By C. S. Roberts

Microstructural studies of a Mg-10.3 pct Al alloy showed that discontinuous precipitation during aging multiplies the grain boundary area available for easy deformation in elevated temperature creep. An increase of strain rate for a 6.2 pct Al alloy at 400°F, where precipitation and creep are concurrent, caused an increase in the volume percentage discontinuously precipitated at the completion of the process. The relatively poor elevated temperature creep resistance of heat treated alloys of the Mg-AI-Zn type was explained in these structural terms. C resistance of the heat treatable Mg-A1 based alloys is poor compared to that of Mg-Ce based alloys. While the latter show a continuous precipitate, Mg-A1 alloys prefer a discontinuous precipitate at grain boundaries. '.:' It has been concluded that the excellent creep resistance of Mg-Ce alloys was primarily due to the continuous precipitation which especially localized at the grain boundaries.' The purpose of the present investigation was to obtain a parallel correlation, if such exists, between the poor creep resistance and the state of precipitation in Mg-A1 alloys. Discontinuous precipitation produces about three times as many true grain boundaries as originally existed. This microstructure would be expected to have a marked influence in creep, where quantity of grain boundary area is important. Experimental Procedure The two experimental alloys contained 6.2 and 10.3 pct Al. They were made from electrolytic magnesium by alloying under flux and casting in 3 in. diam permanent molds. The ingots were extruded into 1 1/4 x 1/8 in. flat stock under the following conditions: billet preheat 700°F (2 hr), container and die temperature 700°F, speed 3 fpm, and area reduction ratio 45:1. The creep specimens were machined from blanks which had been solution heat treated 24 hr at 770°F and aged 16 hr at 400°F. Attempts were made to control the grain size as closely as possible for extruded stock. The grain size after solution heat treatment was about two thousandths of an inch for the 6.2 and five thousandths for the 10.3 pct Al alloy.

Jan 1, 1957

By W. F. Holbrook

IN a previous paper1 a method for the measurement of the comparative desulphurizing power of slags was described and data were presented covering the range of likely slags containing up to 10 per cent MgO In the present work the range is extended to include slags containing up to 20 per cent MgO, and the effect of temperature on 5 per cent and 15 pen cent MgO slags over the range 1475° to 1525° C is included The method used was that described in the previous paper except that some of the temperature measurements were made with a noble-metal thermocouple instead of a tungsten-graphite thermocouple Twelve-gram charges of 0 8 per cent sulphur-metal and 5-gram charge-, of slag were subjected to heating for 30 nun at a prescribed temperature The charges were analyzed for sulphur content For purposes of comparison, desulphurizing power is defined as the ratio of the percentage of sulphur found in the slag to that found in the metal Six slag and metal charges were made coincidentally in 5/8-in holes in a section of an electrode graphite rod One slag and metal charge was used as a control by means of which adjustment in the desulphurization value could be made for small variations in temperature and other factors For convenient presentation of the data, the slags are arranged in groups in each of which one of the four main slag components is constant Thus, the 15 per cent MgO slags are presented separately from those containing 20 per cent MgO SLAGS WITH MAGNESIUM OXIDE CONSTANT 15 Per cent MgO -The data on slags containing 15 per cent MgO cover a composition range of 24 to 50 per cent SI02, 5 to 27 per cent A1203 and 24 to 53 per cent CaO Variation in composition has been in steps of 2 per cent over much of the area Because the change in desulphurization power is generally gradual with gradual change in composition, certain sections have been covered m steps of 4I per cent and even

Jan 1, 1938

By L. S. Darken

IN the study of reactions occurring in liquid iron, alone or in contact with a liquid oxide or slag phase, it has been found that the experimental data over a limited range of concentration can in some cases be repre-sented satisfactorily by the simple equilibrium expression K - (p1)p1 (p2)p2 . (R1)r1(R2)r2 . where (P) denotes the concentration of a product and (R) the concentra-tion of a reactant in the reaction r1R1 + r2R2 + . . . Some of the reactions for which it holds are listed in Table 1. For others, however, the simple equation apparently does not hold. This has been attributed to an improper method of expressing concentration (for instance, weight per cent instead of mol fraction); or it has been supposed that the solutions are not ideal in the sense that the activity of a com-ponent is not proportional to its true mol fraction, But it may be that the problem has been oversimplified by neglecting some molecular species actually present; that is, by considering only the ostensible simple com-ponents and thus leaving out of account possible compound formation. It is the purpose of the present paper to point out how, in a group of related cases, a reasonable consistent assumption relative to the presence of a compound makes it possible to express the experimental data satis-factorily by the simple equilibrium expression when this compound is taken into account, and to bring into harmony data referring to different reactions in liquid iron. There are several a priori reasons for believing that solutions in liquid iron should not deviate far from ideality, provided that the concentration of solute is not too great and is expressed in proper terms. The factors that commonly lead to nonideality in systems at ordinary temperature as ionization or the occurrence of polar and nonpolar molecules-are presumably less effective in metal and in slag systems at high temperature. Again, the type of equation commonly used to express the value of

