Search Documents

By O. N. Carlson, D. G. Alexander

THE hardness anisotropy of metals and alloys has been of increasing interest in recent years but silicon ferrite,1 niobium,2 and tungsten3,4 are the only bcc metals about which this type of information has been reported. This investigation was carried out on vanadium and chromium single crystals in an effort to determine to what degree the hardness variations observed in these metals are due to orientation effects and to compare their behavior with other bcc metals. In earlier work the authors had observed a small angular dependence in the Diamond Pyramid Hardness of single crystalline vanadium on the (100) plane but no anisotropic effects were noted on either the (110) or (111) planes. At the suggestion of R. G. wheeler5 it was decided to investigate this effect in greater detail using the more asymmetric Knoop indentor. The vanadium metal used in the study was prepared by the aluminothermic reduction of V2O5 followed by electron beam melting.6 The principal analyzed impurities were 230 ppm C, 230 ppm O, 65 ppm N, 90 pprn Al, Cr not detected, 50 ppm Fe, 60 ppm Ni, and 200 ppm Si. The chromium was an iodide-refined product obtained from the Chromalloy Corporation. Analysis of this material showed the following amounts of impurities present: 10 ppm C, 9 ppm O, 2 ppm N, 0.4 ppm H, 3 ppm Al, 2 ppm Ca, 2 ppm Cu, 20 ppm Fe, 1 ppm Mg, 0.3 ppm Mn, 1 ppm Mo, 3 ppm Ni, 10 ppm Si, and 1 ppm V. Single crystals of both metals about 1 cm in diam and 10 cm in length were grown by an arc-zone melt- ing technique.7 The chromium crystal was annealed at 1600°C for 6 hr in a purified argon atmosphere to remove any strains or inhomogeneities, but the vanadium was tested in the as-grown condition. The crystals were oriented by the Laue back-reflection method and then sectioned with a spark cutter into individual specimens with a (loo), (110), or (111) plane parallel to the crystal surface. They were mounted in Lucite and carefully ground to a flat surface. The vanadium specimens were then electropolished in a 6 pct perchloric acid-methanol mixture while the chromium specimens were mechanically polished on a Syntron vibratory polisher using an alumina abrasive. The orientation of each crystal was then rechecked by the back-reflection X-ray method. All of them were found to lie within 2 deg of the desired orientation with the exception of the (110)-Oriented chromium crystal which was within 4 deg. Microhardness impressions were taken at 10 deg intervals from the common (110) direction by rotating the crystal in the plane of the crystal surface. A Knoop indentor was used with a 400-g load on the vanadium crystals and an 800-g load on the chromium. The hardness values are averages of 6 impressions and standard deviations were calculated for each set of data. The values reported for the (111) plane of vanadium are based on from 10 to 15 measurements for each point. The microhardness results for vanadium and chromium are plotted as a function of the angular rotation of the long axis of a Knoop indentor from the (110)

Jan 1, 1970

By L. C. Armstrong

Twice in the past two years and in two widely separated localities—ane near Williamsville, Mo., and the other in the Allard Lake district of Quebec— the Contract Drilling Division of the Longyear Company has experienced perplexing difficulties in drilling granitoid igneous rocks. The rocks in both places are characterized by appreciable amounts of feldspar intimately inter-grown with quartz particles of microscopic dimensions. The disappointingly slow rate of advance and the exceptionally high bortz loss, obtaining during the life of these two projects, are ascribed largely to the resistance to abrasion of these two minerals when arranged in this intergrown pattern. Whether all intergrowth-bearing igneous rocks would offer extraordinary resistance to bit progress cannot be stated with assurance on the strength of these experiences alone. More data on diamond drilling this sort of material in a number of localities are needed before any generalizations can be made safely. It should be pointed out that the lack of time and funds made it impossible for the writer, or other persons interested in correlating the details of bit histories with the kinds of rocks drilled, to be present during the performance of the contracts. However, the records kept in the normal course of drilling are deemed complete enough to be reportworthy. This information is presented here together with the findings made in studies of the rocks involved, with the thought that it may attract the comments of others who may have encountered similar refractory drilling conditions. A pooling of knowledge on the problem would be of material aid in devising more efficient cutting tools and procedures for penetrating this kind of rock. Drilling Blastholes in the Williamsville Granite Due to the unsatisfactory perform- ance of pneumatic percussion drills in boring blastholes on a construction contract near Williamsville, Mo., tests were made with a diamond drill. The poor progress achieved and the excessive loss of diamonds, however, soon led to the abandonment of these trials. The diamonds, in all of the bits tried, lost their cutting edges and acquired a polish after being in service for distances ranging from a few inches to a few feet. Coring bits containing surface-set, whole-stone bortz in a tungsten powder matrix were employed. The cost assignable to bortz wear averaged $7.17 per foot. This item of expense is several times the amount normally expended in diamond drilling in firm, unfractured, granitic rocks. Diamond-impregnated, tungsten carbide bits also were used without success. The diamond wear was at the rate of $0.98 per foot, but the diamond chips became too polished for further duty in less than a foot of drilling. The Williamsville granite is pink and medium-grained. In the hand specimen, it has a fresh, sound appearance; it is seemingly composed almost entirely of interlocking grains of feldspar and quartz and has no discernible features suggesting a greater durability than is usually found in rocks with this composition and texture. Microscopic examination, however, reveals a predominance of feldspar grains with more or less regularly distributed and sharply angular masses of quartz (see Fig 1). The pattern assumed by the two minerals in this mode of occurrence is referred to as a "graphic intergrowth," as it bears some resemblance to the cuneiform characters of ancient Persian writing. The other principal constituents are quartz-free feldspars (microcline and orthoclase) and quartz. All of these constituents are in nearly equidimensional grains, ranging up to about 3 mm in length. There are also

