By John Vasey

A shaft of 1690 m depth is currently being sunk to exploit a large copper sulphide orebody. The primary crusher chamber, main pump chamber and the other excavations on the crusher level were developed from the shaft during the sinking operation. The maximum principal stress is horizontal and has a magnitude twice that of the vertical stress. It increased linearly with depth and on the elevation of the crusher level, 1613 m below surface, the stresses induced by mining can exceed the strength of the rock. The development of a workable crusher level layout, and a crusher chamber design and support system are described. Excavation and support of the workings are detailed and a comparison of expected and actual results is made.

Jan 1, 1983

By Fred D. DeVaney

DURING the past few years a radically new process for the magnetic roasting of iron ores has been investigated and developed by Pickands Mather & Co. and the Erie Mining Co. in the Erie laboratory at Hibbing, Minn. This process, originally devised by Dr. P. H. Royster of Washington, D. C., involves the use of a roasting technique quite different from older methods. It has now been demonstrated that iron-bearing materials can be roasted as effectively as by any previously known method, and at a much lower cost. The increasing shortage of highgrade iron ores in this country has accelerated the search for new methods that would permit low grade materials to be utilized. The concept of magnetically roasting low grade nonmagnetic ores such as the oxidized taconites and then separating such material magnetically has always had considerable appeal. The magnetic concentration idea is attractive because of the sharpness of the separations and cheapness of the method. Heretofore, however, the equipment and the processes available for the magnetizing-roasting -step have left much to be desired. The customary equipment available for reduction roasting has been: 1-multiple hearth furnaces, 2-rotary kilns, and 3-shaft type kilns. In addition, it is understood that some work has been done in magnetically roasting fine ores by a process using the FluoSolids principle, but little information on this process is available. The multiple hearth kiln has been used the most but first costs and operating costs have been high because of low capacity, high maintenance, and poor gas utilization. Magnetic roasting can be done in a rotary kiln, but the radiation losses are high and the conversion to magnetite is usually unsatisfactory because of poor contact between the gases and the solids. Of the shaft-type furnaces, probably the most efficient yet developed is that designed by E. W. Davis of the Minnesota Mines Experiment Station. This furnace was operated at Cooley, Minn., during 1934-1937 but was abandoned in 1937 because the operation was uneconomic. Heretofore the basic concept behind most magnetic roasting processes has been the idea of heating iron ore to a temperature of 800° to 1100 °F in a strong reducing atmosphere, preferably either carbon monoxide or hydrogen. Temperatures under 800°F were undesirable since excessive roasting time was required. Temperatures over 1100°F were avoided because of the danger of converting part of the iron to ferrous oxide which is nonmagnetic. In the new roasting process, the operation is carried on in a shaft furnace using a controlled atmosphere containing a low percentage of reducing gas. The temperature in the roasting zone is considerably higher than with the usual reducing gas and this speeds up the reduction time. Portions of the spent furnace gases are cooled and recirculated and this together with the good contact between ore and gas makes for high reducing gas utilization. High heat economy is secured by recuperating heat from the roasted ore by passing the cold reducing gases countercurrent to flow of ore. The heat transfer principle is similar to that employed in a pebble stove and to that used in the Erie Mining Co. furnace at Aurora, Minn., for pelletizing fine magnetite concentrates derived from taconite. The theory of controlled atmosphere during the roasting operation can best be appreciated by inspecting the equilibrium diagram of the Fe-C-O system shown in Fig. 1. An inspection of this diagram shows that in certain areas magnetite, Fe3O4, is the only stable form of iron. A further inspection of this table shows that if the proper ratio is maintained between carbon dioxide to carbon monoxide, such a gas will be reducing with respect to hematite, Fe2O3, and will be oxidizing with respect to both ferrous oxide, FeO, and iron, Fe. It should be kept in mind that the formation of ferrous oxide in a roasting operation is harmful, since this oxide is nonmagnetic; if it forms in any quantity, it will cause substantial loss of iron in the ensuing magnetic separation step. If a ratio of approximately three parts carbon dioxide to one of carbon monoxide is maintained, the resulting operation can be carried on at a relatively high temperature without fear of over-reduction. Specifically, most of the tests in the Erie furnace have been made at a temperature of 1500° to 1600°F, with an entrant gas containing approximately 5 pct carbon monoxide and 15 pct carbon dioxide, with the remainder largely nitrogen. It should be remembered that the ratios of carbon monoxide to carbon dioxide shown in Fig. 1 hold even though the bulk of the gas is an inert gas such as nitrogen. It may surprise many to learn that a gas containing as low as 3 pct carbon monoxide, and 12 pct carbon dioxide with the remainder nitrogen is an extremely effective reducing gas in the 1000° to 1600°F temperature range. The reducing gas is not limited to carbon monoxide, and mixtures of hydrogen and carbon monoxide may be used effectively, provided that a similar ratio is maintained between the reducing gases and carbon dioxide and water vapor. For a more detailed explanation of the theory involved, the reader is referred to U. S. patents 2,528,552 and 2,528,553. From a safety standpoint, the weak reducing gas used in the furnace offers an advantage. Its composition is such that it is well below the limits of explosion should air enter a hot furnace. This condition is not true with the usual reducing furnace, in which a gas rich in carbon monoxide or hydrogen is used. The general furnace design and method of operation may best be understood by an inspection of

Jan 1, 1952

By M. M. Wong, D. E. Couch, G. M. Martinez

The Bureau of Mines electrowon hafnium metal with an average oxygen content of' 150 ppm at 700°C from an electrolyte containing 27 wt pct LiCl, 62 wt pct RbCl, and 11 wt pct HfC14. The average anode and cathode current efficiencies were 90 pct at anode and initial cathode current densities of 86 amp per sq ft. Haf-nium metal with an average oxygen content of 440 ppm was electrowon at 800oC from an electrolyte containing 90 wt pct KC1 and 10 wt pct HfCl4. The average anode and cathode current efficiencies were similar to those obtained in the LiCL-RbCl-HfCl, electrolyte. The chlorine gas given off at the graphite anode was vented through either a silica or a graphite tube to prevent cell corrosion. THE current method for the commercial production of high-purity hafnium is the thermal decomposition of Hfl4.1 The iodide method is not adaptable to continuous process techniques. Nettle, Hiegel, and Baker2 studied the electrorefining of hafnium from hafnium sponge containing 800 ppm oxygen. They failed to obtain hafnium with 600 ppm oxygen in their initial deposits and obtained AEC specification for oxygen only after 75 pct of the soluble hafnium had been removed from the electrolyte. Calculations using their data indicated this was approximately 4 lb of hafnium. The electrolyte was then used to produce approximately 3 lb of hafnium with a low oxygen content. However, no data are shown concerning the amount of anode material initially used or what percent of it was dissolved, therefore, results are not suitable for evaluation of a continuous operation. In general, it was not possible to consistently obtain low oxygen content metal with the electrolytes described by Nettle, Hiegel, and Baker. Wong, Hiegel, and Martinez3 investigated the electrorefining process for hafnium and showed that even by strict control of electrolyte composition only relatively low oxygen reduction could be obtained. The oxygen contained in the hafnium anode material tended to transfer to the cathode deposit and only a limited purification was possible. Both the "iodide" and the "electrorefining" processes depend upon hafnium sponge as a starting material. The sponge is normally produced by magnesium reduction of HfC14 ' and does not meet AEC specifications for hafnium metal. Since only 30 pct of the anode feed could be utilized3 in the electrorefining cells, the Bureau of Mines developed an electrowinning process. HfC14 was used as the feed material for the electro-winning process described in this report. Many of the electrolytes used in the electrorefining studies3 ap- peared to be suitable carrier-electrolytes for HfC14. However, in the initial studies on electrowinning, it was desirable to use electrolytes that had low solidus temperatures and could be operated over a wide temperature range to investigate parameters of the process. Therefore, electrolytes containing LiC1, NaC1, KC1, RbC1, CsC1, and HfC14, in various combinations were explored. EQUIPMENT Chlorinator. Hafnium carbide was chlorinated to produce HfC14 in the batch-type chlorination shown in Fig. 1. Chlorination temperatures were measured with a thermocouple placed in the center of the HfC charge. A flow meter was used to monitor the helium and chlorine. The exhaust side of the silica chlorina-tor tube was equipped with a flask for collecting organic material released during the initial heating of the HfC. The temperature of an internal heater, which extended from the HfC14 condensing flask to the hot end of the chlorinator, was adjusted to prevent the HfC14 from condensing before entering the collection flask. Helium and excess chlorine were exhausted through the lid of the collection flask to an aqueous NaOH solution. Sublimer. Initial studies were conducted using a sublimer, Fig. 2, made by placing a 13/8-in. OD nickel thimble 11 in. long, inside a 11/2-in. ID nickel bell 12 in. long, and locking it in place. This unit was loaded with HfC14 and partially immersed in the molten electrolyte for sublimation directly into the electrolyte. In another sublimer shown in Fig. 3, the HfC14 was contained in a "resin reaction flask". Quartz wool, previously heated to 600aC, secured between two nickel wire screens, was placed just above the HfC14 powder. The lid contained a vacuum outlet, a gage, an argon inlet, and an air-cooled pipe for condensing the HfC14. This sublimer was evacuated and heated. The sublimation temperature was not critical and the sublimer operated satisfactorily at all temperatures between 250" and 350°C. Electrolytic Cell. The electrolyte chamber, Fig. 4, was made of mild steel 8-in. schedule 20 pipe, 30 in. long. The exterior was metallized with a Ni-Cr alloy. The electrolytes were contained in a 16 gage nickel or iron liner with a nickel heat shield on top. The cell was heated by a resistance furnace. A 21/2-in. ID by 25 in. long air lock was connected to one port of a two-port cell cover assembly through a slide valve. The cover assembly of the air lock was electrically insulated from the cell and was equipped with a rubber sleeve that provided for the passage of the cathode lead. This allowed the cathode deposits to be removed and a new nickel cathode to be introduced without allowing air to enter the cell. A tube-rod assembly was bolted to the other port on the cell cover assembly and was sealed by a packing seal. The tube-rod assembly consists of a graphite