Jan 1, 1940

By Charles L. Harness

STRONTIUM is an essential constituent of celestite (strontium sulphate), of the rarer strontianite (strontium carbonate), and of a few very rare minerals. Celestite is the chief ore but strontianite is more valued except for making the purest strontium salts, because of its ease of processing. The public knows strontium mainly as the source of the red flame in fireworks but it has many other uses. PROPERTIES The celestite of commerce is a massive mineral of varying texture: coarsely crystalline, fibrous, bladed, very fine grained or earthy. The color varies greatly with the nature of the impurities but the purer specimens are light blue (Latin, caelum, sky) or white. The strontianite of commerce is a massive mineral, more or less coarsely crystalline. The color varies with the impurities. Distinctive characteristics are effervescence with acids, density (3.68 to 3.71), and crimson strontium flame. A typical British celestite before World War II analyzed: SrSO4, 96.55 pct; SrCO3, 0.17; BaSO4, 0.25; CaSO4, 0.54; MgCO3, 0.15; R20,, 0.90; Si02, 1.38.10 A German strontianite analyzed: SrCO3, 90.9 pct; CaCO3, 7.5; BaCO3, 0.1; Fe2O3, 0.05; A1203, 0.1; SiO2, 0.04; S, 0.1; P, 0.005.10 ORIGIN AND MODE OF OCCURRENCE According to Clarke,9 strontia forms about 0.02 pct of the crust of the earth and is present in most igneous rocks, but in smaller quantities than barium. Under certain conditions, large masses of celestite are deposited from sea water with anhydrite. The presence of large amounts of celestite in some saline deposits and its absence in others suggests that the deposition of celestite depends on whether certain as yet undetermined concentrations of sulphate and chloride ions are reached in the brines. The most extensive of these sedimentary deposits are those of the Keuper (Triassic) in England, of the Zechstein (Permian) in Germany, and of various Cretaceous formations in Texas, Arkansas, and Utah. Of the deposits of southeastern California and western Arizona,

Jan 1, 1949

By Leonid V. Azároff, H. N. Murty

In the course of investigating the soft X-ray absorption spectra of Ni-A1 alloys, Das and ~zfiroff' observed an anomalous brittleness in solid solutions containing 3 to 5 at. pct Al. The brittle alloys also had anomalously larger lattice constants' and the fine structure at the nickel K edge of an alloy containing 3.96 at. pct A1 unexpectedly resembled that of NiA1 more closely than that of a solid solution containing 5.51 at. pct Al. This led them to suggest the possibility that short-range ordering was produced during the homogenization anneal to which each specimen was subjected, similar to that observed in dilute solutions of vanadium and of chromium in nickel: as the principal cause of embrittlement. It was decided to repeat the above measurements on several alloys in this composition range in order to test the above hypothesis and to establish the effect of heat treatment on the alloys' properties. Three solid solutions in this range were prepared containing, respectively, 3.16, 4.00, and 4.54 at. pct Al, in addition to alloys containing 6 and 9 pct. All samples were annealed in vacuum at 1800°F for 100 hr and then furnace-cooled to room temperature, as in the original study. The lattice constants of these alloys are shown by open circles in Fig. 1 and can be seen to fit quite closely the curve established by the previously measured values, indicated by solid circles. (The experimental errors are of the order of the size of the circles, +o.oo~R.) The three alloys containing 3 to 5 at. pct A1 were found to be quite brittle, as previously reported. In order to test the possibility of ordering, these three solid solutions were again heated to 1800°F and, following a few hours at that temperature, were quenched directly to room temperature. All three alloys lost their brittleness. In order to verify the proposed ordering hypothesis, it was decided to subject each sample to several cycles of quenching and annealing (disordering and ordering). After some experimentation, it was established that reproducible results could be obtained by anneal-