Jan 1, 1950

By J. L. Martin, W. M. Campbell

A new electric logging method, called displacement logging, often gives a direct indication of the presence of mobile hydrocarbons in hydrocarbon-bearing formations. This method is based on the detection of a bank of connate water which is formed between the invading mud filtrate and virgin formation fluids in these cases. The existence of this phenomenon has beer, verified by laboratory studies and by actual field logs taken in known oil sands. INTRODUCTION During the past decade increasing use has been made of conventional electric logs to determine the amount of oil or gas in formations traversed by a borehole. This determination requires knowledge of several factors, such as true resistivity of the formation, formation factor, and water resistivity. Sometimes all of the factors necessary to make a reliable saturation calculation are not available. Also, the computations and corrections which are necessary in such a study often require the services of an experienced log analyst. It has long been the desire of exploration people to have a logging device which will locate hydrocarbon-bearing formations directly without requiring complex interpretation methods. The displacement log, while not completely fulfilling this desire, appears to be a Step in that direction. Basis for the Device The basis for this device stems from a phenomenon which occurs when mud filtrate invades a formation which contains displaceable hydrocarbons. As the mud filtrate invades the formation, most of the oil or gas is pushed out of the invaded zone, leaving residual oil. However, in addition to displacing most of the oil or gas, the connate water is also swept out, since the originally irreducible water is mobile in the presence of a water phase.1,2,3 Tonsequently, this irreducible water piles up as a bank between the virgin oil zone and the invading filtrate. If the mud filtrate is of higher resistivity than the formation water— as is commonly the case—the resulting annular zone, containing the bank of formation water, will be of lower resistivity than either the virgin oil-bearing formation resistivity or the invaded zone resistivity. This resistivity configuration, going from high to low to high again as the distance from the borehole increases, is found only in those zones which contain displaceable hydrocarbons. A device which would reliably detect this low resistivity zone would give a direct indication of mobile hydrocarbons. Illustrations This phenomenon is illustrated in Fig. 1 and 2. Fig. 1 shows a sketch of a zone containing salty connate water plus displaceable hydrocarbons, along with graphs showing fluid content and electrical resistivity vs distance from the borehole, before invasion occurs. Fig. 2 shows this zone, together with fluid content and resistivity graphs. after invasion by a fresh water mud. The resistivity pattern on moving away from the borehole is high: low: high. The absence of the low zone phenomenon in water zones is illustrated in Fig. 3 and 4. Fig. 3 shows a sketch of a zone containing salty formation water and residual oil, along with graphs showing fluid content and electrical resistivity vs distance from the borehole, before invasion occurs. Fig. 4 shows this water zone, together with fluid content and resistivity graphs, after invasion bv a fresh water mud. In this case the resistivity pattern on moving away from the borehole is high: low since there is no change in water saturation at the head ol

Jan 1, 1956

By P. R. Sperry, P. A. Beck, Hsun Hu

As described by means of quantitative pole figures, the inside texture of highly rolled aluminum and copper strips may be approximately described by four equivalent ideal orientations near (123) [121]. If rolled in reversed passes, the surface texture of copper is also near (123) [121], that of aluminum is (100) [011]. The inside texture of highly rolled brass is (110) [112]. The surface texture is the same, if rolled in reversed passes. The surface texture of all three metals is related to the inside texture, but asymmetrical, if rolled without reversal between passes. MANY previous investigations dealing with the subject of the present work were reviewed by Wassermann.1 Barrett,2 Brick,3 and Richards.' The recent introduction of quantitative methods for pole figure determination by Decker, Asp, and Harker,5 Schulz5 and others made it possible to reinvestigate some of the finer points which the earlier more qualitative photographic methods left undecided. The rolling textures of silver and of 70-30 cartridge brass have been quite consistently characterized by the ideal orientation of (110) parallel to the plane of rolling and [112] parallel to the rolling direction. On the other hand, it has been recognized by several investigators that certain other face-centered cubic metals, such as copper and aluminum, developed rolling textures rather different from that of brass. These textures have been variously described by the following ideal orientations, singly or in combinations with each other: (110 [112]: (112) [111]; (135) [335]; (135) [211], etc. The discrepancies usually have been attributed to the lack of sharpness in the textures and to the attendant difficulty of associating "ideal orientations" with pole figures showing great scatter of orientations. It seemed desirable to investigate by the new quantitative methods to what extent the apparent lack of sharpness may have been brought about by the qualitative methods used previously, rather than by the textures themselves, and to decide, if possible. between the various ideal orientations which have been proposed. Another problem, not satisfactorily settled by earlier investigations. concerns surface textures in rolled metals. For instance, in rolled aluminum the surface texture in some cases appeared to be similar to the texture inside the sheet, whereas in other cases it was reported to be entirely different.' The conditions under which such differences may have arisen, and the possibility of the occurrence of different surface textures in other face-centered cubic metals do not appear to have been examined in detail. The present work was undertaken to investigate the above questions. Some of the results obtained have been described- riefly. Experimental Procedure Specimen Preparation: In the present investigation 2s aluminum, electrolytic tough-pitch copper, and commercial 70-30 brass were used. These materials were available in the form of cold-drawn rods. 1 in. diam for tough-pitch copper and commercial 70-30 brass and 11/2 in. diam for 2s aluminum. The cold-drawn bars were alternately annealed and rolled 30 pct lengthwise in several cycles until a penultimate thickness of 0.500 in. was reached. The intermediate and the penultimate anneals were carried out for 30 min at 380°C with 2s aluminum, and for 30 min at 550°C with 70-30 brass. For tough-pitch copper, the intermediate anneals were 30 min

Jan 1, 1953

By Robert C. Collins, Clifford L. Jewett

The development and production of artificially colored roofing granules have been key factors in the success of the asphalt roofing industry. They provide protection for the asphalt from solar radiation and satisfy the home-owner's desire for a wide range of attractive colors. As a result, the asphalt shingle has become the most commonly used roofing material today. In addition to providing a stimulus to the asphalt roofing industry, artificial methods of coloring granules completely changed the nature of granule production from one of quarrying, crushing, and screening to a complex technical operation. Today's roofing granules are the result of many years of research, and they are produced in modern plants to exact specifications. History Asphalt roofing materials available today are the product of a long evolution of technological development. Forerunners of the present bituminous products, appearing as early as 1780, were primitive constructions of burlap saturated with crude tar or pitch. An early improvement to this basic effort was the dusting of talc, mica, or other finely ground material on the coated surfaces to keep the roofing from sticking to itself in storage. At times some pigmentation was added with the dusting material for initial color, but this was far from satisfactory. In fact, this early product possessed none of the qualifications of a good roof surfacing material. It was not economical; it was difficult to handle and apply; it was not attractive; it provided no resistance to fire; and it would not withstand the elements as well as other products then in use. Methods and machines were soon devised to saturate endless webs of felt with asphalt from the fast-growing petroleum industry. Even though saturated felt became available, this product of rags and wood fiber had almost the same limitations as burlap and tar. Even with heavier coatings of asphalt applied to both sides of the sheet for rigidity and longer life, the product still lacked color and fire resistance. Further, it was found that constant exposure to the sun soon caused the asphalt to become brittle, and it eventually cracked and leaked. This led to the first important use for crushed mineral products on asphalt-coated shingles and provided the key to the subsequent growth of the asphalt roofing industry. When a layer of crushed mineral was embedded in the surface exposed to the weather, the asphalt coating was protected from ultraviolet light and retained its elasticity over a much longer period of time. In addition to this protection, the mineral surfacing provided some resistance to fire. Fire resistance in the past had been found only in the expensive slate or tile roofs and the unattractive and expensive metal roof coverings which were then available. The most common mineral granule applied to the early asphalt roofing products as they began to make their first significant advances after 1900 was screened waste from slate quarries. Slate granules being available in dull shades of red, green, black, purple and a few other miscellaneous colors did provide a degree of color. Since slate has a flat platelike cleavage, it provides a cheap protective cover for the asphalt-coated sheets. Records show that coarse slate screenings were used for asphalt roofing as early as 1906. As the asphalt roofing industry developed, many other natural colored rocks and minerals were used to coat the surfaces of the roofing. The list included silica