Jan 1, 1970

By Lynn C. Jacobsen

Among the unforeseen consequences of the 1973 Arab oil embargo has been a considerable array of new or increased taxes on the so-called energy minerals. These taxes will be the subject of this report. Both Federal and State taxes have been enacted, but I will be concerned mostly with state severance taxes and particularly those on uranium. Severance taxes are considered to include all taxes having the distinctive feature of being applied on a natural resource at the stage of extraction. The tax may be based on units of production or on value, and if on values it may be on gross value or on gross value less either arbitrary or cost-related deductions. The tax has a number of aliases - resource excise tax, conservation tax, privilege tax, mining excise tax, ad valorem production tax, and more - and this makes comparison of tax burdens among states difficult. The windfall profit tax on oil is an example of a severance tax at the Federal level. Severance taxes are an established feature of state tax systems, but they continue to be a controversial issue, and proposals to raise or modify existing severance taxes are regularly submitted to the legislatures of the Western energy producing states. No concensus exists as to what is a reason- able and proper level of severance taxation or to the form it should take. The taxes which have been adopted by the various states reflect the interaction of a variety of interests and the specific circum- stances in each state. What follows is a summary of theoretical, practical, and emotional viewpoints and arguments that surface in any statehouse in which a severance tax bill has been introduced. The New Mexico experience will be heavily relied upon. THE ECONOMISTS Marginal effects. A severance tax which is based on a gross percentage of revenue or on units of production is a constant addition to variable costs, and to the mine operator has the same effect as any other increase in operating costs. The direction of these effects is straightforward: the tax will cause the property to have a lowered present value, to be mined at a lower rate than without the tax, raise the minimum grade that will be mined, lead to lower total recovery, make marginal properties sub-marginal and discriminate in favor of richer, more profitable operations (Lockner, 1965; Steele, 1967). In the short run, production facilities are fixed and imposition of a severance tax will have little effect on production levels. In the longer term, capital is mobile and investment and exploration expenditures will shift from minerals and jurisdictions with high taxes to those with low taxes. Over a considerable range of taxation the effect will be to change the relative position of the taxing state, but an overly optimistic evaluation of the capacity of mineral producers to absorb a tax can bring an industry to a halt. It is generally acknowledged that imposition of high severance taxes on taconite in Minnesota stopped development completely, and that only the adoption of a constitutional amendment limiting the amount of taxes that could be imposed in the future brought the firms back and encouraged them to make the huge investments required (Weaton, 1969). A tax which is a percentage of the net operating income (gross revenue less cash operating costs) does not influence the cut-off grade for recovery nor change the time preference for extraction, and hence, is free of the negative features of the tax applied to gross revenues or units of production. In theory it is a more efficient tax but relative administrative complexity and inherent difficulty in predicting revenue have discouraged its use. The Wyoming severance tax on uranium, which uses grade of ore as well as price in establishing taxable value, is the most cost related, and hence, the most neutral and efficient of the various state severance taxes on uranium. Economic rent. Despite the discrimination and the anti-conservation aspect inherent in most severance taxes, economists generally endorse their use because they are seen as a vehicle to appropriate rents - that is, returns greater than the long-run competitive supply price. Conspicuous examples of supposed economic rents are the returns to oil producers because of the OPEC cartel, the returns of the uranium producers under AEC buying contracts in the 19501s, and the high prices obtained by the uranium producers for contracts entered into in the 1976-1979 period. Mining of coal in the Western states is believed by some to generate huge economic rents because of the OPEC caused increase in price of a competitive fuel (McLure, 1978, p. 261), and possibly because of clean air regulations favoring the burning of low-sulfur coal. In theory, such surplus returns could be taxed completely away without affecting supply. In practice, the situation is more complex (Steele, 1967, pp. 234-236); economic rent of mineral production is an elusive quantity involving as it does replacement costs, and technical and market risk, and it, like beauty or pornography, probably exists mostly in the eye of the beholder. Rent may also be perceived to be present in the upper portion of a cyclic market which also has a downside. Where rent exists, it is almost certain to be short-lived - cartels self- destruct, government subsidies end, competitive adjustments occur - but the taxes imposed to capture it tend to be immortal. There is little doubt that the perception of un- usual and undeserved (obscene) profits in the mid- and late 1970's was a major factor in the adoption of energy mineral taxes strikingly higher than had been previously considered. At the New Mexico legislature of 1977 supporters of a moderate tax were repeatedly confronted with some variant of the statement, "You can't expect me to believe that a

Jan 1, 1982

By L. W. Saperstein, Y. J. Wang

The development of computer programs to solve complex ventilation networks has reached a point of refinement where these programs become a necessary tool of the ventilating engineer. Such a program is presented. This program has an increased efficiency over its predecessors; it also includes the important facility of fixed quantity branches. This is in addition to the earlier capabilities of free-splitting, internal or external fans, and natural ventilation pressures. The program is written in Fortran IV with double-precision arithmetic and is listed here. Sample problems with input and output are also given. The recent, and presumably continuing, official interest in mine safety is bound to result in more stringent control requirements for ventilation. Anticipating this requirement, the Dept. of Mining, The Pennsylvania State University, has developed a computer program for the solution of complex mine ventilation networks. It is the opinion of this department that the program has sufficient merit to warrant its use in normal industrial operating conditions. Although the undergraduate mining engineering students of this department are routinely trained to use the program, it was felt that this training did not present a fast enough means of dissemination; consequently, this paper was written. The conception of the program is not new;1; however, the present version incorporates features that changes it from a scientific endeavor to a useful operating tool. These features include those of earlier programs, such as free-splitting, external or internal fans, and natural ventilation processes plus the important ability of handling fixed quantity branches, and of increased efficiency giving reduced cost. The facility for fixed quantities will be discussed in more detail. The solution of any network depends upon satisfying Kirchchoff's laws. These state that the sum of flow at any junction is zero, and that the sum of the pressure drop in branches totals the pressure drop in the mesh constituted by those branches, that is that the pressure drop around any mesh is zero. The terminology is derived from Synge," and is, in fact, that used by Topologists. A branch is any airway of uniform characteristics; a junction is where two or more airways meet (the minimum number of two airways is useful for describing the point where a low resistance airway changes into a high resistance one due to some physical constriction); a mesh is a path, along some branches, that returns on to itself, but does not need to traverse the same branch twice in order to do so; and a tree describes all those branches in a network which, while connected through all the junctions, do not form any meshes. Obviously the branches-in-tree are open-ended and can be shown to be one less than the number of junction (J-1). The branches-out-of-tree, also called basic branches, are equal to the number of basic meshes and are M = N — J + 1, where M is the number of meshes and N is the number of branches. The major difference between this network and an electrical one is that the law attributed to Atkinson for pressure drop is utilized rather than Ohm's law. Atkinson stated that the pressure drop (potential) is equal to a resistance factor multiplied by the quantity squared. This is written H = RlQlQ where H is the head loss. Q? is written in this factored fashion so that H will always have the same sign as Q. A negative sign is used to indicate that flow in a branch is opposite to that of its containing mesh. A mesh takes the direction of its basic branch. Utilizing Atkinson's law in Kirchchoff's second law and bearing in mind that the first law must remain satisfied, the program will determine all quantities, or head losses as they are related, for the branches of the network. The program uses a Geuss-Seidel form of in-teration, starting from an arbitrary Q and using a correction factor of the type first suggested by Professor Hardy Cross' that will handle the nonlinear equation of Atkinson's law. A fuller description of the interative process is included in Wang and Hartman.' Iteration continues until the correction factor is less than or equal to a preset error (E) or until a maximum number of iterations (MAXIT) have been reached. Utilizing an E of 50 cfm, sample problems have had rapid solutions. Rapidity of solution is also ensured by the method of selecting meshes and basic branches. This is done by the computer, which chooses the highest resistance branches, fixed quantity branches, and those containing fans, as basic branches. Natural ventilation pressures are handled as fans of constant pressure and may be assigned to any branch. The computer will generate a fan characteristic by polynominal fitting if a few operating points from the desired fan are input. A fan may be placed in any branch of the network, except those with fixed quantities. The strength of the present program over its earlier versions is its ability to handle fixed quantity branches. This means that certain branches can have their quantity determined, or preset, by the ventilating engineer. Operating under this constraint, the program will analyze the network and output the pressure change necessary to achieve this desired quantity. A call for positive head loss would require an auxiliary fan; negative head loss would require a regulator. This represents a powerful tool for the ventilating engineer who must insure that certain quantities of air pass across the operating faces or through working stopes. McPherson6 suggested that a ventilation program would be useful for determining in advance which branches were receiving inadequate air, and that subsequent calculations would then indicate the necessary corrections. The present program makes these corrections. Thus the mine manager can know immediately the consequences of changes to his system;