Jan 1, 1968

By Eugene A. Stephenson

In most instances the fluids produced from underground reservoirs have been described as they appear at the surface, and usually it has not been necessary to distinguish between surface and reservoir phases. More recently it has become imperative to recognize the fact that changes in phase may occur between the reservoir and the receiving unit. The simple terminology of "wet" and "dry" gases and "crude petroleum oil" served our needs fairly well in the shallow, low-temperature and low-pressure fields. It has been left to the legislatures, regulatory commissions, and courts to decide whether a field is or was a gas field, an oil field, or both. This they have done by direct definition and also by implication. For example, in Texas:' (d) The term "gas well" is any well (a) which produces natural gas not associated or blended with crude petroleum oil at the time of production, or (b) which produces more than one hundred thousand (100,000) cubic feet of natural gas to each barrel of crude petroleum oil from the same producing horizon, or (c) which produces natural gas from a formation or producing horizon productive of gas only encountered in a well bore through which crude petroleum oil is also produced through the inside of another string of casing. (e) The term "oil well" is any well which produces one (1) barrel or more of crude petroleum oil to each one hundred thousand (100,000) cubic feet of natural gas. In the state of Louisiana, the same general result is achieved largely by the following paragraph :* Wells producing both oil and gas shall not waste or blow into the air an amount of gas of more value at three cents per thousand cubic feet, than the market value of the oil recovered. The Commissioner of Conservation shall allow a reasonable time to determine the status of any well. This means that for wells making both oil and gas, if n represents the price of oil in dollars, and x the allowable gas waste expressed in M cu. ft. Per day,

Jan 1, 1938

By A. R. Anderson

UNTIL recently all discussions directed at justify-ing the use of mechanical-loading equipment and conveyors have referred chiefly to tons per man and cost per ton. But there is another consideration that ? will speed the adoption of mechanical loading in mines even though tons per man on present day stand-ards were not increased nor the cost per ton decreased. With restricted immigration, improved facilities for education in our mining communities, and increased opportunities for recreation, the type of man who can or will throw 20 tons of coal per day over the side of a mine car is disappearing. Whether we will it or not provision must be made to replace muscular effort by mechanical means. Fortunately, indications are that the process will be accompanied by increased output per man and lower production cost, and though the outlook may now be a bit clouded in spots, all should profit by the change. The operator should enjoy a more stable business with more assured profit, the miners should get a better livelihood with less arduous effort and under safer and pleasanter working conditions, and the consumer should gain the assurance of a supply of coal always available at reasonable prices. That sounds like the millennium in the coal business perhaps. Of course, it is not, but there is just enough of that millennium stuff in it to encourage those of us who are working with today's problems of applying loading and conveying equipment to underground opera-tions. If we discern clearly that there can be no back-sliding, and that all will share in whatever advantages accrue, we will carry on more vigorously, and may right-fully expect to have the necessary cooperation of all the elements within the industry. As nature does not seem to have followed a definite plan in the formation of coal deposits it is not likely that any one standard method or type of equipment can be evolved for mining the coal. The method of mining that maybe most advantageously employed with load-ing machines and conveyors depends on the character of the strata overlying the coal as much as anything else.

Jan 4, 1927

By K. R. Price, M. Gauna

A high seam geologic condition exists at Jim Walter Resources No. 4 mine that requires immediate rib support after a continuous miner cuts a place. High seam mining heights are typically 2.4 to 2.6 m (8 to 9 ft) and a thick rock layer is present in the upper portion of the coal rib side. The 610-m (2000 ft) mining depth at No. 4 mine induces horizontal rib line movement after excavating an entry. Horizontal rib movement greater than 305 mm (12 in.) have been noted. When lateral movement occurs in the high seam areas, the thick rock layer, and the coal above the rock layer, become fractured and tend to roll into the entry. If not adequately supported, large rib rolls develop in the place being bolted as well as in previously mined areas that endanger men and equipment. To control this, rib support must be installed in the roof bolting operation as the bolting crew works toward the face. A rib control system has been developed for this high seam mining condition using a mechanical anchor bolt placed at an angle in the rib and installed with a modified Fletcher DDM-15 bolting machine. More than 120 km (75 miles) of entry have been supported with angle rib bolts. These angle bolts constitute 43% to 60% of the total roof and rib bolt footage in the high seam portions of No. 4 mine. The angle rib bolting system has proven safer, more effective, and more efficient than the earlier support method using bolts installed horizontally into the rib. No rib roll accidents have occurred since the angle drill bolting machines were placed in service in 1981. By securing the broken rib material with an angle bolt anchored above the coal pillar, a more effective means of rib control is achieved. Angle rib bolting does not interfere with continuous miner productivity. In addition, bolting crews are now reduced from three to two people. Total drilling supply costs are about 60% the previous cost, when compared to the previous support method using horizontal rib bolts:

Jan 1, 1985

By John Wulff, J. H. Hollomon

Service failures in brass condenser tubes are often due to corrosion. One of the commonest types of corrosion reveals a surface structure of redeposited copper.' The study of the effect of alloy addition agents in preventing this kind of corrosion has received impetus from the extensive publication of Bengough and May.2 The mechanism of such inhibition gauged from immersion corrosion,2 cell corrosion,3 and electrolytic potential4 measurements is controversial. This controversy may be attributed in part to a lack of definite knowledge5 of the actual nature of the initial films formed in corrosion experiments. In our own corrosion work on copper and 70-30 brass this lack became apparent and necessitated an examination of surface films by X-ray and electron diffraction methods. The present paper is but an introduction to the subject of inhibition and reports the structure of films formed in active corrodents. Experimental Procedure The arsenical coppers and brasses used in this investigation were made by one of the writers* in the plant of the Revere Copper and Brass Co. at Rome, N. Y. Standard commercial melting practice was followed. O.F.H.C. copper and electrolytic zinc were used and all arsenic additions were made by additions of a master copper alloy. The final analyses are given in Table I. Likewise, the extrusion, cold-rolling, and intermediate anneals employed followed standard usage. Final heat-treatments were given to all materials to produce a similar grain size (0.035 to 0.045 mm. for brass and 0.015 to 0.025 for copper) for the alloys containing various percentages of arsenic. Samples 1/2 by M by 1/4 in. were cut from sheet material resurfaced and finished with 0000 metal-lographic papers. The surfaces were all degreased in alcohol and benzine before immersion. After immersion in the corrodent, they were washed gently in tap water, dipped first in alcohol and then in pure benzine and allowed to dry in the diffraction apparatus. The reflection electron diffraction apparatus used has been described by Burwell and Wu1ff.6 Fig. I is typical of the photo-grams obtained. The X-ray apparatus was

Jan 1, 1941

By M. H. Merriss

Some years ago, at the plant of the Baltimore Copper Smelting & Rolling Co., the receipt of large quantities of copper blister running high in lead, nickel, and arsenic resulted in the formation of a great amount of very foul slag, in the anode furnaces. A typical analysis of this slag was: Gold, oz. per ton......... 0.09 Arsenic, per cent.......... 0.60 Silver, oz. per ton......'.. 13.20 Antimony, per cent........ 0.50 Copper, per cent......... 19.50 Silica, per cent............ 28.30 Lead, per cent........... 11.90 FeO, per cent............. 19.20 Nickel, per cent.......... 4.60 CaO, per cent............. 1.60 The problem was to get out the copper in marketable form, to save the gold, silver, and particularly the nickel, and to get rid of as much as possible of the lead, arsenic, and other elements that were valueless to the Baltimore plant. In a copper refinery that does not take custom material for matte smelting, the usual method is to smelt the anode slag with coke in a reducing furnace, the black copper thus formed being sent back to the anode furnaces; this was the custom at Baltimore. An average anode slag will contain, perhaps, 40 per cent. copper and such small quantities of lead, nickel, etc., that smelting will get rid of most of these impurities in the black-copper furnace slag. To treat such an impure slag in this way, however, would result in a large nickel loss, and would send back to the anode furnaces all the lead and nickel not so lost, where it would be slagged off again and returned to the black-copper furnace as a slag still more concentrated in impurities. The result would probably be a constantly increasing amount of anode slag containing a likewise constantly increasing percentage of impurities. To avoid such a disastrous closed circuit some other process had to be devised. A small multiple-tank room, built for impure copper as an adjunct to the main series electrolytic refinery, was available, so the following standard process was suggested:

Jan 1, 1924

By John Wulff, J. H. Hollomon

Service failures in brass condenser tubes are often due to corrosion. One of the commonest types of corrosion reveals a surface structure of redeposited copper.' The study of the effect of alloy addition agents in preventing this kind of corrosion has received impetus from the extensive publication of Bengough and May.2 The mechanism of such inhibition gauged from immersion corrosion,2 cell corrosion,3 and electrolytic potential4 measurements is controversial. This controversy may be attributed in part to a lack of definite knowledge5 of the actual nature of the initial films formed in corrosion experiments. In our own corrosion work on copper and 70-30 brass this lack became apparent and necessitated an examination of surface films by X-ray and electron diffraction methods. The present paper is but an introduction to the subject of inhibition and reports the structure of films formed in active corrodents. Experimental Procedure The arsenical coppers and brasses used in this investigation were made by one of the writers* in the plant of the Revere Copper and Brass Co. at Rome, N. Y. Standard commercial melting practice was followed. O.F.H.C. copper and electrolytic zinc were used and all arsenic additions were made by additions of a master copper alloy. The final analyses are given in Table I. Likewise, the extrusion, cold-rolling, and intermediate anneals employed followed standard usage. Final heat-treatments were given to all materials to produce a similar grain size (0.035 to 0.045 mm. for brass and 0.015 to 0.025 for copper) for the alloys containing various percentages of arsenic. Samples 1/2 by M by 1/4 in. were cut from sheet material resurfaced and finished with 0000 metal-lographic papers. The surfaces were all degreased in alcohol and benzine before immersion. After immersion in the corrodent, they were washed gently in tap water, dipped first in alcohol and then in pure benzine and allowed to dry in the diffraction apparatus. The reflection electron diffraction apparatus used has been described by Burwell and Wu1ff.6 Fig. I is typical of the photo-grams obtained. The X-ray apparatus was

Jan 1, 1941

By W. F. Holbrook

In a previous paper1 a method for the measurement of the comparative desulphurizing power of slags was described and data were presented covering the range of likely slags containing up to 10 per cent MgO. In the present work the range is extended to include slags containing up to 20 per cent MgO, and the effect of temperature on 5 per cent and 15 per cent MgO slags over the range 1475' to 1525' C. is included. The method used was that described in the previous paper except that some of the temperature measurements were made with a noble-metal thermocouple instead of a tungsten-graphite thermocouple. Twelve-gram charges of 0.8 per cent sulphur-metal and 5-gram charges of slag were subjected to heating for 30 min. at a prescribed temperature. The charges were analyzed for sulphur content. For purposes of comparison, desulphurizing power is defined as the ratio of the percentage of sulphur found in the slag to that found in the metal. Six slag and metal charges were made coincidentally in 5/8in. holes in a section of an electrode graphite rod. One slag and metal charge was used as a control by means of which adjustment in the desulphurization value could be made for small variations in temperature and other factors. For convenient presentation of the data, the slags are arranged in groups in each of which one of the four main slag components is constant. Thus, the 15 per cent MgO slags are presented separately from those containing 20 per cent MgO. Slags with Magnesium Oxide Constant 15 Per cent Mg0.—The data on slags containing 15 per cent MgO cover a composition range of 24 to 50 per cent SiO2, 5 to 27 per cent A1203 and 24 to 53 per cent CaO. Variation in composition has been in steps of 2 per cent over much of the area. Because the change in desulphurization power is generally gradual with gradual change in composition, certain sections have been covered in steps of 4 per cent and even

