional line length intercepted. It is usually performed by traversing the specimen under the cross hairs of a microscope and recording the distance travelled in each constituent. e) 4 One-Dimensional Random-Point Count— This could be performed by traversing the specimen with stops at random intervals to identify the constituent then present under the cross hairs. f) A One-Dimensionul Systematic Point Count— Similar to e) except that the traverse is stopped at prescribed (usually equal) intervals. It will be noted that the point-counting procedures b) and c) can be regarded as methods of estimating the areal fraction. Similarly, e) and f) are indirect methods of making a lineal analysis. All of the six procedures described above involve at least one stage of sampling. Thus, quite apart from any experimental errors, there will always be a statistical uncertainty associated with the final results. It is with the calculation of this uncertainty that we will be concerned. To avoid unnecessary repetition, the statistical relationships that will be used in the calculations are collected together in the appendix. For a fuller discussion reference should be made to one of the many textbooks5,6 on statistics. For symbols relating to the specimen structure we will follow as far as possible the terminology used by Smith and Guttman.7

Jan 1, 1962

By M. Mortada

Nonsteady-state flow of slightly compressible liquids in porous media of non-uniform properties has been the subject of a number of recent studies. Most of these studies considered one-dimensional flow in systems with cylindrical geometry and with the properties of the porous medium varying with radial distance only. A. Houpeurt' studied the problem in its general form by examining the solutions of the differential equation, In Eq. 1, the permeability k and the porosity + are arbitrary functions of radial distance. Houpeurt concluded that, except for special forms of the functions k and the problem is not well suited for mathematical treatment, but lends itself to high-speed digital computation. Carslaw and Jaeger' discussed the solution of Eq. 1 for the case in which the permeability varies as a power of the radial distance. P. Albert3 studied analytically the pseudo steady-state solutions in systems of finite radial extent and non-uniform properties. He also obtained some numerical solutions for nonsteady-state flow using a high-speed computer. William Hurst4 examined the interference pressure drop due to a point sink located in an infinite system consisting of two permeability regions in series. In this case, the permeability changed at a radial distance r from the point sink. INTERFERENCE BETWEEN OIL FIELDS IN A NON-UNIFORM AQUIFER The interference pressure drop for oil fields located in an extensive aquifer of uniform properties is discussed in a number of places in the literature. This work considers the interference pressure drop for oil fields located in a non-uniform extensive aquifer comprising two regions of different properties as shown in Fig. 1. Region I of the aquifer extends from which is the radius of Oil Field A, to ar,,, where a>1. It has permeability k,, porosity +, and effective compressibility c,. Oil Field B is located in Region II which extends from ar, to infinity and has different properties from those of Region I, but the same formation thickness h. Region II has permeability k2, porosity and effective compressibility c2. The choice of this type of aquifer should not imply that it is of frequent occurrence. It is chosen primarily to illustrate the effects of non-uniform aquifer properties on oilfield interference. It is of interest to point out that a non-uniform radial aquifer in which both the permeability and the porosity are inversely proportional to the radial distance can be treated in a manner similar to a linear aquifer of uniform properties. The situation where only the permeability varies as the inverse of the radial distance is also amenable to analytical treatment. Both aquifers behave quite differently from a radial aquifer with uniform properties so far as the water influx and the interference pressure drop are concerned. METHOD OF SOLUTION The expression for the interference pressure drop in Oil Field B due to a constant rate of water influx in Oil Field A is developed in the Appendix. This is accomplished by the simultaneous solution of two partial differential equations describing the pressure in Regions I and 11. The two differential equations are solved subject to the following conditions: (1) at r,, the pressure gradient is constant; (2) at ar the pressure and