Jan 1, 1971

By A. E. Bibb, F. W. Kunz

A platelet form of zirconium hydride was found in zirconium and ZY-1 wt pct U single crystals containing hydvogen in the range of 50 to 100 ppm. The habit planes for the hydride plateletg in the zirconium crystals were found to be {1012}, {1121}, and (1122) while the habit planes in the ZY-1 wt pct U crystals were {1121), {1123}, and (1.231). With the exception of the {1231} plane, these have been identified as the twin planes in zirconium. The different effect of hydridc on the mechanical puoperlies of zirconium at high and low strain rates has been explained in terms of the defornzation mechanism and the habit planes of the hydride. ZIRCONIUM and zirconium-base alloys are considered for many nuclear reactor applications, where the pick-up of hydrogen is a distinct possibility, if not an unavoidable occurrence. An excellent example of this is the absorption of hydrogen by zirconium and its alloys during aqueous corrosion, where as much as 30 pct of the hydrogen produced by the corrosion reaction is picked up by the metal. Under the proper conditions, the absorbed hydrogen would precipitate as zirconium hydride and consequently alter the mechanical and physical properties of the zirconium-base alloys. The knowledge obtained from a study of the crystallographic aspects of the hydride precipitation is necessary for the interpretation of the observed changes in the mechanical and physical properties. The deleterious effect of hydrogen on zirconium-base materials is not always observed in normal slow tensile loadings at or above room temperature, but becomes immediately obvious under impact loading, where the energy absorbed decreases with increasing hydrogen content,' and in notched specimens where triaxial loadings are attained.2 This effect is of serious consequence in the applications of Zr where shock loads or high strain rates are experienced. The purpose of this investigation was to determine the crystallographic planes of the Zr and Zr-1 wt pct U matrices upon which zirconium hydride will precipitate and to correlate these with the observed mechanical property data. PROCEDURE Crystal Growth—Single crystals of Zr and Zr-1 wt pct U alloy were used in this investigation. The Zr crystals were made from sponge that had a typical analysis as shown in Table I. Large grains were grown in this material by rapid cooling an arc-melted charge in a button furnace. This operation undoubtedly lowered the volatile impurity concentration below those listed in Table I. Back-reflection Laue patterns of these large grains showed the presence of considerable substructure and lattice distortion within each grain. It was found that an 18-day anneal in an argon atmosphere at 840°C (a high a heat-treatment) followed by furnace cooling, resulted in the further growth of the large grains and removed the detectable substructure ana lattice distortion. Equiaxed crystals with a cube edge of approximately 1/4 in. were produced in this manner. Large crystals of Zircaloy-2 (1.5 wt pct Sn, 0.15 wt pct Fe, 0.1 wt pct Cr, 0.05 wt pct Ni) also were produced by this technique but the large amount of substructure formed could not be removed by annealing. The Zr-1 wt pct U solid solution crystals were produced from an alloy rod consisting of Westing-house-Foote hafnium-free crystal bar zirconium and depleted uranium. The chemical analysis of the alloy is also given in Table I. Three-inch sections were cut from an 0.120-in.-diameter alloy rod and tapered to a fine point on each end. The samples were sealed in evacuated Vycor tubes, homogenized for 5 hr at 1000°C in the ß-phase field, and slowly lowered in a gradient furnace into the a phase (800°C), annealed for 60 hr at this temperature to produce grain growth and furnace cooled. This technique produced large grains approximately 1/2 to 3/4 in. long over the entire cross section of the rod, which were free of observable substructure. Metallographic examination up to X1000 did not show the existence of any second phase in these grains. Crystal Orientation—All crystals were abraded on fine emery paper to produce two flat surfaces 90 deg to each other. The crystals were analyzed by the standard Back-Reflection Laue technique to obtain the crystal orientation with respect to the abraded surfaces. The Back-Reflection Laue Photograms of all crystals used were clear and sharp indicating that the crystals were free from any substructure that could be detected by these means. Hydriding—Only samples containing four to five grains were used for hydriding. Samples that exhibited fine grained patches were discarded. The samples were hydrided using the following technique. After etching in 48 vol. pct HNO3, 48 vol. pct H2O, and 4 vol. pct HF (48 pct) solution, the specimens