Jan 1, 1938

By A. M. Hall

Sulphur, even in small amounts, may often be harmful to nickel and high-nickel alloys, causing impairment of mechanical strength and destruction of malleability and ductility, as shown by Merica and Waltenberg.l,2 It may act either in the form of nonmetallic inclusions produced in the liquid state during furnacing or as reaction products resulting from its diffusion into the solid metal. In recognizing the action of this element, ability to identify its various forms by means of the microscope is often of considerable importance, especially when direct quantitative methods are inapplicable. Of the sulphur compounds associated with nickel and high-nickel alloys, the sulphides that may be found in malleable nickel, Monelt and Inconel are an important group. These sulphides were investi- gated by metallographic methods in order to provide descriptive data by which to identify them. The nominal compositions of malleable nickel, Monel and Inconel are given in Table I. The term "sulphide" is employed here in a very general sense, to designate a substance in which sulphur and one or more metallic elements are combined. The term includes any combinations of compounds and solid solutions. Method of Investigation Three groups of small laboratory melts were made, one group to represent each of the three types of alloy under investigation. Within each group, a number of ingots with a sufficient variety of chemical analyses were prepared so that the effect of each of the elements entering the complete commercial alloy could be isolated and observed. In most cases, to facilitate metallographic study by exaggerating the number and size of the resulting sulphides, somewhat greater amounts of the minor elements were added than are present in the commercial alloys. Likewise, considerably more sulphur was added than is normal, but not enough to complicate the system. Transverse sections were cut at a point one third of the distance from the butt to the head of each ingot, polished and examined with an inverted stage metallo-graph equipped with a combination polar -izing-analyzing vertical illuminator. The light source was a tungsten-mercury vapor arc lamp.

Jan 1, 1943

By F. Cadena, Fred C. Bond, Walter L. Maxon

Grinding is one of the major problems in present-day milling practice, and in many cases, it represents one of the main items of expense. It becomes necessary from time to time, to compare grinding practice in one plant with that in another plant, and in making such comparisons, it would be very desirable were there available accepted standards of grinding resistance for the materials involved. Such a set of grinding constants would also be of considerable value in planning new grinding installations. There have been some tests published, notably those of Lennox,' which have been generally cited as a basis for such comparisons. Most of the tests made have been based upon open-circuit grinding, in which a weighed sample of the ore was crushed to pass a certain mesh, and was then ground under certain conditions, either wet or dry. Grinding was continued until a certain desired fineness was attained, and the comparisons based on the grinding time, or the samples were all ground for a certain specified length of time and comparison based upon the screen analysis of the products. Such methods have been acceptable where the ore was to be ground in open circuit. However, in modern milling practice, many grinding problems involve closed circuits wherein the oversize returns to the mill and a large circulating load builds up. A method of testing that does not take the circulating load into consideration might yield results quite different from those to be expected in practice, because the minerals in the ore that offer maximum resistance to grinding will accumulate in the circulating load up to an equilibrium value. Thus the nature of the ore charge in the mill at any instant may differ greatly from that of the new feed, with a consequent error in the rate of grinding determined by such a method. For example, let it be assumed that an ore to be tested consists of equal parts of difficult grinding mineral and easy grinding mineral. This is to be compared with an ore used as a standard, and consisting of minerals which are all of about the same grindability. If a comparison

Jan 1, 1935

By A. M. Hall

Sulphur, even in small amounts, may often be harmful to nickel and high-nickel alloys, causing impairment of mechanical strength and destruction of malleability and ductility, as shown by Merica and Waltenberg.l,2 It may act either in the form of nonmetallic inclusions produced in the liquid state during furnacing or as reaction products resulting from its diffusion into the solid metal. In recognizing the action of this element, ability to identify its various forms by means of the microscope is often of considerable importance, especially when direct quantitative methods are inapplicable. Of the sulphur compounds associated with nickel and high-nickel alloys, the sulphides that may be found in malleable nickel, Monelt and Inconel are an important group. These sulphides were investi- gated by metallographic methods in order to provide descriptive data by which to identify them. The nominal compositions of malleable nickel, Monel and Inconel are given in Table I. The term "sulphide" is employed here in a very general sense, to designate a substance in which sulphur and one or more metallic elements are combined. The term includes any combinations of compounds and solid solutions. Method of Investigation Three groups of small laboratory melts were made, one group to represent each of the three types of alloy under investigation. Within each group, a number of ingots with a sufficient variety of chemical analyses were prepared so that the effect of each of the elements entering the complete commercial alloy could be isolated and observed. In most cases, to facilitate metallographic study by exaggerating the number and size of the resulting sulphides, somewhat greater amounts of the minor elements were added than are present in the commercial alloys. Likewise, considerably more sulphur was added than is normal, but not enough to complicate the system. Transverse sections were cut at a point one third of the distance from the butt to the head of each ingot, polished and examined with an inverted stage metallo-graph equipped with a combination polar -izing-analyzing vertical illuminator. The light source was a tungsten-mercury vapor arc lamp.