Jan 1, 1975

By M. H. Pilkuhn, H. Rupprecht

p layers on n-type substrates of GaAs were prepared by difhsion of zinc into these substrates. Experimental details about the diffusion technique will be presented. It will be shown that inhomogeneity in the substrate doping level and crystal shucture defects cause nonplanarity in the junction plane. These nonplanarities give rise to high threshold current densities. From incremental sheet-conductivity measurements the zinc profile is derived. Data about surface concentration and gradient of the zinc concentration at the junction are presented. Finally, some results of laser diodes, which were made of wafers with extremely planar diffusion fronts, are discussed. ThE investigations reported here are part of a program concerned with the materials aspect in the fabrication of GaAs laser diodes. This includes studies of the influence of crystal defects introduced both during the growth of the crystal and as a consequence of subsequent diffusion. Compared with the progress made in the investigation of structure defects, for instance by X-ray microscopy in materials like silicon, no similar results are known so far for the case of GaAs. The further progress in laser diodes will depend very much upon our knowledge of these structure defects and subsequently upon our ability to avoid them. Laser diodes of GaAs had been made mostly by diffusing an acceptor impurity, normally zinc, into an n-type substrate. This procedure was found more convenient than the inverse one for various technical reasons. We will follow this line and restrict ourselves to zinc diffusion only in this paper. DIFFUSION TECHNIQUES AND EXPERIMENTAL DETAIL In order to set a refgrence for our experiments, we used a standard procedure for the diffusion runs. The diffusions were carried out in a sealed quartz tube for 2-1/2 hr at 850°C. One milligram zinc arsenide (ZnAsz) per cu cm of the tube volume served as zinc source. Under these conditions the junction depth was between 25 and 30 p. It is assumed, according to the investigations of the zinc arsenide system by V. Lyons and V. ilvestri,' that ZnAs2 dissociates completely at 850°C into ZnsAsz and Asg. Since there is a condensed phase of ZnsAs2 in the tube at 850°C, the partial pressure of zinc is controlled by the pressure of the arsenic formed by the dissociation of ZnAs2. Due to the fact that the zinc partial pressure resulting from the dissociation of ZnsAsz is only a weak function of the partial pressure of arsenic, the amount of the initial ZnAs2 is not very critical. Experimentally, we found that the junction depth, as well as the surface concentration, was practically the same, if the ingots of ZnAs2 varied between 0.2 and 5.0 mg per cu cm. The wafers were oriented with the main faces in (100). Surface damage due to cutting and lapping was removed by a chemical-etch treatment in a rotating beaker (etch solution: HzSOr, H202, and HzO in a ratio 3:l:l). The GaAs substrate material was n type and doped with tellurium, selenium, silicon, or germanium. It was grown by means of horizontal or Czochralski techniques. After the diffusion process, junction depth and planarity were checked either by grooving with a

Jan 1, 1964

By David C. N. Cockburn

INTRODUCTION This paper analyses certain of the financial considerations which will commonly apply in relation to the following questions: - what equity structure or project vehicle should be adopted for the exploration and/or exploitation of a project by more than one unrelated participant? - what vehicle should be adopted by a participant for its participation in a multiparty project? Due to local, politically motivated laws in certain jurisdictions, or due to the overriding requirements of a dominant participant, there may be little choice of the underlying multiparty structure which may be adopted for the exploration, appraisal and/or development phases of a project. Nevertheless, even in such circumstances, attention should be given, at least in the preparation of the related documentation, or in considering methods of participating or funding the project, to certain of the points discussed below. This discussion of financial considerations in the context of the more commonly adopted multiparty structures concentrates primarily on fiscal, financial accounting, financing and funding aspects. TYPES OF PROJECT VEHICLE FOR MULTIPARTY INTERESTS The well known types of vehicle adopted for the participation in a project by more than one participant (assuming that the participants are effectively unrelated) are as follows. Joint Venture (unincorporated joint venture) By far the most commonly adopted structure for mining ventures, a joint venture is usually defined and documented in terms to distinguish it from a partnership for important tax and legal reasons. In essence, this is a contractual association of more than one participant to carry out a specific commercial project or purpose. The relationship between the separate participants and their respective rights, interests, obligations and liabilities are agreed between the participants in one or more contracts (viz Joint Venture Agreements or Joint Operating Agreements together with ancillary documentation). Unlike other project vehicles of participation, in most jurisdictions there is no specific body of law governing joint ventures. The participants thus enjoy contractual freedom to negotiate whatever deal they may wish between themselves. Jointly-Owned Project Company (corporate joint venture) A very familiar vehicle, this is a separate and distinct legal and tax entity incorporated under the company laws of the place of incorporation to undertake specific objects, and granted specific powers, in relation to the Project. Although certain rights, interests and obligations may be circumscribed in the governing corporate instruments by the promoter participants, the corporation laws of the relevant place of incorporation, and the selection of such governing laws (assuming freedom of choice) and future political changes in such corporate laws, should be carefully considered. The use of a company in a multiparty structure may be peripheral to the project itself as a specific purpose vehicle (for example, a joint sales agent or marketing company or a joint borrowing vehicle) or it may form a central function such as in the case of a tolling company which will own the project for legal and taxation purposes and raise financing with the backing of the shareholder participants commonly by the adoption of take-off, throughput and/or user agreements. Partnership This is a legal relationship, subject to the often wide-sweeping restrictions of the relevant local partnership laws, under which the participants have agreed to carry on a business venture together with a view to profit. The effect of the relevant partnership laws, as well as the various types of partnerships and the

Jan 1, 1985

By C. H. Li, J. Washburn, E. R. Parker

Yield stress in single crystals of zinc was shown to be dependent on prior annealing temperature and rate of cooling after annealing. Rate of strain hardening beyond the yield was not sensitive to annealing procedure. A tentative mechanism for the effect was discussed. COMPARATIVE mechanical tests of metal single crystals generally show a large scatter of results. Many factors may contribute to this variation. The present investigation was undertaken to evaluate the influence of two factors not ordinarily considered of major importance—annealing temperature and cooling rate after annealing. Since plastic properties of crystals are thought to depend on the presence of lattice imperfections, it follows that a variation in properties should result from differences in the distribution and density of these imperfections. Furthermore, in the light of current theories of interaction between edge dislocations and lattice vacancies,' it seems possible that annealing temperature and subsequent rate of cooling might play a part in this distribution. Analysis of the effect of these variables on plastic properties may lead to a better understanding of the annealed state. Single crystals of zinc which have been strained in simple shear undergo complete recovery of mechanical properties upon subsequent annealing. This behavior is useful because a single specimen can be used repeatedly, thus eliminating the uncontrollable variables introduced by the use of many crystals. The test section of the crystals used for these experiments was a cylinder 1/8 in. thick with a cross-sectional area of about 1/3 sq in. The specimens were acid-machined from spherical single crystals 1 in. in diameter in such a way that the slip plane (0001) was at right angles to the axis of the cylinder. In testing, a shear stress was applied along one of the slip directions, [2110] in the (0001) plane.' All crystals, unless otherwise noted, were grown in a helium atmosphere from molten 99.99 pct pure Horse Head Special Zinc. Fig. 1 is a family of curves obtained from one crystal. Each curve was obtained by deforming the crystal to 10 pct strain at a rate of 3 pct per min, following an anneal of 1 hr at 260°C. The strain direction was reversed every other time so that no progressive change in shape of the specimen took place during the series of tests. Since the stress-strain curve was reproducible within a fairly narrow range under the same conditions of annealing, it was then possible to determine the effect of changes in annealing conditions. A crystal was tested repeatedly as previously described but the annealing temperature and rate of cooling preceding each test were varied (Fig. 2). Two cooling rates were used, approximately 30°C per min and 3°C per min. Annealing was conducted at three temperatures, 200°, 300°, and 400°C. For a given annealing time and rate of cooling the room temperature flow stress was higher the higher the annealing temperature. The increase in flow stress was small as the annealing temperature was increased from 200° to 300°C but rose rapidly when the annealing temperature was raised from 300" to 400°C. Faster cooling from the high temperature produced an even greater strengthening of the crystal. The curves were obtained in the order indicated by the numbers. The stress level associated with a certain annealing treatment was, within the limits of scatter, always the same regardless of the

