By C. E. Sims, C. A. Zapffe

AN investigation of the behavior of inclusions in steel several years ago1 led to the conclusion that some of the commonly occurring inclusions in steel have appreciable solubilities, particularly in liquid steel. In the belief that further study and clarification of this matter was warranted, a laboratory study of oxides in liquid steel was started. These oxides are generally the result of deoxidation treatment, and the basis of an understanding of their behavior must be, therefore, the behavior of the deoxidizer in liquid iron. The Fe-Si-O system was selected for the first study, and the apparatus used and experiments conducted are described herein. APPARATUS The apparatus is shown in Fig. I and the system is shown by diagram in Fig. 2. Furnace Atmosphere Commercial hydrogen (1) passes through an orifice (2) into a manometric system that measures the tankside pressure (3) and the back pressure (4) in the system. A water trap (5) guards against excess tankside pressure. A by-pass with stopcocks (6 and 7) is provided, so that the hydrogen can be routed directly from the tank to the furnace if desired. When stopcock 7 is closed and stopcock 6 is open, the gas proceeds through the conditioning train, of which the first unit is a furnace (8) that contains platinized asbestos at 350°C. The temperature is measured by a thermo-couple and potentiometer (9) and is controlled by a slidewire resistance (10). In [ ] this furnace free oxygen is converted to water vapor. The exiting gas passes over a water bath (11) kept slightly below boiling temperature by an auxiliary heating unit (12). This unit also heats a surrounding copper coil (13) containing water, and the heated water rises through a collar (14)

Jan 1, 1942

By C.A. Zapfee, C. E. Sims

An investigation of the behavior of inclusions in steel several years ago1 led to the conclusion that some of the commonly occurring inclusions in steel have appreciable solubilities, particularly in liquid steel. In the belief that further study and clarification of this matter was warranted, a laboratory study of oxides in liquid steel was started. These oxides are generally the result of deoxidation treatment, and the basis of an understanding of their behavior must be, therefore, the behavior of the deoxidizer in liquid iron. The Fe-Si-O system was selected for the first study, and the apparatus used and experiments conducted are described herein. Apparatus The apparatus is shown in Fig. r and the system is shown by diagram in Fig. 2. Furnace, A lmosphere Commercial hydrogen (1) passes through an orifice (2) into a manometric system that measures the tankside pressure (3) and the back pressure (4) in the system. A water trap (5) guards against excess tankside pressure. A by-pass with stopcocks (6 and 7) is provided, so that the hydrogen can be routed directly from the tank to the furnace if desired. When stopcock 7 is closed and stopcock 6 is open, the gas proceeds through the conditioning train, of which the first unit is a furnace (8) that contains platinized asbestos at 350°C. The temperature is measured by a thermocouple and potentiometer (9) and is controlled by a slidewire resistance (10). In this furnace fres oxygen is converted to water vapor. The exiting gas passes over a water bath (11) kept slightly below boiling temperature by an auxiliary heating unit (12). This unit also heats a surrounding copper coil (13) containing water, and the heated water rises through a collar (14)

Jan 1, 1943

By Arthur F. Taggart

Some years ago, A. M. Gaudin and one of the authors published a paper showing removal of tar acids from solution by sulfides preferentially as compared to gangues (specifically by galena as compared to quartz).' The underlying phenomenon was classed as adsorption, and the paper went on to develop the general thesis that so far as water-soluble frothing and collecting agents in flotation are concerned, the phenomenon of adsorption is one of controlling importance. Adsorption was defined in that paper as "a process of rearrangement of a system, which results in establishing a difference in concentration, as between the interfacial layers and the bulk of the phases, of a substance or substances initially uniformly dispersed in one or several of the phases." The paper went on to develop the relation between adsorption and surface cnergy according to Gibbs' equation (which may be thrown into the form U/c = KdT/dc, where U = excess concentration in surface layer, c = concentration, T = surface tension, and K is a constant), and pointed out that, according to this equation, degree of adsorption and change in surface tension vary directly. The present paper offers a somewhat different definition for the term adsorption; and sets up, in sweeping terms, the generalization that simple chemical reaction underlies the functioning of the flotation reagents which control mineral collection, when these reagents are soluble in and act from solution in the water of the pulp. Adsorption According to the modified definition, adsorption means concentration at an interface between different phases in a heterogeneous system (thus far the definition runs as before), by the action of some mechanism, of which nothing is properly implied in the word, and concerning which the user of the word is probably in entire ignorance. Thus defined,