Jan 1, 1961

By W. C. Ellis, E. S. Greiner, M. E. Fine

Discontinuous changes of Young's modulus, internal friction, coefficient of expansion, electrical resistivity, and thermoelectric power are evidence for a transition in chromium near 37OC. Although the X-ray diffraction pattern gives no clue, a difference between the thermal expansivity and the temperature dependence of the lattice parameter suggests a crystal-lographic change. Young's modulus data disclosed another transition near THE thermal dependence of a number of proper- ties of chromium indicates a transition occurring over a temperature range near room temperature. Bridgman' noted this first from a minimum in the electrical resistivity near 12°C. In a sample of greater purity, Sochtig' observed the minimum at 41 °C. Erfling3 reported an inflection in the thermal expansivity curve at 36°C. These temperature-dependence curves are reversible with no hysteresis being detected. No discontinuity or inflection has been observed in the heat capacity' or the paramagnetic susceptibility.' Likewise, no one has noted a change in crystal symmetry. In the present investigation Young's modulus, internal friction, coefficient of expansion, electrical resistivity, illustrated in Fig. 1, lattice constant, Fig. 2, thermal electromotive force, Fig. 3, and paramagnetic susceptibility, Fig. 4, were measured over an extended temperature range. The samples were prepared in two ways: (1) By cold pressing a sintered electrolytic powder compact,' and (2) by electroforming from an aqueous solution. The electroformed samples were prepared by R. A. Ehrhardt and G. Bittrich by plating on copper or nickel tubes from an aqueous solution according to the method of Brenner, Burkhead, and Jennings.' The pressed powder samples (method 1) were finally annealed at 1400°C in purified helium: the electroformed samples, packed in powdered chromium, were vacuum-annealed at 1000°C. From the composition of the original powder' the purity of the pressed powder samples is estimated to be 99.8 pct Cr. Spectrochemical analysis furnished by E. K. Jaycox, revealed only slight traces of impurities in the electroformed sample (less than 0.001 pct), neither iron nor nickel being detected. Chromium deposited by this method is reported to contain approximately 0.05 pct 0.- Methods and Data Young's Modulus: For measurement of Young's modulus, an annealed, pressed powder sample, 0.114 x0.237x1.845 in., and an electroformed sample, 0.10 in. od, 0.01 in. id, and 1.86 in. long, were prepared. The resonant frequencies of the rod samples in forced longitudinal vibration were measured at a series of temperatures from —192" to 200°C by a method previously de~cribed.6,7 Because the samples were nonferromagnetic, iron- silicon or molybdenum permalloy tips (0.013 in. thick) were soldered to the ends. The softening temperature of the solder limited the temperature of measurement. Young's modulus, E,, of chromium at temperature, T, may be calculated from the resonant frequency of the composite rod, f,; the thickness of the tips, t; the length of the chromium sample at 25°C, l,.; the density of chromium at 25°C, pc (7.20 g per cc);5 and the thermal expansivity, Al/l25. Modulus differences for two temperatures, ET and E, are accurate to +0.002x10" dynes per cm2. ET = 4PAlc+2tyf Young's modulus at 25°C, Fig. la, is 28.2~10" dynes per cm' (40.8xlO" si) in wrought chromium (upper curve). The modulus of the electroformed sample is apparently lower due to cracks. From the modulus measurements two transitions were observed: one with a critical temperature at 37°C, the other at —152°C. Internal Friction: The internal friction, 1/Q, was determined from the width, Af, of the strain amplitude-frequency curve at 0.707 times the strain amplitude at resonance;' the internal friction, 1/Q, then equals Af/f. Fig. lb shows a sharp peak in internal friction at 38°C. The internal friction of the electroformed sample had a similar maximum. Thermal Expansion: The expansivity measurements, shown in Fig. 2, covering the temperature range —195" to +400°C were made by D. MacNair in an interferometric dilatometer8 sing a sample consisting of three pyramids 0.25 in. high prepared from wrought electrolytic chromium. Below —120°C the experimental points deviated up to ±2x10 from the drawn expansivity curve in Fig. 2 because of decreased precision of the quartz wedge thermometer at low temperatures. Near 38°C the thermal expansivity curve, Fig. 2, goes through an inflection corresponding to a minimum in the coefficient of expansion, Fig. ld, and a relative volume decrease on heating. Electrical Resistivity: The variation of electrical resistivity with temperature measured by the po-tentiometric method is also shown in Fig. l. The resistivity of the wrought chromium (upper curve) at 20°C is 13.6 microhm-cm; of electroformed chromium (lower curve) 12.8 microhm-cm. The lower value reflects higher purity and agrees closely with a published value." A minimum at 40°C occurs in the resistivity curves of both samples. No conclusive evidence for a transition near — 150°C was observed, but the points, Fig. 1, appear to deviate from a smooth curve between —120" and —160°C.

Jan 1, 1952

By R. P. Abendroth

The hydrogen-water vapor ratio at which Fe-Cr alloy, chromium oxide, andiron chromite coexist in equilibrium was determined between 900" and 1200°C. A thermogravimetric method was used to determine equilibrium conditions. The results fit a straight-line relationship in the temperature region studied, and are given by Reduction experiments were also performed to confirm the results of the equilibrium investigation. ThE oxygen pressures at which Fe-Cr alloy, chromium oxide, and iron chromite coexist in equilibrium have been previously determined by Boericke and angert,' Morozov and Novokharski,' and Katsura and uan. Only one determination (at 1300°C) was made by Katsura and Muan, but it agrees with the results of orozov and Novokharski. The results of Boericke and Bangert, however, differ appreciably from the results of these investigators. Previous studies have assumed that the equilibrium metallic phase is pure iron, but Dahl and Van vlack have shown that the iron contains from about 1 wt pct Cr at 1000°C to over 2 wt pct above 1300°C. The chromium oxide also contains a small amount of iron in solid solution. In the present study, hydrogen-water vapor mixtures were equilibrated with the condensed phases, using a therrnogravimetric method to determine equilibrium conditions. The reaction can be written EXPERIMENTAL General Procedure. The starting material was a sintered pellet of Fe2O3-Cr2O3 solid solution with a hole in the center, and was placed on a fused silica hook. This assembly was raised into the preheated hot zone of the furnace in a helium atmosphere, hooked onto a fused silica hangdown suspended from one arm of an Ainsworth Model RV-AU-1 recording balance, and the starting weight determined. A flowing hydrogen-water vapor atmosphere was then exchanged for the helium by evacuation, and the sample reduced until the weight loss indicated the sample composition to be in the alloy-Cr2O3-chromite field. The tem- perature was adjusted incrementally until constant sample weight was achieved for several hours, to within 0.02 mg. A hydrogen-water vapor atmosphere of different composition was then admitted, and the same procedure carried out. At the end of a series of determinations, the sample was examined by X-ray diffraction to verify the presence of the desired phases. Microscopic examination of the silica hook showed no interaction with the sample, nor did it lose any weight. Several criteria were used to insure equilibrium besides constancy of weight. For a given hydrogen-water vapor composition, equilibrium was approached from both oxidizing and reducing sides by varying the furnace temperature slightly. The resulting slow weight loss or gain was observed for several hours. Constant weight could be re-established by returning to the original furnace temperature. The last criterion used was varying the relative amounts of the phases by further reduction or oxidation, and observing any changes in temperature required for constant weight for a given hydrogen-water vapor atmosphere. None were observed. This procedure was essentially the same as approaching the equilibrium from oxidizing and reducing sides, but larger weight excursions were carried out. Sample Preparation. Reagent-grade Fe2O3 and Cr83 powders were mixed in the desired proportions and heated in air at 1250°C for 2 hr. The mixture was re-ground and heated in air overnight at 1250°C. X-ray diffraction showed complete solid-solution formation as a result of this procedure. The solid solution was then pressed into l/2-in.-diam pellets using Carbowax 4000 as a binder. The hole was drilled in the center, and the pellets were sintered 24 hr at 1250°C in air on a bed of Fe2O3-Cr2O3 of the same composition, contained in an alundum boat. After cooling, the pellet surfaces were abraded with 310 paper to remove any surface compositional differences, such as loss of Cr2O3. Chemical analysis of the sintered pellets was 67.16 wt pct CrP3 and 33.02 wt pct Fe203. Atmosphere Generation and Control. The hydrogen-water vapor atmospheres were generated by passing Matheson ultrahigh-purity hydrogen, with no further purification, through two water bubblers contained in a constant-temperature water bath. Since the water-vapor dew points required in this study were below room temperature, the bath was insulated, and was cooled by thermoelectric-immersion devices. The bath temperature was controlled to 0.0l0C. Since rather high flow rates of about 900 ml per min were used through the furnace tube, an independent check of the dew point was made to insure saturation of the hydrogen by the water vapor. Although the dew point could only be determined to within 1/2"C, the determined dew points agreed with the water-bath temper-