Jan 1, 1954

By J. J. Mulligan

Introduction Coal is found in every major geographic region through-out Alaska and in two offshore areas. Since about 1852, more than 100 small mines have opened and closed. In 1981 and 1982 production was almost entirely from one mine in central Alaska. Clearly, the utilization of Alaska's abundant coal resources presents political, economic, and technical problems that are far from solution. Location and Physical Features Figure 1 illustrates the geographical and geological similarity between Alaska and the western US. Alaska's Arctic region generally resembles Wyoming and the Dakotas. The Brooks Range is an extension of the Rocky Mountains. The central region of Alaska between the Brooks Range and the Alaska Range bears a general resemblance to the basin and range country of the western US. The southcentral and southeastern regions have a similar resemblance to the Sierra Nevadas and the West Coast. The Arctic, the central, and the southcentral regions have major coal fields. The southeast region has scattered occurrences. The topographic, climatic, and economic characteristics of each are different. These differences have a large effect on practical mining methods. Description of Alaskan Coal Coal deposits known in Alaska are almost all of Cretaceous or Tertiary age, much younger than the Carboniferous coal deposits of eastern and midwestern states. Consequently, most Alaskan coals have a higher moisture content and a lower heat value. Most Alaskan coals also have a much lower sulfur content. Low volatile bituminous, and anthracite coals occur in Alaska, but most Alaskan coals range downward in rank from high volatile bituminous to subbituminous and lignite. Alaskan coals are similar to coals of the northern Great Plains and the Rocky Mountains. Arctic Region Northern Alaska Coal Fields Northern Alaska coal fields are by far the largest group of coal deposits in Alaska (Fig. 2). Coal-bearing rocks extend from the foothills of the Brooks Range about 160 km (100 miles) northward to within about 80 km (50 miles) of the Arctic coast. The principal known occurrences are between the Colville River and the western coast. However, coal has been found eastward almost to the Canning River and westward under the Arctic Ocean. The northern Alaska coal fields are in a series of Cretaceous rocks that suggest a deltaic depositional environment. The beds tend to occur in series of up to eight or nine beds totaling 6-9 m (20-30 ft) of coal. However, beds 6-12 m (20-40 ft) thick have been reported, and beds 1-3 m (3-10 ft) thick seem to be relatively common. Including thin seams, coal in some places makes up about 10% of the stratigraphic section. However, no area has been explored in sufficient detail to block out any large body of reserves or to make reliable estimates of the total resource. Observation points in drill holes and along river and stream banks are few and far between. Coals in northern Alaskan fields tend to range in rank from bituminous, where moderately folded and faulted in the foothills, to subbittuminous in the gently folded rocks under the coastal plain. Coals toward the eastern extremities of the coal fields may be of Tertiary age and lower in rank, but the same general correlation between degree of folding and increase in rank can be expected. Some higher rank coals in the foothills belt are known to have coking properties but most, and possibly all, require

Jan 1, 1984

By N. J. Grant, C. F. Flo, F. B. Cuff

An investigation of the Ti-Cr system has shown the presence of a complete series of solid solutions in the ß phase, with a minimum in the solid us near 50 pct Cr. An intermetallic compound, TiCr2, forms during cooling from the ß solid solution. There is a eutectoid reaction at the low chromium side of the system. IN view of the recognition of the potentialities of titanium and its alloys as important structural materials there has arisen a need for a systematic investigation of various titanium binary diagrams. Of these, the Ti-Cr system was of particular interest because of the improved properties imparted to titanium by small chromium additions. A literature survey disclosed a partial constitution diagram that had been suggested by Vogel and Wenderott,¹ This diagram, shown in Fig. 1, is the result of work done on the Fe-Cr-Ti ternary system. Alloys containing less than 43 pct Cr were not investigated. In addition to this, a study of alloys in the Ti-Cr system was reported by McPherson and Fontana.² Adenstedt3 furnished a number of dilato-meter curves obtained from specimens containing 5, 10, and 15 pct Cr. Very recently, McQuillan4 submitted a proposed diagram covering the complete range of compositions between titanium and chromium. This diagram was in general agreement with the one described here. Experimental Procedure Sponge titanium (99.7 pct) and electrolytic chromium (Bureau of Mines analysis: 99.03 pct Cr, 0.40 pct Fe, 0.53 pct O2) were used for the initial determination of the system. Subsequent refinement of points, particularly for the low chromium side of the diagram, was accomplished by using iodide titanium and high purity chromium (National Research Corp. analysis: 0.050 pct C, 0.045 pct O2). The Ti-Cr alloys were prepared by melting 25 g charges in an enclosed, water-cooled copper crucible using a movable tungsten electrode. The atmosphere was helium, prepurified by first passing it through a drying agent and then through sponge titanium heated to 850°C. Particular care was taken to avoid any large scale segregation resulting from insufficient mixing of the components. Each charge was melted and kept molten for approximately 1 min, allowed to cool, inverted, remelted, and kept molten for an additional minute. In order to ascertain the amount of impurity pickup (oxygen and nitrogen) during the melting procedure, three iodide titanium specimens were melted in sequence and then checked for increased hardness. The specimens in the as-cast condition showed a relatively large hardness increase over the hardness of the as-received iodide titanium. The scattering on these readings was large. However, after the specimens had been homogenized at 840 °C for 2 hr and slowly cooled, the measured increase in hardness over the as-received titanium was small with a corresponding decrease in scatter. The reason for this hardness change is that in heat treating these specimens below the transformation temperature (885°C) there was a conversion from the as-cast structure to the more nearly equilibrium structure of the annealed specimen. The alloys were analyzed for chromium content and although the actual percentage was invariably low the deviation from the nominal composition never exceeded 0.6 pct Cr.