Jan 1, 1930

By C. A. Zapfee, C. E. Sims

An investigation of the behavior of inclusions in steel several years ago1 led to the conclusion that some of the commonly occurring inclusions in steel have appreciable solubilities, particularly in liquid steel. In the belief that further study and clarification of this matter was warranted, a laboratory study of oxides in liquid steel was started. These oxides are generally the result of deoxidation treatment, and the basis of an understanding of their behavior must be, therefore, the behavior of the deoxidizer in liquid iron. The Fe-Si-O system was selected for the first study, and the apparatus used and experiments conducted are described herein. Apparatus The apparatus is shown in Fig. r and the system is shown by diagram in Fig. 2. Furnace, A lmosphere Commercial hydrogen (1) passes through an orifice (2) into a manometric system that measures the tankside pressure (3) and the back pressure (4) in the system. A water trap (5) guards against excess tankside pressure. A by-pass with stopcocks (6 and 7) is provided, so that the hydrogen can be routed directly from the tank to the furnace if desired. When stopcock 7 is closed and stopcock 6 is open, the gas proceeds through the conditioning train, of which the first unit is a furnace (8) that contains platinized asbestos at 350°C. The temperature is measured by a thermocouple and potentiometer (9) and is controlled by a slidewire resistance (10). In this furnace fres oxygen is converted to water vapor. The exiting gas passes over a water bath (11) kept slightly below boiling temperature by an auxiliary heating unit (12). This unit also heats a surrounding copper coil (13) containing water, and the heated water rises through a collar (14)

Jan 1, 1943

By R. A. Morgen

THE binary system lead-antimony has been the subject of compre-hensive investigations in these laboratories by Dean1 and his associates. The effect of a third constituent on this system, particularly on the lead-rich alloys in which dispersion hardening ,was found, has a commercial value as well as an academic interest. This paper covers the effect of the addition of copper, bismuth and tin, all of which are likely to be found in commercial lead-antimony alloys, and is divided into three parts, as follows: I. The System Lead-Antimony-Copper II. The System Lead-Antimony-Bismuth III. The Lead Corner of the System Lead-Antimony-Tin These three systems are of three different types, and hence may be considered as covering three general kinds of additions. Bismuth forms no compounds with either lead or antimony and forms solid solutions with both. Copper forms several compounds with antimony as well as solid solutions but with lead it forms a two liquid layer system and no appreciable solid solution. Tin is soluble in both lead and antimony in the solid state and also forms a compound with antimony. The effect of small amounts of bismuth on the lead-antimony alloys is small, having no appreciable effect on the solubility of antimony. The temperature of the solidus floor is lowered appreciably by the presence of bismuth, cutting down the range of heat treatment. Copper, on the other hand, due to compound formation, increases the apparent solubility of antimony. The excess antimony is tied up with the copper finally and so is not available for dispersion hardening. The net result of addition of small amounts of copper is to shift the dispersion hardening peak of the

Jan 1, 1927

By F. X. Tartaron

This article is a continuation of a previous paper by the writer in which Kick's Law was stated to be a part of comminution theory. ln the present paper, a broadening of ideas is attempted in order to state a general theory. The word "general" is employed because the new theory includes all previous laws and generalizations which are considered to be essentially correct. These ideas are combined into a coherent whole and the general theory can be expressed by the equation In the author's previous paper on comminution, ' the equations developed were based on Charles' equation of exponents a-n +1 = 0. 2 This paper is divided into two parts, designated as First Approach and Second Approach. In the First Approach, the equations of the previous paper are utilized, with Charles' equation of exponents being necessary. In the Second Approach, a separate and independent method is used to derive the same conclusions as in the First Approach, but without the use of Charles' equation of exponents. Holmes accepts the theoretical foundation of Kick's Law as sound but denies that the law as such operates in comminution. His idea is that Kick's Law requires homogenous matter whereas the presence of cracks, flaws and cleavage planes, which predominate in the coarser particles, makes matter unhomogene-ous. This explains why there is no experimental evidence to support Kick's Law. However, since the basis of the law is theoretically sound, all experimental evidence must be viewed as emanating from it. This requires modification of current comminution equations to fit this concept. Holmes makes the modification by changing the constant exponent n in the general energy equation used by Charles (E = - JCdx/xn) to a variable exponent r. The writer asserts that Kick's Law operates in comminution without modification but it does not