Jan 1, 1967

By W. A. Backofen, R. L. Fleischer

Single crystal, bicrystal, and polycrystal tensile tests of aluminum at 4.2°K, 77°K, and 300°K have been used to examine the role of grain boundaries in the deformation process. Results indicate that a grain boundary may affect the extent and slope of easy glide. The stage II hardening rate, on the other hand, is independent of the presence or absence of grain boundaries. This conclusion allows the size of the region of multiple slip caused by an incompatible grain boundary to be determined. For the size of bicyystal sample used in this study, multiple slip occurs in about half of the cross section. PREVIOUS studies of the stress-strain characteristics of bicrystals of face-centered-cubic metals have been limited to aluminuml-5 at room temperature. Recent results, however, indicate that the stress-strain curves of single crystals of such metals may be separated into at least three stages6 in which different deformation processes are occurring7 provided testing is done at sufficiently low temperatures.' Since for aluminum a well-defined stage II develops only below room temperature, previous studies have not been able to relate effects of grain boundaries to all of the three stages of deformation. It is therefore to be expected that low-temperature deformation of aluminum single crystals and bicrystals should clarify the effects of grain boundaries on the different processes of deformation. EXPERIMENTAL PROCEDURE Single crystals and bicrystals were grown from the melt by the standard techniqueg with aluminum reported by Alcoa to be 99.993 pct pure. Ridges in the boat were used to guide the grain boundary during growth, assuring that the boundary would bisect the sample.10 The rate of furnace motion during growth was 1.0 cm per hr. During growth zone purification resulted, as evidenced by the ability of the first material to freeze to recrystallize at room temperature following severe deformation. Samples were approximately 4.4 X 6.6 mm in cross section and 103.5 mm in length between grips. Samples were annealed at 635" i 5°C for 40 hr and furnace cooled over a 7-hr period. They were then electropolished in a solution of 5 parts methanol to 1 part perchloric acid at a current density of 15 amp per sq dm for about 30 min at temperatures below 0°C. Tensile testing was performed at 295" (room temperature), 77" (sample in liquid nitrogen), and 4.2"K (sample in liquid helium) on the hard-type machine indicated schematically in Fig. 1. The machine con- sists basically of a tube surrounding a rod; one end of the sample is attached to each member, and the rod is pulled up the tube to extend the sample. The rod is rigidly mounted and is moved vertically by a system described by asinski." The pulling force is measured continuously by an electrical strain gage load cell, and the relative displacement of the tube and rod is also recorded continuously by a soft cantilever beam with electrical strain gages. Maximum stress and strain sensitivities were ±2g per sq mm and * 3-10-5. In all tests the strain rate was approximately 5.10-5 per sec. The thin wires in the tensile apparatus introduce softness, which may be corrected for, however, by measuring load vs displacement with the sample replaced by an elastic member. For loads greater than 15 kg the spring constant is 1.875.106 g per cm. The flexible wires also served to reduce substantially the large shearing forces which may arise in the case of grips having horizontal rigidity.'' As in any gripping system, however, bending moments will arise in the course of deformation by single slip. Engineering stress, s = (load)/(original cross-sectional area), and strain, E = (increase in length)/ (original length), are used for stress-strain curves unless otherwise indicated. Tables list resolved shear stress, T=mo and shear strain ? = dm, where m is the usual Schmid resolved shear stress factor for the primary slip system at the start of deformation. The first group of samples to be described forms an isoaxial set, all of the crystals making up the single crystals or bicrystals having the same tensile axis, the orientation of which is indicated by the cross in Fig. 2. For this orientation the primary slip plane and slip direction make angles of 45 deg with the tensile axis and the Schmid factor m has its maximum possible value of 0.5. Rotations about the tensile axis are indexed by means of an angle 0 between the small-area surface of the samples and the projection of the primary slip direction onto the cross section, as defined in Fig. 3. In single crystals, values of 0 were 0 and 90 deg, while in bicrystals 0 values were (0 deg, 180 deg), (90 deg, 270 deg), and (0 deg, 90 deg) as indicated in Fig. 4.

Jan 1, 1961

By G. Bhat, J. F. Libsch

lsoembrittlement curves depicting the influence of time and temperature in the range 800' to 1260°F (425' to 680°C) on the development of embrittlement in a commercial chromium alloy steel and a commercial molybdenum alloy steel are presented. Two distinct regions of embrittlement occur in the chromium alloy steel: I—at 800' to 1000°F (425' to 540°C) and 2—in the region just below the lower critical temperature. Embrittlement is most pronounced at 800' to 1000°F, decreasing very rapidly with increasing temperature above this region, only to increase again as the lower critical temperature is approached. The data suggest two distinct modes of embrittlement with possible superposition of the two modes at extended embrittling times in the temperature range 1100° to 1150°F (590' to 620°C). While the molybdenum alloy steel shows little susceptibility to embrittlement at 800' to 1000°F (425' to 540°C), considerable embrittlement may occur just below the lower critical temperature. THE subject of temper embrittlement in alloy steels has received considerable attention in the last few years. Points of view on the mechanism of embrittlement differ, however, resulting in part from the incompleteness of the data developed and in part from the speculation regarding the susceptibility of plain carbon steel to temper embrittlement. Libsch, Powers, and Bhat1 carried out short-time embrittling treatments on an AISI 1050 steel and demonstrated that hardened plain carbon steels are quite susceptible to embrittlement when tempered in the range from 850°F (455°C) to the lower critical temperature. The isoembrittlement diagram,' representing the embrittling characteristics of this steel, is reproduced in Fig. 1. It is evident from the shape of the curves shown that embrittlement in plain carbon steel increases progressively with both temperature and time in the embrittling range. A comparison of the isoembrittlement diagram for AISI 1050 steel with that presented by Jaffe and Buffum' for an SAE 3140 steel shows that up to 930°F (500°C) the isoembrittlement characteristics of the plain carbon steel are similar to those of SAE 3140 steel, although the embrittlement is much more severe in the latter steel. Above 930°F (500°C), the rate of embrittlement in the plain carbon steel increases continuously with increasing temperature; whereas, in the SAE 3140 steel, the embrittlement rapidly decreases. The influence of alloying elements upon embrittlement during tempering thus appears to cause a decrease in embrittlement above the region of maximum embrittlement, i.e., 850" to 1000°F. The question naturally arises as to what effect individual alloying elements have upon the embrittling characteristics of the plain carbon steel. Current knowledge on the influence of alloying elements on temper brittleness may be found in the review papers of Hollomon" and Woodfine. Hollo-mon," from the results of other investigators, has shown that, in general, the amount of embrittlement increases with increasing alloy content (except for molybdenum and possibly tungsten and columbium). Jaffe and Buffum," by a comparison of the embrittlement in a plain carbon steel with that of a SAE 3140 steel postulated that the presence of alloying elements in moderate amounts tends to retard the development of temper brittleness. It is difficult to determine what effect chromium has upon temper brittleness, since most of the information available has been based on the combined effect of other elements with chromium, particularly nickel and manganese. However, Wilten, and recently Jolivet and Vidal,' Vida1, and Woodfine have reported that chromium steels are temper brittle, that the embrittlement is reversible with a maximum rate of embrittlement at approximately 975°F (525"C)," and that the susceptibility increases with increasing amounts of chromium. Taber, Thorlin, and Wallacel" have found a large embrittling effect with increasing chromium content in a medium C-Mn-Ni steel. But Hultgren and Chang," from their experiments conducted on synthetically prepared ternary Fe-C-Cr alloys, could not conclude that these alloys are susceptible to temper embrittlement. However, on addition of manganese or phosphorus, these Fe-C-Cr alloys became susceptible, from which fact they concluded that the embrittlement developed in chromium-bearing Fe-C alloys is due chiefly to the presence of these elements. Considerable data are available to show that molybdenum decreases the susceptibility of steel to temper embrittlement. However, its effectiveness in preventing or decreasing embrittlement appears limited to its presence in small amounts. Vidal" has shown that a plain 2 pct Mo steel was susceptible. Hultgren and Chang" also have shown that molybdenum additions in excess of 2 pct to synthetically prepared Ni-Cr steels did not prevent embrittlement. Jolivet and Vidal' and Lea and Arnold found that molybdenum reduced temper brittleness. Lea and Arnold further stated that molybdenum decreased the rate of embrittlement rather than the total amount of embrittlement, whereas Preece and Carter" have shown that the presence of molybdenum greatly reduces the equilibrium extent of the change at a given temperature but does not appear to influence the rate of embrittlement. There appears to be very little information as to how molybdenum by itself affects the temper brittleness susceptibility of a plain carbon steel.