Jan 1, 1953

By H. C. Rogers, B. W. Roberts

Vanadium foils and wires, either cold-worked or recrystallized, show a ductile-brittle-ductile fracture sequence with temperature. At about 150°C the hydrogenated vanadium wires are found to be ductile. At room temperature the wires show brittle fracture, and at liquid nitrogen temperature the wires are again ductile, although to a lesser extent than found at 150°C. Hydrogenated cold-rolled vanadium foils have been found to fracture in unusually straight lines along the [100] texture directions. The hydrogen content required to show this [loo] texture fracture is limited to a few atomic percent in range. Hydrogen content above this range causes fracture to occur in random directions. PRELIMINARY experiments with hydrogenated vanadium foils indicated that the embrittling effect of the hydrogen on the vanadium, which was severe at room temperature, was reduced at both lower and higher temperatures. In order to investigate more quantitatively the ductility changes with temperature, vanadium wires were tested in tension at three temperatures. The reduction of area was measured and the fractures examined. Specimen Preparation—The material used was kindly supplied by A. U. Seyboltl in the form of M-in. rod. The nominal analysis was: 99.2 pct V assay, 0.2 pct C, 0.01 pct Si, 0.01 pct Fe, 0.015 pct Ca, 0.02 pct O,, 0.01 pct N2, and 0.003 pct H,. The specimens were 0.035-in. diam wires. These were prepared by cold-swaging the supplied rod to the final diameter without intermediate anneal. They were finished with long-bearing dies. The surface was then given a light polishing with 0 emery paper and degreased in trichlorethylene. An X-ray check indicated that the cold-swaged wire had a fairly strong [110] fiber texture. The wires were then recrystallized in vacuum in continuously pumped quartz tubes at two temperatures to give two different grain sizes. One group of wires was given 45 min at 800°C; another, 60 min at 1000°C. The microstructures in Fig. 1 show the wires after they have been electropolished and elec-troetched in 10 pct HCI. After the 800°C anneal, the vanadium grains had a diameter of 1 to 2p and there appeared to be a tendency to elongation in the longitudinal direction. However, the latter may be an etching effect. After the 1000°C anneal, the grains appeared to be equi-axed, but there was a very large spread in grain size, probably due to some impurity segregation in the wire, Fig. 1, right. The grain diameters varied between the limits of 1 to 150p. The small particles shown particularly clearly in Fig. 1, left, are also visible on the polished surface of all samples before etching and are undoubtedly carbides and nitrides of vanadium. An X-ray check indicated these annealed wires had a strong [110} recrystallization fiber texture. The hydrogenation was carried out in an iron retort with dry hydrogen flowing through it, the retort and contents being heated in a tube furnace with a hydrogen atmosphere. The hydrogenation temperature was approximately 500°C. The hydro-genation times chosen were approximately those which would be just enough to cause the vanadium to be brittle at room temperature and thus allow the greatest chance for ductility to occur at the other two temperatures. Part of the fine grained specimens were hydrogenated for 21/2 min at 490°C. Part of the coarse grained specimens were hydro-genated for 11/2 min at 515°C.

Jan 1, 1957

By John R. Keith

Lead and zinc contents of elm, maple, and oak trees and of soils in which the trees grew were determined in samples from the Upper Mississippi Valley mining district, and from an area outside but contiguous to the district. The lead and zinc analyses of plant materials served to differentiate the mineralized and nonminer-alized areas. Stems contained about two times as much lead and about two to five times as much zinc as did leaves taken from the same stems. Lead and zinc analyses of all soil horizons could be used to differentiate between the two areas. Soils at most sample sites in the mineralized district seemed to be more reliable than plants for geochemical prospecting and are a more practical sampling medium. Soil samples from areas with thick loess cover, however, failed to indicate the presence of mineralized bodies whereas tree samples from the same sites contained anomalous amounts of lead and zinc. It is suggested that in areas of thick loess cover, plant samples could be used in prospecting for lead and zinc. The important part that plants play in the cycling of elements through the soil horizons is well-known. The concentration of elements in the upper soil horizons by the action of plants has been called the Goldschmidt enrichment principle.' The fact that plant species vary greatly in their ability to concentrate particular elements in their tissues is also well-known.' Agricultural literature has dealt extensively with relationships of the major nutritive elements in soils and plants3 The extent, however, to which plant actions cycle the minor nutritive and the nonmetabolic elements in the soil has not been adequately investigated. Lead is non-nutritive and toxic to plants, whereas zinc is a micronutrient in low, but toxic in high, concentrations.4 This report presents the results of a biogeochemical study concerned with the amounts of lead and zinc in some plants and soils that occurred both within and adjacent to the Upper Mississippi Valley lead-zinc district. Field work for this study was done in the summers of 1961 and 1962. SAMPLE TARGETS AND CHEMICAL ANALYSES Geologic and physiographic descriptions of' the district have been made by Heyl 5 and several other authors in a series of U.S. Geological Survey (USGS) reports and quadrangle maps.6-I Sedimentary rocks, mostly dolomite, limestone, shale, and sandstone, of Cambrian, Ordovician, and Silurian age predominate in the area. Mineral deposits are of the vein and cavity-fill type; the principal ore minerals are galena and sphalerite. Vegetation of the area was characterized by Curtis1 6 as southern hardwood forest interspersed with patches of oak savanna and prairie. Plant genera typical of the eastern United States Temperate Zone, including ash, cherry, dogwood, elm, hackberry, hickory, maple, oak, and other woody and herbaceous genera, are present. The natural vegetation has been greatly modified by agricultural, logging, and mining operations. The species of the original flora are present, but not in their former relative abundance. Soils of this district belong, for the most part, to the Brunizem and Gray-Brown Podzolic great soil groups. The Brunizems are the soils developed under prairie vegetation.'' The Gray-Brown Podzolics are the soils developed under deciduous forests,18 They are derived from both bedrock and from loess parent materials, and

Jan 1, 1970

By F. W. Luersson

High carbon, low phosphorus steel can now be made from pig iron containing 0.7 pct P or more, in a commercial sized open hearth furnace. No external heat is required for refining, and steel produced is identical with basic open hearth steel. THE classical Thomas process, which requires liquid pig iron containing over 11/2 pct P, yields a product relatively high in phosphorzs and nitrogen. Unless large quantities of recarburizers are added to the refined steel, the product is low in carbon content. Thus, the Thomas process is not well suited to American raw materials, and its product is often not acceptable according to the standards set by American industry. The shortcomings of the Thomas process have long been recognized; with the advent of low cost oxygen, studies were initiated to develop pneumatic processes which would conceivably overcome the inherent objections to Thomas steelmaking. Several such modified basic pneumatic processes have been tested experimentally in commercial trials during the past decade. Probably the most widely publicized of these developments has been the oxygen converter process as practiced in Austrial,2 and in Canada.8 n this process, oxygen is substituted for air and introduced above the liquid bath in order to increase the heat available to the metallurgical system. This avoids the need for high phosphorus raw materials and gives a product low in nitrogen. In this process, the phosphorus content in the final product depends, to a considerable extent, on the total amount of that element in the burden. The rotary furnace4 which is now in commercial operation at Domnarvet Steelworks, Sweden, is producing low phosphorus steel from iron containing 1.8 to 2 pct P. One or more early slags are removed and by this means high carbon steels of open hearth quality can be produced. At this stage of development there is some question as to the applicability of the rotary process to large heats. Another development has been the use of oxygen in combination with either steam6 or carbon dioxide yn the basic bessemer, thus avoiding the introduction of nitrogen gas into the refining system and giving a product relatively low in nitrogen content. A double slag process has been used in Europe7 in conjunction with a regular Thomas converter, by means of which it is possible to obtain a phosphorus content in the product approaching that obtained in basic open hearth steels. The Turbo-Hearth process:' which uses the side blowing principle so as to produce low nitrogen steel from normal American pig irons, has been developed experimentally in this country. A process fitted to U. S. raw materials All of the preceding processes, with the exception of the rotary furnace, suffer from the common shortcoming that they cannot be adapted to the production of high-carbon, low-phosphorus steels unless large proportions of recarburizers are added. In 1947, a program was initiated by the Inland Steel Company1' to study an oxygen steelmaking process specifically designed to utilize the full range of phosphorus analyses encountered in American pig irons and to give finai products with phosphorus and nitrogen contents comparable to steel produced by the basic open hearth process. Some of the objectives of the proposed process are: 1) the process should be able to accommodate molten pig iron conta;rl;rrg up to 1 pct P., 2) sne process should be subject to close control of carbon analysis, 3) the process should be capable of producing high carbon