Jan 1, 1963

By Donald W. Petrasek

The effects of selected alloying elements on the elevated-temperature tensile properties of copper alloy -tungsten fiber reinforced composites were invcstigated. A cornparison of the elevated-temperature tensile properties of copper alloy - tungsten fiber reinforced composites, representing soluble systems. was made with copper - tungsten fiber reinforced composites, representing a mutually insoluble system. A linear relation between tensile strength and volume percent fiber content existed at elevated temperatures for all the systenzs investigated. The copper alloy composites were weaker in tension at high volume percent fiber contents than copper composites in which alloying with the fiber did not occur. The tensile strength of the alloyed tungsten fiber decreased with increasing penetration of the alloying element into Ihe tungsten fiber. THE technique of combining strong fibers with relatively weak matrix materials so that the fibers are load-carrying members has been utilized for many years in the reinforcement of plastics with glass fibers. This type of strengthening is currently being extended to include the reinforcement of metals with metallic fibers. Investigations of the room-temperature tensile properties of metal-fiber-reinforced metallic composites have been numerous,'-" but the study of tensile properties at elevated temperatures has been limited. In previous work done at the Lewis Research Center' composites consisting of mutually insoluble constituents were investigated. Composites were made of copper reinforced with uniaxially oriented tungsten fibers. The stress-strain behavior and tensile properties of the composites were related to the tensile properties of the base materials. The tensile strength of the composite was directly proportional to the volume percent of tungsten fiber present, and the full strength of the fiber was realized. Few metal fiber - metal matrix systems exist that are mutually insoluble, and those that do exist are not generally practical. An extension of this work was an

Jan 1, 1967

By H. A. Baumann, A. J. Rostosky

EVER since the first installation of wet-washing methods of coal preparation, the removal of the water added by the washing process has created serious technical and operating problems. The rapid development and widespread adoption of wet washing has necessitated a corresponding development of dewatering methods and equipment. The amount of water retained by coal varies with the size of the coal. The moisture that is largely on the surface of the particles is easily shaken off coarse coal; thus coarse coal can be dried comparatively easily and quickly. Fine coal presents a larger surface area than does coarse coal, so its capacity for retaining moisture is greater. In fine coal, moisture below about 5 per cent is held between the coal particles and its removal is difficult. Draining and drying of the finer sizes is a major problem at many washeries. Two common problems of coal-washing practice that are intimately connected with dewatering and drying are the clarification of washery water and the prevention of stream pollution. The first field has been studied from many angles, including the use of coagulating and settling agents followed by vacuum filters to remove the solids, and the use of sludge tanks with dewatering screens incorporated therein. In many districts, the disposal of sludges into streams has been stopped by law. The lack of space for impounding sludges has created problems of disposal in other districts. Reduction in moisture means a saving in freight costs as well as the elimination of difficulties in unloading and storing. Excess moisture in coal causes it to freeze in localities where severe climatic conditions pre¬vail. Excess water in coals to be used in the production of coke and manufactured gas has a chilling effect on the walls of the oven or retort. Dryness of coal is important in producing good briquettes.

Jan 1, 1943

By Phillip B. Bucky, R. S. Taborelli

The term "longwall mining" is best known to coal men, although modifications of the method are continually being used in other fields. Longwall mining is of interest today because it makes for greater inechanization and better supervision at the working face, and therefore lower production costs and increased safety. It is an approach to the factory system of production, the high efficiency of which as compared to that in mines is well known. There is available an accumulation of experience regarding this work but coordination of experience is lacking and this series of experiments was undertaken to help serve this purpose. Model experiments were used for reasons of safety, cost and time, and because it has been previously shown1,2,3 that a scalar inodel built of the same material as the prototype will behave in a manner similar to that of the prototype, with time effects the same, if the effective weight of the model is increased in the same proportion as its linear dimenbions are decreased. This is accomplished by substituting a centrifugal for the gravitational field; i.e., placing the model in a centrifuge and controlling the strength of the centrifugal field by varying the rate of rotation. Many factors affect the behavior of the geologic material overlying a bed, therefore results and conclusions contained in this paper apply only to the conditions presented herein. Longwall Mining What Is Longwall Mining?—Agreement should be reached as to what constitutes longwall mining and therefore what constitutes a longwall face. Let longwall mining be defined as the mining procedure in which the roof and overlying bed breaks tend to parallel the working face. In the ordinary stope or room-and-pillar mining the roof breaks tend to