By V 7. 0 / 300 dpi

LAST fall, having a number of ore samples from mine-development work carried on in spite of the "Revolution," I was forced to do my own assaying again, after a lapse of many years. This gave me an opportunity to build a furnace for crucible assaying, using wood for fuel, along lines which had been developing in my mind since the time 20 years ago, when as general factotum at a little mining camp in western Chihuahua, Mexico, I had converted a crucible charcoal furnace into one using the reverberatory principle. Wood-burning furnaces have been described in technical literature, but I believe the present application will prove helpful to those of the profession who are working in out-of-the-way places. The furnace is shown in detail in Figs. 1, 2 and 3. Remembering the trouble caused by stoking my first charcoal furnace too heavily, I fired this one with but a few sticks of wood at a time. By this method I could run out a charge of 12 crucibles in 30 to 35 min., using 50 sticks of ordinary stove wood. Later I fill up the firebox, holding about 40 sticks, get everything ready, put the crucibles into the melting chamber and "fire up." Just as soon as the fire is well started the draft door is closed and the furnace allowed to heat up slowly for 5 min. Then the draft is opened (the door to the ash-pit) and the fire allowed to roar, which it does. In 20 min. from the time the fire is lighted the fire door is opened, the fire stirred along the grates, and 5 or 6 more sticks of wood thrown in. In 25 min. from the start, the draft is closed again, the cover of the melting chamber pushed back and the charges poured. The melts will be found to be perfect, and the crucibles to pour absolutely clean, if everything has gone right, as will usually be the case. A new charge may be put in, and fired with S to 10 sticks of wood at a tine, and be ready to pour within 20 min.; but it is just as well to leave the crucibles in the melting chamber a full 2.5 min. By using 10 sticks of wood to start the fire and adding 5 sticks as often as needed, which will be as soon as the last sticks fed in are in perfect combustion, the smelting can be completed in from 30 to 35 min., using from 35 to 40 sticks of wood. I consider this to be the best method of stoking.

Jan 10, 1914

By David A. Thomas, Eugene S. Meieran

MECHAMCAL, electrical, and other property measurements are often more easily made on wires than on sheets. In order to carry out transmission electron microscopy on the same material used for property determinations, we have developed a method for preparing thin foil specimens of wires. The technique was developed for 0.030 in. diam tungsten wires, and is a modification of the thinning techniques used by Wilsdorf, et al 1 A length of wire is first ground to about 0.010 in. thick by mounting the wire in low melting temperature wax, hand grinding a longitudinal flat, removing and reversing the wire in the mount, and then grinding a second parallel flat. The 0.030 in. wide and 0.010 in. thick strip is cut into 1/8 in. lengths to fit in the specimen holder of the electron microscope. Next the specimen is gripped in platinum-tipped tweezers (the anode) and placed 2 mm below a hol- low copper cathode with a 0.010 in. ID nozzle. Electrolyte, 10 pct NaOH, flows by gravity feed through the nozzle onto the specimen, as shown in Fig. l(a). Polishing is carried out until a shallow impression is made on one surface, and then the specimen is turned over and the opposite surface indented. The metal between the two impressions should be about half the specimen thickness, as is shown by the heavy line in the cross section in Fig. l(b). The entire specimen is then electropolishedin 2 pct NaOH until a hole appears at the location of the indentations. The apparatus is shown in Fig. 2, and is essentially the same as that used by Wilsdorf et al. at The Franklin Institute. Light is reflected by a mirror onto the bottom surface of the specimen! which is viewed by a stereoscopic microscope placed above it. Polishing is carried out until light is seen, indicating that a hole has formed, and then immediately stopped. The specimen is washed in water. alcohol, and ether, and is then ready for examination. The specimen should be reversed in its platinum clip during electropolishing to insure equal polishing on both sides of the impression. For tungsten, indenting at 120 v and 0.04 amp takes less than 1 min, and final polishing, at 10 v and 1 amp, less than 5 min. The portion of the specimen available for transmission microscopy surrounds the hole, as is seen by the dashed lines in Fig. l(b). Slight electroetch-ing accompanying electropolishing reveals the mi-crostructure, as seen in Fig. 3(a) by light microscopy. Low-magnification electron microscopy, as in Fig. 3(b), enables the same areas and grains to be viewed and identified when subsequently examined at high magnification. Fig. 4 is a typical structure of