Jan 1, 1956

By J. D. Miller, J. E. Sepulveda

Tar sand deposits in the state of Utah contain more than 25 billion bbl of in-place bitumen. Although 30 times smaller than the well-known Athabasca tar sands, Utah tar sands do represent a significant domestic energy resource comparable to the national crude oil reserves (31.3 billion bbl). Based upon a detailed analysis of the physical and chemical properties of both the bitumen and the sand, a hot-water separation process for Utah tar sands is currently being developed in our laboratories at the University of Utah. This process involves intense agitation of the tar sand in a hot caustic solution and subsequent separation of the bitumen by a modified froth flotation technique. Experimental results with an Asphalt Ridge, Utah, tar sand sample indicated that percent solids and caustic concentration were the two most important variables controlling the performance of the digestion stage. These variables were identified by means of an experimental factorial design, in which coefficients of separation greater than 0.90 were realized. Although preliminary in nature, the experimental evidence' gathered in this investigation seems to indicate that a hot-water separation process for Utah tar sands would allow for the efficient utilization of this important energy resource. The projected increase in the ever-widening gap between the domestic energy demand and the domestic energy supply for the next few years has motivated renewed interest in energy sources other than petroleum, such as tar sands, oil shale and coal. Although a number of research programs on the exploitation of national coal and oil shale resources have already been completed, very few programs have been initiated on the processing of tar sand resources in the United States. In recognition of their significance as a domestic energy resource, investigators at the University of Utah have designed an extensive research program on Utah tar sands. An important phase of this program, and the main subject of this publication, is the development of a hot-water process for the recovery of bitumen from Utah tar sands, as a preliminary step toward the production of synthetic fuels and petrochemicals. The term "tar sand" refers to a consolidated mixture of bitumen (tar) and sand. The sand in tar sand is mostly a-quartz as determined from X-ray diffraction patterns. Alternate names for "tar sands" are "oil sands" and "bituminous sands." The latter is technically correct and in that sense provides an adequate description. Tar sand deposits occur throughout the world, often in the same geographical areas as petroleum deposits. Significantly large tar sand deposits have been identified and mapped in Canada, Venezuela and, the United States. By far, the largest deposit is the Athabasca tar sands in the Province of Alberta, Canada. According to the Alberta Energy Resources Conservation Board (AERCB),2,3 proved reserves of crude in-place bitumen in the Athabasca region amount to almost 900 billion bbl. To date, this is the only tar sand deposit in the world being mined and processed for the recovery of petroleum products. Great Canadian Oil Sands, Ltd. (GCOS) produces 20 million bbl of synthetic crude oil per year. Another plant being constructed by Syncrude Canada, Ltd. is expected to produce in excess of 40 million bbl of synthetic crude oil per year. According to the Utah Geological and Mineral Survey (UGMS), tar sand deposits in the state of Utah contain more than 25 billion bbl of bitumen in place, which represent almost 95% of the total mapped resources in the United States.4 The extent of Utah tar sand reserves seems small compared to the enormous potential of Canadian tar sands. Nevertheless, Utah tar sand reserves do represent a significant energy resource comparable to the United States crude oil proved reserves of 31.3 billion bbl in 1976.5 Tar sands in Utah occur in 51 deposits along the eastern side of the state.4 However, only six out of these 51 deposits are worthy of any practical consideration (Fig. 1). As indicated in Table 1, Tar Sand Triangle is the largest deposit in the state and contains about half of the total mapped resources. Information regarding the grade or bitumen content of Utah deposits is still very limited. The bitumen content varies significantly from deposit to deposit, as well as within a given deposit. In any event, the information available6-8 seems to indicate that Utah deposits are not as rich in bitumen as the vast Canadian deposits which average 12 to 13% by weight.9 Although many occurrences of bitumen saturation up to 17% by weight have been detected in the northeastern part of the state (Asphalt Ridge and P. R. Spring), the average for reserves in Utah may well be less than 10% by weight. Separation Technology As in any other mining problem, there are two basic approaches to the recovery of bitumen from tar sands. In one

Jan 1, 1979

By P. M. Kelly, E. P. Butler

Four Mn-CLL alloys, containing 60, 70, 80, and 90 pct Mn, respectively, have been examined in the quenched and the quenched and aged conditions using electron microscopy and electron, neutron, and X-ray diffraction. After certain heat treatments the alloys transform from fee to fct and in the tetraom1 condition show a domain structure parallel to {101} planes. Neutron diffraction indicates that the domains are antiferrornagnetically ordered. The domain boundary contrast has been examined using bright- and dark-field microscopy, and the contrast effects observed under favorable conditions have been used to deduce the c axis orientation in each domain. The domains are extremely mobile and can be nucleated at precipitate particles and screw dislocations. The domain mobility is responsible for the high damping capacity. In the aged material a Mn precipitates in the Kurdjumov-Sachs orientation and results of both electron microscopy and neutron diffraction indicate that the matrix separates into two components—one rich in manganese and the other rich in copper. ALLOYS of manganese and copper have the unusual combination of a high damping capacity and good mechanical properties and have been the subject of a number of investigations as part of a general interest in high damping capacity alloys for engineering purposes.&apos;,&apos; SO far, however, there has been no reported electron metallographic study of these alloys. The Mn-Cu system has an extensive range of solid solubility at high temperatures, and the equilibrium phases are expected to be y (fee) and a Mn. The high damping capacity is associated with a metastable tetragonal structure of variable c/a ratio, which forms from the high-temperature y phase. This latter phase becomes more difficult to retain as the manganese content increases, and alloys containing more than 82 wt pct Mn undergo a reversible martensitic fcc — fct transformation on quenching. The X-ray work of Basinski and christian3 showed that the Ms temperature for the transformation was below room temperature for alloys in the range 70 to 82 pct Mn and increased linearly with manganese content. When quenched from the y region, alloys in the range 50 to 82 pct Mn are cubic at room temperature, but become tetragonal if aged at temperatures between 400" and 600°C. The martensite transformation occurs on cooling from the aging temperature. Tetragonal alloys have a banded microstructure and the bands analyze to be traces of (110) planes. Similar microstructures have been observed in In-Tl4 and in other manganese-base systems, such as Mn-Au5 and Mn-Ni.6 The mobility of the bands in Mn-Cu alloys can be demonstrated by optical examination of a polished specimen surface subjected to a cyclic stress.7 The bands appear and disappear as the stress is varied, and X-ray measurements of the (200,020) and (002) peak intensities confirm that a reversible reorientation of the tetragonal structure occurs. Meneghetti and sidhu8 investigated the magnetic structure of Mn-Cu alloys and found antiferromagnetic ordering in furnace-cooled alloys of composition >69 at. pct Mn. Magnetic super lattice reflections occurred at the (110) and (201) positions and the proposed structure was fct with the spins along the c axis. A more complete investigation by Bacon et al.9 confirmed this structure. The magnetic ordering temperature Tn was found to increase linearly with manganese content in the same way as the Ms temperature, and at any composition, Tn > Ms. This relationship suggested that the magnetic ordering was responsible for the cubic — tetragonal transformation in the manganese-rich alloys. The purpose of this investigation was to study the mechanism of high damping and the structural changes that occur on aging. The main technique used was transmission electron microscopy, but X-ray and neutron diffraction experiments were also carried out. EXPERIMENTAL Materials and Heat Treatment. The four alloys, provided by the Admiralty Materials Laboratory. were of nominai composition 60, 70, 80, and 90 Mn and all had low impurity levels, <0.05 pct C, <0.2 pct Fe. This material was cold-rolled to 200-µ strip with intermediate annealing and then given a final heat treatment of 24 hr in the range 800° to 900°C followed by water quenching. An identical heat treatment was given a length of 3/4-in.-diam bar of the 70/30 alloy from which the neutron diffraction specimens were machined. It was suspected that the tetragonal structures would be metastable at room temperature, and so the alloys were not aged until required for experiments. After aging in a salt bath the alloys were water-quenched. Thin Foil Preparation. Initial thinning to 50 to 75 µ was possible in a solution consisting of: 50 ml nitric acid 25 ml acetic acid 25 ml water The surface deposit and grain boundary etching was removed by a final electropolish at around 20 V in an electrolyte consisting of:

Jan 1, 1969

By D. T. Goettge, E. L. Robinson

The phase changes occurring in low carbon steel during hot strip mill rolling are shown to be metallurgically significant when related to commonly used temperature control points, particularly finishing and coiling temperatures. In combination, these temperatures are shown to have an important influence on the level and uniformity of hardness, grain size, and carbide characteristics of the finished hot and cold rolled sheets. PRODUCTION of wide flat-rolled products ordinarily requires a number of operations in sequence to prepare the material for shipment to the customer. Most products are tailor-made for specific end uses, with each operation contributing certain properties to the finished material. Since the characteristics imparted to the semifinished product by a given step in processing carry through to the finished product in varying degrees, it is important that the intermediate stages of production of flat-rolled strip be carried out with the same care which characterizes the last or finishing operations. The step of hot strip mill rolling is common to the production of all of the various types of flat-rolled product; therefore, the hot strip rolling is an especially important point at which to recognize and control those variables which have an effect on the surface characteristics and metallurgical properties of the finished product and which influence the ease of conducting subsequent operations. Orders entered at a producing mill usually show an end use or describe an article or part into which the ordered product is to be fabricated. Applying his experience as to the properties necessary in a finished sheet to suit the end use and to perform successfully in the fabrication involved, the metallurgist selects a steel of suitable composition and deoxidation practice, and slabs of appropriate dimensions are produced for rolling on the hot strip mill. At this stage of processing, the metallurgist faces the problem of controlling hot strip mill practice in the light of his diagnosis of the properties necessary to meet the end use, paying due attention to the accompanying problem of producing a strip which can meet processing requirements on subsequent units in the mill. It is the purpose of this paper to describe some of the factors which he must consider in solving these problems and to indicate some of the principles which guide him. Equipment, Physical Requirements of the Strip, and Temperature Measurement The metallurgist must, of course, be familiar with the physical layout of the mill, the temperature-measuring equipment available, and the physical requirements of the hot strip product before he can apply his metallurgical knowledge to the problem; hence, the first section will consist of a brief discussion of these matters. The usual hot strip mill consists of reheating furnaces, five or six roughing stands including a scale-breaker, holding table, and second scalebreaker, six-stand finishing mill, runout table with spray cooling facilities, and coilers. A schematic diagram of a typical layout is shown in Fig. 1. Slab temperatures are primarily a function of heating time and furnace temperatures, while mill speeds, spray practice, drafting practice, available water pressure, temperature of the cooling water, cross sectional dimensions of the strip, coil size, and equipment limitations, either singly or in combination, determine what rolling temperatures are practical on a given hot strip mill unit. Thus, it is possible that a set of temperatures which can be utilized successfully on one mill cannot be used on another. However, adjustments in temperatures and rolling practice can usually be made to develop the desired metallurgical properties. In addition to the metallurgical properties developed through proper temperature control, the hot strip mill must also provide strip with certain physical attributes which may be summarized as follows: Strip Cross Section—The strip contour should conform to a section which will give the best results in the cold reduction operation. This is generally recognized as a strip with 0.001 to 0.003 in. crown or shoulder-to-shoulder convexity depending on width, and freedom from concave, flat, or wedge-shaped cross sections which cause metal buildup in cold reduction. Excessive drop off in thickness at the edges can also be very detrimental in cold reducing to light gages. Gage, Width, and Camber—All of these must be controlled. For example, rundown or increasing thickness from the front to the back of the coil results in nonuniformity in the thickness of hot-rolled sheet product and in added difficulty with gage and welds in cold reduction. Similarly, excessive width variation is the cause of guide trouble and excessive edge scrap at later stages of processing, while excessive camber is the source of a variety of processing troubles. Type of Oxide—Product intended for pickling should have a predominance of the type of oxide most easily removable in sulfuric acid. It is generally recognized that this type is obtained by use of maximum table cooling water and cold coiling

Jan 1, 1957

By C. S. Giggins, F. S. Pettit

The oxidation of Ni-Cr alloys in 0.1 atm of oxygen has been studied at temperatures between 800" and 1200°C. For alloys with 30 wt pct or more Cr, continuous layers of Cr2O3 are formed during oxidation. In the case of alloys with chromium concentrations between approximately 5 to 30 wt pct, external scales of Cr203 are formed over grain boundaries whereas internal precipitates of Cr2O3 and external layers of NiO are formed at other areas on the alloy surface. When such conditions are present on the alloy surface, chromium diffuses laterally from those areas covered with a continuous layer of Cr2O3 to areas where a Cr2O3 sub scale exists and it is possible for the sub-scale zone to become separated from the alloy by a continuous layer of Cr2O3. Whether such a state will be attained depends upon the initial grain size of the alloy and the oxidation time. When the concentration of chromium in the alloy is less than 5 pct, Cr2O3 is formed internally both at grain boundaries and within the interior of grains and the alloy is covered with an external layer of NiO. MECHANISMS which describe the growth of oxide scales on nickel-base superalloys are complex and the effects produced by the various elements in these alloys on the oxidation behavior of superalloys are not clearly understood. In order to determine the influence of the different elements on the oxidation behavior of superalloys, it is first necessary to examine the oxidation properties of binary nickel-base systems which contain the principal elements present in the superalloys and then progressively more complex systems until compositions typical of the superalloys are attained. Chromium is present in virtually all nickel-base superalloys and the purpose of the present studies was to examine the selective oxidation of chromium in Ni-Cr alloys. The oxidation characteristics of Ni-Cr alloys have been extensively studied1-" to date principally as a result of the high oxidation resistance exhibited by some of these alloys. Ni-20Cr* has long been known *All compositions are given as wcight percent unless specified otherwise. to be oxidation resistant and is commonly used as resistance heating elements for service temperatures up to 1100°C. This alloy cannot be used for extended periods of time at higher temperatures because of the apparent reaction of the external scale with oxygen to form gaseous CrO3. In spite of the considerable work cited above some important aspects of Ni-Cr oxidation still remain unresolved. Virtually all of the previous studies agree that small additions of chromium to nickel, e.g., <10 wt pct Cr, result in increased oxidation rates as compared to that of pure nickel, whereas larger additions, e.g., 20 to 30 wt pct Cr, form alloys with substantially lower oxidation rates. The controversial aspects of the oxidation mechanisms for these alloys that still remain unresolved are as follows: 1) A description of the oxidation mechanism for the low chromium alloys. 2) A description of the oxidation mechanism for the high chromium alloys, particularly with respect to the composition of the external scale which results in the lower oxidation rates. 3) The specific alloy compositions at which the oxidation mechanism changes from that obtained for low chromium contents to that of the high chromium alloys and the reason for this transition. EXPERIMENTAL The Ni-Cr alloys listed in Table I were prepared from high purity metals by nonconsumably arc melting and casting as buttons. These alloys were then given a preliminary annealing treatment in argon at 815°C for 100 hr to promote homogeneity. Each button was cut into 0.250 in. thick sections that were subsequently cold-rolled to 0.050 in. thicknesses and annealed in argon at 815°C for 48 hr to provide a twinned, equi-axed grain structure. The grain size for these alloys was not uniform and the limits, within which the average grain size lies, are given in Table I for the single-phase alloys. All the alloys were single phase with the exception of the Ni4OCr alloy in agreement with the Ni-Cr phase diagram.&apos;&apos; Rectangular specimens were cut from the sheet to provide surface areas of approximately 2.5 sq cm. Exact areas were determined with a micrometer after surface preparation was completed. All of the specimens except the Ni-40Cr alloy and pure chromium were polished through 600-grit Sic abrasive paper, ultrasonically agitated in ethylene trichloride, rinsed with ethyl alcohol, and electro-polished. The specimens were electropolished in a 10 vol pct H2SO4 (conc), 6 vol pct lactic acid, methyl alcohol solution at 70" to 80°C for 2 min at a current density of 0.8 to 1.2 amp per sq cm. This electro-polishing procedure did not produce acceptable surfaces on the Ni-40Cr alloy nor on pure chromium and the oxidation properties of these materials were obtained for specimens polished through 600-grit Sic

Jan 1, 1970

By Eugene S. Machlin

A classical theory of solid solutions involving neavest-nergkbor intevactions with both central and linked-central forces between atoms has been developed. It has been found that the theory, where it can be checked quantitatively, is in ageement with experiment. The theory encompasses a description of many diverse pkenomena, such as antiphase shift structures, size effect, relative stabilities of various solutions, lattice para,neters, and order-disorder transitions. In particulav. a quantitative prediction not involving adjustable pavameters is made concevning the deviation of the Au-Cu interatonlic distance in long-range ordered (Ll,) Cu-Au I fronl the average distance based on the distances in pure gold and copper. This prediction, which is in agreement with expel-intent, has not been encompassed by any preuious theory. The theory of order-disorder is fragmentary. That is, no one theory exists that can explain the variety of qualitative phenomena observed. Further, many theories are not in good quantitative agreement with experiment. This subject has been reviewed by Muto and Takagi, Tuttman, and Oriani.3 There exists no doubt that the quasi-chemical approximation is not a complete description and that the inclusion of strain energy using macroscopic elasticity theory concepts leads to results in disagreement with experimenL4 The observation of antiphase domains and ordering systems such as Cu-Pt has led to Brillouin zone treat-ment of the order-disorder transition as opposed to the classical Ising model. The objective of this paper is to demonstrate that it is possible to develop a pairwise approximation model that can explain many of the observed order-disorder phenomena that have puzzled investigators in the past. This theory is based upon an empirical model due to ergmman&apos; for the elastic constants of metals. This model is generalized for multicomponent systems. As will be shown, the theory yields a short-range ordering energy for the disordered solution which differs from the ordering energy calculated from the differences in energy of disordered and long-range ordered solutions. It will be demonstrated that there is no necessary correlation between heats of formation and the tendency to order or between size effect and the tendency to order. Also, the existence of antiphase domains and iso-short-range-order systems that form superlattices (Cu-Pt) is predicted on the basis of the theory. Further, the relative stability of competing superlattices is calculable from the theory. If single-crystal elastic-moduli data are available for the pure components and one superlattice then there exists but one adjustable parameter in the calculation of lattice parameters for both the disordered and ordered solid solutions. In one special case, no adjustable parameters are required and a quantitative prediction is made. For the calculation of energies and partial order, there exists but one additional adjustable parameter, the pair-exchange energy V used in the quasi-chemical approximation (or the Ising model.) However, in these calculations, much more precise values are required for the single-crystal elastic moduli than available if the quantitative uncertainties in the predicted values of the energies are to be sufficiently small. THEORY ~er~man&apos; has developed a model with which he was able to obtain fair agreement with experiment for the relations between the elastic constants for metals. This model which we shall call Bergman&apos;s model is a linear combination of his models I and 11. In effect, Bergman, in this model, considers that each interatomic distortion is composed of two components: a classical central force distortion with an associated central force constant and what we shall call a linked-central force distortion with an associated linked central-force constant. The linked-central force distortion component obeys the constraint that the sum of such distortions over all the bonds equals zero. No constraint is imposed on the classical central force distortion component. Bergman&apos; derives the constraint on the linked-central force distortion on the basis of application of Pauling&apos;s relation between bond distortion and bond number to metals.ga This assumption is not logically necessary, however, and the Bergman model may be taken as a mathematical model for elastic constants, e.g., a purely empirical model without a physical basis. In the present work, the method of Bergman has been applied to two-component systems (solid solutions). In place of an external strain—which would allow a calculation of the elastic constants for the two-component system—it is considered that internal interatomic distortions exist as a consequence of having three potentially unequal distortion-free interatomic distances and but one "average" interatomic distance. It is assumed that the distortion-free interatomic distances between atoms of the same element are those found in the pure element having the same undistorted crystal structure as the solid solution. The distortion-free interatomic distance between unlike atoms is in general not measurable except in the probably nonexistent