Jan 1, 1958

By J. B. Dorsey, T. W. Brinkley

Performance of a high-pressure, vaporizing gas-drive project in a volatile oil reservoir is discussed. The project has been in operation for over 8 years. Present recovery from the over-all displaced portion of the reservoir is 40 percent, and an ultimate recovery of 60 percent is indicated. Calculations reflect an over-all displacement volume of 50 percent for the entire reservoir; therefore, ultimate oil recovery will be 30 percent of the entire reservoir oil originally in place. Laboratory vaporization tests conducted prior to project initiation also are presented and discussed, along with an analytical method of determining stock-tank oil production and gar injection requirements related to over-all volumetric displacement efficiency from these data. Introduction The Shoats Creek field is located in Beauregard Parish, La., in the extreme western part of the state (Fig. 1). Discovered in 1956, the field is productive in three Cockfield sand zones, ranging in depth from 8,000 to 9.000 ft. The upper two zones, 1st and 2nd Cockfield, are condensate-bearing gas reservoirs. The lowest zone, the 5th Cockfield, is a volatile-oil reservoir. Laboratory work conducted on crude oil from the 5th Cockfield zone shortly after field discovery demonstrated that, when contacted with dry gas, signidcant volumes of the oil could be vaporized at reservoir temperature and at an appropriately high reservoir pressure. Further study led to the conclusion that early initiation of a crude vaporization project in the 5th Cockfield zone would be superior economically to other methods of reservoir depletion. Consequently, the zone was unitized and gas injection operations started late in 1958. This paper discusses laboratory work performed in conjunction with the project, and project performance to the present. History of Development The 5th Cockfield zone in Shoats Creek is composed of a thin, very shaly, low-permeability sandstone. Oil accumulation is controlled by a structural trap bounded by faults along the north and west and by a water contact on the southern boundary (Fig. 2). The zone covers a productive area of 1,550 acres at an average depth of 9,000 ft. The net sand section is thin, having a maximum thickness of 10 ft and an average thickness of 5.5 ft (Fig. 3). Average reservoir rock properties, as determined from core analysis are presented in Table 1. Shaliness of the zone is illustrated by the typical electric log of the 5th Cockfield section in Fig. 4. Because of the thinness and poor quality of the sand, the 5th Cockfield was developed on a wide spacing. Eleven completions were made in the zone between 1956 and 1961 for an average density of 140 productive acres per completion, with the majority of wells being dually completed in the 2nd and 5th Cockfield. Average initial potential for producers in the 5th Cockfield was 130 BOPD. Oil from the 5th Cockfield has a stock-tank gravity of 50.5" API; with a bubble-point pressure of 3,515 psia, the oil was highly undersaturated at the original reservoir pressure of 4,675 psia. Pertinent properties of the oil as determined in the laboratory are presented in Table 2. Because of the volatile nature of the crude, laboratory studies of its susceptibility to vaporization, as well as a vapor-liquid phase study, were conducted in addition to a standard PVT analysis. The vaporization study was conducted in a visual cell; a stepwise illustration of this work and laboratory measurements are presented in Fig. 5. Field

Jan 1, 1969

By N. J. Grant, A. W. Mullendore, Y. Ishida

Creep tests were performed at 500°F on polished specimens of A1-3 pct Cu at stresses of 2000, 4000, and 6000 psi. The effects of the size and distnbution of the second phase were studied in connection with the mechanisms of deformation, especially grain boundary sliding. Although the amount of grain boundary sliding varied considerably for the different heat treatments, yestriction of grain boundary sliding is not due primarily to precipitate on the grain boundary. NUMEROUS prior investigations of grain boundary sliding, notably those of McLean, 1 Rachinger, 2 Rhines, Bond, and Kissel, 3 and Brunner and Grant,4 have established the importance of this phenomenon in the deformation of pure aluminum and its solid-solution alloys at elevated temperatures. An extension of this kind of study to the case of a simple two-phase structure is an important step towards understanding the deformation behavior of more complex alloys. A two-phase A1-3 pct Cu alloy was selected for this study. The creep behavior of alloys in this system has been studied by Sully and Hardy,5 by Underwood, Marsh, and Manning,' and by Pelloux, Chaudhuri, and Grant.7 In these studies, the prior heat treatments were such that some precipitation took place during the tests in most cases. Pelloux, Chaudhuri, and Grant7 studied the creep of A1-2 and 3 pct Cu alloys in the overaged condition. Their results indicated that the structure most effective in promoting high-temperature strength consisted of a fine, closely spaced grain precipitate and large, widely spaced particles on the grain boundary. The present work consists of quantitative meas- urements of grain boundary sliding during creep of an A1-3 pct CU alloy with four different precipitate distributions. The aims were to quantitatively define the role of the second phase on grain boundary sliding, and to obtain information regarding the mechanism of grain boundary sliding. MATERIALS AND PROCEDURE A high-purity A1-3 pct Cu alloy, kindly supplied by Alcoa, was used in this investigation. The composition of the alloy in weight percent was as shown in Table I. This composition is such that A12Cu exists as a second phase at temperatures below 850°F. A homogeneous grain size of 0.6 to 0.8 mm was obtained by annealing the machined test bars for 5 min at 1000°F, furnace cooling to 930°F, and homogenizing for 5 hr. Following the recrystalli-zation and homogenizing anneal, four different heat treatments shown in Fig. 1 were utilized. The F7 and F5 treatments utilize a furnace cool to the aging temperature while Q7 and Q5 have a water quench from the homogenization temperature before aging. Figs. 2 to 5, and Table 11, show the size and shape of precipitate dispersions obtained with the above heat treatments. The heat treatments produce variations in the dispersion both in the grains and along the grain boundaries. Precipitate particles along the grain boundaries are rounded and large (about 1.5 p diameter) in the F5 and F7 structures (Figs. 3 and 5). The grain boundary precipitate was somewhat smaller (0.9 p diameter) in the Q7 structure and no grain boundary precipitate was detected in the Q5 structure using light microscopy. The pre-