Jan 1, 1963

By K. S. Krishnam, A. G. Guy

VOLUME 6 of the Transactions of the Baikov Institute of Metallurgy, Moscow, is devoted to the subject of "the experimental and theoretical study of the physical characteristics of dilute solid solutions,11 and summarizes work that has been done largely in the years 1958-9. In view of the attention that Soviet investigators have given to this subject, it seemed useful to carry out an independent experimental investigation in an effort to judge the scientific basis and practical significance of this field of study. The present note is a preliminary report of this investigation. The first property studied by the Soviet group was X-ray spectra of solid-solution alloys.' An anomaly observed at low concentrations (--0.05 at. pct) of the alloying element led to the theory that each impurity atom in a transition-metal base alloy is the center of a "block" of affected atoms with a radius of about 10"7 cm. This theory was further developed in a later paper.2 By this time similar anomalies had been found in diffusion coefficients3 and in thermal expansion.4 The entire development up to 1959 was reviewed in a comprehensive paper, and further theoretical ideas were also published at this time. Finally, the volume mentioned above was published in 19607 giving new experimental data on anomalies in optical properties and Hall constant, and a new theoretical treatment also appeared.' Although western scientists have done both theoretical work, summarized recently by Friedel,9 and considerable experimental work on dilute solid solutions, there is little support for the marked anomalies reported in the Soviet papers. Of the physical properties studied by the Soviet investigators, thermal expansion was chosen for the present investigation because of the relative ease of obtaining the necessary precision of measurement. A Leitz dilatometer was used for this purpose, and a special technique involving interchanging of the two specimens being compared permitted a precision of 0.05 x X in average thermal expansion over the range 27° to 600°C. The specimens were heated and cooled in vacuum or in a protective atmosphere at a rate of 50 °C per hr. Ferrovac E iron was used as the comparison specimen and in every case had a coefficient of expansion higher than (or equal to) that of the alloy. Since unintentional impurities are an important factor in studies of dilute alloys, special attention was given to the purity of the iron and the alloys used. The alloys were the same of those used by Abrahamson10 and by Michalak," and their preparation is described in these references. Chemical analyses of the Ferrovac E iron and of typical Fe-W and Fe-Mo alloys are given in Table I. The purity of the iron and alloys is undoubtedly higher than in the

Jan 1, 1962

By M. T. Worley

This paper reports investigative work conducted to develop a method of estimating the groundwater influx from a homogeneous permeable formation into a vertical mine shaft during sinking. A method of analysis was developed using data obtained from pumping tests and a modification of the Theis non-equilibrium interpretation technique. Excess influx of groundwater into mine shafts has long been one of the more important problems encountered in the development of a mining property. Much work has been done on methods of preventing such influx and on pumping schemes to control inflow if preventive measures fail. The fundamental aspects of the problem, on the other hand, seem to have been neglected. The purpose of this paper is to review the fundamentals of groundwater flow and to propose a rapid method of analyzing hydrologic data in order to estimate influx from a homogeneous permeable formation into a mine shaft. Such an estimate of the quantity of water to be encountered is of value in planning grouting, pumping and other programs designed to control that influx. It is emphasized that the proposed method of analysis should be regarded only as a tool to be used in evaluating the problem before investing the capital necessary to begin development of a property. FUNDAMENTALS OF GROUNDWATER FLOW In order to effectively approach the problem of estimating influx into a mine shaft, a knowledge of the fundamentals of fluid flow through a porous medium is necessary. Darcy, in 1856, developed an empirical relationship to explain the flow of water through sand filters. This relationship V = k (dh/dl), is the basis for all other flow formulae. It has been shown that Darcy's relation is a solution of the Laplace equation and thus is analagous to other natural phenomena such as heat flow. Theis, using the analogy of heat flow by conduction, developed an expression for determining the transient or time-dependent groundwater flow through a homogeneous, isotropic medium. The resulting equation Was also derived by Jacob using hydrologic considerations alone.' The individual terms in the equation are described in Table I. It is important to understand the assumptions upon which this equation is based. 1) The medium through which the fluid flows is infinite in areal extent, homogeneous and isotropic. 2) The well into which the fluid discharges completely penetrates the medium. 3) The characteristics of the medium remain constant at all times. 4) The initial pressure surface is horizontal. 5) The confining media are impervious and horizontal. 6) Fluid is removed from storage instantaneously by a decline in pressure. 7) The diameter of the discharge well is infinitesimal with respect to the drainage radius of the medium.