Jan 1, 1967

By James E. York

AT a meeting of the American Society for Testing Materials at Atlantic City, June, 1908, Dr.. C. B. Dudley, in his presidential address,&apos; showed the vital necessity of not only making a steel rail as good as in the past, but of making it considerably better in order to meet the present and prospective require¬ments of railroads. Doctor Dudley requested the co-operation of all who from personal experience could give information that would result in bringing about the production of a steel rail that could be relied upon to meet the present requirements. I have had considerable experience in the practical manufacture of steel of almost every grade, during the past 40 years, and I shall suggest changes that will bring about the results desired. Doctor Dudley has had a long experience as chemical and metallurgical expert for the Pennsylvania railroad, but he frankly admits that up to the present time both he and other metallurgical experts lack the practical knowledge of steel-making that is necessary to state correctly the reasons for the unreliability of the steel rails now produced. The necessity is self-evident for more positive practical knowledge on the part of these experts of what is possible and what is impossible regarding the practical manufacturing of steel rails from the ingot to the, finished product. Chemical knowledge in steel-making is far in advance of what it was years ago, and might be said to cover every requirement (in that department) for producing reliable steel. The study of the metallography of steel has been of great value, also the physical testing of steel, but this knowledge will only de-

May 1, 1909

By Carle R. Hayward

(Wilkes-Barre Meeting, June, 1911.) THE growing importance of metallography has caused a corresponding interest in the improvement of apparatus for preparing specimens of metals and alloys for microscopic examination. The purpose of this paper is to describe an electric heating-furnace, a grinding-and-polishing machine, and a device for mounting specimens, which are used in the metallographical work at the Massachusetts Institute of Technology. These three pieces of apparatus were designed and made in the laboratory of the Institute, and. each possesses some original features which may be of interest. ELECTRIC HEATING-FURNACE., The accurate control of heat necessary for metallographic work is best obtained by the electric-resistance furnace. Unfortunately, however, even the platinum-wound furnaces deteriorate with use and ultimately burn out, while the cheaper resistance-materials are often short-lived. Since the resistance-coil must be replaced from time to time, it is of advantage to be able to make this change with as little trouble as possible, and this is an important feature in the furnace shown in Fig. 1. A is a cylindrical galvanized-iron can, with two handles, B. A porcelain tube, C, passes through the central hole in the cover of the can and rests upon the asbestos disk, D; the bottom of the tube is held in place by the asbestos ring, E. The space, F, around the tube is filled with powdered magnesia. G is an ordinary assay-crucible, with the cover inverted so as to present a smooth top for supporting a second porcelain tube, H. The latter is wound with ?Excello " resistance-tape, 0.014

Dec 1, 1911

By James R. Cudworth

OUR colleges and universities have met many difficulties during the past year. From a period of small enrollments and depleted faculties, the educational institutions have passed quickly to a period of the largest enrollments in their history with inadequate facilities and staffs. The results of the shortsighted policy of the Selective Service system which drained the technical schools and universities of many of the students who were potential teachers are now being felt. The movement of faculty members into positions in industry during the war years has resulted in many of them forsaking permanently the educational field for the higher salaried positions they now occupy. Competition is keen between the educational institutions, and between the institutions and industry, for technically trained men. Dean Holbrook&apos;s statement in last year&apos;s annual review that he thought it would take three or four years to restore our engineering departments to their former level in quality of instructors is even more convincing today. Somehow, the institutions must not only reach their former level in quality of instruction but they must also increase the quantity of their staffs to meet the demands of the ex-service men and the high school graduates for engineering education. The enrollments in the mineral industry fields of mining, metallurgical, geological, petroleum, and ceramic engineering, although greatly increased, are not expanding as much as in the more widely known fields of electrical, mechanical, aeronautical, and civil engineering. In fact, many educators are tremendously worried about the segregation of so many young men in a relatively few fields while the needs of others will remain unanswered.

Jan 1, 1947

By Gregory L. Gullord

In September, 1975, production was begun at the new milling facility of ASARCO Incorporated, the Young Mill. The mill is located adjacent to the Young Mine 35 km (22 miles) east of Knoxville, Tennessee. The Young Mill replaced the obsolete Mascot Mill which had been operating since 1913. The basic flow sheet of Mascot was retained for the construction of the Young Mill, with a 20% increase in capacity included in the design. The Young Mill is capable of processing 7710 - t/d (8500 stpd) of crude ore from three underground mines (Young, Immel and Coy) yielding 300 - t/d (330 stpd) of 63% zinc concentrate. The Young Mill is unique in that 92.5% of the ore milled is recovered as saleable products, including zinc concentrate, construction aggregate, sand and agricultural limestone. Processing at the Young Mill is divided into five basic stages: two-stage crushing, heavy media separation, grinding-flotation, concentrate filtering and drying, and limestone by-products recovery. The ore bodies are located in the Knox formation, which consists of primary dolomite, secondary dolomite and limestone with silicas in the form of chert and jasperoid. The zinc mineralization occurs as an exceptionally pure sphalerite. The ore contains an occasional abundance of pyrite and traces of fluorite and barite. TWO STAGE CRUSHING Ore enters the crushing section from two points. The Young Mine ore is hoisted into a 816 ton (900 st) bin which feeds a 1.52m (60 in) conveyor via a 1.52 m (60 in) vibrating feeder. The Immel ore is trucked 10 km (6 miles) by an independent contractor and weighed on automatic recording truck scales at the entrance to the property.

Jan 1, 1977

By Vincent P. Gianella

THE most intense earthquake on the Pacific coast in the last several years, and probably the second most intense shock to occur in Nevada since it was settled, was felt in many Western States shortly after 10 p.m. on Dec. 20, 1932. Be- cause the rifted area contered about the northern end of Cedar Mountain it is referred to as the Cedar Mountain, Nevada, earthquake. An idea of the intensity of the shock may be gathered from the distance at which it was felt: in Wyoming, Utah, Idaho, Nevada, Washing- ton, Oregon, California and Arizona. It is the strongest quake centering in Nevada since the Pleasant Valley earthquake on Oct. 2, 1915. Despite the strength of the vibrations and the large area over which they were felt, relatively little damage was done. The extent of the damage consisted of a few old stone buildings demolished as shown in Fig. 1, much cracked and fallen plaster, many chimneys shaken down and considerable cracking of brick walls. There were no deaths and four people were but slightly injured. The small amount of damage was due, largely, to the scarcity of structures within the area of strong vibrations, but an important factor was the aridity of the region (see Fig. 2) and the shallowness of soil cover so that there was but little water-saturated loose material in which strong secondary vibrations could be formed. Had this earthquake occurred in a region of heavy precipitation and dense population the damage to property and loss of life would undoubtedly have been large, with consequently much more newspaper publicity.

Jan 1, 1933