Jan 1, 1964

By A. J. Griest, P. D. Frost, J. R. Doig

During the past 5 years, research directed toward the development of titanium alloys having improved strength-ductility relationships and heat treatability has been carried out at Battelle for the U. S. Air Force.1"3 In the course of this work, a method of heat treating ß-stabilized titanium alloys was developed which produced a wide range of useful properties.4 The heat treatment consisted of two steps: a) solution treating at temperatures in the a-ß phase region, and b) overaging at a lower temperature in the range 800°to 1100°F. Corollary to the alloy development work, research was conducted on the mechanism of the heat-treatment reaction. The investigations of Frost and co-workers on isothermal transformation in Ti-Cr5 and Ti-Mn8 alloys disclosed the existence of the transition phase, w, during the course of the decomposition of metastable ß phase. Subsequent work at Battelle7,8 'and at Case Institute by Brotzen and co-workerss further clarified the nature of the decomposition process. Beta decomposition was found to proceed by the following series of reactions: 1 2 3 4 a + Ti, My (in eutectoid systems). ßo, ßr, and ßU refer to ß phase of original, enriched, and ultimate alloy contents, respectively. Omega is a transition phase having a complex structure. 10-13 Step 4, of course, occurs only in ß-eutectoid systems. This paper presents data correlating transformation behavior with mechanical properties for the following alloys: Ti-8Mn, Ti-8Mn-2A1, Ti-4Mn-4A1, Ti-6Al-4V, and Ti-4Fe. The isothermal decomposition of ß in titanium-manganese alloys of similar composition has been investigated by Frost and coworkers8 and the effect of various annealing treatments on alloys in this system has been studied by Holden, Ogden, and Jaffee.14 The compositions Ti-8Mn-2Al, Ti-4Mn-4A1, and Ti-6A1-4V, were studied in the present work in an effort to define more clearly the effect of aluminum on the response to solution and aging treatments. Ogden, Holden, and Jaffee15 have invesitgated the effect of aluminum on the response of a similar alloy (Ti-8.8Mn-2.46A1) to annealing treatments, and Luini and Lee16 have made an exploratory investigation of the heat-treatability of the Ti-4Mn-4Al alloy. The Ti-4Fe alloy was studied as an example of a moderate1y active eutectoid system. Holden, Ogden, and Jaffee 17 have studied Ti-Fe alloys and have presented some hardness data for aging at 400°C for alloys of Ti-2.56, 5.01, and 7.35 iron after quenching from the a-ß field (750°C). EXPERIMENTAL PROCEDURES The experimental procedures generally used in the precipitation-hardening study are outlined in the following sections. Departures from these techniques are noted in the discussions of the individual alloys. Table I presents the nominal and actual compositions of the alloys studied, together with the swaging and rolling temperatures. In all cases, these temperatures were in the a-ß field and the microstructures consisted of an equiaxed a-ß mixture. Melting and Fabrication—Except for the commer-

Jan 1, 1960

By J. P. Boisseau, C. N. J. Wagner, E. N. Aqua

An analysis ulas made of powder-paltern peaks from cold-rolled polycrystalline copper and from copper powders, compacted into briquets (1 in. diameter) with pressures up to about 106 psi. Powder-pattern peaks from both contact faces were measured with a diffractometer and CuKa radiation. Laltice-parameter measurements indicate the presence of residual stresses in the bulk specimen of the order of a - -10 kg per sq mm after 93 pct reduction in thickness, and give some evidence for the occurrence of deformation stacking faults (probability a - 0.003) in both bulk and powder samples. Fourier analyses of the line profiles were carried out on the (111) - (222) and (200) - (400) Pairs of reflections. The particle sizes decrease rapidly with increasing deformation and reach asymptotic values of De (111) = 550A and D, (200) = 350A at about 25 pct reduction in thickness or 80,000 psi pressure for compaction. The anisotropy of the particle sizes indicates the presence of microtwins and stacking faults on (111) planes. The rms strains increase also with deformation and reach limiting values of 2 x 10-3 in the [100] direction and 1 x 10-3 in the [Ill] direction at a distance L = 100A normal to the reflecting planes. THE diffraction of X-rays in cold-worked, polycrystalline, fcc metals and alloys yields Debye-Scherrer patterns in which the individual (hkl) lines may show a broadening, a shift, and an asymmetric shape.' These effects can be explained by the fragmentation of the small, coherently diffracting domains, the presence of residual elastic strains in the lattice, and the formation of stacking faults. X-ray studies of stacking faults in fcc metals and alloys have been methodically performed during the last few years, but so far most of the investigators dealt with cold-worked powder specimens obtained by filing.2-8,10-19 In such specimens, the crystals are randomly oriented and the average elastic strains are assumed to be zero, so that the observed peak shifts are due to stacking faults only. The agreement between X-ray diffraction theory1,20 and experiment is generally good. On the contrary, cold-worked, polycrystalline bulk specimens (after wire drawing, rolling, plastic deformation by tension or compression, etc.) contain residual elastic strains, which may not average to zero in the surface of the specimen and show very strong preferred orientation of certain lattice planes (texture) parallel to the specimen surface. Nonzero elastic strains also produce peak shifts, the magnitudes of which depend upon the crystallographic orientation of the reflecting lattice planes in elastically anisotropic materials as well as on the type of plastic deformation and which have to be taken into account when measuring stacking-fault probabilities in deformed bulk specimens.21-23 The purpose of the present investigations was to perform a detailed X-ray analysis on a bulk specimen of a fcc metal deformed by rolling at room temperature and on powder of the same material deformed by compaction, and to compare these results with those previously obtained on cold-worked filings.18 Pure copper was chosen for this study since it is known to produce only a small quantity of stacking faults by filing at room temperature.3,16,17,19 The residual elastic strain in the surface of the bulk copper should be the predominant factor determining