Jan 1, 1962

By Howard S. Lee

In central Colorado is a great belt of intrusive porphyry nearly 100 miles long (160 km.), extending from the Clear Creek district on the north to Aspen on the south, which includes many of the well known mining camps of the state. Near the southern end of this belt, at Leadville, the occurrence of these intrusives is most marked, resulting in intensive mineralization and the formation of a great variety of large orebodies. During the past 40 years, Leadville has been a steady producer of gold, silver, lead, zinc, manganese, iron, and bismuth, in the forms of sulfide, carbonate and oxide ores. It is the purpose of this paper to discuss pyrite alone, which, under present economic conditions, is valuable chiefly for its sulfur contents. The ore-bearing formation of the Leadville district consists of two beds of limestone separated by a layer of quartzite. The upper limeatone is carbonaceous, and is known locally as the blue limestone. It varies in thickness from 50 to 300 ft. (15 to 91 m.). The lower limestone is Silurian, known locally as white limestone, and is about the same thickness as the upper bed. Underneath the Silurian limestone is a layer of Cambrian quartzite from 100 to 250 ft. (30 to 76 m.) thick resting on Archean granite, which forms the limit of ore deposition. As a rule, there is a sheet of white porphyry above the upper, or blue limestone; a sheet of gray porphyry is associated with the blue limestone, either in or below it, but the porphyries are not so regular as the quartzites and limestones and are not always found in their expected positions. Throughout the district there is an elaborate system of faults and intrusive porphyry dikes, which have an important bearing on ore deposits. The writer has seen two or three orebodies which were not closely associated with either a fault or a porphyry dike, but if the minor fractures and water courses are considered as part of the fault system it is safe to say that all orebodies are directly traceable to one or both of these causes. The distribution of pyrite in the Leadville district is quite general; but, eliminating the smaller bodies and those containing prohibitive quantities of zinc or lead, and considering only the larger deposits commercially valuable for their sulfur, we find the chief pyritic ore-bodies extending in a zone approximately 6000 ft. (1828 m.) long and several hundred feet wide, from the Yak and Moyer, on the south; through the Louisville, Greenback, Mahala, Adams, and Wolftone, on Carbonate Hill; across Yankee Hill, and into the Quadrilateral, Denver City, and Tip Top, on Fryer Hill.

Jan 1, 1920

By C. V. Millikan

Temperature measurement in wells is an old practice and geothermal gradients have been of interest to geologists for many years.le2 Their application to the operation of oil wells is a more recent practice. It has long been recognized that temperature anomalies occur in drilling and producing wells but thermometers that could obtain a satisfactory record of the anomalies were not available. The normal geothermal gradient is con-sidered as being about one degree Fahren-heit for each 60 ft. of depth.4 This "nor-mal " gradient varies in different areas, but whatever it may be in an area there is little variation from the surface to as deep as the : drill penetrates. The normal gradient is appreciably changed by gas expanding ; from the reservoir into the borehole or by the movement of fluid through a borehole : while drilling, producing, or circulating. It is the resulting anomalies and abnormal gradients from which conditions in wells can be interpreted. Some of the applications of such interpretations are locating the position of oil or gas sands, permeable strata in a reservoir zone, gas-oil contact, source of water, casing leaks, and the top of cement behind casing. Thermometers A thermometer for use in wells must be sensitive and have a low thermal lag. The sensitivity should permit recording 0.2OF. or less for differential temperatures although the actual temperature need not be more accurate than 1°F. The thermal lag should be as low as rugged construction will permit in order to allow surveys to be made in a minimum of time. Of the several kinds of thermometers, these requirements are most easily obtained with the vapor-pressure, expansion, and electric-resistance types. Thermometers for use in wells may be self-contained—that is, the complete instrument is lowered into the well and a record made of the temperature—or the thermal element only may be lowered into the well and the temperature recorded at the surface. The vapor-pressure and expansion types are more adaptable for a self-contained instrument while the electric-resistance thermometer is more suitable for surface recording of temperatures. The self-contained instrument can be run against high pressure on a single wire line with only one operator required. The instrument and its hoisting equipment is easily portable and can be mounted on a small car. The disadvantages are a somewhat greater thermal lag and the necessity of completing a run before any temperature or temperature anomaly is known. A surface-recording thermometer has the advantage of being somewhat more sensitive and of having a lower thermal lag. The Operator can see what anomalies are encountered and can immediately change the running conditions of the instrument or the well conditions in order to obtain the most