Jan 1, 1938

By Phillip B. Bucky, R. S. Taborelli

The term "longwall mining" is best known to coal men, although modifications of the method are continually being used in other fields. Longwall mining is of interest today because it makes for greater inechanization and better supervision at the working face, and therefore lower production costs and increased safety. It is an approach to the factory system of production, the high efficiency of which as compared to that in mines is well known. There is available an accumulation of experience regarding this work but coordination of experience is lacking and this series of experiments was undertaken to help serve this purpose. Model experiments were used for reasons of safety, cost and time, and because it has been previously shown1,2,3 that a scalar inodel built of the same material as the prototype will behave in a manner similar to that of the prototype, with time effects the same, if the effective weight of the model is increased in the same proportion as its linear dimenbions are decreased. This is accomplished by substituting a centrifugal for the gravitational field; i.e., placing the model in a centrifuge and controlling the strength of the centrifugal field by varying the rate of rotation. Many factors affect the behavior of the geologic material overlying a bed, therefore results and conclusions contained in this paper apply only to the conditions presented herein. Longwall Mining What Is Longwall Mining?—Agreement should be reached as to what constitutes longwall mining and therefore what constitutes a longwall face. Let longwall mining be defined as the mining procedure in which the roof and overlying bed breaks tend to parallel the working face. In the ordinary stope or room-and-pillar mining the roof breaks tend to

Jan 1, 1938

By Donald H. McLaughlin, Reno H. Sales

ADAPTATION to mining needs of the rich store of geologic knowledge concerning mineral deposits and the application of principles of the science to specific problems in the finding, development and stoping of particular ore bodies are the major tasks of the mining geologist. On him to an increasing degree is placed responsibility for estimation of ore and appraisal of mineralized ground, for explicit guidance of exploration and development, and for reliable advice with regard to the many geologic conditions that influence mining operations. In the long continued and steady efforts to meet these requirements, a special skill in close observation, recording, and quantitative interpretation has been developed, particularly by geologists on staffs of mining companies, which in many districts has proved to be effective, not only for technical ends, but also for advancement of scientific understanding. The foundations for mining geologic work were laid in most districts of the West by investigations of the United States Geological Survey. For years they have provided a reliable basis for geologic thought with regard to ore deposits, and later studies have enriched and supplemented rather than superseded them. In very few districts have the geologic relations stated in the earlier papers needed serious modification or revision, in spite of new evidence subsequently made available in abundance by mining exposures. Indeed, one of the chief satisfactions derived from success in mining geologic work is the assurance that it gives of the correctness bf the major concepts of the science of ore formation, established to so large an extent by the leaders of this notable group among whom Lindgren has been so eminent a figure. The geologists of the Survey have given and are continuing to give the service which can properly be expected of the Federal government. Their work, however, though of the greatest value in establishing the broad geological setting,

Jan 1, 1933

By E. H. Roberts, L. G. Swenson, F. C. Nix, R. A. Morgen

The binary system lead-antimony has been the subject of comprehensive investigations in these laboratories by Dean1 and his associates. The effect of a third constituent on this system, particularly on the lead-rich alloys in which dispersion hardening was found, has a commercial value as well as an academic interest. This paper covers the effect of the addition of copper, bismuth and tin, all of which are likely to be found in commercial lead-antimony alloys, and is divided into three parts, as follows: I. The System Lead-A~ili~r~ony-Copper II. The System Lead-Antimony-Bismuth III. The Lead Corner of the System Lead-Antimony-Ti11 These three systerrls are of three different types, and hence may be considered as covering three general kinds of additions. Bismuth forms no compounds with either lead or antimony and forms solid solutions with both. Copper forms several compounds with antimony as well as solid solutions but with lead it forms a two liquid layer system and no appreciable solid solution. Tin is soluble in both lead and antimony in the solid state and also forms a compound with antimony. The effect of small amounts of bismuth on the lead-antimony alloys is small, having no appreciable effect on the solubility of antimony. The temperature of the solidus floor is lowered appreciably by the presence of bismuth, cutting down the range of heat treatment. Copper, on the other hand, due to compound formation, increases the apparent solubility of antimony. The excess antimony is tied up with the copper finally and so is not available for dispersion hardening. The net result of addition of small amounts of copper is to shift the dispersion hardening peak of the