Jan 1, 1943

By F. C. Stanford

The work of an engineer is to direct natural forces so that the: bring about the results that he wishes to secure. Heretofore he ha concerned himself chiefly with physical forces and inanimate objects until he has secured a truly marvelous degree of control over them The great problem of the present age is to secure a like degree of know1 edge and control of the human factor. Progress has already been made along this line, but it is only a beginning. Wilhelm Ostwald says tha scientific knowledge enables a man to be a true prophet; but it must be remembered that a good many people do not seem to be able to main tain a high average in prophecy. In short, 'the average of knowledge is not equal to the average needs of the present time, but continually fails to keep pace with it. It has been aptly said that the really essentia need of the period is for more brains; if we only had sufficient knowledg and sagacity we could not only solve all difficulties, but prevent then from arising. This generalization holds good for an industrial organization. Th most vital need of the management is for more brains. The logica course for an engineer in charge of an industrial organization is, therefore to direct whatever forces may be at his command toward the development training, and guiding of all the brains in his organization. This is easie said than done, for it involves the carrying on toward two objective: the maximum of productive work, and the development of the individual who perform it. This is essentially like the rebuilding and enlarging of plant, keeping it in full operation the while. On the other hand, if th aim is merely for maximum production from an organization, withou offering opportunity for development, the final outcome will necessari be like that of a plant that is driven at full capacity without stoppin for repairs or improvements; it eventually becomes so run down th either a complete rebuilding is necessary or else it has to be abandone

Jan 1, 1918

By Benjamin C. Craft

As predicted, during 1937 South Louisiana witnessed one of the most active drilling campaigns in the history of the area, resulting in the discovery .of 14 new fields. The economic importance of 10,000-ft. production was far-reaching and the objective depths placed on some wildcats was 12,000 feet. Most of the important discoveries and deep tests were in the delta area between the Atchafalaya and Mississippi Rivers, where the upper Miocene sands were found productive between 10,000 and 11,000 ft. The casing program on these wells usually called for a protection string of 95/8-in. casing at approximately 9500 ft. Drilling barges with the heaviest equipment were used where water transportation was available. The oil production for South Louisiana during 1937 was 62,147,690 bbl., as compared with 51,968,727 bbl. during 1936, an increase of 19.5 per cent. There were 281 oil and gas wells and 172 dry holes completed during 1937 as compared with 262 oil and gas wells and 135 dry holes during the previous period. New Fields Gibson.—The first discovery for the year was in the Gibson area, where Shell Petroleum Corporation's Realty Operators No. 1, sec. 18, 17 S., 15 E., Terrebonne Parish, was completed flowing 780 bbl. of 38° A.P.I. oil daily through a 14/64-in. choke with a tubing pressure of 1700 lb. Production is from upper Miocene sand found from 9461 to 9483 feet. Abbevil1e.—The discovery well for the Abbeville field was Continental Oil Company's Hebert No. 1, sec. 20, 12 S., 3 E., Vermilion Parish, completed flowing 50 bbl. of distillate and 2 million cubic feet of gas through a 3/16-in. choke with a tubing pressure of 2550 lb. The well was plugged back from 12,216 ft. in the Chickisawhay, and is producing through perforations from upper Miocene sand found from 7668 to 7682 ft. Later in the year, the same operators completed Brookshire No. 1, sec. 66, 12 S., 3 E., flowing 366 bbl. of 42° A.P.I. oil per day through a 3/16-in. choke with a tubing pressure of 1800 lb. This well was com-