Jan 1, 1941

By C. A. Hartnagel

The year 1944 marks the eightieth anniversary of the discovery of petroleum by drilling in New York State. It was in 1864 that a half dozen shallow wells were drilled at Limestone in Cattaraugus County, in a region that now forms the northern extension of the 82,000-acre Bradford pool. These early wells found oil, but not in paying quantities. They did, however, attract attention to the district and were a factor in the development of the still active Bradford pool of Pennsylvania and New York. During 1943, the production of petroleum in New York amounted to 5,029,000 bbl. This represents a decrease over the previous year, in which 5,421,000 bbl. was produced. The flush production for the New York fields occurred in the early eighties shortly after the discovery of oil in the Richburg pool of Allegany County. During the flush period, production was in excess of five million barrels annually. By 1887, however, the output had decreased to an amount only slightly more than two million barrels, and through the early years of the present century the annual total was often less than one million barrels. Flooding of the oil sands for increasing productioil was made legal in 1919, and in 1927 the output once more reached the two million mark. Two years later it had increased to over three million barrels. In Table r is shown production since 1935, in which year for the first time the output under flooding methods was in excess of four million barrels. From this table, it is evident that oil production in New 'I'ork is rather well stabilized, and since most of the oil is obtained by the flooding, or water-drive, method, with little or no prospect of discovery of new oil territory, rapid changes in yield from year to year are not to be expected. In thickness, the oil sands have a maximum of about 50 ft., and by means oi flooding may produce 10 to 12 thousand barrels an acre and proportional amounts for thinner sands. In some cases, floods have been developed in sands only 12 ft. thick. Under good flooding conditions a yield of 2000 bbl. an acre is about the lower limit at which oil can bc produced at the present price of $3.00 a barrel. The average cost for the physical development ol a lease, not including the cost ol the lease itself, is $5000 an acre. Since several months must intervene before the flood begins to act on the oil wells, and a year or more is required to bring thc wells to maximum daily production, it is evident that a considerable interval occurs before maximum returns are realized. Once a flood is developed and the wells

Jan 1, 1944

By H. N. Mills

The glass industry is a major user of many industrial minerals in the manufacture of its product. It is the intent of this chapter to: (1) acquaint the reader with the glass industry by including a few production statistics, and (2) cover the various aspects of the major raw materials used to make glass. The matter of glass compositions, properties, and batches is considered beyond the scope of this chapter which deals only with raw materials. For more details on the particular minerals and rocks used in glassmaking, the reader is referred to chapters in the commodity section of this book. Glass Industry Statistics Glass manufacture in the United States can be divided into three major product classifications as follows: 1) Glass containers 2) Pressed and blown glass 3) Flat glass Glass containers include bottles and jars for the packaging of food and beverages, as well as drugs, chemicals, and cosmetics. Pressed and blown glass includes table, kitchen, art and novelty ware, lighting and electronic glassware, and fiber glass. Flat glass covers sheet or window glass, plate, laminated, and safety glass. The US Department of Commerce statistics, as recorded in the 1977 Census of Manufacturers, compares the dollar value of glass shipments for each product category. These statistics are shown in Table 1 (Anon., 1980) and are self-explanatory. A comparison of the tonnage output in each product classification is difficult, as production data is reported in "gross" for glass containers, "pounds" for fiber glass, "pieces" for glassware, [ ] and "square feet" for flat glass. In the case of glass containers, an average "pounds per gross" factor can be applied to the total production figures reported in thousands of gross in Bureau of Census industrial reports. Table 2 presents the calculated annual production tonnage for glass containers for the years 1974-1979. Except for 1979, there was a yearly increase in production. The tonnage figures of Table 2 are further influenced by decreasing weight per gross which has occurred in the glass container industry since 1975. This reflects the gradual shift to lighter weight containers for beverages. Other segments of the glass industry have experienced growth, but the figures in tons are not published information. Fiber glass growth has been influenced by the heavy demand for insulation as part of energy conservation efforts on a national basis. The production of flat glass by the float process has continued to grow with several new plants entering production. All portions of the glass industry experienced the effects of the general economic decline of 1979-1980, but the outlook for the future is bright. Batch Materials For Glass Use Materials and Function Soda-lime-silica glass represents the largest proportion of glass manufactured for commercial use. It is produced by the fluxing and

Jan 1, 1983