By Augustus Locke

The paper has two parts: the field argument and the microscopic argument. The field argument indicates that either the deep chalcocite has replacea sulfide of extraordinarily easy replaceability or it is hypogene. The microscopic argumentindicates that this sulfide, if it existed, must have been hypogene bornite; that this bornite must so excel known bornite in replaceability as to constitute a new variety; that the existence of this new variety is wholly unsupported by evidence; and that the deep Butte chalcocite is therefore hypogene. IN 1900, when the public first heard of "secondary enrichment" the Butte chalcocite seemed clearly supergene. Mining, through successive regions of leached capping, bonanza sulfide, and sulfide less rich, had paused at lean bottom levels which, though chalcocite-bearing, suggested the waning of copper. The deepest chalcocite, at 1500 ft., was yet too shallow to disturb the supergene hypothesis. But, with deeper mining, lean levels yielded to fat ones. Here and there they showed, within the same vein, an inverted distribution, chalcopyrite above and chalcocite below. To the miners' astonishment, they carried chalcocite, unaffected by cross faults, on an independent course to the depth of 2500 ft. The pattern of ore distribution, hitherto revealed only in fragments, was now appearing in perspective, and, in the depth of the chalcocite, was beginning to make Butte differ from all districts where the chalcocite is indubitably supergene. The idea of hypogene origin at length came into favor; by 1913, when Sales1 advocated this origin, the argument had become a powerful one. This argument rested on field evidence; but, already, there was beginning to emerge microscopic evidence not included in this arugment. Especially pertinent was the proof that (1) The deep chalcocite lies in-mixed with bornite, often microscopic; (2) the deep chalcocite often replaces bornite; and (3) replacement of bornite by chalcocite is accom-

Jan 3, 1924

By E. H. Roberts, L. G. Swenson, F. C. Nix, R. A. Morgen

THE binary system lead-antimony has been the subject of comprehensive investigations in these laboratories by Dean' and his associates. The effect of a third constituent on this system, particularly on the lead-rich alloys in which dispersion hardening was found, has a commercial value as well as an academic interest. This paper covers the effect of the addition of copper, bismuth and tin, all of which are likely to be found in commercial lead-antimony alloys, and is divided into three parts, as follows: I. The System Lead-Antimony-Copper II. The System Lead-Antimony-Bismuth III. The Lead Corner of the System Lead-Antimony-Tin These three systems are of three different types, and hence may be considered as covering three general kinds of additions. Bismuth forms no compounds with either lead or antimony and forms solid solutions with both. Copper forms several compounds with antimony as well as solid solutions but with lead it forms a two liquid layer system and no appreciable solid solution. Tin is soluble in both lead and antimony in the solid state and also forms a compound with antimony. The effect of small amounts of bismuth on the lead-antimony alloys is small, having no appreciable effect on the solubility of antimony. The temperature of the solidus floor is lowered appreciably by the presence of bismuth, cutting down the range of heat treatment. Copper, on the other hand, due to compound formation, increases the apparent solubility of antimony. The excess antimony is tied up with the copper finally and so is not available for dispersion hardening. The net result of addition of small amounts of copper is to shift the dispersion hardening peak of the