Jan 1, 1965

By W. T. Cardwell

Physically absurd, triple-valued saturations appear in the straight-forward solution of the Buckley-Leverell equations for the displacement of oil by water or gas. From an engineering viewpoint, the triple value causen no difficulty. It is well known how it may be compensnted in order to obtain physically meaningful, numerical results. From a scientific viewpoint, the question still arises: What did the triple value mean? This paper explains how and why the triple value arose in non-capillary Buckley-Leverett theory. The discussion should serve as a background for the understanding and use of the modern method of characteristics in di.~pkzc(>ment theory. INTRODUCTION Displacement theory was introduced to petroleum technologists in 1 941 by Buckley and Leverett.' Their first equation, which they wrote down without derivation, was equivalent to the following: ?s/?t= - qr/F ?f/?r (1) where S = saturation of displacing fluid (a fraction) r = time q,. = total volumetric velocity of both the displacing phase and the phase being displaced (usually, but not necessarily, assumed to be a constant) F = porosity (a fraction) f - fraction of the total volumetric velocity that is the volumetric velocity of the displacing phase (assumed to he a function of S only x = distance. Buckley and Leverett called Eq. I "a material balance equation". Actually it is derived from both a continuity equation, or material balance equation, and Darcy's law. Buckley and Leverett jumped from their Eq. 1 immediately to their Eq. 2, which was the equivalent of the following: (?x/?t)x = qr/F df/ds = qr/F f'(s) (2) The jump from Eq. 1 to Eq. 2 involves apparently simple mathematics, but in that apparently simple mathematics lies a subtle point that is part of the key to the meaning of the triple value to be discussed here. Eq. 2 may be readily interpreted as saying that a point of constant saturation (on a saturation-vs-dis-tance curve) moves with a constant velocity that is proportional to the total volumetric rate, inversely proportional to the porosity, and is otherwise a function of the saturation itself. So that if one knows the derivativc with respect to saturation of the fractional flow function, f(S), for each saturation, one knows the velocity of each point of the moving saturation-vs-distance curve. The function f(S) can he determined experimentally and its derivative f'(S) can be calculated. It turns out that the experimentally derived f'(S) is not a monotonic function of S, but instead it has a definite maximum and declines away at both high and low saturations. This in turn means, in accordance with Eq. 2, that on a moving saturation-vs-distance curve, ccrtain intermediate saturations will travel faster than the saturations either higher or lower. The result is indicated in Fig. 1. In Fig. 1, the abscissas represent distances along a column of porous medium, which column is assumed to be uniform in cross-section perpendicular to the ab-scissal direction. The ordinates represent fractions of pore space occupied by the displacing phase, which may be either water or gas. It is assumed that the saturation is uniform over all planes perpendicular to the abscissal direction. The saturation is a function only of time and one space variable. Time variation of the saturation is represented by change in shape of a curve such as curve AGJ, which represents the initial saturation-vs-

By H. O. Jahns

This paper describes the application of regression analysis for obtaining a two-dimensional areal description of heterogeneous reservoirs from short-term pressure-time data such as that obtained in interference tests. The method replaces the time-consuming trial-and-error procedure commonly used to match field data on an electric analyzer or digital computer with a systematic search which is programmed for a computer. The computer program adjusts the properties of a reservoir model automatically until a least-squares fit is obtained between observed and calculated pressure data. The reservoir is simulated by a single-phase, compressible, two-dimensional model. It is divided into a number of homogeneous blocks whose transmissibility (kh/F) and storage (Fch) values are varied to obtain the least-squares fit. The reliability of these values is determined from their standard deviations and correlation coefficients. Although the method is rigorously applicable to single-phase flow only, multiphase flow can be handled provided saturation changes are small during the test. Possibly the method can also be used to obtain a reservoir description from pressure-production history, but this application is outside the scope of this work. The paper includes, in addition to a description of the numerical procedure, a discussion of some of the problems associated with the method. Rules are given to help in selecting the number of homogeneous blocks and deciding upon their arrangement. The uniqueness of a reservoir description is considered. Finally, the use of the method is illustrated by the interpretation of field data from two interference tests. INTRODUCTION Pressure data from short-term transient tests, such as single-well and interference tests, are widely used to obtain reservoir properties. These tests are usually analyzed by assuming a simple reservoir model; very often, a homogeneous one is used. As a result, analysis of the transient data from each well frequently gives different values for reservoir properties. The problem then arises to combine all these differing results into a more detailed picture of the reservoir. One technique is to simulate the reservoir with a digital computer or with an electrical analyzer and to adjust the reservoir parameters by trial and error until the simulated pressure data are in reasonable agreement with the observed pressure data for all wells. Although this method has been used for both transient tests and pressure-history data, it is time-consuming and subjective. A second technique uses regression analysis to replace the trial-and-error procedure with a systematic search that can be programmed for a digital computer. Use of regression analysis in reservoir description was proposed recently by Jacquard and Jain.1 They divided the reservoir into a number of homogeneous blocks whose properties are varied until a least-squares fit is obtained between observed and calculated pressures. However, they did not consider their technique to be operational, mainly because of ".. .(I) the lack of experience in using the method .. . notably for the improvement of convergence; and (2) limitations imposed by the insufficiency of available computers". 1 While the analysis presented in this paper applies the same general principle used by Jacquard and Jain, the specific method is significantly different. Some differences are (1) the regression problem is solved in a different way which requires less computer time in most cases; (2) a stepwise solution, in which the detail in the reservoir description is increased from step to step, is used to improve convergence; and (3) the reliability of the estimated reservoir .properties.. as measured by their standard deviation and correlation coefficient, is estimated'

Jan 1, 1967

By F. J. Plecity, J. T. Michalak, W. C. Leslie

Isothermal recrystallization and grain growth in zone- and vacuum-melted irons and Fe-Mn alloys, up to 0.60 pct Mn, were studied in the range 480° to 650° C, after 60 pct cold reduction. In initial stages, rate of grain growth and rate of recrystallization of iron decrease with time. The recrystallization is typical of a growth-controlled process, and rate of growth is determined by the extent of recovery. Mn decreases rates of growth and of recrystallizatzon. The recrystallization process changes at about 0.30 pct Mn and nucleation may become time-depetzdet~t. In recent years, considerable effort has been expended in determining the effects of solute elements on recrystallization and boundary migration in fcc metals. The results have indicated that the effects produced by single solute additions are dependent upon both the element added and its concentration.'-' In contrast, there have been very few attempts to determine the characteristics of recrystallization and boundary migration in high-purity bcc metals, especially after heavy deformation, and the effects thereon of single solute elements.9-11 This study was undertaken to determine the recrystallization characteristics of various "high-purity" irons and the effects of manganese additions at two levels of base purity. It was hoped that the information obtained would improve our understanding of the recrystallization of pure metals and aid in formulating a theory for the effect of solute elements. The interest was not entirely academic, for the annealing of low-carbon steels, which is of very great commercial importance, is but poorly understood. MATERIALS The compositions of the irons and iron-manganese alloys used are listed in Table I. The zone-melted iron and Fe-Mn alloys were made by Battelle Memorial Institute. Iron S-1 was arc-melted in a water-cooled steel mold in an argon atmosphere. The ingot was forged into a bar, then given two horizontal zone-refining passes in an alumina boat. Iron V-4 was treated in a similar manner, but was not zone-refined. The iron for the zone-melted Fe-Mn alloys was induction melted in vacuum in MgO crucibles and cast into alumina molds. The ingots were forged into bars, machined to shape, and a groove milled down one side of each. The best available electrolytic Mn was placed in the grooves, and the bars were zone melted. The vacuum-melted Fe-Mn alloys were induction melted in this Laboratory in MgO crucibles and poured into cast-iron molds. Iron V-5 was purchased from National Research Corp. in the form of a small vacuum-cast ingot. The low-carbon steel was made by induction melting in air at the U.S. Steel Corp. Applied Research Laboratory. The history of the materials prior to the final cold reduction differed; these details are given in the Appendix. The penultimate grain size of the principal materials was kept in the range ASTM 2 to 4, except for the low-carbon steel. PROCEDURES The cold work prior to the final recrystallization anneal was kept constant at 60 pct. It is known that rolling procedure can influence the kinetics of recrystallization of ironI2; therefore, all specimens were rolled in one direction only, between clean,

Jan 1, 1962