Jan 1, 1938

By Raymond Mancha

THE number of installations of propeller mine fans completed during the years of 1936 and 1937 is evidence of the increasing popularity of the propeller fan with the American mining industry. During the period from 1931 to 1936, there were several different low-pressure, low-efficiency propeller fans available, which filled a definite need in replacing inefficient centrifugal fans operated at comparatively low pressure by means of purchased power. Since 1936, however, the trend toward the propeller fan has greatly increased, as propeller fans are now available practically without pressure limitations and capable of efficiencies high enough to warrant replacement of efficient centrifugal fans in many instances. Few manufacturers of propeller mine fans base their fan-operating characteristics upon similar test methods, primarily because of inadequate facilities for testing in the factory and the need of a test code incorporating a calibrated duct or nozzle that makes possible the testing of large propeller fans quickly, accurately and without prohibitive expense and space requirements. As a result, fan manufacturers have resorted to various methods for testing large propeller fans in the factory, and different yardsticks have produced uncomparable and often inaccurate performance data. It is the purpose of this paper to describe and discuss in detail the test procedure of the Jeffrey Manufacturing Co., which has been proved both accurate and practical. Fig. 1 shows a plan, a side elevation and two end elevations of the test duct with a propeller fan of the exhaust type in place. Testing propeller fans exhausting permits greater accuracy than testing these fans blowing, because in the former uniform flow conditions are more easily established at Pitot tube stations where fan pressure and air-volume measurements are desired. Any residual rotation remaining in the air discharged from a propeller fan blowing into a test duct must be removed before an attempt is made to obtain accurate pressure and volume readings. Although various devices for straightening the air may be placed between the blowing fan and the volume-measuring station without resulting complications, uniform flow so obtained at the pressure-measuring station necessitates corrective calculations to compensate for duct resistance

Jan 1, 1939

By N. Lilienberg

Refractory materials play much the same part in the producion of metals as houses and shelter for men, and it therefore seems useful to discuss sometimes the ways of manufacturing them. In fact, it appears to me that too little has been said on this important matter, probably because the manufacturers of fire-brick do not care to publish details for the benefit of competitors, but perhaps, also, by reason of the indulgent indifference of consumers. Judging from the revolutions in the manafacture of iron and steel caused by using calcareous materials for the furnace-bottoms, it does not seem improbable that in the future basic bricks may be produced suffciently strong for building also side-walls and arches, and perhaps, also, for use in blast-furnaces. But the existence of the present difficulties of great shrinkage in burning and small strength against compression, which limit the possibility of using basic bricks to Bessemer converters and such open-hearth furnaces as permit the bottom to be separated from the superstructure, seems to indicate still a long and extensive use of silica fire-bricks. I am not prepared to say anything about American fire-brick making, but knowing that industries abroad are watched with increasing interest by American manufacturers, I have imagined that this association would like to hear some facts about the way firebricks arc made in my country—Sweden. Well-known as it is that Sweden produces a high quality of iron, it is perhaps not so universally known that the same country produces a very high grade of silica fire-brick, whereby most of its own wants are supplied. In giving the following sketch I can, of course, not claim that all the facts are entirely new, but shall consider my object attained if American manufacturers can derive some benefit from the comparison of the following methods with their own, and if some discussion on this important subject can be aroused which will contribute to further progress. In order to show the extensive use of domestic fire-bricks in Sweden, where English bricks are easily obtainable, I mention the fact that about twelve millions of all kinds of fire-bricks (reduced to

Jan 1, 1885

By W. F. Holbrook

In a previous paper1 a method for the measurement of the comparative desulphurizing power of slags was described and data were presented covering the range of likely slags containing up to 10 per cent MgO. In the present work the range is extended to include slags containing up to 20 per cent MgO, and the effect of temperature on 5 per cent and 15 per cent MgO slags over the range 1475' to 1525' C. is included. The method used was that described in the previous paper except that some of the temperature measurements were made with a noble-metal thermocouple instead of a tungsten-graphite thermocouple. Twelve-gram charges of 0.8 per cent sulphur-metal and 5-gram charges of slag were subjected to heating for 30 min. at a prescribed temperature. The charges were analyzed for sulphur content. For purposes of comparison, desulphurizing power is defined as the ratio of the percentage of sulphur found in the slag to that found in the metal. Six slag and metal charges were made coincidentally in 5/8in. holes in a section of an electrode graphite rod. One slag and metal charge was used as a control by means of which adjustment in the desulphurization value could be made for small variations in temperature and other factors. For convenient presentation of the data, the slags are arranged in groups in each of which one of the four main slag components is constant. Thus, the 15 per cent MgO slags are presented separately from those containing 20 per cent MgO. Slags with Magnesium Oxide Constant 15 Per cent Mg0.—The data on slags containing 15 per cent MgO cover a composition range of 24 to 50 per cent SiO2, 5 to 27 per cent A1203 and 24 to 53 per cent CaO. Variation in composition has been in steps of 2 per cent over much of the area. Because the change in desulphurization power is generally gradual with gradual change in composition, certain sections have been covered in steps of 4 per cent and even

Jan 1, 1938