Jan 1, 1928

By L. H. Levenson, Charles S. Barrett

Plastic flow in metal crystals and the changes in orientation resulting from it are generally understood to take place by the following fundamental mechanisms: (1) slip on crystallographic planes, (2) homogeneous crystal rotation resulting from the slip, (3) bending of the 1attice between the planes of slip, and, under certain circumstances, (4) twinning. This paper and a preceding one on iron subjected to uniaxial compression1 concern two additional processes that must now be added to this list: (5) the formation of deformation bands, and (6) the bending and rotation of these bands. The present investigation yields a new understanding and definiteness to the common terms so loosely used when speaking of cold-worked metals —('grain fragmentation," "elongated grains," and "deformation twins," "deformation bands," "etch bands," or "X-bands." Bands have been noted on the polished and etched surfaces of cold-worked metals by various investigators for more than 25 years, ‡ yet their nature and their significance have been so little understood that they are not treated in the most comprehensive modern texts on the deformation of crystals. The experiments in this series show that they are one of the fundamental processes in the deformation of metals, of importance in the development of preferred orientations, in work-hardening (since they have the effect of reducing the effective grain size and interfering with slip), and in the recrystallization process. The present experiments were performed on the same stock of material that was used in the earlier compression experiments1—hydrogen-purified mild steel in which the carbon content had been reduced to the limit detectable under the microscope and in which single crystals could be grown by a strain-anneal treatment.2

Jan 1, 1939

By Charles S. Barrett, L. H. Levenson

Plastic flow in metal crystals and the changes in orientation resulting from it are generally understood to take place by the following fundamental mechanisms: (1) slip on crystallographic planes, (2) homogeneous crystal rotation resulting from the slip, (3) bending of the 1attice between the planes of slip, and, under certain circumstances, (4) twinning. This paper and a preceding one on iron subjected to uniaxial compression1 concern two additional processes that must now be added to this list: (5) the formation of deformation bands, and (6) the bending and rotation of these bands. The present investigation yields a new understanding and definiteness to the common terms so loosely used when speaking of cold-worked metals —('grain fragmentation," "elongated grains," and "deformation twins," "deformation bands," "etch bands," or "X-bands." Bands have been noted on the polished and etched surfaces of cold-worked metals by various investigators for more than 25 years, ‡ yet their nature and their significance have been so little understood that they are not treated in the most comprehensive modern texts on the deformation of crystals. The experiments in this series show that they are one of the fundamental processes in the deformation of metals, of importance in the development of preferred orientations, in work-hardening (since they have the effect of reducing the effective grain size and interfering with slip), and in the recrystallization process. The present experiments were performed on the same stock of material that was used in the earlier compression experiments1—hydrogen-purified mild steel in which the carbon content had been reduced to the limit detectable under the microscope and in which single crystals could be grown by a strain-anneal treatment.2

Jan 1, 1939

By Herman Van Fleet, Frederick W. Neil, O&apos

The object of this paper is to describe the present status and possil~ilities of liquid oxygen as an explosive based upon the investigations, research and practical work of the Ingersoll-Rand Co., and of the Air Reduction Co., from early in 1922 to date. The following work was done. 1. A study of the history and physical theory of L. 0. X. as an explosive. (No attempt will be made in this paper to give the history or theory, as this has already been covered by the literature on the subject.) 2. An investigation of the use and the practice with L. 0. X. in the iron mines of Lorraine where L. 0. X. has its largest application in Europe. Although L. 0. X. is extensively employed in the iron mines of Lorraine, many of the mines using it exclusively, and blasting with it a total of approximately three million tons of iron ore per year, the fact that the mining practice in Lorraine1 is to drill comparatively shallow holes and blast only a few holes at a time, renders the data obtained there of very little value in estimating the possibility of replacing dynamite with L. 0. X. in American mining methods. In fact, in the iron mines in Lorraine, L. 0. X. replaced black powder, or its equivalent. 3. Laboratory research work on properties of absorbent materials. 4. Work in the Bureau of Mines explosive laboratory at Pittsburgh, Pa., on the properties of L. 0. 3. cartridges. 5. Practical work underground with L. 0. X. cartridges in the Kitherbee-Sherman iron mines at Mineville, N. Y. 6. Practical work in the quarries of the Calcite Quarry Co., Myers-town, Pa. 7. Practical blasting in several quarries and open-pit mines.

Jan 1, 1927

By W. B. Price

AT the New York meeting of the American Institute of Mining-and Metallurgical Engineers held in February, 1926, W. H. Bassett and J. C. Bradley presented a paper entitled "Exudations on Copper Castings."§ The purpose of the present paper, as the title suggests, is to call attention to somewhat similar phenomena which the authors have encountered in brass and bronze. From a study of the examples given, a more-or-less speculative theory of "inverse segregation" is advanced. PROTUBERANCES ON ADMIRALTY BRASS In the rolling mill of the Scovill Manufacturing Co., there have been found quite commonly bars of certain alloys which had a sort of shaggy roughness on the surface due to slight metallic protuberances. No special attention was paid to these until some bars were found on which these protuberances were heavy enough at the bottom of the bars to produce a blistered appearance. A sample of the protuberances was milled off the surface of the bar illustrated (Fig.. 1a) and upon analysis was found to contain 66.66 percent. copper, 4.02 per cent. tin and .03 . per cent. lead, whereas the average composition of the bar was 70.21 per cent. copper, 1.21 per cent. tin, and .01 per cent. lead. A sample of the shaggy-rough protuberances at the -very top of a bar was also analyzed and was found to contain 2.45 per cent. tin, indicating that it was probably of the same origin as the blistered areas. These results were not entirely unexpected for previous analyses of this alloy had -revealed that the surface was richer in tin than the rest of the bar. This, of course, is contrary to what we would expect from a consideration of the equilibrium diagram and has been called "inverse segregation."

Jan 10, 1926

By Albert Sauveur

This paper explains the possibility of using advantageously a boiling solution of sodium picrate to reveal dendritic segregation in steel. The mechanism of the action of the reagent is described. The failure of manganese alone to produce persistent dendritic segregation is also considered. IRON, like other metals, solidifies through the formation of dendritic crystals; iron alloys forming solid solutions, like other solid solutions, solidify likewise through the formation of dendritic crystals. The alloying elements or impurities as well as the inclusions segregate generally in the interstices, or "fillings," between the axes and branches of the dendrites; that is, in the portions last to solidify. This results in dendritic segregation or heterogeneity, which is generally persistent and makes possible the revelation of the dendritic crystallization of the metal through the selective action of a suitable etching reagent.1 For this purpose, a cupric solution, such as Le Chatelier's, is generally used, copper being deposited on the pure, or relatively pure, ferrite present in the axes while the fillings remain free, or relatively free., from copper deposition. The dendritic structure, formed on solidification in a steel containing 0.50 per cent. carbon, 0.37 per cent. manganese, 0.12 per cent. silicon, 0.07 per cent. sulfur, and 0.035 per cent. phosphorus is shown, after treatment with Le Chatelier reagent, in Fig. 1 under a magnification of 8 diameters. Commercial steel always contains inclusions of manganese sulfide, which are located in the fillings of the dendrites. Comstock has shown that boiling sodium picrate imparts a dark coloration to these inclusions. We find that this reagent likewise reveals dendritic segregations in commercial steel, as shown in Fig. 2, under a magnification of 8 diameters, which represents the same spot as that shown in Fig. 1. The fillings

Jan 2, 1924

By Frederick O?Neil

SCOPE OF THIS REPORT THE object of this paper is to describe the present status and possibilities of liquid oxygen as an explosive based upon the investigations, research and practical work of the Ingersoll-Rand Co., and of the Air Reduction Co., from early in 1922 to date. The following work was done. 1. A study of the history and physical theory of L. 0. X. as an explosive. (No attempt will be made in this paper to give the history or theory, as this has already been covered by the literature on the subject.) 2. An investigation of the use and the practice with L. 0. X. in the iron mines of Lorraine where L. 0. X. has its largest application in Europe. Although L. 0. X. is extensively employed in the; iron mines of Lorraine, many of the mines using it exclusively, and blasting with it a total of approximately three million tons of iron ore per year, the fact that the mining practice in Lorraine1 is to drill comparatively shallow holes and blast only a few holes at a time, renders the data obtained there of very little value in estimating the possibility of replacing dynamite with L. 0. X. in American mining methods. In fact, in the iron mines in Lorraine, L. 0. X. replaced black powder, or its equivalent. 3. Laboratory research work on properties of absorbent materials. 4. Work in the Bureau of Mines explosive laboratory at Pittsburgh, Pa., on the properties of L. 0. X. cartridges. 5. Practical work underground with L. 0. X. cartridges in the Witherbee-Sherman iron mines at Mineville, N. Y. 6. Practical work in the quarries of the Calcite Quarry Co., Myers-town, Pa. 7. Practical blasting in several quarries and open-pit mines.

Jan 2, 1926